Patent Application
20070207339
The present application relates generally to a process for applying coatings of the type used to protect components exposed to high temperature environments, such as bond coats for protecting the surface of nickel-base superalloys. The present application also relates to forming a protective coating by depositing a Ni—Al based bond coat by cathodic arc deposition on the surface of an aircraft engine component. Another aspect of the present application relates to a coated turbine blade.
Higher operating temperatures for gas turbine engines are continuously sought in order to increase their efficiency. However, as operating temperatures increase, the high temperature durability of the components of the engine must correspondingly increase. Significant advances in high-temperature capabilities have been achieved through the formulation of nickel- and cobalt-base superalloys. Nonetheless, when used to form components of the turbine, combustor and augmentor sections of a gas turbine engine, such alloys alone are often susceptible to damage by oxidation and hot corrosion attack and may not retain adequate mechanical properties. For this reason, these components are often protected by an environmental and/or thermal-insulating coating, the latter of which is termed a thermal barrier coating (TBC) system. Ceramic materials and particularly yttria-stabilized zirconia (YSZ) are widely used as a thermal barrier coating (TBC), or topcoat, of TBC systems used on gas turbine engine components. The TBC employed in the highest-temperature regions of gas turbine engines is typically deposited by electron beam physical vapor deposition (EBPVD) techniques that yield a columnar grain structure that is able to expand and contract without causing damaging stresses that lead to spallation.
To be effective, TBC systems must have low thermal conductivity, strongly adhere to the article, and remain adherent throughout many heating and cooling cycles. The latter requirement is particularly demanding due to the different coefficients of thermal expansion between ceramic topcoat materials and the superalloy substrates they protect. To promote adhesion and extend the service life of a TBC system, an oxidation-resistant bond coat is usually employed. Bond coats are typically in the form of overlay coatings such as MCrAlX (where M is iron, cobalt, and/or nickel, and X is yttrium or another rare earth element), or diffusion aluminide coatings.
While bond coats deposited by various techniques have been successfully employed, there remains a need for a bond coat for thermal barrier coatings that can be applied to aircraft engine components with a low cost process, while at the same exhibiting low porosity and oxidation.
In one embodiment, the present invention generally provides a process for forming a Ni—Al base bond coat on a component designed for use in a hostile thermal environment, such as a superalloy turbine component of a gas turbine engine.
In another embodiment, the present invention is directed to a method for forming a protective bond coating on a substrate. The method comprises the steps of providing an article substrate having a substrate surface, forming a bond coat on the substrate by depositing a beta-phase Ni—Al bond coat by cathodic arc deposition, processing the bond coat by peening to improve the coating structure, and heat treating the bond coat to a preselected temperature for a preselected period of time in a vacuum.
In another embodiment, the present invention is directed to a method for forming a thermal barrier coating system. The method comprises the steps of providing a nickel-base superalloy article substrate comprising a component of a gas turbine engine and having a substrate surface, forming a bond coat on the substrate by depositing a NiAlCrZr layer by cathodic arc deposition, processing the bond coat by peening to improve the coating structure, heat treating the bond coat in a vacuum at a temperature of from about 1975° F. to about 2000° F. for a duration of from about 2 hours to about 4 hours, and depositing a ceramic thermal barrier coating overlying the bond coat surface.
In yet another embodiment, the present invention is directed to a turbine blade. The turbine blade comprises a nickel-base superalloy substrate, a bond coat on the surface of the substrate, and a ceramic thermal barrier coating overlying the bond coat surface. The bond coating is formed by depositing a NiAlCrZr layer by cathodic arc deposition on the surface of the substrate, processing the bond coat by peening to improve the coating structure, and heat treating the bond coat in a vacuum at a temperature of from about 1975° F. to about 2000° F. for a duration of from about 2 hours to about 4 hours.
These and other features, aspects and advantages of embodiments of the present invention will become evident to those skilled in the art from a reading of the present disclosure.
While the specification concludes with claims particularly pointing out and distinctly claiming the invention, it is believed that the present invention will be better understood from the following description in conjunction with the accompanying figures, in which like reference numerals identify like elements, and wherein:
In one embodiment, the present invention is generally applicable to metal components that are protected from a thermally hostile environment by a thermal barrier coating (TBC) system. Notable examples of such components include the high and low pressure turbine nozzles (vanes) and buckets (blades), shrouds, combustor liners, transition pieces and augmentor hardware of gas turbine engines. While this invention is particularly applicable to turbine engine components, the teachings of this invention are generally applicable to any component on which a thermal barrier may be used to thermally insulate the component from its environment.
Referring now to
The component article and hence the substrate 32 may comprise any of a variety of metals or metal alloys, including those based on nickel, cobalt and/or iron alloys or superalloys. In one embodiment, substrate 32 is made of a nickel-base alloy, and in another embodiment substrate 32 is made of a nickel-base superalloy. A nickel-base alloy has more nickel than any other element. The nickel-base superalloy can be strengthened by the precipitation of gamma prime or a related phase. In one example, the nickel-base superalloy has a composition, in weight percent, of from about 4 to about 20 percent cobalt, from about 1 to about 10 percent chromium, from about 5 to about 7 percent aluminum, from about 0 to about 2 percent molybdenum, from about 3 to about 8 percent tungsten, from about 4 to about 12 percent tantalum, from about 0 to about 2 percent titanium, from about 0 to about 8 percent rhenium, from about 0 to about 6 percent ruthenium, from about 0 to about 1 percent niobium, from about 0 to about 0.1 percent carbon, from about 0 to about 0.01 percent boron, from about 0 to about 0.1 percent yttrium, from about 0 to about 1.5 percent hafnium, balance nickel and incidental impurities.
For example, a nickel-base superalloy of interest is available by the trade name Rene N5, which has a nominal composition, by weight of 7.5% cobalt, 7% chromium, 1.5% molybdenum, 6.5% tantalum, 6.2% aluminum, 5% tungsten, 3% rhenium, 0.15% hafnium, 0.004% boron, and 0.05% carbon, with the balance nickel and minor impurities.
In accordance with one embodiment of the present invention, the bond coat 34 is predominantly of the beta (β) NiAl phase, with limited alloying additions. In one embodiment, the NiAl bond coat has an aluminum content of from about 17 to about 25 weight percent and in another embodiment, from about 18 to about 21 weight percent aluminum, balance being essentially nickel. The bond coat 34 may also contain one or more reactive elements, for example, zirconium and/or chromium, such as in the amount of from about 0.8 to about 1.2 weight percent zirconium and from about 5 to about 7 weight percent chromium, and in another embodiment, in an amount of from about 0.9 to about 1.1 weight percent zirconium and from about 5.5 to about 6.5 weight percent chromium.
According to commonly assigned U.S. Pat. No. 6,291,084 to Darolia et al., the presence of chromium in a beta-NiAl overlay coating has a significant effect on the spallation resistance of the ceramic layer 36 adhered to the NiAl bond coat 34 as a result of solid solution strengthening by chromium and precipitation strengthening from fine α—Cr phases dispersed within the beta phase of the coating 34.
In one embodiment, ceramic layer 36 is yttria-stabilized zirconia (YSZ), with a suitable composition being about 3 to about 10 weight percent yttria, though other ceramic materials could be used, such as yttria, nonstabilized zirconia, or zirconia stabilized by other oxides, such as magnesia (MgO), ceria (CeO2), scandia (Sc2O3) or alumina (Al2O3). The ceramic layer 36 is deposited to a thickness that is sufficient to provide the required thermal protection for the underlying substrate, generally on the order of from about 75 to about 350 microns. As with prior art TBC systems, the surface of the bond coat 34 oxidizes to form an oxide surface layer (scale) to which the ceramic layer 36 chemically bonds.
Referring now to
In a third step 60, the bond coat 34 is thereafter processed to achieve improved coating structure, i.e. coating density, by reducing the amount of porosity or voids in the coating. In general, two types of porosity or voiding occur in the coating structure, inter-particle voiding and macro-particle voiding. Inter-particle voiding are voids or defects in the coating structure from prior particle boundaries. Macro-particle voiding are voids or defects in the coating structure due to the presence of large macro particles. In one embodiment, prior to processing, a typical bond coat contains about 5% to about 10% porosity or voids. After processing in accordance with one embodiment of the present invention, the porosity of the bond coat 34 is reduced to less than about 2%.
The processing 60 may be accomplished by shot peening (sometimes termed “peening”). In this technique, the surface of the bond coat 34 is impacted with a flow of shot made of material that is hard relative to the bond coat 34, so that the bond coat 34 is deformed. In one embodiment, ceramic media shot is used. The ceramic media may comprise zirconia (ZrO2), silica (SiO2) and alumina (Al2O3). For example, a ceramic media of interest is available by the trade name Z850, which has a nominal composition, by weight of from about 60 to 70 weight percent ZrO2, from about 27 to about 33 weight percent SiO2 and less than about 10% Al2O3. In one example, the ceramic media has a diameter from about 0.008 to about 0.045 inches, and in another embodiment, from about 0.033 to about 0.045 inches. While spherical shaped ceramic media are typically used, media of other shapes may be used, if desired. In another embodiment, conditioned cut wire media is used. The conditioned cut wire media may comprise plain carbon or stainless steel shot. In one example, the conditioned cut wire media has a diameter from about 0.012 to about 0.94 inches.
In one embodiment, the bond coat 34 is peened with a shot material at a peening intensity of from about 9N to about 8 A, and in another embodiment, from about 9N to about 12N. If the peening intensity is too low, there is insufficient deformation to reduce the porosity. On the other hand, if the peening intensity is too great, there may be cracking or other damage to the bond coat 34 or to the underlying substrate 32. In one embodiment, coverage is in the range of from about 100% to about 1200%. Coverage describes the amount of surface that is peened. For example, 100% coverage describes once over the entire surface while 1200% describes 12 times over the entire surface of the peened article.
After the processing step 60, a fourth step 70 is performed by heat treating the bond coat 34 to enhance diffusion bonding between the coating structure and the substrate and increase the density of the bond coat 34. In one embodiment, a suitable heat treatment is to subject the bond coat 34 to a temperature of from about 1975° F. to about 2000° F. for a duration of from about 2 to about 4 hours in a vacuum, in another embodiment to a temperature of about 1975° F. for a duration of about four hours in a vacuum, and in yet another embodiment to a temperature of about 2000° F. for a duration of about 2 hours.
Thereafter, an optional fifth step 80 may be performed by depositing a ceramic thermal barrier layer 36 overlying the bond coat 34. The ceramic thermal barrier coating 34 may be deposited by any operable technique, for example, electron beam physical vapor deposition, or plasma spray.
Referring now to
The following example is given solely for the purpose of illustration and is not to be construed as limitations of embodiments of the present invention, as many variations of the invention, as many variations of the invention are possible without departing from the spirit and scope of embodiments of the invention.
In the example, the test samples are turbine blades made from a nickel-base superalloy, available by the trade name Rene N5.
A process of one embodiment of the invention is used to form a protective bond coating by cathodic arc deposition on test samples as shown in
While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of embodiments of this invention.