Blend of polyethylene terephthalate matrix and thermotropic liquid crystal block copolymer

Abstract

Blends of a poly(ethylene terephthalate) matrix and a thermotropic liquid crystalline segmented block copolymer comprising rod (e.g., aromatic ester mesogen units containing flexible alkylene spacers) and flexible coil polymer blocks of poly(butylene terephthalate) can be used as molding compositions or in the formation of fibers and films.

Description

BACKGROUND OF THE INVENTION

It is known to blend flexible coil polymers with either liquid crystal homopolymers or liquid crystal random copolymers. A recent review of work in this field is "Polymer Blends Containing Liquid Crystals: A Review", by D. Dutta et al., Polymer Engineering and Science, Mid-September 1990, Vol. 30, No. 17, pp. 1005-1018. The Dutta et al. publication (on pages 1008-1011) discusses certain prior work by Joseph et al. and Misra et al., for example, in which poly(ethylene terephthalate), PET, was used as the matrix material and was mixed with a liquid crystalline copolyester based on parahydroxy benzoic acid (PHB) and PET. In such systems, the flexible coil polymer component (PET) in the liquid crystal polymer was the same as the PET matrix. Dutta et al. also report that Kimura et al. blended a poly(butylene terephthalate), PBT, matrix with a PET/PHB liquid crystal copolymer.

European Patent Publication No. 390,489 shows blends of a crystalline polyalkylene arylate base resin, which in Example 4, can be PET with a random copolyester having a polyalkylene arylate segment which exhibits smectic liquid crystallinity and a polyalkylene arylate segment which does not exhibit smectic liquid crystallinity. This liquid crystal copolyester is derived from the copolymerization of dimethyl terephthalate, dimethyl bibenzoate, and 1,4-butanediol. With such random copolymer additives, the blending operation can readily give rise to transesterification between the matrix and flexible coil polymer moieties in the copolymer.

Quite recently, in contrast to the foregoing systems which rely upon blends of a flexible coil polymer matrix with either a liquid crystal homopolymer or random copolymer, it has been found that a blend can be fabricated from a flexible coil polymer matrix and a thermotropic liquid crystal segmented block copolymer containing mesogenic and flexible coil polymer blocks (as described in U.S. Ser. No. 726,600, filed Jul. 8, 1991). The flexible coil blocks were deemed essential in order to lower the melting point of the liquid crystal-containing additive. For those systems, it was taught that the flexible coil blocks in the block copolymer had to be substantially similar to the composition of the flexible coil polymer matrix, i.e., a PBT matrix and a PBT flexible coil polymer matrix. That application indicates that selection of a PET matrix requires selection of a PET flexible coil block segment. In such block copolymer systems it was perceived that there was a critical need to very closely match the matrix polymer with the flexible coil polymer block segment in the liquid crystal additive in order to enhance compatibility of the blend components.

One fairly recent U.S. patent which describes liquid crystal fiber-reinforced polymer composites and the process for making them is U.S. Pat. No. 4,728,698 to A. Isayev.

SUMMARY OF THE INVENTION

The present invention relates to blends of a PET, rather than PBT, matrix and a thermotropic liquid crystal segmented block copolymer containing mesogenic and flexible coil polymer blocks in which the flexible coil block is PBT. Such blends have utility as molding compositions in the formation of shaped articles and as a composition suitable for the production of fibers and films.

DETAILED DESCRIPTION OF THE INVENTION

The matrix component for the blends of the present invention is of poly(ethylene terephthalate).

The liquid crystalline segmented block copolymer which is intended to be added to the selected flexible coil polymer matrix can be envisioned to have the general formula:

--[[Rod].sub.x --[PBT].sub.y ].sub.p -- where "Rod" indicates the mesogenic block with x, normally from 2 to 50, indicating the number of mesogen repeats, "PBT" indicating the block comprising the PBT segment, with y, normally from about 2 to about 50, indicating the number of repeat units in the flexible coil polymer block, and p representing the repeat units of Rod and PBT blocks. The mole % rod in the total polymer can range from about 4% to about 80%. The repeat unit p can range from about 1 to about very large numbers such as 50-500 for high molecular weight segmented block copolymers.

The rod length, which is responsible for liquid crystalline properties for the block copolymer additive and the % block in the matrix/block copolymer combination need to be appropriately balanced within the general ranges given above.

The type of mesogenic unit for the rod portion of the LC copolymer can be appropriately selected from known mesogenic units (main chain thermotropic liquid crystal polymers) including those of the general structure:

[--A--Y--X--Z--].sub.m (I) as set forth in U.S. Pat. No. 4,952,334, for example, which is incorporated herein by reference. In the above formula, for example, in preferred embodiments, X can be (CH.sub.2).sub.n, where n is an integer of from 2 to 10, m can range from about 2 to about 50, and Y and Z can each be --C(O)O-- or --C(O)NH-- or can be a single bond between two carbon atoms, and A can be p-phenylene, 1,4-, 2,6-, or 1,5-naphthylene, monosubstituted phenylene with methyl, chloro, or phenyl substitution; --ArCH.dbd.CHAr--, where Ar is a phenyl ring, --AR--C(O)OAr--, --Ar--C(O)NHAr--, or --ArOC(O)--Ar--C(O)O--Ar--, as more fully depicted in the aforementioned patent. In addition another mesogenic unit which can be employed has the structure --Ar--C(O)--NH--Ar--NH--C(O)--Ar--. The commercial rod polymers based on oxybenzoate units, 4,4'-biphenylene terephthalate units, and oxynaphthalene carboxylate units (the latter two including copolymers with the oxybenzoate units) can be especially preferred.

A particularly preferred structure for the "Rod" or mesogenic unit is of the general type described by Ober et al. in Polymer Journal, Vol. 14, No. 1, pp. 9-17 (1972) and, in view of its presence in a block copolymer as contrasted to the Ober et al. homopolymer, has the structure:

--[--OArC(O)O(CH.sub.2).sub.n OC(O)ArOC(O)ArC(O)--]--.sub.x where Ar represents phenyl with para- bond sites, n can range from 2 to 10, e.g., 4 and x can range, for example, from about 2 to about 50. These mesogenic units can be characterized as aromatic ester mesogenic units containing a flexible alkylene spacer. The "triad" structure comprising three linearly-aligned aromatic rings, the bis(p-carboxyphenyl) terephthalate moiety, and a flexible spacer of varying length (n), which can be alkylene or alkylene with heteroatom (e.g., oxygen) interruption, is particularly preferred as depicted above. The mesogenic units contain "diad" or "dyad" linkages, --OC(O)ArOC(O)ArC(O)--, at either end adjacent the connection points with the PBT block segments.

Although the particular thermotropic LCP block (e.g., triad with flexible spacer block and polyester block) of structure (I), above, is not a true rigid-rod, it readily assumes an extended chain structure and forms nematic mesophases and consequently high modulus/strength structures. Ideally, the high strength chain extended block polymer molecules would be very finely dispersed in the PET matrix and would be expected to have potential as a high performance molecular composite material.

The foregoing type of thermotropic liquid crystal block copolymer can be synthesized by the process shown in U.S. Ser. No. 726,600. Preferably it is synthesized by the one reactor process described and claimed in U.S. Ser. No. 779,477, filed on Oct. 18, 1991, entitled "Synthesis of Block Liquid Crystal Copolymer", which is incorporated herein by reference.

In the blends of the present invention, the block copolymer additive can be present at about 0.5% to about 99%, by weight of the matrix, more preferably at about 1% to about 35% by weight of the matrix for fiber and molding applications.

The additive acts as a nucleating agent and affects the crystallization behavior of the PET with the blend showing a higher crystallization temperature and a narrow temperature range where crystallization occurs. This provides evidence for the increased orientation and crystallinity provided by the LCP additive. The blend also exhibits a high melt flow rate (the LCP acts as a flow promoter) and, hence, it can be melt processed at temperatures which are 20.degree.-40.degree. C. lower than required for PET homopolymer. Melt Index values (g/10 min. and W-2,160 kg) that were recorded at 260.degree. C. for molding grade PET (ARNITE DO2-300 from Akzo) blends with 0%, 1%, 10% and 20% LCP, respectively, were 17, 31, 56 and 79, respectively. Scanning electron microscopy (SEM) examination of the molded specimens did not show any phase separation.

Fibers prepared from the blends of fiber grade PET with the LCP described herein showed significantly improved tensile properties as well as shrinkage resistance as compared to PET fibers in certain runs. The PET/LCP blends could be melt spun into fibers at temperatures 20.degree.-40.degree. C. lower than required for the PET homopolymer. The drawing temperature of the as-spun fibers should be adjusted according to the respective Tg values as would be known to persons of ordinary skill in the art. As spun, blend fibers demonstrated improved drawing properties as compared to fibers made from PET alone. The Melt Index (g/10 min. and W=2,160 kg) recorded at 270.degree. C. for the blend containing 10% wt LCP was about five times higher than that obtained for PET alone even at 285.degree. C. SEM analysis of the blend fibers showed a fine morphology without phase separation.

The Examples which follow illustrate certain embodiments of the invention.

EXAMPLE 1

This Example relates to blend compositions formed from a PET matrix and a block copolymer of a triaromatic mesogenic unit with butylene spacers within and PBT blocks. Ober et al. in Polymer J. 14, (1), 9 (1982) shows the structure of the mesogenic or "rod" portion only of the thermotropic liquid crystalline block copolymer (abbreviated "LCP" below).

The blends were made as follows:

A series of mixtures of fiber grade PET (AKZO tire yarn chips) and the LCP were tumble mixed for about three hours under nitrogen to yield a stable preblend by the process described and claimed in U.S. Ser. No. 812,607, filed on even date herewith. A portion of the preblend was then extruded in a CSI mixing extruder in the temperature range of 240.degree. C. to 280.degree. C. depending on blend composition using a residence time of 1-2 minutes (Run Nos. 1-10). The extrudate was then ground to 20 mesh size using a Thomas Wiley mill.

Another portion of the preblend was extruded in a Brabender mixer equipped with a single screw extruder at 230.degree.-270.degree. C. (Run No. 11). The extrudate was then pelletized.

Table 1 illustrates thermal properties such as glass transition temperature (Tg), melt temperature (Tm), and crystallization temperature (Tc), which were measured using a Perkin Elmer DSC-7 differential scanning calorimeter. The blend compositions exhibited a single Tg which indicates that both components are highly compatible (even miscible). The blends also showed a higher crystallization temperature as compared to the unmodified PET. Blends containing less than 35% of the LCP show one crystallization temperature. Above 35% LCP, multiple melting and crystallization behavior was observed for the blends, which indicates the presence of a LCP rich phase.

TABLE 1______________________________________ PET/LCP Extrusion Temp Tg Tm TcRun No. (wt/wt) (.degree.C.) (.degree.C.) (.degree.C.) (.degree.C.)______________________________________1 100/0.sup.(a) 275-280 81 246 1642 98/2 275-280 81 248 1823 95/5 256-272 78 248 1904 90/10 260-265 78 248 1785 80/20 260-265 72 249 1796 50/50 250-255 60 246 1717 20/80 245-250 42 201 164 234 2318 10/90 242-247 39 202 185 247 2309 5/95 235-240 36 203 162 252 191 22810 0/100.sup.(a) 235-240 36 204 163 247 187 228 27511 90/10 230-270 78 249 179______________________________________ .sup.(a) for comparison, not part of invention.

Melt flow properties of the selected blend compositions are shown in Table 2. The melt indices of the blends are higher than that of the PET, in turn the blends can be melt-processed at lower temp than the unmodified PET.

TABLE 2______________________________________ PET/LCP MFI.sup.(a)Run No. (wt/wt) g/10 min at 270.degree. C.______________________________________1 100/0.sup.(b) 104 90/10 465 80/20 149______________________________________ .sup.(a) melt flow index at weight = 2160 gm. .sup.(b) for comparison at 285.degree. C., not part of the invention.

EXAMPLE 2

This illustrates a molding composition containing the type of PET matrix and LCP block copolymer described in Example 1. The molding composition blend was formed by the preblending and then melt blending procedure described in Example 1 with molding grade PET (Arnite DO2-300 brand from Akzo) and LCP block copolymer.

The LCP affected the crystallization behavior of the PET. The PET/LCP blends showed higher crystallization temperature and a narrow temperature range where the crystallization occurs. The blends also exhibited a high melt flow rate and hence can be melt-processed at temperatures 20.degree.-40.degree. C. lower than required for the PET homopolymer. Melt Index values (g/10 min and W=2,160 g) recorded at 260.degree. C. for the PET (Arnite DO2-300) blends containing 0, 1, 10 and 20% LCP were 17, 31, 56 and 79, respectively. SEM analysis of the molded specimens showed a very fine structure.

Table 3, below, shows the thermal properties and melt flow index of the blend composition:

TABLE 3______________________________________ PET/LCP Tm Tc MFI.sup.(b)Run No. (wt/wt) (.degree.C.) (.degree.C.) (g/10 min at 260.degree. C.)______________________________________1 100/0.sup.(a) 243 173 172 99/1 243 183 313 95/5 242 180 394 90/10 243 181 565 80/20 243 176 796 50/50 236 157 120 1947 20/80 198 148 190 219 183 236______________________________________ .sup.(a) for comparison, not part of the invention. .sup.(b) melt flow index at weight = 2160 g.

EXAMPLE 3

This Example illustrates some spinning and drawing work in making fibers from blends of 90% PET and 10% of the LCP block copolymer and of 80% PET and 20% LCP.

Melt spinning was conducted on a RANDCASTLE MICROTRUDER apparatus with a 1/4 inch screw extruder and a single spinning hole having a diameter of 0.5 mm and an 1/d of 20. A CSI take-up unit was employed using a range of velocity of 90-100 m/min.

The hot drawing step used two CSI take-up units and a hot plate.

The following spinning and drawing parameters were used:

TABLE 4______________________________________Melt Spinning PET* Blends______________________________________I Zone temperature (.degree.C.): 240 240II Zone Temperature (.degree.C.): 283 266III Zone temperature (.degree.C.): 308 260 Die Temperature (.degree.C.): 317 266Take-up velocity (m/min): 100 90Hot Drawing:Temperature (.degree.C.): 110-115 110-115Feed velocity (m/min): 7.5 10.8Take-up velocity (m/min): 34.1 32.8Draw ratio: 4.5 3.0______________________________________ *for comparison, not part of the invention.

The following differential scanning calorimetry (DSC) data were generated for fibers made from a blend of 90% PET and 10% LCP and control PET in accordance with the above procedure.

TABLE 5______________________________________Parameter PET Blend______________________________________Glass transition temp (.degree.C.): -- --Melt transition temp (.degree.C.): 245 242Crystallization temp (.degree.C.): 198 198Beginning of crystallization (.degree.C.): 218 212End of crystallization (.degree.C.): 172 181Heating and cooling rate - 20 deg/min.______________________________________ Blend fibers of 90:10 and 80:20 PET:LCP revealed improved tensile properties as shown in Table 6. TABLE 6______________________________________ Materials (monofilaments) PET/LCP PET/LCP PET.sup.(a) (90:10) (80:20)______________________________________Linear Density, dtex 8.4 7.5 8.6Tenacity, mN/tex 340 399 329Elongation at break, % 36 16.6 17.3Initial modulus, N/tex 10.7 11.5 12.2______________________________________ .sup.(a) For comparison, not part of the invention.

EXAMPLE 4

This Example illustrates that fibers can be spun from the blends at lower temperatures depending on the LCP content in the blends as compared to unmodified PET. In addition, as-spun blend fibers can be drawn at a higher ratio. Monofilaments were spun using the RANDCASTLE MICROTRUDER apparatus described in Example 3:

TABLE 7______________________________________Melt Spinning PET PET/LCP (90:10)Run No. 1 2 3 4 5______________________________________I Zone Temp (.degree.C.): 260 240 240 240 240II Zone Temp (.degree.C.): 299 276 276 276 278III Zone Temp (.degree.C.): 310 300 300 300 300Die Temp (.degree.C.): 310 263 253 245 253Output (g/min): 0.65 0.75 0.78 0.8 0.7Drawing:Pin Temp (.degree.C.): 78 78 78 78 77Hot Plate (.degree.C.): 210 210 210 210 220Feed Velocity (m/min): 4.6 5.5 5.2 4.6 4.7Take-up Velocity 25.6 40.7 39 31 34.4(m/min):Total Draw Ratio: 5.5 7.4 7.5 6.7 7.35______________________________________

The properties of drawn fibers are shown in Table 8.

TABLE 8______________________________________ PET (a) Blend (90:10)Run No. 1 3 5______________________________________Diameter (.mu.m): 35 36 36Tenacity (mN/tex): 502 652 770Elong. at break (%): 34.1 8.7 7.9Initial Modulus (N/tex): 10.1 13.8 17.1______________________________________

EXAMPLE 5

This illustrates another Example for fiber spinning from the blends and fiber properties (10 filaments yarn).

Spinning was carried out on an 18-mm Fourne extruder. A spinning plate with holes (10) of 450 .mu.m diameter was used. The filter package contained 325 mesh gauzes (44 .mu.m) as the finest filtration medium. Winding took place on a separate Leesona winder. Further spinning conditions for the blend, PET/LCP (90:10), and a control PET are shown in Table 9:

TABLE 9______________________________________ Blend PET______________________________________Temperature (.degree.C.)Zone 1 (.degree.C.) 241 309Zone 2 (.degree.C.) 270 297Zone 3 (.degree.C.) 275 297Die/spinnerette (.degree.C.): 273 297Throughput/hole (g/min): 0.7 0.7Winding speed (m/min): 65 65______________________________________

Drawing of the as-spun blend fibers was performed on a pin (6 cm diameter) and a hot plate (40 cm length, 3 passes). With three godet-idler roller combinations, the draw ratios in the first and second step could be adjusted independently. The conditions are shown in Table 10, below. Quite remarkably, the total draw ratio could be adjusted much higher for the blend yarn than for the PET control.

The properties of drawn yarns are in Table 11, below. The initial modulus was higher for the blend yarn in comparison with that of the PET control. However, the shrinkage was lower.

TABLE 10______________________________________Run No. 1 2 3 4 5______________________________________Polymer Composition Blend* Blend Blend Blend BlendPin temp. (.degree.C.): 83 83 83 82 82Hot plate 211 211 211 222 222temp. (.degree.C.)Feed Velocity 4 4 4 4 4(m/min):Take-up velocity 22 24 26 26.3 27(m/min):Draw ratiofirst stage: 4.38 4.60 4.60 4.50 4.50second stage: 1.26 1.30 1.41 1.46 1.50Total: 5.5 6.0 6.5 6.58 6.75Run No. 6 7 8 9______________________________________Polymer Composition PET PET PET PETPin temp. (.degree.C.): 73 73 78 83Hot plate 211 211 211 211temp. (.degree.C.)Feed Velocity 4 4 4 4(m/min):Take-up velocity 19 20 22 22(m/min):Draw ratiofirst stage: 3.5 3.5 4.38 4.38second stage: 1.36 1.43 1.26 1.26Total: 4.75 5.0 5.5 5.5______________________________________ *The blend used in Run Nos. 1-5 was a 90/10 wt ratio of PET/LCP. TABLE 11______________________________________Run No. 1 2 3 4 5______________________________________Polymer Composition Blend* Blend Blend Blend BlendDraw ratio 5.5 6.0 6.5 6.58 6.75Linear density 200 185 172 172 166(dtex):Tenacity (mN/tex): 492 540 584 610 636Elong. at break (%): 10.9 8.2 6.2 6.6 6.3Initial modulus 11.4 11.7 12.3 12.3 13.4(N/tex):Hot-Air shrinkage (%) 11.1 12.2 12.8 -- 11.4at 190.degree. C.:Run No. 6 7 8 9Polymer Composition PET PET PET PET______________________________________Draw ratio 4.75 5.0 5.5 5.5Linear density 222 208 195 194(dtex):Tenacity (mN/tex): 480 530 590 619Elong. at break (%): 17.2 16.0 11.7 12.0Initial modulus 9.8 10.1 10.3 10.5(N/tex):Hot-Air shrinkage (%) -- -- -- 14.6at 190.degree. C.:______________________________________ *The blend used in Run Nos. 1-5 was a 90/10 wt ratio of PET/LCP.

EXAMPLE 6

This illustrates another Example for fiber spinning from the blends and fiber properties (10 filaments yarn).

Spinning was carried out on an 18-mm Fourne & extruder as in Example 5. Further spinning conditions for the blend, PET/LCP (90:10), and a control PET are shown in Table 12:

TABLE 12______________________________________ Blend PET______________________________________Temperature (.degree.C.)Zone 1 (.degree.C.) 270 295Zone 2 (.degree.C.) 270 290Zone 3 (.degree.C.) 270 290Die/spinnerette (.degree.C.): 290 290Throughput/hole (g/min): 0.7 0.7Winding speed (m/min): 65 65______________________________________

Drawing of the as-spun blend fibers was performed on a pin (6 cm diameter) and a hot plate (40 cm length, 3 passes) as in Example 5. The conditions are shown in Table 13, below. Quite remarkably, the total draw ratio could be adjusted much higher for the blend yarn than for the PET control.

The properties of drawn yarns are in Table 14, below. The initial modulus was higher for the blend yarn in comparison with that of the PET control. However, the shrinkage was lower.

TABLE 13__________________________________________________________________________Run No. 1 2 3 4 5 6 7__________________________________________________________________________Polymer Composition Blend* Blend Blend Blend Blend Blend PETPin temp. (.degree.C.): 58 58 66 66 66 77 75Hot plate 230 230 230 230 230 230 230temp. (.degree.C.)Draw ratiofirst stage: 4.0 4.5 3.5 4.0 4.5 5.0 4.0Total: 6.5 6.5 7.2 7.5 6.7 6.5 5.75__________________________________________________________________________ *The blend used in Run Nos. 1-5 was a 90/10 wt ratio of PET/LCP. TABLE 14__________________________________________________________________________Run No. 1 2 3 4 5 6 7__________________________________________________________________________Polymer Composition Blend* Blend Blend Blend Blend Blend PETDraw ratio 6.5 6.5 7.2 7.5 6.7 6.5 5.75Linear density 109 115 113 110 113 113 122(dtex):Tenacity (mN/tex): 647 640 621 640 620 626 680Elong. at break (%): 6.3 6.5 7.2 7.5 6.7 6.8 10.3Initial modulus (N/tex): 14.3 16.5 15.4 16.0 15.5 15.1 10.8Hot-Air shrinkage (%) at 9.0 9.1 9.1 9.2 9.3 9.3 9.2190.degree. C.:__________________________________________________________________________ *The blend used in Run Nos. 1-5 was a 90/10 wt ratio of PET/LCP.

The foregoing Examples should not be construed in a limiting sense since they are only intended to set forth certain illustrative embodiments of the present invention. The scope of protection sought is set forth in the claims which follow.

Claims

1. A blend of (1) a flexible coil polymer matrix of poly(ethylene terephthalate) and (2) a thermotropic liquid crystalline segmented block copolymer which comprises rod and flexible coil polymer blocks, the rod blocks being main chain, containing a flexible spacer, and being of the formula

--[--OArC(O)O(CH.sub.2).sub.n OC(O)ArOC(O)ArC(O)--]--.sub.x

where Ar represents phenyl with para- bond sites, n can range from 2 to 10, and x can range from about 2 to about 50, the flexible coil blocks being of poly(butylene terephthalate).

2. A blend as claimed in claim 1 wherein the amount of block copolymer in the matrix ranges from about 0.5% to about 99% by weight of the matrix.

3. A blend as claimed in claim 1 wherein the amount of block copolymer in the matrix ranges from about 1% to about 35% by weight of the matrix.

4. A blend as claimed in claim 1 where n is 4.

5. Fibers made from the blend of claim 1.

6. Fibers made from the blend of claim 2.

7. Fibers made from the blend of claim 3.

8. Fibers made from the blend of claim 4.