Patent Application
20230374294
This application claims priority to and the benefit of Korean Patent Application Nos. 10-2022-0062449, filed on May 21, 2022, and 10-2022-0062450, filed on May 21, 2022, the disclosure of which is incorporated herein by reference in its entirety.
Embodiments relate to a biodegradable polyester resin composition and a biodegradable molded article including the biodegradable polyester resin composition.
Recently, a solution to the problem of handling various household items, especially disposable products, is required as concerns about environmental problems increase. Specifically, polymeric materials are inexpensive and have excellent processability properties, so they are widely used to manufacture various products such as films, fibers, packaging materials, bottles, containers, etc. However, polymer materials have the disadvantage that harmful substances are emitted when incinerated when the lifespan of a product is over, and it takes hundreds of years depending on the types thereof to completely decompose them naturally.
To overcome the limitations of the polymers, research on biodegradable polymers that are decomposed within a short period of time is being actively conducted. As biodegradable polymers, polylactic acid (PLA), polybutyleneadipate terephthalate (PBAT), polybutylene succinate (PBS), and the like are being used.
Such biodegradable resin compositions are disclosed in Korean Patent Application No. 2012-0103158, and the like.
Therefore, the present disclosure has been made in view of the above problems, and it is an object of the present disclosure to provide a biodegradable polyester resin composition having improved printability while having improved moisture resistance, and a biodegradable molded article including the biodegradable polyester resin composition.
In accordance with an aspect of the present disclosure, the above and other objects can be accomplished by the provision of A biodegradable polyester resin composition, including: a polyester resin including a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid, wherein a first weight swelling rate of the biodegradable polyester resin composition is 4% to 20%, wherein the first weight swelling rate is measured by a measurement method below:
[Measurement Method]
the biodegradable polyester resin composition is dried at 80° C., placed in a stainless steel mold, and compressed at 210° C. under a pressure of 10 MPa for 3 minutes to produce a polyester sheet having a thickness of 300 μm, an initial weight of the polyester sheet and a weight of the polyester sheet after being immersed in room-temperature ethanol for 2 hours are measured, and the first weight swelling rate is obtained by dividing a difference between the weight of the polyester sheet after being immersed and the initial weight by the initial weight.
In the biodegradable polyester resin composition according to an embodiment, a volume swelling rate of the biodegradable polyester resin composition may be 5% to 20%, wherein the volume swelling rate is measured by a measurement method below:
[Measurement Method]
an initial volume of the polyester sheet and a volume of the polyester sheet after being immersed in room-temperature ethanol for 2 hours are measured, and the volume swelling rate is obtained by dividing a difference between the volume of the polyester sheet after being immersed and the initial volume by the initial volume.
The biodegradable polyester resin composition according to an embodiment may include the silicon element in a content of about 0.1 ppm to 1000 ppm.
In an embodiment, a water contact angle of a surface of the polyester sheet may be 45° to 85°.
In an embodiment, a polarity of the surface of the polyester sheet may be 3 mN/m to 5 mN/m.
The biodegradable polyester resin composition according to an embodiment may further include a metal.
In an embodiment, the metal may include an iron element, wherein a ratio of the iron element relative to the silicon element is 0.1 to 0.7.
In the biodegradable polyester resin composition according to an embodiment, a hydrolysis degree after one week of the biodegradable polyester resin composition may be 35% to 60%, and a hydrolysis degree after three weeks of the biodegradable polyester resin composition may be 85% or more, wherein the hydrolysis degree after one week and the hydrolysis degree after three weeks are measured by a measurement method below:
[Measurement Method]
the hydrolysis degree after one week is a number average molecular weight reduction rate of the biodegradable polyester resin composition placed for one week under high-temperature and high-humidity conditions of 80° C. and a humidity of 100%, compared to an initial number average molecular weight of the biodegradable polyester resin composition, and the hydrolysis degree after three weeks is a number average molecular weight reduction rate of the biodegradable polyester resin composition placed for three weeks under high-temperature and high-humidity conditions of 80° C. and a humidity of 100%, compared to an initial number average molecular weight of the biodegradable polyester resin composition.
In the biodegradable polyester resin composition according to an embodiment, a second weight swelling rate of the biodegradable polyester resin composition may be 4% to 20%, wherein the second weight swelling rate is measured by a measurement method below:
[Measurement Method]
an initial weight of the polyester sheet and a weight of the polyester sheet after being immersed in room-temperature ethanol for 24 hours are measured, and the second weight swelling rate is obtained by dividing a difference between the weight of the polyester sheet after being immersed and the initial weight by the initial weight.
In an embodiment, a difference between the first weight swelling rate and the second swelling rate may be 5% or less.
In accordance with another aspect of the present disclosure, there is provided a biodegradable polyester resin composition, including a polyester resin including a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid, wherein a wet hardness reduction rate of the biodegradable polyester resin composition is 15% or less, wherein the wet hardness reduction rate is measured by a measurement method below:
[Measurement Method]
the biodegradable polyester resin composition is used to manufacture a polyester block having a thickness of 2.5 mm, an initial hardness of the polyester block and a wet hardness of the polyester block after being immersed in water at 30° C. for 24 hours are measured, and the wet hardness reduction rate is obtained by dividing a difference between the initial hardness and the wet hardness by the initial hardness.
In the biodegradable resin composition according to an embodiment, the initial hardness may be a Shore D hardness of 30 to 45, and the wet hardness may be a Shore D hardness of 28 to 43.
In the biodegradable polyester resin composition according to an embodiment, the wet hardness reduction rate may be 12% or less.
In the biodegradable polyester resin composition according to an embodiment, a content of a silicon element in the biodegradable polyester resin composition may be 0.1 ppm to 1000 ppm.
In the biodegradable polyester resin composition according to an embodiment, a water contact angle of a surface of the polyester block may be 45° to 85°.
In the biodegradable polyester resin composition according to an embodiment, a difference between the wet hardness after being immersed in 30° C. water for 1 hour and the wet hardness after being immersed in 30° C. water for 24 hours may be 10% or less based on the initial hardness.
In the biodegradable polyester resin composition according to an embodiment, a difference between the wet hardness after being immersed in 30° C. water for 24 hours and a wet hardness after being immersed in 70° C. water for 24 hours may be 10% or less based on the initial hardness.
In accordance with yet another aspect of the present disclosure, there is provided a biodegradable molded article, including: a polyester resin including a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid, wherein a weight swelling rate of the biodegradable molded article is 4% to 20%, wherein the weight swelling rate is measured by a measurement method below:
[Measurement Method]
the molded article is manufactured into a sample having a thickness of 300 μm, an initial weight of the sample and a weight of the sample after being immersed in room-temperature ethanol for 2 hours are measured, and the weight swelling rate is obtained by dividing a difference between the weight of the sample after being immersed and the initial weight by the initial weight.
In the biodegradable molded article according to an embodiment, a wet hardness reduction rate of the biodegradable molded article may be 15% or less, wherein the wet hardness reduction rate is measured by a measurement method below:
[Measurement Method]
the biodegradable molded article is processed into a block having a thickness of 2.5 mm, an initial hardness of the block and a wet hardness of the block after being immersed in 30° C. water for 24 hours are measured, and the wet hardness reduction rate is obtained by dividing a difference between the initial hardness and the wet hardness by the initial hardness.
The biodegradable molded article according to an embodiment may include an iron element and a silicon element, wherein a mass ratio of the iron element relative to the silicon element is 0.1 to 0.7.
The above and other objects, features and other advantages of the present disclosure will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
Hereinafter, the present disclosure will be described in more detail with reference to the following embodiments. The scope of the present disclosure is not limited to the following embodiments and covers modifications of the technical spirit substantially equivalent thereto.
In the specification, when a certain part “includes” a certain component, this indicates that the part may further include another component instead of excluding another component unless there is no different disclosure.
In addition, it should be understood that all numerical ranges representing physical property values, dimensions, etc. of components described in this specification are modified by the term ‘about’ in all cases unless otherwise specified.
In this specification, Terms such as first, second, primary, and secondary are used to describe various components, and the components are not limited by the terms. The terms are only used for the purpose of distinguishing one component from another.
In this specification, ppm is a unit based on mass. The 1 ppm is 1 in 1 million of the total mass. That is, the 1 ppm is 0.0001 wt % based on the total mass.
The biodegradable polyester resin composition according to an embodiment includes a biodegradable polyester resin. The biodegradable polyester resin composition according to an embodiment may include the biodegradable polyester resin alone or together with other resins or additives.
The biodegradable polyester resin includes a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid. The biodegradable polyester resin includes a diol residue, an aromatic dicarboxylic acid residue and an aliphatic dicarboxylic acid residue. The diol residue is derived from the diol, the aromatic dicarboxylic acid residue is derived from the aromatic dicarboxylic acid, and the aliphatic dicarboxylic acid residue is derived from the aliphatic dicarboxylic acid. The biodegradable polyester resin includes a diol component, an aromatic dicarboxylic acid component and an aliphatic dicarboxylic acid component. Likewise, the diol component may be derived from the diol, the aromatic dicarboxylic acid component may be derived from the aromatic dicarboxylic acid, and the aliphatic dicarboxylic acid component may be derived from the aliphatic dicarboxylic acid.
In a description of the biodegradable polyester resin composition according to an embodiment, a diol residue may be expressed as a diol. In the biodegradable polyester resin, a dicarboxylic acid residue may be expressed as dicarboxylic acid. In addition, the residue may be expressed as a component.
The diol may be an aliphatic diol. The diol may be a bio-derived diol. The diol may be at least one selected from the group consisting of ethanediol, 1,2-propanediol, 1,3-propanediol, 2-methyl-1,3-propanediol, 2,2-dimethyl-1,3-propanediol, 2,2-diethyl-1,3-propanediol, 2-ethyl-2-isobutyl-1,3-propanediol, 1,2-butanediol, 1,4-butanediol, 1,5-pentanediol, 3-methyl-1,5-pentanediol, 2,2,4-trimethyl-1,3-pentanediol, 1,6-hexanediol, 2-ethyl-1,3-hexanediol, 2,4-dimethyl-2-ethyl-1,3-hexanediol, 2,2,4-trimethyl-1,6-hexanediol, 2-methyl-1, 8-octanediol, 1,9-nonanediol, 1,10-decanediol and 1,12-octadecanediol or derivatives thereof.
The diol may be at least one selected from the group consisting of 1,4-butanediol, 1,2-ethanediol, 1,3-propanediol, diethylene glycol and neopentyl glycol or derivatives thereof.
The diol may be at least one selected from the group consisting of 1,4-butanediol, 1,2-ethanediol, 1,3-propanediol or derivatives thereof.
The diol may include 1,4-butanediol or a derivative thereof.
The aromatic dicarboxylic acid may be at least one selected from the group consisting of phthalic acid, terephthalic acid, isophthalic acid, 1,4-naphthalenedicarboxylic acid, 1,5-naphthalenedicarboxylic acid, 2,6-naphthalene dicarboxylic acid, 1,8-naphthalenedicarboxylic acid, 4,4′-diphenyl dicarboxylic acid, 4,4′-diphenyl ether dicarboxylic acid, anthracen dicarboxylic acid, and phenanthren dicarboxylic acid or derivatives thereof.
The aromatic dicarboxylic acid may be at least one selected from the group consisting of terephthalic acid, dimethyl terephthalate, 2,6-naphthalene dicarboxylic acid, isophthalic acid or derivatives thereof.
The aromatic dicarboxylic acid may include terephthalic acid, dimethyl terephthalate or a derivative thereof.
The aliphatic dicarboxylic acid may be at least one selected from the group consisting of oxalic acid, malonic acid, succinic acid, maleic acid, fumaric acid, glutaric acid, adipic acid, pimelic acid, serveric acid, azelaic acid, sebacic acid, dodecanedicarboxylic acid and 1,4-cyclohexanedicarboxylic acid or derivatives thereof.
The aliphatic dicarboxylic acid may be at least one selected from the group consisting of adipic acid, succinic acid and sebacic acid or derivatives thereof.
The aliphatic dicarboxylic acid may include an adipic acid or a derivative thereof.
In the biodegradable polyester resin, a molar ratio of all diol residues including the diol to all dicarboxylic acid residues including the aromatic dicarboxylic acid and the aliphatic dicarboxylic acid may be about 1:0.9 to about 1:1.1. A molar ratio of all diol residues to all dicarboxylic acid residues may be about 1:0.95 to about 1:1.05.
In the biodegradable polyester resin, a molar ratio of the aromatic dicarboxylic acid residue to the aliphatic dicarboxylic acid residue may be about 3:7 to about 7:3. In the biodegradable polyester resin, a molar ratio of the aromatic dicarboxylic acid residue to the aliphatic dicarboxylic acid residue may be about 3.3:6.7 to about 6.7:3.3. In the biodegradable polyester resin, a molar ratio of the aromatic dicarboxylic acid residue to the aliphatic dicarboxylic acid residue may be about 4:6 to about 6:4. In the biodegradable polyester resin, a molar ratio of the aromatic dicarboxylic acid residue to the aliphatic dicarboxylic acid residue may be about 4.2:5.8 to about 5:5.
The biodegradable polyester resin may include a diol residue derived from 1,4-butanediol in a content of about 90 mol % or more based on the total diol. The biodegradable polyester resin may include a diol residue derived from 1,4-butanediol in a content of about 95 mol % or more based on the total diol. The biodegradable polyester resin may include a diol residue derived from 1,4-butanediol in a content of about 98 mol % or more based on the total diol.
The biodegradable polyester resin may include an aromatic dicarboxylic acid residue derived from terephthalic acid or dimethyl terephthalate in a content of about 30 mol % to about 70 mol % based on the total dicarboxylic acid. The biodegradable polyester resin may include an aromatic dicarboxylic acid residue derived from terephthalic acid or dimethyl terephthalate in a content of about 35 mol % to about 65 mol % based on the total dicarboxylic acid. The biodegradable polyester resin may include a dicarboxylic acid residue derived from terephthalic acid or dimethyl terephthalate in a content of about 40 mol % to about 59 mol % based on the total dicarboxylic acid. The biodegradable polyester resin may include an aromatic dicarboxylic acid residue derived from terephthalic acid or dimethyl terephthalate in a content of about 43 mol % to about 53 mol % based on the total dicarboxylic acid.
The biodegradable polyester resin may include an aliphatic dicarboxylic acid residue derived from adipic acid in a content of about 30 mol % to about 70 mol % based on the total dicarboxylic acid. The biodegradable polyester resin may include an aliphatic dicarboxylic acid residue derived from adipic acid in a content of about 35 mol % to about 65 mol % based on the total dicarboxylic acid. The biodegradable polyester resin may include an aliphatic dicarboxylic acid residue derived from adipic acid in a content of about 41 mol % to about 60 mol % based on the total dicarboxylic acid. The biodegradable polyester resin may include an aliphatic dicarboxylic acid residue derived from adipic acid in a content of about 47 mol % to about 57 mol % based on the total dicarboxylic acid.
In addition, the biodegradable polyester resin may include at least one first block and at least one second block. The biodegradable polyester resin may have a molecular structure in which the first block and the second block are alternately bonded.
The first block may include the diol residue and the aromatic dicarboxylic acid residue. The first block may be formed by esterification of the diol and the aromatic dicarboxylic acid. The first block may include only the diol residue and the aromatic dicarboxylic acid residue. The first block may include only repeating units formed by the esterification of the diol and the aromatic dicarboxylic acid. That is, the first block may mean the sum of repeating units of the diol and the aromatic dicarboxylic acid before being combined with the aliphatic dicarboxylic acid.
The second block may include the diol residue and the aliphatic dicarboxylic acid residue. The second block may be formed by esterification of the diol and the aliphatic dicarboxylic acid. The second block may include only the diol residue and the aliphatic dicarboxylic acid residue. The second block may include only repeating units formed by the esterification of the diol and the aliphatic dicarboxylic acid. That is, the second block may mean the sum of repeating units of the diol and the aliphatic dicarboxylic acid before being combined with the aromatic dicarboxylic acid.
In the biodegradable polyester resin, a ratio (X/Y) of the number (X) of the first blocks to the number (Y) of the second blocks may be about 0.5 to about 1.5. In the biodegradable polyester resin, the ratio (X/Y) of the number (X) of the first blocks to the number (Y) of the second blocks may be about 0.6 to about 1.4. In the biodegradable polyester resin, the ratio (X/Y) of the number (X) of the first blocks to the number (Y) of the second blocks may be about 0.7 to about 1.3. In the biodegradable polyester resin, the ratio (X/Y) of the number (X) of the first blocks to the number (Y) of the second blocks may be about 0.75 to about 1.2. In addition, in the biodegradable polyester resin, the ratio (X/Y) of the number (X) of the first blocks to the number (Y) of the second blocks may be 0.8 to 1. The number of the first blocks may be smaller than the number of the second blocks.
The number of the first blocks may be about 30 to about 300. The number of the first blocks may be about 40 to about 250. The number of the first blocks may be about 50 to about 220. The number of the first blocks may be about 60 to about 200. The number of the first blocks may be about 70 to about 200. The number of the first blocks may be about 75 to about 200.
The number of the first blocks may vary depending upon the content of the aromatic dicarboxylic acid, the molecular weight of the biodegradable polyester resin and an alternation ratio to be described below. That is, the number of the first blocks may increase as a molar ratio of the aromatic dicarboxylic acid increases, as the molecular weight of the biodegradable polyester resin increases, and as an alternation ratio to be described below increases.
The number of the second blocks may be about 30 to about 300. The number of the second blocks may be about 40 to about 250. The number of the second blocks may be about 50 to about 220. The number of the second blocks may be about 60 to about 200. The number of the second blocks may be about 70 to about 200. The number of the second blocks may be about 75 to about 200.
When the biodegradable polyester resin includes the first block and the second block within the range, the biodegradable polyester resin composition according to an embodiment may have appropriate biodegradability while having appropriate mechanical strength. In addition, when the biodegradable polyester resin includes the first block and the second block within the range, the biodegradable polyester resin composition according to an embodiment may have improved stiffness while having improved flexibility. Accordingly, the biodegradable polyester resin composition according to an embodiment may be used for an injection-molded article, etc. In addition, when the biodegradable polyester resin includes the first block and the second block within the range, the biodegradable polyester resin composition according to an embodiment may have appropriate biodegradability while having appropriate durability to ultraviolet light, and the like.
The first block may be represented by Formula 1 below:
where R1 is a substituted or unsubstituted arylene group having 6 to 20 carbon atoms, R2 is a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms, and m is 1 to 20.
R1 may be a substituted or unsubstituted phenylene group, and R2 may be a butylene group.
The second block may be represented by Formula 2 below:
where R3 and R4 are each independently a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms, and n is 1 to 20.
R3 and R4 may be a butylene group.
The biodegradable polyester resin may have a structure in which the first block and the second block are alternately bonded to each other. The biodegradable polyester resin may be represented by Formula 3 below.
where R1 is a substituted or unsubstituted arylene group having 6 to 20 carbon atoms, R2 is a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms, and m is 1 to 20. In addition, R3 and R4 are each independently a substituted or unsubstituted alkylene group having 1 to 20 carbon atoms, and n is 1 to 20.
The diol residue may include a residue of 1,4-butanediol or derivative thereof, the aromatic dicarboxylic acid residue may include a residue of terephthalic acid or derivative thereof, and the aliphatic dicarboxylic acid residue may include a residue of adipic acid or derivative thereof.
For example, the biodegradable polyester resin may include a first block including a residue of 1,4-butanediol or derivative thereof and a residue of terephthalic acid or derivative thereof.
Alternatively, the biodegradable polyester resin may include a first block including a residue of 1,4-butanediol or derivative thereof and a residue of dimethyl terephthalate or derivative thereof.
The biodegradable polyester resin may include a second block including a residue of 1,4-butanediol or derivative thereof and a residue of adipic acid or derivative thereof.
Alternatively, the biodegradable polyester resin may include a second block including a residue of 1,4-butanediol or derivative thereof and a residue of succinic acid or derivative thereof.
A biodegradable polyester resin according to an embodiment of the present disclosure may include a first block including a residue of 1,4-butanediol or derivative thereof and a residue of terephthalic acid or derivative thereof; and a second block including a residue of 1,4-butanediol or derivative thereof and a residue of adipic acid or derivative thereof.
The first block may be represented by Formula 4 below, and the second block may be represented by Formula 5 below:
where m is 1 to 20.
where n is 1 to 20.
The biodegradable polyester resin may be represented by Formula 6 below:
where m is 1 to 20, and n is 1 to 20.
When the first block and the second block satisfy the constitution, it may be more advantageous to provide a biodegradable polyester sheet, film or molded article having excellent biodegradability and water degradability and improved properties.
In addition, when the biodegradable polyester resin includes the first block and the second block within the range, the biodegradable polyester resin composition according to an embodiment may have appropriate mechanical properties and appropriate UV resistance.
Since the first and second blocks have the characteristics, the mechanical properties of the biodegradable polyester resin composition according to an embodiment may be improved.
Since the first and second blocks have the characteristics, the biodegradable polyester resin composition according to an embodiment may have appropriate UV resistance.
Since the first and second blocks have the characteristics, the biodegradable polyester resin composition according to an embodiment may have an appropriate biodegradation rate.
Since the first and second blocks have the characteristics, the biodegradable polyester resin composition according to an embodiment may have an appropriate hydrolysis rate.
The biodegradable polyester resin may further include a branching agent. The branching agent may include at least one selected from the group consisting of a trihydric or higher alcohol, an anhydride and a trihydric or higher carboxylic acid. The branching agent may react with the diol, the aromatic dicarboxylic acid and the aliphatic dicarboxylic acid. Accordingly, the branching agent may be included as a part of the molecular structure of the biodegradable polyester resin.
The trihydric or higher alcohol may be at least one selected from the group consisting of glycerol, pentaerythritol or trimethylolpropane.
The trihydric or higher carboxylic acid may be at least one selected from the group consisting of methane tricarboxylic acid, ethanetricarboxylic acid, citric acid, benzene-1,3,5-tricarboxylic acid, 5-sulfo-1,2,4-benzenetricarboxylic acid, ethane-1,1,2,2-tetracarboxylic acid, propane-1,1,2,3-tetracarboxylic acid, butane-1,2,3,4-tetracarboxylic acid, cyclopentane-1,2,3,4-tetracarboxylic acid and benzene-1,2,4,5-tetracarboxylic acid.
The anhydride may include at least one selected from the group consisting of trimellitic anhydride, succinic anhydride, methylsuccinic anhydride, ethylsuccinic anhydride, 2,3-butanedicarboxylic anhydride, 2,4-pentanedicarboxylic anhydride, 3,5-heptanedicarboxylic anhydride, 1,2,3,4-butanetetracarboxylic dianhydride, maleic anhydride, dodecyl succinic anhydride and pyromellitic anhydride.
The branching agent may be included in a content of about 0.1 wt % to about 5 wt % in the biodegradable polyester resin based on the total amount of the biodegradable polyester resin. The branching agent may be included in a content of about 0.1 wt % to about 3 wt % in the biodegradable polyester resin based on the total amount of the biodegradable polyester resin. The branching agent may be included in a content of about 0.1 wt % to about 1 wt % in the biodegradable polyester resin based on the total amount of the biodegradable polyester resin.
Since the biodegradable polyester resin includes the branching agent within the range, the biodegradable polyester resin composition according to an embodiment may have appropriate mechanical characteristics and appropriate biodegradability.
The biodegradable polyester resin may further include polycarbonate diol. The polycarbonate diol may be bonded as a molecular structure to the biodegradable polyester resin to be incorporated therein.
The polycarbonate diol may be prepared by a dehydration condensation reaction of a carbonate and a polyhydric alcohol. The carbonate may be at least one selected from the group consisting of dimethylcarbonate, diethylcarbonate, dibutyl carbonate, diphenyl carbonate and ethylene carbonate. The polyhydric alcohol may be at least one selected from the group consisting of ethylene glycol, diethylene glycol, neopentyl glycol, 1,6-hexanediol and 1,2-propanediol.
The weight average molecular weight of the polycarbonate diol may be about 500 to about 5000. The weight average molecular weight of the polycarbonate diol may be about 700 to about 4000. The weight average molecular weight of the polycarbonate diol may be about 800 to about 3500.
In addition, the viscosity of the polycarbonate diol may be about 300 cps to about 20000 cps. The viscosity of the polycarbonate diol may be about 400 cps to about 15000 cps. The viscosity of the polycarbonate diol may be about 500 cps to about 14000 cps. The viscosity of the polycarbonate diol may be measured according to ASTM/ISO 2555 at room temperature.
The OH value of the polycarbonate diol may be about 20 mgKOH/g to about 350 mgKOH/g. The OH value of the polycarbonate diol may be about 30 mgKOH/g to about 300 mgKOH/g.
The polycarbonate diol may be included in a content of about 0.1 parts by weight to about parts by weight in the biodegradable polyester resin based on 100 parts by weight of the biodegradable polyester resin. The polycarbonate diol may be included in a content of about 0.5 parts by weight to about 3 parts by weight in the biodegradable polyester resin based on 100 parts by weight of the biodegradable polyester resin. The polycarbonate diol may be included in a content of about 1 part by weight to about 3 parts by weight in the biodegradable polyester resin based on 100 parts by weight of the biodegradable polyester resin.
Since the polycarbonate diol has the characterictics, the biodegradable polyester resin composition according to an embodiment may have appropriate wet hardness, appropriate mechanical properties, appropriate solvent resistance, appropriate hydrolysis and appropriate biodegradability.
The biodegradable polyester resin may further include a polyether polyol. The polyether polyol may be bonded as a molecular structure to the biodegradable polyester resin to be incorporated therein.
The polyether polyol may be prepared by additionally reacting an initiator having two or more active hydrogens (—OH or NH2) with propylene oxide (PO) or ethylene oxide (EO). Examples of the polyether polyol include polypropylene glycol, polyethylene glycol, polytetramethylene ether glycol, and the like.
The weight average molecular weight of the polyether polyol may be about 500 to about 5000. The weight average molecular weight of the polyether polyol may be about 700 to about 4000. The weight average molecular weight of the polyether polyol may be about 800 to about 3500.
In addition, the viscosity of the polyether polyol may be about 300 cps to about 20000 cps. The viscosity of the polyether polyol may be about 400 cps to about 15000 cps. The viscosity of the polyether polyol may be about 500 cps to about 14000 cps. The viscosity of the polyether polyol may be measured according to ASTM/ISO 2555 at room temperature.
The polyether polyol may be included in a content of about 0.1 parts by weight to about parts by weight in the biodegradable polyester resin based on 100 parts by weight of the biodegradable polyester resin. The polyether polyol may be included in a content of about 0.5 parts by weight to about 3 parts by weight in the biodegradable polyester resin based on 100 parts by weight of the biodegradable polyester resin. The polyether polyol may be included in a content of about 1 part by weight to about 3 parts by weight in the biodegradable polyester resin based on 100 parts by weight of the biodegradable polyester resin.
Since the polyether polyol has the characteristics, the biodegradable polyester resin composition according to an embodiment may have appropriate wet hardness, appropriate mechanical properties, appropriate solvent resistance, appropriate hydrolysis and appropriate biodegradability.
The biodegradable polyester resin composition according to an embodiment may include the biodegradable resin in a content of about 30 wt % or more based on the total weight of the composition. The biodegradable polyester resin composition according to an embodiment may include the biodegradable resin in a content of about 50 wt % or more based on the total weight of the composition. The biodegradable polyester resin composition according to an embodiment may include the biodegradable resin in a content of about 70 wt % or more based on the total weight of the composition. The biodegradable polyester resin composition according to an embodiment may include the biodegradable resin in a content of about 80 wt % or more based on the total weight of the composition. The biodegradable polyester resin composition according to an embodiment may include the biodegradable resin in a content of about 90 wt % or more based on the total weight of the composition. The biodegradable polyester resin composition according to an embodiment may include the biodegradable resin in a content of about 95 wt % or more based on the total weight of the composition. The biodegradable polyester resin composition according to an embodiment may include the biodegradable resin in a content of about 99 wt % or more based on the total weight of the composition. A maximum content of the biodegradable resin in the biodegradable polyester resin composition according to an embodiment may be about 100 wt % based on the total weight of the composition.
The biodegradable polyester resin composition according to an embodiment may further include a reinforcing material. The reinforcing material may improve the mechanical properties of the biodegradable polyester resin composition according to an embodiment and the mechanical properties of a film or molded article made of the composition. In addition, the reinforcing material may control the deformation characteristics of the biodegradable polyester resin composition according to an embodiment due to ultraviolet rays. In addition, the reinforcing material may control the hydrolysis characteristics of the biodegradable polyester resin composition according to an embodiment. In addition, the reinforcing material may control the biodegradability of the biodegradable polyester resin according to an embodiment.
The reinforcing material may be a fiber derived from biomass. The reinforcing material may be a fiber made of an organic material. The reinforcing material may be nanocellulose.
The nanocellulose may be one or more selected from the group consisting of nanocrystalline cellulose, cellulose nanofiber, microfibrillated cellulose, hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxypropylmethyl cellulose, cellulose acetate, methyl cellulose, ethyl cellulose, propyl cellulose, butyl cellulose, pentyl cellulose, hexyl cellulose and cyclohexyl cellulose.
The nanocellulose may include an ion-bonded metal. The nanocrystalline cellulose may include elemental sodium. In addition, the nanocrystalline cellulose may include sulphate. The nanocrystalline cellulose may include a carboxylate. The nanocrystalline cellulose may include a cellulose hydrogen sulphate sodium salt (Cellulose hydrogen sulphate sodium salt.
The nanocellulose may be represented by Formula 7 below:
[(C6H10O5)xSO3Na], [Formula 7]
where x is 1 to 35, and y is 1 to 10. x may be 15 to 35, and y may be 1 to 10.
The specific surface area of the nanocellulose may be about 200 m2/g to about 600 m2/g. The specific surface area of the nanocellulose may be about 250 m2/g to about 500 m2/g.
The weight average molecular weight of the nanocellulose may be about 10000 g/mol to about 40000 g/mol. The weight average molecular weight of the nanocrystalline cellulose may be about 11000 g/mol to about 35000 g/mol.
The moisture content of the nanocrystalline cellulose may be about 2 wt % to about 8 wt %. The moisture content of the nanocrystalline cellulose may be about 4 wt % to about 6 wt %.
The average diameter of the nanocellulose may be about 0.5 nm to about 10 nm. The average diameter of the nanocellulose may be about 1 nm to about 8 nm. The average diameter of the nanocellulose may be about 1.5 nm to about 7 nm.
The average length of the nanocellulose may be about 20 nm to about 300 nm. The average length of the nanocellulose may be about 30 nm to about 180 nm. The average length of the nanocellulose may be about 35 nm to about 150 nm.
When the diameter and length of the nanocellulose satisfy the ranges, the biodegradability and properties of the biodegradable polyester resin or the biodegradability and properties of a biodegradable polyester sheet, film and molded article made using the biodegradable polyester resin may be further improved
The diameter and length of the nanocellulose may be measured by atomic force microscopy in a water-dispersed state.
The sulfur content of the nanocellulose may be about 0.1 wt % to about 1.2 wt % based on the total amount of the nanocrystalline cellulose. The sulfur content of the nanocellulose may be about 0.2 wt % to about 1.1 wt % based on the total amount of the nanocellulose.
The pH of the nanocellulose may be 5 to 8. The pH of the nanocellulose may be 6 to 8.
The zeta potential of the nanocellulose may be about −25 mV to about −50 mV. The zeta potential of the nanocellulose may be about −30 mV to about −45 mV.
The nanocellulose may be included in a content of about 0.01 parts by weight to about 2 parts by weight in the biodegradable polyester resin composition according to an embodiment based on 100 parts by weight of the biodegradable polyester resin. The nanocellulose may be included in a content of about 0.03 parts by weight to about 1.5 parts by weight in the biodegradable polyester resin composition according to an embodiment based on 100 parts by weight of the biodegradable polyester resin. The nanocellulose may be included in a content of about 0.04 parts by weight to about 1.2 parts by weight in the biodegradable polyester resin composition according to an embodiment based on 100 parts by weight of the biodegradable polyester resin. The nanocellulose may be included in a content of about 0.05 parts by weight to about 1 part by weight in the biodegradable polyester resin composition according to an embodiment based on 100 parts by weight of the biodegradable polyester resin.
Since the nanocellulose has the characteristics, it may be uniformly dispersed in the biodegradable polyester resin composition according to an embodiment.
Since the nanocellulose has the characteristics, it may improve the mechanical properties of the biodegradable polyester resin composition according to an embodiment.
In addition, the nanocellulose severs as a nucleating agent, thereby being capable of improving the crystallization rate of the biodegradable polyester resin composition according to an embodiment. Accordingly, the nanocellulose may increase the crystallization temperature of the biodegradable polyester resin composition according to an embodiment.
Since the nanocellulose has the characteristics, the biodegradable polyester resin composition according to an embodiment may have appropriate UV resistance.
Since the nanocellulose has the characteristics, the biodegradable polyester resin composition according to an embodiment may have an appropriate biodegradation rate.
Since the nanocellulose has the characteristics, the biodegradable polyester resin composition according to an embodiment may have an appropriate hydrolysis rate.
The biodegradable polyester resin composition according to an embodiment may include a metal salt.
The metal salt may be included in a content of about 0.1 ppm to about 1000 ppm based on the total weight of the biodegradable polyester resin composition according to an embodiment. The metal salt may be included in a content of about 1 ppm to about 500 ppm based on the total weight of the biodegradable polyester resin composition according to an embodiment. The metal salt may be included in a content of about 1 ppm to about 100 ppm based on the total weight of the biodegradable polyester resin composition according to an embodiment. The metal salt may be included in a content of about 1 ppm to about 50 ppm based on the total weight of the biodegradable polyester resin composition according to an embodiment.
The metal salt may be at least one selected from the group consisting of a nitrate, a sulfate, hydrochloride, a carboxylate and the like. The metal salt may be at least one selected from the group consisting of titanium salt, silicon salt, sodium salt, calcium salt, potassium salt, magnesium salt, copper salt, iron salt, aluminum salt, silver salt and the like. The metal salt may be at least one selected from the group consisting of magnesium acetate, calcium acetate, potassium acetate, copper nitrate, silver nitrate, sodium nitrate, and the like.
The metal salt may include one or more selected from the group consisting of iron (Fe), magnesium (Mg), nickel (Ni), cobalt (Co), copper (Cu), palladium (Pd), zinc (Zn), vanadium (V), titanium, (Ti), indium (In), manganese (Mn), silicon (Si) and tin (Sn).
In addition, the metal salt may be selected from the group consisting of acetate, nitrate, nitride, sulfide, sulfate, sulfoxide, hydroxide, hydrate, chloride, chlorinate and bromide.
Since the biodegradable polyester resin composition according to an embodiment includes the metal salt within the content, a hydrolysis rate and a biodegradation rate may be appropriately controlled.
Since the biodegradable polyester resin composition according to an embodiment includes the metal salt within the content, a hydrolysis rate and a biodegradation rate may be appropriately controlled.
The biodegradable polyester resin composition according to an embodiment may further include an anti-hydrolysis agent.
The anti-hydrolysis agent may be at least one selected from among silicone-based compounds such as silane, silazane and siloxane.
The anti-hydrolysis agent may include alkoxy silane. The anti-hydrolysis agent may include trimethoxy silane and/or triethoxy silane. The anti-hydrolysis agent may include alkoxy silane including an epoxy group. The anti-hydrolysis agent may include at least one selected from the group consisting of 2-(3,4-epoxycyclohexyl) ethyltrimethoxysilane, 3-glycidoxypropyl methyldimethoxysilane, 3-glycidoxypropyl trimethoxysilane, 3-glycidoxypropyl methyldiethoxysilane and 3-glycidoxypropyl triethoxysilane.
The anti-hydrolysis agent may be included in a content of about 1 ppm to about 10000 ppm in the biodegradable polyester resin composition according to an embodiment. The anti-hydrolysis agent may be included in a content of about 1 ppm to about 1000 ppm in the biodegradable polyester resin composition according to an embodiment. The anti-hydrolysis agent may be included in a content of about 5 ppm to 500 ppm in the biodegradable polyester resin composition according to an embodiment. The anti-hydrolysis agent may be included in a content of about 10 ppm to 300 ppm in the biodegradable polyester resin composition according to an embodiment.
The anti-hydrolysis agent may be bonded to the biodegradable polyester resin. The anti-hydrolysis agent may be chemically bonded to the biodegradable polyester resin. The anti-hydrolysis agent may be chemically bonded to a polymer included in the biodegradable polyester resin. The anti-hydrolysis agent may couple polymers included in the biodegradable polyester resin.
Since the biodegradable polyester resin composition according to an embodiment includes the anti-hydrolysis agent within the range, it may have appropriate hydrolysis resistance. In particular, since the biodegradable polyester resin according to an embodiment includes the anti-hydrolysis agent within the range, it may have appropriate initial hydrolysis characteristics and improved biodegradability.
Accordingly, the biodegradable polyester resin composition according to an embodiment may include a silicon element. The biodegradable polyester resin composition according to an embodiment may include the silicon element in a content of about 1 ppm to about 150 ppm. The biodegradable polyester resin composition according to an embodiment may include the silicon element in a content of about 0.1 ppm to about 100 ppm. The biodegradable polyester resin composition according to an embodiment may include the silicon element in a content of about 0.1 ppm to about 50 ppm. The biodegradable polyester resin composition according to an embodiment may include the silicon element in a content of about 0.1 ppm to about 20 ppm.
In addition, the anti-hydrolysis agent may also react with a terminal carboxyl group or an unreacted carboxyl group. Accordingly, the biodegradable polyester resin composition according to an embodiment may have a low acid value.
In addition, the anti-hydrolysis agent may couple polymers included in the biodegradable polyester resin, so that the biodegradable polyester resin composition according to an embodiment may increase the ratio of high-molecular-weight polymers. Accordingly, the mechanical properties of the biodegradable polyester resin composition according to an embodiment may be improved.
The biodegradable polyester resin composition according to an embodiment may further include a chain extender.
The chain extender may include isocyanate.
The chain extender may be at least one selected from the group consisting of monofunctional isocyanate or polyfunctional isocyanate.
The chain extender may be at least one selected from the group consisting of tolylene 2,4-diisocyanate, tolylene 2,6-diisocyanate, diphenylmethane 4,4′-diisocyanate and 2,4′-diisocyanate, naphthalene 1,5-diisocyanate, xylylene diisocyanate, hexamethylene diisocyanate, pentamethylene diisocyanate, isophorone diisocyanate and methylenebis(4-isocyanatocyclohexane).
The chain extender may include triisocyanate. The chain extender may include tri(4-isocyanatophenyl)methane.
The chain extender may include an acrylic polymer. The acrylic polymer may include an acryl group. The acryl group may be bonded to a main chain as a side chain. The acrylic polymer may include an epoxy group. The epoxy group may be bonded to the main chain as a side chain.
The chain extender may include a styrene-based polymer. The chain extender may include a styrene-based glycidyl acrylate.
The chain extender may be chemically bonded to the biodegradable polyester resin. The chain extender may be chemically bonded to a polymer included in the biodegradable polyester resin. The chain extender may be bonded to a terminal of the polymer included in the biodegradable polyester resin. In addition, the chain extender may be bonded to terminals of three polymers included in the biodegradable polyester resin.
The chain extender may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 0.1 wt % to about 10 wt % based on the total amount of the composition. The chain extender may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 0.2 wt % to about 8 wt % based on the total amount of the composition. The chain extender may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 0.3 wt % to about 7 wt % based on the total amount of the composition.
When the biodegradable polyester resin composition according to an embodiment includes the chain extender within the range, it may have appropriate hydrolysis resistance and appropriate biodegradability.
In addition, the chain extender may react with a terminal carboxyl group or an unreacted carboxyl group. Accordingly, the biodegradable polyester resin composition according to an embodiment may have a low acid value.
In addition, the chain extender couples polymers included in the biodegradable polyester resin, so that the biodegradable polyester resin composition according to an embodiment may increase the ratio of high-molecular-weight polymers. Accordingly, the mechanical properties of the biodegradable polyester resin composition according to an embodiment may be improved.
The biodegradable polyester resin composition according to an embodiment may include an oligomer. The molecular weight of the oligomer may be about 400 to about 1300.
The oligomer may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 3000 ppm to about 30000 ppm based on the total amount of the resin composition. The oligomer may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 5000 ppm to about 20000 ppm based on the total amount of the resin composition. The oligomer may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 5000 ppm to about 15000 ppm based on the total amount of the resin composition. The oligomer may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 7000 ppm to about 15000 ppm based on the total amount of the resin composition.
The oligomer may be a reaction product of at least two or more of the diol, the aromatic dicarboxylic acid and the aliphatic dicarboxylic acid. The oligomer may be a reaction product of 1,4-butanediol, terephthalic acid and adipic acid.
The oligomer may include an oligomer in which a molar ratio of the aliphatic dicarboxylic acid is higher than that of the aromatic dicarboxylic acid. In the oligomer, a ratio of an oligomer containing a relatively large amount of the aliphatic dicarboxylic acid may be higher than a ratio of an oligomer containing a relatively large amount of the aromatic dicarboxylic acid.
The oligomer may appropriately control the hydrolysis degree of the biodegradable polyester resin composition according to an embodiment. The oligomer may be a hydrolysis regulator that appropriately controls the hydrolysis degree of the biodegradable polyester resin composition according to an embodiment.
In addition, the oligomer may appropriately control the biodegradability of the biodegradable polyester resin composition according to an embodiment. The oligomer may be a biodegradation regulator that appropriately controls the biodegradability of the biodegradable polyester resin composition according to an embodiment.
The biodegradable polyester resin composition according to an embodiment may include a heat stabilizer. The heat stabilizer may be a phosphorus-based heat stabilizer.
The heat stabilizer may be at least one selected from the group consisting of an amine-based high-temperature heat stabilizer such as tetraethylenepentamine, triethylphosphonoacetate, phosphoric acid, phosphorous acid, polyphosphric acid, trimethyl phosphate (TMP), triethyl phosphate, trimethyl phosphine, triphenyl phosphine and the like.
In addition, the heat stabilizer may be an antioxidant having an antioxidant function.
The content of the heat stabilizer may be about 3000 ppm or less based on the total weight of the biodegradable polyester resin. The content of the heat stabilizer may be, for example, ppm to 3,000 ppm, 20 ppm to 2,000 ppm, 20 ppm to 1,500 ppm or 20 ppm to 1,000 ppm based on the total weight of the biodegradable polyester resin. When the content of the heat stabilizer satisfies the range, the deterioration of the polymer due to high temperature during the reaction process may be controlled so that terminal groups of the polymer may be reduced and the color may be improved. In addition, the heat stabilizer may suppress the activation of a titanium-based catalyst, thereby controlling a reaction rate.
The biodegradable polyester resin composition according to an embodiment may include an elongation improver. Examples of the elongation improver include oil such as paraffin oil, naphthenic oil, or aromatic oil, or adipate such as dibutyl adipate, diethylhexyl adipate, dioctyl adipate, or diisopropyl adipate.
The elongation improver may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 0.001 parts by weight to about 1 part by weight based on 100 parts by weight of the biodegradable polyester resin. The elongation improver may be included in a content of about 0.01 parts by weight to about 1 part by weight based on 100 parts by weight of the biodegradable polyester resin in the biodegradable polyester resin composition according to an embodiment.
The biodegradable polyester resin composition according to an embodiment may include an inorganic filler. The inorganic filler may be at least one selected from the group consisting of calcium sulfate, barium sulfate, talc, talc powder, bentonite, kaolinite, chalk powder, calcium carbonate, graphite, gypsum, electrically conductive carbon black, calcium chloride, iron oxide, aluminum oxide, potassium oxide, dolomite, silicon dioxide, wollastonite, titanium dioxide, silicate, mica, glass fiber, mineral fiber, and the like.
In particle diameter distribution obtained by laser diffraction for the inorganic filler, a cumulative 50% particle size (D50) based on volume may be about 100 μm or less, about 85 μm or less, about 70 μm or less, about 50 μm or less, about 25 μm or less, about 10 μm or less, about 5 μm or less, about 3 μm or less or about 1 μm or less.
In addition, the specific surface area of the inorganic filler may be about 100 m2/g or more. For example, the specific surface area of the inorganic filler may be about 100 m2/g or more, about 105 m2/g or more or about 110 m2/g or more.
The inorganic filler may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 3 parts by weight to about 50 parts by weight based on 100 parts by weight of the biodegradable polyester resin. The inorganic filler may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 5 parts by weight to about 30 parts by weight based on 100 parts by weight of the biodegradable polyester resin.
The inorganic filler may be included in a content of about 3,000 ppm or less based on the total weight of the biodegradable polyester resin composition according to an embodiment. For example, the content of the inorganic filler may be about 3,000 ppm or less, about 1,500 ppm or less, about 1,200 ppm or less, about 800 ppm or less or about 600 ppm or less, particularly about 50 ppm or more, about 100 ppm or more, about 130 ppm or more, about 150 ppm or more or about 180 ppm or more based on the total weight of the biodegradable polyester resin composition according to an embodiment.
Since the biodegradable polyester resin composition according to an embodiment includes the inorganic filler within the range, the biodegradable polyester resin composition according to an embodiment may have mechanical properties, appropriate UV resistance, an appropriate biodegradation rate and an appropriate hydrolysis rate.
The biodegradable polyester resin composition according to an embodiment may further include a heterogeneous biodegradable resin. The biodegradable polyester resin composition according to an example may be a composite resin composition including two or more types of resins, a filler and an additive.
The heterogeneous biodegradable resin may be at least one selected from the group consisting of polybutylene azelate terephthalate (PBAzT), polybutylene sebacate terephthalate (PBSeT) and polybutylene succinate terephthalate (PBST), polyhydroxyalkanoate (PHA) or polylactic acid (PLA).
The heterogeneous biodegradable resin may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 10 parts by weight to about 100 parts by weight based on 100 parts by weight of the biodegradable polyester resin. The heterogeneous biodegradable resin may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 10 parts by weight to about 60 parts by weight based on 100 parts by weight of the biodegradable polyester resin. The heterogeneous biodegradable resin may be included in the biodegradable polyester resin composition according to an embodiment in a content of about 20 parts by weight to about 50 parts by weight based on 100 parts by weight of the biodegradable polyester resin.
The heterogeneous biodegradable resin may supplement the mechanical, optical and chemical properties of the biodegradable polyester resin. Since the biodegradable polyester resin composition according to an embodiment includes the heterogeneous biodegradable resin in the content, the biodegradable polyester resin composition according to an embodiment may have mechanical properties, appropriate UV resistance, an appropriate biodegradation rate and an appropriate hydrolysis rate.
In addition, the number of carboxyl terminal groups of the biodegradable polyester resin composition according to an embodiment may be about 50 eq/ton or less. For example, the number of the carboxyl terminal groups of the biodegradable polyester resin according to an embodiment may be about 50 eq/ton or less, about 48 eq/ton or less, about 45 eq/ton or less or about 42 eq/ton or less. When the number of the carboxyl terminal groups is adjusted to the range, deterioration may be prevented and improved mechanical properties may be implemented when the biodegradable polyester resin composition according to an embodiment is extruded to form a molded article.
In addition, the intrinsic viscosity (IV) of the biodegradable polyester resin composition according to an embodiment may be about 0.9 dl/g or more. The intrinsic viscosity of the biodegradable polyester resin composition according to an embodiment may be about 0.95 dl/g or more, about 1.0 dl/g or more, about 1.1 dl/g or more, about 1.2 dl/g or more or about 1.3 dl/g or more. The intrinsic viscosity of the biodegradable polyester resin composition according to an embodiment may be about 0.95 dl/g to about 1.7 dl/g. The intrinsic viscosity of the biodegradable polyester resin composition according to an embodiment may be about 1.3 dl/g to about 1.7 dl/g. The intrinsic viscosity of the biodegradable polyester resin composition according to an embodiment may be about 1.4 dl/g to about 1.7 dl/g.
A process of preparing the biodegradable polyester resin composition according to an embodiment is as follows.
Referring to
A method of preparing the biodegradable polyester resin includes a step of preparing a slurry including the diol and the aromatic dicarboxylic acid.
The step of preparing a slurry includes a step of mixing and processing the diol and the aromatic dicarboxylic acid. That is, the step of preparing a slurry is a pretreatment step before an esterification and may be a step of mixing the diol and the aromatic dicarboxylic acid and slurrying the mixture. Here, the diol may include a biomass-based diol component.
The temperature of the slurry of the diol and the aromatic dicarboxylic acid may be about 5° C. to about 15° C. higher than the melting point of the diol. For example, when the diol is 1,4-butanediol, the temperature of the slurry may be about 35° C. to about 45° C.
The diol and the aromatic dicarboxylic acid are fed into and stirred in the slurry stirrer 100, thereby preparing the slurry.
By mixing, pre-treating, and slurrying the diol and the aromatic dicarboxylic acid, the diol and the aromatic dicarboxylic acid may be uniformly reacted and the speed of an esterification may be effectively accelerated, thereby increasing reaction efficiency.
In particular, when an aromatic dicarboxylic acid, such as terephthalic acid, has complete crystallinity and is in powder form, it may be difficult to cause a homogeneous reaction due to very low solubility in the diol. Therefore, the slurrying pretreatment process may play a very important role in providing a biodegradable polyester resin, sheet, film and molded article having excellent properties according to an embodiment of the present disclosure and improving reaction efficiency.
When the aromatic dicarboxylic acid is terephthalic acid, the terephthalic acid is a white crystal that has complete crystallinity and sublimes at around 300° C. under atmospheric pressure without a melting point. In addition, the terephthalic acid has very low solubility in the diol, making it difficult for a homogeneous reaction to occur. Accordingly, when a pretreatment process is performed before an esterification, a uniform reaction may be induced by increasing the surface area for reacting with a diol in a solid matrix of terephthalic acid.
In addition, when the aromatic dicarboxylic acid is dimethyl terephthalate, the dimethyl terephthalate may be made into a molten state at about 142° C. to 170° C. by the pretreatment process and reacted with the diol, so that an esterification can be proceeded faster and more efficiently.
Meanwhile, in the pretreatment step of preparing the slurry, the structure and properties of the biodegradable polyester resin may vary depending on the particle size, particle size distribution, pretreatment reaction conditions, and the like of the aromatic dicarboxylic acid.
For example, the aromatic dicarboxylic acid may include terephthalic acid, and the terephthalic acid may have an average particle diameter (D50) of 10 μm to 400 μm measured by a particle size analyzer Microtrac S3500 in a particle size distribution (PSD), and a standard deviation of the average particle diameter (D50) may be 100 or less. The standard deviation means the square root of the variance. The average particle diameter (D50) of the terephthalic acid may be for example 20 μm to 200 μm, for example 30 μm to 180 μm, or for example 100 μm to 160 μm. When the average particle diameter (D50) of the terephthalic acid satisfies the range, it may be more advantageous in terms of the solubility improvement of the diol and the reaction rate.
In the pretreatment process, the diol and the aromatic dicarboxylic acid may be mixed and fed into the slurry stirrer 100 (tank).
The slurry stirrer 100 may be provided with, for example, an anchor-type bottom, a height to the agitator of 20 mm or more, and two or more rotary blades, which may be more advantageous to achieve an efficient stirring effect.
For example, the slurry stirrer 100 has a height of 20 mm or more to the agitator, i.e., the reactor and the bottom of the agitator may be almost attached to each other. In this case, a slurry may be obtained without precipitation. If the shape, shape and rotary blades of the agitator do not satisfy the conditions, the aromatic dicarboxylic acid may precipitate to the bottom when the diol and the aromatic dicarboxylic acid are initially mixed. In this case, phase separation may occur.
The pretreatment step of preparing the slurry may include a step of mixing the diol and the aromatic dicarboxylic acid and stirring the mixture about 50 rpm to about 200 rpm at about ° C. to about 100° C. for 10 minutes or more, for example 10 minutes to 200 minutes.
The diol may have characteristics as described above.
The diol may be added at one time or dividedly. For example, the diol may be added dividedly when mixing with an aromatic dicarboxylic acid and when mixing with an aliphatic dicarboxylic acid.
The aromatic dicarboxylic acid may have characteristics as described above.
In the pretreatment step of preparing the slurry, a molar ratio of the diol to the aromatic dicarboxylic acid may be about 0.8:1 to about 2:1. In the pretreatment step of preparing the slurry, a molar ratio of the diol to the aromatic dicarboxylic acid may be about 1.1:1 to about 1.5:1. In the pretreatment step of preparing the slurry, a molar ratio of the diol to the aromatic dicarboxylic acid may be about 1.2:1 to about 1.5:1.
When the diol is added in a larger amount than the aromatic dicarboxylic acid, the aromatic dicarboxylic acid may be easily dispersed.
In addition, an additive may be added to the slurry. The nanocellulose and/or the metal salt may be added in the form of a dispersion or solution to the slurry.
In the method of preparing the biodegradable polyester resin, a prepolymer is obtained by esterification using a slurry obtained by mixing and pretreating a diol and an aromatic dicarboxylic acid, and the prepolymer is condensation-polymerized, so that the desired structure and physical properties of the biodegradable polyester resin according to the embodiment of the present disclosure may be efficiently achieved.
The method of preparing the biodegradable polyester resin includes a step of esterifying the slurry and the aliphatic dicarboxylic acid to prepare a prepolymer. The slurry and the aliphatic dicarboxylic acid may be reacted in the ester reaction part.
In the esterification, the reaction time may be shortened by using the slurry. For example, a slurry obtained from the pretreatment step may shorten the reaction time of the esterification by 1.5 times or more.
The esterification may be performed at least twice. A prepolymer to be added to a condensation polymerization process may be formed by the esterification.
In an embodiment, the esterification may be performed at once after adding an aliphatic dicarboxylic acid, or a diol and an aliphatic dicarboxylic acid to the slurry. That is, the esterification may proceed when the slurry is fed into the esterification reactor and the aliphatic dicarboxylic acid alone or the aliphatic dicarboxylic acid and the diol are fed into the esterification reactor.
The diol and the aliphatic dicarboxylic acid may be added in the form of a slurry to a slurry including the aromatic dicarboxylic acid.
In the slurry of the diol and the aliphatic dicarboxylic acid, the average particle diameter (D50) of the aliphatic dicarboxylic acid may be about 50 μm to about 150 μm. In the slurry of the diol and the aliphatic dicarboxylic acid, the average particle diameter (D50) of the aliphatic dicarboxylic acid may be about 60 μm to about 120 μm.
In the esterification, the total number of moles of the diols introduced may be about 1.0 to about 1.8 relative to the total number of moles of the aromatic dicarboxylic acid and the aliphatic dicarboxylic acid. In the esterification, the total number of moles of the diols introduced may be about 1.1 to about 1.6 relative to the total number of moles of the aromatic dicarboxylic acid and the aliphatic dicarboxylic acid.
In addition, the temperature of the slurry of the diol and the aliphatic dicarboxylic acid may be about 5° C. to about 15° C. higher than the melting point of the diol.
In addition, various additives such as the nanocellulose may also be added to the slurry of the diol and the aliphatic dicarboxylic acid.
The esterification may be performed at about 250° C. or less for about 0.5 hours to about hours. Specifically, the esterification may be performed at about 180° C. to about 250° C., about 185° C. to about 240° C. or about 200° C. to about 240° C. under normal pressure or reduced pressure until the theoretical amount of water as a by-product reaches 95%. For example, the esterification may be performed for 0.5 hours to 5.5 hours, 0.5 hours to 4.5 hours or 1 hour to 4 hours, but is not limited thereto.
In an embodiment, the slurry may be mixed with the polycarbonate diol and/or the polyether polyol, and first esterification may be performed. Alternatively, the polycarbonate diol and/or the polyether polyol may be introduced into second esterification.
In addition, after the first esterification, a mixture of the aliphatic dicarboxylic acid and the diol may be fed into the esterification part, and second esterification may be performed with the first esterification product. In addition, the polycarbonate diol and/or the polyether polyol may be added to the second esterification.
The first esterification may be performed at 250° C. or less for 1.25 hours to 4 hours. Specifically, the first esterification may be performed at 180° C. to 250° C., 185° C. to 240° C. or 200° C. to 240° C. under normal pressure or reduced pressure until the theoretical amount of water as a by-product reaches 95%. For example, the first esterification may be performed for 1.25 hours to 4 hours, 1.25 hours to 3.5 hours or 2.5 hours to 3 hours, but is not limited thereto.
The second esterification may be performed for 0.25 hours to 3.5 hours at about 250° C. or less. Specifically, the second esterification may be performed at 180° C. to 250° C., 185° C. to 240° C. or 200° C. to 240° C. under normal pressure or reduced pressure until the theoretical amount of water as a by-product reaches 95%. For example, the second esterification may be performed for 0.5 hours to 3 hours, 1 hour to 2.5 hours or 1.5 hours to 2.5 hours, but is not limited thereto.
In the first esterification and the second esterification, the number ratio, etc. of the first block and the second block may be adjusted by adjusting the reaction temperature, the reaction time, and the contents of diol, aromatic dicarboxylic acid, and aliphatic dicarboxylic acid added, respectively. In addition, when the esterification is divided into the first esterification and the second esterification, the overall esterification may be precisely controlled. Accordingly, when the esterification is divisionally performed, the reaction stability and reaction uniformity of the esterification may be improved.
In addition, in the second esterification, the branching agent may be additionally added. That is, the prepolymer may be formed by reacting the mixture of the aliphatic dicarboxylic acid and the diol, the branching agent and the first esterification product. The characteristics and content of the branching agent may be the same as described above.
By the esterification, a prepolymer may be formed.
The number average molecular weight of the prepolymer may be about 500 to about 10000 g/mol. For example, the number average molecular weight of the prepolymer may be about 500 to about 8500 g/mol, about 500 to about 8000 g/mol, about 500 to about 7000 g/mol, about 500 g/mol to about 5000 g/mol, or about 800 g/mol to about 4000 g/mol. When the number average molecular weight of the prepolymer satisfies the range, the molecular weight of a polymer in a polycondensation reaction may be efficiently increased.
The number average molecular weight may be measured using gel permeation chromatography (GPC). Specifically, data obtained by gel permeation chromatography includes various items such as Mn, Mw and Mp. Thereamong, the molecular weight may be measured based on the number average molecular weight (Mn).
The reinforcing material, the branching agent, the polycarbonate diol, the polyether polyol or the metal salt may be added together with the slurry before the esterification. The reinforcing material, the branching agent, the polycarbonate diol, the polyether polyol and/or the metal salt may be fed into an esterification part 200 in the middle of the esterification. The reinforcing material, the branching agent, the polycarbonate diol, the polyether polyol and/or the metal salt may be added to the esterification product after the esterification. In addition, the reinforcing material, the branching agent, the polycarbonate diol, the polyether polyol and/or the metal salt may be added together with the aliphatic dicarboxylic acid. In addition, the reinforcing material, the branching agent, the polycarbonate diol, the polyether polyol and/or the metal salt may be fed into the esterification part 200 after the first esterification and before the second esterification.
Since the reinforcing material and/or the metal salt is added during the esterification, the reinforcing material and/or the metal salt may be uniformly dispersed in the biodegradable polyester resin.
The reinforcing material may have the above-described characteristics. In particular, the nanocellulose may be used as the reinforcing material.
The nanocellulose may be pre-treated by a bead mill, pre-treated by ultrasonic waves, or pre-treated by high-speed dispersion at about 1000 rpm to about 1500 rpm before being introduced. Specifically, the nano-cellulose may be water-dispersed nano-cellulose pre-treated with a bead mill or pre-treated with ultrasonic waves.
First, the bead mill pretreatment may be performed with a vertical mill or horizontal mill as a wet milling device. The horizontal mill is preferable in that the amount of beads that can be filled into a chamber is larger, and the uneven wear of the machine is reduced, the wear of the beads is reduced, and maintenance is easier, but is not limited thereto.
The bead mill pretreatment may be performed using one or more bead types selected from the group consisting of zirconium, zircon, zirconia, quartz and aluminum oxide.
Specifically, the bead mill pretreatment may be performed using beads having a diameter of about 0.3 mm to about 1 mm. For example, the diameter of the beads may be about 0.3 mm to about 0.9 mm, about 0.4 mm to about 0.8 mm, about 0.45 mm to about 0.7 mm or about 0.45 mm to about 0.6 mm.
When the diameter of the beads satisfies the range, the dispersibility of nanocellulose may be further improved. When the diameter of the beads exceeds the range, the average particle diameter and average particle deviation of nanocellulose increase, resulting in low dispersibility.
In addition, in the bead mill pretreatment, it is preferable to use beads with a higher specific gravity than that of nanocellulose in that sufficient energy can be delivered. For example, the beads may be one or more selected from the group consisting of zirconium, zircon, zirconia, quartz and aluminum oxide which have a higher specific gravity than water-dispersed nanocellulose, and zirconium beads having a specific gravity four times or higher than the water-dispersed nanocellulose are preferred, without being not limited thereto.
In addition, the ultrasonic pretreatment is a method of physically closing or pulverizing nanoparticles with waves generated by emitting 20 kHz ultrasound into a solution.
The ultrasonic pretreatment may be performed for less than 30 minutes at an output of 30000 J/s or less. For example, the ultrasonic pretreatment may be performed at an output of 25000 J/s or less or 22000 J/s or less for 25 minutes or less, 20 minutes or less or 18 minutes or less. When the output and the execution time satisfy the above ranges, the effect, i.e., the improvement of dispersibility, of the ultrasonic pretreatment may be maximized. When the output exceeds the above range, the nanoparticles may rather re-agglomerate and the dispersibility may be lowered.
The nanocellulose according to an embodiment may be pre-treated with a bead mill or pre-treated with ultrasonic waves. Alternatively, the nanocellulose according to an embodiment may be pre-treated with a bead mill and pre-treated with ultrasonic waves. Here, it is preferred to perform ultrasonic pretreatment after pre-treating with a bead mill in terms of improving dispersibility by preventing re-agglomeration.
The nanocellulose according to an embodiment may be pre-treated with a bead mill or pre-treated with ultrasonic waves. Alternatively, the nanocellulose according to an embodiment may be pre-treated with a bead mill and pre-treated with ultrasonic waves. Here, it is preferred to perform ultrasonic pretreatment after pretreatment with a bead mill in terms of improving dispersibility by preventing reagglomeration.
Since the nanocellulose includes an ion-bonded metal, it has very high dispersibility in water. In addition, an aqueous dispersion having a very high dispersion of the nanocellulose may be obtained by the bead mill pretreatment and/or the ultrasonic pretreatment. In the aqueous nanocellulose dispersion, the content of the nanocellulose may be about 1 wt % to about 50 wt %.
In the esterification, a titanium-based catalyst and/or a germanium-based catalyst may be used. Specifically, the titanium-based catalyst and/or the germanium-based catalyst may be added to the slurry, and the esterification may be performed.
In addition, the titanium-based catalyst and/or the germanium-based catalyst may be added to the slurry before the first esterification, and the titanium-based catalyst and/or the germanium-based catalyst may be further added to the product of the first esterification.
The catalyst may be added to the first esterification reactant after the first esterification and before the second esterification.
The biodegradable polyester resin may include one or more titanium-based catalysts selected from the group consisting of titanium isopropoxide, antimony trioxide, dibutyltin oxide, tetrapropyl titanate, tetrabutyl titanate, tetraisopropyl titanate, antimonia acetate, calcium acetate and magnesium acetate, or one or more germanium-based catalysts selected from the group consisting of germanium oxide, germanium methoxide, germanium ethoxide, tetramethyl germanium, tetraethyl germanium and germanium sulfide.
In addition, the content of the catalyst may be about 50 ppm to 2000 ppm based on a total weight of a diol, an aromatic dicarboxylic acid, and an aliphatic dicarboxylic acid. For example, about 60 ppm to about 1600 ppm, about 70 ppm to about 1400 ppm, about 80 ppm to about 1200 ppm or about 100 ppm to about 1100 ppm of titanium-based catalyst or germanium-based catalyst may be included. When the content of the catalyst satisfies the range, the physical properties may be further improved.
In addition, the heat stabilizer may be added together with the slurry before the esterification. The heat stabilizer may be fed into the esterification part 200 in the middle of the esterification. The heat stabilizer may be added to the esterification product after the esterification. In addition, the heat stabilizer may be added together with the aliphatic dicarboxylic acid. In addition, the heat stabilizer may be fed into the esterification part 200 after the first esterification and before the second esterification.
The characteristics of the heat stabilizer may be as described above.
The content of the heat stabilizer may be 3,000 ppm or less based on a total weight of a diol, an aromatic dicarboxylic acid, and an aliphatic dicarboxylic acid. Specifically, the content of the heat stabilizer may be, for example, 10 ppm to 3,000 ppm, 20 ppm to 2,000 ppm, 20 ppm to 1,500 ppm or 20 ppm to 1,000 ppm based on a total weight of a diol, an aromatic dicarboxylic acid, and an aliphatic dicarboxylic acid. When the content of the heat stabilizer satisfies the range, the deterioration of the polymer due to high temperature during the reaction process may be controlled, the terminal groups of the polymer may be reduced and the color may be improved.
After completion of the esterification, one or more selected from the group consisting of an additive such as silica, potassium or magnesium and a color-correcting agent such as cobalt acetate may be further added to the esterification product. That is, after completion of the esterification, the additive and/or the color-correcting agent may be added and stabilized, and then a polycondensation reaction may be performed. The additive and/or the color-correcting agent may be added after completion of the esterification, and may be fed into the polycondensation reaction part 300 together with the prepolymer. Accordingly, the additive and/or the color-correcting agent may be uniformly dispersed in the biodegradable polyester resin.
In addition, after completion of the esterification, the inorganic filler may be added to the esterification product. That is, the inorganic filler is added and stabilized after completion of the esterification, and then the polycondensation reaction may be performed. The characteristics of the inorganic filler are as described above. The inorganic filler may be fed into the polycondensation reaction part 300 together with the prepolymer, and the condensation polymerization process may be performed. Accordingly, the inorganic filler may be uniformly dispersed in the biodegradable polyester resin.
In addition, the first recovery part 510 recovers by-products such as water from the esterification part 200. The first recovery part 510 may recover by-products generated from the esterification by applying vacuum pressure to the esterification part 200 or proceeding with reflux.
The method of preparing the biodegradable polyester resin includes a step of polycondensing the prepolymer. The polycondensation reaction may be performed as follows.
The prepolymer is fed into the polycondensation reaction part 300. In addition, at least one of the reinforcing material, the heat stabilizer, the color-correcting agent, the inorganic filler, the metal salt and other additives may be fed into the polycondensation reaction part 300 together with the prepolymer.
Next, the polycondensation reaction may be performed at about 180° C. to about 280° C. and about 10 torrs or less for about 1 hour to about 5 hours. For example, the polycondensation reaction may be performed at about 190° C. to about 270° C., about 210° C. to about 260° C. or about 230° C. to about 255° C. under about 0.9 torrs or less, about 0.7 torrs or less, about 0.2 tons to about 10 torr, about 0.2 torrs to about 0.9 torrs or about 0.2 tons to about 0.6 torrs for about 1.5 hours to about 5 hours, about 2 hours to about 4.5 hours or about 2 hours to about 4 hours.
In addition, the polycondensation reaction may include first polycondensation and second polycondensation.
For example, the first polycondensation may be performed at about 260° C. or less, about 250° C. or less, about 215° C. to about 250° C., about 215° C. to about 245° C. or about 230° C. to about 245° C. under about 1 torr to about 200 torr, about 2 torrs to about 100 torr, about 4 torrs to about 50 torr, about 5 torrs to about 45 torrs or about 8 tons to about 32 torrs for about 0.5 hours to about 3.5 hours, about 0.5 hours to about 3.0 hours or about 0.5 hours to about 2.8 hours.
In addition, the second polycondensation may be performed at about 220° C. to about 265° C., about 230° C. to about 260° C. or about 235° C. to about 255° C. under about 1 torr or less, about 0.8 torrs or less, about 0.6 tons or less, about 0.1 torrs to about 1 torr, about 0.2 torrs to about 0.8 torrs or about 0.2 tons to about 0.6 torrs for about 0.5 hours to about 4 hours, about 1 hour to about 3.5 hours or about 1.5 hours to about 3.5 hours.
In addition, before the polycondensation reaction, a titanium-based catalyst or a germanium-based catalyst may be further added to the prepolymer. In addition, before the polycondensation reaction, one or more selected from the group consisting of an additive such as silica, potassium or magnesium; an amine-based stabilizer such as trimethyl phosphate, triphenyl phosphate, trimethyl phosphine, phosphoric acid, phosphorous acid, or tetraethylenepentamine; and a polymerization catalyst such as antimony trioxide, antimony trioxide or tetrabutyl titanate may be further added to the prepolymer.
The number average molecular weight of the polymer may be about 30000 g/mol or more. For example, the number average molecular weight of the polymer may be about 33000 g/mol or more, about 35000 g/mol or more or about 40000 g/mol to about 90000 g/mol. When the number average molecular weight of the polymer satisfies the range, physical properties, impact resistance, durability and moldability may be further improved.
In addition, the second recovery part 520 recovers by-products such as water from the polycondensation reaction part 300. The second recovery part 520 may apply vacuum pressure to the polycondensation reaction part 300, and may recover by-products generated in the polycondensation reaction.
The second recovery part 520 may apply a vacuum pressure of about 0.1 torrs to about 1 torr to the inside of the polycondensation reaction part 300. The second recovery part 520 may apply a vacuum pressure of about 0.1 torrs to about 0.9 tons to the inside of the polycondensation reaction part 300.
Next, the anti-hydrolysis agent and/or the chain extender are added to the polymer. Next, the polymer, the anti-hydrolysis agent and the chain extender are uniformly mixed and allowed to stand at about 200° C. to about 260° C. for about 1 minute to about 15 minutes. Accordingly, the polymer reacts with the anti-hydrolysis agent and/or the chain extender.
Alternatively, the anti-hydrolysis agent and/or the chain extender may be fed into the polycondensation reaction part 300 through a static mixer and reacted with the polymer. A reaction temperature of the anti-hydrolysis agent and/or the chain extender in the polycondensation reaction part 300 may be about 200° C. to about 260° C. In addition, a reaction time of the anti-hydrolysis agent and/or the chain extender in the polycondensation reaction part 300 may be about 1 minute to about 15 minutes.
The chain extender may have the characteristics described above.
Accordingly, the biodegradable polyester resin composition according to an embodiment may have appropriate hydrolysis and a high biodegradability degree.
Next, a pellet may be produced from the polymer.
Specifically, the pellet may be produced by cooling the polymer to about 15° C. or less, about 10° C. or less or about 6° C. or less, and then cutting the cooled polymer. Alternatively, the polymer may be cut at about 40° C. to about 60° C.
The cutting step may be performed using any pellet cutting machine used in the art without limitation, and the pellet may have various shapes. The pellet cutting method may include an underwater cutting method or a strand cutting method.
The pellet may be subjected to an additional post-treatment process. The pellet may be fed into the post-treatment part 400, and the post-treatment process may be performed.
The post-treatment process may be performed in the post-treatment part 400. The pellet is fed into the post-treatment part 400. Next, the post-treatment part 400 may melt and re-extrude the fed pellet by frictional heat. That is, the post-treatment part 400 may include an extruder such as a twin-screw extruder.
The temperature of the post-treatment process may be about 230° C. to about 270° C. The temperature of the post-treatment process may be about 230° C. to about 260° C. The temperature of the post-treatment process may be about 240° C. to about 265° C. The temperature of the post-treatment process may be about 240° C. to about 260° C.
The post-treatment process time may be about 30 seconds to about 3 minutes. The post-treatment process time may be about 50 seconds to about 2 minutes. The post-treatment process time may be about 1 minute to about 2 minutes.
Next, A resin extruded by the extruder may be cooled, cut, and processed into post-treated pellets. That is, the resin extruded from the extruder may be reprocessed into a pellet through the cutting step described above.
Crystallinity of the pellet may be improved in the post-treatment process. In addition, the content of the residue included in the pellet may be adjusted in the post-treatment process. In particular, the content of an oligomer contained in the pellet may be controlled by the post-treatment process. The amount of residual solvent contained in the pellet may be controlled by the post-treatment process.
Accordingly, the post-treatment process may appropriately control the mechanical properties, biodegradability, UV resistance, optical properties, or hydrolysis resistance of the biodegradable polyester resin.
After the pellet is produced, the biodegradable polyester resin may be compounded with the heterogeneous biodegradable resin. In addition, at least one of the inorganic filler, the light stabilizer, the color-correcting agent and the other additives may be compounded with the biodegradable polyester resin and the heterogeneous biodegradable resin.
The compounding process may be as follows.
The biodegradable polyester resin and the heterogeneous biodegradable resin are mixed with at least one of the inorganic filler, the heat stabilizer, the color-correcting agent, the metal salt or the other additives and fed into an extruder. The mixed biodegradable polyester resin composition is melted and mixed at about 120° C. to about 260° C. in the extruder. Next, the melt-mixed biodegradable polyester resin composition is extruded, cooled, cut, and re-pelletized. By this process, the biodegradable polyester resin composition according to an embodiment may be prepared by combining it with the heterogeneous biodegradable resin.
Alternatively, the inorganic filler, the heat stabilizer, the color-correcting agent, the metal salt and the other additives may be added in the middle of the process of polymerizing the biodegradable polyester resin.
By the biodegradable polyester resin according to an embodiment, a biodegradable polyester film may be prepared.
The thickness of the biodegradable polyester film may be about 5 μm to about 300 μm4. For example, the thickness of the biodegradable polyester film may be about 5 μm to about 180 μm, about 5 μm to about 160 μm, about 10 μm to about 150 μm, about 15 μm to about 130 μm, about 20 μm to about 100 μm, about 25 μm to about 80 μm or about 25 μm to about 60 μm.
The biodegradable polyester film according to an embodiment may have substantially the same hydrolysis degree and biodegradability as the biodegradable polyester resin composition described above.
Meanwhile, the biodegradable polyester film may be prepared using the biodegradable polyester resin or a biodegradable polyester resin pellet.
Specifically, the method of preparing the biodegradable polyester film may include a step of preparing a biodegradable resin composition according to an example and a step of drying and melt extruding the biodegradable resin composition.
In the step of drying and melt extruding the biodegradable resin composition, the drying may be performed at about 60° C. to about 100° C. for about 2 hours to about 12 hours. Specifically, the drying may be performed at about 65° C. to about 95° C., about 70° C. to about 90° C. or about 75° C. to about 85° C. for about 3 hours to about 12 hours or about 4 hours to about 10 hours. When the drying conditions of the pellet satisfy the ranges, the quality of a produced biodegradable polyester film or molded article may be further improved.
In the drying and melt extruding step, the melt extruding may be performed at about 270° C. or less. For example, the melt extruding may be performed at about 265° C. or less, about 260° C. or less, about 255° C. or less, about 150° C. to about 270° C., about 150° C. to about 255° C. or about 150° C. to about 240° C. The melt extruding may be performed by a blown film process. The melt extruding may proceed in a T-die.
In addition, the film preparation process may be a calendering process.
Biodegradable Polyester Molded Article
A biodegradable polyester molded article may be manufactured using the biodegradable polyester resin.
Specifically, the molded article may be manufactured by molding the biodegradable polyester resin composition in a method, such as extrusion or injection, known in the art, and the molded article may be an injection-molded article, an extrusion-molded article, a thin-film molded product, a blow molding or blow-molded article, 3D filament, an interior material for construction, or the like, but is not limited thereto.
For example, the molded article may be in the form of a film or sheet that can be used as an agricultural mulching film, disposable gloves, a disposable film, a disposable bag, a food packaging material, a volume-rate garbage bag, etc., and may be in the form of a fiber that can be used as woven, knitted, non-woven, or a rope. In addition, as shown in
In particular, since the molded article may be formed from the biodegradable polyester resin capable of improving physical properties such as shock absorption energy and hardness, in particular, impact resistance and durability, it may exhibit excellent properties when applied to packaging materials for products stored and transported at low temperatures, interior materials for automobiles requiring durability, garbage bags, mulching films, and disposable products.
The physical properties of the biodegradable film and the biodegradable molded article may be measured in a manner similar to those of the biodegradable polyester resin composition according to an embodiment.
That is, the biodegradable film and the biodegradable molded article may be processed and measured by cutting, bonding, or grinding to a size similar to that of a sample made of the biodegradable polyester resin composition according to an embodiment.
The biodegradable polyester resin composition according to an embodiment may have a molecular weight reduction rate of about 80% or more. The biodegradable polyester resin composition according to an embodiment may have a molecular weight reduction rate of about 85% or more. The biodegradable polyester resin composition according to an embodiment may have a molecular weight reduction rate of about 90% or more. To measure the molecular weight reduction rate, the biodegradable polyester resin composition was mixed with compost, and a biodegradation acceleration test was conducted at 60° C. and a humidity of 90%. In the polyester resin compositions of the examples and the comparative examples, a number average molecular weight after 63 days had elapsed was measured using gel permeation chromatography (GPC). A molecular weight reduction rate was derived by dividing a difference between an initial number average molecular weight and a number average molecular weight after a certain period by the initial number average molecular weight.
The molecular weight reduction rate may be derived by Equation 1 below.
In Equation 1, the biodegradable polyester resin composition according to an embodiment is mixed with compost and subjected to a biodegradation acceleration test at 60° C. and a humidity of 90% for about 63 days. Before performing the biodegradation acceleration test, an initial number average molecular weight of the biodegradable polyester resin composition and a number average molecular weight after 63 days of the biodegradable polyester resin composition subjected to the biodegradation acceleration test for 63 days are measured by gel permeation chromatography (GPC).
The molecular weight reduction rate was derived by dividing a difference between the initial number average molecular weight and the number average molecular weight after a certain period, e.g., 63 days, by the initial number average molecular weight.
In addition, the compost may include about 40 wt % of pig manure, about 15 wt % of chicken manure, about 37 wt % of sawdust, about 5 wt % of zeolite and about 3 wt % of a microbial agent.
In addition, the compost may be Jisaengto (by-product fertilizer grade 1 compost) manufactured by Taeheung F&G.
In addition, when measuring the molecular weight reduction rate, the biodegradable polyester resin composition according to an embodiment is manufactured as a sheet having a thickness of about 300 μm. Next, the manufactured sheet is cut into a size of about 3 cm×3 cm to produce flakes. The flakes are mixed with the compost, and the biodegradation acceleration test is performed.
The biodegradable polyester film according to an embodiment may have a molecular weight reduction rate as described above. Likewise, the biodegradable polyester film according to an embodiment is cut into a size of about 3 cm×3 cm to produce flakes. The flakes may be mixed with the compost, and the biodegradation acceleration test may be performed.
The biodegradable polyester resin composition according to an embodiment may have a biodegradability of about 80% or more. The biodegradable polyester resin composition according to an embodiment may have a biodegradability of about 85% or more. The biodegradable polyester resin composition according to an embodiment may have a biodegradability of about 90% or more. The biodegradability may be derived from Equation 2 below.
The biodegradability of the biodegradable polyester resin composition according to an embodiment may be measured based on the generation amount of carbon dioxide according to KS M3100-1. Specifically, an inoculum container containing only compost manufactured in a compost factory is prepared, and a test container, into which flakes of the biodegradable polyester resin composition of 5% by weight of the dry weight of the compost are fed, is prepared. Next, the compost and the flakes are incubated for 180 days under conditions of 58±2° C., a moisture content of 50% and an oxygen concentration of 6% or more, carbon dioxide generated in each container is collected, and the amount of carbon dioxide generated in each container is measured by titration of an aqueous phenolphthalein solution. As in Equation 2, the biodegradability was derived from a ratio of carbon dioxide generated in the biodegradable polyester resin composition relative to a theoretical carbon dioxide generation amount
When measuring the biodegradability, flakes of the biodegradable polyester resin composition may be manufactured by the substantially the same method as the method of manufacturing the flakes when measuring the molecular weight reduction rate.
The biodegradable polyester film according to an embodiment may be biodegradable as described above. Likewise, the biodegradable polyester film according to an embodiment is cut into a size of about 3 cm×3 cm, and flakes are manufactured. The flakes may be mixed with the compost, and the biodegradation test may be performed.
The hydrolysis degree of the biodegradable polyester resin composition according to an embodiment may be measured by the following method.
To measure the hydrolysis degree, the biodegradable resin composition according to an example is immersed in 80° C. water (100% RH), and a hydrolysis acceleration test is performed. After a certain period, the number average molecular weight of the biodegradable polyester resin composition according to an embodiment was measured using gel permeation chromatography (GPC). A hydrolysis degree was derived by dividing a difference between an initial number average molecular weight and a number average molecular weight after hydrolysis for a certain period by the initial number average molecular weight.
The hydrolysis degree may be calculated by Equation 3 below.
In Equation 3, the biodegradable polyester resin composition according to one embodiment is immersed in 80° C. water, and then subjected to a hydrolysis acceleration test for a certain period. An initial number average molecular weight of the biodegradable polyester resin composition before performing the hydrolysis acceleration test and a number average molecular weight after hydrolysis of the biodegradable polyester resin composition subjected to the hydrolysis acceleration test for a certain period are measured by gel permeation chromatography (GPC).
The hydrolysis degree was derived by dividing a difference between the initial number average molecular weight and the number average molecular weight after hydrolysis for a certain period by an initial number average molecular weight.
In addition, when measuring the hydrolysis degree, the biodegradable polyester resin composition according to one embodiment is manufactured to a sheet having a thickness of about 300 μm. Next, the manufactured sheet is cut into a size of about 3 cm×3 cm to produce flakes. The flakes may be immersed in the hot water, and the hydrolysis acceleration test may be performed.
In the biodegradable polyester resin composition according to one embodiment, a hydrolysis degree after one week may range from about 40% to about 65%. In the biodegradable polyester resin composition according to an embodiment, the hydrolysis degree after one week may range from about 45% to about 63%.
In the biodegradable polyester resin composition according to one embodiment, a hydrolysis degree after two weeks may range from about 80% to about 93%. In the biodegradable polyester resin composition according to another embodiment, the hydrolysis degree after two weeks may range from about 85% to about 92%.
In the biodegradable polyester resin composition according to one embodiment, a hydrolysis degree after three weeks may range from about 90% to about 97%. In the biodegradable polyester resin composition according to another embodiment, a hydrolysis degree after three weeks may range from about 91% to about 96%.
In the biodegradable polyester resin composition according to one embodiment, a hydrolysis degree after four weeks may range from about 92% to about 99%. In the biodegradable polyester resin composition according to another embodiment, a hydrolysis degree after four weeks may range from about 93% to about 97%.
In the biodegradable polyester resin composition according to one embodiment, a hydrolysis degree after six weeks may be about 94% or more. In the biodegradable polyester resin composition according to another embodiment, a hydrolysis degree after six weeks may be about 95% or more.
In the biodegradable polyester resin composition according to one embodiment, a hydrolysis degree after nine weeks may be about 95% or more. In the biodegradable polyester resin composition according to another embodiment, a hydrolysis degree after nine weeks may be about 96% or more.
The biodegradable polyester resin composition according to one embodiment includes a weight swelling rate. The weight swelling rate may be obtained by dividing a difference between a weight after immersing in an organic solvent and an initial weight by the initial weight. When measuring the weight swelling rate, the biodegradable polyester resin composition according to another embodiment may be processed into the above-described biodegradable polyester sheet shape and immersed in the solvent. In addition, when measuring the weight after the immersion, a solvent remaining on the surface of the biodegradable polyester sheet is removed. In addition, when measuring the weight after the immersion, the biodegradable polyester sheet may be immersed in a room-temperature solvent.
The weight swelling rate of the biodegradable polyester resin composition according to one embodiment may be determined according to the molecular structure of the biodegradable polyester resin, additives such as the nanocellulose, the metal salt or the polycarbonate diol, a modifier such as the chain extender or the anti-hydrolysis agent, and/or a polymerization process.
The weight swelling rate may be calculated by Equation 4 below:
[Equation 4]
The biodegradable polyester resin composition according to one embodiment may have a weight swelling rate after being immersed in ethanol for 2 hours.
In the biodegradable polyester resin composition according to an embodiment, the weight swelling rate after being immersed in ethanol for 2 hours may range from about 4% or more. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 2 hours may range from about 4% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 2 hours may range from about 6% to about 18%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 2 hours may range from about 8% to about 18%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 2 hours may range from about 10% to about 18%.
The biodegradable polyester resin composition according to one embodiment may have a weight swelling rate after being immersed in ethanol for 18 hours.
In the biodegradable polyester resin composition according to this embodiment, the weight swelling rate after being immersed in ethanol for 18 hours may range from about 4% or more. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 18 hours may range from about 4% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 18 hours may range from about 6% to about 18%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 18 hours may range from about 8% to about 18%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 18 hours may range from about 10% to about 18%.
The biodegradable polyester resin composition according to one embodiment may have a weight swelling rate after being immersed in ethanol for 24 hours.
In the biodegradable polyester resin composition according to this embodiment, the weight swelling rate after being immersed in ethanol for 24 hours may range from about 4% or more. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 24 hours may range from about 4% to about 21%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 24 hours may range from about 6% to about 19%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 24 hours may range from about 8% to about 19%. In the biodegradable polyester resin composition according to another embodiment, the weight swelling rate after being immersed in ethanol for 24 hours may range from about 10% to about 19%.
In the biodegradable polyester resin composition according to one embodiment, a difference between the weight swelling rate after being immersed in ethanol for 2 hours and the weight swelling rate after being immersed in ethanol for 18 hours may be about 6% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the weight swelling rate after being immersed in ethanol for 2 hours and the weight swelling rate after being immersed in ethanol for 18 hours may be about 5% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the weight swelling rate after being immersed in ethanol for 2 hours and the weight swelling rate after being immersed in ethanol for 18 hours may be about 4% or less.
In addition, in the biodegradable polyester resin composition according to one embodiment, a difference between the weight swelling rate after being immersed in ethanol for 2 hours and the weight swelling rate after being immersed in ethanol for 24 hours may be about 6% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the weight swelling rate after being immersed in ethanol for 2 hours and the weight swelling rate after being immersed in ethanol for 24 hours may be about 5% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the weight swelling rate after being immersed in ethanol for 2 hours and the weight swelling rate after being immersed in ethanol for 24 hours may be about 4% or less.
In addition, the biodegradable polyester resin composition according to one embodiment includes a volume swelling rate. The volume swelling rate may be obtained by dividing a difference between a volume after immersing in an organic solvent and an initial volume by the initial volume. When measuring the volume swelling rate, the biodegradable polyester resin composition according to this embodiment may be processed into the above-described biodegradable polyester sheet shape and immersed in the solvent. In addition, when measuring the volume after the immersion, a solvent remaining on the surface of the biodegradable polyester sheet is removed. In addition, when measuring the volume after the immersion, the biodegradable polyester sheet may be immersed in a room-temperature solvent.
The volume swelling rate may be derived by Equation 5 below:
The biodegradable polyester resin composition according to one embodiment may have a volume swelling rate after being immersed in ethanol for 2 hours.
In the biodegradable polyester resin composition according to this embodiment, the volume swelling rate after being immersed in ethanol for 2 hours may range from about 5% or more. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 2 hours may range from about 5% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 2 hours may be 6% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 2 hours may range from about 8% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 2 hours may range from about 10% to about 20%.
The biodegradable polyester resin composition according to one embodiment may have a volume swelling rate after being immersed in ethanol for 18 hours.
In the biodegradable polyester resin composition according to this embodiment, the volume swelling rate after being immersed in ethanol for 18 hours may range from about 5% or more. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 18 hours may range from about 5% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 18 hours may be 6% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 18 hours may range from about 8% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 18 hours may range from about 10% to about 20%.
The biodegradable polyester resin composition according to one embodiment may have a volume swelling rate after being immersed in ethanol for 24 hours.
In the biodegradable polyester resin composition according to this embodiment, the volume swelling rate after being immersed in ethanol for 24 hours may range from about 5% or more. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 24 hours may range from about 5% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 24 hours may be 6% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 24 hours may range from about 8% to about 20%. In the biodegradable polyester resin composition according to another embodiment, the volume swelling rate after being immersed in ethanol for 24 hours may range from about 10% to about 20%.
In the biodegradable polyester resin composition according to one embodiment, a difference between the volume swelling rate after being immersed in ethanol for 2 hours and the volume swelling rate after being immersed in ethanol for 18 hours may be about 8% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the volume swelling rate after being immersed in ethanol for 2 hours and the volume swelling rate after being immersed in ethanol for 18 hours may be about 6% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the volume swelling rate after being immersed in ethanol for 2 hours and the volume swelling rate after being immersed in ethanol for 18 hours may be about 5% or less.
In addition, in the biodegradable polyester resin composition according to one embodiment, a difference between the volume swelling rate after being immersed in ethanol for 2 hours and the volume swelling rate after being immersed in ethanol for 24 hours may be about 8% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the volume swelling rate after being immersed in ethanol for 2 hours and the volume swelling rate after being immersed in ethanol for 24 hours may be about 6% or less. In the biodegradable polyester resin composition according to another embodiment, a difference between the volume swelling rate after being immersed in ethanol for 2 hours and the volume swelling rate after being immersed in ethanol for 24 hours may be about 5% or less.
The biodegradable polyester resin composition according to one embodiment may have a wet hardness reduction rate. The wet hardness reduction rate is obtained by dividing a difference between an initial hardness before immersion of the biodegradable polyester resin composition and a wet hardness reduction after immersing the biodegradable polyester resin composition in water at a predetermined temperature for a predetermined time by the initial hardness.
The wet hardness reduction rate may be derived by Equation 6 below:
In the biodegradable polyester resin composition according to one embodiment, a wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 16% or less. The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 15% or less. The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 14% or less. The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 13% or less. The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 12% or less. A minimum value of the wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 1%, about 3%, about 5% or about 6%.
The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be measured by a measurement method below. First, the biodegradable polyester resin composition is processed to manufacture a polyester block having a thickness of about 2.5 mm. The initial hardness of the polyester block is measured before immersion, and the wet hardness of the polyester block immediately after immersing in water at about 30° C. for about 24 hours is measured. Next, the wet hardness reduction rate after immersing at 30° C. for about 24 hours may be derived by Equation 4.
The biodegradable polyester resin composition may be dried at bout 80° C. for about 20 minutes to have a moisture content of about 500 ppm, placed in a stainless steel mold, and compressed at about 210° C. under a pressure of about 10 MPa for about 5 minutes, thereby producing a polyester block having a thickness of about 2.5 mm.
Shore D hardness as the initial hardness may range from about 30 to about 45. The Shore D hardness as the initial hardness may range from about 33 to about 43. The Shore D hardness as the initial hardness may range from about 35 to about 41.
The Shore D hardness as a wet hardness after immersing at 30° C. for 24 hours may range from about 28 to about 43. The Shore D hardness as a wet hardness after immersing at 30° C. for 24 hours may range from about 29 to about 41. The Shore D hardness as a wet hardness after immersing at 30° C. for 1 hour may range from about 30 to about 38.
A wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 16% or less. The wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 15% or less. The wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 14% or less. The wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 13% or less. The wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 12% or less. A minimum value of the wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 1%, about 3%, about 5% or about 6%.
The Shore D hardness as a wet hardness after immersing at 30° C. for 0.5 hours may range from about 28 to about 43. The Shore D hardness as a wet hardness after immersing at 30° C. for 0.5 hours may range from about 29 to about 41. The Shore D hardness as a wet hardness after immersing at 30° C. for 0.5 hours may range from about 30 to about 39.
A deviation between the wet hardness reduction rate after immersing at 30° C. for 24 hours and the wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 10% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 30° C. for 0.5 hours is obtained by dividing an absolute value of a difference between the wet hardness after immersing at 30° C. for 24 hours and the wet hardness after immersing at 30° C. for 0.5 hours by the initial hardness. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 7% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 30° C. for 0.5 hours may be about 5% or less.
A wet hardness reduction rate after immersing at 30° C. for 1 hour may be about 16% or less. The wet hardness reduction rate after immersing at 30° C. for 1 hour may be about 15% or less. The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 14% or less. The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 13% or less. The wet hardness reduction rate after immersing at 30° C. for about 24 hours may be about 12% or less. A minimum value of the wet hardness reduction rate after immersing at 30° C. for 1 hour may be about 1%, about 3%, about 5% or about 6%.
A Shore D hardness as a wet hardness after immersing at 30° C. for 1 hour may range from about 28 to about 43. The Shore D hardness as a wet hardness after immersing at 30° C. for 1 hour may range from about 29 to about 41. The Shore D hardness as a wet hardness after immersing at 30° C. for 1 hour may range from about 30 to about 39.
A deviation of the wet hardness reduction rate after immersing at 30° C. for 1 hour between the wet hardness reduction rate after immersing at 30° C. for 24 hours may be about 10% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for 1 hour and the wet hardness reduction rate after immersing at 30° C. for 24 hours may be about 7% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for 1 hour and the wet hardness reduction rate after immersing at 30° C. for 24 hours may be about 5% or less.
A wet hardness reduction rate after immersing at 30° C. for 18 hours may be about 16% or less. The wet hardness reduction rate after immersing at 30° C. for 18 hours may be about 15% or less. The wet hardness reduction rate after immersing at 30° C. for 18 hours may be about 14% or less. The wet hardness reduction rate after immersing at 30° C. for 18 hours may be about 13% or less. The wet hardness reduction rate after immersing at 30° C. for 18 hours may be about 12% or less. A minimum value of the wet hardness reduction rate after immersing at 30° C. for 18 hours may be about 1%, about 3%, about 5% or about 6%.
A Shore D hardness as a wet hardness after immersing at 30° C. for 18 hours may range from about 28 to about 43. The Shore D hardness as a wet hardness after immersing at 30° C. for 18 hours may range from about 29 to about 41. The Shore D hardness as a wet hardness after immersing at 30° C. for 18 hours may range from about 30 to about 39.
A deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 30° C. for 18 hours may range from about 10% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 30° C. for 18 hours may range from about 7% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 30° C. for 18 hours may range from about 5% or less.
A wet hardness reduction rate after immersing at about 50° C. for 24 hours may range from about 16% or less. The wet hardness reduction rate after immersing at 50° C. for 24 hours may range from about 15% or less. The wet hardness reduction rate after immersing at 50° C. for 24 hours may range from about 14% or less. The wet hardness reduction rate after immersing at 50° C. for 24 hours may range from about 13% or less. The wet hardness reduction rate after immersing at 50° C. for 24 hours may range from about 12% or less. A minimum value of the wet hardness reduction rate after immersing at 50° C. for 24 hours may range from about 1%, about 3%, about 5% or about 6%.
A Shore D hardness as a wet hardness after immersing at 50° C. for 24 hours may range from about 28 to about 43. The Shore D hardness as wet hardness after immersing at 50° C. for 24 hours may range from about 29 to about 41. The Shore D hardness as wet hardness after immersing at 50° C. for 24 hours may be about 30 to about 39.
A deviation between the wet hardness reduction rate after immersing at 30° C. for 24 hours and the wet hardness reduction rate after immersing at 50° C. for 24 hours may be about 10% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 50° C. for 24 hours may be about 7% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 50° C. for 24 hours may be about 5% or less.
A wet hardness reduction rate after immersing at 70° C. for 24 hours may be about 16% or less. The wet hardness reduction rate after immersing at 70° C. for 24 hours may be about 15%. The wet hardness reduction rate after immersing at 70° C. for 24 hours may be about 14% or less. The wet hardness reduction rate after immersing at 70° C. for 24 hours may be about 13% or less. The wet hardness reduction rate after immersing at 50° C. for 24 hours may be about 12% or less. A minimum value of the wet hardness reduction rate after immersing at 50° C. for 24 hours may be about 1%, about 3%, about 5% or about 6%.
A Shore D hardness as a wet hardness after immersing at 70° C. for 24 hours may range from about 28 to about 43. The Shore D hardness as a wet hardness after immersing at 70° C. for 24 hours may range from about 29 to about 41. The Shore D hardness as a wet hardness after immersing at 70° C. for 1 hour may range from about 30 to about 39.
A deviation between the wet hardness reduction rate after immersing at 30° C. for 24 hours and the wet hardness reduction rate after immersing at 70° C. for 24 hours may be about 10% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 70° C. for 24 hours may be about 7% or less. The deviation between the wet hardness reduction rate after immersing at 30° C. for about 24 hours and the wet hardness reduction rate after immersing at 70° C. for 24 hours may be about 5% or less.
In addition, the acid value of the biodegradable polyester resin composition according to an embodiment may range from about 0.01 mg KOH/g to about 3 mg KOH/g. The acid value of the biodegradable polyester resin composition according to onen embodiment may range from about 0.1 mg KOH/g to about 2.5 mg KOH/g. The acid value of the biodegradable polyester resin composition according to another embodiment may range from about 0.1 mg KOH/g to about 2.3 mg KOH/g.
Since the biodegradable polyester resin composition according to one embodiment has an acid value within the specified range above, it may have hydrolysis and biodegradability characteristics as described above.
In addition, the biodegradable polyester resin composition according to one embodiment may include a silicon element. The silicon element may be derived from the anti-hydrolysis agent and the like. The content of the silicon element may range from about 0.1 ppm to about 1000 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the silicon element may range from about 0.5 ppm to about 500 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the silicon element may range from about 1 ppm to about 100 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the silicon element may range from about 1 ppm to about 50 ppm based on the biodegradable polyester resin composition according to another embodiment.
In addition, the biodegradable polyester resin composition according to one embodiment may include a metal element. The metal element may be derived from the metal salt. The content of the metal element may range from about 0.1 ppm to about 200 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the metal element may range from about 0.5 ppm to about 150 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the metal element may range from about 1 ppm to about 100 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the metal element may range from about 1 ppm to about 50 ppm based on the biodegradable polyester resin composition according to another embodiment.
In addition, the biodegradable polyester resin composition according to one embodiment may include an iron element. The iron element may be derived from the metal salt. The content of the iron element may range from about 0.1 ppm to about 200 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the iron element may range from about 0.5 ppm to about 150 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the iron element may range from about 1 ppm to about 100 ppm based on the biodegradable polyester resin composition according to another embodiment. The content of the iron element may range from about 1 ppm to about 50 ppm based on the biodegradable polyester resin composition according to another embodiment.
In addition, a ratio (the ppm content of the iron element/the ppm content of the silicon element) of the content of the silicon element to the content of the iron element may range from about 0.1 to about 0.8. The ratio (the ppm content of the iron element/the ppm content of the silicon element) of the content of the silicon element to the content of the iron element may range from about 0.1 to about 0.7. The ratio (the ppm content of the iron element/the ppm content of the silicon element) of the content of the silicon element to the content of the iron element may range from about 0.3 to about 0.7. The ratio (the ppm content of the iron element/the ppm content of the silicon element) of the content of the silicon element to the content of the iron element may range from about 0.35 to about 0.65.
Since the biodegradable polyester resin composition according to one embodiment includes a silicon element and an iron element within the specified ranges above, it may have appropriate solvent resistance, appropriate hydrolysis and appropriate biodegradability. In particular, a hydrolysis degree may be appropriately controlled depending upon the content of the silicon element, and the biodegradability may be appropriately controlled depending upon the content of the iron element.
The contents of the silicon element and the metal may be measured by inductively coupled plasma optical emission spectroscopy.
In the biodegradable polyester resin composition according to one embodiment, a first weight swelling rate may range from 4% to 20%. The biodegradable polyester resin composition according to another embodiment may have a swelling rate suitable for an organic solvent such as ethanol. That is, the biodegradable polyester resin composition according to an embodiment may have solubility suitable for the organic solvent.
Accordingly, a molded article such as a film made of the biodegradable polyester resin composition according to one embodiment may be printed with an ink containing the organic solvent. That is, the ink may appropriately permeate into the surface of a molded article including the biodegradable polyester resin composition according to an embodiment due to the organic solvent. Accordingly, the biodegradable polyester resin composition according to another embodiment may have improved printability.
In addition, in the biodegradable polyester resin composition according to one embodiment, a wet hardness reduction rate is 15% or less. Accordingly, the biodegradable polyester resin composition according to another embodiment may have a relatively high moisture resistance. The biodegradable polyester resin composition according to another embodiment may maintain high mechanical properties even when exposed to water or in a high-humidity environment.
The biodegradable polyester resin composition according to one embodiment may have appropriate hydrophobicity. Accordingly, the biodegradable polyester resin composition according to an embodiment may have a relatively high moisture resistance. The biodegradable polyester resin composition according to one embodiment may maintain high mechanical properties even when exposed to water or in a high-humidity environment.
Accordingly, the biodegradable polyester resin composition according to one embodiment may have a small change in mechanical properties when used for packaging high-moisture foods or the like.
In addition, the biodegradable polyester resin composition according to one embodiment may have a hydrophobic property. Accordingly, the biodegradable polyester resin composition according to this embodiment may absorb less moisture in the air. Accordingly, the biodegradable polyester resin composition according to this embodiment may have improved storage stability.
The biodegradable polyester resin composition according to one embodiment may include a silicone-based hydrolysis agent. Accordingly, the biodegradable polyester resin composition according to this embodiment may have improved hydrolysis resistance. In addition, the silicone-based hydrolysis agent may function as a coupling agent for coupling a polymer resin included in the polycondensed composition.
Accordingly, the silicone-based hydrolysis agent may improve the polymerization degree of the biodegradable polyester resin composition according to an embodiment.
Accordingly, the biodegradable polyester resin composition according to an embodiment may be biodegraded after use while having improved physical properties during actual use.
The biodegradable polyester resin composition according to one embodiment may be applied to a film for packaging and the like. That is, a film made of the biodegradable polyester resin composition according to one embodiment may be used for general purposes such as packaging. Here, the biodegradable polyester resin composition according to another embodiment may have a low hydrolysis degree in an initial use period, the biodegradable polyester film may maintain mechanical and chemical properties to a certain extent or more within a period of normal use.
At the same time, since the biodegradable polyester resin composition according to one embodiment has a high biodegradability degree, a film made of the biodegradable polyester resin composition according to one embodiment may be degraded when discarded after use.
The above contents are described in more detail through the following examples. However, the following examples are only for illustrating the present disclosure, and the scope of the present disclosure is not limited thereto.
Preparation of Pretreated Cellulose Nanocrystals (CNC)
Dry powder-type cellulose nanocrystals (NVC-100, Manufacturer: Celluforce) having a particle size of about 1 μm to about 50 μm were dispersed in water to have a weight percent of 1% in water, and then sonicated at an output of 20000 J/s for 1 minute using a tip-type ultrasonic disperser, thereby producing pretreated nanocellulose.
Anti-hydrolysis agent #1: 2-(3,4-epoxycyclohexyl) ethyltrimethoxysilane, ShinEtsu KBM-303)
Anti-hydrolysis agent #2: 3-glycidyloxypropyltriethoxy silane(γ-glycidyloxypropyltriethoxysilane)
Metal salt: iron (II) acetate
polycarbonate diol #1 (Nippon Polyurethane Industry, N-965, weight average molecular weight: about 1000)
Polycarbonatediol #2 (RAVECARB 106, Caffaro Industrie)
Preparation of Biodegradable Polyester Resin
First Operation: Pretreating to Obtain Slurry
As shown in Table 1, pretreated nanocellulose, iron nitrate, 1,4-butanediol (1,4-BDO) and terephthalic acid (TPA) were mixed in a molar ratio (1,4-BDO:TPA) of 1.4:1 and fed into a slurry tank (the bottom of the slurry tank was an anchor type, the height to an agitator was 40 mm, and three rotary blades were provided) in a non-catalytic state. Here, D50 of the terephthalic acid (TPA) was 130 μm.
Here, the contents of the nanocellulose and the iron (II) acetate were as in the following Table 1 based on the total weight of the added terephthalic acid, 1,4-butanediol and adipic acid.
Next, the mixture was pretreated by stirring at 60° C. and 100 rpm for 1 hour, and a slurry was obtained by phase separation.
Second Operation: Obtaining Prepolymer
The slurry obtained in the first step was fed into a reactor through a supply line, and tetrabutyl titanate (Dupont, Tyzor® TnBT product) as a titanium-based catalyst was fed at 250 ppm thereinto, followed by performing first esterification at 220° C. under normal pressure for about 2 hours until 95% of by-product water was discharged.
To the reaction product, 53 mol % of 1,4-butanediol (1,4-BDO) based on the total number of moles of diol components, 53 mol % of adipic acid (AA) based on the total number of moles of dicarboxylic acid, and tetrabutyl titanate (Dupont, Tyzor® TnBT product) as a titanium-based catalyst were added in an amount of 200 ppm based on the total weight of a diol, an aromatic dicarboxylic acid and an aliphatic dicarboxylic acid, and then second esterification was performed at 210° C. under normal pressure for about 2 hours 30 minutes until 95% of by-products was discharged, thereby preparing a prepolymer having a number average molecular weight of 1200 g/mol. The content of the polycarbonate diol was as in the following Table 1 based on 100 parts by weight of the total amount of the added terephthalic acid, 1,4-butanediol and adipic acid.
Third Operation: Polycondensing
400 ppm of tetrabutyl titanate (Dupont, Tyzor® TnBT product) as a titanium-based catalyst and 200 ppm of a triethylene phosphate stabilizer, based on the total weight of the prepolymer, were added to the prepolymer and stabilized for about 10 minutes. Next, the temperature of the reaction mixture was elevated to 250° C., and then a polycondensation reaction was carried out at 0.5 tons for 4 hours, thereby preparing a polymer having a number average molecular weight of 55000 g/mol.
Next, about 0.1 parts by weight of an anti-hydrolysis agent, based on 100 parts by weight of the polymer, was added to the polymer. Next, the polymer was subjected to a coupling reaction at about 250° C. for about 10 minutes. Next, the polymer was cooled to 5° C., and then cut with a pellet cutter, thereby obtaining a biodegradable polyester resin pellet.
As shown in Table 1 below, adipic acid, terephthalic acid, cellulose nanocrystals and an anti-hydrolysis agent were used in different contents. Except for the contents and the process, other processes were carried out in the substantially same manner as in Example 1.
As shown in Table 2 below, adipic acid, terephthalic acid, cellulose nanocrystals and an anti-hydrolysis agent were used in different contents. Other processes, except for the contents and the processes, were substantially the same as those of Example 1.
Manufacture of Biodegradable Polyester Sheet
After preparing two Teflon® sheets, a stainless steel (SUS) mold having a size of 12 cm×12 cm was placed on one Teflon® sheet, and about 7 g of the prepared polyester resin pellet was put into the stainless steel (SUS) mold having a size of 12 cm×12 cm. Next, the mold was covered with another Teflon® sheet, and placed in the center of a hot press (manufacturer: Widlab, model name: WL 1600SA) having a surface size of about 25 cm×25 cm. The mold was maintained at about 210° C. under a pressure of about 10 MPa for about 3 minutes, and then detached, followed by immediately cooling in water of 20° C. for about 30 seconds. Next, a biodegradable polyester sheet having an area of about 10 cm×10 cm and a thickness of about 300 μm was manufactured.
Manufacture of Biodegradable Polyester Film
After drying the biodegradable polyester resin pellet at 80° C. for 5 hours, melt extrusion was carried out at 160° C. using Blown Film Extrusion Line (Manufacturer: YOOJIN ENGINEERING), thereby manufacturing a biodegradable polyester film having a thickness of 50 μm.
<Average Particle Diameter (D50) and Standard Deviation of Aromatic Dicarboxylic Acid>
With regard to a particle size distribution (PSD), the average particle diameter (D50) and standard deviation (SD) of an aromatic dicarboxylic acid (TPA or DMT) were obtained using a particle size analyzer Microtrac S3500 (Microtrac Inc) according to the following conditions:
Use environment
The standard deviation means the square root of the variance and may be calculated using software.
<Particle Diameter of Nanocellulose>
The particle size and average particle deviation of nanocellulose were measured using the principle of dynamic light scattering (DLS) at 25° C. and a measurement angle of 175° using Zetasizer Nano ZS (Manufacturer: Marven). Here, a peak value derived through the polydispersity index (PdI) in a confidence interval of 0.5 was measured as a particle diameter.
The biodegradable polyester resins prepared in the examples and the comparative examples were immersed in 80° C. water (100% relative humidity RH), and then an accelerated hydrolysis test was carried out.
Specifically, 5 g of each of the polyester resins of the examples and the comparative examples was added to 500 mL of deionized water (DI Water), and then blocked with a stopper to prevent water from evaporating and subjected to an accelerated hydrolysis test in an 80° C. convection (hot air) oven. The humidity environment of the biodegradable polyester sheet is the same as that at 100% RH because it is created by immersion in water.
The number average molecular weights of the polyester resins of the examples and the comparative examples after a certain period were measured using gel permeation chromatography (GPC). A hydrolysis degree was derived by dividing a difference between the initial number average molecular weight and the number average molecular weight after a certain period by the initial number average molecular weight.
GPC equipment and measurement conditions were as follows:
Each of the biodegradable polyester resins prepared in the examples and the comparative examples was mixed with the following compost, and was subjected to a biodegradation acceleration test at 60° C. and a relative humidity of 90%.
The number average molecular weight of each of the polyester resins of the examples and the comparative examples was measured using the gel permeation chromatography (GPC) after a certain period. Biodegradability was derived by dividing the difference between the initial number average molecular weight and the number average molecular weight after a certain period by the initial number average molecular weight.
Each of the polyester sheets whose initial weight and initial thickness has been measured was immersed in room-temperature ethanol and, respectively after 2 hours, 18 hours and 24 hours, was taken out of the solvent. Next, the weight and thickness of the polyester sheet from which the solvent on the surface was removed were measured. Referring to the weight and thickness changes, the weight swelling rate and the volume swelling rate were measured.
On the surface of each of the biodegradable polyester sheets manufactured in the examples and the comparative examples, the water contact angle and the polarity were measured under the following conditions.
Each of the biodegradable polyester pellets prepared in the examples and the comparative examples was dissolved in about 65 wt % nitric acid solution, and iron and silicon contents were measured by inductively coupled plasma—optical emission spectrometry (ICP OES).
The hydrolysis degrees were measured as shown in Tables 3 and 4 below.
The molecular weight reduction rates and biodegradability were derived as shown in Tables 5 and 6 below.
The contents of an iron element and a silicon element were measured as shown in Tables 7 and 8 below.
As shown in Tables 9 and 10, the weight swelling rate and volume swelling rate for each immersion time in ethanol were measured.
An initial hardness and the wet hardness for each temperature and each immersion time were measured as shown in Tables 11 to 13 below.
As shown in Tables 14 and 15 below, the surface properties of the biodegradable polyester sheets manufactured in the examples and the comparative examples were measured.
As shown in Tables 3 to 15, the biodegradable resin compositions according to the examples may have appropriate hydrolysis and biodegradability.
In addition, as shown in Tables 3 to 15, the biodegradable resin compositions according to the examples have appropriate surface properties while having an appropriate weight swelling rate and volume swelling rate.
Further, as shown in Tables 3 to 15, it can be confirmed that the biodegradable resin compositions according to the examples have an appropriate wet hardness change rate and appropriate surface properties.
In a biodegradable polyester resin composition according to one embodiment, a first weight swelling rate ranges from 4% to 20%. The biodegradable polyester resin composition according to another embodiment can have a swelling rate suitable for an organic solvent such as ethanol. That is, the biodegradable polyester resin composition according to another embodiment can have solubility suitable for the organic solvent.
Accordingly, a molded article such as a film made of the biodegradable polyester resin composition according to one embodiment can be printed with an ink containing the organic solvent. That is, the ink can permeate into the surface of a molded article including the biodegradable polyester resin composition according to one embodiment due to the organic solvent. Accordingly, the biodegradable polyester resin composition according to this embodiment can have improved printability.
In addition, in the biodegradable polyester resin composition according to one embodiment, a wet hardness reduction rate is 15% or less. Accordingly, the biodegradable polyester resin composition according to another embodiment can have high moisture resistance. The biodegradable polyester resin composition according to another embodiment can maintain high mechanical properties even when exposed to water or in a high-humidity environment.
The biodegradable polyester resin composition according to one embodiment can have appropriate hydrophobicity. Accordingly, the biodegradable polyester resin composition according to another embodiment can have high moisture resistance. The biodegradable polyester resin composition according to another embodiment can maintain high mechanical properties even when exposed to water or in a high-humidity environment.
Accordingly, the biodegradable polyester resin composition according to one embodiment can have a small change in mechanical properties when used for packaging high-moisture foods or the like.
In addition, the biodegradable polyester resin composition according to one embodiment can have a hydrophobic property. Accordingly, the biodegradable polyester resin composition according to this embodiment can absorb less moisture in the air. Accordingly, the biodegradable polyester resin composition according to this embodiment can have improved storage stability.
The biodegradable polyester resin composition according to one embodiment can include a silicone-based hydrolysis agent. Accordingly, the biodegradable polyester resin composition according to this embodiment can have improved hydrolysis resistance. In addition, the silicone-based hydrolysis agent can function as a coupling agent for coupling a polymer resin included in the polycondensed composition.
Accordingly, the silicone-based hydrolysis agent can improve the polymerization degree of the biodegradable polyester resin composition according to one embodiment.
Accordingly, the biodegradable polyester resin composition according to this embodiment can be biodegraded after use while having improved physical properties during actual use.
The biodegradable polyester resin composition according to one embodiment can be efficiently applied to a film for packaging and the like. That is, a film made of the biodegradable polyester resin composition according to this embodiment can be used for general purposes such as packaging. Here, the biodegradable polyester resin composition according to one embodiment can have a low hydrolysis degree in an initial use period, and the biodegradable polyester film can maintain mechanical and chemical properties to a certain extent or more within a period of normal use.
At the same time, since the biodegradable polyester resin composition according to one embodiment has a high biodegradability degree, a film made of the biodegradable polyester resin composition according to this embodiment can be degraded when discarded after use. Although the preferred embodiments of the present disclosure have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope of the disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2022-0062449 | May 2022 | KR | national |
| 10-2022-0062450 | May 2022 | KR | national |