The present invention belongs to the field of the chemicals industry and more specifically to the field of the treatment of biomass by hydrothermal carbonisation.
The process of hydrothermal carbonisation (HTC) has been known since Friedrich Bergius described it in 1913; however, industrial plants have only been developed in recent years. Ingelia S.L. is one of the first companies that has developed an industrial process of continuous hydrothermal carbonisation such as are described in the Spanish patents, ES2339320 and ES2339321 and has operated a plant since August 2010. The objective of the process is to enhance biomass with a high moisture content, such as for example garden prunings, leftovers from forestry and agricultural developments, orange peels, olive stones and other leftover fruits and vegetables, etc., by means of applying pressure and temperature in aqueous conditions, obtaining a product in water called biocarbon.
Initially, the manufacture of compressed and dried carbon pellets was developed for application thereof in thermal and/or thermoelectric stations from the aqueous mixture of biocarbon obtained in the HTC process. However, this application required thermal drying of the biocarbon in order to obtain moisture levels lower than 10%, in addition to having the logistical drawbacks of solid fuels, such as the charge and discharge as well as the potential for spontaneous combustion in oxidising atmosphere.
In this regard, the object of the invention is to define a new process of post-treatment for HTC carbon, with the object of reducing the production and transport costs as well as maximizing its use in the form of Biocoal Water Fuel (hereinafter BWF).
In the literature, there exist studies relating to fuel based on a mixture of mineral and water carbon (known as coal water fuel, CWF). Thus for example, Wibberley et al. (Efficient use of Coal Water Fuels”, Technology Assessment Report 74, CSIRO Energy Technology, 2008) described the use of CWF for generating energy, concentrating on the possibilities to reduce the efficiency losses in the different steps of the process.
Other studies referring to CWF have been described by Wilson, R. et al. (“Coal-fuelled diesels for modular power generation”, presented in the Joint Power Generation conference, Kansas City, Mo., 17-21 Oct. 1993, U.S. Pat. No. 4,465,495 (“Process for Making Coal Water Fuel Slurries and Product thereof”), U.S. Pat. No. 3,941,552 (“Burning Water-in-oil Emulsion containing Pulverized Coal”) or U.S. Pat. No. 4,335,684 (“Micronized Coal Water Fuel Slurry for Reciprocating Internal Combustion Engines”).
Although different research studies have been carried out regarding this type of fuel over many decades (even at the beginning of the 20th century), bringing CWF onto the market failed mainly due to the low cost of petrol during the second half of the 20th century and the need to use dispersants owing to the opposing nature of carbon, which is apolar, and water, which is polar. However, given the increase in the cost of petrol in recent years, it has been considered necessary to search for efficient economic alternatives to this type of fuel. Furthermore, biocarbon has a considerable oxygen content, which provides this material with greater polar properties and a certain affinity to water. The present invention thus aims to provide a new biofuel obtained from the product of the HTC process.
As a closer prior art to the present invention, patent ES2339320 must be mentioned, the content of which is incorporated into the present application as reference. In this patent, the hydrothermal carbonisation process is described from an aqueous mixture of biomass, which is carried out over a period of between 2 to 12 hours at a temperature of between 180 and 225° C. and at a pressure of between 10 and 25 bar. As a result of the process, an aqueous mixture of carbonised biomass is obtained with porous particles of different sizes, which is collected from the lower part of the inverted flow vertical reactor in which the hydrothermal carbonisation process takes place. The water content may in particular vary between 80 and 90%.
Although it is possible to achieve the separation of water up to a content of approximately 50% using mechanical means and standard economic processes, in order to reduce the moisture content below 50%, thermal process with elevated cost and/or self-consumption of fuel are required.
With the object of solving this difficulty, the present invention is based on the use of an “energy carrier” which allows a high level of moisture, which is an advantage for the HTC process. This is what happens in the case of the so-called coal water fuel (CWF). Said fuel consists of a mixture of 45 to 75% wt. % of mineral carbon milled into fine particles (less than 500 microns) and of 25% to 55% of water with at least one chemical dispersant, preferably selected from polystyrene, polyolefins and polymethacrylate, said chemical dispersants being used in very small quantities, preferably less than 3 wt. % and more preferably less than 1 wt. %. The big disadvantage of CWF is the nature of the mineral carbon used for its manufacture. Its properties require the addition of a dispersion agent which is a product made by the chemical industry with a certain significant value in the calculation of the price of fuel.
The object of this invention is thus a biofuel (BWF) which is characterised by taking advantage of the characteristics of the carbonised biomass obtained in the HTC process as a mixture with water, with optimised properties with respect to CWF, when having a polarity different to the surfaces. This new biofuel (BWF) is characterised by having the values which are shown in Table 1, where the values indicated with (daf) refer to dry base and without ashes:
A process for obtaining the BWF biofuel previously described is also an object of the invention. This process consists of a post-treatment of the aqueous mixture of carbonised biomass obtained from the HTC process and it is characterised in that it comprises:
In Table 2 the characteristics of the aqueous mixture of carbonised biomass obtained from the HTC process are shown, from which the biofuel BWF, which is the object of the invention, is obtained.
In a particular embodiment of the invention, the process may comprise a pre-treatment prior to the aqueous mixture of the carbonised biomass obtained in the HTC process. This pre-treatment may comprise:
Additionally in one particular embodiment, in which a BWF with a high level of purity is required, the process may comprise an additional step of chemical cleaning for dissolving and removing inorganic elements. This step may preferably be carried out following the step of separating the inorganic substances and prior to the dehydration step. In one preferred embodiment, the chemical cleaning may be carried out by means of the addition of at least one base (preferably selected from among alkaline hydroxides or alkaline earth hydroxides) and/or the addition of at least one acid (for example, mineral acids such as sulphuric acid, hydrochloric acid, phosphoric acid, etc.) to reduce the mineral and halogen content fixed in the biocoal with the aim of reducing the percentage of ash and/or inorganic components.
The ash content in the final product may be adjusted to the requirements of the use of the fuel. An ash content of less than 8 wt. % can usually be guaranteed using relatively simple methods and for specific uses, such as for example in combustion engines, levels can even be less than 2 wt. %.
In a preferred embodiment of the invention, the process may comprise a final step of mixing and metering in at least one chemical dispersant, preferably selected from among polystyrene, polyolefins and polymethacrylate. This addition is preferably carried out following the dehydration step. The percentage of dispersants added to the mixture is preferably less than 3 wt. % and more preferably less than 1 wt. %.
In addition to the chemical dispersant, water may be added until reaching the degree of dilution desired in the final product (BWF).
Lastly, in an additional particular embodiment of the invention, the process may comprise adding, preferably after a dehydration step, an additional percentage (between 5 and 50% of the final mass, preferably between 10 and 20% of the final mass) of water or adding at least one liquid fuel such as for example, ethanol, with the aim of improving the pumping characteristics of the mixture and/or the combustion. In this way, the biofuel obtained from the process described may achieve up to 90 wt. % of water.
It is an additional object of the invention to use the biofuel in an application preferably selected from among:
Among the main advantages of BWF, which is the object of the invention, the following may be pointed out:
A specific and preferred embodiment of the present invention is detailed below in an illustrative and non-limiting manner.
As shown in
The cake obtained is then subjected to a fine grinding process (7) by colloidal milling until a mean particles size of less than 20 microns is obtained. Subsequently, the mixture obtained is subjected to a step of separating the inorganic substances (8) by flotation. With the aim of dissolving and removing the inorganic elements not separated in the previous step, the mixture is subjected to a subsequent step of chemical cleaning (9) with at least one base (preferably alkaline hydroxides or alkaline earth hydroxides) and/or the addition of at least one acid (for example, a mineral acid such as sulphuric acid, hydrochloric acid, phosphoric acid, etc.) to dissolve and remove inorganic elements.
Following the chemical cleaning, the process comprises a step of dehydration (10) until the water content is reduced to a percentage less than 50 wt. %. The characteristics of the final product are those shown in the following table:
Different samples of BWF were prepared from coal coming from the HTC process in the Ingelia prototype reactor, as described in ES2339320. The coal was milled and the water content was adjusted to 55 wt. % for its use in the pumping tests.
abased on dry coal without ashes;
The samples A-C prepared and characterised in example 1 were subjected to a pumping test. To this end, the mixture was introduced into a tube with a diameter of less than 2.8 cm and extruded through a hole of 2.1 mm. A positive result was reported when 90% or more of the mixture was able to be extruded. It was also visually observed whether a separation of the coal and the water took place after or during the extrusion.
a65 wt. % water content.
In all cases, the water carbon mixture could be extruded without the addition of dispersant agents due to the hydrophilic surface. The mixtures behave like Bingham fluids and are stables as such. In order to study the pumping behaviour of the mixture with different concentrations, on one occasion an additional 10% (wt. of the final mass) of water was added and in another case an additional 10% (wt. of the final mass) of ethanol was added. The result obtained was an improvement in the fluidity of the mixture, without producing separation of the coal-liquid mixture. In the case of adding liquid organic compounds, such as for example ethanol, the pumping characteristics are improved at ambient temperatures below 0° C., thus reducing the freezing point of the mixture.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201231451 | Sep 2012 | ES | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/ES2013/070645 | 9/17/2013 | WO | 00 |