Patent Grant
6886984
This application claims priority based on Japanese Patent Application No. 2002-187076, filed Jun. 27, 2002, the entirety of which is incorporated herein by reference.
The present invention relates to a bearing device for internal combustion engines of automobiles or the like, comprising a crankshaft and bearings supporting the crankshaft in an internal combustion engine, and more particular, to a bearing device for internal combustion engines, in which a crankshaft having not been subjected to surface hardening such as induction hardening or the like, and bearings are combined with each other.
Conventionally, in a combination of a crankshaft and bearings (including main bearings and connecting rod bearings) in internal combustion engines of automobiles or the like, steel crankshafts (referred below to as “hardened steel shaft”) having been subjected to surface hardening such as induction hardening or the like, and shafts made of spheroidal graphite cast iron (referred below to as “DCI shaft”) have been used as materials for constitution of a crankshaft, and bearings for respective shafts have been proposed to be put to practical use.
Hereupon, hardened steel shafts are expensive and involve a disadvantage that cutting chips become continuous and spiral in cutting work. Meanwhile, while DCI shafts are inexpensive and involve an advantage that machinability is good, they are low in Young's modulus, so that in the case where the same load as that on hardened steel shafts is applied, vibrations and noise become large to necessarily involve a disadvantage that an increase in shaft diameter is caused when it is tried to maintain a capability comparable to that of hardened steel shafts.
Therefore, development has been recently taken place to use, as crankshafts, non-temper free-cutting steel having an equivalent Young's modulus to that of hardened steel shafts and an excellent machinability, but conventional non-temper free-cutting steel involves a problem that foreign matters contained in a lubricating oil are liable to cause scratches on surfaces of crankshafts.
Hereupon, the invention has been thought of to propose an optimum combination of a crankshaft and bearings in the case where non-temper free-cutting steel having not been subjected to surface hardening such as induction hardening or the like is used for crankshafts. That is, the invention has been thought of in view of the above circumstances, and has its object to provide a bearing device comprising a combination of a crankshaft, for which surface hardening is omitted, and bearings, and capable of ensuring reliability and productivity.
To attain the above object, there is provided a bearing device for internal combustion engines, comprising a crankshaft and bearings supporting the crankshaft in an internal combustion engine, and wherein the crankshaft is made of steel having not been subjected to surface hardening and having a structure, which is mainly composed of pearlite having the pro-eutectoid ferrite fraction of at most 3%, and is processed to have the surface roughness Rz of at most 0.8 μm, and wherein the bearings have an aluminum bearing alloy joined to a back plate thereof and contain, as an alloy component thereof, at least Si particles of less than 4 mass % (the invention according to first aspect).
Crankshaft are fabricated from steel not subjected to surface hardening such as induction hardening or the like and having a structure, which is mainly composed of pearlite having the pro-eutectoid ferrite fraction of at most 3%, whereby precipitation of a ferrite structure having a low hardness is suppressed and thus possible minute scratches on the ferrite structure, caused by foreign matters contained in a lubricating oil and hard particles in a bearing alloy are prevented from growing into giant scratches to lead to an increase in abrasion loss. The relationship between the ferrite fraction and scratching will be described in more detail with reference to FIG. 1.
Then, the ferrite fraction with the scratch evaluation point rate being below 1 is substantially 3% or less. Accordingly, crankshafts are desirably to have the ferrite fraction of 3% or less. Also, when the pro-eutectoid ferrite fraction is over 3%, a ferrite structure is increased to cause much scratching by foreign matters, which finally leads to seizure on bearings. Also, when the surface roughness Rz is over 0.8 μm, early abrasion increases to finally lead to seizure on bearings in some cases.
Meanwhile, in the case where an amount of silicon (referred below to as “Si”) in an aluminum bearing alloy of bearings is less than 4 mass %, an attack of Si particles against crankshafts is suppressed, so that early abrasion and scratching of crankshafts are restricted to be equivalent to or less than abrasion loss and scratching of conventional DCI shafts. An amount of Si is preferably less than 4 mass %, and desirably 0.5 to 3.5 mass %. Provided that an amount of Si is in such range, a concerned combination becomes superior to a combination of a conventional DCI shaft and bearings in terms of abrasion loss.
Also, Si particles of less than 4 mass % contained in the aluminum bearing alloy have a feature in that Si particles having the particle diameter of at most 4 μm have the area ratio of at least 60% relative to a total area of Si particles present on a sliding surface (the invention according to second aspect). In the relationship between the particle diameter and area ratio of Si particles in the aluminum bearing alloy, when Si particles are large in particle diameter and large in area ratio, abrasion loss as well as scratching is also increased as compared with those of conventional DCI shafts. Accordingly, since Si particles having the particle diameter of at most 4 μm are set to have the area ratio of at least 60% relative to a total area of Si particles present on-a sliding surface, Si particles are restricted to cause abrasion loss and scratching, which are equivalent to or less than those of conventional DCI shafts. In addition, the area ratio of Si particles is calculated on the basis of results of measurement obtained by using an image analysis apparatus to analyze a photomicrograph of a sliding surface and measuring particle diameters of all Si particles present in an area of 0.0125 mm2. Particle diameters of Si particles mean diameters of circles having the same areas as those obtained by measuring areas of respective particles.
The aluminum bearing alloy has a feature in that it has a Vickers hardness of at most 70 (the invention according to third). Since an attack of Si particles against crankshafts is abruptly increased when the hardness of the bearing alloy is over a Vickers hardness of 70, the hardness of the bearing alloy must be set at the Vickers hardness of 70 or less. In addition, the Vickers hardness is in some cases referred to as Hv hardness.
Also, the aluminum bearing alloy has a feature in that it has a Vickers hardness (Hv hardness) to meet the formula [B≦(S/2−70) (B: Hv hardness of the aluminum bearing alloy, S: Hv hardness of the crankshaft) (the invention according to fourth aspect)]. As shown in
Further, a conforming layer formed from softer plating or resin coating than the aluminum bearing alloy covers surfaces of the alloy (the inventions according to fifth and sixth aspects). Pb and Sn alloy are used for plating, and a resin liquid obtained by blending a solid lubricant and hard particles with a base resin is used as a coating agent in resin coating. For example, in the case where shaft abrasion loss in a combination of a crankshaft and bearings with no conforming layer of the invention was assumed as shown in
An embodiment of the invention will be described below in detail with reference to the drawings.
In
The crankshaft 3 is made of a steel material with a structure, which is mainly composed of pearlite having the pro-eutectoid ferrite fraction of at most 3%, is machined to have the surface roughness Rz of at most 0.8 μm.
Meanwhile, a method of manufacturing the bearings 5, 6 sliding on the crankshaft 3 comprises cutting a band-shaped bimetal, which is formed by bonding an aluminum bearing metal layer of Al—Sn—Si alloy to a steel back plate, to a predetermined dimension, bending the same into a semi-cylindrical shape, applying machining thereon, and thereafter covering the aluminum bearing metal layer with a conforming layer by means of Pb—Sn alloy plating or resin coating at need. Steel having a thickness of around 0.5 mm to 2 mm is used for the back plate according to the usage, the aluminum bearing metal layer having a thickness of around 0.3 mm to 0.5 mm is bonded to the back plate according to the usage, and the conforming layer has a thickness of 5 to 20 μm or thereabout.
Hereupon, with the bearings 5, 6 according to the embodiment, the aluminum bearing metal layer contains, as its alloy component, at least Si particles of less than 4 mass %, and is manufactured so that Si particles having the particle diameter of at most 4 μm have the area ratio of at least 60% relative to a total area of Si particles present on a sliding surface and the hardness of the aluminum bearing metal layer is at most a Vickers hardness of 70 and satisfies B≦(S/2−70) (B: Hv hardness of the aluminum bearing metal layer, S: Hv hardness of the crankshaft).
An explanation will be given to examples of crankshafts and aluminum bearings, which were manufactured according to the conditions described above. TABLE 5 shows crankshafts of Examples 1 to 6 having the pro-eutectoid ferrite fraction of at most 3% and the surface roughness Rz of at most 0.8 μm and crankshafts of Comparative examples 11 to 21 not meeting either or both of the above conditions, and an investigation was made on abrasion loss for combinations of aluminum bearings (bearings in Example 3 shown in the following TABLE 6) with the crankshafts of Examples 1 to 6 and the crankshafts of Comparative examples 11 to 21 under test conditions indicated in TABLE 3. And a comparison was made between the abrasion loss and abrasion loss generated in combinations of a conventional DCI shaft and bearings to calculate whether the both were equivalent to each other or not, results of which calculation are shown in Graph of FIG. 4.
Then, when the ferrite fraction and the shaft surface roughness Rz in Examples 1 to 6 were plotted in corresponding positions in axes of abscissas and ordinate in Graph shown in
Meanwhile, TABLE 6 shows aluminum bearings of Examples 1 to 7, which had a Si amount of less than 4 mass %, and in which Si particles having a particle diameter of at most 4 μm had the area ratio of at least 60% relative to a total area of Si particles present on a sliding surfaces, and the hardness of an aluminum bearing metal layer was at most a Vickers hardness of 70, and aluminum bearings of Comparative examples 11 to 19, which did not meet one or two or all of the above three conditions, and an investigation was made on shaft roughness variations for combinations of aluminum bearings in Examples 1 to 7 and aluminum bearings in Comparative examples 11 to 19 with a crankshaft (the crankshaft of Example 2 shown in the above TABLE 5) under test conditions indicated in TABLE 4. And a comparison was made between the shaft roughness variations and shaft roughness variations generated in combinations of a conventional DCI shaft and bearings to calculate whether the both were equivalent to each other or not, results of which calculation are shown in Graph of FIG. 5.
Then, when Si amounts and shaft roughness variations in Examples 1 to 7 were plotted in corresponding positions in axes of abscissas and ordinate in Graph shown in
In addition, while bearing alloy components shown in TABLE 6 include Sn, Cu, and so on in addition to Si, it has been found from experimental results that other components than Si had little influence on shaft roughness variation.
As apparent from the above description, according to the invention, there can be provided a bearing device capable of ensuring reliability and productivity, which are equivalent to or more advantageous than those of conventional bearing devices, by a combination of a crankshaft made of steel having not been subjected to surface hardening and having a structure, which is mainly composed of pearlite having the pro-eutectoid ferrite fraction of at most 3%, and processed to have the surface roughness Rz of at most 0.8 μm, and bearings having an aluminum bearing alloy bonded to a back plate thereof and containing, as an alloy component thereof, at least Si particles of less than 4 mass %, among which Si particles having the particle diameter of at most 4 μm have the area ratio of at least 60% relative to a total area of Si particles present on a sliding surface, the bearings having the hardness of at most a Vickers hardness of 70 and satisfying [B≦(S/2−70) (B: Hv hardness of the aluminum bearing alloy, S: Vickers hardness of the crankshaft)].
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-187076 | Jun 2002 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4471030 | Fukuoka et al. | Sep 1984 | A |
| 5536587 | Whitney, Jr. | Jul 1996 | A |
| 6712914 | Suzuki et al. | Mar 2004 | B2 |
| Number | Date | Country |
|---|---|---|
| 2 121 435 A | Dec 1983 | GB |
| 2 358 872 A | Aug 2001 | GB |
| Number | Date | Country | |
|---|---|---|---|
| 20040052438 A1 | Mar 2004 | US |