Patent Grant
10590271
The present invention relates to a binder composition, in particular, a two-package binder composition. The present invention further relates to a paint formulation, in particular, a multi-color paint formulation, comprising the binder composition.
The paint industry now has increased need for paint appearances that meet special customer requirements. Both conventional single-color paints and multi-color paints are being designed for customized appearances. Conventional single-color paints contain one colorant, while multi-color paints contain at least two colorants with different colors. Before application, with conventional operation methods such as spraying, brushing and rolling, the colorants shall be well and stably distributed and protected in the paints so as to provide desired paint film appearances.
The present invention provides a binder composition for paint formulations where after conventional operations such as brushing, trowel, rolling, and spraying, the colorants are protected in the globules of the binder composition and bring to the paint film a desired special appearance.
The present invention provides a binder composition comprising a first binder comprising by dry weight based on total dry weight of the first binder, from 2% to 99% polymer particles, from 0.4% to 40% an anionic polyelectrolyte, and from 0.2% to 50% a colorant.
The present invention further provides a binder composition comprising a first binder and a second binder. The first binder comprises, by dry weight based on total dry weight of the binder composition, from 1% to 98% polymer particles, from 0.3% to 20% an anionic polyelectrolyte, and from 0.1% to 20% a colorant; and the second binder comprises, by dry weight based on total dry weight of the binder composition, from 0.5% to 70% a clay and from 0.03% to 10% a dispersant.
The present invention further provides a paint formulation comprising the binder composition and a continuous phase comprising from 30% to 99%, by dry weight based on total dry weight of the continuous phase, polymer particles. The dry weight ratio of the continuous phase to the binder composition is from 50:1 to 1:20.
The binder composition of the present invention comprises a first binder. The binder composition of the present invention further comprises a second binder.
The First Binder
The first binder of the present invention comprises by dry weight based on total dry weight of the binder composition, from 1% to 98%, preferably from 10% to 90%, and more preferably from 15% to 85%, polymer particles. The polymer particles are from 2% to 99%, preferably from 12% to 92%, and more preferably from 18% to 87% by dry weight based on total dry weight of the first binder.
The polymer particles comprise, as polymerization units, at least one α,β-ethylenically unsaturated nonionic monomer, that is, α,β-ethylenically unsaturated monomer without bearing an ionic charge between pH=1-14. Suitable examples of the α,β-ethylenically unsaturated nonionic monomers include (meth)acrylic ester monomers, i.e., methacrylic ester or acrylic ester monomers including methyl acrylate, ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, decyl acrylate, lauryl acrylate, methyl methacrylate, butyl methacrylate, isodecyl methacrylate, and lauryl methacrylate; (meth)acrylonitrile; styrene and substituted styrene such as α-methyl styrene, and vinyl toluene; butadiene; ethylene; propylene; α-olefin such as 1-decene; vinyl esters such as vinyl acetate, vinyl butyrate, and vinyl versatate; and other vinyl monomers such as vinyl chloride and vinylidene chloride. Preferably, the α,β-ethylenically unsaturated nonionic monomers are ethyl acrylate, methyl methacrylate, 2-hydroxybutyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, vinyl acetate, acrylonitrile, and any combination thereof.
Optionally, the polymer particles further comprise, as polymerization units, from 0.1% to 10%, and preferably from 0.5% to 5%, by dry weight based on total dry weight of the polymer particles, an ethylenically unsaturated monomer carrying at least one functional group selected from carboxyl, carboxylic anhydride, hydroxyl, amide, amino, ureido, acetoacetate, sulphonate, phosphonate, and any combination thereof. Suitable examples of these monomers are ethylenically unsaturated carboxylic or dicarboxylic acid such as acrylic or methacrylic acid, itaconic acid, and maleic acid; ethylenically unsaturated amide such as (meth)acrylamide; ethylenically unsaturated N-alkylolamide such as N-methylol(meth)acrylamide and 2-hydroxyethyl(meth)acrylamide; hydroxyalkyl ester of the carboxylic or dicarboxylic acid, such as hydroxyethyl (meth)acrylate and hydroxypropyl (meth)acrylate; amino-functional monomers such as N,N-dimethylaminoethyl methacrylate; ureido-functional monomers such as methacrylamidoethyl-2-imidazolidinone; monomers bearing acetoacetate-functional groups such as acetoacetoxyethyl methacrylate; and any combination thereof.
The first binder further comprises by dry weight based on total dry weight of the binder composition, from 0.3% to 20%, preferably from 0.5% to 15%, and more preferably from 1% to 10%, an anionic polyelectrolyte. The anionic polyelectrolyte is from 0.4% to 40%, preferably from 0.8% to 30%, and more preferably from 1.0% to 20% by dry weight based on total dry weight of the first binder.
The anionic polyelectrolyte is polyelectrolyte having a carboxylic acid anion, a sulfonic anion, a sulfate anion, a phosphonic anion, and any combination thereof. Preferably, the anionic polyelectrolyte is polyelectrolyte having a carboxylic acid anion. More preferably, it is completely neutralized or partially neutralized. And most preferably, it has a weight average molecular weight (Mw) of from 105 to 108. Suitable examples of the anionic polyelectrolyte include poly(acrylic acid sodium salt), poly(acrylic acid potassium salt), and poly(styrenesulfonic acid sodium salt).
The first binder further comprises by dry weight based on total dry weight of the binder composition, from 0.1% to 20%, preferably from 0.3% to 8%, and more preferably from 0.5% to 6%, a colorant. The colorant is from 0.2% to 50%, preferably from 0.6% to 17%, and more preferably from 0.8% to 10% by dry weight based on total dry weight of the first binder.
The colorants are organic or inorganic colorant particles, and preferably inorganic colorant particles. Suitable examples of the colorant particles include carbon black, lampblack, black iron oxide, red iron oxide, transparent red oxide, yellow iron oxide, transparent yellow oxide, brown iron oxide, phthalocyanine green, phthalocyanine blue, naphthol red, quinacridone red, quinacridone magenta, quinacridone violet, DNA orange, and organic yellow.
Optionally, the first binder further comprises by dry weight based on total dry weight of the binder composition, from 0.1% to 20%, preferably from 0.3% to 15%, and more preferably from 0.5% to 10%, a polysaccharide. The polysaccharide is from 0.2% to 30%, preferably from 0.6% to 20%, and more preferably from 1% to 15% by dry weight based on total dry weight of the first binder.
Examples of such polysaccharide include an acidic polysaccharide that can cross-link or precipitate with metal ions. Suitable examples of the polysaccharide include gellan, pectin, carrageenan, alginic acid, alginates, mixtures or any derivatives thereof. Preferably, the polysaccharide is alginic acid, alginate, or any combination thereof. Preferable, the polysaccharides exclude guar gum, and gelatin.
Optionally, the first binder further comprises by dry weight based on total dry weight of the binder composition, from 1% to 30%, preferably from 2% to 20%, and more preferably from 5% to 10%, pigment particles. The pigment particles are from 0.15% to 80.5%, preferably from 2.2% to 50.5%, and more preferably from 5.2% to 40.5% by dry weight based on total dry weight of the first binder.
The pigment particles refer to inorganic materials which are capable of materially contributing to the opacity (or hiding capability) of a composition. Such materials typically have a refractive index of greater than 1.8, and include titanium dioxide (TiO2), zinc oxide, zinc sulfide, barium sulfate, barium carbonate, and lithopone. Titanium dioxide (TiO2) is preferred.
Optionally, the first binder further comprises by dry weight based on total dry weight of the binder composition, from 0.5% to 50%, preferably from 1% to 30%, and more preferably from 3% to 20%, extender particles. The extender particles are from 0.6% to 50.5%, preferably from 1.5% to 30.5%, and more preferably from 3.5% to 20.5% by dry weight based on total dry weight of the first binder.
The extender particles refer to inorganic materials having a refractive index of less than or equal to 1.8 and greater than 1.3, and include calcium carbonate, calcium sulfate, aluminosilicate, silicate, zeolite, mica, diatomaceous earth, Al2O3, zinc phosphate, solid or hollow glass, and ceramic beads.
The Second Binder
The second binder of the present invention comprises by dry weight based on total dry weight of the binder composition, from 0.5% to 70%, preferably from 1.0% to 30%, and more preferably from 3% to 20%, a clay.
The clay refers to hydrous phyllosilicates with magnesium, aluminum, lithium sodium and other metal elements. Suitable examples of the clay include lithium magnesium silicate commercially available as LAPONITE™ RD and LAPONITE RDS from Rockwood Additives Ltd., aluminum magnesium silicate commercially available as VEEGUM™ from Vanderbilt Company, Inc., and any combination thereof.
The second binder further comprises by dry weight based on total dry weight of the binder composition, from 0.03% to 10%, preferably from 0.1% to 5%, and more preferably from 0.3% to 3%, a dispersant.
Suitable examples of the dispersants include sodium orthophosphate, sodium pyrophosphate, sodium tripolyphosphate, sodium tetraphospahte, sodium hexametaphosphate, sodium carbonate, sodium polyphosphate, sodium metaphosphate, and sodium hydroxide. Sodium ion can be also replaced by other monovalent alkali metal ions, such as lithium and potassium. Preferably, the dispersant is sodium pyrophosphate.
Optionally, the second binder further comprises by dry weight based on total dry weight of the binder composition, from 0.1% to 30%, preferably from 2% to 20%, and more preferably from 5% to 15%, the polymer particles.
Preparation of Either Binder
Either binder of the present invention is prepared by mixing the binder components in water and with stirring. For single-color paints, one colorant is added to the first binder, while for multi-color paints, at least two different colorants are added individually to different first binders. Each first binder comprises only one colorant.
Preparation of the Binder Composition
The binder composition of the present invention is prepared by simply mixing the first binder with the second binder. For multi-color paints, each first binder was mixed with each second binder to prepare different binder compositions. Different binder compositions comprising different first binders comprising different colorants are therefore mixed together to prepare the binder composition for multi-color paints.
The Paint Formulation
The binder composition is made into a paint formulation by dispersing the binder composition into a continuous phase; the continuous phase is prepared by mixing polymer emulsion with paint additives.
Dry weight ratio of the continuous phase to the binder composition (or dispersed phase) is from 50:1 to 1:20, preferably from 20:1 to 1:10, and more preferably from 10:1 to 1:5.
The continuous phase comprises by dry weight based on total dry weight of the continuous phase, from 30% to 99%, preferably from 50% to 95%, and more preferably from 70% to 92%, the polymer particles.
Optionally, the continuous phase further comprises by dry weight based on total dry weight of the continuous phase, from 0.5% to 65%, preferably from 1% to 40%, and more preferably from 5% to 30%, the extender particles.
Multi-color paints may also be prepared through mixing different single-color paint formulation made according to the above process. Suitable examples of the paint additives include coalescing agents, cosolvents, surfactants, buffers, neutralizers, thickeners, non-thickening rheology modifiers, dispersants, humectants, wetting agents, mildewcides, biocides, plasticizers, antifoaming agents, defoaming agents, anti-skinning agents, flowing agents, and anti-oxidants.
Suitable examples of the thickener include alkali-soluble emulsions (ASE), hydrophobically modified alkali soluble emulsions (HASE), hydrophobically modified ethylene oxide-urethane polymers (HEUR), hydrophobically modified hydroxyethyl cellulose (HMHEC), hydrophobically modified polyacrylamide, and fumed silica.
Paint Operations
The paint formulations may be operated by conventional operation methods including troweling, brushing, rolling, and spraying methods.
Suitable substrates for such paint operations include concrete board, cement board, medium-density fiber (MDF) board, particle board, gypsum board, wood, stone, metal, plastics, wall paper and textile. Preferably, all the substrates are pre-primed by waterborne or solvent-borne primers.
1. Preparation of Binder Compositions (Binders) 1 to 7 (For Single-Color Paint), Binder Composition (Binder) 8 (For Multi-Color Paint) and Comparative Binder Compositions (Comparative Binders) 9 to 12
Preparation of the first binder for Binder Composition 1: 0.4 g A-190 poly (acrylic acid sodium salt), was dispersed in 25.9 g DI water by stirring at 200-1500 rpm for 5 min, and then kept at room temperature overnight with stirring at 500-2000 rpm. When the A-190 was dissolved, 24 g PRIMAL TX-010 acrylic emulsion, 1.2 g TEXANOL ester alcohol and 1.0 g XERACOLOUR red colorant were added into the above solution with stirring at 500 rpm for 20 min.
Preparation of the second binder for Binder Composition 1: 2 g HZ-200 clay and 0.2 g sodium pyrophosphate were dispersed in 37.8 g DI water, and then 8 g PRIMAL TX-010 acrylic emulsion was added by stirring at 100-500 rpm for 10 min.
Preparation of binder composition for Binder Composition 1: 52 g first binder and 48 g second binder were mixed by stirring at 10-300 rpm for 10 min.
The first and the second binders for Binder Compositions 2 to 7 and Comparative Binder Compositions 9 to 12 were prepared according to the above process of preparation for the first and the second binders for Binder Composition 1, with detailed binder components listed in Table 1.
The Binder Compositions 1 to 7 and Comparative Binder Compositions 9 to 12 were prepared by mixing corresponding first binder and second binder and stirred at 10-300 rpm for 10 min.
Binder Composition 8 was prepared by mixing at a ratio of 4:5:1 of three different binder compositions each comprising one different red, blue or grey colorant prepared according to the procedure of making Binder Composition 7.
2. Preparation of Single-Color Paint Formulations (Paints) 1 to 7, Multi-Color Paint Formulation (Paint) 8 and Comparative Paint Formulations (Comparative Paints) 9 to 12
Preparation of Paint Formulation 1 (Paint 1) from Binder 1 (without comprising polysaccharide): 3.6 g TEXANOL ester alcohol and 0.5 g NOPCO NXZ defoamer were added into 85 g PRIMAL TX-100 acrylic emulsion under stirring, then 2.0 g ACRYSOL SCT 275 rheology modifier was dispersed into above emulsion, then 48 g Binder 1 was dispersed into the emulsion under stirring at 10-100 rpm for 10 min.
Paint Formulations 2, 3, and Comparative Paint Formulations 9 and 10 (formulations without comprising polysaccharide) were prepared from Binder Compositions 2, 3, and Comparative Binder Compositions 9 and 10, respectively, according to the above process of preparation for Paint Formulation 1.
Preparation of Paint Formulation 4 (Paint 4) from Binder 4 (comprising polysaccharide): 0.35 g TERGITOL 15-S-40 surfactant was added into 70.0 g PRIMAL TX-100 acrylic emulsion by stirring, followed by addition of 0.5 g NOPCO NXZ deformer, 0.9 g 20% CaCl2 solution, 3.2 g TEXANOL ester alcohol, 1.0 g ACRYSOL SCT 275 rheology modifier and 0.3 g ACRYSOL RM-12W rheology modifier in sequence. After that, 10 g Binder 4 was dispersed into the emulsion under stirring at 10-100 rpm for 10 min.
Paint Formulations 5 to 8, and Comparative Paint Formulations 11 and 12 (formulations comprising polysaccharide) were prepared from Binder Compositions 5 to 8, and Comparative Binder Compositions 11 and 12, respectively, according to the above process of preparation for Paint Formulation 4.
1. Colorant Protection
Binder compositions were observed of forming globules when they were added in to the continuous phase and prepared to paint formulations. By observing through naked eyes, if colorants were not released from the globules into the continuous phase or there was no color leaking out of the globules and in contact directly in the case of multi-color paints, the colorant was considered as protected; otherwise, the colorant was considered as not protected.
2. Heat Aging Test
300 mL of each paint formulation was added into a 500 mL capped plastic bottle and heated under 50° C. in a Lindberg/Blue M™ vacuum oven of Thermal Electron Corporation for 10 Days. Paint formulations with good colorant protection were observed by naked eyes for gelation or syneresis after heat aging. Paint formulations were stable if neither gelation nor syneresis was observed.
Comparative Paint Formulation 9 (Comparative Paint 9) lacked the anionic polyelectrolyte, and Comparative Paint Formulation 11 (Comparative Paint 11) comprised insufficient amount of the anionic polyelectrolyte. Both Comparative Paints 9 and 11 could not protect the colorant. The result indicated the importance of the anionic polyelectrolyte, and its concentration.
Comparative Paint Formulation 10 (Comparative Paint 10) comprised an anionic polyelectrolyte of Mw less than 1×105. Comparative Paint 10 could not protect the colorant. The result indicated the importance of anionic polyelectrolyte Mw.
Comparative Paint Formulation 12 (Comparative Paint 12) comprised insufficient amount of the clay in its second paint. Comparative Paint 12 could not protect the colorant. The result indicated the importance of the clay.
Paint Formulations 1 to 8 (Paints 1 to 8) comprised required amounts of required components. Paints 1 to 8 well protected the colorant, and are all heat aging stable.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2015/075462 | 3/31/2015 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2016/154879 | 10/6/2016 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2591904 | Zola | Apr 1952 | A |
| 3058931 | Petty | Oct 1962 | A |
| 3442824 | Chandler et al. | May 1969 | A |
| 3458328 | Zola | Jul 1969 | A |
| 3725089 | Zola | Apr 1973 | A |
| 3950283 | Sellars et al. | Apr 1976 | A |
| 4127687 | Dupont | Nov 1978 | A |
| 4264322 | Lewis et al. | Apr 1981 | A |
| 4385097 | Isozaki et al. | May 1983 | A |
| 4826535 | Godly | May 1989 | A |
| 4898895 | Masuoka et al. | Feb 1990 | A |
| 4954368 | Hartridge et al. | Sep 1990 | A |
| 5114481 | Lynch | May 1992 | A |
| 5114484 | Lynch | May 1992 | A |
| 5114485 | Lynch et al. | May 1992 | A |
| 5199801 | Grehn et al. | Apr 1993 | A |
| 5199980 | Lynch et al. | Apr 1993 | A |
| 5268030 | Floyd et al. | Dec 1993 | A |
| 5314535 | Lynch et al. | May 1994 | A |
| 5318619 | Lynch et al. | Jun 1994 | A |
| 5437719 | Lynch et al. | Aug 1995 | A |
| 5480480 | Lynch et al. | Jan 1996 | A |
| 5593731 | Akagi | Jan 1997 | A |
| 6005031 | Bremer-Masseus et al. | Dec 1999 | A |
| 6074474 | Broome et al. | Jun 2000 | A |
| 8628827 | Espinosa | Jan 2014 | B2 |
| 9598557 | Wang | Mar 2017 | B2 |
| 10017657 | Zhang | Jul 2018 | B2 |
| 20040225051 | Moy | Nov 2004 | A1 |
| 20050056187 | Podlas | Mar 2005 | A1 |
| 20050124759 | Heldmann et al. | Jun 2005 | A1 |
| 20060157196 | Koepnick et al. | Jul 2006 | A1 |
| 20060207476 | Coward et al. | Sep 2006 | A1 |
| 20080289538 | Friedrich et al. | Nov 2008 | A1 |
| 20090170978 | Kelly | Jul 2009 | A1 |
| 20100222459 | Kelly | Sep 2010 | A1 |
| 20110236582 | Scheuing et al. | Sep 2011 | A1 |
| 20120094178 | Loveridge | Apr 2012 | A1 |
| 20150059616 | Yun et al. | Mar 2015 | A1 |
| 20150065168 | Roskind et al. | Mar 2015 | A1 |
| 20150065618 | Yun et al. | Mar 2015 | A1 |
| 20150148457 | Yun et al. | May 2015 | A1 |
| 20170226364 | Zhang et al. | Aug 2017 | A1 |
| 20170298237 | Li et al. | Oct 2017 | A1 |
| 20170335133 | Zhang | Nov 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 560547 | Apr 1987 | AU |
| 1193372 | Sep 1985 | CA |
| 1097782 | Jan 1995 | CN |
| 1117509 | Feb 1996 | CN |
| 1532240 | Sep 2004 | CN |
| 101397433 | Apr 2009 | CN |
| 101397483 | Apr 2009 | CN |
| 101397433 | Jan 2012 | CN |
| 104212276 | Dec 2014 | CN |
| 104212286 | Dec 2014 | CN |
| 10444917 | Mar 2015 | CN |
| 104403470 | Mar 2015 | CN |
| 0287589 | Oct 1988 | EP |
| 0424594 | May 1991 | EP |
| 0505664 | Sep 1992 | EP |
| 0896988 | Feb 1999 | EP |
| 896988 | Feb 1999 | EP |
| 0896989 | Feb 1999 | EP |
| 1004638 | May 2000 | EP |
| 2223940 | Sep 2010 | EP |
| 977145 | Dec 1964 | GB |
| 1441268 | Jun 1976 | GB |
| 2078243 | Jan 1982 | GB |
| 57133170 | Aug 1982 | JP |
| 2657554 | Jun 1991 | JP |
| 2004182789 | Jul 2004 | JP |
| 2006199726 | Aug 2006 | JP |
| 03840280 | Nov 2006 | JP |
| 2007231151 | Sep 2007 | JP |
| 2007238919 | Sep 2007 | JP |
| 2007262350 | Oct 2007 | JP |
| 2007296459 | Nov 2007 | JP |
| 2007321045 | Dec 2007 | JP |
| 2011052052 | Mar 2011 | JP |
| 5149602 | Feb 2013 | JP |
| 541628 | Jan 2006 | KR |
| 854445 | Aug 2008 | KR |
| 854445 | Aug 2008 | KR |
| 2238287 | Oct 2004 | RU |
| 9315153 | Aug 1993 | WO |
| 9523197 | Aug 1995 | WO |
| 9532862 | Dec 1995 | WO |
| 0036029 | Jun 2000 | WO |
| 0248276 | Jun 2002 | WO |
| 2006029407 | Mar 2006 | WO |
| 2009133645 | Nov 2009 | WO |
| 201367243 | May 2013 | WO |
| 2013116004 | Aug 2013 | WO |
| 2013167243 | Nov 2013 | WO |
| 2013181800 | Dec 2013 | WO |
| 2016037312 | Mar 2016 | WO |
| 2016078020 | May 2016 | WO |
| Entry |
|---|
| Machine Translation of CN 104212276 (Year: 2014). |
| International Preliminary Report on Patentability; International Application No. PCT/CN2015/075462; International Filing Date Mar. 31, 2015; dated Jan. 12, 2016; 5 pages. |
| International Search Report; International Application No. PCT/CN2015/075462; International Filing Date Mar. 31, 2015; dated Jan. 12, 2016; 3 pages. |
| Written Opinion of the International Searching Authority; International Application No. PCT/CN2015/075462; International Filing Date Mar. 31, 2015; dated Jan. 12, 2016; 4 pages. |
| European Search Report for European Application No. 1886865.3 dated Oct. 10, 2018, 9 pages. |
| Article 94(3) EPC Communication from EPO dated Jul. 25, 2019. |
| Lechner, M.D. et al., “Makromolekulare Chemie”, Jan. 1, 2003, p. 237. |
| Odian, G., “Principles of Polymerization,” 4th Ed., Feb. 27, 2004, pp. 1-38. |
| Stevens; M.P., “Polymer Chemistry; An Introduction,” 3rd Ed., Dec. 31, 1999; pp. 53-57. |
| U.S. Appl. No. 14/403,695, filed Nov. 25, 2014, US2015/0148457, Pending. |
| U.S. Appl. No. 14/477,263, filed Sep. 4, 2014, US2015/0059616, U.S. Pat. No. 10,023,757. |
| U.S. Appl. No. 14/477,298, filed Sep. 4, 2014, US2015/0065618, U.S. Pat. No. 10,030,162. |
| U.S. Appl. No. 15/502,546, filed Feb. 8, 2017, US2017/0226364, U.S. Pat. No. 10,017,657. |
| U.S. Appl. No. 15/526,381, filed May 12, 2017, US2017/0335133, Pending. |
| U.S. Appl. No. 15/556,302, filed Sep. 12, 2017, US2018/0044516, Pending. |
| U.S. Appl. No. 16/014,465, filed Jun. 21, 2018, US2018/0298226, Pending. |
| International Search Report for International Application No. PCT/CN2014/091562; filed Nov. 19, 2014; dated Jun. 15, 2015; 4 pages. |
| International Search Report; International Application No. PCT/CN2014/086127; filed Sep. 9, 2014; dated Apr. 27, 2015; 4 pages. |
| Written Opinion of the International Searching Authority for International Application No. PCT/CN2014/091562; filed Nov. 19, 2014; dated Jun. 15, 2015; 4 pages. |
| Written Opinion of the International Searching Authority; International Application No. PCT/CN2017/086127; filed Sep. 9, 2014; dated Apr. 27, 2015; 3 pages. |
| Chang et al.; “Effects of mixed hydrocolloids on water-based multicolor coatings”; J. of Beijing Univ, of Chem. Tech.; vol. 37; No. 4; (2010) 5 pages with English Abstract. |
| Thielking et al.; “Cellulose Ethers”; Ullmann's Encyclopedia of Industrial Chemistry; vol. 7; 2006; pp. 381-397. |
| CN Search Report, CN Application No. 201580078125.9, dated Oct. 31, 2019. |
| Huang et al., “Fine Chemical Formula Commonly Used Raw Materials Manual”, Guangdong Science and Technology Press, 1st Ed., Mar. 31, 1998, pp. 1102-1104, English Translation provided on Jan. 9, 2020 (NPL). |
| Wang Duoren, Ed., “Green Water Treatment Agent,” Science and Technology Literature Publishing House, 1st Ed., Nov. 30, 2006, p. 51, English Translation provided on Jan. 9, 2020 (NPL). |
| Number | Date | Country | |
|---|---|---|---|
| 20180044516 A1 | Feb 2018 | US |