Bioabsorbable biomedical implants

Description

BACKGROUND

The present disclosure relates to bioabsorbable stents made of polymeric materials and method of manufacturing the bioabsorbable stents.

SUMMARY OF THE DISCLOSURE

According to one aspect of the present disclosure, a biomedical implant is disclosed as including a tubular scaffold comprising a plurality of interconnected polymer struts. The interconnected polymer struts defines a plurality of deformable cells. The polymer struts have an average thickness of no more than 120 μm.

In one embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 3 months of exposure to saline in vitro. In another embodiment, the tubular scaffold maintains at least 50% of its deployed luminal cross sectional area under a pressure load of 50 mmHg upon 3 months in vivo.

In one embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 6 months of exposure to saline in vitro. In another embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 6 months in vivo.

In one embodiment, at least 80% of the polymer struts are bioabsorbed within 2 years after deployment in vivo. In another embodiment, at least 80% of the polymer struts are bioabsorbed within 1 year after deployment in vivo.

In one embodiment, the polymer struts have an average thickness of no more than 100 μm. In another embodiment, the polymer struts have an average thickness of no more than 80 μm.

In one embodiment, the polymer struts have anisotropic elastic modulus. In a refinement, the polymer struts have an average longitudinal (i.e. along the axis of the polymer struts) elastic modulus and an average lateral elastic modulus, the average longitudinal elastic modulus being greater than the average lateral elastic modulus. In a further refinement, the average longitudinal elastic modulus is at least three times the average lateral elastic modulus. In another further refinement, the average longitudinal elastic modulus is at least five times the average lateral elastic modulus. In yet another further refinement, the average longitudinal elastic modulus is at least ten times the average lateral elastic modulus.

In one embodiment, the polymer struts include polymer chains that are longitudinally (i.e. along the axis of the polymer struts) aligned. In one embodiment, the polymer struts include crystalline domains, in which the polymer chains are longitudinally aligned. In another embodiment, more than 50% of polymer chains in the polymer struts are longitudinally aligned. In another embodiment, more than 70% of the polymer chains in the polymer struts are longitudinally aligned. In another embodiment, more than 90% of the polymer chains in the polymer struts are longitudinally aligned.

In one embodiment, the polymer struts have an average deformation angle of at least 60 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 45 degrees.

In one embodiment, the polymer struts comprises a gel-spun polymer material. In a refinement, the polymer struts are not structurally reinforced with a metal material. In a further refinement, the gel-spun polymer material is selected from the group consisting of polylactides (PLA); poly(lactide-co-glycolide) (PLGA); polyanhydrides; polyorthoesters; poly(N-(2-hydroxypropyl) methacrylamide); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); poly(d-lactide) (DPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(glycolide-co-trimethylene carbonate) (PGA-TMC); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(dl-lactide-co-glycolide) (PGA-DLPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA); poly(glycolide-co-trimethylene carbonate-co-dioxanone) (PDO-PGA-TMC), poly(lactic acid-co-caprolactone) (PLACL), and mixtures or co-polymers thereof.

In one refinement, the gel-spun polymer material is PLGA. In a further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer ranging from 72:28 to 78:22. In another further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer ranging from 62:38 to 68:32. In another further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer ranging from 47:53 to 53:47. In another further refinement, the PLGA has a weight average molecular weight of about 8,000 Dalton to about 12,000 Dalton. In another further refinement, the PLGA has a weight average molecular weight of about 12,000 Dalton to about 16,000 Dalton. In another further refinement, the PLGA has a weight average molecular weight of up to about 90,000 Dalton. In another refinement, the gel-spun polymer material is PLA or LPLA. In another refinement, the gel-spun polymer material is PGA. In some embodiment, the gel spun polymer material (e.g. PLGA, LPLA, PLA, PGA) has a weight average molecular weight of at least 90,000 Dalton, and optionally at least 100,000 Dalton.

In one embodiment, the polymer struts comprises a liquid crystalline polymer material. In a refinement, the liquid crystalline polymer material is drawn from a liquid crystalline melt or solution. In another refinement, the polymer struts are not structurally reinforced with a metal material. In a further refinement, the liquid crystalline polymer material is selected from the group consisting of polylactides (PLA); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); poly(d-lactide) (DPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA), poly(lactic acid-co-caprolactone) (PLACL), and mixtures or co-polymers thereof.

In another refinement, the liquid crystalline polymer material is PLA or LPLA. In another refinement, the liquid crystalline polymer material is PGA. In some embodiment, the liquid crystalline polymer material (e.g. LPLA, PLA, PGA) has a weight average molecular weight of at least 90,000 Dalton, and optionally at least 100,000 Dalton.

In one embodiment, the polymer struts include a polymer material selected from the group consisting of polycarboxylic acids, cellulosic polymers, proteins, polypeptides, polyvinylpyrrolidone, maleic anhydride polymers, polyamides, polyvinyl alcohols, polyethylene oxides, glycosaminoglycans, polysaccharides, polyesters, aliphatic polyesters, polyurethanes, polystyrenes, copolymers, silicones, silicone containing polymers, polyalkyl siloxanes, polyorthoesters, polyanhydrides, copolymers of vinyl monomers, polycarbonates, polyethylenes, polypropytenes, polylactic acids, polylactides, polyglycolic acids, polyglycolides, polylactide-co-glycolides, polycaprolactones, poly(e-caprolactone)s, polyhydroxybutyrate valerates, polyacrylamides, polyethers, polyurethane dispersions, polyacrylates, acrylic latex dispersions, polyacrylic acid, polyalkyl methacrylates, polyalkylene-co-vinyl acetates, polyalkylenes, aliphatic polycarbonates polyhydroxyalkanoates, polytetrahalooalkylenes, poly(phosphasones), polytetrahalooalkylenes, poly(phosphasones), and mixtures, combinations, and copolymers thereof.

In one embodiment, the tubular scaffold is expandable from an undeployed diameter to a nominal diameter without affecting the structural integrity of the tubular scaffold. In a refinement, the tubular scaffold is further expandable from the nominal diameter to an over-deployed diameter without affecting the structural integrity of the tubular scaffold. In a further refinement, the over-deployed diameter is about 1.0 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.5 mm greater than the nominal diameter.

In one refinement, the tubular scaffold is expandable by an inflatable balloon positioned within the tubular scaffold. In a further refinement, the tubular scaffold has a nominal diameter of 2.25 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a nominal diameter of 2.5 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a nominal diameter of 3.0 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a nominal diameter of 3.5 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a nominal diameter of 4.0 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a nominal diameter of 4.5 mm at nominal balloon pressure.

In one refinement, the polymer struts comprise a shape-memory polymer and wherein tubular scaffold is self-expandable. In a further refinement, the tubular scaffold is self-expandable upon change in temperature. In another further refinement, the tubular scaffold is self-expandable upon change in crystallinity of the shape-memory polymer.

In one embodiment, the tubular scaffold is formed from a plurality of sinusoidal polymer fibers. In a refinement, the sinusoidal polymer fibers are interconnected at a plurality of connecting points.

In one embodiment, the tubular scaffold is formed from a single polymer fiber. In a refinement, the single polymer fiber comprises a plurality of sinusoidal sections interconnected at a plurality of connecting points.

In one embodiment, the biomedical implant further includes a pharmaceutical agent incorporated to the tubular scaffold. In a refinement, the pharmaceutical agent is a macrolide immunosuppressant. In a further refinement, the macrolide immunosuppressant is rapamycin or a derivative, a prodrug, a hydrate, an ester, a salt, a polymorph, a derivative or an analog thereof. In another further refinement, the macrolide immunosuppressant is selected from the group consisting of rapamycin, 40-O-(2-Hydroxyethyl)rapamycin, (everolimus), 40-O-Benzyl-rapamycin, 40-O-(4′-Hydroxymethyl)benzyl-rapamycin, 40-O-[4′-(1,2-Dihydroxyethyl)]benzyl-rapamycin, 40-O-Allyl-rapamycin, 40-O-[3′-(2,2-Dimethyl-1,3-dioxolan-4(S)-yl)-prop-2′-en-1′-yl]-rapamycin, (2′:E,4′S)-40-O-(4′,5′-Dihydroxypent-2′-en-1′-yl)-rapamycin, 40-O-(2-Hydroxy)ethoxycar-bonylmethyl-rapamycin, 40-O-(3-Hydroxy)propyl-rapamycin, 40-O-(6-Hydroxy)hexyl-rapamycin, 40-O-[2-(2-Hydroxy)ethoxy]ethyl-rapamycin, 40-O-[(3S)-2,2-Dimethyldioxolan-3-yl]methyl-rapamycin, 40-O-[(2S)-2,3-Dihydroxyprop-1-yl]-rapamycin, 40-O-(2-Acetoxy)ethyl-rapamycin, 40-O-(2-Nicotinoyloxy)ethyl-rapamycin, 40-O-[2-(N-Morpholino)acetoxy]ethyl-rapamycin, 40-O-(2-N-Imidazolylacetoxy)ethyl-rapamycin, 40-O-[2-(N-Methyl-N′-piperazinyl)acetoxy]ethyl-rapamycin, 39-O-Desmethyl-39,40-O,O-ethylene-rapamycin, (26R)-26-Dihydro-40-O-(2-hydroxy)ethyl-rapamycin, 28-O-Methyl-rapamycin, 40-O-(2-Aminoethyl)-rapamycin, 40-O-(2-Acetaminoethyl)-rapamycin, 40-O-(2-Nicotinamidoethyl)-rapamycin, 40-O-(2-(N-Methyl-imidazo-2′-ylcarbethoxamido)ethyl)-rapamycin, 40-O-(2-Ethoxycarbonylaminoethyl)-rapamycin, 40-O-(2-Tolylsulfonamidoethyl)-rapamycin, 40-O-[2-(4′,5′-Dicarboethoxy-1′,2′,3′-triazol-1′-yl)-ethyl]-rapamycin, 42-Epi-(tetrazolyl)rapamycin (tacrolimus), and 42-[3-hydroxy-2-(hydroxymethyl)-2-methylpropanoate]rapamycin. In one refinement, the pharmaceutical agent is rapamycin.

In one refinement, the pharmaceutical agent is impregnated in at least a portion of the tubular scaffold. In a further refinement, the pharmaceutical agent is impregnated in the polymer struts. In a further refinement, the pharmaceutical agent is evenly distributed throughout the polymer struts.

In one refinement, at least a portion of the tubular scaffold is covered with a coating comprising the pharmaceutical agent. In a further refinement, the coating further comprises a coating polymer. In a further refinement, at least 90% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, the coating polymer comprises a bioabsorbable polymer. In a further refinement, the bioabsorbable polymer is selected from the group consisting of polylactides (PLA); poly(lactide-co-glycolide) (PLGA); polyanhydrides; polyorthoesters; poly(N-(2-hydroxypropyl) methacrylamide); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(glycolide-co-trimethylene carbonate) (PGA-TMC); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(dl-lactide-co-glycolide) (PGA-DLPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA); poly(glycolide-co-trimethylene carbonate-co-dioxanone) (PDO-PGA-TMC), polyarginine, and mixtures or co-polymers thereof. In a further refinement, the biodegradable polymer is selected from the group consisting of PLGA, polyarginine, and mixtures thereof.

In one embodiment, the biomedical implant is a vascular stent. In another embodiment, the biomedical implant is a coronary artery stent. In another embodiment, the biomedical implant is a peripheral artery stent. In another embodiment, the biomedical implant is a non-vascular stent. In a refinement, the non-vascular stent is selected from esophageal stent, biliary stent, duodenal stent, colonic stent, and pancreatic stent.

According to another aspect of the present disclosure, a method of forming a gel-spun polyester fiber is provided. The method includes the steps of forming a gel composition comprising the polyester and a solvent; extruding the gel composition through one or more orifices into a stream of drying air; and allowing the solvent to evaporate in the drying air to form the polyester fiber. In a refinement, the method further includes the step of drawing the extruded polymer.

In one embodiment, the method further includes the step of cooling the polyester fiber in a liquid bath.

In one embodiment, the gel composition is extruded through a spinneret.

In one embodiment, the polyester is selected from the group consisting of polylactides (PLA); poly(lactide-co-glycolide) (PLGA); polyanhydrides; polyorthoesters; poly(N-(2-hydroxypropyl) methacrylamide); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); poly(d-lactide) (DPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(glycolide-co-trimethylene carbonate) (PGA-TMC); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(dl-lactide-co-glycolide) (PGA-DLPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA); poly(glycolide-co-trimethylene carbonate-co-dioxanone) (PDO-PGA-TMC), poly(lactic acid-co-caprolactone) (PLACL), and mixtures or co-polymers thereof. In a refinement, the polyester is PLGA. In another refinement, the polyester is PLA or LPLA.

According to another aspect of the present disclosure, a method of forming a liquid crystalline polyester fiber is provided. The method includes the steps of forming a liquid crystalline composition comprising the polyester; and extruding the liquid crystalline composition to form the polyester fiber.

In one embodiment, the polyester is in a melted state and wherein the method further comprises cooling the polyester fiber.

In one embodiment, the liquid crystalline composition further comprises a solvent and wherein the method further comprises allowing the solvent to evaporate.

In one embodiment, the polyester is selected from the group consisting of polylactides (PLA); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); poly(d-lactide) (DPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA), poly(lactic acid-co-caprolactone) (PLACL), and mixtures or co-polymers thereof. In a refinement, the polyester is PLA. In another refinement, the polyester is LPLA. In another refinement, the polyester is PGA.

In some embodiments of the disclosed method of forming a gel-spun polyester fiber and/or forming a liquid crystalline polyester fiber, the polyester fiber has anisotropic elastic modulus. In a refinement, the polyester fiber comprises substantially aligned polymer chains.

According to another aspect of the present disclosure, a method of forming a biomedical implant is disclosed. The method includes the steps of forming one or more polymer fibers comprising longitudinally aligned polymer chains; and interconnecting the polymer fibers to form a tubular scaffold, the tubular scaffold comprising a plurality of interconnected polymer struts to define a plurality of deformable cells.

In one embodiment, the tubular scaffold is form from a plurality of sinusoidal polymer fibers. In a refinement, the sinusoidal polymer fibers are interconnected at a plurality of connecting points.

In one embodiment, the one or more polymer fibers comprise gel-spun polyester. In a refinement, the polyester is selected from the group consisting of polylactides (PLA); poly(lactide-co-glycolide) (PLGA); polyanhydrides; polyorthoesters; poly(N-(2-hydroxypropyl) methacrylamide); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); poly(d-lactide) (DPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(glycolide-co-trimethylene carbonate) (PGA-TMC); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(dl-lactide-co-glycolide) (PGA-DLPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA); poly(glycolide-co-trimethylene carbonate-co-dioxanone) (PDO-PGA-TMC), poly(lactic acid-co-caprolactone) (PLACL), and mixtures or co-polymers thereof. In a further refinement, the polyester is PLGA. In another further refinement, the polyester is PLA or LPLA.

In one embodiment, the one or more polymer fibers comprise liquid crystalline polyester. In a refinement, the polyester is selected from the group consisting of polylactides (PLA); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); poly(d-lactide) (DPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA), poly(lactic acid-co-caprolactone) (PLACL), and mixtures or co-polymers thereof. In a further refinement, the polyester is PLA. In another further refinement, the polyester is LPLA. In another further refinement, the polyester is PGA.

In one embodiment, the one or more polymer fibers have anisotropic elastic modulus.

In one embodiment, the method further includes the step of coating at least a portion of the tubular scaffold with a composition comprising a pharmaceutical agent. In a refinement, the composition further comprises a coating polymer. In further refinement, at least 90% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, the coating polymer comprises a bioabsorbable polymer. In a further refinement, the bioabsorbable polymer is selected from the group consisting of polylactides (PLA); poly(lactide-co-glycolide) (PLGA); polyanhydrides; polyorthoesters; poly(N-(2-hydroxypropyl) methacrylamide); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(glycolide-co-trimethylene carbonate) (PGA-TMC); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(dl-lactide-co-glycolide) (PGA-DLPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA); poly(glycolide-co-trimethylene carbonate-co-dioxanone) (PDO-PGA-TMC), polyarginine, and mixtures or co-polymers thereof. In a further refinement, the biodegradable polymer is selected from the group consisting of PLGA, polyarginine, and mixtures thereof.

In one embodiment, the one or more polymer fibers are gel-spun from a gel composition comprising the polymer and a pharmaceutical agent. In one embodiment, the one or more polymer fibers are extruded from a liquid crystalline composition comprising the polymer and a pharmaceutical agent.

In a refinement, the pharmaceutical agent is a macrolide immunosuppressant. In a further refinement, the macrolide immunosuppressant is rapamycin or a derivative, a prodrug, a hydrate, an ester, a salt, a polymorph, a derivative or an analog thereof. In another further refinement, the macrolide immunosuppressant is selected from the group consisting of rapamycin, 40-O-(2-Hydroxyethyl)rapamycin (everolimus), 40-O-Benzyl-rapamycin, 40-O-(4′-Hydroxymethyl)benzyl-rapamycin, 40-O-[4′-(1,2-Dihydroxyethyl)]benzyl-rapamycin, 40-O-Allyl-rapamycin, 40-O-[3′-(2,2-Dimethyl-1,3-dioxolan-4(S)-yl)-prop-2′-en-1′-yl]-rapamycin, (2′:E,4′S)-40-O-(4′,5′-Dihydroxypent-2′-en-1′-yl)-rapamycin, 40-O-(2-Hydroxy)ethoxycar-bonylmethyl-rapamycin, 40-O-(3-Hydroxy)propyl-rapamycin, 40-O-(6-Hydroxy)hexyl-rapamycin, 40-O-[2-(2-Hydroxy)ethoxy]ethyl-rapamycin, 40-O-[(3S)-2,2-Dimethyldioxolan-3-yl]methyl-rapamycin, 40-O-[(2S)-2,3-Dihydroxyprop-1-yl]-rapamycin, 40-O-(2-Acetoxy)ethyl-rapamycin, 40-O-(2-Nicotinoyloxy)ethyl-rapamycin, 40-O-[2-(N-Morpholino)acetoxy]ethyl-rapamycin, 40-O-(2-N-Imidazolylacetoxy)ethyl-rapamycin, 40-O-[2-(N-Methyl-N′-piperazinyl)acetoxy]ethyl-rapamycin, 39-O-Desmethyl-39,40-O,O-ethylene-rapamycin, (26R)-26-Dihydro-40-O-(2-hydroxy)ethyl-rapamycin, 28-O-Methyl-rapamycin, 40-O-(2-Aminoethyl)-rapamycin, 40-O-(2-Acetaminoethyl)-rapamycin, 40-O-(2-Nicotinamidoethyl)-rapamycin, 40-O-(2-(N-Methyl-imidazo-2′-ylcarbethoxamido)ethyl)-rapamycin, 40-O-(2-Ethoxycarbonylaminoethyl)-rapamycin, 40-O-(2-Tolylsulfonamidoethyl)-rapamycin, 40-O-[2-(4′,5′-Dicarboethoxy-1′,2′,3′-triazol-1′-yl)-ethyl]-rapamycin, 42-Epi-(tetrazolyl)rapamycin (tacrolimus), and 42-[3-hydroxy-2-(hydroxymethyl)-2-methylpropanoate]rapamycin. In a further refinement, the pharmaceutical agent is rapamycin.

INCORPORATION BY REFERENCE

All publications and patent applications mentioned in this specification are herein incorporated by reference to the same extent as if each individual publication or patent application was specifically and individually indicated to be incorporated by reference.

DETAILED DESCRIPTION OF THE DISCLOSURE

The present disclosure is explained in greater detail below. This description is not intended to be a detailed catalog of all the different ways in which the present disclosure may be implemented, or all the features that may be added to the present disclosure. For example, features illustrated with respect to one embodiment may be incorporated into other embodiments, and features illustrated with respect to a particular embodiment may be deleted from that embodiment. In addition, numerous variations and additions to the various embodiments suggested herein will be apparent to those skilled in the art in light of the instant disclosure, which do not depart from the present disclosure. Hence, the following specification is intended to illustrate some particular embodiments of the present disclosure, and not to exhaustively specify all permutations, combinations and variations thereof.

Bioabsorbable Biomedical Implant

Fully bioabsorbable biomedical implants, such as stents made of polymers without metal structural reinforcements, provide several desirable features over metal-based biomedical implants. Yet, the development of fully bioabsorbable polymer stents remains challenging to this date. As bioabsorbable polymer materials used to make the polymer stents are generally weaker than metals (e.g. steel), polymer stents with structural strength and integrity similar to metal stents need to be made of polymer struts with average thickness much greater than that of the metal struts (e.g. greater or significantly greater than 120 μm).

It is contemplated in the present disclosure that the increased strut thickness, while improving the structural strength and integrity of the stents, may adversely affect one or more desirable characteristics of the polymer stent. For example, the thicker struts may result in a stent with larger overall stent profile and less flexibility, and hence more difficult to navigate within blood vessels before deployment. The thicker struts may also lead to lower deformability that limits range of deployment (e.g. less than 10% overexpansion above nominal diameter, or less than about 0.5 mm in a vascular stent). In addition, the thicker struts may take longer to be fully dissolved or degraded, such as between three to five years.

Average Strut Thickness

In one embodiment, the polymer struts have an average thickness of no more than 100 μm. In another embodiment, the polymer struts have an average thickness of no more than 90 μm. In another embodiment, the polymer struts have an average thickness of no more than 80 μm. In another embodiment, the polymer struts have an average thickness of no more than 70 μm. In another embodiment, the polymer struts have an average thickness of no more than 60 μm. In another embodiment, the polymer struts have an average thickness of no more than 50 μm.

In one embodiment, the polymer struts have an average thickness of from 50 μm to about 120 μm. In one embodiment, the polymer struts have an average thickness of from 60 μm to about 120 μm. In one embodiment, the polymer struts have an average thickness of from 70 μm to about 120 μm. In one embodiment, the polymer struts have an average thickness of from 80 μm to about 120 μm. In one embodiment, the polymer struts have an average thickness of from 90 μm to about 120 μm. In one embodiment, the polymer struts have an average thickness of from 100 μm to about 120 μm.

In one embodiment, the polymer struts have an average thickness of from 50 μm to about 100 μm. In one embodiment, the polymer struts have an average thickness of from 60 μm to about 100 μm. In one embodiment, the polymer struts have an average thickness of from 70 μm to about 100 μm. In one embodiment, the polymer struts have an average thickness of from 80 μm to about 100 μm. In one embodiment, the polymer struts have an average thickness of from 90 μm to about 100 μm.

In one embodiment, the polymer struts have an average thickness of from 50 μm to about 90 μm. In one embodiment, the polymer struts have an average thickness of from 60 μm to about 90 μm. In one embodiment, the polymer struts have an average thickness of from 70 μm to about 90 μm. In one embodiment, the polymer struts have an average thickness of from 80 μm to about 90 μm.

In one embodiment, the polymer struts have an average thickness of from 50 μm to about 80 μm. In one embodiment, the polymer struts have an average thickness of from 60 μm to about 80 μm. In one embodiment, the polymer struts have an average thickness of from 70 μm to about 80 μm.

Structural Strength and Integrity

The structural strength and integrity of the disclosed bioabsorbable biomedical implants can be characterized by one or combinations of the following methods.

Radial Strength Testing

This test is conducted to determine and graphically represent the change in stent internal diameter as a function of circumferential pressure and to determine the pressure at which deformation is no longer completely reversible for the disclosed stent. The stents are deployed to nominal pressure and removed from the delivery system. The stents are placed into a sleeve approximately 1 mm larger than the stent diameter. A vacuum is then applied and outer diameter measurements taken at various pressures. The bioabsorbable implants according to the present disclosure should maintain a minimum of at least 50 percent of the original stent diameter after a 50 mm Hg pressure is applied. Some bioabsorbable implants according to the present disclosure should maintain a minimum of at least 80 percent of the original stent diameter after a 50 mm Hg pressure is applied.

Stent Recoil Testing

This test was conducted to quantify the amount of elastic recoil. The stent delivery system is inflated to nominal pressure (9ATM) and the stent is removed allowing for recoil to occur. The inner diameter at each end of the stent is recorded. Recoil is calculated subtracting the recoiled stent inner diameter from the pre-recoil inner diameter.

Stent Expansion Testing

This test is conducted to determine if the plastic deformation experienced by the stent when expanded from the compressed profile to the final maximum deployed diameter (i.e. over-deployed diameter) can produce crack initiation for the disclosed stent. The sample stents are deployed to their largest possible diameters by inflating each delivery system to balloon failure. Each stent is examined at 45× magnification for potential cracks.

Maximum Pressure (Burst Test) Testing

This test is conducted to demonstrate that the delivery system (with mounted stent) will not experience balloon, shaft, proximal adaptation or proximal/distal seal loss of integrity at or below the pressure required to expand the stent to its labeled diameter. Stent delivery systems that had been subjected to all manufacturing and sterilization procedures were pressurized to 90 psi with pressure held for 15 seconds and released for 3 seconds. The cycle was then repeated, increasing inflation pressure by 15 psi each cycle until failure.

In one embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg. In another embodiment, the tubular scaffold maintains at least 60% of its nominal luminal cross sectional area under a pressure load of 50 mmHg. In another embodiment, the tubular scaffold maintains at least 70% of its nominal luminal cross sectional area under a pressure load of 50 mmHg. In another embodiment, the tubular scaffold maintains at least 80% of its nominal luminal cross sectional area under a pressure load of 50 mmHg. In another embodiment, the tubular scaffold maintains at least 90% of its nominal luminal cross sectional area under a pressure load of 50 mmHg. In another embodiment, the tubular scaffold maintains at least 95% of its nominal luminal cross sectional area under a pressure load of 50 mmHg.

In one embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 2 months of exposure to saline in vitro. In another embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 2 month in vivo.

In one embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 3 months of exposure to saline in vitro. In another embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 3 month in vivo.

In one embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 4 months of exposure to saline in vitro. In another embodiment, the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg upon 4 month in vivo.

Polymer Chain Orientation

Strut-Longitudinal Orientation

In one embodiment, each polymer strut includes polymer chains that are longitudinally aligned along a center axis of the polymer strut. In one embodiment, the polymer struts include crystalline domains, in which the polymer chains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 50% of polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 55% of the polymer chains or the crystalline domains in the polymer struts are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 60% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 65% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 70% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 75% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 80% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 85% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 90% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts. In another embodiment, more than 95% of the polymer chains in the polymer struts or the crystalline domains are longitudinally aligned along the center axes of the polymer struts.

As a result of the strut-longitudinal polymer chain orientation, the polymer struts have anisotropic elastic modulus. For example, the polymer struts have an average longitudinal elastic modulus along the center axes of the polymer struts and an average lateral elastic modulus orthogonal to the center axes of the polymer struts, the average longitudinal elastic modulus being greater than the average lateral elastic modulus.

In one embodiment, the average longitudinal elastic modulus is at least 2 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 3 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 4 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 5 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 6 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 7 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 8 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 9 times the average lateral elastic modulus. In another embodiment, the average longitudinal elastic modulus is at least 10 times the average lateral elastic modulus.

Scaffold-Axial Orientation

In one embodiment, the tubular scaffold includes polymer chains that are axially aligned along a center axis of the tubular scaffold. In one embodiment, the polymer struts include crystalline domains, in which the polymer chains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 50% of polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 55% of the polymer chains or the crystalline domains in the polymer struts are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 60% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 65% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 70% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 75% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 80% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 85% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 90% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold. In another embodiment, more than 95% of the polymer chains in the polymer struts or the crystalline domains are axially aligned along a center axis of the tubular scaffold.

As a result of the scaffold-axial polymer chain orientation, the tubular scaffold has anisotropic elastic modulus. For example, the tubular scaffold has an average axial elastic modulus along a center axis of the tubular scaffold and an average circumferential elastic modulus orthogonally surrounding a center axis of the tubular scaffold, the average axial elastic modulus being greater than the average circumferential elastic modulus.

In one embodiment, the average axial elastic modulus is at least 2 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 3 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 4 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 5 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 6 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 7 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 8 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 9 times the average circumferential elastic modulus. In another embodiment, the average axial elastic modulus is at least 10 times the average circumferential elastic modulus.

Scaffold-Circumferential Orientation

In one embodiment, the tubular scaffold includes polymer chains that are circumferential aligned, i.e. orthogonally surrounding a center axis of the tubular scaffold. In one embodiment, the polymer struts include crystalline domains, in which the polymer chains are circumferential aligned. In another embodiment, more than 50% of polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 55% of the polymer chains or the crystalline domains in the polymer struts are circumferential aligned. In another embodiment, more than 60% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 65% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 70% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 75% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 80% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 85% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 90% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned. In another embodiment, more than 95% of the polymer chains in the polymer struts or the crystalline domains are circumferential aligned.

As a result of the scaffold-circumferential polymer chain orientation, the tubular scaffold has anisotropic elastic modulus. For example, the tubular scaffold has an average axial elastic modulus along a center axis of the tubular scaffold and an average radial elastic modulus orthogonal to a center axis of the tubular scaffold, the average circumferential elastic modulus being greater than the average axial elastic modulus.

In one embodiment, the average circumferential elastic modulus is at least 2 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 3 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 4 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 5 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 6 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 7 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 8 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 9 times the average axial elastic modulus. In another embodiment, the average circumferential elastic modulus is at least 10 times the average axial elastic modulus.

Deformation Angle

Further, as a result of the polymer chain orientation, the polymer struts have an average deformation angle, i.e the average angle between the polymer struts when deployed minus the average angle between the polymer structs when undeployed. In one embodiment, the polymer struts have an average deformation angle of at least 90 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 85 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 80 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 75 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 70 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 65 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 60 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 55 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 50 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 45 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 40 degrees. In another embodiment, the polymer struts have an average deformation angle of at least 30 degrees. Without wishing to be bound by any particular theory, it is contemplated that the configuration of the polymer struts according to the specified deformation angle improves the deformability of the polymer stent made of chain-oriented polymers.

Bioabsorbable Polymer Materials

In one refinement, the gel-spun polymer material is PLGA. In a further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer ranging from 82:18 to 88:12. In a further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer ranging from 72:28 to 78:22. In another further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer ranging from 62:38 to 68:32. In another further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer ranging from 47:53 to 53:47. In another further refinement, the PLGA has a ratio of lactic acid monomer to glycolic acid monomer of 50:50.

In another further refinement, the PLGA has a weight average molecular weight of about 8,000 Dalton to about 12,000 Dalton. In another further refinement, the PLGA has a weight average molecular weight of about 12,000 Dalton to about 16,000 Dalton. In another further refinement, the PLGA has a weight average molecular weight of up to about 90,000 Dalton. In another refinement, the gel-spun polymer material is PLA or LPLA. In another refinement, the gel-spun polymer material is PGA. In some embodiment, the gel spun polymer material (e.g. PLGA, LPLA, PLA, PGA) has a weight average molecular weight of at least 90,000 Dalton, and optionally at least 100,000 Dalton

In another refinement, the liquid crystalline polymer material has a crystallinity of at least 30%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 35%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 40%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 45%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 50%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 55%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 60%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 65%. In another refinement, the liquid crystalline polymer material has a crystallinity of at least 70%.

Stent Deployment

In a further refinement, the over-deployed diameter is about 1.0 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.9 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.8 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.7 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.6 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.5 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.4 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.3 mm greater than the nominal diameter. In another further refinement, the over-deployed diameter is about 0.2 mm greater than the nominal diameter.

In one refinement, the tubular scaffold is expandable by an inflatable balloon positioned within the tubular scaffold. In a further refinement, the tubular scaffold has a deployed diameter of 2.25 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a deployed diameter of 2.5 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a deployed diameter of 3.0 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a deployed diameter of 3.5 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a deployed diameter of 4.0 mm at nominal balloon pressure. In another further refinement, the tubular scaffold has a deployed diameter of 4.5 mm at nominal balloon pressure. The nominal balloon pressure may be dependent on the material and design of the balloon. As a non-limiting example, the nominal balloon pressure is 6 atmospheres. As another example, the nominal balloon pressure is 9 atmosphere.

In one embodiment, the tubular scaffold is formed from a plurality of sinusoidal polymer fibers. In a refinement, the sinusoidal polymer fibers are interconnected at a plurality of connecting points.

Many methods for forming wire- or filament-based stents can be used to make the bioabsorbable stents disclosed herein. For example, the methods for forming Wallstent (Boston Scientific), S7 (Medtronic), AngioStent (AngioDynamics), Strecker (Boston Scientific), Expander (Medicorp), Horizon Prostatic (Endocare), Endocoil (InStent), etc, can be used to in light of the present disclosure.

Drug Coating

In one embodiment, the biomedical implant further includes a pharmaceutical agent incorporated to the tubular scaffold. In a refinement, the pharmaceutical agent is a macrolide immunosuppressant. In a further refinement, the macrolide immunosuppressant is rapamycin or a derivative, a prodrug, a hydrate, an ester, a salt, a polymorph, a derivative or an analog thereof. In another further refinement, the macrolide immunosuppressant is selected from the group consisting of rapamycin, 40-O-(2-Hydroxyethyl)rapamycin (everolimus), 40-O-Benzyl-rapamycin, 40-O-(4′-Hydroxymethyl)benzyl-rapamycin, 40-O-[4′-(1,2-Dihydroxyethyl)]benzyl-rapamycin, 40-O-Allyl-rapamycin, 40-O-[3′-(2,2-Dimethyl-1,3-dioxolan-4(S)-yl)-prop-2′-en-1′-yl]-rapamycin, (2′:E,4′S)-40-O-(4′,5′-Dihydroxypent-2′-en-1′-yl)-rapamycin, 40-O-(2-Hydroxy)ethoxycar-bonylmethyl-rapamycin, 40-O-(3-Hydroxy)propyl-rapamycin, 40-O-(6-Hydroxy)hexyl-rapamycin, 40-O-[2-(2-Hydroxy)ethoxy]ethyl-rapamycin, 40-O-[(3S)-2,2-Dimethyldioxolan-3-yl]methyl-rapamycin, 40-O-[(2S)-2,3-Dihydroxyprop-1-yl]-rapamycin, 40-O-(2-Acetoxy)ethyl-rapamycin, 40-O-(2-Nicotinoyloxy)ethyl-rapamycin, 40-O-[2-(N-Morpholino)acetoxy]ethyl-rapamycin, 40-O-(2-N-Imidazolylacetoxy)ethyl-rapamycin, 40-O-[2-(N-Methyl-N′-piperazinyl)acetoxy]ethyl-rapamycin, 39-O-Desmethyl-39,40-O,O-ethylene-rapamycin, (26R)-26-Dihydro-40-O-(2-hydroxy)ethyl-rapamycin, 28-O-Methyl-rapamycin, 40-O-(2-Aminoethyl)-rapamycin, 40-O-(2-Acetaminoethyl)-rapamycin, 40-O-(2-Nicotinamidoethyl)-rapamycin, 40-O-(2-(N-Methyl-imidazo-2′-ylcarbethoxamido)ethyl)-rapamycin, 40-O-(2-Ethoxycarbonylaminoethyl)-rapamycin, 40-O-(2-Tolylsulfonamidoethyl)-rapamycin, 40-O-[2-(4′,5′-Dicarboethoxy-1′,2′,3′-triazol-1′-yl)-ethyl]-rapamycin, 42-Epi-(tetrazolyl)rapamycin (tacrolimus), and 42-[3-hydroxy-2-(hydroxymethyl)-2-methylpropanoate]rapamycin. In one refinement, the pharmaceutical agent is rapamycin.

In one refinement, at least a portion of the tubular scaffold is covered with a coating comprising the pharmaceutical agent. In a further refinement, the coating further comprises a coating polymer. In a further refinement, at least 90% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 85% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 80% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 75% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 70% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 65% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 60% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 55% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer. In a further refinement, at least 50% of the surface area of the pharmaceutical agent is encapsulated in the coating polymer.

In a further embodiment, the pharmaceutical agent is impregnated in at least a portion of the tubular scaffold (e.g. evenly distributed throughout the tubular scaffold) and at least a portion of the tubular scaffold is covered with a coating comprising the pharmaceutical agent, such as in the manner discussed in the paragraph above.

In a further refinement, the coating polymer comprises a bioabsorbable polymer. In a further refinement, the bioabsorbable polymer is selected from the group consisting of polylactides (PLA); poly(lactide-co-glycolide) (PLGA); polyanhydrides; polyorthoesters; poly(N-(2-hydroxypropyl) methacrylamide); poly(dl-lactide) (DLPLA); poly(l-lactide) (LPLA); polyglycolide (PGA); poly(dioxanone) (PDO); poly(glycolide-co-trimethylene carbonate) (PGA-TMC); poly(l-lactide-co-glycolide) (PGA-LPLA); poly(dl-lactide-co-glycolide) (PGA-DLPLA); poly(l-lactide-co-dl-lactide) (LPLA-DLPLA); poly(glycolide-co-trimethylene carbonate-co-dioxanone) (PDO-PGA-TMC), polyarginine, and mixtures or co-polymers thereof. In a further refinement, the biodegradable polymer is selected from the group consisting of PLGA, polyarginine, and mixtures thereof.

Gel-Spun Polymer

In one embodiment, the method further includes the step of cooling the polyester fiber in a liquid bath.

In one embodiment, the gel composition are extruded through a spinneret.

Liquid Crystalline Polyester

In one embodiment, the polyester is in a melted state and wherein the method further comprises cooling the polyester fiber.

In one embodiment, the liquid crystalline composition further comprises a solvent and wherein the method further comprises allowing the solvent to evaporate.

Manufacturing of Bioabsorbable Stent

Manufacturing of Tubular Scaffold

Tubular Scaffold with Strut-Longitudinally Aligned Polymer Orientation

In this non-limiting example, the tubular scaffold of the present disclosure is made by forming a continuous wave form that includes a plurality of struts and a plurality of crowns. Each crown is a curved portion or turn within the wave form that connects adjacent struts to define the continuous wave form. In this example, the struts are substantially straight portions of the wave form. In other examples, the struts are slightly bent or have other shapes, such as a sinusoidal wave, for example. The wave form may be formed by a single polymer fiber or filament or a plurality of interconnected polymer fibers or filaments.

After the wave form is formed, the wave form is wrapped around a mandrel, a center axis of which defines the longitudinal axis of the tubular scaffold. The wave form may be wrapped at an angle that is not perpendicular to the longitudinal axis to form a plurality of helical turns that together generally form a helical coil in the shape of a helix.

The tubular scaffold also includes a plurality of connections that are configured to connect selected crowns of adjacent turns. In one embodiment, the tubular scaffold includes three connections per complete helix turn. In one embodiment, the tubular scaffold includes four connections per complete helix turn. In one embodiment, the tubular scaffold includes five connections per complete helix turn. Other connection numbers and configurations can also be used in light of the present disclosure. In a non-limiting example, the connections are created by fusing the selected crowns together. As used herein, “fusing” is defined as heating the target portions of materials to be fused together, with or without adding any additional material, to a level where the material in the target portions flow together, intermix with one another, and form a fusion when the materials cool down to, for example, room temperature.

Tubular Scaffold with Scaffold-Axially Aligned Polymer Orientation

In this non-limiting example, the tubular scaffold of the present disclosure is made by forming polymer tube in which at least some polymer chains are aligned to a center axis of the polymer tube. In one embodiment, the polymer tube is formed by (1) forming a gel composition comprising the polymer and a solvent; (2) extruding the gel composition to form a tubular structure; and (3) allowing the solvent to evaporate in drying air to form the polyester fiber. In a refinement, the extruded polymer tube undergoes another drawing process. In another embodiment, the polymer tube is formed by (1) forming a liquid crystalline composition (e.g. a melt) containing the polymer; and (2) extruding the liquid crystalline composition to form a tubular structure. In a refinement, the extruded polymer tube undergoes another longitudinal drawing process.

After the polymer tube is formed, the tubular scaffold can be made by laser-cutting a stent design from the polymer tube. In one embodiment, the stent design is cut from the polymer tube using a polymer-compatible laser, such as carbon dioxide laser beam or other suitable laser cutting technologies in light of the present disclosure. In another embodiment, the stent design is cut from the polymer tube by water jet cutting or abrasive water jet cutting. Alternatively, the tubular scaffold can be made through photochemical etching or chemical etching. Many slotted tube stent designs can be used to make the bioabsorbable stents disclosed herein. For example, suitable stent deigns may include, but are not limited to, bStent2 by Medtronic; BiodivYsio by Biocompatibles Ltd.; Velocity, Palmaz-Schatz 153/154, Palmaz-Schatz Crown by Cordis; Express by Boston Scientific; JOSTENT Flex by JOMED; Multi-Link PENTA, Multi-Link Rx, and Multi-Link Vision by Guidant; and NIR and NIR Flex by Medinol. Other stent designs may also be used in light of the present disclosure.

Tubular Scaffold with Scaffold-Circumferentially Aligned Polymer Orientation

In this non-limiting example, the tubular scaffold of the present disclosure is made by first forming a polymer preform containing the bioabsorbable polymer material. In one embodiment, the polymer preform is molded or extruded from a gel composition containing the bioabsorbable polymer material. In another embodiment, the polymer preform is molded or extruded from a liquid crystalline composition containing the bioabsorbabel polymer material. The polymer preform is then radially expanded and/or stretched to desired inner diameter and wall thickness to form the polymer tube in which at least some polymer chains are circumferentially aligned (orthogonal to a center axis of the polymer tube). Without wishing to be bound by any particular theory, it is contemplated in the present disclosure that the radial expansion and stretching of the preform at least partially contribute to the circumferential alignment of the polymer chains in the polymer tube.

Coating of Tubular Scaffold.

Provided herein are methods for coating the tubular scaffold (also referred to as substrate in this section) with a pharmaceutical or biological agent in powder form. Conventional processes for spray coating stents may also be used. For example, the drug and coating polymer may be dissolved in a suitable solvent or mutual solvent before spray coating can occur. Provided herein are methods for depositing a coating polymer and a pharmaceutical or biological agent in powder form onto the substrate. The coating process provides a cost-effective, efficient method for depositing a combination of an inert polymer or polymers and a pharmaceutical or biological agent or agents, onto parts or all surfaces of a substrate, to form a coating that is of a pre-determined, desired thickness, conformal, substantially defect-free, and uniform and the composition of the coating can be regulated. In particular, the coating process addresses the problem of existing coating processes, which do not allow for structural and morphological preservation of the agents deposited during the coating process.

One aspect of the invention entails the deposition of the pharmaceutical or biological agents as dry powder. Dry powder spraying is well known in the art, and dry powder spraying coupled with electrostatic capture has been described, for example in U.S. Pat. Nos. 5,470,603; 6,319,541; or 6,372,246. The deposition of the polymer can be performed in any number of standard procedures, as the morphology of the polymer, so long as it provides coatings possessing the desired properties (e.g. thickness, conformity, defect-free, uniformity etc), is of less importance. The function of the polymer is primarily one of inert carrier matrix for the active components of the coating.

One aspect of the coating process is the combination of two or more of the dry powder, RESS and SEDS spraying techniques.

Another aspect of the coating process involves the dry powder spraying of a pharmaceutical agent, in a preferred particle size and morphology, into the same capture vessel as a polymer that is also dry powder sprayed, whereby the spraying of the agent and the polymer is sequential or simultaneous.

Another specific aspect of the coating process involves the dry powder spraying of an active biological agent, in a preferred particle size and possessing a particular activity, into the same capture vessel as a polymer that is also dry powder sprayed, whereby the spraying of the agent and the polymer is sequential or simultaneous.

Yet another aspect of the coating process involves the dry powder spraying of a pharmaceutical agent, in a preferred particle size and morphology, into the same capture vessel as a polymer that is sequentially or simultaneously sprayed by the RESS spray process.

Yet another aspect of the coating process involves the dry powder spraying of an active biological agent, in a preferred particle size and possessing a particular activity, into the same capture vessel as a polymer that is sequentially or simultaneously sprayed by the RESS spray process.

In some embodiments, the RESS or the SEDS process used in forming the coating is performed with electrically charging the substrate. In some embodiments, the e-RESS or the e-SEDS process used in forming the coating is performed by creating an electrical potential between the substrate and the coating apparatus used in process. In some embodiment, the RESS or the SEDS process used in forming the coating is performed without electrically charging the substrate.

In further aspects of the coating process the substrates that have been coated with pharmaceutical or biological agents and polymers, as described in the above embodiments are then subjected to a sintering process. The sintering process takes place under benign conditions, which do not affect the structural and morphological integrity of the pharmaceutical and biological agents, and refers to a process by which the co-deposited pharmaceutical agent or biological agent-polymer matrix, becomes continuous and adherent to the substrate. This is achieved by treating the coated substrate with a compressed gas, compressed liquid or supercritical fluid at conditions such that it is a poor solvent of the polymers, a weak solvent of the polymers or a non-solvent for the polymers, the pharmaceutical agents and the biological agents, but an agent suitable for the treatment of polymer particles to form continuous polymer coatings. The sintering process takes place under conditions (e.g. mild temperatures), and using benign fluids (e.g. supercritical carbon dioxide) which will not affect the structural and morphological integrity of the pharmaceutical and biological agents. Other sintering processes, which do not affect the structural and morphological integrity of the pharmaceutical and biological agents may also be contemplated by the present invention.

In further aspects of the coating process, it is desirable to create coatings such that release of an active substance occurs with a predetermined elution profile when placed in the desired elution media. Coating properties can be modified in a variety of different ways in order to provide desirable elution profiles.

The chemical composition of the coating polymers can be varied, to provide greater or lesser amounts of coating polymers that will allow or restrict the elution of active substance. For example, if the intended elution media contain water, a higher content of coating polymers that swell in water, will allow for a faster elution of active substance. Conversely, a higher content of coating polymers that do not swell in aqueous media will result in a slower elution rate.

The coating properties can also be controlled by alternating coating polymer layers. Layers of coating polymers of different properties are deposited on the substrate in a sequential manner. By modifying the nature of the polymer deposited in each layer (e.g., depositing layers of different polymers) the elution profile of the coating is altered. The number of layers and the sequence in their deposition provide additional avenues for the design of coatings having controlled elution profiles.

The coating properties can also be modified by control of the macro and/or micro-structure of the polymer coating (diffusion pathways). This may be achieved by varying the coating process(es) or by using different sintering conditions.

The coating process provides several approaches for controlling the elution of a drug or several drugs. For example, in one embodiment, controlled elution is achieved by the segregation of different coating polymers (e.g. PEVA/PBMA). In another embodiment, control of elution is achieved by controlling the conditions during the sintering process such that controlled incomplete sintering of the polymer matrix is obtained, whereby the coating would retain some of the particle-like structure of the polymer particles as deposited. Incomplete sintering would provide pores/voids in the coating and allow additional pathways for elution of the drug, including drug elution around the polymer(s) instead of, or in addition to, elution through the polymer(s). The size of the pores or voids obtained through incomplete sintering of the polymer matrix may be obtained through several methods. For example, the rate of depressurization of a vessel in which the sintering process is carried out provides one avenue for controlling pore size. The size of the cavities or pores in the coating can be controlled by employing a porogen as an excipient and subsequent removal of at least a portion of the porogen, for example by treatment with a solvent of the porogen. Preferably, the porogen solvent comprises a densified gas (e.g.; carbon). In some embodiments the porogen is an SOA or other such hydrophobically derivatized carbohydrate. Removal of at least a portion of the porogen is preferably carried out during the sintering process.

In some aspects of the invention, the active substance elution profile is controllable by altering the coating polymer particle size. The method by which the polymer particles are deposited onto the substrate is thus varied to provide the desired elution rate. For example, for polymers released simultaneously through the same nozzle, RESS release from a supercritical solution would typically result in small polymer particles; RESS-like release from a mixture in a compressed gas usually generates larger polymer particles. Using the SEDS process can result in variable polymer particle size, depending on the particular SEDS conditions employed.

In further aspects of the coating process, the active substance elution profile is controllable by altering the coating polymer particle shape. One way to achieve variation in polymer particle shape is to alter the initial concentration of the polymers. At lower initial concentrations, polymers are deposited as small particles. At increased concentrations, larger particles are formed. At higher concentrations, the formed particles become elongated, until at high concentrations the elongated features become fiber-like and eventually become continuous fibers.

In yet other aspects of the coating process, the active substance elution profile is controllable by creating discrete domains of chemically different polymers. As described above, chemically different polymers will allow or restrict the elution of active substance in different elution media. By changing the position of such polymers in discrete macroscopic domains within the coating, the elution profiles will be adjustable. For example during a process whereby two different polymers are released sequentially through the same nozzle, particles of either polymer could be deposited to position them, for example, closer to the outside, the inside or the middle of the coating on the substrate. In another embodiment, the two polymers may be released simultaneously through two different nozzles at differing and/or alternating deposition rates, resulting in a similar effect. In a further embodiment, the deposition of eluting and non-eluting polymers is alternated to result in a fluctuating type of release. In yet other embodiments, the polymers are deposited to provide for a pulsatile release of active substance. Separation of the polymer(s) providing different domains for drug diffusion is achieved, for example, by subsequent spray of the polymers through same nozzle or by using multiple nozzles. Also, as described above, controlling the elution of the active substance may be achieved by layering of different polymers across the depth of the coating. A combination of domain separation and cross-depth layering is also contemplated for the design of coatings having controlled elution properties.

The deposition of active substance during any of these processes may be constant to provide even distribution throughout the coating, or the spraying of the active substance may be varied to result in differing amounts of active substance in the differing polymeric domains within the coating.

In further aspects of the coating process, the active substance elution profile is controllable by varying the coating sintering conditions. For example, incomplete sintering will create open spaces, or pores in the interstitial spaces between the polymer particles, which will enable faster eluting of active substance from the coating. Another way to utilize the sintering conditions for elution control would be to deliberately create irregular coatings by foaming during the sintering process. Rapid pressure release of a CO₂— or isobutylene-impregnated polymer film induces formation of foamed polymers which would create a coating with increased porosity and be very ‘open’ to diffusion/elution. Thus the elution profile would be controllable by manipulating the foaming conditions, which in turn controls the pore density and size.

Another advantage of the coating process is the ability to create a stent with a controlled (dialed-in) drug-elution profile. Via the ability to have different materials in each layer of the laminate structure and the ability to control the location of drug(s) independently in these layers, the method enables a stent that could release drugs at very specific elution profiles, programmed sequential and/or parallel elution profiles. Also, the present invention allows controlled elution of one drug without affecting the elution of a second drug (or different doses of the same drug).

The embodiments incorporating a stent form or framework provide the ability to radiographically monitor the stent in deployment. In an alternative embodiment, the inner-diameter of the stent can be masked (e.g. by a non-conductive mandrel). Such masking would prevent additional layers from being on the interior diameter (abluminal) surface of the stent. The resulting configuration may be desirable to provide preferential elution of the drug toward the vessel wall (luminal surface of the stent) where the therapeutic effect of anti-restenosis is desired, without providing the same antiproliferative drug(s) on the abluminal surface, where they may retard healing, which in turn is suspected to be a cause of late-stage safety problems with current DESs.

The coating process allows for employing a platform combining layer formation methods based on compressed fluid technologies; electrostatic capture and sintering methods. The platform results in drug eluting stents having enhanced therapeutic and mechanical properties. The coating process is particularly advantageous in that it employs optimized laminate polymer technology. In particular, the coating process allows the formation of discrete layers of specific drug platforms.

The coating process provided herein the drugs and polymers are coated on the stent framework in discrete steps, which can be carried out simultaneously or alternately. This allows discrete deposition of the active agent (e.g.; a drug) within a polymer matrix thereby allowing the placement of more than one drug on a single medical device with or without an intervening polymer layer. For example, the present platform provides a dual drug eluting stent.

Some of the advantages provided by the coating process include employing compressed fluids (e.g., supercritical fluids, for example RESS based methods); solvent free deposition methodology; a platform that allows processing at lower temperatures thereby preserving the qualities of the active agent and the polymer matrix; the ability to incorporate two, three or more drugs while minimizing deleterious effects from direct interactions between the various drugs and/or their excipients during the fabrication and/or storage of the drug eluting stents; a dry deposition; enhanced adhesion and mechanical properties of the layers on the stent framework; precision deposition and rapid batch processing; and ability to form intricate structures.

The coating process may provide a multi-drug delivery platform which produces strong, resilient and flexible drug eluting stents including an anti-restenosis drug (e.g.; a limus or taxol) and anti-thrombosis drug (e.g.; heparin or an analog thereof) and well characterized bioabsorbable polymers. The drug eluting stents provided herein minimize potential for thrombosis, in part, by reducing or totally eliminating thrombogenic polymers and reducing or totally eliminating residual drugs that could inhibit healing.

Definitions

As used in the present specification, the following words and phrases are generally intended to have the meanings as set forth below, except to the extent that the context in which they are used indicates otherwise.

The terms “bioabsorbable,” “biodegradable,” “bioerodible,” “bioresorbable,” and “resorbable” are art-recognized synonyms. These terms are used herein interchangeably. Bioabsorbable polymers typically differ from non-bioabsorbable polymers in that the former may be absorbed (e.g.; degraded) during use. In certain embodiments, such use involves in vivo use, such as in vivo therapy, and in other certain embodiments, such use involves in vitro use. In general, degradation attributable to biodegradability involves the degradation of a bioabsorbable polymer into its component subunits, or digestion, e.g., by a biochemical process, of the polymer into smaller, non-polymeric subunits. In certain embodiments, biodegradation may occur by enzymatic mediation, degradation in the presence of water (hydrolysis) and/or other chemical species in the body, or both. The bioabsorbability of a polymer may be indicated in-vitro as described herein or by methods known to one of skill in the art. An in-vitro test for bioabsorbability of a polymer does not require living cells or other biologic materials to indicate bioabsorption properties (e.g. degradation, digestion). Thus, resorbtion, resorption, absorption, absorbtion, erosion may also be used synonymously with the terms “bioabsorbable,” “biodegradable,” “bioerodible,” and “bioresorbable.” Mechanisms of degradation of a bioabsorbable polymer may include, but are not limited to, bulk degradation, surface erosion, and combinations thereof.

As used herein, the term “biodegradation” encompasses both general types of biodegradation. The degradation rate of a biodegradable polymer often depends in part on a variety of factors, including the chemical identity of the linkage responsible for any degradation, the molecular weight, crystallinity, biostability, and degree of cross-linking of such polymer, the physical characteristics (e.g., shape and size) of the implant, and the mode and location of administration. For example, the greater the molecular weight, the higher the degree of crystallinity, and/or the greater the biostability, the biodegradation of any bioabsorbable polymer is usually slower.

“Degradation” as used herein refers to the conversion or reduction of a chemical compound to one less complex, e.g., by splitting off one or more groups of atoms. Degradation of the coating may reduce the coating's cohesive and adhesive binding to the device, thereby facilitating transfer of the coating to the intervention site

“Pharmaceutical agent” as used herein refers to any of a variety of drugs or pharmaceutical compounds that can be used as active agents to prevent or treat a disease (meaning any treatment of a disease in a mammal, including preventing the disease, i.e. causing the clinical symptoms of the disease not to develop; inhibiting the disease, i.e. arresting the development of clinical symptoms; and/or relieving the disease, i.e. causing the regression of clinical symptoms). It is possible that the pharmaceutical agents of the invention may also comprise two or more drugs or pharmaceutical compounds. Pharmaceutical agents, include but are not limited to antirestenotic agents, antidiabetics, analgesics, antiinflammatory agents, antirheumatics, antihypotensive agents, antihypertensive agents, psychoactive drugs, tranquillizers, antiemetics, muscle relaxants, glucocorticoids, agents for treating ulcerative colitis or Crohn's disease, antiallergics, antibiotics, antiepileptics, anticoagulants, antimycotics, antitussives, arteriosclerosis remedies, diuretics, proteins, peptides, enzymes, enzyme inhibitors, gout remedies, hormones and inhibitors thereof, cardiac glycosides, immunotherapeutic agents and cytokines, laxatives, lipid-lowering agents, migraine remedies, mineral products, otologicals, anti parkinson agents, thyroid therapeutic agents, spasmolytics, platelet aggregation inhibitors, vitamins, cytostatics and metastasis inhibitors, phytopharmaceuticals, chemotherapeutic agents and amino acids. Examples of suitable active ingredients are acarbose, antigens, beta-receptor blockers, non-steroidal antiinflammatory drugs {NSAIDs], cardiac glycosides, acetylsalicylic acid, virustatics, aclarubicin, acyclovir, cisplatin, actinomycin, alpha- and beta-sympatomimetics, (dmeprazole, allopurinol, alprostadil, prostaglandins, amantadine, ambroxol, amlodipine, methotrexate, S-aminosalicylic acid, amitriptyline, amoxicillin, anastrozole, atenolol, azathioprine, balsalazide, beclomethasone, betahistine, bezafibrate, bicalutamide, diazepam and diazepam derivatives, budesonide, bufexamac, buprenorphine, methadone, calcium salts, potassium salts, magnesium salts, candesartan, carbamazepine, captopril, cefalosporins, cetirizine, chenodeoxycholic acid, ursodeoxycholic acid, theophylline and theophylline derivatives, trypsins, cimetidine, clarithromycin, clavulanic acid, clindamycin, clobutinol, clonidine, cotrimoxazole, codeine, caffeine, vitamin D and derivatives of vitamin D, colestyramine, cromoglicic acid, coumarin and coumarin derivatives, cysteine, cytarabine, cyclophosphamide, ciclosporin, cyproterone, cytabarine, dapiprazole, desogestrel, desonide, dihydralazine, diltiazem, ergot alkaloids, dimenhydrinate, dimethyl sulphoxide, dimeticone, domperidone and domperidan derivatives, dopamine, doxazosin, doxorubizin, doxylamine, dapiprazole, benzodiazepines, diclofenac, glycoside antibiotics, desipramine, econazole, ACE inhibitors, enalapril, ephedrine, epinephrine, epoetin and epoetin derivatives, morphinans, calcium antagonists, irinotecan, modafinil, orlistat, peptide antibiotics, phenyloin, riluzoles, risedronate, sildenafil, topiramate, macrolide antibiotics, oestrogen and oestrogen derivatives, progestogen and progestogen derivatives, testosterone and testosterone derivatives, androgen and androgen derivatives, ethenzamide, etofenamate, etofibrate, fenofibrate, etofylline, etoposide, famciclovir, famotidine, felodipine, fenofibrate, fentanyl, fenticonazole, gyrase inhibitors, fluconazole, fludarabine, fluarizine, fluorouracil, fluoxetine, flurbiprofen, ibuprofen, flutamide, fluvastatin, follitropin, formoterol, fosfomicin, furosemide, fusidic acid, gallopamil, ganciclovir, gemfibrozil, gentamicin, ginkgo, Saint John's wort, glibenclamide, urea derivatives as oral antidiabetics, glucagon, glucosamine and glucosamine derivatives, glutathione, glycerol and glycerol derivatives, hypothalamus hormones, goserelin, gyrase inhibitors, guanethidine, halofantrine, haloperidol, heparin and heparin derivatives, hyaluronic acid, hydralazine, hydrochlorothiazide and hydrochlorothiazide derivatives, salicylates, hydroxyzine, idarubicin, ifosfamide, imipramine, indometacin, indoramine, insulin, interferons, iodine and iodine derivatives, isoconazole, isoprenaline, glucitol and glucitol derivatives, itraconazole, ketoconazole, ketoprofen, ketotifen, lacidipine, lansoprazole, levodopa, levomethadone, thyroid hormones, lipoic acid and lipoic acid derivatives, lisinopril, lisuride, lofepramine, lomustine, loperamide, loratadine, maprotiline, mebendazole, mebeverine, meclozine, mefenamic acid, mefloquine, meloxicam, mepindolol, meprobamate, meropenem, mesalazine, mesuximide, metamizole, metformin, methotrexate, methylphenidate, methylprednisolone, metixene, metoclopramide, metoprolol, metronidazole, mianserin, miconazole, minocycline, minoxidil, misoprostol, mitomycin, mizolastine, moexipril, morphine and morphine derivatives, evening primrose, nalbuphine, naloxone, tilidine, naproxen, narcotine, natamycin, neostigmine, nicergoline, nicethamide, nifedipine, niflumic acid, nimodipine, nimorazole, nimustine, nisoldipine, adrenaline and adrenaline derivatives, norfloxacin, novamine sulfone, noscapine, nystatin, ofloxacin, olanzapine, olsalazine, omeprazole, omoconazole, ondansetron, oxaceprol, oxacillin, oxiconazole, oxymetazoline, pantoprazole, paracetamol, paroxetine, penciclovir, oral penicillins, pentazocine, pentifylline, pentoxifylline, perphenazine, pethidine, plant extracts, phenazone, pheniramine, barbituric acid derivatives, phenylbutazone, phenyloin, pimozide, pindolol, piperazine, piracetam, pirenzepine, piribedil, piroxicam, pramipexole, pravastatin, prazosin, procaine, promazine, propiverine, propranolol, propyphenazone, prostaglandins, protionamide, proxyphylline, quetiapine, quinapril, quinaprilat, ramipril, ranitidine, reproterol, reserpine, ribavirin, rifampicin, risperidone, ritonavir, ropinirole, roxatidine, roxithromycin, ruscogenin, rutoside and rutoside derivatives, sabadilla, salbutamol, salmeterol, scopolamine, selegiline, sertaconazole, sertindole, sertralion, silicates, sildenafil, simvastatin, sitosterol, sotalol, spaglumic acid, sparfloxacin, spectinomycin, spiramycin, spirapril, spironolactone, stavudine, streptomycin, sucralfate, sufentanil, sulbactam, sulphonamides, sulfasalazine, sulpiride, sultamicillin, sultiam, sumatriptan, suxamethonium chloride, tacrine, tacrolimus, taliolol, tamoxifen, taurolidine, tazarotene, temazepam, teniposide, tenoxicam, terazosin, terbinafine, terbutaline, terfenadine, terlipressin, tertatolol, tetracyclins, teryzoline, theobromine, theophylline, butizine, thiamazole, phenothiazines, thiotepa, tiagabine, tiapride, propionic acid derivatives, ticlopidine, timolol, timidazole, tioconazole, tioguanine, tioxolone, tiropramide, tizanidine, tolazoline, tolbutamide, tolcapone, tolnaftate, tolperisone, topotecan, torasemide, antioestrogens, tramadol, tramazoline, trandolapril, tranylcypromine, trapidil, trazodone, triamcinolone and triamcinolone derivatives, triamterene, trifluperidol, trifluridine, trimethoprim, trimipramine, tripelennamine, triprolidine, trifosfamide, tromantadine, trometamol, tropalpin, troxerutine, tulobuterol, tyramine, tyrothricin, urapidil, ursodeoxycholic acid, chenodeoxycholic acid, valaciclovir, valproic acid, vancomycin, vecuronium chloride, Viagra, venlafaxine, verapamil, vidarabine, vigabatrin, viloazine, vinblastine, vincamine, vincristine, vindesine, vinorelbine, vinpocetine, viquidil, warfarin, xantinol nicotinate, xipamide, zafirlukast, zalcitabine, zidovudine, zolmitriptan, zolpidem, zoplicone, zotipine and the like. See, e.g., U.S. Pat. No. 6,897,205; see also U.S. Pat. Nos. 6,838,528; 6,497,729.

Examples of therapeutic agents employed in conjunction with the invention include, rapamycin, 40-O-(2-Hydroxyethyl)rapamycin (everolimus), 40-O-Benzyl-rapamycin, 40-O-(4′-Hydroxymethyl)benzyl-rapamycin, 40-O-[4′-(1,2-Dihydroxyethyl)]benzyl-rapamycin, 40-O-Allyl-rapamycin, 40-O-[3′-(2,2-Dimethyl-1,3-dioxolan-4(S)-yl)-prop-2′-en-1′-yl]-rapamycin, (2′:E,4′S)-40-O-(4′,5′-Dihydroxypent-2′-en-1′-yl)-rapamycin, 40-O-(2-Hydroxy)ethoxycar-bonylmethyl-rapamycin, 40-O-(3-Hydroxy)propyl-rapamycin, 40-O-(6-Hydroxy)hexyl-rapamycin, 40-O-[2-(2-Hydroxy)ethoxy]ethyl-rapamycin, 40-O-[(3S)-2,2-Dimethyldioxolan-3-yl]methyl-rapamycin, 40-O-[(2S)-2,3-Dihydroxyprop-1-yl]-rapamycin, 40-O-(2-Acetoxy)ethyl-rapamycin, 40-O-(2-Nicotinoyloxy)ethyl-rapamycin, 40-O-[2-(N-Morpholino)acetoxy]ethyl-rapamycin, 40-O-(2-N-Imidazolylacetoxy)ethyl-rapamycin, 40-O-[2-(N-Methyl-N′-piperazinyl)acetoxy]ethyl-rapamycin, 39-O-Desmethyl-39,40-O,O-ethylene-rapamycin, (26R)-26-Dihydro-40-O-(2-hydroxy)ethyl-rapamycin, 28-O-Methyl-rapamycin, 40-O-(2-Aminoethyl)-rapamycin, 40-O-(2-Acetaminoethyl)-rapamycin, 40-O-(2-Nicotinamidoethyl)-rapamycin, 40-O-(2-(N-Methyl-imidazo-2′-ylcarbethoxamido)ethyl)-rapamycin, 40-O-(2-Ethoxycarbonylaminoethyl)-rapamycin, 40-O-(2-Tolylsulfonamidoethyl)-rapamycin, 40-O-[2-(4′,5′-Dicarboethoxy-1′,2′,3′-triazol-1′-yl)-ethyl]-rapamycin, 42-Epi-(tetrazolyl)rapamycin (tacrolimus), and 42-[3-hydroxy-2-(hydroxymethyl)-2-methylpropanoate]rapamycin (temsirolimus).

The active ingredients may, if desired, also be used in the form of their pharmaceutically acceptable salts or derivatives (meaning salts which retain the biological effectiveness and properties of the compounds of this invention and which are not biologically or otherwise undesirable), and in the case of chiral active ingredients it is possible to employ both optically active isomers and racemates or mixtures of diastereoisomers.

“Stability” as used herein in refers to the stability of the drug in a polymer coating deposited on a substrate in its final product form (e.g., stability of the drug in a coated stent). The term stability will define 5% or less degradation of the drug in the final product form.

“Active biological agent” as used herein refers to a substance, originally produced by living organisms, that can be used to prevent or treat a disease (meaning any treatment of a disease in a mammal, including preventing the disease, i.e. causing the clinical symptoms of the disease not to develop; inhibiting the disease, i.e. arresting the development of clinical symptoms; and/or relieving the disease, i.e. causing the regression of clinical symptoms). It is possible that the active biological agents of the invention may also comprise two or more active biological agents or an active biological agent combined with a pharmaceutical agent, a stabilizing agent or chemical or biological entity. Although the active biological agent may have been originally produced by living organisms, those of the present invention may also have been synthetically prepared, or by methods combining biological isolation and synthetic modification. By way of a non-limiting example, a nucleic acid could be isolated form from a biological source, or prepared by traditional techniques, known to those skilled in the art of nucleic acid synthesis. Furthermore, the nucleic acid may be further modified to contain non-naturally occurring moieties. Non-limiting examples of active biological agents include peptides, proteins, enzymes, glycoproteins, nucleic acids (including deoxyribonucleotide or ribonucleotide polymers in either single or double stranded form, and unless otherwise limited, encompasses known analogues of natural nucleotides that hybridize to nucleic acids in a manner similar to naturally occurring nucleotides), antisense nucleic acids, fatty acids, antimicrobials, vitamins, hormones, steroids, lipids, polysaccharides, carbohydrates and the like. They further include, but are not limited to, antirestenotic agents, antidiabetics, analgesics, antiinflammatory agents, antirheumatics, antihypotensive agents, antihypertensive agents, psychoactive drugs, tranquillizers, antiemetics, muscle relaxants, glucocorticoids, agents for treating ulcerative colitis or Crohn's disease, antiallergics, antibiotics, antiepileptics, anticoagulants, antimycotics, antitussives, arteriosclerosis remedies, diuretics, proteins, peptides, enzymes, enzyme inhibitors, gout remedies, hormones and inhibitors thereof, cardiac glycosides, immunotherapeutic agents and cytokines, laxatives, lipid-lowering agents, migraine remedies, mineral products, otologicals, anti parkinson agents, thyroid therapeutic agents, spasmolytics, platelet aggregation inhibitors, vitamins, cytostatics and metastasis inhibitors, phytopharmaceuticals and chemotherapeutic agents. Preferably, the active biological agent is a peptide, protein or enzyme, including derivatives and analogs of natural peptides, proteins and enzymes.

“Activity” as used herein refers to the ability of a pharmaceutical or active biological agent to prevent or treat a disease (meaning any treatment of a disease in a mammal, including preventing the disease, i.e. causing the clinical symptoms of the disease not to develop; inhibiting the disease, i.e. arresting the development of clinical symptoms; and/or relieving the disease, i.e. causing the regression of clinical symptoms). Thus the activity of a pharmaceutical or active biological agent should be of therapeutic or prophylactic value.

“Secondary, tertiary and quaternary structure” as used herein are defined as follows. The active biological agents of the present invention will typically possess some degree of secondary, tertiary and/or quaternary structure, upon which the activity of the agent depends. As an illustrative, non-limiting example, proteins possess secondary, tertiary and quaternary structure. Secondary structure refers to the spatial arrangement of amino acid residues that are near one another in the linear sequence. The α-helix and the β-strand are elements of secondary structure. Tertiary structure refers to the spatial arrangement of amino acid residues that are far apart in the linear sequence and to the pattern of disulfide bonds. Proteins containing more than one polypeptide chain exhibit an additional level of structural organization. Each polypeptide chain in such a protein is called a subunit. Quaternary structure refers to the spatial arrangement of subunits and the nature of their contacts. For example hemoglobin consists of two α and two β chains. It is well known that protein function arises from its conformation or three dimensional arrangement of atoms (a stretched out polypeptide chain is devoid of activity). Thus one aspect of the present invention is to manipulate active biological agents, while being careful to maintain their conformation, so as not to lose their therapeutic activity.

“Polymer” as used herein, refers to a series of repeating monomeric units that have been cross-linked or polymerized. Any suitable polymer can be used to carry out the present invention. It is possible that the polymers of the invention may also comprise two, three, four or more different polymers. In some embodiments, of the invention only one polymer is used. In some preferred embodiments a combination of two polymers are used. Combinations of polymers can be in varying ratios, to provide coatings with differing properties. Those of skill in the art of polymer chemistry will be familiar with the different properties of polymeric compounds. Examples of polymers that may be used in the present invention include, but are not limited to polycarboxylic acids, cellulosic polymers, proteins, polypeptides, polyvinylpyrrolidone, maleic anhydride polymers, polyamides, polyvinyl alcohols, polyethylene oxides, glycosaminoglycans, polysaccharides, polyesters, polyurethanes, polystyrenes, copolymers, silicones, polyorthoesters, polyanhydrides, copolymers of vinyl monomers, polycarbonates, polyethylenes, polypropylenes, polylactic acids, polyglycolic acids, polycaprolactones, polyhydroxybutyrate valerates, polyacrylamides, polyethers, polyurethane dispersions, polyacrylates, acrylic latex dispersions, polyacrylic acid, mixtures and copolymers thereof. The polymers of the present invention may be natural or synthetic in origin, including gelatin, chitosan, dextrin, cyclodextrin, Poly(urethanes), Poly(siloxanes) or silicones, Poly(acrylates) such as poly(methyl methacrylate), poly(butyl methacrylate), and Poly(2-hydroxy ethyl methacrylate), Poly(vinyl alcohol) Poly(olefins) such as poly(ethylene), poly(isoprene), halogenated polymers such as Poly(tetrafluoroethylene)—and derivatives and copolymers such as those commonly sold as Teflon® products, Poly(vinylidine fluoride), Poly(vinyl acetate), Poly(vinyl pyrrolidone), Poly(acrylic acid), Polyacrylamide, Poly(ethylene-co-vinyl acetate), Poly(ethylene glycol), Poly(propylene glycol), Poly(methacrylic acid); etc. Suitable polymers also include absorbable and/or resorbable polymers including the following, combinations, copolymers and derivatives of the following: Polylactides (PLA), Polyglycolides (PGA), Poly(lactide-co-glycolides) (PLGA), Polyanhydrides, Polyorthoesters, Poly(N-(2-hydroxypropyl) methacrylamide), Poly(1-aspartamide), etc.

“Therapeutically desirable morphology” as used herein refers to the gross form and structure of the pharmaceutical agent, once deposited on the substrate, so as to provide for optimal conditions of ex vivo storage, in vivo preservation and/or in vivo release. Such optimal conditions may include, but are not limited to increased shelf life, increased in vivo stability, good biocompatibility, good bioavailability or modified release rates. Typically, for the present invention, the desired morphology of a pharmaceutical agent would be crystalline or semi-crystalline or amorphous, although this may vary widely depending on many factors including, but not limited to, the nature of the pharmaceutical agent, the disease to be treated/prevented, the intended storage conditions for the substrate prior to use or the location within the body of any biomedical implant. Preferably at least 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90% or 100% of the pharmaceutical agent is in crystalline or semi-crystalline form.

“Stabilizing agent” as used herein refers to any substance that maintains or enhances the stability of the biological agent. Ideally these stabilizing agents are classified as Generally Regarded As Safe (GRAS) materials by the US Food and Drug Administration (FDA). Examples of stabilizing agents include, but are not limited to carrier proteins, such as albumin, gelatin, metals or inorganic salts. Pharmaceutically acceptable excipient that may be present can further be found in the relevant literature, for example in the Handbook of Pharmaceutical Additives: An International Guide to More Than 6000 Products by Trade Name, Chemical, Function, and Manufacturer; Michael and Irene Ash (Eds.); Gower Publishing Ltd.; Aldershot, Hampshire, England, 1995.

“Compressed fluid” as used herein refers to a fluid of appreciable density (e.g., >0.2 g/cc) that is a gas at standard temperature and pressure. “Supercritical fluid”, “near-critical fluid”, “near-supercritical fluid”, “critical fluid”, “densified fluid” or “densified gas” as used herein refers to a compressed fluid under conditions wherein the temperature is at least 80% of the critical temperature of the fluid and the pressure is at least 50% of the critical pressure of the fluid.

Examples of substances that demonstrate supercritical or near critical behavior suitable for the present invention include, but are not limited to carbon dioxide, isobutylene, ammonia, water, methanol, ethanol, ethane, propane, butane, pentane, dimethyl ether, xenon, sulfur hexafluoride, halogenated and partially halogenated materials such as chlorofluorocarbons, hydrochlorofluorocarbons, hydrofluorocarbons, perfluorocarbons (such as perfluoromethane and perfluoropropane, chloroform, trichloro-fluoromethane, dichloro-difluoromethane, dichloro-tetrafluoroethane) and mixtures thereof.

“Sintering” as used herein refers to the process by which parts of the matrix or the entire polymer matrix becomes continuous (e.g., formation of a continuous polymer film). As discussed below, the sintering process is controlled to produce a fully conformal continuous matrix (complete sintering) or to produce regions or domains of continuous coating while producing voids (discontinuities) in the matrix. As well, the sintering process is controlled such that some phase separation is obtained between polymer different polymers (e.g., polymers A and B) and/or to produce phase separation between discrete polymer particles. Through the sintering process, the adhesions properties of the coating are improved to reduce flaking of detachment of the coating from the substrate during manipulation in use. As described below, in some embodiments, the sintering process is controlled to provide incomplete sintering of the polymer matrix. In embodiments involving incomplete sintering, a polymer matrix is formed with continuous domains, and voids, gaps, cavities, pores, channels or, interstices that provide space for sequestering a therapeutic agent which is released under controlled conditions. Depending on the nature of the polymer, the size of polymer particles and/or other polymer properties, a compressed gas, a densified gas, a near critical fluid or a super-critical fluid may be employed. In one example, carbon dioxide is used to treat a substrate that has been coated with a polymer and a drug, using dry powder and RESS electrostatic coating processes. In another example, isobutylene is employed in the sintering process. In other examples a mixture of carbon dioxide and isobutylene is employed.

When an amorphous material is heated to a temperature above its glass transition temperature, or when a crystalline material is heated to a temperature above a phase transition temperature, the molecules comprising the material are more mobile, which in turn means that they are more active and thus more prone to reactions such as oxidation. However, when an amorphous material is maintained at a temperature below its glass transition temperature, its molecules are substantially immobilized and thus less prone to reactions. Likewise, when a crystalline material is maintained at a temperature below its phase transition temperature, its molecules are substantially immobilized and thus less prone to reactions. Accordingly, processing drug components at mild conditions, such as the deposition and sintering conditions described herein, minimizes cross-reactions and degradation of the drug component. One type of reaction that is minimized by the processes of the invention relates to the ability to avoid conventional solvents which in turn minimizes autoxidation of drug, whether in amorphous, semi-crystalline, or crystalline form, by reducing exposure thereof to free radicals, residual solvents and autoxidation initiators.

“Rapid Expansion of Supercritical Solutions” or “RESS” as used herein involves the dissolution of a polymer into a compressed fluid, typically a supercritical fluid, followed by rapid expansion into a chamber at lower pressure, typically near atmospheric conditions. The rapid expansion of the supercritical fluid solution through a small opening, with its accompanying decrease in density, reduces the dissolution capacity of the fluid and results in the nucleation and growth of polymer particles. The atmosphere of the chamber is maintained in an electrically neutral state by maintaining an isolating “cloud” of gas in the chamber. Carbon dioxide or other appropriate gas is employed to prevent electrical charge is transferred from the substrate to the surrounding environment.

“Bulk properties” properties of a coating including a pharmaceutical or a biological agent that can be enhanced through the methods of the invention include for example: adhesion, smoothness, conformality, thickness, and compositional mixing.

The present invention provides several advantages which overcome or attenuate the limitations of current technology for bioabsorbable stents. For example, an inherent limitation of conventional bioabsorbable polymeric materials relates to the difficulty in forming to a strong, flexible, deformable (e.g. balloon deployable) stent with low profile. The polymers generally lack the strength of high-performance metals. The present invention overcomes these limitations by creating a laminate structure in the essentially polymeric stent. Without wishing to be bound by any specific theory or analogy, the increased strength provided by the stents of the invention can be understood by comparing the strength of plywood vs. the strength of a thin sheet of wood.

Embodiments of the invention involving a thin metallic stent-framework provide advantages including the ability to overcome the inherent elasticity of most polymers. It is generally difficult to obtain a high rate (e.g., 100%) of plastic deformation in polymers (compared to elastic deformation where the materials have some ‘spring back’ to the original shape). Again, without wishing to be bound by any theory, the central metal stent framework (that would be too small and weak to serve as a stent itself) would act like wires inside of a plastic, deformable stent, basically overcoming any ‘elastic memory’ of the polymer.

EXAMPLES

The following examples are given to enable those skilled in the art to more clearly understand and to practice the present invention. They should not be considered as limiting the scope of the invention, but merely as being illustrative and representative thereof. The following examples are provided to illustrate selected embodiments. They should not be considered as limiting the scope of the invention, but merely as being illustrative and representative thereof. Thus, the examples provided below, while illustrated with a particular medical device or active agent, are applicable to the range of medical devices and active agents described herein.

Polymer Stent

Example 1
Gel Spun Polymer Fibers

Spinning is manufacturing process for creating polymer fibers. It is a specialized form of extrusion that uses a spinneret to form multiple continuous filaments. First, the polymer being spun must be converted into a fluid state. If the polymer is a thermoplastic then it is just melted, if not then it may be dissolved in a solvent or chemically treated to form soluble or thermoplastic derivatives.

In this non-limiting example, the polymer material for the bioabsorbable stent is formed by gel spinning, also known as dry-wet spinning. The polymer is in a “gel” state, only partially liquid, which keeps the polymer chains somewhat bound together. These bonds produce strong inter-chain forces in the fiber, which increase its tensile strength. The polymer chains within the fibers also have a large degree of orientation, which increases strength.

The fluid polymer is then forced through the spinneret to form polymer filaments. The polymer filaments first pass through air and are cooled further in a liquid bath. This produces strong inter-chain forces in the resulting filaments that can significantly increase the tensile strength of the fibers. In addition, at least a portion of the polymer chains are aligned along the fiber axis by the shear forces during extrusion, which further enhances strength.

Example 2
Bioabsorbable Stent Formation

In this non-limiting example, the tubular scaffold of the present disclosure is made by forming a continuous wave form that includes a plurality of struts and a plurality of crowns. Each crown is a curved portion or turn within the wave form that connects adjacent struts to define the continuous wave form. In this example, the struts are substantially straight portions of the wave form 12. In other examples, the struts 18 are slightly bent or have other shapes, such as a sinusoidal wave, for example. The wave form may be formed by a single polymer fiber or filament or a plurality of interconnected polymer fibers or filaments.

The tubular scaffold also includes a plurality of connections that are configured to connect selected crowns of adjacent turns. In this non-limiting example, the connections are be created by fusing the selected crowns together. As used herein, “fusing” is defined as heating the target portions of materials to be fused together, with or without adding any additional material, to a level where the material in the target portions flow together, intermix with one another, and form a fusion when the materials cool down to, for example, room temperature.

Example 3
Radial Strength Testing

This test is conducted to determine and graphically represent the change in stent internal diameter as a function of circumferential pressure and to determine the pressure at which deformation is no longer completely reversible for the disclosed stent. Fifteen (15) 3.0 mm and fifteen (15) 4.0 mm stents are subjected to all stent-manufacturing procedures. The stents are deployed to nominal pressure and removed from the delivery system. The stents are placed into a sleeve approximately 1 mm larger than the stent diameter. A vacuum is then applied and outer diameter measurements taken at various pressures. All samples should maintain a minimum of at least 50 percent of the nominal stent diameter after a 50 mm Hg pressure is applied.

Example 4
Stent Recoil Testing

This test is conducted to quantify the amount of elastic recoil. Fifteen (15) stent delivery systems of each length and diameter are subjected to all manufacturing and sterilization procedures. The stent delivery system is inflated to nominal pressure (e.g. 9ATM) and the stent is removed allowing for recoil to occur. The inner diameter at each end of the stent is recorded. Recoil is calculated subtracting the recoiled stent inner diameter from the pre-recoil inner diameter. Average recoil may ranged from 0.002 to 0.004 inches.

Example 5
Stent Expansion Testing

This test is conducted to determine if the plastic deformation experienced by the stent when expanded from the compressed profile to the final maximum deployed diameter can produce crack initiation for the disclosed stent. Fifteen (15) samples from each length and diameter are deployed to their largest possible diameters by inflating each delivery system to balloon failure. Each stent is examined at 45× magnification for potential cracks.

Example 6
Maximum Pressure (Burst Test) Testing

This test is conducted to demonstrate that the delivery system (with mounted stent) will not experience balloon, shaft, proximal adaptation or proximal/distal seal loss of integrity at or below the pressure required to expand the stent to its labeled diameter. Stent delivery systems that had been subjected to all manufacturing and sterilization procedures are pressurized to 90 psi with pressure held for 15 seconds and released for 3 seconds. The cycle is then repeated, increasing inflation pressure by 15 psi each cycle until failure.

Example 7
Analysis of the Strut Thickness

Scanning Electron Microscopy (SEM)

A sample coated stent described herein is obtained. Thickness of the device can be assessed using this analytical technique. The thickness of multiple struts were taken to ensure reproducibility and to characterize the coating and stent. The thickness of the coating was observed by SEM using a Hitachi S-4800 with an accelerating voltage of 800V. Various magnifications are used. SEM can provide top-down and cross-section images at various magnifications.

Nano X-Ray Computer Tomography

Another technique that may be used to view the physical structure of a device in 3-D is Nano X-Ray Computer Tomography (e.g. such as made by SkyScan).

Example 8
Determination of the Bioabsorbability of a Device

Techniques presented with respect to showing Bioabsorbability of a polymer coating may be used to additionally and/or alternatively show the bioabsorbability of a device, for example, by GPC In-Vivo testing, HPLC In-Vivo Testing, GPC In-Vitro testing, HPLC In-Vitro Testing, SEM-FIB Testing, Raman Spectroscopy, SEM, and XPS as described herein with variations and adjustments which would be obvious to those skilled in the art. Another technique to view the physical structure of a device in 3-D is Nano X-Ray Computer Tomography (e.g. such as made by SkyScan), which could be used in an elution test and/or bioabsorbability test, as described herein to show the physical structure of the coating remaining on stents at each time point, as compared to a scan prior to elution/bioabsorbtion.

Drug Elution Polymer Stent

Example 11
Determination of an Elution Profile

In Vitro

In one method, a stent described herein is obtained. The elution profile is determined as follows: stents are placed in 16 mL test tubes and 15 mL of 10 mM PBS (pH 7.4) is pipetted on top. The tubes are capped and incubated at 37 C with end-over-end rotation at 8 rpm. Solutions are then collected at the designated time points (e.g. 1 d, 7 d, 14 d, 21 d, and 28 d) (e.g. 1 week, 2 weeks, and 10 weeks) and replenished with fresh 1.5 ml solutions at each time point to prevent saturation. One mL of DCM is added to the collected sample of buffer and the tubes are capped and shaken for one minute and then centrifuged at 200.times.G for 2 minutes. The supernatant is discarded and the DCM phase is evaporated to dryness under gentle heat (40.degree. C.) and nitrogen gas. The dried DCM is reconstituted in 1 mL of 60:40 acetonitrile:water (v/v) and analyzed by HPLC. HPLC analysis is performed using Waters HPLC system (mobile phase 58:37:5 acetonitrile:water:methanol 1 mL/min, 20 uL injection, C18 Novapak Waters column with detection at 232 nm).

In another method, the in vitro pharmaceutical agent elution profile is determined by a procedure comprising contacting the device with an elution media comprising ethanol (5%) wherein the pH of the media is about 7.4 and wherein the device is contacted with the elution media at a temperature of about 37.degree. C. The elution media containing the device is optionally agitating the elution media during the contacting step. The device is removed (and/or the elution media is removed) at least at designated time points (e.g. 1 h, 3 h, 5 h, 7 h, 1 d, and daily up to 28 d) (e.g. 1 week, 2 weeks, and 10 weeks). The elution media is then assayed using a UV-Vis for determination of the pharmaceutical agent content. The elution media is replaced at each time point with fresh elution media to avoid saturation of the elution media. Calibration standards containing known amounts of drug were also held in elution media for the same durations as the samples and used at each time point to determine the amount of drug eluted at that time (in absolute amount and as a cumulative amount eluted).

In another method, the in vitro pharmaceutical agent elution profile is determined by a procedure comprising contacting the device with an elution media comprising ethanol (20%) and phosphate buffered saline (80%) wherein the pH of the media is about 7.4 and wherein the device is contacted with the elution media at a temperature of about 37.degree. C. The elution media containing the device is optionally agitating the elution media during the contacting step. The device is removed (and/or the elution media is removed) at least at designated time points (e.g. 1 h, 3 h, 5 h, 7 h, 1 d, and daily up to 28 d) (e.g. 1 week, 2 weeks, and 10 weeks). The elution media is replaced periodically (at least at each time point, and/or daily between later time points) to prevent saturation; the collected media are pooled together for each time point. The elution media is then assayed for determination of the pharmaceutical agent content using HPLC. The elution media is replaced at each time point with fresh elution media to avoid saturation of the elution media. Calibration standards containing known amounts of drug are also held in elution media for the same durations as the samples and used at each time point to determine the amount of drug eluted at that time (in absolute amount and as a cumulative amount eluted). Where the elution method changes the drug over time, resulting in multiple peaks present for the drug when tested, the use of these calibration standards will also show this change, and allows for adding all the peaks to give the amount of drug eluted at that time period (in absolute amount and as a cumulative amount eluted).

To obtain an accelerated in-vitro elution profile, an accelerated elution buffer comprising 18% v/v of a stock solution of 0.067 mol/L KH₂PO₄and 82% v/v of a stock solution of 0.067 mol/L Na2HPO4 with a pH of 7.4 is used. Stents described herein are expanded and then placed in 1.5 ml solution of this accelerated elution in a 70 degree Celsius bath with rotation at 70 rpm. The solutions are then collected at the following time points: 0 min, 15 min., 30 min., 1 hr, 2 hr, 4 hr, 6 hr, 8 hr, 12 hr, 16 hr, 20 hr, 24 hr, 30 hr, 36 hr and 48 hr. Fresh accelerated elution buffer are added periodically at least at each time point to replace the incubated buffers that are collected and saved in order to prevent saturation. For time points where multiple elution media are used (refreshed between time points), the multiple collected solutions are pooled together for liquid extraction by dichloromethane. Dichloromethane extraction and HPLC analysis is performed in the manner described previously.

In Vivo

Rabbit in vivo models as described above are euthanized at multiple time points. Stents are explanted from the rabbits. The explanted stents are placed in 16 mL test tubes and 15 mL of 10 mM PBS (pH 7.4) is pipette on top. One mL of DCM is added to the buffer and the tubes are capped and shaken for one minute and then centrifuged at 200.times.G for 2 minutes. The supernatant is discarded and the DCM phase is evaporated to dryness under gentle heat (40.degree. C.) and nitrogen gas. The dried DCM is reconstituted in 1 mL of 60:40 acetonitrile:water (v/v) and analyzed by HPLC. HPLC analysis is performed using Waters HPLC system (mobile phase 58:37:5 acetonitrile:water:methanol 1 mL/min, 20 uL injection, C18 Novapak Waters column with detection at 232 nm).

Example 12
Crystallinity of Drug

The presence and or quantification of the active agent crystallinity can be determined from a number of characterization methods known in the art, but not limited to, XRPD, vibrational spectroscopy (FTIR, NIR, Raman), polarized optical microscopy, calorimetry, thermal analysis and solid-state NMR.

X-Ray Diffraction to Determine the Presence and/or Quantification of Active Agent Crystallinity

Active agent and polymer coated proxy substrates are prepared using 316L stainless steel coupons for X-ray powder diffraction (XRPD) measurements to determine the presence of crystallinity of the active agent. The coating on the coupons is equivalent to the coating on the stents described herein. Coupons of other materials described herein, such as cobalt-chromium alloys, may be similarly prepared and tested. Likewise, substrates such as stents, or other medical devices described herein may be prepared and tested. Where a coated stent is tested, the stent may be cut lengthwise and opened to lay flat in a sample holder.

For example XRPD analyses are performed using an X-ray powder diffractometer (for example, a Bruker D8 Advance X-ray diffractometer) using Cu Kα radiation. Diffractograms are typically collected between 2 and 40 degrees 2 theta. Where required low background XRPD sample holders are employed to minimize background noise.

The diffractograms of the deposited active agent are compared with diffractograms of known crystallized active agents, for example micronized crystalline sirolimus in powder form. XRPD patterns of crystalline forms show strong diffraction peaks whereas amorphous show diffuse and non-distinct patterns. Crystallinity is shown in arbitrary Intensity units.

A related analytical technique which may also be used to provide crystallinity detection is wide angle scattering of radiation (e.g.; Wide Angle X-ray Scattering or WAXS), for example, as described in F. Unger, et al., “Poly(ethylene carbonate): A thermoelastic and biodegradable biomaterial for drug eluting stent coatings?” Journal of Controlled Release, Volume 117, Issue 3, 312-321 (2007) for which the technique and variations of the technique specific to a particular sample would be obvious to one of skill in the art.

Raman Spectroscopy

Raman spectroscopy, a vibrational spectroscopy technique, can be useful, for example, in chemical identification, characterization of molecular structures, effects of bonding, identification of solid state form, environment and stress on a sample. Raman spectra can be collected from a very small volume (<1 μm³); these spectra allow the identification of species present in that volume. Spatially resolved chemical information, by mapping or imaging, terms often used interchangeably, can be achieved by Raman microscopy.

Raman spectroscopy and other analytical techniques such as described in Balss, et al., “Quantitative spatial distribution of sirolimus and polymers in drug-eluting stents using confocal Raman microscopy” J. of Biomedical Materials Research Part A, 258-270 (2007), incorporated in its entirety herein by reference, and/or described in Belu et al., “Three-Dimensional Compositional Analysis of Drug Eluting Stent Coatings Using Cluster Secondary Ion Mass Spectroscopy” Anal. Chem. 80: 624-632 (2008) incorporated herein in its entirety by reference may be used.

For example, to test a sample using Raman microscopy and in particular confocal Raman microscopy, it is understood that to get appropriate Raman high resolution spectra sufficient acquisition time, laser power, laser wavelength, sample step size and microscope objective need to be optimized. For example a sample (a coated stent) is prepared as described herein. Alternatively, a coated coupon could be tested in this method. Maps are taken on the coating using Raman microscopy. A WITec CRM 200 scanning confocal Raman microscope using a Nd:YAG laser at 532 nm is applied in the Raman imaging mode. The laser light is focused upon the sample using a 100× dry objective (numerical aperture 0.90), and the finely focused laser spot is scanned into the sample. As the laser scans the sample, over each 0.33 micron interval a Raman spectrum with high signal to noise is collected using 0.3 seconds of integration time. Each confocal cross-sectional image of the coatings displays a region 70 μm wide by 10 μm deep, and results from the gathering of 6300 spectra with a total imaging time of 32 min.

Multivariate analysis using reference spectra from samples of rapamycin (amorphous and crystalline) and polymer are used to deconvolve the spectral data sets, to provide chemical maps of the distribution.

Infrared (IR) Spectroscopy for In-Vitro Testing

Infrared (IR) Spectroscopy such as FTIR and ATR-IR are well utilized techniques that can be applied to show, for example, the quantitative drug content, the distribution of the drug in the sample coating, the quantitative polymer content in the coating, and the distribution of polymer in the coating. Infrared (IR) Spectroscopy such as FTIR and ATR-IR can similarly be used to show, for example, drug crystallinity. The following table lists the typical IR materials for various applications. These IR materials are used for IR windows, diluents or ATR crystals.

MATERIAL
NACL
KBR
CSI
AGCL
GE
ZNSE
DIAMOND

Transmission
40,000~625
40,000~400
40,000~200
25,000~360
5,500~625
20,000~454
40,000~2,500 &

range (cm−1)

1667-33

Water sol
35.7
53.5
44.4
Insol.
Insol.
Insol.
Insol.

(g/100 g, 25 C.)

Attacking
Wet
Wet
Wet
Ammonium
H2SO4,
Acids,
K2Cr2Os,

materials
Solvents
Solvents
Solvents
Salts
aqua
strong
conc.

regin
alkalies,
H2SO4

chlorinated

solvents

In one test, a coupon of crystalline ZnSe is coated by the processes described herein, creating a PDPDP (Polymer, Drug, Polymer, Drug, Polymer) layered coating that is about 10 microns thick. The coated coupon is analyzed using FTIR. The resulting spectrum shows crystalline drug as determined by comparison to the spectrum obtained for the crystalline form of a drug standard (i.e. a reference spectrum).

Differential Scanning Calorimetry (DSC)

DSC can provide qualitative evidence of the crystallinity of the drug (e.g. rapamycin) using standard DSC techniques obvious to one of skilled in the art. Crystalline melt can be shown using this analytical method (e.g. rapamycin crystalline melting—at about 185° C. to 200° C., and having a heat of fusion at or about 46.8 J/g). The heat of fusion decreases with the percent crystallinity. Thus, the degree of crystallinity could be determined relative to a pure sample, or versus a calibration curve created from a sample of amorphous drug spiked and tested by DSC with known amounts of crystalline drug. Presence (at least) of crystalline drug on a stent could be measured by removing (scraping or stripping) some drug from the stent and testing the coating using the DSC equipment for determining the melting temperature and the heat of fusion of the sample as compared to a known standard and/or standard curve.

Confocal Raman Microscopy

Confocal Raman Microscopy can provide nondestructive depth analysis and allows coating specific Raman spectral features to be obtained (Bugay et al., “Raman Analysis of Pharmaceuticals,” in “Applications of Vibrational Spectroscopy in Pharmaceutical Research and Development,” Ed. Pivonka, D. E., Chalmers, J. M., Griffiths, P. R. (2007) Wiley and Sons). In confocal Raman microscopy an aperture is place in a focal place of the collected beam. This limitation defines a shallow portion of the depth of field and thereby provides definition of the z-axis spatial resolution for data collection. By adjusting the aperture and moving the focus within the sample, the sampling position within the sample moves. Moving the sample focus from the top surface, deeper into the specimen facilitates nondestructive depth analysis.

Example 13
Coating Uniformity

The ability to uniformly coat devices, e.g., pre- and post-expansion stents, and balloons, with controlled composition and thickness using electrostatic capture in a rapid expansion of supercritical solution (RESS) experimental series has been demonstrated.

Scanning Electron Microscopy (SEM)

Devices are observed by SEM using a Hitachi S-4800 with an accelerating voltage of 800V. Various magnifications are used to evaluate the integrity, especially at high strain regions. SEM can provide top-down and cross-section images at various magnifications. Coating uniformity and thickness can also be assessed using this analytical technique.

Pre- and post-inflation balloons, for example, may be observed by SEM using a Hitachi S-4800 with an accelerating voltage of 800V. Various magnifications may be used to evaluate the integrity of the layers, and or of the coating.

Scanning Electron Microscopy (SEM) with Focused Ion Beam (FIB)

Devices as described herein, and or produced by methods described herein are visualized using SEM-FIB analysis. Alternatively, a coated coupon could be tested in this method. Focused ion beam FIB is a tool that allows precise site-specific sectioning, milling and depositing of materials. FIB can be used in conjunction with SEM, at ambient or cryo conditions, to produce in-situ sectioning followed by high-resolution imaging. Cross-sectional FIB images may be acquired, for example, at 7000× and/or at 20000× magnification. An even coating of consistent thickness is visible.

Optical Microscopy

An optical microscope may be used to create and inspect the devices and to empirically survey the coating of the substrate (e.g. coating uniformity). Nanoparticles of the drug and/or the polymer can be seen on the surfaces of the substrate using this analytical method. Following sintering, the coatings can be see using this method to view the coating conformality and for evidence of crystallinity of the drug.

Example 14
Total Drug Content on Coated Stent (Used or Unused)

Determination of the total content of the active agent in a coated substrate may be tested using techniques described herein as well as other techniques obvious to one of skill in the art, for example using GPC and HPLC techniques to extract the drug from the coated substrate and determine the total content of drug in the sample.

UV-VIS can be used to quantitatively determine the mass of rapamycin (or another active agent) coated onto the substrates. A UV-Vis spectrum of Rapamycin can be shown and a Rapamycin calibration curve can be obtained, (e.g. λ@ 277 nm in ethanol). Rapamycin is then dissolved from the coated substrate in ethanol, and the drug concentration and mass calculated.

In one test, the total amount of rapamycin (or another active agent) present in units of micrograms per substrate is determined by reverse phase high performance liquid chromatography with UV detection (RP-HPLC-UV). The analysis is performed with modifications of literature-based HPLC methods for rapamycin (or the other active agent) that would be obvious to a person of skill in the art. The average drug content of samples (n=10) from devices comprising stents and coatings as described herein, and/or methods described herein are tested.

While preferred embodiments of the present invention have been shown and described herein, it will be obvious to those skilled in the art that such embodiments are provided by way of example only. Numerous variations, changes, and substitutions will now occur to those skilled in the art without departing from the invention. It should be understood that various alternatives to the embodiments of the invention described herein may be employed in practicing the invention. It is intended that the following claims define the scope of the invention and that methods and structures within the scope of these claims and their equivalents be covered thereby.

Claims

1. A biomedical implant, comprising: a tubular scaffold comprising a plurality of interconnected bioabsorbable polymer struts, the interconnected polymer struts defining a plurality of deformable cells, said polymer struts including polymer chains that are longitudinally aligned along the axis of said polymer struts, and wherein the tubular scaffold has an average axial elastic modulus along an axis of the tubular scaffold and an average circumferential elastic modulus orthogonally surrounding the axis of the tubular scaffold, the average circumferential elastic modulus being greater than the average axial elastic modulus; anda pharmaceutical agent admixed with the bioabsorbable polymer struts of the implant in a manner which does not affect the structural and morphological integrity of the pharmaceutical agent, the pharmaceutical agent being a macrolide immunosuppressant drug in crystalline form,wherein the polymer struts have an average thickness of no more than 120 μm and wherein the pharmaceutical agent is dispersed within and evenly distributed throughout the volume of the polymer struts such that the entirety of the implant is bioabsorbable.
2. The biomedical implant of claim 1, wherein the tubular scaffold maintains at least 50% of its nominal luminal cross sectional area under a pressure load of 50 mmHg.
3. The biomedical implant of claim 1, wherein at least 80% of the polymer struts are bioabsorbed within 2 years after deployment in vivo.
4. The biomedical implant of claim 1, wherein the polymer struts comprises a polymer material selected from the group consisting of polycarboxylic acids, cellulosic polymers, proteins, polypeptides, polyvinylpyrrolidone, maleic anhydride polymers, polyamides, polyvinyl alcohols, polyethylene oxides, glycosaminoglycans, polysaccharides, polyesters, aliphatic polyesters, polyurethanes, polystyrenes, copolymers, silicones, silicone containing polymers, polyalkyl siloxanes, polyorthoesters, polyanhydrides, copolymers of vinyl monomers, polycarbonates, polyethylenes, polypropytenes, polylactic acids, polylactides, polyglycolic acids, polyglycolides, polylactide-co-glycolides, polycaprolactones, poly(e-caprolactone)s, polyhydroxybutyrate valerates, polyacrylamides, polyethers, polyurethane dispersions, polyacrylates, acrylic latex dispersions, polyacrylic acid, polyalkyl methacrylates, polyalkylene-co-vinyl acetates, polyalkylenes, aliphatic polycarbonates polyhydroxyalkanoates, polytetrahalooalkylenes, poly(phosphasones), polytetrahalooalkylenes, poly(phosphasones), and mixtures, combinations, and copolymers thereof.
5. The biomedical implant of claim 1, wherein the macrolide immunosuppressant is selected from the group consisting of rapamycin, 40-O-(2-Hydroxyethyl)rapamycin (everolimus), 40-O-Benzyl-rapamycin, 40-O-(4′-Hydroxymethyl)benzyl-rapamycin, 40-O-[4′-(1,2-Dihydroxyethyl)]benzyl-rapamycin, 40-O-Allyl-rapamycin, 40-O-[3′-(2,2-Dimethyl-1,3-dioxolan-4(S)-yl)-prop-2′-en-1′-yl]-rapamycin, (2′:E,4′S)-40-O-(4′,5′-Dihydroxypent-2′-en-1′-yl)-rapamycin, 40-O-(2-Hydroxy)ethoxycar-bonylmethyl-rapamycin, 40-O-(3-Hydroxy)propyl-rapamycin, 40-O-(6-Hydroxy)hexyl-rapamycin, 40-O-[2-(2-Hydroxy)ethoxy]ethyl-rapamycin, 40-O-[(3S)-2,2-Dimethyldioxolan-3-yl]methyl-rapamycin, 40-O-[(2S)-2,3-Dihydroxyprop-1-yl]-rapamycin, 40-O-(2-Acetoxy)ethyl-rapamycin, 40-O-(2-Nicotinoyloxy)ethyl-rapamycin, 40-O-[2-(N-Morpholino)acetoxy]ethyl-rapamycin, 40-O-(2-N-Imidazolylacetoxy)ethyl-rapamycin, 40-O-[2-(N-Methyl-N′-piperazinyl)acetoxy]ethyl-rapamycin, 39-O-Desmethyl-39,40-O,O-ethylene-rapamycin, (26R)-26-Dihydro-40-O-(2-hydroxy)ethyl-rapamycin, 28-O-Methyl-rapamycin, 40-O-(2-Aminoethyl)-rapamycin, 40-O-(2-Acetaminoethyl)-rapamycin, 40-O-(2-Nicotinamidoethyl)-rapamycin, 40-O-(2-(N-Methyl-imidazo-2′-ylcarbethoxamido)ethyl)-rapamycin, 40-O-(2-Ethoxycarbonylaminoethyl)-rapamycin, 40-O-(2-Tolylsulfonamidoethyl)-rapamycin, 40-O-[2-(4′,5′-Dicarboethoxy-1′,2′,3′-triazol-1′-yl)-ethyl]-rapamycin, 42-Epi-(tetrazolyl)rapamycin (tacrolimus), and 42-[3-hydroxy-2-(hydroxymethyl)-2-methylpropanoate]rapamycin.
6. The biomedical implant of claim 1, wherein the pharmaceutical agent is rapamycin.
7. The biomedical implant of claim 1, wherein at least a portion of the tubular scaffold is covered with a coating comprising a second pharmaceutical agent.
8. The biomedical implant of claim 1, wherein the tubular scaffold has an average axial elastic modulus along an axis of the tubular scaffold and an average circumferential elastic modulus orthogonally surrounding the axis of the tubular scaffold, the average circumferential elastic modulus being greater than the average axial elastic modulus.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application No. 61/777,230, filed Mar. 12, 2013, which application is incorporated herein by reference.

US Referenced Citations (552)

Number	Name	Date	Kind
3087860	Endicott	Apr 1963	A
3123077	Alcamo	Mar 1964	A
3457280	Schmitt et al.	Jul 1969	A
3597449	Deprospero et al.	Aug 1971	A
3737337	Schnoring et al.	Jun 1973	A
3773919	Boswell et al.	Nov 1973	A
3929992	Sehgal et al.	Dec 1975	A
4000137	Dvonch et al.	Dec 1976	A
4188373	Krezanoski	Feb 1980	A
4285987	Ayer et al.	Aug 1981	A
4326532	Hammar	Apr 1982	A
4336381	Nagata et al.	Jun 1982	A
4389330	Tice et al.	Jun 1983	A
4474572	McNaughton et al.	Oct 1984	A
4474751	Haslam et al.	Oct 1984	A
4478822	Haslam et al.	Oct 1984	A
4530840	Tice et al.	Jul 1985	A
4582731	Smith	Apr 1986	A
4606347	Fogarty et al.	Aug 1986	A
4617751	Johansson	Oct 1986	A
4655771	Wallsten	Apr 1987	A
4675189	Kent et al.	Jun 1987	A
4733665	Palmaz	Mar 1988	A
4734227	Smith	Mar 1988	A
4734451	Smith	Mar 1988	A
4758435	Schaaf	Jul 1988	A
4762593	Youngner	Aug 1988	A
4931037	Wetterman	Jun 1990	A
4950239	Gahara	Aug 1990	A
4985625	Hurst	Jan 1991	A
5000519	Moore	Mar 1991	A
5090419	Palestrant	Feb 1992	A
5096848	Kawamura	Mar 1992	A
5102417	Palmaz	Apr 1992	A
5104404	Wolff	Apr 1992	A
5106650	Hoy et al.	Apr 1992	A
5125570	Jones	Jun 1992	A
5158986	Cha et al.	Oct 1992	A
5185776	Townsend	Feb 1993	A
5195969	Wang et al.	Mar 1993	A
5243023	Dezern	Sep 1993	A
5270086	Hamlin	Dec 1993	A
5288711	Mitchell et al.	Feb 1994	A
5320634	Vigil et al.	Jun 1994	A
5324049	Mistrater et al.	Jun 1994	A
5340614	Perman et al.	Aug 1994	A
5350361	Tsukashima et al.	Sep 1994	A
5350627	Nemphos et al.	Sep 1994	A
5342621	Eury	Oct 1994	A
5356433	Rowland et al.	Oct 1994	A
5360403	Mische	Nov 1994	A
5362718	Skotnicki et al.	Nov 1994	A
5366504	Andersen et al.	Nov 1994	A
5368045	Clement et al.	Nov 1994	A
5372676	Lowe	Dec 1994	A
5385776	Maxfield et al.	Jan 1995	A
5387313	Thoms	Feb 1995	A
5403347	Roby et al.	Apr 1995	A
5470603	Staniforth et al.	Nov 1995	A
5494620	Liu et al.	Feb 1996	A
5500180	Anderson et al.	Mar 1996	A
5545208	Wolff et al.	Aug 1996	A
5556383	Wang et al.	Sep 1996	A
5562922	Lambert	Oct 1996	A
5569463	Helmus et al.	Oct 1996	A
5570537	Black et al.	Nov 1996	A
5578709	Woiszwillo	Nov 1996	A
5599576	Opolski	Feb 1997	A
5605696	Eury et al.	Feb 1997	A
5607442	Fischell et al.	Mar 1997	A
5609629	Fearnot et al.	Mar 1997	A
5626611	Liu et al.	May 1997	A
5626862	Brem et al.	May 1997	A
5632772	Alcime et al.	May 1997	A
5669932	Fischell et al.	Sep 1997	A
5674192	Sahatjian et al.	Oct 1997	A
5674242	Phan et al.	Oct 1997	A
5674286	D'Alessio et al.	Oct 1997	A
5725570	Heath	Mar 1998	A
5733303	Israel et al.	Mar 1998	A
5766158	Opolski	Jun 1998	A
5800511	Mayer	Sep 1998	A
5807404	Richter	Sep 1998	A
5811032	Kawai et al.	Sep 1998	A
5824049	Ragheb et al.	Oct 1998	A
5837313	Ding et al.	Nov 1998	A
5843120	Israel et al.	Dec 1998	A
5871436	Eury	Feb 1999	A
5873904	Ragheb et al.	Feb 1999	A
5876426	Kume et al.	Mar 1999	A
5876452	Athanasiou	Mar 1999	A
5913895	Burpee et al.	Jun 1999	A
5924631	Rodrigues et al.	Jul 1999	A
5948020	Yoon et al.	Sep 1999	A
5957975	Lafont et al.	Sep 1999	A
5981568	Kunz et al.	Nov 1999	A
5981719	Woiszwillo et al.	Nov 1999	A
6013855	McPherson et al.	Jan 2000	A
6036978	Gombotz et al.	Mar 2000	A
6039721	Johnson et al.	Mar 2000	A
6068656	Von Oepen	May 2000	A
6071308	Ballou et al.	Jun 2000	A
6077880	Castillo et al.	Jun 2000	A
6090925	Woiszwillo et al.	Jul 2000	A
6099562	Ding et al.	Aug 2000	A
6129755	Mathis et al.	Oct 2000	A
6143037	Goldsten et al.	Nov 2000	A
6143314	Chandrashekar et al.	Nov 2000	A
6146356	Wang et al.	Nov 2000	A
6146404	Kim et al.	Nov 2000	A
6147135	Yuan et al.	Nov 2000	A
6153252	Hossainy et al.	Nov 2000	A
6171327	Daniel et al.	Jan 2001	B1
6190699	Luzzi et al.	Feb 2001	B1
6193744	Ehr et al.	Feb 2001	B1
6206914	Soykan et al.	Mar 2001	B1
6217608	Penn et al.	Apr 2001	B1
6231599	Ley	May 2001	B1
6231600	Zhong et al.	May 2001	B1
6245104	Alt	Jun 2001	B1
6248127	Shah et al.	Jun 2001	B1
6248129	Froix	Jun 2001	B1
6251980	Lan et al.	Jun 2001	B1
6268053	Woiszwillo et al.	Jul 2001	B1
6273913	Wright et al.	Aug 2001	B1
6284758	Egi et al.	Sep 2001	B1
6299635	Frantzen	Oct 2001	B1
6309669	Setterstrom et al.	Oct 2001	B1
6319541	Pletcher et al.	Nov 2001	B1
6325821	Gaschino et al.	Dec 2001	B1
6336934	Gilson et al.	Jan 2002	B1
6342062	Suon et al.	Jan 2002	B1
6344055	Shukov	Feb 2002	B1
6355691	Goodman	Mar 2002	B1
6358556	Ding et al.	Mar 2002	B1
6361819	Tedeschi et al.	Mar 2002	B1
6362718	Patrick et al.	Mar 2002	B1
6364903	Tseng et al.	Apr 2002	B2
6368658	Schwartz et al.	Apr 2002	B1
6372246	Wei et al.	Apr 2002	B1
6387121	Alt	May 2002	B1
6409716	Sahatjian et al.	Jun 2002	B1
6414050	Howdle et al.	Jul 2002	B1
6416779	D-Augustine et al.	Jul 2002	B1
6448315	Lidgren et al.	Sep 2002	B1
6458387	Scott et al.	Oct 2002	B1
6461380	Cox	Oct 2002	B1
6461644	Jackson et al.	Oct 2002	B1
6488703	Kveen et al.	Dec 2002	B1
6495163	Jordan	Dec 2002	B1
6497729	Moussy et al.	Dec 2002	B1
6506213	Mandel et al.	Jan 2003	B1
6511748	Barrows	Jan 2003	B1
6517860	Rosser et al.	Feb 2003	B1
6521258	Mandel et al.	Feb 2003	B1
6524698	Schmoock	Feb 2003	B1
6530951	Bates et al.	Mar 2003	B1
6537310	Palmaz et al.	Mar 2003	B1
6541033	Shah	Apr 2003	B1
6572813	Zhang et al.	Jun 2003	B1
6602281	Klein	Aug 2003	B1
6610013	Fenster et al.	Aug 2003	B1
6627246	Mehta et al.	Sep 2003	B2
6649627	Cecchi et al.	Nov 2003	B1
6660176	Tepper et al.	Dec 2003	B2
6669785	DeYoung et al.	Dec 2003	B2
6669980	Hanson et al.	Dec 2003	B2
6670407	Howdle et al.	Dec 2003	B2
6682757	Wright	Jan 2004	B1
6706283	Appel et al.	Mar 2004	B1
6710059	Labrie et al.	Mar 2004	B1
6720003	Cheng et al.	Apr 2004	B2
6723913	Barbetta	Apr 2004	B1
6726712	Raeder-Devens et al.	Apr 2004	B1
6736996	Carbonell et al.	May 2004	B1
6743505	Antal et al.	Jun 2004	B2
6749902	Yonker et al.	Jun 2004	B2
6755871	Damaso et al.	Jun 2004	B2
6756084	Fulton et al.	Jun 2004	B2
6767558	Wang et al.	Jul 2004	B2
6780475	Fulton et al.	Aug 2004	B2
6794902	Becker et al.	Sep 2004	B2
6800663	Asgarzadeh et al.	Oct 2004	B2
6815218	Jacobsen et al.	Nov 2004	B1
6821549	Jayaraman	Nov 2004	B2
6837611	Kuo et al.	Jan 2005	B2
6838089	Carlsson et al.	Jan 2005	B1
6838528	Zhou	Jan 2005	B2
6858598	McKearn et al.	Feb 2005	B1
6860123	Uhlin et al.	Mar 2005	B1
6868123	Bellas et al.	Mar 2005	B2
6884377	Burnham et al.	Apr 2005	B1
6884823	Plerick et al.	Apr 2005	B1
6897205	Beckert et al.	May 2005	B2
6905555	DeYoung et al.	Jun 2005	B2
6908624	Hossainy et al.	Jun 2005	B2
6916800	McKearn et al.	Jul 2005	B2
6923979	Fotland et al.	Aug 2005	B2
6936270	Watson et al.	Aug 2005	B2
6939569	Green et al.	Sep 2005	B1
6973718	Sheppard et al.	Dec 2005	B2
7056591	Pacetti et al.	Jun 2006	B1
7094256	Shah et al.	Aug 2006	B1
7148201	Stern et al.	Dec 2006	B2
7152452	Kokish	Dec 2006	B2
7160592	Rypacek et al.	Jan 2007	B2
7163715	Kramer	Jan 2007	B1
7169404	Hossainy et al.	Jan 2007	B2
7171255	Holupka et al.	Jan 2007	B2
7201750	Eggers et al.	Apr 2007	B1
7201940	Kramer	Apr 2007	B1
7229837	Chen	Jun 2007	B2
7278174	Villalobos	Oct 2007	B2
7279174	Pacetti et al.	Oct 2007	B2
7282020	Kaplan	Oct 2007	B2
7308748	Kokish	Dec 2007	B2
7323454	De Nijs et al.	Jan 2008	B2
7326734	Zi et al.	Feb 2008	B2
7329383	Stinson	Feb 2008	B2
7378105	Burke et al.	May 2008	B2
7419696	Berg et al.	Sep 2008	B2
7429378	Serhan et al.	Sep 2008	B2
7444162	Hassan	Oct 2008	B2
7455658	Wang	Nov 2008	B2
7455688	Furst et al.	Nov 2008	B2
7456151	Li et al.	Nov 2008	B2
7462593	Cuttitta et al.	Dec 2008	B2
7485113	Varner et al.	Feb 2009	B2
7498042	Igaki et al.	Mar 2009	B2
7524865	D'Amato et al.	Apr 2009	B2
7537610	Reiss	May 2009	B2
7537785	Loscalzo et al.	May 2009	B2
7553827	Attawia et al.	Jun 2009	B2
7713538	Lewis et al.	May 2010	B2
7727275	Betts et al.	Jun 2010	B2
7745566	Chattopadhyay et al.	Jun 2010	B2
7763277	Canham et al.	Jul 2010	B1
7771468	Whitbourne et al.	Aug 2010	B2
7837726	Von Oepen et al.	Nov 2010	B2
7842312	Burgermeister et al.	Nov 2010	B2
7919108	Rees et al.	Apr 2011	B2
7955383	Krivoruchko et al.	Jun 2011	B2
7967855	Furst et al.	Jun 2011	B2
7972661	Pui et al.	Jul 2011	B2
8070796	Furst et al.	Dec 2011	B2
8295565	Gu et al.	Oct 2012	B2
8298565	Taylor et al.	Oct 2012	B2
8333803	Park et al.	Dec 2012	B2
8377356	Huang et al.	Feb 2013	B2
8535372	Fox et al.	Sep 2013	B1
8597716	Castro	Dec 2013	B2
8709071	Huang et al.	Apr 2014	B1
8753659	Lewis et al.	Jun 2014	B2
8753709	Hossainy et al.	Jun 2014	B2
8758429	Taylor	Jun 2014	B2
8795762	Fulton et al.	Aug 2014	B2
8834913	Shaw et al.	Sep 2014	B2
8852625	DeYoung et al.	Oct 2014	B2
8900651	McClain et al.	Dec 2014	B2
9090029	Prevost	Jul 2015	B2
9433516	McClain et al.	Sep 2016	B2
9474833	Ruane	Oct 2016	B2
9486431	McClain et al.	Nov 2016	B2
9510976	Hossainy	Dec 2016	B2
9511554	Dave	Dec 2016	B2
9592141	Ramzi poor	Mar 2017	B2
9668894	Stankus	Jun 2017	B2
20010026804	Boutignon	Oct 2001	A1
20010034336	Shah et al.	Oct 2001	A1
20010037143	Oepen	Nov 2001	A1
20010044629	Stinson	Nov 2001	A1
20010049551	Tseng et al.	Dec 2001	A1
20020007209	Scheerder et al.	Jan 2002	A1
20020051485	Bottomley	May 2002	A1
20020051845	Mehta et al.	May 2002	A1
20020082680	Shanley et al.	Jun 2002	A1
20020091433	Ding et al.	Jul 2002	A1
20020099332	Slepian et al.	Jul 2002	A1
20020125860	Schworn et al.	Sep 2002	A1
20020133072	Wang et al.	Sep 2002	A1
20020144757	Craig et al.	Oct 2002	A1
20020151959	Von Oepen	Oct 2002	A1
20030001830	Wampler et al.	Jan 2003	A1
20030004563	Jackson et al.	Jan 2003	A1
20030028244	Bates et al.	Feb 2003	A1
20030031699	Van Antwerp	Feb 2003	A1
20030077200	Craig et al.	Apr 2003	A1
20030088307	Shulze et al.	May 2003	A1
20030125800	Shulze et al.	Jul 2003	A1
20030143315	Pui et al.	Jul 2003	A1
20030170305	O'Neil et al.	Sep 2003	A1
20030180376	Dalal et al.	Sep 2003	A1
20030185964	Weber et al.	Oct 2003	A1
20030204238	Tedeschi	Oct 2003	A1
20030209835	Chun et al.	Nov 2003	A1
20030222017	Fulton et al.	Dec 2003	A1
20030222018	Yonker et al.	Dec 2003	A1
20030232014	Burke et al.	Dec 2003	A1
20040013792	Epstein et al.	Jan 2004	A1
20040018228	Fischell et al.	Jan 2004	A1
20040022400	Magrath	Feb 2004	A1
20040022853	Ashton et al.	Feb 2004	A1
20040044397	Stinson	Mar 2004	A1
20040059290	Palasis et al.	Mar 2004	A1
20040096477	Chauhan et al.	May 2004	A1
20040102758	Davila et al.	May 2004	A1
20040106982	Jalisi	Jun 2004	A1
20040122205	Nathan	Jun 2004	A1
20040126542	Fujiwara et al.	Jul 2004	A1
20040143317	Stinson et al.	Jul 2004	A1
20040144317	Chuman et al.	Jul 2004	A1
20040147904	Hung et al.	Jul 2004	A1
20040148007	Jackson et al.	Jul 2004	A1
20040157789	Geall	Aug 2004	A1
20040170685	Carpenter et al.	Sep 2004	A1
20040181278	Tseng et al.	Sep 2004	A1
20040193177	Houghton et al.	Sep 2004	A1
20040193262	Shadduck	Sep 2004	A1
20040220660	Shanley et al.	Nov 2004	A1
20040224001	Pacetti et al.	Nov 2004	A1
20040234748	Stenzel	Nov 2004	A1
20040236416	Falotico	Nov 2004	A1
20040260000	Chaiko	Dec 2004	A1
20050003074	Brown et al.	Jan 2005	A1
20050004661	Lewis et al.	Jan 2005	A1
20050010275	Sahatjian et al.	Jan 2005	A1
20050015046	Weber et al.	Jan 2005	A1
20050019747	Anderson et al.	Jan 2005	A1
20050033414	Zhang et al.	Feb 2005	A1
20050038498	Dubrow et al.	Feb 2005	A1
20050048121	East et al.	Mar 2005	A1
20050049694	Neary	Mar 2005	A1
20050053639	Shalaby	Mar 2005	A1
20050060028	Horres et al.	Mar 2005	A1
20050069630	Fox et al.	Mar 2005	A1
20050070989	Lye et al.	Mar 2005	A1
20050070990	Stinson	Mar 2005	A1
20050070997	Thornton et al.	Mar 2005	A1
20050074479	Weber et al.	Apr 2005	A1
20050075714	Cheng et al.	Apr 2005	A1
20050079199	Heruth et al.	Apr 2005	A1
20050079274	Palasis et al.	Apr 2005	A1
20050084533	Howdle et al.	Apr 2005	A1
20050101624	Betts	May 2005	A1
20050131513	Myers et al.	Jun 2005	A1
20050147734	Seppala et al.	Jul 2005	A1
20050159704	Scott et al.	Jul 2005	A1
20050166841	Robida	Aug 2005	A1
20050175772	Worsham et al.	Aug 2005	A1
20050177223	Palmaz	Aug 2005	A1
20050191491	Wang et al.	Sep 2005	A1
20050196424	Chappa	Sep 2005	A1
20050208102	Schultz	Sep 2005	A1
20050209244	Prescott et al.	Sep 2005	A1
20050216075	Wang et al.	Sep 2005	A1
20050222676	Shanley et al.	Oct 2005	A1
20050238829	Motherwell et al.	Oct 2005	A1
20050245637	Hossainy et al.	Nov 2005	A1
20050255327	Chaney	Nov 2005	A1
20050260186	Bookbinder et al.	Nov 2005	A1
20050268573	Maxfield et al.	Dec 2005	A1
20050288481	Desnoyer et al.	Dec 2005	A1
20050288629	Kunis	Dec 2005	A1
20060001011	Wilson et al.	Jan 2006	A1
20060002974	Pacetti et al.	Jan 2006	A1
20060020325	Burgermeister et al.	Jan 2006	A1
20060030652	Adams et al.	Feb 2006	A1
20060045901	Weber	Mar 2006	A1
20060073329	Boyce	Apr 2006	A1
20060089705	Ding et al.	Apr 2006	A1
20060093771	Rypacek et al.	May 2006	A1
20060094744	Maryanoff et al.	May 2006	A1
20060106455	Furst et al.	May 2006	A1
20060116755	Stinson	Jun 2006	A1
20060121080	Lye et al.	Jun 2006	A1
20060121089	Michal et al.	Jun 2006	A1
20060134168	Chappa et al.	Jun 2006	A1
20060134211	Lien et al.	Jun 2006	A1
20060136041	Schmid et al.	Jun 2006	A1
20060147698	Carroll et al.	Jul 2006	A1
20060153729	Stinson	Jul 2006	A1
20060160455	Sugyo et al.	Jul 2006	A1
20060188547	Bezwada	Aug 2006	A1
20060193886	Owens et al.	Aug 2006	A1
20060193890	Owens et al.	Aug 2006	A1
20060198868	DeWitt et al.	Sep 2006	A1
20060210638	Liversidge et al.	Sep 2006	A1
20060216324	Stucke et al.	Sep 2006	A1
20060222756	Davila et al.	Oct 2006	A1
20060228415	Oberegger et al.	Oct 2006	A1
20060228453	Cromack et al.	Oct 2006	A1
20060235506	Ta et al.	Oct 2006	A1
20060276877	Owens et al.	Dec 2006	A1
20060287611	Fleming	Dec 2006	A1
20070009564	McClain et al.	Jan 2007	A1
20070009664	Fallais et al.	Jan 2007	A1
20070026041	DesNoyer et al.	Feb 2007	A1
20070026042	Narayanan	Feb 2007	A1
20070032864	Furst et al.	Feb 2007	A1
20070038227	Massicotte et al.	Feb 2007	A1
20070038289	Nishide et al.	Feb 2007	A1
20070043434	Meerkin et al.	Feb 2007	A1
20070059350	Kennedy et al.	Mar 2007	A1
20070065478	Hossainy	Mar 2007	A1
20070110888	Radhakrishnan et al.	May 2007	A1
20070123973	Roth et al.	May 2007	A1
20070123977	Cottone et al.	May 2007	A1
20070128274	Zhu et al.	Jun 2007	A1
20070148251	Hossainy et al.	Jun 2007	A1
20070154513	Atanasoska et al.	Jul 2007	A1
20070154554	Burgermeister et al.	Jul 2007	A1
20070196242	Boozer et al.	Aug 2007	A1
20070196423	Ruane et al.	Aug 2007	A1
20070198081	Castro et al.	Aug 2007	A1
20070200268	Dave	Aug 2007	A1
20070203569	Burgermeister et al.	Aug 2007	A1
20070219579	Paul	Sep 2007	A1
20070225795	Granada	Sep 2007	A1
20070254012	Ludwig	Nov 2007	A1
20070259017	Francis	Nov 2007	A1
20070280992	Margaron et al.	Dec 2007	A1
20080030066	Mercier et al.	Feb 2008	A1
20080051866	Chen et al.	Feb 2008	A1
20080065192	Berglund	Mar 2008	A1
20080071347	Cambronne	Mar 2008	A1
20080071358	Weber et al.	Mar 2008	A1
20080071359	Thornton et al.	Mar 2008	A1
20080075753	Chappa	Mar 2008	A1
20080077232	Nishide	Mar 2008	A1
20080085880	Viswanath et al.	Apr 2008	A1
20080091008	Viswanath et al.	Apr 2008	A1
20080095919	McClain et al.	Apr 2008	A1
20080097575	Cottone	Apr 2008	A1
20080097591	Savage et al.	Apr 2008	A1
20080098178	Veazey et al.	Apr 2008	A1
20080107702	Jennissen	May 2008	A1
20080118543	Pacetti et al.	May 2008	A1
20080118544	Wang	May 2008	A1
20080124372	Hossainy et al.	May 2008	A1
20080138375	Yan et al.	Jun 2008	A1
20080206304	Lindquist et al.	Aug 2008	A1
20080213464	O'Connor	Sep 2008	A1
20080233267	Berglund	Sep 2008	A1
20080255510	Wang	Oct 2008	A1
20080269449	Chattopadhyay et al.	Oct 2008	A1
20080286325	Reyes et al.	Nov 2008	A1
20080292776	Dias et al.	Nov 2008	A1
20080300669	Hossainy	Dec 2008	A1
20080300689	Hossainy et al.	Dec 2008	A1
20090043379	Prescott	Feb 2009	A1
20090062909	Taylor et al.	Mar 2009	A1
20090068266	Raheja et al.	Mar 2009	A1
20090076446	Dubuclet et al.	Mar 2009	A1
20090076595	Lindquist et al.	Mar 2009	A1
20090082855	Borges et al.	Mar 2009	A1
20090098178	Hofmann et al.	Apr 2009	A1
20090105687	Deckman et al.	Apr 2009	A1
20090105809	Lee et al.	Apr 2009	A1
20090110711	Trollsas et al.	Apr 2009	A1
20090111787	Lim et al.	Apr 2009	A1
20090123515	Taylor et al.	May 2009	A1
20090123521	Weber et al.	May 2009	A1
20090186069	DeYoung et al.	Jul 2009	A1
20090202609	Keough et al.	Aug 2009	A1
20090216317	Cromack et al.	Aug 2009	A1
20090227949	Freyman et al.	Sep 2009	A1
20090231578	Ling et al.	Sep 2009	A1
20090263460	McDonald	Oct 2009	A1
20090285974	Kerrigan	Nov 2009	A1
20090292351	McClain et al.	Nov 2009	A1
20090292776	Nesbitt et al.	Nov 2009	A1
20090297578	Trollsas et al.	Dec 2009	A1
20090300689	Conte et al.	Dec 2009	A1
20100000328	Mahmoud	Jan 2010	A1
20100006358	Ishikawa	Jan 2010	A1
20100015200	McClain et al.	Jan 2010	A1
20100030261	McClain et al.	Feb 2010	A1
20100042206	Yadav et al.	Feb 2010	A1
20100055145	Betts et al.	Mar 2010	A1
20100055294	Wang et al.	Mar 2010	A1
20100063570	Pacetti et al.	Mar 2010	A1
20100063580	McClain et al.	Mar 2010	A1
20100074934	Hunter	Mar 2010	A1
20100131044	Patel	May 2010	A1
20100137491	Rose et al.	Jun 2010	A1
20100155496	Stark et al.	Jun 2010	A1
20100166869	Desai et al.	Jul 2010	A1
20100196482	Radovic-Moreno et al.	Aug 2010	A1
20100198330	Hossainy et al.	Aug 2010	A1
20100198331	Rapoza et al.	Aug 2010	A1
20100211164	McClain et al.	Aug 2010	A1
20100228348	McClain et al.	Sep 2010	A1
20100233332	Xing et al.	Sep 2010	A1
20100239635	McClain et al.	Sep 2010	A1
20100241220	McClain	Sep 2010	A1
20100256746	Taylor et al.	Oct 2010	A1
20100256748	Taylor et al.	Oct 2010	A1
20100262224	Kleiner	Oct 2010	A1
20100272775	Cleek et al.	Oct 2010	A1
20100272778	McClain et al.	Oct 2010	A1
20100285085	Stankus et al.	Nov 2010	A1
20100298928	McClain et al.	Nov 2010	A1
20100303881	Hoke et al.	Dec 2010	A1
20100305689	Venkatraman et al.	Dec 2010	A1
20110009953	Luk et al.	Jan 2011	A1
20110034422	Kannan et al.	Feb 2011	A1
20110159069	Shaw et al.	Jun 2011	A1
20110160751	Granja	Jun 2011	A1
20110172763	Ndondo-Lay	Jul 2011	A1
20110189299	Okubo et al.	Aug 2011	A1
20110190864	McClain et al.	Aug 2011	A1
20110223212	Taton et al.	Sep 2011	A1
20110238161	Fulton et al.	Sep 2011	A1
20110243884	O'Shea	Oct 2011	A1
20110257732	McClain et al.	Oct 2011	A1
20110264190	McClain et al.	Oct 2011	A1
20110301697	Hoffmann et al.	Dec 2011	A1
20120064124	McClain et al.	Mar 2012	A1
20120064143	Sharp et al.	Mar 2012	A1
20120065723	Drasler et al.	Mar 2012	A1
20120101566	Mews et al.	Apr 2012	A1
20120150275	Shaw-Klein	Jun 2012	A1
20120160408	Clerc et al.	Jun 2012	A1
20120172787	McClain et al.	Jul 2012	A1
20120177742	McClain et al.	Jul 2012	A1
20120231037	Levi	Sep 2012	A1
20120239161	Datta et al.	Sep 2012	A1
20120271396	Zheng	Oct 2012	A1
20120280432	Chen et al.	Nov 2012	A1
20120290075	Mortisen et al.	Nov 2012	A1
20120323311	McClain et al.	Dec 2012	A1
20130006351	Taylor et al.	Jan 2013	A1
20130035754	Shulze et al.	Feb 2013	A1
20130084322	Wu	Apr 2013	A1
20130084449	Lewis	Apr 2013	A1
20130087270	Hossainy et al.	Apr 2013	A1
20130110138	Hurtado	May 2013	A1
20130172853	McClain et al.	Jul 2013	A1
20130291476	Broughton, Jr. et al.	Nov 2013	A1
20140035192	Ramzipoor	Feb 2014	A1
20140228932	Rapoza	Aug 2014	A1
20140257465	McClain	Sep 2014	A1
20140287134	To	Sep 2014	A1
20140343667	McClain	Nov 2014	A1
20140350522	McClain et al.	Nov 2014	A1
20140371717	McClain et al.	Dec 2014	A1
20150024116	Matson et al.	Jan 2015	A1
20150025620	Taylor et al.	Jan 2015	A1
20150250926	McClain et al.	Sep 2015	A1
20160067071	Jose	Mar 2016	A1
20160095726	McClain	Apr 2016	A1
20180116837	Ramzipoor	May 2018	A1

Foreign Referenced Citations (193)

Number	Date	Country
2237466	Nov 1998	CA
2589761	Dec 2004	CA
2615452	Jan 2007	CA
2650590	Nov 2007	CA
2679712	Jul 2008	CA
2684482	Oct 2008	CA
2721832	Dec 2009	CA
2423899	Mar 2001	CN
1465410	Jan 2004	CN
1575860	Feb 2005	CN
1649551	Aug 2005	CN
1684641	Oct 2005	CN
101161300	Apr 2008	CN
102481195	May 2012	CN
4336209	Mar 1995	DE
29702671	Apr 1997	DE
29716476	Dec 1997	DE
19633901	Feb 1998	DE
29716467	Feb 1998	DE
19740506	Mar 1998	DE
19754870	Aug 1998	DE
19822157	Nov 1999	DE
69611186	May 2001	DE
0335341	Oct 1989	EP
0604022	Jun 1994	EP
800801	Oct 1997	EP
0876806	Nov 1998	EP
0982041	Mar 2000	EP
1195822	Apr 2002	EP
1325758	Jul 2003	EP
1327422	Jul 2003	EP
1454677	Sep 2004	EP
1502655	Feb 2005	EP
1750784	Feb 2007	EP
1810665	Jul 2007	EP
1909973	Apr 2008	EP
2197070	Jun 2010	EP
2293357	Mar 2011	EP
2293366	Mar 2011	EP
2758253	Jul 1998	FR
1994-098902	Apr 1994	JP
H06218063	Aug 1994	JP
H08206223	Aug 1996	JP
H09-056807	Mar 1997	JP
H1029524	Feb 1998	JP
H10151207	Jun 1998	JP
H10314313	Dec 1998	JP
H1157018	Mar 1999	JP
2000316981	Nov 2000	JP
2001521503	Nov 2001	JP
2003-205037	Jul 2003	JP
2003-533286	Nov 2003	JP
2003-5339493	Nov 2003	JP
2003533492	Nov 2003	JP
2004512059	Apr 2004	JP
2004173770	Jun 2004	JP
2004-518458	Jun 2004	JP
2004-529674	Sep 2004	JP
2004528060	Sep 2004	JP
2005-505318	Feb 2005	JP
2005519080	Jun 2005	JP
2005-523119	Aug 2005	JP
2005-523332	Aug 2005	JP
2005-296690	Oct 2005	JP
2006506191	Feb 2006	JP
2006512175	Apr 2006	JP
2007502281	Feb 2007	JP
2007215620	Aug 2007	JP
2009-501566	Jan 2009	JP
2009529399	Aug 2009	JP
2010052503	Mar 2010	JP
2010515539	May 2010	JP
2010516307	May 2010	JP
2011517589	Jun 2011	JP
2012527318	Nov 2012	JP
10-2004-0034064	Apr 2004	KR
10-1231197	Feb 2013	KR
9409010	Apr 1994	WO
WO-95006487	Mar 1995	WO
9616691	Jun 1996	WO
WO-9620698	Jul 1996	WO
9632907	Oct 1996	WO
9641807	Dec 1996	WO
WO-97045502	Dec 1997	WO
9802441	Jan 1998	WO
9908729	Feb 1999	WO
9915530	Apr 1999	WO
9917680	Apr 1999	WO
99016388	Apr 1999	WO
0006051	Feb 2000	WO
0025702	May 2000	WO
00032238	Jun 2000	WO
0114387	Mar 2001	WO
WO-2001054662	Aug 2001	WO
0187345	Nov 2001	WO
0187368	Nov 2001	WO
WO-2001-087371	Nov 2001	WO
WO-2001087372	Nov 2001	WO
0226281	Apr 2002	WO
WO-2002040702	May 2002	WO
WO 2002043799	Jun 2002	WO
02055122	Jul 2002	WO
WO-2002-074194	Sep 2002	WO
WO-2002090085	Nov 2002	WO
02100456	Dec 2002	WO
WO-2003039553	May 2003	WO
WO-2003-082368	Oct 2003	WO
03090684	Nov 2003	WO
WO-2003101624	Dec 2003	WO
WO-2004009145	Jan 2004	WO
2004028406	Apr 2004	WO
WO-2004028589	Apr 2004	WO
WO-2004043506	May 2004	WO
WO-2004045450	Jun 2004	WO
2004101017	Nov 2004	WO
WO-2004098574	Nov 2004	WO
2005018696	Mar 2005	WO
WO-2005042623	May 2005	WO
WO-2005063319	Jul 2005	WO
WO-2005069889	Aug 2005	WO
WO-2005117942	Dec 2005	WO
WO-2006014534	Feb 2006	WO
WO-2006052575	May 2006	WO
2006063021	Jun 2006	WO
2006063430	Jun 2006	WO
WO-2006065685	Jun 2006	WO
WO-2006083796	Aug 2006	WO
WO-2006099276	Sep 2006	WO
2007017707	Jan 2007	WO
2007017708	Jan 2007	WO
WO-2007-002238	Jan 2007	WO
WO-2007011707	Jan 2007	WO
WO-2007011707	Jan 2007	WO
WO-2007011708	Jan 2007	WO
WO-2007011708	Jan 2007	WO
WO-2007092179	Aug 2007	WO
2007106441	Sep 2007	WO
WO-2007127363	Nov 2007	WO
WO 2007143609	Dec 2007	WO
2008024626	Feb 2008	WO
WO-2008042909	Apr 2008	WO
WO-2008046641	Apr 2008	WO
WO-2008046642	Apr 2008	WO
WO-2008052000	May 2008	WO
WO-2008070996	Jun 2008	WO
WO-2008086369	Jul 2008	WO
WO 2008131131	Oct 2008	WO
WO-20080148013	Dec 2008	WO
09039553	Apr 2009	WO
09051614	Apr 2009	WO
WO-2009051780	Apr 2009	WO
2009096822	Aug 2009	WO
2009113605	Sep 2009	WO
2009120361	Oct 2009	WO
WO-20090146209	Dec 2009	WO
2010001932	Jan 2010	WO
WO-2010009335	Jan 2010	WO
WO-2010075590	Jul 2010	WO
2010086863	Aug 2010	WO
WO-2010111196	Sep 2010	WO
WO-2010111196	Sep 2010	WO
WO-2010111232	Sep 2010	WO
WO-2010111232	Sep 2010	WO
WO-2010111238	Sep 2010	WO
WO-2010111238	Sep 2010	WO
WO-2010120552	Oct 2010	WO
WO-2010120552	Oct 2010	WO
WO-2010121187	Oct 2010	WO
WO-2010121187	Oct 2010	WO
2010135369	Nov 2010	WO
10136604	Dec 2010	WO
WO-2011009096	Jan 2011	WO
WO-2011097103	Aug 2011	WO
2011119159	Sep 2011	WO
WO-2011119762	Sep 2011	WO
WO-2011130448	Oct 2011	WO
WO-2011133655	Oct 2011	WO
WO-2012009684	Jan 2012	WO
WO-2012034079	Mar 2012	WO
WO-2012082502	Jun 2012	WO
WO-2012092504	Jul 2012	WO
WO-2012142319	Oct 2012	WO
WO-2012166819	Dec 2012	WO
2013003644	Jan 2013	WO
WO-2013012689	Jan 2013	WO
WO-2013025535	Feb 2013	WO
WO-2013059509	Apr 2013	WO
WO-2013173657	Nov 2013	WO
WO-2013177211	Nov 2013	WO
WO-2014063111	Apr 2014	WO
2014165264	Oct 2014	WO
2014186532	Nov 2014	WO
2015181826	Dec 2015	WO

Non-Patent Literature Citations (423)

Entry
Abreu Filho et al., “Influence of metal alloy and the profile of coronary stents in patients with multivessel coronary disease,” CLINICS 66(6):985-989 (2011).
Akoh et al., “One-Stage Synthesis of Raffinose Fatty Acid Polyesters.” Journal Food Science 52:1570 (1987).
Albert et al., “Antibiotics for preventing recurrent urinary tract infection in non-pregnant women,” Cochrane Database System Rev. 3, CD001209 (2004).
Au et al., “Methods to improve efficacy of intravesical mitomycin C: Results of a randomized phase III trial,” Journal of the National Cancer Institute, 93(8), 597-604 (2001).
AU2006270221 Exam Report dated Apr. 6, 2010.
AU2007243268 Exam Report dated May 15, 2013.
AU2007243268 Exam Report dated Aug. 31, 2011.
AU2009251504 Exam Report dated Dec. 8, 2011.
AU2009270849 Exam Report dated Feb. 14, 2012.
AU2011232760 Exam Report dated Apr. 10, 2013.
AU2011256902 Exam Report dated Jun. 13, 2013.
AU2012203203 Exam Report dated Apr. 12, 2013.
AU2012203577 Exam Report dated Jun. 7, 2013.
AU2011256902 Office Action dated Jun. 10, 2014.
Balss et al., “Quantitative spatial distribution of sirolumus and polymers in drug-eluting stents using confocal Raman microscopy,” J. of Biomedical Materials Research Part A, 258-270 (2007).
Belu et al., “Three-Dimensional Compositional Analysis of Drug Eluting Stent Coatings Using Cluster Secondary Ioan Mass Spectroscopy,” Anal. Chem. 80:624-632 (2008).
Belu, et al., “Chemical imaging of drug eluting coatings: Combining surface analysis and confocal Rama microscopy” J. Controlled Release 126: 111-121 (2008).
Boneff, “Topical Treatment of Chronic Prostatitis and Premature Ejaculation,” International Urology and Nephrology 4(2):183-186 (1971).
Bookbinder et al., “A recombinant human enzyme for enhanced interstitial transport of therapeutics,” Journal of Controlled Release 114:230-241 (2006).
Borchert et al., “Prevention and treatment of urinary tract infection with probiotics: Review and research perspective,” Indian Journal Urol. 24(2):139-144 (2008).
Brunstein et al., “Histamine, a vasoactive agent with vascular disrupting potential improves tumour response by enhancing local drug delivery,” British Journal of Cancer 95:1663-1669 (2006).
Bugay et al., “Raman Analysis of Pharmaceuticals,” in “Applications of Vibrational Spectroscopy in Pharmaceutical Research and Development,” Ed. Pivonka, D.E., Chalmers, J.M., Griffiths, P.R. Wiley and Sons, p. 1-24. (2007).
CA 2757276 Office Action dated Feb. 15, 2013.
CA 2757276 Office Action dated Feb. 5, 2014.
CA 2794704 Office action dated Feb. 7, 2014.
CA 2613280 Office Action dated Oct. 2, 2012.
CA 2615452 Office Action dated Dec. 19, 2012.
CA 2615452 Office Action dated Oct. 8, 2013.
CA 2650590 Office action dated Jul. 23, 2013.
CA 2613280 Office action dated Dec. 10, 2013.
CA 2667228 Office action dated Jan. 22, 2014.
CA 2679712 Office action dated Feb. 24, 2014.
CA 2684482 Office Action dated Nov. 10, 2011.
CA 2684482 Office Action dated Jul. 11, 2012.
CA 2688314 Office Action dated Jun. 6, 2012.
CA 2667228 office action dated May 7, 2013.
CA 2730995 Office action dated May 29, 2013.
CA 2730995 Office Action dated Sep. 26, 2012.
CA 2730995 Office Action dated Feb. 20, 2014.
CA 2756307 Office Action dated Feb. 18, 2013.
CA 2756307 Office Action dated Mar. 24,2014.
CA 2756386 Office Action dated Mar. 15, 2013.
CA 2756388 Office Action dated Apr. 11, 2013.
CA 2756388 Office Action dated Apr. 14, 2014.
CA 2759015 Office Action dated Apr. 8, 2013.
CA 2759015 Office Action dated Jul. 21, 2014.
CA 2756386 Office Action dated Oct. 24, 2013.
CA 2756386 Office Action dated May 16, 2014.
CA 2805631 Office Action dated Jan. 17, 2014.
CA 2823355 Office Action dated Apr. 14, 2014.
Cadieux et al., “Use of triclosan-eluting ureteral stents in patients with long-term stents,” J. Endourol (Epub) (Jun. 19, 2009).
Channon et al., “Nitric Oxide Synthase in Atherosclerosis and Vascular Injury: Insights from Experimental Gene Therapy,” Arteriosclerosis, Thrombosis and Vascular Biology, 20(8):1873-1881 (2000).
Chen et al. Immobilization of heparin on a silicone surface through a heterobifunctional PEG spacer. Biomaterials. 26(35):7418-24 (2005).
Chłopek et al. “The influence of carbon fibres on the resorption time and mechanical properties of the lactide-glycolide co-polymer.” J. Biomater. Sci. Polymer Edn, vol. 18, No. 11, pp. 1355-1368 (2007).
Clair and Burks, “Thermoplastic/Melt-Processable Polyimides,” NASA Conf. Pub. #2334 (1984), pp. 337-355 (1984).
CN 2006800258093 Office Action dated May 30, 2012.
CN 200780047425.6 Office action dated Aug. 3, 2012.
CN 200780047425.6 Office Action dated Feb. 28, 2013.
CN 200880007308.1 Office Action dated Jul. 3, 2013.
CN 200880007308.1 Office Action dated Nov. 23, 2011.
CN 200880007308.1 Office Action dated Oct. 18, 2012.
CN 200880007308.1 Office Action dated Jan. 2, 2014.
CN 200880020515 Office Action dated Jul. 22, 2013.
CN 200880020515 Office Action dated Oct. 9, 2012.
CN 200880020515 Office Action dated Apr. 15, 2014.
CN 200880100102.3 Office Action dated Apr. 11, 2013.
CN 200880100102.3 Office Action dated Jun. 1, 2012.
CN 200880100102.3 Office Action dated Dec. 11, 2013.
CN 200880100102.3 Office Action dated Aug. 27, 2014.
CN 200980122691 Office Action dated Oct. 10, 2012.
CN 200980136432.2 Office Action dated Jan. 14, 2013.
CN 200980136432.2 Office Action dated Nov. 4, 2013.
CN 200980136432.2 Office Action dated Jul. 3, 2014.
CN 201080024973.9 Office Action dated Dec. 20, 2013.
CN 201080024973.9 Office Action dated Aug. 7, 2014.
Cohen, et al. “Sintering Technique for the Preparation of Polymer Matrices for the Controlled Release of Macromolecules.” Journal of Pharamceutical Sciences, vol. 73, No. 8, p. 1034-1037 (1984).
Colombo et al. “Selection of Coronary Stents,” Journal of the American College of Cardiology, vol. 40, No. 6, . p. 1021-1033 (2002).
CRC Handbook of chemistry and physics. 71st ed. David R. Lide, Editor-in-Chief. Boca Raton, FL, CRC Press; 6-140 (1990).
Cyrus et al., “Intramural delivery of rapamycin with alphavbeta3-targeted paramagnetic nanoparticles inhibits stenosis after balloon injury,” Arterioscler Thromb Vasc Biol 28:820-826 (2008).
DERWENT-ACC-No. 2004-108578 Abstracting 2004003077; Jan. 8, 2004; 3 pages.
DiStasi et al., “Percutaneous sequential bacillus Calmette-Guerin and mitomycin C for panurothelial carcinomatosis,” Can. J. Urol. 12(6):2895-2898 (2005).
Domb and Langer, “Polyanhydrides. I. Preparation of High Molecular Weight Polyanhydrides.” J. Polym Sci. 25:3373-3386 (1987).
Domingo, C. et al., “Precipication of ultrafine organic crystals from the rapid expansion of supercritical solutions over a capillary and a frit nozzle,” J. Supercritical Fluids 10:39-55 (1997).
Dzik-Jurasz, “Molecular imaging in vivo: an introduction,” The British Journal of Radiology, 76:S98-S109 (2003).
EA 200901254 Office Action dated Jul. 29, 2013.
EA 200901254/28 Office Action dated Jun. 28, 2012.
EA 201001497 Office Action dated Feb. 11, 2013.
EA 201001497 Office Action dated Jul. 29, 2013.
Electrostatic Process, Wiley Encyclopedia of Electrical and Electronics Engineering, John Wiley & Sons, Inc. 7:15-39 (1999).
Eltze et al., “Imidazoquinolinon, imidazopyridine, and isoquinolindione derivatives as novel and potent inhibitors of the poly (ADP-ribose) polymerase (PARP): a comparison with standard PARP inhibitors,” Mol. Pharmacol 74(6):1587-1598 (2008).
EP06773731.2 Search Report dated Oct. 2, 2012.
EP06787258.0 Office Action dated Mar. 15, 2013.
EP06787258.0 Search Report dated Feb. 6, 2012.
EP07756094.4 Office Action dated Jan. 21, 2014.
EP07756094.4 Office Action dated May 29, 2013.
EP07756094.4 Search Report dated Aug. 31, 2012.
EP08705772.5 Office Action dated Oct. 30, 2013.
EP08705772.5 Search Report dated Feb. 20, 2013.
EP08733210.2 Office Action dated Jul. 16, 2013.
EP08733210.2 Search Report dated Oct. 23, 2012.
EP08756215.3 Search Report dated Oct. 5, 2011.
EP08756215.3 Search Report dated Jan. 28, 2013.
EP09755571.8 Office Action dated Dec. 13, 2013.
EP09755571.8 Search Report dated Apr. 9, 2013.
EP09798764.8 Search Report dated Sep. 30, 2013.
EP09805981.9 Office Action dated Feb. 13, 2013.
EP10756676.2 Search Report dated Jan. 31, 2014.
EP10756696.0 Search Report dated Oct. 10, 2013.
EP10764884.2 Search Report dated Oct. 28, 2013.
EP10765295.0 Search Report dated Oct. 17, 2013.
EP11769546.0 Search Report dated Sep. 19, 2013.
EP10800642.0 Search Report dated Mar. 19, 2014.
EP11772624.0 Search Report dated Jun. 5, 2014.
EP09798764.8 Office Action dated Jun. 30, 2014.
Ettmayer et al. Lessons learned from marketed and investigational prodrugs. J Med Chem. 47(10):2393-404 (2004).
Fibbi et al., “Chronic inflammation in the pathogenesis of benign prostatic hyperplasia,” Int J Androl. 33(3):475-88 (2010).
Fleischmann et al., “High Expression of Gastrin-Releasing Peptide Receptors in the Vascular bed of Urinary Tract Cancers: Promising Candidates for Vascular Targeting Applications.” Endocr. Relat. Cancer 16(2):623-33 (2009).
Froehlich et al., “Conscious sedation for gastroscopy: patient tolerance and cardiorespiratory parameters,” Gastroenterology 108(3):697-704 (1995).
Fujiwara et al., “Insulin-like growth factor 1 treatment via hydrogels rescues cochlear hair cells from ischemic injury,” NeuroReport 19(16):1585-1588 (2008).
Fulton et al. Thin Fluoropolymer films and nanoparticle coatings from the rapid expansion of supercritical carbon dioxide solutions with electrostatic collection, Polymer Communication. 2627-3632 (2003).
Green et al., “Simple conjugated polymer nanoparticles as biological labels,” Proc Roy Soc A. published online Jun. 24, 2009 doi:10.1098/rspa.2009.0181.
Griebenow et al., “On Protein Denaturation in Aqueous-Organic Mixtures but not in Pure Organic Solvents,” J. Am Chem Soc., vol. 118. No. 47, 11695-11700 (1996).
Hamilos et al., “Differential effects of Drug-Eluting Stents on Local Endothelium-Dependent Coronary Vasomotion.” JACC vol. 51, No. 22, Endothelium and Des Jun. 3, 2008:2123-9 (2008).
Han, et al., “Studies of a Novel Human Thrombomodulin Immobilized Substrate: Surface Characterization and Anticoagulation Activity Evaluation.” J. Biomater. Sci. Polymer Edn, 12 (10), 1075-1089 (2001).
Hartmann et al., “Tubo-ovarian abscess in virginal adolescents: exposure of the underlying etiology,” J. Pediatr Adolesc Gynecol, 22(3):313-16 (2009).
Hasegawa et al., “Nylong 6/Na-montmorillonite nanocomposites prepared by compounding Nylon 6 with Na-montmorillonite slurry,” Polymer 44 2933-2937 (2003).
Hinds, WC. Aerosol Technology, Properties, Behavior and Measurement of Airborne Particles, Department of Environmental Health Sciences, Harvard University School of Public Health, Boston, Massachusetts. 283-314 (1982).
Hladik et al., “Can a topical microbicide prevent rectal HIV transmission?” PLoS Med. 5(8):e167 (2008).
Iconomidou et al., “Secondary Structure of Chorion Proteins of the Teleosatan Fish Dentex dentex by ATR FR—IR and FT-Raman Spectroscopy,” J. of Structural Biology, 132, 112-122 (2000).
ID—W00201003529 Office Action dated Apr. 28, 2014.
IL—208648 Official Notification dated Feb. 9, 2012.
IL—201550 Official Notification dated Dec. 8, 2013.
IN-368/DELNP/2008 Exam Report dated Oct. 17, 2011.
IN-6884/DELNP/2009 Office Action dated Oct. 31, 2013.
IN-7740/DELNP/2009 Office Action dated Jul. 29, 2014.
Jackson et al., “Characterization of perivascular poly(lactic-co-glycolic acid) films containing paclitaxel” Int. J. of Pharmaceutics, 283:97-109 incorporated in its entirety herein by reference (2004).
Jensen et al., Neointimal hyperplasia after sirollmus-eluting and paclitaxel-eluting stend implantation in diabetic patients: the randomized diabetes and drug eluting stent (DiabeDES) intravascular ultrasound trial. European heart journal (29), pp. 2733-2741. Oct. 2, 2008. Retrieved from the Internet. Retrieved on [Jul. 17, 2012]. URL:<http://eurheartj.oxfordjournals.org/content/29/22/2733.full.pdf> entire document.
Jewell, et al., “Release of Plasmid DNA from Intravascular Stents Coated with Ultrathin Multilayered Polyelectrolyte Films” Biomacromolecules. 7: 2483-2491 (2006).
Johns, H.E, J.R.Cunningham, Thomas, Charles C., Publisher, “The Physics of Radiology,” Springfield, IL, pp. 133-143 (1983).
Joner et al. “Site-specific targeting of nanoparticle prednisolone reduces in-stent restenosis in a rabbit model of established atheroma,” Arterioscler Thromb Vasc Biol. 28:1960-1966 (2008).
Jovanovic et al. “Stabilization of Proteins in Dry Powder Formulations Using Supercritical Fluid Technology,” Pharm. Res. 21(11) (2004).
JP 2008-521633 Office Action dated Oct. 12, 2012.
JP2008-521633 Office Action dated Dec. 28, 2011.
JP-2009-534823 Office Action dated Apr. 23, 2013.
JP-2009-534823 Office Action dated Feb. 21, 2012.
JP-2009-534823 Office Action dated Sep. 20, 2012.
JP-2009-545647 Office Action dated Jun. 5, 2012.
JP-2009-545647 Office Action dated May 14, 2013.
JP-2009-545647 Office Action dated Apr. 22, 2014.
JP-2010-504253 Office Action dated Dec. 12, 2011.
JP-2010-504253 Office Action dated Dec. 7, 2012.
JP-2010-510441 Office action dated May 7, 2013.
JP-2011-505248 Office action dated Jun. 4, 2013.
JP-2011-518920 Office action dated Dec. 17, 2012.
JP-2011-518920 Office action dated Oct. 23, 2013.
JP-2012-503677 Office action dated Jan. 18, 2013.
JP-2012-503677 Office action dated Nov. 1, 2013.
JP-2012-151964 Office Action dated Dec. 10, 2013.
JP-2013-024508 Office Action dated May 2, 2014.
JP-2013-190903 Office Action dated Sep. 2, 2014.
Kazemi et al., “The effect of betamethasone gel in reducing sore throat, cough, and hoarseness after laryngo-tracheal intubation,” Middle East J. Anesthesiol. 19(1):197-204 (2007).
Kehinde et al., “Bacteriology of urinary tract infection associated with indwelling J ureteral stents,” J. Endourol. 18(9):891-896 (2004).
Kelly et al., “Double-balloon trapping technique for embolization of a large wide-necked superior cerebellar artery aneurysm: case report,” Neurosurgery 63(4 Suppl 2):291-292 (2008).
Khan et al., “Chemistry and the new uses of Sucrose: How Important?” Pur and Appl. Chem 56:833-844 (1984).
Khan et al., “Cyclic Acetals of 4,1′,6′-Trichloro-4,1′,6′,-Trideoxy-Trideoxy-galacto-Sucrose and their Conversion into Methyl Ether Derivatives.” Carb. Res. 198:275-283 (1990).
Khan et al., “Enzymic Regioselective Hydrolysis of Peracetylated Reducing Disaccharides, Specifically at the Anomeric Centre: Intermediates for the Synthesis of Oligosaccharides.” Tetrahedron Letters 34:7767 (1933).
Khayankarn et al., “Adhesion and Permeability of Polyimide-Clay Nanocomposite Films for Protective Coatings,” Journal of Applied Polymer Science, vol. 89, 2875-2881 (2003).
Koh et al., A novel nanostructured poly(lactic-co-glycolic-acid)—multi-walled carbon nanotube composite for blood-contacting applications: Thrombogenicity studies, Acta Biomaterialia 5:3411-3422 (2009).
KR10-2008-7003756 Office Action dated Sep. 23, 2013.
KR10-2008-7003756 Office Action dated Oct. 30, 2012.
KR10-2013-7031237 Office Action dated Mar. 17, 2014.
Kurt et al., “Tandem oral, rectal and nasal administrations of Ankaferd Blood Stopper to control profuse bleeding leading to hemodynamic instability,” Am J. Emerg. Med. 27(5):631, e1-2 (2009).
Labhasetwar et al., “Arterial uptake of biodegradable nanoparticles: effect of surface modifications,” Journal of Pharmaceutical Sciences, vol. 87, No. 10, 1229-1234 (1998).
Lamm et al., “Bladder Cancer: Current Optimal Intravesical Treatment: Pharmacologic Treatment,” Urologic Nursing 25(5):323-6, 331-2 (Oct. 26, 2005).
Latella et al., “Nanoindentation hardness. Young's modulus, and creep behavior of organic-inorganic silica-based sol-gel thin films on copper,” J Mater Res 23(9): 2357-2365 (2008).
Lawrence et al., “Rectal tacrolimus in the treatment of resistant ulcerative proctitis,” Aliment. Pharmacol Ther. 28(10):1214-20 (2008).
Lee et al., “Novel therapy for hearing loss: delivery of insulin-like growth factor 1 to the cochlea using gelatin hydrogel,” Otol. Neurotol. 28(7):976-81 (2007).
Lehmann et al, “Drug treatment of nonviral sexually transmitted diseases: specific issues in adolescents,” Pediatr Drugs 3(7):481-494 (2001).
Mahoney et al., “Three-Dimensional Compositional Analysis of Drug Eluting Stent Coatings Using Cluster Secondary Ion mass Spectrometry,” Anal. Chem., 80, 624-632 (2008).
Mario, C.D. et al., “Drug-Eluting Bioabsorbable Magnesium Stent,” J. Interventional Cardiology 16(6):391-395 (2004).
Matsumoto, D, et al. Neointimal Coverage of Sirolimus-Eluting Stents at 6-month Follow-up: Evaluated by Optical Coherence Tomography, European Heart Journal, 28:961-967 (2006).
McAlpine, J.B. et al., “Revised NMR Assignments for Rapamycine,” J. Antibiotics 44:688-690 (1991).
Mehik et al., “Alfuzosin treatment for chronic prostatitis/chronic pelvic pain syndrome: a prospecitve, randomized, double-blind, placebo-controlled, pilot study,” Urology 62(3):425-429 (2003).
Mei et al., “Local Delivery of Modified Paclitaxel-Loaded Poly( ε-caprolactone)/Pluronic F68 Nanoparticles for Long-Term Inhibition of Hyperplasia,” Journal of Pharmaceutical Sciences, vol. 98, No. 6, Jun. 2009.
Melonakos et al., Treatment of low-grade bulbar transitional cell carcinoma with urethral instillation of mitomycin C, Adv. Urol., 173694 Epub; (2008).
Merrett et al., “Interaction of corneal cells with transforming growth factor beta2-modified poly dimethyl siloxane surfaces,” Journal of Biomedical Materials Research, Part A, vol. 67A, No. 3, pp. 981-993 (2003).
Merriam-Webster Online Dictionary, obtained online at: http://www.merriam-webster.com/dictionary/derivative, downloaded Jan. 23, 2013.
Middleton and Tipton, Synthetic biodegradable polymers as orthopedic devises. Biomaterials 21:2335-46 (2000).
Minchin, “Nanomedicine: sizing up targets with nanoparticles,” Nature Nanotechnology, vol. 33, 12-13 (2008).
Minoque et al., “Laryngotracheal topicalization with lidocaine before intubation decreases the incidence of coughing on emergence from general anesthesia,” Anesth. Analg. 99(4):1253-1257 (2004).
Mishima et al. “Microencapsulation of Proteins by Rapid Expansion of Supercritical Solution with a Nonsolvent,” AlChE J. 46(4):857-65 (2000).
Mocco et al., “Pharos neurovascular intracranail stent: Elective use for a symptomatic stenosis refractory to medical therapy,” Catheter Cardiovasc. Interv. (epub) (Mar. 2009).
Mollen et al., “Prevalence of tubo-ovarian abcess in adolescents diagnosed with pelvice inflammatory disease in a pediatric emergency department,” Pediatr. Emerg. Care, 22(9): 621-625 (2006).
Moroni et al., “Post-ischemic brain damage:targeting PARP-1 within the ischemic neurovaschular units as a realistic avenue to stroke treatment,” FEBS J. 276(1):36-45 (2009).
Muhlen et al., “Magnetic Resonance Imaging Contrast Agent Targeted Toward Activated Platelets Allows in Vivo Detection of Thrombosis and Monitoring of Thrombolysis Circulation,” 118:258-267 (2008).
Murphy et al., “Chronic prostatitis: management strategies,” Drugs 69(1): 71-84 (2009).
MX/a/2010/01148 Office Action dated Feb. 11, 2014.
NZ 588549 Examination Report dated Mar. 28, 2011.
NZ 600814 Examination Report dated Jun. 29, 2012.
O'Neil et al., “Extracellular matrix binding mixed micelles for drug delivery applications,” Journal of Controlled Release 137:146-151 (2009).
O'Donnell et al., “Salvage intravesical therapy with interferon-alpha 2b plus low dose bacillus Calmette-Guerin alone perviously failed,” Journ. Urology, 166(4):1300-1304 (2001).
Olbert et al., “In vitro and in vivo effects of CpG-Oligodeoxynucleotides (CpG-ODN) on murine transitional cell carcinoma and on the native murine urinary bladder wall,” Anticancer Res. 29(6):2067-2076 (2009).
Ong and Serruys, “Technology Insight: an overview of research in drug-eluting stents,” Nat. Clin. Parct. Cardiovas. Med. 2(12):647-658 (2005).
PCT/US06/24221 International Preliminary Report on Patentability dated Dec. 24, 2007.
PCT/US06/24221 International Search Report dated Jan. 29, 2007.
PCT/US06/27321 International Preliminary Report on Patentability dated Jan. 16, 2008.
PCT/US06/27321 International Search Report dated Oct. 16, 2007.
PCT/US06/27322 International Preliminary Report on Patentability dated Jan. 16, 2008.
PCT/US06/27322 International Search Report dated Apr. 25, 2007.
PCT/US07/10227 International Preliminary Report on Patentability dated Oct. 28, 2008.
PCT/US07/10227 International Search Report dated Aug. 8, 2008.
PCT/US07/80213 International Preliminary Report on Patentability dated Apr. 7, 2009.
PCT/US07/80213 International Search Report dated Apr. 16, 2008.
PCT/US07/82275 International Search Report dated Apr. 18, 2008.
PCT/US07/82775 International Preliminary Report on Patentablity dated Apr. 28,2009.
PCT/US08/11852 International Preliminary Report on Patentability dated Apr. 20, 2010.
PCT/US08/11852 International Search Report dated Dec. 19, 2008.
PCT/US08/50536 International Preliminary Report on Patentability dated Jul. 14, 2009.
PCT/US08/50536 International Search Report dated Jun. 2, 2008.
PCT/US08/60671 International Preliminary Report on Patentability dated Oct. 20, 2009.
PCT/US08/60671 International Search Report dated Sep. 5, 2008.
PCT/US08/64732 International Preliminary Report on Patentability dated Dec. 1, 2009.
PCT/US08/64732 International Search Report dated Sep. 4, 2008.
PCT/US09/41045 International Preliminary Report on Patentability dated Oct. 19, 2010.
PCT/US09/41045 International Search Report dated Aug. 11, 2009.
PCT/US09/50883 International Preliminary Report on Patentability dated Jan. 18, 2011.
PCT/US09/50883 International Search Report dated Nov. 17, 2009.
PCT/US09/69603 International Preliminary Report on Patentability dated Jun. 29, 2011.
PCT/US09/69603 International Search Report dated Nov. 5, 2010.
PCT/US10/28195 International Preliminary Report on Patentability dated Sep. 27, 2011.
PCT/US10/28195 Search Report and Written Opinion dated Jan. 21, 2011.
PCT/US10/28253 International Preliminary Report on Patentability dated Sep. 27, 2011.
PCT/US10/28253 Search Report and Written Opinion dated Dec. 6, 2010.
PCT/US10/28265 International Report on Patentability dated Sep. 27, 2011.
PCT/US10/28265 Search Report and Written Opinion dated Dec. 3, 2010.
PCT/US10/29494 International Preliminary Report on Patentability dated Oct. 4, 2011.
PCT/US10/29494 Search Report and Written Opinion dated Feb. 7, 2011.
PCT/US10/31470 International Preliminary Report on Patentability dated Oct. 18, 2011.
PCT/US10/31470 Search Report and Written Opinion dated Jan. 28, 2011.
PCT/US10/42355 International Preliminary Report on Patentability dated Jan. 17, 2012.
PCT/US10/42355 Search Report dated Sep. 2, 2010.
PCT/US11/032371 International Report on Patentability dated Oct. 16, 2012.
PCT/US11/032371 International Search Report dated Jul. 7, 2011.
PCT/US11/044263 International Search Report, International Preliminary Report on Patentability and Written Opinion dated Feb. 9, 2012.
PCT/US11/051092 International Preliminary Report on Patentability dated Mar. 21, 2013.
PCT/US11/051092 International Search Report dated Mar. 27, 2012.
PCT/US11/051092 Written Opinion dated Mar. 27, 2012.
PCT/US11/22623 International Preliminary Report on Patentability dated Aug. 7, 2012.
PCT/US11/22623 Search Report and Written Opinion dated Mar. 28, 2011.
PCT/US11/29667 International Search Report and Written Opinion dated Jun. 1, 2011.
PCT/US11/67921 International Preliminary Report on Patentability dated Jul. 11, 2013.
PCT/US11/67921 Search Report and Written Opinion dated Jun. 22, 2012.
PCT/US12/040040 International Search Report dated Sep. 7, 2012.
PCT/US12/33367 International Preliminary Report on Patentability dated Oct. 15, 2013.
PCT/US12/33367 International Search Report dated Aug. 1, 2012.
PCT/US12/46545 International Search Report dated Nov. 20, 2012.
PCT/US13/41466 International Search Report and Written Opinion dated Oct. 17, 2013.
PCT/US13/42093 International Search Report and Written Opinion dated Oct. 24, 2013.
PCT/US2011/033225 International Search Report and Written Opinion dated Jul. 7, 2011.
PCT/US2012/60896 International Search Report and Written Opinion dated Dec. 28, 2012.
PCT/US2013/065777 International Search Report and Written Opinion dated Jan. 29, 2014.
PCT/US2014/025017 International Search Report and Written Opinion dated Jul. 7, 2014.
Perry et al., Chemical Engineers Handbook, 5th Edition, McGraw-Hill, New York, 20-106 (1973).
Plas et al., “Tubers and tumors: rapamycin therapy for benign and malignant tumors”, Curr Opin Cell Bio 21: 230-236, (2009).
Poling et al., The Properties of Gases and Liquids. McGraw-Hill. 9:1-9.97 (2001).
Pontari, “Chronic prostatitis/chronic pelvic pain syndrome in elderly men: toward better understanding and treatment,” Drugs Aging 20(15):1111-1115 (2003).
Pontari, “Inflammation and anti-inflammatory therapy in chronic prostatits,” Urology 60(6Suppl):29-33 (2002).
Putkisto, K. et al. “Polymer Coating of Paper Using Dry Surface Treatment—Coating Structure and Performance”, ePlace newsletter, vol. 1, No. 8, pp. 1-20 (2004).
Raganath et al., “Hydrogel matrix entrapping PLGA-paclitaxel microspheres: drug delivery with near zero-order release and implantability advantages for malignant brain tumour,” Pharm Res (Epub) Jun. 20, 2009.
Ranade et al., “Physical characterization of controlled release of paclitaxel from the TAXUS Express2 drug-eluting stent,” J. Biomed Mater. Res. 71(4):625-634 (2004).
Reddy et al., “Inhibition of apoptosis through localized delivery of rapamycin-loaded nanoparticles prevented neointimal hyperplasia and reendothelialized injured artery,” Circ Cardiovasc Interv 1;209-216 (2008).
Ristikankare et al., “Sedation, topical pharnygeal anesthesia and cardiorespiratory safety during gastroscopy,” J. Clin Gastorenterol. 40(1):899-905 (2006).
Sahajanand Medical Technologies (Supralimus Core; Jul. 6, 2008).
Salo et al., “Biofilm formation by Escherichia coli isolated from patients with urinary tract infections,” Clin Nephrol. 71(5):501-507 (2009).
Saxena et al., “Haemodialysis catheter-related bloodstream infections: current treatment options and strategies for prevention,” Swiss Med Wkly 135:127-138 (2005).
Schetsky, L. McDonald, “Shape Memory Alloys”, Encyclopedia of Chemical Technology (3d Ed), John Wiley & Sons vol. 20 pp. 726-736 (1982).
Scheuffler et al., “Crystal Structure of Human Bone Morphogenetic Protein-2 at 2.7 Angstrom resolution,” Journal of Molecular Biology, vol. 287, Issue 1, Mar. 1999, retrieved online at http://www.sciencedirect.com/science/article/pii/S002283699925901.
Schmidt et al., “A Comparison of the Mechanical Performance Characteristics of Seven Drug-Eluting Stent Systems,” Catheterization and Cardiovascular Interventions 73:350-360 (2009).
Schmidt et al., “In vitro measurement of quality parameters of stent-catheter systems,” Biomed Techn 50(S1):1505-1506 (2005).
Schmidt et al., “New aspects of in vitro testing of arterial stents based on the new European standard,” EN 14299, [online] (2009), [retrieved on Mar. 10, 2001] http://www.lib0ev.de/pl/pdf/EN14299.pdf (2009).
Schmidt et al., “Trackability, Crossability, and Pushability of Coronary Stent Systems—An Experimental Approach,” Biomed Techn 47, Erg. 1, S. 124-126 (2002).
Schreiber, S.L. et al., “Atomic Structure of the Rapamycin Human Immunophilin FKBP-12 Complex,” J. Am. Chem. Soc. 113:7433-7435 (1991).
Sen et al., “Topical heparin: A promising agent for the prevention of tracheal stenosis in airway surgery,” J. Surg. Res (Epub ahead of print) Feb. 21, 2009.
Serruys, Patrick et al., Comparison of Coronary-Artery Bypass Surgery and Stenting for the Treatment of Multivessel Disease, N. Engl. J. Med., vol. 344, No. 15, pp. 1117-1124 (2001).
SG201007602-4 Examination Report dated Feb. 13, 2013.
SG201007602-4 Written Opinion dated May 25, 2012.
Shekunov et al. “Crystallization Processes in Pharmaceutical Technology and Drug Delivery Design.” Journal of Crystal Growth 211, pp. 122-136 (2000).
Simpson et al., “Hyaluronan and hyaluronidase in genitourinary tumors.” Front Biosci. 13:5664-5680 (2009).
Smith et al., “Mitomycin C and the endoscopic treatment of laryngotracheal stenosis: are two applications better than one?” Laryngoscope 119(2):272-283 (2009).
Sumathi et al., “Controlled comparison between betamethasone gel and lidocaine jelly applied over tracheal tube to reduce postoperative sore throat, cough, and hoarseness of voice,” Br. J. Anaesth. 100(2):215-218 (2008).
Szabadits et al., “Flexibility and trackability of laser cut coronary stent systems,” Acta of Bioengineering and Biomechanics 11(3):11-18 (2009).
Testa, B. Prodrug research: futile or fertile? Biochem Pharmacol. 68(11):2097-106 (2004).
Thalmann et al., “Long-term experience with bacillus Calmette-Guerin therapy of upper urinary tract transitional cell carcinoma in patients not eligible for surgery,” J Urol. 168(4 Pt 1):1381-1385 (2002).
Torchlin, “Micellar Nanocarriers: Pharmaecutial Perspectives,” Pharmaceutical Research, vol. 24, No. 1, Jan. 2007.
U.S. Appl. No. 11/158,724 Office Action dated Dec. 31, 2013.
U.S. Appl. No. 11/158,724 Office Action dated May 23, 2013.
U.S. Appl. No. 11/158,724 Office Action dated Sep. 17, 2009.
U.S. Appl. No. 11/158,724 Office Action dated Sep. 26, 2012.
U.S. Appl. No. 11/158,724 Office Action dated Sep. 8, 2008.
U.S. Appl. No. 11/158,724 Office Action dated Jun. 25, 2014.
U.S. Appl. No. 11/877,591 Final Action dated Nov. 4, 2013.
U.S. Appl. No. 11/877,591 Office Action dated Feb. 29, 2012.
U.S. Appl. No. 11/877,591 Office Action dated Jul. 1, 2013.
U.S. Appl. No. 11/877,591 Office Action dated Sep. 21, 2012.
U.S. Appl. No. 11/877,591 Office Action dated May 7, 2014.
U.S. Appl. No. 11/995,685 Office Action dated Aug. 20, 2010.
U.S. Appl. No. 11/995,685 Office Action dated Nov. 24, 2009.
U.S. Appl. No. 11/995,687 Office Action dated Apr. 6, 2012.
U.S. Appl. No. 11/995,687 Office Action dated Sep. 28, 2011.
U.S. Appl. No. 12/298,459 Office Action dated Apr. 6, 2012.
U.S. Appl. No. 12/298,459 Office Action dated Aug. 10, 2011.
U.S. Appl. No. 12/298,459 Office Action dated May 31, 2013.
U.S. Appl. No. 12/426,198 Office Action dated Feb. 6, 2012.
U.S. Appl. No. 12/426,198 Office Action dated Feb. 7, 2014.
U.S. Appl. No. 12/426,198 Office Action dated Mar. 23, 2011.
U.S. Appl. No. 12/443,959 Office Action dated Dec. 13, 2012.
U.S. Appl. No. 12/443,959 Office Action dated Feb. 15, 2012.
U.S. Appl. No. 12/504,597 Final Office Action dated Oct. 3, 2012.
U.S. Appl. No. 12/504,597 Office Action dated Apr. 1, 2014.
U.S. Appl. No. 12/504,597 Office Action dated Dec. 5, 2011.
U.S. Appl. No. 12/522,379 Office Action dated Apr. 8, 2014.
U.S. Appl. No. 12/522,379 Final Office Action dated Aug. 28, 2013.
U.S. Appl. No. 12/522,379 Office Action dated Dec. 26, 2012.
U.S. Appl. No. 12/595,848 Office Action dated Jan. 13, 2012.
U.S. Appl. No. 12/595,848 Office Action dated Mar. 15, 2013.
U.S. Appl. No. 12/595,848 Office Action dated Oct. 22, 2013.
U.S. Appl. No. 12/595,848 Office Action dated Jun. 3, 2014.
U.S. Appl. No. 12/601,101 Office Action dated Dec. 27, 2012.
U.S. Appl. No. 12/601,101 Office Action dated Feb. 13, 2014.
U.S. Appl. No. 12/601,101 Office Action dated Mar. 27, 2012.
U.S. Appl. No. 12/601,101 Office Action dated May 22, 2013.
U.S. Appl. No. 12/648,106 Final Office Action dated Sep. 25, 2012.
U.S. Appl. No. 12/648,106 Office Action dated Jan. 30, 2012.
U.S. Appl. No. 12/648,106 Office Action dated Sep. 18, 2013.
U.S. Appl. No. 12/729,156 Final Office Action dated Oct. 16, 2012.
U.S. Appl. No. 12/729,156 Office Action dated Feb. 1, 2012.
U.S. Appl. No. 12/729,156 Office Action dated Feb. 13, 2014.
U.S. Appl. No. 12/729,156 Office Action dated May 8, 2013.
U.S. Appl. No. 12/729,580 Final Action dated Nov. 14, 2013.
U.S. Appl. No. 12/729,580 Office Action dated Apr. 10, 2012.
U.S. Appl. No. 12/729,580 Office Action dated Jan. 22, 2013.
U.S. Appl. No. 12/729,580 Office Action dated Sep. 10, 2014.
U.S. Appl. No. 12/729,603 Final Office Action dated Oct. 10, 2012.
U.S. Appl. No. 12/729,603 Office Action dated Mar. 27, 2012.
U.S. Appl. No. 12/729,603 Office Action dated Jun. 25, 2014.
U.S. Appl. No. 12/738,411 Final Office Action dated Apr. 11, 2013.
U.S. Appl. No. 12/738,411 Office Action dated Aug. 21, 2013.
U.S. Appl. No. 12/738,411 Office Action dated Feb. 6, 2014.
U.S. Appl. No. 12/738,411 Office Action dated May 30, 2014.
U.S. Appl. No. 12/748,134 Office Action dated Jul. 18, 2013.
U.S. Appl. No. 12/751,902 Office Action dated Dec. 19, 2013.
U.S. Appl. No. 12/751,902 Office Action dated Jul. 13, 2012.
U.S. Appl. No. 12/762,007 Final Office Action dated Oct. 22, 2013.
U.S. Appl. No. 12/762,007 Final Office Action dated Apr. 30, 2014.
U.S. Appl. No. 12/762,007 Office action dated Feb. 11, 2013.
U.S. Appl. No. 13/014,632 Office action dated Jan. 10, 2014.
U.S. Appl. No. 13/014,632 Office action dated May 8, 2013.
U.S. Appl. No. 13/086,335 Office action dated May 22, 2013.
U.S. Appl. No. 13/086,335 Office action dated Apr. 4, 2014.
U.S. Appl. No. 13/229,473 Office Action dated Jun. 17, 2013.
U.S. Appl. No. 13/340,472 Office action dated Apr. 26, 2013.
U.S. Appl. No. 13/340,472 Office action dated Jan. 15, 2014.
U.S. Appl. No. 13/340,472 Office action dated Aug. 29, 2014.
U.S. Appl. No. 13/384,216 Final Action dated Nov. 6, 2013.
U.S. Appl. No. 13/384,216 Office action dated Apr. 24, 2013.
U.S. Appl. No. 13/605,904 Office Action dated Jun. 28, 2013.
U.S. Appl. No. 13/605,904 Office Action dated Nov. 27, 2012.
U.S. Appl. No. 13/445,723 Office action dated Mar. 14, 2014.
U.S. Appl. No. 13/090,525 Office action dated Apr. 11, 2014.
U.S. Appl. No. 11/995,685 Office Action dated Jun. 18, 2014.
Unger et al., “Poly(ethylene carbonate): A thermoelastic and biodegradable biomaterial for drug eluting stent coatings?” Journal of Controlled Release, vol. 117, Issue 3, 312-321 (2007).
Verma et al., “Effect of surface properties on nanoparticle-cell interactions,” Small 6(1):12-21 (2010).
Wagenlehner et al., “A pollen extract (Cernilton) in patients with inflammatory chronic prostatitis/chronic pelvic pain syndrome: a multicentre, randomized, prospective, double-blind, placebo-controlled phase 3 study,” Eur Urol 9 (Epub) (Jun. 3, 2009).
Wang et al. Controlled release of sirolimus from a multilayered PLGA stent matrix. Biomaterials 27:5588-95 (2000).
Wang et al., “Treatment with melagatran alone or in combination with thrombolytic therapy reduced ischemic brain injury,” Exp. Neurol 213(1):171-175 (2008).
Warner et al., “Mitomycin C and airway surgery: how well does it work?” Ontolaryngol Head Neck Surg. 138(6):700-709 (2008).
Wermuth, CG Similarity in drugs: reflections on analogue design. Drug Discov Today. 11(7-8):348-54 (2006).
Witjes et al., “Intravesical pharmacotherapy for non-muscle-invasive bladder cancer: a critical analysis of currently available drugs, treatment schedules, and long-term results,” Eur. Urol. 53(1):45-52 (2008).
Wu et al., “Study on the preparation and characterization of biodegradable polylactide/multi-walled carbon nanotubes nanocomposites.” Polymer 48:4449-4458 (2007).
Xu et al., “Biodegradation of poly(l-lactide-co-glycolide tube stents in bile” Polymer Degradation and Stability. 93:811-817 (2008).
Xue et al., “Spray-as-you-go airway topical anesthesia in patients with a difficult airway: a randomized, double-blind comparison of 2% and 4% lidocaine,” Anesth. Analg. 108(2): 536-543 (2009).
Yepes et al., “Tissue-type plasminogen activator in the ischemic brain: more than a thrombolytic,” Trends Neurosci. 32(1):48-55 (2009).
Yousof et al., “Reveratrol exerts its neuroprotective effect by modulating mitochondrial dysfunction and associated cell death during cerebral ischemia,” Brain Res. 1250:242-253 (2009).
Zhou et al. Synthesis and Characterization of Biodegradable Low Molecular Weight Aliphatic Polyesters and Their Use in Protein-Delivery Systems. J Appl Polym Sci 91:1848-56. (2004).
Zilberman et al., Drug-Eluting bioresorbable stents for various applications, Annu Rev Biomed Eng., 8:158-180 (2006).
David Grant, Crystallization Impact on the Nature and Properties of the Crystalline Product, 2003, SSCI, http://www.ssci-inc.com/Information/RecentPublications/ApplicationNotes/CrystallizationImpact/tabid/138/Default.aspx.
Analytical Ultracentrifugation of Polymers and Nanoparticles, W. Machtle and L. Borger, (Springer) 2006, p. 41.
Chalmers, et al. (2007) Wiley and Sons.
European International Search Report of PCT/EP01/05736 dated Oct. 24, 2001.
Finn et al. Differential Response of Delayed Healing . . . Circulation vol. 112 (2005) 270-8.
Greco et al. (Journal of Thermal Analysis and Calorimetry, vol. 72 (2003) 1167-1174.).
Handschumacher, R.E. et al., Purine and Pyrimidine Antimetabolites, Chemotherapeutic Agents, pp. 712-732, Ch. XV1-2, 3rd Edition, Edited by J. Holland, et al., Lea and Febigol, publishers.
Higuchi, Rate of Release of Medicaments from Ointment Bases Containing Drugs in Suspension, Journal of Pharmaceutical Sciences, vol. 50, No. 10, p. 874, Oct. 1961.
Ji, et al., “96-Wellliquid-liquid extraction liquid chromatographytandem mass spectrometry method for the quantitative determination of ABT-578 in human blood samples” Journal of Chromatography B. 805:67-75 (2004).
Ju et al., J. Pharm. Sci. vol. 84, No. 12, 1455-1463.
Levit, et al., “Supercritical CO2 Assisted Electrospinning” J. of Supercritical Fluids, 329-333, vol. 31, Issue 3, (Nov. 2004).
Lewis, D. H., “Controlled Release of Bioactive Agents from Lactides/Glycolide Polymers” in Biodegradable Polymers as Drug Delivery Systems, Chasin, M. and Langer, R., eds., Marcel Decker (1990).
Luzzi, L.A., J. Phann. Psy. 59:1367 (1970).
Park et al., Pharm. Res. (1987) 4(6):457-464.
PCT/EP01/05736 International Preliminary Examination Report dated Jan. 14, 2002.
PCT/EP2000/004658 International Search Report dated Sep. 15, 2000.
PCT/US06/27321 Written Opinion dated Oct. 16, 2007.
PCT/US11/33225 International Search Report and Written Opinion dated Jul. 7, 2011.
PCT/US12/50408 International Search Report dated Oct. 16, 2012.
PCT/US13/41466 International Preliminary Report on Patentability dated Nov. 18, 2014.
PCT/US13/42093 International Preliminary Report on Patentability dated Nov. 25, 2014.
PCT/US14/38117 International Search Report and Written Opinion dated Oct. 7, 2014.
Wang et al. “Synthesis, characterization, biodegradation, and drug delivery application of biodegradable lactic/glycolic acid polymers: I. Synthesis and characterization” J. Biomater. Sci. Polymer Edn. 11(3):301-318 (2000).
Extended European Search Report for Application No. 14797966.0 dated Dec. 19, 2016.
Search Report from Singapore Application No. 2013054127 dated Jul. 26, 2017, 5 pages.
Datenblatt NIRflex® der Firma Medinol, NIRFlex TM Premounted Coronary Stent System, Instructions for Use, Medinol Ingenuity for Life, Doc #912000012 Draft F, Oct. 8, 2003, 18 pages.
Stoeckel et al., “A survey of stent designs”, Minimally Invasive Therapy & Allied Technologies, Jan. 2002, 11 (4), Seite 137-147.
Wenda C. Carlyle et al: “Enhanced drug delivery capabilities from stents coated with absorbable polymer and crystalline drug”, Journal of Controlled Release, vol. 162, No. 3, Sep. 1, 2012 (Sep. 1, 2012 ), pp. 561-567, XP055289527.
“Guidance for Industry / Coronary Drug-Eluting Stents Nonclinical and Clinical Studies”, U.S. Department of Health and Human Services Food Drug Adminstration Center for Devices and Radiological Health (CDRH), Center for Drug-Evaluation and Research (CDER), Mar. 2008, <https://www.fda.gov/media/71521/download>, 89 pages.
Balakrishnan, Brinda, et al. “Intravascular drug release kinetics dictate arterial drug deposition, retention, and distribution.” Journal of Controlled Release 123.2, Nov. 6, 2007, pp. 100-108.
Choi, Jiyeon, et al. “Effect of solvent on drug release and a spray-coated matrix of a sirolimus-eluting stent coated with poly (lactic-co-glycolic acid).” Langmuir 30.33, Publication dated Aug. 4, 2014, pp. 10098-10106.
Medinol Ingenuity for Life, “X-Suit NIR / Bilinary Metallic Stent”, Copyright 2017, <https://www.medinol.com/us/products/x-suit-nir/>, 5 pages.
Medtronic, “EverFlex Self-expanding Peripheral Stent / Vascular Stenting”, last updated Nov. 2017, <https://www .medtronic.com/us-en/healthcareprofessionals/products/cardiovascular/peripheral-biliary-stents/everflex.html>, 6 pages.
Medtronic, “Indications, Safety, and Warnings / IntraStent DoubleStrut LD Biliary Stents”, <https://www.medtronic.com/us-en/healthcareprofessionals/products/cardiovascular/peripheral-biliary-stents/intrastentdoublestrut- ld-biliarv-stent/indicationssafety-warnings.html>, last updated Nov. 2017, 2 pages.
Medtronic, “IntraStent DoubleStrut LD Biliary Stents”, last updated Nov. 2017, <https://www.medtronic.com/us-en/healthcareprofessionals/products/ cardiovascular/peripheral-biliary-stents/intrastentdoublestrut-ld-biliary-stent.html>, 4 pages.
Minami, Yoshiyasu et al., “Endothelial dysfunction following drug-eluting stent implantation: a systematic review of the literature. International Journal of Cardiology”, 165(2), May 10, 2013, pp. 222-228.
Stent: Medline Plus Medical Encyclopedia, National Institutes of Health / U.S. National Library of Medicine, last updated Mar. 23, 2020 <https://medlineplus.gov/ency/article/002303.htm>, 4 pages.
U.S. Department of Health and Human Services Food and Drug Administration Center for Devices and Radiological Health, “Metal Expandable Biliary Stents—Premarket Notificarion (510(k)) Submissions / Guidance for Industry and Food and Drug Administration Staff”, Document issued on Jul. 27, 2019, <https://www.fda.gov/media/72693/download>, 27 pages.

Related Publications (1)

	Number	Date	Country
	20140277401 A1	Sep 2014	US

Provisional Applications (1)

	Number	Date	Country
	61777230	Mar 2013	US

Bioabsorbable biomedical implants

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

Field of Search

CPC

International Classifications

Abstract