Patent Application
20200268267
The present disclosure relates to a bioelectrode and a method for producing a bioelectrode, and specifically relates to a bioelectrode for detecting biosignals such as brainwaves and a method for producing the bioelectrode.
Bioelectrodes have been conventionally used for detecting biosignals. Bioelectrodes are used while being placed in contact with a subject's body. Bioelectrodes are used, for example, in order to detect brainwave signals for analysis of a brain function state with a purpose of early detecting Alzheimer's disease and the like. A bioelectrode for detecting brainwaves is used while its electrode member is directly placed in contact with the scalp of a subject in order to detect brainwave signals. Conventional bioelectrodes include those in the form of a plate-like thin sheet made of a highly conductive metal such as silver or gold. These thin sheet bioelectrodes have insufficient adhesion with skin. In order to lower contact impedance between the electrode and skin, it has been necessary to apply a gel, cream, paste, or the like between the skin and the bioelectrode. These substances applied have to be removed after detection of biosignals, and use thereof has required an effort. Additionally, an electric double layer is formed by ionization of the metal on the interface between the skin and the electrode to thereby generate a polarization voltage. The variation in this polarization voltage causes a baseline variation. In order to stabilize the polarization voltage, there has been required aging for forming a silver chloride film on an electrode surface for a silver electrode.
In contrast, as bioelectrodes requiring no application of a gel or the like, there are bioelectrodes including a metal probe (e.g., see Japanese Patent Application Publication No. 2013-248306) and bioelectrodes formed by impregnating a water-absorbent member such as a sponge with an electrolyte solution in which an amino acid or organic salt dissolved (e.g., see Japanese Patent Application Publication No. 2013-144051).
Metal probes, which are rigid, may cause pain to a subject when allowed to adhere to the scalp. In the case where a plurality of metal probes is provided, a measure is required to make adhesion of all the probes to the scalp satisfactory. For this reason, as in Japanese Patent Application Publication No. 2013-248306, it is necessary to provide the metal probes with a buffering member such as a spring, and thus, the structure of the probes is complicated.
Alternatively, in the case of a bioelectrode in which an electrolyte solution is used to a water-absorbent member as in Japanese Patent Application Publication No. 2013-144051, its performance is degraded due to drying, wetness leads to discomfort, and so on. Furthermore, it is difficult to form the tip end portion of such an electrode such that to the tip end have a pointed shape, and it is not possible to achieve satisfactory elasticity because the electrode is excessively soft. For this reason, it is necessary to reinforce the electrode with another member in order to allow the electrode to adhere to a living body.
As mentioned above, a configuration in which the structure is not complicated, satisfactory elasticity is provided so as not to cause discomfort to a subject, and contact impedance can be reduced has been required from conventional bioelectrodes.
The present disclosure is related to providing a bioelectrode having a structure not complicated, having a satisfactory elasticity, and capable of reducing contact impedance, and a method for producing a bioelectrode.
In accordance with one aspect of the present disclosure, there is provided a bioelectrode comprises a support member, which is a conductive member, and at least one electrode member, which is a member projecting from the support member. At least the electrode member is molded from a conductive rubber containing a silicone rubber and metal particles. The electrode member has an exposed face, which is a face formed by removal of a molded surface layer at the tip end portion of the electrode member.
In the bioelectrode according to one aspect of the present disclosure, the exposed face is formed inclinedly with respect to a support face that supports the electrode member in the support member, and the tip end portion is pointed.
In the bioelectrode according to one aspect of the present disclosure, the inclination of each exposed face is the same with respect to the support face.
In the bioelectrode according to one aspect of the present disclosure, the exposed face is a cut face.
In the bioelectrode according to one aspect of the present disclosure, the exposed face is a polished face.
In the bioelectrode according to one aspect of the present disclosure, the exposed face is a flat face.
In the bioelectrode according to one aspect of the present disclosure, the silicone rubber is a room temperature-curable liquid silicone rubber.
In the bioelectrode according to one aspect of the present disclosure, the metal particles are silver particles.
In accordance with one aspect of the present disclosure, there is provided a method for producing a bioelectrode including a support member, which is a conductive member, and at least one electrode member, which is a member projecting from the support member. The method comprises an electrode member molding step of molding the electrode member by stirring a conductive rubber containing a silicone rubber and metal particles and molding the conductive rubber into a shape projecting from the support member, and an exposed face forming step of forming an exposed face, which is a face at which an interior of a molded surface layer is exposed, by removing the molded surface layer, which is a portion of the surface, at a tip end portion of the electrode member molded by the electrode member molding step.
In the method for producing a bioelectrode according to one aspect of the present disclosure, in the exposed face forming step, the exposed face is formed to be inclined with respect to a support face that supports the electrode member in the support member, and the tip end portion is formed in a manner such that the tip end portion is pointed.
According to the bioelectrode and the method for producing a bioelectrode according to the present disclosure, the structure is not complicated, satisfactory elasticity is provided, and the contact impedance can be reduced.
Hereinafter, embodiments of the present disclosure will be described with reference to the drawings.
The support member 2 supports the electrode member 3 and is formed of a conductive material so as to be electrically connected to the electrode member 3. In the bioelectrode 1 according to the present embodiment, the support member 2 and the electrode member 3 are integrally molded, and the support member 2 is also formed of the same conductive rubber as that for the electrode member 3. The shape of the support member 2 may be, as mentioned below, any shape capable of supporting the electrode member 3 in a state where the electrode member 3 is projecting, and is not limited to a specific shape. The support member 2 has a disk shape or substantially disk shape, as shown in
The support member 2 is provided with a terminal 21, which is to be electrically connected to a measurement apparatus, not shown, for receiving biosignals detected by the bioelectrode 1 and processing, analyzing, displaying or the like the biosignals received. The terminal 21 is, for example, as shown in
A plurality of the electrode members 3 is provided in the bioelectrode 1 as shown in
The tip end 31 of each of the electrode members 3 has the exposed face 32, which is a face formed by removal of a molded surface layer, as shown in
The conductive rubber forming the electrode members 3 is a rubber containing a silicone rubber and metal particles, as mentioned above. The silicone rubber is, for example, a room temperature-curable liquid silicone rubber, and the metal particles are, for example, silver particles. The metal particles may be any metal particles as long as being a metal-based material having electrical conductivity. The metal particles may be, for example, particles made of a carbon-based material such as carbon black or carbon nanotubes.
A room temperature-curable liquid silicone rubber is a silicone rubber which is in the form of liquid or paste before curing and turns into a rubber elastic body usually at 20° C. to 100° C. due to progress of a curing reaction. The curing reactions include a reaction that gradually progresses by moisture (water) in air and a reaction that readily progresses by addition of a curing agent to a main material. The silicone rubber may be one to be cured by either type of the curing reactions. As the room temperature-curable liquid silicone rubber, only one type of room temperature-curable liquid silicone rubber may be used, or a plurality types of room temperature-curable liquid silicone rubbers may be mixed and used.
As silver particles in the conductive rubber, silver particles in the form of particles containing an aggregated silver powder and a flaky silver powder can be used. The aggregated silver powder is a silver powder of a plurality of particulate primary particles three-dimensionally aggregated, and the flaky silver powder a silver powder having a scale-like shape. The average particle size of the aggregated silver powder and the flaky silver powder is not limited to a specific value. For example, as the aggregated silver powder, those having an average particle size in the range of 4 μm to 8 μm are preferable, and as the flaky silver powder, those having an average particle size in the range of 5 μm to 15 μm are preferable. The total amount of the aggregated silver powder and the flaky silver powder to be compounded can be appropriately set in the range where the electrical conductivity can be imparted, and is, for example, preferably in the range of 50 parts by weight to 500 parts by weight, particularly preferably in the range of 100 parts by weight to 300 parts by weight, based on 100 parts by weight of the liquid silicone rubber. As for the ratio between the content of the aggregated silver powder and the content of flaky silver powder, it is preferable to make the content of the aggregated silver powder and the content of the flaky silver powder equivalent.
Note that the conductive rubber forming the electrode members 3 may further contain other components in addition to the components mentioned above in a range where the effects of the present disclosure are not compromised. As other components, compounding agents commonly used in the rubber industry, for example, a reinforcing agent, a filler such as dry silica, an anti-aging agent, a processing aid, and a plasticizer can be appropriately compounded.
As mentioned above, the electrode members 3, which are members formed by curing the silicone rubber, have flexibility and resilience, have satisfactory adhesion on the body of a subject, have a soft skin feel, are unlikely to cause discomfort even when allowed to adhere for a long period, and thus can maintain a stable contact with the subject's body.
The electrode members 3 are molded by curing the silicone rubber as a binder including metal particles compounded. On the surface of the intermediate product 40 of each electrode member 3 molded, the molded surface layer 42, which is a layer containing a small amount of metal particles, is formed (see
In contrast, as shown in
Next, a method for producing the bioelectrode 1 having the configuration mentioned above will be described. The method for producing the bioelectrode 1 includes an electrode member molding step and an exposed face forming step. The electrode member molding step is a step of molding the electrode members 3 by stirring a conductive rubber containing a silicone rubber and metal particles and molding this conductive rubber into a shape projecting from the support member 2, and the exposed face forming step is a step of forming the exposed face 32, which is a face at which the interior of the molded surface layer 42 is exposed, by removing the molded surface layer 42, which is a portion of the surface, at the tip end 31 of each electrode member 3 as the intermediate product 40 molded by the electrode member molding step. Hereinafter, the method for producing the bioelectrode 1 will be specifically described.
The bioelectrode 1, as mentioned above, is integrally molded from the same conductive rubber. In a mold, the conductive rubber is cured, and the support member 2 and electrode members 3 are integrally molded. In other words, the support member 2 and electrode members 3 are integrally molded in the electrode member molding step. However, in an as-molded state in the electrode member molding step, no exposed face 32 is formed in each electrode member 3, and each electrode member 3 is molded in the form of the intermediate product 40 having a tip end part 41 extending beyond the tip end 31 (see
Next, in the exposed face forming step, the tip end part 41 of the electrode member 3 of the intermediate product 40 is removed, the tip end 31 is formed in the electrode member 3, and the exposed face 32 is formed on the tip end 31 (see
As mentioned above, in the bioelectrode 1, the electrode members 3 are formed of a conductive rubber, therefore the bioelectrode 1 has satisfactory elasticity so as not to cause discomfort to a subject, and additionally can uniformly adhere to a target site of a subject. For this reason, a reinforcing member, such as a core material for imparting elasticity to the electrode members 3, is not required. It is also possible to form the electrode members 3 only from a conductive rubber, therefore the structure of the electrode members 3 is not complicated, and thus the production can be facilitated. The electrode members 3 have the exposed faces 32 formed by removal of the molded surface layers 42, therefore the bioelectrode 1 does not require use of a conductive gel, electrolyte solution, or the like, are easily used, and additionally cause no discomfort to a subject. It is also possible to reduce the contact impedance by means of the exposed face 32.
As mentioned above, the bioelectrode 1 according to the first embodiment of the present disclosure has a structure not complicated, has satisfactory elasticity, and can reduce the contact impedance.
Next, an evaluation test for the contact impedance of the bioelectrode 1 according to the first embodiment of the present disclosure will be described. The present inventors produced the above-described bioelectrodes 1 according to the first embodiment of the present disclosure (Examples 1 and 2) and conducted a contact impedance evaluation test on the bioelectrodes 1. The present inventors also produced a bioelectrode as a comparative example (Comparative Example 1) and conducted the same contact impedance evaluation test on Comparative Example 1. Comparative Example 1 is a bioelectrode including electrode members as intermediate products 40 as shown in
The contact impedance evaluation test was conducted by measuring the contact impedance of each of Examples 1 and 2 and Comparative Example 1 by using an LCR meter as shown in
As for Examples 1 and 2 and Comparative Example 1, a conductive rubber of components compounded shown in the following Table 1 was centrifuged. The centrifuged rubber was injected into a mold and cross-linked under cross-linking conditions as shown in Table 2. The cross-linked rubber was subjected to a salt water treatment in an autoclave under salt water treatment conditions shown in Table 3 to thereby produce each of the intermediate products 40 of Examples 1 and 2 and the bioelectrodes of Comparative Example 1. Then, for the intermediate products 40 of Examples 1 and 2, the molded surface layer 42 of the tip end part 41 in each electrode member 3 as the intermediate product 40 was removed by the method of removal treatment on molded surface layer shown in the following Table 4 to form the tip end 31 having the exposed face 32 in each electrode member 3, and thus, bioelectrodes of Examples 1 and 2 were each produced. Removal of the molded surface layer 42 in each electrode member 3 as the intermediate product 40 of each of Examples 1 and 2 was conducted by removing the tip end part 41 in a width of approximately 1 mm by each of the method of removal treatment on molded surface layer.
The test results of the present contact impedance evaluation test are shown in
Hereinafter, a second embodiment of the present disclosure will be described with reference to the drawings.
The tip end portion 71 of the electrode member 7 contacts a body of a subject, and the bioelectrode 5 makes biosignals of the subject detectable via the electrode member 7. The bioelectrode 5 is, for example, a bioelectrode for detecting brainwaves, which contacts a head of a subject to detect brainwaves. The bioelectrode 5 is not limited to these for detecting brainwaves, and is applicable to other devices for detecting biosignals such as wearable information devices. Hereinafter, the configuration of the bioelectrode 5 will be specifically described.
The support member 6 supports the electrode member 7 and is formed of a conductive material so as to be electrically connected to the electrode member 7. In the bioelectrode 5 according to the present embodiment, the support member 6 and the electrode member 7 are integrally molded, and the support member 6 is also formed of the same conductive rubber as that for electrode member 7. The shape of the support member 6 is, as mentioned below, required to be a shape capable of supporting the electrode member 7 in a state where the electrode member 7 is projecting, and is not to be limited to a specific shape. The support member 6 has a disk shape or substantially disk shape, as shown in
The support member 6 is provided with a terminal 61, which is to be electrically connected to a measurement apparatus, not shown, for receiving biosignals detected by the bioelectrode 5 and processing, analyzing, displaying or the like the biosignals received. The terminal 61 is, for example, as shown in
In the support member 6, the terminal 61 is integrally formed with other portions by the same conductive rubber, but the terminal may be one formed as a separate body from the other portions by a different material. In such a case, the terminal 61 can be formed of a material suitable for electrical connection to the connecting cable L. For example, the terminal 61 may be produced from a metal, and may be adhesively provided on the terminal side face 63 of the support member 6 by using a conductive adhesive or may be provided by being embedded more internally than the terminal side face 63 such that a portion of the terminal 61 projects from the terminal side face 63.
A plurality of the electrode members 7 is provided in the bioelectrode 5 as shown in
With such a pointed shape, the bioelectrode 5 can reduce contact impedance between a scalp of a subject and the electrode members 7 because the tip end of the pointed tip end portion 71 of each electrode members 7 pushes hair of the subject aside to easily approach the scalp. Also, the electrode members 7 are molded from a flexible conductive rubber. Thus, even when the tip end of the tip end portion 71 is made to have a pointed shape and to contact the scalp, it is possible to cause no pain and make discomfort unlikely to occur.
Additionally, the tip end portion 71 of each electrode member 7 has an exposed face 72, which is a face formed by removal of a molded surface layer, and the exposed face 72 is formed to be inclined with respect to the support face 62 that supports the electrode members 7 in the support member 6. The exposed face 72 is a face diagonally facing with respect to a direction in which the electrode members 7 extend, is a flat face or substantially flat face, and a face diagonally intersecting with the direction in which the electrode members 7 extend.
Each exposed face 72 is elliptical or substantially elliptical, and the exposed faces 72 have the same or the substantially same shape as each other. The exposed faces 72 of the electrode members 7, which are provided in a manner such that the electrode members 7 are concentrically or substantially concentrically arranged at equiangular or substantially equiangular intervals with respect to the center or substantial center of the support member 6, have the same or substantially same inclination with respect to the support face 62 as each other, and are formed along the circumferential direction while facing the same or substantially same direction as each other. Note that the inclination of each exposed face 72 is not particularly limited as long as the tip end of each tip end portion 71 can push hair of a subject aside to thereby allow each tip end portion 71 to approach a scalp.
The exposed face 72 may be a curved face or may be a face having a curved face and a flat face. The exposed face 72 is, as mentioned below, a face formed by removing a molded surface layer 82 of a tip end part 81 from an intermediate product 80 of each electrode member 7 molded from a conductive rubber (see
The conductive rubber forming the electrode members 7 is a rubber containing a silicone rubber and metal particles, as mentioned above. The silicone rubber is, for example, a room temperature-curable liquid silicone rubber, and the metal particles are, for example, silver particles. The metal particles may be any metal particles as long as being a metal-based material having electrical conductivity. The metal particles may be, for example, particles made of a carbon-based material such as carbon black or carbon nanotubes.
As silver particles in the conductive rubber, silver particles in the form of particles containing an aggregated silver powder and a flaky silver powder can be used. The average particle size of the aggregated silver powder and the flaky silver powder is not limited to a specific value. For example, as the aggregated silver powder, those having an average particle size in the range of 4 μm to 8 μm are preferable, and as the flaky silver powder, those having an average particle size in the range of 5 μm to 15 μm are preferable. The total amount of the aggregated silver powder and the flaky silver powder to be compounded can be appropriately set in the range where the electrical conductivity can be imparted, and is, for example, preferably in the range of 50 parts by weight to 500 parts by weight, particularly preferably in the range of 100 parts by weight to 300 parts by weight, based on 100 parts by weight of the liquid silicone rubber. As for the ratio between the content of the aggregated silver powder and the content of flaky silver powder, it is preferable to make the content of the aggregated silver powder and the content of the flaky silver powder equivalent.
Note that the conductive rubber forming the electrode members 7 may further contain other components in addition to the components mentioned above in a range where the effects of the present disclosure are not compromised. As other components, compounding agents commonly used in the rubber industry, for example, a reinforcing agent, a filler such as dry silica, an anti-aging agent, a processing aid, and a plasticizer can be appropriately compounded.
As mentioned above, the electrode members 7, which are members formed by curing the silicone rubber, have flexibility and resilience, have satisfactory adhesion on the body of a subject, have a soft skin feel, are unlikely to cause discomfort even when allowed to adhere for a long period, and thus can maintain a stable contact with the subject's body.
In contrast, as shown in
Next, a method for producing a bioelectrode 5 having the configuration mentioned above will be described. The method for producing the bioelectrode 5 includes an electrode member molding step and an exposed face forming step. The electrode member molding step is a step of molding the electrode members 7 by stirring a conductive rubber containing a silicone rubber and metal particles and molding this conductive rubber into a shape projecting from the support member 6, and the exposed face forming step is a step of forming the exposed face 72, which is a face at which the interior of the molded surface layer 82 is exposed, by removing the molded surface layer 82, which is a portion of the surface, at the tip end portion 71 of each electrode member 7 as the intermediate product 80 molded by the electrode member molding step. In the exposed face forming step, the exposed face 72 is formed inclinedly with respect to the support face 62 that supports the electrode members 7 in the support member 6, and the tip end portion 71 is formed pointed. Hereinafter, the method for producing the bioelectrode 5 will be specifically described.
The bioelectrode 5, as mentioned above, is integrally molded from the same conductive rubber. In a mold, the conductive rubber is cured, and the support member 6 and electrode members 7 are integrally molded. In other words, the support member 6 and electrode members 7 are integrally molded in the electrode member molding step. However, in an as-molded state in the electrode member molding step, no exposed face 72 is formed in each electrode member 7, and each electrode member 7 is molded in the form of the intermediate product 80 having a tip end part 81 extending beyond the exposed face 72 (see
Next, in the exposed face forming step, the tip end part 81 of the electrode member 7 of the intermediate product 80 is diagonally removed at an incline with respect to the support face 62, and the exposed face 72 is formed in the tip end portion 71 (see
Removal of the molded surface layer 82 at the tip end part 81 of the intermediate product 80 can be conducted by various methods and is conducted by cutting and polishing, for example. An example of cutting is cutting with a cutting tool such as a cutter, and an example of polishing is surface polishing. In each electrode member 7 of the bioelectrode 5 completed, the tip end portion 71 has the exposed face 72, and the exposed face 72 exposes a portion of the conductive rubber inside the molded surface layer 82 which has been removed. At the exposed face 72, more metal particles are exposed than those at the molded surface layer 82. For this reason, it is possible to enlarge the effective contact area, which is the contact area between a subject to be contacted and metal particles at the tip end portion 71 of each electrode member 7, and the tip end portion 71 of each electrode member 7 can reduce the contact impedance.
The exposed face 72 is preferably one that exposes a large amount of metal particles. In the exposed face forming step, a method of removing the molded surface layer 82 such that metal particles are not removed from the exposed face 72 is preferred to a method of removing the molded surface layer 82 such that metal particles are removed from the exposed face 72. For this reason, as the method of removing the molded surface layer 82 in the exposed face forming step, cutting with a sharp edge tool is preferable.
As mentioned above, in the bioelectrode 5, the electrode members 7 are formed of a conductive rubber, therefore the bioelectrode 5 has satisfactory elasticity so as not to cause discomfort to a subject, and additionally can uniformly adhere to a target site of a subject. For this reason, a reinforcing member, such as a core material for imparting elasticity to the electrode members 7, is not required. It is also possible to form the electrode members 7 only from a conductive rubber therefore the structure of the electrode members 7 is not complicated, and thus the production can be facilitated.
The electrode members 7 have the exposed faces 72 formed by removal of the molded surface layer 82, therefore the bioelectrode 5 does not require use of a conductive gel, electrolyte solution, or the like, are easily used, and additionally cause no discomfort to a subject. It is also possible to reduce the contact impedance by means of the exposed face 72. Additionally, the tip end part of the tip end portion 71 of each electrode member 7 is pointed. Thus, it is possible to reduce the contact impedance between a scalp and the electrode members 7 because the tip end of the pointed tip end portion 71 of each electrode member 7 pushes hair of a subject aside to easily approach the scalp. Also, the electrode members 7 are molded from a flexible conductive rubber. Thus, even when the tip end of the tip end portion 71 is made to have a pointed shape and to contact a scalp, it is possible to cause no pain and make discomfort unlikely to occur.
As mentioned above, the bioelectrode 5 according to the second embodiment of the present disclosure has a structure not complicated, has satisfactory elasticity, and can reduce the contact impedance.
Next, an evaluation test for the contact impedance of the bioelectrode 5 according to the second embodiment of the present disclosure will be described. The present inventors produced the above-described bioelectrode 5 according to the second embodiment of the present disclosure (Example 3), and conducted a contact impedance evaluation test on the bioelectrode 5. The present inventors also produced a bioelectrode as a Comparative Example (Comparative Example 2) and conducted the same contact impedance evaluation test on Comparative Example 2.
Comparative Example 2 is a bioelectrode including electrode members as intermediate products 80 as shown in
The contact impedance evaluation test was conducted by measuring the contact impedance of each of Example 3 and Comparative Example 2 by using an LCR meter as shown in
As measurement value of the contact impedance, value at one minute after the contact of each of Example 3 and Comparative Example 2 with the scalp was employed. Note that the following LCR meter was used as the LCR meter and the following electroencephalographic paste was used as the electroencephalographic paste to be used for the reference electrode.
As for Example 3 and Comparative Example 2, a conductive rubber of components compounded shown in the following Table 5 was centrifuged. The centrifuged rubber was injected into a mold and cross-linked under cross-linking conditions as shown in Table 6. The cross-linked rubber was subjected to a salt water treatment in an autoclave under salt water treatment conditions shown in Table 7 to thereby produce each of the intermediate products 80 of Example 3 and Comparative Example 2.
Then, for the intermediate product 80 of Example 3, the molded surface layer 82 of the tip end part 81 in each electrode member 7 as the intermediate product 80 is removed diagonally with respect to the support face 62 by the method of removal treatment on molded surface layer shown in the following Table 8 to form the tip end portion 71 having the exposed face 72 in each electrode member 7, and thus the bioelectrode of Example 3 was produced.
The test results of the present contact impedance evaluation test are shown in
Accordingly, it can be seen that Example 3, in which the exposed face 72, at which the molded surface layer of the tip end part of each electrode member is removed, contacts the scalp of the subject, can reduce the contact impedance more than Comparative Example 2, in which the molded surface layer of the tip end part of each electrode member contacts the scalp of the subject.
Although the embodiments of the present disclosure has been described hereinabove, the present disclosure is not limited to the embodiments of the present disclosure described above and includes any aspects included in the concept and claims of the present disclosure. The configurations each may be appropriately and selectively combined to solve or provide at least part of the above-described problems or effects. For example, the shape, material, arrangement, size, and the like of each component in the embodiments described above may be appropriately changed in accordance with specific use aspects of the present disclosure.
For example, the shape of the support member 2, 6 is not limited to the shape mentioned above and may be a different shape. Similarly, the shape of the electrode member 3, 7 is not limited to the shape mentioned above and may be a different shape.
The support member 2, 6 and the electrode member 3, 7 may be separate bodies from each other. The electrode member 3, 7, after formed by the electrode member molding step and the exposed face forming step mentioned above, may be attached and fixed to the support member 2, 6 formed as separate bodies to thereby form the bioelectrode 1, 5. Fixing of the electrode member 3, 7 to the support member 2, 6 may be achieved with a conductive adhesive or may be achieved with engagement such as fitting. For example, a recessed part or protruding part is formed at the bottom of the electrode member 3, 7, and the corresponding protruding part or recessed part is formed in the support member 2, 6. The recessed part and the protruding part are engaged with each other to thereby enable the electrode member 3, 7 to be fixed to the support member 2, 6. The electrode member 3, 7 may be detachably fixed to the support member 2, 6.
When the support member 2, 6 and the electrode member 3, 7 are separate bodies, both the support member 2, and the electrode member 3, 7 may be formed with the same material using the conductive rubber mentioned above or may be formed with different materials. When the support member 2, 6 is formed with a material different from that of the electrode member 3, 7, the support member 2, 6 can be formed with a material having electrical conductivity different from the conductive rubber. As the material having electrical conductivity for the support member 2, 6, a material having electrical conductivity suitable for supporting the electrode member 3, 7 is preferable. For example, it is possible to use a metal, such as stainless, copper, or aluminum, having a strength enough to stably support the electrode member 3, 7. The material of the support member 2, 6 is not limited thereto, and materials having electrical conductivity can be used.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-195921 | Oct 2018 | JP | national |
| 2018-195922 | Oct 2018 | JP | national |
The present application is a continuation application of International Patent Application No. PCT/JP2019/040640 filed on Oct. 16, 2019, which claims the benefit of Japanese Patent Application No. 2018-195921, filed on Oct. 17, 2018, and Japanese Patent Application No. 2018-195922, filed on Oct. 17, 2018. The contents of these applications are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2019/040640 | Oct 2019 | US |
| Child | 16871353 | US |