The present disclosure relates to a blown bottle, an ink cartridge, and a method for manufacturing a blown bottle.
Injection blow molding such as discussed in Japanese Patent Application Laid-Open No. 2017-113933 has been known as a kind of molding method. In injection blow molding, a test tube-shaped preform is first molded. The preform is then molded into a desired shape by blowing air into the heated preform, and pressing the inflated preform against the inner surface of a mold.
According to an aspect of the present disclosure, a blown bottle includes at least two layers including an inner layer and an outer layer, wherein the inner layer includes an inner layer flange, and the outer layer includes an outer layer flange, and wherein a protrusion is formed on either one of the inner layer flange or the outer layer flange, a recess is formed in the other, and the protrusion is fitted to the recess.
Further features of the present disclosure will become apparent from the following description of exemplary embodiments with reference to the attached drawings.
In injection blow molding, a heated preform is molded into a desired shape by longitudinally stretching the heated preform with a stretch rod and then laterally stretching and inflating the preform with pressurized air. According to a study made by the present inventors, if a material having a low heat resistance or low crystallinity is subjected to injection blow molding, deformation may occur in the molded article (post-molding shrinkage) due to stress relaxation of strain caused by the stretching, and the article may fail to provide a needed shape. In particular, if a two-layer preform is subjected to blow molding and a welding rib is arranged on a portion that deforms, welding is unable to be performed as designed. This can result in weak welding or occurrence of leakage from that portion.
The present disclosure is directed to suppressing the occurrence of deformation due to post-molding shrinkage after injection blow molding of a two-layer preform.
A blown bottle according to an exemplary embodiment of the present disclosure will be concretely described by using an ink cartridge that is an example of the blown bottle. The blown bottle according to the present exemplary embodiment is not limited to an ink cartridge. For example, the blown bottle according to the present exemplary embodiment can be used as a food or drink container or a medicine container.
The interior of the casing 9 serves as an ink holding portion for holding ink, and ink is injected into the interior of the casing 9. After the injection of the ink, the joint member 1 is joined to the casing 9, and the air in the casing 9 is bled through an air bleed port 14 of the joint member 1. The air bleed port 14 is then sealed with a film. The air check valve 7 here closes off the joint member 1 from the casing 9 so that air will not flow back into the casing 9 between the air bleeding process and the film welding process.
A protrusion is provided on the joint member 1, and an electrode portion 3 is provided on the protrusion. The electrode portion 3 is intended to make contact with connector pins of the recording apparatus. The cover member 2 is attached to cover the joint member 1. The cover member 2 has functions such as protecting the joint member 1, or the electrode portion 3 in particular, and serving as an insertion guide in attaching the ink cartridge 13.
The casing 9 is a portion molded by injection blowing. The casing 9 includes two layers, an outer layer 10 and an inner layer 11. The outer layer 10 is an outside layer illustrated in solid lines in
In supplying the ink from the ink cartridge 13 to the recording apparatus, the ink reception pipe provided on the recording apparatus is initially inserted into the insert portion 4, and the interior of the joint member 1 is depressurized. The air check valve 7 is opened by the depressurization. The ink in the casing 9 then moves into the joint member 1 via the ink channel member 8, and is supplied to the recording apparatus via the ink reception pipe.
The ink channel member 8 includes two channels so that ink accumulating vertically below and ink located vertically above in the casing 9 can be supplied at predetermined densities. Examples of material forming the ink channel member 8 include PE and PP.
As the ink is supplied and the amount of ink held inside the inner layer 11 decreases, the inner layer 11 deforms depending on the decreased volume of the ink. The inner layer 11 collapses when the held ink is finally used up.
An air communication port 12 is formed in the outer layer 10. Air is let into between the outer layer 10 and the inner layer 11 through the air communication port 12, so that the inner layer 11 can collapse as the ink is supplied. The outer layer 10 includes an outer layer flange as its flange. The inner layer 11 includes an inner layer flange as its flange. The inner layer flange and the joint member 1 are joined by thermal welding, whereby a closed space is formed. The inner layer flange and the outer layer flange will be described in detail below.
In view of making full use of the ink, the inner layer 11 can be made of soft material. In view of flexibility, examples of the material forming the inner layer 11 can include polyolefin resins, olefin-based thermally plastic elastomers, and styrene-based thermally plastic elastomers. The inner layer 11 can be made of at least one of such materials. If the inner layer 11 and the outer layer 10 are simultaneously molded by injection blow molding, the formation material of the inner layer 11 can be one having a similar temperature range suitable for air blowing to that of the formation material of the outer layer 10. Specifically, at least either PE or PP can be used. In view of flexibility and injection blowability, linear low density polyethylene (LLDPE) in particular can be suitably used among PEs. The bending modulus of the inner layer 11 can be 1000 MPa or less, desirably 300 MPa or less.
The outer layer 10 is an outside member of the ink cartridge 13 and functions as an exterior member. The outer layer 10 can therefore have a rigidity higher than that of the inner layer 11, and can be made of material having a high rigidity. The material forming the outer layer 10 can also have high injection blowability. Specifically, a PE resin selected from a group including polyethylene terephthalate (PET), polyethylene naphthalate, or polybutylene terephthalate can be used. PET can be suitably used in particular. PET characteristically increases sharply in viscosity when stretched by air blowing. Stretched thin portions then become less stretchable while unstretched thick portions are stretchable. As a result, the entire article can be stretched to have a uniform thickness.
Next, a method for manufacturing the casing 9, which is a blown bottle, of the ink cartridge 13 will be described. The casing 9 of the ink cartridge 13 is manufactured by injection blow molding two layers of preforms including one for the outer layer 10 and one for the inner layer 11.
As illustrated in
After the preform 15 formed in two layers is prepared, the preform 15 is set on a blow carrier. The blown portion 25 of the preform 15 is then heated by heaters so that both the blown portions of the inner layer preform 16 and the outer layer preform 17 reach or exceed their glass transition temperature. The interior of the preform 15 is then stretched (elongated) in a stretching direction 26 by using a stretch rod inserted into a mold. At the same time, about 30 atmospheres of air is blown into the preform 15 to mold the preform 15 into a desired blown bottle (casing) shape.
In view of blow molding, the blown bottle (casing) can have a circular columnar (cylindrical) shape. The inner layer preform 16 and the outer layer preform 17 may be separately molded by injection blow molding and stacked afterward. Simultaneous injection blow molding can reduce the number of steps and can form a blown bottle having high volumetric efficiency.
In view of a size stretchable from a two-layer preform, the height of the blown bottle (casing) can be 40 mm or more and 350 mm or less. From a similar point of view, the width (maximum outer diameter) of the blown portion of the blown bottle can be 10 mm or more and 130 mm or less. The height of a blown bottle refers to the length of the blown bottle in the stretching direction 26 of the preform. The width of a blown bottle refers to the length of the blown bottle in a direction orthogonal to the stretching direction 26 of the preform.
The thickness of the blown portion of the blown bottle (casing) can be determined from the size of the two-layer preform 15 and that of the blow-molded container. In particular, if the two-layer blown bottle includes the outer layer 10 and the inner layer 11 that are separated, the outer layer 10 and the inner layer 11 can each have a thickness of 0.05 mm or more and 3.00 mm or less. If the outer layer 10 and the inner layer 11 are simultaneously molded by injection blow molding, the outer layer 10 can desirably have a thickness of 0.30 mm or more and 2.00 mm or less in view of strength. Similarly, if the outer layer 10 and the inner layer 11 are simultaneously molded by injection blow molding, the inner layer 11 can desirably have a thickness of 0.05 mm or more and 0.20 mm or less in view of flexibility.
Next, the flanges provided on the casing 9 of the ink cartridge 13 will be described.
Injection blow molding is a molding method for molding a desired shape by longitudinally stretching a heated preform with a stretch rod and then laterally stretching and inflating the preform with pressurized air. If a material having a low heat resistance or low crystallinity is subjected to injection blow molding, deformation can occur due to post-molding shrinkage from stress relaxation and a needed shape can fail to be achieved. Now, a deformation that can occur in injection blow molding of a two-layer preform due to post-molding shrinkage will be described.
Post-molding shrinkage can be suppressed by using materials having a high heat resistance and high crystallinity. However, such materials are not suitable as materials for forming the inner layer of an ink cartridge. Moreover, injection blowing involves longitudinal stretching and is thus susceptible to shrinkage, compared to direct blowing.
In the present exemplary embodiment, a protrusion is formed on either one of the inner layer flange 20 and the outer layer flange 18, and a recess is formed in the other. The protrusion is fitted to the recess, whereby the flange deformation is suppressed. A configuration illustrated in
In injection blowing, stretching and air blowing are often performed with the flange of a preform fixed by a jig. In such a case, the flange needs to have strength not to cause deformation from a stress during stretching or during air blowing. The thickness of the outer layer flange 18 (the length of the portion denoted by W1 in
Next, the depth of the recess 28 will be described. As illustrated in
As described above, the outer layer flange 18 can be provided with either the recess 28 or the protrusion 29. To prevent formation of a thin portion in the flanges, the recess 28 can be formed if the length obtained by subtracting the thickness W2 of the inner layer flange 20 from the thickness W1 of the outer layer flange 18 is greater than the thickness W2 of the inner layer flange 20. The protrusion 29 can be formed if the length is smaller than the thickness W2 of the inner layer flange 20.
Since the recess 28 and the protrusion 29 play the role of a wall against deformation of the inner layer flange 20, the recess 28 and the protrusion 29 can be formed at right angles to the direction of deformation as much as possible. Specifically, the inner walls of the recess 28 and the outer walls of the protrusion 29 can be extended at angles of 80°-100° with respect to the horizontal direction of
The present exemplary embodiment will be described in more detail below by using examples.
A configuration of example 1 will be described with reference to
In example 1, LLDPE was used as the material for forming the inner layer 11, and PET was used as the material for forming the outer layer 10. A two-layer preform 15 including a stack of two such layers was initially formed. The two-layer preform 15 was formed so that the inner layer preform 16 to be the inner layer 11 had a thickness of 1.0 mm and the outer layer preform 17 to be the outer layer 10 had a thickness of 2.8 mm. The height of the outer layer preform 17 was 90.0 mm.
Since the flanges 18 and 20 are provided on the unblown portions, the flanges 18 and 20 do not change in size whether in the preform 15 state or in the casing 9 state after being molded into a blown bottle. The thicknesses of the flanges 18 and 20 of the preform 15 will be described with reference to the enlarged view of the flanges 18 and 20 of the casing 9 in
Using such a two-layer preform 15, injection blow molding was performed in an injection blow molding machine (FRB-1, manufactured by Frontier, Inc.). For the injection blow molding, the two-layer preform 15 was initially rotated and heated from outside by using halogen heaters. Specifically, six heaters were arranged at positions 20 mm from the surface of the outer layer preform 17 at pitches of 15 mm, and the preform 15 was heated for 50 seconds. The output values of the halogen heaters were adjusted so that the temperature of the outer layer preform 17 after the heating process was controlled to be 70° C. or more and 160° C. or less. The molding temperature was checked by measuring the temperature of the two-layer preform 15 immediately after the heating (i.e., the temperature of the outer layer preform 17 immediately before injection blowing) with a noncontact temperature sensor.
The heated preform 15 was inserted into a mold, and then the mold was closed and the interior of the preform 15 was axially stretched by a stretch rod. At the same time, 30 atmospheres of air was blown in to mold the entire article into a bottle shape. In such a manner, the casing 9, which was a blown bottle, of the ink cartridge 13 was formed. A recess and a protrusion that fits thereto were formed in/on the flanges 18 and 20. Both the recess and the protrusion were extended along the height direction of the casing 9, and formed an angle of 90° with respect to the extending direction of the outer layer flange 18 and the inner layer flange 20.
The molded casing 9 had a diameter of 57.0 mm and a height of 200.0 mm. An average thickness of the outer layer 10 in the blown portion after blow molding (measured at 10 arbitrary distributed points) was 0.5 mm. An average thickness of the inner layer 11 in the blown portion (measured at 10 arbitrary distributed points) was 0.1 mm.
The molded casing 9 of the ink cartridge 13 was visually observed to check the state of the inner layer flange 20. No deformation was observed in the inner layer flange 20, and a favorable casing was obtained.
A configuration of example 2 will be described with reference to
In example 2, the recess 28 in the outer layer flange 18 was arranged at a position shifted from the welding rib 19 formed on the inner layer flange 20 with respect to the height direction of the casing 9 (stretching direction of the preform 15) (at a position such that the centers of the recess 28 and the welding rib 19 does not overlap even if extended in the height direction of the casing 9). In other respects, the casing 9 of the ink cartridge 13 was molded in a similar manner to example 1.
The molded casing 9 of the ink cartridge 13 was visually observed to check the state of the inner layer flange 20. No deformation was observed in the inner layer flange 20, and a favorable casing was obtained. Fewer sink marks were observed on the welding rib 19 than in example 1.
A configuration of example 3 will be described with reference to
In example 3, the protrusion 29 was formed on the outer layer flange 18 instead of the recess 28. A recess to which the protrusion 29 is fitted was formed in the inner layer flange 20. In other respects, the casing 9 of the ink cartridge 13 was molded in a similar manner to example 2.
The molded casing 9 of the ink cartridge 13 was visually observed to check the state of the inner layer flange 20. No deformation was observed in the inner layer flange 20, and a favorable casing was obtained.
A configuration of example 4 will be described with reference to
As illustrated in
The molded casing 9 of the ink cartridge 13 was visually observed to check the state of the inner layer flange 20. No deformation was observed in the inner layer flange 20, and a favorable casing was obtained.
In example 4, the partial segmentation of the recess 28 provided walls 35 for stopping movement in a rotational direction about the stretching direction 26 of the preform 15. Movement of the outer layer flange 18 in the rotational direction can thus also be restricted.
A configuration of example 5 will be described with reference to
The molded casing 9 of the ink cartridge 13 was visually observed to check the state of the inner layer flange 20. No deformation was observed in the inner layer flange 20, and a favorable casing was obtained.
According to the configuration of example 5, surfaces parallel to the height direction of the casing 9 (stretching direction) can be formed without forming a difference in level in the height direction (stretching direction) by a protrusion or a recess. Deformation of the inner layer flange 20 can thus be suppressed. Such a configuration is effective if sufficient thicknesses are difficult to provide in the height direction of the flanges 18 and 20.
A configuration of a comparative example will be described with reference to
In the comparative example, neither the recess 28 nor a protrusion that fits thereto was formed. In other respects, the casing 9 of the ink cartridge 13 was molded in a similar manner to example 1.
The molded casing 9 of the ink cartridge 13 was visually observed to check the state of the inner layer flange 20. The inner layer flange 20 was found to be deformed and separated from the outer layer flange 18.
While the present disclosure has been described with reference to exemplary embodiments, it is to be understood that the disclosure is not limited to the disclosed exemplary embodiments. The scope of the following claims is to be accorded the broadest interpretation so as to encompass all such modifications and equivalent structures and functions.
This application claims the benefit of Japanese Patent Application No. 2018-008171, filed Jan. 22, 2018, which is hereby incorporated by reference herein in its entirety.