This invention pertains to new biocompatible polymers, a process for their preparation and compositions containing them.
Known in the prior art are polymer derivatives of dextrans obtained by substitution by carboxymethyl, carboxymethyl-benzylamide and carboxymethyl-benzylamide-sulfonate residues. These polymers, the process for their preparation and their properties, are described in French Patent No. 2,461,724 as well as in U.S. Pat. No. 4,740,594. Among these polymers, certain of them imitate the properties of heparin and can be used as plasma substitution products because of their anticoagulant and anticomplement properties. Others imitate a different property of heparin which consists of a stabilization, protection and potentiation of the in vitro biological activity of the growth factors of the FGF family (Tardieu et al., Journal of Cellular Physiology, 1992, 150, pages 194 to 203). Furthermore, French Patent No. 2,644,066 describes the use of carboxymethyl-benzylamide-sulfonate derivatives of dextran, referred to as CMDBS, alone or associated with FGFs, for cicatrization.
More recently, French Patent Nos. 2,718,023, 2,718,024 and 2,718,026 proposed the use of polymers capable of protecting, stabilizing and potentiating growth factors that have an affinity for heparin, such as the fibroblast growth factors or FGF and Transforming Growth Factor beta (TGFβ), as a drug for the treatment of lesions of the gastrointestinal tract, nervous system and muscle tissues, respectively. To illustrate this protective effect of the CMBDS dextran derivatives, these patents present the results of the proteolytic digestion by trypsin of FGF1, FGF2 or TGFβ. These properties of protection, stabilization and potentiation of the growth factors with an affinity for heparin enabled characterization of a new class of polymers, designated as HBGFPP to indicate “Heparin-Binding Growth Factor Protector and Potentiator”, that exhibit cicatrizing and repair activities in relation to muscle, nervous and gastrointestinal tract tissues, and which are devoid of anticoagulant activity at the doses employed.
In addition to the above HBGFPP applications, French Patent No. 2,718,025 proposes the use of these polymers as drugs for the treatment of inflammations. This anti-inflammatory activity is illustrated by the in vitro inhibitory action against proteolytic enzymes implicated in the inflammatory reaction such as leukocyte elastase or plasmin and in vivo by histological studies demonstrating a reduced inflammatory cellular reaction in tissues treated by CMDBS dextran derivatives.
However, these CMDBS dextran derivatives are compounds which are difficult to synthesize and present the risk of salting out residues that are known for their toxic effects such as benzylamine. Furthermore, the applications of the HBGFPP and thus of the CMDBS proposed in the prior art are limited solely to the repair and cicatrization of certain tissues.
The invention relates to a biocompatible polymer constituted by a sequence of identical or different components of the general formula (I): AaXxYy, in which A represents a monomer, X represents a carboyxl group fixed on a monomer A, Y represents a sulfate or sulfonate group fixed on a monomer A; a represents the number of monomers A, x represents the substitution rate of the set of monomers A by the groups X, y represents the substitution rate of the set of monomers A by the groups Y. The invention also relates to the pharmaceutical or diagnostic compositions containing at least one polymer of general formula (I).
This invention resolves the drawbacks of the prior art by providing new biocompatible polymers which are easy to prepare and present the properties of the HBGFPP but also, in an unexpected manner, novel properties which enable very extensive fields of application, especially in therapeutics, which are not limited to just a few types of particular organs, tissues or cells. The polymers of the invention are, therefore, referred to below as “RGTA” for “ReGeneraTing Agents”.
The polymers of the invention have a molar mass greater than about 5,000 da and are constituted by a sequence of identical or different components of the following general formula (I):
AaXxYy
in which:
The radical R of the groups X and Y in formula (I) is advantageously selected from among an alkyl, allyl, aryl, linear or branched group.
In the definition of the substitution rates cited above, a substitution rate x of 100% is understood to mean that each monomer A of the polymer of the invention contains statistically one X group. Similarly, a substitution rate y of 100% is understood to mean that each monomer of the polymer of the invention contains statistically one Y group. Substitution rates higher than 100% manifest the fact that each monomer bears statistically more than one group of the type under consideration. Conversely, substitution rates lower than 100% manifest the fact that each monomer bears statistically less than one group of the type under consideration.
The polymers offer the remarkable advantage of presenting in vivo a slow degradability, which differentiates them from the heparan sulfates which are products that are naturally and rapidly degraded by heparinase or heparitinase. Furthermore, the polymers of the invention neither contain nor release toxic products after degradation, in contrast to the CMDBS, which have benzylamine groups.
The monomers A which constitute the base elements of the polymers of formula I can be identical or different, and are selected from among all types of monomers such as, for example, those proposed for the HBGFPP such as the sugars, esters, alcohols, amino acids, nucleotides and the like. Among these, preference is given especially to the -oses, and especially to glucose.
The number of monomers A is defined in a manner such that the mass of the polymers of the invention is greater than approximately 5,000 da. Consequently, the RGTA can be constituted by diverse homomeric as well as heteromeric polymerizable structures such as, for example: the polyester copolymers of biosynthesis or chemical synthesis such as the aliphatic polyesters or those of natural origin such as the polyhydroxylalcanoates. Also applicable are polysaccharides and their derivatives of bacterial origin such as cellulose, xanthan, dextran and the like, unicellular or multicellular plant extracts such as starch, plant cellulose or alginates or their derivatives, the fucanes and their derivatives and the like, or animal extracts such as hyaluronic acid or chitin and the like, or products of synthesis such as those obtained by copolymerization. Synthesized proteins such as the natural or chemically modified polyamino acids such as, for example, collagen can also be employed in the constitution of the polymers of the invention.
The selection of the polymer structure of the RGTA is based on the various forms of presentation which can be used depending on the tissue or the organ to be treated or the physicochemical characteristics such as the solubility, the spatial conformation with the solutions, suspensions, gels, powders, sponges, films, compact moldable materials, porous, semiporous or nonporous materials, materials that crumble or materials that do not crumble, materials that erode and materials that do not erode, materials that can be colonized or materials that can not be colonized, etc.
Heparin or its fragments with weak anticoagulant properties and natural heparan sulfates and their fragments are excluded from the scope of the present invention because:
The polymers of the invention can also comprise functional chemical groups, designated Z, which are different from X and Y, and capable of conferring on the polymers of the invention supplementary biological or physicochemical properties. Thus, the groups Z are useful for conferring on the RGTA a better solubility or lipophilic properties enabling better diffusion or tissue penetration, for example, increasing the amphiphilic properties, enabling crossing the blood-brain barrier and the like. As an example, the groups Z, which can be identical or different, can be amino acids, fatty acids, fatty alcohols, ceramides or derivatives thereof, or nucleotide addressing sequences.
The groups Z can also represent identical or different active agents, such as therapeutic or diagnostic agents, for example, an anti-inflammatory, antimicrobial, antibiotic and the like or an enzyme, a growth factor and the like.
The polymers of the invention in which Z is present have the following formula II:
AaXxYyZz
in which A, X, Y, a, x, and y have the same meanings as defined above and z represents the substitution rate of the set of monomers A by the groups Z, which is comprised between approximately 0 and 50%, preferably on the order of 30%. The groups X, Y and Z can be fixed directly on the monomer A or fixed to each other with only one of them being fixed to the monomer A. Thus, the groups Z can be fixed by covalence directly on the monomers A or fixed by covalence on the groups X and/or Y.
However, the groups Z can also be conjugated to the polymers of formula (I) by bonds other than covalent bonds, such as ionic or hydrophilic interactions, depending on the nature of A, X and Y. The polymers of the invention can then constitute a vectorization system of Z. Thus, the polymers of the invention are useful for transporting an active agent Z, such as a growth factor or an enzyme, to the level of the injured or diseased tissue as defined below in the context of the applications of the polymers of the invention.
The polymers in which the groups R of X and Y or the groups Z are capable of inducing toxic effects directly or after degradation are not included within the scope of this invention. Among the groups Z excluded from the invention can be cited those groups constituting mutagenic agents or those known to be carcinogenic or exhibiting other toxic properties. This is the case of benzylamine which can be precipitated out from the benzylamide group contained in the CMDBS and the carcinogenic properties of which are well known by the expert in the field (Wiessler M, et al., Carcinogenesis 1983; 4(7): 867-871; Singer G M, et al., J Med. Chem. 1983; 26(3): 309-312). CMDBS is consequently excluded from the polymers of the invention.
The invention also pertains to the pharmaceutical or diagnostic compositions containing at least one polymer as defined above associated in the composition with a pharmaceutically acceptable vehicle. These compositions can be used in humans as well as in animals. In fact, as with the HBGFPP described in the prior art, the polymers of the invention present the following properties:
Thus, the polymers of the invention constitute a new class of agents that promote the repair of muscle and nervous tissues, and those of the gastrointestinal tract and which present, as reported in U.S. Pat. No. 5,693,625 for the CMDBS, properties on cutaneous cicatrization and that of the cornea or on flat bone as described by Blanquaert F et al. (Bone, 1995; 17(6): 499-506). However, the polymers of the invention also present unexpected properties in relation to the CMDBS. As an example, we can cite the effect of the CMDBS on cranial bone defects (Blanquaert F et al., Bone, 1995; 17(6): 499-506) which a priori is not transposable to long bone. Flat bone and long bone are of a completely different nature because:
The invention, therefore, pertains more particularly to the previously described biocompatible polymers of formulas (I) and (II) which are devoid of significant anticoagulant activity. These polymers present an anticoagulant activity lower than about 10 IU/mg at single or daily doses comprised:
The anticoagulant activity of the polymers of the invention at the doses indicated above is for a person weighing about 70-kg lower than:
Remarkably, the polymers of the invention are devoid of significant anticoagulant activity at the doses specified above but still present the capacity of preserving or restoring tissue homeostasis. The invention, therefore, pertains particularly to the use of the aforementioned polymers for the preparation of a drug that is useful for the prevention or treatment of dysfunctions of tissue homeostasis and which do not present significant anticoagulant activity.
In a completely surprising manner, we found that the polymers of the invention can be administered via routes other than those described in the prior art for the CMDBS which only envisaged local administration at the level of the injured tissue. Thus, it is possible to select among the polymers of the invention those which are suitable, for example, because of their solubility, for the selected route of administration: intravenous, intra-arterial, intramuscular, intraperitoneal, intraocular, into the cerebrospinal fluid or directly into the central nervous system to cross over the blood brain barrier, as well as orally. All of these routes of administration, possibly even combined, have been shown to be particularly effective.
Thus, the invention concerns pharmaceutical compositions in which the polymer of the invention is associated with a pharmaceutical vehicle in a form enabling oral, cutaneous, subcutaneous, topical, intramuscular, intravenous or intra-arterial administration or administration into any of the fluid compartments of the organism. Studies performed in the framework of this invention revealed that the RGTA act especially within the dosage windows beyond which satisfactory biological effects were not always obtained. These optimal effective doses are defined below and depend on the route of administration and the type of lesion.
Advantageously, in a manner to completely cover the surface of a wound or to fill the volume of a tissue lesion, the pharmaceutical compositions are dosed to allow administration of about 0.001 to about 1 milligram of polymer per square centimeter or of about 0.005 to about 1 am of polymer per cubic centimeter of tissue to be treated. Thus, the compositions of the invention preferably contain between about 0.01 and about 10 milligrams of polymer per milliliter of physiological solution of dissolution.
For administration via the systemic route (venous, arterial), via the intraperitoneal route or intraocular route, into the cerebrospinal fluid, into the intracochlear fluid or into any peritissular or intratissular fluids, the compositions of the invention are dosed to allow administration of between about 0.1 and about 100 milligrams of polymer per kilogram of weight of the human or animal to be treated.
For administration via the intramuscular route, the compositions of the invention are dosed to allow administration of between about 0.2 and about 500 milligrams of polymer per kilogram of weight of the human or animal to be treated, preferably between about 1 and about 50 mg per kg.
For oral administration, the compositions of the invention are dosed to allow administration of between about 1 and about 5000 milligrams of polymer per kilogram of weight of the human or animal to be treated, preferably between about 10 and about 500 mg per kg.
Furthermore, the previously reported properties of the HBGFPP, i.e., that they present a cicatrizing and repairing activity on the muscle and nervous tissues and on those of the gastrointestinal tract and that they can be used as drugs for the treatment of inflammations, we have demonstrated the remarkable effects of the polymers of the invention on the regulation of the homeostasis of the mass and the functionality of the tissues and organs, demonstrating that they act on tissular and cellular regeneration, protection, preservation and aging in vivo and ex vivo, as well as antifibrotic activities and protective activities against the deleterious effects of ischemias, ionizing radiation and oxidizing products induced by diseases or stress or stemming from food. Consequently, the RGTA should be considered to be regulators of tissular homeostasis in that they regulate the mass of the regenerated tissues and they act on the reorganization of the matrix in that they exert an antifibrotic and cicatricial effect on the tissues and organs subjected to acute as well as chronic destructive processes.
These properties of the RGTA are characterized by unique effects on the quality and rate of the tissue repairs. These effects are manifested by an almost complete reconstitution and identity with the original tissue structure (prior to the lesion) and by the almost complete absence of cicatricial traces such as in particular signs of fibrosis or loss of its functional integrity. More particularly, the research results which will be presented below in the experimental part demonstrated the in vivo tissue protection and regeneration properties of the RGTA in the following models:
Thus, the properties below of the polymers of the invention have been particularly demonstrated:
Thus, unexpectedly, the inventors discovered that the RGTA presented the capacity to:
The RGTA act as protective and reparative agents of the deleterious effects associated with tissue stress. Thus, in ischemia, regardless of its origin or in response to a cellular or tissular aggression, for example, under the effect of ionizing radiation, or in response to an invasion by a pathogenic agent, regardless of whether it be viral, microbial, parasitic or even of the type causing pathologies of the TSSE (Transmissible Subacute Spongiform Encephalopathies) type such as prions, or during vascular rupture caused by hemorrhages whose effects are harmful by causing functional losses, for example, in the case of hemorrhages of the retinal vessels which can lead to blindness or in the brain which can lead to loss of motor functions or others.
Consequently, the invention pertains to pharmaceutical compositions containing at least one RGTA in both human and animal fields of applications. These compositions are beneficial in medical, veterinary and cosmetic fields as well as in alimentary fields as preservatives of foods or nutriments that naturally contain antioxidants or to which are added antioxidants such as animal or plant SOD.
The protective qualities of endogenous SOD or SOD that is provided exogenously are reinforced by the RGTA. Thus, the RGTA can be administered in all cases in which the beneficial effects of SOD have been described.
For the treatment of diseases in which exogenously supplied SOD has been shown to be effective, the therapeutic effects resulting from the protective effect of endogenous SOD can then act more effectively in the presence of RGTA. The RGTA limit or avoid exogenous intakes from acting indirectly as antioxidant agents. The following therapeutic effects result from these effects:
The administration of RGTA alone or in association with. SOD would be beneficial against disorders of the heart, brain and central nervous system as in the case of lesions of the spinal cord (Nakauchi et al., Effects of lecithinized superoxide dismutase on rat spinal cord injury, J. Neurotrauma, 1996, 13, 573-82) or of the retina.
In the treatment of respiratory insufficiencies associated with diaphragmatic fatigue (Supinski et al., Effects of free radical scavengers on diaphragmatic fatigue, Am. J. Respir. Crit. Care Med., 1997, 155, 622). This could be notably of value in patients with muscular dystrophy.
All tissues, especially those for which the endogenous active SOD level is higher (vascular endothelial cells, in the liver, the kidneys, the cardiac and skeletal muscles, the pancreas, the epithelial cells of the intestinal mucosa, the colon, the trachea, the esophagus, the conjunctive tissue and cartilage).
The treatment of the deleterious effects associated with diabetes such as the diabetic retinopathies (Szabo et al., Direct measurement of free radicals in ischemic/reperfused diabetic rat retina, Clin. Neurosci., 1997, 4, 240-5).
The treatment of leprosy (Serum, zinc, copper, magnesium, proteins and superoxide dismutase in leprosy patients on multidrug therapy—a follow-up study, Indian J. Lepr., 1996, 68, 325-53).
In the treatment of endotoxic shock (Hepatic response to the oxidative stress induced by E. coli endotoxin, Mol. Cell. Biochem. 1996, 159, 115-121).
In the treatment of the lesions induced by the stress caused by the presence of pathogenic agents of all types, especially viruses, including the AIDS virus, or the agents that induce TSSE such as the prions.
In the preventive and/or curative treatment against irradiations. Thus, the adverse effects of radiotherapy can be reduced by a preventive and/or curative treatment with RGTA. The use of the RGTA allows reduction of the dose of radiotherapy under cancer treatment conditions (Prevention of radioinduced cystisi by orgotein; a randomized study, Anticancer Res., 1996, 16, 2025-8) or enable prevention of the clastogenic effects induced by the irradiation. The hyperthermic effects associated with radiotherapy can be diminished by the use of RGTA in the same manner as SOD (Kandasamy et al., Involvement of superoxide dismutase and glutathione peroxidase in attenuation of radiation-induced hyperthermia by interleukin 1 alpha in rats, Brain Res., 1993, 606, 106-10).
In the protection against the effects induced by ultraviolet radiation, for example on the retina. (Oguni et al., Chronic retinal effects by ultraviolet irradiation with special reference to superoxide dismutase, Histol. Histopathol., 1996, 11, 695-702) and the treatment of uveitis (Koch et al., Effects of different antioxidants on lens-induced uveitis, Ger. J. Ophthalmol., 1996, 5; 1185-8). The treatment with RGTA can be alone or in association with SOD and its use can be medical as well as cosmetic.
In the treatment of hypertension. In fact, the activity of endogenous SOD is diminished in subjects with hypertension (Jun Ke Yan and Catalano, Increased superoxide anion production in humans, a possible mechanism for the pathogenesis of hypertension, J. Hum. Hypertens. 1996, 10, 305-309). The intake of RGTA can have the effect of augmenting this activity and reducing the hypertension.
The RGTA are also useful for the conservation of organs or tissues as well as in the maintenance of biological fluids such that the following applications can be envisaged:
The invention pertains to pharmaceutical compositions containing at least one polymer as defined above and intended for the treatment and/or prevention of tissular lesions and disorders, such as those found in traumatology, requiring reparative or plastic surgery of cutaneous or deeper floors such as those of muscles, bone, brain, heart, viscera, etc., in the degenerative diseases possibly associated with fibrosis, in the losses of tissue mass such as osteoporosis or myopathies, in the cardiovascular and neurological fields, in dermatology, etc.
A remarkable property of the RGTA is their capacity to fix themselves on the injured tissues, which enables the use of the RGTA as targeting vectors in a therapeutic and/or diagnostic objective. Consequently, the polymers of the invention can be coupled to molecules, represented above by the group Z, endowed with therapeutic activities or to molecules that facilitate the repair of the injured tissue.
Other advantages and characteristics of the invention will become manifest from the examples below concerning, on the one hand, the preparation of polymers of the invention in which the polymer skeleton is of the polyester type or of a polysaccharide nature and, on the other hand, the properties of the polymers of the invention.
A) Preparation of the Polymers of the Invention
In this example, the polymer of the invention is a copolymer of β-malic acids of general formula (II), the components A of which, substituted by X and/or Y and/or Z, are represented in
Pcoo− corresponds to a polymer composed exclusively of carboxylic or carboxylate groups X. P1S and P2S correspond to polymers composed of sulfonate groups Y and hydrophobic butyl groups Z in addition to the groups X.
The synthesis of this polymer proceeds from the preparation of β-substituted β-lactones and is followed by an anionic polymerization by ring opening. The three β-lactones synthesized are shown in
The monomers are obtained from DL-aspartic acid in four steps prior to the polymerization as shown in
The synthesis of the alkyl malolactonate is performed from DL-aspartic acid in which R represents —CH2—C6H5 (benzyl malolactonate) or —CH(CH3)—CH2—CH3 (2-butyl malolactonate) or CH2—CH═CH2 (allyl malolactonate).
I—Synthesis of the Monomers (Aspartic Acid Pathway)
1) Synthesis of (2R,S)bromosuccinic acid
Synthesis of (2R,S)bromosuccinic acid is obtained after a diazotation reaction of DL-aspartic acid. For this reaction, the carbon bearing the amine group undergoes a double inversion of configuration (Guérin et al., Optically active poly(β-malic acid), 1985, Polymer Bulletin, 14: 187).
100 g (0.75 moles) of DL-aspartic acid and 415 g (4.04 moles; 5.5 eq.) of sodium bromide are dissolved in 1620 milliliters of 2N sulfuric acid in an ice bath. Then 62 g (0.9 moles; 1.2 eq.) of sodium nitrite are added in small quantities, under agitation. Thirty minutes after the end of this addition, the reactional medium is neutralized with 8 g (0.13 moles; 0.18 eq.) of urea for 30 minutes at room temperature. The bromosuccinic acid is extracted with 1 liter of ethyl acetate and the aqueous phase washed with 1 liter of ethyl acetate. The organic phases are dried over magnesium sulfate, filtered on a Büchner funnel then the ethyl acetate is eliminated in the Rotavapor.
The bromosuccinic acid is then recrystallized 4 times in acetonitrile, filtered on a Büchner funnel then dried for 4 h at 45° C. under vacuum in a desiccator.
The synthesis of the monoesters comprises the prior preparation of the anhydride without racemization of the chiral centers. The anhydride is synthesized from (2R,S)2-bromosuccinic acid under the action of a dehydrating agent, trifluoroacetic anhydride (TFAA), under anhydrous conditions and under nitrogen. The following step is the opening of the anhydride by an alcohol which leads to two monoesters, only one of which will be lactonizable. The choice of the alcohol is based on the nature of the desired lactone.
a) Synthesis of benzyl bromosuccinate
Fifty g (0.25 moles) of bromosuccinic acid are degassed under a nitrogen stream for 2 h. In an ice bath, 125 milliliters of anhydrous tetrahydrofuran (THF) then 43.4 milliliters (0.30 moles; 1.2 eq.) of trifluoroacetic anhydride (TFAA) are added drop by drop by a dropping funnel. The solution is left for 2 h at room temperature under agitation, then the THF, the TFA formed and the TFAA in excess are eliminated in the Rotavapor. The bromosuccinic anhydride is allowed to degas for 2 hours.
Then 27.7 milliliters (0.25 moles; 1 eq.) of benzyl alcohol are added. The solution is agitated at 40° C. under an inert atmosphere for 12 h. The mixture of monoesters obtained in this manner is dissolved in 150 milliliters of ether. The etherized phase is washed 3 times with 100 milliliters of water, dried on magnesium sulfate and filtered on a Büchner funnel.
The same protocol as previously employed is used but 17.86 milliliters (0.25 moles; 1 eq.) of allyl alcohol are added. The reactional medium is agitated for 22 h at 60° C. under an inert atmosphere rather than for 12 h at 40° C. The monoesters are purified in identical manner.
The same protocol as above in 2)b), but with 18.8 g (1 eq.) of (RS)2-butanol that has been distilled in advance. The reactional medium is agitated for 12 hours at 60° C. under an inert atmosphere.
The lactonization reaction is performed on the sole lactonizable monoester and presents an inversion of configuration. It is performed directly on the mixture of monoesters after neutralization at pH 7.2 with 2N soda. The reaction takes place in a dichloromethane/water biphasic medium. The lactone is purified by silica column chromatography. The nature of the eluent varies depending on the nature of the lactone. This lactone is then distilled on an appropriate column.
a) Synthesis of benzyl malolactonate
71 g (of which 70% is lactonizable monoester, i.e., 0.173 moles) of the mixture of monoesters are dissolved in 300 milliliters of ether and 250 milliliters of water in a balloon flask. A 2N solution of sodium hydroxide is added drop by drop until reaching pH 7.2, then 450 milliliters of dichloromethane are added. The flask is placed on a refrigerant system and the biphasic system is strongly agitated for 3 h at 40° C.
After decantation, the organic phase is washed 2 times with 250 milliliters of water then 2 times with 250 milliliters of brine, dried over magnesium sulfate and filtered. The solvent is eliminated in the Rotavapor. This lactone is purified on silica column (eluent: 8/2 dichloromethane/petroleum ether) and distilled 3 times under vacuum.
According to the same protocol as above in 3)a), but the pH of the aqueous phase is 7.8 rather than 7.2 and the solution is agitated for 5 h rather than 3 h. The lactone is purified on silica column (eluent: 4/6 petroleum ether/ethyl ether) and is distilled 3 times under vacuum.
The same protocol is employed as in 3)a) above. The lactone is purified on silica column (eluent: 8/2 dichloromethane/petroleum ether) and is distilled 3 times under vacuum.
The lactones were polymerized in the presence of tetramethyl ammonium benzoate (10−3 eq.) at 37° C. for 15 days. The polymerization was monitored by infrared analysis with observation of the disappearance of the lactone band at 1850 cm−1.
1) Synthesis of allyl butyl-co-malate benzyl-co-malate polymalate
Five g (24.2 mmoles) of benzyl malolactonate, 1.4 g (9.3 mmoles) of allyl malolactonate and 0.7 g (4.1 mmoles) of butyl malolactonate are degassed for 2 h and transferred via cannula into a balloon flask containing 471 milliliters of a primer solution (tetraethylammonium benzoate: 10−3 eq.; 37.72·10−6) at 80·10−3 M which was degassed in advance for 2 h under a nitrogen stream. The copolymerization was performed at 37° C. for 15 days under an inert atmosphere and under agitation. The polymer was then dissolved in a minimum of chloroform. The chains were terminated by addition of a drop of concentrated hydrochloric acid and the polymer was precipitated with ethanol then dried under vacuum at 40° C. for 48 h.
1.12 g (7.91 mmoles of unsaturated units) of polymer are dissolved in 3 milliliters of anhydrous dichloromethane in a balloon flask. A solution containing 466.34 milligrams (4.69 mmoles; 6 eq.) of metachloroperbenzoic acid (MCPBA) in 2 milliliters of dichloromethane is added by cannula. The mixture is agitated for 24 hours at room temperature. The polymer is then precipitated with ethanol and dried in a desiccator under vacuum.
The molar mass did not change upon epoxidation because MCPBA does not induce a modification of the chain length.
3) Hydrogenolysis of allyl butyl-co-malate benzyl-co-malate polymalate
Four g of the polymer are dissolved in 5 milliliters of freshly distilled dioxane on sodium in a balloon flask. 800 milligrams (20% by weight) of palladium on active charcoal are added and the hydrogenolysis is begun. When the volume of hydrogen consumed no longer increases (24 h after the beginning of the reaction), the hydrogenolysis is stopped. The solution is filtered on Celite and the dioxane is eliminated in the Rotavapor.
Four g of polymer (i.e., 5.64·10−3 moles of epoxide) are dissolved in 20 milliliters of water. 2.14 g of sodium bisulfite (2 eq., 11.28·10−3 moles) are added. The pH of the solution is adjusted to 7.4 (Housse-Ferrari, “Preparation and characterization of porous silicas modified by polymers and copolymers of N,N′-dimethyl acrylamide”, Thesis, University of Paris VI, Jan. 30, 1990). The solution is left under agitation for 7 h in ice then ultrafiltered for 24 h at 4° C. against water and lyophilized.
I—Synthesis of carboxymethyl dextran sulfates Designated CMDS
In this example, the polymer of the invention is constituted of substituted dextran in which the glucose A motifs substituted by X and/or Y and in which Z is nothing are represented in
The polymers of type CMDS in which Z=nothing contain multiple types of monomers. The first types of substituted monomers are the carboxymethyl glucose of type A-X substituted in position 2 and/or 3 and/or 4 (motifs presented in
The different monomers constituting the CMOS polymer are thus either unsubstituted glucose or glucose carboxymethyl or glucose sulfate or glucose carboxymethyl sulfate. The different isomeric forms are diagramed in
The monomers obtained in this manner are either glucose sulfate in position 2, 3 and/or 4 and/or glucose carboxymethyl sulfate. The sulfate is fixed either on the glucose or on the carboxylic group.
Thus, in
1) Synthesis of carboxymethyl dextran sulfate Designated CMnDSm
a) Carboxymethylation
The first dextran carboxymethylation step is performed according to the protocol described in Mauzac et al. (Mauzac et al., Anticoagulant activities of dextran derivatives. Part I: Synthesis and characterization, 1984, Biomaterials 6/61-63). It comprises an etherification of the hydroxyl functions of the glucose residue of the dextran in order to obtain a carboxymethyl dextran. This reaction can be reproduced multiple times and results in products referred to as CMnD in which n represents the number of carboxymethylation steps. The various products referred to as CMnD are characterized by an increasing percentage of COOH. This process thus makes it possible to obtain different rates of carboxymethylation of the dextran as indicated in the table of
Thus, in a refrigerated 250-milliliter balloon flask, Dextran T40 (37.37 g, 9.34 10−4 mole), from Sigma and of molecular weight 40,000 D, is solubilized (182 milliliters of distilled water) at 4° C. A soda solution (74 g, 1.85 mole in 124 milliliters of distilled water), also cooled to 4° C., is poured slowly into the Dextran solution while maintaining constant the temperature of 4° C. Monochloroacetic acid (76.2 g, 0.806 mole), reduced to a fine powder, is added slowly while maintaining the same reaction temperature. However, the temperature of the reactional medium rises at the end of the reaction from 4° C. to 21° C. within several minutes. The mixture is then brought to 50° C. in a thermostated oil bath for 40 minutes. During heating, the reactional medium acquires a yellow coloration. After cooling, the pH is neutralized to 7.2 with glacial acetic acid (Takakura, 1990). The carboxymethyl dextran is collected by precipitation in cold absolute ethanol (5 to 6 times the reactional volume). It is then dried in an oven under vacuum. The polymer CM1D is purified by ultrafiltration then lyophilized (mass=55 g gross).
The presence of the carboxylic ions is quantified by reverse acid-basic quantification using nitric acid. The base used is 1 N soda. The result is expressed in % of COOH groups. % COOH of CM1D=48.98%. This percentage means that statistically approximately one out of every two glucose units was carboxymethylated.
In practice, this reaction can be performed multiple times to attain the desired substitution rates. The same protocol was, therefore, applied for the synthesis of CM2D from CM1D and of CM3D from CM2D:
The sulfatation reaction of the residual hydroxyl functions after the carboxymethylation steps is performed with chlorosulfonic acid. It produces the compounds referred to as CMnDSm which are presented in
Example of Sulfatation of CM1D
Five hundred milligrams (MW=7.8 mmol/g) of carboxymethyl1dextran (CM1D) are dispersed in 40 milliliters of dry dichloromethane. The number of hydroxyl residues that remain free and capable of reacting in a sulfatation reaction is nOH=4·10−3 mole. The reaction was performed in the presence of one chlorosulfonic acid equivalent (nClSO3H=4·10−3 mole) or approximately=0.5 g or a volume of 0.3 milliliters, the density of the chlorosulfonic acid solution being 1.75. The 0.3 milliliters of chlorosulfonic acid are diluted in 4 milliliters of dehydrated dichloromethane. The CM1DS1 obtained in this manner is recovered by filtration of the reactional medium under vacuum on frit.
The same reaction can be performed in the presence of 0.5 or 1.5 or 2 or 3 equivalents of acid chlorosulfonic acid or an excess so as to graft the increasing quantities of O-sulfate groups. The RGTA polymers thereby obtained are referred to as CMnDSm, with n=1, 2, etc. and m=0.5, 1, 2, etc.
Using the same principle and with the goal of comparing these polymers with other sulfated molecules, we considered as comparison products with the CMnDSm either commercial dextran sulfates (Pharmacia Biotech product, code 17-0270-01) or dextrans sulfated from dextran T40 in the presence of m equivalents of chlorosulfonic acid, i.e., under reaction conditions comparable to those employed for producing the CMnDSm.
The results of different quantitative determination of the X groups by titration and the Y groups by elemental analysis of the levels of sulfur atoms make it possible to specify the corresponding values x and y for each of the CMnDSm compounds synthesized. These data are presented in
2) Synthesis of the carboxymethyl dextran-phenyl sulfonate Polymers Indicated as CM2DPhS and of a carboxymethyl dextran sulfate phenyl sulfonate Designated CM2DPhSS
These polymers are constituted by a sequence of motifs shown in
In this example, the group Z is phenyl sulfonate indicated as PhS.
The polymer CM2D (2 g; 3.90 mmol) is dissolved in 13 milliliters of distilled water. The pH of the solution is adjusted to 3.5 with 3 M HCl. The coupling agent EEDQ (1.93 g, 2 eq.) is dissolved in 16 milliliters of ethanol (0.12 g of EEDQ/milliliter) at 40° C. The EEDQ solution is added progressively to the polymer and the reactional mixture is strongly agitated for 30 minutes. The phenylsulfanilic acid salt (NH2PhSO3Na, 3.045 g, 2 eq.) is then added in small amounts. The pH of the reaction is adjusted to 9 with soda. The mixture is agitated at room temperature for 4 hours and then neutralized with dilute HCl. The product CM2DPhS is then ultrafiltered, evaporated under vacuum and then lyophilized (1.66 g).
These polymers are constituted by a sequence of motifs of type A-X, A-Y and A-Z as shown in
The same protocol as employed above was applied to CM2D with, in a first stage, the addition of an ethylenediamine group Z, indicated as DE, so as to yield the product designated CM2DE.
The sulfatation protocol was performed on a fraction of this polymer using 1 chlorosulfonic acid equivalent. The products obtained correspond to the CM2DES1 represented in
These syntheses make it possible to graft the N-sulfate groups in addition to the O-sulfate groups of the CMDS. These different polymers enable evaluation of the specific roles of th N-sulfate and O-sulfate groups of the CM2DES in relation to the phenyl sulfonate groups, indicated as PhS, of the compounds CM2DPhS, the sulfate and sulfonate compounds of the CM2DPhSS or to the compounds. In this type of polymer, it would seem that the sulfate groups are essentially linked to the properties of the RGTA.
4) Synthesis of the Polymers of carboxymethyl dextran-phenylalanine sulfate Designated CM3DPheS and of carboxymethyl dextran-tyrosine sulfate Designated CM3DTrS Represented in
These polymers are constituted of a sequence of motifs of type A-X, A-Y and A-Z as shown in
In these polymers, Z is an amino acid with either phenylalanine (Phe) or tyrosine (Tyr) and Y is an —OSO3− group.
These syntheses were performed so as to evaluate the importance of the aromatic structures of these two amino acids Phe and Tyr by replacing the benzylamine indicated as B as is known in the CMBDS of the prior art, but the salting out of which in in vivo applications can be detrimental by generating risks of tumorigenicity.
The polymer CM3D (% COOH=136%, 0.6 g, 3.014 mmol) is dissolved in 6 milliliters of distilled water. The pH of the solution is adjusted to 3.5 with 3M HCl. The coupling agent EEDQ (745 milligrams, 1 eq.) is dissolved in 6.2 milliliters of ethanol at 40° C. The EEDQ solution is added to the polymer drop by drop and the reactional mixture is agitated vigorously for 30 minutes at room temperature. The phenylalanine methyl ester (1.3 g, 2 eq.) is added very slowly to the mixture and the pH is brought from 5 to 9 with soda. The reaction is maintained at room temperature for 4 hours. The solution is then neutralized with dilute HCl. The polymer CM3DPhe is then ultrafiltered, evaporated under vacuum and then lyophilized (524 milligrams).
The same protocol was performed on the CM3D with the tyrosine methyl ester CM3DTyr.
The sulfatation protocol was performed on these two polymers using 2 chlorosulfonic acid equivalents.
The polymers are constituted by a sequence of motifs of type A-X, A-Y and A-Z as represented in
These compounds respond to formula (I) in which Y═—OSO3− and Z is oleic or palmitic acid. These fatty, acids were grafted to evaluate the importance of the hydrophobicity/hydrophilia balance of the polymers in addition to the role itself of these fatty acids.
To the polymer CM1D (1 g, 2.43 mmol) dissolved in DMSO (16 milliliters) was added triethylamine (0.8 milliliters) and then oleic chloride (1.6 milliliters) was added drop by drop. The reactional mixture was agitated at room temperature for 2 hours. The polymer was precipitated in 120 milliliters of ethyl acetate, centrifuged and then dried under vacuum. The precipitate was dissolved in 20 milliliters of 2M sodium acetate and the salt formed was precipitated in ethanol (160 milliliters), filtered, dissolved in 20 milliliters of distilled water then finally dialyzed against water. After dialysis (24 h), the solution evaporated under vacuum yielded the lipid dextran CM1Doleic (751 milligrams).
The same protocol was performed with the palmitic chloride polymer CM1Dpalm.
The sulfatation protocol was performed on these two polymers using 1 chlorosulfonic acid equivalent.
The different examples presented which involve grafting a group Z yield the compounds, the definitions of several of which are presented in Table II below.
Table II above indicates the percentages of substitution of the polymers containing a group Z.
6) Purification Steps for the Different Dextran Derivatives of the Above Examples
a) Dialysis to Equilibrium
After each synthesis step the polymers are collected in solid form (precipitation or filtration followed by lyophilization). The polymers are then resolubilized in the minimum volume of distilled water and then introduced into dialysis tubing (Spectrapor) with a cut-off threshold of 6000 to 8000 g/mole−1. The dialysis is performed against twice-distilled water (MilliQ) in a ratio of 1 volume of product per 50 volumes of water for 4 to 5 days with two changes of water per day.
b) Chromatography
The preceding step is associated with HPLC chromatography on molecular sieve (Column TSK) in order to establish the molar masses of the purified polymers.
c) Tangential Ultrafiltration
After the dialysis, the content of the tubing is ultrafiltered in an ultrafiltration cell (Pellikon, Millipore) on a cellulose membrane with a cutoff threshold of 10,000 g/mole−1. The quality of the purification was monitored with a conductimetry cell. When the conductivity of the water eliminated at the outlet of the cell had returned to the conductivity of pure distilled water (2 μS), the purification was stopped and the solution was concentrated prior to lyophilization.
7) Determination of the Percentages of Substitution
For the two groups of examples presented above, the percentages of substitution of the groups X, Y and possibly Z were determined in the following manner.
a) Poly β-malic acid Polymers (Examples 1)
For these polymers, the percentages of substitution are defined a priori in relation to the proportion of the different monoesters subjected to polymerization.
a) Dextran Polymers (Examples 2)
Two cases must be envisaged for these polymers obtained from dextran depending on the definition of the group Z.
The first case corresponds to the case of the CMnDSm in which Z=nothing; the second case depends on the chemical nature of Z.
On each glucose residue, three hydroxyl functions are capable of reacting. A relative molar mass of 54 g/mole−1 is attributed to each hydroxyl function, i.e., one third of the molecular mass of 162 g/mole−1 of a constitutive residue of dextran, It is assumed that each hydroxyl has the same reactivity and that the substitutions first affect each glucose unit once prior to a possible second substitution on the same residue.
A dextran T 40 of 40,000 g/mole−1 thus contains 247 glucose residues of molar mass 162 g/mole−1.
The substitution rates attained during the carboxymethylations are determined by acid-base determination with an automatic titrimeter (Tacussel). This determination finds a value x1 corresponding to the number of moles of acid fixed per gram of polymer.
Thus, when a hydroxyl is substituted, there appears on the glucose a motif: —OCH2COONa. Each of these substituted subunits has a relative molecular mass of 240 g/mole−1.
Multiple motifs appear after sulfatation.
The rates of free carboxylic groups determined by acid-base determination gives a value X2 which is always lower than the initial value X. The difference X1−X2 corresponds to the motifs —OCH2COO—SO3Na. Each of these substituted subunits has a molecular mass of 320 g/mole−1.
NMR analysis revealed that the S corresponds to a sulfatation of the free hydroxyls of the glucose residues in addition to the preceding reaction. In this case, a motif —OSO3Na appears. Each of these sulfated glucose subunits has a relative molecular mass of 200 g/mole−1. The microanalyses provide the rates of S as a percentage of the mass of the polymer.
It is, therefore, possible at the end of synthesis to obtain the percentages of free carboxyl radicals X1 and X2 determined respectively before and after the sulfatation step, taking into account that the polymer contains:
Based on these data, it is possible to establish the percentage of substitution of the groups X and Y.
Thus, the percentage of sulfur provided by the microanalysis results (S %) make it possible to determine the number of atoms of sulfur (ΣS) grafted on the polymer. This number of atoms is ΣS=(S %×MM)/32×100, in which 32 is the atomic mass of S and MM is the molar mass of the synthesized polymer.
It is possible to obtain from this the percentage Y of radicals SO3− as equal to: (100×S %×MM)/247×3200.
In the second case in which the grafted group Z is for example tyrosine, the same reasoning is applicable with the value of nitrogen given by the elemental analysis results.
B) Properties of the Polymers of the Invention
The properties that are common to the RGTA and the HBGFPP
The coagulation tests were performed using the Activated Cephalin Time technique or A.C.T. (Biggs, 1972, In: Human Blood Coagulation, Oxford Blackwell Scientific Publications). One hundred microliters of a polymer solution at different concentrations in Owen Koller buffer are incubated for 5 minutes at 37° C. with 100 microliters of plasma poor in platelets and 100 microliters of a solution of rabbit brain cephalin. 100 microliters of 0.25 M calcium chloride are added and the time until appearance of the coagulum is referenced by chronometry.
As shown in
This example considers the effect of the polymers on the stabilization of FGF1 and the effect on the potentiation of FGF1 and FGF2. These effects are evaluated on the growth of 3T3 BALB/c or CCL39 cells. The conditions employed for these experiments are those described in the prior art in the patents relative to the HBGFPPs which are incorporated in the present invention by reference.
1) Effects of the Polymers of the Invention on the Stabilization of FGF1 or FGF2
The results obtained show that all of the polymers tested exert at 20° C. as well as at 37° C. protective effects comparable to those of heparin, and with greater efficacy in some cases.
2) Effects of the Polymers of the Invention on the Potentiation of FGF1 or FGF2
The protocol is the same as described previously with a variable quantity of FGF possibly associated with a constant quantity of polymer. The concentration of polymer employed corresponds to that which potentiates to the maximum the mitogenic effect of the FGF. These tests are performed on 3T3 cells for FGF1 and FGF2. The controls are the same as those previously cited with the exception of a systematic determination for each test of the ED50 value.
The molecules of these two families of tested polymers potentiate the actions of FGF1 and FGF2 because ED50 values are obtained for FGF values that are lower or comparable to that obtained in the presence of heparin (
Trypsin is a proteolytic enzyme with a broad spectrum of action which is used in in vitro tests and which is one of the primordial functional enzymes in the digestive process.
The test for protection against trypsin was therefore performed. One nanogram/final milliliter of iodinated FGF2 or 5 micrograms/final milliliter of trypsin are incubated in a first step for 15 minutes at 37° C. with different concentrations of polymers (0.5 to 500 micrograms/milliliter) in a 100 mM Tris HCl buffer, 0.18 M NaCl, Brij 0.03% pH 7.6. Five micrograms/final milliliter of trypsin or 1 nanogram/final milliliter of iodinated FGF2 are then added respectively. The total reactional volume is 30 μl. The enzymatic reaction is stopped after 2 h of incubation at 37° C. by addition of Laemmli buffer and heating for 5 minutes at 90° C. (Laemmli U.K. Cleavage of structural proteins during assembly of the head of the bacteriophage T4, Nature, 1970, 227: 680-685).
Each sample is placed on a 15% polyacrylamide gel. Migration is performed for 1 h at 200 V in ice. The gels are dried for 2 h at 80° C. under vacuum and exposed at −80° C. in the presence of an autoradiographic film. The intensity of the bands is measured by image analysis and the percentage of FGF2 protected in relation to percentage of FGF2 degraded is calculated.
Protection of FGF1 and TGFβ
Most of these polymers exert a protective effect which is comparable to that of heparin which was used as positive reference.
Leukocyte elastase and plasmin are key proteases in the installation and unfolding of the inflammatory tests. These tests are intended to establish whether the polymers protect the growth factors from degradations by human leukocyte elastase.
The tests for protection against leukocyte elastase are therefore performed. The protocol employed is the same as that used with trypsin with 30 nanograms/final milliliter of elastase and 0.5 to 500 micrograms/milliliter of polymers. The buffer is 100 mM Tris HCl, 0.18 M NaCl, 0.03% Brij pH 8. The intensity of the bands is evaluated by image analysis and the percentage of nondegraded FGF2 is calculated. The positive control for these tests is heparin. Dextran T40 and dextran sulfate were used as internal references.
The model employed for evaluating most effectively the cicatrizing properties of the RGTA was that of the crushed muscle as defined and presented in French Patent No. 2 718 026.
After crushing the EDL (Extensor Digitorum Longus) of the rear paw of the rat and injection of the crushed muscle into a solution of physiological serum containing or not containing the test substances, the muscles treated in this manner are recovered 8 days after the operation. Analysis of the weights as well as a histological study make possible quantification of the effects of the polymers on muscular regeneration. The results are expressed in % in relation to the characteristics of a muscle that only received an injection of the physiological serum without polymer under the same experimental conditions.
It is important to note that these effects on muscular regeneration are obtained not only by in situ injection of the polymers but also by intravenous, intra-arterial or intramuscular injection as long as the doses injected are selected in relation to the routes of administration.
The model employed for evaluating the cicatrizing properties of the RGTA is the method already known in the prior art and described by Blanquaert F, et al., Bone, 1995; 17(6): 499-506.
This model comprises performing a circular trepanation of 5 millimeters in diameter in the calvaria of an adult rat. The defect is filled with a collagen buffer that has been cut to the same dimensions and impregnated with or not impregnated with a solution containing the RGTA. In the example presented here, the polymers studied are the type CMS polymers (RGTA 1005 and 1012) and the β-malic acid copolymers (RGTA 2011). Table III below presents the percentages of osseous filling established by image analysis of the radiographs taken 35 days after treatment.
Thus, both types of polymers stimulate osseous regeneration since under the cicatrization conditions the sagittal suture forms ad integrum.
The production of O2− ions and that of hydrogen peroxide (H2O2) represent radicals that exert especially destructive cytotoxic effects. SOD or superoxide dismutase are enzymes engaged in the detoxification of these radicals. They are agents that preserve the organism from oxidative stress.
The RGTA present various types of activity in relation to SOD:
In all cases, the quantitative determination of SOD activity is performed using Pick's technique (Freund M and Pick E, The mechanism of action of lymphokines. IX. The enzymatic basis of hydrogen production by lymphokine-activated macrophages. J Immunol 1986, 15; 137(4): 1312-1318). This technique is based on the determination of the O2− ions by reduction of cytochrome c. MnSOD (Sigma ref. S 8151) at 30 U/milliliter is dissolved in the presence of different RGTA at the concentration of 10 micrograms/milliliter. These mixtures are subjected to different treatments.
The SOD activity is evaluated in the presence of different concentrations of polymers under normal reactional conditions.
The mixtures of SOD and polymers are either subjected at room temperature to the action of trypsin (same conditions as for the protection tests of Example 5) or they are subjected to thermal treatment at 60° C. for 30 minutes. The residual catalytic activity of the SOD of these mixtures is then evaluated by conventional enzymatic techniques or on a cellular system.
The samples treated in this manner are incubated in a suspension of monocytes (2.5·106 cells/milliliter) stimulated by 200 nM of PMA. This condition induces the production of superoxide anion by these monocytes activated into macrophages. The stimulation by PMA induces an increase in the production of superoxide ions normally produced at a basal level in the absence of activation. The addition of active MnSOD used as positive control diminishes the quantity of superoxide ions produced.
Under these conditions, the lower the production of superoxide ions, the higher will be the residual catalytic activity of the SOD contained in the mixtures. Thus, these tests make it possible to evaluate the protective and potentiator effects of the polymers on the activity of exogenous as well as endogenous SOD.
Conclusion: Thus, the polymers exert potentiator and protective effects in both acellular and cellular systems. Thus, the addition of different polymers modulates the catalytic activity of SOD added endogenously as well as SOD produced endogenously by the cells.
1) Introduction
Calpaine 1 (Sigma P 4533) is used in this example. Thus, 0.78 enzyme unit (57.2 nM) are incubated in 1 milliliter of 50 mM Tris-HCl buffer, pH 7.4, 0.5% Brij, 2 mM CaCl2, 2 mMDT and 0.15M NaCl. The RGTA solutions to be tested are added over 5 minutes at 27° C. The substrate (250 micromolar of N-succinyl-leu-tyr-amido-7-methyl coumarin, from Sigma (S 1153) is then added to a quartz tank to which the mixture described above is then added. Measurements are then performed every 3 to 5 minutes by excitation at 380 nm and detection in fluorescence at 460 nm of the transformation of the substrate into 7-amino-4-methyl coumarin (according to the protocol described by Sasaki, Kikuchi, Yumoto N, Yoshimura and Murachi T, 1984, in J. Biol. Chem. 259 (20), p 12489-12494).
The results obtained are summarized in
2) Conclusion
We can predict from the results obtained in the inhibition of the activity of calpaine by the RGTA that the RGTA have a protective activity against the lesions induced by cerebral ischemia as could be anticipated from the publications of Markgraf C G et al. (Stroke, 1998, 29, 152-158) or Saido et al. (Neuroscience Letters, 1997, 16; 227: 75-78) which describe the effect of calpaine inhibitors such as MDL28170 or the protein calpastatine in the treatment of postischemic lesions of the cortex or hippocampus. Administration of RGTA via the local or intravenous route has the effect of inhibiting the calpaines and promoting the repair of the nervous tissue which has been injured especially by lack of oxygen supply as is the case in ischemia.
a) Inhibitory Activity of Heparinase and Heparitinase
Measurement of the inhibition by the RGTA of heparinase or heparitinase activities is performed using as substrate heparan sulfates radio-tagged with sulfur 35 and present in an extracellular matrix synthesized by endothelial cells cultured in the presence of Na2 35SO4 for 7 days. The protocol used is the one described by Ishai-Michaeli Ret al. (Importance of size and sulfation of heparin in release of basic fibroblast growth factor from the vascular endothelium and extracellular matrix. Biochemistry 1992; 31(7): 2080-2088). The extracellular matrix obtained after elimination of the endothelial cells is then incubated for 24 h at 37° C. in the presence or absence of heparinase and 0.5 microgram/ml of RGTA. The incubation medium is collected and deposited on a Sepharose 6.B column in accordance with the protocol described in Ishai-Michaeli (Biochemistry 1992; 313(7): 2080-2088) to measure the degradation of radio-labeled heparan sulfates.
The formation of a fibrous or fibrotic tissue is an essential physiological step associated with the processes of tissue repair and restructuring. The fibrotic tissue is a filling tissue, normally transitory, intended to conserve the structural and functional integrity of the tissues and organs. It is characterized by its richness in collagens of the extracellular matrix.
When this condition persists or develops, it corresponds to a pathology that illustrates a disturbance of the structural and functional homeostasis of the tissues and is manifested by an abnormally high accumulation of extracellular matrix which generates a fibrosis. A fibrosis, regardless of its origin, is characterized by:
A fibrosis can be induced either subsequent to a trauma of various origins (infectious, mechanical, toxic, etc.) or subsequent to ionizing radiation (notably by γ rays). In this case, we are dealing with radioinduced fibroses as is frequently the case in patients undergoing radiotherapy.
The collagens are the major components of the extracellular matrix of normal tissues as well as of fibrotic tissues. The collagens are essentially synthesized by the mesenchymal cells such as the fibroblasts and the smooth muscle cells. In a fibrous tissue, the total collagen is quantitatively increased due to reasons affecting on both the quantitative and qualitative levels the synthesis and/or degradation of the collagens, i.e., the dynamic of the restructuring. Fibroses are characterized by an increase in type III collagen, with this taking place preferentially in the case of radioinduced fibroses. This increase in type III collagen is associated with an increase but to a lesser degree in the ratio between type III collagen and type I collagen. Another collagen, type V collagen, is associated with the quality of the organization of the collagen fibers in the matrix, i.e., the fibrillogenesis. In fibrotic tissues, the decline in the levels of type V collagen is one of the origins of the loss of structure of the collagen fibers of the extracellular matrix.
The cellular model employed in this example is that of HISM cells, Human Intestinal Smooth Muscle cells (American Type Culture Collection, Rockville, Md. ATCC CRL 192), stemming from the muscularis propria of human jejunum (Graham M., Diegelmann R., Elson C., Bitar K. and Ehrlich H., Proc. Soc. Exp. Biol. Med. 176 (1984) 503). This line of human intestinal smooth muscle cells was used to evaluate the effects of radiation on cellular survival and the induction of fibrotic phenomena analyzed by means of the quantity and quality of the types of collagen secreted by these normal cells or in an inflammatory situation or in the repair process by a fibrosis.
The cells are cultured in DMEM medium containing 1 g/l of glucose, 1% of L-glutamine, 1% penicillin-streptomycin and 10% of fetal calf serum and conserved in an incubator at 37° C. under an atmosphere saturated at 5% CO2 and 95% relative humidity, in 75-cm2 plates. The HISM cells are seeded on plates with 24 flat-bottom wells at the rate of 20,000 cells per well. The volume of each well is brought up to 2 milliliters of medium. Various growth kinetics are implemented in the presence or lack of presence of RGTA at different concentrations ranging from 0.4 to 400 micrograms/milliliter.
Irradiation is performed from a 60cobalt irradiation source in an incubator in which the culture plates are arranged. Two plates are subjected simultaneously to this irradiation the source of which is vertical and the doses are evaluated in relation to the surface irradiated. The irradiator flow rate is 1 Gy/min. The doses absorbed are 10 Gy for an irradiation time per plate of 10 minutes.
Different protocols are used to evaluate the role of the RGTA depending on whether they are added to the culture medium before, during or after the irradiation, i.e., at the preventive or curative level, or both at the same time. Table IV below provides more specific information on the different protocols.
The preventive effect is evaluated by addition of RGTA (+) at the dose of 400 micrograms/ml in the culture medium 48 hours prior to the irradiation. The curative effect is evaluated by addition of RGTA 2 hours after irradiation at the same doses as for the preventive effect. For the cumulative preventive and curative effects, the cells are continuously cultured in the presence of the same doses of RGTA.
72 hours after the irradiation, the cells are incubated in a medium free of serum in the presence of tritiated proline (10 microCi/ml) and ascorbic acid (50 micrograms/ml) for 24 hours. The supernatant is then collected and the cellular layer is recovered using a robber-policeman in a final volume of 18 ml. The culture media and the recovered cellular layers are extensively dialyzed (cutoff threshold of 6 to 8 kDa) against flowing water (24 hours at 4° C.) to eliminate the small molecules from the macromolecules. After dialysis, aliquot fractions are collected and hydrolyzed (6M HCl, 105° C., 24 h) for determination of the radioactivity of the hydroxy(3H)proline, specific marker of the collagens. At this stage, an aliquot fraction is used for quantification by counting of the radioactivity of the total synthesis of the collagens.
The remaining volume is dialyzed again in the presence of pepsin and collagen I against 0.5 M acetic acid for 24 h at 4° C. The pepsin will digest the noncollagenic contaminants which will be eliminated in the dialysate in the form of peptides. Type I collagen is added to augment the proportion of collagen which is low in each sample and to trend towards an enzyme/substrate ratio of 1:5. The reaction conditions are as follows: 1 ml of pepsin solution (0.5 M)+1 ml of solution of collagen 1 (0.5 M)+0.514 ml of acetic acid to have a final concentration of acetic acid of 0.5M in an 18-ml sample. Each dialysate obtained in this manner is lyophilized in the cold state (−50° C.) and conserved at −20° C. until use.
The different collagen a chains are separated by polyacrylamide gel electrophoresis in the presence of SDS (Sodium Dodecyl Sulfate) in accordance with Leammli's method, after reduction with β-mercaptoethanol. The radioactivity incorporated in each collagen is determined by hydrolysis of the α chains obtained by cutting off the gel bands corresponding to each collagen chain of a specific type. These bands are then dissolved in oxygenated water at 60° C. and the radioactivity contained in the different dissolved bands is counted with the liquid scintillation β counter or by direct autoradiography on the gels.
The electrophoretic separation is performed with 5 microliters of collagen V and 50 microliters of each reduced sample.
These gels allow various types of processing:
The aliquot fractions collected after the dialysis against flowing water are hydrolyzed (6M HCl, 105° C., 24 h) in sealed ampoules. The acetic acid is then evaporated, and then the content of the ampoule is resuspended in 1 ml of distilled water. The proline and hydroxyproline are separated by the method of Rojkind and Gonzales (Rojkind M and Gonzalez E, An improved method for determining specific radioactivities of proline-14C and hydroxyproline-14C in collagen and noncollagenous proteins. Analytical Biochemistry 1974; 57(1): 1-7). The principle is based on oxidizing the proline and hydroxyproline with chloramine T. The proline is transformed into pyrroline carboxylate which is soluble in toluene whereas the hydroxyproline is transformed into water-soluble carboxylate. After treatment, the proline and hydroxyproline fractions are recovered for each sample and quantified by measurement of the radioactivity.
Under normal conditions, the HISM cells are characterized by the quantity of collagen synthesized (
Under normal conditions, the collagen that comprises the majority of the collagen is type I collagen. Type III and type V collagens are present in smaller proportions. The quantity of type V collagen is associated with the quality of the organization of the fibrillogenesis.
Type III collagen is a “warning” collagen, theoretically synthesized in a transitory manner in the case of reaction to a stress but in a permanent manner in the case of a fibrosis. The proportional quantity of type III collagen in relation to type I collagen increases in a noteworthy manner in situations involving response to a tissular lesion, stress or aggression such as for example ionizing radiation. Type III collagen becomes preponderant in the matrices of tissues presenting an acute as well as a chronic fibrotic reaction. This collagen can be considered to be a signaling component of the fibrotic reaction.
When the HISM cells are cultured under control conditions, i.e., without RGTA, they synthesize these three types of collagen (
The presence of different RGTA (RGTA 1005 and RGTA 1025) restores almost exactly the control behavior of the cells despite their exposure to the irradiation.
The RGTA also act on the survival of the cells (
As discussed in example 12 above, fibrosis manifests an alteration in growth of the mesenchymal cells associated with a modification of the quantity and quality of the collagens synthesized.
This example uses another cellular model which comprises smooth muscle cells from the pig aorta. These cells are obtained by means of the aorta explant method. The aorta is composed of three cellular layers: the adventitia (external layer) which contains the fibroblastic cells, the media (central layer) which contains the smooth muscle cells (SMC) and the intima (internal layer) which contains the endothelial cells.
The media is removed and torn up into tiny pieces. The explants are cultured on a 25-cm2 plate containing DMEM 1 g/l of glucose with phenol red, with the addition of 20% of fetal calf serum (FCS), 1% of L-glutamine and 1% of penicillin-streptomycin. The cells become detached from these explants and colonize the medium (stage P0). Two weeks after the beginning of the culture phase, the cells are congealed at a cellular density of 2 million cells in 10% DMSO and DMEM 20% FCS.
The growth kinetics are determined by evaluating the number of cells per well by means of an automatic particle counter (Coulter Counter ZM, Coultronics) which was previously calibrated by an evaluation of the cell diameter by means of a Malassez cell. Each counting was performed on an average of 4 wells from which the cells were detached by means of 500 microliters/well of a trypsin-EDTA (10 mM) solution.
The smooth muscle cells were seeded under the same experimental conditions as the HISM cells. The growth kinetics were determined in the presence of or lack of presence of polymers of the series RGTA 1000 to 1025 for the polymers in which Z is nothing, and of the series RGTA 1110 to 1115 for the polymers in which Z exists, and of heparin as control, at different concentrations ranging from 0.4 to 400 mg/ml.
The percentage of inhibition of the proliferation is calculated according to the following formula:
I %=100×(1−net growth with polymers/net control growth)
in which net growth represents the difference between the quantity of cells counted when they merge with the number of cells seeded at the beginning of culturing.
The control corresponds to the smooth muscle tissue cultures in the absence of polymers. Heparin and the RGTA represent the different effectors tested which are capable of modifying the biological activity of the cell.
Under the same conditions as employed for the HISM cells, the synthesis and typing of the collagen by the smooth muscle cells was determined.
These effects confirm the antifibrotic properties of the polymers of the invention.
This example illustrates the effect of the RGTA on deep cutaneous cicatrization after suture in the rat.
Male Hairless rats weighing 250 grams were anesthetized by an IM injection of ketamine and Largactil. Two 3-cm excisions were made laterally in relation to the dorsal axis of symmetry of the animals on each side of the spinal column (
The photographs of
A histological analysis performed at 60 days revealed that the skins of the untreated animals (D1) presented a dermis that was absolutely not mature whereas the animals treated with the RGTA revealed only a slight dermal trace at the deep level. The histology of the skin of the treated animals (D2) has an appearance comparable to the skin of a control animal not subjected to any cicatricial processes whatsoever. In this model, the RGTA not only accelerate the cicatrization rate of the cutaneous floor but also and especially enable a restoration of the cicatricial tissue which results in a regenerated tissue in which no trace of fibrosis can be detected. This example shows that the RGTA are especially powerful regulators of tissular homeostasis.
This example demonstrates, using the polymer RGTA 1005, the protective effects of the RGTA against tissular damage which enabled conservation of 80% of the mass of an organ compared to the untreated organs (
The model employed is inspired by the model described by Hansen-Smith, F. M., Carlson, B. M. & Irwin, K. L. (1980, Revascularization of the freely grafted extensor digitorum longus muscle in the rat. Am. J. Anat. 158, 65-82). The experimental procedure consists of sectioning the neurovascular trunk of the EDL muscles (Extensor Digitorum Longus) on the two rear paws of adult Wistar rats (350 g) at the level of its entry in the muscle and of completing the ischemia by a ligature of the two tendons. An injection of 100 microliters of an RGTA 1005 solution at 50 micrograms per milliliter in physiological serum was then made directly into an EDL muscle. The same volume of physiological serum without RGTA was injected into the other contralateral muscle.
Seven days after the injection, the muscles were removed and examined with a microscope after histological preparation. In each group of treated or untreated muscles, groups of parameters such as the mean diameter of the muscle, the thickness of the epimysium, of the peripheral zone and the mean diameter of the ischemic zone were measured using a 10× objective and a micrometric scale. The number of layers of muscle fibers that survived the ischemia in the peripheral zone was counted in thirty different fields selected at random and observed with a 20× objective.
It can be seen in
This example illustrates the reconstruction of an osseous defect created in the diaphysial shaft of a rat femur, restored to the original state after 8 weeks and better at 12 weeks, with reconstitution of a medullary cavity identical to the original one and mature cortices as in the original unfractured bone (
Male Wistar rats (Ico: WI (IOPS AF/Han), Iffa Credo) weighing from 275 to 325 grams were used. The study was performed in accordance with the EEC recommendations on animal experimentation (decree 87-848—Apr. 19, 1987). The animals were anesthetized by injection of sodium pentobarbital. The femur was approached laterally. The muscle and periosteal tissues were separated from the diaphysial shaft. A high-density polyethylene plate was fixed to the surface of the femur with Kirschner pins. A segmentary defect of 5 millimeters was implemented in the middle of the femoral diaphysis. An implant was inserted in the place of the osseous defect prior to suturing the tissues. This implant corresponds to a demineralized allogenic osseous matrix prepared from femoral diaphyses from other rats according to the procedure described by F. Blanquaert et al. (1995, Bone, 17: 499-506), which were impregnated or not impregnated with RGTA 1012 by incubation in a saline solution comprising 100 micrograms per milliliter of this product. The animals were then maintained in cages without ambulatory restraints. The femurs of the animals were radiographed every two weeks for 12 weeks before being euthanized. The femurs were then collected and subjected to the treatments required for histological study. The radiographs were studied especially in their densitometric aspects by image analysis.
In
FIGS. 29-I1, 29-I2, 29-J1 and 29-J2 show the effect of RGTA 1015 on the reformation rate of the long bone. Radiographs I1 and I2 were taken at 8 weeks; the radiographs J1 and J2 were taken at 12 weeks. I1 and J1 correspond to the treatment presented in 29-E and 29-F in which the osseous defect was filled solely by the demineralized osseous matrix without RGTA. I2 and J2 correspond to the treatment presented in 29-G and 29-H in which the osseous defect was filled by the demineralized osseous matrix impregnated in a solution of RGTA 1015. These radiographs show an acceleration of the cicatrization and especially of the maturation of the reformed bones and in terms of a pronounced corticalization (I2 and J2) which can not be detected in I1 and J1. RGTA 1015 acts as a regeneration agent which enables accelerated reconstitution of the osseous structure of long bone with a structure identical to that of the original bone.
Thus, in a surprising manner, RGTA 1012 impregnated in the demineralized osseous matrix, compared to a matrix impregnated in physiological serum without the polymer, induces an extremely significant acceleration in the restructuring and maturation processes of the bone. This effect is manifested in the appearance of new cortices after only 8 weeks whereas this phenomenon did not take place under the control condition. After 12 weeks, six of the seven animals treated by the association with RGTA 1012 presented in the radiological study the evidence of a complete union of the defect with the reformation of thick and delimited cortices whereas without CM1DS2 only the union is observable with radiological images of immature bone without corticalization. A quantitative image analysis study of the radiographs confirmed these observations. This study also showed that the profile of the bones treated by RGTA 1012 is comparable to that of normal bone, with the only difference being that the osseous material has a relatively low density at the experimental time point of 12 weeks. Projection of the density of the bone that is newly formed in the original defect shows that the treatment by the polymer RGTA 1012 induces a tissular restructuring via the cortical reformation and a medullary cavity.
The histological studies correlate with and confirm the results established on the basis of image analysis of the radiological data. These histological studies demonstrate the presence of new cortices constituted of compact bone with still several regions of marrow and the presence of a medullary cavity in continuity with the original diaphysial shaft, filled with new bone marrow. The femurs treated without RGTA 1012 do not show any figure of maturation. The reconstituted bone does not present any specific organization. It is constituted by a heterogeneous mixture of compact bone and medullary tissue without specific territorial delimitation.
These results illustrate the osteoinductive effects of the polymers of the invention on their capacity to induce not only the repair of the long bones but also and especially their potential to regulate the homeostasis of the regenerated tissues at the level of their mass as well as their reorganization.
The properties of the RGTA as regulatory agent of the homeostasis of the osseous tissues, i.e., of the tissular mass, its functionality and its restructuring are confirmed by Example 17 below.
The model used in this example pertains to the osseous restructuring of the mandible of the hamster.
Periodontal disease is induced in golden Syrian hamsters (Dépré breeding center, references HSM 41/50) after two weeks of a hyperglucidic diet. The feed administered was composed of sucrose (56%), powdered skimmed milk (28%), whole wheat flour (6%), brewer's yeast (4%), powdered alfalfa (3%), liver powder (1%) and sodium chloride (2%).
The animals were distributed into experimental groups. Fourteen animals constituted the control groups which received a normal diet comprised of dry feed. Twenty-four animals constituted the experimental groups subjected to the hyperglucidic diet. They developed chronic periodontal disease which was established at the end of two months. After this time point, the experimental groups received each week for 3 weeks an intramuscular injection of RGTA 1005 at different doses comprised between 0.1 and 15 milligrams per kilogram in a volume of 0.5 millimeters of buffered physiological serum. The control groups received an injection of physiological serum without RGTA 1005 (SHAM). The animals' weights were measured each week. One month after each type of treatment, the animals were sacrificed, the mandibles were collected and prepared for histological study. The inclusions of the operative pieces were implemented in stabilized methyl methacrylate.
In this model of periodontal disease, only 200 micrometers in height could be processed for each hemimandible. The system is standardized to always study the same sequence of sections at a depth that is defined and referenced by the osseous tissues between the roots of the two first molars of the lingual side.
The periodontal disease at the level of these molars is manifested by the appearance of a periodontal pouch which delimits a volume filled with bacterial plaque. This disease leads to a notable destruction of the periodontal bone which is characterized by a notable osteoclastic resorption and a reduction in the osseous surfaces in apposition, i.e., to an osteosynthesis phase.
The osseous resorption is quantified by measuring the zones of contact between the bone and the osteoclasts (Oc). These are giant cells that are stained blue by toluidine blue. The apposition in turn is characterized by a band of osteoid tissue, identified by an attenuated blue coloration covered by osteoblasts. In contrast to the osteoclasts, the osteoblasts are cells of small size, of cubic form and mononuclear. The quantifications of these phenomena are performed with an imaging system that uses an image-processing program.
These effects were obtained by intramuscular injection. They show that the RGTA regulate the osseous tissue mass by re-equilibrating the balance of the restructuring between resorption and apposition.
This example illustrates the capacity presented by the polymers of the invention for fixing themselves in a specific manner and concentrating at the level of the sites of tissular injury.
In the model of the regeneration of crushed muscle described in Example 7, a lesion is implemented on the EDL of the left paw of the animals. Each animal receives an intravenous injection of 2·106 cpm of RGTA 1012 radiolabeled with tritium by the company SibTech, Inc. (NY, USA). The specific activity of this tracer is 20 millicurie per milligram.
At different postoperative times, the injured EDL muscles of the left paws and the uninjured muscles of the right paws were collected and frozen in liquid nitrogen. The implementation of frozen histological sections enabled, by means of a beta imager (Societe Biospace), measurement of the quantity of radiolabeled product fixed at the level of the tissue sections studies. The results presented in Table V below show that the injured muscles concentrated after 24 hours a quantity of radioactive product approximately 5 times greater than the uninjured muscles the labeling level of which did not differ from the device's background noise.
These results demonstrate the autotargeting capacities of the polymers of the invention which concentrate themselves specifically at the level of the tissues presenting a disorder or a lesion. Thus, a particularly interesting property of these polymers resides in their capacity to vectorize a medical or diagnostic principle.
In the field of periodontics, a macroscopic study of the loss of alveolar bone was performed on the periodontitis of the hamster.
After a 2-month period for induction of the disease, the animals (n=20) were treated via the IM route for an additional 2 months without acting on the initial cause of the disease, i.e., the bacterial component. Other animals were left untreated (n=20). These two groups were compared with healthy hamsters (no periodontitis) (n=12).
At the end of the experimental period, all fleshy tissues were removed from the superior maxillaries so as to enable determination of the bone loss. The zone of the first molar was photographed in a standardized manner. A reference line was traced on each photograph which corresponded to the enamel-cement junction. Then a second line was traced which ran along the contours of the osseous ridge. These two lines were reunited in front of and behind the first molar. This surface was measured.
It should be noted that in the controls, there is a zone of denudation of the root which corresponds to:
In our animals this denudation represented 0.96 mm2.
In the diseased animals, the bone loss was 1.34 mm2, which includes the initial physiological zone (which was destroyed over the course of the periodontitis) and a part of the loss due to aging. Nevertheless, we could conclude that the disease induced a bone loss on the order of 0.38 mm2 (difference: p<0.0001).
In the treated animals, there is always an incompressible zone (the same is true of the controls). The denudation of the root represents 1.02 mm2 in these animals. Thus, there is a net deficit in relation to the controls of 0.06 mm2 (difference not significant) and an improvement by 0.32 mm2 in relation to the untreated animals (p=0.0005).
| Number | Date | Country | Kind |
|---|---|---|---|
| 98 09309 | Jul 1998 | FR | national |
This application is a Continuation of U.S. application Ser. No. 12/212,093, filed Sep. 17, 2008, which is a Continuation of application Ser. No. 10/695,574, filed Oct. 28, 2003, which is a Divisional of application Ser. No. 09/765,788, filed Jan. 19, 2001 now U.S. Pat. No. 6,689,741, issued Feb. 10, 2004, which is a continuation of International Application No. PCT/FR99/01774, with an international filing date of Jul. 20, 1999, which claims priority to French Patent Application No. 98/09309, filed Jul. 21, 1998, the disclosure of the prior applications are incorporated in its entirety by reference. This application is a continuation of application Ser. No. 10/695,574, filed Oct. 28, 2003, which is a divisional of application Ser. No. 09/765,788, filed Jan. 19, 2001 (now U.S. Pat. No. 6,689,741, issued Feb. 10, 2004), which is a continuation of International Application No. PCT/FR99/01774, with an international filing date of Jul. 20, 1999, which is based on French Patent Application No. 98/09309, filed Jul. 21, 1998.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3762924 | Morii et al. | Oct 1973 | A |
| 3907755 | Margraff et al. | Sep 1975 | A |
| 4740594 | Mauzac et al. | Apr 1988 | A |
| 4755379 | Jozefonvicz et al. | Jul 1988 | A |
| 4931553 | Gill et al. | Jun 1990 | A |
| 4935338 | Masuda et al. | Jun 1990 | A |
| 5314881 | Rapisarda | May 1994 | A |
| 5691625 | Kumar et al. | Nov 1997 | A |
| 5693625 | Barritault et al. | Dec 1997 | A |
| 5852003 | Barritault et al. | Dec 1998 | A |
| 5852004 | Barritault et al. | Dec 1998 | A |
| 6517824 | Kohn et al. | Feb 2003 | B1 |
| 6573251 | Gautron et al. | Jun 2003 | B2 |
| 6689741 | Barritault et al. | Feb 2004 | B2 |
| 20040131583 | Barritault et al. | Jul 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 231 334 | Jan 1988 | CA |
| 25 156 | Mar 1959 | DE |
| 1 152 396 | Aug 1963 | DE |
| 1152 396 | Aug 1963 | DE |
| 62 514 | Apr 1967 | DE |
| 1 572 267 | Jan 1971 | DE |
| 25 156 | Jan 1984 | DE |
| 0 066 283 | Dec 1982 | EP |
| 0 168 277 | Jan 1986 | EP |
| 0 450 398 | Oct 1991 | EP |
| 0 557 887 | Sep 1993 | EP |
| 894.508 | Dec 1944 | FR |
| 894508 | Dec 1944 | FR |
| 2 461 724 | Feb 1981 | FR |
| 2 644 066 | Sep 1990 | FR |
| 2 718 023 | Oct 1995 | FR |
| 2 718 024 | Oct 1995 | FR |
| 2 718 025 | Oct 1995 | FR |
| 2 718 026 | Oct 1995 | FR |
| 49-48785 | Nov 1974 | JP |
| 61-9431 | Jan 1986 | JP |
| 2-231075 | Sep 1990 | JP |
| 5-313295 | Nov 1993 | JP |
| 2000-516971 | Jan 1998 | JP |
| 10-501568 | Feb 1998 | JP |
| 2000-516211 | Dec 2000 | JP |
| 328094 | May 1970 | RU |
| WO 9526739 | Oct 1995 | WO |
| WO 9803572 | Jan 1998 | WO |
| WO 9803573 | Jan 1998 | WO |
| Entry |
|---|
| Catherine Alexakis et, al., “Regulation of the Collagen Phenotype Expression of Gamma-Irradiated Vascular Smooth Muscle Cells by Heparin Mimetics (RGTA),” Wiley Periodicals, Inc., 2004, pp. 594-602. |
| Catherine Alexakis et al., “Reversal of Abnormal Collagen Production in Chron's Disease Intesyinal Biopsies Treated with Regenerating Agents,” Gut. 2004. 53:85-90. |
| Catherine Alexakis et al., “Heparan Mimetic Regulates Collagen Expression and TGF-β1 Distribution in Gamma-Irradiated Human Intestinal Smooth Muscle Cells,” The FASEB Journal, 2001, vol. 15, pp. 1546-1554. |
| Emmanuel Petit et al., “Control Sulfatation of Natural Anionic Bacterial Polysaccharides Can Yield Agents with Specific Regenerating Activity in Vivo”, Biomacromolecules, 2004. 5(2):445-452. |
| Hidetoshi Yamauchi et al., “New Agents for the Treatment of Infracted Myocardium.” The FASEB Journal, Sep. 8, 2000, 14(14) : 2133-2134. |
| Patricia Mestries et al., “Specific RGTA Increases Collagen V Expression by Cultured Aortic Smooth Muscle Cells Via Activation and Protection of Transforming Gromh Factor-β1,” Matrix Biology, 2001, pp. 171-181. |
| Pascal Desgranges et al., “A Substituted Dextran Enhances Muscle Fiber Survival and Regeneration in Ischemic and Denervated Rat EDL Muscle,” The FASEB Journal, 999, pp. 761-766. |
| Catherine Alexakis et al., “Structurally Different RGTAs Modulate Collagen-Type Expression by Cultured Aortic Smooth Muscle Cells Via Different Pathways Involving Fibroblast Growth Factor-2 or Transforming Growth Factor-β1,” The FASEB Journal, 2004, 18(10): 1147-9. |
| Viviane Jeanbat-Mimaud et al., “Bioactive Functionalized Polymer of Malic Acid for Bone Repair and Muscle Regeneration,” J. Biomater. Sci. Polymer Edn., 2000. vol. 11, No. 9, pp. 979-991. |
| K.W. Walton et al., “The Histochemical Basis of Metachromasia,” Brit, J. Exptl. Pathol., 1954, pp. 227-240. |
| C.H. Rückardt et al., “Pathological and Anatomical Findings After Administration of Dextran Sulfate and Carboxymethyl Dextran Sulfates in Experimental Animals,” Acta Biol. Med. Ger., 1963, vol. 10, pp. 126-146. |
| F. Gensicke et al., “Microdistribution of Radio Sulfur in Rabbits After Intravenous Injection of 35S-Labled Dextran and Carboxymethyl Dextran Sulfates,” Acta Biol. Med. Ger., 1965, vol. 14, Nos. 3-4 pp. 409-416. |
| Susumu Sasaki, “Production of Lymophocytosis by Polysaccharide Polysulphates (Heparinoids),” Nature, 1967, vol. 214, pp. 1041-1042. |
| G. Baggi et al., Influence of Chondroitin Sulfate on the Process of Cicatrization of Experimentally Produced Cutaneous Injuries, Minerva Chirurgica, 1970, vol. 25 (3), pp. 181-184. |
| Bruce Alberts et al., “Molecular Biology of the Cell,” Garland Publishing, Inc., New York, 1983, p. 703. |
| Didier Letourneur et al., “In Vitro Stimulation of Human Endothelial Cells by Derivatized Dextrans,” in Vitro Cell. Dev. Biol.:Anim, 1993, vol. 29A (1), pp. 67-72. |
| Didier Letourneur et al., “Antiproliferative Capacity of Synthetic Dextrans on Smooth Muscle Cell Growth; TheModel of Derivatized Dextrans as Heparin-Like Polymers,” 1993, J. Biomater. Sci. Polym. Ed., vol. 4 (5), pp. 431-444. |
| Marie-Agnes Leboucher-Durand et al., “Poly(β-malic acid) Derivatives with Unsaturated Lateral Groups: Epoxidation as Model Reaction of the Double Bonds Reactivity,” Reactive & Functional Polymers, 1996, vol. 31, No. 1, pp. 57-65. |
| O. Maiga-Revel et al., “New Investigations on Heparin-Like Derivatized Dextrous: CMDBS, Synergistic Role of Benzylamide and Sulfate Substituents in Anticoagulant Activity,” Carbohydrate Polymers, 1997, vol. 32, No. 2, pp. 89-93. |
| Alt, K. W. et al., “Evidence for Stone Age Cranial Surgery” Nature, May 22, 1997, vol. 387, p. 360. |
| Biggs, R. et al., “Human Blood Coagulation Haemostasis and Thrombosis” Blackwells, 1984, 3rd edition, p. 601. |
| Blanquaert, F. et al., “Heparan-Like Molecules Induce the Repair of Skull Defects,” Bone, Dec. 1995, vol. 17, No. 6, pp. 499-506. |
| Bostantjopoulou, S. et al., “Superoxide Dismutase Activity in Early and Advanced Parkinson's Disease,” Funct. Neurol., Mar.-Apr. 1997, vol. 12, No. 2, pp. 63-68. |
| D'Agnillo, F. et al., “Reduction of Hydoxyl Radical Generation in a Rat Hindlimb Model of lschemia-Reperfusion Injury Using Crosslinked Hemoglobin-Supeoxide Distnutase-Catalase.” Artif. Cells Blood Substiti. Immobil. Biotechnol, Jan.-Mar. 1997, vol. 25, Nos. 1-2, pp. 163-180. |
| Fernandez-Novoa, L. et al., “Effects of Anapsos on the Activity of the Enzyme Cu-Zn-superoxide Dismutase in an Animal Model of Neuronal Degeneration.” Methods Find Exp. Clin. Pharmacol., Mar. 1997, vol. 19, No. 2, pp. 99-106. |
| Freund, M. et al., “The Mechanism of Action of Lymphokines—IX. The Enzymatic Basis of Hydrogen Peroxide Production by Lymphokine-Activated Macrophages,” The Journal or Immunology, Aug. 15, 1986, vol. 137, No. 4, pp. 1312-1318. |
| Guerin, P. et al., “Optically Active Poly. (β-Malic-Acid),” Polymer Bulletin, 1985, vol. 14; pp. 187-192. |
| Hansen-Smith, F. M. et al., “Revascularization of the Freely Grafted Extensor Digitorum Longus Muscle in the Rat,” American Journal of Anatomy, 1980, vol. 158, pp. 65-82. |
| Ishai-Michaeli, R. et al, Importance of Size and Sulfation of Heparin in Release of Basic Fibroblast Growth Factor from the Vascular Endothelium and Extracellular Matrix, Biochemistry, 1992; vol. 31, pp. 2080-2088 (first page only). |
| Jun, T, et al., “Increased Superoxide Anion Production in Humans, a Possible Mechanism for the Pathogenesis of Hypertension,” Journal of Human Hypertension, 1996, vol. 10, No. 5, pp. 305-310. |
| Kandasamy, S. B. et al,. “Involvement of Superoxide Dismutase. and Gluthathione Peroxidase in Attenuation of Radiation-Induced Hyperthermia by Interleukin-1α in Rats,” Brain Research, 1993, vol. 606, No. 1, pp. 106-110. |
| Koch, F. H. et al., “Effects of Difterent Antioxidants on Lens-Induced Uveitis;” Ger. J. Ophthalmol., Jul. 1996, vol. 5, No. 4, pp. 1185-1188. |
| Laemmli, U.K, “Cleavage of Structural Proteins during Assembly of the Head of Bacteriophage T4,” Nature, Aug. 15, 1970, vol. 227, pp. 680-685. |
| Markgraf, C. G. et al., “Six-Hour Window of Opportunity for Calpain Inhibition in Focal Cerebral Ischemia in Rats.” Stroke. 1998. vol. 29, pp. 152-158. |
| Mauzac, M. et al., “Anticoagulant Activity of Dextram Derivatives Part I: Synthesis and Characterization.” Biomaterials. Sep. 1984, vol. 5, pp. 301-304. |
| Meddaho, A. et al., Inhibition by Dextran Derivatives of FGF-2 Plastnin-Mediated Degradation, Biochimie, 1995, vol. 77, pp. 703-706. |
| Nakauchi, K. et al., “Effects of Lecithinized Superoxide Dismatase on Rat Spinal Cord Injury,” J. Neurotrauma, Oct. 1996, vol. 13, No. 10 pp. 573-582. |
| Oguni, M. et al., “Chronic Retinal Effects by Ultraviolet Irradiation with Special Reference to Superoxide Dismutase,” Histol. Histopathol., Jul. 1996, vol. 11, No. 3, pp. 695-702. |
| Portolés, M. T. et al., “Hepatic Response to the Oxidative Stress Induced by E. coli Endotoxin Glutathione as an Index of the Acute Phase during the Endotoxic Shock,” Molecular and Cellular Biochemistry, 1996, vol. 159, pp. 115-121. |
| Razack, S. et al., “Crosslinked Hemoglobin-Superoxide Dismutase-Catalase Scavenges Free Radicals in a Rat Model of Intestinal Ischernia-Reperfusion Injury,” Artificial Cells, Blood Substitutes, and Immobilization Biotechnology, 1997, vol. 25, Nos. 1-2, pp. 181-192. |
| Rojkind, M. et al., “An Improved Method for Determining Specific Radioactivities of Proline-14C and Hydroxyproline-14C in Collagen and in Noncollagenous Proteins,” Analytical Biochemistry, Jan. 1974; vol. 57, issue 1. pp. 1-7. |
| Saido, T. C. et al., “Up- and Down-Regulation of Calpain Inhibitor Polyeptide, Calpastatin, in Postischemic Hippocampus.” Neuroscience Letters, 1997, vol. 227, pp. 75-78. |
| Sanchiz, F. et al., “Prevention of Radioinduced Cystitis by Orgotein; a Randomized Study,” Anticancer Res., Jul.-Aug. 1996, vol. 16, No. 4A, pp. 2025-2028. |
| Sasaki, T. et al., “Comparative Specificity and Kinetic Studies on Porcine Calpain I and Calpain II with Naturally Occurring Peptides and Synthetic Fluorogenic Substrates.” The Journal of Immunology, Oct. 25, 1984, vol. 259, No. 20, pp. 12489-12494. |
| Sethi, N. C. et al., “Serum Zinc,. Copper, Magnesium, Proteins and Superoxide Dismutase in Leprosy Patients on Multidrug Therapy—a Follow-Up Study,” Indian J. Lepr., Oct.-Dec. 1996. vol. 68, No. 4, pp. 325-333. |
| Shaheen, A. A. et al., “Effect of Various Stressors on the Level of Lipid Peroxide Antioxidants and Na+,K++-ATPase Activity in Rat Brain,” Experientia, 1996, vol. 52, pp. 336-339. |
| Singer, G. M. et al., “Mutagenicity and Chemistry of N-Nitroso-N-(p-substituted-benzyl)methylamines,” Journal of Medicinal Chemistry, Mar. 1983, vol. 26, No. 3, pp. 309-312. |
| Supinski, G. et al., “Effect of Free Radical. Scavengers on Diaphragmatic Fatigue,” Am. J. Respir. Cri. Care Med., Feb. 1997, vol. 155, No. 2, pp. 622-629. |
| Szabo, M. E, et al, “Direct Measurement of Free Radicals in lschemic/Reperfused Diabetic at Retina,” Clin. Neurosci., 1997, vol. 4, No. 5, pp. 240-245. |
| Tardieu, M. et al., “Derivatized Dextrans Mimic Heparin as Stabilizers, Potentiators, and Protectors of Acidic or Basic EGF.” Journal of Cellular Physiology, 1992, vol. 150, pp. 194-203. |
| Wiessler. M. et al., “Biological Activity of Benzylating N-Nitroso Compounds, Models of Activated N-Nitrosomethylberzylarninc,” Carcinogenesis, 1983, vol. 4, No. 7, pp. 867-871. |
| Graham, M. F. et al., “Isolation and Culture of Human Intestinal Smooth Muscle Cells,” Proceedings of the Society fir Experimental Biology and Medicine, 1984, vol. 176, No. 4, pp. 503-507. |
| Number | Date | Country | |
|---|---|---|---|
| 20110243881 A1 | Oct 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09765788 | Jan 2001 | US |
| Child | 10695574 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12212093 | Sep 2008 | US |
| Child | 13160099 | US | |
| Parent | 10695574 | Oct 2003 | US |
| Child | 12212093 | US | |
| Parent | PCT/FR99/01774 | Jul 1999 | US |
| Child | 09765788 | US |