Claims
- 1. A method for preparing low density cellular polyurethanes, said method comprising reacting a polyol having at least two reactive hydrogen atoms, as determined by the Zerewitinoff method, with an organic polyfunctional isocyanate in the presence of
- (a) from 0.5 to 40%, based on the weight of said polyol, of a blowing agent consisting essentially of water and from 10 to 90%, based on the total weight of said blowing agent, of methylene chloride,
- (b) a catalytically effective amount of a gel catalyst selected from the group consisting of stannous salts of monocarboxylic acids, wherein the acids contain from 1 to 20 carbon atoms, and organotin compounds of the general formula R.sub.a SnX.sub.4-a, wherein R is selected from alkyl and alkenyl radicals, each of which contain from 1 to 18 carbon atoms, cycloalkyl, aryl, alkaryl and aralkyl hydrocarbon radicals, and the foregoing radicals when inertly substituted, and X represents a monovalent radical selected from the group consisting of halogen atoms and radicals of the general formula R'COO--, R'S--, R'O-- and --SR"COOR' wherein R' is in turn selected from the same group as R and R" is an alkylene radical containing from 1 to 8 carbon atoms, and
- (c) a catalytically effective amount of a blowing catalyst composition consisting essentially of an antimony carboxylate, a potassium carboxylate and a zinc carboxylate, wherein the hydrocarbyl portions of said carboxylates contain from 1 to 20 carbon atoms and wherein each of said antimony and potassium carboxylates constitutes from 10 to 40% by weight of said catalyst composition and the zinc carboxylic constitutes the remaining 20 to 80% by weight.
- 2. A method according to claim 1 wherein said antimony, potassium, and zinc carboxylates exhibit the general formulae Sb(OOCR.sup.1).sub.3, KOOCR.sup.2, and Zn(OOCR.sup.3).sub.2, respectively, and wherein R.sup.1, R.sup.2 and R.sup.3 are individually selected from the group consisting of hydrocarbyl containing from 1 to 20 carbon atoms.
- 3. A method according to claim 2 wherein R.sup.1, R.sup.2 and R.sup.3 are alkyl.
- 4. A method according to claim 2 wherein R.sup.1, R.sup.2 and R.sup.3 are ##STR1##
- 5. A method according to claim 7 wherein said composition contains a solvent for said antimony, potassium, and zinc carboxylates, said solvent being miscible with said polyol.
- 6. A method according to claim 5 wherein said solvent is a liquid polypropylene glycol.
BACKGROUND OF THE INVENTION
This application is a continuation-in-part of Application Ser. No. 879,633, filed on Feb. 21, 1978 & now U.S. Pat. No. 4,173,691 issued Nov. 6, 1979.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3620985 |
Larkin et al. |
Nov 1971 |
|
3940517 |
De Leon |
Feb 1976 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
879633 |
Feb 1978 |
|