During a combustion cycle of an internal combustion engine (ICE), air/fuel mixtures are provided to cylinders within an engine block of the ICE. The air/fuel mixtures are compressed and/or ignited and combusted to provide output torque via reciprocating pistons positioned within the cylinders.
According to an aspect of an exemplary embodiment, a piston for an internal combustion engine is provided. The piston can include a piston head defined by a top surface, a circumferential side surface, a bottom cavity, and a thermal insulation coating (TIC) applied to at least a portion of the top surface. The piston head also includes a top portion which defines the top surface and is made from an aluminum material, and a bottom portion which forms the remainder of the piston head and is made from a ferrous material. The top portion and the bottom portion can be joined by welding. The TIC can be silica. The top surface of the piston head can be anodized prior to application of the TIC. The TIC can have a thickness of about 0.05 millimeters to about 0.15 millimeters. The piston head includes a crown, defined by an annular surface extending inward from the circumferential surface and defining the piston head top surface, a crown bowl surface, and an inner crown circumferential surface extending between an inner edge of the annular surface and an outer periphery of the crown bowl surface. The crown bowl surface can be convex. The TIC can be further applied to at least a portion of one or more of the crown bowl surface and the inner crown circumferential surface. The circumferential side surface can include one or more circumferential piston ring grooves.
According to an aspect of an exemplary embodiment, an internal combustion engine is provided. The engine can include a cylinder block defining one or more cylinder bores, one or more pistons corresponding to each of the one or more cylinder bores and configured to reciprocate therein. Each piston can include a piston head defined by a top crown, a circumferential side surface, a bottom cavity, and a thermal insulation coating (TIC) applied to at least a portion of the annular surface. The top crown can be defined by an annular surface extending inward from the circumferential surface and defining the piston head top surface, a crown bowl surface, and an inner crown circumferential surface extending between an inner edge of the annular surface and an outer periphery of the crown bowl surface. The piston head includes a top portion which defines the top surface and comprises an aluminum material, and a bottom portion forming the remainder of the piston head and comprises a ferrous material. The top portion and the bottom portion of each piston head can be joined by welding. The TIC of each piston head can be silica. The top surface of the piston head can be anodized prior to application of the TIC. The TIC can have a thickness of about 0.05 millimeters to about 0.15 millimeters. The TIC can be further applied to at least a portion of one or more of the crown bowl surface and the inner crown circumferential surface. The top portion can be configured such that the top portion defines each portion of crown to which the TIC is applied. The TIC can be further applied to at least a portion of the crown bowl surface and the inner crown circumferential surface.
Other objects, advantages and novel features of the exemplary embodiments will become more apparent from the following detailed description of exemplary embodiments and the accompanying drawings.
Embodiments of the present disclosure are described herein. It is to be understood, however, that the disclosed embodiments are merely examples and other embodiments can take various and alternative forms. The figures are not necessarily to scale; some features could be exaggerated or minimized to show details of particular components. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for teaching one skilled in the art to variously employ the present invention. As those of ordinary skill in the art will understand, various features illustrated and described with reference to any one of the figures can be combined with features illustrated in one or more other figures to produce embodiments that are not explicitly illustrated or described. The combinations of features illustrated provide representative embodiments for typical applications. Various combinations and modifications of the features consistent with the teachings of this disclosure, however, could be desired for particular applications or implementations.
Provided herein are bimetallic pistons, and engines incorporating the same, comprising thermal insulation coatings (TIC). Specifically, pistons comprising pistons heads having an upper aluminum portion and a lower ferrous portion provided enhanced mechanical benefits while minimizing undesired heat transfer. The aluminum top portions are compatible with various TICs, for example silica TICs.
Referring to
Piston head 30 is defined by the top surface 31 and a circumferential side surface 32. Circumferential side surface 32 extends downward from top surface 31 and generally defines the cylindrical piston head 30. Piston head 30 may be non-cylindrical in some embodiments, so long as the top surface 31 generally corresponds to the cross sectional geometry of the cylinder bore 13. Piston head 30 can optionally include one or a plurality of circumferential axially spaced piston ring grooves 33 may optionally extend inward from the circumferential side surface, said piston ring grooves being configured to receive a piston ring (not shown). Piston rings can be utilized for one or more a sealing, the combustion chamber 15, controlling oil migration within the cylinder bore 13, and preventing the escape of pressurized gases to a crankcase 9. Piston head 30 can optionally further include a bottom cavity 34. Piston head 30 can further include a pin boss portion 52 which extends downward from top surface 31 for disposition within bottom cavity 34.
Piston 20 is configured for slidable reciprocating motion within the cylinder bore 13. Circumferential side surface 32 is engageable with cylinder wall 14 to guide piston 20 in its reciprocating motion and to absorb thrust forces that may be imposed upon piston 20 by the cylinder wall 14. The top surface 31 forms one wall a the combustion chamber 15 that, upon movement of the piston 20, causes the expansion or contraction of the combustion chamber 15 as is required for operation in an internal combustion engine working cycle. To utilize piston 20 as a means for developing power, piston 20 is operatively engaged with external elements, such as a crankshaft 62 of a vehicle. Crankshaft 62 can translate reciprocating movement of one or more pistons 20 to rotational motion and translate the latter to one or more wheels of a vehicle drivetrain, for example. Crankshaft 62 can be operatively coupled to one or more pistons 20 via one or more respective connecting rods 58; each connecting rod 58 can couple to a piston pin bore 54 of a pin boss 52 via a piston pin 56, for example. In some embodiments, piston pin bore 54 can be formed in one or more places through the circumferential side surface 32. In such an embodiment, the pin boss 52 can be an optional feature.
Top portion 35 defines the top surface 31. In some embodiments, top portion 35 defines the top surface 31 upon which the TIC 38 is applied. Thereafter, top portion 35 and bottom portion 36 can vary relative to a height H of piston head 30.
Top portion 35 comprises aluminum, or a suitable aluminum alloy as are known in the art. In one embodiment, top portion 35 comprises an aluminum-silicon alloy. An aluminum-silicon alloy can comprise up to about 30% silicon, or about 5% to about 25% silicon. In one embodiment, an aluminum-silicon alloy can comprises a eutectic alloy having about 12% silicon, and optionally about 1% each of one or more of copper, nickel and magnesium. In some embodiments, top portion 35 comprises a hyper-eutectic aluminum-silicon alloy having about 17% to about 25% silicon. Top portion 35 can be cast or forged, for example. Bottom portion 36 comprises a ferrous material, such as cast iron, steel, stainless steel, or steel alloys as are known in the art. Some examples of suitable steel alloys include 38MnSiVS5, 42CrMo4, and 38MnVS6, among others. Top portion 35 and bottom portion 36 can be joined at an interface 37 by various suitable methods. In some embodiments, top portion 35 and bottom portion 36 can he joined by welding. Aluminum top portion 35 and ferrous bottom portion 36 can be welded using bimetallic transition inserts, for example. In other embodiments, aluminum top portion 35 and ferrous bottom portion 36 can be welded by dip coating or brazing. In some embodiments, top portion 35 and bottom portion 36 can be joined by mechanical means such as screws or bolts. In some embodiments, top portion 35 comprises a sheath which is disposed about bottom portion 36, such as by compression fitting, for example.
In some embodiments, as shown in
Suitable TIC 38 includes those which exhibit suitable heat-shielding performance and are compatible with aluminum top portion 35 such that TIC 38 exhibits suitable bonding when applied thereto. In one embodiment, TIC 38 comprises silica (SiO2). [Are there any other suitable aluminum-compatible TICS which might be good alternatives to silica.?] A silica TIC 38 can be applied to the top surface 31 of top portion 35 by treating top surface 31 to form a high porosity aluminum oxide surface. The high porosity aluminum oxide surface can be about 50 microns to about 150 microns thick, about 70 microns to about 120 microns thick, or about 80 microns to about 100 microns thick. In a specific example, the high porosity aluminum oxide surface is about 90 microns thick. Top surface 31 can be treated to form porous aluminum oxide by anodizing, for example. Silica can thereafter be applied to, or otherwise formed upon, top surface 31. For example, in one embodiment, top surface 31 can be exposed to a heated solution of comprising alcohol and sodium silicate. In one embodiment, top surface 31 can be exposed to perhydropolysilazane which forms a silica layer thereon upon reacting with water vapor. In another embodiment, top surface 31 can be exposed to a heated solution of dibutyl ether (90-99% by weight) and perhydropolysilazane (1-10% by weight). The TIC 38 layer can vary in thickness based upon the desired insulating characteristics, and TIC 38 bonding capabilities. In some embodiments, TIC 38 comprises a thickness of up to about 0.1 millimeters, up to about 0.125 millimeters, or up to about 0.15 millimeters. In some embodiments TIC 38 comprises a thickness of about 0.05 millimeters to about 0.15 millimeters.
While exemplary embodiments are described above, it is not intended that these embodiments describe all possible forms encompassed by the claims. The words used in the specification are words of description rather than limitation, and it is understood that various changes can be made without departing from the spirit and scope of the disclosure. As previously described, the features of various embodiments can be combined to form further embodiments of the invention that may not be explicitly described or illustrated. While various embodiments could have been described as providing advantages or being preferred over other embodiments or prior art implementations with respect to one or more desired characteristics, those of ordinary skill in the art recognize that one or more features or characteristics can be compromised to achieve desired overall system attributes, which depend on the specific application and implementation. These attributes can include, but are not limited to cost, strength, durability, life cycle cost, marketability, appearance, packaging, size, serviceability, weight, manufacturability, ease of assembly, etc. As such, embodiments described as less desirable than other embodiments or prior art implementations with respect to one or more characteristics are not outside the scope of the disclosure and can be desirable for particular applications.