Patent Grant
7448631
1. Field of the Invention
The present invention relates to a braiding yarn made of expanded graphite which is suitable for a gland packing that is to be used in a shaft seal part of a fluid apparatus or the like, and also to such a gland packing.
2. Description of Related Art
Conventionally, a braiding yarn made of expanded graphite has been proposed in which plural expanded graphite tapes having a predetermined width are stacked to constitute an expanded graphite base member, and the outer periphery of the expanded graphite base member is externally reinforced by knitting or tubular-plain-stitching reinforcing wire members such as stainless steel wires (for example, see Japanese Patent Application Laying-Open No. 6-17937).
In the braiding yarn made of expanded graphite having this configuration, the outer periphery of the expanded graphite base member is covered by, for example, knitting reinforcing wire members such as stainless steel wires. During a process of braiding plural yarns to produce a gland packing, therefore, the knit of the reinforcing wire members sufficiently resists tensile and torsional forces produced in each of the yarns, whereby the expanded graphite base member in the knit is prevented from being broken.
However, the braiding yarn made of expanded graphite in which the outer surface of the expanded graphite base member is covered by knitting or tubular-plain-stitching reinforcing wire members such as stainless steel wires has a problem in that the process of covering the expanded graphite base member with knitting or tubular-plain-stitching the reinforcing wire members requires a long time period and hence the productivity is poor.
The inventor thought up a configuration in which an expanded graphite base member is externally reinforced by spirally winding a reinforcing wire member therearound.
However, it was found that, when such a braiding yarn made of expanded graphite is bent with a small radius of curvature, the reinforcing wire member on the inner peripheral side of the bent portion slacks, and the reinforcing wire member separates and protrudes from the outer face of the expanded graphite base member on the inner peripheral side of the bent portion.
In the case where the counter member is, for example, a rotation shaft, when such slack once occurs, the slack is repeatedly bent in the forward and reverse rotational directions of the rotation shaft in accordance with forward and reverse rotations of the rotation shaft. When time elapses, there arises a possibility that the basal portion of the slack is broken. When such breakage occurs, a broken surface may damage the counter member. In the case where the counter member is a stem, in accordance with reciprocal motion of the stem, such slack is repeatedly bent in the reciprocal directions, and, when time elapses, there arises a possibility that the basal portion of the slack is broken. When such breakage occurs, a broken surface may damage the counter member.
The invention has been conducted in order to solve the problems. It is an object of the invention to provide a braiding yarn made of expanded graphite in which a reinforcing wire member is spirally wound around an expanded graphite base member, and, even when the braiding yarn is bent with a small radius of curvature, the reinforcing wire member can be surely prevented from slacking on the inner peripheral side of the bent portion, and the sealing property is not impaired, and also a gland packing in which such a braiding yarn made of expanded graphite is used.
In the braiding yarn disclosed in Japanese Patent Application Laying-Open No. 6-17937, most of the outer surface of the expanded graphite base member is covered by the knitted or tubular-plain-stitched reinforcing wire members such as stainless steel wires, and therefore there is a problem in that the adaptability and sealing property with respect to a counter member such as a rotation shaft or a stem (hereinafter, referred to merely as “counter member”) which are characteristics of the expanded graphite base member cannot be sufficiently exerted. As shown in
The invention has been conducted in order to solve the problems. It is another object of the invention to provide a braiding yarn made of expanded graphite which has sufficient resistance due to external reinforcement against tensile and torsional forces produced in each of yarns during a process of producing a gland packing, and in which the productivity can be enhanced, and the adaptability and sealing property with respect to a counter member can be improved.
It is a further object of the invention to provide a gland packing in which an externally reinforced braiding yarn is used, and in which the adaptability and sealing property with respect to a counter member can be improved.
The braiding yarn made of expanded graphite of the invention is a braiding yarn made of expanded graphite in which an expanded graphite base member is externally reinforced by a reinforcing wire member, and characterized in that the reinforcing wire member is configured by a thin wire member having a diameter of 0.05 to 0.2 mm, and the reinforcing wire member is spirally wound around an outer periphery of the expanded graphite base member at a narrow pitch of 0.5 to 5 mm without slack.
In the braiding yarn made of expanded graphite of the invention, preferably, the reinforcing wire member is wound around the outer periphery of the expanded graphite base member by a tightening force of 0.1 to 30 N without slack.
In the braiding yarn made of expanded graphite of the invention, preferably, the reinforcing wire member is configured by a metal wire.
In the braiding yarn made of expanded graphite of the invention, preferably, internal reinforcing members are embedded in the expanded graphite base member.
In the braiding yarn made of expanded graphite of the invention, preferably, the reinforcing wire member such as the metal wire is wound around the expanded graphite base member as at least a single spiral.
In the braiding yarn made of expanded graphite of the invention, preferably, the reinforcing wire member such as the metal wire is wound around the expanded graphite base member as at least two spirals which intersect with each other.
The gland packing of the invention is a gland packing in which a plurality of braiding yarns are braided or twisted, and characterized in that
each of the braiding yarns is formed by externally reinforcing an expanded graphite base member by means of a reinforcing wire member, the reinforcing wire member is configured by a thin wire member having a diameter of 0.05 to 0.2 mm, and the reinforcing wire member is spirally wound around an outer periphery of the expanded graphite base member at a narrow pitch of 0.5 to 5 mm without slack.
In the gland packing of the invention, preferably, the reinforcing wire member is wound around the outer periphery of the expanded graphite base member by a tightening force of 0.1 to 30 N without slack.
In the gland packing of the invention, preferably, the reinforcing wire member is configured by a metal wire.
In the gland packing of the invention, preferably, internal reinforcing members are embedded in the expanded graphite base member.
In the gland packing of the invention, preferably, the reinforcing wire member is wound around the expanded graphite base member as at least a single spiral.
In the gland packing of the invention, preferably, the reinforcing wire member is wound around the expanded graphite base member as at least two spirals which intersect with each other.
The other braiding yarn made of expanded graphite of the invention is characterized in that a thin reinforcing wire member having a diameter of 0.05 to 0.2 mm is spirally embedded in a longitudinal direction on an outer surface side of an expanded graphite base member. In this case, as the reinforcing wire member, various wire members including: organic wire members such as rayon, phenol, aramid, PBI, PBO, PTFE, PPS, and PEEK; inorganic wire members such as glass fibers, carbon fibers, and ceramic fibers; wire members of mineral fibers; and metal wire members such as stainless steel, inconel, and monel can be selectively used in accordance with the use.
In the other braiding yarn made of expanded graphite of the invention, preferably, the expanded graphite base member is formed by a twisted expanded graphite tape, and the reinforcing wire member is embedded in an inner side of and along an edge of the expanded graphite tape which is spirally exposed from an outer surface of the twisted expanded graphite base member.
In the other braiding yarn made of expanded graphite of the invention, preferably, the reinforcing wire member is spirally embedded in a state where part or whole of a section of the reinforcing wire member bites into an outer surface of the expanded graphite base member.
The other gland packing of the invention is a gland packing in which a plurality of braiding yarns are braided or twisted, and characterized in that, in each of the braiding yarns, a thin reinforcing wire member having a diameter of 0.05 to 0.2 mm is spirally embedded in a longitudinal direction on an outer surface side of an expanded graphite base member. In this case, in the same manner as described above, as the reinforcing wire member, various wire members including: organic wire members such as rayon, phenol, aramid, PBI, PBO, PTFE, PPS, and PEEK; inorganic wire members such as glass fibers, carbon fibers, and ceramic fibers; wire members of mineral fibers; and metal wire members such as stainless steel, inconel, and monel can be selectively used in accordance with the use.
In the other gland packing of the invention, preferably, the expanded graphite base member of the braiding yarn is formed by a twisted expanded graphite tape, and the reinforcing wire member is embedded in an inner side of and along an edge of the expanded graphite tape which is spirally exposed from an outer surface of the twisted expanded graphite base member.
In the other gland packing of the invention, preferably, the reinforcing wire member of the braiding yarn is spirally embedded in a state where part or whole of a section of the reinforcing wire member bites into an outer surface of the expanded graphite base member.
The invention exerts the following functions and effects.
According to the braiding yarn made of expanded graphite of the invention, the reinforcing wire member is configured by a thin wire member having a diameter of 0.05 to 0.2 mm, and the reinforcing wire member is wound around an outer periphery of the expanded graphite base member at a narrow pitch of 0.5 to 5 mm without slack. Therefore, it is possible to attain an effect that, even when the braiding yarn made of expanded graphite is bent with a small radius of curvature, the reinforcing wire member is surely prevented from slacking on the inner peripheral side of the bent portion, and the sealing property is not impaired.
As the reinforcing wire member, various wire members including: organic wire members (for example, rayon, phenol, aramid, PBI, PBO, PTFE, PPS, and PEEK); inorganic wire members (for example, glass fibers, carbon fibers, and ceramic fibers); wire members of mineral fibers; and metal wire members (for example, stainless steel, inconel, and monel) can be selectively used in accordance with the use.
According to the braiding yarn made of expanded graphite of the invention, the reinforcing wire member is wound around the outer periphery of the expanded graphite base member by a tightening force of 0.1 to 30 N. Even when the braiding yarn is bent with a small radius of curvature, therefore, it is possible to more surely prevent the reinforcing wire member from slacking on the inner peripheral side of the bent portion.
According to the braiding yarn made of expanded graphite of the invention, the reinforcing wire member is configured by a metal wire. A metal wire is easily plastically deformed. When the reinforcing wire member is spirally wound around the outer periphery of the expanded graphite base member, therefore, the reinforcing wire member is plastically deformed so as be adapted more preferably to the expanded graphite base member, and more surely prevented from slacking.
According to the braiding yarn made of expanded graphite of the invention, internal reinforcing members (for example, organic, inorganic, mineral, or metal fiber members, or organic, inorganic, mineral, or metal wire members) are embedded in the expanded graphite base member. Therefore, the tensile and torsional strengths of the expanded graphite base member itself are improved.
According to the braiding yarn made of expanded graphite of the invention, the reinforcing wire member is wound around the expanded graphite base member as at least a single spiral without slack. Even when the braiding yarn made of expanded graphite is bent with a small radius of curvature, therefore, the metal wire can be surely prevented from slacking on the inner peripheral side of the bent portion.
According to the braiding yarn made of expanded graphite of the invention, the reinforcing wire member is wound around the expanded graphite base member as at least two spirals which intersect with each other. Even when the braiding yarn made of expanded graphite is bent with a small radius of curvature, therefore, the metal wire can be surely prevented from slacking on the inner peripheral side of the bent portion.
According to the gland packing of the invention, the reinforcing wire member in each of braided or twisted braiding yarns is configured by a thin wire having a diameter of 0.05 to 0.2 mm, and the reinforcing wire member is spirally wound around an outer periphery of the expanded graphite base member at a narrow pitch of 0.5 to 5 mm without slack. As a result, even when the gland packing is bent with a small radius of curvature, it is possible to surely prevent the reinforcing wire member from slacking on the inner peripheral side of the bent portion. Moreover, the sealing property is not impaired.
As the reinforcing wire member, as described above, various wire members including: organic wire members (for example, rayon, phenol, aramid, PBI, PBO, PTFE, PPS, and PEEK); inorganic wire members (for example, glass fibers, carbon fibers, and ceramic fibers); wire members of mineral fibers; and metal wire members (for example, stainless steel, inconel, and monel) can be selectively used in accordance with the use.
According to the gland packing of the invention, in the state where the reinforcing wire member is wound around the outer periphery of the expanded graphite base member by a tightening force of 0.1 to 30 N, even when the gland packing is bent with a small radius of curvature, it is possible to more surely prevent the reinforcing wire member from slacking on the inner peripheral side of the bent portion.
According to the gland packing of the invention, the reinforcing wire member is configured by a metal wire. A metal wire is easily plastically deformed. When the reinforcing wire member is spirally wound around the outer periphery of the expanded graphite base member, therefore, the reinforcing wire member is plastically deformed so as be adapted more preferably to the expanded graphite base member, and more surely prevented from slacking.
The metal wire is adapted more preferably to the outer periphery of the expanded graphite base member, and spirally wound therearound without slack. Even when the gland packing is bent with a small radius of curvature, it is possible to more surely prevent the reinforcing wire member from slacking on the inner peripheral side of the bent portion.
According to the gland packing of the invention, the internal reinforcing members (for example, organic, inorganic, mineral, or metal fiber members, or organic, inorganic, mineral, or metal wire members) are embedded in the expanded graphite base member. Therefore, a gland packing having a high pressure resistance can be obtained. Moreover, places of the expanded graphite base member where a crack is produced during a braiding or twisting process can be reduced, and a more preferable sealing property can be obtained.
According to the gland packing of the invention, a metal wire is wound around the expanded graphite base member as at least a single spiral. Even when the gland packing is bent with a small radius of curvature, therefore, the metal wire can be surely prevented from slacking on the inner peripheral side of the bent portion.
According to the gland packing of the invention, a metal wire is wound around the expanded graphite base member as at least two spirals which intersect with each other. Even when the gland packing is bent with a small radius of curvature, therefore, the metal wire can be surely prevented from slacking on the inner peripheral side of the bent portion.
According to the other braiding yarn made of expanded graphite of the invention, the reinforcing wire member is configured by a thin wire having a diameter of 0.05 to 0.2 mm, and the thin reinforcing wire member is spirally embedded in a longitudinal direction on the outer surface side of the expanded graphite base member. Therefore, the reinforcing wire member resists tensile and torsional forces produced in each of the yarns during a process of producing the gland packing, and the expanded graphite base member is prevented from being broken.
Since the reinforcing wire member is requested simply to be spirally wound around the outer periphery of the expanded graphite base member, moreover, the time period required in the process of the winding is very shorter than that required in the process of covering through knitting or tubular-plain-stitching in the conventional art, and therefore the productivity can be enhanced.
The reinforcing wire member is configured by a thin wire having a diameter of 0.05 to 0.2 mm, and spirally embedded in the outer periphery of the expanded graphite base member. Therefore, the contact pressure and area of the expanded graphite base member with respect to a counter member such as a rotation shaft or a stem can be sufficiently ensured as compared with a conventional braiding yarn configured by an expanded graphite base member which is mostly covered by knitted or tubular-plain-stitched reinforcing wire members. Therefore, it is possible to attain an effect that the adaptability and sealing property with respect to a counter member can be improved.
According to the other braiding yarn made of expanded graphite of the invention, the expanded graphite base member which is configured by twisting an expanded graphite tape can improve the tensile and torsional strengths of the expanded graphite base member itself, and the improved strengths cooperate with the reinforcing action of the reinforcing wire member, so that a braiding yarn made of expanded graphite which is highly resistant to tension and torsion can be obtained. Since the reinforcing wire member is embedded in the inner side of and along an edge of the spiral expanded graphite tape of the expanded graphite base member, moreover, the whole outer surface of the expanded graphite base member can be exposed. Therefore, the contact pressure and area of the expanded graphite base member with respect to a counter member can be easily ensured, and the adaptability and sealing property can be further improved.
According to the other braiding yarn made of expanded graphite of the invention, the reinforcing wire member is spirally embedded in a state where part or whole of a section of the reinforcing wire member bites into the outer surface of the expanded graphite base member. Therefore, the outer surface of the expanded graphite base member can be made closer to a counter member by a degree corresponding to the biting amount. When the expanded graphite base member receives an external compression load to expand, the contact pressure and area with respect to the counter member can be easily ensured, and the adaptability and sealing property with respect to the counter member can be further improved.
According to the other gland packing of the invention, in each of the plural braided or twisted branding yarns, a thin reinforcing wire member having a diameter of 0.05 to 0.2 mm is spirally embedded in the longitudinal direction on an outer surface side of an expanded graphite base member. Therefore, the reinforcing wire member can exert a sufficient resistance force due to the external reinforcement against tensile and torsional forces produced in each of the yarns during a process of producing the gland packing. Since the reinforcing wire member is requested simply to be spirally wound around the outer periphery of the expanded graphite base member, moreover, the time period required in the process of the winding is very shorter than that required in the process of covering through knitting or tubular-plain-stitching in the conventional art, and therefore the productivity can be enhanced. The reinforcing wire member is configured by a thin wire having a diameter of 0.05 to 0.2 mm, and spirally embedded in the outer periphery of the expanded graphite base member. Therefore, the contact pressure and area of the expanded graphite base member with respect to a counter member can be sufficiently ensured as compared with those in a conventional braiding yarn configured by an expanded graphite base member which is mostly covered by knitted or tubular-plain-stitched reinforcing wire members. Consequently, the adaptability and sealing property with respect to the counter member can be improved.
According to the other gland packing of the invention, the expanded graphite base member of the braiding yarn is formed by twisting an expanded graphite tape. Therefore, the tensile and torsional strengths of the expanded graphite base member itself can be improved, and the improved strengths cooperate with the reinforcing action of the reinforcing wire member, so that a braiding yarn made of expanded graphite which is highly resistant to tension and torsion can be obtained. Since the reinforcing wire member is embedded in the inner side of and along an edge of the spiral expanded graphite tape of the expanded graphite base member, moreover, it is possible to obtain a gland packing which is excellent in adaptability and sealing property with respect to a counter member.
According to the other gland packing of the invention, the reinforcing wire member of the braiding yarn is spirally embedded in a state where part or whole of a section of the reinforcing wire member bites into the outer periphery of the expanded graphite base member. Therefore, it is possible to obtain a gland packing in which the contact pressure and area of the expanded graphite base member with respect to a counter member is easily ensured and the adaptability and sealing property with respect to a counter member are excellent.
Hereinafter, a first embodiment of the invention will be described with reference to the accompanying drawings.
As the reinforcing wire member 3, a thin wire member of stainless steel (SUS 304) having a diameter of 0.05 to 0.2 mm, preferably 0.1 to 0.2 mm is used. The braiding yarn made of expanded graphite 1 is configured by winding the stainless steel wire around the outer periphery of the expanded graphite base member 2 by a tightening force of 0.1 to 30 N, preferably 10 to 20 N without slack.
As described above, the reinforcing wire member 3 is configured by the thin wire member having a diameter of 0.05 to 0.2 mm, and the thin reinforcing wire member 3 is spirally wound at a narrow pitch P of 0.5 to 5 mm around the outer periphery of the expanded graphite base member 2 without slack. Even when the braiding yarn made of expanded graphite 1 is bent with a small radius of curvature, therefore, the reinforcing wire member 3 can be surely prevented from slacking on the inner peripheral side of the bent portion, and the contact pressure and area of the expanded graphite base member 2 with respect to a counter member such as a rotation shaft or a stem can be sufficiently ensured, whereby the adaptability and sealing property with respect to a counter member can be improved.
When the diameter of the reinforcing wire member 3 is smaller than 0.05 mm, the reinforcing wire member 3 is easily broken away during the winding process by the tightening force of 0.1 to 30 N, and the assuredness of the tight spiral winding on the outer periphery of the expanded graphite base member 2 without slack is lowered. When the diameter of the reinforcing wire member 3 is larger than 0.2 mm, the distance L between the outer face of the expanded graphite base member 2 and the apex of the outer face of the reinforcing wire member 3 is increased as shown in
When the pitch P of the spirally wound reinforcing wire member 3 is smaller than 0.5 mm, the surface coverage ratio of the reinforcing wire member 3 is excessively high. Therefore, the expanded graphite base member 2 hardly outward expands, the contact area of the expanded graphite base member 2 with respect to the counter member is reduced, and the adaptability and sealing property are reduced. When the pitch P is larger than 5 mm, even in the case where the reinforcing wire member 3 is wound around the outer periphery of the expanded graphite base member 2 without slack, the winding angle of the reinforcing wire member 3 with respect to the axis of the twisted expanded graphite base member 2 becomes small, and the reinforcing wire member 3 easily slacks. Therefore, it is necessary to wind the reinforcing wire member 3 around the outer periphery of the expanded graphite base member 2 at a narrow pitch of 0.5 to 5 mm.
The spiral winding of the reinforcing wire member 3 is not restricted to the single-spiral winding such as shown in
When the reinforcing wire member 3 is wound as two spirals around the outer periphery of the expanded graphite base member 2 without slack in this way, the reinforcing action of the reinforcing wire member 3 is largely enhanced as compared with that in the configuration where the reinforcing wire member is wound as a single spiral. Therefore, the situation where the braiding yarn is cut off during a braiding or twisting process for forming a gland packing is less caused, and places of the expanded graphite base member 2 where a crack is produced can be remarkably reduced.
As shown in
When the inner reinforcing members 6 are embedded as described above, places of the expanded graphite base member 2 where a crack is produced during a braiding or twisting process for forming a gland packing are remarkably reduced.
Expanded graphite tapes having a width of 20 mm and a thickness of 0.2 mm were twisted to form expanded graphite base members 2. The reinforcing wire member 3 of a stainless steel wire having a diameter of 0.05 to 0.2 mm was wound as a single spiral around the outer periphery of each of the base members at a pitch of 0.5 to 6.0 mm without slack, thereby producing braiding yarns made of expanded graphite 1A having an outer diameter of about 3 mm (the configuration of
As seen from Table 1 above, when the diameter of the reinforcing wire member 3 is 0.05 to 0.2 mm and the winding pitch P of the reinforcing wire member 3 is 0.5 to 6.0 mm, in the all of the braiding yarns made of expanded graphite 1A, 1B, no slack was observed in the reinforcing wire member 3 on the inner peripheral side of the bent portion in the case where the braiding yarn was bent with a radius of curvature of 2 mm. By contrast, when the radius of curvature of the inner periphery was 1 mm, in the all of the braiding yarns made of expanded graphite 1A, 1B, a slack was observed in the reinforcing wire member 3 on the inner peripheral side of the bent portion in the case where the winding pitch P of the reinforcing wire member 3 was 6.0 mm.
Braiding yarns made of expanded graphite 1A, 1B, which are identical with the braiding yarns made of expanded graphite 1A, 1B having the single and two spiral configurations produced in the experiment of Table 1 above, were produced. The braiding yarns made of expanded graphite 1A, 1B were formed into a ring-like shape having inner diameter of 32 mm, and used for sealing a stem. Under conditions of the tightening pressure of 39.2 MPa and the pressure of hot water×the temperature: 17.2 MPa×350° C., leaking of the hot water was checked after first, second, and third cycles of three hours (500 reciprocations). The results are listed in Table 2 below.
As shown in Table 2 above, it was ascertained that, in the all of the braiding yarns made of expanded graphite 1A, 1B, leakage did not occur, and the sealing property is not adversely affected.
Next, embodiments of the gland packing of the invention according to claim 7 will be described.
Referring to
The manner of braiding is not restricted to the eight-strand square braiding, and it is a matter of course that the sixteen-, eighteen-, twenty four-, or thirty two-strand square braiding, or the tubular braiding in which a core is inserted may be employed.
Braiding yarns made of expanded graphite 1A, 1B which are identical with the braiding yarns made of expanded graphite 1A, 1B having the single and two spiral configurations produced in the experiment of Table 1 above were produced. Gland packings which were braided by bundling eight, sixteen, twenty-four, or thirty-two braiding yarns made of expanded graphite 1A, 1B were bent with a radius of curvature of inner periphery of 20 mm or 10 mm, and presence or absence of a slack in the reinforcing wire members 3 on the inner peripheral side of the bent portion was observed. The results are listed in Table 3 below.
In table 3 above, it was ascertained that no slack in the reinforcing wire member was produced on the inner peripheral side of the bent portion of the gland packing, not only in the case where the gland packing was bent with a radius of curvature of 20 mm of the inner periphery, but also in the case where the gland packing was bent with a smaller radius of curvature of 10 mm of the inner periphery.
The eight, sixteen, twenty-four, and thirty-two braiding gland packings which were used in the experiment of Table 3 above were formed into a ring-like shape having inner diameter of 32 mm, and used for sealing a stem. Under conditions of the tightening pressure of 39.2 MPa and the pressure of hot water×the temperature: 17.2 MPa×350° C., leaking of the hot water was checked after first, second, and third cycles of three hours (500 reciprocations). The results are listed in Table 4 below.
As shown in Table 4 above, it was ascertained that, in the all of the gland packings, leakage did not occur, and the sealing property is not adversely affected.
[Other Modifications]
The expanded graphite base member 2 may be an expanded graphite base member 2 which is configured by stacking a plurality of expanded graphite tapes as shown in
Of course, the form of the gland packing is not restricted to that which is obtained by braiding plural braiding yarns. For example, the gland packing may be produced by twisting plural braiding yarns.
In the above, the configurations in which the braiding yarns made of expanded graphite 1 of the inventions set forth in claims 1 to 6 are used as braiding yarns of the gland packing 4 have been described. The gland packing 4 of the invention is not restricted to these configurations, and may be configured as set forth in claims 7 to 12 after braiding or in the use.
Hereinafter, a second preferred embodiment of the invention will be described with reference to the drawings.
As the reinforcing wire member 3, a thin wire member of stainless steel (SUS 304) having a diameter of 0.05 to 0.2 mm, preferably 0.1 to 0.2 mm is used. The braiding yarn made of expanded graphite 1 is configured by spirally winding the stainless steel wire around the outer surface of the expanded graphite base member 2 by a tightening force of 0.1 to 30 N, preferably 10 to 20 N without slack, so that the reinforcing wire member is embedded in the inner side of and along the edge 4 of the expanded graphite tape.
As described above, the reinforcing wire member 3 is configured by a thin wire member having a diameter of 0.05 to 0.2 mm, and the thin reinforcing wire member 3 is embedded in the outer periphery of the expanded graphite base member 2 on the inner side of and along the edge 4 of the expanded graphite tape. Therefore, the reinforcing wire member can exert a sufficient resistance force due to the external reinforcement and against tensile and torsional forces produced in each of the braiding yarns 1 during the process of producing the gland packing.
The reinforcing wire member 3 is requested simply to be spirally wound around the outer surface of the expanded graphite base member 2. Therefore, the time period required in the process of the winding is very shorter than that required in the process of knitting or tubular-plain-stitching in the conventional art, and the productivity can be enhanced.
The reinforcing wire member 3 is configured by a thin wire member having a diameter of 0.05 to 0.2 mm, and embedded without being exposed from the outer surface of the expanded graphite base member 2. Therefore, the contact pressure and area of the expanded graphite base member 2 with respect to a counter member such as a rotation shaft or a stem can be sufficiently ensured, so that the adaptability and sealing property with respect to the counter member can be enhanced.
When the diameter of the reinforcing wire member 3 is smaller than 0.05 mm, the reinforcing wire member 3 is easily broken away during the winding process by the tightening force of 0.1 to 30 N, and therefore the configuration lacks the assuredness of the tight spiral winding on the outer periphery of the expanded graphite base member 2. When the diameter of the reinforcing wire member 3 is larger than 0.2 mm, the reinforcing wire member is hardly embedded in the inner side of the edge 4 of the expanded graphite tape. Therefore, it is preferable to configure the reinforcing wire member 3 by a thin wire member having a diameter of 0.05 to 0.2 mm, preferably 0.1 to 0.2 mm.
The reinforcing wire member 3 is not restricted to be spirally wound on the inner side and along the edge 4 of the expanded graphite tape of the expanded graphite base member 2 as shown in
The winding of the reinforcing wire member 3 may be formed as an external reinforcement of two spirals which are wound in opposite directions to intersect with each other. In the same manner as the above described embodiment, the reinforcing wire member 3 is spirally wound as a single spiral at a narrow pitch of 0.5 to 5 mm, preferably a narrow pitch of 1 to 3 mm without slack.
When the reinforcing wire member 3 is spirally embedded in the state where part or whole of a section of the reinforcing wire member 3 bites into the outer surface of the expanded graphite base member 2 as described above, the outer surface of the expanded graphite base member 2 can be made closer to a counter member 9 by a degree corresponding to the biting amount of the reinforcing wire member 3 as shown in
Next, an embodiment of the gland packing according to the invention of claim 16 will be described.
As shown in
The expanded graphite base member 2 may be an expanded graphite base member 2 which is configured by stacking a plurality of expanded graphite tapes as shown in
Of course, the form of the gland packing 4 is not restricted to a gland packing having a form which is obtained by braiding plural braiding yarns made of expanded graphite 1. For example, the gland packing may be produced by twisting plural braiding yarns made of expanded graphite 1.
An example of the braiding yarn made of expanded graphite will be described. Expanded graphite tapes having a width of 20 mm and a thickness of 0.2 mm were twisted to form expanded graphite base members 2. The reinforcing wire member 3 of a stainless steel wire having a diameter of 0.05 to 0.2 mm was wound as a single spiral around the outer surfaces of the expanded graphite base members 2 at a pitch of 0.5 to 6.0 mm without slack so as to be embedded in the inner side of and along an edge 4 of each of the expanded graphite tapes, thereby producing braiding yarns made of expanded graphite 1A having an outer diameter of about 3 mm (the braiding yarn made of expanded graphite 1 of
The thus produced braiding yarns made of expanded graphite 1A, 1B respectively having the single and two spiral reinforcing wire member configurations were formed into a ring-like shape having an inner diameter of 32 mm, and used for sealing a stem. Under conditions of the tightening pressure of 39.2 MPa and the pressure of hot water×the temperature: 17.2 MPa×350° C., leaking of the hot water was checked after first, second, and third cycles of three hours (500 reciprocations). The results are listed in the table of
As apparent from the table, it was ascertained that the all of the braiding yarns made of expanded graphite 1A, 1B are excellent in adaptability and sealing property with respect to a stem, and are free from leakage.
An example of the gland packing will be described. Braiding yarns made of expanded graphite 1A, 1B which are identical with the braiding yarns made of expanded graphite 1A, 1B respectively having the single and two-spiral reinforcing wire member configurations produced in Example 2-1 were produced. Gland packings of the eight-, sixteen-, eighteen-, twenty four-, or thirty two-strand square braiding were produced by braiding a bundle of eight, sixteen, twenty-four, or thirty-two braiding yarns made of expanded graphite 1A, 1B. The gland packings were formed into a ring-like shape having an inner diameter of 32 mm, and used for sealing a stem. Under conditions of the tightening pressure of 39.2 MPa and the pressure of hot water×the temperature: 17.2 MPa×350° C., leaking of the hot water was checked after first, second, and third cycles of three hours (500 reciprocations). The results are listed in the table of
As apparent from the table, it was ascertained that the all of the gland packings are excellent in adaptability and sealing property with respect to a stem, and are free from leakage.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2004-104046 | Mar 2004 | JP | national |
| 2004-104070 | Mar 2004 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 559080 | Hughes | Apr 1896 | A |
| 1325876 | McClure | Dec 1919 | A |
| 1840449 | Hubbard et al. | Jan 1932 | A |
| 2249981 | Roe | Jul 1941 | A |
| 2722861 | Francis | Nov 1955 | A |
| 3438841 | Zumeta et al. | Apr 1969 | A |
| 5339520 | Leduc | Aug 1994 | A |
| 5549306 | Ueda | Aug 1996 | A |
| 5699680 | Guerlet et al. | Dec 1997 | A |
| 6502382 | Fujiwara et al. | Jan 2003 | B1 |
| 6644007 | Fujiwara et al. | Nov 2003 | B2 |
| 7140171 | Ueda et al. | Nov 2006 | B2 |
| 7353645 | Ueda et al. | Apr 2008 | B2 |
| 20050238862 | Ueda et al. | Oct 2005 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 098 116 | May 2001 | EP |
| 6-17937 | Jan 1994 | JP |
| WO 2004025149 | Mar 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20050218604 A1 | Oct 2005 | US |