The present invention relates generally to wind turbine multi-panel blades and particularly to a bonding method for a wind turbine multi-panel blade and to a wind turbine multi-panel blade bonded using said method.
Wind turbines include a rotor that supports a number of blades extending radially therefrom for capturing the kinetic energy of the wind and causing a rotational motion of a driving train coupled to an electric generator for producing electrical power.
The amount of energy produced by wind turbines is dependent on the rotor blade sweeping surface that receives the action from the wind and consequently increasing the length of the blades leads normally to an increase of the power output of the wind turbine.
However, the size of the blades for land-based wind farms is presently limited to some extent by transportation and infrastructure requirements. In particular, the size of bridges and tunnels limit the size of the blade maximum chord.
To solve the transportation problems posed particularly by lengthy blades the prior art teaches the division of the blade in two or more longitudinal sections provided with joining means, so that each section may be manufactured individually and all sections may be assembled at the wind turbine site. Examples of this prior art are the following.
DE 3 109 566 discloses a wind turbine blade subdivided into at least two longitudinal sections which are held together by an expanding bolt.
U.S. Pat. No. 4,389,182 discloses a wind turbine blade subdivided into several longitudinal sections that are interconnected by tensioning members such as steel cables extending through the blade sections.
EP 1 244 873 A1 discloses a wind turbine blade subdivided into longitudinal sections that are joined by means of a butt joint comprising a number of clips arranged along the joint, having the respective ends fixed to the sections to be joined, and bolts for fixing said clips.
WO 2005/100781, WO 2006/103307, WO 2007/051879 in the name of the applicant, disclose wind turbine blades subdivided into longitudinal sections having improved joining means.
There is also prior art teaching the division of the blade in several transversal sections in addition or independently to the division in longitudinal sections. Examples of this prior are the following.
EP 1 184 566 A1 discloses a wind turbine blade which is formed by assembling one, two or more longitudinal sections, each of which comprises a core formed by a longitudinal carbon-fibre tube on which a series of carbon fibre or fiberglass cross ribs are mounted and a cover formed by fiberglass or carbon-fibre joined to said ribs.
WO 01/46582 A2 discloses a wind turbine blade having a plurality of segmented elements attached to a load transmitting box spar and separated by elastic joins which enable the segments to move in relation to one another in order to minimize the tensile stress in the region of the blade in which the segments are located.
EP 1 965 074 in the name of the applicant discloses a wind turbine blade composed of two cap prefabricated panels and two web prefabricated panels placed side by side in a box shape and at least two shell longitudinal sections forming, respectively, the leading edge and the trailing edge of the corresponding blade section that are placed adjacently to a central spar section, the aerodynamic profile of the blade being defined by said cap panels and said shell panels.
One known method for bonding blade components of segmented blades such as those above-mentioned is an adhesive bonding. The typical technique for the application of the adhesive in one surface of said components is distributing the adhesive from a container to which is pumped from a mixing machine in which the dosage of the components of the adhesive is made and controlled.
This process has several drawbacks: it requires very demanding application times, the workers who perform the operation need protective equipment and a correct application on the bonding surface is difficult. On the other hand, said process involves the use of an excess of adhesive and therefore an increase of weight and cost.
The current trend in the wind industry to big rotor blades demands new rotor blades designs suitable for complying with the transportation requirements and with the quality manufacturing requirements involved by blades that can reach lengths of 100 m and chords of 8 m so there is a particular demand for improving the adhesive unions of segmented blades.
The present invention is intended to satisfy said demand.
An object of the present invention is to provide a method for bonding prefabricated parts of a wind turbine blade that allows the control of the volume of the adhesive material and consequently a weight reduction.
Another object of the present invention is to provide a method for bonding prefabricated parts of a wind turbine blade that facilitates the application of the adhesive material on the bonding areas.
In one aspect these and other objects are met by a method for bonding a first and a second prefabricated parts of a wind turbine blade comprising the steps of:
In preferred embodiments the adhesive material used for disposing said bands is provided in one of the following formats: tape, strip, roll. Therefore it is used an adhesive material in a format that facilitates its application on the bonding surfaces as well as a full control of its weight.
In preferred embodiments the adhesive material used for disposing said bands is provided in blocks. Therefore it used an adhesive material in a format fully adapted for its application in bands.
In preferred embodiments, the adhesive material has a consistence in the uncured state that allows that said bands maintain its original geometry when they are not subjected to a pressure and that the height of said bands is reduced in a proportion comprised between the 25%-95% (preferably 50%-95%) of the original height when they are subjected to a pressure comprised between 0.05 and 2 MPa. Therefore it is used an adhesive material with the consistence needed for, on the one side, allowing its application in a semi-solid state and, on the other side, controlling its flow during the curing stage on the typical conditions where the bonding of prefabricated parts of a wind turbine blade takes place.
In preferred embodiments, the shear adhesion of said adhesive material in the cured state is greater than 15 MPa. Therefore it is used an adhesive material with the required shear adhesion for bonding prefabricated parts of a wind turbine blade.
In preferred embodiments, said predetermined conditions of pressure and temperature are the following: the pressure is comprised between 0.05 and 2 MPa and the temperature is comprised between 40° C. and 100° C. These are the typical conditions for bonding prefabricated parts of a wind turbine blade so that the method according to the invention does not need any special equipment.
In preferred embodiments said adhesive material is a one-component adhesive material selected among one of the following: polyurethane, epoxy resins, vinyl esters or methacrylate. Hereby it is achieved a bonding method using well-known adhesive components.
In preferred embodiments the dimensions of said bands in the uncured state are: a width comprised between 30-150 mm, a height comprised between 2-40 mm and a separation between traces comprised between 20-300 mm. Therefore the method is applicable for bonding prefabricated parts of wind turbine blades of very different dimensions.
In preferred embodiments for bonding a first part belonging to an spar of the blade and a second part belonging to a shell of the blade, the dimensions of said bands in the uncured state are the dimensions mentioned in the preceding paragraph.
In preferred embodiments for bonding panels of an spar of the blade or for bonding shells of a blade, said bands have a width comprised between 30-150 mm, a height comprised between 2-25 mm and a separation between traces comprised between 20-50 mm.
The invention also refers to the use of the above-mentioned method for bonding prefabricated parts of a wind turbine blade and to a wind turbine blade comprising at least two prefabricated parts bonded using the above-mentioned method, whether if they belong to one module of the blade or if they belong to the whole blade.
Other features and advantages of the present invention will be understood from the following detailed description in relation with the enclosed drawings.
a shows in a schematic perspective view the main components of the inboard module of a wind turbine blade split in two modules.
b shows in a schematic perspective view the main components of the spar of said inboard module.
a,
3
b;
5
a,
5
b;
7
a,
7
b are, respectively, schematic plan and cross-sectional views by the plane A-A of the initial state of an adhesive bonding between two components of said inboard module according to three embodiments of this invention.
a,
4
b;
6
a,
6
b;
8
a,
8
b are, respectively, schematic plan and cross-sectional views by the plane A-A of the final state of an adhesive bonding between two components of said inboard module according to three embodiments of this invention.
In a multi-panel wind turbine blade, the whole blade may be split into, for example, an outboard and an inboard modules and each of them in several prefabricated parts for an assembly on site or in a factory.
As illustrated in
All those spar single components are prefabricated and then assembled bonding the flanges 31, 33 of said components.
In a further step the inboard module is assembled bonding the prefabricated upper and lower shells 17, 19 to the spar 15 and bonding the borders of the upper and lower shells 17, 19.
In this inboard module there are therefore three different bonding areas: the bonding areas 41 in the flanges 31, 33 of the spar components, the bonding areas 51 between the spar caps 21, 23 and, respectively, the upper and lower shells 17, 19 and the bonding areas 61 between the borders of the upper and lower shells 17, 19.
Other multi-panel wind turbine blade configurations does not necessarily have the same three bonding areas. Therefore in the following we will refer separately to said bonding areas 41, 51, 61 and the skilled man will easily understand which of them would be applicable to any particular wind turbine blade configuration.
The basic idea of the present invention is using an adhesive material that:
In general terms it is considered that for the different bonding areas of a wind turbine blade, said bands shall have a width W comprised between 30-150 mm, a height H comprised between 2-40 mm and a separation S1 between traces comprised between 20-300 mm.
In embodiments of the present invention an adhesive bonding in the bonding area 41 between, for instance, the upper cap 21 and the trailing edge web 27 is carried out disposing bands 45 of an adhesive material in a manageable uncured state following traces 43 signaled on the bonding area 41 of the trailing edge web 27 with a separation S1 between them as shown in
In a particular embodiment of this invention for said bonding areas 41 between spar components, the bands 45, having a width W comprised between 30-150 mm and a height H comprised between 2-25 mm, have been disposed on the bonding area 41 with a separation S1 between the traces 43 comprised between 20-50 mm. After the bonding process, the width is increased in approximately a 50% and the height is decreased in approximately a 50%. These results show that using an adhesive of a suitable fluency the final shape of the adhesive bands can be controlled avoiding the typical losses of the known adhesive unions.
In embodiments of the present invention an adhesive bonding in the bonding area 51 between, for instance, the upper shell 17 and the upper cap 21 is carried out disposing bands 55 of an adhesive material in a manageable uncured state following traces 53 signaled on the bonding area 51 of the upper cap 21 with a separation S1 between them as shown in
In the case shown in
In embodiments of the present invention an adhesive bonding in a bonding area 61 between, for instance, the leading edge of the upper shell 17 and the leading edge of the lower shell 19 will be carried out in a similar manner to the bonding area 41 between spar components.
Although the present invention has been fully described in connection with preferred embodiments, it is evident that modifications may be introduced within the scope thereof, not considering this as limited by these embodiments, but by the contents of the following claims.