Black colorant for ink-jet printing ink, ink-jet printing ink, and aqueous pigment dispersion containing the black colorant

BACKGROUND OF THE INVENTION

[0001] The present invention relates to a black colorant for ink-jet printing ink, an ink-jet printing ink and an aqueous pigment dispersion containing the black colorant, and more particularly, to a black colorant for ink-jet printing ink exhibiting not only a high blackness and an excellent tinting strength, but also excellent dispersibility and light resistance in spite of fine particles; an ink-jet printing ink not only exhibiting excellent dispersion stability and light resistance, but also being free from clogging at a head portion of an ink-jet recording apparatus; and an aqueous pigment dispersion containing the black colorant.

[0002] In recent years, the development of various OA devices such as personal computers has rapidly spread in both business and domestic applications. An ink jet printer as one of recording apparatuses for these OA devices has also been widely used owing to the recent tendency of a low price and a high performance thereof.

[0003] Upon practical use, it is important that the ink jet printers have a higher reliability and a broader applicability. To meet the requirements, ink-jet printing inks used in the ink jet printers have been required to be free from clogging at a head portion of the printers, and exhibit an excellent dispersion stability, a high print image density, excellent water resistance and light resistance, or the like.

[0004] Hitherto, various dyes have been used as black colorants for ink-jet printing inks because of nonoccurrence of clogging at a head portion of the printers, a good dispersion stability, a good chroma and a good transparency. However, these dyes have problems due to toxicity. In order to solve the problems as well as satisfy the recent requirement for light resistance of printed matters, it has been attempted to use pigments instead of the dyes. As to this fact, Japanese Patent Application Laid-Open (KOKAI) No. 11-131001(1999) describes that “ . . . Dyes have problems such as poor water resistance and light resistance of images printed therewith owing to inherent properties thereof. To solve the problems, it has been attempted to develop inks using pigments instead of the dyes”.

[0005] When the black pigments such as carbon black, etc. are used as a black colorant for ink-jet printing inks, it is possible to form printed images having a high image density as well as excellent water resistance and light resistance as compared to in the case of using dyes as the black colorant. However, since 80% of the ink-jet printing inks are generally constituted of water, it has been difficult to disperse carbon black having a hydrophobic surface as well as organic black pigments in an aqueous medium. In addition, since the pigments are usually insoluble in water, etc., unlike the dyes, it has been difficult to preserve ink-jet printing inks using such pigments at a stable condition for a long period of time, and there arises such a problem that a head portion of an ink-jet recording apparatus tends to be clogged therewith.

[0006] On the other hand, if the particle size of the black colorant is reduced, it will be expected that the ink using such a black colorant can be prevented from clogging at the head portion, and can be improved in transparency. However, the black colorant having a small particle size tends to cause problems such as poor dispersibility in ink composition, low light resistance of ink using such a black colorant, or the like.

[0007] Conventionally, there are known ink-jet printing inks using pigments (Japanese Patent Application Laid-Open (KOKAI) Nos. 9-227812(1997), 11-131001(1999) and 2000-53901); colorants prepared by coupling pigments with resins particles using a coupling agent (Japanese Patent Nos. 2903631 and 3097208); and colorants prepared by bonding dyes onto the surface of silica particles through a coupling agent (Japanese Patent No. 3105511).

[0008] At present, it has been strongly required to provide a black colorant for ink-jet printing ink, which is not only excellent in tinting strength, light high blackness. However, conventional black colorants have still failed to satisfy these requirements.

[0009] That is, in Japanese Patent Application Laid-Open (KOKAI) Nos. 9-227812(1997) and 2000-53901, there is described an aqueous ink-jet recording liquid containing pigments and colloidal silica for the purpose of obtaining high-quality printed images. However, the pigments exhibit a poor dispersibility in an ink-jet printing ink composition, so that the resultant ink-jet printing ink fails to exhibit a good dispersion stability and a sufficient light resistance of printed images thereof. In addition, since a large amount of the colloidal silica not contributing to coloring is contained in the ink composition, it is difficult to sufficiently increase the pigment concentration thereof, thereby failing to obtain high-density printed images.

[0010] In Japanese Patent Application Laid-Open (KOKAI) No. 11-131001(1999), there is described an ink-jet recording liquid containing pigments adhered with fine particles of silica or barium sulfate. However, since an adhesion force of the fine particles onto the surface of the pigments is very weak, the fine particles tend to be desorbed from the pigments when dispersed in the ink-jet printing ink composition, so that it has been difficult to obtain an ink-jet printing ink having excellent dispersion stability and anti-clogging property as well as excellent light resistance of printed images thereof.

[0011] In Japanese Patent Nos. 2903631 and 3097208, there is described an ink-jet printing ink, in which the particles prepared by reacting pigments and resin particles using a coupling agent are dispersed. Since the coupling reaction is conducted in a solution as shown in the below-mentioned Comparative Examples, a sufficient shear force cannot be applied to the pigments. Therefore, it is difficult to disperse the black pigments in the form of fine particles, thereby failing to uniformly adhere the pigments onto the surface of the resin particles.

[0012] In Japanese Patent No. 3105511, there are described particles prepared by adhering dyes onto the surface of silica particles through a silane-based coupling agent. As shown in the below-mentioned Comparative Examples, since the dyes are adhered onto the surface of silica particles, the obtained colored silica particles fail to show a sufficient light resistance.

[0013] Further, in Japanese Patent Application Laid-Open (KOKAI) Nos. 11-323174(1999) and 2001-11339, there are described iron-based black composite particles comprising black iron oxide particles or black iron oxide hydroxide particles; a coating layer formed on the surface of the black iron oxide particles or black iron oxide hydroxide particles, which comprises organosilane compounds obtainable from alkoxysilanes, or polysiloxanes; and a carbon black coat formed on the surface of the coating layer. However, as shown the Comparative Example mentioned later, since the iron-based particles as core particles have a specific gravity as high as 4.3 to 5.5 and the amount of the carbon black coat is not more than 30 parts by weight based on 100 parts by weight of the core particles, the obtained iron-based black composite particles have a high specific gravity. Therefore, it may be difficult to obtain an ink-jet printing ink having a sufficient dispersion stability when the iron-based particles are used as a black colorant therefor.

[0014] As a result of the present inventors' earnest studies, it has been found that a black colorant having an average particle diameter of 0.001 to 0.15 μm and comprising extender pigments as core particles, a gluing agent-coating layer formed on at least a part of the surface of the core particle, and a black pigment coat formed onto at least a part of the gluing agent-coating layer, exhibits not only a high tinting strength and a high blackness, but also excellent dispersibility and light resistance in spite of fine particles, and is suitably used as a black colorant for ink-jet printing ink. The present invention has been attained on the basis of the findings.

SUMMARY OF THE INVENTION

[0015] An object of the present invention is to provide a black colorant for ink-jet printing ink, in which black pigments are adhered onto the surface of extender pigment through a gluing agent in the form of a uniform adhesion coat while being kept in an extremely finely dispersed state, and which can exhibit not only a high tinting strength and a high blackness but also excellent dispersibility and light resistance in spite of fine particles.

[0016] Another object of the present invention is to provide an ink-jet printing ink exhibiting not only excellent dispersion stability and light resistance but also being free from clogging at a head portion of an ink-jet recording apparatus.

[0017] A further object of the present invention is to provide an aqueous pigment dispersion containing the black colorant for ink-jet printing ink.

[0018] To accomplish the aims, in a first aspect of the present invention, there is provided a black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, comprising:

[0019] extender pigments as core particles;

[0020] a gluing agent-coating layer formed on at least a part of the surface of the core particle; and

[0021] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer.

[0022] In a second aspect of the present invention, there is provided a black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, a BET specific surface area value of 15 to 1,000 m2/g, a specific gravity of 1.3 to 3.0 and a blackness L* value of not more than 22.0, comprising:

[0023] extender pigments as core particles;

[0024] a gluing agent-coating layer formed on at least a part of the surface of said core particle; and

[0025] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer in the amount of 1 to 500 parts by weight based on 100 parts by weight of said extender pigments.

[0026] In a third aspect of the present invention, there is provided a black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, comprising:

[0027] extender pigments as core particles;

[0028] a gluing agent-coating layer formed on at least a part of the surface of said core particle;

[0029] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer; and

[0030] an outer coating layer formed on at least a part of said black pigment coat, comprising at least one material selected from the group consisting of anionic surfactants, nonionic surfactants, cationic surfactants and polymeric dispersing agents.

[0031] In a fourth aspect of the present invention, there is provided a black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, comprising:

[0032] extender pigments as core particles;

[0033] a coating layer formed on at least a part of the surface of said core particle, comprising at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon;

[0034] a gluing agent-coating layer formed on at least a part of the surface of said coating layer;

[0035] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer.

[0036] In a fifth aspect of the present invention, there is provided a black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, comprising:

[0037] extender pigments as core particles;

[0038] a coating layer formed on at least a part of the surface of said core particle, comprising at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon,

[0039] a gluing agent-coating layer formed on at least a part of the surface of said coating;

[0040] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer; and

[0041] an outer coating layer formed on at least a part of said black pigment coat, comprising at least one material selected from the group consisting of anionic surfactants, nonionic surfactants, cationic surfactants and polymeric dispersing agents.

[0042] In a sixth aspect of the present invention, there is provided an ink-jet printing ink comprising an ink base solution and black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, comprising:

[0043] extender pigments as core particles;

[0044] a gluing agent-coating layer formed on at least a part of the surface of said core particle; and

[0045] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer.

[0046] In a seventh aspect of the present invention, there is provided an ink-jet printing ink comprising the black colorant as defined in any one of first to fifth aspects and an ink base solution

[0047] the amount of said black colorant being 1 to 20% by weight based on the weight of the ink base solution.

[0048] In an eighth aspect of the present invention, there is provided a aqueous pigment dispersion comprising a base solution for the aqueous pigment dispersion and 10 to 40% by weight of black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, comprising:

[0049] extender pigments as core particles;

[0050] a gluing agent-coating layer formed on at least a part of the surface of said core particle; and

[0051] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer.

[0052] In a ninth aspect of the present invention, there is provided an ink-jet printing ink comprising a dispersant, water and a aqueous pigment dispersion comprising a base solution for the aqueous pigment dispersion and 10 to 40% by weight of black colorant for ink-jet printing ink, having an average particle diameter of 0.001 to 0.15 μm, comprising:

[0053] extender pigments as core particles;

[0054] a gluing agent-coating layer formed on at least a part of the surface of said core particle; and

[0055] a black pigment coat uniformly formed on at least a part of said gluing agent-coating layer.

BRIEF DESCRIPTION OF THE DRAWINGS

[0056]
FIG. 1 is a micrograph (×50,000) of silica particles obtained in Example 1;

[0057]
FIG. 2 is a micrograph (×50,000) of black pigments used in Example 1;

[0058]
FIG. 3 is a micrograph (×50,000) of a black colorant used in Example 1;

[0059]
FIG. 4 is a micrograph (×50,000) of a simple mixture of silica particles and black pigments used in Example 1;

[0060]
FIG. 5 is a micrograph (×50,000) of black pigments C used in Example 17;

[0061]
FIG. 6 is a micrograph (×50,000) of a black colorant for ink-jet printing ink obtained in Example 17; and

[0062]
FIG. 7 is a micrograph (×50,000) of a simple mixture of silica particles used in Example 1 and black pigments C used in Example 17 for comparison.

DETAILED DESCRIPTION OF THE INVENTION

[0063] The present invention will now be described in detail below.

[0064] First, the black colorant for ink-jet printing ink according to the present invention is described.

[0065] The black colorant for ink-jet printing ink according to the present invention has an average particle diameter of 0.001 to 0.15 μm and comprises extender pigments as core particles, a gluing agent-coating layer formed on at least a part of the surface of the respective core particles, and a black pigment coat formed onto at least a part of the gluing agent-coating layer.

[0066] As the extender pigments used in the present invention, there may be exemplified silica particles such as silica powder, white carbon particles, fine silicic acid powder and diatomaceous earth particles, clay particles, calcium carbonate particles, precipitated barium sulfate particles, alumina white particles, talc, transparent titanium oxide particles, satin white particles or the like. Among these extender pigments, silica particles are preferred in the consideration of good blackness of the obtained black colorant for ink-jet printing ink.

[0067] The extender pigments as the core particles may be those having any suitable shape such as spherical particles, granular particles. In the consideration of good dispersion stability of the obtained ink-jet printing ink, spherical particles or granular particles having a sphericity (average particle diameter (average maximum diameter)/average minimum diameter; hereinafter referred to merely as “sphericity”) of from 1.0 to less than 2.0.

[0068] The extender pigments as the core particles have an average particle diameter of preferably 0.0009 to 0.14 μm, more preferably 0.002 to 0.11 ,μm still more preferably 0.004 to 0.09 μm.

[0069] When the average particle diameter of the extender pigments as core particles is more than 0.14 μm, the obtained black colorant may become coarse, so that the ink-jet printing ink obtained by using such a coarse black colorant may tend to be deteriorated in dispersion stability, and cause clogging in a head portion of an ink-jet recording apparatus. When the average particle diameter of the extender pigments is less than 0.0009 μm, such particles may tend to be agglomerated due to fine particles. As a result, it may be difficult to form a uniform gluing agent-coating layer on the surface of the extender pigments, and uniformly adhere the black pigments in the form of a uniform adhesion coat onto the surface of the gluing agent-coating layer.

[0070] The extender pigments have a BET specific surface area value of preferably not less than 15 m2/g, more preferably not less than 20 m2/g, most preferably not less than 25 m2/g. When the BET specific surface area value is less than 15 m2/g, the extender pigments may become coarse and the obtained black colorant may also become coarse, so that the ink-jet printing ink produced by using such a coarse black colorant may tend to be deteriorated in dispersion stability, and cause clogging of a head portion of an ink-jet recording apparatus. In the consideration of forming a uniform gluing agent-coating layer on the surface of the extender pigments and uniformly adhering the black pigments in the form of a uniform adhesion coat onto the surface of the gluing agent-coating layer, the upper limit of the BET specific surface area value of the extender pigments is preferably 1,000 m2/g, more preferably 750 m2/g, most preferably 500 m2/g.

[0071] The extender pigments as the core particles used in the present invention have a specific gravity of preferably 1.3 to 4.2, more preferably 1.4 to 3.8, still more preferably 1.5 to 3.4. When the specific gravity of the core particles is more than 4.2, the specific gravity of the obtained black colorant may also become too high.

[0072] As to the hue of the extender pigments as the core particles, the C* value thereof is preferably not more than 12.0, more preferably not more than 10.0, still more preferably not more than 8.00. When the C* value of the core particles is more than 12.0, it may be difficult to obtain the aimed black colorant exhibiting a high blackness.

[0073] The extender pigments used in the present invention have a hiding power of preferably less than 200 cm2/g, more preferably not more than 150 cm2/g, most preferably not more than 100 cm2/g. When the hiding power of the extender pigments is not less than 200 cm2/g, it may be difficult to obtain a black colorant having a high blackness.

[0074] The gluing agent used in the present invention may be of any kind as long as the black pigment can be adhered onto the surface of the core particle therethrough. Examples of the preferred gluing agents may include organosilicon compounds such as alkoxysilanes, fluoroalkylsilanes and polysiloxanes; various coupling agents such as silane-based coupling agents, titanate-based coupling agents, aluminate-based coupling agents and zirconate-based coupling agents; oligomer compounds; polymer compounds or the like. These gluing agents may be used alone or in the form of a mixture of any two or more thereof. In the consideration of adhesion strength of the black pigment onto the surface of the core particle through the gluing agent, the more preferred gluing agents are the organosilicon compounds such as alkoxysilanes, fluoroalkylsilanes and polysiloxanes, and various coupling agents such as silane-based coupling agents, titanate-based coupling agents, aluminate-based coupling agents and zirconate-based coupling agents.

[0075] In particular, in the case where silica particles are used as the core particles, the gluing agent is preferably composed of organosilicon compounds or a silane-based coupling agent. Also, in the case where fine carbon black particles are used as the black pigments, the gluing agent is preferably composed of organosilicon compounds.

[0076] As organosilicon compounds used in the present invention, at least one organosilicon compound selected from the group consisting of (1) organosilane compounds obtained from alkoxysilane compounds; (2) polysiloxanes, or modified polysiloxanes selected from the group consisting of (2-A) polysiloxanes modified with at least one compound selected from the group consisting of polyethers, polyesters and epoxy compounds (hereinafter referred to merely as “modified polysiloxanes”), and (2-B) polysiloxanes whose molecular terminal is modified with at least one group selected from the group consisting of carboxylic acid groups, alcohol groups and a hydroxyl group; and (3) fluoroalkyl organosilane compounds obtained from fluoroalkylsilane compounds.

[0077] The organosilane compounds (1) can be produced from alkoxysilane compounds represented by the formula (I):

R1aSiX4-a (I)

[0078] wherein R1 is C6H5—, (CH3)2CHCH2— or n-CbH2b+1— (wherein b is an integer of 1 to 18); X is CH3O— or C2H5O—; and a is an integer of 0 to 3.

[0079] Specific examples of the alkoxysilane compounds may include methyltriethoxysilane, dimethyldiethoxysilane, phenyltriethyoxysilane, diphenyldiethoxysilane, dimethyldimethoxysilane, methyltrimethoxysilane, phenyltrimethoxysilane, diphenyldimethoxysilane, isobutyltrimethoxysilane, decyltrimethoxysilane or the like.

[0080] Among these alkoxysilane compounds, in view of the desorption percentage and the adhering strength of the black pigments, methyltriethoxysilane, methyltrimethoxysilane, dimethyldimethoxysilane and isobutyltrimethoxysilane, phenyltriethyoxysilane are preferred, and methyltriethoxysilane and methyltrimethoxysilane are more preferred.

[0081] As the polysiloxanes (2), there may be used those compounds represented by the formula (II):

[0082] wherein R2 is H— or CH3—, and d is an integer of 15 to 450.

[0083] As the modified polysiloxanes (2-A), there may be used:

[0084] (a1) polysiloxanes modified with polyethers represented by the formula (III):

[0085] wherein R3 is —(—CH2—)h—; R4 is —(—CH2—)i—CH3; R5 is —OH, —COOH, —CH═CH2, —CH(CH3)═CH2 or —(—CH2—)j—CH3; R6 is —(—CH2—)k—CH3; g and h are an integer of 1 to 15; i, j and k are an integer of 0 to 15; e is an integer of 1 to 50; and f is an integer of 1 to 300;

[0086] (a2) polysiloxanes modified with polyesters represented by the formula (IV):

[0087] wherein R7, R8 and R9 are —(—CH2—)q— and may be the same or different; R10 is —OH, —COOH, —CH═CH2, —CH(CH3)═CH2 or —(—CH2—)r—CH3; R11 is —(—CH2—)s—CH3; n and q are an integer of 1 to 15; r and s are an integer of 0 to 15; e′ is an integer of 1 to 50; and f′ is an integer of 1 to 300;

[0088] (a3) polysiloxanes modified with epoxy compounds represented by the formula (V):

[0089] wherein R12 is —(—CH2—)v—; v is an integer of 1 to 15; t is an integer of 1 to 50; and u is an integer of 1 to 300; or a mixture thereof.

[0090] As the terminal-modified polysiloxanes (2-B), there may be used those represented by the formula (VI):

[0091] wherein R13 and R14 are —OH, R16OH or R17COOH and may be the same or different; R15 is —CH3 or —C6H5; R16 and R17 are —(—CH2—)y—; wherein y is an integer of 1 to 15; w is an integer of 1 to 200; and x is an integer of 0 to 100.

[0092] In view of the desorption percentage and the adhering effect of the black pigment, polysiloxanes having methyl hydrogen siloxane units, the polysiloxanes modified with the polyethers and the polysiloxanes whose terminals are modified with carboxylic acid groups are preferred.

[0093] The fluoroalkyl organosilane compounds (3) may be produced from fluoroalkylsilane compounds represented by the formula (VII):

CF3 (CF2)zCH2CH2 (R18)a′SiX4-a′ (VII)

[0094] wherein R18 is CH3—, C2H5—, CH3O— or C2H5O—; X is CH3O— or C2H5O—; and z is an integer of 0 to 15; and a′ is an integer of 0 to 3.

[0095] Specific examples of the fluoroalkylsilane compounds may include trifluoropropyl trimethoxysilane, tridecafluorooctyl trimethoxysilane, heptadecafluorodecyl trimethoxysilane, heptadecafluorodecylmethyl dimethoxysilane, trifluoropropyl ethoxysilane, tridecafluorooctyl triethoxysilane, heptadecafluorodecyl triethoxysilane, or the like. Among these fluoroalkylsilane compounds, in view of the desorption percentage and the adhering strength of the black pigment, trifluoropropyl trimethoxysilane, tridecafluorooctyl trimethoxysilane and heptadecafluorodecyl trimethoxysilane are preferred, and trifluoropropyl trimethoxysilane and tridecafluorooctyl trimethoxysilane are more preferred.

[0096] As the silane-based coupling agents, there may be exemplified vinyltrimethoxysilane, vinyltriethoxysilane,

[0097] γ-aminopropyltriethoxysilane,

[0098] γ-glycidoxypropyltrimethoxysilane,

[0099] γ-mercaptopropyltrimethoxysilane,

[0100] γ-methacryloxypropyltrimethoxysilane,

[0101] N-β(aminoethyl) -γ-aminopropyltrimethoxysilane,

[0102] γ-glycidoxypropylmethyldimethoxysilane,

[0103] γ-chloropropyltrimethoxysilane or the like.

[0104] As the titanate-based coupling agents, there may be exemplified isopropyltristearoyl titanate, isopropyltris(dioctylpyrophosphate)titanate, isopropyltri(N-aminoethyl-aminoethyl)titanate, tetraoctylbis(ditridecylphosphate)titanate, tetra(2,2-diaryloxymethyl-1-butyl)bis(ditridecyl)phosphate titanate, his(dioctylpyrophosphate)oxyacetate titanate, bis(dioctylpyrophosphate)ethylene titanate or the like.

[0105] As the aluminate-based coupling agents, there may be exemplified acetoalkoxyaluminum diisopropilate, aluminumdiisopropoxymonoethylacetoacetate, aluminumtrisethylacetoacetate, aluminumtrisacetylacetonate or the like.

[0106] As the zirconate-based coupling agents, there may be exemplified zirconiumtetrakisacetylacetonate, zirconiumdibutoxybisacetylacetonate, zirconiumtetrakisethylacetoacetate, zirconiumtributoxymonoethylacetoacetate, zirconiumtributoxyacetylacetonate or the like.

[0107] It is preferred to use oligomer compounds having a molecular weight of from 300 to less than 10,000. It is preferred to use polymer compounds having a molecular weight of about 10,000 to about 100,000. In the consideration of forming a uniform coating layer on the core particles, the oligomers or polymer compounds are preferably in a liquid state, or soluble in water or various solvents.

[0108] The amount of the gluing agent-coating layer is preferably 0.01 to 15.0% by weight, more preferably 0.02 to 12.5% by weight, still more preferably 0.03 to 10.0% by weight (calculated as C) based on the weight of the gluing agent-coated core particles.

[0109] When the amount of the gluing agent-coating layer is less than 0.01% by weight, it may be difficult to adhere not less than one part by weight of the black pigment onto 100 parts by weight of the core particles. When the amount of the gluing agent-coating layer is more than 15.0% by weight, since it is possible to adhere 1 to 500 parts by weight of the black pigment onto 100 parts by weight of the core particles therethrough, it is unnecessary to form the gluing agent-coating layer in an amount of more than 15.0% by weight.

[0110] As the black pigments, there may be used carbon black particles such as furnace black, channel black and acetylene black, and aniline black particles. In the consideration of good tinting strength of the obtained black colorant, among these black pigments, the carbon black particles are preferred.

[0111] Specific examples of the carbon black particles may include #3050, #3150, #3250, #3750, #3950, MA100, MA7, #1000, #2400B, #30, MA77, MA8, #650, MA11, #50, #52, #45, #2200B and MA600 (tradenames; produced by Mitsubishi Kagaku Co., Ltd.); SEAST 9H, SEAST 7H, SEAST 6, SEAST 3H, SEAST 300 and SEAST FM (tradenames; produced by Tokai Carbon Co., Ltd.), Raven 1250, Raven 860, Raven 1000 and Raven 119OULTRA (tradenames; produced by Columbian Chemicals Co.); KETJENBLACK EC and KETJENBLACK EC600JD (tradenames; produced by Ketjen Black International Company); BALCK PEARLS-L, BALCK PEARLS 1000, BALCK PEARLS 4630, VULCAN XC72, REGAL 660 and REGAL 400 (tradenames; produced by Cabot Specialty Chemicals Inc.); or the like.

[0112] The amount of the black pigments adhered is preferably 1 to 500 parts by weight, more preferably 30 to 400 parts by weight, most preferably 50 to 300 parts by weight based on 100 parts by weight of the extender pigments.

[0113] When the amount of the black pigments adhered is less than one part by weight, the amount of the black pigments coated on the surface of the extender pigments is too small, so that it may be difficult to obtain the aimed black colorant having a high blackness. When the amount of the black pigments adhered is more than 500 parts by weight, the black pigments may tend to be desorbed from the surface of the obtained black colorant because of a too large amount of the black pigments adhered. As a result, the resultant black colorant may tend to be deteriorated in dispersibility in ink-jet printing ink.

[0114] The particle shape and particle size of the black colorant for ink-jet printing ink according to the present invention may mainly depend upon those of the extender pigments as core particles. Specifically, the black colorant may have a particle shape similar to that of the core particles as well as a slightly larger particle size than that of the core particles.

[0115] Specifically, the black colorant for ink-jet printing ink according to the present invention has an average particle diameter of usually 0.001 to 0.15 μm, preferably 0.003 to 0.12 μm, more preferably 0.005 to 0.10 μm.

[0116] When the average particle diameter of the black colorant is more than 0.15 μm, it may be difficult to inhibit the ink-jet printing ink obtained by using such a black colorant from clogging a head portion of an ink-jet recording apparatus, because of a too large particle size thereof. When the average particle diameter of the black colorant is less than 0.001 μm, the black colorant tends to be agglomerated together due to fine particles, so that it may become difficult to disperse the black colorant in the ink-jet printing ink.

[0117] The black colorant of the present invention have a BET specific surface area value of preferably 15 to 1,000 m2/g, more preferably 20 to 750 m2/g, most preferably 25 to 500 m2/g. When the BET specific surface area value is less than 15 m2/g, the obtained black colorant may become coarse, so that it may be difficult to inhibit the ink-jet printing ink obtained using such a black colorant from clogging a heat portion of an ink-jet recording apparatus. When the BET specific surface area value is more than 1,000 m2/g, the obtained black colorant may tend to be agglomerated together due to fine particles, resulting in deteriorated dispersibility in ink-jet printing ink.

[0118] As to the blackness of the black colorant of the present invention, the L* value thereof is preferably not more than 22.0, more preferably not more than 21.0, still more preferably not more than 20.0. When the L* value is more than 22.0, the obtained colorant may tend to exhibit a too high brightness and, therefore, may fail to show an excellent blackness. The lower limit of the L* value of the black colorant is 14.5.

[0119] The black colorant of the present invention has a specific gravity of preferably 1.3 to 3.0, more preferably 1.4 to 2.6, most preferably 1.5 to 2.2. When the specific gravity of the black colorant is more than 3.0, the ink-jet printing ink obtained by using such a black colorant may tend to be deteriorated in dispersion stability.

[0120] The tinting strength of the black colorant for ink-jet printing ink according to the present invention is preferably not less than 110%, more preferably not less than 115%, still more preferably not less than 120% when measured by the below-mentioned evaluation method.

[0121] The degree of desorption of the black pigments from the black colorant for ink-jet printing ink according to the present invention is preferably the rank 5 or 4, more preferably the rank 5 when visually observed and evaluated by the below-mentioned method. When the degree of desorption of the black pigments is the rank 1, 2 or 3, uniform dispersion of the black colorant for ink-jet printing ink in ink-jet printing inks or vehicles tends to be inhibited by the desorbed black pigments.

[0122] As to the light resistance of the black colorant for ink-jet printing ink according to the present invention, the ΔE* value thereof is preferably not more than 3.0, more preferably not more than 2.5, still more preferably not more than 2.0 when measured by the below-mentioned evaluation method. When the ΔE* value is more than 3.0, images printed with an ink-jet printing ink using such a black colorant as well as paints and resin compositions using the black colorant may fail to show a sufficient light resistance.

[0123] At least a part of the surface of the black colorant for ink-jet printing ink according to the present invention may be further coated, if required, with a surfactant and/or a polymeric dispersing agent. The black colorant coated with the surfactant and/or polymeric dispersing agent can be improved in dispersibility in ink-jet printing inks as well as dispersion stability as compared to the uncoated black colorant.

[0124] Examples of the surfactant may include anionic surfactants, nonionic surfactants and cationic surfactants. In the consideration of the effect of improving dispersibility in ink-jet printing inks as well as dispersion stability, among these surfactants, the anionic surfactants and nonionic surfactants are preferred.

[0125] Specific examples of the preferred anionic surfactants may include fatty acid salts, sulfuric acid esters, sulfonic acid salts, phosphoric acid esters or the like. Among these anionic surfactants, sulfuric acid esters and sulfonic acid salts are more preferred.

[0126] Specific examples of the preferred nonionic surfactants may include polyethylene glycol-type nonionic surfactants such as polyoxyethylene alkyl ethers and polyoxyethylene aryl ethers; polyhydric alcohol-type nonionic surfactants such as sorbitan fatty acid esters; or the like. Among these nonionic surfactants, polyethylene glycol-type nonionic surfactants are more preferred.

[0127] Specific examples of the preferred cationic surfactants may include amine salt-type cationic surfactants, quaternary ammonium salt-type cationic surfactants or the like. Among these cationic surfactants, the quaternary ammonium salt-type cationic surfactants are more preferred.

[0128] As the polymeric dispersing agent, there may be used alkali-soluble resins such as styrene-acrylic acid copolymers, styrene-maleic acid copolymers, polyacrylic acid derivatives or the like.

[0129] The coating amount of the surfactant and/or polymeric dispersing agent is preferably 0.1 to 10.0% by weight, more preferably 0.2 to 7.5% by weight, still more preferably 0.3 to 5.0% by weight (calculated as C) based on the weight of the black colorant coated with the surfactant and/or polymeric dispersing agent.

[0130] When the coating amount of the surfactant and/or polymeric dispersing agent is less than 0.1% by weight, it may be difficult to improve the dispersibility in ink-jet printing inks as well as the dispersion stability. When the coating amount of the surfactant and/or polymeric dispersing agent is more than 10% by weight, the effect of improving the dispersibility in ink-jet printing inks as well as the dispersion stability is already saturated. Therefore, it is unnecessary and meaningless to coat the black colorant with the surfactant and/or polymeric dispersing agent in such a large amount.

[0131] The black colorant coated with the surfactant and/or polymeric dispersing agent according to the present invention is substantially the same in particle size, BET specific surface area value, specific gravity, blackness, tinting strength, light resistance and degree of desorption of black pigments as those of the black colorant uncoated with the surfactant and/or polymeric dispersing agent according to the present invention.

[0132] In the black colorant for ink-jet printing ink according to the present invention, if required, the surface of the core particle may be previously coated with at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon. The black colorant for ink-jet printing ink using the core particles having such a coat composed of at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon (hereinafter referred to merely as “intermediate coat”), can be more effectively reduced in amount of black pigments desorbed from the surface of the extender pigments as compared to those using the core particles having no intermediate coat.

[0133] The amount of the intermediate coat is preferably 0.01 to 20% by weight (calculated as Al, SiO2 or a sum of Al and SiO2) based on the weight of the extender pigments as the core particles coated with the intermediate coat.

[0134] When the amount of the intermediate coat is less than 0.01% by weight, it may be difficult to attain the effect of reducing the amount of black pigments desorbed. As long as the amount of the intermediate coat is in the range of 0.01 to 20% by weight, the effect of reducing the amount of black pigments desorbed can be sufficiently attained. Therefore, it is unnecessary to form the intermediate coat in an amount of more than 20% by weight.

[0135] The black colorant for ink-jet printing ink produced by using the extender pigments as the core particles having the intermediate coat according to the present invention are substantially the same in particle size, BET specific surface area value, specific gravity, blackness, tinting strength and light resistance as those of the black colorant using the extender pigments as the core particles having no intermediate coat according to the present invention. The degree of desorption of the black pigments from the black colorant can be improved by forming the intermediate coat on the extender pigments as the core particles such that the black colorant can show a black pigment desorption degree of preferably the rank 5.

[0136] Next, the ink-jet printing ink containing the black colorant of the present invention is described.

[0137] The ink-jet printing ink of the present invention comprises the black colorant for ink-jet printing ink according to the present invention, a dispersant and water, and may further contain, if required, a water-soluble resin, a penetrant, a humectant, a water-soluble solvent, a pH modifier, a preservative or the like.

[0138] The amount of the black colorant contained in the ink-jet printing ink is usually 1 to 20% by weight based on the weight of the ink base solution.

[0139] The amount of the dispersant contained in the ink-jet printing ink is preferably 5 to 200% by weight, more preferably 7.5 to 150% by weight, still more preferably 10 to 100% by weight based on the weight of the black colorant for the ink-jet printing ink.

[0140] As the dispersant, there may be used the same surfactants and/or polymeric dispersing agents as used for coating the surface of the black colorant. In the consideration of good dispersibility of the black colorant in the ink-jet printing ink and good dispersion stability of the obtained ink, as the surfactant, anionic surfactants and nonionic surfactants are preferred, and as the polymeric dispersing agent, water-soluble resins such as styrene-acrylic acid copolymers are preferred.

[0141] As the solvent for the ink-jet printing ink, water may be used, if required, in combination with a water-soluble organic solvent. The amount of the water-soluble organic solvent contained in the ink-jet printing ink is preferably 1 to 50% by weight, more preferably 1 to 40% by weight, still more preferably 1 to 30% by weight based on the weight of the ink base solution.

[0142] Examples of the water-soluble organic solvent may include monohydric alcohols such as methanol, ethanol, n-propanol and isopropanol; dihydric alcohols such as ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol and dipropylene glycol; trihydric alcohols such as glycerol; polyalkylene glycols such as polyethylene glycol; lower alkyl esters of polyhydric alcohols such as diethylene glycol monobutyl ether, ethylene glycol monobutyl ether and ethylene glycol monoethyl ether; or the like. These water-soluble organic solvents may be used alone or in the from of a mixture of any two or more thereof. Among these water-soluble organic solvents, dihydric alcohols are preferred.

[0143] The black colorant dispersed in the ink-jet printing ink according to the present invention has an average dispersed particle diameter (D50) of preferably not more than 0.2 μm, more preferably not more than 0.15 μm, still more preferably not more than 0.1 μm. When the dispersed particle diameter (D50) of the black colorant contained in the ink is more than 0.2 μm, a head portion of the ink-jet recording apparatus may tend to be clogged therewith, and the dispersibility of the black colorant in the ink-jet printing ink may tend to be deteriorated.

[0144] The dispersion stability of the ink-jet printing ink according to the present invention is preferably the rank 4 or 5, more preferably the rank 5 when visually observed and evaluated by the below-mentioned method. The percentage of change in dispersed particle diameter (D50) is preferably not more than 10%, more preferably not more than 8%.

[0145] As to the blackness of printed images formed by using the ink-jet printing ink of the present invention, the L* value thereof is preferably not more than 22.0, more preferably not more than 21.0, most preferably not more than 20.0. When the L* value is more than 22.0, the resultant printed images tends to exhibit a too high brightness and, therefore, may fail to exhibit an excellent blackness. The lower limit of the L* value of the printed images is 14.5.

[0146] As to the light resistance of the printed images obtained by using the ink-jet printing ink of the present invention, the ΔE* value thereof is preferably not more than 3.0, more preferably not more than 2.5, still more preferably not more than 2.0.

[0147] The ink-jet printing ink of the present invention has an anti-clogging property at a head portion of preferably the rank 4 or 5, more preferably the rank 5 when visually observed and evaluated by the below-mentioned method.

[0148] Next, the aqueous pigment dispersion containing the black colorant for the ink-jet printing ink according to the present invention which dispersion is used for the production of the ink-jet printing ink, is described.

[0149] The aqueous pigment dispersion of the present invention contains the black colorant for ink-jet printing ink according to the present invention in an amount of usually 10 to 40% by weight, preferably 15 to 35% by weight.

[0150] The aqueous pigment dispersion of the present invention comprises the above black colorant for ink-jet printing ink, a dispersant and water, and may further contain, if required, a water-soluble resin, a water-soluble solvent or the like.

[0151] As the dispersant for the aqueous pigment dispersion, there may be used the same dispersants as those used in the above ink-jet printing ink.

[0152] The dispersed particle diameter (D50) of the black colorant contained in the aqueous pigment dispersion of the present invention is preferably not more than 0.15 μm, more preferably not more than 0.12 μm, still more preferably not more than 0.09 μm.

[0153] The dispersion stability of the aqueous pigment dispersion of the present invention is preferably the rank 4 or 5, more preferably the rank 5 when visually observed and evaluated by the below-mentioned method. The percentage of change in the dispersed particle diameter (D50) is preferably not more than 12%, more preferably not more than 10%.

[0154] The ink-jet printing ink obtained by using the aqueous pigment dispersion of the present invention can exhibit a more excellent dispersion condition such that the dispersed particle diameter (D50) of the black colorant contained in the ink is preferably not more than 0.15 μm, more preferably not more than 0.12 μm, still more preferably not more than 0.09 μm.

[0155] Next, the process for producing the black colorant for ink-jet printing ink according to the present invention, is described.

[0156] The black colorant for ink-jet printing ink according to the present invention can be produced by mixing the extender pigments as the core particles with the gluing agent to form a gluing agent-coating layer on at least a part of the surface of the respective extender pigments; and then mixing the extender pigments coated with the gluing agent with the black pigments to form a black pigment coat on at least a part of the gluing agent-coating layer.

[0157] The formation of the gluing agent-coating layer on the surface of the extender pigments as the core particles may be performed by mechanically mixing and stirring the extender pigments as the core particles with the gluing agent, or by mechanically mixing and stirring the extender pigments as the core particles and the gluing agent while spraying the gluing agent onto the extender pigments. A substantially whole amount of the gluing agent added can be used for coating the surface of the extender pigments as the core particles.

[0158] Meanwhile, in the case where alkoxysilanes or fluoroalkylsilanes are used as the gluing agent, a part of the alkoxysilanes or fluoroalkylsilanes may be coated in the form of organosilane compounds produced from the alkoxysilanes or fluoroalkyl organosilane compounds produced form fluoroalkylsilanes through the coating step. Even in such a case, subsequent adhesion of the black pigment on the gluing agent-coating layer is not adversely affected.

[0159] In order to uniformly coat the gluing agent over the surface of the extender pigments as the core particles, it is preferred that the agglomerated extender pigments are previously deaggregated using a crusher.

[0160] The mixing and stirring of the extender pigments as the core particles with the gluing agent, the mixing and stirring of the black pigment with the gluing agent-coated extender pigments, the mixing and stirring of the gluing agent with the extender pigments as the core particles coated with the black pigment coat through the gluing agent, and the mixing and stirring of the black pigment and the extender pigments having the colored adhesion layer and the gluing agent-coating layer formed thereon, is preferably carried out using an apparatus capable of applying a shear force to the powder mixture, especially such an apparatus capable of simultaneously effecting shear action, spatula stroking and compression. Examples of such apparatuses may include wheel-type kneaders, ball-type kneaders, blade-type kneaders, roll-type kneaders or the like. Among these apparatuses, the wheel-type kneaders are preferred to effectively practice the present invention.

[0161] Specific examples of the wheel-type kneaders may include edge runners (similar in meaning to mix muller, Simpson mill and sand mill), multi mill, Stotz mill, Wet pan mill, corner mill, ring muller or the like. Among these kneaders, preferred are edge runners, multi mill, Stotz mill, Wet pan mill and ring muller, and more preferred are edge runners. Specific examples of the ball-type kneaders may include vibration mill or the like. Specific examples of the blade-type kneaders may include Henschel mixer, planetary mixer, Nauter mixer or the like. Specific examples of the roll-type kneaders may include extruders or the like.

[0162] The conditions of the mixing and stirring treatment may be selected so as to uniformly coat the surface of the particle with the gluing agent. Specifically, the mixing and stirring conditions may be appropriately controlled such that the linear load is usually 19.6 to 1,960 N/cm (2 to 200 Kg/cm), preferably 98 to 1,470 N/cm (10 to 150 Kg/cm), more preferably 147 to 980 N/cm (15 to 100 Kg/cm); the treating time is usually 5 minutes to 24 hours, preferably 10 minutes to 20 hours; and the stirring speed is usually 2 to 2,000 rpm, preferably 5 to 1,000 rpm, more preferably 10 to 800 rpm.

[0163] The amount of the gluing agent added is preferably 0.15 to 45 parts by weight based on 100 parts by weight of the extender pigments as the core particles. When the gluing agent is added in an amount of 0.15 to 45 parts by weight, it is possible to adhere 1 to 500 parts by weight of the black pigment onto 100 parts by weight of the extender pigments as the core particles.

[0164] After the surface of the core particle is coated with the gluing agent, the black pigment is added, and then mixed and stirred with the coated core to adhere the black pigment onto the gluing agent-coating layer. The obtained particles may be further subjected to drying or heating treatments, if required.

[0165] As the adding method of the black pigments, a continuous addition method and a divided addition method may be exemplified. In case of continuously adding the black pigments, the black pigment may be added slowly and little by little, especially for a period of 5 minutes to 24 hours, preferably 5 minutes to 20 hours. In case of dividedly adding the black pigments, the adding step of the black pigments of 5 to 25 parts by weight based on 100 parts by weight of the extender pigments as the core particles, and mixing and stirring step under the following conditions can be repeated until the added amount of the black pigments reaches a predetermined amount thereof.

[0166] The mixing and stirring conditions may be appropriately selected so as to form a uniform black pigment coat on the gluing agent-coating layer, and may be controlled such that the linear load is usually 19.6 to 1,960 N/cm (2 to 200 Kg/cm), preferably 98 to 1,470 N/cm (10 to 150 Kg/cm), more preferably 147 to 980 N/cm (15 to 100 Kg/cm); the treating time is usually 5 minutes to 24 hours, preferably 10 minutes to 20 hours; and the stirring speed is usually 2 to 2,000 rpm, preferably 5 to 1,000 rpm, more preferably 10 to 800 rpm.

[0167] The amount of the black pigments added is usually 1 to 500 parts by weight, preferably 30 to 400 parts by weight, more preferably 50 to 300 parts by weight based on 100 parts by weight of the extender pigments as the core particles. When the amount of the black pigments added is out of the above-specified range, it may be difficult to obtain the aimed black colorant for ink-jet printing ink.

[0168] The heating temperature used in the drying and heating treatments is preferably 40 to 150° C., more preferably 60 to 120° C., and the heating time is preferably 10 minutes to 12 hours, more preferably 30 minutes to 3 hours.

[0169] Meanwhile, in the case where alkoxysilanes or fluoroalkylsilanes are used as the gluing agent, a coating layer composed of organosilane compounds obtainable from the alkoxysilanes or fluorine-containing organosilane compounds obtainable from the fluoroalkylsilanes is finally formed on the surface of the extender pigments as the core particles when treated through these steps.

[0170] In the production of the black colorant for ink-jet printing ink according to the present invention, the black pigments added are finely divided and adhered in the form of a uniform adhesion coat on the surface of the extender pigments via the gluing agent-coating layer when treated through the above steps.

[0171] The black colorant for ink-jet printing ink whose surface is coated with the surfactant and/or polymeric dispersing agent according to the present invention can be produced by coating the above-obtained black colorant with the surfactant and/or polymeric dispersing agent.

[0172] The formation of the surfactant and/or polymeric dispersing agent coating layer on the surface of the black colorant may be performed by mechanically mixing and stirring the black colorant with the surfactant and/or polymeric dispersing agent.

[0173] The amount of the surfactant and/or polymeric dispersing agent added is preferably 0.05 to 50 parts by weight based on 100 parts by weight of the black colorant. By adding the surfactant and/or polymeric dispersing agent in an amount of 0.05 to 50 parts by weight, it is possible to further improve a dispersibility of the black colorant in ink-jet printing ink, and a dispersion stability of the obtained ink.

[0174] The core particles may be previously coated, if required, with at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon, prior to mixing and stirring with the gluing agent.

[0175] The formation of the intermediate coat is conducted as follows. That is, an aluminum compound, a silicon compound or both the aluminum and silicon compounds are added to a water suspension prepared by dispersing the core particles in water. The resultant mixture is mixed and stirred together and then, if required, the pH value thereof is adjusted adequately, thereby forming the intermediate coat, on the surface of the core particle. Thereafter, the thus-obtained core particles coated with at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon are filtered out, washed with water, dried and then pulverized, and may be further subjected to subsequent treatments such as deaeration and compaction, if required.

[0176] Examples of the aluminum compound may include aluminum salts such as aluminum acetate, aluminum sulfate, aluminum chloride and aluminum nitrate, alkali aluminates such as sodium aluminate, or the like.

[0177] Examples of the silicon compound may include water glass #3, sodium orthosilicate, sodium metasilicate or the like.

[0178] Next, the process for producing the ink-jet printing ink according to the present invention, is described.

[0179] The ink-jet printing ink according to the present invention can be produced by mixing and dispersing a necessary amount of the black colorant for ink-jet printing ink according to the present invention, a dispersant and water, if required, together with various additives such as a penetrant, a humectant, a water-soluble solvent, a pH modifier and a preservative using a dispersing device to form a primary dispersion; further mixing and dispersing the obtained dispersion together with water, a water-soluble solvent and other additives; and then filtering the resultant dispersion using a membrane filter.

[0180] As the dispersing device, there may be used a ball mill, a sand mill, an attritor, a roll mill, a beads mill, a colloid mill, an ultrasonic homogenizer, a high-pressure homogenizer or the like.

[0181] Next, the process for producing the aqueous pigment dispersion according to the present invention is described.

[0182] The aqueous pigment dispersion according to the present invention can be produced by mixing and dispersing a necessary amount of the black colorant, a dispersant and water, if required, together with various additives such as a water-soluble resin and a water-soluble solvent using a dispersing device; and then filtering the resultant dispersion using a membrane filter.

[0183] As the dispersing device, there may be used a disper, a ball mill, a sand mill, an attritor, a roll mill, a beads mill, a colloid mill, an ultrasonic homogenizer, a high-pressure homogenizer or the like.

[0184] When the aqueous pigment dispersion of the present invention is used for the production of the ink-jet printing ink, a necessary amount of the aqueous pigment dispersion, a dispersant and water are mixed and dispersed, if required, together with various additives such as a water-soluble resin, a penetrant, a humectant, a water-soluble solvent, a pH modifier and a preservative using a dispersing device, and the resultant dispersion is filtered using a membrane filter to produce the ink-jet printing ink.

[0185] The aqueous pigment dispersion of the present invention may be used in such an amount that the concentration of pigments contained in the obtained ink-jet printing ink is in the range of 1 to 20% by weight.

[0186] As the dispersing device, there may be used the same dispersing devices as described above.

[0187] The point of the present invention is that the black colorant for ink-jet printing ink comprising the extender pigments as the core particles, the gluing agent-coating layer formed on at least a part of the surface of the extender pigments as the core particle and the black pigments adhered in the form of a uniform adhesion coat onto at least a part of the gluing agent-coating layer, can exhibit not only a high tinting strength and a high blackness, but also excellent dispersibility and light resistance in spite of fine particles.

[0188] The reason why the black colorant for ink-jet printing ink according to the present invention can exhibit a high blackness, is considered as follows. That is, since the extender pigments as the core particles have a low chroma and a low hiding power, the black pigments can exhibit an inherent hue thereof without being hidden and interfered by the hue of the core particles.

[0189] The reason why the black colorant for ink-jet printing ink according to the present invention can exhibit an excellent dispersibility, is considered as follows. That is, since the extender pigments as the core particles used have a relatively high dispersibility and the black pigments are strongly adhered onto the surface of the core particles through the gluing agent, the amount of the black pigments desorbed from the black colorant, so that the black colorant is well dispersed in the system without disturbance by the desorbed black pigments.

[0190] Also, when the surface of the black colorant for ink-jet printing ink is coated with the surfactant and/or polymeric dispersing agent, the ink-jet printing ink using such a coated black colorant can exhibit a more excellent dispersion stability. The reason therefor is considered to be that by coating the surface of the black colorant of the present invention with the surfactant and/or polymeric dispersing agent capable of acting as a hydrophilic surface modifier, the black colorant can be uniformly and stably dispersed in the ink-jet printing ink almost constituted of water.

[0191] The ink-jet printing ink of the present invention can exhibit not only an excellent dispersion stability, but also is free from clogging at a head portion of an ink-jet recording apparatus. In addition, printed images formed by using the ink-jet printing ink can exhibit a high blackness and an excellent light resistance.

[0192] The reason why the ink-jet printing ink of the present invention can exhibit an excellent dispersion stability, is considered as follow. That is, in general, the black pigments are present in the ink base solution in the form of dispersed particles having a dispersed particle diameter (D50) of about 0.2 μm and, therefore, tend to be self-agglomerated and precipitated with the passage of time. On the contrary, in the case of the black colorant for ink-jet printing ink according to the present invention, since the black pigments are adhered in the form of a uniform adhesion coat onto the surface of the extender pigments ordinarily used as an anti-precipitating agent, the individual black colorant particles can exist in the ink base solution in a well-dispersed condition.

[0193] The reason why the ink-jet printing ink of the present invention is free from clogging at a head portion of an ink-jet recording apparatus, is considered as follows. That is, in general, black pigments are difficult to finely disperse in the ink base solution. In addition, since the black pigments are ordinary present in the ink base solution in the form of dispersed particles having a dispersed particle diameter (D50) of about 0.2 μm, the black pigments tend to be self-agglomerated with the passage of time. As a result, the particle size of the agglomerated black pigments becomes larger than a nozzle diameter of the head portion of the ink-jet recording apparatus, thereby causing clogging of the head portion. On the contrary, in the case of the black colorant for ink-jet printing ink according to the present invention, since the black pigments are adhered onto the surface of the extender pigments in the form of a uniform adhesion coat, the black colorant for ink-jet printing ink according to the present invention can be present in the ink base solution in a well-dispersed condition without self-agglomeration thereof.

[0194] The reason why the printed images obtained using the ink-jet printing ink of the present invention can exhibit a high blackness, is considered as follows. That is, in the case of the black colorant for ink-jet printing ink according to the present invention, the black pigments which are usually present in the ink base solution in the form of dispersed particles having a dispersed particle diameter (D50) of about 0.2 μm, are adhered onto the surface of the extender pigments in the form of a uniform adhesion coat, namely the individual black pigments can be kept in such a state similar to particles extremely finely dispersed in the ink. In addition, the black colorant itself can exhibit an excellent dispersibility in the ink.

[0195] The reason why the printed images obtained using the ink-jet printing ink of the present invention can exhibit an excellent light resistance, is considered as follows. The black colorant of the present invention, which are obtained by adhering the black pigments having a remarkably excellent light resistance in the form of a uniform adhesion coat as compared to dyes onto the surface of the extender pigments, is used as a black colorant for the ink-jet printing ink.

[0196] The black colorant for ink-jet printing ink according to the present invention can exhibit not only a high tinting strength and a high blackness, but also excellent dispersibility and light resistance in spite of fine particles and, therefore, can be suitably used as a black colorant for ink-jet printing ink.

[0197] The ink-jet printing ink of the present invention can exhibit an excellent dispersion stability, and can be prevented from clogging a head portion of an ink-jet recording apparatus. In addition, the printed images obtained using the ink-jet printing ink of the present invention can exhibit a high blackness and an excellent light resistance. Therefore, the ink-jet printing ink of the present invention can be suitably used as an ink for ink-jet recording.

EXAMPLES

[0198] The present invention is described in more detail by Examples and Comparative Examples, but the Examples are only illustrative and, therefore, not intended to limit the scope of the present invention.

[0199] Various properties were evaluated by the following methods.

[0200] (1) The average particle size of the particles was expressed by an average value of 350 particles observed on a micrograph (×50,000).

[0201] (2) The sphericity was expressed by a ratio of average particle diameter (average maximum diameter) to average minimum diameter.

[0202] (3) The specific surface area was expressed by the value measured by a BET method.

[0203] (4) The specific gravity of each of the extender pigments, black pigments, black colorant was measured using a “Multi-Volume Densitometer 1305-Model” (manufactured by Micro-Meritix Co., Ltd.).

[0204] (5) The amounts of Al and Si present on the surface of the extender pigments coated with the intermediate coating layer, and the amount of Mn contained in Mn-containing hematite particles as the below-mentioned core particles 6 were measured by a fluorescent X-ray analyzer “3036M-Model” (manufactured by RIGAKU DENKI KOGYO CO., LTD.) according to “General Rule for Fluorescent X-ray Analysis” prescribed in JIS K0119.

[0205] (6) The amount of the gluing agent-coating layer formed on the surface of the extender pigments, the amount of the black pigments adhered to the black colorant, and the amount of the surfactant and/or polymeric dispersing agent coated on the surface of the black colorant, were respectively determined by measuring the carbon contents using “Horiba Metal, Carbon and Sulfur Analyzer EMIA-2200 Model” (manufactured by Horiba Seisakusho Co., Ltd.).

[0206] (7) The degree of desorption of the black pigments from the core particles was visually observed and evaluated by the following method, and the observation results were classified into the following five ranks. The rank 5 represents that the amount of the black pigments desorbed from the surface of the extender pigments was smallest.

[0207] That is, 2 g of the particles to be measured and 20 ml of ethanol were placed in a 50-ml conical flask and then was subjected to ultrasonic dispersion for 60 minutes. Thereafter, the obtained dispersion was centrifuged at a rotating speed of 10,000 rpm for 15 minutes to separate the particles from the solvent. The obtained particles were dried at 80° C. for one hour, and the micrograph (×50,000) thereof was visually observed to count the number of the desorbed and re-aggregated black pigment particles present in visual field of the micrograph. The micrograph was compared with a micrograph (×50,000) of mixed particles obtained by simply mixing the core particles with the black pigments without forming the gluing agent-coating layer. The results are classified into the following five ranks.

[0208] Rank 1; Number of desorbed and re-aggregated particles was substantially the same as that in the simply mixed particles;

[0209] Rank 2; 30 to 49 desorbed and re-aggregated particles per 100 core particles were recognized;

[0210] Rank 3; 10 to 29 desorbed and re-aggregated particles per 100 core particles were recognized;

[0211] Rank 4; 5 to 9 desorbed and re-aggregated particles per 100 core particles were recognized;

[0212] Rank 5; 0 to 4 desorbed and re-aggregated particles per 100 core particles were recognized.

[0213] (8) The hue of the extender pigments and the blackness of each of the black pigments and the black colorant, were measured by the following method.

[0214] That is, 0.5 g of each sample and 0.5 ml of castor oil were intimately kneaded together by a Hoover's muller to form a paste. 4.5 g of clear lacquer was added to the obtained paste and was intimately kneaded to form a paint. The obtained paint was applied on a cast-coated paper by using a 150 μm (6-mil) applicator to produce a coating film piece (having a film thickness of about 30 μm). The thus obtained coating film piece was measured by a Multi-Spectro-Colour-Meter “MSC-IS-2D” (manufactured by SUGA SHIKENKI CO., LTD.) to determine color specification values (L*, a* and b* values) according to JIS Z 8729. The hue of the extender pigments was expressed by the L*, a* and b* values and the blackness of each of the black pigments and the black colorant was expressed by the L* value. Here, the L* value represents a brightness, and the smaller the L* value, the more excellent the blackness. Meanwhile, the C* value representing chroma is calculated according to the following formula:

C* =
( (a*)2+(b*)2)½

[0215] (9) The tinting strength of each of the black colorant was measured by the following method.

[0216] That is, a primary color enamel and a vehicle enamel prepared by the below-mentioned method were respectively applied on a cast-coated paper by using a 150 μm (6-mil) applicator to produce coating film pieces. The thus obtained coating film pieces were measured by a Multi-Spectro-Colour-Meter “MSC-IS-2D” (manufactured by SUGA SHIKENKI CO., LTD.) to determine a color specification value (L* value) thereof according to JIS Z 8729. The difference between the obtained L* values was represented by a ΔL* value.

[0217] Next, as a standard sample for the black colorant, a mixed pigment was prepared by simply mixing the black pigments and the extender pigments at the same mixing ratio as used for the production of the black colorant for ink-jet printing ink. Using the thus prepared mixed pigment as standard sample, the same procedure as defined above was conducted to prepare an primary color enamel and a vehicle enamel, to form coating film pieces and to measure L* values thereof. The difference between the L* values was represented by a ΔLs* value.

[0218] From the obtained ΔL* value of the black colorant for ink-jet printing ink and ΔLs* value of the standard sample, the tinting strength (%) was calculated according to the following formula:

Tinting strength (%)=100+{(ΔLs* −ΔL*)×10}

Preparation of Primary Color Enamel

[0219] 10 g of the above sample particles, 16 g of an amino alkyd resin and 6 g of a thinner were blended together. The resultant mixture was added together with 90 g of 3 mm glass beads into a 140-ml glass bottle, and then mixed and dispersed for 45 minutes by a paint shaker. The obtained mixture was mixed with 50 g of an amino alkyd resin, and further dispersed for 5 minutes by a paint shaker, thereby obtaining an primary color enamel.

Preparation of Vehicle Enamel

[0220] 12 g of the above-prepared primary color enamel and 40 g of Aramic White (titanium dioxide-dispersed amino alkyd resin) were blended together, and the resultant mixture was mixed and dispersed for 15 minutes by a paint shaker, thereby preparing a vehicle enamel.

[0221] (10) The hiding power of each of the extender pigments and black pigments was measured by the cryptometer method according to JIS K5101-8.2 using the above-prepared primary color enamel.

[0222] (11) The light resistance of each of the black colorant for ink-jet printing ink was measured by the following method.

[0223] That is, the primary color enamel as prepared above was applied onto a cold-rolled steel plate (0.8 mm×70 mm×150 mm; JIS G-3141) and dried to form a coating film having a thickness of 150 μm. One half of the thus prepared test specimen was covered with a metal foil, and an ultraviolet light was continuously irradiated over the test specimen at an intensity of 100 mW/cm2 for 6 hours using “EYE SUPER UV TESTER SUV-W13” (manufactured by IWASAKI DENKI CO., LTD.). Then, the hues (L*, a* and b* values) of the UV-irradiated portion and the metal foil-covered non-irradiated portion of the test specimen were respectively measured using a Multi-Spectro-Colour-Meter “MSC-IS-2D” (manufactured by SUGA SHIKENKI CO., LTD.). The ΔE* value was calculated from differences between the measured hue values of the metal foil-covered non-irradiated portion and the UV-irradiated portion according to the following formula:

ΔE*=[(ΔL*)2+(Δa*)2+(Δb*)2]½

[0224] wherein ΔL* represents the difference between L* values of the non-irradiated and UV-irradiated portions; Δa* represents the difference between a* values of the non-irradiated and UV-irradiated portions; and Δb* represents the difference between b* values of the non-irradiated and UV-irradiated portions.

[0225] (12) The dispersed particle diameter (D50) of particles contained in the ink-jet printing ink and aqueous pigment dispersion was measured by a laser diffraction-type particle size distribution measuring device “Model HELOSLA/KA” (manufactured by SYMPATEC Co., Ltd.).

[0226] (13) The dispersion stability of each of the ink-jet printing ink and the aqueous pigment dispersion was evaluated as follows. That is, 25 ml of an ink-jet printing ink or aqueous pigment dispersion to be measured was placed in a tube color comparison and allowed to stand at 60° C. for one month. Then, the degree of precipitation of the black colorant contained in the ink-jet printing ink or aqueous pigment dispersion was visually observed and evaluated. The observation results were classified into the following five ranks.

[0227] Rank 1: Length of uncolored portion was not less than 10 cm;

[0228] Rank 2: Length of uncolored portion was from 5 cm to less than 10 cm;

[0229] Rank 3: Length of uncolored portion was from 1 cm to less than 5 cm;

[0230] Rank 4: Length of uncolored portion was less than 1 cm;

[0231] Rank 5: Uncolored portion was not recognized.

[0232] (14) The percentage of change in dispersed particle diameter (D50) of particles contained in each of the ink-jet printing ink and aqueous pigment dispersion was determined as follows. That is, after an ink or aqueous pigment dispersion to be measured was allowed to stand at 60° C. for one month, the dispersed particle diameter (D50) of particles contained therein was measured by a laser diffraction-type particle size distribution measuring device “Model HELOSLA/KA” (manufactured by SYMPATEC Co., Ltd.). The percentage of change in dispersed particle diameter (D50) was expressed by the value (%) obtained by dividing the amount of change in dispersed particle diameter (D50) between before and after the standing test by the dispersed particle diameter (D50) measured before the standing test.

[0233] (15) The blackness of the ink-jet printing ink were expressed by the color specification value (L* value) according to JIS Z 8729 by measuring the hue of images printed on a plain paper “KB” (produced by KOKUYO CO., LTD.) using a Multi-Spectro-Colour-Meter “MSC-IS-2D” (manufactured by SUGA SHIKENKI CO., LTD.).

[0234] (16) The light resistance of the ink-jet printing ink was measured by the following method.

[0235] That is, images were printed on a plain paper “KB” (produced by KOKUYO CO., LTD.) using an ink-jet printing ink to be measured. One half of the thus printed paper was covered with a metal foil, and an ultraviolet light was continuously irradiated over the paper at an intensity of 100 mW/cm2 for 6 hours using “EYE SUPER UV TESTER SUV-W13” (manufactured by IWASAKI DENKI CO., LTD.). Then, the hues (L*, a* and b* values) of the printed images on the UV-irradiated portion and the metal foil-covered non-irradiated portion of the paper were respectively measured using a Multi-Spectro-Colour-Meter “MSC-IS-2D” (manufactured by SUGA SHIKENKI CO., LTD.). The ΔE* value was calculated from differences between the measured hue values of the printed images formed on the metal foil-covered non-irradiated portion and UV-irradiated portion of the paper according to the above formula. The light resistance of the ink-jet printing ink was expressed by the ΔE* value.

[0236] (17) The anti-clogging property of the ink-jet printing ink was determined as follows. That is, an ink to be measured was filled in an ink cartridge of an ink jet printer “DESKJET 970Cxi” (manufactured by HEWLETT PACKARD CORP.) to repeatedly print ink images on plain papers “KB” (produced by KOKUYO CO., LTD.) at room temperature. The printed images were visually observed to examine the degrees of non-uniformity, lack and non-jetted defects thereof. The observation results were classified into the following five ranks.

[0237] Rank 1: Non-uniformity, lack or non-jetted defects of printed images were caused subsequent to the first printed paper;

[0238] Rank 2: Non-uniformity, lack or non-jetted defects of printed images were not caused until the 5th printed paper;

[0239] Rank 3: Non-uniformity, lack or non-jetted defects of printed images were not caused until the 10th printed paper;

[0240] Rank 4: Non-uniformity, lack or non-jetted defects of printed images were not caused until the 20th printed paper;

[0241] Rank 5: Non-uniformity, lack or non-jetted defects of printed images were not caused until the 25th printed paper.

Example 1

Production of Black Colorant

[0242] 350 g of methyl hydrogen polysiloxane (tradename: “TSF484”, produced by GE TOSHIBA SILICONE CO., LTD.) was added to 7 kg of silica particles as shown in the micrograph (×50,000) of FIG. 1 (particle shape: spherical shape; average particle diameter: 0.022 μm; sphericity: 1.06; BET specific surface area value: 193.8 m2/g; specific gravity: 2.32; L* value: 92.4; a* value: 0.2; b* value: 0.4; C* value: 0.4; hiding power: 10 cm2/g) while operating an edge runner, and the resultant mixture was mixed and stirred for 45 minutes under a linear load of 588 N/cm (60 Kg/cm) at a stirring speed of 22 rpm.

[0243] Then, 7.0 kg of black pigments as shown in the micrograph (×50,000) of FIG. 2 (kind: carbon black (furnace black); particle shape: granular shape; average particle diameter: 0.022 μm; BET specific surface area value: 133.5 m2/g; specific gravity: 1.84; L* value: 14.6) were added to the above-obtained mixture for 30 minutes while operating the edge runner, and the resultant mixture was mixed and stirred for 120 minutes under a linear load of 588 N/cm (60 Kg/cm) at a stirring speed of 22 rpm, thereby adhering the carbon black onto the methyl hydrogen polysiloxane coating layer formed on the respective silica particles. The obtained particles were dried at 80° C. for 60 minutes using a dryer, thereby obtaining a black colorant.

[0244] The thus obtained black colorant was in the form of spherical particles having an average particle diameter of 0.026 μm and a sphericity of 1.06, and had a BET specific surface area value of 125.4 m2/g; a specific gravity of 2.05; a blackness (L* value) of 16.5; a tinting strength of 137%; a light resistance (ΔE* value) of 1.1; and a black pigment desorption degree of Rank 5; and a coating amount of methyl hydrogen polysiloxane of 1.34% by weight (calculated as C). Further, it was confirmed that the amount of the carbon black adhered was 48.70% by weight (calculated as C; corresponding to 100 parts by weight based on 100 parts by weight of the silica particles).

[0245] As a result of observing the micrograph (×50,000) of the obtained black colorant as shown in FIG. 3, since almost no black pigments were recognized from the micrograph, it was confirmed that a substantially whole amount of the black pigments used contributed to the formation of the black pigment coat on the coating layer composed of methyl hydrogen polysiloxane. Further, it was recognized that the black pigments adhered no longer maintained the particle shape and size of those initially added, more specifically, the black pigments had a much finer particle size than that of the core particles and were adhered onto the surface of the extender pigments in the form of a uniform adhesion coat.

[0246] On the other hand, the extender pigments and the black pigments were simply mixed with each other by the same method as defined above except that no gluing agent was used. The micrograph (×50,000) of the thus obtained simply mixed particles is shown in FIG. 4. As is apparent from the micrograph of FIG. 4, in the case where the black pigments and the silica particles were simply mixed with each other without using the gluing agent, it was confirmed that the black pigments were not reduced in particle size, and both the particles were dispersed separately and independently from each other, thereby failing to form a uniform and dense black pigment coat adhered onto the surface of the extender pigments.

Example 2

Production of Ink-jet Printing Ink I

[0247] 88.5 parts by weight of ion-exchanged water and 1.2 parts by weight of a dispersant (mixture of polyacrylic acid and styrene-maleic acid copolymer (mixing ratio: 8:2)) were charged into a sand mill and mixed with each other. Then, 10.0 parts by weight of the black colorant obtained in Example 1 and 0.3 part by weight of a defoaming agent (silicone-based defoamer) were added to the mixed solution, and the resultant mixture was mixed and dispersed for one hour, thereby obtaining a primary dispersion for an ink-jet printing ink.

[0248] Next, the following components were mixed and stirred at the mixing ratio shown below, and the resultant mixture was passed through a 0.5 μm-mesh membrane filter, thereby obtaining an ink-jet printing ink.

Ink Composition

[0249]

1

Primary dispersion for ink-jet printing ink
10.0
parts by weight

Diethylene glycol
2.0
parts by weight

Ion-exchanged water
8.0
parts by weight

[0250] The thus obtained ink-jet printing ink had a dispersed particle diameter (D50) of 0.03 μm; a dispersion stability (by visual observation) of Rank 5; a percentage of change in dispersed particle diameter of 6.4%; a blackness (L* value) of 17.8; a light resistance (ΔE* value) of 1.8; and an anti-clogging property of Rank 5.

Example 3

Production of Aqueous Pigment Dispersion

[0251] 78.5 parts by weight of ion-exchanged water and 1.2 parts by weight of a dispersant (mixture of polyacrylic acid and styrene-maleic acid copolymer (mixing ratio: 8:2)) were charged into a sand mill and mixed with each other. Then, 20.0 parts by weight of the black colorant obtained in Example 1 and 0.3 part by weight of a defoaming agent (silicone-based defoamer) were added to the mixed solution, and the resultant mixture was mixed and dispersed for one hour and passed through a 0.5 μm-mesh membrane filter, thereby obtaining an aqueous pigment dispersion.

[0252] The thus obtained aqueous pigment dispersion had a dispersed particle diameter (D50) of 0.04 μm; a dispersion stability (by visual observation) of Rank 5; and a percentage of change in dispersed particle diameter (D50) of 7.9%.

Example 4

Production of Ink-jet Printing Ink II

[0253] 25.0 parts by weight of the aqueous pigment dispersion obtained in Example 3, 64.6 parts by weight of ion-exchanged water, 10.0 parts by weight of diethylene glycol, 0.3 part by weight of a dispersant (mixture of polyacrylic acid and styrene-maleic acid copolymer (mixing ratio: 8:2)) and 0.1 part by weight of a defoaming agent (silicone-based defoamer) were charged into a sand mill, mixed and dispersed for one hour and then passed through a 0.5 μm-mesh membrane filter, thereby obtaining an ink-jet printing ink II.

[0254] The thus obtained ink-jet printing ink had a dispersed particle diameter (D50) of 0.02 μm; a dispersion stability (by visual observation) of Rank 5; a percentage of change in dispersed particle diameter (D50) of 5.8%; a blackness (L* value) of 17.7; a light resistance (ΔE* value) of 1.7; and an anti-clogging property of Rank 5.

Core Particles 1 to 7

[0255] Core particles 1 to 7 having properties shown in Table 1 were prepared.

Core particles 8

[0256] A slurry containing silica particles was obtained by dispersing 20 kg of silica particles (core particles 1) in 150 liters of water. The pH value of the thus obtained slurry containing the silica particles was adjusted to 10.5, and then the slurry concentration was adjusted to 98 g/liter by adding water thereto. After 150 liters of the slurry was heated to 60° C., 2,722 ml of a 1.0 mol/liter NaAlO2 solution (corresponding to 0.5% by weight (calculated as Al) based on the weight of the silica particles) was added to the slurry. After allowing the obtained slurry to stand for 30 minutes, the pH value of the slurry was adjusted to 7.5 by using acetic acid. After further allowing the resultant slurry to stand for 30 minutes, the slurry was subjected to filtration, washing with water, drying and pulverization, thereby obtaining the silica particles whose surface was coated with hydroxides of aluminum.

[0257] Various properties of the obtained silica particles coated with the hydroxides of aluminum are shown in Table 3.

Core Particles 9 to 13

[0258] The same procedure as defined for the production of the above core particles 8, was conducted except that kinds of core particles, and kinds and amounts of additives added in the surface-treating step were changed variously, thereby obtaining surface-treated core particles.

[0259] The essential treatment conditions are shown in Table 2, and various properties of the obtained surface-treated core particles are shown in Table 3.

[0260] Meanwhile, in Tables, “A” and “S” as described in “kind of coating material used in surface-treating step” represent hydroxides of aluminum and oxides of silicon, respectively.

Black Pigments A to C

[0261] Black pigments A to C having properties as shown in Table 4 were prepared.

Examples 5 to 17 and Comparative Examples 1 to 5

[0262] The same procedure as defined in Example 1 was conducted except that kinds of core particles, kinds and amounts of gluing agents added in coating step with gluing agent, linear load and treating time for edge runner treatment used in the coating step with gluing agent, kinds and amounts of black pigments adhered in black pigment-adhering step, and linear load and treating time for edge runner treatment used in the black pigment-adhering step, were changed variously, thereby obtaining black colorants.

[0263] Meanwhile, in Example 8, the black pigments A were intermittently added six times in an amount of 20 parts by weight each, to 100 parts by weight of the core particles such that the total amount of the black pigments A added was 120 parts by weight.

[0264] In Example 14, 100 parts by weight of the black pigments B were continuously added to 100 parts by weight of the core particles for 100 minutes.

[0265] The essential production conditions are shown in Tables 5 and 6, and various properties of the obtained black colorants are shown in Tables 7 and 8.

Comparative Example 6 (Follow-up Test of Example 1 of Japanese Patent No. 3097208)

[0266] The silica particles (core particles 1) were dispersed in distilled water at the below-mentioned blending ratio. A silane-based coupling agent (γ-aminopropyl triethoxysilane) was gradually added to the obtained dispersion. After completion of addition of the silane-based coupling agent, the dispersion was allowed to stand at 50° C. for several hours until the reaction between the silica particles and the silane-based coupling agent was completed. Meanwhile, the termination of the reaction between the silica particles and the silane-based coupling agent was determined using FT-IR “MAGNA-IR” (manufactured by Nicolett Co., Ltd.). The resultant dispersion was transferred into an attritor, and the black pigments A (carbon black) were added to the dispersion. The resultant mixture was dispersed for 12 hours to conduct the reaction between the silane-based coupling agent and the black pigments A.

Dispersion Composition

[0267]

2

Silica particles
10.0
parts by weight

Distilled water
84.3
parts by weight

Silane-based coupling agent
0.2
part by weight

Black pigments A
5.0
parts by weight

[0268] Various properties of the thus obtained colored silica particles are shown in Table 8.

Comparative Example 7 (Follow-up Test of Examples of Japanese Patent No. 3105511)

[0269] 9.6 g of the silica particles (core particles 1) were placed in a 500-ml round bottom flask equipped with a magnetic stirrer and a Dean-Stark trap, and dried therein at 100° C. for 24 hours. 300 ml of toluene previously dried by azeotropic distillation under a nitrogen atmosphere, and 2.96 g of a silane-based coupling agent (γ-aminopropyl triethoxysilane) were added to the dried silica particles. The obtained suspension was refluxed at 111° C. for 5 hours, cooled to room temperature, and then centrifuged at a rotating speed of about 10,000 rpm. After removing a supernatant from the suspension, the resultant precipitate was washed with 500 ml of dichloromethane, and successively the mixture of the precipitate and dichloromethane was centrifuged. After a supernatant was removed from the mixture, the obtained residues were dried at 40° C. for 2.5 days in a vacuum dryer (200 mmHg), thereby obtaining 9.6 g of white particles (yield: 76%).

[0270] Next, an aqueous mixture prepared by dispersing 1.0 g of the above silica particles containing the silane-based coupling agent and 1.0 g of naphthol blue black in 40 ml of water, was placed in a round bottom flask equipped with a magnetic stirrer, stirred therein at room temperature for 18 hours, and then centrifuged. The resultant residues were dispersed in water and then centrifuged until the supernatant became colorless. The obtained residues were re-dispersed in water, and then freeze-dried using a freeze dryer, thereby 0.75 g of colored silica particles.

[0271] Various properties of the obtained colored silica particles are shown in Table 8.

Example 18

[0272]

20
g of sodium docecylbenzenesulfonate (anionic surfactant) was added to 2 kg of the black colorant obtained in Example 5, and the resultant mixture was stirred at 30° C. for 30 minutes using a Henschel mixer, thereby obtaining coated black colorants.

[0273] The essential production conditions are shown in Table 9, and various properties of the obtained coated black colorants are shown in Table 10.

Examples 19 to 23

[0274] The same procedure as defined in Example 18 was conducted except that kinds of black colorants, kinds and amounts of surfactants and/or polymeric dispersing agents, and conditions for edge runner treatment used in the coating step, were changed variously, thereby obtaining black colorants coated with the surfactants and/or polymeric dispersing agents.

[0275] The essential production conditions are shown in Table 9, and various properties of the obtained coated black colorants are shown in Table 10.

Examples 24 to 42 and Comparative Examples 8 to 17

[0276] The same procedure as defined in Example 2: Production of ink-jet printing ink A was conducted except that kinds of black colorants were changed variously, thereby obtaining ink-jet printing inks.

[0277] The essential production conditions are shown in Tables 11 and 12, and various properties of the obtained ink-jet printing inks are shown in Tables 13 to 14.

Examples 43 to 54 and Comparative Examples 18 to 25

[0278] The same procedure as defined in Example 3 was conducted except that kinds of black colorants were changed variously, thereby obtaining aqueous pigment dispersions.

[0279] The essential production conditions and various properties of the obtained aqueous pigment dispersions are shown in Tables 15 and 16.

Examples 55 to 66 and Comparative Examples 26 to 33

[0280] The same procedure as defined in Example 4 was conducted except that kinds of aqueous pigment dispersions were changed variously, thereby obtaining ink-jet printing inks.

[0281] The essential production conditions and various properties of the obtained ink-jet printing inks are shown in Tables 17 and 18.

3TABLE 1Properties of core particlesAverageKind ofparticlecorediameterparticlesKindShape(μm)CoreSilicaSpherical0.021particles 1CoreSilicaGranular0.013particles 2CoreSilicaGranular0.048particles 3CoreSilicaSpherical0.005particles 4CoreAluminaGranular0.098particles 5CorePrecipitatedGranular0.059particles 6barium sulfateCoreMn-containingGranular0.282particles 7hematiteparticles(Mn content:12.6 wt. %)Properties of core particlesKind ofBET specificSpecificcoreSphericitysurface areagravityparticles(−)value (m2/g)(−)Core1.02196.22.19particles 1Core1.28256.32.43particles 2Core1.11168.42.11particles 3Core1.03312.62.28particles 4Core1.3141.33.65particles 5Core1.2221.34.15particles 6Core1.363.85.01particles 7Properties of core particlesHueL*a*b*C*HidingKind of corevaluevaluevaluevaluepowerparticles(−)(−)(−)(−)(cm2/g)Core93.10.10.30.36particles 1Core94.00.3−0.10.311particles 2Core95.10.40.20.410particles 3Core92.20.11.31.36particles 4Core96.30.10.20.118particles 5Core91.60.31.11.113particles 6Core22.85.51.35.71,680particles 7

[0282]

4

TABLE 2

Surface-treating step

Additives
Coating material

Core
Kind of

Calculated
Amount

Calculated
Amount

particles
core particles
Kind
as
(wt. %)
Kind
as
(wt. %)

Core
Core
Sodium
Al
0.5
A
Al
0.49

particles 8
particles 1
aluminate

Core
Core
Aluminum
Al
2.0
A
Al
1.96

particles 9
particles 2
sulfate

Core
Core
Aluminum
Al
5.0
A
Al
4.76

particles 10
particles 3
sulfate

Core
Core
Aluminum
Al
2.0
A
Al
1.96

particles 11
particles 4
sulfate

Core
Core
Water
SiO2
0.5
S
SiO2
0.48

particles 12
particles 5
glass #3

Core
Core
Sodium
Al
2.0
A
Al
1.93

particles 13
particles 6
aluminate

Water
SiO2
0.5
S
SiO2
0.47

glass #3

[0283]

5

TABLE 3

Properties of surface-treated core

particles

BET

specific

Average

surface

particle

area
Specific

Kind of core
diameter
Sphericity
value
gravity

particles
(μm)
(−)
(m2/g)
(−)

Core
0.022
1.02
186.3
2.20

particles 8

Core
0.015
1.28
211.4
2.45

particles 9

Core
0.050
1.11
129.1
2.18

particles 10

Core
0.005
1.03
296.4
2.31

particles 11

Core
0.099
1.31
40.8
3.60

particles 12

Core
0.061
1.22
21.9
4.13

particles 13

Properties of surface-treated core

particles

Hue

L*
a*
b*
C*
Hiding

Kind of core
value
value
value
value
power

particles
(−)
(−)
(−)
(−)
(cm2/g)

Core
93.1
0.1
0.1
0.1
6

particles 8

Core
94.1
0.2
0.1
0.2
10

particles 9

Core
94.6
0.2
0.1
0.2
11

particles 10

Core
92.0
0.1
1.4
1.4
6

particles 11

Core
93.8
0.1
0.3
0.3
21

particles 12

Core
91.0
0.4
0.8
0.9
14

particles 13

[0284]

6

TABLE 4

Properties of black pigments

Average

particle
BET specific
Specific
Blackness

Black

diameter
surface area
gravity
(ΔL* value)

pigments
Kind
Shape
(μm)
value (m2/g)
(−)
(−)

Black
Carbon black
Granular
0.022
134.0
1.82
16.6

pigments A
(furnace black)

Black
Carbon black
Granular
0.045
71.2
1.95
17.1

pigments B
(acetylene black)

Black
Aniline black
Granular
0.312
56.8
1.74
15.9

pigments C

[0285]

7

TABLE 5

Production of black colorant

Coating step with gluing agent
Adhesion step with black pigments

Coating

Amount

Additives

amount
Black pigments

adhered

Amount

(cal-

Amount

(cal-

Kind of

added
Edge runner treatment
culated

added
Edge runner treatment
culated

core

(wt.
Linear load
Time
as C)

(wt.
Linear load
Time
as C)

Examples
particles
Kind
part)
(N/cm)
(Kg/cm)
(min)
(wt. %)
Kind
part)
(N/cm)
(Kg/cm)
(min)
(wt. %)

Example
Core
Methyl
4.0
588
60
30
1.06
A
50.0
588
60
60
32.18

5
particles 1
hydrogen

polysiloxane

Example
Core
γ-amino-
10.0
588
60
60
1.63
B
100.0
588
60
60
48.63

6
particles 2
propyl

triethoxy-

silane

Example
Core
Methyl
2.0
294
30
30
0.13
C
100.0
588
60
90
40.01

7
particles 3
triethoxy-

silane

Example
Core
Methyl
8.0
588
60
30
2.10
A
120.0
735
75
60
54.35

8
particles 4
hydrogen

polysiloxane

Example
Core
Isopropyl
1.0
441
45
20
0.74
A
100.0
588
60
60
48.92

9
particles 5
triiso-

stearoyl

titanate

Example
Core
Water-soluble
2.0
735
75
60
1.00
B
120.0
588
60
30
54.36

10
particles 6
acrylic

resin

Example
Core
Methyl
4.0
588
60
90
0.25
A
30.0
588
60
90
22.86

11
particles 8
triethoxy-

silane

Example
Core
Methyl
2.0
294
30
60
0.54
B
100.0
441
45
120
48.77

12
particles 9
hydrogen

polysiloxane

Example 13
Core
Methyl
5.0
588
60
45
0.41
C
150.0
735
75
120
47.52

particles 10
trimethoxy-

silane

Example 14
Core
Methyl
5.0
588
60
20
1.05
B
100.0
588
60
30
49.56

particles 11
hydrogen

polysiloxane

Example 15
Core
Phenyl
6.0
490
50
30
2.04
A
50.0
588
60
30
32.35

particles 12
triethoxy-

silane

Example 16
Core
Dimethyl
5.0
735
75
45
0.94
B
100.0
294
30
40
48.76

particles 13
dimethoxy-

silane

Example 17
Particles
Methyl
5.0
588
60
45
1.35
C
100.0
588
60
120
40.13

used in
hydrogen

Example 1
polysiloxane

[0286]

8

TABLE 6

Production of black colorant

Coating step with gluing agent
Adhesion step with black pigments

Coating

Amount

Additives

amount
Black pigments

adhered

Amount

(cal-

Amount

(cal-

added
Edge runner treatment
culated

added
Edge runner treatment
culated

Comparative
Kind of core

(wt.
Linear load
Time
as C)

(wt.
Linear load
Time
as C)

Examples
particles
Kind
part)
(N/cm)
(Kg/cm)
(min)
(wt. %)
Kind
part)
(N/cm)
(Kg/cm)
(min)
(wt. %)

Comparative
Core
—
—
—
—
—
—
A
50.0
588
60
60
32.30

Example 1
particles 1

Comparative
Core
Methyl
0.005
588
60
30
1 × 10−3
A
50.0
588
60
60
32.15

Example 2
particles 1
hydrogen

poly-

siloxane

Comparative
Core
Methyl
4.0
588
60
30
1.07
A
0.5
588
60
60
0.48

Example 3
particles 1
hydrogen

poly-

siloxane

Comparative
Core
Methyl
4.0
588
60
30
1.06
A
750.0
588
60
60
87.79

Example 4
particles 1
hydrogen

poly-

siloxane

Comparative
Core
Methyl
4.0
588
60
30
1.06
A
50.0
588
60
60
32.22

Example 5
particles 7
hydrogen

poly-

siloxane

[0287]

9

TABLE 7

Properties of black colorant

Average

particle

BET specific
Specific
Blackness
Tinting
Light resistance
Degree of desorption

diameter
Sphericity
surface area
gravity
(L* value)
strength
(ΔE* value)
of black pigments

Examples
(μm)
(−)
value (m2/g)
(−)
(−)
(%)
(−)
(−)

Example 5
0.023
1.02
152.1
2.04
17.9
127
1.8
5

Example 6
0.018
1.28
180.5
2.13
18.7
136
1.6
5

Example 7
0.052
1.11
98.3
1.92
17.0
122
1.9
5

Example 8
0.009
1.03
198.6
1.99
17.2
140
1.8
5

Example 9
0.100
1.31
50.4
2.73
17.3
136
1.5
4

Example 10
0.063
1.22
37.2
2.93
19.0
136
1.4
4

Example 11
0.024
1.03
156.6
2.08
17.2
136
1.0
5

Example 12
0.020
1.28
170.9
2.19
19.1
130
1.6
5

Example 13
0.055
1.12
80.1
1.91
16.9
124
1.5
5

Example 14
0.008
1.03
211.4
2.03
17.3
135
1.4
5

Example 15
0.103
1.31
49.5
2.93
20.8
128
1.3
5

Example 16
0.064
1.22
35.7
2.99
20.2
129
1.1
5

Example 17
0.026
1.06
106.3
2.01
17.0
123
1.8
5

[0288]

10

TABLE 8

Properties of black colorant

Average

particle

BET specific
Specific
Blackness
Tinting
Light resistance
Degree of desorption

Comparative
diameter
Sphericity
surface area
gravity
(L* value)
strength
(ΔE* value)
of black pigments

Examples
(μm)
(−)
value (m2/g)
(−)
(−)
(%)
(−)
(−)

Comparative
0.022
1.06
172.3
2.07
23.0
102
6.3
1

Example 1

Comparative
0.022
1.05
160.5
2.07
22.8
105
6.0
2

Example 2

Comparative
0.021
1.02
191.2
2.14
34.5
101
1.7
—

Example 3

Comparative
0.033
1.08
141.3
1.86
16.8
197
5.5
1

Example 4

Comparative
0.283
1.39
14.8
3.87
17.4
118
3.5
1

Example 5

Comparative
0.021
1.02
163.8
2.05
18.0
108
6.9
1

Example 6

Comparative
0.021
1.02
180.1
2.14
23.4
95
11.2
—

Example 7

[0289]

11

TABLE 9

Production of surface-coated black colorant

Coating step with surfactant

Coating

Additives

amount

Kind of

Amount
Treating

(calculated

black

added
temperature
Treating time
as C)

Examples
colorant
Kind
(wt. part)
(° C.)
(min)
(wt. %)

Example 18
Example 5
Sodium
1.0
30
30
0.61

dodecylbenzene

sulfonate

Example 19
Example 7
Sodium acrylate
2.0
25
30
0.70

Example 20
Example 9
Sodium
1.0
30
20
0.48

laurylsulfate

Example 21
Example 10
Nonylphenyl
5.0
30
30
3.69

polyethylene

glycol ether

Example 22
Example 12
Sodium
1.0
25
20
0.60

dodecylbenzene

sulfonate

Example 23
Example 14
Sodium
2.0
35
30
1.21

dodecylbenzene

sulfonate

[0290]

12

TABLE 10

Properties of black colorant

BET

specific

Average

surface

Light

particle

area
Specific
Blackness
Tinting
resistance

diameter
Sphericity
value
gravity
(L* value)
strength
(ΔE* value)

Examples
(μm)
(−)
(m2/cr)
(−)
(−)
(%)
(−)

Example 18
0.023
1.02
145.6
2.02
18.0
128
1.7

Example 19
0.052
1.11
94.5
1.90
17.2
122
1.8

Example 20
0.100
1.31
48.2
2.71
17.4
137
1.6

Example 21
0.064
1.22
34.3
2.84
19.3
136
1.3

Example 22
0.020
1.28
168.0
2.18
19.2
131
1.5

Example 23
0.009
1.03
176.4
2.01
17.5
136
1.3

[0291]

13

TABLE 11

Production of black ink-jet printing ink

Black colorant

Colloidal silica

Amount

Amount

blended

blended

(wt.

(wt.

Examples
Kind
part)
Kind
part)

Example 24
Example 5
5.0
—
—

Example 25
Example 6
5.0
—
—

Example 26
Example 7
5.0
—
—

Example 27
Example 8
5.0
—
—

Example 28
Example 9
5.0
—
—

Example 29
Example 10
5.0
—
—

Example 30
Example 11
5.0
—
—

Example 31
Example 12
5.0
—
—

Example 32
Example 13
5.0
—
—

Example 33
Example 14
5.0
—
—

Example 34
Example 15
5.0
—
—

Example 35
Example 16
5.0
—
—

Example 36
Example 17
5.0
—
—

Example 37
Example 18
5.0
—
—

Example 38
Example 19
5.0
—
—

Example 39
Example 20
5.0
—
—

Example 40
Example 21
5.0
—
—

Example 41
Example 22
5.0
—
—

Example 42
Example 23
5.0
—
—

[0292]

14

TABLE 12

Production of black ink-jet printing ink

Black colorant
Colloidal silica

Amount

Amount

Comparative

blended

blended

Examples
Kind
(wt. part)
Kind
(wt. part)

Comparative
Black
5.0
Core
10.0

Example 8
pigments A

particles 1

Comparative
Black
5.0
Core
10.0

Example 9
pigments B

particles 7

Comparative
Black
5.0
Core
10.0

Example 10
pigments C

particles 1

Comparative
Comparative
5.0
—
—

Example 11
Example 1

Comparative
Comparative
5.0
—
—

Example 12
Example 2

Comparative
Comparative
5.0
—
—

Example 13
Example 3

Comparative
Comparative
5.0
—
—

Example 14
Example 4

Comparative
Compartive
5.0
—
—

Example 15
Example 5

Comparative
Comparative
5.0
—
—

Example 16
Example 6

Comparative
Comparative
5.0
—
—

Example 17
Example 7

[0293]

15

TABLE 13

Properties of black ink-jet printing ink

Dispersion stability

Percentage of

change in

Dispersed

diperesed

Light

particle
Visual
particle
Blackness
resistance
Anti-clogging

diameter
observation
diameter
(L* value)
(ΔE* value)
property

Examples
(μm)
(−)
(%)
(−)
(−)
(−)

Example 24
0.03
5
6.6
18.0
1.8
5

Example 25
0.03
5
6.8
18.7
1.5
5

Example 26
0.06
5
6.4
17.2
1.8
5

Example 27
0.02
5
6.5
17.4
1.8
5

Example 28
0.13
4
8.8
17.4
1.5
4

Example 29
0.08
4
9.2
19.2
1.4
4

Example 30
0.03
5
5.6
17.3
1.0
5

Example 31
0.03
5
5.3
19.4
1.5
5

Example 32
0.06
5
5.1
17.0
1.4
5

Example 33
0.02
5
5.4
17.4
1.5
5

Example 34
0.13
4
8.4
20.9
1.3
4

Example 35
0.08
4
8.9
20.4
1.0
4

Example 36
0.03
5
6.6
17.1
1.7
5

Example 37
0.03
5
4.4
18.2
1.6
5

Example 38
0.03
5
4.5
17.3
1.7
5

Example 39
0.12
5
6.7
17.6
1.5
5

Example 40
0.08
5
7.5
19.5
1.3
5

Example 41
0.03
5
3.9
19.4
1.3
5

Example 42
0.02
5
4.0
17.5
1.4
5

[0294]

16

TABLE 14

Properties of black ink-jet printing ink

Dispersion stability

Percentage of

change in

Dispersed

despersed

Light

particle
Visual
particle
Blackness
resistance
Anti-clogging

Comparative
diameter
observation
diamerter
(L* value)
(ΔE* value)
property

Examples
(μm)
(−)
(%)
(−)
(−)
(−)

Comparative
0.08
1
18.8
17.3
6.8
2

Example 8

Comparative
0.14
1
20.1
18.0
6.6
2

Example 9

Comparative
0.66
1
24.9
17.2
8.9
1

Example 10

Comparative
0.22
1
18.0
23.4
6.3
2

Example 11

Comparative
0.21
2
17.1
23.0
6.1
2

Example 12

Comparative
0.07
3
13.5
35.1
1.8
3

Example 13

Comparative
0.18
2
17.0
17.2
5.4
2

Example 14

Comparative
0.22
2
22.2
17.9
3.4
1

Example 15

Comparative
0.16
1
15.3
18.3
6.7
2

Example 16

Comparative
0.08
3
8.6
23.6
11.1
3

Example 17

[0295]

17

TABLE 15

Properties of aqueous pigment dispersion

Dispersion stability

Production of aqueous pigment dispersion

Percentage of

Black colorant
Colloidal silica

change in

Amount

Amount
Dispersed

dispersed

blended

blended
particle
Visual
particle

(wt.

(wt.
diameter
observation
diameter

Examples
Kind
part)
Kind
part)
(μm)
(−)
(%)

Example 43
Example 5
20.0
—
—
0.06
5
8.1

Example 44
Example 7
20.0
—
—
0.08
5
8.4

Example 45
Example 9
20.0
—
—
0.16
4
10.6

Example 46
Example 10
20.0
—
—
0.10
4
10.4

Example 47
Example 12
20.0
—
—
0.06
5
6.6

Example 48
Example 14
20.0
—
—
0.05
5
7.3

Example 49
Example 18
20.0
—
—
0.05
5
5.1

Example 50
Example 19
20.0
—
—
0.05
5
5.2

Example 51
Example 20
20.0
—
—
0.13
5
7.6

Example 52
Example 21
20.0
—
—
0.09
5
8.1

Example 53
Example 22
20.0
—
—
0.05
5
4.8

Example 54
Example 23
20.0
—
—
0.04
5
5.0

[0296]

18

TABLE 16

Properties of aqueous pigment dispersion

Dispertion stability

Production of aqueous pigment dispersion

Percentage of

Black colorant
Colloidal silica

change in

Amount

Amount
Dispersed

dispersed

blended

blended
particle
Visual
particle

Comparative

(wt.

(wt.
diameter
observation
diameter

Examples
Kind
part)
Kind
part)
(μm)
(−)
(%)

Comparative
Black
10.0
Core
10.0
0.18
1
21.6

Example 18
pigments A

particles 1

Comparative
Comparative
20.0
—
—
0.31
1
21.5

Example 19
Example 1

Comparative
Comparative
20.0
—
—
0.33
2
21 2

Example 20
Example 2

Comparative
Comparative
20.0
—
—
0.23
3
17.3

Example 21
Example 3

Comparative
Comparative
20.0
—
—
0.26
2
21.2

Example 22
Example 4

Comparative
Comparative
20.0
—
—
0.28
2
26.3

Example 23
Example 5

Comparative
Comparative
20.0
—
—
0.24
1
18.6

Example 24
Example 6

Comparative
Comparative
20.0
—
—
0.19
3
13.8

Example 25
Example 7

[0297]

19

TABLE 17

Properties of aqueous pigment dispersion

Dispersion stability

Percentage of

change in

Production of ink-jet printing ink
Dispersed

dispersed

Light

Aqueous pigment dispersion
particle
Visual
particle
Blackness
resistance
Anti-clogging

Amount blended
diameter
observation
diameter
(L* value)
(ΔE* value)
property

Examples
Kind
(wt. part)
(μm)
(−)
(%)
(−)
(−)
(−)

Example 55
Example 43
25.0
0.02
5
6.4
18.0
1.7
5

Example 56
Example 44
25.0
0.05
5
6.3
17.3
1.6
5

Example 57
Example 45
25.0
0.10
4
8.3
17.3
1.5
4

Example 58
Example 46
25.0
0.06
4
8.6
19.0
1.4
4

Example 59
Example 47
25.0
0.02
5
5.2
19.2
1.4
5

Example 60
Example 48
25.0
0.02
5
5.1
17.8
1.4
5

Example 61
Example 49
25.0
0.02
5
4.2
18.1
1.5
5

Example 62
Example 50
25.0
0.03
5
4.2
17.3
1.6
5

Example 63
Example 51
25.0
0.09
5
6.5
17.5
1.4
5

Example 64
Example 52
25.0
0.05
5
7.1
19.3
1.2
5

Example 65
Example 53
25.0
0.02
5
3.8
19.1
1.2
5

Example 66
Example 54
25.0
0.03
5
3.6
17.6
1.1
5

[0298]

20

TABLE 18

Properties of aqueous pigment dispersion

Dispersion stability

Percentage of

change in

Production of ink-jet printing ink
Dispersed

dispersed

Light

Aqueous pigment dispersion
particle
Visual
particle
Blackness
resistance
Anti-clogging

Comparative

Amount blended
diameter
observation
diameter
(L* value)
(ΔE* value)
property

Examples
Kind
(wt. part)
(μm)
(−)
(%)
(−)
(−)
(−)

Comparative
Comparative
25.0
0.08
1
18.4
18.7
6.7
2

Example 26
Example 18

Comparative
Comparative
25.0
0.20
1
17.8
23.3
6.2
2

Example 27
Example 19

Comparative
Comparative
25.0
0.19
2
17.0
22.8
6.1
2

Example 28
Example 20

Comparative
Comparative
25.0
0.06
3
13.3
35.0
1.8
3

Example 29
Example 21

Comparative
Comparative
25.0
0.17
2
16.8
17.2
5.3
2

Example 30
Example 22

Comparative
Comparative
25.0
0.21
2
21.9
17.8
3.3
1

Example 31
Example 23

Comparative
Comparative
25.0
0.15
1
15.1
18.1
6.5
2

Example 32
Example 24

Comparative
Comparative
25.0
0.07
3
8.5
23.5
11.0
3

Example 33
Example 25

Number	Date	Country	Kind
2001-173289	Jun 2001	JP
2002-59463	Mar 2002	JP

Black colorant for ink-jet printing ink, ink-jet printing ink, and aqueous pigment dispersion containing the black colorant

Information

Publication Number

Date Filed

Date Published

Inventors

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Priority Claims (2)