Patent Application
20190202190
This application claims all benefits accruing under 35 U.S.C. § 119 from China Patent Application No. 201711465821.2, filed on Dec. 28, 2017, in the China Intellectual Property Office, the contents of which are hereby incorporated by reference. The application is also related to copending applications entitled, “DOUBLE-SIDED TAPE WITH EXTENDED TEMPERATURE RANGE”, filed ______ (Atty. Docket No. US72473). The application is also related to copending applications entitled, “BONDING METHOD OF FIXING AN OBJECT TO A ROUGH SURFACE”, filed ______ (Atty. Docket No. US72472)
The present disclosure relates to a bonding method, and more particularly, relates to a bonding method using a carbon nanotube structure.
In conventional bonding methods, double-sided tape or adhesive is used for bonding and fixing objects. However, an application temperature range of conventional bonding methods is narrow, viscosity of the double-sided tape or adhesive used in conventional bonding methods is significantly reduced or even lost at high temperatures or at low temperatures.
Implementations of the present technology will now be described, by way of example only, with reference to the attached figures, wherein:
The disclosure is illustrated by way of example and not by way of limitation in the figures of the accompanying drawings in which like references indicate similar elements. It should be noted that references to “another,” “an,” or “one” embodiment in this disclosure are not necessarily to the same embodiment, and such references mean “at least one.”
It will be appreciated that for simplicity and clarity of illustration, where appropriate, reference numerals have been repeated among the different figures to indicate corresponding or analogous elements. In addition, numerous specific details are set forth in order to provide a thorough understanding of the embodiments described herein. However, it will be understood by those of ordinary skill in the art that the embodiments described herein can be practiced without these specific details. In other instances, methods, procedures, and components have not been described in detail so as not to obscure the related relevant feature being described. Also, the description is not to be considered as limiting the scope of the embodiments described herein. The drawings are not necessarily to scale, and the proportions of certain parts have been exaggerated to better illustrate details and features of the present disclosure.
Several definitions that apply throughout this disclosure will now be presented.
The term “substantially” is defined to be essentially conforming to the particular dimension, shape, or other feature which is described, such that the component need not be exactly or strictly conforming to such a feature. The term “comprise,” when utilized, means “include, but not necessarily limited to”; it specifically indicates open-ended inclusion or membership in the so-described combination, group, series, and the like.
Referring to
step (S1), providing a first object 10 comprising a first surface 100 and a second object 20 comprising a second surface 200;
step (S2), laying a carbon nanotube structure 30 on and in direct contact with the first surface 100, wherein the carbon nanotube structure 30 comprises a super-aligned carbon nanotube film. The super-aligned carbon nanotube film comprises a plurality of carbon nanotubes, each of the plurality of carbon nanotubes extends substantially along a same direction, and an extending direction is substantially parallel to a surface of the super-aligned carbon nanotube film, the first surface, and the second surface;
step (S3), laying the second object 20 on and in direct contact with the carbon nanotube structure 30, wherein the carbon nanotube structure 30 is located between the first object 10 and the second object 20; and
step (S4), applying a pressure to the first object 10 and the second object 20, to make the first object 10 and the second object 20 bonded together and form a three-layer structure.
In step (S1), the material and the shape of the first object 10 and the second object 20 are not limited. Examples of the shape of the first object 10 and the second object 20 comprise cube, cuboid, cone, and cylinder. Examples of the material of the first object 10 and the second object 20 can comprise glass, quartz, silicon, and polyethylene (PET). Both the first surface 100 and the second surface 200 can be a flat surface or a curved surface. The shape of the second object 20 and the shape of the first object 10 can be the same or different. The material of the second object 20 and the material of the first object 10 can be the same or different. In one embodiment, both the first object 10 and the second object 20 are square silicon wafers having a side length of 7 mm.
The carbon nanotube structure 30 bonds with the first surface 100 and the second surface 200 only by van der Waals force. If the first surface 100 and the second surface 200 are too rough, such as the surface roughness of the first surface 100 and the second surface 200 being larger than 1.0 micrometer, or the first surface 100 and the second surface 200 being contaminated and not clean, then the van der Waals force between the carbon nanotube structure 30 and the first surface 100 and the van der Waals force between the carbon nanotube structure 30 and the second surface 200 is decreased. The adhesion between the carbon nanotube structure 30 and the first surface 100 and the adhesion between the carbon nanotube structure 30 and the second surface 200 thus decreases. In all embodiments, the first surface 100 and the second surface 200 are clean and smooth surfaces. The phrase “clean and smooth surfaces” refers the surfaces being substantially free of impurities, dust and the like, and having a small surface roughness. In one embodiment, both the first surface 100 and the second surface 200 have the surface roughness less than or equal to 1.0 micrometer. In one embodiment, both the first surface 100 and the second surface 200 have the surface roughness less than or equal to 500 nanometers. In one embodiment, both the first surface 100 and the second surface 200 have the surface roughness less than or equal to 100 nanometers. When the first surface 100 and the second surface 200 are clean surfaces and the surface roughness is less than or equal to 1.0 micrometer, the van der Waals force between the carbon nanotube structure 30 and the first surface 100 and the van der Waals force between the carbon nanotube structure 30 and the second surface 200 are large, therefore, there is greater adhesion between the carbon nanotube structure 30 and the first surface 100 and between the carbon nanotube structure 30 and the second surface 200.
In step (S2), referring to
In one embodiment, the plurality of carbon nanotubes is pure carbon nanotubes. The pure carbon nanotubes mean that the carbon nanotubes are not modified by physical or chemical methods, there are few or no impurities adhered on surfaces of the carbon nanotubes, and a purity of the carbon nanotubes is better than or equal to 99.9%. Therefore, the bonding method has substantially no environmental effects. Since the plurality of carbon nanotubes is pure carbon nanotubes, and a specific surface area of each of the plurality of carbon nanotube is very large, the super-aligned carbon nanotube film has strong viscosity. The carbon nanotube structure 30 thus has strong viscosity, therefore, the first object 10 and the second object 30 can be strongly bonded together by the bonding method.
The super-aligned carbon nanotube film is a free-standing film. The term ‘free-standing’ means films that do not have to be supported by a substrate, and can be self-supporting to maintain a film shape. Therefore, the carbon nanotube structure 30 comprising the super-aligned carbon nanotube film can be directly laid on the first surface 100.
Referring to
In one embodiment, the carbon nanotube structure 30 consists of one super-aligned carbon nanotube film. The method of laying the carbon nanotube structure 30 on and in direct connect with the first surface 100 comprises step (S21), providing a super-aligned carbon nanotube array and step (S22), drawing the super-aligned carbon nanotube film from the super-aligned carbon nanotube array, and directly laying the super-aligned carbon nanotube film on the first surface 100 without any other steps of treating the super-aligned carbon nanotube film. For example, after drawing the super-aligned carbon nanotube film from the super-aligned carbon nanotube array and before laying the super-aligned carbon nanotube film on the first surface 100, the super-aligned carbon nanotube film is not chemically or physically treated.
The step (S22) comprises step (S221), of selecting, a plurality of carbon nanotube segments with a certain width from the super-aligned carbon nanotube array; and step (S222), of stretching, the plurality of carbon nanotube segments substantially perpendicularly to a growth direction of the super-aligned carbon nanotube array at a certain speed, to obtain the super-aligned carbon nanotube film, and directly laying the super-aligned carbon nanotube film on the first surface 100 without any other steps of treating the super-aligned carbon nanotube film.
The carbon nanotube structure 30 may comprise at least two super-aligned carbon nanotube films. The step (S22) further comprises step (S223) of laying, at least one super-aligned carbon nanotube film on the super-aligned carbon nanotube film obtained in step (S222), and overlapping the at least one super-aligned carbon nanotube film in parallel to the super-aligned carbon nanotube film in step (S222).
In one embodiment, the method of laying the carbon nanotube structure 30 on the first surface 100 comprises providing a support structure and drawing at least one super-aligned carbon nanotube film from the super-aligned carbon nanotube array. The at least one super-aligned carbon nanotube film is laid on the support structure, to form the carbon nanotube structure 30 and transferring the carbon nanotube structure 30 from the support structure to the first surface 100. The support structure can be a substrate or a frame structure. In one embodiment, the support structure is the frame structure, the carbon nanotube structure 30 is partially suspended to form a suspended portion. The transferring of the carbon nanotube structure 30 from the support structure to the first surface 100 comprises directly placing the suspended portion on the first surface 100 and then removing the frame structure.
The plurality of carbon nanotubes of the super-aligned carbon nanotube array are pure. In one embodiment, a length of each of the plurality of carbon nanotubes in the super-aligned carbon nanotube array is longer than 300 micrometers.
A method for making the super-aligned carbon nanotube array can be a chemical vapor deposition (CVD) method, an arc discharge preparation method, or an aerosol preparation method. In one embodiment, the super-aligned carbon nanotube array is obtained by the chemical vapor deposition (CVD) method. The chemical vapor deposition (CVD) method comprises the steps of (a) providing a substrate, in which the substrate can be selected from the group consisting of a P-type silicon substrate, an N-type silicon substrate, and a silicon substrate formed with an oxide layer. Then (b) forming a catalyst layer on a surface of the substrate, in which a material of the catalyst layer can be selected from the group consisting of iron (Fe), cobalt (Co), nickel (Ni) and alloy of any combination thereof. Step (c) is annealing the substrate with the catalyst layer in air at 700° C. to 900° C. for about 30 minutes to 90 minutes and (d) disposing the substrate in a reaction chamber. The reaction chamber is heated in protective gas to 500° C.˜740° C., and a carbon source gas is introduced into the reaction chamber for about 5 minutes to about 30 minutes. The super-aligned carbon nanotube array is grown from the substrate. A height of the carbon nanotube of the super-aligned carbon nanotube array is ranged from about 200 micrometers to about 400 micrometers. The carbon source gas can be chemically active hydrocarbons, such as acetylene. The protective gas can be nitrogen, ammonia, or an inert gas.
In one embodiment, in step (S2), after drawing the super-aligned carbon nanotube film from the super-aligned carbon nanotube array and before directly laying the super-aligned carbon nanotube film on the first surface 100, the super-aligned carbon nanotube film is stretched along the extending direction of the plurality of carbon nanotubes of the super-aligned carbon nanotube film. In some embodiments, a length of the stretching is from about 1 millimeter to about 3 millimeters. In one embodiment, the stretch length is about 3 millimeters. The step of stretching the super-aligned carbon nanotube film can make the extension directions of the randomly aligned carbon nanotubes consistent with the extension direction of the majority of the carbon nanotubes in the super-aligned carbon nanotube film, thereby smoothing the surface of the super-aligned carbon nanotube film.
Referring to
The number of the super-aligned carbon nanotube films of the carbon nanotube structure 30 can be selected according to actual needs. In one embodiment, the carbon nanotube structure 30 comprises 5 to 30 layers of the super-aligned carbon nanotube films overlapped and paralleled with each other. In one embodiment, the carbon nanotube structure 30 comprises 10 to 15 layers of the super-aligned carbon nanotube films overlapped and paralleled with each other. In another embodiment, the carbon nanotube structure 30 comprises 10 layers of the super-aligned carbon nanotube films overlapped and paralleled with each other.
Referring to
In step (S4), a magnitude of the pressure is selected according to the volume of the first object 10 and the second object 20, the area of the first surface 100 and the second surface 200, and the like. In one embodiment, the amount of the pressure ranges from about 10 N/cm2 to 20 N/cm2. In one embodiment, the amount of the pressure is about 20 N/cm2.
Referring to
In one embodiment, after step (S4), further comprises step (S5) cooling the three-layer structure to about −196° C.˜−100° C.
In one embodiment, after step (S4), further comprises step (S5) heating the three-layer structure to about 800° C.˜1000° C.
In one embodiment, the carbon nanotube structure 30 includes at least one super-aligned carbon nanotube film, and the super-aligned carbon nanotube film consists of a plurality of carbon nanotubes. The plurality of carbon nanotubes extend substantially along a same direction and are joined end-to-end by van der Waals force.
In one embodiment, the carbon nanotube structure 30 includes a plurality of carbon nanotubes. The plurality of carbon nanotubes are joined end-to-end by van der Waals force and extends substantially along a same direction. An extending direction of the plurality of carbon nanotubes is parallel to a length direction of the carbon nanotube structure 30. The plurality of carbon nanotubes can be pure carbon nanotubes. The pure carbon nanotubes mean that carbon nanotubes are not modified by physical or chemical processes, there being few or no impurities adhered on surface of the carbon nanotubes, and a purity of the carbon nanotubes is better than or equal to 99.9%.
The carbon nanotube structure 30 bonds the first object 10 and the second object 20 together only by van der Waals force. Van der Waals force is little affected by temperature, the carbon nanotube structure 30 used in the bonding method still has excellent viscosity at high and low temperatures. Furthermore, the absence or almost complete absence of impurities adhered on surfaces of the plurality of carbon nanotubes of the carbon nanotube structure 30, such as amorphous carbon or residual catalyst metal particles, gives high thermal stability to the carbon nanotube structure 30. The carbon nanotube structure 30 does not readily oxidized even at a high temperature. Therefore, the bonding method can be implemented at high and low temperatures. In one embodiment, the bonding method is performed at a temperature from about −196° C. to about 1000° C. Referring to
In the bonding method, the carbon nanotube structure 30 bonds the first object 10 and the second object 20 together only by van der Waals force. When the first object 10 and the second object 20 need to be separated, only a small force, without heating or dissolving with solvent, is required. The carbon nanotube structure 30 can be removed from the first surface 100 and the second surface 200 without causing damage to the first surface 100 and the second surface 200 during or after the separation. A position for bonding can be adjusted in the bonding method.
It is to be understood that the above-described embodiments are intended to illustrate rather than limit the present disclosure. Variations may be made to the embodiments without departing from the spirit of the present disclosure as claimed. Elements associated with any of the above embodiments are envisioned to be associated with any other embodiments. The above-described embodiments illustrate the scope of the present disclosure but do not restrict the scope of the present disclosure.
Depending on the embodiment, certain of the steps of a method described may be removed, others may be added, and the sequence of steps may be altered. The description and the claims drawn to a method may include some indication in reference to certain steps. However, the indication used is only to be viewed for identification purposes and not as a suggestion as to an order for the steps.