BIPOLAR PLATE AND FUEL CELL

Abstract

A bipolar plate and a fuel cell are provided. The bipolar plate for the fuel cell has a plurality of flow channels, and a rib is defined between neighboring two flow channels. A top surface of the rib may be a roughened surface or have a porous structure in order to improve performance of the fuel cell.

Description

CROSS-REFERENCE TO RELATED APPLICATION

This application claims the priority benefit of Taiwan application serial no. 100147421, filed on Dec. 20, 2011. The entirety of the above-mentioned patent application is hereby incorporated by reference herein and made a part of this specification.

TECHNICAL FIELD

The technical field relates to a bipolar plate capable of improving performance of a fuel cell and a fuel cell having the bipolar plate.

BACKGROUND

As shown in FIG. 1A, a fuel cell is generally composed of a bipolar plate 100 with a membrane electrode assembly 102 in between. The bipolar plate 100 is generally made of a graphite material or a metallic material, and the bipolar plate 100 may have a plurality of flow channels 100a after mechanical processing (including milling, punching, stamping, . . . etc.) or chemical processing (including etching, electroplating . . . etc.). The flow channels 100a are used for fuel (e.g., hydrogen and oxygen) transportation. Hence, the length, the sectional shape, and the size of the flow channels 100a may affect electrochemical reaction in the membrane electrode assembly 102, and further affects the overall electricity generation efficiency of the fuel cell. In addition to the flow channels 100a, the majority of the bipolar plate 100 further includes a plurality of ribs 104. The ribs 104 are used for supporting the membrane electrode assembly 102, and transferring electrons during the electrochemical reaction of the fuel cell.

FIG. 1B merely illustrates a portion where the rib 104 depicted in FIG. 1A is in contact with the membrane electrode assembly 102, wherein the membrane electrode assembly 102 includes a gas diffusion layer (GDL) 106, a catalyst 108, and a membrane 110. Since the rib 104 is generally made of a graphite material or a metallic material, the fuel may not be able to pass through the ribs 104; thus, the fuel may diffuse only within areas 112. In this case, the catalyst 108 within the overlap between the rib 104 and thereof may be lack of fuel; thereby, the electrochemical reactions of the catalyst 108 may be blocked, the effective utilization of the catalyst 108 may be decrease, and the material of the fuel-lacking area may be degraded.

SUMMARY

One of exemplary embodiments comprises a bipolar plate for a fuel cell. The bipolar plate has a plurality of flow channels, wherein a rib is defined between neighboring two of the flow channels, and a top surface of the rib is a roughened surface.

One of exemplary embodiments comprises a bipolar plate for a fuel cell. The bipolar plate has a plurality of flow channels, wherein a rib is defined between neighboring two of the flow channels, and a top portion of the rib has a porous structure.

One of exemplary embodiments comprises a fuel cell including a plurality of bipolar plates and at least one membrane electrode assembly (MEA). The bipolar plates have the porous structure on the top surfaces of the ribs, and the MEA is disposed among the bipolar plates. The porous structure is compressed in contact with the MEA.

Several exemplary embodiments accompanied with figures are described in detail below to further describe the disclosure in details.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide further understanding, and are incorporated in and constitute a part of this specification. The drawings illustrate exemplary embodiments and, together with the description, serve to explain the principles of the disclosure.

FIG 1A is a cross-sectional view of a conventional fuel cell.

FIG. 1B is an enlarged partial view of FIG. 1A.

FIG. 2 is a schematic cross-sectional view of a bipolar plate for a fuel cell according to a first exemplary embodiment.

FIG. 3 is a schematic cross-sectional view of a bipolar plate for a fuel cell according to a second exemplary embodiment.

FIG. 4 is a schematic cross-sectional view of a fuel cell according to a third exemplary embodiment.

FIG. 5A is a SEM picture of a bipolar plate in Reference Experiment.

FIG. 5B is a SEM picture of a bipolar plate in Experiment 1.

FIG. 5C is a SEM picture of a bipolar plate in Experiment 2.

FIG. 5D is a SEM picture of a bipolar plate in Experiment 3.

FIG. 6 is a polarization curve diagram of the fuel cells respectively using each of the bipolar plates provided in Reference Experiment and the Experiments on conditions of cell temperature at 66° C., the temperature of humidification being 60° C. at anode, and the temperature of humidification being 55° C. at cathode.

FIG. 7 is a polarization curve diagram of the fuel cells respectively using each of the bipolar plates provided in Reference Experiment and the Experiments on conditions of fuels with 65% RH and cell temperature at 70° C.

DETAILED DESCRIPTION OF DISCLOSED EMBODIMENTS

FIG. 2 is a schematic cross-sectional view of a bipolar plate for a fuel cell according to a first exemplary embodiment.

With reference to FIG. 2, a bipolar plate 200 of the first exemplary embodiment has a plurality of flow channels 200a, wherein a rib 202 is defined between neighboring two of the flow channels 200a, and a top surface of the rib 202 is a roughened surface 202a. Further, if a pore diameter of the roughened surface 202a of the rib 202 is approximately between 20 μm and 200 μm, the fuel supply (lateral diffusion) capacity may be increased to improve overall performance of the fuel cell.

In the first exemplary embodiment, if a pore area fraction of the roughened surface 202a of the rib 202 is approximately between 50% and 90%, the fuel supply capacity may also be increased. The so-called “pore area fraction” is the result of the following formula:

A _P/(A_R+A_P)×100%

, wherein A_R denotes the area of the top surface of the rib 202; A_P denotes the pore area of the roughened surface 202a of the rib 202.

In addition, in the first exemplary embodiment, if roughness of the roughened surface 202a of the rib 202 is approximately between 0.1 μm and 10 μm, the fuel supply capacity may also be increased to improve the overall performance of the fuel cell.

A side surface 202b of the rib 202 may be a flat surface but is not limited thereto. The flow channels 200a are generally formed through mechanical processing, so that the bipolar plate 200 is an integral structure.

In the first exemplary embodiment, a material of the bipolar plate 200 may be metal, graphite, or a composite material. For example, the material of the bipolar plate 200 may be metal, such as aluminum, titanium, stainless steel, and so on. A protection film may be formed on all surfaces of the bipolar plate 200 in order to prevent the metal from oxidation. For example, when the bipolar plate 200 is made of titanium, a titanium nitride thin film may be deposited on the surface of the bipolar plate 200 to prevent titanium from oxidation and to maintain the conductivity of titanium.

FIG. 3 is a schematic cross-sectional view of a bipolar plate for a fuel cell according to a second exemplary embodiment.

With reference to FIG. 3, a bipolar plate 300 of the second exemplary embodiment has a plurality of flow channels 300a, wherein a rib 302 is defined between neighboring two of the flow channels 300a. A top portion of the rib 302 has a porous structure 304 with hydrophobicity and a porosity range of, for example, 30%˜80%. The thickness T₀ of the porous structure 304 is approximately 1/10 to 3/10 of the thickness T_r of the rib 302.

In the second exemplary embodiment, the porous structure 304 is composed of a conductive material and a hydrophobic material but is not limited thereto. The conductive material may be, for example, carbon black, graphite, carbon fiber, or metal; the hydrophobic material includes any proper material, such as tetrafluoroethylene and the likes. The addition amount of the hydrophobic material, for example, is less than 60 wt %. The material of the bipolar plate 300 may be referred to as those described in the first exemplary embodiment.

FIG. 4 is a schematic cross-sectional view of a fuel cell according to a third exemplary embodiment, wherein the reference numbers of the second exemplary embodiment are used to denote like or similar elements.

With reference to FIG. 4, the fuel cell of the third exemplary embodiment includes two bipolar plates 300 and a membrane electrode assembly (MEA) 400. The MEA 400 at least includes a membrane 402, a catalyst 404, and a gas diffusion layer (GDL) 406. The MEA 400 between the bipolar plates 300 is in contact with the bipolar plates 300 through the GDL 406. More particularly, a porous structure 304 on a top surface of a rib 302 is compressed in contact with the MEA 400. As such, not only the fuel supply (lateral diffusion) capacity may be increased, but also the conductivity between the rib 302 and the GDL 406 may be ensured. For example, the porosity of the porous structure 304 is in inverse proportion to the compression degree of the porous structure 304. The less the porosity, the greater the compression degree, and vice versa.

The so-called “compression degree” refers to the ratio of (T₀−T_x)/T₀, which is the original thickness T₀ of the porous structure 304 minus the thickness T_x after forming the fuel cell, and divided by the original thickness T₀; for example, the compression degree of the porous structure 304 of the third exemplary embodiment is approximately between 40% and 80%.

Several experiments are described below to prove the efficacy of the above exemplary embodiments.

Reference Experiment

A graphite carbon plate is applied as a bipolar plate, and flow channels are formed on the bipolar plate through mechanical processing. The result is as shown in the SEM picture of FIG. 5A.

Experiment 1

Experiment 1 is similar to Reference Experiment. Namely, a graphite carbon plate is applied as a bipolar plate, except that after the flow channels are formed, the top surface of the rib is roughened through applying surface polishing and ultrasonic cavitation techniques. The result is as shown in the SEM picture of FIG. 5B. Upon comparison of FIG. 5A and FIG. 5B, it is known that the surface of the rib in contact with the MEA may be roughened through applying the surface treatment technique, and the pore diameter thereof is approximately 20 μm.

Experiment 2

Experiment 2 is similar to Reference Experiment. Namely, a graphite carbon plate is applied as a bipolar plate except that after the flow channels are formed, the top surface of the rib is roughened through applying an electrical discharge processing technique. The result is as shown in the SEM picture of FIG. 5C. Upon comparison of FIG. 5A and FIG. 5C, it is known that the surface of the rib in contact with the MEA is roughened through applying the surface treatment technique, and the pore diameter thereof is greater than 50 μm.

Experiment 3

Experiment 3 is similar to Reference Experiment. Namely, a graphite carbon plate is applied as a bipolar plate, except that after the flow channels are formed, the structure of the top portion of the rib is changed to a porous structure through applying a porous material lamination technique. The result of changing the surface portion of the rib is as shown in the SEM picture of FIG. 5D. In view of FIG. 5D, it is known that the porous material structure is composed of conductive carbon powder, carbon fiber, and hydrophobic material. The original porosity of the porous material is approximately 80%, while the hydrophobicity of the porous material is approximately 23%. After forming the fuel cell, the compression degree of the porous material is approximately 50%, while the porosity thereof is approximately 60%.

Measurement 1

Each “pore area fraction” of the bipolar plates is calculated from the SEM pictures of Reference Experiment and Experiments 1 and 2, and the roughness of the roughened surface of the rib of each of the bipolar plates is measured. The result is shown in TABLE 1 below.

	TABLE 1
	Reference	Experiment	Experiment
	Experiment	1	2
Pore area fraction of the	5	63	77
rib surface (%)
Average roughness Ra of the	0.1~0.2	0.4~0.9	3.5~4.2
rib surface (μm)

Measurement 2

Each of the bipolar plates provided in Reference Experiment and Experiments 1-3 is composed together with a MEA to form single cells, and a performance test is carried out on each of the single cells.

FIG. 6 is a polarization curve diagram of the fuel cells respectively using each of the bipolar plates provided in Reference Experiment and the Experiments under a humidified environment, in which the temperature of cell is 66° C., the temperature of anodic humidification is 60° C. and the temperature of cathodic humidification is 55° C. In view of FIG. 6, it is apparent that the performance of the fuel cells in Experiments 1-3 is better than that in Reference Experiment.

FIG. 7 is a polarization curve diagram of the fuel cells respectively using each of the bipolar plates provided in Reference Experiment and the Experiments on conditions of fuels with 65% RH and cell temperature at 70° C. It is also apparent that the performance of the fuel cells in Experiments 1-3 is better than that in Reference Experiment.

In view of the above, the disclosure utilizes surface structure processing technique to roughen the surface of the rib and to form the porous structure thereof, so as to respectively improve transmission of electrons (by reducing contact resistance) and enhance the fuel supply (lateral diffusion) capacity. As such, the overall performance of the fuel cell may be improved.

It will be apparent to those skilled in the art that various modifications and variations can be made to the structure of the disclosed embodiments without departing from the scope or spirit of the disclosure. In view of the foregoing, it is intended that the disclosure cover modifications and variations of this disclosure provided they fall within the scope of the following claims and their equivalents.

Claims

1. A bipolar plate for a fuel cell, the bipolar plate comprising a plurality of flow channels, wherein a rib is defined between neighboring two of the flow channels, and the bipolar plate is characterized in that: a top surface of the rib is a roughened surface.

2. The bipolar plate for the fuel cell according to claim 1, wherein the roughened surface of the rib has a pore diameter of approximately 20 μm to 200 μm.

3. The bipolar plate for the fuel cell according to claim 1, wherein the roughened surface of the rib has a pore area fraction of approximately 50% to 90%.

4. The bipolar plate for the fuel cell according to claim 1, wherein the roughened surface of the rib has a roughness of approximately 0.1 μm to 10 μm.

5. The bipolar plate for the fuel cell according to claim 1, wherein a side surface of the rib is a flat surface.

6. The bipolar plate for the fuel cell according to claim 1, wherein a material of the bipolar plate comprises metal, graphite, or a composite material.

7. A bipolar plate for a fuel cell, the bipolar plate having a plurality of flow channels, wherein a rib is defined between neighboring two of the flow channels, and the bipolar plate is characterized in that: a top portion of the rib has a porous structure.

8. The bipolar plate for the fuel cell according to claim 7, wherein the porous structure comprises a conductive material and a hydrophobic material.

9. The bipolar plate for the fuel cell according to claim 8, wherein the conductive material comprises carbon black, graphite, carbon fiber or metal.

10. The bipolar plate for the fuel cell according to claim 8, wherein the hydrophobic material comprises tetrafluoroethylene.

11. The bipolar plate for the fuel cell according to claim 8, wherein an addition amount of the hydrophobic material is less than 60 wt %.

12. The bipolar plate for the fuel cell according to claim 7, wherein the porous structure has a porosity range of approximately 30% to 80% and hydrophobicity.

13. The bipolar plate for the fuel cell according to claim 7, wherein a material of the bipolar plate comprises metal, graphite, or a composite material.

14. A fuel cell, comprising: a plurality of bipolar plates, wherein each of the bipolar plates has a plurality of flow channels, and a rib is defined between neighboring two of the flow channels; andat least one membrane electrode assembly (MEA), disposed among the bipolar plates, wherein a top portion of the rib has a porous structure, and the porous structure is compressed in contact with the membrane electrode assembly.

15. The fuel cell according to claim 14, wherein the porous structure comprises a conductive material and a hydrophobic material.

16. The fuel cell according to claim 15, wherein the conductive material comprises carbon black, graphite, carbon fiber, or metal.

17. The fuel cell according to claim 15, wherein the hydrophobic material comprises tetrafluoroethylene.

18. The fuel cell according to claim 15, wherein an addition amount of the hydrophobic material is less than 60 wt %.

19. The fuel cell according to claim 14, wherein the porous structure has a porosity range of approximately 30% to 80% and hydrophobicity.

20. The fuel cell according to claim 14, wherein a material of the bipolar plate comprises metal, graphite, or a composite material.

21. The fuel cell according to claim 14, wherein the porous structure is compressed in contact with a gas diffusion layer of the membrane electrode assembly.