Patent Application
20170334147
The invention is in the fields of mechanical engineering and construction, especially mechanical construction, for example automotive engineering, aircraft construction, shipbuilding, machine construction, toy construction etc.
In the automotive, aviation and other industries, there has been a tendency to move away from steel constructions and to use lightweight material such as aluminum or magnesium metal sheets or polymers, such as carbon fiber reinforced polymers or glass fiber reinforced polymers or polymers without reinforcement, for example polyesters, polycarbonates, etc. instead.
The new materials cause new challenges in bonding elements of these materials—especially in bonding flattish object to another object.
To meet these challenges, the automotive, aviation and other industries have started heavily using adhesive bonds. Adhesive bonds can be light and strong but suffer from the disadvantage that there is no possibility to long-term control the reliability, since a degrading adhesive bond, for example due to an embrittling adhesive, is almost impossible to detect without entirely releasing the bond.
FR 1 519 111 teaches a method of fastening a screw or similar fixation element to a thermoplastic body by applying high-frequency vibration to it to displace thermoplastic matter and cause it to flow in an interior cavity of the fixation element. U.S. Pat. No. 5,271,785, FR 2,112,523, U.S. Pat. No. 3,184,353, U.S. Pat. No. 3,654,688, and GB 1,180,383 teach securing a metallic body to a thermoplastic body by bringing the bodies into contact and subjecting the metallic body to mechanical vibration until thermoplastic material of the thermoplastic body liquefies, the metallic body is essentially fully enwrapped in the thermoplastic body, and thermoplastic material flows into recesses of the metallic body. All of these methods are suitable only for anchoring a metallic part in a deep thermoplastic object, and the required energy input and corresponding impact on the parts to be connected is substantial.
US 2010/0079910 teaches manufacturing an electronic device with a plastic housing part and a metallic housing part, wherein the plastic housing part is attached to the metallic housing part by an ultrasonic bond. The applications of the concept taught in US 2010/0079910 are limited.
A further concept of prior art approaches includes shaping the thermoplastic body to include a flange-like protrusion into which a fastening element, such as a nut, is pressed. This concept, however, has the disadvantage of being more complex, as shaping plastic parts that otherwise may have a simple, for example sheet-like, form with a flange, which depending on the application needs to have a precisely defined position, may drastically increase the manufacturing cost.
It is an object of the present invention to provide a method of bonding two objects together, the method overcoming drawbacks of prior art methods and being especially suited for bonding a second object to a first object of a polymer-based material. It is a further object to provide equipment for carrying out the method.
According to an aspect of the invention, a method of bonding a second object to a first object, the method including the steps of:
The liquefaction of the flow portion in this is primarily caused by friction between the vibrating second object and the surface of the first object, which friction heats the first object superficially.
A special property of the approach according to many embodiments of the invention is therefore also that the flow portion that has been generated in a contact zone between the first and second objects may immediately flow into existing cavities of the second object, and thereby the zone that is influenced by the heat generated during the process remains small, for example essentially restricted to the intermixing zone.
The flow behavior of the flow portion will be influenced by the fact that due to the approach according to the present invention, a material flow is generated towards the surface of the non-liquefiable material (i.e. the second object; convergent flow), to which surface, by the vibrations and friction, heat is continuously supplied. Thus, generally little heat will flow away. Therefore, a large penetration depth of thermoplastic material into the coupling structures becomes achievable even after a short process time, the flow not being stopped by heat loss of liquefied material coming into contact with cold spots. This is in contrast for example to the “Woodwelding” process as, for example, described in WO 98/42988 where there is a divergent flow by liquefied material flowing away from the interface zone and thus transporting heat away into structures that have remained cold.
The first and second objects are construction components (construction elements) in a broad sense of the word, i.e. elements that are used in any field of mechanical engineering and construction, for example automotive engineering, aircraft construction, shipbuilding, building construction, machine construction, toy construction, etc. Generally, the first and second objects will both be artificial, man-made objects, and at least the first object will include artificial material; the additional use of naturally grown (non-living matter) material, such as wood-based material, in the first and/or second object is not excluded.
The materials of the first object and of the second object may be homogeneous or inhomogeneous. For example, the first object may have the thermoplastic material and in addition include other, non-liquefiable material, and/or it may have a plurality of layers of thermoplastic material of different compositions. Similarly, the second object may include different portions of different materials, as explained in more detail hereinafter. Additionally or as an alternative, in embodiments, the second object may be caused to penetrate through a plurality of objects (the first object plus at least one further object) to secure the plurality of objects to each other, as also explained in more detail hereinbelow.
The coupling-in structure may be a coupling-in face, especially constituted by a proximal-most end face, with or without guiding structures (such as a guiding hole for an according protrusion of the tool), for a separate sonotrode that serves as the tool. In alternative embodiments, the coupling-in structure may include a coupling that couples the second object directly to a vibration generating apparatus, which vibration generating apparatus then serves as the tool. Such a coupling may for example be by a thread or a bayonet coupling or similar. Thus in these embodiments, the second object is at the same time a sonotrode coupled to a vibration generating apparatus.
In other embodiments, the tool is a sonotrode fastened to a vibration generating apparatus. Sonotrodes of this kind are for example known from ultrasonic welding.
In even further embodiments, the tool may be an intermediate piece (different from the first object), against which intermediate piece a sonotrode presses and which is of a material that does not liquefy under the conditions that apply during the process. Generally, the approach according to aspects of the invention excludes that the vibrations are coupled into second object only via first object; rather a physical contact between the second object and the vibrating tool is required.
The flow portion of the thermoplastic material is the portion of the thermoplastic material that during the process and due to the effect of the mechanical vibrations is caused to be liquefied and to flow.
The coupling structures of the second object are of a material that is not liquefiable. As explained in more detail hereinafter, this definition includes the possibility that the material is liquefiable at a substantially higher temperature than the material of the first object, such as a temperature higher by at least 50°. In addition or as an alternative, the condition may hold that at a temperature at which the first object's thermoplastic material is flowable, the viscosity of the material of the second object is higher than the viscosity of the thermoplastic material of the first object by orders of magnitude, for example by at least a factor between 103 and 105. In addition or as an alternative to including a different liquefiable matrix material with a different liquefaction temperature and/or different glass transition temperature, this can also be achieved by a higher filling grade of for example a fiber filler.
Coupling structures may include sequences of radial protrusions and indentations (such as ribs/grooves), an open porous foam-like structure, openings open to the distal side, which openings define an undercut by being widened, at least into one lateral direction, towards a proximal side, etc. Any structure that defines an undercut with respect to axial directions is suitable.
In coupling structures that include sequences of radial protrusions and indentations (for example around an outer surface of a portion of the second object or along an interior surface of the second object), d depth of the intermixing zone may be defined as radial depth into which the flow portion penetrates starting at outermost protrusions, In coupling structures that include an open porous structure, the depth of the intermixing zone may be defined as the depth of the open porous structure into which the thermoplastic material penetrates starting at the surface of the open porous structure, measured perpendicularly thereto. Similarly, in coupling structures that include openings open to the distal side the depth of the intermixing zone may be defined as the depth into which the thermoplastic material penetrates starting at the distally facing surface.
Especially, in embodiments the mechanical vibration transmitting parts of the second object consist of metal and/or other hard materials (glasses, ceramics, etc.) and/or thermosetting plastics and/or thermoplastics that remain below their glass transition temperature during the entire process.
In a special group of embodiments, the second object includes a second thermoplastic material having a liquefaction temperature substantially higher than the liquefaction temperature of the first object thermoplastic material. Then, after the step of causing a flow portion of the thermoplastic material of the first object is liquefied, the second object may be pressed against a support or a non-liquefiable portion of the first object while coupling vibrations into the second object is continued (with a same or a higher or possibly even a lower intensity than initially) until a second flow portion of the second thermoplastic material is liquefied and leads to a deformation of the second object. Especially, this further method step may be carried out as described in WO 2015/117253, incorporated herein by reference, until a foot portion and/or a head portion of the second object is created for bonding the first and second objects together by an additional rivet effect.
While embodiments of this special group of embodiments include the second object, after the bonding process, reaching through the first object to the distal side, in an alternative group of embodiments the distal side is left intact, i.e. an intermixing zone that includes portions of the first and second objects does not reach to the distal side.
In embodiments, the second object is anchored in a depth-effective manner by providing the second object with an anchoring portion that extends along the anchoring axis, optionally with structure elements that are arranged on a peripheral surface of the second object and/or along an inner surface of an axially extending portion of the second object.
In embodiments, especially the penetration depth, by which the second objects penetrates into the first object, i.e. the axial extension of those parts of the second object that penetrate into the first object, is larger (for example substantially larger) than a depth of the intermixing zone, i.e. the zone in which both, portions of the first and second object are present after the bonding process. In other words, in these embodiments including depth-effective anchoring, a width of the one part of the second object that penetrates into the first object in at least one lateral dimension, and often in both lateral dimensions, is smaller than the penetration depth by which the second object penetrates into the first object. The depth of the intermixing zone is then defined as the characteristic depth of the structure elements on the peripheral surface, i.e., a depth measured perpendicular to the anchoring axis.
Embodiments of a group include, in addition or as an alternative to including depth-effective anchoring, a bonding surface with a plurality of structure elements that are spaced laterally from each other and/or possibly form an extended, for example circumferential, groove, the bonding surface following a surface portion of the first object. For example, if the first object is planar, the structure elements will extend along a plane.
Embodiments, for example embodiments that include a depth-effective anchoring, may include providing a bore in the first object prior to the step of pressing, and in the step of pressing, a part of the second object is pressed into the bore. In this, a bore diameter is preferably chosen to be less than an outer diameter of the part pressed into the bore. Such a bore may be a blind hole or a through bore. Also anchoring in other indentations such as grooves etc. is possible.
A through bore may also be advantageous in embodiments, in which the second object is comparably thin, such as a thermoplastic sheets. The method of bonding a second object to the first object may then include lining the through bore with the second object, for example for the purpose of fastening a further object thereto, to serve as a feedthrough, serve as barrier that is crossable under pre-defined conditions only (as is the case for a septum or for a second object with a removable cover or similar) or have another purpose. In embodiments of this special category, the thickness of the first object may correspond to 2-40 times or 2-20 times, especially between 3 times and 10 times the interpenetration depth (depth of the intermixing zone).
In accordance with an even further group of embodiments, the bonding is carried out in a “planar bond” or “flattish bond” manner, with a comparably small penetration depth. This group of embodiments may especially be suited also for bonding a second object to a first object that is comparably thin or that is sensitive to damages or has high requirements for leaving other surfaces than the one to which the second object is bonded intact.
In embodiments of this group, the second object includes a plurality of structure elements for the liquefied material to flow into, which structure elements are spaced laterally from each other, i.e. extend along a plane which during the anchoring is parallel to a surface plane of the first object or, if the case may be, extend along another, non-planar surface of the first object. Especially, the bond between the first and second object may be a planar bond, wherein the area of the interface between the first and second object is essentially parallel to the surface plane of the first object and has, at least in one dimension, preferably in both in-plane dimensions, substantially greater than the penetration depth, for example greater by at least a factor 2 or 3, at least a factor 5, or at least a factor 10. In this, the penetration depth may be equal to the depth of the intermixing zone or may be smaller than the latter.
Embodiments that include bonding with a small penetration depth compared to the depth of the intermixing zone may also include bonding of the second object to a not planar surface portion of the first object. For example, the first object may have a certain proximally facing surface contour, and the second object may have an overall shape following this contour or may be deformable to do so.
Alternatively, the first object may have a countersunk or opening or opening provided with another structure along its periphery, wherein the second object has an accordingly adapted (for example conical if the opening is countersunk) shape. In embodiments where the first object is comparably thin and there are requirements for the distal surface, the structure elements of the second object may in such embodiments adapted to the depth. Especially, the relative sizes of the structure elements may decrease towards distally, so that their capacity to accommodate flowable material decreases towards the distal side, and accordingly does the heat impact.
In embodiments, a design criterion is that the volume of structure elements (such as indentations or pores) into which the liquefied material can flow is larger than the displaced volume. This leads to a criterion for embodiments of the invention according to which along the surface parts that include the coupling structures the porosity is at least 50% for a certain depth. The porosity here is defined as a fraction that empty spaces take up of the total volume, measured from an outer convex hull to a certain depth (corresponding to a depth of the intermixing zone, measured in axial direction); it may apply also to macroscopic structures that are not necessarily viewed as “pores”. If this optional design criterion is fulfilled, no volume has to be displaced to the surface or sideways or similar.
More in general, in embodiments, the method may include causing the flow portion to flow into the indentations and/or pores and preventing the flow portion from flowing to regions laterally of the second object.
To this end, optionally, in addition to providing an indentation/pore volume satisfying the above condition, the method may also include pressing a (non-vibrating) retaining device against proximal surface of the first object in a vicinity of the second object, for example around the interface between the first and second objects. Such a retaining device may prevent bulges or the like around the location where the second object is anchored in the first object.
In embodiments of this group of “planar bond” or other “flattish bond” anchoring, the second object in addition to cavities (indentations/pores) includes a distal protruding structure that may for example serve as energy director. Especially, such distal protruding structure may have a shape with a portion that tapers towards the distal side, for example ending in a tip or edge or rounded distal end. In this case, a lateral distance between the distal protruding structure and the cavity accommodating the flow portion may be minimal. Especially, any spacing between such distal protruding structure and the cavity may be avoided, so that the overall shape of the second object at the distal surface is undulated between the distal protrusion and cavity.
In embodiments of all groups described hereinbefore, the coupling structures that include an undercut with respect to axial (proximodistal) directions and thereby make a positive-fit connection possible, are pre-manufactured properties of the second object.
In addition or as an alternative, the second object may include a deformable portion, and the method may include making a structure for a positive-fit connection during the process of pressing the second object against the first object while mechanical vibrations are coupled into the second object.
For example, the second object may include a plurality of deformable legs or a deformable collar extending in a substantially axial direction as a deformable structure. During the process, the deformable structure is bent away from the axial direction so that after re-solidification an undercut is formed.
Embodiments using this principle of deformation may feature the advantage that the effective anchoring area may, due to the deformation, be larger than the surface area portion of the first object penetrated by the second object, i.e. the footprint may be enlarged compared to an embodiment without the deformation.
A further possible advantage is that, for example, a lightweight deformable material may be used for the deformable portion. Especially, a material may be used that is deformable at the temperature at which the process takes place but that exhibits substantial stiffness at room temperature (or, more generally, the temperature at which the assembly will be used). For example, the deformable portion may be of a thermoplastic material with a glass transition temperature that is substantially higher than the glass transition temperature of the first object thermoplastic material of which the flow portion is formed.
In a specific embodiment, of this principle, PBT (Polybutylene terephthalate) was used as the first object thermoplastic material, which material becomes flowable at temperatures of about 180° C., and PEEK was used as a material of the second object's portion that includes the deformable portion. PEEK is not liquid/flowable at 180° C. but is above its glass transition temperature (being about 140° C.).
More in general, in embodiments in which the deformable portion includes a thermoplastic material, it may be advantageous if the glass transition temperature of the deformable portion is between the glass transition temperature of the first object thermoplastic material and the temperature at which the thermoplastic material becomes sufficiently flowable.
In this text, the liquefaction temperature or the temperature at which a thermoplastic material becomes flowable is assumed to be the melting temperature for crystalline polymers, and for amorphous thermoplastics a temperature above the glass transition temperature at which the becomes sufficiently flowable, sometimes referred to as the ‘flow temperature’ (sometimes defined as the lowest temperature at which extrusion is possible), for example the temperature at which the viscosity drops to below 104 Pa*s (in embodiments, especially with polymers substantially without fiber reinforcement, to below 103 Pa*s).
For applying a counter force to the pressing force, the first object may be placed against a support, for example a non-vibrating support. According to a first option, such a support may include a supporting surface vis-à-vis the spot against which the first object is pressed, i.e. distally of this spot. This first option may be advantageous because the bonding can be carried out even if the first object by itself does not have sufficient stability to withstand the pressing force without substantial deformation or even defects.
In embodiments that include deforming the second object during the process of pressing the second object against the first object, the support may include a shaping feature that assists the deformation process. For example, the support may be shaped to have a shaping protrusion or shaping indentation, to cause an outward bending or inward bending of the deformable structure, respectively.
It is further possible that the method uses a cooling effect by the support on the thermoplastic material of the first object, whereby the thermoplastic material of the first object is kept at a cooler temperature and thus remains harder at an interface to the support. Thereby, the deformable structure will be caused to deform such as not to get too close to the interface with the support.
According to a second option, the distal side of the first object may be exposed, for example by the first object being held along the lateral sides or similar. This second option features the advantage that the distal surface will not be loaded and will remain unaffected if the second object does not reach to the distal side.
In embodiments, the first object is placed against a support with no elastic or yielding elements between the support and the first object, so that the support rigidly supports the first object.
In a group of embodiments, the second object includes an inner portion and an outer portion, with a gap therebetween. Then, the coupling structures of the second object may include outer structures of the inner portion and/or inner structures of the outer portion and/or outer structures of the outer portion, and the step of causing a flow of the flow portion includes causing a flow into the gap.
According to an option, inner and outer portions may together be of one piece.
In a group of embodiments, the second object includes a first portion of a first material and a second portion of a second material. This group of embodiments, for example, may make possible to save cost if the first portion includes critical sections, such as a thread or other structure for connecting a further element to the assembly of the first and second objects, is made of a high-quality building material, for example stainless steel, titanium, aluminum, copper, etc., whereas the second portion may include a lower cost material and primarily serve for stabilization of the second object with respect to the first object.
Especially, if the second object includes an inner portion and an outer portion, the inner portion may be of the first material and the outer portion may be of the second material. Thereby, by the flow of the flow portion into the gap, the second object itself is also stabilized, in addition to being bonded to the first object.
Embodiments that include a first portion of a first material and a second portion of a second material may, for example, include embodiments of the above-discussed group that include a deformable portion. In these, the deformable portion may, for example, belong to the second portion of a second material, and mounting structure for mounting a further object to the first object or for another function may be of another, not deformable material, such as of a hard metal.
An further advantage of embodiments with a first and a second material (in addition to optionally including a deformable portion, with the above-discussed advantages) is that they provide the possibility of using a lightweight and/or low cost material for those parts of the second object that use up a lot of space (for example, to yield a sufficiently large footprint in the above sense) while maintaining the possibility of having a sufficiently stable/stiff functional piece, for example with a thread or other functional structure, constituted by the first portion.
If the second material is itself capable of being deformed and possibly capable of flowing, at temperatures above the liquefaction temperature of the first object material, this approach may feature the even further advantage that the first and second portions may optionally be assembled in situ if they are initially not connected with each other or only loosely connected. For example, the second material may flow relative to the first material to embed a part of the first portion, for example in a positive-fit like manner.
In a group of embodiments, the second object may constitute a mounting piece (mounting pillar, mounting plug, etc.) for mounting a further object to the first object. Especially, an inner portion of the above-described kind may include a mounting structure, such as a thread or bayonet fitting structure or guide bushing or snap-on structure, etc. The outer portion may serve as a fastening flange for fastening the mounting structure. Compared to prior art fastening flanges, this approach has substantial advantages:
Instead of two separate steps for providing a fastening flange and for mounting the fastening element to the fastening flange, the entire structure may be attached in one single step.
The positioning of the mounting piece may optionally be done directly at the otherwise completed first object, for example after the latter has been placed relative to further parts and/or for example in presence of the further object. Thus, during the manufacturing of the first object itself, there is no need for a precise alignment step. Therefore, the precision of the positioning in relation to the end product may be drastically increased.
Due to the approach according to the invention, anchoring of the mounting structure is effective also in situations where the first object is comparably thin and/or where another, distal surface of the first object needs to remain unaffected. This is in contrast to the above-discussed prior art approaches that include plunging a metallic body (threaded bush or the like) in a thermoplastic object.
Especially, in embodiments the second object includes a proximal body and, distally thereof, a plurality of distal extensions that in the step of pressing are pressed into the first object. Especially, the distal extensions may include at least one outer extension and at least one inner extension.
For example, the proximal body may include a portion in the above-mentioned sense of a second material, and, embedded therein, a portion of a first material, which portion of the first material is accessible from the proximal side also after the step of letting the thermoplastic material re-solidify, and which may have the mounting structure. The portion of the first material may extend distally to form at least one of the distal extensions (such as a central protrusion) or may be restricted to the proximal side.
In a group of embodiments, the first object is a flattish object, such as a polymer plate, for example a polymer cover.
The bond between the second object and the first object may have any purpose of a bond between two objects. For example, in the automotive or aviation industries, the bond may be a bond between a structural element of plastic (first object) and a metallic or compound material structural element.
In a group of embodiments, the second object may be an anchor in the first object for fastening a further element thereto.
In another group of embodiments, the second object may be a connector that bonds a further, third object to the first object by the method described herein. These embodiments thus concern:
A method of connecting a third object to a first object by bonding a second object to the first object and thereby securing the third object to the first object, the method including the steps of:
Especially, in the step of arranging the third object relative to the first object, the third object may be placed proximally of the first object, and after the step of arranging, the second object may be caused to penetrate the third object until a distal portion thereof reaches the first object for the second object to be pressed against the first object.
For example, to this end, the third object may be of a liquefiable thermoplastic material or otherwise penetrable material for the second object to penetrate through the third object until its distal portion reaches the first object.
Then, it is further possible to arrange the coupling structure of the second object in a manner that a positive-fit connection is also caused with the third object, in addition to the connection with the first object.
In addition or as an alternative, the third object may include a bore through which the distal portion of the third object is guided to reach the first object.
For securing the third object to the first object, the second object may include a head or bridge portion that rests against a proximally facing surface portion of the third object while the distal portion of the second object is anchored in the first object.
In addition or as an alternative, if the third object includes thermoplastic material, a positive-fit connection between the second and third objects may be caused by material of the third object penetrating into structures of the second object, in addition to material of the first object interpenetrating the coupling structures.
In addition or as yet another alternative, thermoplastic material of the third object may be caused to be welded to thermoplastic material of the first object by the effect of the second object being pressed into the assembly of the third and first objects or may be caused to interpenetrate flowable material of the first object in a non-mixing manner to yield a mechanical and/or adhesive connection after the re-solidification.
It is even an option that material of the third object that is bonded to the first object includes an elastomeric material or other material, even if such material is not liquefiable, and even if no pre-manufactured opening is present. Especially, a cutting portion of the second object may pierce through a portion of the third object until it comes into contact with the first object placed distally thereof.
In this way (bonding of not meltable or meltable soft material to a thermoplastic first object), connections between hard and soft materials become possible, that for example cannot be processed together in hard/soft injection molding. An example would be the bonding of a damping cushion (third object) to a thermoplastic first object, such as a thermoplastic sheet.
In a group of embodiments, the second object comprises, at the surface that during the pressing and vibrating is in direct contact with the first object, structures serving as energy directors, such as edges or tips. While for ultrasonic welding and also for the “Woodwelding” process as for example described in WO 98/42988 or WO 2008/080 238, energy directors are known, they will generally be present on the object of the material to be liquefied. Embodiments of the present invention, however, reverse this by providing energy directors on material that is not liquefied but is interpenetrated by liquefied material.
The invention also concerns a connecting element for being secured, in a method as described in this text, to a first object that includes a thermoplastic material. More in particular, any properties of second objects that are described and/or claimed referring to the method may be properties of the connecting element and vice versa.
In this text the expression “thermoplastic material being capable of being made flowable e.g. by mechanical vibration” or in short “liquefiable thermoplastic material” or “liquefiable material” or “thermoplastic” is used for describing a material including at least one thermoplastic component, which material becomes liquid (flowable) when heated, in particular when heated through friction i.e. when arranged at one of a pair of surfaces (contact faces) being in contact with each other and vibrationally moved relative to each other, wherein the frequency of the vibration has the properties discussed hereinbefore. In some situations, for example if the first object itself has to carry substantial loads, it may be advantageous if the material has an elasticity coefficient of more than 0.5 GPa. In other embodiments, the elasticity coefficient may be below this value, as the vibration conducting properties of the first object thermoplastic material do not play a role in the process since the mechanical vibrations are transferred directly to the second object by the tool.
Thermoplastic materials are well-known in the automotive and aviation industry. For the purpose of the method according to the present invention, especially thermoplastic materials known for applications in these industries may be used.
A thermoplastic material suitable for the method according to the invention is solid at room temperature (or at a temperature at which the method is carried out). It preferably includes a polymeric phase (especially C, P, S or Si chain based) that transforms from solid into liquid or flowable above a critical temperature range, for example by melting, and re-transforms into a solid material when again cooled below the critical temperature range, for example by crystallization, whereby the viscosity of the solid phase is several orders of magnitude (at least three orders of magnitude) higher than of the liquid phase. The thermoplastic material will generally include a polymeric component that is not cross-linked covalently or cross-linked in a manner that the cross-linking bonds open reversibly upon heating to or above a melting temperature range. The polymer material may further include a filler, e.g. fibres or particles of material that has no thermoplastic properties or has thermoplastic properties including a melting temperature range that is considerably higher than the melting temperature range of the basic polymer.
In this text, generally a “non-liquefiable” material is a material that does not liquefy at temperatures reached during the process, thus especially at temperatures at which the thermoplastic material of the first object is liquefied. This does not exclude the possibility that the non-liquefiable material would be capable of liquefying at temperatures that are not reached during the process, generally far (for example, by at least 80° C.) above a liquefaction temperature of the thermoplastic material or thermoplastic materials liquefied during the process. The liquefaction temperature is the melting temperature for crystalline polymers. For amorphous thermoplastics the liquefaction temperature (also called “melting temperature in this text”) is a temperature above the glass transition temperature at which the becomes sufficiently flowable, sometimes referred to as the ‘flow temperature’ (sometimes defined as the lowest temperature at which extrusion is possible), for example the temperature at which the viscosity drops to below 104 Pa*s (in embodiments, especially with polymers substantially without fiber reinforcement, to below 103 Pa*s)), of the thermoplastic material.
For example, the non-liquefiable material may be a metal, such as aluminum or steel, or wood, or a hard plastic, for example a reinforced or not reinforced thermosetting polymer or a reinforced or not reinforced thermoplastic with a melting temperature (and/or glass transition temperature) considerably higher than the melting temperature/glass transition temperature of the liquefiable part, for example with a melting temperature and/or glass transition temperature higher by at least 50° C. or 80° C.
Specific embodiments of thermoplastic materials are: Polyetherketone (PEEK), polyesters, such as polybutylene terephthalate (PBT) or Polyethylenterephthalat (PET), Polyetherimide, a polyamide, for example Polyamide 12, Polyamide 11, Polyamide 6, or Polyamide 66, Polymethylmethacrylate (PMMA), Polyoxymethylene, or polycarbonateurethane, a polycarbonate or a polyester carbonate, or also an acrylonitrile butadiene styrene (ABS), an Acrylester-Styrol-Acrylnitril (ASA), Styrene-acrylonitrile, polyvinyl chloride, polyethylene, polypropylene, and polystyrene, or copolymers or mixtures of these.
In embodiments in which both, the first and the second object include thermoplastic material, the material pairing is chosen such that the melting temperature of the second object material is substantially higher than the melting temperature of the first object material, for example higher by at least 50°. Suitable material pairings are for example polycarbonate or PBT for the first object and PEEK for the second object.
In addition to the thermoplastic polymer, the thermoplastic material may also include a suitable filler, for example reinforcing fibers, such as glass and/or carbon fibers. The fibers may be short fibers. Long fibers or continuous fibers may be used especially for portions of the first and/or of the second object that are not liquefied during the process.
The fiber material (if any) may be any material known for fiber reinforcement, especially carbon, glass, Kevlar, ceramic, e.g. mullite, silicon carbide or silicon nitride, high-strength polyethylene (Dyneema), etc.
Other fillers, not having the shapes of fibers, are also possible, for example powder particles.
Mechanical vibration or oscillation suitable for the method according to the invention has preferably a frequency between 2 and 200 kHz (even more preferably between 10 and 100 kHz, or between 20 and 40 kHz) and a vibration energy of 0.2 to 20 W per square millimeter of active surface. The vibrating tool (e.g. sonotrode) is, e.g., designed such that its contact face oscillates predominantly in the direction of the tool axis (longitudinal vibration) and with an amplitude of between 1 and 100 μm, preferably around 30 to 60 μm. Such preferred vibrations are, e.g., produced by ultrasonic devices as, e.g., known from ultrasonic welding.
In this text, the terms “proximal” and “distal” are used to refer to directions and locations, namely “proximal” is the side of the bond from which an operator or machine applies the mechanical vibrations, whereas distal is the opposite side. A broadening of the connector on the proximal side in this text is called “head portion”, whereas a broadening at the distal side is the “foot portion”. The “axis” is the proximodistal anchoring axis along which the pressure in the step of pressing is applied. In many embodiments, the mechanical vibrations are longitudinal vibrations with respect to the axis.
In the following, ways to carry out the invention and embodiments are described referring to drawings. The drawings are schematic in nature. In the drawings, same reference numerals refer to same or analogous elements. The drawings, unless otherwise specified, show views of cross sections along a plane parallel to the anchoring axis (“vertical” cross sections). The drawings show:
The second object is, for example, metallic or of plastic (thermosetting or thermoplastic). If the second object is liquefiable, the liquefaction temperature is such that it is not flowable at temperatures at which the first thermoplastic is flowable. For example, the melting temperature of the second object material is higher than the melting temperature of the first material by at least 50° or at least 80° C.
The second object has a structure capable of making a positive-fit connection with material of the first object after the latter has flown. More in particular, the second object has a surface portion that has an undercut with respect to axial directions (axis 10). For example, the surface structure includes at least one rib 4 running in a non-axial direction or at least one hump. In the depicted embodiment the second object is assumed to be rotationally symmetrical about the axis 10 and includes a plurality of circumferential ribs 4 between which grooves 5 are formed.
At the distal end, the second object has a tip 3, and at the proximal end, a head portion 6 forms a proximally facing coupling face for the mechanical vibrations.
A sonotrode 7 is used to press the second object against the first object while mechanical vibrations are coupled into the second object. As shown in
After the vibrations have stopped, the liquefied thermoplastic material will again solidify, leaving the second object solidly anchored in the first object (
The second object in this and other embodiments described in this text may have the function of serving as a connector, (nut, threaded bolt, etc.) feedthrough, bushing, other connector etc.
In
In cases where:
For the diameter dh of the bore, the following considerations may apply (not only for shapes like the one shown in
In the different embodiments described in this text, the distal tip 3 or edge as well as edges of the ribs or other protruding features of the coupling structure serve as energy directors for the liquefaction of the thermoplastic material.
The embodiments described herein show a sonotrode 7 (or ‘horn’) as a separate piece that is pressed against the proximally facing coupling face of the second object.
However, especially in embodiments in which the second object is metallic, the second object may be a sonotrode directly coupled to a vibration generating apparatus. It may, for example, be provided with a proximal thread or bayonet-coupling structure or similar for being fastened to an according coupling of the vibration generating apparatus.
While the embodiments of
When the second object is pressed into the first object while thermoplastic material of the first object is liquefied, portions of the liquefied material flow into the gap (flow 11 in
The following options apply:
While the first and second portions 21, 22 in the embodiment of
In
For a gap between an inner portion 21 and an outer portion 22, a minimal width of 0.1 mm should be present in order for the thermoplastic material to be capable to flow into.
The embodiment of
In the hereinbefore described embodiments, the second object is anchored in a depth-effective manner by providing the second object with an anchoring portion that extends along the anchoring axis, and in some embodiments with the aid of a bore in the first object. These embodiments may have a plurality of structure elements (the grooves 5, for example) into which liquefied material of the first object may flow, which structure elements are spaced axially from each other, such as arranged along a shaft and/or tube or similar.
In the variant of
After the process of bonding the second object 2 to the first object 1, the effective height h of the proximal body 29 is higher than its initial physical axial extension, because the flow portion of the thermoplastic material has filled the gap 23 between the inner and outer portions (backflow) (
The situation after the process as shown in
If necessary, additional stability with respect to axial forces may be provided if the outer portion is provided with inner structures (grooves or similar) that are embedded by the flow portion of the thermoplastic material to yield another positive-fit connection.
In the configuration depicted in
It may in special embodiments extend to not even reach the plane defined by the proximal surface in the assembled state (
The embodiment of
More in particular, in the embodiment of
As illustrated in
Yet another optional feature of this embodiment and of other embodiments of the invention is schematically illustrated in
The feature of having the distal surface of the first object distally of the interface to the second object exposed is independent of the other features described referring to
In the embodiment of
The width w of the bond/of the intermixing zone in embodiments of a planar bond in at least one lateral dimension and often in both lateral dimensions is substantially larger than the penetration depth, this being a further possible characteristic of planar bonds.
With respect to
The first object includes a through bore 20 in which the second object is anchored.
To this end, in a first stage, illustrated in
The support 42 against which the first object is placed in this embodiment includes a mould portion that forms a cavity 44 when the first object abuts against the support. The second object is provided with an excess length so that at some stage of the process, before a distally facing stop face of the head portion 6 abuts against the first object, the distal end of the anchoring portion abuts against the support 42. Thereafter, the pressing force and the mechanical vibrations are further applied and possibly intensified until also thermoplastic material of the second object 2 becomes flowable (flow 51 in
The fact that thermoplastic material of the first object has flowed into structures of the second object in addition to contributing to the anchoring also causes a sealing effect.
While in the embodiment of
In the variant shown in
Embodiments of the combined bonding process with the additional rivet effect are also especially suited for bonding a further object to the first object, with the rivet-like connector constituted by the second object securing the first and further objects to each other, as explained referring to other embodiments in more detail hereinafter.
In the depicted embodiment, the second object is of one piece forming the inner and outer parts 21, 22. The gap 23 in embodiments like 4a, 4b, 4, 8 and others may be viewed as opening open to the distal side encompassing the central protrusion 21.
Compared to embodiments with just one pin-shaped shaft, the embodiments with an inner portion and an outer portion due to the interplay between the inner and outer portions bring about additional anchoring stability, especially if the thermoplastic material of the first object is comparably soft or thin or brittle.
In the embodiment of
The embodiment of
The second object 2 includes protruding structures 36 with distal edges or tips 3 that serve as energy directors and cause a swift onset of the liquefaction around the protruding structures.
A volume V1 of the protruding structures is smaller than or equal to a volume V2 of the indentations (see
The indentations and protrusions are arranged immediately next to each other. I.e., there is no distance e (
In the embodiment of
In the embodiment of
Also other cross sectional shapes may be feasible, including more edgy shapes as illustrated in
In contrast, for example, to second objects 2 of the kind illustrated in
In the hereinbefore described embodiments, the coupling structures that include an undercut with respect to axial (proximodistal) directions and thereby make a positive-fit connection possible are pre-manufactured properties of the second object. Hereinafter, embodiments where this form lock structure is formed during the process by deformation are described.
Firstly, the method in embodiments further includes pressing a retaining device 93 against the proximal face of the first object in a vicinity of the second object while the second object is bonded to the first object (in
Secondly, similarly to the embodiments of
Generally, the second object may have the purpose of serving as an anchor for a further object to be attached to the first object, or may itself be such a second object (in the above figures, the first object are illustrated without any functional structures for such purpose, however, any such structures such as fastening structures or other functional structures are possible.
Hereinafter, embodiments in which a further object (“third object”) is bonded to the first object in the bonding process by bonding the second object to it, are described.
The third object may include a thermoplastic material capable of being welded to the thermoplastic material of the first object 1. For example, it may be of a thermoplastic material with a same polymer matrix. In a region around the second object, due to the liquefaction caused in the process a weld may be caused, as indicated by the circles 101. More in general, material of the third object in the process is pressed into the first object to contribute to the connection after re-solidification. This also holds if the materials of the first and third objects cannot be welded because they do not mix in the liquid state.
In addition or as an alternative to being driven through material of the third object, the second object (connector) may also be driven through a pre-made opening of the third object for its distal portion to be anchored in the first object. Such a pre-made opening may have a diameter allowing the second object to reach through it substantially without resistance (see an embodiment described hereinafter) or may encounter substantial resistance so that mechanical energy is absorbed also there.
Similarly, the embodiment of
In this embodiment, instead of the barbs, the legs 112 have distal arrow portions 115. Combinations would be possible.
A further, optional feature that does not depend on the legs is constituted by a central hole 116 that may be used for guiding during the assembly process, for example together with a collar 117. Other uses of such a hole and/or collar are possible, including the fastening of a further object to the second object.
The second object of
Instead of being formed into a hollow cylinder, a perforated metal sheet or a mesh may be brought into other shapes for constituting a connector of the described kind.
A further option in addition to cylindrical (
An even further variant is a square (in cross section perpendicular to the axial direction) or other closed or open shape with a curve or buckling.
Second objects having structures as the ones described referring to
Second objects with thin structures as the ones described referring to
Second objects 2 as connectors of the kind described referring to
In this special example, the third object 100 includes a foam that by insertion of the second object 2 is compressed (compressed portion 102). Optionally, the second object may include relaxation openings 133 or other shape features that allow compressed material to flow away in case the foam has thermoplastic properties (which is not necessary).
While
In the embodiment of
The second object in the depicted embodiment includes a resilient barb structure 118 that allows pushing the distal portion of the second object through the bore 109 but that ensures anchoring in the first object 1 after liquefaction and re-solidification. The second object also has a proximal head portion 6 for securing the third object 100 against the first object 1.
As an alternative to having a resilient barb structure 118, the second object in a configuration like the one of
The bond of the second object to the first object is a flattish bond, similar to the one taught with respect to
According to yet another alternative, illustrated in
In the variant of
Both measures have the effect that more energy is absorbed and more material is liquefied at more proximal, peripheral locations than at more distal, central locations around the opening. The effect is that the distal surface of the first object is kept intact.
In the embodiment of
In order to be stable with respect to buckling, the metal sheet or mesh may extend in a curved shape (for example, by forming a cylinder) or wave shape (perpendicular to the drawing plane) or other non-straight shape, as described hereinbefore.
In an example, the main body of the second object 2 may be of a liquefiable material (liquefiable at a same temperature as the thermoplastic material of the first object, at higher temperatures, or even at slightly lower temperatures), with the protruding structures 161 cast into them. In embodiments, a porosity of the structures may be at least 50%.
| Number | Date | Country | Kind |
|---|---|---|---|
| 01684/14 | Nov 2014 | CH | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2015/075592 | 11/3/2015 | WO | 00 |