BIS(TRIMETHYLSILYL) SIX-MEMBERED RING SYSTEMS AND RELATED COMPOUNDS AS REDUCING AGENTS FOR FORMING LAYERS ON A SUBSTRATE

FIELD OF THE INVENTION

In at least one aspect, the present invention is related to the formation of metal films from “metalorganic” precursors and a reducing agent.

BACKGROUND OF THE INVENTION

The growth of thin films is a central step in the fabrication of many functional materials and devices. While film growth efforts have been traditionally directed toward films greater than 100 nm, recent trends in several areas are calling for the growth of films ranging in thickness from a few atomic layers to tens of nanometers.

In the microelectronics arena, copper has replaced aluminum as the interconnect material in integrated circuits due to its lower resistivity and higher resistance to electromigration. Ultrathin (2-8 nm) manganese-silicon-oxygen layers have been proposed as replacements for existing nitride-based copper diffusion barrier layers in future devices. Since copper does not nucleate well on SiO₂and other surfaces, it is difficult to deposit copper metal onto the surface features of microelectronic substrates. Accordingly, there has been considerable interest in the formation of seed layers of metals such as chromium, cobalt, and others which adhere better to substrates, and upon which copper films can be subsequently grown.

Atomic layer deposition (ALD) is a thin film deposition technique that addresses many of the current technological demands. ALD affords inherently conformal coverage and sub-nanometer film thickness control due to its self-limited growth mechanism. In a typical ALD process, a substrate is contacted with a first chemical composition that modifies the substrate for a first predetermined period of time (a pulse). Such modification involves adsorption to the surface of the substrate, reaction with the surface of the substrate, or a combination of adsorption and reaction. A purging gas is introduced to remove any lingering first gaseous chemical composition in the vicinity of the substrate. A second gaseous chemical composition that reacts with the modified substrate surface is introduced for a second predetermined period of time into the vicinity of the substrate to form a portion of the thin film. A purging gas is subsequently introduced to remove any lingering second chemical composition in the vicinity of the substrate. These steps of contacting the substrate with the first chemical composition, purging, contacting the substrate with the second gaseous chemical composition, and purging are usually repeated a plurality of times until a film of desired thickness is coated onto the substrate. Although the prior art ALD processes work well, there is unfortunately only a limited number of chemical precursors having the requisite thermal stability, reactivity, and vapor pressure for ALD.

Accordingly, there is a need for improved methods and reagents for depositing thin films by atomic layer deposition.

SUMMARY OF THE INVENTION

The present invention solves one or more problems of the prior art by providing, in at least one embodiment, a method of reducing a compound having an atom in an oxidized state. The method includes a step of reacting a first compound having an atom in an oxidized state with a reducing agent to form a second compound having the atom in a reduced state relative to the first compound. The atom in an oxidized state is selected from the group consisting of Groups 2-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al. The reducing agent is selected from the group consisting of compounds described by formulae IA and IB:

embedded image

In another embodiment, a method of reducing a compound having an atom in an oxidized state using gas phase reactants is provided. The method includes a step of providing a vapor of first compound. The atom in an oxidized state is selected from the group consisting of Groups 2-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al. The method also includes a step of providing a vapor of a reducing agent. The reducing agent is selected from the group consisting of compounds described by formulae IA and IB:

embedded image

wherein:

X¹is CR⁶(SiR¹R^1′R^1″) or N(SiR¹R^1′R^1″);

X²is CR⁷(SiR¹R^1′R^1″) or N(SiR¹R^1′R^1″); and

R¹, R^1′, R^1″, R², R³, R⁴, R⁵, R⁶, and R⁷are each independently H, C_1-10alkyl, C_6-14aryl, or C_4-14heteroaryl. The vapor of the first compound and the vapor of the reducing agent are reacted to form to a second compound having the atom in a reduced state relative to the first compound.

In another embodiment, a method of forming a layer by an ALD process is provided. The method includes a step of contacting a substrate with a vapor of a first compound having an atom in an oxidized state to form a first modified surface. The atom in an oxidized state is selected from the group consisting of Groups 2-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al. The first modified surface is optionally contacted with an acid for a second predetermined pulse time to form a second modified surface. The first modified surface or the second modified surface is contacted with a reducing agent for a third predetermined pulse time to form the layer on the substrate. The reducing agent is selected from the group consisting of:

embedded image

In another embodiment, a method for forming a metal is provided. The method includes a step of contacting a metal-containing compound having at least one diazabutadiene ligand, the metal-containing compound having formula III or IV:

embedded image

with an activating compound, the activating compound being an acid or a diketone at a sufficient temperature to form a metal film,

wherein:

M is a transition metal selected from groups 3-10 of the periodic table, Ru, Pd, Pt, Rh, Ir, Mg, Al, Sn, or Sb;

R₈is C₁-C₁₂alkyl, amino (i.e., —NH₂), or C₆-C₁₈aryl;

R₉is hydrogen, C₁-C₁₀alkyl, C₆-C₁₈aryl, amino, C₁-C₁₂alkylamino, or C₂-C₂₂dialkylamino; and

X is Cl, Br, or I.

In another embodiment, a method for depositing a thin metal film on a surface of a substrate is provided. The method includes a step of contacting the substrate with a vapor of a metal-containing compound having formula III or IV to form a modified surface on the substrate:

embedded image

wherein:

M is a transition metal selected from groups 3-10 of the periodic table, Ru, Pd, Pt, Rh, Ir, Mg, Al, Sn, or Sb;

R₈is C₁-C₁₂alkyl, amino (i.e., —NH₂), or C₆-C₁₈aryl;

R₉is hydrogen, C₁-C₁₀alkyl, C₆-C₁₈aryl, amino, C₁-C₁₂alkylamino, or C₂-C₂₂dialkylamino; and

X is Cl, Br, or I. The modified surface is then contacted with a vapor of an activating compound to form at least a portion of the thin film on the surface of the substrate. Characteristically, the activating compound is an acid or a diketone at a sufficient temperature to form a metal film.

embedded image

wherein:

M is a transition metal selected from groups 3-10 of the periodic table, Ru, Pd, Pt, Rh, Ir, Mg, Al, Sn, or Sb;

R₈is C₁-C₁₂alkyl, amino (i.e., —NH₂), or C₆-C₁₈aryl;

R₉is hydrogen, C₁-C₁₀alkyl, C₆-C₁₈aryl, amino, C₁-C₁₂alkylamino, or C₂-C₂₂dialkylamino; and

X is Cl, Br, or I. The first modified surface is then contacted with a vapor of an activating compound to form a second modified surface. Characteristically, the activating compound is an acid or a diketone. The second modified surface is then contacted with a reducing agent having formula IA or IB to form at least a portion of a metal film on the substrate.

BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments of the present invention will become more fully understood from the detailed description and the accompanying drawings, wherein:

FIG. 1 provides additional examples of reducing agents encompassed by the present invention;

FIG. 2A is a schematic flowchart illustrating an ALD deposition process using the bis(trimethylsilyl) six-membered ring systems of an embodiment of the invention;

FIG. 2B is a schematic flowchart illustrating an ALD deposition process using the bis(trimethylsilyl) six-membered ring systems of an embodiment of the invention;

FIG. 2C is a schematic flowchart illustrating an ALD deposition process using the bis(trimethylsilyl) six-membered ring systems of an embodiment of the invention;

FIG. 2D is a schematic illustration of an ALD deposition system used in an embodiment of the present invention;

FIG. 2E is a schematic cross-section of a vapor source containing the reducing agents;

FIG. 3 provides examples of acids that can be reacted with the compounds of formula I;

FIG. 4 provides X-ray diffraction spectra showing CuCl formed by the solution reductions of CuCl₂and CuCl₂.H₂O by 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene;

FIG. 5 provides an X-ray diffraction spectrum showing copper metal formed by the solution reduction of CuCl₂to CuCl by 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene, and the subsequent disproportionation to copper metal by ethylenediamine;

FIG. 6 provides a scanning electron micrograph of a copper film (˜8 nm) on a ruthenium-coated (5 nm) SiO₂wafer;

FIG. 7 provides a cyclic voltammogram of pyrazine referenced to Ag/AgNO₃;

FIG. 8 provides an X-ray diffraction spectrum showing copper metal formed by the solution reduction of Cu(tmhd)₂by 1,4-bis(trimethylsilyl)-1,4-dihydropyrazine;

FIG. 9 provides a cross-sectional SEM micrograph of a copper film on a SiH substrate formed from Cu(dmap)₂;

FIG. 10 provides a top-down SEM micrograph of a copper film on Co/SiO₂formed from Cu(dmap)₂;

FIG. 11 provides XPS survey scans of a 51 nm copper film deposited on SiH at 150° C. formed from Cu(dmap)₂;

FIG. 12 provides an XPS high-resolution multiplex of the Cu 2p3 region of a film formed from Cu(dmap)₂;

FIG. 13 provides a cross-sectional SEM micrograph of a nickel film on a Si(100) substrate formed from Ni(dmap)₂;

FIG. 14 provides a cross-sectional SEM micrograph of a nickel film on a Ru/SiO₂substrate formed from Ni(dmap)₂;

FIG. 15 provides XPS survey scans of a 32 nm nickel film deposited on Pd at 150° C. formed from Ni(dmap)₂;

FIG. 16 provides an XPS high-resolution multiplex of the Ni 2p3 region of a film formed from Ni(dmap)₂;

FIG. 17 provides a cross-sectional SEM micrograph of a chromium film on a Ru/SiO₂substrate formed from Cr(dad^tBu2)₂;

FIG. 18 provides a cross-sectional SEM micrograph of chromium film on a SiO₂substrate formed from Cr(dad^tBu2)₂;

FIG. 19 provides XPS survey scans of a 124 nm thick chromium film deposited on thermal SiO₂at 225° C. formed from Cr(dad^tBu2)₂;

FIG. 20 provides an XPS high-resolution multiplex of the Cr 2p3 region of a film formed from Cr(dad^tBu2)₂;

FIG. 21 provides a cross-sectional SEM micrograph of a manganese film on a Ru/SiO₂substrate formed from Mn(dad^tBu2)₂;

FIG. 22 provides a top-down SEM micrograph of a manganese film on a Ru/SiO₂substrate formed from Mn(dad^tBu2)₂;

FIG. 23 provides XPS survey scans of a 27 nm manganese film deposited on SiO₂at 225° C. formed from Mn(dad^tBu2)₂;

FIG. 24 provides an XPS high-resolution multiplex of the Mn 2p3 region of a film formed from Mn(dad^tBu2)₂;

FIG. 25 provides a cross-sectional SEM micrograph of an iron film on a thermal SiO₂substrate formed from Fe(dad^tBu2)₂;

FIG. 26 provides a top-down SEM micrograph of an iron film on thermal SiO₂formed from Fe(dad^tBu2)₂;

FIG. 27 provides XPS survey scans of a 35 nm thick iron film deposited on Ru/SiO₂at 225° C. formed from Fe(dad^tBu2)₂;

FIG. 28 provides an XPS high-resolution multiplex of the Fe 2p3 region of a film formed from Fe(dad^tBu2)₂;

FIG. 29 provides a cross-sectional SEM micrograph of a cobalt film on a Ru/SiO₂substrate formed from Co(dad^tBu2)₂;

FIG. 30 provides a top-down SEM micrograph of a cobalt film on a thermal SiO₂substrate formed from Co(dad^tBu2)₂;

FIG. 31 provides XPS survey scans of a 24 nm thick cobalt film deposited on Ru/SiO₂at 180° C. from Co(dad^tBu2)₂;

FIG. 32 provides an XPS high-resolution multiplex of the Co 2p3 region of a film formed from Co(dad^tBu2)₂;

FIG. 33 provides an X-ray diffraction spectrum of showing cobalt metal on a SiO₂substrate formed from Co(dad^tBu2)₂;

FIG. 34 provides a cross-sectional SEM micrograph of a nickel film on a Ru/SiO₂substrate formed from Ni(dad^tBu2)₂;

FIG. 35 provides a top-down SEM micrograph of a nickel film on a copper substrate formed from Ni(dad^tBu2)₂;

FIG. 36: provides XPS survey scans of a 34 nm thick nickel film deposited on Ru/SiO₂at 180° C. from Ni(dad^tBu2)₂;

FIG. 37: provides an XPS high-resolution multiplex of the Ni 2p3 region for a film formed from Ni(dad^tBu2)₂;

FIG. 38 provides X-ray diffraction (XRD) spectra for solution reaction precipitates formed from the reaction with titanium tetrachloride and CHD (e.g., formula IA) and titanium tetrachloride and DHP (e.g., formula IB);

FIG. 39A provides an SEM cross-section for an ALD film deposited on a platinum substrate from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 39B provides an SEM cross-section for an ALD film deposited on a silicon substrate with a thermal silicon oxide layer from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 39C provides an SEM cross-section for an ALD film deposited on a palladium substrate from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 39D provides an SEM cross-section for an ALD film deposited on a cobalt substrate from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 40 provides XPS survey scans for an ALD film deposited on a platinum substrate from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 41 provides XPS multiplex scans for an ALD film deposited on a platinum substrate from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 42 provides XPS survey scans for ALD film deposited on a silicon substrate with a thermal silicon oxide layer from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 43 provides XPS multiplex scans for an ALD film deposited on silicon substrate with a thermal silicon oxide layer from the reaction with titanium tetrachloride and CHD at 180° C.;

FIG. 44A provides an SEM cross-section for an ALD film deposited on a platinum substrate from the reaction with titanium tetrachloride and DHP;

FIG. 44B provides an SEM cross-section for an ALD film on a silicon substrate with a thermal silicon oxide layer from the reaction with titanium tetrachloride and DHP;

FIG. 44C provides an SEM cross-section for an ALD film on a palladium substrate from the reaction with titanium tetrachloride and DHP;

FIG. 44D provides an SEM cross-section for an ALD film on a cobalt substrate from the reaction with titanium tetrachloride and DHP;

FIG. 45 provides X-ray diffraction (XRD) spectra for ALD films formed from the reaction with titanium tetrachloride and DHP on a platinum substrate and a silicon oxide substrate;

FIGS. 46A and B provide Energy-dispersive X-ray (EDS) spectra for ALD films formed from the reaction with titanium tetrachloride and DHP on a platinum substrate and a silicon oxide substrates;

FIG. 47 provides XPS survey scans for an ALD film deposited on a platinum substrate from the reaction with titanium tetrachloride and DHP at 100° C.;

FIG. 48 provides XPS multiplex scans for an ALD film deposited on a platinum substrate from the reaction with titanium tetrachloride and DHP at 100° C.;

FIG. 49 provides XPS survey scans for an ALD film deposited a silicon substrate with a thermal silicon oxide layer from the reaction with titanium tetrachloride and DHP at 100° C.;

FIG. 50 provides XPS multiplex scans for an ALD film deposited on a silicon substrate with a thermal silicon oxide layer from the reaction with titanium tetrachloride and DHP at 100° C.;

FIG. 51A provides a SEM cross-section of an aluminum film deposited on a silicon substrate with a thermal silicon oxide layer from trimethylaluminum and DHP at 180° C.;

FIG. 51B provides a SEM cross-section of an aluminum film deposited on a cobalt-coated silicon substrate from trimethylaluminum and DHP at 180° C.;

FIG. 52 provides XPS survey scans for an ALD film deposited on a cobalt-coated silicon substrate from trimethylaluminum and DHP at 180° C.;

FIG. 53 provides XPS multiplex scans for an ALD film deposited on a cobalt-coated silicon substrate from trimethylaluminum and DHP at 180° C.;

FIG. 54A provides an SEM cross-section for an ALD film deposited on a platinum substrate from antimony trichloride and DHP at 180° C.;

FIG. 54B provides an SEM top-down view for an ALD film deposited on a platinum substrate from antimony trichloride and DHP at 180° C.;

FIG. 54C provides an SEM cross-section for an ALD film deposited on a palladium substrate from antimony trichloride and DHP at 180° C.;

FIG. 54D provides an SEM top-down view for an ALD film deposited on a palladium substrate from antimony trichloride and DHP at 180° C.;

FIG. 55 provides XPS survey scans for an ALD film deposited on a palladium substrate from antimony trichloride and DHP at 180° C.;

FIG. 56 provides XPS multiplex scans for an ALD film deposited on a palladium substrate from antimony trichloride and DHP at 180° C.;

FIG. 57 provides sheet resistances for cobalt films grown on Ru, Pt, and Pd substrates;

FIG. 58 provides growth rates and sheet resistances versus temperature for cobalt films on a Ru substrate;

FIGS. 59A, B, C, and D provide SEM cross-sectional micrographs of cobalt films on Ru substrates;

FIGS. 60A, B, C, and D provide SEM cross-sectional micrographs of cobalt films on Ru substrates;

FIGS. 61A, B, C, and D provide SEM top-down view micrographs of cobalt films on Ru substrates;

FIGS. 62A, B, C, and D provide SEM top-down view micrographs of cobalt films on Ru substrates;

FIG. 63A provides a TEM image of methanol-washed un-capped Si particles;

FIG. 63B provides a TEM image of methanol-washed un-capped Si particles;

FIG. 64 provides an EDS analysis of methanol-washed Si particles;

FIG. 65 provides a PXRD spectrum of Si particles;

FIG. 66A provides a TEM image of Si particles;

FIG. 66B provides a size distribution of Si particles;

FIG. 67A provides a TEM image of Si particles in which methanol was added before reaction with 1-octanol;

FIG. 67B provides a TEM image of Si particles in which methanol was added before reaction with 1-octanol;

FIG. 68 provides the PXRD spectrum of the formed Ge particles; and

FIG. 69 provides a TEM image of the Ge nanoparticles. Since the samples were handled outside after isolation, it is believed that the lighter area around the nanoparticles may be due to the surface oxidation.

DESCRIPTION OF THE INVENTION

Reference will now be made in detail to presently preferred compositions, embodiments, and methods of the present invention which constitute the best modes of practicing the invention presently known to the inventors. The Figures are not necessarily to scale. However, it is to be understood that the disclosed embodiments are merely exemplary of the invention that may be embodied in various and alternative forms. Therefore, specific details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for any aspect of the invention and/or as a representative basis for teaching one skilled in the art to variously employ the present invention.

Except in the examples, or where otherwise expressly indicated, all numerical quantities in this description indicating amounts of material or conditions of reaction and/or use are to be understood as modified by the word “about” in describing the broadest scope of the invention. Practice within the numerical limits stated is generally preferred. Also, unless expressly stated to the contrary: percent, “parts of,” and ratio values are by weight; “R” groups include H, C_1-10alkyl, C_2-10alkenyl, C_6-14aryl (e.g., phenyl, halo, or C_4-14heteroaryl; the description of a group or class of materials as suitable or preferred for a given purpose in connection with the invention implies that mixtures of any two or more of the members of the group or class are equally suitable or preferred; description of constituents in chemical terms refers to the constituents at the time of addition to any combination specified in the description, and does not necessarily preclude chemical interactions among the constituents of a mixture once mixed; the first definition of an acronym or other abbreviation applies to all subsequent uses herein of the same abbreviation and applies mutatis mutandis to normal grammatical variations of the initially defined abbreviation; and, unless expressly stated to the contrary, measurement of a property is determined by the same technique as previously or later referenced for the same property.

It is also to be understood that this invention is not limited to the specific embodiments and methods described below, as specific components and/or conditions may, of course, vary. Furthermore, the terminology used herein is used only for the purpose of describing particular embodiments of the present invention and is not intended to be limiting in any way.

It must also be noted that, as used in the specification and the appended claims, the singular form “a,” “an,” and “the” comprise plural referents unless the context clearly indicates otherwise. For example, reference to a component in the singular is intended to comprise a plurality of components.

Throughout this application, where publications are referenced, the disclosures of these publications in their entireties are hereby incorporated by reference into this application to more fully describe the state of the art to which this invention pertains.

ABBREVIATIONS

“ALD” is atomic layer deposition.

“CVD is chemical vapor deposition.

“RT” means “room temperature.”

“s” means “seconds.”

“THF” means “tetrahydrofuran.”

“DME” means “1,2-dimethoxyethane.”

“CHD” means 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene.

“DHP” means 1,4-bis(trimethylsilyl)-1,4-dihydropyrazine.

“dad” means diazadiene.

“dad^tBu2” means “1,4-di-tert-butyldiazadiene.”

“XPS” means “X-ray photoelectron spectroscopy.”

“SEM” means “scanning electron microscopy.”

“XRD” means “X-ray diffraction.”

“acac” is acetylacetonate.

“Cp” is cyclopentadienyl.

“dmap” is 1-dimethylamino-2-methyl-2-propoxy.

“en” is ethylene diamine.

“Et” is ethyl.

“EtCp” is ethylcyclopentadienyl.

“Et₂amd” is N, N′-diethylacetamidinate.

“Et₂fmd” is N,N′-diethylformamidinate.

“hfac” is 1,1,1,5,5,5-hexafluoro-acetylacetonate.

“iPr₂amd” is N, N′-diisopropylacetamidinate.

“iPr₂fmd” is N,N′-diisopropylformamidinate.

“iPrCp” is isopropylcyclopentadienyl.

“Me” is methyl.

“Me₂amd” is N, N′-dimethylacetamidinate.

“Me₂fmd” is N,N′-dimethylformamidinate.

“Mes” is 2,4,6-Me₃C₆H₂or mesityl.

“MeCp” is methylcyclopentadienyl.

“Me₅Cp” is pentamethylcyclopentadienyl.

“Me₂fmd” is N,N′-dimethylformamidinate.

“Me₂bmd” is N—N′-dimethylbutyramidinate.

“Me₂pmd” is N, N′-dimethylpropionamidinate.

“mmp” is 1-methoxy-2-methyl-2-propoxy.

“OtPe” is tert-pentoxy.

“od” is octane-2 4-dionate.

“OiPr” is isopropoxy.

“OtBu” is tert-butoxy.

“OEt” is ethoxy.

“tBu₂amd” is N, N′-di-tert-butylacetamidinate.

“tBuEtamd” is N-tert-butyl-N′-ethylacetamidinate.

“tBuEtpmd” is N-tert-butyl-N′-ethyl-propionamidinate.

“tBuEtbmd” is N-tert-butyl-N′-ethylbutyramidinate.

“thd” is 2,2,6,6-tetramethyl-heptane-3,5-dionate.

“TEM” is transmission electron microscopy.

“PXRD” is powder X-ray diffraction.

“EDS” is Energy-dispersive X-ray spectroscopy.

The term “standard electrode potential” means the electrical potential (i.e., the voltage developed) of a reversible electrode at standard state in which solutes are at an effective concentration of 1 mol/liter, the activity for each pure solid, pure liquid, or for water (solvent) is 1, the pressure of each gaseous reagent is 1 atm., and the temperature is 25° C. Standard electrode potentials are reduction potentials.

In an embodiment, a method of reducing a compound having an atom in an oxidized state is provided. The method is particularly suited for forming metal-containing layers (e.g., metal layers) by ALD and by chemical vapor deposition (CVD). The method includes a step of reacting a first compound having an atom in an oxidized state with a reducing agent to form a second compound having the atom in a reduced state relative to the first compound. The atom in an oxidized state is selected from the group consisting of Groups 2-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al. In a refinement, the atom in an oxidized state includes atoms from this group having a standard electrode potential greater than −2.4 V relative to a reference electrode potential (e.g., standard hydrogen electrode or a standard Ag/AgNO₃electrode). In particular, such atoms are selected from the group consisting of Groups 3-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al. In a variation, M is a transition metal. Examples of useful transition metals for M include, but are not limited to, Cu, Ni, Co, Cr, Mn, Fe, W, Mo, Ti, Zr, Hf, Rf, V, Nb, Ta, Re, Ru, Rh, Ir, Pd, Pt, and Au. Particularly useful examples for M include, but are not limited to, Cr(II), Mn(II), Fe(II), Co(II), and Ni(II). In a refinement, M is a transition metal selected from groups 3-7 of the periodic table. The compounds with an atom in an oxidized state include an atom in an oxidation state greater than 0 (e.g., 1, 2, 3, 4, 5, or 6). Typically, the compounds with an atom in an oxidized state are metal-containing compounds. Useful metal-containing compounds are organometallic compounds and metal halides with vapor pressures sufficient for ALD or CVD processes. In a refinement, the compounds containing an atom in an oxidized state have vapor pressures of at least 0.01 torr at 100° C. In a further refinement, the compounds containing an atom in an oxidized state have vapor pressures of at least 0.05 torr to about 700 torr at 100° C. Characteristically, the reducing agent is selected from the group consisting of compounds described by formulae IA and IB:

embedded image

wherein:

X¹is CR⁶(SiR¹R^1′R^1″) or N(SiR¹R^1′R^1″);

X²is CR⁷(SiR¹R^1′R^1″) or N(SiR¹R^1′R^1″);

R¹, R^1′, R^1″, R², R³, R⁴, R⁵, R⁶, and R⁷are each independently H, C_1-10alkyl, C_6-14aryl, or C_4-14heteroaryl.

In a variation of compounds having formulae IA and IB, the reducing agent is selected from the group consisting of:

embedded image

and combinations thereof. The compound described by formula IIB is found to be particularly useful in forming metal-containing films. Particularly useful examples of the reducing agent are 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene and 1,4-bis(trimethylsilyl)-1,4-dihydropyrazine.

With reference to FIG. 1, additional examples of reducing agents are provided. In these examples, R¹, R^1′, R^1″, R², R³, R⁴, R⁵, R⁶, and R⁷are each independently H, C_1-10alkyl, C_6-14aryl, or C_4-14heteroaryl. In a refinement of the compounds described by formulae IA, IB, IIA, IIB, IIC, IID and the compounds of FIG. 1, R¹, R^1′, R^1″ are each independently C_1-10alkyl; R², R³, R⁴, R⁵are each independently H or C_1-10alkyl; and R⁶, and R⁷are H. In another refinement, R¹, R^1′, R^1″ are each independently hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, t-butyl, or phenyl. In still another refinement, R², R³, R⁴, and R⁵are each independently hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, t-butyl, or phenyl. In yet another refinement, R⁶, R⁷are each independently hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, t-butyl, or phenyl. In a particularly useful example, R¹, R^1′, R^1″ are methyl; R⁶, R⁷are hydrogen; and R², R³, R⁴, and R⁵are hydrogen or methyl. In another useful example, R¹, R^1′, R^1″ are methyl; R⁶, R⁷are hydrogen; R², R³, R⁴, and R⁵are hydrogen or methyl.

As set forth above, the first compound includes an atom in an oxidized state selected from Groups 2-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al. In particular, the atom in an oxidized state is in an oxidation state of +1, +2, +3, +4, +5, or +6. In a refinement, the atom in an oxidized state is a transition metal. Particularly useful examples of the atom in an oxidized state include, but are not limited to, Cu, Cr, Mn, Fe, Co, Ti, or Ni.

Although the present invention is not limited by the type of the first compound that includes an atom in an oxidized state, compounds of the following structures are particularly useful:

ML_n

ML_nY_m

wherein M is an atom selected from Groups 2 to 12 of the Periodic Table, As, Sb, Bi, Se, and Te; L is an anionic ligand; n is the number of anionic ligands; Y is a neutral ligand and m is the number of neutral ligands. Examples for Y include, but are not limited to, 2,2′-Bipyridine, H₂O, CH₃CN, C₅H₅N (pyridine), CO, ethylenediamine, 1,10-phenanthroline, PPh₃, NH₃, and the like. Typically, n will be of sufficient number to neutralize any charge on M. In a refinement, n is from 1 to 6 and m is from 1 to 5. Examples for L include optionally-substituted cyclopentadienyl, optionally-substituted β-diketonates, optionally-substituted amidinates, optionally-substituted guanidinates, optionally-substituted β-aminoalkoxides, optionally-substituted allyls, and optionally-substituted tris(pyrazolyl)borates.

In a variation, the first compound having an atom in an oxidized state is diazadiene compound described by the following formula:

embedded image

with an activating compound. The activating compound is an acid or a diketone at a sufficient temperature to form a metal film,

wherein:

M is a transition metal selected from Groups 3-10 of the Periodic Table, Ru, Pd, Pt, Rh, and Ir;

In a refinement, M are the atoms in an oxidized state as set forth above;

R₈is C₁-C₁₂alkyl, amino (i.e., —NH₂), or C₆-C₁₈aryl;

R₉is hydrogen, C₁-C₁₀alkyl, C₆-C₁₈aryl, amino, C₁-C₁₂alkylamino, or C₂-C₂₂dialkylamino and X is Cl, Br, or I. In a refinement, M is Mg, Al, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Sn, or Sb. In another refinement, when the metal-containing compound has formula II, M is Cr, Mn, Fe, Ni, Co, Zn, Al, or Mg. In still another refinement, M is Mg, Al, Sn, or Sb. In a useful variation, the C_2-5diketone is a 1, 3-diketone. It should be appreciated that the reaction of the present embodiment can be in the gas or liquid phases. In other variations, the reaction is an ALD reaction as set forth below.

In another variation, the first compound having an atom in an oxidized state is described by the following formula:

M((NR₁₀)₂)_n

wherein:

M is a metal selected from Groups 2 to 12 of the Periodic Table, As, Sb, Bi, Se, and Te or the subgroups for the atom in an oxidized state set forth above;

R₁₀is C_1-6alkyl, Si(R₁₁)₃;

R₁₁is C_1-6alkyl, and

n is 2, 3, 4, 5, or 6.

In another variation, the first compound having an atom in an oxidized state is described by the following formula:

M(OR₁₀)_n

wherein:

M is a metal selected from Groups 2 to 12 of the Periodic Table, As, Sb, Bi, Se, and Te or the subgroups for the atom in an oxidized state set forth above;

R₁₀is C_1-6alkyl; and

n is 2, 3, 4, 5, or 6.

In another variation, the first compound having an atom in an oxidized state is β-diketone compounds described by the following formula:

embedded image

M is a metal selected from Groups 2 to 12 of the Periodic Table, As, Sb, Bi, Se, and Te or the subgroups for the atom in an oxidized state set forth above;

R₁₂, R₁₃, R₁₄are independently H, C_1-10alkyl, C_1-8perfluoroalkyl, CF₃, C_1-10polyether groups, and the like; and

n is 2, 3, 4, 5, or 6.

In another variation, the first compound having an atom in an oxidized state is amidinate compounds described by the following formula:

embedded image

wherein:

M is a metal selected from Groups 2 to 12 of the Periodic Table, As, Sb, Bi, Se, and Te or the subgroups for the atom in an oxidized state set forth above;

R₁₅, R₁₆, R₁₇are independently H, C_1-10alkyl, C_1-8perfluoroalkyl, CF₃, C_1-10polyether groups, and the like; and

n is 2, 3, 4, 5, or 6.

Specific examples for the compounds including an atom in an oxidized state include, but are not limited to, Ag₂(tBu₂-amd)₂, Al(CH₃)₃, Al(NMe₂)₃, Al₂(NMe₂)₆, Al₂(C₂H₅)₄(μ-C₂H₅)₂, AlMe₂(OiPr), Ba(thd)₂, Ca(tBu₂amd)₂, Ce(thd)₄, Co₂(CO)₆(C₂R₂), Co(C₅H₅)₂, CpCo(CO)₂, CoCp(C₆Me₆), Co(C₆Me₆)₂, CpCo(CO)₂), Co(acac)₂, Co(acac)₃, Co(iPr₂amd), Co(thd)₃, Co(thd), Co(tBuEtamd)₂, Co(tBuEtpmd)₂, CrCp₂, Cr(acac)₃, Cr(Et₂amd)₃, Cu₂(iPr₂amd)₂, Cu(hfac)₂), Cu(hfac)₂, Cu(thd)₂, Dy(thd)₃, Fe(iPr₂amd)₂, Er(tBu₂amd)₃, Fe(tBuEtamd)₂, Fe(thd)₃, Ga(Et₂amd)₃, Gd(iPr₂amd)₃, Gd(thd)₃, HfCl₄, Hf(OtBu)₄, Hf(mmp)₄, Hf(Me₂fmd)₄, Hf(Me₂-pmd)₄, Hf(Me₂bmd)₄, Ho(thd)₃, Ir(acac)₃, La(thd)₃, La[N(SiMe₃)₂]₃, La(iPr₂fmd)₃, La(tBu₂fmd)₃, Lu(Et₂fmd)₃, Lu(Et₂amd)₃, Mg(tBu₂amd)₂, Mg(iPr₂amd)₂, Mn(thd)₃, Mn(EtCp)₂, Mo(Mes)(CO)₃, Nb(OEt)₅, Ni(dmamp)₂, Ni(tBu₂amd), Pb(OtBu)₂, Pr(iPr₂amd)₃, Si(OEt)₄, Si(OtBu)₃OH, Si(OtPe)₃OH, Ta(OEt)₅, Ti(iPr₂amd)₃, Ti(OMe)₄, Ti(OEt)₄, Ti(OiPr)₄, Nd(thd)₃, Ni(acac)₂, Ni(thd)₂, Pb(thd), Er(thd)₃, Eu(thd)₃, Fe(acac)₃, Ru(thd)₃, Ru(od)₃, Ru (tBu₂amd)₂(CO)₂, Sc(thd)₃, Sc(Et₂amd)₃, Sr(tBu₂amd)₂, Sm(thd)₃, Sr(thd)₂, Sr(methd)₂, Tm(thd)₃, Y(thd)₃Mg(thd)₂, Hf(NMe₂)₄, Hf(NEtMe)₄, Hf(NEt₂)₄, Pr[N(SiMe₃)₂]₃, Sb(NMe₂)₃, Ru(EtCp)₂, TiCl₄, NiCp₂, Sr(Me₅Cp)₂, Ta(NMe₂)₅, Ta(NEt₂)₅, Ta(NtBu)(NEt₂)₃, Ti(NMe₂)₄, Ti(NEtMe)₄, V(Et₂amd)₃, V(iPr₂amd)₃, WF₆, W(NtBu)₂(NMe₂)₂, Y(iPr2amd)₃, Zn[N(SiMe₃)₂]₂, Zn(CH₂CH₃)₂, Zn(iPr₂amd)₃, Zn(iPr₂amd)₂, Zr(Me₂amd)₄, Zr(Me₂fmd)₄, Zr(Me₂bmd)₄, Zr(Me₂pmd)₄, Zr(NMe₂)₄, Zr(NEtMe)₄, Zr(NEt₂)₄, ZrCp₂Me₂, Al(OR)₃, SiH₂(NR₂)₂, SiH(NR₂)₃, Si₂Cl₆, Si₃Cl₈, Ti(NMe₂)₄, Ti(NMeEt)₄, Ti(NEt₂)₄, CpTi(NMe₂)₃, (2-tBuallyl)Co(CO)₃, where R is C_1-6alkyl. Additional examples include, but are not limited to Cp and substituted versions of Ni, Co, Fe, Mn, Cr, Cu alkoxides with beta-amino groups, TiBr₄, TiI₄, TiF₄, halides and pseudohalides of Nb(V), Ta(V), Mo(IV), Mo(V), Mo(VI), W(IV), W(V), W(VI), Al(III), Si(IV), Ge(IV), Ge(II), Sn(II), Sn(IV), Sb(III), Sb(V), Al(NMe₂)₃, volatile Si(IV) compounds, volatile Si(IV) hydrides, volatile Ge(IV) compounds, volatile Ge(IV) hydrides, and halides of Se and Te.

In another refinement of the present embodiment, a method for forming a metal is provided. In this context, the metal is characterized as having metal atoms in the zero oxidation state. The present refinement can be carried out either in solution or in the vapor phase (e.g. ALD, CVD, etc) at temperatures from about 50 to 400° C. In another refinement, the metal deposition is carried out at temperatures from about 75 to 200° C.

In a further refinement, a method of forming a metal film by an ALD process is provided. The method comprises a deposition cycle which includes contacting the substrate with vapor of a first compound having an atom in an oxidized state as set forth above such that at least a portion of the vapor of the first compound adsorbs or reacts with a substrate surface to form a modified surface. The deposition cycle further includes contacting the modified surface with a vapor of the reducing agents set forth above to react and form at least a portion of the metal film. Typically, the first compound having an atom in an oxidized state is contacted with the reducing agent at a temperature from about 50 to 400° C. The present reaction is used in an ALD process as set forth below.

With reference to FIG. 2A, a method for forming a layer by an ALD process is schematically illustrated. In step a), substrate 10 is contacted with a vapor G1 of a first compound having an atom in an oxidized state to form a first modified surface 12. The atom in an oxidized state is selected from the group consisting Groups 2-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al. In particular, the first compound is as set forth above. In step b) the first modified surface 12 is contacted with a reducing agent G2 for a predetermined pulse time to form layer 14 on the substrate 10. The details of the reducing agent are as set forth above. Purging steps P1 and P2 are performed after steps a) and b), respectively. Loop L indicates that steps a), P1), b), and P2) are repeated a plurality of times in order to build up a final layer 16 of predetermined thickness monolayer by monolayer. Additional details of this ALD process are set forth below.

With reference to FIG. 2B, a method for forming a layer by an ALD process is schematically illustrated. In step a), substrate 10 is contacted with a vapor G1 of a first compound having an atom in an oxidized state to form a first modified surface 12. The atom in an oxidized state is selected from the group consisting of Groups 2-12 of the Periodic Table, the lanthanides, As, Sb, Bi, Te, Si, Ge, Sn, and Al In particular, the first compound is as set forth above. In step b), the first modified surface 12 is contacted with an acid Al for a second predetermined pulse time to form a second modified surface 12′. In step c), the second modified surface 12′ is contacted with a reducing agent G2 for a third predetermined pulse time to form layer 14 on the substrate. Purging steps P1, P2, and P3 are performed after steps a), b), and c), respectively. Loop L indicates that steps a), P1), b), P2), c), and P3 are repeated a plurality of times in order to build up a final layer 16 of predetermined thickness monolayer by monolayer. The details of the reducing agent are as set forth above. Additional details of this ALD process are set forth below.

With reference to FIG. 2D, deposition includes reaction chamber 22, substrate holder 24, and vacuum pump 26. Typically, the substrate is heated via heater 28. The method has a deposition cycle comprising contacting substrate 30 with a vapor of the first compound having an atom in an oxidized state as set forth above. In particular, the vapor is introduced from precursor source 32 into reaction chamber 22 for a predetermined pulse time. The pulse time is controlled via control valve 34. At least a portion of the vapor of the first compound modifies (e.g, adsorbs or reacts with) substrate surface 36 to form a modified surface. The method further comprises contacting the modified surface with a vapor of the reducing agent as set forth above from source 40 for a predetermined pulse time controlled by valve 42.

In a variation of the present embodiment, the method further comprises removing at least a portion of the vapor of the first compound that is lingering in the gas phase (i.e., has not adsorbed or reacted with the substrate) from the vicinity of the substrate before introducing the vapor of the reducing agent and removing at least a portion of the vapor of the reducing agent from the vicinity of the substrate. The metal-containing compound and the reducing agent are removed in purging steps by introducing a purge gas from purge source 44 into reaction chamber 22 for a predetermined purge time. The purge time is controlled by control valve 46.

In another variation, the method further includes at least one additional deposition cycle comprising sequentially contacting the substrate with the vapor of the first compound and then the vapor of the reducing agent. In some refinements, the substrate is contacted for a plurality of additional deposition cycles. For example, the substrate may be contacted with from 1 to several thousand deposition cycles depending on the thickness of the film desired. In particular, the substrate is contacted with the vapor of the first compound having an atom in an oxidized state and then the vapor of the reducing agent for 1 to 5000 deposition cycles. In another refinement, the substrate is contacted with the vapor of the first compound having an atom in an oxidized state and then the vapor of the reducing agent for 10 to 2000 deposition cycles. In still another refinement, the substrate is contacted with the vapor of the first compound having an atom in an oxidized state and then the vapor of the reducing agent for 20 to 1000 deposition cycles.

The system of FIG. 2D uses a source 40 for providing the vapor of a reducing agent. FIG. 2E provides a schematic cross-section of such a vapor source. Reducing agent source 40 includes vessel 60 and reducing agent 62 which is contained within and held by the vessel. Reducing agent 62 is one or more of the reducing agents set forth above. In particular, reducing agent 62 is described by IA, IB, IIA, IIB, IIC, and IID. In a refinement, at least a portion of the reducing agent is in the liquid phase. Valve 64 is attached to vessel 60. Valve 64 prevents escape of the reducing agent when the valve is closed and allows escape (i.e., passage into the ALD reaction chamber 22 through output conduit 66) of the reducing agent when the valve is opened. In a refinement, source 40 is a bubbler having an input conduit 70 for flowing a gas into vessel 60 and out of output conduit 66 thereby transferring the reducing agent. Valve 72 allows input conduit 70 to be opened and closed. In a refinement, in a refinement reducing agent source 40 includes fitting 74 positioned outside of and in fluid communication with valve 64. Optional, fitting 76 is position outside of and in fluid communication with valve 72. Fittings 74 and 76 allow attachment of the reducing agent source to ALD or CVD equipment.

In another embodiment, a system and method of forming a metal-containing film is provided. With reference to FIG. 2D, the vapor of the first compound having an atom in an oxidized state is introduced from precursor source 32 into reaction chamber 22 for a first predetermined pulse time. The first predetermined pulse time should be sufficiently long that available binding sites on the substrate surface (coated with metal layers or uncoated) are saturated (i.e., metal-containing compound attached). Typically, the first predetermined pulse time is from 1 second to 20 seconds. The first predetermined pulse time is controlled via control valve 34. At least a portion of the vapor of the metal-containing compound modifies (e.g, adsorbs or reacts with) substrate surface 36 to form a first modified surface. Reaction chamber 22 is then purged with an inert gas from purge source 44 for a first purge time. The first purge time is sufficient to remove the metal-containing compound from reaction chamber 22 and is typically from 0.5 seconds to 2 minutes.

In the next reaction step of the deposition cycle, an acid such as formic acid is then introduced from acid source 50 into reaction chamber 22 for a second predetermined pulse time. Examples of other suitable acids are provided in FIG. 3. In FIG. 3, R²⁰is H (i.e., hydride), C_1-8alkyl, C_6-12aryl, or C_1-8fluoroalkyl, X is N₃⁻, NO₃⁻, halide (e.g., Cl, F, Br), and o is an integer from 1 to 6. In a refinement, R²⁰is hydride, C_1-4alkyl, C_6-10aryl, or C_1-4fluoroalkyl, X is N₃⁻, NO₃⁻, halide (e.g., Cl, F, Br), and n is an integer from 1 to 6. Examples of useful alkyl groups include, but are not limited to, methyl, ethyl, n-propyl, isopropyl, n-butyl, t-butyl, iso-butyl, sec-butyl, and the like. Examples of useful aryl groups include, but are not limited to, phenyl, tolyl, naphthyl, and the like. The second predetermined pulse time is controlled via valve 52 and should be sufficiently long that available binding sites on the first modified substrate surface are saturated and a second modified surface is formed. Typically, the second predetermined pulse time is from 0.1 second to 20 seconds. Reaction chamber 22 is then purged with an inert gas for a second purge time (typically, 0.5 seconds to 2 minutes as set forth above).

In the final reaction step of the deposition cycle, a reducing agent as set forth above is then introduced from reducing agent source 40 into reaction chamber 22 for a third predetermined time controlled by valve 42. The third predetermined pulse time should be sufficiently long that available binding sites on the second modified substrate surface are saturated, with a metal layer being formed thereon. Typically, the third predetermined pulse time is from 0.1 second to 20 seconds. Reaction chamber 22 is then purged with an inert gas for a third purge time (typically, 0.5 second to 2 minutes as set forth above).

During film formation by the method of the present embodiment, the substrate will be at a temperature suitable to the properties of the chemical precursor(s) and film to be formed. In a refinement of the method, the substrate is set to a temperature from about 0 to 1000° C. In another refinement of the method, the substrate has a temperature from about 50 to 450° C. In another refinement of the method, the substrate has a temperature from about 100 to 250° C. In still another refinement of the method, the substrate has a temperature from about 150 to 400° C. In another refinement of the method, the substrate has a temperature from about 200 to 300° C.

Similarly, the pressure during film formation is set at a value suitable to the properties of the chemical precursors and film to be formed. In one refinement, the pressure is from about 10⁻⁶Torr to about 760 Torr. In another refinement, the pressure is from about 0.1 millitorr to about 10 Torr. In still another refinement, the pressure is from about 1 to about 100 millitorr. In yet another refinement, the pressure is from about 1 to 20 millitorr.

Pulse times and purge times also depend on the properties of the chemical precursors and the geometric shape of the substrates. Thin film growth on flat substrates uses short pulse and purge times, but pulse and purge times in ALD growth on 3-dimensional substrates can be very long. Therefore, in one refinement, pulse times and purge times are each independently from about 0.0001 to 200 seconds. In another refinement, pulse and purge times are each independently from about 0.1 to about 10 seconds.

In another embodiment, a method for forming a metal is provided. The method of this embodiment is an advancement of the method of U.S. patent application Ser. Nos. 13/818,154 and 13/930,471, the entire disclosures of which are hereby incorporated by reference. The method includes a step of contacting a metal-containing compound having at least one diazabutadiene ligand, the metal-containing compound having formula III or IV:

embedded image

with an activating compound. The activating compound is an acid or a diketone at a sufficient temperature to form a metal film,

wherein:

M is a transition metal selected from Groups 3-10 of the Periodic Table, Ru, Pd, Pt, Rh, and Ir;

R₈is C₁-C₁₂alkyl, amino (i.e., —NH₂), or C₆-C₁₈aryl;

R₉is hydrogen, C₁-C₁₀alkyl, C₆-C₁₈aryl, amino, C₁-C₁₂alkylamino, or C₂-C₂₂dialkylamino and X is Cl, Br, or I. In a refinement, M is Mg, Al, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Sn, or Sb. In another refinement, when the metal-containing compound has formula II, M is Cr, Mn, Fe, Ni, Co, Zn, Al, or Mg. In still another refinement, M is Mg, Al, Sn, or Sb. In a useful variation, the C_2-5diketone is a 1, 3-diketone. It should be appreciated that the reaction of the present embodiment can be in the gas or liquid phases. In other variations, the reaction is an ALD reaction as set forth below.

In another variation of the present embodiment, M is a metal, and in particular, a transition metal in a 0, 1+, 2+, 3+, or 4+ oxidation state. Examples of useful transition metals for M include, but are not limited to, Cu, Ni, Co, Cr, Mn, Fe, W, Mo, Ti, Zr, Hf, Rf, V, Nb, Ta, Re, Ru, Rh, Ir, Pd, Pt, and Au. Particularly useful examples for M include, but are not limited to, Cr(II), Mn(II), Fe(II), Co(II), and Ni(II).

As set forth above, R₈is a C₁-C₁₂alkyl or C₆-C₁₈aryl. In a variation, R₈is C₁-C₄alkyl. Specific examples for R₈include, but are not limited to, methyl, ethyl, propyl, n-butyl, sec-butyl, isobutyl, t-butyl, and the like. In a particularly useful refinement, R₁is t-butyl. In another variation, R₈is C₆-C₁₀aryl. In this refinement, specific examples for R₁include, but are not limited to, phenyl, biphenyl, napthyl, and the like. In a further refinement, it should be appreciated that the definitions for R₁include substituted variations of such groups. Examples of substituents include, but are not limited to, halogen, hydroxyl, —NO₂, and in the case of aryl, C₁-C₄alkyl. These substituents are particularly relevant when R₁is aryl.

As set forth above, R₉is C₁-C₁₂alkyl or C₆-C₁₈aryl. In a variation, R₉is C₁-C₄alkyl. In this refinement, specific examples for R₈include, but are not limited to, methyl, ethyl, propyl, n-butyl, sec-butyl, isobutyl, t-butyl, and the like. It should also be appreciated that when R₉is C₁-C₁₂alkylamino or C₂-C₂₂dialkylamino, the alkyl component is the same as set forth for when R₈is a C₁-C₁₂alkyl. Therefore, additional specific examples for R₉include, but are not limited to, methylamino, ethylamino, propylamino, diethylamino, dimethylamino, dipropylamino, and the like. In another refinement, R₉is C₆-C₁₀aryl. In this refinement, specific examples for R₁include, but are not limited to, phenyl, biphenyl, napthyl, and the like. In a further refinement, it should be appreciated that the definitions for R₉include substituted variations of such groups. Examples of substituents include, but are not limited to, halogen, hydroxyl, —NO₂, and in the case of aryl, C₁-C₄alkyl. These substituents are particularly relevant when R₁is aryl.

As set forth above, the methods of the invention use an activating compound, such as an acid. Particularly useful activating compounds are C_1-5organic acids (e.g., C_1-5carboxylic acids) such as formic acid and C_1-8diketones. Examples of other suitable acids are provided in FIG. 3. In FIG. 3, R²⁰is H (i.e., hydride), C_1-8alkyl, C_6-12aryl, or C_1-8fluoroalkyl, X is N₃⁻, NO₃⁻, halide (e.g., Cl, F, Br), and n is an integer from 1 to 6. In a refinement, R²⁰is hydride, C_1-4alkyl, C_6-10aryl, or C_1-4fluoroalkyl, X is N₃⁻, NO₃⁻, halide (e.g., Cl, F, Br), and n is an integer from 1 to 6. Examples of useful alkyl groups include, but are not limited to, methyl, ethyl, n-propyl, isopropyl, n-butyl, t-butyl, iso-butyl, sec-butyl, and the like. Examples of useful aryl groups include, but are not limited to, phenyl, tolyl, naphthyl, and the like.

In another variation, when M is Ni, Co, Fe, Mn, Mg, Zn or Cr, the diazabutadiene ligand is a radical anion having the following formula:

embedded image

In still another variation, when M is Ti, the diazabutadiene ligand is a dianion having the following formula:

embedded image

In yet another variation, when M is Al, the metal-containing compound includes a diazabutadiene ligand that is a radical ion having the following formula:

embedded image

and a diazabutadiene ligand that is a dianion having the following formula:

embedded image

With reference to FIG. 2C, a method of forming a thin metal film is schematically illustrated. In step a), substrate 10 is contacted with a vapor of a metal-containing compound G1 having formula III or IV to form a modified surface 12 on the substrate 10. The modified surface is then contacted with the activating compound Al to form at least a portion of the metal film on the substrate. The present variation is particularly useful when M is Co, Ni, Cr, Fe, and Mn.

With reference to FIG. 2B, another variation for forming a metal film is schematically illustrated. In step a), substrate 10 is contacted with a vapor of a metal-containing compound G1 having formula III or IV to form a first modified surface 12 on the substrate 10. In step b), the first modified surface 12 is then contacted with a vapor of the activating compound Al to form a second modified surface 12′. In step c), the second modified surface 12′ is then contacted with the vapor of a reducing agent G2 to form at least a portion of a metal film on the substrate. Examples of suitable reducing agents include, but are not limited to, hydrazine, hydrazine hydrate, alkyl hydrazines, 1,1-dialkylhydrazines, 1,2-dialkylhydrazines, H₂, H₂plasma, ammonia, ammonia plasma, silanes, disilanes, trisilanes, germanes, diborane, formalin, amine borane, dialkyl zinc, alkyl aluminum, alkyl gallium, alkyl indium complexes, and other plasma-based gases, and combinations thereof. Additional examples of reducing agents include the bis(trimethylsilyl) six-membered ring systems and related compounds as set forth above.

With reference to FIG. 2D, deposition system 20 includes reaction chamber 22, substrate holder 24, and vacuum pump 26. Typically, the substrate is heated via heater 28. The method has a deposition cycle comprising contacting substrate 30 with a vapor of the compound having formula III or IV or the variations of these compounds as set forth above. In particular, the vapor is introduced from precursor source 32 into reaction chamber 22 for a predetermined pulse time. The pulse time is controlled via control valve 34. At least a portion of the vapor of the compound having formula III or IV modifies (e.g, adsorbs or reacts with) substrate surface 36 to form a modified surface. The method further comprises contacting the modified surface with a vapor of the activating compound (e.g., C_1-5organic acids such as formic acid and C_1-8diketone) as set forth above from source 50 for a predetermined pulse time to form a metal layer or metal-containing layer.

In a variation of the present embodiment, the method further comprises removing at least a portion of the vapor of the compound having formula III or IV that is lingering in the gas phase (i.e., has not adsorbed or reacted with the substrate) from the vicinity of the substrate before introducing the vapor of the activating compound and removing at least a portion of the vapor of the activating compound from the vicinity of the substrate. The metal-containing compound and the activating compound are removed in purging steps by introducing a purge gas from purge source 44 into reaction chamber 22 for a predetermined purge time. The purge time is controlled by control valve 46.

In another variation, the method further includes at least one additional deposition cycle comprising sequentially contacting the substrate with the vapor of the compound having formula III or IV and then the vapor of the reducing agent. In some refinements, the substrate is contacted for a plurality of additional deposition cycles. For example, the substrate may be contacted with from 1 to several thousand deposition cycles depending on the thickness of the film desired. In particular, the substrate is contacted with the vapor of the compound having formula III or IV and then the vapor of the activating compound for 1 to 5000 deposition cycles. In another refinement, the substrate is contacted with the vapor of the compound having formula III or IV and then the vapor of the activating compound for 10 to 2000 deposition cycles. In still another refinement, the substrate is contacted with the vapor of the compound having formula III or IV and then the vapor of the activating compound for 20 to 1000 deposition cycles.

In another embodiment, a method of forming a metal-containing film is provided. With reference to FIG. 2D, the vapor of the compound having formula III or IV is introduced from precursor source 32 into reaction chamber 22 for a first predetermined pulse time. The first predetermined pulse time should be sufficiently long that available binding sites on the substrate surface (coated with metal layers or uncoated) are saturated (i.e., metal-containing compound attached). Typically, the first predetermined pulse time is from 1 second to 20 seconds. The first predetermined pulse time is controlled via control valve 34. At least a portion of the vapor of the metal-containing compound modifies (e.g, adsorbs or reacts with) substrate surface 36 to form a first modified surface. Reaction chamber 22 is then purged with an inert gas from purge gas source 44 for a first purge time. The first purge time is sufficient to remove the metal-containing compound from reaction chamber 22 and is typically from 0.5 seconds to 2 minutes.

In the next reaction step of the deposition cycle, the activating compound (e.g., C_1-5organic acids such as formic acid and C_1-8diketone) as set forth above is then introduced from source 50 into reaction chamber 22 for a second predetermined pulse time. The second predetermined pulse time is controlled via valve 52 and should be sufficiently long that available binding sites on the first modified substrate surface are saturated and a second modified surface is formed. Typically, the second predetermined pulse time is from 0.1 second to 20 seconds. The second predetermined pulse time is controlled via control valve 32. Reaction chamber 12 is then purged with an inert gas for a second purge time (typically, 0.5 seconds to 2 minutes as set forth above).

In the final reaction step of the deposition cycle, a reducing agent having formula IA or IB or the derivatives thereof as set forth above is then introduced from reducing agent source 40 into reaction chamber 22 for a third predetermined time controlled by valve 42. The third predetermined pulse time should be sufficiently long that available binding sites on the second modified substrate surface are saturated, with a metal layer being formed thereon. Typically, the third predetermined pulse time is from 0.1 second to 20 seconds. Reaction chamber 22 is then purged with an inert gas for a third purge time (typically, 0.5 seconds to 2 minutes as set forth above).

In a variation of the present embodiment, the method further includes at least one additional deposition cycle comprising sequentially contacting the substrate with the vapor of the compound having formula III or IV and then the vapor of the reducing agent. In some refinements, the substrate is contacted for a plurality of additional deposition cycles. For example, the substrate may be contacted with from 1 to several thousand deposition cycles depending on the thickness of the film desired. In particular, the substrate is contacted with the vapor of the compound having formula III or IV and then the vapor of the activating compound for 1 to 5000 deposition cycles. In another refinement, the substrate is contacted with the vapor of the compound having formula III or IV and then the vapor of the activating compound for 10 to 2000 deposition cycles. In still another refinement, the substrate is contacted with the vapor of the compound having formula III or IV and then the vapor of the activating compound for 20 to 1000 deposition cycles.

During film formation by the methods set forth above, the substrate will be at a temperature suitable to the properties of the chemical precursor(s) and film to be formed. In a refinement of the method, the substrate is set to a temperature from about 0 to 1000° C. In another refinement of the method, the substrate has a temperature from about 50 to 450° C. In another refinement of the method, the substrate has a temperature from about 100 to 250° C. In still another refinement of the method, the substrate has a temperature from about 150 to 400° C. In another refinement of the method, the substrate has a temperature from about 200 to 300° C.

The following examples illustrate the various embodiments of the present invention. Those skilled in the art will recognize many variations that are within the spirit of the present invention and scope of the claims.

Experimental Section

All experiments employed the use of anhydrous reagents and solvents, obtained from Sigma Aldrich. Syntheses of CHD and DHP were carried out using Schlenk line techniques, following previously referenced literature procedures contained in U.S. patent application Ser. No. 13/930,471 filed Jun. 28, 2013. Solution reactions and sample preparations for deposition experiments were conducted in an argon dry box. A Picosun R-75BE ALD reactor was used for thin film depositions. The reactor was operated under a constant stream of nitrogen (99.9995%) at a pressure of 10-12 mbar. Film thicknesses were determined using cross-sectional field emission scanning electron microscopy (FESEM) on a JEOL-6510LV electron microscope. Powder and thin film XRD experiments were performed on a Rigaku R200B 12 kW rotating anode diffractometer, using Cu K_αradiation (1.54056 Å) at 40 kV and 150 mA. XPS analysis was performed on a Perkin-Elmer 5500 XPS system using monochromatized Al K_αradiation. AugerScan v3.2 was used as the analysis software. Deposited thin films were exposed to air for several days prior to XPS analysis.

1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene

Scheme 1 illustrates the synthesis of 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene according to a literature procedure (Laguerre, M.; Dunogues, J.; Calas, R.; Duffaut, N. J. Organomet. Chem. 1976, 112, 49-59).

The air-sensitive product was a clear liquid, and was pure by ¹H NMR.

embedded image

Solution reductions were attempted with a variety of metal salts, using five molar equivalents of 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene (Table 1). Analysis by XRD confirmed that CuCl₂and CuCl₂.H₂O were each reduced to CuCl, (FIG. 4). However, CHD was unable to reduce any of the salts to elemental metal. A CuCl₂.DME adduct was reduced to a CuCl species by CDH. Subsequent addition of ethylenediamine resulted in a disproportionation reaction and precipitation of copper metal (FIG. 5).

TABLE 1

Solution reduction reactions of various metal salts with

1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene.

Reaction

Reaction

Time
Reflux
Time
solution →

ML₂
Sol
Vol
Temp
(min)
Temp
(min)
Precipitate

CuCl₂•H₂O
THF
15 ml
RT
60
—
—
milky white

→ CuCl

(insoluble)

CuCl₂•H₂O
THF
50 ml
0° C.
5
65° C.
65
milky white

→ CuCl

(insoluble)

CuCl₂•DME
DME
45 ml
RT
20
95° C.
75
milky white

→ add en

→ Cu metal

CuBr₂
THF
30 ml
RT
60
—
—
milky white

→ CuBr

(probably)

Cu(dmap)₂
THF
15 ml
RT
80
65° C.
60
dark orange

→ none

Cu(hfac)₂
THF
50 ml
RT
35
65° C.
60
light green

→ none

Cu(tmhd)₂
THF
50 ml
RT
60
65° C.
60
light blue

→ none

Cu(HCOO)₂
THF
50 ml
0° C.
5
65° C.
60
aqua green

→ none

CoCl₂
THF
50 ml
RT
60
65° C.
60
light blue

→ none

ZnCl₂
THF
50 ml
RT
105
65° C.
60
clear

→ none

Copper metal film growth was attempted by ALD using bis(dimethylaminopropanoxide)copper [Cu(dmap)₂] and 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene as reagents. Various substrates were tested for film growth, including Si(100), SiH, thermal SiO₂, Cu, Pt, Pd, TiN, and Ru/SiO₂. Each cycle consisted of a 3.0 s pulse of Cu(dmap)₂, a 10.0 s purge, a 1.0 s pulse of 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene, and a final 10.0 s purge. The 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene bubbler was maintained at 70° C. and the reaction chamber was held at 150° C. After 1,000 cycles, a copper film was clearly observable on the ruthenium substrate. A growth rate of 0.08 Å/cycle was determined after measurement of the film by SEM. Copper metal was not observed on any other substrates.

Scheme 2 provides a reaction scheme for a two-step ALD process using Cu(dmap)₂and 1,4-bis(trimethylsilyl)-2-methyl-1,4-cyclohexadiene:

embedded image

FIG. 6 provides a scanning electron micrograph of a copper film (˜8 nm) on a ruthenium-coated (5 nm) SiO₂wafer.

Computational Screening

Modifications to the ring substituents were explored computationally as a possible means of increasing reactivity. Using Gaussian 09, numerous bis(silyl)hexadiene structures were optimized with the 6-311+G(d,p) basis set at the B3LYP level in the gas phase. The total electronic energy of the silylated structure was subtracted from that of the aromatic structure. The energy difference of each molecular variant was expressed relative to the toluene analogue (CHD), which was normalized to zero. This model considers only the relative change in the electronic energy of the reducing agent upon aromatization, irrespective of the ligand system being used. Reaction kinetics and changes in system entropy were not taken into account. To reduce the computational effort, the trimethylsilyl groups were approximated by SiH₃groups. Scheme 3 provides a partial reaction showing the desilylation of the non-conjugated cyclohexadiene backbone resulting in the formation of an aromatic product:

embedded image

Table 2 shows representative combinations of ring substituents, along with the relative electronic energy differences. The structure with three methoxy groups shows the greatest improvement, with −3.636 kcal per mole upon aromatization relative to CHD. These data do not indicate significant improvements to the initial CHD structure, and thus, were not explored experimentally.

TABLE 2

Representative values of the relative electronic energy

difference upon aromatization with respect to CHD.

ΔE_rel

R₂
R₃
R₄
[kcal/mol]

H
H
H
−0.031

CH₃
H
H
—

CH₃
CH₃
H
−3.038

CH₃
H
CH₃
−0.036

H
CH₃
CH₃
0.089

CH₃
CH₃
CH₃
−3.147

NO₂
H
H
1.346

NO₂
NO₂
H
0.585

NO₂
H
NO₂
4.162

H
NO₂
NO₂
4.982

NO₂
NO₂
NO₂
3.618

OCH₃
H
H
2.560

OCH₃
OCH₃
H
−2.610

ΔE_rel

R₂
R₃
R₄
[kcal/mol]

OCH₃
H
OCH₃
2.070

H
OCH₃
OCH₃
0.389

OCH₃
OCH₃
OCH₃
−3.636

Si(CH₃)₃
H
H
−1.824

CH₃
NO₂
H
0.390

CH₃
H
NO₂
0.520

H
CH₃
NO₂
1.124

CH₃
CH₃
NO₂
−2.737

CH₃
NO₂
CH₃
0.256

NO₂
CH₃
CH₃
−1.648

NO₂
NO₂
CH₃
0.190

NO₂
CH₃
NO₂
2.487

CH₃
NO₂
NO₂
3.118

Subsequently, attention focused on modifying the ring system itself. It is postulated that an 8 π electron anti-aromatic structure would have a greater driving force toward aromatization than would any 4 π electron non-conjugated system. The 1,4-bis(trimethylsilyl)-1,4-dihydropyrazine (DHP) molecule was previously crystallized as a planar structure (Hausen, H. D.; Mundt, O.; Kaim, W. J. Organomet. Chem. 1985, 296, 321-337) possessing anti-aromatic character and a very low first vertical ionization energy of 6.16 (eV) (Kaim, W. J. Am. Chem. Soc. 1983, 105, 707-713). The trimethylsilyl moieties should be highly reactive towards the ligands (e.g. halogens), affording a trimethylsilated ligand byproduct. The resulting pyrazine dianion may simultaneously coordinate to the metal cation. Subsequent formation of an aromatic pyrazine byproduct may facilitate the reduction to elemental metal. Pyrazine has a cathodic potential of −2.4 V as measured relative to Ag/AgNO₃(FIG. 7). Thus, this approach may enable the thermal reduction of numerous metal precursors that are otherwise unreactive towards conventional coreagents at temperatures suitable for ALD.

1,4-bis(trimethylsilyl)-1,4-dihydropyrazine

1,4-bis(trimethylsilyl)-1,4-dihydropyrazine was prepared on a 40 g scale following a literature procedure (Sulzbach, R. A.; Iqbal, A. F. M. Angew. Chem. Int. Ed. Engl. 1971, 10, 127). The air-sensitive, yellow solid was purified by sublimation at 80° C./0.05 Torr. Preparative sublimation of the product yielded 97.1% recovery with no residue. The thermal decomposition temperature was determined to be greater than 265° C.

embedded image

Solution reactions were conducted with a variety of metal salts in THF. Upon refluxing with DHP, precipitate formation was observed from Cu, Ni, Co, Fe, Zn, and Cr salts (Table 3). Copper precipitate was observed as regions of copper-colored film on the flask and metallic flakes in solution, while cobalt and iron precipitated out as the ferromagnetic metals, sticking to the stir bar. The precipitate resulting from the reaction of copper bis(2,2,6,6-tetramethyl-3,5-heptanedionate) [Cu(tmhd)₂] with DHP was identified as copper metal by XRD (FIG. 8).

TABLE 3

Reaction matrix of metal salts with DHP

Reaction
Reflux
Reaction

Time

Time
solution →

ML₂
THF
Temp
(min)
Temp
(min)
Precipitate

Cu(dmap)₂
50 ml
RT
15
65° C.
60
Cu flakes; Cu &

green residue on

flask

Cu(tmhd)₂
70 ml
RT
30
65° C.
95
Cu & green flakes;

Cu & purple residue

on flask

NiCl₂
50 ml
RT
15
65° C.
70
Tan powder

CoCl₂
40 ml
RT
35
65° C.
60
Dark green powder

at RT (sticks to

stir bar)

FeCl₂
60 ml
RT
35
65° C.
60
Film on flask; black

powder (sticks to

stir bar)

ZnCl₂
75 ml
RT
15
65° C.
60
Few metallic flakes

→ white precipitate

after about 3 days

CrCl₂
70 ml
RT
23
65° C.
60
Silver-colored flakes

→ grey suspension

MnCl₂
50 ml
RT
15
65° C.
60
None

A binary process using Cu(dmap)₂and DHP at 150° C. failed to produce films on any substrates (Si(100), SiH, thermal SiO₂, Cu, Pt, Pd, TiN, and Ru/SiO₂, Co/SiO₂). A three-step process was subsequently attempted, whereby formic acid was used to produce the metal formate, which was then reduced to copper metal by 1,4-bis(trimethylsilyl)-1,4-dihydropyrazine. Subsequent applications of this general approach used numerous metal precursors, including Cu and Ni(dmap)₂and various metal 1,4-di-tert-butyldiazadiene complexes [M(dad^tBu2)₂]. Each deposition cycle consisted of a precursor pulse (3.0 s for M(dmap)₂and 6.0 s for M(dad^tBu2)₂), a 5.0 s purge, a 0.2 s pulse of formic acid, a 5.0 s purge, a 1.0 s pulse of DHP, and a final 10.0 s purge. Delivery temperatures were maintained at 100° C. and 150° C. for M(dmap)₂and M(dad^tBu2)₂precursors, respectively. Delivery temperatures were maintained at 70° C. and 21° C. for DHP and formic acid, respectively. Selected films from each deposition were characterized by SEM, XRD, and XPS as provided by FIGS. 9-37.

Aluminum and Titanium Experimental Section
Solution Screening Experiments:
TiCl₄+CHD

TiCl₄was reacted with a 2.5 molar excess of CHD in toluene. Upon addition of the TiCl₄to the CHD solution, the mixture turned a dark rust-brown color with a dark precipitate. The mixture was stirred at ambient temperature for ˜24 hrs. The solvent was removed under vacuum using a hot water bath. XRD analysis of the precipitate powder showed the major reflection of Ti metal (2θ=38.4°, FIG. 38).

TiCl₄+DHP

TiCl₄was reacted with a 2.6 molar excess of DHP in toluene. TiCl₄dissolved in toluene yielding a clear bright orange-colored solution. Upon addition of DHP, the solution immediately turned black with a very dark green/black precipitate. The mixture was stirred for ˜24 hrs at ambient temperature. The solvent was removed under vacuum using a hot water bath. A small peak in the XRD spectrum matched that for the major reflection of Ti metal (2θ=38.48, FIG. 38). FIG. 38 provides XRD patterns for solution reaction precipitates formed from the reaction with TiCl₄and CHD and TiCl₄and DHP. The spectra show peaks corresponding to titanium metal, thereby verifying the formation of titanium metal in the zero oxidation state.

SiCl₄+DHP

DHP completely dissolved in 40 mL of toluene, yielding a yellow solution. SiCl₄was directly added to the DHP solution, immediately producing a very faint white cloudiness near the bottom of the flask. The mixture was stirred at ambient temperature for ˜72 hrs. A white precipitate was allowed to settle to the bottom of the flask. The solvent was removed under vacuum using a hot water bath. The yellow solution became increasingly dark as the solvent was removed; approximately 2-3 mL of liquid remained that would not evaporate. The remaining dark yellow slurry immediately turned brown upon air exposure. XRD analysis of the powder did not show any identifiable reflections.

ALD Deposition Experiments:
TiCl₄+CHD

Titanium film growth was demonstrated using TiCl₄+CHD. Each cycle consisted of a 0.2 s pulse of TiCl₄, a 15.0 s purge, a 1.0 s pulse of CHD, and a 10.0 s purge. The TiCl₄bubbler was maintained at 20° C. and the reaction chamber was held at 180° C. The temperature of the solid state booster for CHD delivery was set to 75° C. After 1,000 cycles, definitive films were observed on Pd, Pt, and SiO₂with growth rates of approximately 0.09 Å/cycle, 0.15 Å/cycle, and 0.08 Å/cycle, respectively. Discontinuous (island-type) growth was observed by SEM on the Co substrate. Faint films were observed on the Ru and Cu substrates; their presence was confirmed by SEM analysis.

As used herein for the ALD experiments, platinum substrates consist of silicon substrates with a thermal oxide over coated with a platinum layer. Palladium substrates consist of silicon substrates with a thermal oxide over coated with a palladium layer. Cobalt substrates consist of silicon substrates with a thermal oxide over coated with a cobalt layer. It should be appreciated that SEM cross-sections are not able to distinguish the metal coating the substrate and the ALD film deposited thereon.

FIG. 39A provides an SEM cross-section for an ALD film deposited on a platinum substrate from the reaction with TiCl₄and CHD at 180° C. From the micrograph, the combined platinum and titanium thickness is about 25 nm with an approximate platinum layer thickness of about 14 to 18 nm and a titanium layer thickness from 7 to 11 nm. FIG. 39B provides an SEM cross-section for an ALD film deposited on a silicon substrate with a thermal silicon oxide layer from the reaction with TiCl₄and CHD at 180° C. From the micrograph, the titanium layer thickness is about 8 nm. FIG. 39C provides an SEM cross-section for an ALD film deposited on a palladium substrate from the reaction with titanium tetrachloride and CHD at 180° C. From the micrograph, the combined palladium and titanium thickness is about 29 nm with an approximate palladium layer thickness of about 12 to 14 nm and a titanium layer thickness from 15 to 17 nm. FIG. 39D provides an SEM cross-section for an ALD film deposited on a cobalt substrate from the reaction with titanium tetrachloride and CHD at 180° C. From the micrograph, the combined cobalt and titanium thickness is about 11 nm with an approximate cobalt layer thickness of about 6 to 10 nm and titanium layer thickness of about 1 to 5 nm.

FIGS. 40 and 41 respectively show XPS survey scans and XPS multiplex scans for an 8 nm ALD film deposited on a platinum substrate by reacting TiCl4 and CHD at 180 C. The scans confirm the presence of a titanium-containing film. FIGS. 42 and 43 respectively show XPS survey scans and XPS multiplex scans for an 8 nm ALD film deposited on a silicon oxide coated silicon substrate by reacting TiCl4 and CHD at 180 C. The scans confirm the presence of a titanium-containing film.

TiCl₄+DHP

Titanium film growth was demonstrated using TiCl₄+DHP. Each cycle consisted of a 0.2 s pulse of TiCl₄, a 15.0 s purge, a 1.0 s pulse of DHP, and a 10.0 s purge. The TiCl₄bubbler was maintained at 20° C. and the reaction chamber was held at 100° C. The temperature of the solid state booster for DHP delivery was set to 75° C. After 3,000 cycles, definitive film growth was achieved on Pd, Pt, TiN, Co, Cu, Ru, Si(100), and SiO₂. Average approximate growth rates were determined by SEM analysis: Pd (0.04 Å/cycle), Pt (0.11 Å/cycle), TiN (0.04 Å/cycle), Co (0.13 Å/cycle), Cu (0.11 Å/cycle), Ru (0.08 Å/cycle), Si (0.11 Å/cycle), and SiO₂(0.12 Å/cycle).

FIG. 44A provides an SEM cross-section for an ALD film deposited on a platinum substrate from the reaction with titanium tetrachloride and DHP. From the micrograph, the combined platinum and titanium thickness is about 48 nm with an approximate platinum layer thickness of about 14 to 18 nm and a titanium layer thickness from 30 to 34 nm. FIG. 44B provides an SEM cross-section for an ALD film on a silicon substrate with a thermal silicon oxide layer from the reaction with titanium tetrachloride and DHP. From the micrograph, the titanium layer thickness is about 35 nm. FIG. 44C provides an SEM cross-section for an ALD film on a palladium substrate from the reaction with titanium tetrachloride and DHP. From the micrograph, the combined palladium and titanium thickness is about 24 nm with an approximate palladium layer thickness of about 12 to 14 nm and a titanium layer thickness of about 10 to 12 nm. FIG. 44D provides an SEM cross-section for an ALD film on a cobalt substrate from the reaction with titanium tetrachloride and DHP. From the micrograph, the combined cobalt and titanium thickness is about 48 nm with an approximate titanium layer thickness of about 6 to 10 nm and a titanium layer thickness of about 38 to 42 nm.

FIG. 45 provides X-ray diffraction (XRD) spectra for ALD films formed from the reaction with TiCl₄and DHP on platinum substrates and silicon oxide substrates. It should be noted that the major Ti reflection appears on the Pt substrate as a minor component (2θ=38.48°) and the major TiO₂reflection appears on the SiO₂substrate as a minor component (2θ=44.67°). The thicknesses of the titanium films are about 30 to 35 nm. FIG. 46 provides EDS spectra for ALD films formed from the reaction with TiCl₄and DHP on platinum substrates and silicon oxide substrates. The oxide film gradually changes in oxidation state from TiO₂→Ti₂O₃→TiO→(by XPS analysis). It is hypothesized that oxide growth is controlled by oxygen diffusion through the existing oxide film (Brunette, D. M.; Tengvall, P.; Textor, M.; Thomsen, P. Titanium in Medicine; Springer, 2001; pp. 178-182). Finally, the thickness of the interfacial gradient layer is 39±2 nm for polished commercially prepared titanium by RBS analysis (Brunette, D. M.; Tengvall, P.; Textor, M.; Thomsen, P. Titanium in Medicine; Springer, 2001; pp. 178-182). FIGS. 47 and 48, respectively, show XPS survey scans and XPS multiplex scans for a 34 nm ALD film deposited on a platinum substrate by reacting TiCl4 and DHP at 100 C. The scans confirm the presence of a titanium-containing film. FIGS. 49 and 50, respectively, show XPS survey scans and XPS multiplex scans for a 35 nm ALD film deposited on a silicon oxide coated silicon substrate by reacting TiCl4 and DHP at 100 C. The scans confirm the presence of a titanium-containing film.

Al(CH₃)₃+DHP

Aluminum film growth was demonstrated using Al(CH₃)₃and DHP. Each cycle consisted of a 0.1 s pulse of Al(CH₃)₃, a 8.0 s purge, a 1.0 s pulse of DHP, and a 10.0 s purge. The temperature of the Al(CH₃)₃and DHP bubblers were 20° C. and 70° C., respectively. The reaction chamber was maintained at 180° C. After 1,000 cycles, films were observed on the Co and SiO₂substrates. The film on SiO₂was very thin, but observable by SEM. The growth rate on the Co substrate was approximately 0.15 Å/cycle.

FIG. 51A provides a SEM cross-section for an aluminum-containing film deposited on a silicon oxide coated silicon substrate from trimethylaluminum and DHP at 180° C. From the micrograph, the aluminum layer thickness of about 2 nm. FIG. 51B provides a SEM cross-section for an aluminum-containing film deposited on a cobalt-coated silicon substrate from trimethylaluminum and DHP at 180° C. From the micrograph, the combined cobalt and aluminum thickness is about 23 nm with the cobalt layer having a thickness from about 6 to 10 nm and the aluminum layer having a thickness from about 13 to 17 nm.

FIGS. 52 and 53 respectively show XPS survey scans and XPS multiplex scans for a 15 nm film deposited on a cobalt-coated substrate by reacting trimethylaluminum and DHP at 180 C. The scans confirm the presence of an aluminum-containing film.

SbCl₃+DHP

Antimony film growth was demonstrated using SbCl₃and DHP. Each cycle consisted of a 5.0 s pulse of SbCl₃, a 15.0 s purge, a 1.0 s pulse of DHP, and a 10.0 s purge. The temperature of the solid state booster for SbCl₃delivery was set to 40° C. The DHP bubbler was set to 70° C. and the reaction chamber was held at 180° C. After 1,000 cycles, films were deposited on Cu, Pt, and Pd substrates. A growth rate of 0.20 Å/cycle was achieved on the Pt substrate. Growth on the Cu and Pd substrates was non-uniform and granular. Analysis by top-down SEM revealed dense crystalline morphologies on the Pt and Pd substrates.

FIG. 54A provides an SEM cross-section for an ALD film deposited on a platinum substrate from SbCl₃and DHP at 180° C. From the micrograph, the combined platinum and antimony thickness is about 35 nm with the cobalt layer having a thickness from about 14 to 18 nm and the antimony layer having a thickness from about 17 to 21 nm. FIG. 54B provides an SEM top-down view for an ALD film deposited on a platinum substrate from antimony trichloride and DHP at 180° C. FIG. 54C provides an SEM cross-section for an ALD film deposited on a palladium substrate from SbCl₃and DHP at 180° C. From the micrograph, the combined platinum and antimony thickness is about 64 to 136 nm with the cobalt layer having a thickness from about 12 to 14 nm and the antimony layer having a thickness from about 50 to 124 nm. This film is granular and highly non-uniform.

FIG. 54D provides an SEM top-down view for an ALD film deposited on a palladium substrate from SbCl₃and DHP at 180° C. FIGS. 55 and 56, respectively, show XPS survey scans and XPS multiplex scans for a 20 nm film deposited on a platinum substrate by reacting SbCl₃and DHP at 180 C. The scans confirm the presence of an antimony-containing film.

Synthesis of Metal Complexes:

The synthesis of the 1,4-di-tert-butyl-1,4-diazabutadiene ligand (dad^tBu2) was performed in accordance with a literature procedure (Kliegman, J. M.; Barnes, R. K. Tetrahedron 1970, 26, 2555-2560):

embedded image

A previously reported procedure was used for the subsequent syntheses of Cr—, Mn—, Fe—, Co—, and Ni(dad^tBu2)₂compounds (Knisley, T. J.; Ariyasena, T. C.; Sajavaara, T.; Saly, M. J.; Winter, C. H. Chem. Mater. 2011, 23, 4417-4419). The syntheses of Mg— and Zn(dad^tBu2)₂followed an identical process. This general method was modified for the syntheses of Al— and Ti(dad^tBu2)₂compounds, whereby the reagents were cooled to −78° C. prior to cannulation of the ligand to the metal salt.

Crystal structures have been published for several M(dad^tBu2)₂complexes (M=Mg, Al, Cr, Fe, Co, Ni, Zn) (Cardiner, M. G.; Hanson, G. R.; Henderson, M. J.; Lee, F. C. Raston, C. L. Inorg. Chem. 1994, 33, 2456-2461; Geoffrey, F.; Cloke, N.; Dalby, C. I.; Henderson, M. J.; Hitchcock, P. B.; Kennard, C. H. L.; Lamb, R. N.; Raston, C. L. J. Chem. Soc., Chem. Commun. 1990, 1394-1396; Knisley, T. J.; Ariyasena, T. C.; Sajavaara, T.; Saly, M. J.; Winter, C. H. Chem. Mater. 2011, 23, 4417-4419). Ti(dad^tBu2)₂and Mn(dad^tBu2)₂have been reported in the literature, however, their structures have not been published (Tom Dieck, H.; Rieger, H. J.; Fendesak, G. Inorganica Chimica Acta 1990, 177, 191-197; Knisley, T. J.; Ariyasena, T. C.; Sajavaara, T.; Saly, M. J.; Winter, C. H. Chem. Mater. 2011, 23, 4417-4419). Following the synthesis outlined in Scheme 3, a low-resolution structure of Ti(dad^tBu2)₂was obtained with crystals grown by sublimation of the crude product at 120° C./0.05 Torr.

embedded image

The procedure outlined in Scheme 2 afforded a mixture of Al(dad^tBu2)Cl₂and Al(dad^tBu2)₂. These products were separable due to their difference in volatility. The novel Al(dad^tBu2)Cl₂compound sublimed at 105° C./0.05 Torr, while the unexpected Al(dad^tBu2)₂product sublimed at 130° C./0.05 Torr. Preparative sublimation studies on Al(dad^tBu2)Cl₂resulted in 88.9% recovered material, with 5.5% non-volatile residue. The melting point was determined as 157-158° C.

embedded image

The general class of M(^R2DAD)Cl₂(R=iPr, tBu, phenyl, methylphenyl, etc.) compounds may be especially useful for the deposition process described herein. Previously reported compounds of this family include 1,4-di(4-methylphenyl)1,4-diazabutadiene]ZnCl₂^Land Ti(dad^tBu2)Cl₂(Tom Dieck, H.; Rieger, H. J.; Fendesak, G. Inorganica Chimica Acta 1990, 177, 191-197) however, the latter exists as a dimer in the solid state, where the titanium atoms are bridged by two chloro ligands. To date, no compounds of this general class have been used as precursors for film growth.

ALD Deposition Experiments

Co(dad^tBu2)₂+HCOOH

Metallic cobalt films were grown by ALD using a binary process of Co(dad^tBu2)₂+HCOOH. Each cycle consisted of a 6.0 s pulse of Co(dad^tBu2)₂, a 5.0 s purge, a 0.2 s pulse of HCOOH, and a 5.0 s purge. The Co(dad^tBu2)₂was delivered by a solid state booster, maintained at a temperature of 140° C., affording a source temperature of 137±1° C. The HCOOH was delivered by a bubbler maintained at 23° C. Purified nitrogen was used as the carrier gas, with flow rates of 80 sccm for both precursors. The temperature of the reaction chamber spanned a range of 140-240° C. during the deposition experiments. All films were grown for 1000 cycles and allowed to cool to ambient temperature before exposure to air. Growth was achieved on a variety of metallic and insulating substrates, including Si(100), SiO₂, Cu, Pt, Pd, and Ru.

Cobalt films deposited within the 165-200° C. window had extremely low sheet resistivities of 1-2Ω/□ when grown on Ru, Pt, and Pd substrates (FIG. 57). The bulk resistivities of the cobalt films grown on Ru within the 165-225° C. temperature range are 13-19 μΩ cm; these values approach that of bulk cobalt metal (6.24 μΩ cm at 20° C.).

Films deposited on Ru substrates at 165° C., 180° C., and 200° C. had respective growth rates of 1.15 Å/cycle, 1.06 Å/cycle, 1.27 Å/cycle. A region of constant growth was observed from 170-180° C. (FIG. 58). Cross-sectional SEM micrographs show uniform, granular films within the 160-220° C. range (FIGS. 59-60). Top-down SEM micrographs of these films show a granular morphology suggestive of metallic films (FIGS. 61-62). Analogous processes have been used for the deposition of elemental Ni films and films containing Cr, Fe, and Mn.

Preparation of Silicon Particles

All reactions were carried out under an argon atmosphere using standard Schlenk line and glovebox techniques.

Un-Capped Si Particles

The synthesis of Si particles was performed by taking 2.5 mmol of SiCl₄and 5 mmol of 1,4-bis(trimethylsilyl)dihydropyrazine (DHP) in 15 mL of toluene and refluxing at 110° C. for 6 hours. Then, the solvent and other by-products were removed from the reaction mixture by vacuum drying for 30 mins. A dark brown solid product was isolated and purified using methanol by sonication followed by centrifuging 3 times. The resultant solid was then dried for further characterization. FIG. 63 provides TEM images of methanol washed un-capped Si particles. FIG. 64 provides EDS analysis of methanol washed Si particles. The EDS data exhibits an intense Si signal that is consistent with literature reports for silicon and negligible amounts of C and Cl. EDS collected in different areas of the grid shows very similar signal pattern. The possible existence of surface oxidation is noted since the samples were handled outside after isolation. FIG. 65 provides a PXRD scan of Si particles which matches published reference samples. FIG. 66 provides a TEM image and size distribution of Si particles;

1-Ocatanol Capped Si Particles

The reaction was initiated as explained above by taking SiCl₄and DHP in toluene and refluxing 110° C. After 3 hours of refluxing, 2 mL of 1-ocatanol was added to the reaction flask. The reaction was continued for another 3 hours. The isolation of particles was carried out as explained in the previous section. It was observed that 1-octanol may react with unreacted species in the reaction mixture. In order to prevent that, MeOH was used as a killing agent. FIG. 67 provides TEM images of Si particles in which methanol was added before reaction with 1-octanol. In general smaller particles are observed with two size distributions (3-4 nm and 12-20 nm)

Preparation of Germanium Particles

The synthesis of Ge particles was performed by reacting GeCl₄with 1,4-bis(trimethylsilyl)dihydropyrazine (DHP) at a GeCl₄:DHP=1:2 molar ratio. The reduction of GeCl₄is observed to be very fast compared to SiCl₄. The solution turns black (cloudy) immediately upon addition of GeCl₄to the DHP/Toluene mixture at room temperature. FIG. 68 provides the powder X-ray diffraction pattern of the formed Ge particles. The major peaks are matched with the Ge pdf pattern after annealing. FIG. 69 provides TEM images of the Ge nanoparticles. Since the samples were handled outside after isolation, it is believed that the lighter area around the nanoparticles may be due to the surface oxidation.

While embodiments of the invention have been illustrated and described, it is not intended that these embodiments illustrate and describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention.

	Number	Date	Country
	61974115	Apr 2014	US
	61902264	Nov 2013	US

	Number	Date	Country
Parent	14318501	Jun 2014	US
Child	15010762		US

	Number	Date	Country
Parent	13930471	Jun 2013	US
Child	14318501		US

BIS(TRIMETHYLSILYL) SIX-MEMBERED RING SYSTEMS AND RELATED COMPOUNDS AS REDUCING AGENTS FOR FORMING LAYERS ON A SUBSTRATE

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

International Classifications

Abstract

Description

Claims

CROSS-REFERENCE TO RELATED APPLICATIONS

Provisional Applications (2)

Continuations (1)

Continuation in Parts (1)