Abstract
Embodiments are directed to a catalyst system comprising metal ligand complexes and processes for polyolefin polymerization using the metal ligand complex having the following structure: where each X is selected from the group consisting of —(CH2)SiRX3.
Description
TECHNICAL FIELD

Embodiments of the present disclosure generally relate to olefin polymerization catalyst systems and processes and, more specifically to bis-phenyl-phenoxy polyolefin procatalyst having two methylenetrialkylsilicon ligands on the metal for improved solubility in non-aromatic hydrocarbons.


BACKGROUND

Olefin-based polymers such as polyethylene, ethylene-based polymer, polypropylene, and propylene-based polymer are produced via various catalyst systems. Selection of such catalyst systems used in the polymerization process of the olefin-based polymers is an important factor contributing to the characteristics and properties of such olefin-based polymers.


Polyethylene and polypropylene are manufactured for a wide variety of articles. The polyethylene and polypropylene polymerization process can be varied in a number of respects to produce a wide variety of resultant polyethylene resins having different physical properties that render the various resins suitable for use in different applications. The ethylene monomers and, optionally, one or more co-monomers are present in liquid diluents (such as solvents), such as an alkane or isoalkane, for example isobutene. Hydrogen may also be added to the reactor. The catalyst systems for producing polyethylene may typically comprise a chromium-based catalyst system, a Ziegler-Natta catalyst system, and/or a molecular (either metallocene or non-metallocene (molecular)) catalyst system. The reactants in the diluent and the catalyst system are circulated at an elevated polymerization temperature around the reactor, thereby producing polyethylene homopolymer or copolymer. Either periodically or continuously, part of the reaction mixture, including the polyethylene product dissolved in the diluent, together with unreacted ethylene and one or more optional co-monomers, is removed from the reactor. The reaction mixture, when removed from the reactor, may be processed to remove the polyethylene product from the diluent and the unreacted reactants, with the diluent and unreacted reactants typically being recycled back into the reactor. Alternatively, the reaction mixture may be sent to a second reactor, serially connected to the first reactor, where a second polyethylene fraction may be produced. Despite the research efforts in developing catalyst systems suitable for olefin polymerization, such as polyethylene or polypropylene polymerization, there is still a need to increase the efficiencies of catalyst systems that are capable of producing polymer with high molecular weights and a narrow molecular weight distribution.


SUMMARY

Molecular catalyst systems are not easily solubilized in apolar solvents. Since ethylene and other olefins are polymerized in apolar solvents, a large amount of solvent (or an undesirable solvent, i.e. toluene) is used in order to dissolve a small amount of catalyst. As a result there is an ongoing need to solubilize a catalyst system with a lesser amount of solvent, while maintaining catalyst efficiency, reactivity, and the ability to produce polymers with a high or low molecular weight.


According to some embodiments, a catalyst system may include a metal-ligand complex according to formula (I):




embedded image


In formula (I), M is a metal chosen from titanium, zirconium, or hafnium, the metal being in a formal oxidation state of +2, +3, or +4. Each X is selected from the group consisting of —(CH2)SiRX3, where each RX is independently a (C1-C30)hydrocarbyl and at least one RX is (C2-C30)hydrocarbyl, where any two RX or all three RX are optionally covalently linked; each Z is independently chosen from —O—, —S—, —N(RN)—, or —P(RP)—; R1 and R16 are independently selected from the group consisting of —H, (C1-C40)hydrocarbyl, (C1-C40)heterohydrocarbyl, —Si(RC)3, —Ge(RC)3, —P(RP)2, —N(RN)2, —ORC, —SRC, —NO2, —CN, —CF3, RCS(O)—, RCS(O)2—, —N═C(RC)2, RCC(O)O—, RCOC(O)—, RCC(O)N(R)—, (RC)2NC(O)—, halogen, radicals having formula (II), radicals having formula (III), and radicals having formula (IV):




embedded image


In formulas (II), (III), and (IV), each of R31-35, R41-48, and R51-59 is independently chosen from —H, (C1-C40)hydrocarbyl, (C1-C40)heterohydrocarbyl, —Si(RC)3, —Ge(RC)3, —P(RP)2, —N(RN)2, —ORC, —SRC, —NO2, —CN, —CF3, RCS(O)—, RCS(O)2—, (RC)2C═N—, RCC(O)O—, RCOC(O)—, RCC(O)N(RN)—, (RC)2NC(O)—, or halogen, provided at least one of R1 or R16 is a radical having formula (II), a radical having formula (III), or a radical having formula (IV).


In formula (I), each of R2-4, R5-8, R9-12, and R13-15 is independently selected from —H, (C1-C40)hydrocarbyl, (C1-C40)heterohydrocarbyl, —Si(RC)3, —Ge(RC)3, —P(RP)2, —N(RN)2—ORC, —SRC, —NO2, —CN, —CF3, RCS(O)—, RCS(O)2—, (RC)2C═N—, RCC(O)O—, RCOC(O)—, RCC(O)N(R)—, (RC)2NC(O)—, and halogen. L is (C2-C40)hydrocarbylene or (C2-C40)heterohydrocarbylene; and each RC, RP, and RN in formula (I) is independently a (C1-C30)hydrocarbyl, (C1-C30)heterohydrocarbyl, or —H. The metal-ligand complex according to formula (I) has a solubility greater than the solubility of a comparative complex having a structure according to formula (Ia):




embedded image


In formula (Ia), M, each Z, each R1-16 each R31-35, each R41-48, each R51-59, L, each RC, each RP, and each RN all are identical to corresponding groups of the metal-ligand complex according to formula (I).







DETAILED DESCRIPTION

Specific embodiments of catalyst systems will now be described. It should be understood that the catalyst systems of this disclosure may be embodied in different forms and should not be construed as limited to the specific embodiments set forth in this disclosure. Rather, embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the subject matter to those skilled in the art.


Common abbreviations are listed below:


R, Z, M, X and n: as defined above; Me: methyl; Et: ethyl; Ph: phenyl; Bn: benzyl; i-Pr: iso-propyl; t-Bu: tert-butyl; THF: tetrahydrofuran; Et2O: diethyl ether; CH2Cl2: dichloromethane; C6D6: deuterated benzene or benzene-d6: CDCl3: deuterated chloroform; Na2SO4: sodium sulfate; MgSO4: magnesium sulfate; HCl: hydrogen chloride; n-BuLi: butyllithium; HfCl4: hafnium(IV) chloride; HfBn4: hafnium(IV) tetrabenzyl; ZrCl4: zirconium(IV) chloride; ZrBn4: zirconium(IV) tetrabenzyl; ZrBn2Cl2(OEt2): zirconium (IV) dibenzyl dichloride mono-diethyletherate; HfBn2Cl2(OEt2): hafnium (IV) dibenzyl dichloride mono-diethyletherate; N2: nitrogen gas; PhMe: toluene; PPR: parallel polymerization reactor; MAO: methylaluminoxane; MMAO: modified methylaluminoxane; NMR: nuclear magnetic resonance; mmol: millimoles; mL: milliliters; M: molar; min or mins: minutes; h or hrs: hours; d: days; rpm: revolution per minute; STP: standard pressure and temperature.


The term “independently selected” is used herein to indicate that the R groups, such as, R1, R2, R3, R4, and R5, can be identical or different (e.g., R1, R2, R3, R4, and R5 may all be substituted alkyls or R1 and R2 may be a substituted alkyl and R3 may be an aryl, etc.) A chemical name associated with an R group is intended to convey the chemical structure that is recognized in the art as corresponding to that of the chemical name. Thus, chemical names are intended to supplement and illustrate, not preclude, the structural definitions known to those of skill in the art.


The term “procatalyst” refers to a compound that has catalytic activity when combined with an activator. The term “activator” refers to a compound that chemically reacts with a procatalyst in a manner that converts the procatalyst to a catalytically active catalyst. As used herein, the terms “co-catalyst” and “activator” are interchangeable terms.


When used to describe certain carbon atom-containing chemical groups, a parenthetical expression having the form “(Cx-Cy)” means that the unsubstituted form of the chemical group has from x carbon atoms to y carbon atoms, inclusive of x and y. For example, a (C1-C50)alkyl is an alkyl group having from 1 to 50 carbon atoms in its unsubstituted form. In some embodiments and general structures, certain chemical groups may be substituted by one or more substituents such as RS. An RS substituted chemical group defined using the “(Cx-Cy)” parenthetical may contain more than y carbon atoms depending on the identity of any groups RS. For example, a “(C1-C50)alkyl substituted with exactly one group RS, where RS is phenyl (—C6H5)” may contain from 7 to 56 carbon atoms. Thus, in general when a chemical group defined using the “(Cx-Cy)” parenthetical is substituted by one or more carbon atom-containing substituents RS, the minimum and maximum total number of carbon atoms of the chemical group is determined by adding to both x and y the combined sum of the number of carbon atoms from all of the carbon atom-containing substituents RS.


The term “substitution” means that at least one hydrogen atom (—H) bonded to a carbon atom or heteroatom of a corresponding unsubstituted compound or functional group is replaced by a substituent (e.g. RS). The term “persubstitution” means that every hydrogen atom (H) bonded to a carbon atom or heteroatom of a corresponding unsubstituted compound or functional group is replaced by a substituent (e.g., RS). The term “polysubstitution” means that at least two, but fewer than all, hydrogen atoms bonded to carbon atoms or heteroatoms of a corresponding unsubstituted compound or functional group are replaced by a substituent. The term “—H” means a hydrogen or hydrogen radical that is covalently bonded to another atom. “Hydrogen” and “—H” are interchangeable, and unless clearly specified have identical meanings.


The term “(C1-C50)hydrocarbyl” means a hydrocarbon radical of from 1 to 50 carbon atoms and the term “(C1-C50)hydrocarbylene” means a hydrocarbon diradical of from 1 to 50 carbon atoms, in which each hydrocarbon radical and each hydrocarbon diradical is aromatic or non-aromatic, saturated or unsaturated, straight chain or branched chain, cyclic (having three carbons or more, and including mono- and poly-cyclic, fused and non-fused polycyclic, and bicyclic) or acyclic, and substituted by one or more RS or unsubstituted.


In this disclosure, a (C1-C50)hydrocarbyl may be an unsubstituted or substituted (C1-C50)alkyl, (C3-C50)cycloalkyl, (C3-C20)cycloalkyl-(C1-C20)alkylene, (C6-C40)aryl, or (C6-C20)aryl-(C1-C20)alkylene (such as benzyl (—CH2—C6H5)).


The terms “(C1-C50)alkyl” and “(C1-C18)alkyl” mean a saturated straight or branched hydrocarbon radical of from 1 to 50 carbon atoms and a saturated straight or branched hydrocarbon radical of from 1 to 18 carbon atoms, respectively, that is unsubstituted or substituted by one or more RS. Examples of unsubstituted (C1-C50)alkyl are unsubstituted (C1-C20)alkyl; unsubstituted (C1-C10)alkyl; unsubstituted (C1-C50)alkyl; methyl; ethyl; 1-propyl; 2-propyl; 1-butyl; 2-butyl; 2-methylpropyl; 1,1-dimethylethyl; 1-pentyl; 1-hexyl; 1-heptyl; 1-nonyl; and 1-decyl. Examples of substituted (C1-C40)alkyl are substituted (C1-C20)alkyl, substituted (C1-C10)alkyl, trifluoromethyl, and [C45]alkyl. The term “[C45]alkyl” means there is a maximum of 45 carbon atoms in the radical, including substituents, and is, for example, a (C27-C40)alkyl substituted by one RS, which is a (C1-C5)alkyl, respectively. Each (C1-C5)alkyl may be methyl, trifluoromethyl, ethyl, 1-propyl, 1-methylethyl, or 1,1-dimethylethyl.


The term “(C6-C50)aryl” means an unsubstituted or substituted (by one or more RS) mono-, bi- or tricyclic aromatic hydrocarbon radical of from 6 to 40 carbon atoms, of which at least from 6 to 14 of the carbon atoms are aromatic ring carbon atoms. A monocyclic aromatic hydrocarbon radical includes one aromatic ring; a bicyclic aromatic hydrocarbon radical has two rings; and a tricyclic aromatic hydrocarbon radical has three rings. When the bicyclic or tricyclic aromatic hydrocarbon radical is present, at least one of the rings of the radical is aromatic. The other ring or rings of the aromatic radical may be independently fused or non-fused and aromatic or non-aromatic. Examples of unsubstituted (C6-C50)aryl include: unsubstituted (C6-C20)aryl, unsubstituted (C6-C18)aryl; 2-(C1-C5)alkyl-phenyl; phenyl; fluorenyl; tetrahydrofluorenyl; indacenyl; hexahydroindacenyl; indenyl; dihydroindenyl; naphthyl; tetrahydronaphthyl; and phenanthrene. Examples of substituted (C6-C10)aryl include: substituted (C1-C20)aryl; substituted (C6-C18)aryl; 2,4-bis([C20]alkyl)-phenyl; polyfluorophenyl; pentafluorophenyl; and fluoren-9-one-1-yl.


The term “(C3-C50)cycloalkyl” means a saturated cyclic hydrocarbon radical of from 3 to 50 carbon atoms that is unsubstituted or substituted by one or more RS. Other cycloalkyl groups (e.g., (Cx-Cy)cycloalkyl) are defined in an analogous manner as having from x to y carbon atoms and being either unsubstituted or substituted with one or more RS. Examples of unsubstituted (C3-C40)cycloalkyl are unsubstituted (C3-C20)cycloalkyl, unsubstituted (C3-C10)cycloalkyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, and cyclodecyl. Examples of substituted (C3-C40)cycloalkyl are substituted (C3-C20)cycloalkyl, substituted (C3-C10)cycloalkyl, cyclopentanon-2-yl, and 1-fluorocyclohexyl.


Examples of (C1-C50)hydrocarbylene include unsubstituted or substituted (C6-C50)arylene, (C3-C50)cycloalkylene, and (C1-C50)alkylene (e.g., (C1-C20)alkylene). The diradicals may be on the same carbon atom (e.g., —CH2—) or on adjacent carbon atoms (i.e., 1,2-diradicals), or are spaced apart by one, two, or more than two intervening carbon atoms (e.g., 1,3-diradicals, 1,4-diradicals, etc.). Some diradicals include 1,2-, 1,3-, 1,4-, or an α,ω-diradical, and others a 1,2-diradical. The α,ω-diradical is a diradical that has maximum carbon backbone spacing between the radical carbons. Some examples of (C2-C20)alkylene α,ω-diradicals include ethan-1,2-diyl (i.e. —CH2CH2—), propan-1,3-diyl (i.e. —CH2CH2CH2—), 2-methylpropan-1,3-diyl (i.e. —CH2CH(CH3)CH2—). Some examples of (C6-C50)arylene α,ω-diradicals include phenyl-1,4-diyl, napthalen-2,6-diyl, or napthalen-3,7-diyl.


The term “(C1-C50)alkylene” means a saturated straight chain or branched chain diradical (i.e., the radicals are not on ring atoms) of from 1 to 50 carbon atoms that is unsubstituted or substituted by one or more RS. Examples of unsubstituted (C1-C50)alkylene are unsubstituted (C1-C20)alkylene, including unsubstituted —CH2CH2—, —(CH2)3—, —(CH2)4—, —(CH2)5—, —(CH2)6—, —(CH2)7—, —(CH2)8—, —CH2C*HCH3, and —(CH2)4C*(H)(CH3), in which “C*” denotes a carbon atom from which a hydrogen atom is removed to form a secondary or tertiary alkyl radical. Examples of substituted (C1-C50)alkylene are substituted (C1-C20)alkylene, —CF2—, —C(O)—, and —(CH2)14C(CH3)2(CH2)5— (i.e., a 6,6-dimethyl substituted normal-1,20-eicosylene). Since as mentioned previously two RS may be taken together to form a (C1-C18)alkylene, examples of substituted (C1-C50)alkylene also include 1,2-bis(methylene)cyclopentane, 1,2-bis(methylene)cyclohexane, 2,3-bis(methylene)-7,7-dimethyl-bicyclo[2.2.1]heptane, and 2,3-bis(methylene)bicyclo[2.2.2]octane.


The term “(C3-C50)cycloalkylene” means a cyclic diradical (i.e., the radicals are on ring atoms) of from 3 to 50 carbon atoms that is unsubstituted or substituted by one or more RS.


The term “heteroatom,” refers to an atom other than hydrogen or carbon. Examples of groups containing one or more than one heteroatom include O, S, S(O), S(O)2, Si(RC)2, P(RP), N(RN), —N═C(RC)2—, Ge(RC)—, or —Si(RC)—, where each RC and each RP is unsubstituted (C1-C18)hydrocarbyl or —H, and where each RN is unsubstituted (C1-C18)hydrocarbyl. The term “heterohydrocarbon” refers to a molecule or molecular framework in which one or more carbon atoms of a hydrocarbon are replaced with a heteroatom. The term “(C1-C50)heterohydrocarbyl” means a heterohydrocarbon radical of from 1 to 50 carbon atoms, and the term “(C1-C50)heterohydrocarbylene” means a heterohydrocarbon diradical of from 1 to 50 carbon atoms. The heterohydrocarbon of the (C1-C50)heterohydrocarbyl or the (C1-C50)heterohydrocarbylene has one or more heteroatoms. The radical of the heterohydrocarbyl may be on a carbon atom or a heteroatom. The two radicals of the heterohydrocarbylene may be on a single carbon atom or on a single heteroatom. Additionally, one of the two radicals of the diradical may be on a carbon atom and the other radical may be on a different carbon atom; one of the two radicals may be on a carbon atom and the other on a heteroatom; or one of the two radicals may be on a heteroatom and the other radical on a different heteroatom. Each (C1-C50)heterohydrocarbyl and (C1-C50)heterohydrocarbylene may be unsubstituted or substituted (by one or more RS), aromatic or non-aromatic, saturated or unsaturated, straight chain or branched chain, cyclic (including mono- and poly-cyclic, fused and non-fused polycyclic), or acyclic.


The (C1-C50)heterohydrocarbyl may be unsubstituted or substituted. Non-limiting examples of the (C1-C50)heterohydrocarbyl include (C1-C50)heteroalkyl, (C1-C50)hydrocarbyl-O—, (C1-C50)hydrocarbyl-S—, (C1-C50)hydrocarbyl-S(O)—, (C1-C50)hydrocarbyl-S(O)2—, (C1-C50)hydrocarbyl-Si(RC)2—, (C1-C50)hydrocarbyl-N(RN)—, (C1-C50)hydrocarbyl-P(RP)—, (C2-C50)heterocycloalkyl, (C2-C19)heterocycloalkyl-(C1-C20)alkylene, (C3-C20)cycloalkyl-(C1-C19)heteroalkylene, (C2-C19)heterocycloalkyl-(C1-C20)heteroalkylene, (C1-C50)heteroaryl, (C1-C19)heteroaryl-(C1-C20)alkylene, (C6-C20)aryl-(C1-C19)heteroalkylene, or (C1-C19)heteroaryl-(C1-C20)heteroalkylene.


The term “(C4-C50)heteroaryl” means an unsubstituted or substituted (by one or more RS) mono-, bi-, or tricyclic heteroaromatic hydrocarbon radical of from 4 to 50 total carbon atoms and from 1 to 10 heteroatoms. A monocyclic heteroaromatic hydrocarbon radical includes one heteroaromatic ring; a bicyclic heteroaromatic hydrocarbon radical has two rings; and a tricyclic heteroaromatic hydrocarbon radical has three rings. When the bicyclic or tricyclic heteroaromatic hydrocarbon radical is present, at least one of the rings in the radical is heteroaromatic. The other ring or rings of the heteroaromatic radical may be independently fused or non-fused and aromatic or non-aromatic. Other heteroaryl groups (e.g., (Cx-Cy)heteroaryl generally, such as (C4-C12)heteroaryl) are defined in an analogous manner as having from x to y carbon atoms (such as 4 to 12 carbon atoms) and being unsubstituted or substituted by one or more than one RS. The monocyclic heteroaromatic hydrocarbon radical is a 5-membered ring or a 6-membered ring. The 5-membered ring monocyclic heteroaromatic hydrocarbon radical has 5 minus h carbon atoms, where h is the number of heteroatoms and may be 1, 2, or 3; and each heteroatom may be O, S, N, or P.


Examples of 5-membered ring heteroaromatic hydrocarbon radicals include pyrrol-1-yl; pyrrol-2-yl; furan-3-yl; thiophen-2-yl; pyrazol-1-yl; isoxazol-2-yl; isothiazol-5-yl; imidazol-2-yl; oxazol-4-yl; thiazol-2-yl; 1,2,4-triazol-1-yl; 1,3,4-oxadiazol-2-yl; 1,3,4-thiadiazol-2-yl; tetrazol-1-yl; tetrazol-2-yl; and tetrazol-5-yl. The 6-membered ring monocyclic heteroaromatic hydrocarbon radical has 6 minus h carbon atoms, where h is the number of heteroatoms and may be 1 or 2 and the heteroatoms may be N or P.


Examples of 6-membered ring heteroaromatic hydrocarbon radicals include pyridine-2-yl; pyrimidin-2-yl; and pyrazin-2-yl. The bicyclic heteroaromatic hydrocarbon radical can be a fused 5,6- or 6,6-ring system. Examples of the fused 5,6-ring system bicyclic heteroaromatic hydrocarbon radical are indol-1-yl; and benzimidazole-1-yl. Examples of the fused 6,6-ring system bicyclic heteroaromatic hydrocarbon radical are quinolin-2-yl; and isoquinolin-1-yl. The tricyclic heteroaromatic hydrocarbon radical can be a fused 5,6,5-; 5,6,6-; 6,5,6-; or 6,6,6-ring system. An example of the fused 5,6,5-ring system is 1,7-dihydropyrrolo[3,2-f]indol-1-yl. An example of the fused 5,6,6-ring system is 1H-benzo[f]indol-1-yl. An example of the fused 6,5,6-ring system is 9H-carbazol-9-yl. An example of the fused 6,5,6-ring system is 9H-carbazol-9-yl. An example of the fused 6,6,6-ring system is acrydin-9-yl.


The term “(C1-C50)heteroalkyl” means a saturated straight or branched chain radical containing one to fifty carbon atoms and one or more heteroatom. The term “(C1-C50)heteroalkylene” means a saturated straight or branched chain diradical containing from 1 to 50 carbon atoms and one or more than one heteroatoms. The heteroatoms of the heteroalkyls or the heteroalkylenes may include Si(RC)3, Ge(RC)3, Si(RC)2, Ge(RC)2, P(RP)2, P(RP), N(RN)2, N(RN), N, O, ORC, S, SRC, S(O), and S(O)2, wherein each of the heteroalkyl and heteroalkylene groups are unsubstituted or are substituted by one or more RS.


Examples of unsubstituted (C2-C40)heterocycloalkyl include unsubstituted (C2-C20)heterocycloalkyl, unsubstituted (C2-C10)heterocycloalkyl, aziridin-1-yl, oxetan-2-yl, tetrahydrofuran-3-yl, pyrrolidin-1-yl, tetrahydrothiophen-S,S-dioxide-2-yl, morpholin-4-yl, 1,4-dioxan-2-yl, hexahydroazepin-4-yl, 3-oxa-cyclooctyl, 5-thio-cyclononyl, and 2-aza-cyclodecyl.


The term “halogen atom” or “halogen” means the radical of a fluorine atom (F), chlorine atom (Cl), bromine atom (Br), or iodine atom (I). The term “halide” means anionic form of the halogen atom: fluoride (F), chloride (C), bromide (Br), or iodide (I).


The term “saturated” means lacking carbon-carbon double bonds, carbon-carbon triple bonds, and (in heteroatom-containing groups) carbon-nitrogen, carbon-phosphorous, and carbon-silicon double bonds. Where a saturated chemical group is substituted by one or more substituents RS, one or more double and/or triple bonds optionally may be present in substituents RS. The term “unsaturated” means containing one or more carbon-carbon double bonds or carbon-carbon triple bonds, or (in heteroatom-containing groups) one or more carbon-nitrogen double bonds, carbon-phosphorous double bonds, or carbon-silicon double bonds, not including double bonds that may be present in substituents RS, if any, or in aromatic rings or heteroaromatic rings, if any.


Embodiments of this disclosure include catalyst systems that include a metal-ligand complex according to formula (I):




embedded image


In formula (I), M is a metal chosen from titanium, zirconium, or hafnium, the metal being in a formal oxidation state of +2, +3, or +4. Each X is selected from the group consisting of —(CH2)SiRX3, where each RX is independently a (C1-C30)hydrocarbyl or a (C1-C30)heterohydrocarbyl and at least one RX is (C2-C30)hydrocarbyl, where any two RX or all three RX are optionally covalently linked. The metal-ligand complex has 6 or fewer metal-ligand bonds and can be overall charge-neutral or may have a positive-charge associated with the metal center. Each Z is independently chosen from —O—, —S—, —N(RN)—, or —P(RP)—; selected from oxygen or sulfur.


In embodiments, the catalyst system may include a metal-ligand complex according to formula (I), in which each of R1 and R16 is independently selected from the group consisting of —H, (C1-C40)hydrocarbyl, (C1-C40)heterohydrocarbyl, —Si(RC)3, —Ge(RC)3, —P(RP)2, —N(RN)2, —ORC, —SRC, —NO2, —CN, —CF3, RCS(O)—, RCS(O)2—, —N═C(RC)2, RCC(O)O—, RCOC(O)—, RCC(O)N(R)—, (RC)2NC(O)—, halogen, radicals having formula (II), radicals having formula (III), and radicals having formula (IV):




embedded image


In formula (II), (III), and (IV), each of R31-35, R41-48, and R51-59 is independently chosen from —H, (C1-C40)hydrocarbyl, (C1-C40)heterohydrocarbyl, —Si(RC)3, —Ge(RC)3, —P(RP)2, —N(RN)2, —ORC, —SRC, —NO2, —CN, —CF3, RCS(O)—, RCS(O)2—, (RC)2C═N—, RCC(O)O—, ROC(O)—, RCC(O)N(RN)—, (RC)2NC(O)—, or halogen, provided that at least one of R1 or R16 is a radical having formula (II), a radical having formula (III), or a radical having formula (IV).


In formula (I), each of R2-4, R5-8, R9-12, and R13-15 is independently selected from —H, (C1-C40)hydrocarbyl, (C1-C40)heterohydrocarbyl, —Si(RC)3, —Ge(RC)3, —P(RP)2, —N(RN)2—ORC, —SRC, —NO2, —CN, —CF3, RCS(O)—, RCS(O)2—, (RC)2C═N—, RCC(O)O—, RCOC(O)—, RCC(O)N(R)—, (RC)2NC(O)—, and halogen. In one or more embodiments, L is (C2-C40)hydrocarbylene or (C2-C40)heterohydrocarbylene; and each RC, RP, and RN in formula (I) is independently a (C1-C30)hydrocarbyl, (C1-C30)heterohydrocarbyl, or —H.


In embodiments, the metal-ligand complex according to formula (I) has a solubility greater than the solubility of a corresponding comparative complex having a structure according to formula (Ia):




embedded image


In formula (Ia), M, n, each Z, each R1-16 each R31-35, each R41-48, each R51-59, L, each RC, each RP, and each RN all are identical to corresponding groups of the metal-ligand complex according to formula (I). Thus, the corresponding comparative complex differs from the metal-ligand complex according to formula (I) in that all groups X of the metal-ligand complex according to formula (I) are replaced with methyl groups.


The metal-ligand complex of formula (I) and the corresponding comparative complex of formula (Ia) both have a weight percent (wt. %) solubility in various solvents. In general, as used herein, weight percent (wt. %) solubility of a solute in a solution is the weight of the solute divided by the weight of the solution, multiplied by 100. Solubility measurements of individual metal-ligand complexes are conducted as follows: The solute (procatalyst) is added to a solvent such as methylcyclohexane (MCH) or Isopar-E™, such that the amount of solute added is greater than the amount that will dissolve in that amount of solvent. The resulting suspension is stirred for an hour and then allowed to sit overnight. After sitting overnight (approximately 16 hours), the suspension is filtered through a 0.2-μm PTFE syringe filter into a tared vial. The amount of solution in the tared vial is weighed, and the solvent is removed under reduced pressure. The weight of the residual solid is measured after all solvent is removed. The wt. % solubility is determined by dividing the weight of the residual solid by the weight of solution in the tared vial and multiplying by 100.


In one or more embodiments, the metal-ligand complex according to formula (I) has a weight percent (wt. %) solubility from 1.5 wt. % to 50 wt. % in methylcyclohexane (MCH) at ambient temperature and pressure. All individual values and subranges encompassed by “from 1.5 wt. % to 50 wt. %” are disclosed herein as separate embodiments. For example, in some embodiments, the solubility of the metal-ligand complex according to formula (I) is from 2.5 wt. % to 15 wt. %, from 1.5 wt. % to 10 wt. %, or from 3.0 wt. % to 15 wt. % in MCH, and in other embodiments, the solubility is greater than 20 wt. % in MCH at standard temperature and pressure (STP) (temperature of 22.5±2.5° C. and a pressure of approximately 1 atmosphere).


In one or more embodiments, the metal-ligand complex according to formula (I) has a wt. % solubility from 1.5 wt. % to 50 wt. % in Isopar-E™ at ambient temperature and pressure. All individual values and subranges encompassed by “from 1.5 wt. % to 50 wt. %” are disclosed herein as separate embodiments. For example, in some embodiments, the metal-ligand complex according to formula (I) has a wt. % solubility from 2.5 wt. % to 15 wt. %, from 2.5 wt. % to 10 wt. %, or from 3.0 wt. % to 15 wt. % in Isopar-E™, and in other embodiments, the wt. % solubility is greater than 20 wt. % in Isopar-E™ at STP.


The metal-ligand complex of formula (I) in MCH at STP has a wt. % solubility of W, as measured by the procedure previously described. The corresponding metal-ligand complex of formula (Ia) in MCH at STP has a wt. % solubility in MCH at STP of Y, as measured by the same procedure as the corresponding metal-ligand complex of formula (I). A wt. % solubility ratio (SR) is defined as W divided by Y (W/Y). For example, Complex A, a metal-ligand complex of formula (I), has a wt. % solubility of 10 wt. % in MCH at STP, as measured by the procedure in the preceding paragraphs. Complex B, the corresponding metal-ligand complex of formula (Ia), has a wt. % solubility of 2 wt. % in MCH at STP, as measured by the same procedure as Complex A. Thus, Complex A has a SR of 5.


In one or more embodiments of this disclosure, the SR of the metal-ligand complex of formula (I) is at least 1.5, at least 2, or at least 3. In some embodiments, the SR is from 1.5 to 50, from 2 to 50, from 2 to 10, from 3 to 15, or from 1.5 to 100. All individual values and subranges encompassed by “from 2 to 100” are disclosed herein as separate embodiments.


Industrial-scale polymerization processes typically involve large volumes of procatalyst solutions in non-aromatic hydrocarbon solvents. When procatalyst solubility is low in non-aromatic hydrocarbons, very dilute solutions must be used. This necessitates larger volumes of solvent to transport the procatalyst. Increasing procatalyst solubility, can therefor lead to a greener process, as smaller solvent volumes could be used. Dilute solutions can also lead to process disruptions. In some cases, the procatalyst is so insoluble in non-aromatic hydrocarbons that even dilute solutions cannot be used, and undesirable aromatic hydrocarbon solvents are required.


In some embodiments, any or all of the chemical groups (e.g., L, R1-16, R31-35, R41-48, R51-59) of the metal-ligand complex of formula (I) may be unsubstituted. In other embodiments, none, any, or all of the chemical groups, L, R1-16, R31-35, R41-48, R51-59, of the metal-ligand complex of formula (I) may be substituted with one or more than one RS. When two or more than two RS are bonded to a same chemical group of the metal-ligand complex of formula (I), the individual RS of the chemical group may be bonded to the same carbon atom or heteroatom or to different carbon atoms or heteroatoms. In some embodiments, none, any, or all of the chemical groups L, R1-16, R31-35, R41-48, R51-59 may be persubstituted with RS. In the chemical groups that are persubstituted with RS, the individual RS may all be the same or may be independently chosen.


In one or more embodiments, each X is independently —(CH2)SiRX3, in which each RX is independently a (C1-C30)alkyl or a (C1-C30)heteroalkyl and at least one RX is (C2-C30)alkyl. In some embodiments, when one of RX is a (C1-C30)heteroalkyl, the hetero atom is silica. In some embodiments, RX is methyl, ethyl, propyl, 2-propyl, butyl, 1,1-dimethylethyl (or tert-butyl), pentyl, hexyl, heptyl, n-octyl, tert-octyl, or nonyl.


In one or more embodiments X is —(CH2)Si(CH3)2(CH2CH3); —(CH2)Si(CH3)(CH2CH3)2, —(CH2)Si(CH2CH3)3, —(CH2)Si(CH3)2(n-butyl), —(CH2)Si(CH3)2(n-hexyl), —(CH2)Si(CH3)(n-Oct)RX, —(CH2)Si(n-Oct)RX2, —(CH2)Si(CH3)2(2-ethylhexyl), —(CH2)Si(CH3)2(dodecyl), —CH2Si(CH3)2CH2Si(CH3)3 (also referred to herein as —CH2Si(CH3)2CH2TMS). Optionally, in some embodiments, the metal-ligand complex according to formula (I), exactly two RX are covalently linked or exactly three RX are covalently linked.


In one or more embodiments, L is chosen from (C2-C12)alkylene, (C2-C12)heteroalkylene, (C6-C50)arylene, (C5-C50)heteroarylene, (—CH2Si(RC)2CH2—), (—CH2CH2Si(RC)2CH2CH2—), (—CH2CH2Ge(RC)2CH2CH2—), or (—CH2Ge(RC)2CH2—), in which RC is (C1-C30)hydrocarbyl. In some embodiments, L is —(CH2)x—, in which subscript x is from 2 to 5. In other embodiments, subscript x, of —(CH2)x—, is 3 or 4. In some embodiments, L is 1,3-bis(methylene)cyclohexane or 1,2-bis(2-yloethyl)cyclohexane.


In some embodiments, in the metal-ligand complex of formula (I), either one of R1 or R16, or both R1 and R16, are chosen from radicals having formula (II), formula (III), or formula (IV):




embedded image


When present in the metal-ligand complex of formula (I) as part of a radical having formula (II), formula (III), or formula (IV), the groups R31-35, R41-48, and R51-59 of the metal-ligand complex of formula (I) are each independently chosen from (C1-C40)hydrocarbyl, (C1-C40)heterohydrocarbyl, Si(RC)3, P(RP)2, N(RN)2, ORC, SRC, NO2, CN, CF3, RCS(O)—, RCS(O)2—, (RC)2C═N—, RCC(O)O—, RCOC(O)—, RCC(O)N(RN)—, (RN)2NC(O)—, halogen, hydrogen (—H), or combinations thereof. Independently each RC, RP, and RN are unsubstituted (C1-C18)hydrocarbyl, (C1-C30)heterohydrocarbyl, or —H.


The groups R1 and R16 in the metal-ligand complex of formula (I) are chosen independently of one another. For example, R1 may be chosen from a radical having formula (II), (III), or (IV) and R16 may be a (C1-C40)hydrocarbyl; or R1 may be chosen from a radical having formula (II), (III), or (IV) and R16 may be chosen from a radical having formula (II), (III), or (IV) the same as or different from that of R1. Both R1 and R16 may be radicals having formula (II), for which the groups R31-35 are the same or different in R1 and R16. In other examples, both R1 and R16 may be radicals having formula (III), for which the groups R41-48 are the same or different in R1 and R16; or both R1 and R16 may be radicals having formula (IV), for which the groups R51-59 are the same or different in R1 and R16.


In some embodiments, at least one of R1 and R16 is a radical having formula (II), where R32 and R34 are tert-butyl.


In some embodiments, when at least one of R1 or R16 is a radical having formula (III), one of or both of R43 and R46 is tert-butyl and each of R41-42, R44-45, and R47-48 are —H. In other embodiments, one of or both of R42 and R47 is tert-butyl and R41, R43-46, and R48 are —H. In some embodiments, both R42 and R47 are —H.


In one or more embodiments, R3 and R14 are (C1-C12)alkyl. In some embodiments, R3 and R14 are tert-octyl, n-octyl, methyl, ethyl, propyl, 2-propyl, butyl, 1,1-dimethylethyl (or tert-butyl). In one or more embodiments, R6 and R11 are halogen. In some embodiments, R3 and R14 are methyl; and R6 and R11 are halogen.


In some embodiments of the metal-ligand complex of formula (I), when R5-7 are fluorine, not more than one of R10-12 is fluorine. In other embodiments, when R10-12 are fluorine, not more than one of R5-7 is fluorine. In other embodiments, fewer than four of R5-7 and R10-12 are fluorine. In one or more embodiments, R7, R8, R9, and R10 are —H. In some embodiments, R7 and R10 are halogen. In some embodiments, two of R5-7 are fluorine and two of R10-12 are fluorine.


The M in the metal-ligand complex of formula (I) may be a transition metal such as titanium (Ti), zirconium (Zr), or hafnium (Hf), and the transition metal may have a formal oxidation state of +2, +3, or +4.


The metal M in the metal-ligand complex of formula (I) may be derived from a metal precursor that is subsequently subjected to a single-step or multi-step synthesis to prepare the metal-ligand complex. Suitable metal precursors may be monomeric (one metal center), dimeric (two metal centers), or may have a plurality of metal centers greater than two, such as 3, 4, 5, or more than 5 metal centers. Specific examples of suitable hafnium and zirconium precursors, for example, include, but are not limited to HfCl4, HfMe4, Hf(CH2Ph)4, Hf(CH2CMe3)4, Hf(CH2SiMe3)4, Hf(CH2Ph)3Cl, Hf(CH2CMe3)3Cl, Hf(CH2SiMe3)3Cl, Hf(CH2Ph)2Cl2, Hf(CH2CMe3)2Cl2, Hf(CH2SiMe3)2Cl2, Hf(NMe2)4, Hf(NEt2)4, and Hf(N(SiMe3)2)2Cl2; ZrCl4, ZrMe4, Zr(CH2Ph)4, Zr(CH2CMe3)4, Zr(CH2SiMe3)4, Zr(CH2Ph)3Cl, Zr(CH2CMe3)3Cl, Zr(CH2SiMe3)3Cl, Zr(CH2Ph)2Cl2, Zr(CH2CMe3)2Cl2, Zr(CH2SiMe3)2Cl2, Zr(NMe2)4, Zr(NEt2)4, Zr(NMe2)2Cl2, Zr(NEt2)2Cl2, Zr(N(SiMe3)2)2Cl2, TiBn4, TiCl4 and Ti(CH2Ph)4. Lewis base adducts of these examples are also suitable as metal precursors, for example, ethers, amines, thioethers, and phosphines are suitable as Lewis bases. Specific examples include HfCl4(THF)2, HfCl4(SMe2)2 and Hf(CH2Ph)2Cl2(OEt2). Activated metal precursors may be ionic or zwitterionic compounds, such as (M(CH2Ph)3+)(B(C6F5)4) or (M(CH2Ph)3+) (PhCH2B(C6F5)3) where M is defined above as being Hf or Zr.


In the metal-ligand complex of formula (I), each Z independently is O, S, N(C1-C40)hydrocarbyl, or P(C1-C40)hydrocarbyl. In some embodiments, each Z is different. For example, one Z is O and the other Z is NCH3. In some embodiments, one Z is O and one Z is S. In another embodiment, one Z is S and one Z is N(C1-C40)hydrocarbyl, (for example, NCH3). In a further embodiment, each Z is the same. In yet another embodiment, each Z is O. In another embodiment, each Z is S.


Cocatalyst Component


The catalyst system comprising a metal-ligand complex of formula (I) may be rendered catalytically active by any technique known in the art for activating metal-based catalysts of olefin polymerization reactions. For example, the procatalyst according to a metal-ligand complex of formula (I) may be rendered catalytically active by contacting the complex to, or combining the complex with, an activating co-catalyst. Additionally, the metal-ligand complex according for formula (I) includes both a procatalyst form, which is neutral, and a catalytic form, which may be positively charged due to the loss of a monoanionic ligand, such a benzyl or phenyl. Suitable activating co-catalysts for use herein include alkyl aluminums; polymeric or oligomeric alumoxanes (also known as aluminoxanes); neutral Lewis acids; and non-polymeric, non-coordinating, ion-forming compounds (including the use of such compounds under oxidizing conditions). A suitable activating technique is bulk electrolysis. Combinations of one or more of the foregoing activating co-catalysts and techniques are also contemplated. The term “alkyl aluminum” means a monoalkyl aluminum dihydride or monoalkylaluminum dihalide, a dialkyl aluminum hydride or dialkyl aluminum halide, or a trialkylaluminum. Examples of polymeric or oligomeric alumoxanes include methylalumoxane, triisobutylaluminum-modified methylalumoxane, and isobutylalumoxane.


Lewis acid activating co-catalysts include Group 13 metal compounds containing (C1-C20)hydrocarbyl substituents as described herein. In some embodiments, Group 13 metal compounds are tri((C1-C20)hydrocarbyl)-substituted-aluminum or tri((C1-C20)hydrocarbyl)-boron compounds. In other embodiments, Group 13 metal compounds are tri(hydrocarbyl)-substituted-aluminum, tri((C1-C20)ohydrocarbyl)-boron compounds, tri((C1-C10)alkyl)aluminum, tri((C6-C18)aryl)boron compounds, and halogenated (including perhalogenated) derivatives thereof. In further embodiments, Group 13 metal compounds are tris(fluoro-substituted phenyl)boranes, tris(pentafluorophenyl)borane. In some embodiments, the activating co-catalyst is a tris((C1-C20)hydrocarbyl borate (e.g. trityl tetrafluoroborate) or a tri((C1-C20)hydrocarbyl)ammonium tetra((C1-C20)hydrocarbyl)borane (e.g. bis(octadecyl)methylammonium tetrakis(pentafluorophenyl)borane). As used herein, the term “ammonium” means a nitrogen cation that is a ((C1-C20)hydrocarbyl)4N+ a ((C1-C20)hydrocarbyl)3N(H)+, a ((C1-C20)hydrocarbyl)2N(H)2+, (C1-C20)hydrocarbylN(H)3+, or N(H)4+, wherein each (C1-C20)hydrocarbyl, when two or more are present, may be the same or different.


Combinations of neutral Lewis acid activating co-catalysts include mixtures comprising a combination of a tri((C1-C4)alkyl)aluminum and a halogenated tri((C6-C18)aryl)boron compound, especially a tris(pentafluorophenyl)borane. Other embodiments are combinations of such neutral Lewis acid mixtures with a polymeric or oligomeric alumoxane, and combinations of a single neutral Lewis acid, especially tris(pentafluorophenyl)borane with a polymeric or oligomeric alumoxane. Ratios of numbers of moles of (metal-ligand complex): (tris(pentafluoro-phenylborane): (alumoxane) [e.g., (Group 4 metal-ligand complex):(tris(pentafluoro-phenylborane):(alumoxane)] are from 1:1:1 to 1:10:30, in other embodiments, from 1:1:1.5 to 1:5:10.


The catalyst system that includes the metal-ligand complex of formula (I) may be activated to form an active catalyst composition by combination with one or more cocatalysts, for example, a cation forming cocatalyst, a strong Lewis acid, or combinations thereof. Suitable activating co-catalysts include polymeric or oligomeric aluminoxanes, especially methyl aluminoxane, as well as inert, compatible, noncoordinating, ion forming compounds. Exemplary suitable co-catalysts include, but are not limited to modified methyl aluminoxane (MMAO), bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(1-)amine, and combinations thereof.


In some embodiments, more than one of the foregoing activating co-catalysts may be used in combination with each other. A specific example of a co-catalyst combination is a mixture of a tri((C1-C4)hydrocarbyl)aluminum, tri((C1-C4)hydrocarbyl)borane, or an ammonium borate with an oligomeric or polymeric alumoxane compound. The ratio of total number of moles of one or more metal-ligand complexes of formula (I) to total number of moles of one or more of the activating co-catalysts is from 1:10,000 to 100:1. In some embodiments, the ratio is at least 1:5000, in some other embodiments, at least 1:1000; and 10:1 or less, and in some other embodiments, 1:1 or less. When an alumoxane alone is used as the activating co-catalyst, preferably the number of moles of the alumoxane that are employed is at least 100 times the number of moles of the metal-ligand complex of formula (I). When tris(pentafluorophenyl)borane alone is used as the activating co-catalyst, in some other embodiments, the number of moles of the tris(pentafluorophenyl)borane that are employed to the total number of moles of one or more metal-ligand complexes of formula (I) from 0.5:1 to 10:1, from 1:1 to 6:1, or from 1:1 to 5:1. The remaining activating co-catalysts are generally employed in approximately mole quantities equal to the total mole quantities of one or more metal-ligand complexes of formula (I).


In some embodiments, when more than one of the foregoing co-catalysts is used in combination with a second co-catalyst, one of the co-catalysts may function as a scavenger. The purpose of the scavenger is to react with any water or other impurities present in the system that would otherwise react with the catalyst leading to reduced efficiency.


Polyolefins


The catalytic systems described in the preceding paragraphs are utilized in the polymerization of olefins, primarily ethylene and propylene. In some embodiments, there is only a single type of olefin or α-olefin in the polymerization scheme, creating a homopolymer. However, additional α-olefins may be incorporated into the polymerization procedure. The additional α-olefin co-monomers typically have no more than 20 carbon atoms. For example, the α-olefin co-monomers may have 3 to 10 carbon atoms or 3 to 8 carbon atoms. Exemplary α-olefin co-monomers include, but are not limited to, propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene, and 4-methyl-1-pentene. For example, the one or more α-olefin co-monomers may be selected from the group consisting of propylene, 1-butene, 1-hexene, and 1-octene; or in the alternative, from the group consisting of 1-hexene and 1-octene.


The ethylene-based polymers, for example homopolymers and/or interpolymers (including copolymers) of ethylene and optionally one or more co-monomers such as α-olefins, may comprise from at least 50 mole percent (mol %) monomer units derived from ethylene. All individual values and subranges encompassed by “from at least 50 mole percent” are disclosed herein as separate embodiments; for example, the ethylene based polymers, homopolymers and/or interpolymers (including copolymers) of ethylene and optionally one or more co-monomers such as α-olefins may comprise at least 60 mole percent monomer units derived from ethylene; at least 70 mole percent monomer units derived from ethylene; at least 80 mole percent monomer units derived from ethylene; or from 50 to 100 mole percent monomer units derived from ethylene; or from 80 to 100 mole percent monomer units derived from ethylene.


In some embodiments, the ethylene-based polymers may comprise at least 90 mole percent units derived from ethylene. All individual values and subranges from at least 90 mole percent are included herein and disclosed herein as separate embodiments. For example, the ethylene-based polymers may comprise at least 93 mole percent units derived from ethylene; at least 96 mole percent units; at least 97 mole percent units derived from ethylene; or in the alternative, from 90 to 100 mole percent units derived from ethylene; from 90 to 99.5 mole percent units derived from ethylene; or from 97 to 99.5 mole percent units derived from ethylene.


In some embodiments of the ethylene-based polymer, the amount of additional α-olefin is less than 50 mole percent (mol %); other embodiments include at least 1 mol % to 25 mol %; and in further embodiments the amount of additional α-olefin includes at least 5 mol % to 103 mol %. In some embodiments, the additional (α-olefin is 1-octene.


Any conventional polymerization processes may be employed to produce the ethylene-based polymers. Such conventional polymerization processes include, but are not limited to, solution polymerization processes, gas phase polymerization processes, slurry phase polymerization processes, and combinations thereof using one or more conventional reactors such as loop reactors, isothermal reactors, fluidized bed gas phase reactors, stirred tank reactors, batch reactors in parallel, series, or any combinations thereof, for example.


In one embodiment, the ethylene-based polymer may be produced via solution polymerization in a dual reactor system, for example a dual loop reactor system, wherein ethylene and, optionally, one or more α-olefins are polymerized in the presence of the catalyst system, as described herein, and optionally one or more co-catalysts. In another embodiment, the ethylene-based polymer may be produced via solution polymerization in a dual reactor system, for example a dual loop reactor system, wherein ethylene and optionally one or more α-olefins are polymerized in the presence of the catalyst system in this disclosure, and as described herein, and optionally one or more other catalysts. The catalyst system, as described herein, can be used in the first reactor, or second reactor, optionally in combination with one or more other catalysts. In one embodiment, the ethylene-based polymer may be produced via solution polymerization in a dual reactor system, for example a dual loop reactor system, wherein ethylene and optionally one or more α-olefins are polymerized in the presence of the catalyst system, as described herein, in both reactors.


In another embodiment, the ethylene-based polymer may be produced via solution polymerization in a single reactor system, for example a single loop reactor system, in which ethylene and optionally one or more α-olefins are polymerized in the presence of the catalyst system, as described within this disclosure, and optionally one or more cocatalysts, as described in the preceding paragraphs.


The ethylene-based polymers may further comprise one or more additives. Such additives include, but are not limited to, antistatic agents, color enhancers, dyes, lubricants, pigments, primary antioxidants, secondary antioxidants, processing aids, UV stabilizers, and combinations thereof. The ethylene-based polymers may contain any amounts of additives. The ethylene-based polymers may compromise from about 0 to about 10 percent by the combined weight of such additives, based on the weight of the ethylene-based polymers and the one or more additives. The ethylene-based polymers may further comprise fillers, which may include, but are not limited to, organic or inorganic fillers. The ethylene-based polymers may contain from about 0 to about 20 weight percent fillers such as, for example, calcium carbonate, talc, or Mg(OH)2, based on the combined weight of the ethylene-based polymers and all additives or fillers. The ethylene-based polymers may further be blended with one or more polymers to form a blend.


In some embodiments, a polymerization process for producing an ethylene-based polymer may include polymerizing ethylene and at least one additional α-olefin in the presence of a catalyst system, wherein the catalyst system incorporates at least one metal-ligand complex of formula (I). The polymer resulting from such a catalyst system that incorporates the metal-ligand complex of formula (I) may have a density according to ASTM D792 (incorporated herein by reference in its entirety) from 0.850 g/cm3 to 0.950 g/cm3, from 0.880 g/cm3 to 0.920 g/cm3, from 0.880 g/cm3 to 0.910 g/cm3, or from 0.880 g/cm3 to 0.900 g/cm3, for example.


In another embodiment, the polymer resulting from the catalyst system that includes the metal-ligand complex of formula (I) has a melt flow ratio (I10/I2) from 5 to 15, in which melt index I2 is measured according to ASTM D1238 (incorporated herein by reference in its entirety) at 190° C. and 2.16 kg load, and melt index I10 is measured according to ASTM D1238 at 190° C. and 10 kg load. In other embodiments the melt flow ratio (I10/I2) is from 5 to 10, and in others, the melt flow ratio is from 5 to 9.


In some embodiments, the polymer resulting from the catalyst system that includes the metal-ligand complex of formula (I) has a molecular-weight distribution (MWD) from 1.5 to 25, where MWD is defined as Mw/Mn with Mw being a weight-average molecular weight and Mn being a number-average molecular weight. In other embodiments, the polymers resulting from the catalyst system have a MWD from 1.5 to 6. Another embodiment includes a MWD from 1.5 to 3; and other embodiments include MWD from 2 to 2.5.


Embodiments of the catalyst systems described in this disclosure yield unique polymer properties as a result of the high molecular weights of the polymers formed and the amount of the co-monomers incorporated into the polymers.


All solvents and reagents are obtained from commercial sources and used as received unless otherwise noted. Anhydrous toluene, hexanes, tetrahydrofuran, and diethyl ether are purified via passage through activated alumina and, in some cases, Q-5 reactant. Solvents used for experiments performed in a nitrogen-filled glovebox are further dried by storage over activated 4 Å molecular sieves. Glassware for moisture-sensitive reactions is dried in an oven overnight prior to use. NMR spectra are recorded on Varian 400-MR and VNMRS-500 spectrometers. 1H NMR data are reported as follows: chemical shift (multiplicity (br=broad, s=singlet, d=doublet, t=triplet, q=quartet, p=pentet, sex=sextet, sept=septet and m=multiplet), integration, and assignment). Chemical shifts for 1H NMR data are reported in ppm downfield from internal tetramethylsilane (TMS, δ scale) using residual protons in the deuterated solvent as references. 13C NMR data are determined with 1H decoupling, and the chemical shifts are reported downfield from tetramethylsilane (TMS, δ scale) in ppm versus the using residual carbons in the deuterated solvent as references.


SymRAD HT-GPC Analysis


The molecular weight data is determined by analysis on a hybrid Robot-Assisted Dilution High-Temperature Gel Permeation Chromatographer (Sym-RAD-GPC) built by Symyx/Dow. The polymer samples are dissolved by heating for 120 minutes at 160° C. in 1,2,4-trichlorobenzene (TCB) at a concentration of 10 mg/mL stabilized by 300 parts per million (ppm) of butylated hydroxyl toluene (BHT). Each sample was diluted to 1 mg/mL immediately before the injection of a 250 μL aliquot of the sample. The GPC is equipped with two Polymer Labs PLgel 10 μm MIXED-B columns (300×10 mm) at a flow rate of 2.0 mL/minute at 160° C. Sample detection is performed using a PolyChar IR4 detector in concentration mode. A conventional calibration of narrow polystyrene (PS) standards is utilized with apparent units adjusted to homo-polyethylene (PE) using known Mark-Houwink coefficients for PS and PE in TCB at this temperature.


1-Octene Incorporation IR Analysis


The running of samples for the HT-GPC analysis precedes the IR analysis. For the IR analysis, a 48-well HT silicon wafer is utilized for deposition and analysis of 1-octene incorporation of samples. For the analysis, the samples are heated to 160° C. for less than or equal to 210 minutes; the samples are reheated to remove magnetic GPC stir bars and are shaken with glass-rod stir bars on a J-KEM Scientific heated robotic shaker. Samples are deposited while being heated using a Tecan MiniPrep 75 deposition station, and the 1,2,4-trichlorobenzene is evaporated off the deposited wells of the wafer at 160° C. under nitrogen purge. The analysis of 1-octene is performed on the HT silicon wafer using a NEXUS 670 E.S.P. FT-IR.


Batch Reactor Polymerization Procedure


The batch reactor polymerization reactions are conducted in a one gallon (3.79 L), stirred autoclave reactor that is charged with ca. 1.35 kg of Isopar™ E mixed alkanes solvent and 1-octene (250 g). The reactor is then heated to the desired temperature and charged with hydrogen (if desired), followed by an amount of ethylene to bring the total pressure to ca. 450 psig (2.95 MPa). The ethylene feed was passed through an additional purification column prior to entering the reactor. The catalyst composition was prepared in a drybox, under inert atmosphere, by mixing the desired pro-catalyst and a cocatalyst (a mixture of 1.2 equiv of tetrakis(pentafluorophenyl)borate(1-)amine, and 50 equiv of triisobutylaluminum modified alumoxane (MMAO-3A)), with additional solvent, to give a total volume of about 17 mL. The activated catalyst mixture was then quick-injected into the reactor. The reactor pressure and temperature were kept constant, by feeding ethylene during the polymerization, and cooling the reactor as needed. After 10 minutes, the ethylene feed was shut off, and the solution transferred into a nitrogen-purged resin kettle. The polymer was thoroughly dried in a vacuum oven, and the reactor was thoroughly rinsed with hot Isopar™ E between polymerization runs.


EXAMPLES

Example 1 comprises synthetic procedures for intermediates of procatalsyts, for reagents used to make procatalsyts, and for isolated procatalysts themselves. One or more features of the present disclosure are illustrated in view of the examples as follows:


Example 1—Synthesis of Procatalyst 1



embedded image


A solution of Intermediate 1 (2.271 g, 1.84 mmol) in a mixture of benzene (40 mL) and toluene (40 mL) was chilled in a glovebox freezer (−35° C.). A 14 mL solution of dimethyloctylsilylmethyllithium in hexane (0.13 M, 1.84 mmol) was added to the solution and the reaction mixture was stirred over the weekend at ambient temperature to give a clear colorless solution. At this time the solution was cooled in the glovebox freezer, additional dimethyloctylsilymethyllithium (5.26 mL, 0.69 mmol)) was added, and the reaction mixture was stirred overnight at 60° C. Thrice more the reaction mixture was cooled in the glovebox freezer, more dimethyloctylsilymethyllithium (4.5 mL, 0.59 mmol; 2.8 mL, 0.36 mmol; 2.2 mL, 0.29 mmol) was added, and the reaction mixture was stirred overnight. The reaction mixture was filtered and the volatiles were removed under reduced pressure. The residue was extracted with warm (50° C.) hexanes, the extract was filtered, and the volatiles were removed under reduced pressure. The residue was extracted a second time with warm (50° C.) hexanes, the extract was filtered from a small amount of insoluble material, and the volatiles were removed under reduced pressure to give the product as a slightly sticky beige solid. This reaction provided a yield of 2.13 g, 83.6% yield.



1H NMR (400 MHz, Benzene-d6) δ 8.37-8.26 (m, 1.5H), 8.17 (ddt, J=7.8, 6.8, 1.3 Hz, 1.7H), 8.14-7.82 (m, 3.5H), 7.69-7.17 (m, 13.3H), 7.13-6.64 (m, 10.4H), 4.93 (dd, J=8.3, 1.2 Hz, 0.9H), 4.68 (dd, J=8.2, 1.2 Hz, 0.8H), 4.19 (dd, J=12.4, 8.6 Hz, 1.3H), 3.85 (d, J=11.0 Hz, 1.1H), 3.76 (d, J=10.8 Hz, 0.7H), 3.38 (d, J=12.4 Hz, 1.3H), 3.19 (d, J=10.9 Hz, 1.1H), 2.21-2.00 (m, 6H), 1.85-0.33 (m, 73H), 0.32-0.25 (m, 4.6H), 0.22-0.04 (m, 5.4H), 0.02 (s, 1H), 0.00-−0.13 (m, 2.3H), −0.15 (d, J=2.5 Hz, 2.6H), −0.33 (s, 1.3H), −0.38 (s, 1.6H), −1.70 (dd, J=372.3, 13.0 Hz, 1.7H), −1.73 (dd, J=272.4, 13.1 Hz, 1.8H).


Procatalyst 1, Comparative Procatalyst C1, and Comparative Procatalyst C2 were individually reacted using the polymerization conditions in a single reactor system, as previously described. Properties for the resulting polymers are reported in Table 2. Comparative Procatalyst C1 has a structure according to formula (Ia). When compared to Comparative Procatalyst C1 and Comparative Procatalyst C2, a significant increase in weight percent solubility was observed for the Procatalyst 1, which is a metal-ligand complex according to formula (I).




embedded image









TABLE 1







Solubility Data at 25° C.













Solubility
Solubility




Procatalyst
(wt. %)
Ratio
Solvent







Comparative C1
1.5
N/A
Methylcyclohexane



Comparative C2
1.1
N/A
Isopar ™ E



Procatalyst 1
>10 wt. %
≥6.67
Methylcyclohexane

















TABLE 2







Batch Reactor Screening of Procatalyst 1 and Comparative C1
















H2**
Efficiency*
Mw

Tm
Density


Catalyst
T (° C.)
(mmol)
(MM g/g)
(kg/mol)
Mw/Mn
(° C.)
(g/cm3)

















Comparative C1
160
0
1.82
1,055
2.6
89
0.8909


Comparative C2
160
0
1.07
1,076
2.5
90
0.8933


Comparative C2
190
0
0.24
519
2.3
91
0.8949


Comparative C2
190
0
0.15
494
2.3
91
0.8936





*Efficiency is defined in units of 106 grams polymer per gram of active metal (Hf or Zr).


**H2 (mol %) is defined as: the mole fraction of hydrogen, relative to ethylene, fed into the reactor.













TABLE 3







Batch Reactor Screening of Procatalyst 1 and Comparative C1















T
**H2
*Efficiency
Mw
Mw/
Tm
Density


Catalyst
(° C.)
(mmol)
(MM g/g)
(kg/mol)
Mn
(° C.)
(g/cm3)

















Comparative C1
160
0
1.01
1,038
3.0
88
0.8901


Procatalyst 1
160
0
0.09
1,080
2.9
89
0.8915


Procatalyst 1
160
40
0.10
486
2.3
89
0.8929


Comparative C1
190
0
0.22
495
2.3
90
0.8923


Procatalyst 1
190
0
0.01
548
2.5
91
0.8951


Procatalyst 1
190
40
0.02
313
2.4
92
0.8964





*Efficiency is defined in units of 106 grams polymer per gram of active metal (Hf or Zr).


**H2 (mol %) is defined as: the mole fraction of hydrogen, relative to ethylene, fed into the reactor.






Batch reactor conditions for Table 3: 1.47 kg of Isopar™ E; 100 grams of octene; 105 grams of ethylene were added at 160° C. or 88 grams of ethylene were added at 190° C.; RIBS: catalyst ratio was approximately 1.2; Procatalyst: activator ratio was 1:1.2; activator was [HNMe(C18H37)2][B(C6F5)4]; MMAO-3A was used as an impurity scavenger at a MMAO-3A:procatalyst mole ratio of approximately 50; total pressure was initially 410 psig.

Claims
  • 1. A catalyst system comprising a metal-ligand complex according to formula (I):
  • 2. The catalyst system according to claim 1, wherein: M is zirconium or hafnium;each X is —(CH2)Si(CH2CH3)3; andeach Z is oxygen.
  • 3. The catalyst system according to claim 1, wherein: M is zirconium or hafnium;each X is selected from the group consisting of —(CH2)Si(CH3)(n-Oct)RX; andeach Z is oxygen.
  • 4. The catalyst system according to claim 1, wherein exactly two RX are covalently linked or exactly three RX are covalently linked.
  • 5. A catalyst system comprising a metal-ligand complex according to formula (I):
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a National Stage Entry under 35 U.S.C. 071 of International Patent Application No. PCT/US2018/051638, filed Sep. 19, 2018, which claims priority to U.S. Provisional Patent Application Ser. No. 62/565,771, filed Sep. 29, 2017, both of which are incorporated by reference in their entirety.

PCT Information
Filing Document Filing Date Country Kind
PCT/US2018/051638 9/19/2018 WO 00
Publishing Document Publishing Date Country Kind
WO2019/067274 4/4/2019 WO A
US Referenced Citations (54)
Number Name Date Kind
5064802 Stevens et al. Nov 1991 A
5153157 Hlatky et al. Oct 1992 A
5296433 Siedle et al. Mar 1994 A
5321106 Lapointe Jun 1994 A
5350723 Neithamer et al. Sep 1994 A
5425872 Devore et al. Jun 1995 A
5625087 Neithamer et al. Apr 1997 A
5721185 Lapointe et al. Feb 1998 A
5783512 Jacobsen et al. Jul 1998 A
5883204 Spencer et al. Mar 1999 A
5919983 Rosen et al. Jul 1999 A
6103657 Murray Aug 2000 A
6515155 Klosin et al. Feb 2003 B1
6696379 Carnahan et al. Feb 2004 B1
6869904 Boussie et al. Mar 2005 B2
7060848 Boussie et al. Jun 2006 B2
7163907 Canich et al. Jan 2007 B1
7951882 Arriola et al. May 2011 B2
8609794 Klosin et al. Dec 2013 B2
8729201 Fontaine et al. May 2014 B2
9029487 Klosin et al. May 2015 B2
9102819 Kapur et al. Aug 2015 B2
9200185 Knutson et al. Dec 2015 B2
9511567 Hu et al. Dec 2016 B2
9522855 Klosin et al. Dec 2016 B2
9527940 Demirors et al. Dec 2016 B2
9527941 Demirors et al. Dec 2016 B2
9601230 Nair et al. Mar 2017 B2
9601231 Klosin et al. Mar 2017 B2
9605098 Klosin et al. Mar 2017 B2
9643900 Arriola et al. May 2017 B2
20040005984 Boussie et al. Jan 2004 A1
20040127614 Jiang et al. Jul 2004 A1
20050080281 Boussie et al. Apr 2005 A1
20050288412 Hohner et al. Dec 2005 A1
20070136496 Hendel et al. Jun 2007 A1
20100036069 Konze et al. Feb 2010 A1
20110039082 Yun et al. Feb 2011 A1
20110082249 Shan et al. Apr 2011 A1
20110146044 Pecherzewski Jun 2011 A1
20110282018 Klosin et al. Nov 2011 A1
20110313106 Shan et al. Dec 2011 A1
20120116034 Oswald et al. May 2012 A1
20130030135 Hagadorn et al. Jan 2013 A1
20130090430 Robert et al. Apr 2013 A1
20130144018 Klosin et al. Jun 2013 A1
20140330056 Klosin et al. Nov 2014 A1
20140357918 Klosin et al. Dec 2014 A1
20150337062 Demirors et al. Nov 2015 A1
20150337063 Demirors et al. Nov 2015 A1
20150344601 Demirors et al. Dec 2015 A1
20150344602 Demirors et al. Dec 2015 A1
20170101494 Fontaine et al. Apr 2017 A1
20170101495 Kapur et al. Apr 2017 A1
Foreign Referenced Citations (40)
Number Date Country
102712795 Oct 2012 CN
1069848 May 1967 GB
2000159829 Jun 2000 JP
2001525859 Dec 2001 JP
2005523921 Aug 2005 JP
2011525212 Sep 2011 JP
2013521382 Jun 2013 JP
2013534934 Sep 2013 JP
2013541631 Nov 2013 JP
2013544940 Dec 2013 JP
2005108460 Nov 2005 WO
2007136493 Nov 2007 WO
2007136494 Nov 2007 WO
2007136495 Nov 2007 WO
2007136496 Nov 2007 WO
2010061630 Jun 2010 WO
2011025784 Mar 2011 WO
2011041696 Apr 2011 WO
2011109563 Sep 2011 WO
2011146044 Nov 2011 WO
2011146291 Nov 2011 WO
2012004676 Jan 2012 WO
2012004683 Jan 2012 WO
2012013699 Feb 2012 WO
2012027448 Mar 2012 WO
2012064630 May 2012 WO
2012068576 May 2012 WO
2012069428 May 2012 WO
2012071459 May 2012 WO
2013101375 Jul 2013 WO
2014058639 Apr 2014 WO
2014105411 Jul 2014 WO
2014105412 Jul 2014 WO
2014105413 Jul 2014 WO
2014209927 Dec 2014 WO
2015045928 Apr 2015 WO
2015045930 Apr 2015 WO
WO2016014749 Jan 2016 WO
2017058981 Apr 2017 WO
2018022238 Feb 2018 WO
Non-Patent Literature Citations (15)
Entry
Zimm, Bruno H., “Apparatus and Methods for Measurement and Interpretation of the Angular Variation of Light Scattering; Preliminary Results on Polystyrene Solutions”, Journal of Chemical Physics, vol. 16, 12, 1099-1116 (1948).
G. Soave, “Redlick-Kwong-Soave (RKS) Equation of State,” Chemical Engineering Science, 1972, vol. 27, pp. 1197-1203.
Balke et al.., “A Strategy for Interpreting Multidetector Size-Exclusion Chromotography Data II”, Chromatography of Polymers, Chapter 13, pp. 199-219 (1992).
Mourey and Balke, Chromatography of Polymers, Chapter 12, pp. 180-198, (1992).
Han et al., “Synthesis of diindeno-Fused 4H-Cyclopenta[def]phenanthren-4-ones and Related Compounds via Benzannulated Enediynyl Propargylic Alcohols” , J. Org. Chem., 2005, 70: 6, 2406-2408.
Zhang et al., Zirconium Complexes of the Tridentate Bis(aryloxide)-N-heterocyclic-carbene ligand: Chloride and Alkyl Functionalized Derivatives, Journal of Organometallic Chemistry, 2006, 234-242.
Monrabal et al., “Crystallization Elution Fractionation and Thermal Gradient Interaction Chromatography Techniques Comparison”, Macromol. Symp. 2007, 257, 71-79.
Yau, Wallace W. “Examples of Using 3D-GPC-TREF for Polyolefin Characterization” , Macromol. Symp., 2007, 257, 29-45.
Bonvonsombat et al., “Regioselective Iodination of Phenol and Analogues Using N-Iodosuccinimide and p-toluenesulfonic Acid” , Tetrahedrom Letters, 2009, 50: 22, 2664-2667.
Randoll et al., “Stereoselective and Regioselective Propylene Polymerization with Group 4 Bisphenolate Ether Complexes”, Journal of Polymer Science: Part A: Polymer Chemistry, 2012, 2604-2611.
International Search Report and Written Opinion pertaining to PCT/US2018/051638, dated Feb. 5, 2019.
International Search Report and Written Opinion pertaining to PCT/US2018/051680, dated Feb. 5, 2019.
International Search Report and Written Opinion pertaining to PCT/US2018/051939, dated Dec. 10, 2019.
Kiesewetter et al., “Stereospecific Octahedral Group 4 Bis(phenolate) Ether Complexes for Olefin Polymerization”, J. Am. Chem. Soc., 2010, 132, 5566-5567.
Office Action dated Jun. 25, 2020 pertaining to U.S. Appl. No. 16/646,228 filed Mar. 11, 2020, 29 pgs.
Related Publications (1)
Number Date Country
20200270376 A1 Aug 2020 US
Provisional Applications (1)
Number Date Country
62565771 Sep 2017 US