Blue fluorescent material and display panel

Information

  • Patent Grant
  • 11437581
  • Patent Number
    11,437,581
  • Date Filed
    Wednesday, September 25, 2019
    5 years ago
  • Date Issued
    Tuesday, September 6, 2022
    2 years ago
Abstract
The present application provides a blue fluorescent material and an OLED display panel, wherein the blue fluorescent material is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane; wherein the tert-butyl pyrene increases an external quantum efficiency of the OLED display panel, and the tetrahedral structure increases distance between activated particles and reduces a concentration quenching. The charge carrier transport unit improves a balance of the carrier transfer and alleviates a problem that the current OLED display panel has a low luminous efficiency of the blue light material.
Description
FIELD OF INVENTION

The present application relates to the field of display, and in particular to a blue fluorescent material and a display panel.


BACKGROUND OF INVENTION

Organic light-emitting diodes (OLEDs) have attracted much attention in academia and industry due to their high contrast ratio, wide viewing angles, low voltage, lightweight, self-illumination, and flexible display panels.


In order to achieve full-color OLED display and high electroluminescence efficiency, excellent color purity and long-life blue light, green light, and red light materials are essential. At present, green light and red light materials have met the requirements of the industry, while blue light materials are far less than the requirements of the industry in regard to efficiency and longevity. Therefore, current OLED display panels have a problem that the luminous efficiency of the blue light material is low, and needs to be solved.


TECHNICAL PROBLEM

The present application provides a blue fluorescent material and a display panel to alleviate the problem that the blue light material in the current OLED display panel has low luminous efficiency.


SUMMARY OF INVENTION

To solve the above problem, the present application provides a blue fluorescent material, wherein the blue fluorescent material is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane.


In the present application, the blue fluorescent material has a structural formula of:




embedded image


In the blue fluorescent material provided by the present application, X1, X2 and X3 of the structural formula are the same ligand.


In the blue fluorescent material provided by the present application, the X1, the X2, and the X3 each are one of




embedded image


embedded image


In the blue fluorescent material provided by the present application, at least two of X1, X2, and X3 of the structural formula are different ligands.


In the blue fluorescent material provided by the present application, the X1 and the X2 are the same ligand, and the X1 and the X3 are different ligands.


In the blue fluorescent material provided by the present application, the X2 and the X3 are the same ligand, and the X1 and the X2 are different ligands.


In the blue fluorescent material provided by the present application, the X1, the X2, and the X3 each are one of hydrogen,




embedded image


embedded image


In the blue fluorescent material provided by the present application, the X1, the X2 and the X3 are different ligands.


In the blue fluorescent material provided by the present application, the X1, the X2, and the X3 each are one of hydrogen,




embedded image


embedded image


In the blue fluorescent material provided by the present application, a R group of any one of:




embedded image


embedded image



is a C1-C22 alkyl group, or a C1-C22 alkoxy group, or a C1-C22 heteroalkyl group, respectively.


In the blue fluorescent material provided by the present application, a structure of the blue fluorescent material includes:




embedded image


embedded image


The application also provides a method for preparing a blue fluorescent material, including preparing a precursor and reacting the precursor with a predetermined charge carrier transport unit to obtain a target blue fluorescent molecule.


In the preparation method of the blue fluorescent material provided by the present application, the specific steps of preparing the precursor include: dissolving




embedded image



in 100 ml of dehydrogenated and deoxygenated tetrahydrofuran in a single-necked flask to obtain a solution; taking out a small amount of the solution and transferring the solution to a 250 ml of a three-necked flask, adding magnesium (4.4 mmol, 0.11 g) and iodine thereto to obtain a mixed solution and stirring the mixed solution until the mixed solution fades; pouring a remaining portion of the solution into the three-necked flask and stirring the mixed solution for 2 hours to obtain a Grignard reagent; introducing the Grignard reagent into a one-necked flask containing




embedded image



and cyclohexanone (4.4 mmol, 0.43 g) to react for 5 hours to obtain a reaction solution; quenching the reaction solution by adding a little amount of water thereto, then pouring the reaction solution into 100 ml of water, extracting the reaction solution mixed with water with dichloromethane for three times to obtain an organic phase solution, combining the organic phase solution, and then drying, filtering, and vacuum drying the organic phase solution; and separating and purifying the organic phase solution by column chromatography method to obtain




embedded image



of a pale-yellow precursor powder.


In the preparation method of the blue fluorescent material provided by the present application, the steps of reacting the precursor with the predetermined charge carrier transport unit to obtain the target blue fluorescent molecule includes: taking the precursor (2.2 mmol, 0.78 g), the predetermined charge carrier transport unit (2.0 mmol) and 100 ml of dichloromethane to 250 ml of a two-necked flask, drop wise adding BF3.Et2O solution (2.2 mmol, 0.3 ml ) into the two-necked flask under Ar2, and stirring for 24 hours to obtain a reaction solution; quenching the reaction solution by adding a little amount of water thereto, then pouring the reaction solution into 100 ml of water, extracting the reaction solution mixed with water with dichloromethane for three times to obtain organic phase solution, combining the organic phase solution, and then drying, filtering, and vacuum drying the organic phase solution; and separating and purifying the organic phase solution by column chromatography method to obtain a target blue fluorescent molecule.


The application also provides an organic light-emitting diode (OLED) display panel, including: a substrate; and a pixel electrode layer, a hole transport layer, a hole injection layer, a luminescent material layer, an electron injection layer, an electron transport layer, and a common electrode layer sequentially disposed on the substrate; wherein the luminescent material layer includes a red light material layer, a green light material layer, and a blue light material layer; the blue light material layer is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane.


In the OLED display panel provided by the present application, the blue fluorescent material has a structural formula of:




embedded image


In the OLED display panel provided by the present application, X1, X2 and X3 of the structural formula are the same ligand.


In the OLED display panel provided by the present application, at least two of X1, X2, and X3 of the structural formula are different ligands.


BENEFICIAL EFFECT

The present application provides a blue fluorescent material and an OLED display panel, wherein the blue fluorescent material is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane; wherein the tert-butyl pyrene increases an external quantum efficiency of the OLED display, and the tetrahedral structure increases distance between activated particles and reduces a risk of concentration quenching and greatly increases membrane fluorescence quantum efficiency. In addition, the transport unit with high charge carrier mobility can improve a balance of the charge carrier transport, increase a probability of recombination, further improve an external quantum efficiency of an OLED display device, and alleviate the problem of low luminous efficiency of current OLED display panel.





DESCRIPTION OF DRAWINGS

In order to more clearly illustrate the technical solutions in the embodiments of the present invention, the following figures described in the embodiments will be briefly introduced. It is obvious that the drawings described below are merely some embodiments of the present invention, other drawings can also be obtained by the person ordinary skilled in the field based on these drawings without doing any creative activity.



FIG. 1 is a flowchart of preparing a blue fluorescent material according to an embodiment of the present application.



FIG. 2 is a schematic structural diagram of an OLED display panel according to an embodiment of the present disclosure.





EMBODIMENTS

The following description of the embodiments is provided to illustrate the specific embodiments of the invention. Directional terminology mentioned in the application, such as “above”, “under”, “front”, “back”, “left”, “right”, “inside”, “outside”, “side”, etc., are only refer to the directions of the accompanying drawings. Therefore, the directional terminology used is for illustrating and understanding the application and is not intended to limit the application. In the figures, structurally similar elements are denoted by the same reference numerals.


OLED display device utilizes electroluminescence of electrons and holes in a luminescent material layer to display so that materials of the luminescent material layer play a critical role in the display of OLED display device, and high luminous efficiency is an important prerequisite for a practical application of such materials. One of the most effective ways to increase luminous efficiency is to increase a doping concentration of activated ions. The pyrene blue light molecule with a rigid planar structure can achieve external quantum efficiency of 11% through triplet-triplet fusion (traditional singlet blue fluorescent material does not exceed 5%). However, its tight π-π stacking causes a concentration quenching effect, that is, a large amount of non-radiation relaxation and reverse energy transmission, resulting in a significant decrease in luminous intensity and efficiency.


In view of a problem that the blue light material of the current OLED display panel has low luminous efficiency, the present application provides a blue fluorescent material to alleviate the problem.


In one embodiment, the present application provides a blue fluorescent material, which is a tetrahedral structure having a structural formula of




embedded image


The embodiment of the present application provides a blue fluorescent material, which is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane, the tert-butyl pyrene increases an external quantum efficiency of the OLED display panel. The tetrahedral structure increases distance between activated particles and reduces the concentration quenching. In addition, the transport unit with high charge carrier mobility improves a balance of the charge carrier transport, increases a probability of recombination, further improves an external quantum efficiency of an OLED display device, and alleviates a problem of low luminous efficiency of the current OLED display panel.


Different ligands will produce blue fluorescent materials with different structures. Different charge carrier transport unit that shares a carbon with tert-butyl pyrene and a different number of the charge carrier transport units will obtain different blue fluorescent materials. Specific structural formulas of the blue fluorescent material will be described in detail below by the embodiments.


In one embodiment, X1, X2 and X3 is the same ligand selected from:




embedded image


embedded image


embedded image


In another embodiment, X1 and X2 are the same ligands, and the X1 and the X3 are different ligands; or the X2 and the X3 are the same ligand, and the X1 and the X2 are different ligands, they are selected from: hydrogen,




embedded image


embedded image


embedded image


In another embodiment, the X1, the X2, and the X3 are different ligands, they are selected from: hydrogen,




embedded image


embedded image


In the above embodiments, a R group of any one of




embedded image


embedded image



is a C1-C22 alkyl group, or a C1-C22 alkoxy group, or a C1-C22 heteroalkyl group, respectively.


Specific structures of




embedded image



include:




embedded image


One embodiment of the present application provides a method for preparing a blue fluorescent material, the specific steps are shown in FIG. 1, including: S1, preparing a precursor; and S2, reacting the precursor with a predetermined charge carrier transport unit to obtain a target blue fluorescent molecule.


An embodiment of the present application provides a method for preparing a blue fluorescent material, the blue fluorescent material of a tetrahedral structure is formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane; wherein the tert-butyl pyrene can achieve relatively high external quantum efficiency. Moreover, the tetrahedral structure increases distance between activated particles, reduces a risk of concentration quenching and greatly increases membrane fluorescence quantum efficiency. In addition, the transport unit with high charge carrier mobility improves a balance of the charge carrier transport, increases a probability of recombination, further improves an external quantum efficiency of an OLED display device, and alleviates a problem of low luminous efficiency of the current OLED display panel.


In one embodiment, the specific steps of preparing the precursor of S1 include: dissolving




embedded image



in 100 ml of dehydrogenated and deoxygenated tetrahydrofuran in a single-necked flask to obtain a solution; taking out a small amount of the solution and transferring the solution to a 250 ml three-necked flask, adding magnesium (4.4 mmol, 0.11 g) and iodine thereto to obtain a mixed solution and stirring the mixed solution until a color of the mixed solution fades; pouring a remaining portion of the solution into the three-necked flask and stirring the mixed solution for 2 hours to obtain a Grignard reagent; introducing the Grignard reagent into a one-necked flask containing




embedded image



and cyclohexanone (4.4 mmol, 0.43 g) to react for 5 hours to obtain a reaction solution; quenching the reaction solution by adding a little amount of water thereto, then pouring the reaction solution into 100 ml of water, extracting the reaction solution mixed with water with dichloromethane for three times to obtain an organic phase solution, combining the organic phase solution, and then drying, filtering, and vacuum drying the organic phase solution; and separating and purifying the organic phase solution by column chromatography method to obtain




embedded image



of a pale-yellow precursor powder.


In the embodiment, the synthetic route of the precursor




embedded image



is:




embedded image


In one embodiment, a target structure of the blue fluorescent material is




embedded image



the specific steps S2 of reacting the precursor with the charge carrier transport unit include: taking




embedded image



and 100 ml of dichloromethane to a 250 ml two-necked flask, adding BF3.Et2O (2.2 mmol, 0.3 ml) dropwise thereto under an Ar2 atmosphere and stirring for 24 hours.


Quenching the reaction solution by adding a little amount of water, then pouring the reaction solution into a water of 100 ml, extracting for three times with dichloromethane, and performing processes of organic phases combining, drying, filtering, and vacuum drying.


Performing isolation and purification by column chromatography to obtain a white powder




embedded image



10.87 g, yield 71%.


In the embodiment, the synthetic route of




embedded image



is:




embedded image


In one embodiment, the target structure of the blue fluorescent material is




embedded image



the specific steps S2 of reacting the precursor with the charge carrier transport unit include: taking




embedded image



and 100 ml of dichloromethane to a two-necked flask of 250 ml, adding BF3.Et2O (2.2 mmol, 0.3 ml) dropwise thereto under an Ar2 atmosphere and stirring for 24 hours.


Quenching the reaction solution by adding a little amount of water, then pouring the reaction solution into a water of 100 ml, extracting for three times with dichloromethane, and performing processes of organic phases combining, drying, filtering, and vacuum drying.


Performing isolation and purification by column chromatography to obtain a white powder




embedded image



20.91 g, yield 75%.


In the embodiment, the synthetic route of




embedded image



is:




embedded image


In one embodiment, the target structure of the blue fluorescent material is




embedded image



the specific steps S2 of reacting the precursor with the charge carrier transport unit include: taking




embedded image



and 100 ml of dichloromethane to a 250 ml two-necked flask, adding BF3.Et2O (2.2 mmol, 0.3 ml) dropwise thereto under an Ar2 atmosphere and stirring for 24 hours.


Quenching the reaction solution by adding a little amount of water, then pouring the reaction solution into a water of 100 ml, extracting for three times with dichloromethane, and performing processes of organic phases combining, drying, filtering, and vacuum drying.


Performing isolation and purification by column chromatography to obtain a white powder




embedded image



31 g, yield 78%.


In the embodiment, the synthetic route of




embedded image



is:




embedded image


In one embodiment, the target structure of the blue fluorescent material is




embedded image



the specific steps S2 of reacting the precursor with the charge carrier transport unit include: taking




embedded image



and 100 ml of dichloromethane to a 250 ml two-necked flask, adding BF3.Et2O (2.2 mmol, 0.3 ml) dropwise thereto under an Ar2 atmosphere and stirring for 24 hours.


Quenching the reaction solution by adding a little amount of water, then pouring the reaction solution into a water of 100 ml, extracting for three times with dichloromethane, and performing processes of organic phases combining, drying, filtering, and vacuum drying.


Performing isolation and purification by column chromatography to obtain a white powder




embedded image



40.89 g, yield 75%.


In the embodiment, the synthetic route of




embedded image



is:




embedded image


In one embodiment, the target structure of the blue fluorescent material is




embedded image



the specific steps S2 of reacting the precursor with the charge carrier transport unit include: taking




embedded image



and 100 ml of dichloromethane to a 250 ml two-necked flask, adding BF3.Et2O (2.2 mmol, 0.3 ml) dropwise thereto under an Ar2 atmosphere and stirring for 24 hours.


Quenching the reaction solution by adding a little amount of water, then pouring the reaction solution into a water of 100 ml, extracting for three times with dichloromethane, and performing processes of organic phases combining, drying, filtering, and vacuum drying.


Performing isolation and purification by column chromatography to obtain a white powder




embedded image



50.79 g, yield 63%.


In the embodiment, the synthetic route of




embedded image



is:




embedded image


In one embodiment, the target structure of the blue fluorescent material is




embedded image



the specific steps S2 of reacting the precursor with the charge carrier transport unit include: taking




embedded image



and 100 ml of dichloromethane to a two-necked flask of 250 ml, adding BF3.Et2O (2.2 mmol, 0.3 ml) dropwise thereto under an Ar2 atmosphere and stirring for 24 hours.


Quenching the reaction solution by adding a little amount of water, then pouring the reaction solution into a water of 100 ml, extracting for three times with dichloromethane, and performing processes of organic phases combining, drying, filtering, and vacuum drying.


Performing isolation and purification by column chromatography to obtain a white powder




embedded image



60.79 g, yield 65%.


In the embodiment, the synthetic route of




embedded image



is:




embedded image


In one embodiment, the target structure of the blue fluorescent material is




embedded image



the specific steps S2 of reacting the precursor with the charge carrier transport unit include: taking




embedded image



and 100 ml of dichloromethane to a two-necked flask of 250 ml, adding BF3.Et2O (2.2 mmol, 0.3 ml) dropwise thereto under an Ar2 atmosphere and stirring for 24 hours.


Quenching the reaction solution by adding a little amount of water, then pouring the reaction solution into a water of 100 ml, extracting for three times with dichloromethane, and performing processes of organic phases combining, drying, filtering, and vacuum drying.


Performing isolation and purification by column chromatography to obtain a white powder




embedded image



70.87 g, yield 65%.


In the embodiment, the synthetic route of




embedded image



is:




embedded image


The present application further provides an OLED display panel. In one embodiment, as shown in FIG. 2, the display panel 1 includes:


A substrate 10, in an embodiment of the present application, the substrate 10 is a TFT substrate, including a base substrate 101, a semiconductor active layer 102, a gate insulating layer 103, a gate layer 104, an interlayer insulating layer 105, a source/drain layer 106, and a passivation layer 107 which are stacked from bottom to top;


A pixel electrode layer 20 formed on the substrate 10, and is one selected from a group consisting of indium tin oxide (ITO), indium gallium zinc oxide (IGZO), zinc oxide (ZnO), tin oxide (SnO), indium zinc oxide (IZO), gallium zinc oxide (GaZnO), and zinc tin oxide (ZTO);


A pixel defining layer 30 formed on the first electrode layer 20 for defining a light emitting region;


A light-emitting function layer 40 formed in a light-emitting region of the pixel defining layer 30, including a hole injection layer 401, a hole transport layer 402, a light-emitting material layer 403, an electron transport layer 404, and an electron injection layer 405 which are stacked from bottom to top, wherein the light-emitting material layer 403 further includes a red light material layer 4031, a green light material layer 4032, and a blue light material layer 4033. The blue light material layer 4033 contains a blue fluorescent material which is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane;


A common electrode layer 50 formed on the light-emitting function layer 40, wherein the material thereof is one or more of aluminum (Al), calcium (Ca), magnesium (Mg), and silver (Ag); and


An encapsulation layer 60 formed on the second electrode layer 50, including a first inorganic layer 601, an organic layer 602, and a second inorganic layer 603.


An embodiment of the present application provides an OLED display panel, a blue light material layer of the OLED display panel includes a blue fluorescent material. The blue fluorescent material is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane; wherein the tert-butyl pyrene increases an external quantum efficiency of the OLED display, and the tetrahedral structure increases distance between activated particles and reduces a risk of concentration quenching and greatly increases membrane fluorescence quantum efficiency. In addition, the transport unit with high charge carrier mobility improves a balance of the charge carrier transport, increases a probability of recombination, further improves the external quantum efficiency of an OLED display device, and alleviates a problem of low luminous efficiency of the current OLED display panel.


The above embodiments are references to the OLED display panel provided by the present application, but are not limited to the OLED display panel described in the above embodiments. The preparation of the OLED display panel can be carried out by methods known in the art.


In one embodiment, a structural formula of the blue fluorescent material in the blue material layer 4033 is




embedded image



wherein the X1, the X2 and the X3 may be the same ligand or different ligands.


In one embodiment, the X1, the X2, and the X3 are the same ligand, and they are selected from:




embedded image


embedded image


embedded image


In another embodiment, the X1 and the X2 are the same ligand, and the


X1 and the X3 are different ligands, they are selected from: hydrogen,




embedded image


embedded image


embedded image


In further another embodiment, the X1, the X2 and the X3 are different ligands and they are selected from: hydrogen,




embedded image


embedded image


embedded image


In the above embodiments, a R group of any one of




embedded image


embedded image



is a C1-C22 alkyl group, or a C1-C22 alkoxy group, or a C1-C22 heteroalkyl group, respectively.


A specific structure of the




embedded image



includes:




embedded image


Different structures of the blue fluorescent materials have different improvement effects on the luminous efficiency of OLED display device.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); a material of the hole injection layer 401 is poly (3,4-ethylenedioxythiophene) (PEDOT) and poly (styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis [N,N-bis (4-methylphenyl) aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis[2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 8230 cd/m2, a highest current efficiency can reach 8.12 cd/A, and the Y color coordinate is 0.19.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); materials of the hole injection layer 401 are poly(3,4-ethylenedioxythiophene) (PEDOT) and poly(styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis[N,N-bis(4-methylphenyl)aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis [2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 8740 cd/m2, a highest current efficiency can reach 8.14 cd/A, and the Y color coordinate is 0.23.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); materials of the hole injection layer 401 are poly(3,4-ethylenedioxythiophene) (PEDOT) and poly(styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis[N,N-bis(4-methylphenyl)aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis[2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 8230 cd/m2, a highest current efficiency can reach 8.12 cd/A, and Y color coordinate is 0.19.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); materials of the hole injection layer 401 are poly(3,4-ethylenedioxythiophene) (PEDOT) and poly (styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis[N,N-bis(4-methylphenyl)aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis[2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 6770 cd/m2, a highest current efficiency can reach 5.9 cd/A, and Y color coordinate is 0.16.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); materials of the hole injection layer 401 are poly(3,4-ethylenedioxythiophene) (PEDOT) and poly(styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis[N,N-bis(4-methylphenyl)aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis[2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 5740 cd/m2, a highest current efficiency can reach 5.35 cd/A, and Y color coordinate is 0.14.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); materials of the hole injection layer 401 are poly(3,4-ethylenedioxythiophene) (PEDOT) and poly (styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis[N,N-bis(4-methylphenyl)aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis[2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 8750 cd/m2, a highest current efficiency can reach 7.84 cd/A, and Y color coordinate is 0.18.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); materials of the hole injection layer 401 are poly(3,4-ethylenedioxythiophene) (PEDOT) and poly(styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis[N,N-bis(4-methylphenyl)aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis[2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 7430 cd/m2, a highest current efficiency can reach 6.5 cd/A, and Y color coordinate is 0.17.


In one embodiment, a material of pixel electrode layer 20 is indium tin oxide (ITO); materials of the hole injection layer 401 are poly(3,4-ethylenedioxythiophene) (PEDOT) and poly(styrenesulfonic acid) (PSS), and has a thickness of 40 nm; a material of the hole transport layer 402 is 4,4′-cyclohexyl bis[N,N-bis(4-methylphenyl)aniline (TAPC), and a thickness is 10 nm; materials of the blue light material layer 4033 are




embedded image



and bis[2-((oxo)diphenylphosphino)phenyl]ether (DPEPO), a mass ratio of




embedded image



to the entire blue light material layer 4033 is 4% and a thickness of the blue light material layer 4033 is 20 nm; a material of the electron transport layer 404 is 1,3,5-tris[(3-pyridyl)-3-phenyl]benzene (TmPyPB), and has a thickness of 30 nm; a material of the electron injection layer 405 is lithium fluoride (LiF) and has a thickness of 1 nm; and a material of the common electrode layer 50 is metal aluminum (Al) and has a thickness of 100 nm.


In the embodiment, a maximum brightness of the OLED display device can reach 7640 cd/m2, a highest current efficiency can reach 6.91 cd/A, and Y color coordinate is 0.2.


According to the above embodiments, it can be known that the present application provides a blue fluorescent material and an OLED display panel, the blue fluorescent material is a tetrahedral structure formed by simultaneously connecting a tert-butyl pyrene and a charge carrier transport unit to a same carbon of cyclohexane, wherein the tert-butyl pyrene increases an external quantum efficiency of the OLED display, and the tetrahedral structure increases distance between activated particles and reduces a risk of concentration quenching and greatly increases membrane fluorescence quantum efficiency. In addition, the transport unit with high charge carrier mobility improves a balance of the charge carrier transport, increases a probability of recombination, further improves an external quantum efficiency of an OLED display device, and alleviates a problem of low luminous efficiency of the current OLED display panel.


The description of the above exemplary embodiments is only for the purpose of understanding the invention. It is to be understood that the present invention is not limited to the disclosed exemplary embodiments. It is obvious to those skilled in the art that the above exemplary embodiments may be modified without departing from the scope and spirit of the present invention.

Claims
  • 1. A blue fluorescent material represented by a chemical formula of:
  • 2. A blue fluorescent material represented by a chemical formula of:
  • 3. A blue fluorescent material represented by a chemical formula of:
Priority Claims (1)
Number Date Country Kind
201910437252.3 May 2019 CN national
PCT Information
Filing Document Filing Date Country Kind
PCT/CN2019/107771 9/25/2019 WO
Publishing Document Publishing Date Country Kind
WO2020/237936 12/3/2020 WO A
US Referenced Citations (7)
Number Name Date Kind
8709613 Funahashi Apr 2014 B2
20050236977 Yamada Oct 2005 A1
20070252511 Funahashi Nov 2007 A1
20090096356 Murase Apr 2009 A1
20150299380 Cooper Oct 2015 A1
20170029362 Howard, Jr. Feb 2017 A1
20190229277 Hatakeyama Jul 2019 A1
Foreign Referenced Citations (6)
Number Date Country
107445929 Dec 2017 CN
107445929 Dec 2017 CN
110003090 Jul 2019 CN
2010195708 Sep 2010 JP
20160056522 May 2016 KR
101837049 Mar 2018 KR
Non-Patent Literature Citations (2)
Entry
S. Kim et al., 160 Synthetic Metals, 1259-1265 (2010) (Year: 2010).
A highly efficient deep blue fluorescent OLED based on diphenylaminofluorenylstyrene-containing emitting materials OLEDDesign, Synthesis and Performance of High-Efficiency Phosphorescent OLED Materials.
Related Publications (1)
Number Date Country
20200373495 A1 Nov 2020 US