Battery with Acidified Cathode and Lithium Anode

Abstract
A battery comprising an acidified metal oxide (“AMO”) material, preferably in monodisperse nanoparticulate form 20 nm or less in size, having a pH <7 when suspended in a 5 wt % aqueous solution and a Hammett function H0 >−12, at least on its surface.
Description
FIELD

This disclosure is in the field of materials useful in chemical energy storage and power devices such as, but not limited to, batteries. More specifically, this disclosure relates to a battery cell with a cathode and/or an anode comprising acidified metal oxide (“AMO”) nanomaterials. In some embodiments, a battery cell is constructed with an AMO cathode and an anode consisting substantially of elemental lithium.


BACKGROUND OF THE INVENTION

Metal oxides are compounds in which oxygen is bonded to metal, having a general formula MmOx. They are found in nature but can be artificially synthesized. In synthetic metal oxides the method of synthesis can have broad effects on the nature of the surface, including its acid/base characteristics. A change in the character of the surface can alter the properties of the oxide, affecting such things as its catalytic activity and electron mobility. The mechanisms by which the surface controls reactivity, however, are not always well characterized or understood. In photocatalysis, for example, the surface hydroxyl groups are thought to promote electron transfer from the conduction band to chemisorbed oxygen molecules.


Despite the importance of surface characteristics, the metal oxide literature, both scientific papers and patents, is largely devoted to creating new, nanoscale, crystalline forms of metal oxides for improved energy storage and power applications. Metal oxide surface characteristics are ignored and, outside of the chemical catalysis literature, very little innovation is directed toward controlling or altering the surfaces of known metal oxides to achieve performance goals.


The chemical catalysis literature is largely devoted to the creation of “superacids”—acidity greater than that of pure sulfuric acid (18.4 M H2SO4)—often used for large-scale reactions such as hydrocarbon cracking. Superacidity cannot be measured on the traditional pH scale, and is instead quantified by Hammett numbers. Hammett numbers (H0) can be thought of as extending the pH scale into negative numbers below zero. Pure sulfuric acid has an H0 of −12.


There are, however, many reaction systems and many applications for which superacidity is too strong. Superacidity may, for example, degrade system components or catalyze unwanted side reactions. However, acidity may still be useful in these same applications to provide enhanced reactivity and rate characteristics or improved electron mobility.


The battery literature teaches that acidic groups are detrimental in batteries, where they can attack metal current collectors and housings and cause deterioration in other electrode components. Further, the prior art teaches that an active, catalytic electrode surface leads to electrolyte decomposition which can result in gas generation within the cell and ultimately in cell failure.


A need exists for battery implementation having a synthetic metal oxide that is acidic but not superacidic at least on its surface and is deployed within the anode and/or cathode. Further, existing battery construction techniques should be updated to take full advantage of the new materials available according to the present disclosure as well as previously known materials.


SUMMARY OF THE INVENTION

This application describes materials corresponding to acidified metal oxides (“AMO”) and applications for using the AMOs, including in batteries, such as in battery electrode materials, as catalysts, as photovoltaic or photoactive components, and sensors. Techniques for preparing AMOs and devices comprising AMOs are further disclosed. The disclosed AMOs are optionally used in combination with acidic species to enhance their utility.


This application further describes high capacity electrochemical cells including electrodes comprising a metal oxide. Techniques for preparing metal oxides and electrochemical cells comprising metal oxides are further disclosed. Optionally, the disclosed metal oxides are used in conjunction with conductive materials to form electrodes. The formed electrodes are useful with metallic lithium and conventional lithium ion electrodes as the corresponding counter electrodes. The disclosed metal oxides are optionally used in combination with acidic species to enhance their utility.


The AMOs described include those in the form of a nanomaterial, such as a nanoparticulate form, which may be monodispersed or substantially monodispersed and have particle sizes less than 100 nm, for example. The disclosed AMOs exhibit low pH, such as less than 7 (e.g., between 0 and 7), when suspended in water or resuspended in water after drying, such as at a particular concentration (e.g., 5 wt. %), and further exhibit a Hammett function, H0, that is greater than −12 (i.e., not superacidic), at least on the surface of the AMO.


The surface of the AMOs may optionally be functionalized, such as by acidic species or other electron withdrawing species. Synthesis and surface functionalization may be accomplished in a “single-pot” hydrothermal method in which the surface of the metal oxide is functionalized as the metal oxide is being synthesized from appropriate precursors. In some embodiments, this single-pot method does not require any additional step or steps for acidification beyond those required to synthesize the metal oxide itself, and results in an AMO material having the desired surface acidity (but not superacidic).


Optionally, surface functionalization occurs using strong electron-withdrawing groups (“EWGs”)—such as SO4, PO4, or halogens (Br, Cl, etc.)—either alone or in some combination with one another. Surface functionalization may also occur using EWGs that are weaker than SO4, PO4, or halogens. For example, the synthesized metal oxides may be surface-functionalized with acetate (CH3COO), oxalate (C2O4), and citrate (C6H5O7) groups.


Despite the conventional knowledge that acidic species are undesirable in batteries because they can attack metal current collectors and housings and cause deterioration in other electrode components, and that active, catalytic electrode surfaces can lead to electrolyte decomposition, gas generation within the cell, and ultimately in cell failure, the inventors have discovered that acidic species and components can be advantageous in batteries employing AMO materials in battery electrodes.


For example, the combination or use of the AMO with acidic species can enhance the performance of the resultant materials, systems or devices, yielding improved capacity, cyclability, and longevity of devices. As an example, batteries employing AMO materials in combination with acidic electrolytes or electrolytes containing acidic species as described herein exhibit considerable gains in capacity, such as up to 100 mAh/g or more greater than similar batteries employing non-acidified electrolytes or electrolytes lacking acidic species. In some mebodiments, improvements in capacity between 50 and 300 mAh/g may be achieved. In addition, absolute capacities of up to 1000 mAh/g or more are achievable using batteries having acidified electrolytes or electrolytes including acidic species. Moreover, cycle life of a battery may be improved through the use of acidic electrolytes or electrolytes containing acidic species, such as where a battery's cycle life is extended by up to 100 or more charge-discharge cycles.


In addition or alternatively, batteries including an electrode, such as a cathode or anode, that is itself acidic or that includes acidic species, such as an organic acid, may also be beneficial and, again, contrary to the conventional teaching in battery technology. For example, batteries incorporating acidic electrodes or acidic species within the electrode may enhance the performance and yield improved capacity, cyclability, and longevity, particularly when used in electrodes including AMO materials. Capacity gains of up to 100 mAh/g or greater are achievable. Cycle life of a battery may also be improved through the use of acidic electrodes or electrodes containing acidic species, such as where a battery's cycle life is extended by up to 100 or more cycles. As an example, an acidic electrode or an electrode that includes acidic species may exhibit a pH less than 7 (but not be superacidic), such as when components of the electrode are suspended in water (or resuspended in water after drying) at 5 wt. %.


Electrodes corresponding to the present disclosure may comprises a layered structure including a first set of layers comprising a conductive material and a second set of layers comprising the metal oxide, such as an acidified metal oxide (AMO) nanomaterial. Optionally, the first set of layers and the second set of layers may be provided in an alternating configuration. Optionally, the first set of layers and the second set of layers independently comprises between 1 and 20 layers. Optionally, the first set of layers and the second set of layers independently have thicknesses of between 1 μm and 50 μm, between 2 μm and 25 μm, between 3 μm and 20 μm, between 4 μm and 15 μm, or between 5 μm and 10 μm. Optionally, the metal oxide comprises between 5 and 90 weight percent of the second set of layers, such as 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, or 90 weight percent. Optionally, the conductive material and the binder each independently comprise between 5 and 90 weight percent of the first set of layers such as 25, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, or 90 weight percent.


A first electrode optionally comprises the metal oxide at up to 95 weight percent of the first electrode, up to 80 weight percent of the first electrode, up to 70 weight percent of the first electrode, between 1 and 50 weight percent of the first electrode, between 1 and 33 weight percent of the first electrode, between 15 and 25 weight percent of the first electrode, between 55 and 70 weight percent of the first electrode, between 20 and 35 weight percent of the first electrode, between 5 and 15 weight percent of the first electrode. Specific examples of metal oxide weight percents for the first electrode include 1%, 5%, 11%, 12%, 13%, 14%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30%, 31%, 32%, 33%, 60%, 61%, 62%, 63%, 64%, 65%, etc. Optionally, the conductive material and the binder each independently comprise the majority of the remainder of the first electrode. For example, the conductive material and the binder each independently comprise between 10 and 74 weight percent of the first electrode. Optionally, the conductive material and the binder each together comprise between 20 and 90 weight percent of the first electrode. Optionally, the AMO nanomaterial is added as a dopant of 1-10% by weight to a conventional lithium ion electrode, such as graphite, lithium cobalt oxide, etc.


Various materials are useful for the electrodes described herein. Example metal oxides include, but are not limited to, a lithium containing oxide, an aluminum oxide, a titanium oxide, a manganese oxide, an iron oxide, a zirconium oxide, an indium oxide, a tin oxide, an antimony oxide, a bismuth oxide, or any combination of these. Optionally, the oxides are in the form of an AMO. As described herein, the metal oxide optionally comprises and/or is surface functionalized by one or more electron withdrawing groups selected from Cl, Br, BO3, SO4, PO4, NO3, CH3COO, C2O4, C2HO2O4, C6H8O7, or C6H5O7. Example conductive material comprises one or more of graphite, conductive carbon, carbon black, Ketjenblack, or conductive polymers, such as poly(3,4-ethylenedioxythiophene) (PEDOT), polystyrene sulfonate (PSS), PEDOT:PSS composite, polyaniline (PANI), or polypyrrole (PPY).


In some embodiments, electrodes comprising AMO nanomaterials are used in conjunction with other electrodes to form a cell. For example, a second electrode of such a cell may comprise graphite, metallic lithium, sodium metal, lithium cobalt oxide, lithium titanate, lithium manganese oxide, lithium nickel manganese cobalt oxide (NMC), lithium iron phosphate, lithium nickel cobalt aluminum oxide (NCA), an AMO nanomaterial, or any combination of these. In a specific embodiment, the first electrode comprises an AMO of SnO2, and the second electrode comprises metallic lithium.


Various materials are useful for the electrodes described herein. Example metal oxides include, but are not limited to, a lithium containing oxide, an aluminum oxide, a titanium oxide, a manganese oxide, an iron oxide, a zirconium oxide, an indium oxide, a tin oxide, an antimony oxide, a bismuth oxide, or any combination of these. Optionally, the oxides are in the form of an AMO. As described herein, the metal oxide optionally comprises and/or is surface functionalized by one or more electron withdrawing groups selected from Cl, Br, BO3 SO4, PO4, NO3, CH3COO, C2O4, C2H2O4, C6H8O7, or C6H5O7. Example, conductive material comprises one or more of graphite, conductive carbon, carbon black, Ketjenblack, or conductive polymers, such as poly(3,4-ethylenedioxythiophene) (PEDOT), polystyrene sulfonate (PSS), PEDOT:PSS composite, polyaniline (PANI), or polypyrrole (PPY).


As a further example, batteries in which the electrode is formed using a slurry may also be beneficial and contrary to the conventional teaching in battery technology. As described herein, the AMO material may optionally formed into battery electrode by first forming a slurry of the AMO material with one or more binder compounds, solvents, additives (e.g., conductive additives or acidic additives), and/or other wet processing materials. The slurry may be deposited on a conductive material or current collector in order to form an electrode. Such a slurry and/or a solvent may optionally be acidic or include acidic species and, again, allow for improvements in capacity, cyclability, and longevity of the resultant battery. Optionally, all or a portion of the solvent may be evaporated, leaving the AMO material, binder, additives, etc. The resultant material may optionally exhibit its own acidity, such having a pH less than 7 (but not superacidic), when suspended in water (or resuspended in water after drying) at 5 wt. %, for example.


Various techniques may be used for making the metal oxide. Optionally, making a metal oxide comprises forming a solution comprising a metal salt, ethanol, and water; acidifying the solution by adding an acid to the solution; basifying the solution by adding an aqueous base to the solution; collecting precipitate from the solution; washing the precipitate; and drying the precipitate.


Optionally, making an electrode further comprises depositing a further conductive layer over the electrode layer, such as a conductive layer that comprises a second conductive material. Optionally, depositing the conductive layer include forming a conductive slurry using the second conductive material, a second binder, and a second solvent; depositing a conductive slurry layer on the electrode layer; and evaporating at least a portion of the second solvent to form the conductive layer. Optionally, making an electrode comprises forming 1-20 additional conductive layers comprising the conductive material and 1-20 additional electrode layers comprising the metal oxide. For example, an electrode may comprise a layered structure including a first set of layers comprising a second conductive material and a second set of layers comprising the metal oxide, such as where the first set of layers and the second set of layers are provided in an alternating configuration. Example layers include those independently having thicknesses of between 1 um and 50 um. Example layers include those comprising between 10 and 90 weight percent of the metal oxide. Example layers include those independently comprising between 5 and 85 weight percent of the conductive material and/or binder.


Electrodes formed using the methods of this aspect may have a metal oxide content of up to 80 weight percent. Electrodes formed using the methods of this aspect may have a conductive material and/or binder content of between 10 and 70 weight percent of the electrode.


As described above, acidic species may optionally be included as an additive to any of the components of a battery, such as an electrode or an electrolyte. Optionally, a battery comprising an AMO may include an electrolyte positioned between the electrodes in which acidic species are dissolved in a solvent. Such an electrolyte may also be referred to herein as an acidified electrolyte. The electrolyte may optionally include one or more lithium salts dissolved in the solvent, such as LiPF6, LiAsF6, LiClO4, LiBF4, LiCF3SO3, and combinations of these. It will be appreciated that the electrolyte may be positioned not only in the space separating the electrodes (i.e., between the electrodes), but may also penetrate through or into pores of the electrodes and/or through or into pores of any materials or structures optionally positioned between the electrodes, such as a separator.


Example acidic species useful with the AMOs, electrodes, and electrolytes described herein include but are not limited to organic acids, such as carboxylic acids. Example acidic species include those exhibiting a pKa in water of between −10 and 7, between −5 and 6, between 1 and 6, between 1.2 and 5.6, or about 4. Specific example organic acids include, for example, oxalic acid, carbonic acid, citric acid, maleic acid, methylmalonic acid, formic acid, glutaric acid, succinic acid, methylsuccinic acid, methylenesuccinic acid, citraconic acid, acetic acid, benzoic acid. Example organic acids include dicarboxylic acids, such as those having a formula of




embedded image


where R is a substituted or unsubstituted C1-C20 hydrocarbon, such as a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aromatic or heteroaromatic, a substituted or unsubstituted amine, etc. Example organic acids also include those having a formula of




embedded image


where L is a substituted or unsubstituted C1-C20 divalent hydrocarbon, such as a substituted or unsubstituted alkylene group, a substituted or unsubstituted arylene group, a substituted or unsubstituted heteroarylene group, a substituted or unsubstituted amine, etc. Organic acids may include organic acid anhydrides, such as having a formula of




embedded image


where R1 and R2 are independently a substituted or unsubstituted C1-C20 hydrocarbon, such as a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aromatic or heteroaromatic group, a substituted or unsubstituted amine, etc. Optionally, R1 and R2 can form a ring. Example organic acid anhydrides include any anhydrides of the above mentioned organic acids. Specific organic acid anhydrides include, but are not limited to glutaric anhydride, succinic anhydride, methylsuccinic anhydride, maleic anhydride, and itaconic anhydride.


Useful concentrations of the acidic species in either or both the electrolyte and the AMO electrode include from 0 wt. % to 10 wt. %, 0.01 wt. % to 10 wt. %, from 0.1 wt. % to 10 wt. %, from 1 wt. % to 5 wt. %, or from 3 wt. % to 5 wt. %.


Useful solvents include those employed in lithium ion battery systems, for example, such as ethylene carbonate, butylene carbonate, propylene carbonate, vinylene carbonate, dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethylmethyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, fluoroethylene carbonate and mixtures thereof. Other useful solvents will be appreciated to those skilled in the art. Optionally, when an acidic species and metal salt are dissolved in a solvent to form an electrolyte, the electrolyte itself exhibits an acidic condition (i.e., pH less than 7).


Example binders useful with the batteries and electrodes described herein include Styrene Butadiene Copolymer (SBR), Polyvinylidene Fluoride (PVDF), Carboxy methyl cellulose (CMC), Styrene Butadiene Rubber (SBR), acrylonitrile, polyacrylic acid (PAA), polyvinyl alcohol (PVA), polyamide imide (PAI), and any combination of these. Optionally, conductive polymers may be useful as a binder.


Other example additives useful with the AMOs and electrodes described herein include, but are not limited to conductive additives. Example conductive additives include graphite, conductive carbon, carbon black, Ketjenblack, and conductive polymers, such as poly (3,4-ethylenedioxythiophene (PEDOT), polystyrene sulfonate (PS S), PEDOT:PSS composite, polyaniline (PAM), and polypyrrole (PPY). Conductive additives may be present, for example, in an electrode, at any suitable concentration such as at weight percents greater than 0 and as high as 35 wt. %, 40 wt. % or more. Optionally, conductive additives are present in an electrode at a range of 1 wt. % to 95 wt. %, 1 wt. % to 35 wt. %, 1 wt. % to 25 wt. %, 5 wt. % to 40 wt. %, 10 wt. % to 40 wt. %, 15 wt. % to 40 wt. %, 20 wt. % to 40 wt. %, 25 wt. % to 40 wt. %, 30 wt. % to 40 wt. %, 35 wt. % to 40 wt. %, 40 wt. % to 45 wt. %, 40 wt. % to 50 wt. %, 40 wt. % to 55 wt. %, 40 wt. % to 60 wt. %, 40 wt. % to 65 wt. %, 40 wt. % to 70 wt. %, 40 wt. % to 75 wt. %, 40 wt. % to 80 wt. %, 40 wt. % to 85 wt. %, 40 wt. % to 90 wt. %, or 40 wt. % to 95 wt. %.


Methods of making batteries are also described herein. An example method of making a battery comprises making an AMO nanomaterial; forming a first electrode of or comprising the AMO nanomaterial; forming an electrolyte by dissolving one or more metal salts in a solvent; and positioning the electrolyte between the first electrode and a second electrode. Another example method of making a battery comprises making an AMO nanomaterial; forming a first electrode of or comprising the AMO nanomaterial and one or more metal salts; and positioning the electrolyte between the first electrode and a second electrode.


Electrolytes for use in batteries are also disclosed herein. For example, the disclosed electrolytes are useful in batteries comprising a first electrode and a second electrode, such as a first electrode that comprises an acidified metal oxide (AMO) nanomaterial. Example electrolytes comprise a solvent and one or more metal salts dissolved in the solvent. Optionally, an acidic species is dissolved in the solvent, such as an acidic species that is different from the one or more metal salts.


As described above, a variety of acidic species are useful in the disclosed electrolytes, such as an acidic species comprising an organic acid and/or an organic acid anhydride. Example organic acids include, but are not limited to, oxalic acid, acetic acid, citric acid, maleic acid, methylmalonic acid, glutaric acid, succinic acid, methylsuccinic acid, methylenesuccinic acid, citraconic acid, or any combination of these. Example organic acid anhydrides include, but are not limited to glutaric anhydride, succinic anhydride, methylsuccinic anhydride, maleic anhydride, itaconic anhydride, or any combination of these. Other acidic species examples are described above. Useful acidic species include, but are not limited to, those exhibiting a pKa of between −10 and 7, between −5 and 6, between 1 and 6, between 1.2 and 5.6, or about 4. The acidic species may optionally be present in the electrolyte at any suitable concentration, such as from 0.01 wt. % to 10 wt. %, from 0.1 wt. % to 10 wt. %, from 1 wt. % to 5 wt. %, or from 3 wt. % to 5 wt. %.


It will be appreciated that lithium metal salts, such as LiPF6, LiAsF6, LiClO4, LiBF4, LiCF3SO3, may be useful components of the disclosed acidified electrolytes. Example solvents include, but are not limited to, ethylene carbonate, butylene carbonate, propylene carbonate, vinylene carbonate, dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethylmethyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, fluoroethylene carbonate and mixtures thereof. Example solvents may be useful in metal ion batteries, such as lithium ion batteries.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a simplified cutaway view of an example lithium ion battery cell.



FIG. 2 is another simplified cutaway view of a lithium ion battery cell with the electrolyte substantially contained by the separator.



FIG. 3 is a schematic of a lithium ion battery comprising multiple cells.



FIG. 4 shows differences in the cyclic voltammogram of AMO tin prepared by the method disclosed herein relative to that of commercially available, non-AMO tin when cycled against Li.



FIG. 5 shows the total reflectance of AMO tin oxide is different than that of commercially available, non-AMO tin oxide.



FIG. 6 is X-ray photoelectron spectroscopy (XPS) data showing surface functionalization arising endogenously from the synthesis method disclosed herein. Numbers shown are atomic concentrations in %. The far-right column lists the corresponding pH of the synthesized nanoparticles as measured when dispersed at 5 wt % in aqueous solution.



FIG. 7 provides electron micrograph images showing differences in morphology between AMO nanoparticles synthesized under identical conditions except for the use of a different group for functionalization.



FIG. 8 shows the difference in morphology and performance of AMO nanoparticles synthesized under identical conditions except for having two different total reaction times.



FIG. 9 provides representative half-cell data showing differences in behavior between spherical and elongated (needle-like or rod-like) AMOs upon cycling against lithium.



FIG. 10 provides X-ray photoelectron spectroscopy analysis of the surface of AMO nanoparticles synthesized using both a strong (phosphorous containing) and weak (acetate) electron withdrawing group shows greater atomic concentration of phosphorous than of the bonds associated with acetate groups.



FIG. 11A provides data showing visible light activity degradation data for different AMOs.



FIG. 11B provides data showing ultraviolet light activity degradation data for different AMOs.



FIG. 12 is a graph comparing two AMOs, one having higher capacity for use in a primary (single use) battery application and the other having higher cyclability for use in a secondary (rechargeable) battery application.



FIG. 13 provides charge and discharge capacity data and Columbic efficiency data, illustrating that AMOs can result in enhanced battery performance, without deterioration of battery components or gas generation.



FIG. 14 shows capacity and cycling data for an AMO in standard, acidified, and basified electrolyte systems.



FIG. 15 shows capacity and cycling data for an AMO, and for the same AMO from which the acidification was removed by solvent washing.



FIG. 16 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 17 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 18 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 19 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 20 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 21 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 22 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 23 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 24 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 25 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 26 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 27 provides an electron micrograph image of a synthesized material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the synthesized material.



FIG. 28 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 29 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 30 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 31 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 32 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 33 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 34 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 35 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 36 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 37 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 38 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 39 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 40 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 41 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 42 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 43 provides data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising an AMO material.



FIG. 44 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 45 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 46 provides an electron micrograph image of an AMO material and data including a plot of measured capacity versus cycle number as well as a plot of the voltage as a function of time during cycling for a battery cell including an electrode comprising the AMO material.



FIG. 47 is a plot of temperature and voltage for a cell constructed according to the present disclosure and subjected to a nail penetration test.



FIG. 48A is a plot of temperature and voltage for a cell constructed according to the present disclosure and subjected to an overcharge test.



FIG. 48B is a plot of the overcharge test of FIG. 48A focusing on the start of the test.





DEFINITIONS

For the purposes of this disclosure, the following terms have the following meanings:


Acidic oxide—a term used generally in the scientific literature to refer to binary compounds of oxygen with a nonmetallic element. An example is carbon dioxide, CO2. The oxides of some metalloids (e.g., Si, Te, Po) also have weakly acidic properties in their pure molecular state.


Acidified metal oxide (“AMO”)—a term used here to denote a binary compound of oxygen with a metallic element which has been synthesized or modified to have an acidity greater than that of its natural mineralogical state and also a Hammett function, H0 >−12 (not superacidic). The average particle size is also less than that of the natural mineralogical state. Naturally occurring mineralogical forms do not fall within the scope of the inventive AMO material. A synthesized metal oxide, however, that is more acidic than its most abundant naturally occurring mineralogical form (of equivalent stoichiometry) but not superacidic falls within the bounds of this disclosure and can be said to be an AMO material provided it satisfies certain other conditions discussed in this disclosure.


Acidic—a term used generally in the scientific literature to refer to compounds having a pH of less than 7 in aqueous solution.


Electron-withdrawing group (“EWG”)—an atom or molecular group that draws electron density towards itself. The strength of the EWG is based upon its known behavior in chemical reactions. Halogens, for example are known to be strong EWGs. Organic acid groups such as acetate are known to be weakly electron withdrawing.


Hammett function—An additional means of quantifying acidity in highly concentrated acid solutions and in superacids, the acidity being defined by the following equation: H0=pKBH++log([B]/[BH+]). On this scale, pure 18.4 molar H2SO4 has a H0 value of −12. The value H0 =−12 for pure sulfuric acid must not be interpreted as pH=−12, instead it means that the acid species present has a protonating ability equivalent to H3O+ at a fictitious (ideal) concentration of 1012 mol/L, as measured by its ability to protonate weak bases. The Hammett acidity function avoids water in its equation. It is used herein to provide a quantitative means of distinguishing the AMO material from superacids. The Hammett function can be correlated with colorimetric indicator tests and temperature programmed desorption results.


Metal oxide—a term used generally in the scientific literature to refer to binary compounds of oxygen with a metallic element. Depending on their position in the periodic table, metal oxides range from weakly basic to amphoteric (showing both acidic and basic properties) in their pure molecular state. Weakly basic metal oxides are the oxides of lithium, sodium, magnesium, potassium, calcium, rubidium, strontium, indium, cesium, barium and tellurium. Amphoteric oxides are those of beryllium, aluminum, gallium, germanium, astatine, tin, antimony, lead and bismuth.


Monodisperse—characterized by particles of uniform size which are substantially separated from one another, not agglomerated as grains of a larger particle.


pH—a functional numeric scale used generally in the scientific literature to specify the acidity or alkalinity of an aqueous solution. It is the negative of the logarithm of the concentration of the hydronium ion [H3O+]. As used here it describes the relative acidity of nanoparticles suspended in aqueous solution.


Surface functionalization—attachment of small atoms or molecular groups to the surface of a material.


Superacid—substances that are more acidic than 100% H2SO4, having a Hammett function, H0 <−12.


DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Referring now to FIG. 1, a lithium ion battery cell 100 is illustrated in a simplified cutaway view. The cell 100 may comprise a casing or container 102. In some embodiments, the casing 102 is a polymer or an alloy. The casing 102 chemically and electrically isolates the contents of the cell 100 from adjacent cells, from contamination, and from damaging or being damaged by other components of the device into which the cell 100 is installed. A full battery may contain a plurality of cells arranged in a series and/or parallel configuration. The battery may have a further casing or securement mechanism binding the plurality of cells together as is known in the art.


The cell 100 provides a cathode 104 and an anode 106. The contents of the cell 100 undergo a chemical reaction when a conduction path is provided between the cathode 104 and anode 106 that is external to the cell 100. As a result of the chemical reaction, electrons are provided at the anode 106 that flow to the cathode 104 via the circuit provided external to the battery (sometimes referred to as the load). At a basic level, during discharge of the cell 100, the materials comprising the anode 106 are oxidized providing the electrons that flow through the circuit. The materials comprising the cathode 104, as recipient of the electrons given up by the anode 106, are reduced.


Within the cell 100, during discharge, metallic cations move through an electrolyte 108 from the anode 106 to the cathode 104. In the case of a lithium based battery, the metallic cation may be a lithium cation (Li+). The electrolyte 108 may be a liquid electrolyte such as a lithium salt in an organic solvent (e.g., LiClO4 in ethylene carbonate). Other lithium based electrolyte/solvent combinations may be used as are known in the art. In some cases, the electrolyte 108 may be a solid electrolyte such as a lithium salt in a polyethylene oxide. Optionally, the electrolyte may comprise a polymer electrolyte. Example electrolytes include those described in U.S. Patent Application Publication 2017/0069931, which is hereby incorporated by reference.


A separator 110 may be employed to prevent contact between the electrodes 104, 106. The separator 110 may be a porous layer of material that is permeable to the lithium ions and the electrolyte 108 but not otherwise electrically conductive so as to prevent internal shorting of the cell 100. As is known in the art, the separator 110 may comprise glass fibers or may comprise a polymer, possibly with a semi-crystalline structure. Additional components, such as current collectors, may also be included in the cell 100, but are not shown in FIG. 1.


Together the anode 104, cathode 106, electrolyte 108, and separator 110 form the completed cell 100. Since the separator 110 is porous, the electrolyte 108 may flow into, or be contained by, the separator 110. Under normal operating conditions, the porosity of the separator 110 allows for ion (Li+) flow between the electrodes 104, 106 via the electrolyte 108. As is known in the art, a separator can be constructed so as to melt and close the internal pore structure to shut down the cell in the event of exposure to excess heat or a runaway exothermic reaction.


Most lithium-based cells are so-called secondary batteries. They can be discharged and recharged many times before the chemical or structural integrity of the cell falls below acceptable limits. Cells and batteries according to the present disclosure are considered to be both primary (e.g., single use) and secondary batteries.


In the case of the cell 100 being a secondary cell (or part of a secondary battery) it should be understood that the cell 100 may be recharged either alone or as a component of a completed system wherein multiple cells are recharged simultaneously (and possibly in the same parallel or series circuit).


A reverse voltage is applied to the cell 100 in order to effect charging. It should be understood that various schemes for effective recharging of lithium batteries can be employed. Constant current, variable current, constant voltage, variable voltage, partial duty cycles, etc., may be employed. The present disclosure is not intended to be limited to a particular charging methodology unless stated in the claims. During charging of cell 100, element 115 represents a voltage source that is applied between cathode 104 and anode 106 to provide electrons from cathode 105 to anode 106 and allow chemical reactions to take place. Lithium ions are shuttled from cathode 104 to the anode 106 through electrolyte 108 and separator 110.


As examples, cathode 104 or anode 106 may independent comprise an AMO material disclosed herein. For use of an AMO material as a cathode, an anode may correspond to lithium metal or a lithium intercalation material, such as graphite. Optionally, electrolyte 108 may include an acidic species, such as dissolved in an organic solvent with a lithium salt. In addition to or alternative to use of an acidic species in electrolyte 108, an electrode (i.e., cathode 104 or anode 106) may optionally comprise an AMO and an acidic species. Oxalic acid is an exemplary acidic species.


Without wishing to be bound by any theory, it is believed that the presence of acidic species in the cathode 104 or anode 106 and/or electrolyte 108 improves a surface affinity of the AMO material toward lithium ions, resulting in an improved ability to take up lithium ions during discharge and overall improvement to capacity as compared to a similar cell lacking acidic species or having a basified electrode or electrolyte (i.e., including basic species). Alternatively or additionally, the presence of acidic species may allow for additional active sites for lithium uptake in cathode 104.


It should be understood that FIG. 1 is not to scale. A shown in FIG. 2, in most applications, the separator 110 occupies most or all of the space between the electrodes 104, 106 and is in contact with the electrodes 104, 106. In such case, the electrolyte 108 is contained within the separator 110 (but may also intrude into the pores or surface of the anode or cathode). FIG. 2 is also not necessarily to scale. The actual geometry of a cell can range from relatively thin and flat pouches, to canister type constructions, to button cells and others. Cell construction techniques such as winding or bobbin or pin type assemblies may be used.


Current collectors known in the art and other components (not shown) may also be relied upon to form a cell 100 into a commercially viable package. Although overall shape or geometry may vary, a cell or battery will normally, at some location or cross section, contain the electrodes 104, 106 separated rather than touching, and have the electrolyte 108 and possibly separator 110 between them. Cells may also be constructed such that there are multiple layers of anodes and cathodes. Cells may be constructed such that two cathodes are on opposite sides of a single anode or vice versa.


A functional or operational battery intended for a specific purpose may comprise a plurality of cells arranged according to the needs of particular application. An example of such a battery is shown schematically in FIG. 3. Here the battery 300 comprises four lithium cells 100 arranged in series to increase voltage. Capacity can be increased at this voltage by providing additional stacks of four cells 100 in parallel with the stack shown. Different voltages can be achieved by altering the number of cells 100 arranged in series.


A positive electrode 306 may be accessible on the outside of a casing 302 of the battery 300. A negative electrode 304 is also provided. The physical form factor of the electrodes 304, 306 may vary according to application. Various binders, glues, tapes and/or other securement mechanisms (not shown) may be employed within a battery casing 302 to stabilize the other components. Batteries based on lithium technology are generally operable, rechargeable, and storable in any orientation (if a secondary cell). As discussed above, cells 100 may take on various different geometric shapes. Thus FIG. 3 is not meant to represent any particular physical form factor of the battery 300.


The battery 300 may also comprise various adjunct circuitry 308 interposing the positive electrode 308 and the lithium cells 100 within the casing 302 of the battery 300. In other embodiments, the adjust circuitry interposes the negative electrode 304 and the lithium cells 100 instead of, or in addition to, interposing the positive electrode 306 and the lithium cells 100. The adjunct circuitry 308 may include short circuit protection, overcharge protection, overheating shutdown and other circuitry as is known in the art to protect the battery 300, the cells 100, and/or any load attached to the battery 300.


The composition of materials chosen for the cathode 104, anode 106, and electrolyte may be critical to the performance of the cell 100 and any battery of which it forms a part. In the context of the present disclosure, various examples of AMOs and methods for their production are provided in this regard. These AMOs are suitable for use in forming anodes or cathodes in half cells, cells, and batteries. The AMOs of the present disclosure are otherwise compatible with known lithium cell technology including existing anode and cathode compositions, electrolyte formulations, and separator compositions.


In the context of the present disclosure, various examples of AMOs and methods for their production and use are provided. These AMOs are suitable for use in forming cathodes or anodes in half cells, cells, and batteries. The disclosed AMOs are otherwise compatible with conventional lithium battery technology, including existing anode compositions, cathode compositions, electrolyte formulations, and separator compositions. It will be appreciated that the material of the anode 106 chosen for a cell or battery according to the present disclosure may be less electronegative than the material of the cathode to suitably complement the cathodic materials. In one particular embodiment, the disclosed AMOs are useful as a cathode in a cell having a metallic lithium anode.


In various embodiments of the present disclosure, the cathode 104 comprises an AMO material having a surface that is acidic but not superacidic. This would be in contrast to materials previously known and utilized as cathodes such as lithium cobalt or lithium manganese materials. The AMO materials of the present disclosure and methods for their production are described below. In other embodiments, the anode 106 comprises an AMO material of the present disclosure having a surface that is acidic but not super acidic.


The surfaces of metal oxides are ideally arrays of metal and oxygen centers, ordered according to the crystalline structure of the oxide. In reality the arrays are imperfect, being prone to vacancies, distortion, and the effects of surface attachments. Regardless, any exposed metal centers are cationic (positively charged) and can accept electrons, thus functioning by definition as Lewis acid sites. Oxygen centers are anionic (negatively charged) and act as Lewis base sites to donate electrons. This leads to the well-known amphotericity of metal oxide surfaces.


Under normal atmospheric conditions, the presence of water vapor will adsorb to the metal oxide surface either molecularly (hydration) or dissociatively (hydroxylation). Both OH− and H++species can adsorb on the oxide surface. The negatively-charged hydroxyl species will attach at the metal, cationic (Lewis acid, electron accepting) centers, and the H+will attach at the oxygen, anionic (Lewis base, electron donating) centers. Both adsorptions lead to the presence of the same functional group—a hydroxyl—on the metal oxide surface.


These surface hydroxyl groups can serve as either Bronsted acids or as Bronsted bases, because the groups can either give up or accept a proton. The tendency of an individual hydroxyl group to be a proton donor or a proton acceptor is affected by the coordination of the metal cation or oxygen anion to which it is attached. Imperfections of the metal oxide surface such as oxygen vacancies, or coordination of the surface groups with other chemical species, mean that all cations and anions are not equally coordinated. Acid-base sites will vary in number and in strengths. When broadly “totaled” across the surface of the oxide, this can give the surface an overall acidic or basic character.


The quantity and strength of Lewis acid and base sites (from the exposed metal cations and oxygen anions, respectively) and Bronsted acid and base sites (from the surface hydroxyl groups)—add broad utility and functionality to the metal oxide and its use in both chemical reactions and device applications. The sites are a strong contributor to the chemical reactivity of the metal oxide. They can serve as anchor sites to which other chemical groups, and even additional metal oxides, may be attached. And they can affect surface charge, hydrophilicity and biocompatibility.


One way of altering the surface of metal oxides is to attach small chemical groups or electron-withdrawing groups (“EWGs”) in a process known as surface functionalization. The EWG induces polarization of the hydroxide bonds and facilitates dissociation of hydrogen. For example, a stronger EWG should lead to a more polarized bond and therefore a more acidic proton. The acidity of Lewis sites can be increased by inducing polarization that facilitates the donation of electrons to the site. When compounds so made are placed in water, the acidic protons will dissociate and so reduce the aqueous pH measurement.


Though somewhat imprecise when working with solid acid/base systems rather than liquid ones, traditional methods of pH measurement utilizing titrations, pH paper and pH probes can be used to evaluate the acidity of metal oxides dispersed in aqueous solution. These measurements can be supplemented by the use of techniques including but not limited to colorimetric indicators, infrared spectroscopy, and temperature programmed desorption data to establish the acidified nature of the metal oxide surface. Surface groups can be examined by standard analytical techniques including but not limited to x-ray photoelectron spectroscopy.


Surface functionalization can be accomplished post-synthesis, including but not limited to exposing the metal oxide to acidic solutions or to vapors containing the desired functional groups. It can also be accomplished via solid state methods, in which the metal oxide is mixed and/or milled with solids containing the desired functional groups. However, all of these methods require an additional surface functionalization step or steps beyond those required to synthesize the metal oxide itself.


Synthesis and surface functionalization of the AMO material may be accomplished in a “single-pot” hydrothermal synthesis method or its equivalent in which the surface of the metal oxide is functionalized as the metal oxide is being synthesized from appropriate precursors. A precursor salt containing an EWG is solubilized and the resulting solution is acidified using an acid containing a second EWG. This acidified solution is then basified and the basified solution is heated then washed. A drying step produces the solid AMO material.


By way of example, a preferred embodiment of an AMO form of tin oxide was synthesized and simultaneously surface functionalized using the following single-pot method:

    • 1. Initially, seven grams (7 g) of a tin (II) chloride dihydrate (SnCl2 H2O) is dissolved in a solution of 35 mL of absolute ethanol and 77 mL distilled water.
    • 2. The resulting solution is stirred for 30 minutes.
    • 3. The solution is acidified by the addition of 7 mL of 1.2M HCl, added dropwise, and the resulting solution is stirred for 15 minutes.
    • 4. The solution is basified by the addition of 1M of an aqueous base, added dropwise until the pH of the solution is about 8.5.
    • 5. The resulting opaque white suspension is then placed in a hot-water bath (˜60° to 90° C.) for at least 2 hours while under stirring.
    • 6. The suspension is then washed with distilled water and with absolute ethanol.
    • 7. The washed suspension is dried at 100° C. for 1 hour in air and then annealed at 200° C. for 4 hours in air.


      This method results in an AMO of tin, surface-functionalized with chlorine, whose pH is approximately 2 when resuspended and measured in an aqueous solution at 5 wt % and room temperature. By definition its Hammett function, H0 >−12. Although an open system such as a flask is described here, a closed system such as an autoclave may also be used.


Utilizing the single pot method disclosed above, a number of AMO's have been synthesized. Table 1 below describes the precursors and acids that have been used. In some instances, a dopant is utilized as well:

















Precursor
Dopant
Acid









SnAc

CH3COOH



SnAc

H2SO4



SnAc

HNO3



SnAc

H3PO4



SnAc

C6H8O7



SnAc

C2H2O4



SnAc
FeAc
HCl



SnAc
FeAc
H2SO4



SnAc
FeAc
HNO3



SnAc
FeAc
C2H2O4



SnAc
FeAc
H3PO4



SnAc
FeAc
C6H8O7



SnAc
HBr



SnAc
H3BO3



SnSO4
MnCl2
H2SO4



SnCl2
MnCl2
HCl



SnCl2
FeCl3 & AlCl3
HCl



FeCl3
SnCl2
HCl



Fe(NO3)3

HNO3



BiCl3

HCl



Zr(SO4)2

H2SO4



TiOSO4

H2SO4



Sb2(SO4)3

H2SO4



In(Cl)3

HCl



In2(SO4)3

H2SO4



In(III)Br

HBr



InCl3

HCl



LiAc & FeCl3
SnCl2
HCl







where Ac is an acetate group with the chemical formula C2H3O2






In some embodiments, the electron withdrawing groups have a carbon chain length of 6 or less and/or an organic mass or 200 or less (AMU). In some embodiments, the electron withdrawing groups have a carbon chain length or 8 or less, or 10 or less, and/or an organic mass of 500 or less.


It will be appreciated that the method's parameters can be varied. These parameters include, but are not limited to, type and concentration of reagents, type and concentration of acid and base, reaction time, temperature and pressure, stir rate and time, number and types of washing steps, time and temperature of drying and calcination, and gas exposure during drying and calcination. Variations may be conducted singly, or in any combination, possibly using experimental design methodologies. Additionally, other metal oxide synthesis methods—e.g., spray pyrolysis methods, vapor phase growth methods, electrodeposition methods, solid state methods, and hydro- or solvo thermal process methods—may be useful for achieving the same or similar results as the method disclosed here.


A variety of annealing conditions are useful for preparing AMO nanomaterial. Example annealing temperatures may be below 300° C., such as from 100° C. to 300° C. Example annealing time may range from about 1 hours to about 8 hours, or more. Annealing may take place under a variety of atmospheric conditions. For example, annealing may occur in air at atmospheric pressure. Annealing may occur at elevated pressure (greater than atmospheric pressure) or reduced pressure (less than atmospheric pressure or in a vacuum). Annealing may alternatively occur in a controlled atmosphere, such as under an inert gas (e.g., nitrogen, helium, or argon) or in the presence of an oxidizing gas (e.g., oxygen or water).


A variety of drying conditions are useful for preparing AMO nanomaterials. Example drying temperatures may be from 50° C. to 150° C. Example drying time may range from about 0.5 hours to about 8 hours, or more. Drying may take place under a variety of atmospheric conditions. For example, drying may occur in air at atmospheric pressure. Drying may occur at elevated pressure (greater than atmospheric pressure) or reduced pressure (less than atmospheric pressure or in a vacuum). Drying may alternatively occur in a controlled atmosphere, such as under an inert gas (e.g., nitrogen, helium, or argon) or in the presence of an oxidizing gas (e.g., oxygen or water).


The performance characteristics of the AMO nanomaterials of the present disclosure differ from those of non-acidified metal oxide nanoparticles. As one example, FIG. 4 shows differences in the cyclic voltammogram of AMO tin prepared by the single-pot method relative to that of commercially available, non-AMO tin when cycled against lithium. For example, the surface-functionalized AMO material exhibits better reversibility than the non-AMO material. The presence of distinct peaks in the CV of the AMO material may indicate that multiple electron transfer steps are occurring during charging/discharging. For example, a peak at higher voltage may indicate direct oxidation/reduction of the AMO material, while a peak at lower voltage may originate due to changing the material structure of the AMO material (i.e., alloying).


As another example, FIG. 5 shows the total reflectance of AMO tin oxide is different than that of commercially available, non-AMO tin oxide. The data indicates that the AMO has a lower band gap and therefore more desirable properties as a component of a photovoltaic system in addition to use as an anode according to the present disclosure.


The AMO material may be thought of as having the general formula





MmOx/G


where

    • MmOx is the metal oxide, m being at least 1 and no greater than 5, x being at least 1 and no greater than 21;
    • G is at least one EWG that is not hydroxide, and
    • simply makes a distinction between the metal oxide and the EWG, denoting no fixed mathematical relationship or ratio between the two.


      G may represent a single type of EWG, or more than one type of EWG.


Exemplary AMOs are acidified tin oxides (SnxOy), acidified titanium dioxides (TiaOb), acidified iron oxides (FecOd), and acidified zirconium oxide (ZrcOf). Exemplary electron-withdrawing groups (“EWGs”) are Cl, Br, BO3, SO4, PO4 and CH3COO. Regardless of the specific metal or EWG, according to the present disclosure, the AMO material is acidic but not superacidic, yielding a pH <7 when suspended in an aqueous solution at 5 wt % and a Hammett function, H0 >−12, at least on its surface.


The AMO material structure may be crystalline or amorphous (or a combination thereof), and may be utilized singly or as composites in combination with one another, with non-acidified metal oxides, or with other additives, binders, or conductive aids known in the art. In other words, an anode prepared to take advantage of the AMO's of the present disclosure may or may not comprise other materials. In one embodiment, the AMO may be layered upon a conductive material to form the cathode 104. In some embodiments, the AMO material is added to a conductive aid material such as graphite or conductive carbon (or their equivalents) in a range of 10 wt % to 80 wt % and upwards of 90 wt % to 95 wt %. In preferred embodiments, the AMO was added at 10 wt %, 33 wt %, 50 wt %, and 80 wt %.


To maximize the amount of overall surface area available, the AMO should be in nanoparticulate form (i.e., less than 1 micron in size) and substantially monodispersed. More preferably, the nanoparticulate size is less than 100 nm and, even more preferably, less than 20 nm or 10 nm.


Mixed-metal AMOs, in which another metal or metal oxide is present in addition to the simple, or binary oxide, have been reduced to practice in forming anodes utilized in half cells, cells, and batteries. These mixed-metal AMOs may be thought of as having the general formula





MmNnOx/G and MmNnRrOx/G


where:

    • M is a metal and m is at least 1 and no greater than 5;
    • N is a metal and n is greater than zero and no greater than 5;
    • R is a metal and r is greater than zero and no greater than 5;
    • O is total oxygen associated with all metals and x is at least 1 and no greater than 21;
    • simply makes a distinction between the metal oxide and the electron-withdrawing surface group, denoting no fixed mathematical relationship or ratio between the two; and


G is at least one EWG that is not hydroxide.


G may represent a single type of EWG, or more than one type of EWG.


Some prior art mixed metal oxide systems, of which zeolites are the most prominent example, display strong acidity even though each simple oxide does not. Preferred embodiments of the mixed-metal AMO of this disclosure differ from those systems in that any embodiment must include at least one AMO which is acidic (but not superacidic) in simple MmOx/G form. Preferred mixed metal and metal oxide systems are SnxFecOy+d and SnxTiaOy+b, where y+d and y+b may be an integer or non-integer value.


In another embodiment, the mixed metal AMO material is produced via the single-pot method with one modification: synthesis begins with two metal precursor salts rather than one, in any proportion. For example, Step 1 of the single-pot method may be altered as follows: Initially, 3.8 g of tin (II) chloride dihydrate (SnCl2 2H2O) and 0.2 g of lithium chloride (LiCl) are dissolved in a solution of 20 mL of absolute ethanol and 44 mL distilled water.


Metal precursor salts as shown in Table 1 could also be used, in any proportion. The metal precursor salts could have the same or differing anionic groups, depending on the desired product; could be introduced at different points in the synthesis; or could be introduced as solids or introduced in a solvent. In some embodiments, a first metal precursor salt may be used for the primary structure (i.e., larger proportion) of the resultant AMO, and a second (and optionally a third) metal precursor salt may be added as a dopant or as a minor component for the resultant AMO.


Experimentation with the single-pot method led to seven notable findings. First, in all cases both surface functionalization and acidity arise endogenously (see FIG. 6), rather than created post-synthesis. Unlike prior art surface functionalization methods, the single-pot method does not require any additional step or steps for surface functionalization beyond those required to synthesize the metal oxide itself, nor does it make use of hydroxyl-containing organic compounds or hydrogen peroxide.


Second, the method is broadly generalizable across a wide range of metal oxides and EWGs. Using the methods of the present disclosure, metal oxides of iron, tin, antimony, bismuth, titanium, zirconium, manganese, and indium have been synthesized and simultaneously surface-functionalized with chlorides, sulfates, acetates, nitrates, phosphates, citrates, oxalates, borates, and bromides. Mixed metal AMOs of tin and iron, tin and manganese, tin and manganese and iron, tin and titanium, indium and tin, antimony and tin, aluminum and tin, lithium and iron, and lithium and tin also have been synthesized. Additionally, surface functionalization can be accomplished using EWGs that are weaker than halogens and SO4 yet still produce acidic but not superacidic surfaces. For example, the method also has been used to synthesize AMOs surface-functionalized with acetate (CH3COO), oxalate (C2O4), and citrate (C6H5O7). A variety of Examples are described below.


Third, there is a synergistic relationship between the EWG and other properties of the nanoparticles such as size, morphology (e.g., plate-like, spherical-like, needle- or rod-like), oxidation state, and crystallinity (amorphous, crystalline, or a mixture thereof). For example, differences in morphology can occur between AMO nanoparticles synthesized under identical conditions except for the use of a different EWG for surface functionalization (see FIG. 7). The surface functionalization may act to “pin” the dimensions of the nanoparticles, stopping their growth. This pinning may occur on only one dimension of the nanoparticle, or in more than one dimension, depending upon exact synthesis conditions.


Fourth, the character of the AMO is very sensitive to synthesis conditions and procedures. For example, differences in morphology and performance of the AMD's nanoparticles can occur when synthesized under identical conditions except for having two different total reaction times (see FIGS. 8 & 9). Experimental design methodologies can be used to decide the best or optimal synthesis conditions and procedures to produce a desired characteristic or set of characteristics.


Fifth, both the anion present in the precursor salt and the anion present in the acid contribute to the surface functionalization of the AMO. In one preferred embodiment, tin chloride precursors and hydrochloric acid are used in a synthesis of an AMO of tin. The performance of these particles differ from an embodiment in which tin chloride precursors and sulfuric acid are used, or from an embodiment in which tin sulfate precursors and hydrochloric acid are used. Therefore, matching the precursor anion and acid anion is preferred in some embodiments.


Sixth, when utilizing a precursor with a weak EWG and an acid with a strong EWG, or vice versa, the strongly withdrawing anion will dominate the surface functionalization. This opens up a broader range of synthesis possibilities, allowing functionalization with ions that are not readily available in both precursor salts and acids. It may also permit mixed functionalization with both strong and weak EWGs. In one example, a tin acetate precursor and phosphoric acid are used to synthesize an AMO of tin. X-ray photoelectron spectroscopy analysis of the surface shows a greater atomic concentration of phosphorous than of the bonds associated with acetate groups (see FIG. 10).


Seventh, and last, while the disclosed method is a general procedure for synthesis of AMOs, the synthesis procedures and conditions may be adjusted to yield sizes, morphologies, oxidation states, and crystalline states as are deemed to be desirable for different applications. As one example, catalytic applications might desire an AMO material which is more active in visible light (see FIG. 11A) or one which is more active in ultraviolet light (see FIG. 11B).


In another example, the AMO material may be used as a battery electrode. A primary (single-use) battery application might desire an AMO with characteristics that lead to the highest capacity, while a secondary (rechargeable) battery application might desire the same AMO but with characteristics that lead to the highest cyclability. FIG. 12 compares the cyclability of two different batteries constructed from AMO materials, including a chlorine containing AMO and a sulfur containing AMO. The AMO material can result in enhanced battery performance, without deterioration of battery components or gas generation (see FIG. 13). This is exactly opposite what the prior art teaches.


In FIG. 13, the charge-discharge cyclability of a battery constructed as a half-cell of an AMO nanomaterial electrode versus lithium metal is shown, showing cyclability for up to 900 charge-discharge cycles, while still maintaining useful capacity and exceptional columbic efficiency. Such long cyclability is exceptional, particularly against the lithium metal reference electrode, as lithium metal is known to grow dendrites during even low cycle numbers, which can enlarge and result in dangerous and catastrophic failure of a battery cell.


According to the present disclosure, in a complete cell, the anode 106 comprising the disclosed AMO may be utilized with a known electrolyte 108 and a cathode 104 comprising known materials such as lithium cobalt oxide (LiCoO2). The material comprising the separator 110 may likewise be drawn from those currently known in the art.


In a complete cell, the cathode 104 comprising the disclosed AMO may be utilized with a known electrolyte 108 and an anode 106 comprising known materials such as carbon on copper foil, which display less electronegativity than AMO's of the present disclosure. The material comprising the separator 110 and electrolyte 108 may likewise be drawn from those currently known in the art as discussed above.


Various layering and other enhancement techniques may be deployed to maximize capacity for holding lithium ions for powering the cell 100. It should also be understood that a battery based on an AMO cathode 104 according to the present disclosure can be deployed as a secondary (e.g., rechargeable) battery but can also serve as a primary battery. Although the AMO anodes of the present disclosure lend themselves to a reversible battery chemistry, a cell or battery constructed as described herein, may be satisfactorily deployed as a primary cell or battery.


In the battery industry, the word ‘formation’ is used to denote initial charge or discharge of the battery carried out at the manufacturing facility prior to the battery being made available for use. The formation process is generally quite slow and may require multiple cycles directed at converting the active materials as-manufactured into a form that is more usable for cell cycling. These conversions may be alterations of the structure, morphology, crystallinity, and/or stoichiometry of the active materials.


Cells and batteries constructed according to the present disclosure, in some embodiments, do not require initial formation and therefore are ready to use as primary cells or batteries. In other cases, limited or rapid formation may be employed. Moreover, by deploying the cells and batteries of the present disclosure as primary cells that are not intended to be recharged, some of the safety issues that may be inherent with lithium battery chemistry are mitigated, as it is known in the art that the safety issues more frequently arise during battery cycling. However, following an initial primary discharge, cells and batteries disclosed herein are optionally suitable for use as secondary battery systems which may undergo many charge-discharge cycles, such as up to tens, hundreds, or even thousands of cycles.


In other embodiments according to the present disclosure, the cathode 104 comprises nanoparticles of tin oxide (SnO2) but it has not been acidified in accordance with the AMD's described above. Known electrolytes 108, anodes 106, and separators 110, or those otherwise described in this disclosure may be utilized with such embodiments.


It will be appreciated that other battery constructions are possible using the AMO material. For example, a battery may comprise a first electrode comprising an AMO nanomaterial, a second electrode, and an electrolyte positioned between the first electrode and the second electrode. As an example, in a lithium ion battery, the first electrode may operate as a cathode or an anode. For example, in operation as a cathode, the second electrode may correspond to lithium metal, graphite, or another anodic material. As another example, in operation as an anode, the second electrode may correspond to a LiCoO2, LiMn2O4, LiNiO2, or another cathodic material. Useful materials for the second electrode include, but are not limited to, graphite, lithium metal, sodium metal, lithium cobalt oxide, lithium titanate, lithium manganese oxide, lithium nickel manganese cobalt oxide (NMC), lithium iron phosphate, lithium nickel cobalt aluminum oxide (NCA), or any combination of these.


It will be appreciated that the AMO materials disclosed herein may also be added as dopants to conventional lithium ion cell anodes and/or cathodes, such as in amounts between 0.01 wt. % and 10 wt. %, or for example, an amount of about 1 wt. %, 5 wt. % or 10 wt. % of AMO material in an electrode. The disclosed AMO materials provide an incredible capacity for storing lithium atoms and by adding these materials to conventional lithium ion cell electrodes, the ability of these composite. As one specific example, an electrode comprises LiCoO2 and an AMO. As another example, an electrode comprises a carbonaceous material, such as graphite, and an AMO.


The AMO materials of the present disclosure may optionally be used with an acidic component, such as a binder, an acidic electrolyte, or an acidic electrolyte additive. This may be in the context of an anode, cathode, half-cell, complete cell, integrated battery, or other components. The inventors have surprisingly found that including acidic components and/or acidic species, such as organic acids or organic acid anhydrides, in a battery comprising an AMO material results in an increase in the capacity of versus batteries where the acidic species are not included. Again, the prior art teaches against use of acidic species, as these species may degrade metal current collectors and housings and cause deterioration in other electrode components.


As shown in FIG. 14, which provides comparative cyclability data for AMO-based batteries formed of the same materials and structure except for one having a standard electrolyte, one having a basified electrolyte, and one having an acidified electrolyte. The batteries included a construction as follows: all cathodes included the same AMO material; all anodes were lithium metal; the standard electrolyte was a 1:1:1 mix of dimethylene carbonate, diethylene carbonate, and ethylene carbonate with 1 M LiPF6; the acidified electrolyte was the standard electrolyte with 3 wt. % succinic anhydride; the basified electrolyte was the standard electrolyte with 3 wt. %


dimethylacetamide. All batteries were cycled at the same discharge rate. As illustrated, the battery with the acidified electrolyte system exhibits the best cycling ability, maintaining the highest capacity over the largest number of cycles.



FIG. 15 provides additional comparative cyclability data for two different batteries with the same battery construction including an acidified electrolyte, except that the AMO material of one battery is deacidified by washing with a solvent. The batteries included a construction as follows: the cathodes included the AMO material; the electrolyte was a 1:1:1 mix of dimethylene carbonate, diethylene carbonate, and ethylene carbonate with 1 M LiPF6 and 3 wt. % succinic anhydride; the anodes were lithium metal. The batteries were cycled at the same discharge rate. The battery having the acidified AMO material exhibits higher capacity retention vs. cycle number, indicating that the acidified surface of the AMO may interact with the acidified electrolyte, providing enhanced performance.


Several acidic electrolytes have been developed and/or tested and been found to operate advantageously with the cell chemistry described herein.


EXAMPLE 1

AMO of Tin Oxide Functionalized by Acetate/Chloride


A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a soft, grey material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 16 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 2

AMO of Tin Oxide Functionalized by Acetate/Sulfate


A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of sulfuric acid (H2SO4). The resultant AMO nanomaterial was a grey, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 17 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 3

AMO of Tin Oxide Functionalized by Acetate/Nitrate


A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of nitric acid (HNO3). The resultant AMO nanomaterial was a grey, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 18 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 4

AMO of Tin Oxide Functionalized by Acetate/Phosphate


A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of phosphoric acid (H3PO4). The resultant AMO nanomaterial was a brown, soft, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 19 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 5
AMO of Tin Oxide Functionalized by Acetate/Citrate

A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of citric acid (C6H8O7). The resultant AMO nanomaterial was a brown, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 20 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 6

AMO of Tin Oxide Functionalized by Acetate/Citrate


A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of oxalic acid (C2H2O4). The resultant AMO nanomaterial was a taupe, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 21 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 7

AMO of Tin Oxide Doped with Iron Oxide and Functionalized by Acetate/Chloride


A doped tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution with a lesser amount of iron acetate. The solution was acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a soft and flaky, creamy grey material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 22 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 8

AMO of Tin Oxide Doped with Iron Oxide and Functionalized by Acetate/Sulfate


A doped tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution with a lesser amount of iron acetate. The solution was acidified by addition of sulfuric acid (H2SO4). The resultant AMO nanomaterial was a pale, taupe colored, soft, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 23 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 9

AMO of Tin Oxide Doped With Iron Oxide and Functionalized by Acetate/Nitrate


Two doped tin oxide AMO samples were synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution with a lesser amount of iron acetate (Fe(CH3COO)3). The solution was acidified by addition of nitric acid (HNO3). The resultant AMO nanomaterial was a soft, white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 24 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 10

AMO of Tin Oxide Doped with Iron Oxide and Functionalized by Acetate/Oxalate


A doped tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution with a lesser amount of iron acetate (Fe(CH3COO)3). The solution was acidified by addition of oxalic acid (C2H2O4). The resultant AMO nanomaterial was a soft, white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 25 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 11

AMO of Tin Oxide Doped with Iron Oxide and Functionalized by Acetate/Phosphate


A doped tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution with a lesser amount of iron acetate (Fe(CH3COO)3). The solution was acidified by addition of phosphoric acid (H3 SO4). The resultant AMO nanomaterial was a white, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 26 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 12

Tin Oxide Doped with Iron Oxide and Functionalized by Acetate/Citrate


A doped tin oxide was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution with a lesser amount of iron acetate (Fe(CH3COO)3). The solution was acidified by addition of citric acid (C6H8O7). The resultant material did not form particles, and was a yellow, glassy hard material, which was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 27 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 13

AMO of Tin Oxide Functionalized by Acetate/Bromide


A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of hydrobromic acid (HBr). The resultant AMO nanomaterial was a grey, soft, powdery material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 28 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 14

AMO of Tin Oxide Functionalized by Acetate/Borate


A tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin acetate (Sn(CH3COO)2) was dissolved in an ethanol/water solution and acidified by addition of boric acid (H3BO3). The resultant AMO nanomaterial was a grey, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 29 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 15

AMO of Tin Oxide Doped with Manganese Oxide and Functionalized by Sulfate/Chloride


A doped tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin sulfate (SnSO4) was dissolved in an ethanol/water solution with a lesser amount of manganese chloride (MnCl2). The solution was acidified by addition of sulfuric acid (H2SO4). The resultant AMO nanomaterial was a very soft, tan material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 30 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 16

AMO of Tin Oxide Doped with Manganese Oxide and Functionalized by Chloride


A doped tin oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, tin chloride (SnCl2) was dissolved in an ethanol/water solution with a lesser amount of manganese chloride (MnCl2). The solution was acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a soft, greyish brown material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 31 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 17

AMO of Tin Oxide Doped with Iron Oxide and Aluminum Oxide and Functionalized by Chloride


Two doped tin oxide AMO samples were synthesized using a single-pot hydrothermal synthesis method. Briefly, tin chloride (SnCl2) was dissolved in an ethanol/water solution with lesser amounts of both iron chloride (FeCl3) and aluminum chloride (AlCl3). The solution was acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial for the first sample was a light tan, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 32 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling. The resultant AMO nanomaterial for the second sample was a light grey, flaky material.


EXAMPLE 18

AMO of Iron Oxide Doped with Tin Oxide and Functionalized by Chloride


A doped iron oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, iron chloride (FeCl3) was dissolved in an ethanol/water solution with a lesser amount of tin chloride (SnCl2). The ratio of iron to tin was 95:5. The solution was acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a soft, red material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 33 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 19

AMO of Iron Oxide Doped with Tin Oxide and Functionalized by Chloride


A doped iron oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, iron chloride (FeCl3) was dissolved in an ethanol/water solution with a lesser amount of tin chloride (SnCl2). The ratio of iron to tin was 95:5. The solution was acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a black, glassy material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 34 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 20

AMO of Iron Oxide Functionalized by Nitrate


An iron oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, iron nitrate Fe(NO3)3 was dissolved in an ethanol/water solution and acidified by addition of nitric acid (HNO3). The resultant AMO nanomaterial was a black, glassy material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 35 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 21

AMO of Bismuth Oxide Functionalized by Chloride


A bismuth oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, bismuth chloride (BiCl3) was dissolved in an ethanol/water solution and acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a soft, white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 36 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 22

AMO of Zirconium Oxide Functionalized by Sulfate


A zirconium oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, zirconium sulfate (Zr(SO4)2) was dissolved in an ethanol/water solution and acidified by addition of sulfuric acid (H2SO4). The resultant AMO nanomaterial was a flaky, white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 37 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 23

AMO of Titanium Oxide Functionalized by Sulfate


A titanium oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, titanium oxysulfate (TiOSO4) was dissolved in an ethanol/water solution and acidified by addition of sulfuric acid (H2SO4). The resultant AMO nanomaterial was a white, flaky material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 38 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 24

AMO of Antimony Oxide Functionalized by Sulfate


An antimony oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, antimony sulfate (Sb2(SO4)3) was dissolved in an ethanol/water solution and acidified by addition of sulfuric acid (H2SO4). The resultant AMO nanomaterial was a very soft, white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 39 depicts a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 25

AMO of Indium Oxide Functionalized by Chloride


An indium oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, indium chloride (InCl3) was dissolved in an ethanol/water solution and acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 40 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 26

AMO of Indium Oxide Functionalized by Sulfate


An indium oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, indium sulfate (In2(SO4)3) was dissolved in an ethanol/water solution and acidified by addition of sulfuric acid (H2SO4). The resultant AMO nanomaterial was a white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 41 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 27

AMO of Indium Oxide Functionalized by Bromide


An indium oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, indium bromide (InBr3) was dissolved in an ethanol/water solution and acidified by addition of hydrobromic acid (HBr). The resultant AMO nanomaterial was a blue-white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 42 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 28

AMO of Indium Oxide Functionalized by Chloride


An indium oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, indium chloride (InCl3) was dissolved in an ethanol/water solution and acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was grey with a yellow ring and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 43 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 29

Mixed AMO Of Lithium Oxide and Iron Oxide Doped with Tin Oxide and Functionalized by Chloride/Acetate


A doped mixed lithium oxide and iron oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, lithium acetate (Li(CH3COO)) and iron chloride (FeCl3) were dissolved in an ethanol/water solution with a lesser amount of tin chloride (SnCl2). The solution was acidified by addition of hydrochloric acid (HCl). During synthesis, a tan, pinkish color with a green ring on the flask developed. The final AMO nanomaterial, however, was grey and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 44 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 30

Mixed AMO of Lithium Oxide and Iron Oxide Doped with Tin Oxide and Functionalized by Chloride/Acetate


A doped mixed lithium oxide and iron oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, lithium acetate (Li(CH3COO)) and iron chloride (FeCl3) were dissolved in an ethanol/water solution with a lesser amount of tin chloride (SnCl2). The solution was acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a golden pale material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 45 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


EXAMPLE 31

Mixed AMO of Lithium Oxide and Iron Oxide Doped with Tin Oxide and Functionalized by Chloride/Acetate


A doped mixed lithium oxide and iron oxide AMO was synthesized using a single-pot hydrothermal synthesis method. Briefly, lithium acetate (Li(CH3COO)) and iron chloride (FeCl3) were dissolved in an ethanol/water solution with a lesser amount of tin chloride (SnCl2). The solution was acidified by addition of hydrochloric acid (HCl). The resultant AMO nanomaterial was a light creamy white material and was formed into an electrode. The electrode was assembled in a battery cell against lithium metal and cycled by discharging to zero volts, followed by charging to 1.5 volts. FIG. 46 depicts an electron micrograph image of the AMO nanomaterial, a plot of the measured capacity versus cycle number, as well as a plot of the voltage as a function of time during cycling.


At the present time, lithium batteries are perceived to be a safety risk in certain situations. For example, airline regulations currently require partial discharge of lithium batteries that are to be carried in the cargo hold. Fires have been reported in devices utilizing lithium batteries resultant from runaway exothermal reactions. Moreover, lithium fires can be difficult to extinguish with popularly deployed fire suppression systems and devices. For these reasons, lithium containing compounds rather than metallic lithium is used in many commercial battery cells.


Use of lithium containing compounds in an anode, rather than lithium metal, may, however, limit the amount of lithium available for reaction and incorporation into the cathode upon discharge, and may thus also limit the capacity of such cells. The presently disclosed AMO materials, however, show not only large uptake of lithium during discharge but also enhanced safety characteristics. For example, when battery cells comprising the AMO material in a cathode and a lithium metal electrode are subjected to safety tests, such as nail penetration tests, shorting tests, and overvoltage tests, the cells perform well and do not appear to pose an unacceptable risk of fire or explosion. This may be because the AMO's passivate lithium metal within a cell or battery. Even using solid or pure lithium as an anode, devices employing AMO's of the present disclosure as a cathode do not appear to pose an unacceptable risk of fire or explosion. The novel safety results may also be due to the low operating voltage of cells constructed according to the present disclosure, which in some embodiments is <1.5 V compared to a traditional lithium ion operating voltage of >3.0 V.


Several cells were constructed with a cathode comprising an AMO (SnO2) according to the present disclosure. The cathode was prepared from a composition of the AMO (SnO2), Ketjen black (KB), polyvinylidene fluouride (PVDF), and polyaryl amide (PAA) at a ratio of 63/10/26.1/0.9 by volume. Double-sided layers of this composition were prepared at 4mg/cm2 per side. Six of these layers comprised the cathode. The area of the prepared cathode was 9×4 cm2. A separator was obtained from Targray Technology International, Inc. and comprised a 25 μm thick layer of polypropylene. The separator was 9.4×4.4 cm2 in area. An electrolyte was prepared from 1M LiPF6 in a solvent of ethylene carbonate, diethyl carbonate, and dimethyl carbonate in a 1/1/1 ratio by volume. The anode was a 50 μm thick layer of lithium metal of 9.2×4.2 cm2 in area.


Two of the constructed cells were discharged prior to a safety test and found to have an actual capacity of 1.7 Ah, and a specific capacity of 1575 mAh/g SnO2.



FIG. 47 is a plot of temperature and voltage for a cell constructed as described above and subjected to a nail penetration test. The test was conducted at room temperature and no events (e.g., fires) were observed. It can also be seen that the temperature and voltage remained stable.



FIG. 48A is a plot of temperature and voltage for a cell constructed as described above and subjected to an overcharge test. A 1A current was applied. Apart from some gassing from the cell no adverse events were observed over the timeframe of the test. FIG. 48B is a plot of the overcharge test of FIG. 48A focusing on the start of the test.


It should be understood that the examples constructed for purpose of penetration tests are not intended to be limiting with respect to the entire disclosure herein. Cells and batteries of various sizes, capacities, and materials may be constructed according to the present disclosure. Utilizing the AMO's of the present disclosure, such batteries would reap the benefits of the increased safety demonstrated herein, whether such safety is ultimately due to lithium passivation, lower voltage, or other factors.


Embodiments of constructed electrochemical cells incorporating AMO material as a cathode and lithium as an electrode have been tested to successfully undergo up to 900 or more charge-discharge cycles without resulting in catastrophic and destructive failure. Stated another way, embodiments of constructed electrochemical cells incorporating AMO material as a cathode and lithium as an electrode have been tested to successfully undergo up to 900 or more charge-discharge cycles and still hold a charge and maintain useful capacity.


Without wishing to be bound by any theory, the enhanced safety provided by use of AMO-based cathode materials in lithium cells may arise from the ability of the AMO material to passivate metallic lithium and prevent dendrite formation. The inventors have observed that, upon cycling, the metallic lithium anode did not appear to grow or otherwise form dendrites, but the lithium anode took on a softer and less crystalline appearing structure. In some embodiments, the lithium anode may be passivated, such as by cycling as a component of an electrochemical cell as described herein, and then removed from the electrochemical cell and used as an electrode in a new electrochemical cell with a different cathode. Additionally, cells constructed according to the present disclosure make use of low operating voltages, such as between 1 and 2 volts, which contrasts with the typical voltage of a lithium or lithium-ion battery cell, which operate commonly around 3-4.2 volts. Such a difference in operational voltage may, in part, account for the safety of the disclosed cells.


With respect to construction of cells or batteries using lithium as an anode according to the present disclosure, in some embodiments, the entire anode (100%) is metallic lithium. The metallic lithium may only be substantially pure in that a minute percentage of the anode may comprise trace elements and impurities that do not affect the performance of the cell or battery in a measurable way. In various embodiments, the anode comprises at least 50%, 55%, 60%, 65%, 75%, 80%, 85%, 90%, or 95% metallic lithium.


For purposes of the present disclosure the term “metallic lithium” refers to lithium in its neutral atomic state (i.e., non-ionic state). The term metallic lithium is intended to distinguish over other forms of lithium including lithium ions and lithium compounds. The term metallic lithium may refer to neutral atomic lithium present in mixtures that comprise lithium atoms, such as mixtures of lithium and other elements, compounds, or substances. The term metallic lithium may refer to neutral atomic lithium present in lithium alloys, such as a metallic mixture including lithium and one or more other metals. The term metallic lithium may refer to neutral atomic lithium present in composite structures including lithium and one or more other materials. Electrodes comprising or including metallic lithium may include other materials besides lithium, but it will be appreciated that metallic lithium may correspond to an active material of such an electrode. In some cases, an anode in an electrochemical cell comprises metallic lithium.


For purposes of this disclosure, metallic lithium may be taken to mean lithium that is not reacted with any other element so as to have formed a compound (at least at the time of battery or cell construction). In some embodiments, a portion of the anode may be metallic lithium while a portion of the anode may be a lithium compound containing various percentages of lithium that is reacted with other elements to form a lithium compound. The metallic lithium may be arranged to be segregated geometrically on or in the anode relative to the lithium compound portion of the anode.


All references throughout this application, for example patent documents including issued or granted patents or equivalents, patent application publications, and non-patent literature documents or other source material, are hereby incorporated by reference herein in their entireties, as though individually incorporated by reference.


All patents and publications mentioned in the specification are indicative of the levels of skill of those skilled in the art to which the invention pertains. References cited herein are incorporated by reference herein in their entirety to indicate the state of the art, in some cases as of their filing date, and it is intended that this information can be employed herein, if needed, to exclude (for example, to disclaim) specific embodiments that are in the prior art. For example, when a compound is claimed, it should be understood that compounds known in the prior art, including certain compounds disclosed in the references disclosed herein (particularly in referenced patent documents), are not intended to be included in the claim.


When a group of substituents is disclosed herein, it is understood that all individual members of those groups and all subgroups and classes that can be formed using the substituents are disclosed separately. When a Markush group or other grouping is used herein, all individual members of the group and all combinations and subcombinations possible of the group are individually included in the disclosure. As used herein, “and/or” means that one, all, or any combination of items in a list separated by “and/or” are included in the list; for example “1, 2 and/or 3” is equivalent to “‘1’ or ‘2’ or ‘3’ or ‘1 and 2’ or ‘1 and 3’ or ‘2 and 3’ or ‘1, 2 and 3’”.


Every formulation or combination of components described or exemplified can be used to practice the invention, unless otherwise stated. Specific names of materials are intended to be exemplary, as it is known that one of ordinary skill in the art can name the same material differently. One of ordinary skill in the art will appreciate that methods, device elements, starting materials, and synthetic methods other than those specifically exemplified can be employed in the practice of the invention without resort to undue experimentation. All art-known functional equivalents, of any such methods, device elements, starting materials, and synthetic methods are intended to be included in this invention. Whenever a range is given in the specification, for example, a temperature range, a time range, or a composition range, all intermediate ranges and subranges, as well as all individual values included in the ranges given are intended to be included in the disclosure.


As used herein, “comprising” is synonymous with “including,” “containing,” or “characterized by,” and is inclusive or open-ended and does not exclude additional, unrecited elements or method steps. As used herein, “consisting of” excludes any element, step, or ingredient not specified in the claim element. As used herein, “consisting essentially of” does not exclude materials or steps that do not materially affect the basic and novel characteristics of the claim. Any recitation herein of the term “comprising,” particularly in a description of components of a composition or in a description of elements of a device, is understood to encompass those compositions and methods consisting essentially of and consisting of the recited components or elements. The invention illustratively described herein suitably may be practiced in the absence of any element or limitation that is not specifically disclosed herein.


The terms and expressions which have been employed are used as terms of description and not of limitation, and there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the invention claimed. Thus, it should be understood that although the present invention has been specifically disclosed by preferred embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those skilled in the art, and that such modifications and variations are considered to be within the scope of this invention as defined by the claims.

Claims
  • 1. A battery cell having an electrode comprising at least one solid metal oxide material, wherein the metal oxide is surface functionalized with a material that is substantially monodispersed and provides acidic electron withdrawing groups having a molecular weight of less than 200, and having an opposing electrode comprising at least 50% metallic lithium when the battery cell is constructed.
  • 2. The battery cell of claim 1, wherein the material that surface functionalizes the surface of the metal oxide is acidic but not superacidic, having a pH <7 when suspended in an aqueous solution at 5 wt % and a Hammett function H0 >−12.
  • 3. The battery cell of claim 2, wherein the material that surface functionalizes the surface of the metal oxide is acidic but not superacidic, having a pH <5 when suspended in an aqueous solution at 5 wt % and a Hammett function H0 >−12.
  • 4. The battery cell of claim 2, wherein the opposing electrode is 95% or greater metallic lithium when the battery cell is constructed.
  • 5. The battery cell of claim 2, wherein a surface of the opposite electrode comprises pure metallic when the battery cell is constructed.
  • 6. The battery cell of claim 2, wherein at least a geometric portion of the opposing electrode consists of metallic lithium when the battery cell is constructed.
  • 7. A battery cell having a cathode comprising a solid metal oxide nanomaterial being in a form MmOxG, where Mm is a metal, Ox is total oxygen, MmOx is a metal oxide, G is at least one electron-withdrawing surface group, and “/” makes a distinction between the metal oxide and the electron-withdrawing surface group, the battery electrode solid metal oxide nanomaterial having a pH<5 when re-suspended, after drying, in water at 5 wt % and a Hammett function H0 >−12, at least on its surface, wherein an anode of the battery comprises at least 50% metallic lithium that is not reacted with other elements at the time of construction of the battery cell.
  • 8. The battery cell of claim 7, wherein the solid metal oxide nanomaterial comprising the cathode includes a second different metal “Nn”, where n is greater than zero and no greater than 5.
  • 9. The battery cell of claim 8, wherein the solid metal oxide nanomaterial comprising the cathode includes a third different metal “Rr”, where r is greater than zero and no greater than 5.
  • 10. The battery cell of claim 7, further comprising an anode of a non-acidic material.
  • 11. The battery cell of claim 7, wherein the anode comprises at least 95% metallic lithium.
  • 12. A method comprising: providing a metallic lithium anode in a battery cell;providing a cathode in the battery cell that comprises at least one solid metal oxide nanomaterial including a surface that is acidic but not superacidic, the surface having a pH<5 when re-suspended, after drying, in water at 5 wt % and a Hammett function H0 >−12.
  • 13. A method of passivating a metallic lithium anode in a battery cell comprising providing a cathode in the battery cell that comprises at least one solid metal oxide nanomaterial including a surface that is acidic but not superacidic, the surface having a pH<5 when re-suspended, after drying, in water at 5 wt % and a Hammett function H0 >−12.
  • 14. A battery cell comprising an anode, an electrolyte, and a cathode, wherein one of the cathode comprises at least one solid metal oxide nanomaterial including a surface that is acidic but not superacidic, the surface having a pH<5 when re-suspended, after drying, in water at 5 wt % and a Hammett function H0 >−12, and wherein at least part of the anode consists essentially of metallic lithium.
CROSS-REFERENCE To RELATED CASE

This is a divisional application claiming priority to U.S. patent application Ser. No. 15/981,350, filed May 16, 2018, which claims the benefit of U.S. provisional patent application Ser. No. 62/507,659, filed on May 17, 2017, entitled “Battery with Acidified Cathode and Lithium Anode,” and incorporates such applications by reference into this disclosure as if fully set out at this point.

Provisional Applications (1)
Number Date Country
62507659 May 2017 US
Divisions (1)
Number Date Country
Parent 15981350 May 2018 US
Child 16792409 US