Patent Grant
11833723
The present invention relates to a blow-molded foam and a process for producing the same.
A foam blow-molding process is carried out by extruding a thermoplastic resin containing a foaming agent added thereto into an atmosphere as a parison and inserting the parison between split mold blocks (e.g., refer to Patent Document 1).
As a blow-molded foam product obtained by such a process, there has been known one that principally contains a polypropylene-based resin having predetermined physical properties (e.g., refer to Patent Document 2).
In such a blow-molded foam product, however, when being released to the atmosphere, foamed cells in the parison are abruptly expanded to make cells larger. Occasionally, there is a possibility that the cells are ruptured.
In order to overcome this disadvantage, there has been examined a process for making foamed cells finer in diameter while maintaining a high expansion ratio.
For example, there has been mentioned a foam duct molded by foam blow-molding in which a supercritical fluid is added as a foaming agent (e.g., refer to Patent Document 3).
As described in Patent Document 3, in the foam duct having the fine foamed cells, the diameters of the respective foamed cells are made smaller, but are different in size from one another. Consequently, the resulting foam duct fails to provide satisfactory smoothness on a surface thereof.
The present invention has been devised in view of the circumstances described above, and an object thereof is to provide a blow-molded foam which has homogeneous foamed cells in size, is light in weight, and is excellent in surface smoothness, and a process for producing the same.
The present inventors have eagerly conducted studies for solving the problems described above and, as a result, have found out that the following configurations are allowed to solve the problems. Thus, the present inventors have completed the present invention.
That is, the present invention relates to (1) a blow-molded foam having a wall portion formed in such a manner that a thermoplastic resin containing a foaming agent mixed therewith is subjected to blow molding, wherein the wall portion has a closed cell structure in which a plurality of foamed cells are contained, the wall portion has an expansion ratio of not less than 2.0 times, the wall portion has an outer face having a center-line average surface roughness Ra of less than 9.0 μm, and the foamed cell has a cell diameter having a standard deviation of less than 40 μm in a thickness direction of the wall portion.
The present invention also relates to (2) a blow-molded foam according to the configuration (1), wherein the thermoplastic resin is a polyolefin-based resin.
The present invention also relates to (3) a blow-molded foam according to the configuration (2), wherein the polyolefin-based resin is a propylene homopolymer having a long-chain branched structure.
The present invention also relates to (4) a blow-molded foam according to any one of the configurations (1) to (3), wherein an average cell diameter of the foamed cell in the thickness direction of the wall portion is less than 300 μm.
The present invention also relates to (5) a blow-molded foam according to any one of the configurations (1) to (3), wherein an average cell diameter of the foamed cell in the thickness direction of the wall portion is less than 100 μm, and the standard deviation of the cell diameter of the foamed cell in the thickness direction of the wall portion is less than 30 μm.
The present invention also relates to (6) a blow-molded foam according to any one of the configurations (1) to (5), which is a climate control duct for vehicles.
The present invention also relates to (7) a process for producing the blow-molded foam according to any one of the configurations (1) to (6), including: a mixing step of adding a thermoplastic resin to a foaming agent and mixing the thermoplastic resin with the foaming agent in an extruder to prepare a resin mixture; a retaining step of retaining the resin mixture at a cylinder-shaped space defined between a mandrel and a die outer cylinder; an extruding step of extruding a parison from a die slit by use of a ring-shaped piston; and a molding step of subjecting the parison to blow molding by clamping split mold blocks with the parison inserted therebetween and blowing air on the parison.
The present invention also relates to (8) a process according to the configuration (7), wherein the thermoplastic resin is a polyolefin-based resin, and the foaming agent is in a supercritical state.
The present invention also relates to (9) a process according to the configuration (7) or (8), wherein in the extruding step, the parison is extruded at an extrusion rate of not less than 700 kg/hr.
In the blow-molded foam according to the present invention, the wall portion has the closed cell structure in which the plurality of foamed cells are contained and also has the expansion ratio set within a predetermined range. Thus, it is possible to reduce the weight of the blow-molded foam. Moreover, the standard deviation of the cell diameter of the foamed cell in the thickness direction of the wall portion is set within a predetermined range. Thus, it is possible to make the foamed cells homogeneous in size. Further, the center-line average surface roughness Ra of the outer face of the wall portion is set within a predetermined range. Thus, it is possible to achieve high surface smoothness.
Therefore, for example, in a case where the blow-molded foam is used as a climate control duct for vehicles, it is possible to reduce frictional resistance against flowing air and to improve ventilation efficiency. Thus, it is possible to reduce pressure loss of climate control air and to reduce a possibility that condensed moisture adheres to an outside of a wall face of the duct.
Moreover, in a case where the blow-molded foam is used as a skinned panel, it is possible to improve a deposition strength of a reinforcing rib to be formed on an inside of a wall face of the panel and a deposition strength of a skin to be bonded to an outside of the wall face of the panel. Further, it is also possible to provide high rigidity and excellent appearance.
In the case where the thermoplastic resin is a polyolefin-based resin, the blow-molded foam is improved in impact resistance because this material is excellent in flexibility. Preferably, the polyolefin-based resin is a propylene homopolymer having a long-chain branched structure. In this case, the resin is foamed with ease, so that the resulting foamed cells are made homogeneous.
In the case where the average cell diameter of the foamed cell in the thickness direction of the wall portion is less than 300 μm, the blow-molded foam is further improved in surface smoothness. More preferably, the average cell diameter is less than 100 μm.
In the process for producing a blow-molded foam according to the present invention, the resin mixture is retained at the predetermined position. Thus, it is possible to homogenize foamed cells in size. Moreover, the resin mixture is extruded at the predetermined extrusion rate by use of the ring-shaped piston. Thus, it is possible to subject the resin mixture to blow molding with the size of the foamed cell maintained.
Accordingly, the process for producing a blow-molded foam allows production of a blow-molded foam which has homogeneous foamed cells in size, is light in weight and is excellent in surface smoothness. Moreover, the foamed cells are made finer by use of a foaming agent which is a supercritical fluid.
In the process for producing a blow-molded foam, when the extrusion rate of the parison is not less than 700 kg/hr in the extruding step, the foamed cells are further homogenized in size.
Preferred embodiments of the present invention will be described in detail below with reference to the attached drawings if necessary. In the drawings, identical reference signs designate identical components, and duplicate description is not given here. Moreover, positional relations such as a up-to-down relation and a right-to-left relation are determined based on the positional relations illustrated in the drawings, unless otherwise specified. In the respective drawings, further, dimensional ratios are not intended to be limited to ratios illustrated in the drawings.
The following description is given about a case where a blow-molded foam according to a first embodiment of the present invention is used as a climate control duct.
As illustrated in
The climate control duct 1 has a hollow structure in which a cross section is has a rectangular shape. That is, the cross section of the main body 11 has a hollow structure surrounded with the wall portion.
Therefore, the climate control duct 1 is allowed to guide climate control air to the hollow portion.
In the climate control duct 1, the main body 11 is curved smoothly, and has such a function that the climate control air that has been allowed to flow into the air inlet 13 is made to flow out from the air outlet 12 that is directed in an “L”-shaped direction relative to a direction in which the climate control air has been allowed to flow in.
For example, in a climate control duct for vehicles, the air inlet 13 is coupled to an air conditioner unit, and climate control air supplied from the air conditioner unit is allowed to flow through the hollow portion, and can be discharged from the air outlet 12 that is disposed at a desired position.
The wall portion has a closed cell structure in which a plurality of foamed cells are contained. Herein, the closed cell structure refers to a structure having a plurality of foamed cells, and means a structure in which at least a closed cell ratio is not less than 70%.
In the climate control duct 1, the wall portion has the closed cell structure, so that the climate control duct 1 is excellent in surface smoothness and outer appearance.
In particular, the climate control duct is advantageous in improving ventilation efficiency and in reducing generation of condensed moisture.
The foamed cells are preferably designed to have an average cell diameter of less than 300 μm in a thickness direction of the wall portion, more preferably, less than 100 μm. Herein, the average cell diameter refers to an average value of the maximum diameters of the respective cells in the thickness direction of the wall portion.
When the average cell diameter is not less than 300 μm, the surface roughness becomes large in comparison with a case where the average cell diameter falls within the range described above, and tends to cause degradation in surface smoothness.
In the climate control duct 1, the average wall thickness of the wall portion is preferably not more than 3.5 mm.
When the average wall thickness exceeds 3.5 mm, an air passage is narrowed in comparison with the average wall thickness that falls within the range described above, and tends to cause degradation in ventilation efficiency.
In the climate control duct 1, the outer face of the wall portion preferably has a center-line average surface roughness Ra of less than 9.0 μm, more preferably, less than 6.0 μm. Herein, the center-line average surface roughness Ra is a value measured in conformity with JIS B0601.
When the center-line average surface roughness is set to less than 9.0 μm, it is possible to provide excellent surface smoothness and outer appearance. In particular, the resulting climate control duct is advantageous in improving ventilation efficiency and in reducing generation of condensed moisture.
In the climate control duct 1, the standard deviation of cell diameter of the foamed cell in the thickness direction of the wall portion is less than 40 μm. Herein, the standard deviation of the cell diameter indicates the evenness of the foamed cell diameters, and the smaller the standard deviation, the more even foamed cell diameter is provided.
When the standard deviation of the cell diameter exceeds 40 μm, deviations in the foamed cell diameters become greater. Consequently, the surface smoothness and outer appearance tend to become deteriorated. The standard deviation of the cell diameter is more preferably less than 30 μm.
In the climate control duct 1, the expansion ratio of the wall portion is not less than 2.0 times. Herein, the expansion ratio is a value obtained by dividing the density of a thermoplastic resin used upon the foam blow-molding by the apparent density of the wall face of the blow-molded foam.
When the expansion ratio is less than 2.0 times, it is not possible to obtain a lightweight blow-molded foam.
The blow-molded foam 1 (climate control duct) according to this embodiment is obtained in such a manner that a thermoplastic resin containing a foaming agent mixed therewith is subjected to blow molding.
Examples of such a thermoplastic resin include polyolefin-based resins such as a polyethylene resin and a polypropylene resin. Since the polyolefin-based resin is excellent in flexibility, it is possible to improve impact resistance of the blow-molded foam.
Among these, the thermoplastic resin preferably has a propylene unit, and specific examples thereof include a propylene homopolymer, an ethylene-propylene block copolymer, an ethylene-propylene random copolymer, and the like.
Moreover, among these, the propylene homopolymer having a long-chain branched structure is more preferably used. In this case, the resin is foamed with ease since its melt tension becomes higher, and foamed cells are further homogenized.
The propylene homopolymer having a long-chain branched structure is preferably prepared as a propylene homopolymer having a weight-average branching index of not more than 0.9. Moreover, the weight-average branching index g′ is represented by V1/V2, and V1 represents a limiting viscosity number of a branched polyolefin, while V2 represents a limiting viscosity number of a linear polyolefin having the same weight-average molecular weight as that of the branched polyolefin.
As the thermoplastic resin, a polypropylene resin having a melt tension in a range from 30 to 350 mN at 230° C. is preferably used. Herein, the melt tension refers to a fused-state tension. When the melt tension falls within the range, the foaming polypropylene-based resin exhibits a strain hardening characteristic, and is allowed to provide a high expansion ratio.
The thermoplastic resin preferably has a melt flow rate (MFR) in a range from 1 to 10 at 230° C. Herein, the MFR is a value measured in conformity with JIS K-7210.
When the MFR is less than 1, it tends to become difficult to raise the extrusion rate in comparison with the case where the MFR falls within the range. When the MFR exceeds 10, it tends to become difficult to carry out blow molding due to occurrence of drawdown or the like in comparison with the case where the MFR falls within the range.
A styrene-based elastomer and/or a low-density polyethylene are preferably added to the thermoplastic resin. By adding the styrene-based elastomer or the low-density polyethylene to the thermoplastic resin, it is possible to improve the impact strength of the blow-molded foam at a low temperature.
Although not particularly limited, any elastomer may be used as the styrene-based elastomer, as long as it has a styrene unit with hydrogen added to its molecule. Examples thereof include hydrogenated elastomers such as a styrene-ethylene butylene-styrene block copolymer, a styrene-ethylene propylene-styrene block copolymer, and a styrene-butadiene random copolymer.
The compounding ratio of the styrene-based elastomer is preferably set within a range of less than 40 wt % with respect to the thermoplastic resin.
Moreover, the content of styrene in the styrene-based elastomer is preferably less than 30 wt %, more preferably less than 20 wt %, from the viewpoint of impact strength at a low temperature.
As the low-density polyethylene, from the viewpoint of impact strength at a low temperature, those having a density of not more than 0.91 g/cm3 are preferably used. In particular, a linear ultra-low density polyethylene, polymerized by a metallocene-based catalyst, is preferably used.
The compounding ratio of the low-density polyethylene is preferably in a range less than 40 wt % with respect to the thermoplastic resin.
The thermoplastic resin is foamed by using a foaming agent before being subjected to blow molding.
Examples of the foaming agent include inorganic foaming agents such as air, carbon dioxide gas, nitrogen gas and water, or organic foaming agents such as butane, pentane, hexane, dichloromethane and dichloroethane.
Among these, air, carbon dioxide gas or nitrogen gas is preferably used as the foaming agent. In this case, it becomes possible to prevent tangible matters from being mingled therein, and consequently to suppress degradation of durability and the like.
Moreover, as the foaming method, a supercritical fluid is preferably used. That is, carbon dioxide gas or nitrogen gas is preferably brought into a supercritical state, and allowed to foam the resin mixture. In this case, it is possible to uniformly generate cells positively.
In addition to the styrene-based elastomer, low-density polyethylene and foaming agent, a core agent, a colorant and the like may be added to the thermoplastic resin.
In the climate control duct 1 (blow-molded foam) according to this embodiment, the wall portion has the closed cell structure in which the plurality of foamed cells are contained. When the expansion ratio of the wall portion is set within the predetermined range, it is possible to provide a lightweight structure. When the standard deviation of the cell diameter of the foamed cell in the thickness direction of the wall portion is set within the predetermined range, it is possible to provide homogeneous foamed cells in size. When the center-line average surface roughness Ra on the outer face of the wall portion is set within the predetermined range, it is possible to achieve high surface smoothness.
Moreover, the climate control duct 1 has a low frictional resistance against flowing air, and the ventilation efficiency can be improved. Thus, the pressure loss of climate control air is reduced, thereby making it possible to reduce generation of condensed moisture on the outside of the wall face of the duct.
The following description is given about a process for producing the blow-molded foam according to the present invention.
As illustrated in
In the process for producing a blow-molded foam according to this embodiment, since the parison is extruded at a predetermined extrusion rate by using the ring-shaped piston, the blow molding is carried out, with the size of the foamed cells being maintained.
With this arrangement, the process for producing the blow-molded foam makes it possible to obtain a blow-molded foam which has homogeneous foamed cells in size, is light in weight, and is excellent in surface smoothness.
The following description is given about the respective steps in detail.
(Mixing Step)
The mixing step S1 is a step of adding a thermoplastic resin to a foaming agent and mixing the thermoplastic resin with the foaming agent in the extruder to prepare a resin mixture. In this case, any one of conventionally known machines may be used on demand as the extruder.
Moreover, in the process for producing the blow-molded foam according to this embodiment, the polyolefin-based resin described above is used as the thermoplastic resin, and the foaming agent is used in its supercritical state. By using the foaming agent that is a supercritical fluid, the foamed cells are made finer.
Herein, the foaming agent is preferably prepared as a carbon dioxide gas or a nitrogen gas. These gases can be made into a supercritical state under comparatively moderate conditions.
More specifically, in the case where the carbon dioxide gas is used as the supercritical fluid, the following conditions are set: the critical temperature is 31° C. and the critical pressure is not less than 7.4 MPa. In the case where the nitrogen gas is used as the supercritical fluid, the following conditions are set: the critical temperature is 149.1° C. and the critical pressure is not less than 3.4 MPa.
Moreover, by allowing the polyolefin-based resin to foam by using the supercritical fluid, a resin mixture is obtained. At this time, as described above, a styrene-based elastomer and/or a low-density polyethylene may be added to the polyolefin.
(Retaining Step)
The retaining step S2 is a step of retaining the resin mixture at a cylinder-shaped space defined between a mandrel and a die outer cylinder. The retaining step is carried out using an extrusion head.
As illustrated in
In the retaining step S2, the resin mixture extruded by an extruder (not illustrated) moves along the periphery of the mandrel 27, is dropped in the cylinder-shaped space 29 between the mandrel 27 and the die outer cylinder 28, and is retained at the cylinder-shaped space 29.
Herein, the amount of resin to be retained is preferably 5 to 40 liters.
In the process for producing a blow-molded foam according to this embodiment, since a system in which the resin mixture is retained in the cylinder-shaped space 9 is prepared, the sizes of the foamed cells are made even during the period that the resin mixture is retained.
(Extruding Step)
The extruding step S3 is a step of extruding a parison from a die slit by use of a ring-shaped piston. That is, after a predetermined amount of the resin has been retained at the cylinder-shaped space 29, the parison (not illustrated) is discharged through the die slit 21 by pressing the ring-shaped piston 22 downward.
In the process for producing a blow-molded foam according to this embodiment, since a system in which the ring-shaped piston 22 extrudes the parison in the die (an accumulator-inside-die system or an accumulator head system) is adopted, it is possible to shorten the distance of the die slit 21, and also to increase the extrusion rate. Thus, it becomes possible to maintain the state of the foamed cells.
On the other hand, a conventional extrusion head illustrated in
Herein, the extrusion rate of the parison is preferably not less than 700 kg/hr. In this case, it is possible to obtain a blow-molded foam having excellent surface smoothness. Moreover, the accumulator inside the die, which is used in the present invention, has an injection rate of not less than 200 cm3/sec, preferably, not less than 500 cm3/sec.
(Molding Step)
The molding step S4 is a step of subjecting the parison to blow molding by clamping split mold blocks with the parison inserted therebetween and blowing air on the parison.
As illustrated in
Thereafter, air is blown on the parison 32, so that the parison 32 is subjected to blow molding.
Herein, the pressure used for blowing air is preferably 0.05 to 0.15 MPa, from the viewpoint of maintaining the shape of foamed cell.
Thus, a blow-molded foam is obtained.
In the process for producing a blow-molded foam according to this embodiment, by retaining a resin mixture at a predetermined position, the foamed cells can be homogenized in size, and by extruding the resin mixture at a predetermined extrusion rate by using a ring-shaped piston, blow molding is carried out with the size of the foamed cell appropriately maintained.
With this configuration, it becomes possible to obtain a blow-molded foam which has homogeneous foamed cells in size, which is light in weight and which is excellent in surface smoothness.
The following description is given about a structure in which the blow-molded foam according to the present invention is utilized as a skinned panel as a second embodiment of the present invention.
As illustrated in
As illustrated in
Upon the clamping of the parison in the molding step, the reinforcing ribs 6 are formed by pressing the parison wall portion onto the parison side face in a manner so as to be folded down, by a slide core having a protruding shape in one direction.
Therefore, in the production of the skinned panel, in the molding step, the reinforcing ribs 6 are also formed simultaneously with the bonding of the skin material 4.
Herein, the wall portion is synonymous with the “wall portion” in the blow-molded foam according to the first embodiment, and since the structures and physical properties thereof are also the same, the description thereof will be omitted.
Moreover, the process for producing the blow-molded foam according to the second embodiment is the same as the process for producing the blow-molded foam according to the first embodiment, except for the foregoing difference in the molding step.
In the skinned panel 3 (blow-molded foam) according to this embodiment, the wall portion has a closed cell structure in which a plurality of foamed cells are formed. When the expansion ratio of the wall portion is set in a predetermined range, it is possible to provide a lightweight structure. When the standard deviation of the cell diameter of the foamed cell in the thickness direction of the wall portion is set in a predetermined range, it is possible to provide the homogeneous foamed cells in size. When the center-line average surface roughness Ra on the outer face of the wall portion is set in a predetermined range, it is possible to achieve high surface smoothness.
Moreover, it is possible to improve the deposition strength of the reinforcing ribs formed inside the wall face of the panel and the deposition strength of the skin bonded outside the wall face of the panel. Further, it is also possible to provide high rigidity and excellent outer appearance.
The following description is given about the present invention more specifically based upon examples and comparative examples; however, the present invention is not intended to be limited by the following examples.
A propylene homopolymer (thermoplastic resin: trade name: PF814, made by SunAllomer) (70 wt %) having an MFR of 3.0 g/min at 230° C., with a long-chain branched structure introduced therein, and a crystalline ethylene-propylene block copolymer (NOVATECH PP EC9, made by Japan Polychem) (30 wt %) having an MFR of 0.5 g/min at 230° C. were mixed to form a mixture, and 96 parts by weight of this mixture, 3 parts by weight of talc MB (master batch) serving as a core agent and 1 part by weight of black MB (master batch) serving as a colorant were mixed. The density of the resin mixture was 0.91 g/cm3.
To this was added carbon dioxide gas in a supercritical state as a foaming agent to be foamed so that a resin mixture was prepared. After having been mixed in an extruder, the resin mixture was retained at a cylinder-shaped space defined between a mandrel and a die outer cylinder by using an extrusion head illustrated in
The same processes as those of Example 1 were carried out except that the extrusion rate was changed to 750 kg/hr so that a sample B was obtained.
The same processes as those of Example 1 were carried out except that in place of the carbon dioxide gas, nitrogen gas was used so that a sample C was obtained.
The same processes as those of Example 1 were carried out except that in place of the carbon dioxide gas, nitrogen gas was used, and that the extrusion rate was changed to 700 kg/hr so that a sample D was obtained.
The same processes as those of Example 1 were carried out except that in place of the carbon dioxide gas, nitrogen gas was used, and that the extrusion rate was changed to 600 kg/hr so that a sample E was obtained.
The same processes as those of Example 1 were carried out except that the extrusion rate was changed to 600 kg/hr so that a sample F was obtained.
In place of the extrusion head illustrated in
Except for the above-mentioned points, the same processes as those of Example 1 were carried out so that a sample G was obtained.
The same processes as those of Comparative Example 1 were carried out except that in place of the carbon dioxide gas, nitrogen gas was used so that a sample H was obtained.
The same processes as those of Comparative Example 1 were carried out except that the extrusion rate was changed to 300 kg/hr so that a sample I was obtained.
The physical properties of the samples A to I obtained in Examples 1 to 6 and Comparative Examples 1 to 3 were evaluated as described below. In each of the samples A to I, comparatively flat portions of three points, that is, two ends and the center portion in the longitudinal direction, were cut off by a microtome (RM2145, made by LEICA), and the cut-off cross section was photographed by a CCD camera (VH-630, made by Keyence).
1. Average Thickness (mm)
In each of samples A to I, thicknesses were measured from the photographs with respect to the 3 points photographed by the CCD camera, and an average value of the respective values was calculated.
2. Expansion Ratio
The expansion ratio was calculated by dividing the density of each of resin mixtures used in the samples A to I by the apparent density of the corresponding wall faces of the samples A to I.
3. Average Cell Diameter (μm)
With respect to the 3 points photographed by the CCD camera in each of the samples A to I, the sizes of cell diameters in the thickness direction at 5 points taken with equal intervals from the outside to the inside in the thickness direction of the wall face were measured from the photograph, and an average value was calculated.
4. Center-Line Average Surface Roughness (Ra) (μm)
In conformity with JIS B0601, the center-line average surface roughness of each of the samples A to I was measured by using a surface-roughness measuring device (SURFCOM 470A, made by Tokyo Seimitsu Co., Ltd.). With respect to the measuring points of the surface roughness of a blow-molded foam, 5 points on the outside of the wall face and 5 points on the inside of the wall face of the blow-molded foam were measured, and an average value was obtained.
5. Standard Deviation of Cell Diameter (μm)
From the values of the cell diameters in the thickness direction of total 15 points measured upon calculating the average cell diameter, the standard deviation was calculated and found.
Table 1 shows the results obtained by these evaluations.
In the samples A to F of Examples 1 to 6, by using the accumulator inside the die, which had a high injection rate, a parison could be extruded in a short period of time so that it was possible to obtain a blow-molded foam with a small standard deviation of the cell diameter of foamed cells (with less deviations in the distribution of cell diameters) and high surface smoothness.
Moreover, it was found that, by using nitrogen in a supercritical state as a foaming agent, the diameter of the foamed cells could be made smaller.
In contrast, in the samples G to I of Comparative Examples 1 to 3, deviations occurred in the distribution of the cell diameters of foamed cells. This is presumably caused by the fact that, in the case where the accumulator outside the die is used, since, upon extrusion of a thermoplastic resin in a fused state stored in the cylinder, the thermoplastic resin is extruded, with its flowing direction being changed by 90 degrees at the cross-head portion, and since the distance from the cylinder placed outside the die to the die slit from which the parison is extruded becomes comparatively longer, the pressure loss of the thermoplastic resin to be extruded becomes greater.
Next, the effects of the samples A to I obtained by Examples 1 to 6 and Comparative Examples 1 to 3 were evaluated as described below:
1. Photographs
In the samples A and G obtained in Example 1 and Comparative Example 1, comparatively flat portions in the center portion in the longitudinal direction were cut off by a microtome (RM2145, made by LEICA), and the cut-off cross section was photographed by a CCD camera (VH-630, made by Keyence).
2. Peel Strength (gf)
To a test piece cut off from each of the samples A to I was adhered a non-woven fabric (hereinafter, referred to as “packing”) (thickness: 3 mm, width: 10 mm) to which double-sided tapes had been bonded, and one of the end faces of the packing was adhered and secured to the test piece, with the other end face being attached to a tensile testing machine.
Moreover, the other end face of the packing was pulled by the tensile testing machine in a manner so as to be folded over to the other end face side, and the peel strength at this time was measured. Herein, as the packing, a non-woven fabric/acryl-based adhesive material (interior member securing double-sided tape #5782, made by Sekisui Chemical Co., Ltd.) having an adhesive strength of 18.6 N/25 mm measured in conformity with JIS Z0237 (1800 peeling method) was used, and the tension rate was set to 300 mm/min.
Table 2 shows the results of the tests.
3. Outer Appearance
The outer appearance of each of the samples A to I was visually evaluated in accordance with the following criteria.
Excellent: The surface was smooth, with a uniform outer appearance.
Moderate: Although the surface was comparatively smooth, the outer appearance was inferior in uniformity.
Bad: Surface irregularities were clearly observed visually, and the outer appearance was inferior.
Table 2 shows the results of the tests.
In the samples A to F of Examples 1 to 6 of the present invention, the peel strength was excellent in comparison with those of the samples G to I of Comparative Examples 1 to 3. Thus, the blow-molded foam of the present invention was confirmed to be excellent in smoothness.
In view of these facts, it was confirmed that the present invention could provide a blow-molded foam which has homogeneous foamed cells in size, is light in weight and is excellent in surface smoothness.
In addition to a climate control duct for vehicles and a skinned panel, the blow-molded foam of the present invention is applicable to an interior material for vehicles, and the like. The blow-molded foam makes it possible to devote to weight reduction of a vehicle without causing degradation of various physical properties as plastic parts.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-093894 | Mar 2008 | JP | national |
The present application is a continuation of U.S. patent application Ser. No. 16/457,846, filed Jun. 28, 2019 which is a continuation of U.S. patent application Ser. No. 15/156,297, filed May 16, 2016 which is a continuation of U.S. patent application Ser. No. 13/950,248, filed Jul. 24, 2013, which is a continuation of U.S. patent application Ser. No. 12/935,520, filed Nov. 10, 2010, which is a national phase of PCT/JP2009/001519 filed Mar. 31, 2009, and claims priority from Japanese Application Number 2008-093894 filed Mar. 31, 2008. The disclosures of all of the above-listed prior-filed applications are hereby incorporated by reference herein in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4397797 | Nojiri et al. | Aug 1983 | A |
| 4577998 | Dorrn | Mar 1986 | A |
| 4874649 | Daubenbuchel et al. | Oct 1989 | A |
| 4931327 | Liu et al. | Jun 1990 | A |
| 5830393 | Nishikawa et al. | Nov 1998 | A |
| 5930570 | Saito et al. | Jul 1999 | A |
| 6376059 | Anderson et al. | Apr 2002 | B1 |
| 6432525 | Gokuraku et al. | Aug 2002 | B1 |
| 6706223 | Anderson et al. | Mar 2004 | B1 |
| 6749794 | Spengler | Jun 2004 | B2 |
| 6875484 | Kogure et al. | Apr 2005 | B1 |
| 7169338 | Imanari et al. | Jan 2007 | B2 |
| 7332215 | Tokura et al. | Feb 2008 | B2 |
| 8043695 | Ballard et al. | Oct 2011 | B2 |
| 8397932 | Ichikawa et al. | Mar 2013 | B2 |
| 8517059 | Onodera et al. | Aug 2013 | B2 |
| 8714401 | Ichikawa et al. | May 2014 | B2 |
| 9340091 | Onodera | May 2016 | B2 |
| 10369727 | Onodera | Aug 2019 | B2 |
| 10434691 | Onodera | Oct 2019 | B2 |
| 20020172739 | Anderson et al. | Nov 2002 | A1 |
| 20030051764 | Jungers | Mar 2003 | A1 |
| 20040074554 | Starita | Apr 2004 | A1 |
| 20070006986 | Derleth et al. | Jan 2007 | A1 |
| 20080308674 | Frantz et al. | Dec 2008 | A1 |
| 20090026198 | Ichikawa et al. | Jan 2009 | A1 |
| 20110073211 | Onodera et al. | Mar 2011 | A1 |
| 20110104414 | Onodera et al. | May 2011 | A1 |
| 20130149480 | Ichikawa et al. | Jun 2013 | A1 |
| 20130164474 | Igarashi et al. | Jun 2013 | A1 |
| 20140353273 | Koiso et al. | Dec 2014 | A1 |
| 20150044406 | Akuzawa et al. | Feb 2015 | A1 |
| 20150258718 | Onodera et al. | Sep 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 63-309434 | Dec 1998 | JP |
| 2001-527106 | Dec 2001 | JP |
| 2002-192601 | Jul 2002 | JP |
| 2003-236918 | Aug 2003 | JP |
| 2004-116959 | Apr 2004 | JP |
| 2005-241157 | Sep 2005 | JP |
| 2006-181957 | Jul 2006 | JP |
| 3745960 | Dec 2006 | JP |
| 9932544 | Jul 1999 | WO |
| Entry |
|---|
| Intemational Search Report in PCT/JP2009/001519, dated Jul. 7, 2009. 2pp. |
| Office Action in JP Application No. 2008-093894, dated Mar. 6, 2012. 6pp. |
| Office Action in JP Application No. 2008-093894, dated May 22, 2012. 4pp. |
| Number | Date | Country | |
|---|---|---|---|
| 20210276232 A1 | Sep 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16457846 | Jun 2019 | US |
| Child | 17326645 | US | |
| Parent | 15156297 | May 2016 | US |
| Child | 16457846 | US | |
| Parent | 13950248 | Jul 2013 | US |
| Child | 15156297 | US | |
| Parent | 12935520 | US | |
| Child | 13950248 | US |