Bonding to calcified tissues

Abstract

Bonding to calcified tissues, including human teeth, tooth dentine and bone, is achieved through the medium of crystal growth adhered to the tissue. The crystals preferably comprise gypsum crystals which are formed by contacting the tissue surface with a mildly acidic solution containing sulphate ions.

Description

FIELD OF INVENTION

The present invention relates to the bonding of materials to calcified surfaces.

BACKGROUND OF THE INVENTION

One of the major problems in surgical reconstruction of disease-damaged calcified tissues is the attachment of prosthetic or restorative materials to the tissue surface. This is a particular problem in the restoration of teeth since the functional mechanical, thermal and environmental stresses on the restoration interface usually lead to interfacial leakage between the restoration and the tooth when the restorative material is held in place merely by gross mechanical interlocking. This leakage may lead to penetration of bacteria and/or bacterial by-products along the tissue-material interface and a renewed process of dental decay. The concept of an adhesively-bonded prosthetic and restorative material has been extensively investigated in recent years but a reliable long term bond has been found to be difficult to establish under practical clinical conditions. Further, the use of chemically-active materials to develop chemical bonding at the adhesive interface may pose biocompatibility problems. The development of an attachment mechanism which would allow functional stress transfer across the interface between reconstructive materials and calcified tissues and also minimize leakage in situations such as tooth restoration, therefore, would be extremely beneficial in many medical and dental procedures.

In dentistry a widely used mechanism for attachment of polymerizable resin materials is the so-called acid etch technique. In this procedure, the tooth enamel surface is treated for about one minute with an acid solution or gel, usually 30 to 50% phosphoric acid. This treatment results in dissolution of the outer layer of the enamel to a depth of around 20 micrometers and the production of a clean etched porous surface. When a fluid polymerizable resin composition is placed on the etched surface, capillary action draws the monomers into the surface porosity to a depth of as much as 100 micrometers. After setting of the resin composition by chemical activation or radiation-induced polymerization, a strong bond of the resin to the tooth is induced by virtue of the extensive micromechanical interlocking created through penetration of the resin into the many pores in the etched surface of the enamel. Such a bond is as strong as the weaker of the resin and the enamel surface. This acid-etch technique has been used to attach resin coatings to teeth to seal the fissures in the biting surfaces to prevent decay and to provide facings which improve the aesthetic appearance of the teeth. Another preventive dentistry application of the acid-etch technique is to bond orthodontic attachments directly to the tooth in order to move teeth within the jaws. For restorative purposes, acid-etching is used to improve the bond of restorative resins to fractured teeth and to minimize leakage around composite resin fillings. Still other applications include the splinting of loose teeth and temporary tooth replacement.

Although the acid-etch technique has proved to be extremely useful, certain disadvantages have become apparent. Among these are the loss of a significant depth of the outer enamel which contains most of the anticariogenic fluoride and the difficulty of removing bonded orthodontic attachments because of the deep penetration of resin into the etched enamel surface. In the latter application, the clinical removal of the attached resin consumes considerable time and can result in surface damage to the tooth surface because of the instrumentation needed to remove the assimilated resin.

SUMMARY OF INVENTION

In accordance with the present invention, there is provided a method of bonding materials to teeth and other calcified tissues which overcomes the disadvantages of the acid-etch technique and which has other advantages. The inventive procedure involves the formation on the tooth surface of an adherent crystalline deposit which has morphological characteristics permitting fluid materials, such as, polymerizable resins, to flow around the individual crystals, so that, after setting, the crystals act as anchoring points for the resin layer to the tooth surface.

The bonding of the resin to the tooth, therefore, is achieved by micromechanical interlocking of the resin with the crystal growth on the tooth surface. By the proper choice of crystal growth characteristics, a bond strength of dental resins to tooth enamel surfaces can be achieved which is equivalent to the acid-etch technique, while at the same time minimizing enamel loss and permitting easy removal and clean-up when debonding is necessary, thereby overcoming the disadvantages of the acid-etch technique. Fluoride may be incorporated within the crystal deposit so as to provide resistance to decay and to demineralization at the tooth surface.

The crystal growth procedure of this invention is useful in all the clinical situations where the acid-etch technique is used. In addition, the present invention is applicable as a general bonding method to all types of calcified tissues, including tooth dentine and bone.

BRIEF DESCRIPTION OF DRAWINGS

FIGS. 1 to 4 are scanning electron micrographs of crystal growth formed on tooth enamel.

DESCRIPTION OF PREFERRED EMBODIMENTS

In a preferred embodiment of the invention, crystal growth on the calcified tissue surface is produced by interaction with a solution containing ionic species which result in an outgrowth of insoluble calcium salts which are bonded to the tissue surface. In order to confine the reaction to a specific area of tissue, the solution is often provided in a viscous or gel-like form to limit flow during application of the solution. After completion of crystal growth, which occurs rapidly, typically in about 2 to 6 minutes, the reactant solution is washed away and the tissue surface is dried prior to the application of resin or other bonding agent.

In order to facilitate the crystal growth, the solution may be mildly acidic in order to effect a slight chemical reaction with the tissue surface to release calcium ions therefrom which then form a salt with the crystal-forming ionic species in the solution, the salt depositing in crystalline form. The crystals are nucleated within the tissue surface and thereby are firmly attached to it. The removal of calcium ions from the tissue surface to effect crystal formation involves considerably less damage to the surface when compared to the acid-etch technique.

The crystal growth generally is needle-like and occurs in random directions with respect to the tooth surface in dense formation, causing the intermeshing of crystals which enhances the anchoring capability of the crystal growth. Gypsum crystals typically are about 20 micrometers long and 2 to 5 micrometers thick.

One convenient agent for effecting the crystal formation procedure used in this invention is an aqueous solution of polyacrylic acid containing sulphate ions. The polyacrylic acid may have a molecular weight of from 1000 to 100,000 and a concentration of from about 10 to about 60%. In this instance, the crystal growth consists of gypsum crystals (CaSO.sub.4.2H.sub.2 O). In order to achieve significant crystal growth, the solution contains at least about 1% of SO.sub.4.sup.= ions, with the upper limit of sulphate concentration being limited by solubility considerations and the desire to avoid over-etching of the tooth surface. The application of a drop of polyacrylic acid containing the sulphate ion to tooth enamel results in the formation of a dense growth of needle-shaped gypsum crystals having a spherulitic habit. The viscosity and reactivity of the solution may be varied by varying the concentration and/or molecular weight of the polyacrylic acid. Alternative acids include phosphoric and sulphuric acids.

EXAMPLES

EXAMPLE 1

Solution of polyacrylic acid of molecular weights varying from 5000 (5T) to 80,000 (80T) of solution concentrations of 20 to 50 percent were formed by aqueous polymerization of acrylic acid using ammonium persulphate as initiator. These solutions were applied to calcified tissue.

Scanning electron microscopy showed a copious growth of gypsum crystals with all solutions containing more than about 1 percent sulphate ions. Solutions containing less than this amount or dialysed free of sulphate ions (D) did not produce crystal growth. However, upon addition of the appropriate amount of sulphate ions, in the form of sulphuric acid or ammonium sulphate, crystal growth occurred.

In all cases, crystal growth was complete in a period of 2 to 6 minutes. Four of the SEM's at 2000.times.magnification for 5T polyacrylic acid solutions are reproduced as FIGS. 1 to 4. The process conditions for each Figure is reproduced in the following Table I:

TABLE I______________________________________ Solution Treatment Concentration TimeFIG. (%) (mins)______________________________________1 20 12 30 13 40 14 40 5______________________________________

Calcium release from the tooth enamel surface was also determined and compared with that obtained with phosphoric acid solutions. The results are reproduced in the following Table II:

TABLE II______________________________________ Total Ca.sup.++ Treatment Time Released (mean)Acid (min) (microg.)______________________________________50T 5 17250T 15 9250T D 5 12250T D 15 1585T 5 2265T D 5 14850% H.sub.3 PO.sub.4 5 103465% H.sub.3 PO.sub.4 5 1518______________________________________

It will be seen from the above Table II that the calcium released by acid-etch is many multiples of the calcium released by the polyacrylic acid solutions used in this invention. The calcium release values correspond approximately to an etch depth of about 7 micrometers for the polyacrylic acid and approximately 64 micrometers for the phosphoric acid.

EXAMPLE 2

Solutions of polyacrylic acid of molecular weight 12,000 (12T) containing at least 1% SO.sub.4.sup.= were used to treat surfaces of extracted human premolar teeth for four minutes followed by washing and drying. Orthodontic brackets were bonded to the prepared tooth surfaces using two commercial orthodontic bonding resins. Similar specimens were prepared using the acid-etch technique using 37% orthophosphoric acid for 90 seconds. Details of the specimens are reproduced in the following Table III:

TABLE III______________________________________ ToothTooth Group Conditioning Bonding Agent______________________________________1 20% 12T + 3.9% SO.sub.4 Adhesive A.sup.(1)2 20% 12T + 3.9% SO.sub.4 Adhesive B.sup.(2)3 40% 12T Adhesive A4 40% 12T Adhesive B5 37% phosphoric acid Adhesive A6 37% phosphoric acid Adhesive B______________________________________ Notes: .sup.(1) Adhesive A is a commercial orthodontic bonding resin sold under the trademark "ORTHOMITE IIS" by Rocky Mountain Orthodontics, Colorado .sup.(2) Adhesive B is a commercial orthodontic bonding resin sold under the trademark "AUTOTACH" by L. D. Caulk Co., Milford

After the specimens were stored at 37.degree. C. and 100% relative humidity for 24 hours, the tensile bond strengths were determined using an Instron testing machine.

The bond test results, in terms of the absolute force required to achieve fracture along the bracket-tooth interfacial bond and the force per unit area of bracket-tooth interfacial bond, are reproduced in the following Table IV:

TABLE IV______________________________________ Bond Fracture Force Coeff. StrengthTooth No. in mean Range of Var- kg/Group Group (kg) S.D. (kg) iation cm.sup.2 PSI______________________________________1 10 7.84 1.81 5.7 to 11.1 23.08 25.13 359.22 10 10.64 3.12 5.8 to 16.0 29.32 34.1 487.73 10 5.67 1.08 4.5 to 7.2 19.05 18.17 259.84 10 4.33 0.92 3.0 to 5.7 21.25 13.88 198.55 10 11.11 1.64 7.8 to 12.6 14.76 35.6 509.26 10 14.38 1.91 11.3 to 17.1 13.28 46.09 659.1______________________________________

The results of Table IV show that the bond strength can be varied as desired depending on the conditions of formation of the crystal growth and can be made to approach that of the acid-etch technique.

EXAMPLE 3

A solution of polyacrylic acid of molecular weight 12,000 (12T) was prepared as described in Example 1 and adjusted to a concentration of 35%. The sulphate concentration was 3.7%. This solution was used to treat the labial surfaces of bovine teeth and orthodontic attachments were bonded as described in Example 2. The bonded assemblies were stored in water at 37.degree. C. for varying periods of time up to 4 weeks before testing the tensile bond strength.

The results, in terms of the force per unit area of attachment-tooth interfacial bond required to achieve fracture, are reproduced in the following Table V:

TABLE V______________________________________ Bond Strength Treatment Coeffi- Time Bond- Sam- cient ofTreat- (Water ing ple mean Variationment Storage) Agent Size (kg/cm.sup.2) S.D. (%)______________________________________None(Control) 24 hrs A.sup.(1) 25 21.7 16.8 79.7 B.sup.(2) 28 18.7 16.6 88.8Acid 24 hrs A 16 107.1 26.6 24.8Etch B 25 117.0 26.0 22.212T 24 hrs A 18 113.0 31.9 28.2 B 23 118.0 23.9 20.212T 1 wk A 15 127.4 29.1 22.8 B 15 118.1 13.9 11.812T 2 wk A 12 83.5 25.5 30.5 B 15 110.8 22.3 20.112T 4 wk A 12 78.4 24.4 31.1 B 14 107.8 36.2 33.6Acid 1 wk A 14 117.1 34.1 29.1Etch B 15 130.3 20.6 15.8Acid 2 wk A 12 100.9 26.4 26.1Etch B 17 129.4 18.7 14.5Acid 4 wk A 12 87.7 38.1 43.4Etch B 15 112.2 18.3 16.3______________________________________ Notes: .sup.(1) Bonding Agent A is a commercial orthodontic bonding resin sold under the trademark "ORTHOMITE IIS" by Rocky Mountain Orthodontics, Colorado .sup.(2) Bonding Agent B is a commercial orthodontic bonding resin sold under the trademark "CONCISE" by 3M Company, Minnesota

The results of the above Table V illustrate that comparable results for the crystal bond technique when compared to the acid etch technique even after 4 weeks of water storage.

SUMMARY OF DISCLOSURE

In summary of this disclosure, the present invention provides a new method of bonding to teeth and other calcified tissues which is a substantial improvement over the conventional acid-etch technique. Modifications are possible within the scope of this invention.

Claims

1. In a method of bonding materials to calcified tissues including human teeth, the improvement which comprises forming a crystal growth of gypsum crystals having a length of about 20 micrometers and a thickness of about 2 to 5 micrometers adhered to and nucleated within a surface of said tissues and interlocking said bonding with said crystal growth.

2. The method of claim 1 wherein said crystal growth is formed by interacting said calcified tissue with a solution containing ionic species capable of forming said gypsum crystals.

3. The method of claim 2 wherein said solution is of a substantially non-flowing viscosity, whereby said solution may be confined to a specific region of said surface.

4. The method of claim 2 or 3 wherein said solution is mildly acidic to effect a slight chemical reaction with the tissue surface to release calcium ions therefrom.

5. The method of claim 2 wherein said solution is an aqueous solution of polyacrylic acid containing at least about 1% of sulphate ions.

6. The method of claim 5 wherein said polyacrylic acid has a molecular weight of about 1000 to 100,000 and a concentration of from about 10 to about 60%.

7. A method of treating calcified tissue, which comprises contacting a surface of said tissue with a substance capable of forming gypsum crystals having a length of about 20 micrometers and a thickness of about 2 to 5 micrometers attached to and nucleated within the surface for a time sufficient to form said crystals, and subsequently removing said substance from said surface.

8. The method of claim 7 wherein said substance is an aqueous solution of polyacrylic acid having a molecular weight of about 1000 to 100,000 containing at least about 1% of sulphate ions and a concentration from about 10 to about 60%, to form needle-shaped gypsum crystals nucleated within the tissue surface and having a spherulistic habit.

9. The method of claim 8 wherein said solution additionally contains fluoride ions.

10. The method of claim 8 or 9 wherein said solution has a substantially non-flowing viscosity, whereby said solution may be confined to a specific region of said surface, and said removal of said substance from said surface is effected by washing said solution from said surface.

11. The method of claim 7 wherein said calcified tissue is human teeth.