Aspects of the present disclosure relate generally to cables, such as fiber optic cables that may support and carry optical fibers as well as other cable components. More specifically, aspects of the present disclosure relate to a binder film for constraining elements of a cable, such as buffer tubes wound around a central strength member in a core of a fiber optic cable.
Loose tube fiber optic cables typically use crisscrossing binder yarns that are counter-helically wrapped about a core of the cable to constrain stranded buffer tubes containing optical fibers, particularly with arrangements of the buffer tubes that include reverse-oscillatory winding patterns of the buffer tubes where the lay direction of the buffer tubes periodically reverses around a (straight) central strength member along the length of the core. The central strength member is typically a rod of a rigid material. Buffer tubes are typically cylindrical tubes (generally 2 to 3 mm in outer diameter) that contain optical fibers. Open space in the interior of a buffer tube may be water-blocked with grease.
Applicants have found that stranded buffer tubes, particularly those stranded in a reverse-oscillating pattern, function as a loaded dual-torsion spring with bias to unwind and correspondingly stretch out along the length of the cable. The binder yarns constrain the buffer tubes in the reversals. However, use of binder yarns may limit the length of cable that can be manufactured without stopping a manufacturing line. For example, due to finite lengths of binder yarns on a bobbin, the manufacturing line may be stopped every 20 kilometers (km) to switch out bobbins. Stopping the manufacturing line and switching out components reduces efficiency. Further, binder yarns may impart distortions or stress concentrations in the stranded buffer tubes, where the binder yarns pass over the respective buffer tubes, potentially resulting in attenuation of optical fibers therein. The level of attenuation is a function of the tension in the binder yarns, which itself may be a function of the number, arrangement, structure, and materials of the buffer tubes, among other variables. Application of binder yarns may accordingly limit the speed of a stranding machine, depending upon allowable binder-yarn tension. A need exists for a binder system that allows for faster manufacturing of cables, reduces potential for attenuation of optical fibers in the cables (such as by avoiding point loading of buffer tubes), and/or allows for long, continuous lengths of such cables to be efficiently manufactured.
To this end, Applicants have experimented with manufacturing stranded cable cores without binder yarns. In one experiment, Applicants attempted to extrude a thin film over a core of stranded buffer tubes with binder yarns removed. The buffer tubes had previously conformed to the stranding pattern about the core and the pattern remained when the binder yarns were removed. However, a “bird cage” (also called “bird nest”) or jumble of stranded buffer tubes appeared upon extruding the thin film, which became more and more pronounced until the manufacturing line had to be stopped. Applicants theorize that the buffer tubes migrated axially forcing them outward and away from the central strength member when the binder yarns were removed. The jacket did not cool (and constrict) fast enough, with the stranded buffer tubes held down, to sufficiently couple the stranded buffer tubes to the central strength member of the cable. Instead, the buffer tubes shifted axially due to release of spring forces and pull of the extrusion cone, creating the “bird's cage.”
In another experiment, Applicants circumferentially taped only the reversal points of the stranded buffer tubes and to then extruded a jacket over the taped stranded buffer tubes. However, with this experiment a “bird cage” formed, resulting in bulges in the cable just prior to each reversal point of the stranded buffer tubes along the length of the cable. Applicants theorize that the stranded buffer tubes shifted axially between reversals. Release of spring forces in the stranded buffer tubes lifted the buffer tubes away from the central strength member. Axial loading (pulling) on the stranded elements by the extrusion cone then moved the buffer tubes axially, where excess length built up until coupling occurred with the tape. In view of the experimentation, a need exists for a binder system that overcomes some or all of the drawbacks associated with binder yarns, while limiting and/or controlling the impact of unwinding, outward- and axial-migration of the buffer tubes due spring forces in stranded buffer tubes and axial forces from extrusion.
One embodiment relates to a fiber optic cable, which includes a core and a binder film surrounding the core. The core includes a central strength member and core elements, such as buffer tubes containing optical fibers, where the core elements are stranded around the central strength member in a pattern of stranding including reversals in lay direction of the core elements. The binder film is in radial tension around the core such that the binder film opposes outwardly transverse deflection of the core elements. Further, the binder film loads the core elements normally to the central strength member such that contact between the core elements and central strength member provides coupling therebetween, limiting axial migration of the core elements relative to the central strength member.
Another embodiment relates to a fiber optic cable, which includes a core of the cable having at least one optical fiber, a binder film surrounding the core, and powder particles. The binder film is in tension around the core. The powder particles are water-absorbing powder particles that include a super-absorbent polymer. At least some of the powder particles are attached to the binder film.
Yet another embodiment relates to a method of manufacturing a fiber optic cable, which includes a step of stranding core elements around a central strength member in a pattern of stranding including reversals in lay direction of the core elements. The core elements include a buffer tube surrounding at least one optical fiber, and one or more additional core elements. The one or more additional core elements include at least one of a filler rod and an additional buffer tube. The method includes a step of extruding a binder film to surround the core elements immediately after stranding the core elements, within a distance of at least ten lay lengths of the strand from the closing point where the core elements come together in the pattern of stranding of the core. The method may further include a step of constraining the stranded core elements while the binder film contracts and cools, thereby allowing the binder film to load the stranded core elements against the central strength member to arrest axial migration of the stranded core elements during manufacturing of the cable.
In accordance with yet other aspects of the present disclosure, a fiber optic cable comprises a cable core of core elements and a protective sheath surrounding the core elements. The protective sheath is continuous peripherally around the core elements, forming a continuous closed loop when viewed in cross-section, and continuous lengthwise along a length of the cable. The cable core is devoid of any ripcords. An armor surrounds the cable core, the armor comprising a single overlap portion when the fiber optic cable is viewed in cross-section, and a jacket surrounds the armor, the jacket having at least two longitudinal discontinuities extruded therein.
In accordance with yet other aspects of the present disclosure, a method of accessing core elements of a fiber optic cable without the use of ripcords includes making a ring cut of the jacket at a mid-span location and making a longitudinal cut in the jacket where at least one of the two longitudinal discontinuities are located, the longitudinal cut orthogonally intersecting the ring cut. The method also includes grasping the jacket at the intersection of the longitudinal cut and the ring cut and peeling back the jacket so that the jacket separates along the discontinuities a predetermined length and removing the predetermined length of jacket peeled back from the core to expose the armor and define an access section. The method further includes scoring the armor near an end of the access section to remove a small section of the armor and expose the cable core, and removing a remaining portion of the armor in the access section by pulling the armor away from the cable core so that the overlap portion separates around the cable core as it is being pulled past the cable core.
Additional features and advantages are set forth in the Detailed Description that follows, and in part will be readily apparent to those skilled in the art from the description or recognized by practicing the embodiments as described in the written description and claims hereof, as well as the appended drawings. It is to be understood that both the foregoing general description and the following Detailed Description are merely exemplary, and are intended to provide an overview or framework to understand the nature and character of the claims.
The accompanying Figures are included to provide a further understanding, and are incorporated in and constitute a part of this specification. The drawings illustrate one or more embodiments, and together with the Detailed Description serve to explain principles and operations of the various embodiments. As such, the disclosure will become more fully understood from the following Detailed Description, taken in conjunction with the accompanying Figures, in which:
Before turning to the following Detailed Description and Figures, which illustrate exemplary embodiments in detail, it should be understood that the present inventive technology is not limited to the details or methodology set forth in the Detailed Description or illustrated in the Figures. For example, as will be understood by those of ordinary skill in the art, features and attributes associated with embodiments shown in one of the Figures or described in the text relating to one of the embodiments may well be applied to other embodiments shown in another of the Figures and/or described elsewhere in the text.
Referring to
In some embodiments, the core elements 114 include a tube 116, such as a buffer tube surrounding at least one optical fiber 118, a tight-buffer surrounding an optical fiber, or other tube. According to an exemplary embodiment, the tube 116 may contain two, four, six, twelve, twenty-four or other numbers of optical fibers 118. In contemplated embodiments, the core elements 114 additionally or alternatively include a tube 116 in the form of a dielectric insulator surrounding a conductive wire or wires, such as for a hybrid cable.
In some embodiments, the tube 116 further includes a water-blocking element, such as gel (e.g., grease, petroleum-based gel) or an absorbent polymer (e.g., super-absorbent polymer particles or powder). In some such embodiments, the tube 116 includes yarn 120 carrying (e.g., impregnated with) super-absorbent polymer, such as at least one water-blocking yarn 120, at least two such yarns, or at least four such yarns per tube 116. In other contemplated embodiments, the tube 116 includes super-absorbent polymer without a separate carrier, such as where the super-absorbent polymer is loose or attached to interior walls of the tube. In some such embodiments, particles of super-absorbent polymer are partially embedded in walls of the tube 116 (interior and/or exterior walls of the tube) or bonded thereto with an adhesive. For example, the particles of super-absorbent polymer may be pneumatically sprayed onto the tube 116 walls during extrusion of the tube 116 and embedded in the tube 116 while the tube 116 is tacky, such as from extrusion processes.
According to an exemplary embodiment, the optical fiber 118 of the tube 116 is a glass optical fiber, having a fiber optic core surrounded by a cladding (shown as a circle surrounding a dot in
According to an exemplary embodiment, the core 112 of the cable 110 includes a plurality of additional core elements (e.g., elongate elements extending lengthwise through the cable 110), in addition to the tube 116, such as at least three additional core elements, at least five additional core elements. According to an exemplary embodiment, the plurality of additional core elements includes at least one of a filler rod 122 and/or an additional tube 116′. In other contemplated embodiments, the core elements 114 may also or alternatively include straight or stranded conductive wires (e.g., copper or aluminum wires) or other elements. In some embodiments, the core elements are all about the same size and cross-sectional shape (see
Referring now to
According to an exemplary embodiment, the binder film 126 includes (e.g., is formed from, is formed primarily from, has some amount of) a polymeric material such as polyethylene (e.g., low-density polyethylene, medium density polyethylene, high-density polyethylene), polypropylene, polyurethane, or other polymers. In some embodiments, the binder film 126 includes at least 70% by weight polyethylene, and may further include stabilizers, nucleation initiators, fillers, fire-retardant additives, reinforcement elements (e.g., chopped fiberglass fibers), and/or combinations of some or all such additional components or other components.
According to an exemplary embodiment, the binder film 126 is formed from a material having a Young's modulus of 3 gigapascals (GPa) or less, thereby providing a relatively high elasticity or springiness to the binder film 126 so that the binder film 126 may conform to the shape of the core elements 114 and not overly distort the core elements 114, thereby reducing the likelihood of attenuation of optical fibers 118 corresponding to the core elements 114. In other embodiments, the binder film 126 is formed from a material having a Young's modulus of 5 GPa or less, 2 GPa or less, or a different elasticity, which may not be relatively high.
According to an exemplary embodiment, the binder film 126 is thin, such as 0.5 mm or less in thickness (e.g., about 20 mil or less in thickness, where “mil” is 1/1000th inch). In some such embodiments, the film is 0.2 mm or less (e.g., about 8 mil or less), such as greater than 0.05 mm and/or less than 0.15 mm. In some embodiments, the binder film 126 is in a range of 0.4 to 6 mil in thickness, or another thickness. In contemplated embodiments, the film may be greater than 0.5 mm and/or less than 1.0 mm in thickness. In some cases, for example, the binder film 126 has roughly the thickness of a typical garbage bag. The thickness of the binder film 126 may be less than a tenth the maximum cross-sectional dimension of the cable, such as less than a twentieth, less than a fiftieth, less than a hundredth, while in other embodiments the binder film 126 may be otherwise sized relative to the cable cross-section. In some embodiments, when comparing average cross-sectional thicknesses, the jacket 134 is thicker than the binder film 126, such as at least twice as thick as the binder film 126, at least ten times as thick as the binder film 126, at least twenty times as thick as the binder film 126. In other contemplated embodiments, the jacket 134 may be thinner than the binder film 126, such as with a 0.4 mm nylon skin-layer jacket extruded over a 0.5 mm binder film.
The thickness of the binder film 126 may not be uniform around the bound stranded elements 114. Applicants have found some migration of the material of the binder film 126 during manufacturing. For example, the belts 322 (e.g., treads, tracks) of the caterpuller 320 shown in
Use of a relatively thin binder film 126 allows for rapid cooling (e.g., on the order of milliseconds, as further discussed with regard to the process 310 shown in
Still referring to
According to an exemplary embodiment, powder particles 132, such as super-absorbent polymer and/or another powder (e.g., talc), or another water-absorbing component (e.g., water-blocking tape, water-blocking yarns) are attached to the outer surface of the central strength member 124. At least some of the powder particles 132 may be partially embedded in the up-jacket 130, and attached thereto by pneumatically spraying the particles 132 against the up-jacket 130 while the up-jacket 130 is in a tacky and/or softened state. The powder particles 132 may increase or otherwise affect coupling between the central strength member 124 and the core elements 114 around the central strength member 124.
Alternatively or in addition thereto, the particles 132 may be attached to the up-jacket 130 with an adhesive. In some embodiments, the central strength member 124 includes the rod 128 without an up-jacket, and the particles 132 may be attached to the rod 128. In contemplated embodiments, a strength member, such as a glass-reinforced rod or up-jacketed steel rod, includes super-absorbent polymer or other particles 132 attached to the outer surface thereof, as disclosed above, without the strength member being a central strength member.
In some embodiments, the core elements 114 are stranded (i.e., wound) about the central strength member 124. The core elements 114 may be stranded in a repeating reverse-oscillatory pattern, such as so-called S-Z stranding (see generally
In other contemplated embodiments, the core elements 114 are non-stranded. In some such embodiments, the core elements 114 include micro-modules or tight-buffered optical fibers that are oriented generally in parallel with one another inside the binder film 126. For example, harness cables and/or interconnect cables may include a plurality of micro-modules, each including optical fibers and tensile yarn (e.g., aramid), where the micro-modules are bound together by the binder film 126 (see generally
Referring now to
In some embodiments, at least some of the powder particles 136 are coupled directly or indirectly to the binder film 126 (e.g., attached bound directly thereto, adhered thereto, in contact therewith), such as coupled to a surface of the binder film 126, coupled to an exterior surface of the binder film 126, coupled to an outside surface of the binder film 126 and/or an inside surface of the binder film 126. According to an exemplary embodiment, at least some of the powder particles 136 are partially embedded in the binder film 126, such as passing partly through a surrounding surface plane of the binder film 126 while partially projecting away from the surface of the binder film 126; or, put another way, having a portion thereof submerged in the binder film 126 and another portion thereof exposed. In some embodiments, a rotating die may be used to increase normal force on the tubes.
The powder particles 136 may be attached to the binder film 126 by pneumatically spraying the powder particles onto the binder film 126, into and outside of the associated extrusion cone (see also
According to an exemplary embodiment, the powder particles 132, 136 include super-absorbent polymer particles, and the amount of super-absorbent polymer particles is less than 100 grams per square meter of surface area (g/m2) of the respective component to which the powder particles are coupled (central strength member 124 or binder film 126). In some such embodiments, the amount of super-absorbent polymer particles is between 20 and 60 g/m2, such as between 25 and 40 g/m2. According to an exemplary embodiment, the amount of super-absorbent polymer or other water-blocking elements used in the cable is at least sufficient to block a one-meter pressure head of tap water in a one-meter length of the cable 110, 210, according to industry standard water penetration tests, which may correspond to the above quantities, depending upon other characteristics of the respective cable 110, 210, such as interstitial spacing between core elements 114.
According to an exemplary embodiment, at least some of the powder particles 136 are positioned on an inside surface of the binder film 126 (see
Powder particles 136 positioned on the outside surface of the binder film 126 may provide water blocking between the binder film 126 and components of the cable 210 exterior thereto, such as metal or dielectric armor 138 (
According to an exemplary embodiment, embedded material discontinuities 140 (
In some embodiments, the jacket 134 and binder film 126 may blend together during extrusion of the jacket 134 over the binder film 126, particularly if the jacket 134 and the binder film 126 are formed from the same material without powder particles 136 therebetween. In other embodiments, the jacket 134 and the binder film 126 may remain separated or at least partially separated from one another such that each is visually distinguishable when the cable 110, 210 is viewed in cross-section. In some embodiments, the binder film 126 and the jacket 134 are not colored the same as one another. For example, they may be colored with visually distinguishable colors, having a difference in “value” in the Munsell scale of at least 3. For example, the jacket 134 may be black while binder film 126 may be white or yellow, but both including (e.g., primarily consisting of, consisting of at least 70% by weight) polyethylene.
In accordance with yet other aspects of the present disclosure,
As shown in
In various embodiments, armor layer 138 may be formed from a variety of strengthening or damage resistant materials. In the embodiment shown in
In accordance with aspects of the present invention, the binder film 126 surrounds and binds together the core elements 114. The binder film 126 forms a protective sheath that protects the buffer tubes 116 and other core elements 114, for example, during a mid-span access procedure as described infra (see
In some contemplated embodiments, the jacket 134 is opaque, such as colored black and/or including ultra-violet light blocking additives, such as carbon-black; but the binder film 126 is translucent and/or a “natural”-colored polymer, without added color, such that less than 95% of visible light is reflected or absorbed by the binder film 126. Accordingly, in at least some such embodiments, upon opening or peeling back the jacket 134 away from the binder film 126 and core 112, the tube 116 and at least some of the plurality of additional core elements 114 are at least partially visible through the binder film 126 while being constrained thereby with the binder film 126 unopened and intact, such as visible upon directing light from a 25 watt white light-bulb with a 20-degree beam directly on the binder film 126 from a distance of one meter or less in an otherwise unlit room. In contemplated embodiments, the core includes a tape or string (e.g., polymeric ripcord), beneath the binder film 126 and visible through the binder film 126, which may include indicia as to contents of the core 112 or a particular location along the length of the cable 110.
According to an exemplary embodiment, the binder film 126 is continuous peripherally around the core, forming a continuous closed loop (e.g., closed tube) when viewed from the cross-section, as shown in
In some embodiments, around the cross-sectional periphery of the binder film 126, the binder film 126 takes the shape of adjoining core elements 114 and extends in generally straight paths over interstices 144 (
In some embodiments, the binder film 126 arcs into the interstices 144 (
Use of a continuous binder film 126 may block water from being able to reach the core 112. In other embodiments, the binder film 126 includes pinholes or other openings. In some contemplated embodiments, binder films may be extruded in a criss-crossing net mesh pattern of film strips, or as a helical or counter-helical binder film strip(s), such as via rotating cross-heads or spinnerets. Either the core or the cross-head may be rotated, and the core may be rotated at a different rate than the cross-head, or vice versa. In other contemplated embodiments, a pre-formed curled or C-shaped tube may be used as the binder 126, where the core 112 is bound thereby.
Referring once more to
In some embodiments, the tension T of the binder film 126 has a distributed loading of at least 5 newtons (N) per meter (m) length of the cable 110, 210, which may be measured by measuring the average diameter of an intact binder film 126 surrounding the core elements 114, then opening the binder film 126, removing the core elements 114, allowing time for the binder film 126 to contract to an unstressed state (e.g., at least a day, depending upon material) at constant temperature, then measuring the decrease in binder film 126 widthwise dimension (i.e., compared to the average periphery). The tension T is the loading required to stretch the binder film 126 to the original width.
Referring now to
An industry-standard definition for the lay length of helically stranded elements (e.g., helical lay length) is the lengthwise distance along the cable (and along a central strength member, if present) for a full turn of the stranded elements about the lengthwise axis of the cable (e.g., the length through the center of a single helical spiral). An industry-standard definition for the lay length of reverse-oscillatory stranded elements, such as SZ stranded elements, is the lengthwise distance between reversal points of the strand divided by the sum of turns of the stranded elements (such as turns about a central strength member) between the reversal points, which may include a fraction of a turn; akin to the “average” helical lay length.
In the space 316 and outside the extrudate cone of the binder film 126, powder particles 136 (see
Air flows carrying the powder particles 136 may synergistically be used to hasten cooling of the binder film 126, and may still further be used to shape or thin-out the binder film 126. Additional flows of cooling fluid 318 (e.g., dry air if associated binder film 126 surface(s) are with super-absorbent polymer particles; fine water mist or water bath, if surfaces are without super-absorbent polymer particles) may be used to further hasten cooling of the binder film 126 so that the binder film 126 will be sufficiently cooled and solidified in order to constrain the core elements 114 within fractions of a second after stranding of the core elements 114. Furthermore, air flows carrying the powder particles 136 may be coordinated on opposite sides of the binder film to control shaping of the binder film 126 and/or prevent distortion of the binder film 126. Adherence of the particles 136 to the binder film 126 may assist containing the particles 136 during cable end- and mid-span access.
In some embodiments, the binder film 126 is continuous and watertight, which may prevent the powder particles 136 (e.g., super-absorbent polymer particles) in the interior of the binder film 126 from absorbing moisture or water on the exterior of the binder film 126. To prevent axial migration of water along the exterior of the binder film 126, between the binder film 126 and additional cabling layers—such as metallic armor, nonmetallic armor, additional strength elements, and/or an additional exterior jacket over the cable core; the powder particles 136 may be applied to the exterior of the binder film 126 while the binder film 126 is still molten and immediately prior to receipt of the cable 110, 210 by an anti-torsion caterpuller 320. The caterpuller 320 may be particularly useful for reverse-oscillatory stranding patterns, such as so-called “SZ” strands, because the caterpuller 320 holds down and constrains the reversal. As such, the caterpuller is preferably positioned within a distance of at least one lay length of the strand from the closing point of the core elements 114, where the core elements 114 come together at the trailing end of the stranding machine in the pattern of stranding of the core 112. The extrusion head 414 and extrudate cone (see
Particularly in stranding arrangements of core elements 114 that include reverse-oscillatory winding patterns (e.g., S-Z stranding), the anti-torsion caterpuller 320 may serve to apply an opposing torque to torque induced by tension and rotation of the core elements 114. Belts 322 of the anti-torsion caterpuller 320 may be coupled together so that the belts 322 register on the centerline of the cable 110, 210, which permits automatic adjustment of the spacing of the belts for different cable diameters. According to an exemplary embodiment, the caterpuller 320 is located within 100 mm of the release point of the oscillating nose piece 312 or the closing point of the core elements 114, where the core elements 114 come together, such as to contact one another and/or a central strength member (see, e.g., central strength member 124 as shown in
According to an exemplary embodiment, the binder film 126 maintains the integrity of the core 112 during subsequent processing steps, which may include tight bends of the cable 110, 210 and/or applications of additional cable components. In some embodiments, the binder film 126 has the additional advantageous feature of removal by initiating a tear (see
Still referring to
Such a manufacturing process 310 may remove a need for some or all binder yarns and water-blocking tape, described in the Background, and replace such components with a continuously-extruded binder film 126 that may have super-absorbent polymer particles 136 embedded in the interior surface of the binder film 126 and/or on the exterior surface of the binder film 126. In addition, the binder film 126 may constrain the reversal of stranded core elements 114 in the radial direction. Rip cords 142, material discontinuities 140, or other access features may be integrated with the cable 110, 210, such as being located outside of, in, or underneath the binder film 126 for either armored-type cable (see generally
Referring again to
As shown in
Use of a binder film 126, as disclosed herein, may permit continuous or near-continuous cable 110, 210 production, may eliminate binder yarn indentations on core elements 114, may remove cable binding as a production speed constraint, may permit stranding to be speed matched with jacketing, may contribute to the strength of the jacket 134, may replace water-blocking tape, may eliminate the associated tape inventory and the tape-width inventory subset, may allow access by ripcord 142 to the core elements 114 (where binder yarns generally cannot be cut by the ripcord, as discussed), may provide significant cost savings in materials, and/or may allow for removal of water-blocking yarn wrapped around the central strength member in some conventional cables.
In alternate contemplated embodiments of the above-disclosed cables 110, 210 and manufacturing methods 310 and equipment, a capstan may be used in place of the caterpuller 320. In some embodiments, water-absorbent powder 136 may not be applied to the exterior of the binder film 126, and a water bath may be used to increase the cooling rate. Further, the caterpuller 320 or at least a portion thereof may be submerged in the water bath. In some embodiments, water-absorbent powder 136 may not be applied to the interior surface of the binder film 126, or to either the interior or the exterior surfaces of the binder film 126. Thermoplastics and/or materials other than polyethylene may be used to form the binder film 126. The binder film 126 may be of various colors, and may have UV stabilizers that permit the binder film 126 as the exterior of a finished outdoor product. The binder film 126 may be printed upon. The binder film 126 may include tear features 140, such as those as disclosed herein with regard to the jacket 134. In some embodiments, the binder film 126 may surround a broad range of different types of stranded cable components, such as S-Z stranded tight-buffered fibers, filler rods, fiberglass yarns, aramid yarns, and other components.
Referring to
Referring now to
According to an exemplary embodiment, the material of the binder film 126 may be selected such that the melting temperature of the material of the binder film 126 is less (e.g., at least 30° C. less, at least 50° C. less) than the extrusion temperature (e.g., about 200-230° C.±20° C.) of a jacket 134 (see
Further, Applicants have found that application of the binder film 126 at extrusion temperatures above the melting temperature of the stranded elements 114 (e.g., at least 30° C. above, at least 50° C. above) does not melt or substantially deform the stranded elements 114. As such, the binder film 126 may include the same or similarly-melting polymers as buffer tubes 116, 116′ stranded in the core 112, such as polypropylene. Further, Applicants have found very little or no sticking between the binder film 126 and buffer tubes 116, 116′ stranded in the core 112, presumably due to the rapid cooling techniques disclosed herein, such as actively directing a flow of cooling air, caterpuller 320 in a water bath, thin film layer, binder film material selected for solidification/crystallization temperatures of the binder film 126 close to the extrusion temperature, and/or other techniques.
Further, the graphical representation in
From a different perspective, the effectiveness of a material for the binder film 126 may be related to temperature of crystallization, at which crystals start growing and therefore mechanical properties start developing. It is Applicants' understanding that the temperature of crystallization is around 140° C. for nucleated polypropylene (e.g., N05U-00), while the temperature of crystallization is at a lower temperature for high-density polyethylene (e.g., 7590), such as less than 125° C. Applicants theorize that materials that crystallize at higher temperatures will lock down faster and may work better for binder film 126 applications as disclosed herein (i.e. such materials apply more radial force to the core 112 earlier).
Further, it is Applicants' understanding that, to some degree, draw-down of the materials continues until the glass-transition temperature is reached. In the case of polypropylene, glass-transition temperature may be reached about −10° C. and for polyethylene −70° C. (but may be as high as −30° C.). Accordingly, such low temperatures will not likely be reached in processing/manufacturing, so the binder film 126 may actively continue to shrink post-processing (until glass-transition temperatures are reached), which may further improve coupling between the stranded elements 114 and the central strength member 124. For other possible binder film materials, such as polybutylene terephthalate, with a glass-transition temperature of about 50° C., the normal force applied to the stranded elements may be less because the binder film 126 may stop actively shrinking or having a bias to shrink.
Further, Applicants have found that the greater strength of polypropylene relative to polyethylene allows the binder film 126 to be thinner for a polypropylene binder film 126 to provide the same amount of coupling force between the stranded elements 114 and the central strength member 124. For example, a 0.15 mm binder film 126 of polyethylene was found to have about a 70 N radial force, while a 0.15 mm binder film 126 of polypropylene had about an 85 N radial force. However, polyethylene is typically considerably less expensive than polypropylene, and in other embodiments, polyethylene may be used for the binder film 126.
In some embodiments, the binder film 126 is formed from a first material and the jacket 134 is formed from a second material. The second material of the jacket 134 may include, such as primarily include (>50% by weight), a first polymer such as polyethylene or polyvinyl chloride; and the first material of the binder film 126 may include, such as primarily include, a second polymer, such as polypropylene. In some embodiments, the first material further includes the first polymer (e.g., at least 2% by weight of the first material, at least 5% by weight, at least 10% by weight, and/or less than 50% by weight, such as less than 30% by weight). Inclusion of the first polymer in the first material of the binder film 126, in addition to primarily including the second polymer in the first material, may facilitate bonding between the first and second materials so that the binder film 126 may be coupled to the jacket 134 and automatically removed from the core 112 when the jacket 134 is removed from the core 112, such as at a mid-span access location.
As shown in
Via pull-through testing, Applicants have found that the magnitude of the static friction force is related to the thickness of the binder film 126. For a polypropylene binder film 126 of at least 0.02 mm but less than 0.04 mm in average wall thickness, the static friction force for a 100 mm section of stranded elements 114 (without a jacket) is at least 10 N, such as about 12.4 N, and/or the average static friction force for a 200 mm section of stranded elements 114 is at least 20 N, such as about 23.1 N. Accordingly, for such a binder film 126, the reverse-oscillatory stranding pattern must be such that the net spring force of the stranded elements 114 is about 10 N or less for a 100 mm section to prevent axial migration of the stranded elements 114 and formation of a “bird cage” during manufacturing. Applicants have also found, for a polypropylene binder film 126 of at least 0.08 mm but less than 0.15 mm in average wall thickness, the average static friction force for a 100 mm section of stranded elements is at least 20 N, such at least 30 N, and/or the average static friction force for a 200 mm section of stranded elements is at least 40 N, such as at least 50 N. Some testing included stranded elements bound by both binder film 126 and binders yarns to determine the contribution of the binder film 126.
Referring to
The lengthwise incision 726 provides an opening through which the stranded elements 718 can be unwound at a reversal 714 to provide extra length for handing the stranded elements 718, and one or more of the elements 718 may be tapped at the mid-span location. For example,
As mentioned above, the material of the binder film 716 may be selected so that the binder film 716 is at least partially translucent, as shown in
In accordance with yet other aspects of the present invention, a mid-span access procedure for an armored cable, such as cable 210 shown in
As shown in
As shown in
As shown in
As shown in
The construction and arrangements of the cables, as shown in the various exemplary embodiments, are illustrative only. Although only a few embodiments have been described in detail in this disclosure, many modifications are possible (e.g., variations in sizes, dimensions, structures, shapes, and proportions of the various elements, values of parameters, mounting arrangements, use of materials, colors, orientations) without materially departing from the novel teachings and advantages of the subject matter described herein. For example, in some embodiments, cables include multiple layers or levels of core elements stranded around a central strength member 124, where each layer includes a binder film 126 constraining the respective layer and where binder film 126 of the outer layer(s) indirectly surrounds the binder film 126 of the inner layer(s). In contemplated embodiments, the binder film 126 is not extruded, but is formed from laser-welded tape and/or a heat shrink material, for example. Some elements shown as integrally formed may be constructed of multiple parts or elements, the position of elements may be reversed or otherwise varied, and the nature or number of discrete elements or positions may be altered or varied. In some contemplated embodiments, the binder film 126 with water-blocking powder, as disclosed herein, may function as an extruded water-blocking element, thereby allowing for continuous cable manufacturing without replacing reels of the water-blocking tape; which, for example, may block water between armor (or other outer layers in a cable 210) and a core 112, such as a core of stacked fiber optic ribbons or a mono-tube core, or between other components in a cable. The order or sequence of any process, logical algorithm, or method steps may be varied or re-sequenced according to alternative embodiments. Other substitutions, modifications, changes and omissions may also be made in the design, operating conditions and arrangement of the various exemplary embodiments without departing from the scope of the present inventive technology.
This application is a continuation-in-part of U.S. application Ser. No. 14/430,399 filed Mar. 23, 2015, which is a national stage application of International Application No. PCT/US2013/061133 filed Sep. 23, 2013, which claims priority to U.S. application Ser. No. 13/790,329 filed Mar. 8, 2013 and U.S. Application No. 61/705,769 filed on Sep. 26, 2012, the content of each of which is relied upon and incorporated herein by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4312566 | Jackson | Jan 1982 | A |
| 4496214 | Oestreich et al. | Jan 1985 | A |
| 4515435 | Anderson | May 1985 | A |
| 4535098 | Evani et al. | Aug 1985 | A |
| 4645298 | Gartside, III et al. | Feb 1987 | A |
| 4723831 | Johnson et al. | Feb 1988 | A |
| 4730894 | Arroyo | Mar 1988 | A |
| 4767184 | Ogasawara et al. | Aug 1988 | A |
| 4796970 | Reeve et al. | Jan 1989 | A |
| 4930860 | Tansey | Jun 1990 | A |
| 4973611 | Puder | Nov 1990 | A |
| 4993804 | Mayr et al. | Feb 1991 | A |
| 5155789 | Le Noane et al. | Oct 1992 | A |
| 5157752 | Greveling et al. | Oct 1992 | A |
| 5173961 | Chiasson | Dec 1992 | A |
| 5179611 | Umeda et al. | Jan 1993 | A |
| 5233678 | Katurashima et al. | Aug 1993 | A |
| 5240532 | Yu | Aug 1993 | A |
| 5283014 | Oestreich et al. | Feb 1994 | A |
| 5388175 | Clarke | Feb 1995 | A |
| 5440660 | Dombrowski et al. | Aug 1995 | A |
| 5671312 | Jamet | Sep 1997 | A |
| 5684904 | Bringuier et al. | Nov 1997 | A |
| 5703983 | Beasley, Jr. | Dec 1997 | A |
| 5970196 | Greveling et al. | Oct 1999 | A |
| 6101305 | Wagman et al. | Aug 2000 | A |
| 6137936 | Fitz et al. | Oct 2000 | A |
| 6185352 | Hurley | Feb 2001 | B1 |
| 6193824 | Einsle et al. | Feb 2001 | B1 |
| 6215931 | Risch et al. | Apr 2001 | B1 |
| 6314713 | Fitz et al. | Apr 2001 | B1 |
| 6304701 | Bringuier et al. | Oct 2001 | B1 |
| 6318061 | Schneider et al. | Nov 2001 | B1 |
| 6334015 | Jamet | Dec 2001 | B2 |
| 6389204 | Hurley | May 2002 | B1 |
| 6480653 | Pierre et al. | Nov 2002 | B1 |
| 6483971 | Gaillard et al. | Nov 2002 | B2 |
| 6487346 | Nothofer | Nov 2002 | B2 |
| 6546712 | Moss et al. | Apr 2003 | B2 |
| 6560390 | Grulick | May 2003 | B2 |
| 6563991 | Witt et al. | May 2003 | B1 |
| 6584251 | Ardouin | Jun 2003 | B1 |
| 6597844 | Witt et al. | Jul 2003 | B1 |
| 6603908 | Dallas et al. | Aug 2003 | B2 |
| 6658184 | Bourget et al. | Dec 2003 | B2 |
| 6721480 | Bocanegra et al. | Apr 2004 | B1 |
| 6760523 | V. Nechitailo | Jul 2004 | B2 |
| 6798958 | Bourget et al. | Sep 2004 | B2 |
| 6853781 | Chastain et al. | Feb 2005 | B2 |
| 6856748 | Elkins, II et al. | Feb 2005 | B1 |
| 6870995 | Johnson et al. | Mar 2005 | B2 |
| 6901191 | Hurley et al. | May 2005 | B2 |
| 6912347 | Rossi et al. | Jun 2005 | B2 |
| 6931190 | Ino et al. | Aug 2005 | B2 |
| 6937801 | McAlpine et al. | Aug 2005 | B2 |
| 6937802 | Jamet et al. | Aug 2005 | B2 |
| 6957000 | McAlpine et al. | Oct 2005 | B2 |
| 6973246 | Bocanegra et al. | Dec 2005 | B2 |
| 7054531 | Hurley et al. | May 2006 | B2 |
| 7082241 | Jamet et al. | Jul 2006 | B2 |
| 7123801 | Fitz | Oct 2006 | B2 |
| 7174076 | Park et al. | Feb 2007 | B2 |
| 7200307 | Bau′ et al. | Apr 2007 | B2 |
| 7212715 | Dallas et al. | May 2007 | B2 |
| 7242830 | Storaasli et al. | Jul 2007 | B2 |
| 7242831 | Fee | Jul 2007 | B2 |
| 7321709 | Yokokawa et al. | Jan 2008 | B2 |
| 7359600 | Kim et al. | Apr 2008 | B2 |
| 7373057 | Pizzorno et al. | May 2008 | B2 |
| 7382955 | Keller | Jun 2008 | B1 |
| 7391943 | Blazer et al. | Jun 2008 | B2 |
| 7431963 | Konstadinidis et al. | Oct 2008 | B2 |
| 7567741 | Abernathy et al. | Jul 2009 | B2 |
| 7570852 | Nothofer et al. | Aug 2009 | B2 |
| 7570854 | Keller et al. | Aug 2009 | B2 |
| 7630605 | Bringuier et al. | Dec 2009 | B2 |
| 7742667 | Paschal et al. | Jun 2010 | B2 |
| 7750060 | Zahora et al. | Jul 2010 | B2 |
| 7970247 | Barker | Jun 2011 | B2 |
| 7974507 | Lovie et al. | Jul 2011 | B2 |
| 7995886 | Pizzorno et al. | Aug 2011 | B2 |
| 8031997 | Overton | Oct 2011 | B2 |
| 8041167 | Overton | Oct 2011 | B2 |
| 8116604 | Bonicel et al. | Feb 2012 | B2 |
| 8118282 | Griffioen et al. | Feb 2012 | B2 |
| 8165439 | Overton | Apr 2012 | B2 |
| 8175434 | Davidson et al. | May 2012 | B2 |
| 8180190 | Bringuier et al. | May 2012 | B2 |
| 8189974 | Hashimoto et al. | May 2012 | B2 |
| 8306377 | Keller et al. | Nov 2012 | B2 |
| 8355613 | Weimann | Jan 2013 | B2 |
| 8467645 | Keller et al. | Jun 2013 | B2 |
| 8467650 | Overton et al. | Jun 2013 | B2 |
| 8494327 | Keller et al. | Jul 2013 | B2 |
| 8498509 | Tatat | Jul 2013 | B2 |
| 8798418 | Davies | Aug 2014 | B2 |
| 8805144 | McAlpine et al. | Aug 2014 | B1 |
| 8913862 | Emmerich et al. | Dec 2014 | B1 |
| 9097875 | Blazer et al. | Aug 2015 | B1 |
| 9482839 | Sandate Aguilar et al. | Nov 2016 | B2 |
| 9547147 | Bringuier et al. | Jan 2017 | B2 |
| 20030035635 | Chastain et al. | Feb 2003 | A1 |
| 20030091307 | Hurley | May 2003 | A1 |
| 20030165310 | Moon et al. | Sep 2003 | A1 |
| 20040240806 | Lail et al. | Dec 2004 | A1 |
| 20040252954 | Ginocchio et al. | Dec 2004 | A1 |
| 20050013573 | Lochkovic et al. | Jan 2005 | A1 |
| 20050031283 | Fabian et al. | Feb 2005 | A1 |
| 20050063650 | Castellani et al. | Mar 2005 | A1 |
| 20050094953 | Park | May 2005 | A1 |
| 20060045443 | Blazer | Mar 2006 | A1 |
| 20060093268 | Zimmel | May 2006 | A1 |
| 20060193575 | Greenwood et al. | Aug 2006 | A1 |
| 20080076315 | McCormack et al. | Mar 2008 | A1 |
| 20080193091 | Herbst | Aug 2008 | A1 |
| 20080273845 | Weimann | Nov 2008 | A1 |
| 20080279514 | Kundis et al. | Nov 2008 | A1 |
| 20080279515 | Bickham et al. | Nov 2008 | A1 |
| 20080298754 | Wunsch et al. | Dec 2008 | A1 |
| 20090003780 | Bringuier et al. | Jan 2009 | A1 |
| 20090032985 | Alrutz | Feb 2009 | A1 |
| 20090116797 | Stingl et al. | May 2009 | A1 |
| 20090214167 | Lookadoo et al. | Aug 2009 | A1 |
| 20090297104 | Kachmar | Dec 2009 | A1 |
| 20090317039 | Blazer | Dec 2009 | A1 |
| 20100027949 | Bringuier et al. | Feb 2010 | A1 |
| 20100067856 | Knoch et al. | Mar 2010 | A1 |
| 20100080521 | Bardroff et al. | Apr 2010 | A1 |
| 20100119202 | Overton | May 2010 | A1 |
| 20100150505 | Testu et al. | Jun 2010 | A1 |
| 20100189399 | Sillard et al. | Jul 2010 | A1 |
| 20100202741 | Ryan et al. | Aug 2010 | A1 |
| 20110091171 | Tatat et al. | Apr 2011 | A1 |
| 20110110635 | Toge et al. | May 2011 | A1 |
| 20110135816 | Burns et al. | Jun 2011 | A1 |
| 20110194825 | Parris | Aug 2011 | A1 |
| 20110268398 | Quinn et al. | Nov 2011 | A1 |
| 20120063731 | Fitz et al. | Mar 2012 | A1 |
| 20120099825 | Messer | Apr 2012 | A1 |
| 20120134634 | Keller et al. | May 2012 | A1 |
| 20120257864 | Consonni et al. | Oct 2012 | A1 |
| 20120281953 | Choi et al. | Nov 2012 | A1 |
| 20130058614 | Gimblet et al. | Mar 2013 | A1 |
| 20150110451 | Blazer et al. | Apr 2015 | A1 |
| 20160299306 | McAlpine et al. | Oct 2016 | A1 |
| 20160306128 | Chiasson et al. | Oct 2016 | A1 |
| 20160306129 | Hurley et al. | Oct 2016 | A1 |
| 20160306130 | Bringuieretal | Oct 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 102023357 | Nov 2012 | CN |
| 1531352 | Dec 2009 | EP |
| 1610163 | Oct 2011 | EP |
| 1982222 | Jun 2012 | EP |
| 2064163 | Jun 1981 | GB |
| 2096343 | Oct 1982 | GB |
| 3137607 | Jun 1991 | JP |
| 3137607 | Nov 2007 | JP |
| 2010-39018 | Feb 2010 | JP |
| 10028844 | Feb 2001 | KR |
| 99057674 | May 2001 | KR |
| 20010045604 | Jun 2001 | KR |
| 101140219 | May 2012 | KR |
| 2001021706 | Mar 2001 | WO |
| 2002099491 | Dec 2002 | WO |
| 2006034722 | Apr 2006 | WO |
| 2011137236 | Nov 2011 | WO |
| 2012071490 | May 2012 | WO |
| 2013063041 | May 2013 | WO |
| 2013130121 | Sep 2013 | WO |
| 2013172878 | Nov 2013 | WO |
| Entry |
|---|
| Hogari et al., Feb. 1998, “Optical Fiber Cables for Residential and Business Premises,” Journal of Lightwave Technology, vol. 16, No. 2, pp. 207-213. |
| Marik, J., “Advanced SZ Stranding Technology for Enhanced Applications,” 4 pages, Last accessed on Feb. 21, 2014 from http://rosendahlaustria.com/custom/rosendahlaustria /Rosendahl_Products_PDF/1062003111324_p1_.pdf. |
| Marelli et al., Nov. 11-14, 2007, “Indoor Cables for FTTH Applications, Allowing Quick and Simple Subscriber Connection,” 56th IWCS Conference: Proceedings of the International Wire & Cable Symposium (IWCS), Inc., pp. 121-127. |
| Nextrom, “SZ Stranding Line OFC 70,” 2 pages, Last accessed on Feb. 21, 2014 from http://www.nextrom.com/877_en_SZ-Stranding-Line.aspx. |
| Prysmian Cables & Systems, Oct. 5, 2005, “Glossary Excerpt from Prysmian's Wire and Cable Engineering Guide,” Revision 3, pp. 1-40, Retrieved from www.prysmian.com. |
| Rechberger, M., Hörschläger, W., “Buffering & SZ-Stranding Process for Compact Dry Tube FO-Cable,” Proceedings of the 56th Annual International Wire & Cable Symposium, 2007, pp. 614-617, Last accessed on Feb. 24, 2014 from http://ecadigitallibrary.com/pdf/IWCS07/15_5.pdf. |
| Tsumura, et al., “Development of Microduct Cable with Enhanced Mid Span Access,” Proceedings of the 54th International Wire & Cable Symposium, presented Nov. 13-16, 2005, Providence, Rhode Island, International Wire and Cable Symposium, Incorporated, 2005, pp. 426-430. |
| Non-Final Rejection for U.S. Appl. No. 13/790,329, dated Aug. 16, 2013—12 pages. |
| Non-Final Rejection Response for U.S. Appl. No. 13/790,329, dated Nov. 12, 2013—8 pages. |
| Non-Final Rejection Response for U.S. Appl. No. 13/790,329, dated Oct. 11, 2013—20 pages. |
| Non-Final Rejection Response for U.S. Appl. No. 14/091,548, dated Mar. 7, 2014—15 pages. |
| Patent Cooperation Treaty International Search Report, International Application No. PCT/US2013/061133; dated Apr. 25, 2014—7 pages. |
| Patent Cooperation Treaty International Search Report, International Application No. PCT/US2013/061133; dated Jan. 8, 2014—3 pages. |
| USPTO, Non-Final Rejection for U.S. Appl. No. 13/790,329, dated Aug. 16, 2013—12 pages. |
| USPTO, Non-Final Rejection for U.S. Appl. No. 14/091,548, dated Jan. 29, 2014—17 pages. |
| USPTO, Notice of Allowance for U.S. Appl. No. 13/790,329, dated Nov. 12, 2013—8 pages. |
| USPTO, Notice of Allowance for U.S. Appl. No. 14/091,548, dated Apr. 3, 2014—12 pages. |
| U.S. Appl. No. 13/790,329, filed Mar. 8, 2013, Bradley J. Blazer, 48 pages. |
| U.S. Appl. No. 61/892,534, filed Oct. 18, 2013, Bradley J. Blazer, 42 pages. |
| U.S. Appl. No. 14/099,921, filed Dec. 7, 2013, Mario Sergio Sandate Aguilar, 35 pages. |
| U.S. Appl. No. 14/136,311, filed Dec. 20, 2013, Anne G. Bringuier, 22 pages. |
| U.S. Appl. No. 61/921,755, filed Dec. 30, 2013, David Wesley Chiasson, 42 pages. |
| U.S. Appl. No. 61/921,763, filed Dec. 30, 2013, William Carl Hurley, 45 pages. |
| U.S. Appl. No. 61/921,769, filed Dec. 30, 2013, Anne G. Bringuier, 30 pages. |
| U.S. Appl. No. 61/921,777, filed Dec. 30, 2013, Warren W. McAlpine, 56 pages. |
| U.S. Appl. No. 14/192,007, filed Feb. 27, 2014, Warren W. McAlpine,18 pages. |
| U.S. Appl. No. 14/231,875, filed Apr. 1, 2014, Michael Emmerich, 38 pages. |
| CN2013800548679 Search Report dated Aug. 28, 2017; 2 Pages, Chinese Patent Office. |
| International Search Report and Written Opinion PCT/US2017/055257 dated Dec. 28, 2017. |
| Corning Cable Systems, “Outer Sheath and interlocking armor removal from Corning Cable Systems intrabuilding cables” SRP-004-094, Issue 4. Aug. 2007. |
| English Translation CN201380054867.9 Second Office Action dated Apr. 10, 2018, China Patent Office. |
| BR212015006760-9 Office Action dated Apr. 25, 2019, Brazil Patent Office, 6 Pgs (No Translation Available). |
| EP17860540.8 Office Action dated Apr. 17, 2020; 9 Pages; European Patent Office. |
| Number | Date | Country | |
|---|---|---|---|
| 20170131496 A1 | May 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61705769 | Sep 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/US2013/061133 | Sep 2013 | US |
| Child | 14430399 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14430399 | Mar 2015 | US |
| Child | 15289943 | US |