Patent Grant
10160905
The present invention relates to a phosphor emitting blue-green visible light by near-ultraviolet ray excitation, particularly a blue-green light-emitting phosphor excellent in light-emitting properties, a light-emitting element, light-emitting device and white-light-emitting device using the blue-green light-emitting phosphor.
Phosphors, whose emission wavelengths vary depending on the types, find use in a wide variety of industries in accordance with the emission wavelengths.
In the lighting field, for example, white light can be theoretically obtained by mixing phosphors displaying light's three primary colors (red, blue, green). To obtain lighting simulating sun light for use in lighting, it has been desired to develop white light having further higher color-rendering property. Because of this, phosphors are required which can broadly emit light having a color displayed in the middle region of three primary colors of light.
Of the phosphors, what is strongly required at present, is a blue-green light-emitting phosphor, which emits blue-green visible light in the intermediate region between blue and green. Since the blue-green light-emitting phosphor emits blue-green visible light, it is an important phosphor which fills a valley formed between blue and green wavelength regions in the emission spectrum. If the blue-green light-emitting phosphor has a sufficient intensity and half width, it can realize white light (lighting) having further higher color-rendering property and capable of substituting for a blue phosphor.
As the blue-green light-emitting phosphor as mentioned above, a halophosphate phosphor is known, which contains an alkaline earth metal, phosphoric acid, a halogen and europium, as constituent elements. Although the blue-green light-emitting phosphor emits blue-green light, not only brightness and high-temperature property are insufficient but also half width is narrow. Thus, the light-emitting properties of the blue-green light-emitting phosphor had many points to be improved.
To improve the light-emitting properties of such a halophosphate phosphor, it has been proposed to add a large amount of alkaline earth metal, in particular, strontium (Sr) as a constituent element, thereby improving light-emitting properties. For this purpose, various types of phosphors have been suggested.
For example, as a conventional blue-green light-emitting phosphor, a phosphor containing Sr: M (M represent a metal element except Eu and Sr) in a ratio of a:b (a and b satisfy the conditions: a+b≤5 and a≥0.1 or b≥3), is known (see, Patent Literatures 1 and 2).
As another conventional blue-green light-emitting phosphor, a phosphor contains (Sr,Ca) and Ba, wherein a ratio of (Sr,Ca):Ba is defined as a:b (a and b satisfy conditions: a+b=5−x (0.3≤x≤1.2) and 0.12≤b/(a+b)≤0.4), is known (see, Patent Literature 3). As another conventional blue-green light-emitting phosphor, a phosphor containing (Sr,Ca) and Ba in a ratio of a:b (a and b satisfy the conditions: a+b=5−x (0.3≤x≤1.2) and 0.05≤b/(a+b)≤0.6), is known (see, Patent Literature 4).
As another conventional blue-green light-emitting phosphor, a phosphor containing Sr and Ba in a ratio of a:b (a and b satisfy the conditions: a+b=5−x (0.3≤x≤1.2) and 0.1≤b/(a+b)≤0.6), is known (see, Patent Literature 5). As another conventional blue-green light-emitting phosphor, a phosphor containing (Sr,Ca) and Ba in a ratio of a:b (a and b satisfy the conditions: a+b=5−x (0.3≤x≤1.2) and 0.05≤b/(a+b)≤0.6), is known (see Patent Literature 6).
Patent Literature 1: Japanese Patent Laid-Open No. 2004-253747
Patent Literature 2: Japanese Patent Laid-Open No. 2010-21578
Patent Literature 3: International Publication No. WO2012/114640
Patent Literature 4: International Publication No. WO2011/105571
Patent Literature 5: Japanese Patent Laid-Open No. 2011-225822 issue
Patent Literature 6: Japanese Patent Laid-Open No. 2011-225823 issue
In the conventional blue-green light-emitting phosphors, performance degradation, such as deterioration of high-temperature property, is caused by high content of strontium (Sr). The high-temperature property is a very important property. If high-temperature property is poor, the phosphor easily deteriorates when it is used in high-temperature conditions. In addition, due to low durability, the phosphor is quickly used up, increasing maintenance cost. Likewise, such a phosphor has practical disadvantages.
Particularly, in lighting uses, high power and high-level continuous operation are required for phosphors. Because of this, phosphors must maintain high emission intensity (wide light-emitting area) even in high-temperature conditions (for example, a high temperature (condition) exceeding 100° C.); in other words, excellent high-temperature property.
The present invention was made in order to solve the aforementioned problems. An object of the invention is to provide a blue-green light-emitting phosphor having excellent high-temperature property and excellent light-emitting properties such as brightness and half width.
The present inventors conducted intensive studies. As a result, they focused on barium (Ba) belonging to the alkaline earth metal, as a constituent element of a halophosphate phosphor and formed a phosphor by significantly increasing the content of Ba more than ever within a predetermined range. They found that the phosphor, upon irradiation with a near-ultraviolet ray, emits blue-green visible light having a broad spectrum and exhibiting more excellent high-temperature property, brightness and half width than conventional phosphors. Based on the finding, the present invention was attained.
More specifically, the blue-green light-emitting phosphor disclosed in this application is a phosphor constituted of a plurality of alkaline earth metal elements including a barium element, phosphoric acid and a halogen element, and Eu as an activator, in which the molar ratio of the barium element to the total content of the alkaline earth metal elements is larger than 60% and smaller than 95%, and upon irradiation with a near-ultraviolet ray, the blue-green light-emitting phosphor is excited to thereby emit blue-green visible light.
The blue-green light-emitting phosphor disclosed in this application is, if necessary, represented by in a general formula:
Bab(Sr,Ca,Mg)c(PO4)dXe:Eua
where X represents a halogen element, 0<a<1.5, 3.5≤b≤8.5, 0≤c≤5.9, 5.4≤d≤6.6, 1.8≤e≤2.2, 0.6<b/(b+c)<0.95.
The light-emitting element disclosed in this application has a blue-green light-emitting phosphor as mentioned above. The light-emitting device disclosed in this application has a blue-green light-emitting phosphor as mentioned above. The white-light-emitting device disclosed in this application has a blue-green light-emitting phosphor as mentioned above, a red phosphor and a green phosphor, and may further optionally have a blue phosphor. The white-light-emitting device (disclosed in this application) is constituted of a first phosphor, which is a blue-green light-emitting phosphor as mentioned above and emits blue-green light of 430 to 500 nm, a second phosphor emitting green to yellow light of 500 to 580 nm, a third phosphor emitting red to deep red light of 580 to 700 nm and an LED element emitting near-ultraviolet light of 350 to 430 nm, and the first phosphor, second phosphor and third phosphor are directly or indirectly excited by light from the LED element to emit white light.
The blue-green light-emitting phosphor according to the present invention is a phosphor constituted of a plurality of alkaline earth metal elements including a barium element, phosphoric acid and a halogen element, and Eu as an activator, in which the molar ratio of the barium element to the total content of the alkaline earth metal elements is larger than 60% and smaller than 95%, and upon irradiation with a near-ultraviolet ray, the blue-green light-emitting phosphor is excited to thereby emit blue-green visible light.
The near-ultraviolet ray to be applied as an excitation source is not particularly limited as long as the wavelength thereof falls within a general wavelength region of near-ultraviolet rays of 200 nm or more; for example, a near-ultraviolet ray having a wavelength region of 370 nm to 420 nm can be used. The blue-green light-emitting phosphor according to the present invention, upon irradiation with the near-ultraviolet ray, emits blue green visible light having a broad emission spectrum having an emission peak within a wavelength region of 470 nm to 490 nm and having high color-rendering property.
As described above, the blue-green light-emitting phosphor according to the present invention, which emits blue green visible light having a broad emission spectrum, can be used in combination with other phosphors known in the art to form a light-emitting element or a light-emitting device which can be used as a light source emitting white light close to sun light.
According to the present invention, blue-green visible light having such a broad emission spectrum and excellent temperature property (high-temperature property) can be obtained. However, in conventional phosphors, in which the molar ratio of a barium element to the all alkaline earth metal elements is 60% or less and 95% or more (the phosphors disclosed in Patent Literatures 1 to 6, all have a molar ratio of a barium element of 60% or less), excellent properties, in particular, temperature property, cannot be obtained. This is also confirmed by the present inventors (see Examples described later).
More specifically, to describe the high-temperature property of a phosphor, if the molar ratio of a barium element to the all alkaline earth metal elements is 60% or less, the light-emitting area of a phosphor remains low; however, if the molar ratio is larger than 60%, the light-emitting area of the phosphor sharply increases in proportional to an increase in molar ratio of the barium element. Whereas, if the molar ratio of the barium element exceeds 95%, the light-emitting area of the phosphor sharply decreases. In the blue-green light-emitting phosphor according to the present invention, however, a decrease of emission intensity by heat is suppressed even in high temperature conditions. It has been confirmed that the phosphor of the invention has high heat resistance (see Examples described later).
A mechanism to produce such an excellent effect has not yet been specifically elucidated; however, it is presumed that a barium element, which is contained as a constituent element in the blue-green light-emitting phosphor according to the present invention in a molar ratio of 60% or larger and smaller than 95%; in other words, a high-content barium element, mutually interacts with other alkaline earth metal elements on the atomic level and produces a favorable effect on light emission; in particular, these elements produce a specific crystal structure, based on which the phosphor exhibits high-temperature property.
Actually, in view of crystal structure, the following facts were confirmed: if the molar ratio of a barium element to the all alkaline earth metal elements is 60% or less, a crystal phase (SCA phase: crystal structure mainly consisting of Sr) exhibiting an X-ray diffraction pattern, which has three diffraction peaks derived from the (211) plane, (112) plane, and (300) plane at a 2θ value of about 30°, is shown; in contrast, if the molar ratio of a barium element to the all alkaline earth metal elements is larger than 60%, a crystal phase (BCA phase: crystal structure mainly consisting of Ba) having two diffraction peaks derived from the (112) plane and (300) plane, is shown. Likewise, a crystal structural change was confirmed (see, Examples described later).
According to an embodiment of the present invention, a blue-green light-emitting phosphor is represented by the following general
Bab(Sr,Ca,Mg)c(PO4)dXe:Eua formula:
where X represents a halogen element, 0<a<1.5; 9.5≤a+b+c≤10.5; 5.4≤d≤6.6; 1.8≤e≤2.2; 0.6<b/(b+c)<0.95.
The composition of individual constituent elements in the general formula is specified from composition by mole in a starting material. More specifically, a, b, c, d, and e defined in the general formula respectively represent the composition by mole of Eu, Ba, (Sr,Ca,Mg), (PO4), and X in the starting material.
The expression “(Sr,Ca,Mg)” means that at least one element of Sr, Ca, and Mg is contained. More specifically, the expression “(Sr,Ca,Mg)” may be a case where any one element of Sr, Ca and Mg is contained; a case where two elements of Sr, Ca and Mg are contained or a case where all elements of Sr, Ca and Mg are contained.
It is preferable that the blue-green light-emitting phosphor according to the present invention contains Ca and Mg in order to obtain a broader light-emitting region. The content of Ca, however, was a cause of deteriorating temperature property in conventional phosphors; whereas, in the blue-green light-emitting phosphor according to the present invention, even if Ca is contained, excellent properties, i.e., a broader light-emitting region, can be obtained while maintaining temperature property.
It is also preferable that 50 mol % or more of the halogen elements constituting the blue-green light-emitting phosphor according to the present invention is constituted of a chlorine element. If 50 mol % or more of the halogen elements is constituted of a chlorine element, light-emitting properties are improved such that a satisfactory light-emitting area and chromaticity region are maintained.
It is also preferable that the blue-green light-emitting phosphor according to the present invention contains at least one co-activating element selected from the group of rare earth metals and transition metals consisting of Sc, Y, La, Gd, Tb, Lu, Pr, Ce, Cr, V, Mn and Zn. If such a co-activating element is contained, the half width and maximum excitation wavelength can be improved, and a satisfactory chromaticity region can be produced.
The blue-green light-emitting phosphor according to the present invention can be constituted of a blue-green light-emitting phosphor as mentioned above, for example, in an amount of 10 to 90 wt % and at least one phosphor selected from the group of blue phosphors and green phosphors consisting of BaMgAl10O17:Eu, (Ba, Sr)3MgSi3O8:Eu, Sr10(PO4)6Cl2:Eu, Sr2P2O7:Eu, Ca2PO4Cl:Eu, Ba2PO4Cl:Eu, (Ba,Sr)2SiO4:Eu and (Ba,Sr,Ca)Al2O4:Eu.
With this constitution, it is confirmed that an excellent half width (FWHM) of 50 to 100 nm is provided and excellent light-emitting properties, i.e. a rectangle chromaticity region defined by a chromaticity value x=0.10 to 0.25 and a chromaticity value y=0.05 to 0.40 is formed (see, Examples described later).
A method for synthesizing the blue-green light-emitting phosphor according to the present invention having such excellent properties is not particularly limited; however, the blue-green light-emitting phosphor can be produced, for example, by homogeneously mixing a Eu source serving as a light emission center, an alkaline earth source, a phosphorus source and a halogen source by a dry or wet method and calcinating the mixture in a reducing atmosphere.
The individual starting compounds are not particularly limited as long as a compound containing at least one of constituent element (for example, Ba, Sr, Ca, Mg, P, a halogen element, and Eu) of the blue-green light-emitting phosphor according to the present invention is used so as to obtain a blue-green light-emitting phosphor containing desired constituent elements (containing every constituent element without fail).
As an example of such a starting compound, an oxide, a hydroxide or a carbide containing constituent elements of a blue-green light-emitting phosphor can be used. For example, in the case of a barium (i.e., one of constituent elements of a blue-green light-emitting phosphor), e.g., barium oxide, barium hydroxide or barium carbonate can be used as a starting compound. This is because, in producing of the blue-green light-emitting phosphor according to the present invention, individual starting compounds are subjected to a heat treatment, with the result that constituent elements alone finally remain (from the starting compounds) by the heat treatment. Thus, the blue-green light-emitting phosphor according to the present invention can be produced without being affected by the types of starting compounds.
Examples of the Eu source and alkaline earth source include oxides, hydroxides, carbonates, sulfates, nitrates, organic acid salts and halogenates of Eu, Ba, Sr, Ca and Mg. Examples of the phosphorus source include ammonium phosphate, ammonium dihydrogen phosphate, ammonium monohydrogen phosphate, alkaline earth phosphate, alkaline earth hydrogen phosphate, phosphorus oxide, phosphoric acid and condensed phosphoric acid. Examples of the halogen source include a halogenated alkaline earth salt, a halogenated alkaline earth hydrate and an ammonium halide.
The blue-green light-emitting phosphor according to the present invention can be synthesized by a method primarily employing, for example, a self-flux reaction. More specifically, a starting compound, i.e., a halogen source, is used as a flux for a calcination reaction and individual starting compounds are excessively supplied within the range that the excellent effect of the present invention is not undermined. In this manner, the excellent properties of the present invention tend to be easily obtained. Note that it is desirable that a composition of a product to be synthesized from the excessive contents is estimated in advance.
As the starting compounds, for example, anhydrous BaCl2 and SrCl2 can be used in order to easily obtain excellent properties. However, the starting compounds are not limited to these, for example, hydrates can be used. As an example of a starting compound, a compound having a mixing ratio of BaHPO4:SrHPO4=BaCl2:SrCl2 can be mentioned.
The blue-green light-emitting phosphor according to the present invention can be used for a light-emitting element having the blue-green light-emitting phosphor. The blue-green light-emitting phosphor according to the present invention can be also used for a light-emitting device having the blue-green light-emitting phosphor. In particular, the blue-green light-emitting phosphor according to the present invention can be used for a white-light-emitting device having the blue-green light-emitting phosphor, a red phosphor and a green phosphor. In this case, it was confirmed that white light having a broad light emission spectrum and high color-rendering property never ever obtained in the art can be obtained. Further, in the white-light-emitting device, if the content or emission color (chromaticity) of the blue-green light-emitting phosphor according to the present invention is controlled, which leads to controlling the wavelength band and wavelength intensity of the blue-green light-emitting phosphor, with the result that the color temperature of the white light to be obtained can be freely controlled. Owing to the control, for example, white light with a bluish tone close to fluorescent color to white light with an orangish tone close to the color of a light bulb (even if these fall within the same white light but differ in tone), can be selectively obtained.
According to an embodiment of the present invention, the light-emitting device is constituted of the blue-green light-emitting phosphor according to the present invention and a light-emitting element, which emits near-ultraviolet light. In the device, the blue-green light-emitting phosphor according to the present invention is irradiated with a near-ultraviolet ray from the light-emitting element, which emits near-ultraviolet light, to efficiently emit blue-green visible light. Use of the light-emitting device according to the present invention is not particularly limited. The device can find use in a wide variety of fields and can be used, for example, as various types of lighting apparatuses such as a lighting apparatus for plant breeding.
According to an embodiment of the present invention, the white-light-emitting device is constituted of a first phosphor, which is a blue-green light-emitting phosphor according to the present invention and emits blue-green light of 430 to 500 nm, a second phosphor emitting green to yellow light of 500 to 580 nm, a third phosphor emitting red to deep red light of 580 to 700 nm and an LED element emitting near-ultraviolet light of 350 to 430 nm, in which the first phosphor, second phosphor and third phosphor are directly or indirectly excited by light from the LED element to emit white light.
As the first phosphor, a blue-green light-emitting phosphor obtained in any one of Examples can be used.
The second phosphor is not particularly limited as long as it is a phosphor emitting light in a green wavelength band; and a phosphor containing a Eu-activated alkaline earth silicate-based phosphor or an alkaline earth silicate nitride-based phosphor is preferably used. Examples thereof include (Ba,Sr,Ca,Mg)2SiO4:Eu (BOSE), Si6-zAlzOzN8-z (β SiAlON), (Ba, Sr) Si2O2N2, (Ba, Sr, Ca) MgAl10O17:Eu2+, Mn2+ (BAMN) and (Ca, Sr)8Mg (SiO4)4Cl2:Eu.
The third phosphor is not particularly limited as long as it is a phosphor emitting color in a red to deep red wavelength band. A phosphor containing at least one of a Eu-activated alkaline earth oxynitride phosphor, a Eu-activated alkaline earth silicate-based phosphor and a Mn-activated fluoride complex red phosphor is preferably used. Examples thereof include (Ba,Sr,Ca)3SiO5:Eu (for example, Sr3SiO5:Eu (SSE)), (Ba, Sr, Ca)2(Si,Al)5N8:Eu, (Ca, Sr) AlSi(O,N)3, (Sr,Ca)AlN3:Eu (SCASN), K2(Si,Ge,Ti)F6:Mn4+ (KSF) and Li(Eu,RE)W2O8 (where RE includes at least one of Sc, Y, La, Gd and Lu) (LEW).
It is confirmed that the white-light-emitting device according to the present invention has high color-rendering property and is also quantitatively confirmed that the device has excellent property based on a general color-rendering index (Ra) or color-rendering index (CRI) of 95 or more. The color-rendering property refers to an index indicating the effect of a light-source spectrum on the color appearance of an object. The color-rendering property can be quantitatively evaluated by converting the difference between the light of interest and sun light into a numerical value (sun light is specified as a reference value of 100). Note that, as the general color-rendering index (Ra) or color-rendering index (CRI) becomes closer to 100, it is evaluated that the color-rendering property is higher. Since the white-light-emitting device of the present invention has such excellent properties, the device can be used in a wide variety of light sources such as a backlight source of a wide color gamut and an illumination light source having high color-rendering.
The white-light-emitting device according to the present invention is constituted, without requiring an additional light source emitting blue light, based on the mechanism where the color temperature of white light changes depending on the content of a blue green component contained in the blue-green light-emitting phosphor (BCA) according to the present invention. This is an excellent characteristic. More specifically, a conventional blue-green light-emitting phosphor has been considered for making up for blue-green light of a white-light-emitting device; however, in the blue-green light-emitting phosphor according to the present invention, the blue-green light-emitting phosphor can be used as an alternative substance for the blue phosphor itself. In contrast, the white-light-emitting device of the present invention can employ another blue phosphor. In this case, pure blue color derived from the blue phosphors and blue-green derived from the blue-green light-emitting phosphor according to the present invention are superimposed to successfully obtain white light further closer to sun light. Further, the white-light-emitting device of the present invention makes it possible to prepare new blue-green by controlling the mixing ratio of blue color and blue-green color. In this manner, a white light source having variety color temperatures can be produced (see, Examples described later).
The features of the present invention will be further clearly described by way of Examples below; however, the present invention is not limited by Examples.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.5:8.0:1.5:6:2 and mixed by use of a mortar. The mixture was placed in a crucible made of alumina and kept in an electric furnace at 900° C. for 2 hours in the atmosphere, ground, sieved, and further kept in a nitrogen atmosphere containing 5% hydrogen gas at 1150° C. for 5 hours for calcination. The calcined product was washed with water, dried and classified to obtain a blue-green light-emitting phosphor corresponding to Eu0.5Ba8.0Sr1.5(PO4)6Cl2. The X-ray diffraction pattern of the phosphor was measured by using an X ray diffraction device (XRD6100, manufactured by Shimadzu Corporation) employing CuKα ray as a radiation source. Light-emitting properties of the phosphor excited at 400 nm were measured by a fluorescence spectrophotometer (FP6500, Manufactured by JASCO).
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.5:8.0:1.5:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.5Ba8.4Sr1.1(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.6:7.7:1.7:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba7.7Sr1.7(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.6:8.1:1.3:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba8.1Sr1.3(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.6:6.5:2.9:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba6.5Sr2.9(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.6:7.4:2.0:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba7.4Sr2.0(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing no Ba. Starting materials, Eu2O3, SrCO3, SrHPO4 and SrCl2 were weighed such that the final molar ratio of Eu:Sr:P:Cl was 0.5:9.5:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.5Sr9.5(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighed such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.5:2.2:7.3:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.5Ba2.2Sr7.3(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2, SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.6:3.5:5.9:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba3.5Sr5.9(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing no Sr. Starting materials, Eu2O3, BaCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.6:9.4:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba9.4(PO4)6Cl2, and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.5:4.2:5.3:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.5Ba4.2Sr5.3(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca and Mg. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, Mg(OH)2, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:Mg:P:Cl was 0.3:5.0:3.0:1.5:0.2:6:2 and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.3Ba5.0Sr3.0Ca1.5Mg0.2(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.3:9.25:0.45:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.3Ba9.25Sr0.45(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
The compositions of the phosphors obtained in Examples 1 to 6 and Comparative Examples 1 to 7 are shown in the following table. The X-ray diffraction patterns of the phosphors obtained in Examples 1 to 6 and Comparative Examples 1 to 7 are shown in
Further, similarly to the above, starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.9:7.1:2.0:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.9Ba7.1Sr2.0(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:P:Cl was 0.9:6.6:1.5:1.0:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.9Ba6.6Sr1.5Ca1.0(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 1.0:5.7:3.3:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.0Ba5.7Sr3.3(P4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 1.0:6.7:2.3:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.0Ba6.7Sr2.3(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 1.2:6.3:2.5:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.0Ba6.7Sr2.3(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:P:Cl was 1.0:6.7:2.1:0.2:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.0Ba6.7Sr2.1Ca0.2(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca and Mg. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, Mg(OH)2, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:Mg:P:Cl was 1.0:5.7:2.8:0.4:0.1:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.0Ba5.7Sr2.8Ca0.4Mg0.1(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 1.5:7.2:1.3:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.5Ba7.2Sr1.3(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Mg. Starting materials, Eu2O3, BaCO3, SrCO3, Mg(OH)2, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Mg:P:Cl was 0.5:7.2:1.8:0.5:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.5Ba7.2Sr1.8Mg0.5(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:P:Cl was 0.5:0.6:6.5:1.4:1.5:6:2 and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba6.5Sr1.4Ca1.5(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:P:Cl was 0.6:6.5:2.4:0.5:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba6.5Sr2.4Ca0.5(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.9:3.2:5.9:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.9Ba3.2Sr5.9(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 1.35:2.95:5.7:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.35Ba2.95Sr5.7(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 1.5:2.95:5.55:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu1.5Ba2.95Sr5.55(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:P:Cl was 0.6:3.4:4.5:1.5:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba3.4Sr4.5Ca1.5(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
A phosphor was formed of a composition containing Ca. Starting materials, Eu2O3, BaCO3, SrCO3, CaCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:Ca:P:Cl was 0.6:3.4:5.5:0.5:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.6Ba3.4Sr5.5Ca0.5(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.9:3.7:5.4:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.9Ba3.7Sr5.4(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
Starting materials, Eu2O3, BaCO3, SrCO3, BaHPO4, SrHPO4, BaCl2 and SrCl2 were weighted such that the final molar ratio of Eu:Ba:Sr:P:Cl was 0.8:5.0:4.2:6:2, and then, the same procedure as in Example 1 was repeated to produce a blue-green light-emitting phosphor corresponding to Eu0.8Ba5.0Sr4.2(PO4)6Cl2 and the X-ray diffraction pattern and light-emitting properties of the phosphor were obtained.
The compositions of the phosphors obtained in Examples 7 to 17 and Comparative Examples 8 to 14 are shown in the following table. The light-emitting properties of the phosphors obtained in Examples 7 to 17 are shown in
If the case where a phosphor is used in lighting where high power and high-level continuous operation are required is presumed, emission performance at 150° C. becomes important. Thus, the phosphors obtained in Examples 1 to 6 and Comparative Examples 1 to 7 were subjected to measurement of brightness, light-emitting area, maintenance rate, light-emitting area at 150° C. and brightness at 150° C. The results are shown in the following table, together with the molar ratio [Ba] of a barium element to the all alkaline earth metal elements (More specifically, molar ratio (Ba)/molar ratio (Sr+Ca+Mg)) in each of the phosphors.
Similarly to the above, the phosphors obtained in Examples 7 to 17 and Comparative Examples 8 to 14 were subjected to measurement of brightness, light-emitting area, maintenance rate, light-emitting area at 150° C. and brightness at 150° C.
The results are shown in the following table.
(Dependency of Light-Emitting Area on Barium Concentration)
The dependency of the light-emitting areas of the phosphors obtained in Examples mentioned above on barium concentration is shown in the graph of
(Correlation Between the Molar Ratio of Barium Element and Crystal Structure Observed in X-Ray Diffraction Pattern)
With respect to the phosphors obtained in Examples and Comparative Examples mentioned above, X-ray diffraction patterns of the phosphors different in the molar ratio of a barium element to the all alkaline earth metal elements, are shown in
(Correlation Between the Mixing Ratio of Europium and Light-Emitting Area)
Correlation of the Eu mixing ratio and the light-emitting area, which was observed in the phosphors obtained in Examples and Comparative Examples mentioned above, is shown in
(Correlation Between Europium Mixing Ratio and Temperature Property)
Correlation of the Eu mixing ratio and temperature property (light-emitting area maintenance rate at 150° C.), which was observed in the phosphors obtained in Examples 4, 7 and 14 and Comparative Examples 3, 8, and 10, is shown in the following table and
From the results, it was confirmed that if the molar ratio [Ba] of a barium element to the all alkaline earth metal elements is high, satisfactory temperature property is obtained, regardless of the mixing ratio of europium. Likewise, if [Ba] is high, particularly in the case where the europium mixing ratio is high, high light-emitting area and brightness (property) are obtained. Even in this case, high maintenance rate is obtained. Thus, it is considered that a phosphor having excellent light-emitting properties in practice can be obtained.
(Tuning and Broadening Emission)
Correlation of the mixing ratios of Ca and Mg and temperature property, which was observed in the phosphors obtained in Examples 5, 16, and 17 and Comparative Examples 3, 11, and 12, is shown in the following table. Furthermore, the correlation of the mixing ratio of Ca and emission wavelength, which was observed in the blue-green light-emitting phosphors obtained in Examples 5, 16, and 17, is shown in
As is apparent from the results, in the blue-green light-emitting phosphors obtained in Examples, excellent (property of) half width (FWMH) was obtained by adding Ca and Mg. From this, it was confirmed that a light-emitting region can be more broadened. In conventional phosphors, temperature property deteriorates by adding Ca. However, in the blue-green light-emitting phosphors according to Examples of the present invention, even if Ca is contained, a light-emitting region can be more broadened while maintaining temperature property. It was confirmed that the phosphors of the invention have such an excellent property.
(Tabularization of Light-Emitting Area)
The light-emitting areas of the blue-green light-emitting phosphors obtained in Examples 1 to 17 are shown in
(Chromaticity Range of Blue-Green Light)
Chromaticity ranges of the blue-green light-emitting phosphors obtained in Examples 1 to 17 are shown in
(Use of Simulated Solar Lighting)
To check use of simulated solar lighting, illuminating devices were constituted of the blue-green light-emitting phosphors obtained in Examples 4 and 17 and other phosphors in combination. The emission spectra thereof are shown in
From the results, it was confirmed that a valley between blue and green in the emission spectrum is filled with the emission of a blue-green light-emitting phosphor of Example, with the result that simulated solar lighting (white-light-emitting device) having a spectrum close to that of sun light can be obtained. In the white-light-emitting device as mentioned above, the wavelength band and wavelength intensity of the blue-green light-emitting phosphor according to Example can be controlled by controlling the mixing ratio of the blue-green light-emitting phosphors or emission color thereof; with the result that the color temperature of the white light to be obtained can be freely controlled. Owing to the control, for example, white light with a bluish tone close to fluorescent color to white light with an orangish tone close to the color of a light bulb (even if these fall within the same white light but differ in tone) can be selectively obtained.
(Use of High Color-Rendering White-Light-Emitting Device)
Use of high color-rendering white-light-emitting devices employing the blue-green light-emitting phosphors according to Examples was checked. As such a white-light-emitting device, a device was constituted of a blue-green light-emitting phosphor (blue-green light-emitting phosphors (BCA) (J1, J12) according to Examples 1, 12 and a blue light-emitting phosphor (H1) according to Comparative Example 1) emitting blue to blue-green light of 430 to 500 nm, β SiAlON (or BOSE) emitting green to yellow light of 500 to 580 nm, SCASN emitting red to deep red light of 580 to 700 nm, and an LED element emitting near-ultraviolet light of 350 to 430 nm.
The white-light-emitting device, as shown in
(1) For Phosphor Resin Mixture A: Purple LED+(BCA (J12)+(H1))+β-SiAlON+SCASN
As an LED chip, a commercially available chip (400 nm) was used and embedded in a commercially available silicon resin consisting of (BCA (J12): (H1)): β-SiAlON: SCASN=(50:50): 12:20 to obtain a white-light-emitting device (white LED light-emitting device) having a structure shown in
(2) For Phosphor Resin Mixture B: Purple LED+(BCA (J1))+BOSE+SCASN
As an LED chip, a commercially available chip (400 nm) was used and embedded in a commercially available silicon resin consisting of BCA (J1):BOSE:SCASN=100:12:18 to obtain a white-light-emitting device (white LED light-emitting device) having a structure shown in
(3) For Phosphor Resin Mixture C: Purple LED+BCA (J18)+β-SiAlON+SCASN
A white-light-emitting device was prepared by using a blue-green light-emitting phosphor except the blue-green light-emitting phosphor (BCA) (J1, J12) according to Example. First, a blue-green light-emitting phosphor, Eu0.6Ba7.9Sr1.45Mg0.05(PO4)6Cl2 (defined as phosphor J18) to be used in the white-light-emitting device was synthesized in the same manner as in Examples.
(Production of Blue-Green Light-Emitting Phosphor Eu0.6Ba7.9Sr1.45Mg0.05(PO4)6Cl2 (Phosphor J18))
Starting materials, Eu2O3, BaCO3, SrCO3, Mg2 (OH)2CO3, (NH4)2HPO4, BaCl2.2H2O, SrCl2.6H2O were weighted such that the final molar ratio of Eu:Ba:Sr:Mg:P:Cl was 0.6:7.9:1.45:0.05:6:2, and mixed by use of a mortar. The mixture was placed in a crucible made of alumina and kept in an electric furnace at 900° C. for 2 hours in the atmosphere, ground, sieved, and further kept in a nitrogen atmosphere containing 5% hydrogen gas at 1150° C. for 5 hours for calcination. The calcined product was washed with water, dried and classified to obtain a blue-green light-emitting phosphor (phosphor J18). The X-ray diffraction pattern of the phosphor was measured by using an X ray diffraction device (XRD6100, manufactured by Shimadzu Corporation) employing CuKα ray as a radiation source. The results are shown in
Subsequently, as an LED chip, a commercially available chip (400 nm) was used and embedded in a commercially available silicon resin consisting of BCA (J18): β-SiAlON:SCASN=100:17:50 to obtain a white-light-emitting device (white LED light-emitting device) having a structure shown in
The measurement results of the color-rendering property of the white-light-emitting device using each of phosphor resin mixtures A, B, C are shown in Table 7 and
From the results, it was confirmed that, in the white-light-emitting device, the color temperature of white light changes depending on the degree of a blue green component contained in a blue-green light-emitting phosphor (BCA) emitting blue-green light and thereby, white light having high color-rendering property can be realized without additionally using other blue phosphors, as shown in the results of the phosphor resin mixtures B and C (as to color temperature, mixture B: neutral white, mixture C: warm white). Also, in the white-light-emitting device, a conventional blue phosphor can be mixed in addition to the blue-green light-emitting phosphor (BCA) obtained, as shown in the results of the phosphor resin mixture A. From this, it was found that a white light phosphor having high color-rendering property in a further wider color temperature range can be obtained by using various phosphors in combination (for example, white-light-emitting device, which emits cold white light having a color temperature of 10000K, can be realized by selecting blue phosphors and optimally mixing them).
In the following table 7 and
And, as a color-rendering index:
(CRI)=(ΣR1 to 15)/15.
Also, in
From the results, it was confirmed that the white-light-emitting devices using the phosphor resin mixture A, B and C each exhibit extremely high color-rendering property (a general color-rendering index (Ra) or color-rendering index (CRI) of 95 or more). Further, from the results shown in
Also, the emission spectra of the white-light-emitting devices using the phosphor resin mixture A, B and C are shown in
| Number | Date | Country | Kind |
|---|---|---|---|
| 2015-136468 | Jul 2015 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2016/067792 | 6/15/2016 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/006725 | 1/12/2017 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4458176 | Chenot | Jul 1984 | A |
| 20030080341 | Sakano | May 2003 | A1 |
| 20100142189 | Hong | Jun 2010 | A1 |
| 20100164365 | Yoshino | Jul 2010 | A1 |
| 20120212123 | Sakuta | Aug 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 2004-253747 | Sep 2004 | JP |
| 2010-021578 | Jan 2010 | JP |
| 2011-225822 | Nov 2011 | JP |
| 2011-225823 | Nov 2011 | JP |
| WO-2007037120 | Apr 2007 | WO |
| WO-2009107535 | Sep 2009 | WO |
| WO-2011105571 | Sep 2011 | WO |
| WO-2012114640 | Aug 2012 | WO |
| Entry |
|---|
| International Search Report issued in Application No. PCT/JP2016/067792, dated Sep. 20, 2016. |
| Number | Date | Country | |
|---|---|---|---|
| 20180171220 A1 | Jun 2018 | US |