Patent Application
20160058568
This present invention generally relates to spinal fixation devices, and spinal implants, suitable for use in orthopedic applications in which the implant is subjected to dynamic, compressive loads. The implants of the present invention may be used in procedures such as cervical fusion, Anterior Lumbar Interbody Fusion (ALIF), Posterior Lumbar Interbody Fusion (PLIF), and Transforaminal Lumbar Interbody Fusion (TLIF). They may be implanted between adjacent vertebrae to treat or prevent back pain in patients with conditions such as degenerative disc disease. The present invention also relates to methods of making bioactive implants and apparatuses for manipulating them.
Lower back and neck pain is oftentimes attributed to the rupture or degeneration of intervertebral discs due to degenerative disk disease, spondylolisthesis, deformative disorders, trauma, tumors and the like. This pain typically results from the compression of spinal nerve roots by damaged discs between the vertebra, the collapse of the disc, or the resulting adverse effects of bearing the patient's body weight through a damaged, unstable vertebral structure. To remedy this, spinal implants have been inserted between vertebral bodies to restore the structure to its previous height and conformation and stabilize motion at that spinal segment.
Surgical treatments to restore vertebral height typically involve excision of the ruptured soft disc between two vertebrae, usually with subsequent insertion of a spinal implant or interbody fusion device to fuse and stabilize the segment. Spinal implants or interbody fusion devices have been used to fuse adjacent vertebral bodies since the 1960's. Currently, spinal implant devices are comprised of either allograft materials, natural, porous materials such as coral, or synthetic materials. A major drawback associated with allograft devices is the risk of disease transmission. Further, since companies that provide allograft implants obtain their supply from donor tissue banks, there tend to be limitations on supply. Synthetic devices, which are predominantly comprised of metals, such as titanium, also present drawbacks. For instance, the appearance of metal spinal implants on x-ray tends to have an artificial fuzziness, which makes assessment of fusion (one of the clinical criteria of a successful interbody fusion device) very difficult. Moreover, synthetic materials of this type (metals) tend to have mechanical properties that are unevenly matched to bone. Coral and other natural materials generally perform poorly.
Accordingly, there is a need in the art for a synthetic spinal implant material that does not carry the risk of disease transmission as with allograft materials.
There is also a need for a synthetic spinal implant material with a radiopacity similar to bone. A radiopacity similar to bone would allow for visualization of the implant between the vertebrae to assess radiographic fusion without distortion.
Further, there is a need for implants with mechanical properties similar to that of bone that can share the physiologic, dynamic compressive loads rather than shield them.
Moreover, there is a need for implants that are comprised of a material that bonds directly to bone and is bioactive.
In addition to the material limitations associated with existing implants on the market, there is also a need to provide spinal implants that are anatomically shaped with proper geometry and features to prevent expulsion or retropulsion. The term “expulsion” as used herein relates to the migration of the implant device in a forward (or backward) direction from the intervertebral space. Moreover, there is a need for a device with an increased surface area to allow for optimal contact with the cortical bone to prevent subsidence or sinking of the implant into each adjacent vertebra. There is a need to provide an implant that is bioactive with an open geometry for packing with graft materials that allows enhanced fusion between the endplates of adjacent vertebrae both via the bioactive surface of the implant and a preferred graft-packed opening.
The invention will be more clearly understood when considered in conjunction with the drawing figures, wherein:
a and 3b provide side views illustrating the cervical implant 10 with and without a lordotic angle, respectively.
a through 47c provide a front view of the insertion tool 500 being used to adjust the position of the implant 10 between the two vertebral bodies.
a provides a radiograph of an implant of the present invention after insertion between adjacent vertebrae in a sheep spine, and
a, b, c provide implants of the present invention with basic or wave-like tooth profile, pyramid tooth profile, and oblique tooth profile, respectively.
The present invention provides spinal implants that have a radiopacity similar to bone for facilitating radiographic assessment of fusion. The present invention also provides spinal implants having properties and geometries that enhance bone contact, stability and fusion between adjacent vertebral bodies. The implants of the present invention are comprised of bioactive and biocompatible materials capable of withstanding physiologic dynamic, compressive loads. As used herein, bioactive relates to the chemical formation of a calcium phosphate layer, such as, via ion exchange between surrounding fluid and the implant material. More broadly, it also relates to a material that elicits a reaction which leads to bone formation or attachment into or adjacent to the implant, for example, bone formation or apposition directly to the implant usually without intervening fibrous tissue. Biocompatible as used herein relates to a material that does not invoke a prolonged, adverse immunologic or host response.
The present invention also provides methods for making such implants and instrumentation for inserting same. In one embodiment of the present invention, there is provided a spinal implant comprised of a top and a bottom surface having a substantially trapezoidal cross-section, a plurality of wave-like protrusions, and at least one opening. The top and bottom surface are preferably substantially convex with respect to each other; and have a pair of medial and lateral sides that extend between the top and bottom surfaces. The medial and lateral sides preferably have at least one indentation and at least one opening. A pair of anterior and posterior sides preferably extends between the top and bottom surfaces and contacts at least a portion of the pair of medial and lateral sides. The anterior or posterior sides also preferably have at least one opening.
In another embodiment of the present invention the implant has a generally trapezoidal, ring-shaped body with bowed sides and convex superior and inferior surfaces. Such configuration is particularly suitable for use in orthopedic applications, such as in the spine, as a spinal implant. The implant is anatomically shaped to prevent subsidence and preferably includes projections, ridges, warps or teeth on the superior and inferior surfaces for gripping adjacent bone and preventing migration of the device. The implant also preferably has at least one opening which accommodates insertion of the device and at least one opening which accommodates packing of the implant with graft material to facilitate the formation of a solid fusion structure.
In certain embodiments of the present invention, the implant materials of the present invention can be comprised of a biocompatible polymeric matrix reinforced or coated with bioactive fillers and fibers. The implants can probably be comprised of a diurethane dimethacrylate (DUDMA) and tri-ethylene glycol dimethacrylate (TEGDMA) blended resin and a plurality of fillers and fibers including bioactive fillers and E-glass fibers. The implants may also be comprised of a variety of other monomers and fillers as described herein.
The present invention provides bioactive and biocompatible implant materials for formulation of shaped bodies capable of withstanding large dynamic, compressive loads, especially spinal implants. Further, the implant materials of the present invention overcome the risks associated with disease transmission present with allograft devices. Moreover, the implant materials of the present invention exhibit a radiopacity similar to that of bone for radiographic assessment of fusion as described in U.S. Pat. No. 6,987,136, issued Jan. 17, 2006, and incorporated herein by reference in its entirety.
The materials of this invention are preferably comprised of a biocompatible, hardenable polymeric matrix reinforced with bioactive and non-bioactive fillers. The materials can be comprised of about 10% to about 90% by weight of the polymeric matrix and about 10% to about 90% by weight of one or more fillers. The materials can also be comprised of about 20% to about 50% by weight of the polymeric matrix and about 50% to about 80% by weight of one or more fillers. In order to promote bone bonding to the implants, the implants of the present invention can be comprised of a bioactive material that can comprise a polymeric blended resin reinforced with bioactive ceramic fillers. Examples of such bioactive materials can be found, for example, in U.S. Pat. Nos. 5,681,872 and 5,914,356 and 6,987,136, which are assigned to the assignee of the present invention and incorporated herein by reference in their entireties.
The polymeric matrixes of the implant materials are comprised of polymerizable monomer, monomers, dimers or trimers. They can comprise ethylenically unsaturated monomers or even an acrylate functional group. The term “monomers,” as used herein, can also represent dimers, trimers, resins, resin components, or any other polymerizable component. Examples of the monomers include, but are not limited to, DUDMA, bisphenol-A-glycidyl methacrylate (bis GMA), TEGDMA, ethoxylated bisphenol-A-dimethacrylate (bis-EMA), or combinations thereof. Still, further examples of monomers that can be used in the present invention include the adducts of 2,2,3-trimethylhexane diisocyanate with hydroxyethyl methacrylate, hydroxypropyl methacrylate, and other hydroxyacrylic acrylic species can also be used. Other examples of polymerizable species that can be used in the present invention include those disclosed in U.S. Pat. Nos. 5,681,872 and 5,914,356, and 6,987,136, which are incorporated herein by reference in their entireties.
Methyl methacrylate, ethyl methacrylate, propyl methacrylate, higher methacrylates, acrylates, ethacrylates, and similar species can be employed as all or part of the polymerizable materials of the implant materials of the present invention. It is also possible to employ other types of polymerizable material such as epoxide compounds, polyurethane-precursor species, and a wide host of other materials. For example, other monomers useful in the production of hardenable compositions of this invention include methyl-, ethyl, isopropyl-, tertbutyloctyl-, dodecyl-, cyclohexyl-, chloromethyl-, tetrachloroethyl-, perfluorooctyl-, hydroxyethyl-, hydroxypropyl-, hydroxybutyl-, 3-hydroxyphenyl-, 4-hydroxphenyl-, aminoethyl-, aminophenyl-, thiophenyl-, acrylate, methacrylate, ethacrylate, propacrylate, butacrylate, and chloromethacrylate, as well as the homologous mono-acrylic acid esters of bisphenol-A, dihydroxydiphenyl sulfone, dihydroxydiphenyl ether, dihydroxybiphenyl, dihydroxydiphenyl sulfoxide, and 2,2bis(4-hydroxy-2,3,5,6-tetrafluorophenyl)propane. Polymerizable monomers capable of sustaining a polymerization reaction such as the di-, tri-, and higher acrylic ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, trimethylene glycol dimethacrylate, trimethylol propane trimethacrylate, analogous acrylates, and similar species are also useful. Polyetheretherketone (PEEK), carbon fiber reinforced PEEK, and carbon fiber reinforced barium sulfate impregnated Peek may also be used. Other polymers that may be used include polyethlene and polylactic acid (PLA). PLA may be used with pteroylgutamic acid (PGA) or PGA may be used without PLA. Poly-L-lactic acid (PLLA) may also be used. It is also possible to employ mixtures of more than two polymerizable species to good effect.
The implant materials can also comprise non-bioactive substances. Titanium, stainless steel, and cobalt chromium may also be used in the substances that comprise the spinal implant.
The implant materials of the present invention can further comprise polymeric additives that include, but are not limited to, polymerization inhibitors, polymerization activators, polymerization initiators, stabilizers such as UV-9, radiopacifiers, reinforcing components (i.e., fibers, particles, micro spheres, flakes, etc.), bioactive fillers, neutralizing resins, diluting resins, antibiotic agents, coloring agents, plasticizers, coupling agents, free radical generators, radiographic contrast agents, and antibiotics.
In many embodiments, the implant materials include a blended resin of DUDMA to impart strength, TEGDMA to impart flexibility, a benzoyl peroxide initiator (BPO) or any peroxide initiator that is consumed during the polymelization reaction, and at least one polymer stabilizer. The implant materials can also include a plurality of fillers and fibers. The fillers can be of the combeite type, such as the combeite filler described in U.S. Pat. Nos. 5,681,872 and 5,914,356, incorporated herein by reference in their entireties, to render the material bioactive and encourage direct bone bonding. Alternatively, the filler can be selected from a group of fillers including, but not limited to, borosilicate, silica, Wollastonite, hydroxyapatite (HA), beta-tricalcium phosphate, calcium sulfate, alumina, and the like. In embodiments where the implants further comprise fibers, the fibers can further include E-glass fibers of the composition type [SiO2 CaO Al2O3 B2O3], A-glass fibers, silica, or a plurality of other fibers including but not limited to Kevlar and carbon fibers for imparting toughness and strength to the implant. In certain embodiments, the fillers and fibers are surface treated for incorporation and bonding between them and the resin. For example, the fillers and fibers can be silanated, silicone-oil treated, or provided with coupling agents such alumina, titania, or zirconia coupling agents.
In one embodiment of the present invention, the monomers, fillers, and other additives are blended together to form a paste composition. The paste compositions are easily mixed via a low speed, high shear rotary mixer. The duration of the blending operation will vary depending upon the constituents that comprise the paste composition precursors. In one embodiment, the blending of the monomers and other additives within the paste composition precursors activates the polymerization of the composition. In another embodiment, exposure to heat either during or after blending activates the polymerization. The exposure can occur in temperature ranges of about 40° C. to about 180° C. or about 60° C. to about 120° C. in some instances.
The implant materials of the present invention can be comprised of a one-paste system or combined with two or more paste compositions to form a multiple paste system. Depending upon whether the implant material is a one paste or multiple paste system determines the hardening of the material. The paste compositions of the present invention can be hardened by thermal energy, photochemical energy, and treatment by chemical process. One skilled in the art may also choose to do so in a controlled fashion. In certain embodiments wherein the implant materials comprise a one-paste system, the paste composition is hardened or cured via exposure to heat or light. Alternatively, the paste composition could be cured via gamma radiation. In some embodiments, additional exposure to gamma radiation can impart additional strength. In other embodiments wherein the implant materials comprise a multiple paste system, the paste compositions are admixed and hardened via thermal energy or heat cured. The paste compositions can also be chemically cured via catalyst or redox systems. It will be understood, however, that a wide variety of polymerization systems and materials for use therein can be employed to good advantage in connection with the present invention and all such systems are contemplated hereby. Depending upon the system that is employed, the paste composition can generally comprise heat-culling catalysts, photopolymerization, or redox (i.e. N,N(dihydroxyethyl)-p-toluidine(DHEPT), BPO, Fe(II), tertiary butyl hydro-peroxide (t-BHP)) initiators. Polymerization materials and catalytic systems known in the art and not inconsistent with the objects of this invention can be employed.
In multiple paste systems where heat curing is used to harden the composition, a catalytic system is employed such that when two components of the hardenable composition are mixed together, the catalytic action begins, leading to hardening. This system is familiar and can be applied to a wide variety of polymerizable species including many which are suitable in the present invention. Radical initiators such as peroxides, especially benzoyl peroxide (also called dibenzoyl peroxide) are conventional, economic, and convenient. A stabilizer such as butyl hydroxy toluene is customary, as is employment of co-catalysts like dimethyl-p-toluidine, N-N-substituted toluidine, and other conventional catalysts including tertiary amine structures with double bond functionality like diethyl aminoethyl methacrylate and N,N-dimethyl-p-toluidine. In general, one of the pastes incorporates both the radical initiator and stabilizer, such as a peroxide, and the other paste incorporates the accelerator, such as an amine or toluidine. Curing is initiated by an oxidation-reduction mechanism upon mixing the two pastes together.
In paste systems where culling via exposure to heat or other means is used to harden the composition, a photoinitiation system can be included with the hardenable compositions and the same caused to be activated by exposure to actinic light of a suitable wavelength. Both ultraviolet and visible photocuring systems are known for use in restorative surgery and dentistry and any such system can be employed herein. Exemplary systems are described in U.S. Pat. No. 4,110,184 to Dart et al., U.S. Pat. No. 4,698,373 to Tateosian et al., U.S. Pat. No. 4,491,453 to Koblitz et al., and U.S. Pat. No. 4,801,528 to Bennett, which are incorporated herein by reference in their entireties to provide enablement for such known systems.
A particularly useful system employs visible light culling, thus avoiding the potential danger inherent in culling with ultraviolet radiation. Visible light culling has been well refined in the dental field and the same can also be applied to restorations of bony tissues. Quinones, as a class, find wide utility as photochemical initiators for visible light sensitizing systems, preferably when the same are admixed with tertiary amines. Some skilled artisans may prefer that an alpha diketone (quinone) such as camphoroquinone or biacetyl be admixed with an amine reducing agent such as n-alkyl dialkanolamine or trialkanolamine. Other such photo-initiator systems include a 2-benzyl-2-(dimethylamino)-4′-morpholinobutyrophenone, or 50%/50% weight composition of 2-hydroxyethyl-2-methyl-1-phenyl-1-propanone and diphenyl(2,4,6-trimethylbenzyl)phosphine oxide. However, other such curing systems or combinations of curing systems can also be employed with the materials of the present invention.
In some embodiments, one or more fillers are blended into the paste composition after the monomers and other additives comprising the resin blend have been combined. The fillers are preferably added incrementally to avoid binding during the blending process. A vacuum may be applied during blending to minimize porosity and dusting. In embodiments complising multiple fillers, such as E-glass fibers, borosilicate fillers, silica fillers, and combeite fillers, the E-glass fibers may be added first followed by the remaining fillers in a designated order. Alternatively, one or more fillers may be pre-blended together prior to incorporation into the resin blend. After the filler has been combined with the resin mixture, the completed paste mixture may be agitated via a vibrating table, ultrasonic, or similar means for a period of time ranging from about 5 minutes to about 60 minutes to further reduce porosity. A vacuum may be applied during the agitation step.
Although the uses described above are exemplary for the present invention, there are other embodiments that may be foreseen by those skilled in the art. Within the dental field, the implants of the present invention can have use as dental crowns (temporary or crown) and dental implants, including Maryland bridges. The implant materials can also have use as implants for other areas of the animal body. Such foreseeable implants include cochlear, cranial, tumor, sternum, or other custom implants that can be MRI compatible or functional shapes made for the body. Other embodiments can be used for formulation of universal plates for orthopedic use, bone screws, rods, and pins for orthopedic use (IM nails, femoral rods or plugs, long bone fractures, etc.), tendon anchors, suture anchors and tacks, graft retainers, and marrow sampling ports.
Other uses include non-articulating artificial joint surfaces, sensor anchors or housings, bone spacers or wedges (tibial, femoral), cartilage beds or anchors, or drug delivery. It is also foreseeable that the implant materials can be used in methods for repairing the iliac harvest site. The materials can be incorporated into drug delivery beads into bone or in interbody balls. There can also be applications for mandibular joints (TMJ) and orbital reconstruction.
One embodiment of the present invention involves machining of the implantable materials into morsels for use in methods to treat segmental defects. The morsels can also be used for minimally invasive load bearing applications. The material can be made into a mesh for postero-lateral fusion or cages for other materials. Other embodiments involve the material being used as a cannulated screw with peripheral holes used in methods for treating vertebral augmentation. The present invention can have embodiments involving synthetic bones.
The bioactive implant material may be formed into a variety of shapes for use as spinal implantation or spinal fixation devices. In one embodiment, the implant material is preferably formed into a cervical implant device. While the present invention is described in terms of the implant material of the present invention, it is understood that other materials may be used to form the cervical implant of the present invention.
The implant also comprises a top surface 20 and a bottom surface 30 that is generally opposite the top surface 20. The top 20 and bottom surfaces 30 can also be convex, or outwardly curved, in the longitudinal cross-section. The curvature and shape of each side grants the implant superior anatomical compatibility. The surfaces also maximize contact with cortical bone to minimize subsidence of the implant into the endplates.
The top 20 and bottom 30 surfaces further include a plurality of projections 25, preferably wave-like or scalloped in shape (i.e., pointed apex with rounded valleys), for gripping adjacent vertebrae. The scalloped shape tooth design eliminates the stress concentration typically associated with other tooth designs and more evenly distributes the compressive physiologic loads from the bone to the implant. The projections 25 can be substantially uniform, upwardly protruding ribs. One skilled in the art would recognize these projections 25 as being substantially uniform, upwardly protruding, elongated ribs separated by concave channels. In alternative embodiments, the projections are randomly disposed or, in other words, situated in various directions. These projections 25 may also be upwardly protruding spikes. The wave-like shape of the projections 25 increases the surface area of the implant for maximal vertebral contact. Further, the wave-like projections 25 provide significant resistance to expulsion and retropulsion. In certain preferred embodiments, the projections 25 have an angular pitch of between 1.75 degrees to 1.9 degrees, a minimum depth of 0.022 inches, and an internal radius of about 0.022 inches. Other dimensional sizes of the projections 25 would not depart from the present invention including upwardly protruding spikes.
a and 3b illustrate two alternative embodiments of the present invention.
In
The implant also has a handling feature that may comprise at least one pair of elongated side recesses 43 and 53 for receiving forceps and a front recess 63 for receiving an impaction tool. The front recess 63 may be used in conjunction with the anterior side 60 and front opening 65 as to communicate with an implant holder or insertion tool. The front recess 63 may be elongated with a major axis that is substantially transverse. The front recess 63 may have an aperture, the front opening 65, formed therein. This handling feature allows for handling and insertion of the spinal implant using instruments such as forceps. In some embodiments, the handling feature consists of only the front recess 63. In
In
The bioactive material of the present invention may also be formed into an implant suitable for ALIF procedures. ALIF implant devices are generally suitable for implantation in the lumbar regions of the spine.
Also in
Similar to the cervical implant 10, the ALIF implant has a major recess 135 that forms a through-aperture. This shape maximizes contact with the cortical bone in the thoracic and lumbar regions. In preferred embodiments, the top 140 and bottom 150 surfaces are substantially identical in size and shape. The major recess 135 also maximizes the chances of fusion because graft or resorbable material may be packed within implant 10. It should be noted that in preferred embodiments, posterior side 190 does not have an opening therethrough. This is to prevent leakage of graft materials from the major recess 135 into the spinal canal.
The implant also has a handling feature comprising recesses 147 and 157 along the top 140 and bottom 150 surfaces extending from either the anterior 180 and posterior 190 sides that act as guide rails and at least one recess 185 in the anterior or sidewalls 160 for receiving an impaction tool.
The bioactive material of the present invention may also be formed into an implant suitable as for PLIF procedures. PLIF implant devices are generally suitable for implantation in the lumbar regions of the spine.
The PLIF implant 240 of the present invention may be in a variety of different sizes to accommodate differences in the patient's anatomy or the location in the spine. As
The implant also comprises a major recess 245 formed in the body creating a longitudinal through-aperture in communication with the top 250 and bottom 260 surfaces, at least one minor recess 275 formed in the body creating a latitudinal through-aperture in communication with the medial 280 and lateral 270 sides, both through apertures in communication with each other. The convergence of these through-apertures forms a cavity inside the implant in which graft material may be placed. This cavity formed by the through-apertures promotes bone growth and fusion between the adjoining vertebral bodies. Opening 245 may be packed with graft material to promote bone growth and fusion. Graft materials suitable for this purpose includes any of the materials disclosed herein. Blood and other biological fluids can be provided to the graft material through the minor recess 275.
The implant also comprises a handling feature comprising a pair of anterior recesses 273 formed at points where the anterior 290 side communicates with the medial 280 and lateral 270 sides. The anterior recesses 273 are used for receiving a manipulator. There are also a pair of posterior recess 283 formed at points where the posterior 300 side communicates with the medial 280 and lateral sides. The handling feature also includes a front opening 295 formed in the anterior 290 side. The handling feature facilitates the handling and insertion of the spinal implant into an intervertebral space.
In
Implant 240 may further include an opening 295 in posterior side 300, that is preferably internally threaded to accommodate an insertion tool, but that does not completely extend through the thickness of the posterior wall. This facet of the design is a safety feature implemented to prevent leakage of graft materials and the like, that may be placed in the hollow interior of the implant, into the spinal canal.
Implant 240 may be used alone or in conjunction with a complimentary implant. The two implants can be placed alongside one another as in a mirror image with the lateral 270 sides facing one another. This configuration allows bone graft material to be placed between two implants 240 and provides for maximum contact between natural bone and the implants.
The bioactive material of the present invention may also be formed into an implant (
In another embodiment of the present invention, the TLIF implant x1 of the present invention may be in a variety of different sizes to accommodate differences in patient's anatomy or the location of the spine that the implant x1 will be inserted. The TLIF implant x1 may be a variety of different sizes to accommodate differences in the patient's anatomy or the location in the spine. As
Top surface and bottom surface x2 and x3 further define at least one major recess x5 to promote bone growth and fusion between the adjoining vertebral bodies. The major recess x5 creates a longitudinal through-aperture in communication with the top x2 and bottom x3 surfaces. The major recess x5 may be packed with graft material to further promote bone growth and fusion. Graft materials suitable for this purpose includes any of the materials disclosed herein.
As
The implant also comprises a handling feature comprising a pair of anterior recesses x11 formed at points where the anterior x6 side communicates with the medial x8 and lateral x9 sides and a pair of posterior recess x10 formed at points where the posterior x7 side communicates with the medial x8 and lateral x9 sides. The pairs of recesses (x10 and x11) may be used for communication with a manipulator or instrument, such as, forceps. The handling feature also includes a front recess x14 formed in the anterior x6 side and a rear recess formed in the postelior x7 side both communicating with a through-aperture. This through-aperture is also in communication with the cavity formed in the spinal implant by the longitudinal and latitudinal through-apertures. The handling feature facilitates the handling and insertion of the spinal implant into an intervertebral space.
In certain embodiments, medial x8 and lateral x9 sides may further comprise at least one opening x12 and x13 to allow fluid to enter the interior of the implant after insertion to provide graft material placed in the center of the implant with blood or other biological fluids.
Implant x1 may further include an opening x14 in both of the anterior x6 and posterior x7 sides that may be internally threaded to accommodate an insertion tool. The front recess x14 may have an internal taper to mate with a tapered insertion instrument.
As shown in
The TLIF implant of the present invention is designed to engage the cortical rim of the vertebrae, the strongest portion of the vertebrae, and, as such, increases biomechanical stability. Additionally, the placement of this type of implant is generally less invasive and less destructive than other procedures, and may be cost effective since only one implant is used.
The present invention also provides surgical instrumentation to aid in the insertion, placement, or removal of the implants of the present invention.
An exemplary implant material for the manufacture of spinal implants in accordance with the invention was formulated to exhibit biocompatibility and bioactivity for bone bonding, radiopacity similar to bone in order to be able to assess fusion, mechanical strength to support physiologic loads, and bone-like stiffness to allow for good load sharing among the elements of the spine.
One implant material includes a polymeric blended resin, comprising 20% to about 50% by weight of the implant material total composition. The resin blend can be further comprised of from about 30% to about 90% by weight of resin OUOMA, about 10% to about 0.25% by weight of butyrated hydroxy toluene (BHT).
The remainder of the implant material is comprised of a plurality of fillers. The fillers can be further comprised up to about 40% by weight of filler surface treated E-glass® fibers to impart fracture toughness and mechanical strength. The filler also can have an average length of about 3000 μm or less and an average diameter range of about 5 μm to 50 μm; about 5% to about 50% by weight of filler surface treated, silanated combeite filler having bioactive characteristics which promote bone bonding; up to about 50% by weight of filler of a surface treated borosilicate glass filler having an average diameter of −10 μm (e.g., 90% of the particles have a diameter of less than 10 μm, measured by laser analysis); and up to about 30% by weight of filler of a surface treated silica for imparting mechanical strength and to act as a rheology modifier. In this particular example, the filler is comprised of about 20% by weight surface treated E-glass® fibers, about 20% by weight of filler surface treated, silanated combeite filler, about 23% by weight of filler of a surface treated borosilicate glass filler, and about 5% by weight of filler is surface treated silica. Once all components are combined, the formulated material is hardened via conventional heating processes, which initiates the polymerization reaction.
Quantitative Evaluation: Three tensile bar samples of polymerized bioactive material of the type described herein, approximately 4 mm in thickness, were arranged onto x-ray film, and a 16-step Aluminum step was placed on top. The 10-mm thick Aluminum step was placed so that it was partly shielding a polymerized sample and partly over x-ray film only (these materials were situated in a Faxitron x-ray cabinet). The use of an Aluminum background allowed for more reproducible comparison between x-rays than the use of exposed film alone. The other two samples were placed at the ends of the wedge in order to balance it.
The lowest stage in the Faxitron cabinet was used and its focus-film distance was 50 mm. The 4-mm thick samples were exposed using appropriate exposure time and voltage (180 sec., 80 kVp). A background optical density ranging from 0.8 to 1.2 defined an appropriate exposure.
After the film had been exposed to x-rays, it was removed from the Faxitron and developed.
Using the densitometer, Background (B), Sample(S) and Aluminum (A) density values were recorded.
The same process was used to determine the radiopacity values of gamma irradiated material as prepared in accordance with Example 1 above.
The percent relative linear attenuation coefficient, α, was calculated as follows:
where:
Quantitatively, the material, before gamma irradiation, had an average radiopacity value of 45.55.
Quantitatively, the material, after gamma irradiation, had an average radiopacity value of 42.94.
A total of three lots of polymerized bioactive material consisting of three samples per lot of material was evaluated and compared directly to Aluminum for radiopacity determination. All testing was conducted in accordance with Orthovita's Technical Operating Procedure. Results summarized in the preceding tables indicate that the bioactive spinal material has an average radiopacity value of 45.55 before gamma irradiation and a radiopacity value of 42.94 after gamma irradiation. Statistical analysis of results demonstrates that there is not a significant amount of variance between lots and data records, p=0.445 for pre-gamma data and p=0.624 for post-gamma data. Statistical analysis also shows that there is not a significant amount of variance between pre and post gamma data. This indicates that gamma irradiation does not significantly affect the radiopacity of the material.
Radiopacity of polymerized material for medical use is clinically important due to the frequency of using x-rays in measuring the placement, function, form, and effectiveness of the material. Both pre and post gamma bioactive implants have a radiopacity value that will allow for good radiographic viewing that will aid in the placement and postoperative monitoring of spinal implants made from this material. Radiopacity values for the bioactive spinal implant material of the present invention compare favorably with human bone, which has a radiopacity range of between 24 to 52.
As observed in
Samples were prepared using the bioactive material described herein. Tests were performed using ASTM Guidelines on an Instron Model 8516 in order to obtain ranges of values of mechanical properties of the material as shown in the table below.
Bioactivity testing was performed on disc shaped implants comprised of the material described herein. Bioactivity for this Example was defined as the ability of the implant to form a calcium phosphate layer on its surface.
Uncured samples of the material described in Example 1 were injected into 5 cc syringes. The material was heated at 100° C. for 1 hour for complete polymerization. The rods formed within the syringe were cut into thin disks (approximately 1 mm thick) using a Buehler diamond blade saw. Simulated body fluid (SBF) was prepared according to the Kokubo recipe (fluid which simulates blood plasma) and using a balance, 250 grams of simulated body fluid was weighed into 5 high density polyethylene (HDPE) bottles. One disk of material was placed in each of the five bottles. The containers of SBF containing the disks were placed at 37° C. for specified intervals. The time intervals were 6, 12, 19, 30, and 50 days. A sample size of 1 disk was prepared at each time period. At these time points, one disk of material was removed from its bottle. The sample was dried with compressed air prior to analysis. The SBF was not analyzed prior to immersion of samples and was discarded after the last sample was removed.
As a non-destructive test, Fourier Transform Infrared Spectroscopy (FTIR) was performed first on the samples. The samples were analyzed using the Nicolet Instruments Magna 560 FTIR. The stage used for this analysis was a single-bounce Attenuated Total Reflectance (ATR) with a diamond crystal and KRS-5 lenses. This stage permitted a surface analysis of the composites through the entire mid-infrared spectrum from 4000 to 400 cm−1 samples were analyzed at a 4 cm−1 resolution. The samples were placed in direct contact with the ATR crystal. Contact was maximized via an anvil on the opposite side of the sample. Spectra were collected on several areas of the composite samples. At each time point, spectra were analyzed for the presence of key calcium phosphate bands as compared to the Day 0 control. [0158] After FTIR analysis, the same samples were then used for Scanning Electron Microscopy/Energy Dispersive Spectroscopy (SEM/EDS). Samples were coated with a thin layer of gold-palladium using a Hummer Sputter Coater. Samples were painted with a small amount of conductive silver paint, when necessary. The operation procedure of the SEM analysis followed the standard procedure for the operation of the JEOL JSM-840A and the EDS analysis. A few of the thin disks were cut exposing the cross-section of the composite. The cross-sections were embedded in epoxy resin revealing the cut surface. Upon complete curing of the epoxy, samples were polished on the Buehler EcoMet3. Final polishing consisted of a 1-micron diamond suspension.
The characterization of bioactivity of the polymerized composite surface by scanning electron microscopy consisted of the following parameters: appearance of calcium phosphate deposition (white in back-scattered electron imaging “BSEI” mode) and thickness of calcium phosphate layer. The characterization of bioactivity of the polymerized composite surface by energy dispersive spectroscopy consisted of the following parameters: calcium and phosphorous detection and reduction in sodium levels at a bioactive filler.
The Rhakoss FTIR results are shown in
The following table outlines the peaks seen on the material in comparison with hydroxyapatite at Day 50 and the molecular assignments:
Day 0 back-scattered electron (BSE) image of a cross-section of the material is illustrated in
By 50 days, the material exhibited a thick, dense CaP layer. Again, this layer covered the entire surface of the composite. The CaP crystals were mature with the appearance of stacked plates. The CaP thickness was measured as approximately 10 microns, and was interdigitated into bioactive fillers at the surface of the composite.
The early FTIR results showed few spectral changes in the material. Both the Day 6 and Day 19 samples showed the same type of strong organic absorptions as seen in the Day 0 sample.
By Day 50, the material exhibited a thick surface coating of calcium phosphate. Spectra taken at various locations on the material showed only inorganic phosphate absorbencies, and none of the organic bands seen in the previous samples (Day 0, 6, and 19). The depth of penetration for this FTIR technique is 2-microns. This indicates that the thickness of the calcium phosphate growth is at least 2-microns thick.
The Day 50 spectra were compared against several types of calcium phosphates in the User library. The best spectral match for both samples was hydroxyapatite. This close match indicates that hydroxyapatite is the calcium phosphate species growing on the sample surface. The primary hydroxyapatite band seen occurs around 1014 cm−1. This band demonstrates a more resolved hydroxyapatite shoulder at 955 cm−1, pointing to a mature species.
At the Day 50 time period, the matelial appears to have a larger surface coverage of calcium phosphate and a thickness of CaP deposition. The evaluations of the cross-sectioned samples provided an accurate measurement of the CaP thickness. Also, the CaP layer was evaluated for its interdigitation into the composite. Several observations of the CaP migrating into a bioactive E-glass ceramic filler at the surface were noted.
Based on the results presented herein, the material of the present invention can be described as bioactive.
Static compression was performed on 6 spinal implants of the type shown in
Fatigue testing was performed on 6 spinal implants of the type shown in
An axial compression test was performed on a spinal implant of the type represented in
Implant failure occurred at approximately 41 kN (about 9000 lbf), approximately 12 times body weight.
An axial compression test was performed on two spinal implants of the type represented in
Pull-out testing of various implants was performed in order to evaluate various teeth profiles. Implants of the type shown in
For testing, each implant from each group was placed between foam bone squares in an MTS with a preload of 500 N, a value chosen for its relevance to the lumbar spine. Pull-out tests were performed at 0.4 mm/s and load-displacement was recorded. The maximum average pull-out load for the basic design was approximately 1000 N, for the pyramid design was approximately 650N and for the oblique design was approximately 710N. The basic tooth profile appeared to have the greatest pull-out resistance based on this test-in which the pull was in the AP direction.
Samples of a bioactive spinal implant material were tested for biocompatibility using ISO Guidelines 10993-1, Biological evaluation of medical devices. Under these guidelines and in compliance with U.S. Food and Drug Administration's Good Laboratory Practice Regulation, 21 CPR, Part 58, the material was evaluated for cytotoxicity, sensitization, intracutaneous reactivity, acute toxicity, and genotoxicity. All results were negative and showed the material to be non-cytotoxic, non-allergenic, a non-irritant, non-toxic, non-mutagenic, and non-genotoxic. In addition, material exhibits a degree of polymerization above 98% and analysis revealed organic leachate less than 0.01 ppm/g of monomer elution.
Spinal implants of the type shown in
The bony endplates were cleaned and penetrated so that there was vascular blood flow across the endplate. To facilitate placement of the implants, the disc space was distracted using a distracter instrument. Two bioactive spinal implants of the type shown in
An interference screw and washer system was placed ventrally to prevent hyperextension of the motion segment and subsequent dislodgment or migration of the implant devices. Following placement, the vessels were allowed to return to their normal position. The posterior peritoneal sheath was then closed with running absorbable suture. The bowel content was allowed to go back into position followed by standard closure of the ventral abdominal wall, the midline fascia, and the skin with subcuticular absorbable suture material.
Radiographs were taken immediately postoperative to verify implant placement and serve as baseline for comparison.
The rate and quality of healing were assessed using radiographs and CT scans taken at 1, 2, 3 and 6 months (
At six months post-operatively, animals were anesthetized (induction by ketamine (10-15 mg/kg BW IM), and, at the discretion of the attending veterinarian, diazepam (10 mg, IM) or acepromazine (1.0 mg/kg, IM) and then euthanized. Following euthanasia, the lumbar spine was retrieved en bloc and the specimens were photographed and observed grossly.
Immediately after sectioning, the excised spinal specimens were inspected for successful fusion and structural integrity of each motion segment. The screw and washer system was removed and the cranial segments were separated from the caudal segments and the specimens photographed and observed grossly.
Specimens without sufficient structural integrity for mechanical testing were immediately prepared for histologic evaluation. Those with sufficient structural integrity were mechanical tested and then prepared for histological evaluation.
All procedures were performed in accordance with Albany Medical College's Internal Animal Care and Use Committee and Quality Assurance Unit.
Bridging bone was found around the implants in all cases. In all cases, the non-destructive flexion testing supported the presence of fusion. There were no Rhakoss particulates noted, and there were no signs of adverse response to the implants. In fact, minimal scar tissue was observed.
A resin blend (about 20% to about 50% of total implant composition) of urethane dimethacrylate (DUDMA), triethyleneglycol dimethacrylate (TEGDMA), initiator and stabilizer were poured into a Ross planetary mixing system (Hauppauge, N.Y.). The mixer was sealed, mixing was commenced and a vacuum was applied. After the mixer was turned off and the vacuum released, one or more fillers (about 15% to about 80% of the total implant composition) such as E-glass fibers, borosilicate fillers, silica fillers, and combeite fillers were added. Mixing was commenced and a vacuum was drawn upon the addition of each increment of filler. Once all of the fillers were incorporated into the resin, a vacuum was drawn for additional minutes. The mixture was then agitated on a vibrating table with vacuum for about 5 minutes to 60 minutes. The material was extruded into a mold cavity for molding into various bulk geometries.
The mold cavities were heated in a Despatch LFD Series oven and cured at about 40° C. to about 180° C. for a time duration of about 1 hour to 20 hours to form a molded body. Various shaped bodies or implant bodies were then formed.
The materials can also be hot extruded, injection molded, compression molded, or reacted in a mold with a catalyst other than heat.
The cylindrical stock was machined at MedSource (Laconia, N.H.) into spinal implants of the various shapes disclosed herein, having a generally anatomical shape with convex superior and inferior surfaces, lordotic angles and the like.
Those skilled in the art will appreciate that numerous changes and modifications may be made to the preferred embodiments of the invention and that such changes and modifications may be made without departing from the spirit of the invention. It is therefore intended that the appended claims cover all such equivalent variations as fall within the true spirit and scope of the invention.
This application is a continuation of U.S. application Ser. No. 14/244,354, filed Apr. 3, 2014, which is a divisional of U.S. application Ser. No. 11/736,314, filed Apr. 17, 2007 and now U.S. Pat. No. 8,715,353, which is a divisional of U.S. application Ser. No. 10/256,566, filed Sep. 26, 2002 and now U.S. Pat. No. 7,238,203, which claims priority to U.S. Provisional Application No. 60/339,871, filed on Dec. 12, 2001, the contents of which are incorporated herein by reference in their entireties.
| Number | Date | Country | |
|---|---|---|---|
| 60339871 | Dec 2001 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11736314 | Apr 2007 | US |
| Child | 14244354 | US | |
| Parent | 10256566 | Sep 2002 | US |
| Child | 11736314 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14244354 | Apr 2014 | US |
| Child | 14936139 | US |