The present disclosure relates generally to bladders for articles of footwear, and to methods of making bladders for articles of footwear.
This section provides background information related to the present disclosure, which is not necessarily prior art.
Articles of footwear conventionally include an upper and a sole structure. The upper may be formed from any suitable material(s) to receive, secure, and support a foot on the sole structure. The upper may cooperate with laces, straps, or other fasteners to adjust the fit of the upper around the foot. A bottom portion of the upper, proximate to a bottom surface of the foot, attaches to the sole structure.
Sole structures generally include a layered arrangement extending between a ground surface and the upper. One layer of the sole structure includes an outsole that provides abrasion-resistance and traction with the ground surface. The outsole may be formed from rubber or other materials that impart durability and wear-resistance, as well as enhance traction with the ground surface. Another layer of the sole structure includes a midsole disposed between the outsole and the upper. The midsole provides cushioning for the foot and may be partially formed from a polymer foam material that compresses resiliently under an applied load to cushion the foot by attenuating ground-reaction forces. The midsole may additionally incorporate a fluid-filled chamber to increase durability of the sole structure, as well as to provide cushioning to the foot by compressing resiliently under an applied load to attenuate ground-reaction forces. Sole structures may also include a comfort-enhancing insole or a sockliner located within a void proximate to the bottom portion of the upper and a stroble attached to the upper and disposed between the midsole and the insole or sockliner.
Fluid-filled chambers for use in footwear are typically formed from two barrier layers of polymer material that are sealed or bonded together to form a chamber. Often, the chamber is pressurized with a fluid, such as air, and may incorporate tensile members to retain a desired shape of the chamber when pressurized. Generally, fluid-filled chambers are designed with an emphasis on balancing support for the foot and cushioning characteristics that relate to responsiveness as the fluid-filled chamber resiliently compresses under an applied load. The fluid-filled chamber as a whole, however, fails to adequately dampen oscillations by the foot as the fluid-filled chamber compresses to attenuate ground-reaction forces. Accordingly, creating a midsole from a fluid-filled chamber that dampens foot oscillation and provides acceptable cushioning for the foot while attenuating ground-reaction forces is difficult to achieve.
The drawings described herein are for illustrative purposes only of selected configurations and are not intended to limit the scope of the present disclosure.
Corresponding reference numerals indicate corresponding parts throughout the drawings.
Example configurations will now be described more fully with reference to the accompanying drawings. Example configurations are provided so that this disclosure will be thorough, and will fully convey the scope of the disclosure to those of ordinary skill in the art. Specific details are set forth such as examples of specific components, devices, and methods, to provide a thorough understanding of configurations of the present disclosure. It will be apparent to those of ordinary skill in the art that specific details need not be employed, that example configurations may be embodied in many different forms, and that the specific details and the example configurations should not be construed to limit the scope of the disclosure.
The terminology used herein is for the purpose of describing particular exemplary configurations only and is not intended to be limiting. As used herein, the singular articles “a,” “an,” and “the” may be intended to include the plural forms as well, unless the context clearly indicates otherwise. The terms “comprises,” “comprising,” “including,” and “having,” are inclusive and therefore specify the presence of features, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, steps, operations, elements, components, and/or groups thereof. The method steps, processes, and operations described herein are not to be construed as necessarily requiring their performance in the particular order discussed or illustrated, unless specifically identified as an order of performance. Additional or alternative steps may be employed.
When an element or layer is referred to as being “on,” “engaged to,” “connected to,” “attached to,” or “coupled to” another element or layer, it may be directly on, engaged, connected, attached, or coupled to the other element or layer, or intervening elements or layers may be present. In contrast, when an element is referred to as being “directly on,” “directly engaged to,” “directly connected to,” “directly attached to,” or “directly coupled to” another element or layer, there may be no intervening elements or layers present. Other words used to describe the relationship between elements should be interpreted in a like fashion (e.g., “between” versus “directly between,” “adjacent” versus “directly adjacent,” etc.). As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.
The terms first, second, third, etc. may be used herein to describe various elements, components, regions, layers and/or sections. These elements, components, regions, layers and/or sections should not be limited by these terms. These terms may be only used to distinguish one element, component, region, layer or section from another region, layer or section. Terms such as “first,” “second,” and other numerical terms do not imply a sequence or order unless clearly indicated by the context. Thus, a first element, component, region, layer or section discussed below could be termed a second element, component, region, layer or section without departing from the teachings of the example configurations.
In one configuration, a bladder for an article of footwear is provided and includes a plate, a first tensile layer disposed adjacent to a first side of the plate, and a second tensile layer disposed on an opposite side of the plate from the first tensile layer, the second tensile layer joined to the first tensile layer through the plate by a plurality of inner bonds. The bladder additionally includes a first barrier layer disposed adjacent to the first tensile layer and joined to the first tensile layer by a plurality of first outer bonds to form a first chamber, one or more of the first outer bonds interposed between adjacent ones of the inner bonds.
The bladder may include one or more of the following optional features. For example, the first tensile layer and the second tensile layer may be formed of a first elastomeric material and the first barrier layer may be formed of a second elastomeric material different from the first elastomeric material. Additionally or alternatively, the first elastomeric material may have a lower melting temperature than the second elastomeric material.
In one configuration, a second barrier layer may be disposed adjacent to the second tensile layer and may be joined to the second tensile layer by a plurality of second outer bonds to form a second chamber on the opposite side of the plate than the first chamber. In this configuration, the first chamber may be fluidly isolated from the second chamber by at least one of the first tensile layer and the second tensile layer. Additionally or alternatively, the first chamber may have a different pressure than the second chamber.
The plate may include a plurality of apertures extending through the plate with each of the inner bonds being formed within one of the apertures.
In one configuration, the second tensile layer may be joined to the first tensile layer around a periphery of the plate. Additionally or alternatively, the first tensile layer and the second tensile layer may be detached from the plate between the inner bonds to form one or more tensile elements. Further, each of the first outer bonds may be formed with one of the tensile elements.
In another configuration, a bladder for an article of footwear is provided and includes a plate having one or more apertures, a first tensile layer disposed adjacent to a first side of the plate, a second tensile layer disposed on an opposite side of the plate from the first tensile layer and joined to the first tensile layer within each of the one or more apertures, and a first barrier layer disposed adjacent to the first tensile layer and joined to the first tensile layer at discrete locations to form a first chamber.
The bladder may include one or more of the following optional features. For example, the first tensile layer and the second tensile layer may be formed of a first elastomeric material and the first barrier layer may be formed of a second elastomeric material different from the first elastomeric material. Additionally or alternatively, the first elastomeric material may have a lower melting temperature than the second elastomeric material.
A second barrier layer may be disposed adjacent to the second tensile layer and may be joined to the second tensile layer by a plurality of second outer bonds to form a second chamber on the opposite side of the plate than the first chamber. The first chamber may be fluidly isolated from the second chamber by at least one of the first tensile layer and the second tensile layer. The first chamber may have a different pressure than the second chamber.
In one configuration, the second tensile layer may be joined to the first tensile layer around a periphery of the plate. Additionally or alternatively, the first tensile layer and the second tensile layer may be detached from the plate between the apertures to form one or more tensile elements. In this configuration, the first barrier layer may be attached to each of the one or more tensile elements of the first tensile layer and/or may be attached to the first tensile layer along each of the apertures.
Referring to
As illustrated in
While the configurations 10a-10d described in each of the regions 2, 3, 4, 5 may all be incorporated into a single bladder 10 in the manner shown and described herein, it will be appreciated that bladders manufactured according to the principles of the present disclosure can include any combination of one or more of the configurations shown in
Referring now to
With continued reference to
In some configurations (10a, 10b), the thickness of the plate 18 may be substantially constant, while in other configurations (10c, 10d), the plate 18 may have a variable thickness. Optionally, the peripheral portion 28 defines a peripheral flange 32 extending outwardly from the interior portion 26 at an oblique angle relative to the interior portion 28. Additionally or alternatively, the interior portion 26 and/or the peripheral portion 28 may include protuberances 34 formed on the first side 20 and/or the second side 22 to provide the plate 18 with a variable thickness. In the illustrated example, the plate 18 includes a protuberance 34 formed as a rib 34 extending from the first side 20 of the peripheral flange 32. However, in other examples, the plate 18 may include one or more projections formed in the interior region 26 and/or on the second side 22.
The plate 18 is formed, at least in part, by a material having a greater stiffness than the barrier layers 14a, 14b, 16a, 16b, and forms an internal structure or skeleton of the bladder 10. In some examples, the plate 18 includes one or more polymeric materials having a higher melting temperature than at least the tensile layers 14a, 14b. In other examples, the plate 18 may be formed of or include composite materials and/or metal materials. The first and second sides 20, 22 of the plate 18 are configured to inhibit bonding between the plate 18 and the tensile layers 14a, 14b. Thus, the plate 18 itself may be formed of a material that is incompatible (i.e., resistant to bonding) with the material of the tensile layers 14a, 14b. Additionally or alternatively, the sides 20, 22 of the plate 18 may be coated or covered with a bond inhibitor to prevent joining of the tensile layers 14a, 14b and the plate 18.
With continued reference to
When the bladder 10 is assembled, the inner surfaces 36a, 36b of the tensile layers 14a, 14b face the plate 18 and are joined to each other by inner bonds 42 through one or more of the apertures 30 of the plate 18. The inner surfaces 36a, 36b may also be joined to each other along the outer periphery of the plate 18, such that at least a portion of the plate 18 is enclosed between the tensile layers 14a, 14b.
Referring still to
When the bladder 10 is assembled, the inner surfaces 44a, 44b of the outer barrier layers 16a, 16b face the outer surfaces 38a, 38b of the tensile layers 14a, 14b. As described in greater detail below with respect to each of the configurations 10a-10d, the inner surfaces 44a, 44b of the outer barrier layers 16a, 16b may be joined to the outer surfaces 38a, 38b of the tensile layers 14a, 14b, respectively, to define a geometry (e.g., thicknesses, width, and lengths) of the bladder 10. For example, the inner surfaces 44a, 44b of the outer barrier layers 16a, 16b may be joined to the outer surfaces 38a, 38b of the tensile layers 14a, 14b by a plurality of outer bonds 50 in the interior portion 26 to form first and second web areas 52a, 52b of the bladder 10. Similarly, the outer peripheries of the barrier layers 14a, 14b, 16a, 16b may be joined together to form a peripheral seam 54 extending around the bladder 10 to seal the fluid (e.g., air) within the fluid-filled chamber chambers 12a, 12b. Thus, the chambers 12a, 12b are associated with areas of the bladder 10 where the inner surfaces 44a, 44b of the outer barrier layers 16a, 16b are not joined together and, therefore, are separated from the outer surfaces 38a, 38b of the tensile layers 14a, 14b. As shown in the figures, a space formed between opposing surfaces 38a, 38b, 44a, 44b of the tensile layers 14a, 14b and outer barrier layers 16a, 16b defines an interior void 56a, 56b of each of the chambers 12a, 12b.
The barrier layers 14a, 14b, 16a, 16b can each be produced from an elastomeric material that includes one or more thermoplastic polymers and/or one or more cross-linkable polymers. In an aspect, the elastomeric material can include one or more thermoplastic elastomeric materials, such as one or more thermoplastic polyurethane (TPU) copolymers, one or more ethylene-vinyl alcohol (EVOH) copolymers, and the like. The tensile layers 14a, 14b are formed of a first elastomeric material and the outer barrier layers 16a, 16b are formed of a second elastomeric material.
The first elastomeric material is selected with a first melting temperature suitable for allowing the tensile layers 14a, 14b to be melded to each other through the plate 18 without affecting the material properties of the plate 18. For instance, the first melting temperature of the first elastomeric material is low enough that the plate 18 will not be melted, deformed, or weakened when subjected to the first melting temperature during assembly of the bladder 10. Accordingly, elastomeric material having different melting temperatures can be selected as the tensile layer 14a, 14b depending on the material of the plate 18 (e.g., polymeric, composite, metal). In some examples, where the plate 18 is formed of a polymeric material having a relatively low melting point (compared to metals or composites), the first elastomeric material may be a low-melt TPU having a melting temperature that is less than a melting temperature of the material of the plate 18.
The second elastomeric material of the outer barrier layers 16a, 16b may be different than the first elastomeric material of the tensile layers 14a, 14b. For example, where a low-melt TPU material is utilized as the first elastomeric material, a conventional TPU material having a higher melting temperature may be utilized as the second elastomeric material. Utilizing a conventional TPU having a higher melting temperature for the second elastomeric material provides the outer barrier layers 16a, 16b of the chambers 12a, 12b with improved durability.
One or more of the barrier layers 14a, 14b, 16a, 16b can independently be transparent, translucent, and/or opaque. As used herein, the term “transparent” for a barrier layer and/or a fluid-filled chamber means that light passes through the barrier layer in substantially straight lines and a viewer can see through the barrier layer. In comparison, for an opaque barrier layer, light does not pass through the barrier layer and one cannot see clearly through the barrier layer at all. A translucent barrier layer falls between a transparent barrier layer and an opaque barrier layer, in that light passes through a translucent layer but some of the light is scattered so that a viewer cannot see clearly through the layer.
As used herein, the term “barrier layer” (e.g., barrier layers 14a, 14b, 16a, 16b) encompasses both monolayer and multilayer films. In some embodiments, one or more of the barrier layers 14a, 14b, 16a, 16b is produced (e.g., thermoformed or blow molded) from a monolayer film (a single layer). In other embodiments, one or more of the barrier layers 14a, 14b, 16a, 16b is produced (e.g., thermoformed or blow molded) from a multilayer film (multiple sublayers). In either aspect, each layer or sublayer can have a film thickness ranging from about 0.2 micrometers to about be about 1 millimeter. In further embodiments, the film thickness for each layer or sublayer can range from about 0.5 micrometers to about 500 micrometers. In yet further embodiments, the film thickness for each layer or sublayer can range from about 1 micrometer to about 100 micrometers.
As used herein, “polyurethane” refers to a copolymer (including oligomers) that contains a urethane group (—N(C═O)O—). These polyurethanes can contain additional groups such as ester, ether, urea, allophanate, biuret, carbodiimide, oxazolidinyl, isocynaurate, uretdione, carbonate, and the like, in addition to urethane groups. In an aspect, one or more of the polyurethanes can be produced by polymerizing one or more isocyanates with one or more polyols to produce copolymer chains having (—N(C═O)O—) linkages.
Examples of suitable isocyanates for producing the polyurethane copolymer chains include diisocyanates, such as aromatic diisocyanates, aliphatic diisocyanates, and combinations thereof. Examples of suitable aromatic diisocyanates include toluene diisocyanate (TDI), TDI adducts with trimethyloylpropane (TMP), methylene diphenyl diisocyanate (MDI), xylene diisocyanate (XDI), tetramethylxylylene diisocyanate (TMXDI), hydrogenated xylene diisocyanate (HXDI), naphthalene 1,5-diisocyanate (NDI), 1,5-tetrahydronaphthalene diisocyanate, para-phenylene diisocyanate (PPDI), 3,3′-dimethyldiphenyl-4, 4′-diisocyanate (DDDI), 4,4′-dibenzyl diisocyanate (DBDI), 4-chloro-1,3-phenylene diisocyanate, and combinations thereof. In some embodiments, the copolymer chains are substantially free of aromatic groups.
In particular aspects, the polyurethane polymer chains are produced from diisocynates including HMDI, TDI, MDI, H12 aliphatics, and combinations thereof. In an aspect, the thermoplastic TPU can include polyester-based TPU, polyether-based TPU, polycaprolactone-based TPU, polycarbonate-based TPU, polysiloxane-based TPU, or combinations thereof.
In another aspect, the polymeric layer can be formed of one or more of the following: EVOH copolymers, poly(vinyl chloride), polyvinylidene polymers and copolymers (e.g., polyvinylidene chloride), polyamides (e.g., amorphous polyamides), amide-based copolymers, acrylonitrile polymers (e.g., acrylonitrile-methyl acrylate copolymers), polyethylene terephthalate, polyether imides, polyacrylic imides, and other polymeric materials known to have relatively low gas transmission rates. Blends of these materials, as well as with the TPU copolymers described herein and optionally including combinations of polyimides and crystalline polymers, are also suitable.
The barrier layers 14a, 14b, 16a, 16b may include two or more sublayers (multilayer film) such as shown in Mitchell et al., U.S. Pat. No. 5,713,141 and Mitchell et al., U.S. Pat. No. 5,952,065, the disclosures of which are incorporated by reference in their entirety. In embodiments where the barrier layers 14a, 14b, 16a, 16b include two or more sublayers, examples of suitable multilayer films include microlayer films, such as those disclosed in Bonk et al., U.S. Pat. No. 6,582,786, which is incorporated by reference in its entirety. In further embodiments, the barrier layers 14a, 14b, 16a, 16b may each independently include alternating sublayers of one or more TPU copolymer materials and one or more EVOH copolymer materials, where the total number of sublayers in each of the barrier layers 14a, 14b, 16a, 16b includes at least four (4) sublayers, at least ten (10) sublayers, at least twenty (20) sublayers, at least forty (40) sublayers, and/or at least sixty (60) sublayers.
The bladder 10 can be produced from the barrier layers 14a, 14b, 16a, 16b using any suitable technique, such as thermoforming (e.g. vacuum thermoforming), blow molding, extrusion, injection molding, vacuum molding, rotary molding, transfer molding, pressure forming, heat sealing, casting, low-pressure casting, spin casting, reaction injection molding, radio frequency (RF) welding, and the like. In an aspect, the barrier layers 14a, 14b, 16a, 16b can be produced by co-extrusion followed by vacuum thermoforming to produce an inflatable chamber 12a, 12b, which can optionally include one or more valves (e.g., one way valves) that allows the chamber 12a, 12b to be filled with the fluid (e.g., gas).
The chambers 12a, 12b can be provided in a fluid-filled (e.g., as provided in bladder 10) or in an unfilled state. The chambers 12a, 12b can be filled to include any suitable fluid, such as a gas or liquid. In an aspect, the gas can include air, nitrogen (N2), or any other suitable gas. In other aspects, the chambers 12a, 12b can alternatively include other media, such as pellets, beads, ground recycled material, and the like (e.g., foamed beads and/or rubber beads). The fluid provided to the chambers 12a, 12b can result in the chambers 12a, 12b being pressurized. Alternatively, the fluid provided to the chambers 12a, 12b can be at atmospheric pressure such that the chambers 12a, 12b are not pressurized but, rather, simply contain a volume of fluid at atmospheric pressure.
The chambers 12a, 12b desirably have a low gas transmission rate to preserve its retained gas pressure. In some embodiments, the chambers 12a, 12b have a gas transmission rate for nitrogen gas that is at least about ten (10) times lower than a nitrogen gas transmission rate for a butyl rubber layer of substantially the same dimensions. In an aspect, the chambers 12a, 12b have a nitrogen gas transmission rate of 15 cubic-centimeter/square-meteratmosphereday (cm3/m2·atm·day) or less for an average film thickness of 500 micrometers (based on thicknesses of barrier layers 14a, 14b, 16a, 16b). In further aspects, the transmission rate is 10 cm3/m2·atm·day or less, 5 cm3/m2·atm·day or less, or 1 cm3/m2·atm·day or less.
Turning now to
With reference to
With the components 14a, 14b, 18 positioned within the mold cavity 114a, the first tool 102a is then moved to a closed position (
The first tool 102a may be a thermoforming tool 102a configured to subject the components 14a, 14b, 18 to a combination of heat and pressure to join the tensile layers 14a, 14b together. However, in other examples, the tensile layers 14a, 14b may be chemically attached (e.g., adhesives) or may be joined together using ultrasonic welding. As discussed above, the sides 20, 22 of the plate 18 are inhibited from bonding to the tensile layers 14a, 14b by forming the plate 18 of an incompatible material or by coating the sides 20, 22 with a bond inhibitor. For example, where thermoforming (melding) is used, the plate 18 may have a higher melting temperature than the tensile layers 14a, 14b to prevent melding between the plate 18 and the tensile layers 14a, 14b at the melting temperature of the tensile layers 14a, 14b. In other examples, a chemical coating may prevent adhesion, or a mechanical barrier may prevent attachment. Thus, while the tensile layers 14a, 14b may be compressed directly or indirectly against the plate 18 during the second step (
Turning now to
At
The profiles of the mold surfaces 120a, 122a of the second tool 104a respectively define the shapes of the first and second chambers 12a, 12b in the first configuration 10a of the bladder 10. For instance, the mold surfaces 120a, 122a each include interior projections 126a corresponding to the web areas 52a, 52b and peripheral projections 126b corresponding to the peripheral seam 54. The interior projections 126a of each mold surface 120a, 122a are aligned with the tensile elements 60 of the chassis 58, between the inner bonds 42. Thus, as discussed below, the interior projections 126a are configured to compress the outer barrier layers 16a, 16b against the tensile elements 60 formed by the tensile layers 14a, 14b. The peripheral projections 126b are positioned outwardly from the outer periphery 24 of the plate 18, and are configured to compress the outer peripheries 48a, 48b of the outer layers 16a, 16b against the first portion of the peripheral seam 54 formed by the tensile layers 14a, 14b.
The mold surfaces 120a, 122a also include recesses 128a, 128b formed between the projections 126a, 126b, which correspond to the shapes of the chambers 12a, 12b. In the illustrated example, the upper and lower mold surfaces 120a, 122a each include interior recesses 128a corresponding to interior subchambers 62 and peripheral recesses 128b corresponding to peripheral subchambers 64. Here, the interior recesses 126a of the upper mold 116a are shallower than the interior recesses 126a of the lower mold 118a, whereby the interior recesses 126a of the upper mold 116a form interior subchambers 62 in the first chamber 12a that have a lesser height than the interior subchambers 62 of the second chamber 12b.
Turning now to
In the closed position, the interior projections 126a and the peripheral projections 126b of each mold 116a, 118a are aligned with each other across the barrier layers 16a, 16b and the chassis 58, such that the barrier layers 16a, 16b and the chassis 58 are compressed between opposing (i.e., facing) distal ends of corresponding projections 126a, 126b. As shown, the interior projections 126a of each mold 116a, 118a are aligned with each other across the tensile elements 60 of the chassis 58 to form a first plurality of the outer bonds 50 between the first interior barrier layer 14a and the first outer barrier layer 16a on the first side 20 of the plate 18, and a second plurality of the outer bonds 50 between the second tensile layer 14b and the second outer barrier layer 16b on the second side 22 of the plate 18. The peripheral projections 126b are aligned with each other across the portion of the peripheral seam 54 formed by the tensile layers 14a, 14b, and are configured to compress the outer barrier layers 16a, 16b against the tensile layers 14a, 14b to join the outer barrier layers 16a, 16b to the peripheral seam 54.
With the outer barrier layers 16a, 16b joined to the tensile layers 14a, 14b at the outer bonds 50 and the peripheral seam 54, the bladder 10 can be removed from the second tool 104a, as shown in
As shown and discussed above, the different profiles imparted to the outer barrier layers 16a, 16b during the vacuum forming process result in the first chamber 12a and the second chamber 12b having different profiles. Additionally, the interior voids 56a, 56b of the chambers 12a, 12b may be provided with different pressures. For instance, the interior void 56a of the first chamber 12a may have a greater pressure than the interior void 56b of the second chamber 12b, or vice versa. Optionally, spaces 66 formed between the tensile elements 60 and the plate 18 may also be pressurized with same or different pressures than the pressures of the interior voids 56a, 56b.
With particular reference to
As shown in
Referring to
Turning to
With particular reference to
As shown in
In
Referring to
With continued reference to
With particular reference to
The system 100d and method of
Thus, in contrast to the first and second configurations 10a, 10b where the peripheral subchamber 64 is entirely filled with fluid, and the third configuration 10c where the protuberance 34 is contained within the natural profile of the peripheral chamber 64, in the fourth configuration 10d, the protuberance 34 imparts an extended profile to the peripheral subchamber 64. Again, while the illustrated example shows the protuberance 34 disposed in the peripheral portion 28 of the plate 18, the plate 18 may additionally or alternatively include projections formed in the interior portion 28 on either side 20, 22.
The systems 100a-100d and methods for forming the different configurations 10a-10d of the bladder 10 described above provide several advantages. Initially, providing the plate 18 within the bladder 10 allows an overall stiffness of the bladder 10 to be tuned. For instance, plates formed of different materials, shapes, and thicknesses may be incorporated within the bladder to provide the bladder 10 with integrated stiffness and support. In addition to providing structural benefits, the plate 18 simplifies formation of the bladder 10 by defining bonding locations 42 for the tensile layers 14a, 14b, which ultimately results in the formation of the tensile elements 60 used to constrain expansion of the outer barrier layers 16a, 16b.
Here, the use of tensile layers 14a, 14b having a material with a lower melting temperature than the material(s) of the plate 18 allows the tensile layers 14a, 14b to be joined to each other through the plate 18 in a single molding step without affecting the properties of the plate 18. These tensile layers 14a, 14b offer multiple benefits. For example, the tensile layers 14a, 14b provide a simplified tensile structure within the barrier layer, whereby the tensile elements 60 are simply formed by attaching the tensile layers 14a, 14b to each other at discrete locations. Additionally, the tensile layers 14a, 14b isolate the first chamber 12a and the second chamber 12b, such that the first chamber 12a can be pressurized with a different pressure than the second chamber 12b. Accordingly, the barrier 10 may be tuned with first and second chambers 12a, 12b having different pressures and shapes.
The following Clauses provide an exemplary configuration for a bladder for an article of footwear described above.
Clause 1: A bladder for an article of footwear, the bladder comprising a plate, a first tensile layer disposed adjacent to a first side of the plate, a second tensile layer disposed on an opposite side of the plate from the first tensile layer, the second tensile layer joined to the first tensile layer through the plate by a plurality of inner bonds, and a first barrier layer disposed adjacent to the first tensile layer and joined to the first tensile layer by a plurality of first outer bonds to form a first chamber, one or more of the first outer bonds interposed between adjacent ones of the inner bonds.
Clause 2: The bladder of Clause 1, wherein the first tensile layer and the second tensile layer are formed of a first elastomeric material and the first barrier layer is formed of a second elastomeric material different from the first elastomeric material.
Clause 3: The bladder of Clause 2, wherein the first elastomeric material has a lower melting temperature than the second elastomeric material.
Clause 4: The bladder of any of the preceding Clauses, further comprising a second barrier layer disposed adjacent to the second tensile layer and joined to the second tensile layer by a plurality of second outer bonds to form a second chamber on the opposite side of the plate than the first chamber.
Clause 5: The bladder of Clause 4, wherein the first chamber is fluidly isolated from the second chamber by at least one of the first tensile layer and the second tensile layer.
Clause 6: The bladder of Clause 4, wherein the first chamber has a different pressure than the second chamber.
Clause 7: The bladder of any of the preceding Clauses, wherein the plate includes a plurality of apertures extending through the plate and each of the inner bonds is formed within one of the apertures.
Clause 8: The bladder of any of the preceding Clauses, wherein the second tensile layer is joined to the first tensile layer around a periphery of the plate.
Clause 9: The bladder of any of the preceding Clauses, wherein the first tensile layer and the second tensile layer are detached from the plate between the inner bonds to form one or more tensile elements.
Clause 10: The bladder of Clause 9, wherein each of the first outer bonds is formed with one of the tensile elements.
Clause 11: A bladder for an article of footwear, the bladder comprising a plate having one or more apertures, a first tensile layer disposed adjacent to a first side of the plate, a second tensile layer disposed on an opposite side of the plate from the first tensile layer and joined to the first tensile layer within each of the one or more apertures, and a first barrier layer disposed adjacent to the first tensile layer and joined to the first tensile layer at discrete locations to form a first chamber.
Clause 12: The bladder of Clause 11, wherein the first tensile layer and the second tensile layer are formed of a first elastomeric material and the first barrier layer is formed of a second elastomeric material different from the first elastomeric material.
Clause 13: The bladder of Clause 12, wherein the first elastomeric material has a lower melting temperature than the second elastomeric material.
Clause 14: The bladder of any of the preceding Clauses, further comprising a second barrier layer disposed adjacent to the second tensile layer and joined to the second tensile layer by a plurality of second outer bonds to form a second chamber on the opposite side of the plate than the first chamber.
Clause 15: The bladder of Clause 14, wherein the first chamber is fluidly isolated from the second chamber by at least one of the first tensile layer and the second tensile layer.
Clause 16: The bladder of Clause 14, wherein the first chamber has a different pressure than the second chamber.
Clause 17: The bladder of any of the preceding Clauses, wherein the second tensile layer is joined to the first tensile layer around a periphery of the plate.
Clause 18: The bladder of any of the preceding Clauses, wherein the first tensile layer and the second tensile layer are detached from the plate between the apertures to form one or more tensile elements.
Clause 19: The bladder of Clause 18, wherein the first barrier layer is attached to each of the one or more tensile elements of the first tensile layer.
Clause 20: The bladder of Clause 18, wherein the first barrier layer is attached to the first tensile layer along each of the apertures.
The foregoing description has been provided for purposes of illustration and description. It is not intended to be exhaustive or to limit the disclosure. Individual elements or features of a particular configuration are generally not limited to that particular configuration, but, where applicable, are interchangeable and can be used in a selected configuration, even if not specifically shown or described. The same may also be varied in many ways. Such variations are not to be regarded as a departure from the disclosure, and all such modifications are intended to be included within the scope of the disclosure.
This application is a continuation of U.S. application Ser. No. 17/317,793, filed on May 11, 2021, which claims priority under 35 U.S.C. § 119(e) to U.S. Provisional Application No. 63/023,271, filed on May 12, 2020. The disclosures of these prior applications are considered part of the disclosure of this application and are hereby incorporated by reference in their entirety.
Number | Date | Country | |
---|---|---|---|
63023271 | May 2020 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 17317793 | May 2021 | US |
Child | 18421515 | US |