Bipolar articles and related methods

Abstract
The invention provides bipolar articles (e.g., batteries and capacitors) with new architectures and methods of making and using the same. Articles are provided with interpenetrating anode and cathode structures that allow for improved power density, and arbitrary form factors that allow for formation in substantially any desired shape. The articles are useful for embedding or integral formation in various electronic devices to provide more efficient use of space in the devices. The articles optionally include self-organizing bipolar structures.
Description
BACKGROUND OF THE INVENTION

1. Field of the Invention


The invention relates generally to bipolar articles, such as batteries, and in particular to bipolar articles having interpenetrating current collectors and/or arbitrary form factors that are useful, e.g., for integral formation or embedding in various electronic devices.


2. Summary of the Related Art


Batteries, and particularly rechargeable batteries, are widely used in a variety of devices such as cellular telephones, laptop computers, personal digital assistants, and toys. One example of a rechargeable battery is a lithium solid polymer electrolyte rechargeable battery. This battery can be charged by applying a voltage between the battery's electrodes, which causes lithium ions and electrons to be withdrawn from lithium hosts at the battery's cathode. Lithium ions flow from the cathode to the battery's anode through a polymer electrolyte, and are reduced at the anode, with the overall process requiring energy. Upon discharge, the reverse occurs: lithium ions and electrons are allowed to re-enter lithium hosts at the cathode, while lithium is oxidized to lithium ions at the anode. This is an energetically favorable process that drives electrons through an external circuit, thereby supplying electrical power to a device to which the battery is connected.


Currently available batteries typically have a layered design. Manufacturing constraints generally limit the available shapes or form factors of these batteries. Common form factors include cylinders, button cells (thin discs), relatively thick (>3 mm) prismatic forms, and relatively thin (<0.5 mm) prismatic forms. The relatively thick prismatic forms typically are made by rolling and pressing long coated cathode and anode electrode assemblies separated by a thin separator, or by stacking or laminating layers of cathode/electrolyte/anode material. Some of these prismatic forms are made using a jelly roll or pressed cylinder process. The relatively thin (<0.1 mm) prismatic forms are generally made using thin film processes such as physical vapor deposition.


The energy density of these currently available batteries is relatively low, due to poor volumetric utilization of space within devices in which the batteries are used. For example, short diffusion distances are required for lithium ion transport in a lithium battery. Therefore, the distances between current collectors in a multi-laminate battery structure is small, e.g., less than about 250 μm. The large number of current collectors reduces the volume and weight fractions of electroactive material in the battery. In addition, extra components generally are needed in the devices in which the batteries are used, in order to allow the batteries to be inserted and connected. Such components include an internal chamber with suitable fit and finish for consumer use, an extra set of interconnects to attach the battery to the device, and additional parts to allow the battery to be exchanged, such as, e.g., a battery cover.


Therefore, a need exists for alternative battery designs that allow for more efficient use of space within electronic devices, and thus provide improved power and energy densities.


Recently “three-dimensional batteries” have been proposed, which have anodes and cathodes with active surface areas exposed in three dimensions. Such structures potentially can improve upon the results obtained using standard battery geometries by allowing for more optimal use of materials through independent variation of the ionic and electronic transport path lengths within the device. The present invention provides advances within the emerging field of three-dimensional batteries.


SUMMARY OF THE INVENTION

The present invention provides bipolar articles (i.e., articles such as batteries and capacitors that have two poles, one positive and one negative, that are electrically insulated from one another) having new architectures, such as interpenetrating anode and cathode structures, allowing for improved energy density, and arbitrary form factors, allowing for formation in substantially any desired shape. Such articles are useful for embedding or integral formation in various electronic devices to provide more efficient use of space in the devices. Some of the bipolar articles provided include self-organizing bipolar structures, or sequentially assembled structures. Methods of making and using the articles are also provided.


Accordingly, in one aspect, the invention provides a bipolar article having an arbitrary form factor. The article includes a bipolar structure having an anode, a cathode, and an electrolyte in contact with and separating the anode and cathode. The anode and cathode are interpenetrating. The article further includes a cathode current collector that is in electronic communication with the cathode, and an anode current collector that is in electronic communication with the anode. The bipolar article has a desired arbitrary configuration. The terms “arbitrary form factor” and “arbitrary configuration,” as used herein with respect to a bipolar article as a whole, refer to a bipolar article having an overall form that is not cylindrical or prismatic. “Prismatic” refers to a square or rectangular block having equal thickness across its length and width. In certain embodiments, a bipolar article of arbitrary form factor has a thickness that varies across the length and/or width of the article. In certain embodiments, a bipolar article of arbitrary form factor has a thickness that varies over a length scale that is independent of any length scale of the internal electrode structure of the article. In some instances, a bipolar article of arbitrary form factor takes on the form of a device or housing in which it is contained, or some other conformal or complex shape, for example, a shape including non-planar surfaces.


In another aspect, the invention provides a battery powered device including an interpenetrating electrode battery, which, in some instances, is a self-organizing battery, a housing, and a mechanism powered by the battery. The battery is integrated in the housing or formed in a cavity in the housing. In this context, “integrated” means that the battery is substantially space-filling within the housing. Particularly useful batteries are space-filling in a form factor that is neither cylindrical nor prismatic.


Still another aspect of the invention provides a bipolar article containing first and second interpenetrating electrodes and a plurality of first interpenetrating current collector features wired in parallel and in electronic communication with the first interpenetrating electrode. The article further contains a second current collector in electronic communication with the second interpenetrating electrode. The plurality of first interpenetrating current collector features is distributed through the thickness of the article. In some embodiments, the current collector features are spaced apart at distances and in locations chosen to maximize power density. In certain embodiments, the current collector features are spaced apart at distances and in locations chosen to maximize energy density. For example, in a lithium ion (Li-ion) battery, adjacent current collector features are spaced apart at a distance greater than about 500 μm, in some instances greater than about 750 μm, or greater than about 1000 μm.


Another aspect of the invention provides a multi-layered Li-ion battery having an energy density greater than about 212 Wh/kg.


Still another aspect of the invention provides a bipolar article including a bipolar structure having an anode, a cathode, and an electrolyte in contact with and separating the anode and the cathode. At least one of the anode and the cathode includes a lithium-containing electroactive material. The article further includes a cathode current collector that is in electronic communication with the cathode, and an anode current collector that is in electronic communication with the anode. At least one of the anode and cathode current collectors includes one or more features projecting into the bipolar structure containing the anode and the cathode. The minimum distance between adjacent current collectors is at least about 500 μm, in some instances at least about 750 μm, and in certain instances at least about 1000 μm.


Another aspect of the invention provides a bipolar article including a bipolar structure having an anode network and a cathode network, a cathode current collector that is attractive to the cathode network and repulsive to the anode network, and an anode current collector that is attractive to the anode network and repulsive to the cathode network. At least one of the anode and cathode current collectors is structured and arranged to reduce the effective thickness of the respective network attracted thereto. The effective thickness is reduced by interweaving the current collector through the bipolar article in such a way that the electrical path length within the network is less than it would be if the current collector were not there. The location of the current collector balances the electrical and ionic conductivities of the system, as described in more detail below.


Yet another aspect of the invention provides a bipolar article including a porous first electrode and at least one first current collector, at least a portion of which is embedded within and in electronic communication with the porous first electrode. An electronically insulating, ionically conductive material coats the pore structure of the porous first electrode. Within the pores of the coated porous first electrode is a second electrode having opposite polarity to the porous first electrode. A second current collector is in electronic communication with the second electrode.


In still another aspect, the invention provides a method of making a bipolar article having an arbitrary form factor. The method includes providing a first current collector in a mold having a configuration corresponding to the desired arbitrary form factor, and depositing on the first current collector a first electrode material, an electrolyte material, and a second electrode material. At least one of the electrode materials is configured to have one or more features projecting into the electrolyte material and the other electrode material. A second current collector is provided on the first electrode, electrolyte, and second electrode materials.


Another aspect of the invention provides a method of making a bipolar article having an arbitrary form factor, in which the arbitrary form factor includes a thickness that varies across the length or width of the article. The method includes providing a first current collector in a mold having a configuration corresponding to the desired arbitrary form factor, and depositing on the first current collector a first electrode material, an electrolyte material, and a second electrode material. A second current collector is provided on the first electrode material, electrolyte material, and second electrode material. The method produces a bipolar article having a thickness that varies across the length or width of the article.


Still another aspect of the invention provides a method of making a layered interpenetrating bipolar article. The method includes providing a first current collector and depositing on the first current collector an electrode region. The electrode region contains an interpenetrating network including an anode material, an electrolyte material, and a cathode material. A second current collector is provided on the electrode region. The foregoing method steps are repeated at least once. The method further includes electrically connecting the first current collectors with each other and with one of the anode or cathode materials, and electrically connecting the second current collectors with each other and with the other of the anode or cathode materials.


In yet another aspect, the invention provides a method of making an interpenetrating bipolar article. The method includes providing a first current collector having at least one prong, and depositing on the first current collector an electrode region. The electrode region contains an interpenetrating network including an anode material, an electrolyte material, and a cathode material. The prong of the first current collector extends into one of the anode and cathode materials. A second current collector is provided on the electrode region.


Another aspect of the invention provides a method of making an interpenetrating bipolar article. The method includes assembling a mold containing a first current collector and suspending a plurality of second current collector mesh layers above the first current collector in the mold. A self-organizing bipolar material is introduced into the mold, so that the first and second current collectors are covered with the self-organizing bipolar material. The self-organizing bipolar material is cured to form interpenetrating anode and cathode networks separated by an intervening electrolyte. One of the anode and cathode networks is attractive to the first current collector and repulsive to the second current collector, and the other of the anode and cathode networks is attractive to the second current collector and repulsive to the first current collector.




BRIEF DESCRIPTION OF THE DRAWINGS

The invention is described with reference to the following figures, which are presented for the purpose of illustration only and which are not intended to be limiting of the invention.



FIG. 1 is a schematic illustration of an exemplary cell having interpenetrating electrodes.



FIG. 2 is a schematic illustration of a self-organizing battery structure having an arbitrary form factor according to certain embodiments of the invention.



FIG. 3 is a schematic illustration of a battery structure embedded in a device according to certain embodiments of the invention.



FIG. 4 is a schematic illustration of a self-organizing bipolar article according to certain embodiments of the invention.



FIG. 5 is a schematic illustration of a stamping process for making a bipolar article of arbitrary form factor with a self-organizing system according to certain embodiments of the invention.



FIG. 6A is a schematic illustration of a stamping process for embedding a self-organizing battery in a device according to certain embodiments of the invention.



FIG. 6B is a schematic illustration of a stamping process for embedding an interpenetrating electrode battery in a device according to certain embodiments of the invention.



FIG. 7 is a schematic illustration of a multi-layered battery structure according to certain embodiments of the invention.



FIG. 8 is a schematic illustration of a method for making a self-organizing multi-layered battery according to certain embodiments of the invention.



FIG. 9 is a schematic illustration of a battery structure with interpenetrating current collectors according to certain embodiments of the invention.


FIGS. 10A-B are schematic illustrations of methods for making a self-organizing battery with interpenetrating current collectors according to certain embodiments of the invention.



FIG. 11A is a schematic illustration of a self-organizing battery structure with layered mesh current collectors according to certain embodiments of the invention.



FIG. 11B is an enlarged view of a portion of a mesh layer shown in FIG. 11A.



FIG. 12 is a schematic illustration of a method for making a self-organizing mesh layer battery according to certain embodiments of the invention.




DETAILED DESCRIPTION

In general, factors associated with optimizing both energy and power densities in bipolar articles include (1) having a balanced cell with equal capacities of the anode and cathode, (2) having a maximum amount of active material (anode and cathode) in relation to electrolyte and packaging, (3) establishing a minimum distance between the anode and cathode, and (4) establishing a maximum electrical conductivity within the anode and cathode network. In the past, attempts to increase the energy capacity of a battery by increasing battery thickness and electrode size have not been fully successful, because they often result in reduced in power density. This is due to an imbalance that occurs between the electronic and ionic conductivities in the battery system, because (i) the electronic conductivity decreases with the increasing bulk of the electrode, and (ii) the ionic conductivity decreases across the electrode/electrolyte/electrode stack.


Traditional two-dimensional battery geometries (without interpenetrating electrodes) are inherently unbalanced because ions (e.g. Li+) and electrons flow in parallel directions, such that their transport path lengths within the device cannot be independently adjusted. Such a design does not allow for optimal use of materials, and generally results in an ionic transport path length that is longer than desired, and excess electronic conductivity in one or both electrodes. In contrast, in “three dimensional batteries” having interpenetrating electrodes with active surface areas exposed in three dimensions, the directions of ion and electron flow are decoupled and can be adjusted independently. This allows for better balancing of cell parameters by more optimal use of materials, ultimately leading to improved cell performance.



FIG. 1 illustrates an exemplary cell 100 having interpenetrating anodes and cathodes. For example, in a lithium ion system, the following relationship provides a balance of the two cell properties, electronic conductivity and ionic conductivity:

σe˜1/(w2Lis/l2+w*a/σLie/l2)   (1)

where σe is the electronic conductivity of the cathode 102 and anode 104 electrodes in an interpenetrating system, σLis is the ionic conductivity of lithium through the cathode 102 and anode 104 electrodes, σLie is the ionic conductivity of lithium through the electrolyte 106, l is the length of the electrode extension 108, a is the electrolyte thickness, and w is the width of the electrode extension 108. One of skill in the art will appreciate that Equation (1) can be modified accordingly if the ionic conductivity of lithium is different through the cathode 102 and the anode 104. Thus, higher electrode electrical conductivities are necessary for larger lengths of electrode extension. Accordingly, increasing the thickness of a battery structure to increase the energy capacity often is not feasible, because the resulting increased electrode thickness increases impedance and lowers power density, and the electrical conductivity of the electrodes is not sufficient to allow high power densities.


Three-dimensional designs can be enhanced by spacing current collectors throughout the cell to balance the ionic and electronic conductivities, while minimizing the total current collector volume. The spacing between current collectors in a three-dimensional design can be greater than is possible for a traditional two-dimensional design, because current collector placement is no longer dictated by ionic conductivity (i.e., the ionic and electronic transport paths are decoupled). Thus, the interpenetrating electrode structure of the three-dimensional design provides greater power at any given current collector spacing. For example, a three-dimensional lithium ion battery of reasonable power can be provided with distances between adjacent current collectors of greater than 500 μm, and in some instances greater than 750 μm, or greater than 1000 μm. In comparison, one of skill in the art will appreciate that the current collector spacing in a two-dimensional lithium ion battery of comparable or lower power is generally no more than about 200 μm to about 250 μm. Three-dimensional designs also provide higher energy at a given power compared to two-dimensional designs. By allowing for increased thickness with a reduced number of current collectors, an interpenetrating electrode battery provides equivalent power and higher energy density compared to a standard geometry battery of the same size.


By way of example, a thick (e.g., greater than about 1 mm in thickness) interpenetrating electrode electrochemical cell is provided with multiple current collectors that are wired in parallel and distributed throughout the thickness of the battery. In general, the energy density of a desirable cell is maximized for a specified rate capability. Because current collectors occupy space within the electrode assembly, in at least some instances it is desirable to reduce the number of layers within the cell. However the rate capability of a cell is inversely proportional to its impedance or resistance. As a result, in at least some instances an optimized cell is one in which the number of layers is minimized for a specified rate capability. In addition, the cycle life of a battery tends to be degraded if it is used at a rate capability significantly above its design limit.


In an exemplary cell, the number of layers in the cell and the spacing between current collectors are chosen to satisfy the design parameters described above with respect to Equation 1. The resistance of interpenetrating cells in the battery is modeled as a network of resistors. In general, there are two cases for such layered cells: symmetric, in which each layer is uniquely served by a single pair of current collectors; and asymmetric, in which, for example, each layer is served by a single cathode current collector, but multiple layers are served by a single anode collector. A symmetric design generally is suitable for cathode and anode networks with similar levels of resistivity, whereas asymmetric designs generally are more applicable for cathode and anode networks with a large difference in resistivity. The model presented in this example is for symmetric designs, although alternative embodiments having asymmetric designs are also contemplated. The general relationship for the resistance of the cell is as follows:
Rcell=Rlayern(2)

where Rlayer is the resistance of the layer and n is the number of layers in the cell. In this example, Rlayer is represented by the following relationship:

Rlayer=Rccc+Rcccc+Rcn+Relectrolyte+Ran+Racc,   (3)

where Rccc and Racc are the electrical resistances of the cathode and anode current collectors (CC), respectively, Rcccc is the resistance of the cathode current collector coating, Rcn and Ran are the electrical resistances of the cathode and anode networks, respectively, and Relectrolyte is the ionic resistance of the electrolyte layer. A specific example of such a cell is set forth in detail in Example 1 below.


In general, because the electronic and ionic conductances are balanced in a three-dimensional battery with interpenetrating current collectors, the energy density of such a battery is greater than that of a corresponding two-dimensional battery. In some instances, energy density performance advantages are in the range of about 10%, about 25%, or about 50%. For example, compared to a two-dimensional Li-ion battery providing an energy density of about 170 Wh/kg, a three-dimensional Li-ion battery providing a performance advantage of about 25% would have an energy density of about 212.5 Wh/kg.


Arbitrary Form Factors


In some embodiments, the present invention provides a bipolar article constructed to have virtually any desired form factor or shape. In certain embodiments, bipolar articles having arbitrary form factors are embedded in various devices such as, e.g., cellular telephones, personal digital assistants, laptop computers, and the like, or are integrated into a portion, e.g., a wall of a device. The efficient use of space arising from arbitrary form factors provides for greater practical energy densities. Furthermore, bipolar articles having arbitrary form factors advantageously allow for a reduced number of parts in devices in which they are used, thereby simplifying the design and reducing the cost of the devices. Relatively time-efficient and inexpensive methods of making the bipolar articles described herein are also provided. Some particularly useful bipolar articles include self-organizing structures.



FIG. 2 illustrates one non-limiting example of a battery with arbitrary form factor. The battery includes cathode and anode networks 200, 202 separated by an electrolyte 204. Although not shown in the figure, in some embodiments, the networks 200, 202 are self-organizing and/or have an interpenetrating structure. In certain embodiments, the cathode and anode are sequentially assembled. The cathode and anode networks 200, 202 are connected to respective cathode and anode current collectors 206, 208.



FIG. 3 illustrates an example of a bipolar article of arbitrary form factor that is embedded in a device. In the illustrated embodiment, a battery 300 and associated current collectors 302, 304 are embedded in a device housing 306, effectively using available space in the device. As another non-limiting example, a very thin battery (e.g., about 1 mm thick) is embedded in the housing of a laptop computer behind the LCD display. Such a battery extending to the full screen size of a typical display provides an energy density of about 600 Wh/l and a capacity of about 43 Wh. In alternative embodiments, batteries are embedded or integrally formed in other spaces in laptops or other devices, such as, e.g., circuit boards or electronic components, such as DRAM chips.


In certain embodiments, a battery or other bipolar article of arbitrary form factor is produced using techniques such as, for example, coating, stamping, embossing, printing, or injection molding. One non-limiting example of a method for making a bipolar article of arbitrary form factor employs a direct writing process to build up layers with an arbitrary surface topology. For example, a battery is made by depositing individual particles of anode, cathode, and electrolyte with a predetermined length, width and height onto an appropriate substrate. Layers are built up sequentially until the desired overall thickness of the battery is achieved. The battery is constructed so that (i) the cathode particles are interconnected to the cathode current collector, (ii) the anode particles are interconnected to the anode current collector, and (iii) the electrolyte separates the anode and cathode particles. Non-limiting examples of useful processes for forming the layers of the device include ink jet printing, laser induced forward transfer, matrix-assisted pulsed laser evaporation, and photolithographic techniques.


Multilayer coatings are well known in the manufacture of photographic films, with some film structures including as many as 15 distinct layers. Such films are often manufactured using a coating process known as simultaneous multilayer coating. In this process, multiple liquid layers are simultaneously extruded from a slot coating head with multiple dies onto an inclined plane and then onto a moving web. Intermixing between layers does not occur when the liquids are sufficiently viscous that their flow through the die slot and onto the inclined plane is of low Reynolds number (i.e., laminar flow). In some embodiments, a similar approach is used to make a bipolar article of arbitrary form factor. For example, a 3-die slot head is employed, in which the lowest slot extrudes a cathode electrode slurry, the intermediate slot extrudes a separator/electrolyte, and the upper slot extrudes an anode slurry. Using cathode, anode, and separator/electrolyte materials known in the art, a thin film battery is prepared in a single pass by coating cathode, separator/electrolyte, and anode layers onto a cathode current collector that has the desired arbitrary shape, and laminating the dried coating to an anode current collector. In certain embodiments, repulsive forces between the anode and cathode particles ensure that the coating operation, drying, and subsequent lamination result in a thin film structure with no shorting, e.g., as described in more detail below.


Interpenetrating Current Collector Structures


In some embodiments, the present invention provides bipolar articles having geometries that reduce the electron transport pathway to the current collector within an electrode, thereby increasing the electronic conductivity of the system and allowing the use of thicker batteries (e.g., greater than about 0.1 mm) without loss of power density (e.g., power density greater than 300 W/kg and energy density greater than 450 Wh/l). For example, certain embodiments provide thick batteries with interpenetrating current collectors that have sufficient conductivity for high power density. For a constant footprint, increasing the thickness of a battery increases its energy capacity, making it more suitable for a wide range of applications. Moreover, bipolar devices with new architectures as described herein provide for high energy and power density in a high capacity battery with relatively thin electrode layers, thus avoiding the problems (e.g., long drying time) associated with thick, difficult to process electrode layers.


In some embodiments, the desired reduced electron transport path length is achieved via a bipolar article with interpenetrating current collectors. The interpenetrating structure of the current collectors (particularly the cathode current collector) increases their conductivity, because the distance of electron transport through the relatively resistive electrode is reduced, thus allowing for thick battery structures. The term “interpenetrating current collector” as used herein, refers to a current collector that extends some distance into one or more electrodes or electrode cells. The term “electrode cell” refers to an anode and cathode separated by an electrolyte. FIG. 7 illustrates an example of a structure having interpenetrating current collectors extending into a plurality of electrode cells. FIG. 9 illustrates an example of a structure having interpenetrating current collectors extending into electrodes.


Interpenetrating current collectors are provided using various geometries, for example, a current collector that projects into the electrode or is interdigitated in two or three dimensions with the other current collector (with intervening electrodes and electrolyte). In some embodiments, a reduced transport path length is achieved by use of an interpenetrating current collector that projects into the body of the corresponding electrode. The term “project,” as used herein with respect to current collectors, means that the current collector extends a distance outward from a plane defining the current collector and into the corresponding electrode.


In certain embodiments, a reduced diffusion path length is achieved using a bipolar device, e.g., a battery, with stacked electrode layers with alternating anode and cathode orientations, and multiple surfaces of the current collectors in contact with the electrodes. These and other beneficial alternative structures with interpenetrating current collectors are described in more detail below. Further non-limiting examples of useful geometries for interpenetrating current collectors are as described in the following paragraphs for interpenetrating electrodes.


In at least some embodiments, interpenetrating electrodes are used, which decrease the ionic transport distances between electrodes in a device. Interpenetrating electrodes are described in detail in international patent application PCT/US02/23880, published as WO 03/012908, which is incorporated by reference herein. The term “interpenetrating electrodes,” as used herein, refers to first and second electrodes configured such that that each electrode forms a network that is continuous in two or three dimensions, and each electrode extends into the other electrode to a distance greater than the smallest lateral dimension of the entities comprising the networks. By way of non-limiting example, in various embodiments, the two electrodes exhibit complementary geometries that form interlocking, infused, or interdigitated structures, or one electrode material permeates into voids or spaces in the other electrode material. In some embodiments, the nature of the interpenetration is such that the network provides multiple pathways to the current collector. In one class of interpenetrating structures, separation without a change in the shape or connectivity of an electrode is prevented by the topology of the interpenetrating network.


Due to their interpenetrating features, the two electrodes of the bipolar device approach one another very closely, while maintaining a large interfacial area and decreasing the required volume of electrolyte. In some instances, the average thickness of the layer of electrolyte or separator between the electrodes is less than about 100 μm, e.g., as low as about 1 μm. In certain embodiments, the interpenetrating features of the electrodes have an average protrusion length (corresponding to length l in FIG. 1) of about 10 μm to about 5,000 μm. Such designs decrease the volume of the system by reducing the volume that would normally be consumed by the separator, electrolyte, binder, conductive additive, and other inert components that, in some embodiments, do not store lithium.


By reducing the ionic transport distance between electrodes and permitting independent variation of the electronic and ionic transport path lengths within a battery, interpenetrating electrode structures provide similar power with larger spaces between current collectors compared to typical battery geometries. The use of fewer, more widely spaced current collectors in interpenetrating electrode batteries leaves more room for electroactive material within a battery of a given volume, therefore providing a higher energy density than a standard battery of the same size.


Self-Organizing Systems


Some particularly useful bipolar devices having interpenetrating current collectors, arbitrary form factors, or both, include self-organizing systems. Such systems are described, for example, in U.S. patent application Ser. No. 10/206,662, entitled “Battery Structures, Self-Organizing Structures and Related Methods,” filed on Jun. 26, 2002, which is incorporated by reference herein. That application describes the use of various self-organizing structures to form bipolar devices (e.g., batteries), particularly those having interpenetrating cathode and anode networks. Briefly, as described in that application, self-organizing systems used to form batteries and other bipolar devices contain materials that exert attracting and repelling forces to produce interpenetrating self-organizing structures. The same principle of mutually repulsive and self-attractive surfaces is useful to organize a bipolar device on a current collector.



FIG. 4 schematically illustrates an example of a self-organizing interpenetrating bipolar device. The bipolar device includes a cathode storage compound 400 (“material 1”) and an anode storage compound 402 (“material 3”), which are both dispersed in an electrolyte 404 (“material 2”). The materials 1 and 3 contact respective current collectors 406, 408. The materials 1, 2, and 3 are selected such that when materials 1 and 3 are dispersed in material 2, materials 1 and 3 repel each other. Also, the particles of material 1 self-attract and thereby aggregate, as do the particles of material 2. The system thus allows for the provision of self-organizing and separated cathode and anode networks. This allows for the formation of a self-organizing, co-continuous, interpenetrating microstructure, in which one electrode is continuously wired to a current collector, and another electrode to another current collector. A repelling dispersion force ensures electronic isolation of the two networks.


The principles of surface forces are used in the organization of bipolar devices. Van der Waals (vdW) forces between molecules and condensed phases are composed of three contributions, a Keesom force due to interactions between oriented permanent dipoles, a Debye force due to polarization induced in other molecules by a permanent dipole, and a London dispersion force due to polarization induced in other molecules by oscillations in the electron cloud of interatomic bonds. Of these, the London dispersion force is the most universal, since it does not require the existence of permanent dipoles. An important parameter scaling the dispersion force is the Hamaker constant A. For symmetric combinations of materials (e.g., 121 or 212), the Hamaker constant A121=A212 is always positive, leading to an attractive dispersion force (FvdW<0). For asymmetric combinations (e.g., 123), the dispersion force can be either attractive or repelling. For most materials, and especially low refractive index materials (n<2), the dominant interactions occur in the optical frequency range, and the Hamaker constant can be approximated to good accuracy using optical index and static dielectric constant approximations as represented by the following equation:
A12334kT(E1-E2E1+E2)(E3-E2E3+E2)+38hve2(n12-n22)(n32-n22)(n12+n22)1/2(n32+n22)1/2{(n12+n22)1/2+(n32+n22)1/2}

The electronic frequency ve corresponds to the mean ionization frequency of the materials present. Typically, ve≈3×1015 Hz. k is Boltzmann's constant and h is Plank's constant. The refractive indices in the visible range for mediums 1, 2, and 3 are n1, n2, and n3, respectively. E1, E2, and E3 are the static relative dielectric constants. The first term in the equation gives the zero frequency energy of the van der Waals interaction, and includes the Keesom and Debye dipolar contributions. For two non-polar media acting over a third medium, the first term is not significant.


When the indices are ordered as n1>n2>n3, A123 is negative. Thus, the sign and magnitude of the Hamaker constant can be readily estimated from optical and dielectric data, while more precise quantification, where necessary, is possible with full-spectral methods.


To provide a self-organizing system for two dissimilar materials 1 and 3 separated by a medium 2, the vdW interaction is rendered repelling through judicious selection of materials characterized by a negative Hamaker constant A123. Numerous combinations of materials 1, 2, and 3 provide such a self-organizing system. Table 1 lists non-limiting examples of some useful materials and combinations.

TABLE 1Dispersion-Force Organized SystemsSystemMaterial 1 (Cathode)Material 2 (Separator/Electrolyte)Material 3 (Anode)1LiCoO2Poly(ethylene oxide) (PEO) orMesocarbon microbeads (MCMB)or,Mg-doped LiCoO2poly(ethylene glycol) (PEG)an unlithiated metal anode, such as Sn,LiMn2O4poly(styrene) (PS)Zn, Al, or Si, in each case coated with:LiMnO2poly(acrylonitrile) (PAN)POMA/PVDF orLiNiO2(each of the above optionallyPOTh/PVDFdoped with a lithium salt for Li+conductivity)PEO or PVDF dissolved in a highrefractive index solvent such asdiiodomethane, 1,3-diiodopropane, N,N-dimethylformamide (DMF),bromobenzene, cyclohexane, ordimethylpropylene urea (DMPU),the solvent being subsequentlyevaporated and an organic liquidelectrolyte being infused.2Cathodes as in System 1,Same as in System 1Mesocarbon microbeads (MCMB)coated with:an unlithiated metal anode, such asPOMA1/PVDF2Sn, Zn, Al, or SiPOTh3/PVDFPEDT4/PTFE5PEDT/PP6PEDT/HDPE73LiFePO4Same as in System 1Mesocarbon microbeads (MCMB)Li2Fe2(SO4)3,a lithiated metal anode such as Li,V6O11LiAl, Li3Al, LiZn, LiAg, Li10Ag3,V2O5Li5B4, Li7B6, Li12Si7, Li21Si8,Li13Si4, Li21Si5, Li5Sn2, Li13Sn5,Li7Sn2, Li22Sn5, Li2Sb, Li3Sb,LiBi, or Li3Bi4LiFePO4Li2OB2O3—Bi2O3 glassMesocarbon microbeads (MCMB)Li2Fe2(SO4)3,Li2O—B2O3—PbO glassa lithiated metal anode such as Li,V6O11LiAl, Li3Al, LiZn, LiAg, Li10Ag3,V2O5Li5B4, Li7B6, Li12Si7, Li21Si8,Li13Si4, Li21Si5, Li5Sn2, Li13Sn5,Li7Sn2, Li22Sn5, Li2Sb, Li3Sb,LiBi, or Li3Bi5Cathodes as in System 1,Same as in System 1Mesocarbon microbeadscoated with:(MCMB)vanadium oxidean unlithiated metal anode, suchhydrated vanadiumas Sn, Zn, Al, or Sioxidevanadium oxide - PEOblendvanadium-boron-oxidevanadium-silicon-oxidevanadium-phosphorus-oxide
1Poly(2-methoxyaniline)

2Poly(vinylidene fluoride)

3Poly(3-octylthiophene)

4Poly(3,4-ethylenedioxythiophene)

5Poly(tetrafluoroethylene)

6Polypropylene

7High density polyethylene


Accordingly, in some embodiments, useful cathode and anode materials include, but are not limited to, one or more of LiCoO2, Li(Mgx,Co1-x)O2, LiNiO2, LiMn2O4, LiMnO2, Li(AlxMn1-x)O2, doped and undoped LiFePO4, Li2Fe2(SO4)3, V2O5, V6O11, C, amorphous carbon, graphite, mesocarbon microbeads (MCMB), Li, LiAl, Li9Al4, Li3Al, Zn, LiZn, Ag, LiAg, Li10Ag3, B, Li5B4, Li7B6, Ge, Si, Li12Si7, Li21Si8, Li13Si4, Li21Si5, Sn, Li5Sn2, Li13Sn5, Li7Sn2, Li22Sn5, Sb, Li2Sb, Li3Sb, Bi, LiBi, Li3Bi, SnO, MnO, Mn2O3, MnO2, Mn3O4, CoO, NiO, FeO, LiFe2O4, TiO2, LiTi2O4, Sn-B-P-O compounds, and glass. In particular embodiments, an anode includes one or more of the following materials: carbon, amorphous carbon, graphite, mesocarbon microbeads, Li, LiAl, Li9Al4, Li3Al, Zn, LiZn, Ag, LiAg, Li10Ag3, B, Li5B4, Li7B6, Ge, Si, Li12Si7, Li21Si8, Li13Si4, Li21Si5, Sn, Li5Sn2, Li13Sn5, Li7Sn2, Li22Sn5, Sb, Li2Sb, Li3Sb, Bi, LiBi, and Li3Bi, SnO2, SnO, MnO, Mn2O3, MnO2, Mn3O4, CoO, NiO, FeO, LiFe2O4, TiO2, LiTi2O4, and glass. In certain embodiments, a cathode includes one or more of the following materials: LiCoO2, LiCoO2 doped with Mg, LiNiO2, LiMn2O4, LiMnO2, LiMnO2 doped with Al, doped and undoped LiFePO4, LiMnPO4, LixV6O13, Li2Fe2(SO4)3, V2O5, V6O11, and SnO2.


In some embodiments, the separator/electrolyte medium 2 includes, but is not limited to, one or more of the following materials, selected to provide a repelling interaction or to wet between the cathode and anode materials 1 and 3: organic materials, such as, e.g., poly(ethylene oxide) (PEO), poly(styrene) (PS), poly(acrylonitrile) (PAN), poly(vinylidene fluoride) (PVDF), diiodomethane (DIM), 1,3-diiodopropane, N,N-dimethylformamide (DMF), dimethylpropylene urea (DMPU), ethylene carbonate (EC), diethylene carbonate (DEC), dimethyl carbonate (DMC), propylene carbonate (PC), and block copolymer lithium electrolytes, the preceding organic materials being doped with a lithium salt, such as, e.g., LiClO4, LiPF6, LiAsF6, LiHgI3, LiCF3SO3 or LiBF4, to provide lithium ionic conductivity; and inorganic materials, such as, e.g., LiI, LiF, LiCl, Li2O—B2O3—Bi2O3 compounds including glass, Li2O—B2O3—P2O5 compounds including glass, Li2O—B2O3—PbO compounds including glass, and sols or gels of the oxides or hydroxides of Ti, Zr, Pb, or Bi.


The cathode and/or anode materials 1 and 3 are optionally coated. For example, in certain embodiments a coating is provided on the cathode storage compound or the anode storage compound in order to obtain a repelling dispersion force between the two in the separator/electrolyte medium. Non-limiting examples of useful coating materials include electronically conductive polymers and blends thereof, e.g., polythiophene, polyanaline, poly(o-methoxyaniline) (POMA) or poly(3-octylthiophene) (POTh) with PVDF, PEO, or conductive oxides such as indium tin oxide (ITO). Some particularly useful coatings include poly(3,4-ethylene dioxythiophene)(PEDT) or poly(3,4 ethylene dioxythiophene)-polystyrene sulfonate (PEDT-PSS) with polytetrafluoroethylene (PTFE), PTFE derivatives, or PVDF.


A detailed description of useful coating materials is contained in U.S. patent application Ser. No. 10/354,405, entitled “Electrodes and Related Devices,” filed on Jan. 30, 2003, which is incorporated by reference herein. For example, as described in that application, coatings generally are selected to provide both the desired surface attractive and/or repulsive forces and adequate conductivity for electrochemical device function. Thus, the coating includes a conductive material, such as, e.g., a conductive polymer or a copolymer or blend of conductive polymers. Examples of conductive polymers include, without limitation, polyanilines (e.g., poly(2-methoxyaniline)), polythiophenes (e.g., poly(3-octylthiophene) and poly(3,4-ethylene dioxythiophene)), polypyrroles, polyetheylenes, and derivatives thereof. Other non-limiting examples of useful conductive materials include pure elements, such as carbon black, lithium, nickel, and zinc; metal oxides, such as vanadium oxide, indium tin oxide, titanium oxide, manganese oxide, and nickel oxide; and metal sulfides. In some instances, the coating material includes a dopant to improve conductivity. Suitable dopants include, but are not limited to, counter-ion sources such as, e.g., polystyrene sulfonate, hydrochloric acid, and lithiated compounds, tosylate ion, camphorsulfonic acid, dodecylbenzene sulfonic acid, perfluorodecane sulfonic acid, trifluoroacetic acid, and perchloric acid.


Some useful coatings also include a material with low refractive index, for example, to make the refractive index of the entire coating layer less than that of the electrolyte material being used. The amount of low index material in the coating is chosen to provide a desired average refractive index for the coating layer. Suitable low refractive index materials include, but are not limited to, fluorinated polymers, polypropylene, and vanadium oxide. Non-limiting examples of fluorinated polymers include PTFE, PVDF, fluorinated esters of methacrylic acid (e.g., hexafluoroisopropylmethacrylate, heptafluorobutylmethacrylate, trifluoroethylmethacrylate, and pentafluorobutylmethacrylate), fluorinated esters of methacrylic acid, and copolymers and blends thereof.


In some alternative embodiments, a separator/electrolyte material is selected to give a repelling dispersion force between the cathode and anode storage compounds, even in the absence of a coating. As a non-limiting example, the separator/electrolyte is an inorganic glassy material selected to have sufficiently high refractive index to provide a repelling dispersion force between the cathode and anode compounds, as well as sufficiently high lithium ionic conductivity and low electronic conductivity to act as an electrolyte.


To form a bipolar article, the self-organizing mixture is cured, and the anode and cathode networks are wired only to anode and cathode current collectors, respectively. One non-limiting example of a way to achieve proper wiring is to use surface forces on the anode and cathode particles for proper positioning. The principles that allow the respective networks to form and yet repel each other are used to wire the networks to their respective current collectors. Each current collector has a surface that attracts either the cathode or the anode and repels the other. In some embodiments, at least one of the current collectors is coated to provide the desired attractive and repulsive forces. Useful coating materials include those described above for coating anode and cathode materials. However, as one of skill in the art will appreciate, somewhat different selection criteria apply for choosing a coating for a current collector, as opposed to an electrode coating. For a current collector coating, ionic conductivity is not required. Also, the electrical conductivity of the coating is less important, because electrons need to travel through only a single coating layer to cross into the current collector. Furthermore, thicker coatings are suitable for coating current collectors, e.g., up to about 1 μm coating thickness for a 10 μm thick current collector. In comparison, particle coatings are generally thinner, e.g., up to about 0.1 μm coating thickness for a 5 μm wide cathode particle.


For example, in some embodiments, London Dispersion Forces are used. One current collector is coated with a thin layer of a conductive low refractive index material, such as a conductive polymer blend, which attracts low refractive index active materials (e.g., appropriately-encapsulated LiCoO2 particles) and repels high refractive index active materials (e.g., MCMB). The opposing current collector is chosen to have a high refractive index (e.g., pure Cu), which has the opposite attracting and repelling effects. In at least some embodiments, in order to make use of surface forces that are strong over relatively small length scales (less than about a few microns for London Dispersion Forces in most systems), the self-organizing composition is well-mixed, so that the anode and cathode particles are randomly and homogeneously distributed on a micron-level length scale.


Alternatively, fields such as gravity or magnetism are used to wire the cathode and anode networks to their respective current collectors, again by appropriate selection of materials. In the case of gravity, materials are selected to provide a density contrast. As a non-limiting example, the density of the anode (e.g., MCMB) is less than that of the solvent/electrolyte (e.g., DIM+PEO+Li salt), which is less than that of the cathode (e.g., LiCoO). In such a system the anode current collector is above the cathode current collector.


Alternatively, a layered approach is used in conjunction with surface forces. In this approach, a thin (˜10× the active particle diameter) coating of an active material appropriate for connection to a current collector is coated sequentially in the immediate proximity of the current collector and the self-organizing mixture. For example, a bottom current collector is deposited, followed by a layer of the appropriate active material, followed by a layer of self-organizing mixture of the nominal thickness of the cell layer, followed by a layer of the other active material, followed by the other current collector. Due to the high loading of the active materials (>˜50%), shorting does not result.


The following are non-limiting examples of specific architectures contemplated for the bipolar devices as described herein, and specific methods of producing such devices.


Methods of Making Interpenetrating Electrode Batteries Having Arbitrary Form Factors


A battery having virtually any desired form factor or shape is prepared with interpenetrating electrodes, for example, using the self-organizing principles described above. Such batteries are useful to efficiently utilize space in devices in which they are used. Suitable materials for making the battery include, e.g., traditional battery materials used in the field and self-assembling systems such as those described above.


Processes useful for making batteries or other bipolar articles of arbitrary form factor with interpenetrating electrodes include, but are not limited to, coating, stamping, embossing, printing, and injection molding. One non-limiting example of a stamping process, illustrated in FIG. 5, is as follows:

    • (1) Prepare a self-assembling mixture 500.
    • (2) Tape cast a cell precursor slab 505, for example, by tape casting the self-assembling mixture 500 on a current collector 510.
    • (3) Stamp the mixture 500 with a form 520 while the mixture 500 is still viscous, optionally shaping one or both sides of the mixture 500.
    • (4) Allow the stamped mixture 500 to self-assemble and cure, forming anode and cathode networks 530, 540 with electrolyte 545 disposed there between.
    • (5) Form or attach a second current collector 550 to the battery 560.


The current collectors 510, 550 optionally extend over the entire surfaces of the respective anode and cathode components. In alternative embodiments, current collectors extend over only portions of the anode and cathode as illustrated in FIG. 2.


In some embodiments, interpenetrating electrode batteries are embedded or integrally formed within various device, such as, e.g., cell phones, personal digital assistants, laptop computers, and the like. Various processes are useful for embedding interpenetrating electrode batteries in devices. For example, FIG. 6A illustrates a process in which a self-organizing battery is formed by stamping into a device as follows:

    • (1) Prepare a self-assembling mixture 600.
    • (2) Attach a first current collector 610 to a surface of a device 620, e.g., within the device housing 630.
    • (3) Deposit the self-assembling mixture 600 on the first current collector.
    • (4) Stamp the self-assembling mixture 600 to form fit the desired surface topology.
    • (5) Attach a second current collector 640 to the surface of the battery 650 opposite the first current collector 610.
    • (6) Allow the stamped mixture 600 to set.
    • (7) Apply a protective overcoat 660 to the battery 650.


      Alternatively, the mixture 600 is injected into a cavity in the device and cured using the self-assembling principles described above.



FIG. 6B illustrates a similar process for making an interpenetrating electrode battery with non-self assembling electrode materials by stamping into a device as follows:

    • (1) Prepare a cathode mixture 602.
    • (2) Attach a first current collector 610 to a surface of the device 620, e.g., within the device housing 630.
    • (3) Deposit the cathode mixture 602 on the first current collector.
    • (4) Stamp the cathode mixture 602 to provide a first reticulated electrode.
    • (5) Coat the surface 604 of the stamped cathode mixture 602 with an ionically permeable separator layer 606.
    • (6) Coat the ionically permeable separator layer 606 with an anode material 608.
    • (7) Attach a second current collector 640 to the anode 608.
    • (8) Apply a protective overcoat 660 to the battery 650.


      In certain embodiments, the separator layer 606 includes a Kynar-based material with a PVDF-rich binder.


      Multi-Layered Battery



FIG. 7 illustrates one example of a multi-layered battery including three battery layers 700, 702, 704 separated by an anode current collector 706 and a cathode current collector 708. In the illustrated embodiments, the battery layers 700, 702, 704 are self-organizing. Each layer 700, 702, 704 includes self-organizing cathode and anode networks. In some alternative embodiments, non-self-organizing, e.g., sequentially deposited, layers are employed. Although not shown in the figure, in some embodiments, the anode and cathode networks are interpenetrating. The battery layers are oriented in an alternating arrangement such that the anode network of one layer faces the anode network of an adjacent layer, and the cathode network of one layer faces the cathode network of an adjacent layer. The battery layers 700, 702 are separated by the cathode current collector 708, which is in contact with the cathode networks of the layers. The battery layers 702, 704 are separated by the anode current collector 706, which is in contact with the anode networks of the layers. The cathode current collector 708 is electrically connected to an outer cathode current collector, and the anode current collector 706 is electrically connected to an outer anode current collector. In particular embodiments, the anode and cathode current collectors 706, 708 are electrically insulated from each other to inhibit shorting. In some instances, the battery layers 700, 702, 704 each have a thickness of about 0.1 mm to about 5 mm, and the anode and cathode current collectors 706, 708 each have a thickness of about 0.005 mm to about 0.05 mm. This allows for a high battery to current collector ratio, e.g., a ratio greater than about 10:1, and in some instances significantly greater than 10:1. A higher battery to current collector ratio provides higher energy density.


In some embodiments, a multi-layered battery is made by depositing multiple battery layers on multiple current collectors. FIG. 8 illustrates a non-limiting example of a method for making a self-organizing multi-layered battery as follows:

    • (1) Deposit a first layer of self-organizing material 810 on an outer cathode current collector 800, and cure.
    • (2) Affix an anode current collector 820 on the first layer 810.
    • (3) Deposit a second layer of self-organizing material 830 on the anode current collector 820, and cure.
    • (4) Affix a cathode current collector 840 on the second layer 830.
    • (5) Deposit a third layer of self-organizing material 850 on the cathode current collector 830, and cure.
    • (6) Affix an outer anode 860 to the third layer 850.
    • (7) Electrically connect the anode current collectors 820, 860 to each other, and the cathode current collectors 800, 840 to each other.


      In some alternative embodiments, all of the layers 810, 830, 850 are cured at the same time, self-assembling into anode and cathode networks according to the self-organizing principles described above. In certain alternative embodiments, non-self-organizing anode and cathode materials are employed.


      Interpenetrating Current Collector with Projecting Elements



FIG. 9 illustrates an example of a battery with an interpenetrating current collector structure. The battery includes a cathode current collector 900, an anode current collector 902, and a self-organizing battery structure 904 disposed there between. The self-organizing battery structure forms cathode and anode networks, which are in contact with their respective current collectors. Although not shown in the figure, in some embodiments the anode and cathode networks themselves are interpenetrating. Each current collector 900, 902 includes a plurality of projecting elements or prongs 906, which extend into spaces 908 between projecting elements of the other current collector 900, 902. By way of the prongs 906, each of the current collectors 900, 902 penetrates into the self-organizing electrode assembly 904 for a distance that is less than the full dimensionality of the cell. The cathode and anode current collectors 900, 902 have an interpenetrating arrangement, and define a serpentine gap there between. In some alternative embodiments, only one of the current collectors includes projecting elements, and the other current collector has a planar or other structure.



FIG. 10A illustrates a non-limiting example of a method for making a self-organizing battery with interpenetrating current collectors as follows:

    • (1) Deposit self-organizing material 110 on the first current collector 112, which can be either the anode or the cathode current collector.
    • (2) Position the other current collector 114 in an interpenetrating arrangement with and spaced apart from the first current collector 112.
    • (3) Cure the self-organizing material 110 to form cathode and anode networks 116, 118 with electrolyte 117 disposed there between. The networks 116, 118 are in contact with their respective current collectors 114, 112.


      One exemplary alternative method, illustrated in FIG. 10B, is as follows:
    • (1) Arrange the anode and cathode current collectors 112, 114 in a spaced-apart, interpenetrating arrangement.
    • (2) Introduce the self-organizing material 120 in the serpentine gap 119 between the current collectors 112, 114.
    • (3) Cure the self-organizing material 110 to form cathode and anode networks 116, 118 with electrolyte 117 disposed there between. The networks 116, 118 are in contact with their respective current collectors 114, 112.


      One of skill in the art will understand that, while self-organizing materials constitute one particularly useful set of materials for making batteries with interpenetrating current collectors and other alternative bipolar structures described herein, such structures are also suitably produced using various non-self-organizing materials known in the field. For example, in some embodiments, a laminar approach is used, providing anode, cathode, and electrolyte layers on current collectors to form a battery having interpenetrating current collectors and/or arbitrary form factors from standard battery materials known in the art.


      Mesh Layer Structure


Another example of an interpenetrating current collector structure includes an open or porous current collector that is inserted into an electrode. For example, FIGS. 11A-B illustrate an example of a battery with an open, e.g., mesh current collector. As shown in the side view of FIG. 11A, the battery includes a first generally planar current collector 120, on which is a battery 122. In the illustrated embodiment, the battery 122 is self-organizing. One or more mesh layers 124 forming the second current collector extend through the self-organizing battery 122 at spaced-apart positions above the first current collector 120. In various embodiments, the mesh layers 124 form either the anode or cathode current collector. In some instances, the mesh layers are used as the cathode current collector, because the electrical conductivity of the cathode network sometimes is not sufficient to provide high power density in thick batteries. FIGS. 11A-B show the mesh layers forming the cathode current collector. FIG. 11B is an enlarged top view of a portion of one of the mesh layers 124. The mesh layers include a plurality of openings 126. The openings 126 are large enough to allow multiple anode network elements or particles 128 and cathode network elements or particles 129 to fit therein. For example, in certain embodiments, the cathode and anode elements or particles 129, 128 have a diameter on the order of 2 μm, and the mesh spacing is greater than about 200 μm. In some alternative embodiments, the cathode and anode elements or particles 129, 128 have a diameter on the order of 200 μm, and the mesh spacing is greater than about 20 mm. In the embodiment illustrated in FIG. 11B, the mesh 124 is attractive to and thereby in contact with the cathode network particles 129, and is repulsive to the anode network particles 128.


One non-limiting example of a method for making a self-organizing mesh layer battery, illustrated in FIG. 12, is as follows:

    • (1) Assemble a mold 130 having an anode current collector 132 and a plurality of spaced apart cathode current collector mesh layers 134 suspended above the anode current collector 132.
    • (2) Introduce a self-organizing battery mixture 136 into the mold 130 covering the current collectors 132, 134.
    • (3) Cure the self-organizing material 136, and remove the battery from the mold 130.


      In some alternative embodiments, a generally continuous manufacturing process is used in which the self-organizing material is continuously deposited on moving, continuous sheets of current collector material (i.e., layers of cathode current collector suspended over an anode current collector). The self-organizing material cures while moving, and is cut in desired sizes. Such continuous manufacturing processes are suitable for producing not just the present mesh embodiment, but also various other device architectures described herein. Furthermore, as noted above, self-organizing materials are useful, but various alternative materials known in the field are suitable for producing the mesh layered battery and other bipolar structures described herein.


      Porous Electrode


Another example of an interpenetrating current collector structure includes a current collector that is introduced into a porous electrode, which, in at least some instances, has an arbitrary form. In some embodiments, a battery with a porous electrode structure is provided. A first highly “open” porous electrode (e.g., sintered LMCO) is fabricated with pore diameters much greater than the primary particle size of the material to be used as the opposite electrode. This first structure is formed partially or completely of a storage electrode material by a process such as, for example, pressing, aggregation, or sedimentation of particles or coated particles into a preform mold of the desired arbitrary shape, or stamping of particles or coated particles into the desired arbitrary shape. Current collector(s) (e.g., having forms as described elsewhere herein) are inserted into the porous network prior to such pressing, aggregation, etc. The particles are optionally heat treated or sintered to improve the strength and electrical conductivity of the porous structure. In some embodiments, a powder preform of the first electrode is formed into the desired arbitrary shape as a “green body” prior to sintering. Current collectors are embedded within the powder preform and sintered in place. After sintering, the pellet with embedded current collectors optionally is etched to fully remove any current collector from the pore space. In some alternative embodiments, the porous structure is formed using a removable pore-forming material, or phase-separation or precipitation of the constituents of the structure from a liquid or solid followed by removal of a pore forming material. In other alternative embodiments, an active material is directly fabricated as a foam. Further useful methods for forming the structure include, but are not limited to, lamination of porous layers, layer-by-layer additive or subtractive deposition methods, such as lithographic patterning and selective etching, and three-dimensional printing of the structure material.


An electronically insulating, ionically conducting layer is formed upon the surfaces of the first structure. For example, the insulating layer is an organic or inorganic solid electrolyte, or is a separator that is subsequently infiltrated with a liquid or solid electrolyte to provide ionic conductivity. The insulating layer coats the internal and external surfaces of the first structure, and is formed by a method such as, for example, infiltration of the first structure with the insulator in a molten form, infiltration of the first structure with a liquid containing the constituents of the electronic insulator, deposition of the insulator constituents from a vapor phase such as by chemical or physical vapor deposition or plasma-enhanced deposition, reaction of the material of the first structure with a vapor phase or a deposited material to form the surface insulating layer, electrolytic or electrochemical deposition, or a combination of such methods. As a non-limiting example, the interior pore space and optionally the current collector penetrating into the pore space is coated with a precursor to an electrolyte (e.g., PEO+electrolyte salt mixture). The insulating layer is formed in one or in multiple process steps. The structure has substantially open porosity after the insulating layer is formed on internal surfaces of the first structure.


The open porosity in the insulator-coated first structure is then infiltrated with the second electrode material, or a composite mixture containing the second storage material, resulting in a second interpenetrating electrode that substantially occupies the pore space in the first structure. The second interpenetrating electrode forms an electronically conductive network, and is electronically isolated from the first electrode by an intervening electrolyte layer. In some embodiments, the first structure is infiltrated with a fluid comprising the second electrode material, and a reaction of the first structure with the second electrode material or other constituents of the fluid is used to form an electrolyte layer. The second electrode material is infiltrated, for example, as a melt, as a vapor phase species, by electrolytic or electroless plating, as a liquid solution that subsequently dries or is reacted to form the second electrode material, or as a suspension of the second electrode material in a liquid.


In certain embodiments, a suspension of the second electrode material is used. The liquid in which the second electrode material is dispersed is optionally a liquid or solid electrolyte, or contains a binder or the constituents of an electrolyte in a solvent, or contains a material that improves the electronic conductivity of the second interpenetrating electrode, such as, e.g., fine carbon or metal particles, or the constituents of an electronically conductive polymer. As a non-limiting example, a coated perform porous electrode is infiltrated with a mixture including the opposite electrode material (e.g., MCMB), and optionally a precursor to an electrolyte (e.g., PEO+electrolyte salt mixture), and optionally a conductive additive to provide a supplemental current path—effectively acting as a current collector.


In some embodiments, a self-organizing system is used, in which second electrode particles and electrolyte materials are selected to exhibit the desired attractive and repulsive forces. Thus, when the first porous electrode structure is infiltrated with a suspension containing the second electrode material, a repulsive force results between the two electrode materials, causing their electronic isolation from each other. Accordingly, the electrolyte coats the walls of the first porous electrode, while the second electrode accumulates in the interior pore space. The repulsive properties of first porous electrode and second electrode particles prevents the deposition of second electrode particles on the walls of the first porous electrode form, thereby avoiding shorting of the system.


After infiltration of the first porous electrode by the second electrode material and the attachment of a second current collector to this material, a device comprising interpenetrating electrodes is obtained. In certain embodiments, the second current collector is inserted in the interpenetrating electrode structure to create an interpenetrating current collector. For example, in one such embodiment, a second current collector is used that has similar repulsive force characteristics as the second electrode material.


The following non-limiting examples further illustrate certain embodiments of the invention.


EXAMPLE 1

A thick symmetric electrochemical cell with interpenetrating electrodes is provided, with multiple current collectors wired in parallel distributed throughout the thickness of the battery. The current collectors are configured in parallel by embedding them so that the cathode collector only connects to the cathode network and the anode collector only connects to the anode network. The approximate spacing between current collectors and the number of layers in the cell are chosen by balancing design parameters as discussed in detail above with respect to Equations 1-3. The interpenetrating current collector structure allows for a cell that provides similar rate capability with significantly fewer layers, and thus reduced current collector volume, compared to a standard cell, and significantly improved rate capability and life cycle compared to a three-dimensional battery with only a single set of current collectors. The interpenetrating current collectors overcome the inherent shortcomings in electronic conductivity over large distances to allow for a battery with a thickness greater than 0.1 μmm, a power density greater than 300 W/kg, and an energy density of greater than 450 Wh/l.


The parameters of the cell are listed in Table 2 below. These parameters reflect a circuit in which charge moves through the cathode current collector across some fraction of the layer thickness of the cathode network, across the electrolyte layer, across the complementary fraction of the layer thickness of the anode network, and through the anode current collector for a number of layers in parallel. Some bounding estimates for the cell resistance are made. For example, the area fraction values assume a mesh with 67% open space along its length and thickness for the current collector layers, and assume that the area fraction is equivalent to the proportion of solids loading for the network and electrolyte layers. The anode and cathode current collector resistivities are known in the art, the anode and cathode network resistivity values are based on measurements of a conventional cell, and the electrolyte layer resistivity is based on the value for PEO at 40° C., which is known in the art. The area value for the electrolyte layer assumes a one-dimensional interpenetrating network with a 6 μm repeat distance.


The values in Table 2 reflect charge transfer halfway through the interpenetrating network (0.1 cm over a 0.2 cm full layer thickness).

TABLE 2ThicknessWidthLengthNumber ofCell(cm)(cm)(cm)Layers0.63.24.83ThicknessAreaResistivityLengthAreaResistanceLayer Network(cm)Fraction(Ω cm)(cm)(cm2)(Ω)Cathode Current Collector0.00250.332.60 × 1064.80.0030.005Cathode CC Coating0.00010.331000.00015.0690.002Cathode Network0.20.3330.15.0690.059Electrolyte Layer0.00020.31500,0000.00025.1200.020Anode Network0.20.360.50.15.5300.009Anode Current Collector0.00250.331.70 × 1064.80.0030.003Layer Resistance0.094Total Cell Resistance0.031


The DC resistance (effectively equivalent to the AC impedance at 1000 Hz) of the three-layer cell as shown in Table 2 is 31 mΩ for a 1.5 Ah capacity. The effective DC resistance of conventional prismatic Li-ion cells is in the range of 30-50 mΩ for 0.8-2.0 Ah capacities, respectively. Thus, without major changes to the resistivities of the cathode and anode networks and the electrolyte layer, the three-layer interpenetrating electrode system achieves effective DC resistances on the order of those for conventional cells. The resistivity of the cathode current collector coating is substantially less than 10,000 Ωcm. For a thin coating about 1 μm thick, a resistivity on the order of 100 Ωcm contributes 2 mΩ to the total layer resistance. The cathode network is generally the most resistive component of the cell.


The power density of conventional prismatic Li-ion cells is on the order of 300 W/kg. Consideration of two factors indicates that the power density of the cell described in Table 2 is at least about 300 W/kg. First, the effective DC resistance of the cell is 31 mΩ, a value on the order of that measured for conventional cells with similar capacities. Second, polarization within the cell is the primary mechanism controlling power density. For conventional batteries, polarization is dominated by Li transfer through the relatively thick (on the order of 100 μm) electrolyte layer. For the cell described in Table 2, the electrolyte layer is relatively thin, on the order of 1 μm. Because the rate of mass transfer is proportional to the square of the distance, the power density of the cell described in Table 2 is significantly greater than that of a conventional cell.


EXAMPLE 2

A self-organizing bipolar system, suitable for use in making articles having interpenetrating current collectors and/or arbitrary form factors as described in Examples 3-8 below, is made using the components listed in Table 3.

TABLE 3Cathode Current CollectorAlCathode CC Coating10% PEDT-PSS (30 nm) with 90% PTFEpowderCathodeLMCO (3% MgO) (density ˜5 g/cc)Encapsulant10% PEDT-PSS (30 nm) with 90% PTFEpowderAnode6 μm MCMB (density 2.1 g/cc)Anode Current CollectorCuElectrolytePEO + LiClO4Solventdiiodomethane (DIM) + acetonitrile (AN)


Coated Cathode Current Collector


Aluminum (Al) disks are coated with a conductive polymer blend of poly(3,4-ethylenedioxythiophene)poly(styrenesulfonate) (PEDT-PSS) and polytetrafluoroethylene (PTFE) to function as the cathode current collector. This coating has a refractive index that renders it attractive to the cathode material, lithium magnesium cobaltate (LMCO), and repulsive to the anode material, mesocarbon microbeads (MCMB).


The coating solution is prepared with 10 wt % PEDT-PSS, available under the trade name Baytron P from Bayer Corp. (one part poly(ethylene dioxythiophene) and 2 parts poly(styrene sulphonic acid)); 86.6 wt % Teflon from DuPont (Grade MP1100; narrow particle size distribution—1.5 to 4 μm); 3.3 wt % nonionic fluorinated surfactant, Zonyl FSN from DuPont (a perfluoroalkyl ethoxylated surfactant); and the balance water. 1.45 g of a 1.3 wt % PEDT-PSS dispersion is placed in a glass vial with a magnetic stir bar. With agitation, 0.611 g water is added. After this dilution, 126 μl of 5 wt % Zonyl FSN is added, followed by 145 μl of N-methyl-2-pyrrolidinone. Finally, 0.163 g Teflon MP1100 powder is added, and the mixture is either agitated for at least 1 hour or sonified for 5 minutes. The resulting dispersion is 7.54 wt % solids.


The aluminum disks are prepared by taking extra heavy duty Reynolds aluminum and punching out disks of {fraction (9/16)} in. diameter. Each disk is flattened smooth and then rinsed in acetone for 2 min., followed by ethanol for 2 min., and then dried. Each disk is then mounted on a glass plate using low tack adhesive, and the dull side of the disk is coated by applying 50 μl of the coating dispersion. The disks are dried at 75° C. for 40 min., and then at 150° C. for 1 hour. The dried coating thickness is 20 μm. The through conductivity is measured to be 5 Ω (for a contact diameter of 0.25 in.), which corresponds to a volumetric conductivity of 1.26×10−3 S/cm.


Coated cathode material


The cathode material is lithium magnesium cobaltate (LMCO) having a density of about 5 g/cc and a mean grains size of about 4 μm. As discussed above, properties such as density are factors meaningful to the gravitational settling of particles during self-organization. Grain size is a factor for device stability, with particle size generally being chosen to be less than the device dimension in order to avoid short-circuiting. The LMCO is encapsulated with a mixture of 90 wt % PTFE and 10 wt % PEDT-PSS by spray-drying, providing a conductive coating of about 5 S/cm at a thickness of about 35 nm, representing a volumetric particle loading of about 5%.


A 1.3 wt % aqueous dispersion of PEDT-PSS, (particle size˜30 nm, Baytron-PH, H. C. Starck) is mixed with an aqueous dispersion of PTFE (particle size 0.05-0.35 μm, Zonyl PTFE K-20, DuPont) that has been freed from surfactant by exhaustive dialysis against pure water. A minimum amount of nonionic perfluorinated surfactant is then added to aid final dispersion stability. The PEDT-PSS/PTFE mixture is prepared so that the ratio of solids PEDT-PSS:PTFE is 1:9. The volume of LMCO powder to be added to this mixture is calculated so that the volume ratio of LMCO:(PEDT-PSS+PTFE) is 95:5. A volume of water equal to the calculated volume of LMCO is added to the PEDT-PSS/PTFE mixture to dilute it, and then LMCO is added under high shear mixing to produce a well-dispersed mixture. The resulting mixture has a solids loading of about 50% by volume, with mass ratios of LMCO:PTFE:PEDT-PSS of 95:4.5:0.5. The mixture is spray-dried to form LMCO particles encapsulated with PEDT-PSS/PTFE.


In another experiment, LMCO is encapsulated with a mixture of 90 wt % PTFE and 10 wt % PEDT-PSS by a mechanofusion process. LMCO, water, PEDT-PSS, and PTFE latex are mixed as described above, and the mixture is subjected to a mechanofusion process. In this process, small particles of PTFE and PEDT-PSS are coated onto the surface of the LMCO particles by the force applied to the particles as the mixture is repeatedly passed through a narrow channel in a mechanofusion apparatus. This process also serves to make the particles more uniform in aspect ratio.


Self-Organizing Slurry


The electrolyte is a solid polymer electrolyte including polyethylene oxide (PEO) and lithium perchlorate (LiClO4). In order to promote self-organization, the electrolyte is dissolved in solution to which the solid electrode components are added.


Poly(ethylene oxide) (PEO, 1 g, Polyox® WSR N80, Dow Chemical Co., molecular weight 200,000), is dissolved in 10 ml of acetonitrile by stirring and heating in a closed container for 1 hour at 50° C. Then 0.15 g of anhydrous lithium perchlorate is added to the solution (Li:O ratio 1:16) and stirred until the salt is completely dissolved; then 10 ml of diiodomethane is added. The PEO-Li salt complex solution is used to prepare a casting slurry by adding a predetermined amount of positive and negative active materials.


The anode material, mesocarbon microbeads (MCMB) with a mean grain size of ˜5 μm, and the encapsulated LMCO cathode particles are mixed into the dissolved electrolyte in an anode to cathode capacity ratio of 1.05. The solids loading of the dried sauce is ˜70%. The MCMB is combined with the electrolyte solution and magnetically stirred at ˜70° C. As soon as the MCMB is completely wet, the encapsulated cathode is added. The mixture is magnetically stirred until well mixed at ˜70° C.


EXAMPLE 3

A high surface area interface battery is made using a self-organizing mixture as described in Example 2. The heated self-organizing slurry is fed into a hopper of a stencil printer. Individual battery sections are printed into stencils to provide a final battery stack that is 32 mm wide×48 mm long, with a thickness of 0.1 mm. The slurry is cast on a PEDT-PSS/PTFE-coated cathode collector as described in Example 2. An open mesh anode current collector is placed on top of the stencil. After vacuum curing, the energy density of the resulting symmetric cell about 600 Wh/l. 23 sections are stacked with a thin mylar layer placed between each one, providing a total battery thickness of 2.4 mm. The energy density of the resulting symmetric cell is about 575 Wh/l.


In another experiment, 14 individual sections are stacked with alternating sections flipped, such that the cathode and anode current collectors of adjacent sections are in contact with each other and the total battery thickness is 3.5 mm. The energy density of the resulting symmetric cell is 600 Wh/l.


EXAMPLE 4

A self-organizing mixture as described in Example 2 is formed into a battery using injection molding. The heated mixture is injected at atmospheric pressure into a heated shaped preform with overall dimensions of about 30 mm×50 mm. The preform has three stepped layers. The bottom layer is 28 mm wide×48 mm long×2 mm deep, the middle layer is 30 mm wide×50 mm long×2 mm high, and the top layer is 32 mm wide×52 mm long×2 mm high. Prior to mixture injection, a current collector assembly is placed in the preform in an alternating sequence of coated cathode current collectors and anode current collectors. The current collectors have dimensions that allow them to fit at close tolerance in their respective preform layers. They are held apart at a separation of 2 mm by an inert polymeric fixture. The current collectors are mesh, with a “hard” temper to prevent shorting during mixture injection. After curing at atmospheric pressure, the cells are removed from the preform and the terminals are connected to the exposed collectors at each layer. The energy density of the resulting symmetric cell is 600 Wh/l.


EXAMPLE 5

A battery having an arbitrary form factor, with final dimensions about 2×20×60 mm3 and a patterned lower surface, is made using an injection molding process. A self-organizing mixture as described in Example 2 is injected into a perform having the desired arbitrary form factor. Prior to injection of the self-organizing mixture, a coated cathode current collector is pressed into a conformal shape on the bottom of the lower preform surface. After injection, an expanded metal anode current collector is placed over the mixture. The AC impedance at 1000 Hz is about 125 mΩ and the power density is less than 300 W/kg. The energy density of the final battery is 600 Wh/l, and its capacity is about 390 mAh. The average separation between cathode and anode is about 2 μm.


EXAMPLE 6

An embedded battery is made directly in the casing of a laptop computer using stencil printing, with final dimensions of 1×300×240 mm3. Four sequential stencil prints are carried out, each 0.25 mm thick. Each print is carried out by first depositing a thin coated cathode current collector, printing a self-organizing mixture as described in Example 2, covering the printed mixture with a mesh anode current collector, curing, and covering the anode current collector with a mylar sheet. The four layers are wired in parallel, resulting in a 14.8 V battery. The energy density of the final battery is 600 Wh/l and its capacity is about 2920 mAh. The AC impedance at 1000 Hz is about 2 mΩ and the power density is greater than 4,500 W/kg. The average separation between cathode and anode is 2 μm.


EXAMPLE 7

A self-organized battery is made using tape casting. A heated self-organizing slurry as described in Example 2 is tape cast onto a heated and coated cathode current collector to a thickness of 4 mm and a width of 10 cm. An expanded metal anode current collector is held in position midway through the thickness of the sheet, and extends out either side of the 10 cm wide slab. Midway through the curing process, after the viscosity of the slab has increased and the repulsive forces between anode and cathode are still operative, the slab is cut once length wise and periodically width wise to form cells with dimensions of 5 cm×3 cm. An expanded metal coated cathode current collector is placed on top of each cell. After complete curing, cathode terminals are attached to either side of the cell and an anode terminal is attached to the extended current collector. The energy density of the symmetric cell is 600 Wh/l.


EXAMPLE 8

A battery with final dimensions 6×32×48 mm3 is made according to a tape casting process as described in Example 7. The battery has two expanded metal coated cathode current collectors and two expanded metal anode current collectors. The current collectors are equi-spaced through the thickness of the cell, creating three layers that are each 2 mm thick. The AC impedance at 1000 Hz is ˜31 mΩ and the power density is greater than 300 W/kg. The energy density of the final battery is 600 Wh/l and its capacity is about 1495 mAh. The average separation between cathode and anode is 2 μm.


As will be apparent to one of skill in the art from a reading of this disclosure, the present invention can be embodied in forms other than those specifically disclosed above without departing from the spirit or essential characteristics of the invention. The particular embodiments of the invention described above are, therefore, to be considered as illustrative and not restrictive. The scope of the invention is as set forth in the appended claims, rather than being limited to the examples contained in the foregoing description.

Claims
  • 1. A bipolar article having an arbitrary form factor, the article comprising: (a) a bipolar structure having an anode, a cathode, and an electrolyte in contact with and separating the anode and cathode, wherein the anode and cathode are interpenetrating; (b) a cathode current collector that is in electronic communication with the cathode; and (c) an anode current collector that is in electronic communication with the anode, wherein the bipolar article has a desired arbitrary configuration.
  • 2. The article of claim 1, wherein the anode and cathode are self-assembling networks of particles disposed in the electrolyte, and wherein the cathode current collector is attractive to the cathode network and repulsive to the anode network, and the anode current collector is attractive to the anode network and repulsive to the cathode network.
  • 3. The article of claim 2, wherein one or both of the anode and cathode current collectors comprises a coating providing a repulsive force between the current collector and the opposite anode or cathode network.
  • 4. The article of claim 3, wherein the coating includes one or more of a conductive oxide, polythiophene, polyanaline, poly(o-methoxyaniline) (POMA), poly(3-octylthiophene) (POTh), poly(3,4-ethylene dioxythiophene) (PEDT), poly(3,4 ethylene dioxythiophene)-polystyrene sulfonate (PEDT-PSS), poly(vinylidene fluoride) (PVDF), poly(ethylene oxide) (PEO), polytetrafluoroethylene (PTFE), and derivatives thereof.
  • 5. The article of claim 1, wherein the anode, electrolyte, and cathode are sequentially deposited.
  • 6. A device comprising the bipolar article of claim 1.
  • 7. The device of claim 6, wherein the arbitrary configuration of the bipolar article is conformal with at least one surface of the device.
  • 8. The device of claim 6, wherein the device has a cavity, and wherein the arbitrary configuration of the bipolar article is space-filling within the cavity.
  • 9. The device of claim 6, wherein the device is a cellular telephone, laptop computer, personal digital assistant, or toy.
  • 10. The article of claim 1, wherein the bipolar article is a battery.
  • 11. A bipolar article having an arbitrary form factor, the article comprising: (a) a bipolar structure having an anode, a cathode, and an electrolyte in contact with and separating the anode and cathode; (b) a cathode current collector that is in electronic communication with the cathode; and (c) an anode current collector that is in electronic communication with the anode, wherein the bipolar article has an arbitrary configuration that has a thickness that varies across the length or width of the article.
  • 12. The article of claim 11, wherein the anode and cathode are interpenetrating.
  • 13. The article of claim 12, wherein the anode and cathode are self-assembling networks of particles disposed in the electrolyte, and wherein the cathode current collector is attractive to the cathode network and repulsive to the anode network, and the anode current collector is attractive to the anode network and repulsive to the cathode network.
  • 14. The article of claim 13, wherein one or both of the anode and cathode current collectors comprises a coating providing a repulsive force between the current collector and the opposite anode or cathode network.
  • 15. The article of claim 14, wherein the coating includes one or more of a conductive oxide, polythiophene, polyanaline, poly(o-methoxyaniline) (POMA), poly(3-octylthiophene) (POTh), poly(3,4-ethylene dioxythiophene) (PEDT), poly(3,4 ethylene dioxythiophene)-polystyrene sulfonate (PEDT-PSS), poly(vinylidene fluoride) (PVDF), poly(ethylene oxide) (PEO), polytetrafluoroethylene (PTFE), and derivatives thereof.
  • 16. The article of claim 11, wherein the anode, electrolyte, and cathode are sequentially deposited.
  • 17. A device comprising the bipolar article of claim 11.
  • 18. The device of claim 17, wherein the arbitrary configuration of the bipolar article is conformal with at least one surface of the device.
  • 19. The device of claim 17, wherein the device has a cavity, and wherein the arbitrary configuration of the bipolar article is space-filling within the cavity.
  • 20. The device of claim 17, wherein the device is a cellular telephone, laptop computer, personal digital assistant, or toy.
  • 21. The article of claim 11, wherein the bipolar article is a battery.
  • 22. A battery powered device comprising: (a) an interpenetrating electrode battery; (b) a housing; and (c) a mechanism powered by the battery, wherein the battery is integrated in the housing.
  • 23. The device of claim 22, wherein the battery is formed in a cavity in the housing.
  • 24. The device of claim 22, wherein the battery has interpenetrating electrodes that are formed from a self-organizing bipolar material.
  • 25. The device of claim 22, wherein the battery has interpenetrating electrodes that are sequentially deposited.
  • 26. The device of claim 22, wherein the device is a cellular telephone, laptop computer, personal digital assistant, or toy.
  • 27. A bipolar article comprising: (a) first and second interpenetrating electrodes; (b) a plurality of first interpenetrating current collector features wired in parallel and in electronic communication with the first interpenetrating electrode; and (c) a second current collector in electronic communication with the second interpenetrating electrode, wherein the plurality of first interpenetrating current collector features is distributed through the thickness of the article.
  • 28. The article of claim 27, wherein the interpenetrating current collector features comprise prongs at least partially embedded in the first electrode.
  • 29. The article of claim 27, wherein the interpenetrating current collector features comprise a mesh.
  • 30. The article of claim 29, wherein the mesh defines a plurality of openings, each opening having a width greater than about 200 μm.
  • 31. The article of claim 27, wherein the interpenetrating current collector features are distributed through the thickness of the article with a spacing between adjacent current collector features that is selected to reduce the electronic transport path length within the bipolar article to provide increased power density of the article.
  • 32. The article of claim 27, wherein the interpenetrating current collector features are distributed through the thickness of the article with a spacing between adjacent current collector features that is selected to increase the volume percentage of electrode material in the article to provide increased energy density of the article.
  • 33. The article of claim 27, wherein the second current collector includes interpenetrating features distributed throughout the thickness of the article.
  • 34. The article of claim 33, wherein the interpenetrating features comprise prongs.
  • 35. The article of claim 27, wherein at least one of the interpenetrating electrodes is a porous electrode.
  • 36. The article of claim 27, wherein the interpenetrating electrodes are formed from a self-organizing bipolar material.
  • 37. The article of claim 27, wherein the interpenetrating electrodes are sequentially deposited.
  • 38. The article of claim 27, having a power density greater than about 300 W/kg.
  • 39. A bipolar article comprising: (a) a bipolar structure having an anode, a cathode, and an electrolyte in contact with and separating the anode and the cathode, wherein at least one of the anode and the cathode includes a lithium-containing electroactive material; (b) a cathode current collector that is in electronic communication with the cathode; and (c) an anode current collector that is in electronic communication with the anode, wherein at least one of the anode and cathode current collectors includes one or more features projecting into the bipolar structure containing the anode and the cathode, and wherein the minimum distance between adjacent current collectors is at least about 500 μm.
  • 40. The article of claim 39, wherein the minimum distance between adjacent current collectors is at least about 750 μm.
  • 41. The article of claim 39, wherein the minimum distance between adjacent current collectors is at least about 1000 μm.
  • 42. The article of claim 39, wherein both the anode and cathode current collectors include projecting features.
  • 43. The article of claim 42, wherein the projecting features are prongs.
  • 44. The article of claim 39, wherein the projecting feature is a mesh.
  • 45. The article of claim 44, wherein the mesh layer defines a plurality of openings, each opening having a width greater than about 200 μm.
  • 46. The article of claim 44, including multiple layered meshes electrically wired in parallel.
  • 47. The article of claim 39, wherein the anode includes one or more materials selected from the group consisting of carbon, amorphous carbon, graphite, mesocarbon microbeads, Li, LiAl, Li9Al4, Li3Al, Zn, LiZn, Ag, LiAg, Li10Ag3, B, Li5B4, Li7B6, Ge, Si, Li12Si7, Li21Si8, Li13Si4, Li21Si5, Sn, Li5Sn2, Li13Sn5, Li7Sn2, Li22Sn5, Sb, Li2Sb, Li3Sb, Bi, LiBi, and Li3Bi, SnO2, SnO, MnO, Mn2O3, MnO2, Mn3O4, CoO, NiO, FeO, LiFe2O4, TiO2, LiTi2O4, and glass.
  • 48. The article of claim 39, wherein the cathode includes one or more materials selected from the group consisting of LiCoO2, LiCoO2 doped with Mg, LiNiO2, LiMn2O4, LiMnO2, LiMnO2 doped with Al, doped and undoped LiFePO4, LiMnPO4, LixV6O13, Li2Fe2(SO4)3, V2O5, V6O11, and SnO2.
  • 49. The article of claim 39, wherein the anode and cathode are self-assembling networks of particles disposed in the electrolyte, and wherein the cathode current collector is attractive to the cathode network and repulsive to the anode network, and the anode current collector is attractive to the anode network and repulsive to the cathode network.
  • 50. The article of claim 49, wherein one or both of the anode and cathode current collectors comprises a coating providing a repulsive force between the current collector and its respective anode or cathode network.
  • 51. The article of claim 50, wherein the coating includes one or more of a conductive oxide, polythiophene, polyanaline, poly(o-methoxyaniline) (POMA), poly(3-octylthiophene) (POTh), poly(3,4-ethylene dioxythiophene) (PEDT), poly(3,4 ethylene dioxythiophene)-polystyrene sulfonate (PEDT-PSS), poly(vinylidene fluoride) (PVDF), poly(ethylene oxide) (PEO), polytetrafluoroethylene (PTFE), and derivatives thereof.
  • 52. The article of claim 39, wherein the electrolyte is selected from the group consisting of LiI, LiF, LiCl, Li2O—B2O3—Bi2O3 compounds, Li2O—B2O3—P2O5 compounds, Li2O—B2O3—PbO compounds, and sols and gels of oxides and hydroxides of Ti, Zr, Pb, and Bi.
  • 53. The article of claim 39, wherein the electrolyte is selected from the group consisting of poly(ethylene oxide) (PEO), poly(styrene) (PS), poly(acrylonitrile) (PAN), poly(vinylidene fluoride) (PVDF), diiodomethane (DIM), 1,3-diiodopropane, N,N-dimethylformamide (DMF), dimethylpropylene urea (DMPU), ethylene carbonate (EC), diethylene carbonate (DEC), dimethyl carbonate (DMC), propylene carbonate (PC), and block copolymer lithium electrolytes, the material being doped with a lithium salt to provide lithium ionic conductivity.
  • 54. The article of claim 39, wherein at least one of the anode and cathode is a porous electrode.
  • 55. The article of claim 39, wherein the anode, electrolyte, and cathode are sequentially deposited.
  • 56. The article of claim 39, having a power density greater than about 300 W/kg.
  • 57. A bipolar article comprising: (a) a porous first electrode; (b) at least one first current collector, wherein at least a portion of the first current collector is embedded within and in electronic communication with the porous first electrode; (c) an electronically insulating, ionically conductive material coating the pore structure of the porous first electrode; (d) within the pores of the coated porous first electrode, a second electrode having opposite polarity to the porous first electrode; and (e) a second current collector in electronic communication with the second electrode.
  • 58. A multi-layered lithium ion battery having an energy density greater than about 212 Wh/kg.
  • 59. A method of making a bipolar article having an arbitrary form factor, the method comprising: (a) providing a first current collector in a mold having a configuration corresponding to the desired arbitrary form factor; (b) depositing on the first current collector a first electrode material, an electrolyte material, and a second electrode material, wherein at least one of the electrode materials is configured to have one or more features projecting into the electrolyte material and the other electrode material; and (c) providing a second current collector on the first electrode, electrolyte, and second electrode materials.
  • 60. The method of claim 59, wherein the first electrode, electrolyte, and second electrode materials are deposited sequentially.
  • 61. The method of claim 59, wherein the first and second electrode and electrolyte materials are deposited by coating, printing, or injection molding.
  • 62. The method of claim 59, further comprising stamping or embossing one of the current collectors or electrode materials to provide a surface having an arbitrary configuration.
  • 63. The method of claim 59, wherein the electrolyte comprises an ionically permeable separator.
  • 64. The method of claim 59, wherein the mold is an electronic device or device housing.
  • 65. The method of claim 59, wherein the first and second electrode and electrolyte materials are included in a self-organizing bipolar material.
  • 66. The method of claim 65, further comprising curing the self-organizing bipolar material.
  • 67. The method of claim 66, wherein curing the self-organizing bipolar material forms cathode and anode networks, and wherein one of the first and second current collectors is attractive to the cathode network and repulsive to the anode network, and the other of the first and second current collectors is attractive to the anode network and repulsive to the cathode network.
  • 68. A bipolar article having an arbitrary form factor made by the method of claim 59.
  • 69. A method of making a bipolar article having an arbitrary form factor including a thickness that varies across the length or width of the article, the method comprising: (a) providing a first current collector in a mold having a configuration corresponding to the desired arbitrary form factor; (b) depositing on the first current collector a first electrode material, an electrolyte material, and a second electrode material; and (c) providing a second current collector on the first electrode material, electrolyte material, and second electrode material, whereby a bipolar article is formed with an arbitrary configuration that has a thickness that varies across the length or width of the article.
  • 70. The method of claim 69, wherein the first electrode, electrolyte, and second electrode materials are deposited sequentially.
  • 71. The method of claim 69, wherein the anode, cathode, and electrolyte materials are deposited by coating, printing, or injection molding.
  • 72. The method of claim 69, wherein the electrolyte comprises an ionically permeable separator.
  • 73. The method of claim 69, wherein the mold is an electronic device or device housing.
  • 74. The method of claim 69, wherein at least one of the electrode materials is configured to have one or more features projecting into the electrolyte material and the other electrode material.
  • 75. A bipolar article having an arbitrary form factor made by the method of claim 69.
  • 76. A method of making a layered interpenetrating bipolar article, the method comprising: (a) providing a first current collector; (b) depositing on the first current collector an electrode region comprising an interpenetrating network including an anode material, an electrolyte material, and a cathode material; (c) providing a second current collector on the electrode region; (d) repeating steps (a) through (c) at least once; and (e) electrically connecting the first current collectors with each other and with one of the anode or cathode materials, and electrically connecting the second current collectors with each other and with the other of the anode or cathode materials.
  • 77. The method of claim 76, wherein steps (a) through (c) are repeated between about two times and about ten times.
  • 78. The method of claim 76, wherein the anode, electrolyte, and cathode materials are deposited sequentially.
  • 79. The method of claim 76, wherein the anode, electrolyte, and cathode materials are provided in a self-organizing bipolar material.
  • 80. An interpenetrating bipolar article made by the method of claim 76.
  • 81. A method of making an interpenetrating bipolar article, the method comprising: (a) providing a first current collector having at least one prong; (b) depositing on the first current collector an electrode region comprising an interpenetrating network including an anode material, an electrolyte material, and a cathode material, whereby the prong of the first current collector extends into one of the anode and cathode materials; and (c) providing a second current collector on the electrode region.
  • 82. The method of claim 81, wherein the anode material, the electrolyte material, and the cathode material are deposited sequentially.
  • 83. The method of claim 81, wherein the anode, cathode, and electrolyte materials are provided in a self-organizing bipolar material.
  • 84. An interpenetrating bipolar article made by the method of claim 81.
  • 85. A method of making an interpenetrating bipolar article, the method comprising: (a) assembling a mold containing a first current collector; (b) suspending a plurality of second current collector mesh layers above the first current collector in the mold; (c) introducing a self-organizing bipolar material to the mold, thereby covering the first and second current collectors with the self-organizing bipolar material; and (d) curing the self-organizing bipolar material to form interpenetrating anode and cathode networks separated by an intervening electrolyte, wherein one of the anode and cathode networks is attractive to the first current collector and repulsive to the second current collector, and the other of the anode and cathode networks is attractive to the second current collector and repulsive to the first current collector.
  • 86. The method of claim 85, further comprising providing a spacing between adjacent second current collector mesh layers of at least about 500 μm.
  • 87. The method of claim 86, wherein the spacing provided between adjacent second current collector mesh layers is least about 750 μm.
  • 88. The method of claim 86, wherein the spacing provided between adjacent second current collector mesh layers is least about 1000 μm.
  • 89. The method of claim 85, wherein each second current collector mesh layer defines a plurality of openings, each opening having a width greater than about 200 μm.
  • 90. An interpenetrating bipolar article made by the method of claim 85.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to U.S. Provisional Application Nos. 60/398,902 and 60/399,050, both filed on Jul. 26, 2002.

Provisional Applications (2)
Number Date Country
60398902 Jul 2002 US
60399050 Jul 2002 US