Embodiments of the present invention relate to a bipolar storage battery.
These days, the number of power generation facilities utilizing natural energy such as sunlight and wind power is increasing. In such a power generation facility, the amount of power generated cannot be controlled, and thus a storage battery is used to level the power load. That is, when the amount of power generated is larger than the consumption, the storage battery is charged with the difference, and when the amount of power generated is smaller than the consumption, the storage battery is discharged of the difference. As the storage battery described above, a lead-acid storage battery is frequently used from the viewpoint of economic efficiency, safety, etc. As such a conventional lead-acid storage battery, for example, one described in Patent Publication No. H06-349519 A is known.
The lead-acid storage battery described in Patent Publication No. H06-349519 A includes bipolar plates each including a positive active material layer and a negative active material layer provided on one surface and the other surface of a conductive metal base material. The bipolar plates are sandwiched between a pair of end plates, and a separator is provided between each pair of adjacent bipolar plates. The lead-acid storage battery used for power storage systems like those described above needs to have life properties of capability of withstanding long-term operation in view of its uses.
Various conditions such as environments in actual operation and performance of storage batteries are different. Therefore, there may be a case where active material is locally used due to various factors such as the potential distribution of the substrate and the concentration difference of the electrolytic solution. If such a state continues, a state called softening occurs, in which the life of the storage battery is shortened, and the life of the storage battery may end early.
Further, the separator sandwiched between the positive active material layer and the negative active material layer facing each other has a role of coming into contact with the positive active material layer and the negative active material layer to bring the electrolytic solution impregnated in the separator into contact with the positive active material layer and the negative active material layer, and also has a role of pressing the positive active material layer and the negative active material layer. In view of such roles of the separator, if the surface pressure applied to the positive active material layer or the negative active material layer by the separator is non-uniform, the holding force of both active material layers is reduced, and a reduction in battery capacity due to peeling of an active material layer may result.
An object of the present invention is to provide a bipolar storage battery in which local use of active material during charging and discharging is suppressed to achieve uniform use of active material in a cell. Even if unevenness in use of active material due to local use occurs, the unevenness can be tolerated to extend the life of the storage battery.
Another object of the present invention is to provide a bipolar storage battery in which the surface pressure applied to an active material layer based on the placement of a separator can be made as uniform as possible to prevent peeling of the active material layer, and the maintenance of battery capacity and an increase in life can be achieved.
A bipolar storage battery according to one aspect of the present invention includes cell members arranged with spacing in a stacked manner, each of the cell members including a positive electrode including a positive current collector and a positive active material layer, a negative electrode including a negative current collector and a negative active material layer, and separators interposed between the positive electrode and the negative electrode, and space-forming members forming a plurality of spaces individually accommodating the plurality of cell members. Each of the space-forming members includes a substrate and a frame body, the substrate covers at least one of a side of the positive electrode or a side of the negative electrode of the cell member, and the frame body surrounds a side surface of the cell member. Each of the plurality of separators has a first surface and a second surface with different surface roughness, and a surface in contact with at least the positive active material layer is a surface having a smaller surface roughness (i.e., a finer surface roughness) than the first surface or the second surface. The positive current collector and the negative current collector may be made of lead or a lead alloy.
Further, a bipolar storage battery according to one aspect of the present invention includes cell members arranged with spacing in a stacked manner, each of the cell members including a positive electrode including a positive current collector and a positive active material layer, a negative electrode including a negative current collector and a negative active material layer, and separators interposed between the positive electrode and the negative electrode, and space-forming members forming a plurality of spaces individually accommodating the plurality of cell members. Each of the space-forming members includes a substrate and a frame body, the substrate covers at least one of a side of the positive electrode or a side of the negative electrode of the cell member, and the frame body surrounds a side surface of the cell member. Each of the plurality of separators has a first surface and a second surface with different surface roughness, and surfaces in contact with the positive active material layer and the negative active material layer are each a surface having a smaller surface roughness than the first surface or the second surface.
According to the present invention, a bipolar storage battery according to one aspect of the present invention includes cell members arranged with spacing in a stacked manner, each of the cell members including a positive electrode including a positive current collector and a positive active material layer, a negative electrode including a negative current collector and a negative active material layer, and separators interposed between the positive electrode and the negative electrode, and space-forming members forming a plurality of spaces individually accommodating the plurality of cell members. Each of the space-forming members includes a substrate and a frame body, the substrate covers at least one of a side of the positive electrode or a side of the negative electrode of the cell member, and the frame body surrounds a side surface of the cell member. Each of the plurality of separators has a first surface and a second surface with different surface roughness, and surfaces in contact with the positive active material layer and the negative active material layer are each a surface having a smaller surface roughness than the first surface or the second surface. By adapting such a configuration, local use of active material during charging and discharging can be suppressed to achieve uniform use of active material in a cell. Even if unevenness in use of active material due to local use occurs, the unevenness can be tolerated to extend the life of the storage battery.
Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings. Note that the embodiments described below illustrate an example of the present invention. In addition, various changes or improvements can be added to the embodiments, and a mode to which such changes or improvements are added can also be included in the present invention. These embodiments and modifications thereof are included in the scope and gist of the invention and are included in the scope of the invention described in the claims and its equivalents. Note that, hereinafter, a lead-acid storage battery will be described as an example from among various storage batteries.
Overall Configuration
First, an overall configuration of a bipolar lead-acid storage battery in an embodiment of the present invention is described.
As illustrated in
Here, although
In the following, as illustrated in
The cell member 110 includes a positive electrode 111, a negative electrode 112, and a separator 113 (also called an electrolyte layer). The positive electrode 111 includes positive lead foil 111a and a positive active material layer 111b. The negative electrode 112 includes negative lead foil 112a and a negative active material layer 112b.
The separator 113 is impregnated with an electrolytic solution. The separator 113 is interposed between the positive electrode 111 and the negative electrode 112. In the cell member 110, the positive lead foil 111a, the positive active material layer 111b, the separator 113, the negative active material layer 112b, and the negative lead foil 112a are stacked in this order.
In the bipolar lead-acid storage battery 100 in the embodiment of the present invention, the separator 113 is composed of a plurality of sheets. Specifically, the separator 113 in the embodiment of the present invention is composed of two separators (i.e., a first separator 113A and a second separator 113B). In the following, when collectively describing these two separators, they are each referred to as a “separator 113” as above.
The first separator 113A and the second separator 113B have a first surface and a second surface, respectively. The surfaces constituting each of the separators 113 is in contact with the positive active material layer 111b or the negative active material layer 112b, or adjacent separators 113 are in contact each other. The two surfaces are formed to have different surface roughness.
A surface with small surface roughness is a fine surface (i.e., a finer surface roughness), and a surface with large surface roughness is a rough surface (i.e., a rougher surface roughness). In the separator 113 in the embodiment of the present invention, there is a difference in surface roughness between the first surface and the second surface described above. That is, of the first surface and the second surface, one is a surface with small surface roughness, and the other is a surface with large surface roughness.
Note that in the following description, for convenience of description, a surface with small surface roughness is referred to as a “first surface”, and a surface with large surface roughness is referred to as a “second surface”. The relationships among the first surface, the second surface, and the difference in surface roughness are merely for convenience, and a surface with large surface roughness can be referred to as the first surface, as a matter of course.
In the embodiment of the present invention, a surface where the separator 113 in the bipolar lead-acid storage battery 100 is in contact with the positive active material layer 111b or the negative active material layer 112b is the first surface with small surface roughness. Therefore, for example, in the case where the first separator 113A and the second separator 113B are provided as the separator 113, in each separator 113, the first surfaces with small surface roughness of the separators are in contact with the positive active material layer 111b and the negative active material layer 112b.
In this case, the second surfaces with large surface roughness of the first separator 113A and the second separator 113B are placed in positions facing each other. Therefore, the second surface of the first separator 113A and the second surface of the second separator 113B are in contact with each other.
This point will now be described using
The first surface 113Aa of the first separator 113A is in contact with the positive active material layer 111b in a facing manner. On the other hand, the first surface 113Ba of the second separator 113B is in contact with the negative active material layer 112b in a facing manner. As a result, the second surface 113Ab of the first separator 113A and the second surface 113Bb of the second separator 113B are in contact with each other in a facing manner.
Although herein a description is given using an example in which two separators of the first separator 113A and the second separator 113B are provided as an example of a plurality of separators 113, the number of separators 113 is not limited to two and may be, for example, three or more.
Also, a case where one separator 113 is bent and placed between the positive active material layer 111b and the negative active material layer 112b is treated as the case where a plurality of separators 113 are provided. That is, for example, bending originally one separator 113 in half creates the same state as a case where two different separators are stacked. The bending in this case is performed such that the second surface with large surface roughness is on the inside. When bending is performed in this manner, the first surface with small surface roughness is exposed on the side exposed to the front, and the second surfaces are in contact with each other in a facing manner. Then, the first surfaces exposed to the front are in contact individually with the positive active material layer 111b and the negative active material layer 112b.
The dimensions in the X-direction and the Y-direction of the positive lead foil 111a are larger than the dimensions in the X-direction and the Y-direction of the positive active material layer 111b. Similarly, the dimensions in the X-direction and the Y-direction of the negative lead foil 112a are larger than the dimensions in the X-direction and the Y-direction of the negative active material layer 112b. For the dimension in the Z-direction (e.g., a thickness), the positive lead foil 111a is larger (thicker) than the negative lead foil 112a, and the positive active material layer 111b is larger (thicker) than the negative active material layer 112b.
The plurality of cell members 110 are arranged with spacing in a stacked manner in the Z-direction, and substrates 121 of the bipolar plates 120 are arranged in the portions of spacing. That is, the plurality of cell members 110 are stacked in a state where the substrate 121 of a bipolar plate 120 is sandwiched between cell members 110.
Thus, the plurality of bipolar plates 120, the first end plate 130, and the second end plate 140 are space-forming members for forming a plurality of spaces C (also called cells) individually accommodating the plurality of cell members 110.
That is, the bipolar plate 120 is a space-forming member including a substrate 121 covering both the positive electrode side and the negative electrode side of cell members 110 and having a rectangular planar shape and a frame body 122 surrounding side surfaces of the cell members 110 and covering the four end surfaces of the substrate 121.
As illustrated in
The substrate 121, the frame body 122, and the column 123 that constitute the bipolar plate 120 are integrally formed of, for example, a thermoplastic resin. Examples of the thermoplastic resin forming the bipolar plate 120 include acrylonitrile-butadiene-styrene copolymer (ABS) resin and/or polypropylene. These thermoplastic resins are excellent in moldability and in sulfuric acid resistance. Hence, even when the electrolytic solution comes into contact with the bipolar plate 120, decomposition, deterioration, corrosion, and the like hardly occur in the bipolar plate 120.
In the Z-direction, the dimension of the frame body 122 is larger than the dimension (e.g., thickness) of the substrate 121, and the dimension between the protrusion end surfaces of the column 123 is the same as the dimension of the frame body 122. The plurality of bipolar plates 120 are stacked such that frame bodies 122 and columns 123 are in contact with each other, and thereby a space C is formed between a substrate 121 and a substrate 121. The dimension in the Z-direction of the space C is held by columns 123 in contact with each other.
Through holes 111c, 111d, 112c, 112d, and 113a allowing the column 123 to penetrate are formed in the positive lead foil 111a, the positive active material layer 111b, the negative lead foil 112a, the negative active material layer 112b, and the separator 113, respectively.
The substrate 121 of the bipolar plate 120 has a plurality of through holes 121a penetrating the plate surface. A first recess 121b is formed on one surface of the substrate 121, and a second recess 121c is formed on the other surface. The depth of the first recess 121b is deeper than the depth of the second recess 121c. The dimensions in the X-direction and the Y-direction of the first recess 121b and the second recess 121c are made to correspond to the dimensions in the X-direction and the Y-direction of the positive lead foil 111a and the negative lead foil 112a.
The substrate 121 of the bipolar plate 120 is placed between adjacent cell members 110 in the Z-direction. The positive lead foil 111a of the cell member 110 is placed in the first recess 121b of the substrate 121 of the bipolar plate 120 via an adhesive layer 150.
On an outer edge portion of the positive lead foil 111a, a cover plate 170 for covering the outer edge portion is provided. The cover plate 170 is a thin plate-shaped frame body and has a rectangular inner shape line and a rectangular outer shape line. An inner edge portion of the cover plate 170 overlaps with an outer edge portion of the positive lead foil 111a, and an outer edge portion of the cover plate 170 overlaps with a peripheral edge portion of the first recess 121b of one surface of the substrate 121.
That is, the rectangle forming the inner shape line of the cover plate 170 is smaller than the rectangle forming the outer shape line of the positive lead foil 111a. Further, the rectangle forming the outer shape line of the cover plate 170 is larger than the rectangle forming the opening plane of the first recess 121b.
The adhesive layer 150 runs around from an end surface of the positive lead foil 111a to an outer edge portion on the opening side of the first recess 121b and is placed between an inner edge portion of the cover plate 170 and an outer edge portion of the positive lead foil 111a. The adhesive layer 150 is placed also between an outer edge portion of the cover plate 170 and one surface of the substrate 121.
That is, the cover plate 170 is fixed by the adhesive layer 150 over a peripheral edge portion of the first recess 121b of one surface of the substrate 121 and an outer edge portion of the positive lead foil 111a. Thereby, the outer edge portion of the positive lead foil 111a is covered with the cover plate 170 also in a boundary portion with the peripheral edge portion of the first recess 121b.
The negative lead foil 112a of the cell member 110 is placed in the second recess 121c of the substrate 121 of the bipolar plate 120 via an adhesive layer 150. Although not illustrated in
A conduction body 160 is placed in the through hole 121a of the substrate 121 of the bipolar plate 120. Both end surfaces of the conduction body 160 are in contact with and coupled to the positive lead foil 111a and the negative lead foil 112a. That is, the positive lead foil 111a and the negative lead foil 112a are electrically connected by the conduction body 160. As a result, all the plurality of cell members 110 are electrically connected in series.
As illustrated in
The planar shape of the substrate 131 is a rectangle, and the four end surfaces of the substrate 131 are covered with the frame body 132. The substrate 131, the frame body 132, and the column 133 are integrally formed of, for example, the thermoplastic resin described above.
Although the number of columns 133 protruding from one surface of the substrate 131 may be one or more, the number of columns 133 is a number corresponding to the number of columns 123 of the bipolar plate 120 to be brought into contact with the columns 133.
In the Z-direction, the dimension of the frame body 132 is larger than the dimension (e.g., thickness) of the substrate 131, and the dimension between the protrusion end surfaces of the column 133 is the same as the dimension of the frame body 132. The first end plate 130 is stacked such that the frame body 132 and the column 133 are in contact with the frame body 122 and the column 123 of the bipolar plate 120 placed most on the outside (i.e., the positive electrode side).
Thereby, a space C is formed between the substrate 121 of the bipolar plate 120 and the substrate 131 of the first end plate 130. The dimension in the Z-direction of the space C is held by the column 123 of the bipolar plate 120 and the column 133 of the first end plate 130 in contact with each other.
Through-holes 111c, 111d, and 113a allowing the column 133 to penetrate are formed in the positive lead foil 111a, the positive active material layer 111b, and the separator 113 of the cell member 110 placed most on the outside (i.e., the positive electrode side), respectively.
A recess 131b is formed on one surface of the substrate 131 of the first end plate 130. The dimensions in the X-direction and the Y-direction of the recess 131b are made to correspond to the dimensions in the X-direction and the Y-direction of the positive lead foil 111a.
The positive lead foil 111a of the cell member 110 is placed in the recess 131b of the substrate 131 of the first end plate 130 via an adhesive layer 150. Like on the substrate 121 of the bipolar plate 120, the cover plate 170 is fixed to one surface side of the substrate 131 by the adhesive layer 150. Thereby, the outer edge portion of the positive lead foil 111a is covered with the cover plate 170 also in a boundary portion with the peripheral edge portion of the recess 131b.
Further, the first end plate 130 includes a positive electrode terminal, which is not illustrated in
The second end plate 140 is a space-forming member including a substrate 141 covering the negative electrode side of the cell member 110 and a frame body 142 surrounding a side surface of the cell member 110. Further, the second end plate 140 includes a column 143 vertically protruding from one surface of the substrate 141 (e.g., a surface facing the substrate 121 of the bipolar plate 120 placed most on the negative electrode side).
The planar shape of the substrate 141 is a rectangle, and the four end surfaces of the substrate 141 are covered with the frame body 142. The substrate 141, the frame body 142, and the column 143 are integrally formed of, for example, the thermoplastic resin described above. Although the number of columns 143 protruding from one surface of the substrate 141 may be one or more, the number of columns 143 is a number corresponding to the number of columns 123 of the bipolar plate 120 to be brought into contact with the columns 143.
In the Z-direction, the dimension of the frame body 142 is larger than the dimension (e.g., the thickness) of the substrate 131, and the dimension between the protrusion end surfaces of the two column 143 is the same as the dimension of the frame body 142. The second end plate 140 is stacked such that the frame body 142 and the column 143 are in contact with the frame body 122 and the column 123 of the bipolar plate 120 placed most on the outside (i.e., the negative electrode side).
Thereby, a space C is formed between the substrate 121 of the bipolar plate 120 and the substrate 141 of the second end plate 140. The dimension in the Z-direction of the space C is held by the column 123 of the bipolar plate 120 and the column 143 of the second end plate 140 in contact with each other.
Through-holes 112c, 112d, and 113a allowing the column 143 to penetrate are formed in the negative lead foil 112a, the negative active material layer 112b, and the separator 113 of the cell member 110 placed most on the outside (i.e., the negative electrode side), respectively.
A recess 141b is formed on one surface of the substrate 141 of the second end plate 140. The dimensions in the X-direction and the Y-direction of the recess 141b are made to correspond to the dimensions in the X-direction and the Y-direction of the negative lead foil 112a.
The negative lead foil 112a of the cell member 110 is placed in the recess 141b of the substrate 141 of the second end plate 140 via an adhesive layer 150. Further, the second end plate 140 includes a negative electrode terminal, which is not illustrated in
Here, when joining facing bipolar plates 120, the first end plate 130, and the facing bipolar plate 120, or the second end plate 140 and the facing bipolar plate 120, for example, various welding methods such as vibration welding, ultrasonic welding, and hot plate welding can be employed. Among the welding methods, vibration welding is performed by vibrating surfaces to be joined while pressurizing the surfaces at the time of joining and has a fast cycle of welding and good reproducibility. Therefore, vibration welding is more preferably used.
The objects to be welded include not only frame bodies placed in facing positions on facing bipolar plates 120, the first end plate 130, and the second end plate 140 but also the columns.
Although not illustrated in the drawing, a notch forming an injection hole for introducing an electrolytic solution into the space C is formed in one of the four end surfaces of the frame body. For example, in the case where notches are formed on a side surface of the frame body existing on the right side in the drawing, the notches have shapes penetrating the frame body in the X-direction and recessed in semicircular arc shapes from both end surfaces in the Z-direction of the frame body. The notch does not participate in the joint structure described above, and when the joint structure described above is being formed by vibration welding, a circular injection hole is formed by facing notches.
Manufacturing Method
The bipolar lead-acid storage battery 100 of this embodiment can be manufactured by, for example, a method including the steps described below.
Step of Producing Bipolar Plate Equipped with Positive Lead Foil and Negative Lead Foil
First, the substrate 121 of the bipolar plate 120 is put on a work table with the first recess 121b side faced upward. The adhesive 150 is applied to the first recess 121b, and the positive lead foil 111a is put in the first recess 121b. At this time, the column 123 of the bipolar plate 120 is passed through the through hole 111c of the positive lead foil 111a. The adhesive 150 is cured to attach the positive lead foil 111a to one surface of the substrate 121.
Next, the substrate 121 is put on the work table with the second recess 121c side faced upward, and the conduction body 160 is inserted into the through hole 121a. Then, the adhesive 150 is applied to the second recess 121c, and the negative lead foil 112a is put in the second recess 121c. At this time, the column 123 of the bipolar plate 120 is passed through the through hole 112c of the negative lead foil 112a. The adhesive 150 is cured to attach the negative lead foil 112a to the other surface of the substrate 121.
Next, the substrate 121 is put on the work table with the first recess 121b side faced upward. The adhesive 150 is applied onto an outer edge portion of the positive lead foil 111a and the upper surface of the substrate 121 forming an edge portion of the first recess 121b, the cover plate 170 is put on the adhesive 150, and the adhesive 150 is cured. Thereby, the cover plate 170 is fixed over the outer edge portion of the positive lead foil 111a and a portion of the substrate 121 continuing on the outside of the outer edge portion (i.e., a peripheral edge portion of the first recess 121b).
Next, resistance welding is performed to connect the conduction body 160, the positive lead foil 111a, and the negative lead foil 112a. Thus, a bipolar plate 120 equipped with positive lead foil 111a and negative lead foil 112a is obtained. A necessary number of bipolar plates 120 equipped with positive lead foil 111a and negative lead foil 112a are prepared.
Step of Producing End Plate Equipped with Positive Lead Foil
The substrate 131 of the first end plate 130 is put on a work table with the recess 131b side faced upward. The adhesive 150 is applied to the recess 131b, the positive lead foil 111a is put in the recess 131b, and the adhesive 150 is cured. At this time, the column 133 of the end plate 130 is passed through the through hole 111c of the positive lead foil 111a. The adhesive 150 is cured to attach the positive lead foil 111a to one surface of the substrate 131.
Next, the adhesive 150 is applied onto an outer edge portion of the positive lead foil 111a and the upper surface of the substrate 131 forming an edge portion of the recess 131b, the cover plate 170 is put on the adhesive 150, and the adhesive 150 is cured. Thereby, the cover plate 170 is fixed over the outer edge portion of the positive lead foil 111a and a portion of the substrate 131 continuing on the outside of the outer edge portion. Thus, a first end plate 130 equipped with positive lead foil 111a is obtained.
Step of Producing End Plate Equipped with Negative Lead Foil
The substrate 141 of the second end plate 140 is put on a work table with the recess 141b side faced upward. The adhesive 150 is applied to the recess 141b, the negative lead foil 112a is put in the recess 141b, and the adhesive 150 is cured. At this time, the column 143 of the second end plate 140 is passed through the through hole 112c of the negative lead foil 112a. The adhesive 150 is cured to obtain the second end plate 140 with the negative lead foil 112a attached to one surface of the substrate 141.
Step of Stacking and Joining Plates
First, the first end plate 130 to which the positive lead foil 111a and the cover plate 170 are fixed is put on a work table with the positive lead foil 111a faced upward. The positive active material layer 111b is put in the cover plate 170 and is put on the positive lead foil 111a. At this time, the column 133 of the first end plate 130 is passed through the through hole 111d of the positive active material layer 111b. Next, the separators 113 (i.e., the first separator 113A, the second separator 113B) and the negative active material layer 112b are put on the positive active material layer 111b.
Next, on the first end plate 130 in this state, the negative lead foil 112a side of the bipolar plate 120 equipped with positive lead foil and negative lead foil is put to be faced downward. At this time, the column 123 of the bipolar plate 120 is passed through the through hole 113a of the separator 113 and the through hole 112d of the negative active material layer 112b and is put on the column 133 of the first end plate 130. Further, the frame body 122 of the bipolar plate 120 is put on the frame body 132 of the first end plate 130.
In this state, the first end plate 130 is fixed, and vibration welding is performed while the bipolar plate 120 is vibrated in a diagonal direction of the substrate 121. Thereby, the frame body 122 of the bipolar plate 120 is joined onto the frame body 132 of the first end plate 130. Further, the column 123 of the bipolar plate 120 is joined onto the column 133 of the first end plate 130.
As a result, the bipolar plate 120 is joined onto the first end plate 130, and the cell member 110 is placed in the space C formed by the first end plate 130 and the bipolar plate 120. The positive lead foil 111a is exposed on the upper surface of the bipolar plate 120.
Next, the positive active material layer 111b, the separator 113, and the negative active material layer 112b are put in this order on the coupled body thus obtained in which the bipolar plate 120 is joined onto the first end plate 130. After that, another bipolar plate 120 equipped with positive lead foil and negative lead foil is put with the negative lead foil 112a side faced downward.
In this state, the coupled body is fixed, and vibration welding is performed while the other bipolar plate 120 equipped with positive lead foil and negative lead foil is vibrated in a diagonal direction of the substrate 121. This vibration welding step is continually performed until a necessary number of bipolar plates 120 are joined onto the first end plate 130.
Finally, the positive active material layer 111b, the separators 113 (i.e., the first separator 113A, the second separator 113B), and the negative active material layer 112b are put in this order on the uppermost bipolar plate 120 of the coupled body in which all the bipolar plates 120 are joined. Then, the second end plate 140 is further put with the negative lead foil 112a side faced downward.
In this state, the coupled body is fixed, and vibration welding is performed while the second end plate 140 is vibrated in a diagonal direction of the substrate 141. Thereby, the second end plate 140 is joined onto the uppermost bipolar plate 120 of the coupled body in which all the bipolar plates 120 are joined.
Although in the above description a flow of sequentially stacking components from the first end plate 130 toward the second end plate 140 is described, this stacking order may be reversed, and components may be sequentially stacked from the second end plate 140 toward the first end plate 130.
Step of Liquid Injection and Chemical Conversion
In the step of stacking and joining plates described above, a joint structure based on vibration welding of facing surfaces of frame bodies is formed, and a circular injection hole is formed in, for example, the position of each space C on one end surface in the X-direction of the bipolar lead-acid storage battery 100 by notches of the facing frame bodies. A predetermined amount of an electrolytic solution is injected into each space C through the injection hole, and the separator 113 is impregnated with the electrolytic solution. Then, chemical conversion is performed under predetermined conditions, and thereby the bipolar lead-acid storage battery 100 can be produced.
The injection hole may be formed by providing a notch in the frame body in advance as described above or may be formed by using a drill or the like after joining frame bodies.
The present invention will now be described more specifically by showing Examples and Comparative Examples. First, the configuration of a bipolar lead-acid storage battery used as each of Examples and Comparative Examples was set as follows.
That is, the bipolar lead-acid storage battery includes a plurality of cell members each including a positive electrode including a positive active material layer, a negative electrode including a negative active material layer, and an electrolytic layer interposed between the positive electrode and the negative electrode and a plurality of frame units forming a plurality of spaces (also called cells) individually accommodating the plurality of cell members. The frame unit is composed of a substrate surrounding at least one of the positive electrode side and the negative electrode side of the cell member and a frame surrounding the side surface of the cell member. The frame unit is formed of resin.
The cell members and the substrates of the frame units described above are alternately stacked, and the plurality of cell members are electrically connected in series such that the voltage is 12 V. Surfaces of adjacent frame units in contact with each other are joined via a joining material made of metal. A separator is placed in the electrolytic layer described above. As the separator, an Absorptive Glass Mat (AGM) separator manufactured by Nippon Sheet Glass Co., Ltd. was used.
Using a 12-V bipolar lead-acid storage battery like that described above, the capacity test and the life test shown below were performed.
First, a capacity test was performed, and the result of a 10-hour rate capacity test was taken as the battery capacity. The capacity test was performed by putting the battery in a water bath at 25° C.±2° C. As a specific condition, discharging (−4.5 A) is performed at 0.1 C with respect to 45 Ah, which is the rated capacity of the battery. Discharging is performed at a 10-hour rate current until the terminal voltage of the battery drops to 1.8 V/cell, and the discharge duration is recorded. The 10-hour rate capacity was obtained from the discharge current and the discharge duration.
On the other hand, based on the result of the capacity test, a life test was performed in a pattern in which discharging and charging were repeated with the depth of discharge, which is the ratio of the amount of discharge to the discharge capacity, set to 70% with respect to the rated capacity. Specifically, the pattern is as follows.
First, a bipolar lead-acid storage battery in a fully charged state is prepared. The bipolar lead-acid storage battery is discharged at a current value of 0.1 C with respect to the 10-hour rate rated capacity obtained in the capacity test. Because the depth of discharge is set to 70% as described above, the discharge time is set to 7 hours.
Then, constant current-constant voltage (CC-CV) charging is performed. Specifically, charging is performed at a current value of 0.1 C with respect to the 10-hour rate rated capacity, and when the terminal voltage of the battery reaches 2.45 V/cell, constant voltage charging is performed. Then, charging is performed until the amount of charged electricity reaches 104% of the amount of discharged electricity. The discharging and the charging are taken as one cycle, and this cycle is repeated 1000 times.
After that, the bipolar lead-acid storage battery is disassembled to extract the positive active material. The extracted positive active material is washed with water and dried, and the positive active material is divided into four in the up-down direction.
Then, the crystallite size of βPbO2 is found in various sites of the positive active material, and the differences are measured. Because the active material undergoes grain growth in accordance with charging and discharging, if the active material is locally used, grain growth progresses more in this portion, and the crystallite size of βPbO2 increases. Thus, when there is a difference of 100 Å (angstroms) or more in the crystallite size of βPbO2 between sites, it is determined that the active material is locally used, and the determination was set to unsuitable (indicated by “×” in the following table). On the other hand, when a difference of 100 Å (angstroms) or more was not observed, it was determined that the active material was not locally used, and the determination was set to suitable (indicated by “o” in the following table).
The test was performed on two Examples and two Comparative Examples. A difference in these four tests is whether a surface with small surface roughness of the separator is placed in a position facing the positive active material layer or the negative active material layer, or a surface with large surface roughness is placed in a position facing the positive active material layer or the negative active material layer. Table 1 shows the contact surfaces of the separator with the positive active material layer and the negative active material layer, and the determination in the test result.
In Table 1, three items of “PAM facing surface”, “NAM facing surface”, and “determination” are provided. “PAM” among these items indicates a positive active material layer, and “NAM” indicates a negative active material layer. Therefore, the “PAM facing surface” indicates which of a surface with large surface roughness and a surface with small surface roughness of the separator is in contact as a surface facing the positive active material layer. Similarly, the “NAM facing surface” indicates which of a surface with large surface roughness and a surface with small surface roughness of the separator is in contact as a surface facing the negative active material layer.
“Rough” in the items of “PAM facing surface” and “NAM facing surface” indicates a surface with large surface roughness, that is, the second surface in the above description. On the other hand, “fine” indicates a surface with small surface roughness, that is, the first surface in the above description. Therefore, in Example 1, first surfaces of the separator, that is, “fine” surfaces with small surface roughness are in contact with both the positive active material layer and the negative active material layer in a facing manner.
In contrast, for example, in Example 2, a first surface of the separator is in contact as the “PAM facing surface” in a facing manner, whereas a second surface of the separator, that is, a “rough” surface with large surface roughness is in contact as the “NAM facing surface” in a facing manner.
Thus, referring to the four cases of Examples and Comparative Examples shown in Table 1, in Example 1, a surface with small surface roughness, which is a first surface of the separator, is in contact with each of the positive active material layer and the negative active material layer, whereas in Example 2, Comparative Example 1, and Comparative Example 2, a surface with large surface roughness, which is a second surface of the separator, is in contact with either or both of the positive active material layer and the negative active material layer.
In Example 1 and Example 2, a difference of 100 Å (angstroms) or more was not observed in crystallite size between any sites, and therefore the determination was “suitable”. On the other hand, in the two Comparative Examples, a difference of 100 Å (angstroms) or more was observed in crystallite size between sites, and therefore the determination was “unsuitable”.
As is clear from the above test results, the bipolar lead-acid storage battery in the embodiment of the present invention includes a plurality of separators arranged to be sandwiched between a positive active material layer and a negative active material layer, each of the separators having a first surface and a second surface with different surface roughness. Then, the surface to be in contact with each of the positive active material layer and the negative active material layer is set to be a surface having a smaller surface roughness than the first surface or the second surface. Thus, the surface pressure of the separator applied to the active material layer is made uniform. Thereby, the usage rates in various sites of the separator are equalized.
Further, as shown in Example 2, it is recognized that, by employing a configuration in which at least the surface in contact with the positive active material layer is a surface with small surface roughness, the surface pressure of the separator applied to the active material layer is made uniform and the usage rates in various sites of the separator are equalized.
Therefore, in the bipolar lead-acid storage battery, local use of active material during charging and discharging can be suppressed to achieve uniform use of active material in a cell. Further, even if unevenness in use of active material due to local use occurs, the unevenness can be tolerated by making such a setting, and therefore the life of the storage battery can be extended.
Further, by placing a surface with small surface roughness of the separator such that such a surface faces each of the positive active material layer and the negative active material layer or faces at least the positive active material layer, the surface pressure applied to the active material layer based on the placement of the separator can be made as uniform as possible. Therefore, peeling of the active material layer can be prevented, and the maintenance of battery capacity and an increase in life can be achieved.
Furthermore, by placing the separator in the above manner, a portion where surfaces with large surface roughness of the separator are arranged in a facing manner is generated, and therefore the separator layer can be prevented from collapsing during assembly of the bipolar lead-acid storage battery.
A life test was further performed on the basis of the test results shown in Table 1, and the results of the life test are shown in Table 2 below.
In Table 2 above, a total of seven Examples of Examples 3 to 8 in addition to Example 1 described above are shown. In all of these seven Examples, “fine” surfaces with small surface roughness, which are first surfaces of the separator, are in contact with the positive active material layer and the negative active material layer. However, what is different between Examples is the surface roughness of the surfaces of the separator in contact with the positive active material layer and the negative active material layer.
Here, the surface roughness of the separator used in each Example was measured as follows. For the measurement of surface roughness, an image acquired using an apparatus (MXB-2500 REZ) of Hirox Co., Ltd. was subjected to a 3D automatic tiling function of image processing software “HiroxRH-2000” of the same company, Hirox Co., Ltd. The separator to be measured was formed into a flat plate shape of 50 mm×50 mm (=250 mm2). The measurement magnification was set to 200 to 600 times, and the cut-off value (λc) was set to 8.0 to 0.8. At this time, the measurement magnification and the cut-off value are adjusted so that an appropriate measurement result can be obtained by paying attention to the relationship between “surface roughness” and “undulation”. The measurement of the surface roughness of the separator in each of the present Examples and Comparative Examples was performed before the separator was impregnated with an electrolytic solution. However, the measurement may be performed after the separator is impregnated with an electrolytic solution, washed with water, and dried, or may be performed after the storage battery is disassembled to extract the separator and the separator is washed with water and dried.
The result is the ten-point average roughness (Rz) (i.e., surface roughness) of the “fine” surface with small surface roughness shown in Table 2. The larger the value of the surface roughness shown in Table 2 is, the larger the surface roughness is, among surfaces classified as “fine”.
In Table 2, the surfaces of the separator in contact with both the positive active material layer and the negative active material layer of Example 1 are first surfaces, and the surface roughness are each 100 μm (micrometers). On the other hand, in Examples 3 to 8, the value of the surface roughness is smaller than in Example 1.
Therefore, for example, when Example 1 and Example 6 are compared, the surfaces of the separator in contact with the positive active material layer and the negative active material layer are “fine” in both Examples. However, the separator in Example 1 can be said to be “rougher” than the surfaces of the separator in contact with the positive active material layer and the negative active material layer in Example 6.
Then, the crystallite size of βPbO2 is found in various sites of the positive active material in these seven kinds of Examples, and the differences are measured. The determination at this time is based on the premise that a difference of 100 Å (angstroms) or more is not observed in crystallite size between any sites.
That is, none of the Examples has a difference of 100 Å (angstroms) or more in crystallite size between before and after the test. Then, for example, when the determination result of Example 1 is “o”, a case where the above size difference is a still smaller value than the result of Example 1 is indicated by “⊙”.
Referring to Table 2, the determination when the surface roughness of the surfaces of the separator in contact with the positive active material layer and the negative active material layer is “100 μm” (Example 1) is “o”. As shown in Example 6, also when the surface roughness of the surfaces of the separator in contact with the positive active material layer and the negative active material layer is “5 μm”, the determination is similarly “o”.
On the other hand, when both the surface roughness of the surfaces of the separator in contact with the positive active material layer and the negative active material layer are “15 μm or more and 90 μm or less” (Examples 3 to 5), the determination is “⊙”. Further, even when the surface roughness of the separator in contact with the positive active material layer and the negative active material layer are different, if the surface roughness is within the above range of 15 μm or more and 90 μm or less (i.e., between 15 μm and 90 μm, inclusive), the determination is “⊙” (Examples 7 and 8).
From the above test results, in the bipolar lead-acid storage battery, when the surface roughness of the separator placed to be sandwiched between the positive active material layer and the negative active material layer is 15 μm or more and 90 μm or less (i.e., between 15 μm and 90 μm, inclusive), local use of active material during charging and discharging can be suppressed to achieve uniform use of active material in a cell. Further, even if unevenness in use of active material due to local use occurs, the unevenness can be tolerated by making such a setting, and therefore the life of the storage battery can be extended.
Further, when the surface roughness is at least 15 μm or more and 90 μm or less (i.e., between 15 μm and 90 μm, inclusive), even if the values of the surface roughness of the surfaces in contact with the positive active material layer and the negative active material layer are different, the above effect can be similarly obtained.
Note that, as described above, in the embodiments of the present invention, a bipolar lead-acid storage battery has been described as an example. However, when the above description applies also to other storage batteries in which other metals are used instead of lead for current collectors, the application of the above description is not excluded, as a matter of course.
The following is a list of reference signs used in this specification and in the drawings.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2021-053389 | Mar 2021 | JP | national |
This application is a continuation of PCT Application No. PCT/JP2021/041940, filed Nov. 15, 2021, the content of which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2021/041940 | Nov 2021 | US |
| Child | 18473907 | US |