Patent Application
20210084897
The present disclosure relates to the field of antibacterial materials, in particular to a bio-based polymer material with antibacterial effect and its use in preparing antibacterial materials.
There are a large number of microorganisms such as bacteria, fungi, and viruses in the environment where people live. When they multiply under certain conditions, they will not only cause discoloration, mold, and degradation of materials, but also threaten human health. With the improvement of living standards, people have higher and higher requirements for the quality of the living environment and sanitary conditions. Therefore, the research and development of antibacterial agents and antibacterial materials has extremely important significance.
Antibacterial agents are mainly classed into three types: inorganic antibacterial agents, organic antibacterial agents and natural antibacterial agents. The antibacterial active ingredients used in inorganic antibacterial agents mainly include metal ions such as silver and zinc and metal salt compounds, which have the advantages of good heat resistance, antibacterial durability, and no drug resistance, but their chemical properties are active and unstable and expensive. Organic antibacterial agents refer to an antibacterial agent that uses organic acids, quaternary ammonium salts, benzimidazoles and other organic substances as antibacterial active substances. They have broad antibacterial spectrum, but their antibacterial duration is short, chemical stability is poor, and microorganisms are easy to produce chemical resistance, especially they have poor heat resistance, which limit the application range. Natural antibacterial agents are derived from plants, animals or microorganisms, and effective antibacterial materials are obtained through extraction and purification. The resources are extremely rich, and the natural antibacterial agents are safe, non-toxic and have good antibacterial effects.
Poly 3-hydroxybutyrate (PHB) is a polyester produced by microorganisms. It has excellent biodegradability, biocompatibility and optical activity. It is widely used in the filed such as textiles, food packaging, surgical sutures, and tissue engineering scaffolds. In addition, PHB is resistant to ultraviolet rays and does not easily cause inflammation, Because it is produced by microbial cells, it does not contain toxic substances such as heavy metals, and is an extremely clean polymer material.
In order to expand the range of antibacterial materials, one of the objectives of the present disclosure is to provide a bio-based material with antibacterial effects.
Another object of the present disclosure is to provide the use of the bio-based material.
The bio-based material with antibacterial effect provided by the present disclosure comprises a polymer represented by formula (1) as an antibacterial active ingredient,
wherein R represents a C1-C5 alkyl, m represents an integer of 0-3, and n represents an integer of 1-20.
The inventors discovered that the polymer represented by formula (1), such as poly-3-hydroxybutyrate with a low degree of polymerization, has excellent antibacterial activity, thereby providing a novel bio-based antibacterial material.
The bio-based material with antibacterial effect provided by the present disclosure may also comprise polyethylene glycol, and a mixture of polyethylene glycol and the polymer represented by the formula (1) as an antibacterial active ingredient.
The inventors also found that: the polymer represented by formula (1), such as poly-3-hydroxybutyrate with low polymerization degree, is mixed with polyethylene glycol to form a mixture. The two materials act synergistically, and the resulting mixture also has excellent antibacterial activity, which can provide another novel bio-based antibacterial material.
In the bio-based material with antibacterial effect provided by the present disclosure, the polyethylene glycol may be all polyethylene glycol products in a fluid state, and preferably may be polyethylene glycol with a number average molecular weight of 200 to 2000.
In the bio-based material with antibacterial effect provided by the present disclosure, the mass ratio of the polymer represented by formula (1) to polyethylene glycol may be 1:10-10:1.
In the bio-based material with antibacterial effect provided by the present disclosure, the polymer represented by formula (1) and polyethylene glycol in the mixture have a certain viscosity. The mixing time and increase the mixing temperature may be appropriately increased during the mixing stage. Preferably, the preparation process may comprise: mixing the polymer represented by formula (1) and polyethylene glycol at 80-300° C. and stirring for 10 min-6 h.
In the bio-based material with antibacterial effect provided by the present disclosure, the substituent R in formula (1) may preferably be methyl, ethyl, propyl or isopropyl. In the No-based material with antibacterial effect provided by the present disclosure, in in formula (1) can preferably be expressed as 0 or 1.
In the bio-based material with antibacterial effect provided by the present disclosure, the polymer represented by formula (1) may preferably be poly-3-hydroxybutyrate with a low degree of polymerization, which may be synthesized by chemical methods or may be derived from the decomposition of PHB polymer. More preferably, it can be derived from the decomposition of PHB polymer produced by microbial fermentation, and the end groups are hydroxyl and carboxyl, respectively. The poly-3-hydroxybutyrate with a low degree of polymerization may have a degree of polymerization of 1-20, preferably 4-13.
In the bio-based material with antibacterial effect provided by the present 2.0 disclosure, in addition to the polymer represented by formula (1) or a mixture of the polymer represented by formula (1) and polyethylene glycol as an active ingredient, it can comprise any additional ingredients, additives, auxiliary substances, etc. other than the active ingredients used in the existing antibacterial materials, as long as the active ingredients can be made into any form or type of antibacterial material without affecting the antibacterial activity of the active ingredients, which is not limited in the present disclosure.
The present disclosure also provides the use of the bio-based material with antibacterial effect described in any one of the above technical solutions in preparing antibacterial materials.
The present disclosure also provides the use of the polymer represented by formula (1) or the mixture of the polymer represented by formula (1) and polyethylene glycol in the preparation of antibacterial materials,
wherein R represents a C1-C5 alkyl, m represents an integer of 0-3, and n represents an integer of 1-20.
In the use provided by the present disclosure, the polyethylene glycol may be all polyethylene glycol products in a fluid state, and preferably may be polyethylene glycol with a number average molecular weight of 200-2000.
In the use provided by the present disclosure, the mass ratio of the polymer represented by formula (1) to polyethylene glycol may be 1:10-10:1.
In the application provided by the present disclosure, the substituent R in formula (1) may preferably be methyl, ethyl, propyl or isopropyl. In the use provided by the present disclosure, m in formula (1) can be expressed as 0 or 1.
In the use provided by the present disclosure, the polymer represented by formula (1) may preferably be poly-3-hydroxybutyrate with a low degree of polymerization, which may be synthesized by chemical methods or may be derived from the decomposition of PHB polymer. More preferably, it can be derived from the decomposition of PHB polymer produced by microbial fermentation, and the end groups are hydroxyl and carboxyl, respectively. The poly-3-hydroxy/butyrate with a low degree of polymerization may have a degree of polymerization of 1-20, preferably 4-13.
In the above use, the antibacterial material can be of any form or type, as long as the active ingredient can be used in the antibacterial material without affecting the antibacterial activity of the active ingredient.
The antibacterial materials involved in the present disclosure include but are not limited to antibacterial formulations, antibacterial fabrics, sanitary products, medical materials, etc., and are especially suitable for textile, medical and health fields. For example, it can combine with or modify existing polymer textile. For another example, it can be used in antibacterial formulations, and used in preparations such as drugs and disinfectants. For another example, it can be used in medical materials, and can be used as wound covering materials, dressings, surgical sutures, and implant materials, drug carriers and other biomedical materials. The antibacterial material involved in the present disclosure can be used alone or in combination with other antibacterial formulations and antibacterial materials, and can also be used to modify or reform other antibacterial materials.
The bio-based material with antibacterial effect provided by the present disclosure has the following advantages:
(1) It has excellent, stable and long-lasting antibacterial activity, and has significant antibacterial effects against a variety of bacteria and fungi.
(2) In addition to antibacterial activity, the bio-based material of the present disclosure also has excellent properties such as biodegradability, and biocompatibility. It can be derived from bio-based products produced by microbial fermentation, with low cost, high safety, and environmental friendly.
(3) it can be made into various forms or types of antibacterial materials, and can also be used in combination with other antibacterial materials, or used to modify other materials to obtain better antibacterial formulations and antibacterial materials, which greatly enriches the types of antibacterial materials.
(4) The present disclosure does not require a complicated preparation process, and is suitable for industrial production and large-scale use.
To make the objects, technical solutions, and advantages of the present disclosure clearer, the technical solutions of the exemplary embodiments of the present disclosure will be further described below.
The chemical reagents used in the following examples are commercially available products unless otherwise specified, and the operations or instruments used in the following examples are common operations or instruments in the art unless otherwise specified.
The preparation process of poly-3-hydroxybutyrate with a low polymerization degree was as follows: 10 g of PHB masterbatch prepared by microbial method was added into 200 mL chloroform and refluxed for 24 h. Then, the mixture was added into 1 L methanol, filtered, and then the solvent was removed from the filtrate by rotary evaporation, to obtain a poly-3-hydroxybutyrate with a low degree of polymerization. An appropriate amount of poly-3-hydroxybutyrate with a low degree of polymerization was dissolved in 1:1 DCM/methanol, filtered with a 0.45 μm microporous membrane. As shown in
It can be seen from the mass spectrum of
the molecular weight of the repeating unit is 86, and n is 4-13.
The poly-3-hydroxybutyrate with a low degree of polymerization of Example 1 was mixed uniformly with PEG with a number average molecular weight of 600 in a mass ratio of 1:1, heated and stirred at 150° C. for 4 hours. Then, it was cooled to room temperature for further use.
The poly-3-hydroxybutyrate with a low degree of polymerization of Example 1 was mixed uniformly with PEG with a number average molecular weight of 600 in a mass ratio of 1:10, heated and stirred at 150° C. for 4 hours. Then, it was cooled to room temperature for further use.
The poly-3-hydroxybutyrate with a low degree of polymerization of Example 1 and the mixtures of the poly-3-hydroxybutyrate with a low degree of polymerization and PEG of Examples 2 and 3 were diluted to 20 mg/mL, with phosphate buffer. The shaking method (see the Chinese national standard GB15979-2002) was used to detect their antibacterial activity, wherein the PBS group was used as a blank control. The antibacterial performance results obtained were shown in Table 1.
Staphylococcus aureus
Pneumoniae bacteria
Candida
albicans
From the results in Table 1, it can be seen that poly-3-hydroxybutyrate with low polymerization degree had very excellent antibacterial activity against Staphylococcus aureus, and obvious antibacterial activity against Pneumoniae bacteria; while the mixture of poly-3-hydroxybutyrate with low polymerization degree and polyethylene glycol had excellent antibacterial activity against both Staphylococcus aureus and Pneumoniae bacillus. In addition, the mixture had a very significant antibacterial rate against Candida albicans and had a broad-spectrum antibacterial effect.
After placing the materials obtained in Examples 1-3 for several months, the antibacterial activity was tested according to the above method. The results were almost the same as the aforementioned test results. It can be seen that their properties were stable, and the antibacterial activity was stable and lasting.
It is not difficult to conclude that the bio-based polymer material of the present disclosure has extremely high application potential in the field of antibacterial formulations and antibacterial materials, especially as medical antibacterial materials.
Although the preferred embodiments of the present disclosure have been disclosed in order to illustrate the present disclosure, those skilled in the art should understand that various modifications, additions and replacements can be made to the present disclosure without departing from the concept and scope of the present disclosure as defined by the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201810431508.5 | May 2018 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2018/085991 | 6/15/2018 | WO | 00 |