Patent Grant
7495044
This invention relates to improvements in biodegradable polymeric products particularly starch based polymers.
There is an increasing demand for many plastic products used in packaging to be biodegradable. Trays in biscuit and chocolate packages are one example. Starch films have been proposed as biodegradable alternatives for some time. U.S. Pat. No. 3,949,145 proposed a starch/polyvinyl alcohol/glycerol composition for use as a biodegradable agricultural mulch sheet.
Difficulties have been encountered in producing starch based polymers particularly by hot melt extrusion. The molecular structure of the starch is adversely affected by the shear stresses and temperature conditions needed to plasticise the starch and pass it through the extrusion die. For most products foaming has to be avoided and this generally requires attention because of the water content of the starch. Foaming has been avoided by degassing the melt prior to exiting the die as suggested in U.S. Pat. Nos. 5,314,754 and 5,316,578. The latter patent also avoids adding water to the starch. As explained in U.S. Pat. No. 5,569,692 by not drying starch and avoiding the addition of water the starch can be processed at temperatures between 120° C. and 170° C. because the water bound to the starch does not generate a vapour pressure such as to require high pressures. Another approach to improving the melt processability of starch is to provide an additive as in U.S. Pat. No. 5,362,777 which reduces the melting point of the starch. The additive is selected from dimethyl sulfoxide, a selection of polyols and amino or amide compounds.
In order to produce starch polymers for particular applications they have been blended with a range of other polymers. Biodegradable blown films are disclosed in U.S. Pat. No. 5,322,866 which blends raw starch, polyvinyl alcohol and talc with glycerol and water. U.S. Pat. No. 5,449,708 discloses compositions of starch ethylene acrylic acid and a salt of stearic acid plus a glycerol based lubricant. Flexible and clear transparent sheets are disclosed in U.S. Pat. No. 5,374,304. These are composed of a high amylose starch and a glycerol plasticizer. The use of starch in conjunction with high amylose or modified starches has also been proposed. U.S. Pat. Nos. 5,314,754, and 5,316,578 both suggest the use of modified starches including hydroxypropyl substituted starches. Hydroxypropylation reportedly increases elongation at break and burst strength and improved resilience in the polymers. Although the efficacy of these special and modified starches is recognised, their cost inhibits the commercial acceptability of the products made from them.
It is an object of this invention to provide a biodegradable polymer which can be processed and thermoformed into sheet and shaped products without difficulty and have acceptable properties for its intended uses.
To this end the present invention provides a process for forming biodegradable polymers which includes the steps of
a) forming a mixture of starch, a modified starch, a water soluble polymer or copolymer containing vinyl alcohol units, up to 20% of added water or a polyol plasticizer and 0.4 to 1.5% by weight of a C2-22 fatty acid or salt,
b) working the mixture and forming a melt within the temperature range of 130° C. to 160° C.
c) reducing the temperature and further working the mixture and the extruding the mixture or injecting the mixture into a mould at a temperature of 85° C. to 105° C. without the need to remove water.
The process as defined allows starch based mixtures to be extruded without foaming. The need to vent the extruder to remove water prior to the mix exiting the extrusion die is not needed. Both rigid sheet and flexible starch based films can be made using this process. The foaming temperature of the mix is raised above the temperature at which the melt is most easily plasticised and extruded.
In another aspect, the present invention provides a biodegradable polymer having the composition
a) from 8 to 80% by weight of a starch modified to include an hydroxyalkyl C2-6 group or modified by reaction with an anhydride of a dicarboxylic acid
b) from 0 to 87.9% of starch
c) from 4 to 11% by weight of a water soluble polymer selected from polyvinylacetate, polyvinyl alcohol and copolymers of ethylene and vinylalcohol which have a melting point compatible with the molten state of the starch components
d) from 0 to 20% by weight of a polyol plasticiser
e) from 0.1 to 1.5% by weight of a C12-22 fatty acid or salt and
f) from 0 to 12% by weight of added water.
The compositions defined include formulations suitable for forming films or thermoforming rigid products such as packaging trays. The defined compositions are easier to process as they can be extruded in film or sheet form without foaming. The extruded sheet can be thermoformed into shaped trays or containers for use as biodegradable packaging. Usually the need to vent the extruder to remove water prior to the mix exiting the extrusion die is not needed with these formulations.
The upper limit to the content of the modified starch is determined by its cost. This component contributes structural benefits to the resulting material. A preferred component is hydroxypropylated amylose. Other substituents can be hydroxyethyl or hydroxybutyl to form hydroxyether substitutions, or anhydrides such as maleic phthalic or octenyl succinic anhydride can be used to produce ester derivatives. The degree of substitution [the average number of hydroxyl groups in a unit that are substituted] is preferably 0.05 to 2. The preferred starch is a high amylose maize starch. A preferred component is a hydroxypropylated high amylose starch A939 marketed by Goodman Fielder. A preferred concentration range to meet cost parameters for biscuit trays is 12 to 24%.
The other starch component is any commercially available starch. This may be derived from wheat, maize, potato, rice, oat, arrowroot, and pea sources.
Generally the water content is about 10 to 15%. A preferred concentration range for starch is 50 to 70.6%
The polymer component c) of the composition is preferably compatible with starch, water soluble, biodegradable and has a low melting point compatible with the processing temperatures for starch. Polyvinyl alcohol is the preferred polymer but polymers of ethylene-vinyl alcohol, ethylene vinyl acetate or blends with polyvinyl alcohol may be used. A preferred concentration range for sheet material is 7 to 9%.
The preferred plasticiser is glycerol although ethylene glycol and diethylene glycol are also suitable as is sorbitol. Cost and food contact are important issues in choosing the appropriate plasticizer. For low humidity environments such as biscuit packages it has been found that lower plasticizer content improves the toughness and long term resilience of the material. This is partly due to the properties of the starch ether component and the fact that at low humidity plasticizers such as glycerol tend to remove water from the starch polymer and make it more brittle. It is possible to process the formulation with no plasticizer and the rigid polymer formed is flexible and has good impact resistance at low humidity. When the plasticiser content is low additional water is added to improve processing. Thus the plasticizer content is preferably 0 to 12% and the water content is 12 to 0%. For film processing the plasticizer content is preferably higher than for rigid sheet products. Higher concentrations of plasticiser improve flexibility and for flexible packaging films or mulch films the preferred plasticiser content is 10 to 16%. The fatty acid or fatty acid salt component is preferably present in concentrations of 0.6 to 1%. Stearic acid is the preferred component. Sodium and potassium salts of stearic acid can also be used. Again cost can be a factor in the choice of this component but lauric, myristic, palmitic, linoleic and behenic acids are all suitable. It is found that the acid tends to accumulate near to the surface of the composition as it is extruded.
Processing conditions depend on the formulations and the desired properties of the product to be produced. The materials need to be heated above 140° C. in the extruder to fully gelatinise the starches. The die temperature needs to be controlled below 110° C. to avoid foaming.
The preferred method of carrying out this invention involves mixing the starch, modified starch, vinylalcohol polymer lubricant and fatty acid components into a free flowing powder. The premixing can be carried out in any conventional mixer. The powder is then introduced into a screw extruder and subjected to an elevated temperature by the shearing action of the screw and the application of external heat to the barrel. The temperature is raised to a maximum in the range of 130° C. to 160° C. Any liquid components including additional water are introduced during this initial phase. The melt that is formed is then propelled toward the die and in moving forward the temperature is reduced to a value in the range of 85° C. to 105° C.
A typical extrusion for rigid products has the following parameters:
Temperature profile ° C.: 60, 70, 90, 110, 130, 145, 130, 120, 110
Screw Speed 120 rpm
Die Pressure 1400 psi
Flexible film can be formed by simply extruding from a sheet forming die and then increasing the speed of the take-off roller to achieve the reduced thickness needed for flexible film. Cooling of the film between the die and the roller is usually needed to ensure that the film does not adhere to the roller. De-humidified air to cool the film also assists in removing excess moisture from the film surface. If the film is formed by the blown tube method dehumidified air is used to blow the film as it exits the die. Talc may also be entrained in the air stream to reduce blocking of the film.
Biscuit trays were made by extruding a sheet and subsequently thermo forming the tray in a hot press. A twin screw extruder was used with a screw speed of 130 rpm. The barrel temperature profile was 95 [die], 95 [adapter], 95, 95, 95, 95, 100, 130, 140, 150, 140, 110, 90, 60. The process avoided foaming at the die and did not require venting of the barrel to remove moisture.
The formulations and the initial observations of the trays' performance are given in the table 1.
More detailed tests were carried out on sheets made from examples 9 to 14 and these results are shown in tables 2, 3 & 4.
From the above tests and examples and based on cost considerations a suitable formulation for this biscuit tray application is:
The trays are biodegradable and have strength and flexibility properties comparable to the non biodegradable materials currently used. The costs of production are also comparable.
The effect of stearic acid content on the composition was tested using a formulation of:
The mixture was processed at a feed rate of 1.5 a screw speed of 100 rpm and the temperature profile was 70, 90, 100, 130, 140, 140, 130, 115, 110, 110, 110 [die]
The results show that torque is decreased with increase in stearic acid content. Output mass speaks at a stearic acid content of 1.2 g. the preferred range of stearic to 1.5%.
The following four formulations have also been found suitable for use in forming packaging trays for foodstuffs such as chocolates and biscuits.
The following four formulations have also been found suitable for use in forming packaging trays for foodstuffs such as chocolates and biscuits.
Formulations as shown in table 5 were prepared for the purpose of assessing their performance under low and high humidity conditions and to assess the performance of the plasticiser under these conditions.
Table 6 shows the strength characteristics at 65% RH and table 7 shows the characteristics at 15% RH for these formulations.
Tables 6 and 7 show that under high or medium relative humidity Glycerol improves toughness as measured by elongation. Under low relative humidity the glycerol absorbs water from the starch in the polymer and this decreases toughness.
Two formulations were prepared on being formula B of example 27 and the outer being the same except that 50% of the A939 was replaced by wheat starch. Both formulas were processed extruded as sheet and then thermoformed into biscuit trays. The trays were used in a product trial where biscuits were placed in the tray packaged and then stored for three months. The performance and appearance of the trays were acceptable and as good as conventional non-biodegradable trays. The significant advantage of the trays made by both formulations were that disposal was much simpler. Conventional trays are difficult for consumers to compress and their volume cannot be significantly reduced but by simply running these trays under a tap they can be compressed by hand into a small disposable pellet.
From the above description and examples it can be seen that the present invention provides a biodegradable starch polymer that is comparable in price and performance characteristics to conventional non-biodegradable polymers. Consequently packaging of products such as biscuits and chocolates using a rigid thermoformed tray can be just as presentable and attractive with the added benefit of being environmentally friendly. Similarly packaging of products such as bread, in flexible packaging films, can also be attractive and biodegradable.
| Number | Date | Country | Kind |
|---|---|---|---|
| PP7696 | Dec 1998 | AU | national |
| PP7697 | Dec 1998 | AU | national |
| PP7702 | Dec 1998 | AU | national |
| PQ1847 | Jul 1999 | AU | national |
This application is a Continuation of co-pending application Ser. No. 10/805,224, filed on Mar. 22, 2004; which is a Continuation of application Ser. No. 09/857,611, filed on Jun. 8, 2001, which in turn claims priority to PCT application, PCT/AU99/01101, filed Dec. 13, 1999, which claims the benefit of the following Australian applications: PP 7696, PP 7697, PP 7702, filed Dec. 14, 1998, and PQ 1847, filed Jul. 27, 1999. The entire contents of these applications are hereby incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3033853 | Klug | May 1962 | A |
| 3949145 | Otey et al. | Apr 1976 | A |
| 4125495 | Griffin | Nov 1978 | A |
| 4863655 | Lacourse et al. | Sep 1989 | A |
| 5314754 | Knight | May 1994 | A |
| 5316578 | Buehler et al. | May 1994 | A |
| 5322866 | Mayer et al. | Jun 1994 | A |
| 5362777 | Tomka et al. | Nov 1994 | A |
| 5374304 | Frische et al. | Dec 1994 | A |
| 5393804 | George et al. | Feb 1995 | A |
| 5436078 | Buhler et al. | Jul 1995 | A |
| 5444107 | Ajioka et al. | Aug 1995 | A |
| 5449708 | Schiltz | Sep 1995 | A |
| 5462983 | Bloembergen et al. | Oct 1995 | A |
| 5552461 | Redd et al. | Sep 1996 | A |
| 5569692 | Bastioli et al. | Oct 1996 | A |
| 5691403 | Shitaohzono et al. | Nov 1997 | A |
| 5760118 | Sinclair et al. | Jun 1998 | A |
| 5821286 | Xu et al. | Oct 1998 | A |
| 5852114 | Loomis et al. | Dec 1998 | A |
| 5869647 | Narayan et al. | Feb 1999 | A |
| 5874486 | Bastioli et al. | Feb 1999 | A |
| 6200404 | Andersen et al. | Mar 2001 | B1 |
| 6235815 | Loercks et al. | May 2001 | B1 |
| 6284838 | Silbiger | Sep 2001 | B1 |
| 6369215 | Peltonen et al. | Apr 2002 | B1 |
| 6387991 | Hayes | May 2002 | B1 |
| Number | Date | Country |
|---|---|---|
| 8-245836 | Sep 1996 | JP |
| 8-325447 | Dec 1996 | JP |
| 10-087846 | Apr 1998 | JP |
| 10-173341 | Jun 1998 | JP |
| WO 9216583 | Oct 1992 | WO |
| WO 9403543 | Feb 1994 | WO |
| WO-98-31523 | Jul 1998 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070148383 A1 | Jun 2007 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10805224 | Mar 2004 | US |
| Child | 11680899 | US | |
| Parent | 09857611 | US | |
| Child | 10805224 | US |