Patent Grant
11746193
This application is the U.S. National Phase of PCT Appln. No. PCT/CN2018/116374 filed Nov. 20, 2018, the disclosure of which is incorporated in its entirety by reference herein.
The present invention relates to the field of silicone-based softeners for textile finishing.
CN100368467C discloses a composition for fiber treatment and finishing that comprises quaternized aminoalkylpolysiloxanes, and nonionogenic interface-active compounds containing ethylene oxide and propylene oxide (EO/PO) units. According to Example 1 therein, the quaternized aminoalkylpolysiloxanes were obtained by the acid-catalyzed reaction of N,N,N′,N′-tetramethyl-1,6-hexanediamine, JEFFAMINE ED600 polyetheramine and an epoxyalkyl silicone oil.
U.S. Pat. No. 5,807,956 discloses a copolymer of (AB)nA type comprising polysiloxane and polyetheramine units, which can be used as a softener that imparts durable hydrophilicity. The polysiloxane units have the general formula [X(CaH2aO)bR2 [SiO(R1)2]c Si(R1)2 R2(OCaH2a)b X], and the polyetheramine units have the general formula [YO(CaH2aO)dY], where X is a ring opened epoxide, and Y is a secondary or tertiary amine.
The existing softener products available on the market rarely offer both a soft feel and excellent hydrophilicity.
The present invention relates to a block-modified polysiloxane. Compositions comprising the block-modified polysiloxane can be used in the field of textile finishing. Emulsions comprising the compositions have a very small and narrowly distributed particle size and superior penetration, and offer prominent softening properties and good hydrophilicity.
The present invention relates to a block-modified polysiloxane, which is a linear or cyclic polysiloxane copolymer and contains repeating structural units having the following structural formula (1) or (2):
where X is a divalent hydrocarbon radical having at least 3 carbon atoms, which contains at least one hydroxyl group and is interrupted by an oxygen atom, and the X groups in the repeating units can be the same or different;
M is a divalent hydrocarbon radical, or CaH2a, where a is a positive integer between 1 and 10, preferably between 2 and 4, and the M groups in the repeating units can be the same or different;
N stands for nitrogen;
m is a positive integer between 10 and 200, preferably between 20 and 150, more preferably between 30 and 60;
n is a positive integer, between 50 and 350, preferably between 70 and 300, more preferably between 80 and 200;
Me denotes methyl;
R1, R2, R3 and R4 can be the same or different, and are each independently an alkyl group having from 1 to 4 carbon atoms or a benzyl group or H;
R5 and R6 can be the same or different, and are each independently H, or an alkyl group having from 1 to 20 carbon atoms, which can optionally be substituted by oxygen atoms;
A− is an inorganic or organic anion.
The block-modified polysiloxane above, can contain repeating structural units having the following structural formula (3) or (4):
where Y is the structure —B-[EO]v[PO]w—,
where EO is ethylene oxide and PO is propylene oxide;
B is a linear or branched C1-C6 alkylene group, preferably a C2-C4 alkylene group;
v is a number between 0 and 200, preferably between 1 and 50, more preferably between 5 and 30;
w is a number between 0 and 200, preferably between 1 and 20, more preferably between 1 and 10;
v+w≥1, preferably v+w≥9, more preferably 20≥v+w≥10:
v/w is between 1.1 and 5, preferably between 2 and 4, more preferably between 2 and 3;
R6 and R7 can be the same or different, and are each independently H, or an alkyl group having from 1 to 20 carbon atoms;
A− is an inorganic or organic anion, preferably acetate.
In block-modified polysiloxane above, X is a ring opened epoxide selected from the group consisting of
where a can be the same or different, and is an integer between 2 and 4; b can be the same or different, and is an integer between 0 and 100; f is an integer between 2 and 6.
A composition comprising the block-modified polysiloxane above.
A composition comprising the block-modified polysiloxane above and Component (C)—aminoalkyl silicone oil.
An emulsion composition comprising the block-modified polysiloxane above and Component (C)—aminoalkyl silicone oil.
The invention further pertains to a composition containing the block-modified polysiloxane above, prepared from the reaction including raw materials:
Component (A)—epoxyalkyl silicone oil;
Component (B)—polyetheramine;
Component (C)—aminoalkyl silicone oil,
and wherein in the block-modified polysiloxane above or the compositions above, the reaction is an epoxy ring-opening reaction.
Component (A), epoxyalkyl silicone oil, of the present invention is a di-epoxyalkyl-terminated polydimethylsiloxane, preferably a di-epoxyalkyl-terminated polydimethylene having the following structural formula (5):
n is a positive integer, between 50 and 350, preferably between 70 and 300, more preferably between 80 and 200;
Me denotes methyl;
Epoxy is selected from the group consisting of
where a is an integer between 2 and 4; b can be the same or different, and is an integer between 0 and 100; f is an integer between 2 and 6.
In compositions above, the epoxy in Component (A), epoxyalkyl silicone oil, is preferably selected from the group consisting of
Component (B), polyetheramine, of the present invention is a type of substance having the structural formula NRa—B-[EO]v[PO]w—NRa, where
v is a number between 0 and 200, preferably between 1 and 50, more preferably between 5 and 30;
w is a number between 0 and 200, preferably between 1 and 20, more preferably between 1 and 10;
B is a linear or branched C2-C6 alkylene group, preferably a propylene group;
R can be the same or different, and is independently H, or an alkyl group having from 1 to 6 carbon atoms;
a can be the same or different, and is an integer between 1 and 4.
Component (C), an aminoalkyl silicone oil of the present invention, is a di-aminoalkyl-terminated polydimethylsiloxane, preferably di-3-aminopropyl-terminated polydimethylsiloxane, more preferably di-3-aminopropyl-terminated polydimethylsiloxane having the following structural formula (6):
M is a divalent hydrocarbon radical, or CaH2a, where a is a positive integer between 1 and 10, preferably between 2 and 4, and the M groups in the repeating units can be the same or different;
R1, R2, R3 and R4 can be the same or different, and are each independently an alkyl group having from 1 to 4 carbon atoms or a benzyl group or H;
m is a positive integer between 10 and 200, preferably between 20 and 150, more preferably between 30 and 60;
Me denotes methyl.
The block-modified polysiloxane above or the compositions above, have a content of the unopened epoxide groups of less than 0.05 mmol/g, preferably less than 0.03 mmol/g, more preferably 0.01 mmol/g, measured by nuclear magnetic resonance (NMR).
The block-modified polysiloxane above or the compositions above, which have an amine value of from 0.01 to 0.5 meg/g, preferably from 0.03 to 0.3 meg/g, more preferably from 0.05 to 0.2 meg/g, more preferably from 0.1 to 0.2 meg/g, measured by nuclear magnetic resonance (NMR).
The amine value denotes how many milligrams of potassium hydroxide are equivalent to the amine content of one gram of substance.
The block-modified polysiloxane above or the compositions above preferably have a solids content of from 30 to 70 wt %, more preferably from 40 to 60% wt %, most preferably from 45 to 55 wt %.
The solids content herein is measured as follows: 2 g of the sample is placed on a watch glass, dried at 105° C. for 2 hours, and then weighed.
In the compositions above, the molar ratio of the epoxide groups in Component (A), epoxyalkyl silicone oil, to the amino-functional groups in Component (B), polyetheramine, ranges from 1.01 to 2, preferably from 1.1 to 1.5.
In the compositions above, the molar ratio of the epoxide groups in Component (A), epoxyalkyl silicone oil, to the amino-functional groups in Component (C), aminoalkyl silicone oil, ranges from 1 to 5, preferably from 1.5 to 3.5.
In the compositions above, the molar ratio of the amino-functional groups in both Component (B) polyetheramine and Component (C) aminoalkyl silicone oil to the epoxide groups in Component (A), epoxyalkyl silicone oil, ranges from 1.01 to 3, preferably from 1.1 to 2, more preferably from 1.1 to 1.4.
In the compositions above, the molar ratio of the aminofunctional groups in Component (C), aminoalkyl silicone oil, to the amino functional groups in Component (B), polyetheramine, ranges from 0.2 to 0.8, preferably from 0.4 to 0.7.
In the compositions above, the weight ratio of Component (B), based on the total weight of Component (A) epoxyalkyl silicone oil, Component (B) polyetheramine, and Component (C) aminoalkyl silicone oil, ranges from 1 to 15 wt %, preferably from 1.5 to 12 wt %, more preferably from 5 to 10 wt %.
In the compositions above, the weight ratio of Component (C), based on the total weight of Component (A) epoxy alkyl silicone oil, Component (B) polyetheramine, and Component (C) aminoalkyl silicone oil, ranges from 5 to 30 wt %, preferably from 5 and 20 wt %, more preferably from 10 to 15 wt %.
The block-modified polysiloxane or the compositions above may be prepared through the following process:
Component (A), epoxyalkyl silicone oil, is first reacted with Component (B), polyetheramine, and then Component (C), aminoalkyl silicone oil, is added into the system for further reaction.
The block-modified polysiloxane or the compositions above may be prepared through the following process:
Component (A), epoxyalkyl silicone oil, is first reacted with Component (C), aminoalkyl silicone oil, and then component (B), polyetheramine, is added into the system for further reaction.
The block-modified polysiloxane or the compositions above may be prepared through the following process:
Component (A), epoxyalkyl silicone oil, Component (B), polyetheramine, and Component (C), aminoalkyl silicone oil, are simultaneously added into the system for reaction.
The invention further relates to an emulsion, which comprises the block-modified polysiloxane above and has a particle size D50 of from 10 to 100 nm, preferably from 10 to 50 nm; and a emulsion, which comprises the composition above and has a particle size D50 of from 10 to 100 nm, preferably from 10 to 50 nm, more preferably from 10 to 29 nm.
In the emulsion above the span of the particle size distribution is less or equal to 1.5, preferably less or equal to 1.35.
Analysis the particle size is by Dynamic light scattering in the present invention.
Referenced Standards: The method complied with standards ISO 13321, ISO 22412 and 21 CFR Part 11.
Equipment used in Malvern Nano ZS90 (available from Malvern Instruments Ltd.)
Determination method: At 25° C., the samples were placed in the measuring device. The span of the particle size distribution in the present invention is defined as: (D90-D10)/D50,
where D50 is defined as the value of the particle size at 50% in the cumulative distribution. For example, if D50=0.68 μm, then 50% of the particles in the sample are larger than 0.68 μm, and 50% smaller than 0.68 μm. D10 or D90 is defined as the value of the particle size at 10% or 90% in the cumulative distribution respectively. For example, if D10=0.1 μm, then 10% of the particles in the sample are smaller than 0.1 μm; if D90=1 μm, then 90% of the particles in the sample are smaller than 1 μm.
The emulsions above may further comprises nonionic surfactants of alkyl alcohol polyoxyethylene ether and/or alkyl acid polyoxyethylene ester types.
In the emulsions above, the nonionic surfactants have an HLB value of from 8 to 16, preferably from 9 to 15, more preferably from 10 to 14.
In the emulsions above, the solids content ranges from 10 to 30 wt %, preferably from 10 to 20 wt %, more preferably from 13 to 18 wt %.
The invention further pertains to the use of the block-modified polysiloxanes above in the field of textile finishing,
use of the compositions above in the field of textile finishing,
use of the emulsions above in the field of textile finishing, and.
use of the compositions above in textile softeners, fabric softeners, smoothing agents and finishing.
Textiles are made of cellulose fibers, protein fibers, synthetic fibers or a mixture thereof, and have a fabric structure.
Raw materials used in the invention are as follows:
HP80X: a hydrogen-terminated polydimethylsiloxane from Jiangxi Xinjiayi New Materials Co., Ltd., having a hydrogen content of 0.03 wt % and a molecular weight (Mw) of 6666.6 g/mol.
HYC-12: a hydrogen-terminated polydimethylsiloxane from Zhejiang Sucon Silicone Co., Ltd., having a hydrogen content of 0.016 wt % and a molecular weight (Mw) of 12500 g/mol.
HP1000: a hydrogen-terminated polydimethylsiloxane from Jiangxi Xinjiayi New Materials Co., Ltd., having a hydrogen content of 0.01 wt % and a molecular weight (Mw) of 20000 g/mol.
AGE: a commercially available allyl glycidyl ether, having a molecular weight (Mw) of 114.14 g/mol.
Pt catalyst: a chloroplatinic acid.
JEFFAMINE ED600: a polyetheramine from Huntsman, having the general formula NH2CH(CH3)CH2-[EO]v—[PO]w—NH2, where EO stands for OCH2CH2, an ethylene oxide unit, PO stands for OCH(CH3)CH2, a propylene oxide unit, v≈9 and W≈3.6.
WACKER FLUID NH 40D: an aminoalkyl silicone oil, specifically di-3-aminopropyl terminated polydimethylsiloxane from Wacker Chemicals, having a molecular weight of from 2900 to 3300 g/mol and an amine value of from 0.77 to 0.91 mmol/g.
WACKER FLUID NH 130D: an aminoalkyl silicone oil, specifically di-3-aminopropyl terminated polydimethylsiloxane from Wacker Chemicals, having a molecular weight of from 9500 to 12000 g/mol and an amine value of from 0.16 to 0.21 mmol/g.
RH-NB-8168-9: a linear multi-component copolymer block-modified silicone from Ningbo Runhe High-Tech Materials Co., Ltd., containing units that enable di-epoxyalkyl-terminated silicone oil to undergo ring-opening reaction with polyetheramine.
Emulsifier 1: an iso-tridecanol polyoxyethylene ether from Sasol, having 10 EO units and an HLB value of 13.5.
Emulsifier 2: an iso-tridecanol polyoxyethylene ether from Sasol, having 5 EO units and an HLB value of 10.5.
According to Table 1, HP80X, HYC-12 and HP1000 were reacted with AGE for a period of time under a nitrogen atmosphere at temperatures from 80 to 150° C. in the presence of the platinum catalyst. The resulting mixture was then evaporated by vacuum distillation at 135° C. to obtain epoxyalkyl silicone oil 1-3. The concentration of Pt during the reaction was 6 ppm. Epoxyalkyl silicone oil 1 or 2 or 3 is a di-epoxyallyl-terminated silicone oil.
The preparation process of the compositions according to Table 2 is as follows:
(1) the epoxyalkyl silicone oils, polyetheramine and isopropyl alcohol were reacted for 2 hours under a nitrogen atmosphere at 80° C.;
(2) an aminoalkyl silicone oil (such as WACKER FLUID NH 40D or WACKER FLUID NH 130D) was added into, and reacted for 2.5 to 5 hours with the product of step (1) at controlled temperatures from 84 to 90° C.;
(3) acetic acid was added into the product of step (2) while stirred slowly to react for a certain period of time until the pH value was adjusted to about 7;
(4) the mixture of step (3) was cooled down to obtain the block-modified polysiloxane of the invention and compositions formed thereof.
According to Table 3, the inventors of the present invention unexpectedly found that Emulsion Examples 1 and 2 led to microemulsions having a particle size of about 20 nm, while Comparative Example 2 comprising RH-NB-8168-9 only led to a regular emulsion having a particle size of about 250 nm. As shown in Table 3, the block-modified polysiloxanes of the invention have properties that are quite different from those of RH-NB-8168-9 and WACKER NH 130D as a comparison, exhibiting for example remarkably improved self-emulsification ability. With good thermal stability and long-term storage stability, the microemulsions have a small particle size, which enables easier contact with the microstructure of textiles, and thus better penetration.
Softness Finishing Process:
Textile Under Test: Polyester Flannel
Preparation of finishing liquid→impregnation for 5 min, bath ratio 1:20→spinning for 5 min (liquid entrainment rate of 250% to 300%)→oven drying (at 1050° C. for 20 min) setting (at 180° C. for 30 s)→room temperature balance→hand feel evaluation
Hand Feel Test:
According to Table 5, the inventors of the present invention unexpectedly found that Emulsion Example 1 offered a softer and silky hand, which made its softening properties prominent. Compared with Emulsion Example 1, Emulsion Comparative Example 2, which also contains units that enable the epoxyalkyl silicone oil to react with polyetheramine, failed to convey a soft and slippery hand.
Hydrophilicity Test:
According to AATCC Test Method 79-2010, Absorbency of Bleached Textiles, a drop of water is dripped with a dropper onto the surface of a horizontally spread textile from 3 cm high above the textile, and the moisturizing time is the time elapsed for the reflective surface of the waterdrop to disappear. The shorter the moisturizing time, the stronger the hydrophilicity of the textile.
The hydrophilicity is indicated by a 5-level scale, where 1 is the worst and 5 is the best. Specifically, moisturizing time (tm)<5 s scores 5; 5 s<tm<20 s scores 4; 20 s<tm<1 min scores 3; 1 min<tm<5 min scores 2; tm>5 min scores 1.
According to Table 6, the inventors of the present invention unexpectedly found that Emulsion Examples 1 and 2 did not exhibit a significant reduction in hydrophilicity, while having both good hydrophilicity and prominent soft properties, which mean an excellent overall performance profile.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2018/116374 | 11/20/2018 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2020/102966 | 5/28/2020 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4366001 | Ona | Dec 1982 | A |
| 4533714 | Sebag | Aug 1985 | A |
| 4584342 | Kondow | Apr 1986 | A |
| 5807956 | Czech | Sep 1998 | A |
| 6515094 | Czech | Feb 2003 | B2 |
| 6730766 | Schattenmann | May 2004 | B2 |
| 10052582 | Liu | Aug 2018 | B1 |
| 20030045666 | Schattenmann et al. | Mar 2003 | A1 |
| 20040225099 | Hohberg et al. | Nov 2004 | A1 |
| 20060100396 | Guth et al. | May 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 100368467 | Feb 2008 | CN |
| 103214679 | Jul 2013 | CN |
| 19817776 | Oct 1999 | DE |
| 10195202 | Jul 1998 | JP |
| 11199691 | Jul 1999 | JP |
| 11288087 | Oct 1999 | JP |
| 2000143797 | May 2000 | JP |
| 2012107127 | Jun 2012 | JP |
| 2017182061 | Oct 2017 | WO |
| 2018183057 | Oct 2018 | WO |
| Entry |
|---|
| Product data sheet for Gelest DMS-A21 (no date). |
| Product data sheet for Gelest DMS-E21 (no date). |
| Supplemental European Search Report for EP Application 18940757.0, dated Apr. 20, 2021. |
| Number | Date | Country | |
|---|---|---|---|
| 20210388163 A1 | Dec 2021 | US |