Brake disc for a disc braking system

Information

  • Patent Grant
  • 6161661
  • Patent Number
    6,161,661
  • Date Filed
    Tuesday, June 6, 2000
    24 years ago
  • Date Issued
    Tuesday, December 19, 2000
    23 years ago
Abstract
A brake disk has a thickness D1 and includes two friction plates disposed parallel to each other, between which an airflow duct having a width D2 is located in a substantially central position. The brake disk is made of a gray cast iron material containing molybdenum. The ratio of the disk thickness D1 to the airflow duct width D2 is 3.0.ltoreq.D1/D2.ltoreq.5. The brake disk has a great resistance to temperature change and a long operating life.
Description

BACKGROUND AND SUMMARY OF INVENTION
The invention relates to a brake disk for disk brakes, especially for disk brakes of utility vehicles.
In EP 0 778 355 A1 such a brake disk is disclosed, which has a disk thickness D1 and two friction disks arranged parallel to one another, between which an air channel lying substantially centrally with a width D2 is formed. The ratio between the disk thickness D1 and air channel thickness D2 is about 3.6 in a disk casting. The disk brake consists of a gray cast iron material with a relatively low molybdenum content of 0.01 to 0.6 percent.
It is already known also from WO96/07766 (PCT/SE95/00927) to provide the gray cast metal with an addition of molybdenum. However, it is stated in this publication that a molybdenum content of 0.3% or more is disadvantageous, since it makes the cost of the material increase too greatly and manufacture is difficult.
A brake disk of gray cast iron material with a molybdenum content is also disclosed in DE 40 26 611 C2.
The design of the generic brake disk has proven to be basically sound. In this connection, see DE 195 44 559 C1. There is a need for improvement, however, with regard to a further reduction of the disk's tendency to form cracks and with regard to increasing the life of the disk. The same problem is also true of the brake disk disclosed in DE 40 26 611 C2. Additional state of the art which deals with brake disks and their materials is disclosed in DE 44 26 0911 A1, DE 37 04 679 A1, DE-OS 22 35 627, DE 94 00 562 U1 and DE 87 08 264 U1.
Setting out from the generic state of the art the invention is addressed to the problem of optimizing the brake disk in regard to a further reduction of the tendency toward cracking and in regard to increasing the useful life.
The invention solves this problem in the generic brake disk and in brake disks in which the ratio between disk thickness D1 and air channel width D2 satisfies the condition
3.0.ltoreq.D1/D2.ltoreq.5,
that the brake disk consists of a gray cast iron material with a molybdenum content that amounts to 0.6 to 0.8 percent.
The invention thus again departs from the trend of the industry, according to which the width of the cooling channel is to be maximized in order on the one hand to enlarge the cooling streams between the friction rings and on the other hand to minimize the weight of the brake disk. The invention makes use of the knowledge that possibly too much attention has been paid to the parameter, "disk weight,"0 the past. Another feature of the brake disk of the invention is to be seen in the material, according to which a greater molybdenum content in the gray casting is between 0.6 and 0.8% again contributes to a decided lengthening of the life of the disk. In the experiment, increases of useful life of more than 40 percent, and typically even 60 percent, compared with variants with no molybdenum content.
The invention also, by the selection of the cooling channel width, increases the heat capacity and the rigidity of the brake disk, on the one hand, and at the same time reduces the brake disk to a genuine minimum. Thus, in the experiment under extreme conditions, the useful life until the disk cracks through is often even doubled and thus the life of the disk is definitely lengthened. Nevertheless, the cooling is only unimportantly poorer than in the case of the disks of the state of the art in which the ratio D1/D2 is around 2.5 to 2.8.
Especially preferred variants of the invention are distinguished by the fact that the ratio between disk thickness and air channel width satisfies the condition 3.0.ltoreq.D1/D2.ltoreq.5. At the same time the invention is especially suitable for brake disks with a diameter that is greater than or equal to 300 mm (e.g., 430 to 460 mm), the thickness D1 being about 45 mm and the air channel width D2 being 12 mm. This brake disk design is suitable for example for utility vehicle disk brakes with 22.5" (571.5 mm) [wheel rims], and it is especially advantageous for utility vehicle disk brakes with a ratio between the disk's inside diameter and the disk's outside diameter of about 0.6.
According to the invention the brake disk is made from a gray iron casting (iron, traces of other alloy metals and impurities caused by fusion) with the stated molybdenum content. Compared with conventional brake disks, the brake disk of the invention offers an increase of the useful life by a factor of 3 to 4, without thereby appreciably increasing the brake pad's liability to wear. Preferably, the molybdenum content of the gray casting is between 0.75% and 0.76%, especially at 0.752%. A special advantage of the high molybdenum content is that, being a microcarbide former, the molybdenum prevents the propagation of heat cracks in the brake disk. In contrast to the known niobium microcarbide former, molybdenum also increases the thermostability of the gray casting. Especially in combination with the geometric design of the invention, there is such an increase internal combustion engine he life of the disk that it even pays to increase the Mo content still further.
Advantageously, the gray cast iron also contains chromium (Cr) in an amount of 0.2 to 0.3%. Chromium forms the microcarbide in conjunction with the molybdenum. Preferentially the brake disk gray casting has a total of the following additives: C: 3.8-4%, Si: 1.4-1.8%, Mn: 0.6-0.8%, P: <0.1%, S: K 0.12%, Cr: <0.2-0.3%, Cu: <0.2%, Ni: <0.1%, Mo: 0.6 to 0.8% and V: <0.1%. dr
BRIEF DESCRIPTION OF THE DRAWINGS
The invention is further described below in connection with the drawing, wherein:
FIG. 1 is a partially sectioned view of a brake disk according to the invention, and
FIG. 2 is a test diagram of hot-crack tests.





DETAILED DESCRIPTION OF THE DRAWINGS
The brake disk 1 has two friction disks 3 and 4 joined together by bridges 2, so that an air and cooling channel 5 is formed between the friction disks aligned parallel to one another. On the inner circumference of friction disk 3 a pot-like projection 6 is formed for the mounting of the brake disk 1 on a wheel axle. The brake disk 1 can also, of course, be made multipartite--e.g., in the manner of DE 195 44 559 C1--and/or it can be discontinuous.
The brake disk 1 represented in FIG. 1 is in practice made such that the total disk thickness D1 is 45 mm and the air channel width D2, 12 mm. In the case of brake disks whose air channel has a constant width, the width D2 is defined by the closest point. There is thus a ratio of D1 to D2 of 3.75 (in case of a wide diameter of 430-460 mm for 22.5" rims). In the state of the art the air channel width of 17 to 18 mm has been the established practice. The mass of the brake disk increases according to the cooling channel geometry (web size etc.) by only about 2-3 kg. It also proves advantageous that for the same energy input the temperature of the brake disk increases less than in the case of larger air channel width and thus less heat capacity.
Any further reduction of the cooling channel width D2 is uneconomical for production reasons, since the sand core for the formation of the air channel when the brake disk is cast is no longer manageable. The claimed ratio between the magnitudes D1 and D2 is rather an optimization of the brake disk geometry according to the parameters: danger of cracking, weight, cooling performance, producibility and economy.
FIG. 2 shows by way of example, with the aid of test diagrams of common stress and heat cracking tests, that in utility vehicle brake disks with a thickness D1 of 45 mm and a ratio between disk inside diameter and disk outside diameter around 0.6, with a reduction of the air channel width to about 12 mm (and to a value of around 12 mm in the hatched corridor), even in the case of a disk without Mo a clear prolongation of disk life beyond the life of a corresponding disk with an air channel width D2 of 17 mm can be attained. In comparison with the life of the "17 mm air-channel disk" the life increases by more than 100% when the air channel width is reduced to 12 mm. In the case of a brake disk of gray cast iron with a molybdenum content around 0.6-0.8%, especially 0.75% (and the following additional additives: C: 3.8-4%, Si: 1.4-1.8%, Mn: 0.6 to 0.8%, P: <0.1%, S: <0.12%, Cr: <0.2%, Ni: <0.1% and V: <0.1%) the useful life clearly increases again, especially when the air channel width of the disk with Mo added is around 12 mm. The life of the brake pad is reduced but minimally or not appreciably by the narrowing of the air channel.
Claims
  • 1. A brake disk for disk brakes, comprising:
  • a disk having a thickness D1 and comprising two friction disks arranged parallel to one another and an air channel having a width D2 essentially centrally situated between the two friction disks;
  • wherein a ratio between disk thickness D1 and air channel width D2 is 3.0.ltoreq.D1/D2.ltoreq.5,
  • wherein the brake disk comprises a gray cast iron material having a molybdenum content of 0.6 to 0.8%.
  • 2. A brake disk according to claim 1, wherein said brake disk has a diameter of at least 300 mm.
  • 3. A brake disk according to claim 1, wherein said brake disk has a diameter of 430-460 mm.
  • 4. A brake disk according to claim 1, wherein the thickness D1 is about 45 mm.
  • 5. A brake disk according to claim 1, wherein the width of the air channel is about 12 mm.
  • 6. A brake disk according to claim 1, wherein a ratio between a disk inside diameter and a disk outside diameter is about 0.6.
  • 7. A brake disk according to claim 1, wherein the two friction disks are equally thick.
  • 8. A brake disk according to claim 1, wherein the two friction disks are joined together by bridges.
  • 9. A brake disk according to claim 1, wherein the brake disk is made as a discontinuous, multipartite brake disk.
  • 10. A brake disk according to claim 1, wherein the Mo content of the gray cast iron is 0.75% to 0.76%.
  • 11. A brake disk according to claim 1, wherein the gray cast iron contains chromium.
  • 12. A brake disk according to claim 11, wherein the chromium content of the gray cast iron is 0.2 to 0.3%.
  • 13. A brake disk according to claim 1, wherein the gray cast iron has the following additives:
  • C: 3.8-4%,
  • Si: 1.4-1.8%,
  • Mn: 0.6-0.8%,
  • P: less than 0.1%,
  • S: less than 0.12%
  • Cr: less than 0.2-0.3%,
  • Cu: less than 0.2%,
  • Ni: less than 0.1%,
  • Mo: 0.6 to 0.8%,
  • V: less than 0.1%.
  • 14. A brake disk according to claim 1, wherein the ratio between disk thickness D1 and air channel width D2 is 3.2.ltoreq.D1/D2.ltoreq.4.
  • 15. A utility vehicle disk brake comprising a brake disk according to claim 1, wherein said utility vehicle disk brake has 22.5 inch wheel rims.
Priority Claims (1)
Number Date Country Kind
197 47 111 Oct 1997 DEX
PCT Information
Filing Document Filing Date Country Kind 102e Date 371c Date
PCT/EP98/06581 10/16/1998 6/6/2000 6/6/2000
Publishing Document Publishing Date Country Kind
WO99/23394 5/14/1999
US Referenced Citations (8)
Number Name Date Kind
5032194 Metzler Jul 1991
5139117 Melinat Aug 1992
5323883 Mibe et al. Jun 1994
5427212 Shimazu et al. Jun 1995
5492205 Zhang Feb 1996
5706915 Shimazu et al. Jan 1998
5878848 Zhang Mar 1999
5948353 Lawrence et al. Sep 1999
Foreign Referenced Citations (9)
Number Date Country
143264 Jun 1985 EPX
9778355 Jun 1997 EPX
40 26 611 Feb 1992 DEX
94 00 562 May 1995 DEX
185 33 136 Mar 1996 DEX
197 19 353 Nov 1997 DEX
91-94983 Jul 1997 JPX
2057609 Apr 1981 GBX
2307959 Jun 1997 GBX