Patent Application
20140057154
The invention is directed to new or improved battery separators, components, batteries, and/or related methods of production and/or use, to a battery separator with a gel impregnated nonwoven for use in a lead acid battery, to gel impregnated nonwovens, and to batteries including such separators or nonwovens.
Lead acid batteries have evolved, over time, as the demands for a source of mobile electric power have grown. This technology is getting ready to evolve once again with the rising popularity of the hybrid electric vehicle (HEV) or ‘micro HEV.’ The demands on the battery for the HEV are different from those of the conventional gasoline powered vehicle. For example, the HEV's battery will operate in a partial state of charge (PSoC), approximately 50 to 80% charge. As such, the battery will undergo shallow charge/recharge cycles, and will not undergo overcharge where dissociation of water evolves hydrogen and oxygen that mixes stratified acid within the cell. Additionally, retention of active material is also an issue that must be addressed.
Accordingly, there is a need for new separator technology to meet and overcome the new challenges arising with the advent of the HEVs.
For the purpose of illustrating the invention, there is shown in the drawings a form that is presently preferred; it being understood, however, that this invention is not limited to the precise arrangements and instrumentalities shown.
In one embodiment, battery separator for a lead acid battery includes a gel impregnated nonwoven. The nonwoven preferably includes an acid dissolvable fiber and a non-acid dissolvable fiber. The gel may have a basis weight in a range of about 20-160% of the nonwoven's basis weight. In another embodiment, battery separator for a lead acid battery includes a microporous membrane with the gel impregnated nonwoven adhered thereto.
Referring to
The microporous membrane 12 may be any conventional microporous membrane. In one embodiment, the membrane 12 may be the membrane conventionally used in lead acid batteries, for example those available from Daramic LLC of Owensboro, Ky. Such conventional membranes may be made of a filled polymer, where the polymer may be a polyolefin, such as ultrahigh molecular weight polyethylene (UHMWPE) and the filler is a silica, see for example U.S. Pat. No. 3,351,495; U.S. Pat. No. 3,917,772; U.S. Pat. No. 4,927,722; U.S. Pat. No 5,230,843; U.S. Pat. No. 5,679,479; U.S. Pat. No. 5,776,630; U.S. Pat. No. 5,789,103; U.S. Pat. No. 6,410,183; WO001/13,442; Besenhard, J. O., Editor, Handbook of Battery Materials, Wiley-VCH Verlag GmbH, Weinheim, Germany (1999), Chapter 9, pp. 245-292, which are incorporated herein by reference. These membranes may include a plurality of ribs 16 standing up on a backweb 18. The ribs 16 generally run in the machine direction (MD). The membrane 14 may also include a plurality of lateral edge ribs 20. Lateral edge ribs 20 also stand up on backweb 18, but generally have a height less than the height of ribs 16. Lateral edge ribs 20 generally run in the machine direction (MD). Membrane 12 may also include a plurality of negative cross ribs 22 (not shown). The negative cross ribs 22 stand up from the back side of the membrane (i.e., the side opposite the side with ribs 16) and generally run in the cross machine direction (TD).
The gel impregnated nonwoven 14 may be adhered to the membrane 12. Adhered, in one embodiment, refers to joined together or bonded. The nonwoven 14 may be bonded to the tops of the ribs 16. The bonds 24 may be formed by gluing and/or welding. Welding may include pressure welding, thermal welding, and/or ultrasonic welding.
The nonwoven of the gel impregnated nonwoven 14 may be any nonwoven. In one embodiment, the nonwoven may be a blend of acid dissolvable fibers and non-acid dissolvable fibers. The acid dissolvable fibers may be any fiber that is dissolvable in the acid of the battery's electrolyte (in the lead acid battery, this acid is typically sulfuric acid) and allows the gel (or its precursor) to adhere thereto. In one embodiment, the dissolvable fiber may be a cellulosic fiber, polyamide (e.g., nylon) fiber, co-polymers thereof, or blends thereof. The non-dissolvable fibers may be any fiber that is not dissolvable in the acid of the battery's electrolyte and may or may not allow the gel to adhere thereto. In one embodiment, the non-dissolvable fibers may be synthetic fibers, glass fibers, or a blend thereof. The synthetic fibers include polyolefins (e.g., polyethylene, polypropylene, polybutylene, etc.), polyesters (i.e., polyethylene terephthalate (PET), polybutylene terephthalate (PBT), etc.), acrylics, co-polymers thereof, and/or blends thereof. The weight ratio of the dissolvable fibers to the non-dissolvable fibers, in one embodiment may be in the range of about 20-80:20-80; in another embodiment, the ratio may be about 30-70:30-70; in yet another embodiment, the ratio may be about 40-60:40-60; and including all sub sets in the ranges set forth before. The basis weight of the nonwoven may be in the range of about 10-50 grams/square meter (gsm), in another embodiment, about 20-40 gsm, or another embodiment, about 25-35 gsm, and including all sub sets in the ranges set forth before. The nonwoven may have a porosity greater than about 100 l/m2·s, or about 1200 l/m2·s, or about 1500 l/m2·s. In one embodiment, the nonwoven may be the ‘pasting paper’ used in the formation of the plates or electrodes of the lead acid battery. One such pasting paper is commercially available from Glatfelter GmbH as DYNAGRID NG 28.
The gel (or gelling agent) of the gel impregnated nonwoven 14 may be any material capable of forming a gel when brought into contact with the electrolyte of the battery. The gel is formed when this material is in contact with the electrolyte. These gels may be capable of surviving the electrolyte of the battery, for example having the solubility and physical adsorption properties enabling semi-dissolution resulting in gel formation and acid incorporation within the pH constraints of the battery's electrolyte. For example, the gelling agent may be applied to the nonwoven in a slurry (gelling agent), fluid (optional), and binder (optional). Then, the slurry may be dried, whereby the gelling agent is adhered to (or impregnated into) the nonwoven. When the gel impregnated separator is immersed in the electrolyte, the gelling agent adsorbs the acid of the electrolyte, swells, and thereby forms the gel. In one embodiment, the gel is a silica (SiO2) based gel. The silica may be any silica including precipitated, fumed, colloidal, and/or chemically modified. In another embodiment, the gelling agent may be a silicate and/or a non-silicate mineral or chemical compound or a superabsorbent polymer.
The gel is impregnated into the nonwoven. Impregnated means that the gel is adhered to all or most of the fibers of the nonwoven, while at least some of the porosity of the nonwoven is maintained. The gel may be impregnated into the nonwoven in any manner. The gel (or its precursor) may typically be applied to the nonwoven in a non-gel state (i.e., the precursor). The gel may be applied to the nonwoven by curtain-coating, dipping, spraying, rolling, brushing, and the like. In one embodiment, the gel may comprise about 20-160 weight % of the basis weight of the nonwoven; in another embodiment, from about 25-150 weight %; in yet another embodiment, from about 40-100%; in yet another embodiment, from about 50-80%; and including all sub sets in the ranges set forth before. A binder may be added to the gelling agent (or its precursor) prior to application to the nonwoven in order to aid in the adhesion of this material to the nonwoven. The binder may be any binder. In one embodiment, the binder may be latex, polyvinyl alcohol (PVA), and combinations thereof.
In use, the gel impregnated nonwoven may be placed adjacent to (and pressed against) the positive electrode (referring to battery discharge) and the microporous membrane, if used, may be placed adjacent to the negative electrode (referring to discharge). While not being bound to any particular theory, it is believed that when the inventive separator is placed in the electrolyte of the battery, the acid dissolves away the dissolvable fibers leaving the gel intact to form a hollow tube of residual material. This hollow tube is very porous and reduces the resistance of the separator, in comparison to the gel impregnated nonwoven with the dissolvable fibers intact.
The foregoing separator may be used in any battery. In one embodiment, the battery may be a lead acid battery. The separator may be used in, for example, batteries for use in the following exemplary applications: ISS (idle stop start batteries), HEV (hybrid electric vehicle batteries), and EFB (electric fuel batteries)
The TABLE shows a comparison between nonwovens with and without gelling agent. The nonwoven used was Glatfelter's DYNAGRID 328NG pasting paper (basis weight 28 gsm) and having 40 wt % dissolvable fiber (cellulosic) and 60 wt % non-dissolvable fiber (polyester).
Each nonwoven was treated as follows: A—nonwoven without gelling agent soaked in sulfuric acid for 24 hours; B—nonwoven with 11 gsm of silica after 2 weeks in a cell; C—nonwoven with 16 gsm of silica after 2 weeks in a cell; and D—nonwoven with 21 gsm of silica after 2 weeks in a cell. Five sheets were tested and the average resistance was reported.
In accordance with at least selected embodiments, aspects or objects, the present invention addresses the need for, provides or is directed to new or improved battery separators, components, batteries, and/or related methods of production and/or use, to battery separators with a gel impregnated nonwoven for use in a lead acid batteries, to gel impregnated nonwovens, and/or to batteries including such separators or nonwovens.
In accordance with at least selected embodiments, aspects or objects, the present invention addresses the need for, provides or is directed to a battery separator for a lead acid battery comprising: a gel impregnated nonwoven, said nonwoven comprising an acid dissolvable fiber and a non-acid dissolvable fiber. The above battery separator wherein said nonwoven having a basis weight and said gel having a basis weight in a range of about 20-160% of said nonwoven basis weight. The above battery separator wherein said gel being a silica gel. The above battery separator wherein said acid dissolvable fibers being cellulosic fibers. The above battery separator wherein said non-dissolvable fibers being polymer and/or glass fibers. The above battery separator wherein a weight ratio of dissolvable fiber to non-dissolvable fiber being in a range of about 20-80:20-80. The above battery separator further comprising a microporous membrane adhered to said gel impregnated nonwoven. The above battery separator wherein said membrane being a polymer filled membrane. The above battery separator wherein said polymer being a polyolefin. The above battery separator wherein said filler being a silica based material. The above battery separator wherein said membrane having ribs. The above battery separator wherein said ribs being ribs running in a machine direction and/or a cross machine direction and being on the positive or negative face. The above battery separator wherein said nonwoven being adhered to said membrane by bonding. The above battery separator wherein said bonding being gluing and/or welding. The above battery separator wherein said welding including pressure, thermal, and/or ultrasonic. In a battery, the improvement comprising the above battery separator.
A battery separator for a lead acid battery comprising: a nonwoven having non-dissolvable fibers, and tubes formed of a gel. In a battery, the improvement comprising the above battery separator.
A gel impregnated nonwoven for use in a composite battery separator for a lead acid battery such as an ISS, HEV, or EFB battery, and comprising a gel impregnated nonwoven having non-dissolvable fibers, and tubes formed of a gel. In a battery, the improvement comprising the above nonwoven.
In at least one particular embodiment, a battery separator for a lead acid battery includes a gel impregnated nonwoven. The nonwoven includes an acid dissolvable fiber and a non-acid dissolvable fiber. The gel may have a basis weight in a range of about 20-160% of the nonwoven's basis weight. In another embodiment, a battery separator for a lead acid battery includes a microporous membrane with the gel impregnated nonwoven adhered thereto.
The present invention may be embodied in other forms without departing from the spirit and the essential attributes thereof, and, accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicated the scope of the invention.
This application claims priority to and the benefit of co-pending provisional U.S. application Ser. No. 61/692,058 filed Aug. 22, 2012 which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 61692058 | Aug 2012 | US |