1. Field of the Invention
The present invention relates to brake shoes are formed from a polymer that is obtained by cross-linking SBR with peroxide of adhesive or sulfur, so that said bicycle brake shoe does not excessively wear the rim while maintaining good performance in wet conditions.
2. Description of the Prior Arts
There are several types of bicycle braking devices on the current market. The types of bicycle braking devices include rim brakes and caliper brake, and the caliper brakes generally includes: a cantilever type, a side pull type, a center pull type.
All these prior art bicycle brakes are equipped with brake shoes typically molded from a rubber that is cross-linked with sulfur. The braking surfaces of the bicycle rim maybe hard and shiny surfaces that have been anodized, or the braking surface can be been ground and then polished to form a bicycle rim with softer braking surfaces. In the case of the anodized rim, the braking surfaces are hard and shiny which provides good braking performance in dry conditions, but poor braking performance in wet conditions. In the case of ground and polished braking surfaces, the conventional rubber brake shoes provide good braking performance in dry conditions, and better braking performance in wet conditions than hard and shiny braking surfaces with an anodized finish.
Attempts have been made to improve braking performance, especially in wet conditions, by manufacturing rubber brake shoes with refractory fillers. For example, rubber brake shoes have been manufactured with alumina (Al2O3). While such improved rubber brake shoes provide good wet and dry performance, such brake shoes with alumina cause too much wear of soft braking surfaces in the ground and polished types of rims. The trend in the bicycle industry is to produce more and more rims that have ground and polished braking surfaces. Since these braking surfaces are softer than the braking surfaces of the anodized rim, the alumina-improved brake shoes should not be used because of the excessive amount of wear on these types of rims.
The present invention has arisen to mitigate and/or obviate the afore-described disadvantages.
One object of the present invention is to provide bicycle brake shoes that have improved braking performance in wet conditions.
Another object of the present invention is to provide bicycle brake shoes that do not excessively wear the rim during deceleration or stopping of the rim by the bicycle brake shoes braking while maintaining good performance in wet conditions.
The foregoing objects can be further attained by providing a bicycle brake shoe comprising a rim contacting portion with a braking surface formed from a polymer that is obtained by cross-linking Styrene butadiene rubber (SBR) with peroxide of adhesive (PO), and the polymer is further added with predetermined superaddition.
The foregoing objects can be further attained by providing a bicycle brake shoe comprising a rim contacting portion with a braking surface formed from a polymer that is obtained by cross-linking Styrene butadiene rubber (SBR) with sulfur (S).
The present invention will become more obvious from the following description when taken in connection with the accompanying drawings, which show, for purpose of illustrations only, the preferred embodiments in accordance with the present invention.
Referring initially to
As seen in
As shown in
Basically, braking device 11 is coupled to the front fork 12 of the bicycle 10 such that it can move between a release position and a brake position.
In the release position, the brake shoes 20 of the braking device 11 do not engage the rim 20 so that the wheel 13 is free to rotate.
In the brake position, the brake shoes 20 of the braking device 11 are pivoted such that the bicycle brake shoes 20 grip the braking surfaces 132 of the rim 131 to decelerate or stop rotation of the wheel 13.
In particular, the rider will operate the brake operating device 14 which in turn will pull cable 141 to cause the brake shoes 20 of the braking device 11 to engage the braking surfaces 132 of the rim 131 of the wheel 13. Since most braking devices are well known to those skilled in the art, the braking device 11 will only be briefly discussed and illustrated herein to the extent needed to understand the present invention.
Basically, each braking device 11 has a pair of brake mechanisms 15 that are pivotally coupled to front fork 12. Each of the braking mechanisms 15 have a brake arm 151, and a pair of brake shoe holders 152 to which the brake shoes 20 are secured in a conventional manner. A link 142 and one end of cable 141 interconnect the upper ends of brake arms 151 such that the brake mechanisms 15 pivot together in a conventional manner.
The brake shoe holders 152 are coupled to the brake arms 151 by a center post 16 and a nut 161. In operation, when the rider operates the brake lever of the brake operating device 14, the inner wire of the cable 141 is pulled within the outer casing of the cable 141 so that the upper portions of the brake arms 151 are pulled inwardly. Thereafter, the friction pads 20 on the brake shoe holders 152 and pad supports 162 are pressed against the side surfaces of the rim 131, thus causing a braking action to be performed.
Once the rider releases the brake lever of the brake operating device 14, the brake wire of the cable 141 is relaxed so that the coil springs within the brake arm cause the brake arms 151 to pivot in the opening direction. As a result, the tip ends of the brake shoes 20 (or so-called friction pads) on the brake shoe holders 152 are withdrawn from the side surfaces of rim 131 so that the braking action is released.
As best seen in
The brake shoes 20 in this embodiment are formed from a polymer that is obtained by cross-linking Styrene butadiene rubber (SBR) with peroxide of adhesive (PO), and the polymer is further added with predetermined superaddition. The braking distances for bicycle brake shoes 20 of the present invention in wet conditions are substantially equal to the braking distances for the prior art bicycle brake shoes. However, the amount of rim wear for bicycle brake shoes 20 of the present invention is substantially reduced as compared to prior art bicycle brake shoes, where a substantial amount of alumina is used.
The aforementioned superaddition includes Stearic Acid, Zinc Stearate, Wax, ZnO, Barium Sulfate, Calcium Stearate, which can be added to the polymer that is obtained by cross-linking SBR with peroxide of adhesive or sulfur, as needed and/or desired, so as to adjust property of the brake shoes 20.
Referring now to
Referring to
In manufacturing the bicycle brake shoes, the various materials to be blended are first measured by weight to the appropriate weight percentage and then mixed together. Next, the mixture is processed in a conventional manner to form an extruded sheet of rubber. The sheet of rubber is then cut into individual sheets that are used in a conventional molding process to form a plurality of bicycle brake shoes with rim contacting portions composed of the rubber compound, as mentioned above.
During the molding process, the attachment portion and the rim contacting portion are preferably integrally formed as a one-piece, unitary member. Alternatively, the attachment portion can be formed of separate piece that is integrally attached to the rim contacting portion by adhesive or the like after molding the rim contacting portion as mentioned above. Moreover, one end of the center post can be embedded within the attachment portion and/or the rim contacting portion during the molding process mentioned above.
The bicycle brake shoes in accordance with the present invention are made from the polymer that is obtained by cross-linking SBR with peroxide of adhesive or sulfur. The wet braking distance for conventional bicycle brake shoes is very poor, while very little rim wear occurs. Accordingly, rubber brake shoes have been manufactured with alumina (Al2O3 in order to improve the wet braking performance, while such improved rubber brake shoes with alumina cause too much wear of soft braking surfaces in the ground and polished types of rims. The braking distances for bicycle brake shoes 20 of the present invention in wet conditions are substantially equal to the braking distances for the prior art bicycle brake shoes with alumina. However, the amount of rim wear for bicycle brake shoes 20 of the present invention is substantially reduced as compared to prior art bicycle brake shoes, where a substantial amount of alumina is used.
While we have shown and described various embodiments in accordance with the present invention, it should be clear to those skilled in the art that further embodiments may be made without departing from the scope of the present invention.