Disposable garments, such as infant and children's diapers, swimwear and training pants, as well as adult incontinence garments, conventionally include materials that are joined together and connected using a bonding process, or the materials are bonded in related converting systems prior to bonding the materials together. For example, a training pant or other pant-type garment may have a front side panel and a back side panel that are bonded together at a side seam to provide a complete side panel. The side panels are typically connected at the side seam using an ultrasonic process such as the process described by You et al. in
The ability to form strong ultrasonic bonds using conventional processes is limited by several factors, including the process converting speeds or production line speeds, bonding time or dwell time, and the thickness and/or basis weight of the materials being bonded. Moreover, in the case of rotary ultrasonic or pressure bonding of high loft substrates, bonding pattern roll pins have a tendency of piercing the elastomeric material instead of creating a suitable bond.
A bonding process that provides sufficient bond strength for high loft substrates and does not decrease production line speeds is needed in the industry.
The present invention is generally directed to a method of bonding high loft substrates efficiently by placing the high loft substrate in a stretched condition in preparation for bonding. According to an aspect of the invention, this can be readily achieved by feeding in less substrate to the process than an amount of substrate being extracted from the process. Generally, a lower loft substrate results, which is more suitable for bonding. The component parts of the bonding system are simple, reliable and economical to manufacture and use. Other advantages of the invention will be apparent from the following description and the attached drawings or can be learned through practice of the invention.
In one aspect of the invention, a method of bonding material in a process system for producing a bonded product includes the steps of loading a plurality of rolls of elastomeric material in an unwind system; programming a controller with an unwind speed and a rewind speed, the controller in communication with the unwind system and a rewinder disposed downstream from the unwind system for respective communication of the unwind and rewind speeds to the unwind system and the rewinder; unwinding a quantity of material from the plurality of rolls of elastomeric material into a pressure bonder system disposed upstream of the rewinder, the pressure bonder system and the rewinder operating faster than the unwind system operating at the unwind speed to generate a speed differential, wherein the speed differential imparts a stretched state to the quantity of material; and bonding the stretched quantity of material with a pressure bonder of the pressure bonder system. The plurality of rolls of elastomeric material can include a high loft elastomeric material. The plurality of rolls of elastomeric material can also include a stretch bonded laminate, a vertical filament stretch bonded laminate, a continuous filament stretch bonded laminate or combinations of these laminates. Further, the quantity of material can be polyesters, polyolefins and combinations thereof.
Also in this aspect of the invention, the unwind system can have an unwinder for unwinding at least one of the rolls of elastomeric material. Further in this aspect, the controller can be a computer or a programmable logic controller to program the rewind speed at least twice as fast as the unwind speed. In one example, the unwind speed is from about 600 feet per minute to about 1200 feet per minute, although the unwind speed can be orders of magnitude slower or faster with the rewind speed being at least somewhat faster than the unwind speed.
Further in this aspect of the invention, the pressure bonder can have a pattern roll and an anvil for exerting a pressure to bond the quantity of material with a pattern between the pattern roll and the anvil. For example, the pressure can be a lineal pressure of about 0.05*106 N/m up to about 6*106 N/m.
Alternatively, or additionally, the pressure bonder in this aspect of the invention can include a bonding roll and an anvil, which exert a pressure such as the pressure noted above to induce internal heating in the quantity of material to fuse a plurality of fibers of the quantity of material into a bond between the pattern roll and the anvil.
Still further in this aspect of the invention, the method of bonding material can include at least two rolls providing respective first and second quantities of material. The first and second quantities of material can be stretched equally before bonding by the pressure bonder. Also, one or more of the quantities of material can stretched from about 25% to about 200% before bonding by the pressure bonder, more particularly, from about 50% to about 150% before bonding by the pressure bonder. The quantities of material can be stretched in a machine direction or transverse to the machine direction before bonding by the pressure bonder, or the quantities of material can be stretched transverse to the machine direction and in the machine direction before bonding by the pressure bonder. In these aspects of the invention, the bonding step imparts a bond to the quantity of material having a bond strength greater than a material strength of the quantity of material such that material failure of the quantity of material occurs before failure of the bond.
Also in this aspect of the invention, the plurality of rolls of elastomeric material can be a single roll and the quantity of material can be folded at least once to generate at least two layers of material, the at least two layers of material being equally stretched before bonding by the pressure bonder.
Further in this aspect of the invention, the quantity of material can be nipped with a nip to stretch the quantity of material before bonding by the pressure bonder, the nip being disposed between the unwind system and the rewinder and operating at the unwind speed.
In another aspect of the invention, a method of bonding material in a process system for producing a bonded product includes the steps of loading a first roll of high loft elastomeric material in a first unwinder and a second roll of high loft elastomeric material in a second unwinder; programming a controller with an unwind speed and a rewind speed, the controller in communication with the first and second unwinders and a rewinder disposed downstream from the first and second unwinders for respective communication of the unwind and rewind speeds to the first and second unwinders and the rewinder; unwinding a first quantity of material from the first roll and a second quantity of material from the second roll into a nip disposed upstream of a pressure bonder system, the pressure bonder system and the rewinder operating faster than the first and second unwinders and the nip to generate a speed differential, wherein the speed differential imparts a stretched state to the first and second quantities of material; and bonding the stretched first and second quantities of material together with a pressure bonder of the pressure bonder system. In this aspect, the first and second quantities of material can be a high loft elastomeric material, a stretch bonded laminate, a vertical filament stretch bonded laminate, a continuous filament stretch bonded laminate, a polyester, a polyolefin and combinations of these.
Also in this aspect of the invention, the controller can be a computer or a programmable logic controller to control the rewind speed at least twice as fast as the unwind speed.
Further in this aspect, the pressure bonder includes a pattern roll and an anvil, the pattern roll and the anvil being configured to exert a pressure to bond the first and second quantities of material with a pattern between the pattern roll and the anvil. Alternatively or additionally, the pressure bonder includes a bonding roll and an anvil, the bonding roll and the anvil being configured to exert a pressure to induce internal heating in the first and second quantities of material to fuse a plurality of fibers of the first and second quantities of material into a bond between the pattern roll and the anvil. The quantities of material are stretched from about 25% to about 200% before bonding by the pressure bonder, more particularly, from about 50% to about 150% before bonding by the pressure bonder. The quantities of material can be stretched in a machine direction before bonding by the pressure bonder, or the quantities of material can be stretched transverse to a machine direction before bonding by the pressure bonder. Alternatively, the quantities of material can be stretched transverse to the machine direction and in the machine direction before bonding by the pressure bonder. In this aspect, the bonding step imparts a bond to the quantities of material having a bond strength greater than a material strength of the quantities of material such that material failure of the quantities of material occurs before failure of the bond. Also in this aspect, at least one of the quantities of material can be folded at least once to generate at least two layers, the at least two layers being equally stretched before bonding by the pressure bonder.
In yet another aspect of the invention, a method of bonding material in a process system for producing a bonded product includes the steps of providing a roll of elastomeric material; programming a controller with a first speed and a second speed, the controller in communication with the roll of elastomeric material and a bonder system disposed downstream from the roll of elastomeric material for respective communication of the first and second speeds to the roll of elastomeric material and the bonder system; feeding a quantity of material from the roll of elastomeric material at the first speed into the bonder system, the bonder system operating at the second speed faster than the first speed to generate a speed differential, wherein the speed differential imparts a stretched state to the quantity of material; and bonding the stretched quantity of material with a bonder of the bonder system. In this aspect, the roll of elastomeric material is a high loft elastomeric material. Also in this aspect of the invention, the controller can be a computer or a programmable logic controller for controlling the first and second speeds; for example, to set the first speed at least twice as fast as the second speed
Other features and aspects of the invention are discussed in greater detail below.
A full and enabling disclosure of the present invention, including the best mode thereof to one skilled in the art, is set forth more particularly in the remainder of the specification, including reference to the accompanying figures, in which:
Repeat use of reference characters in the present specification and drawings is intended to represent the same or analogous features or elements of the present invention.
Within the context of the present description, the following terms may have the following meanings:
“Machine direction” (MD) refers to the length of a fabric or material in the direction in which it is produced or converted, as opposed to “cross direction” or “cross-machine direction” (CD or CMD), which refers to the width of a fabric in a direction generally perpendicular to the machine direction.
“Attached” and “joined” refers to the bonding, adhering, connecting, and any other method for attaching or joining two elements. Two elements will be considered to be attached or joined together when they are bonded directly to one another or indirectly to one another, such as when each is directly attached to an intermediate element.
“Sheet” refers to a layer, which may be a film, a foram, or a nonwoven web.
“Member” when used in the singular can refer to a single element or a plurality of elements.
The term “composite nonwoven fabric”, “composite nonwoven”, “laminate”, or “nonwoven laminate”, as used herein, unless otherwise defined, refers to a material having at least one elastic material joined to at least one sheet material. In most embodiments such laminates or composite fabric will have a gatherable layer, which is bonded to an elastic layer or material so that the gatherable layer may be gathered between bonding locations. As set forth herein, the composite elastic laminate may be stretched to the extent that the gatherable material gathered between the bond locations allows the elastic material to elongate. This type of composite elastic laminate is disclosed, for example, in U.S. Pat. No. 4,720,415 to Vander Wielen et al., which is incorporated herein in its entirety by reference thereto.
As used herein, the term “nonwoven web” refers to a web having a structure of individual fibers or threads that are interlaid, but not in an identifiable, repeating manner. Nonwoven webs have been, in the past, formed by a variety of processes such as, for example, meltblowing processes, spunbonding processes and bonded carded web processes.
The term “continuous filaments”, as used herein, refers to strands of continuously formed polymeric filaments. Such filaments will typically be formed by extruding molten material through a die head having a certain type and arrangement of capillary holes therein.
As used herein, the term “meltblown fibers” means fibers formed by extruding a molten thermoplastic material through a plurality of fine, usually circular, die capillaries as molten thermoplastic material or filaments into a high velocity gas (e.g. air) stream which attenuates the filaments of molten thermoplastic material to reduce their diameter, which may be to microfiber diameter. Thereafter, the meltblown fibers are carried by the high velocity gas stream and are deposited on a collecting surface to form a web of randomly disbursed meltblown fibers. Such a process is disclosed, for example, U.S. Pat. No. 3,849,241 to Butin, which is incorporated herein in its entirety by reference thereto.
As used herein, the term “spunbonded fibers” refers to small diameter fibers formed by extruding a molten thermoplastic material as filaments from a plurality of fine, usually circular, capillaries of a spinerette with the diameter of the extruded filaments then being rapidly reduced as by, for example, eductive stretching or other well-known spun-bonding mechanisms. The production of spun-bonded nonwoven webs is illustrated in patents such as, for example, U.S. Pat. Nos. 4,340,563 to Appel et al., and 3,692,618 to Dorschner et al. The disclosures of these patents are incorporated herein in their entireties by reference thereto.
“Extendable” or “extensible” means that property of a material or composite by virtue of which it stretches or extends in the direction of an applied biasing force by at least about 25% of its relaxed length. An extendable material does not necessarily have recovery properties. For example, an elastomeric material is an extendable material having recovery properties. A meltblown web may be extendable, but not have recovery properties and, thus, be an extensible but non-elastic material.
“Elastomeric,” “elastic,” and “elasticized” refer to a material or composite which can be stretched or elongated by at least 25% of its relaxed length and which will recover, upon release of the applied force, at least 10% of its elongation. It is generally preferred that the elastomeric material or composite be capable of being elongated by at least 100%, more preferably by at least 300%, of its relaxed length and recover at least 50% of its elongation.
“Non-extensible” refers to a material that does not stretch or extend by at least about 25% of its relaxed length without fracture upon application of a biasing force. Materials that are extensible or elastomeric are not considered “non-extensible.”
“Untensioned” as used herein to describe a material web does not mean lacking all tension. In order to handle and process moving webs, some moderate amount of tension is needed to hold the web or material in place. An “untensioned” web or material, as used herein, is under enough tension to process the material, but less than that required to cause substantial deformation of the material.
“Necked material” refers to any material, which has been constricted in at least one dimension by processes such as, for example, drawing.
“Neck-bonded” laminate refers to a composite material having an elastic member that is bonded to a member while the member is extended in the machine direction creating a necked material that is elastic in the cross-direction. Examples of neck-bonded laminates are disclosed in U.S. Pat. Nos. 4,965,122; 4,981,747; 5,226,992; and 5,336,545, which are incorporated herein by reference in their entirety for all purposes.
“Reversibly-necked material” refers to a necked material that has been treated while necked to impart memory to the material so that when force is applied to extend the material to it pre-necked dimensions, the necked and treated portions will generally recover to their necked dimensions upon termination of the force. A reversibly-necked material may include more than one layer. For example, multiple layers of spunbonded web, multiple layers of meltblown web, multiple layers of bonded carded web or any other suitable combination of mixtures thereof. The production of reversibly-necked materials is described in U.S. Pat. Nos. 4,965,122 and 4,981,747, incorporated herein by reference for all purposes.
“Stretch-bonded” laminate refers to a composite material having at least two layers in which one layer is a gatherable layer and the other layer is an elastic layer. The layers are joined together when the elastic layer is in an extended condition so that upon relaxing the layers, the gatherable layer is gathered. For example, one elastic member can be bonded to another member while the elastic member is extended at least about 25% of its relaxed length. Such a multilayer composite elastic material may be stretched until the non-extensible layer is fully extended. Examples of stretch-bonded laminates are disclosed, for example, in U.S. Pat. Nos. 4,789,699, 4781,966, 4,720,415, 4,657,802, and 4,655,760, which are incorporated herein by reference in their entirety for all purposes.
“Neck stretch-bonded” laminate refers a laminate made from the combination of a neck-bonded laminate and a stretch-bonded laminate. Examples of necked stretch bonded laminates are disclosed in U.S. Pat. Nos. 5,114,781 and 5,116,662, which are incorporated herein in their entirety by reference thereto for all purposes. A necked stretch bonded laminate can be stretchable in both the machine and cross-machine directions.
Various aspects and embodiments of the invention will be described in the context of a material for disposable absorbent articles, such as disposable diapers, children's training pants, incontinence articles, feminine care products, diaper pants, disposable swim pants and the like. It should be appreciated that this is for illustrative purposes only, and that the invention is not limited to any particular absorbent article or absorbent articles in general. The material according to the invention may have beneficial uses in any number of applications, such as protective medical clothing, drapes, gowns and the like.
It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention.
The present disclosure is generally directed to a method for producing a bonded substrate. More particularly, the present disclosure is directed to stretching a high loft substrate to facilitate bonding of the substrate with a folded section of that substrate, with one or more other substrates, during converting processes or a combination of these. Through the above processes, a lower loft substrate results, which is more suitable for bonding.
Referring now to
As shown in
As shown more particularly in
More particularly, the nip 16 in
With more particular reference to the pressure bonder 18 shown in
In the nip region between the pattern roll 32 and the anvil roll 34, the invention can be configured to provide a distinctive lineal-pressure value F, which has the units of force per lineal distance, and may also be referred to as the nip force value. The lineal-pressure value can be determined by the formula:
F=QT/L;
where: QT=the total force which is exerted by the forcing mechanism to urge the pattern roll 32 toward contact with the anvil roll 34;
L=an average length of contact between the peripheral bonding surfaces of the bonding elements and the surface of the anvil roll 34 if the pattern roll 32 contacted the anvil roll 34 as measured along an axial cross direction of the anvil roll 34.
The average length of contact, L, can be determined by the following formula:
L=n*G/S
where: n=the number of pin lines; G=bonding surface area of an individual bonding element (e.g., bonding surface area of an individual bonding pin); S=the MD pin spacing distance.
For circular pins; G=(π*d2)÷4. Accordingly, for the circular pins:
L=(n*π*d2)/(4*S)
where: d=the pin diameter and π=3.14.
In particular aspects, the lineal pressure value can be at least a minimum of about 0.05*106 N/m. The lineal pressure value can alternatively be at least about 0.05*106 N/m and can optionally be at least about 1*106 N/m to provide desired benefits. In other aspects, the lineal pressure value can be up to a maximum of about 10*106 N/m or more. The lineal pressure value can alternatively be up to about 6×106N/M and can optionally be up to about 4.5*106 N/m to provide desired effectiveness. Further details of pressure bonding methods as described by example above can be found in U.S. patent application Ser. No. 11/138,099, which is incorporated herein by reference.
With further reference now to
Turning now to
The fibers 37 shown in
Other exemplary elastomeric materials that may be used include polyurethane elastomeric materials such as those available under the trademark ESTANE from B.F. Goodrich & Co., polyamide elastomeric materials such as those available under the trademark PEBAX from the Rilsan Company, and polyester elastomeric materials such as those available under trade designation HYTREL from E.I. DuPont De Nemours & Company. However, the invention is not limited to only such elastomeric materials. For example, various latent elastic materials such as the Arnitel-brand polymers may be utilized to provide the necessary elasticity characteristics to the continuous filaments.
Likewise, the above-referenced materials, and others, may be utilized in forming the outer facings of the presently described laminate. In particular, various webs may be utilized that are formed from elastomeric or nonelastomeric fibers. Various polyester elastic materials are, for example, disclosed in U.S. Pat. No. 4,741,949 to Morman et al., which is incorporated herein in its entirety by reference thereto. Other useful elastomeric polymers also include, for example, elastic copolymers of ethylene and at least one vinyl monomer such as, for example, vinyl acetates, unsaturated aliphatic monocarboxylic acids, and esters of such monocarboxylic acids. The elastic copolymers and formation of elastomeric fibers from these elastic copolymers are disclosed in, for example, U.S. Pat. No. 4,803,117, which is also incorporated herein in its entirety by reference thereto.
With brief reference once more to
The present invention may be better understood with respect to the following tests and examples.
The following tests were performed on the samples that were produced. See, e.g., the elastomeric composite 36 and the bonds 38 described above.
Porosity was measured using STM (scientific, technical and medical) procedure number 3801. Porosity was measured using a Frazier air permeability tester. The units are cubic feet per minute per square foot (cfm per ft2) units.
Elongation was measured using test procedure number STM 529-W. Elongation may be tested using any suitable tensile testing equipment, such as those available from the Syntech Corporation of Cary, N.C., or from the Instron Corporation of Canton, Mass.
In a Peel Test, a laminate is tested for the amount of force needed to pull the layers of the laminate apart. The peel strength was measured using testing procedure number STM 751-W. The samples were tested in the cross machine direction. Any suitable tensile testing equipment may be used in order to perform the procedure.
The following example was performed in order to determine the effect of stretching webs of material, such as webs 24A, 24B discussed herein, prior to bonding using a bonder such as the bonder 18 as shown in
Manual checks of bond strength of the bonded materials 24A, 24B revealed material failure generally before bond failure.
These and other modifications and variations to the present invention may be practiced by those of ordinary skill in the art, without departing from the scope and spirit of the present invention, which is more particularly set forth in the appended claims. In addition, it should be understood that aspects of the various embodiments might be interchanged either in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only and is not intended to limit the invention so further described in such appended claims.
The present application is a continuation application and claims priority to U.S. patent application Ser. No. 11/303,074 filed on Dec. 14, 2005, now abandoned. The disclosure of which is hereby incorporated by reference.
Number | Name | Date | Kind |
---|---|---|---|
3692618 | Dorschner et al. | Sep 1972 | A |
3849241 | Butin et al. | Nov 1974 | A |
4340563 | Appel et al. | Jul 1982 | A |
4655760 | Morman et al. | Apr 1987 | A |
4657802 | Morman | Apr 1987 | A |
4720415 | Wielen et al. | Jan 1988 | A |
4741949 | Morman et al. | May 1988 | A |
4781966 | Taylor | Nov 1988 | A |
4789699 | Kieffer et al. | Dec 1988 | A |
4803117 | Daponte | Feb 1989 | A |
4854984 | Ball et al. | Aug 1989 | A |
4919738 | Ball et al. | Apr 1990 | A |
4965122 | Morman | Oct 1990 | A |
4981747 | Morman | Jan 1991 | A |
5114781 | Morman | May 1992 | A |
5116662 | Morman | May 1992 | A |
5226992 | Morman | Jul 1993 | A |
5336545 | Morman | Aug 1994 | A |
5609702 | Andersen | Mar 1997 | A |
5647864 | Allen et al. | Jul 1997 | A |
5763041 | Leak et al. | Jun 1998 | A |
6114263 | Benson | Sep 2000 | A |
6340782 | Kling et al. | Jan 2002 | B1 |
6627564 | Morman | Sep 2003 | B1 |
6740200 | Seymour et al. | May 2004 | B2 |
6969441 | Welch et al. | Nov 2005 | B2 |
7108759 | You et al. | Sep 2006 | B2 |
20020153086 | Alper | Oct 2002 | A1 |
20040006323 | Hall | Jan 2004 | A1 |
20040102754 | Morman et al. | May 2004 | A1 |
20060148358 | Hall et al. | Jul 2006 | A1 |
20060258249 | Fairbanks | Nov 2006 | A1 |
20060266473 | Senapati et al. | Nov 2006 | A1 |
Number | Date | Country |
---|---|---|
0432755 | Jun 1991 | EP |
0432763 | Jun 1991 | EP |
Number | Date | Country | |
---|---|---|---|
20100139846 A1 | Jun 2010 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 11303074 | Dec 2005 | US |
Child | 12707169 | US |