Patent Grant
8565568
The present invention relates to the field of fiber optic transmission and, more specifically, to a multimode optical fiber having reduced bending losses and a broad bandwidth for high-data-rate applications.
An optical fiber (i.e., a glass fiber typically surrounded by one or more coating layers) conventionally includes an optical fiber core, which transmits and/or amplifies an optical signal, and an optical cladding, which confines the optical signal within the core. Accordingly, the refractive index of the core nc is typically greater than the refractive index of the optical cladding ng (i.e., nc>ng).
For optical fibers, the refractive index profile is generally classified according to the graphical appearance of the function that associates the refractive index with the radius of the optical fiber. Conventionally, the distance r to the center of the optical fiber is shown on the x-axis, and the difference between the refractive index (at radius r) and the refractive index of the optical fiber's outer cladding (e.g., an outer optical cladding) is shown on the y-axis. The refractive index profile is referred to as a “step” profile, “trapezoidal” profile, “alpha” profile, or “triangular” profile for graphs having the respective shapes of a step, a trapezoid, an alpha, or a triangle. These curves are generally representative of the optical fiber's theoretical or set profile. Constraints in the manufacture of the optical fiber, however, may result in a slightly different actual profile.
Generally speaking, two main categories of optical fibers exist: multimode fibers and single-mode fibers. In a multimode optical fiber, for a given wavelength, several optical modes are propagated simultaneously along the optical fiber. In a single-mode optical fiber, the signal propagates in a fundamental LP01 mode that is guided in the fiber core, while the higher order modes (e.g., the LP11 mode) are strongly attenuated. The typical diameter of a single-mode or multimode glass fiber is 125 microns. The core of a multimode optical fiber typically has a diameter of between about 50 microns and 62.5 microns, whereas the core of a single-mode optical fiber typically has a diameter of between about 6 microns and 9 microns. Multimode systems are generally less expensive than single-mode systems, because multimode light sources, connectors, and maintenance can be obtained at a lower cost.
Multimode optical fibers are commonly used for short-distance applications requiring a high bandwidth, such as local networks or LAN (local area network). Multimode optical fibers have been the subject of international standardization under the ITU-T G.651.1 recommendations, which, in particular, define criteria (e.g., bandwidth, numerical aperture, and core diameter) that relate to the requirements for optical fiber compatibility. The ITU-T G.651.1 standard is hereby incorporated by reference in its entirety.
In addition, the OM3 standard has been adopted to meet the demands of high-bandwidth applications (i.e., a data rate higher than 1 GbE) over long distances (i.e., distances greater than 300 meters). The OM3 standard is hereby incorporated by reference in its entirety. With the development of high-bandwidth applications, the average core diameter for multimode optical fibers has been reduced from 62.5 microns to 50 microns.
Typically, an optical fiber should have the highest possible bandwidth to perform well in a high-bandwidth application. For a given wavelength, the bandwidth of an optical fiber may be characterized in several different ways. Typically, a distinction is made between the so-called “overfilled launch” condition (OFL) bandwidth and the so-called “effective modal bandwidth” condition (EMB). The acquisition of the OFL bandwidth assumes the use of a light source exhibiting uniform excitation over the entire radial surface of the optical fiber (e.g., using a laser diode or light emitting diode (LED)).
Recently developed light sources used in high-bandwidth applications, such as VCSELs (Vertical Cavity Surface Emitting Lasers), exhibit an inhomogeneous excitation over the radial surface of the optical fiber. For this kind of light source, the OFL bandwidth is a less suitable measurement, and so it is preferable to use the effective modal bandwidth (EMB). The calculated effective bandwidth (EMBc) estimates the minimum EMB of a multimode optical fiber independent of the kind of VCSEL used. The EMBc is obtained from a differential-mode-delay (DMD) measurement (e.g., as set forth in the FOTP-220 standard).
An exemplary method of measuring DMD and calculating the effective modal bandwidth can be found in the FOTP-220 standard, which is hereby incorporated by reference in its entirety. Further details on this technique are set forth in the following publications, each of which is hereby incorporated by reference: P. F. Kolesar and D. J. Mazzarese, “Understanding Multimode Bandwidth and Differential Mode Delay Measurements and Their Applications,” Proceedings of the 51st International Wire and Cable Symposium, pp. 453-460; and D. Coleman and Philip Bell, “Calculated EMB Enhances 10 GbE Performance Reliability for Laser-Optimized 50/125 μm Multimode Fiber,” Corning Cable Systems Whitepaper.
The TIA-492AAAC-A standard, which is hereby incorporated by reference in its entirety, specifies the performance requirements for 50-micron-diameter multimode optical fibers used over long distances in Ethernet high-bandwidth transmission network applications. The OM3 standard requires, at a wavelength of 850 nanometers, an EMB of at least 2,000 MHz·km. The OM3 standard assures error-free transmissions for a data rate of 10 Gb/s (10 GbE) up to a distance of 300 meters. The OM4 standard requires, at a wavelength of 850 nanometers, an EMB of at least 4,700 MHz·km to obtain error-free transmissions for a data rate of 10 Gb/s (10 GbE) up to a distance of 550 meters. The OM4 standard is hereby incorporated by reference in its entirety. Typically, at a wavelength of 1300 nanometers, the OM3 and OM4 standards guarantee an OFL bandwidth that is greater than 500 MHz·km. An optical fiber presenting a high bandwidth at wavelengths of both 850 nanometers and 1300 nanometers enables fast signal transmission to be obtained over a wide range of wavelengths.
In a multimode optical fiber, the difference between the propagation times, or group delay times, of the several modes along the optical fiber determine the bandwidth of the optical fiber. In particular, for the same propagation medium (i.e., in a step-index multimode optical fiber), the different modes have different group delay times. This difference in group delay times results in a time lag between the pulses propagating along different radial offsets of the optical fiber.
For example, as shown in the graph on the right side of
As depicted in
To reduce intermodal dispersion, the multimode optical fibers used in telecommunications generally have a core with a refractive index that decreases progressively from the center of the optical fiber to its interface with a cladding (i.e., an “alpha” core profile). Such an optical fiber has been used for a number of years, and its characteristics have been described in “Multimode Theory of Graded-Core Fibers” by D. Gloge et al., Bell System Technical Journal 1973, pp. 1563-1578, and summarized in “Comprehensive Theory of Dispersion in Graded-Index Optical Fibers” by G. Yabre, Journal of Lightwave Technology, February 2000, Vol. 18, No. 2, pp. 166-177. Each of the above-referenced articles is hereby incorporated by reference in its entirety.
A graded-index profile (i.e., an alpha-index profile) can be described by a relationship between the refractive index value n and the distance r from the center of the optical fiber according to the following equation:
wherein,
α≧1, and α is a non-dimensional parameter that is indicative of the shape of the index profile;
n1 is the maximum refractive index of the optical fiber's core;
a is the radius of the optical fiber's core; and
where n0 is the minimum refractive index of the multimode core, which may correspond to the refractive index of the outer cladding (most often made of silica).
A multimode optical fiber with a graded index (i.e., an alpha profile) therefore has a core profile with a rotational symmetry such that along any radial direction of the optical fiber the value of the refractive index decreases continuously from the center of the optical fiber's core to its periphery. When a multimode light signal propagates in such a graded-index core, the different optical modes experience differing propagation mediums (i.e., because of the varying refractive indices). This, in turn, affects the propagation speed of each optical mode differently. Thus, by adjusting the value of the parameter α, it is possible to obtain a group delay time that is virtually equal for all of the modes. Stated differently, the refractive index profile can be modified to reduce or even eliminate intermodal dispersion.
In practice, however, a manufactured multimode optical fiber has a graded-index central core surrounded by an outer cladding of constant refractive index. The core-cladding interface interrupts the core's alpha-index profile. Consequently, the multimode optical fiber's core never corresponds to a theoretically perfect alpha profile (i.e., the alpha set profile). The outer cladding accelerates the higher-order modes with respect to the lower-order modes. This phenomenon is known as the “cladding effect.” In DMD measurements, the responses acquired for the highest radial positions (i.e., nearest the outer cladding) exhibit multiple pulses, which results in a temporal spreading of the response signal. Therefore, bandwidth is diminished by this cladding effect.
Multimode optical fibers are commonly used for short-distance applications requiring a high bandwidth, such as local area networks (LANs). In such applications, the optical fibers may be subjected to accidental or otherwise unintended bending, which can give rise to signal attenuation and modify the mode power distribution and the bandwidth of the optical fiber.
It is therefore desirable to achieve multimode optical fibers that are unaffected by bends having a radius of curvature of less than 10 millimeters. One proposed solution involves adding a depressed trench between the core and the cladding. Nevertheless, the position and the depth of the trench can significantly affect the optical fiber's bandwidth.
Japanese Patent Publication No. JP 2006/47719 A, which is hereby incorporated by reference in its entirety, discloses a graded-index optical fiber having a depressed trench in its cladding. Nevertheless, the disclosed optical fiber does not exhibit high bandwidth at wavelengths of both 850 nanometers and 1300 nanometers. Moreover, the disclosed optical fiber's cladding effect is not mentioned.
International Publication No. WO-A-2008/085851 (and its counterpart U.S. Pat. No. 7,787,731), each of which is hereby incorporated by reference in its entirety, discloses a graded-index optical fiber having a depressed trench in its cladding. Nevertheless, the disclosed optical fiber does not exhibit high bandwidth at wavelengths of both 850 nanometers and 1300 nanometers, and its cladding effect is not mentioned. Moreover, the publication fails to provide a value for the disclosed optical fiber's calculated mode dispersion with a mask covering the outer portion of the fiber-core, as defined in the FOTP-220 standard.
U.S. Patent Application Publication No. 2009/0154888, which is hereby incorporated by reference in its entirety, discloses a graded-index optical fiber having a depressed trench in its cladding. Nevertheless, the disclosed optical fiber does not exhibit high bandwidth at wavelengths of both 850 nanometers and 1300 nanometers, and its cladding effect is not mentioned. Moreover, the publication fails to provide a value for the disclosed optical fiber's calculated mode dispersion with a mask covering the outer portion of the fiber-core, as defined in the FOTP-220 standard.
European Patent No. EP 0131729 (and its counterpart U.S. Pat. No. 4,715,695), each of which is hereby incorporated by reference in its entirety, discloses a graded-index optical fiber having a depressed trench in its cladding. According to this patent, to achieve a high bandwidth, the distance between the end of the graded-index core and the beginning of the depressed trench should be between 0.5 micron and 2 microns. Nevertheless, the disclosed optical fiber exhibits higher bending losses than desired and does not exhibit high bandwidth at wavelengths of both 850 nanometers and 1300 nanometers. Moreover, the disclosed optical fiber's cladding effect is not mentioned.
Therefore, a need exists for a graded-index multimode optical fiber having reduced bending losses, a high bandwidth at wavelengths of both 850 nanometers and 1300 nanometers, and a reduced cladding effect for high-data rate applications.
Accordingly, in one aspect, the present invention embraces an optical fiber that includes a central core, an inner cladding, a buried trench, and an outer cladding (e.g., an outer optical cladding). Typically, the optical fiber's central core is a glass-based central core having an alpha-index profile (i.e., a graded-index profile) and an outer radius r1. The central core's alpha-index profile has a minimum refractive index at the central core's outer radius r1 that corresponds to a refractive index difference Δnend with respect to the outer cladding. Stated differently, the central core has an outer radius r1 and an alpha-index profile, and, at the central core's outer radius r1, a refractive index difference Δnend with respect to the outer cladding (e.g., the innermost portion of the outer cladding). The central core's alpha-index profile also has a maximum refractive index difference Δn1 with respect to the outer cladding (e.g., at the center of the central core).
The optical fiber's inner cladding is positioned between the central core and the outer cladding. The inner cladding has an outer radius r2, a width w2, and a refractive index difference Δn2 with respect to the outer cladding.
The optical fiber's buried trench (i.e., a depressed trench) is positioned between the inner cladding and the outer cladding. The buried trench has an outer radius rext, a width w3, and a refractive index difference Δn3 with respect to the outer cladding.
In an exemplary embodiment, the inner cladding's refractive index difference Δn2, the inner cladding's width W2, and the buried trench's refractive index difference Δn3 satisfy the following inequalities:
1000×Δn3>A×(1000×Δn2)2+B×(1000×Δn2)+C; and
1000×Δn3<D×(1000×Δn2)2+E×(1000×Δn2)+F;
A=182.29×w23−550×w22+545×w2−177.32,
B=−135.42×w23+402×w22−399×w2+130.22,
C=15×w23−57.25×w22+60.9×w2−25.37,
D=−83.137×w23+235.06×w22−219.52×w2+66.66,
E=129.56×w23−388.67×w22+378.13×w2−121.11, and
F=−48.28×w23+137.84×w22−129.9×w2+38.97.
In another exemplary embodiment, the inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the buried trench's refractive index difference Δn3 satisfy the following inequality:
1000×Δn3<G×(1000×Δn2)2+H×(1000×Δn2)+I;
G=−147.08×w23+542×w22−678.78×w2+285.01,
H=472.92×w23−1771×w22+2196.6×w2−905.87, and
I=−409.17×w23+1476.5×w22−1778×w2+710.81.
In yet another exemplary embodiment, the inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the optical fiber's bending losses for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 850 nanometers (i.e., PPC7.5 mm) satisfy the following inequality:
J×(1000×Δn2)+K<PPC7.5 mm<L×(1000×Δn2)+M,
J=0.046×w2−0.082,
K=−0.206×w2+0.203,
L=−0.030×w2−0.221, and
M=−0.339×w2+0.687.
In yet another exemplary embodiment, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 850 nanometers, the optical fiber exhibits bending losses of about 0.2 dB or less (e.g., about 0.1 dB or less).
In yet another exemplary embodiment, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 850 nanometers, the optical fiber exhibits bending losses of about 0.05 dB or less (e.g., about 0.01 dB or less).
In yet another exemplary embodiment, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 1300 nanometers, the optical fiber exhibits bending losses of about 0.5 dB or less (e.g., about 0.3 dB or less).
In yet another exemplary embodiment, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 1300 nanometers, the optical fiber exhibits bending losses of about 0.2 dB or less (e.g., about 0.1 dB or less).
In yet another exemplary embodiment, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 1300 nanometers, the optical fiber exhibits bending losses of about 0.05 dB or less.
In yet another exemplary embodiment, at a wavelength of 850 nanometers, the optical fiber has an overfilled launch (OFL) bandwidth of about 1,500 MHz·km or greater (e.g., about 3,500 MHz·km or greater).
In yet another exemplary embodiment, at a wavelength of 1300 nanometers, the optical fiber has an overfilled launch (OFL) bandwidth of about 500 MHz·km or more (e.g., about 650 MHz·km or more).
In yet another exemplary embodiment, at a wavelength of 850 nanometers, the optical fiber has an outer DMD value of less than 0.33 picoseconds per meter (ps/m).
In yet another exemplary embodiment, the optical fiber has a numerical aperture of between about 0.185 and 0.215.
In yet another exemplary embodiment, the central core's alpha index profile has an alpha parameter of between about 1.9 and 2.1.
In yet another exemplary embodiment, the central core's maximum refractive index difference Δn1 with respect to the outer cladding is between about 11×10−3 and 16×10−3.
In yet another exemplary embodiment, the inner cladding's width w2 is between about 0.5 micron and 2 microns.
In yet another exemplary embodiment, the inner cladding's refractive index difference Δn2 is between about −0.6×10−3 and 2×10−3 (e.g., between about 0.1×10−3 and 2×10−3).
In yet another exemplary embodiment, the inner cladding's refractive index difference Δn2 is greater than about 0.2×10−3 (e.g., 0.8×10−3 or higher).
In yet another exemplary embodiment, the buried trench's refractive index difference Δn3 is between about −15×10−3 and −3×10−3.
In yet another exemplary embodiment, the buried trench's width w3 is between about 3 microns and 5 microns.
In yet another exemplary embodiment, the buried trench has a volume v3 of between about 220%·μm2 and 1,200%·μm2 (e.g., between 250%·μm2 and 750%·μm2).
In yet another exemplary embodiment, the buried trench's outer radius rext is about 32 microns or less (e.g., about 30 microns or less).
In yet another exemplary embodiment, at a wavelength of 850 nanometers, the optical fiber has an outer DMD value of less than 0.33 ps/m (e.g., less than 0.20 ps/m).
In yet another exemplary embodiment, at a wavelength of 850 nanometers, the optical fiber has an outer DMD value of less than 0.14 ps/m.
In yet another exemplary embodiment, the optical fiber has the following characteristics: a buried trench having an outer radius rext of about 32 microns or less; an outer DMD value of less than 0.33 ps/m; at a wavelength of 1300 nanometers, an overfilled launch (OFL) bandwidth of at least about 500 MHz·km; for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 850 nanometers, bending losses of about 0.2 dB or less; and, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 1300 nanometers, bending losses of about 0.5 dB or less.
In another aspect, the present invention embraces an optical transmission system that includes at least a portion of an optical fiber in accordance with the foregoing. In an exemplary embodiment, the optical system has a data rate of at least 10 Gb/s over at least 100 meters (e.g., 300 meters).
The foregoing illustrative summary, as well as other exemplary objectives and/or advantages of the invention, and the manner in which the same are accomplished, are further explained within the following detailed description and its accompanying drawings.
The present invention embraces a multimode optical fiber having reduced bending losses, a high bandwidth at wavelengths of both 850 nanometers and 1300 nanometers, and a reduced cladding effect. The present multimode optical fiber is especially suitable for high-data rate applications.
As noted,
Typically, the central core's alpha-index profile has a minimum refractive index value at the central core's radius r1 that is less than the refractive index value of the outer cladding. Thus, Δnend is negative when expressed as a refractive index difference with the outer cladding (e.g., ncore(r1)−ncladding). That said, in some alternative embodiments, the central core's alpha-index profile may have a minimum refractive index value at the central core's radius r1 that is equal to that of the outer cladding (i.e., the central core's refractive index difference Δnend may be zero).
In an exemplary embodiment, the central core's refractive index difference Δnend (i.e., at the end of the central core's alpha profile) is greater than about −1×10−3 and less than 0. Stated differently, with respect to the outer cladding, the central core has a negative refractive index difference Δnend of greater than about −1×10−3. The central core's maximum refractive index difference Δn1 is typically between about 11×10−3 and 16×10−3. The alpha parameter of the central core's alpha profile is typically between about 1.9 and 2.1. Typically, the central core's outer radius r1 is about 25 microns.
The optical fiber also includes an inner cladding positioned between the central core and the outer cladding (e.g., immediately surrounding the central core). The inner cladding has an outer radius r2, a width w2, and a refractive index difference Δn2 with respect to the outer cladding. The inner cladding's refractive index difference Δn2 is typically between about −0.6×10−3 and 2×10−3 (e.g., between about 0.2×10−3 and 2×10−3). The inner cladding's width w2 is typically between about 0.5 micron and 2 microns (e.g., between 0.8 micron and 1.6 microns). Without being bound to any particular theory, the present inventors have found that the inner cladding can facilitate a reduction in the optical fiber's cladding effect and the achievement of a high bandwidth at the wavelengths of 850 nanometers and 1300 nanometers.
A buried trench (i.e., a depressed trench) is typically positioned between the inner cladding and the outer cladding (e.g., immediately surrounding the inner cladding). The buried trench has a width w3, an outer radius rext, and a refractive index difference Δn3 with respect to the outer cladding. Typically, the term “buried trench” is used to describe a radial portion of an optical fiber that has a refractive index that is substantially less than the refractive index of the outer cladding. In exemplary embodiments, the buried trench's refractive index difference Δn3 is between about −15×10−3 and −3×10−3 (e.g., between −10×10−3 and −5×10−3). The buried trench's width w3 may be between about 3 microns and 5 microns.
Generally speaking, a refractive index difference can also be expressed as a percentage using the following equation:
where n(r) is the comparative refractive index value as a function of radial position (e.g., the refractive index nt of a buried trench), and ncladding is the refractive index value of the outer cladding. Those of ordinary skill in the art will recognize that this equation can be used if the refractive index varies over a given section of the optical fiber (i.e., the refractive index value varies as a function of radial position) or if the refractive index is constant over a given section.
Those of ordinary skill in the art will recognize that the outer cladding typically has a constant refractive index.
That said, if the outer cladding has a non-constant refractive index, refractive index differences are typically measured with respect to the innermost portion of the outer cladding (i.e., that portion of the outer cladding that is closest to the central core and that may affect the propagation of optical signals within the optical fiber).
Thus, a constant refractive index difference with respect to an outer cladding can be expressed as a percentage using the following equation:
where n is the comparative refractive index value (e.g., the refractive index nt of a buried trench), and ncladding is the refractive index value of the outer cladding.
As used herein, the volume v of a buried trench is defined by the following equation:
in which rint and rext are the inner radius and outer radius of the buried trench, respectively, and Δ%(r) is the buried trench's refractive index difference with respect to the outer cladding expressed in terms of percentage. Those of ordinary skill in the art will recognize that this equation can be used for both rectangular and non-rectangular trenches.
If a buried trench has a rectangular shape (i.e., a step index profile), the equation (above) can be simplified to the following equation:
v=|Δ%×π×(rext2−rint2)|
in which rext and rint are the outer radius and inner radius of the buried trench, respectively, and Δ% is the buried trench's refractive index difference with respect to the outer cladding expressed as a percentage.
In some exemplary embodiments, the optical fiber of the present invention includes buried trench having a volume v3 of between about 220%·μm2 and 1,200%·μm2 (e.g., between 250%·μm2 and 750%·μm2). Without being bound to any particular theory, the present inventors have found that the buried trench can facilitate a reduction in the optical fiber's bending losses.
In an exemplary embodiment, the inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the buried trench's refractive index difference Δn3 satisfy the following inequalities:
1000×Δn3>A×(1000×Δn2)2+B×(1000×Δn2)+C; and
1000×Δn3<D×(1000×Δn2)2+E×(1000×Δn2)+F;
A=182.29×w23−550×w22+545×w2−177.32,
B=−135.42×w23+402×w22−399×w2+130.22,
C=15×w23−57.25×w22+60.9×w2−25.37,
D=−83.137×w23+235.06×w22−219.52×w2+66.66,
E=129.56×w23−388.67×w22+378.13×w2−121.11, and
F=−48.28×w23+137.84×w22−129.9×w2+38.97.
Without being bound to any particular theory, the present inventors have found that the above-described relationships facilitate the achievement of optical fibers exhibiting reduced bending losses, a reduced cladding effect, and a high bandwidth at the wavelengths of 850 nanometers and 1300 nanometers.
In this regard, for two turns around a radius of curvature (i.e., a bend radius) of 7.5 millimeters at a wavelength of 850 nanometers, the optical fiber typically exhibits bending losses of about 0.2 dB or less (e.g., about 0.1 dB or less). More typically, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 850 nanometers, the optical fiber exhibits bending losses of less than 0.05 dB (e.g., less than 0.01 dB).
For two turns around a radius of curvature of 7.5 millimeters at a wavelength of 1300 nanometers, the optical fiber typically exhibits bending losses of about 0.5 dB or less (e.g., about 0.3 dB or less). More typically, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 1300 nanometers, the optical fiber exhibits bending losses of less than 0.2 dB (e.g., about 0.1 dB or less). In some exemplary embodiments, for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 1300 nanometers, the optical fiber exhibits bending losses of less than 0.05 dB.
The optical fiber of the present invention typically has a high bandwidth at a wavelength of 850 nanometers and 1300 nanometers. In particular, at a wavelength of 850 nanometers, the optical fiber typically has an overfilled launch (OFL) bandwidth of at least about 1,500 MHz·km (e.g., at least 3,500 MHz·km). Additionally, at a wavelength of 1300 nanometers, the optical fiber typically has an overfilled launch (OFL) bandwidth of at least about 500 MHz·km (e.g., at least 650 MHz·km).
As noted, however, OFL bandwidth is not the only parameter used to evaluate an optical fiber's suitability for high-data-rate applications. To improve optical fiber performance for high-data-rate applications, reducing the cladding effect in the optical fiber (e.g., at the core-cladding interface) can be important.
An optical fiber's cladding effect may be evaluated using differential-mode-delay measurements acquired with an outer mask. For example, for a 50-micron central core (i.e., a central core diameter of 50±3 microns or radius of 25±1.5 microns), the differential-mode-delay value on the outer mask 0-23 microns can be obtained using the method of the FOTP-220 standard. In this regard, a differential mode delay value on the outer mask 0-23 microns (i.e., DMDext, the outer DMD (0-23 microns)) is measured using the DMD method over the radial offset range from the center of the central core (i.e., 0 microns) to 23 microns. In other words, when calculating an optical fiber's outer DMD value, the signals for radial offset values greater than 23 microns are not considered.
Those of ordinary skill in the art will recognize that the dimensions of an outer mask may be modified for optical fibers having larger or smaller core diameters. For example, a mask with larger dimensions (e.g., a larger inner and outer radius) might be used with respect to a multimode optical fiber having a 62.5-micron diameter core. Similarly, a mask with smaller dimensions (e.g., a smaller inner and outer radius) might be used with respect to a multimode optical fiber having a core that is less than 50 microns.
The outer DMD originates from a plot for DMD measured over 750 meters of optical fiber. The light source used may be a pulsed Ti:sapphire laser emitting at 850 nanometers. The source emits pulses of less than 40 ps at quarter height, and the RMS (Root Mean Square) spectral width is less than 0.1 nanometer.
An exemplary optical fiber according to the present invention exhibits improved outer DMD values. In particular, at a wavelength of 850 nanometers, the exemplary optical fiber typically exhibits an outer DMD value of less than about 0.33 ps/m (e.g., less than 0.20 ps/m). More typically, the exemplary optical fiber exhibits an outer DMD value of 0.14 ps/m or less.
In some exemplary embodiments, the optical fiber employing a buried trench with a small outer radius rext has a reduced cladding effect, improved bending losses, and a high bandwidth at the wavelengths of 850 nanometers and 1300 nanometers. The optical fiber's refractive index profile makes it possible to use a high depressed-trench volume v3, while limiting the combined width of the central core, the inner cladding, and the buried trench. In other words, the optical fiber's refractive index profile achieves low bending losses because of the buried trench's volume v3, yet typically maintains a small buried trench outer radius rext and a high bandwidth at the wavelengths of 850 nanometers and 1300 nanometers
Those of ordinary skill in the art will understand that, when manufacturing a primary preform such as via a Plasma Chemical Vapor Deposition (PCVD) process, employing a buried trench having a reduced outer radius rext permits thicker central core depositions. The primary preform may then be provided with an outer overcladding layer to achieve the desired ratio between the central core's radius and the final preform's outer radius. Increasing the thickness of the central core deposit allows a thicker outer overcladding layer to be provided during the overcladding process. Thus, larger final preforms can be achieved while maintaining the desired ratio between the central core's radius and the final preform's outer radius. Increasing the final preform's size permits more optical fiber to be drawn from the final preform. In sum, the smaller the buried trench's outer radius rext, the more optical fiber that can be produced from a single optical preform. Furthermore, when the outer radius rext is small, it is easier to monitor the quality of the central core's alpha index profile. Thus, optical-fiber production costs can be reduced, and optical-fiber production speeds can be increased.
In some exemplary embodiments, the buried trench's outer radius rext is about 32 microns or less (e.g., 30 microns or less). Consequently, the exemplary optical fiber makes it possible to achieve low bending losses and a high bandwidth at the wavelengths of 850 nanometers and 1300 nanometers with a limited outer radius rext. Furthermore, the exemplary optical fiber facilitates reduced production costs and an enhanced production rates.
Nevertheless, reducing the outer radius rext increases the risk that the buried trench will disturb the higher order modes and thereby reduce the optical fiber's bandwidth. In this regard, the present inventors have found that the inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the buried trench's refractive index difference Δn3 can be selected to achieve an overfilled launch (OFL) bandwidth of at least about 500 MHz·km at a wavelength of 1300 nanometers and DMD measurements at 850 nanometers that comply with the OM3 and OM4 standards.
Overfilled launch (OFL) bandwidths at a wavelength of 1300 nanometers are depicted on the right-hand y-axis. The outer DMD measurements and overfilled launch bandwidths are plotted as a function of the inner cladding's refractive index difference Δn2, which is depicted on the x-axis.
As shown in
Without being bound to any particular theory, the present inventors have found that the acceleration of pulses that propagate at radial distances in the outer portion of the central core may be controlled by adjusting the inner cladding's refractive index difference Δn2. In this regard, the pulses that propagate at radial distances in the outer portion of the central core may be accelerated slightly to maintain outer DMD values that comply with the OM4 standard (e.g., as depicted at point 2). Furthermore, the pulses that propagate at radial distances in the outer portion of the central core may be accelerated slightly more, which slightly degrades the outer DMD values (see small graph 3 in
Thus, the inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the buried trench's refractive index difference Δn3 can be selected to achieve an optical fiber that complies with the OM3 standard at a wavelength of 850 nanometers, particularly the OM3 standard's mode dispersion criteria. Thus, at a wavelength of 850 nanometers, the optical fiber has (i) an effective modal bandwidth (EMB) greater than 2,000 MHz·km; (ii) an outer DMD value of less than 0.33 ps/m; (iii) an OFL bandwidth greater than 1,500 MHz·km; (iv) a numerical aperture of between 0.185 and 0.215; (v) an outer buried trench radius rext of less than 32 microns; and (vi) a buried trench volume v3 of more than 220%·μm2. Furthermore, the optical fiber typically complies with the OM3 standard at a wavelength of 1300 nanometers and may exhibit, at a wavelength of 1300 nanometers, an overfilled launch (OFL) bandwidth of at least 500 MHz·km.
In another exemplary embodiment, the inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the buried trench's refractive index difference Δn3 satisfy the following inequality:
1000×Δn3<G×(1000×Δn2)2+H×(1000×Δn2)+I;
G=−147.08×w23+542×w22−678.78×w2+285.01,
H=472.92×w23−1771×w22+2196.6×w2−905.87, and
I=−409.17×w23+1476.5×w22−1778×w2+710.81.
Without being bound to any particular theory, the present inventors have found that the above-described relationships facilitate the achievement of optical fibers that comply with the OM4 standard at a wavelength of 850 nanometers, particularly the OM4 standard's mode dispersion criteria. Furthermore, the above-described relationships facilitate the achievement of optical fibers that comply with the OM4 standard at a wavelength of 1300 nanometers.
In yet another exemplary embodiment, the inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the optical fiber's bending losses for two turns around a radius of curvature of 7.5 millimeters at a wavelength of 850 nanometers (i.e., PPC7.5 mm) satisfy the following inequality:
J×(1000×Δn2)+K<PPC7.5 mm<L×(1000×Δn2)+M,
J=0.046×w2−0.082,
K=−0.206×w2+0.203,
L=−0.030×w2−0.221, and
M=−0.339×w2+0.687.
Without being bound to any particular theory, the present inventors have found that the above-described relationships facilitate the achievement of optical fibers that comply with the OM4 standard at a wavelength of 850 nanometers, particularly the OM4 standard's mode dispersion criteria. Furthermore, the above-described relationships facilitate the achievement of optical fibers that comply with the OM4 standard at a wavelength of 1300 nanometers.
As noted, both of the above-described relationships facilitate the achievement of optical fibers that comply with the OM4 standard at a wavelength of 850 nanometers, especially the OM4 standard's mode dispersion criteria. Thus, at a wavelength of 850 nanometers, the optical fibers have (i) an effective modal bandwidth (EMB) greater than 4,700 MHz·km; (ii) an outer DMD value of less than 0.14 ps/m; (iii) an OFL bandwidth greater than 3,500 MHz·km; (iv) a numerical aperture of between 0.185 and 0.215; (v) an outer buried trench radius rext of less than 32 microns; and (vi) a buried trench volume v3 of more than 220%·μm2. Furthermore, the above-described relationships facilitate the achievement of optical fibers that comply with the OM4 standard at a wavelength of 1300 nanometers and may exhibit, at a wavelength of 1300 nanometers, an overfilled launch (OFL) bandwidth of at least 500 MHz·km.
Aspects of the present invention will be better understood with reference to the exemplary optical-fiber profiles provided in the following tables. Table 1 (below) shows simulated fiber-profile-parameters of exemplary optical fibers in accordance with the present invention, as well as fiber-profile-parameters of comparative optical fibers.
The first column of Table 1 provides the reference number for each optical fiber. The second column shows the central core's outer radius rt. The third and fourth columns, respectively, show the inner cladding's width w2 and the buried trench's width w3. The fifth, sixth, and seventh columns, respectively, show the central core's maximum refractive index difference Δnt, the inner cladding's refractive index difference Δn2, and the buried trench's refractive index difference Δn3. The eighth and final column shows the buried trench's volume v3. Each of the optical fibers of Table 1 has a graded-index central core having the same alpha parameter.
Optical fibers 1-4, 6-8, and 11 are exemplary optical fibers in accordance with the present invention, and optical fibers 5, 9, 10, and 12 are comparative optical fibers. Optical fibers 5, 7, and 9 include buried trenches having the same width w3 and refractive index difference Δn3, but their respective inner cladding-dimensions are different. Optical fibers 10 and 11 include buried trenches having the same width w3 and refractive index difference Δn3 and inner claddings having the same refractive index difference Δn2, but the width w2 of their respective inner claddings is different.
Table 2 (below) provides the simulated optical properties of the exemplary and comparative optical fibers of Table 1.
In Table 2, the first column repeats the references of Table 1. The second column shows outer DMD values (DMDext) at a wavelength of 850 nanometers. The third and fourth columns, respectively, show the OFL bandwidth at 850 nanometers and the OFL bandwidth at 1300 nanometers. The fifth and sixth columns, respectively, show the bending losses for two turns around a radius of curvature of 7.5 millimeters at 850 nanometers and the bending losses for two turns around a radius of curvature of 7.5 millimeters at 1300 nanometers.
Optical fibers 5, 7, and 9 exhibit good performance characteristics at a wavelength of 850 nanometers. For example, at a wavelength of 850 nanometers, optical fibers 5, 7, and 9 have outer DMD values (DMDext) and overfilled launch (OFL) bandwidths that comply with the OM3 standard. Furthermore, at a wavelength of 850 nanometers, optical fibers 7 and 9 have outer DMD values (DMDext) and overfilled launch (OFL) bandwidths that comply with the OM4 standard. Optical fibers 5, 7, and 9 also exhibit low bending losses. For two turns around a radius of curvature of 7.5 millimeters at 850 nanometers, optical fibers 5, 7, and 9 exhibit bending losses of less than 0.05 dB. For two turns around a radius of curvature of 7.5 millimeters at 1300 nanometers, optical fibers 5, 7, and 9 exhibit bending losses of less than 0.2 dB.
At a wavelength of 1300 nanometers, however, optical fibers 5 and 9 have an overfilled launch (OFL) bandwidth of less than 500 MHz·km, which does not satisfy the OM3 and OM4 standards for a wavelength of 1300 nanometers. Exemplary optical fiber 7 has an overfilled launch (OFL) bandwidth of greater than 500 MHz·km. Without being bound to any particular theory, the present inventors have found that the relationship between the characteristics of the inner cladding and the buried trench facilitates the achievement of an improved OFL bandwidth at 1300 nanometers while maintaining good optical performance at both 850 nanometers and 1300 nanometers.
Optical fibers 10 and 11 exhibit low bending losses at wavelengths of 850 nanometers and 1300 nanometers. Without being bound to any particular theory, the present inventors believe that these two optical fiber's bending loss values are similar because they have relatively similar buried trench volumes. At a wavelength of 1300 nanometers, optical fiber 10 has an OFL bandwidth greater than 800 MHz·km. Nevertheless, at a wavelength of 850 nanometers, optical fiber 10 has an outer DMD (DMDext) value that is greater than 0.33 ps/m and, therefore, does not comply with the OM3 standard. Exemplary optical fiber 11, however, includes an inner cladding having a width w2 that facilitates a reduction in its outer DMD (DMDext) value at a wavelength of 850 nanometers. Thus, exemplary optical fiber 11 exhibits good optical performance characteristics at a wavelength of both 850 nanometers and 1300 nanometers.
Optical fiber 12 has a low buried trench volume and an inner cladding that fails to provide desirable optical characteristics. In this regard, it exhibits high bending losses and, at a wavelength of 850 nanometers, an outer DMD (DMDext) value that is greater than 0.33 ps/m.
Table 3 (below) shows fiber-profile-parameters of a comparative manufactured optical fiber 13 and an exemplary manufactured optical fiber 14 in accordance with the present invention. Optical fibers 13 and 14 include graded-index central cores having the same alpha parameter.
The first column of Table 3 provides the reference number for each optical fiber. The second column shows the central core's outer radius rt. The third and fourth columns, respectively, show the inner cladding's width w2 and the buried trench's width w3. The fifth, sixth, and seventh columns, respectively, show the central core's maximum refractive index difference Δnt, the inner cladding's refractive index difference Δn2, and the buried trench's refractive index difference Δn3. The eighth and final column shows the buried trench's volume v3.
Table 4 (below) provides the optical characteristics as measured on fabricated optical fiber examples 13 and 14. Bending loss measurements were performed in accordance with the recommendations of the standard ITU-T G.651.1 (July 2007), which is hereby incorporated by reference in its entirety. The measurement was applied in compliance with the IEC 60793-1-7 standard, which describes the procedure for measuring losses in optical fibers due to macrobending. The IEC 60793-1-7 standard is hereby incorporated by reference in its entirety. The injection conditions applied were those specified in the IEC 61280-4-1 standard, which describes injection conditions for measuring attenuation in multimode fibers. The IEC 61280-4-1 standard is hereby incorporated by reference in its entirety. By way of example, for the measurements performed at 850 nanometers, the source used was a Ti:sapphire laser of small spectral width and short emitted pulse duration in order to give better accuracy in mode dispersion measurements.
In Table 4, the first column repeats the references of Table 3. The second column shows outer DMD values (DMDext) at a wavelength of 850 nanometers. The third and fourth columns, respectively, show the OFL bandwidth at 850 nanometers and the OFL bandwidth at 1300 nanometers. The fifth and sixth columns, respectively, show the bending losses for two turns around a radius of curvature of 7.5 millimeters at 850 nanometers and the bending losses for two turns around a radius of curvature of 7.5 millimeters at 1300 nanometers.
As noted, optical fiber 13 is a comparative optical fiber. The inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the buried trench's refractive index difference Δn3 do not satisfy the previously discussed relationships. Additionally, at a wavelength of 1300 nanometers, comparative optical fiber 13 exhibits an overfilled launch (OFL) bandwidth that is less than 500 MHz·km.
Optical fiber 14, however, is an exemplary optical fiber according to the present invention. The inner cladding's refractive index difference Δn2, the inner cladding's width w2, and the buried trench's refractive index difference Δn3 satisfy the previously discussed relationships. Furthermore, exemplary optical fiber 14 exhibits good bending losses, a small outer DMD value at a wavelength of 850 nanometers, and a high bandwidth at a wavelength of 1300 nanometers.
Curves, 1, 2, and 3 represent the following functions respectively:
1000×Δn3>A×(1000×Δn2)2+B×(1000×Δn2)+C;
1000×Δn3<D×(1000×Δn2)2+E×(1000×Δn2)+F; and
1000×Δn3<G×(1000×Δn2)2+H×(1000×Δn2)+I;
A=182.29×w23−550×w22+545×w2−177.32,
B=−135.42×w23+402×w22−399×w2+130.22,
C=15×w23−57.25×w22+60.9×w2−25.37,
D=−83.137×w23+235.06×w22−219.52×w2+66.66,
E=129.56×w23−388.67×w22+378.13×w2−121.11,
F=−48.28×w23+137.84×w22−129.9×w2+38.97,
G=−147.08×w23+542×w22−678.78×w2+285.01,
H=472.92×w23−1771×w22+2196.6×w2−905.87, and
I=−409.17×w23+1476.5×w22−1778×w2+710.81.
If an optical fiber complies with the OM4 standard, then it also satisfies the OM3 standard. Accordingly, the entire shaded zone (i.e., between curve 1 and curve 3) contains pairs (Δn2, Δn3) that comply with the OM3 standard regarding DMD mode dispersion at 850 nanometers, particularly the outer DMD (DMDext) criteria at a wavelength of 850 nanometers. The non-hatched, gray zone (i.e., between curve 1 and curve 2) contains pairs (Δn2, Δn3) that comply with the OM4 standard regarding DMD mode dispersion at 850 nanometers, particularly the outer DMD (DMDext) criteria at a wavelength of 850 nanometers.
The pairs (Δn2, Δn3) below curve 1 fail to comply with the OM3 standard because, at a wavelength of 1300 nanometers, the resulting optical fibers have overfilled launch (OFL) bandwidths that are less than 500 MHz·km. For example, at a wavelength of 1300 nanometers, comparative optical fiber 5 has an overfilled launch (OFL) bandwidth of less than 500 MHz·km. See also Tables 1 and 2.
Each pair (Δn2, Δn3) above curve 1 and below curve 3 has an overfilled launch (OFL) bandwidth of at least 500 MHz·km at a wavelength of 1300 nanometers and complies with the OM3 standard at a wavelength of 850 nanometers (e.g., an outer DMD (DMDext) value of less than 0.33 ps/m). For example, exemplary optical fibers 3 and 4 fall between curve 1 and curve 3. See also Tables 1 and 2.
Each pair (Δn2, Δn3) above curve 1 and below curve 2 has an overfilled launch (OFL) bandwidth of at least 500 MHz·km at a wavelength of 1300 nanometers and complies with the OM4 standard at a wavelength of 850 nanometers (e.g., an outer DMD (DMDext) value of less than 0.14 ps/m). For example, exemplary optical fiber 4 falls between curve 1 and curve 2. See also Tables 1 and 2.
In another exemplary embodiment, the present invention embraces a multimode optical fiber that includes a central core, an inner cladding, and a buried trench. The central core has an outer radius r1, a maximum refractive index difference Δn1 with respect to the outer cladding, and an alpha index profile. The central core's maximum refractive index difference Δn1 is typically at the center of the central core (i.e., at a radius equal to zero). The central core's alpha-index profile has a minimum refractive index at the central core's outer radius r1 that corresponds to a refractive index difference Δnend with respect to the outer cladding. Stated differently, at the central core's outer radius r1, the central core has a refractive index difference Δnend with respect to the outer cladding.
The optical fiber also includes an inner cladding positioned between the central core and the outer cladding (e.g., immediately surrounding the central core). The inner cladding has an outer radius r2, a width w2, and a refractive index difference Δn2 with respect to the outer cladding.
A buried trench is typically positioned between the inner cladding and the outer cladding (e.g., immediately surrounding the inner cladding). The buried trench has a width w3, an outer radius rext, and a refractive index difference Δn3 with respect to the outer cladding. The buried trench's outer radius rext is less than 32 microns (e.g., less than 30 microns).
At a wavelength of 850 nanometers, the exemplary optical fiber has an outer DMD (DMDext) of less than 0.33 ps/m. In some embodiments, at a wavelength of 850 nanometers, the exemplary optical fiber has an outer DMD (DMDext) of less than 0.23 ps/m (e.g., less than 0.14 ps/m). At a wavelength of 1300 nanometers, the exemplary optical fiber has an overfilled launch (OFL) bandwidth of at least 500 MHz·km. For two turns around a radius of curvature of 7.5 millimeters at a wavelength of 850 nanometers, the exemplary optical fiber exhibits bending losses of less than 0.2 dB. For two turns around a radius of curvature of 7.5 millimeters at a wavelength of 13000 nanometers, the exemplary optical fiber exhibits bending losses of less than 0.5 dB.
According to one embodiment, the optical fiber of the present invention complies with ITU-T Recommendation G.651.1. As such, it has a central-core diameter of 50 microns (i.e., a central-core radius r1 of 25 microns) and/or a numerical aperture of 0.2±0.015.
In another aspect, the present invention embraces a multimode optical system that includes at least a portion of an optical fiber as disclosed herein. In particular, the optical system can exhibit a data rate of at least 10 Gb/s over at least 100 meters (e.g., 300 meters).
The present optical fibers may facilitate the reduction in overall optical-fiber diameter. As will be appreciated by those having ordinary skill in the art, a reduced-diameter optical fiber is cost-effective, requiring less raw material. Moreover, a reduced-diameter optical fiber requires less deployment space (e.g., within a buffer tube and/or fiber optic cable), thereby facilitating increased fiber count and/or reduced cable size.
Those having ordinary skill in the art will recognize that an optical fiber with a primary coating (and an optional secondary coating and/or ink layer) typically has an outer diameter of between about 235 microns and about 265 microns (μm). The component glass fiber itself (i.e., the glass core and surrounding cladding layers) typically has a diameter of about 125 microns, such that the total coating thickness is typically between about 55 microns and 70 microns.
With respect to the present optical fiber, the component glass fiber typically has an outer diameter of about 125 microns. With respect to the optical fiber's surrounding coating layers, the primary coating typically has an outer diameter of between about 175 microns and about 195 microns (i.e., a primary coating thickness of between about 25 microns and 35 microns), and the secondary coating typically has an outer diameter of between about 235 microns and about 265 microns (i.e., a secondary coating thickness of between about 20 microns and 45 microns). Optionally, the present optical fiber may include an outermost ink layer, which is typically between two and ten microns in thickness.
In one alternative embodiment, an optical fiber may possess a reduced diameter (e.g., an outermost diameter between about 150 microns and 230 microns). In this alternative optical fiber configuration, the thickness of the primary coating and/or secondary coating is reduced, while the diameter of the component glass fiber is maintained at about 125 microns. (Those having ordinary skill in the art will appreciate that, unless otherwise specified, diameter measurements refer to outer diameters.)
By way of illustration, in such exemplary embodiments the primary coating layer may have an outer diameter of between about 135 microns and about 175 microns (e.g., about 160 microns), typically less than 165 microns (e.g., between about 135 microns and 150 microns), and usually more than 140 microns (e.g., between about 145 microns and 155 microns, such as about 150 microns).
Moreover, in such exemplary embodiments the secondary coating layer may have an outer diameter of between about 150 microns and about 230 microns (e.g., more than about 165 microns, such as 190-210 microns or so), typically between about 180 microns and 200 microns. In other words, the total diameter of the optical fiber is reduced to less than about 230 microns (e.g., between about 195 microns and 205 microns, and especially about 200 microns). By way of further illustration, an optical fiber may employ a secondary coating of about 197 microns at a tolerance of +/−5 microns (i.e., a secondary-coating outer diameter of between 192 microns to 202 microns). Typically, the secondary coating will retain a thickness of at least about 10 microns (e.g., an optical fiber having a reduced thickness secondary coating of between 15 microns and 25 microns).
In another alternative embodiment, the outer diameter of the component glass fiber may be reduced to less than 125 microns (e.g., between about 60 microns and 120 microns), perhaps between about 70 microns and 115 microns (e.g., about 80-110 microns). This may be achieved, for instance, by reducing the thickness of one or more cladding layers. As compared with the prior alternative embodiment, (i) the total diameter of the optical fiber may be reduced (i.e., the thickness of the primary and secondary coatings are maintained in accordance with the prior alternative embodiment) or (ii) the respective thicknesses of the primary and/or secondary coatings may be increased relative to the prior alternative embodiment (e.g., such that the total diameter of the optical fiber might be maintained).
By way of illustration, with respect to the former, a component glass fiber having a diameter of between about 90 and 100 microns might be combined with a primary coating layer having an outer diameter of between about 110 microns and 150 microns (e.g., about 125 microns) and a secondary coating layer having an outer diameter of between about 130 microns and 190 microns (e.g., about 155 microns). With respect to the latter, a component glass fiber having a diameter of between about 90 and 100 microns might be combined with a primary coating layer having an outer diameter of between about 120 microns and 140 microns (e.g., about 130 microns) and a secondary coating layer having an outer diameter of between about 160 microns and 230 microns (e.g., about 195-200 microns).
Reducing the diameter of the component glass fiber might make the resulting optical fiber more susceptible to microbending attenuation. That said, the advantages of further reducing optical-fiber diameter may be worthwhile for some optical-fiber applications.
As noted, the present optical fibers may include one or more coating layers (e.g., a primary coating and a secondary coating). At least one of the coating layers—typically the secondary coating—may be colored and/or possess other markings to help identify individual fibers. Alternatively, a tertiary ink layer may surround the primary and secondary coatings.
The present optical fibers may be manufactured by drawing from final preforms.
A final preform may be manufactured by providing a primary preform with an outer overcladding layer (i.e., an overcladding process). The outer overcladding layer typically consists of doped or undoped, natural or synthetic, silica glass. Several methods are available for providing the outer overcladding layer.
In a first exemplary method, the outer overcladding layer may be provided by depositing and vitrifying natural or synthetic silica particles on the outer periphery of the primary preform under the influence of heat. Such a process is known, for example, from U.S. Pat. Nos. 5,522,007, 5,194,714, 6,269,663, and 6,202,447, each of which is hereby incorporated by reference in its entirety.
In another exemplary method, a primary preform may be overcladded using a silica sleeve tube, which may or may not be doped. This sleeve tube may then be collapsed onto the primary preform.
In yet another exemplary method, an overcladding layer may be applied via an Outside Vapor Deposition (OVD) method. Here, a soot layer is first deposited on the outer periphery of a primary preform, and then the soot layer is vitrified to form glass.
The primary preforms may be manufactured via outside vapor deposition techniques, such as Outside Vapor Deposition (OVD) and Vapor Axial Deposition (VAD). Alternatively, the primary preforms may be manufactured via inside deposition techniques in which glass layers are deposited on the inner surface of a substrate tube of doped or undoped silica glass, such as Modified Chemical Vapor Deposition (MCVD), Furnace Chemical Vapor Deposition (FCVD), and Plasma Chemical Vapor Deposition (PCVD).
By way of example, the primary preforms may be manufactured using a PCVD process, which can precisely control the central core's gradient refractive index profile.
A depressed trench, for instance, may be deposited on the inner surface of a substrate tube as part of the chemical vapor deposition process. More typically, a depressed trench may be manufactured either (i) by using a fluorine-doped substrate tube as the starting point of the internal deposition process for deposition of the gradient refractive index central core or (ii) by sleeving a fluorine-doped silica tube over the gradient refractive index central core, which itself may be produced using an outside deposition process (e.g., OVD or VAD). Accordingly, a component glass fiber manufactured from the resulting preform may have a depressed trench located at the periphery of its central core.
As noted, a primary preform may be manufactured via an inside deposition process using a fluorine-doped substrate tube. The resulting tube containing the deposited layers may be sleeved by one or more additional fluorine-doped silica tubes so as to increase the thickness of a depressed trench, or to create a depressed trench having a varying refractive index over its width. Although not required, one or more additional sleeve tubes (e.g., fluorine-doped substrate tubes) may be collapsed onto the primary preform before an overcladding step is carried out. The process of sleeving and collapsing is sometimes referred to as jacketing and may be repeated to build several glass layers on the outside of the primary preform.
The present optical fibers may be deployed in various structures, such as those exemplary structures disclosed hereinafter.
For example, one or more of the present optical fibers may be enclosed within a buffer tube. For instance, optical fiber may be deployed in either a single-fiber loose buffer tube or a multi-fiber loose buffer tube. With respect to the latter, multiple optical fibers may be bundled or stranded within a buffer tube or other structure. In this regard, within a multi-fiber loose buffer tube, fiber sub-bundles may be separated with binders (e.g., each fiber sub-bundle is enveloped in a binder). Moreover, fan-out tubing may be installed at the termination of such loose buffer tubes to directly terminate loose buffered optical fibers with field-installed connectors.
In other embodiments, the buffer tube may tightly surround the outermost optical fiber coating (i.e., tight buffered fiber) or otherwise surround the outermost optical-fiber coating or ink layer to provide an exemplary radial clearance of between about 50 and 100 microns (i.e., a semi-tight buffered fiber).
With respect to the former tight buffered fiber, the buffering may be formed by coating the optical fiber with a curable composition (e.g., a UV-curable material) or a thermoplastic material. The outer diameter of tight buffer tubes, regardless of whether the buffer tube is formed from a curable or non-curable material, is typically less than about 1,000 microns (e.g., either about 500 microns or about 900 microns).
With respect to the latter semi-tight buffered fiber, a lubricant may be included between the optical fiber and the buffer tube (e.g., to provide a gliding layer).
As will be known by those having ordinary skill in the art, an exemplary buffer tube enclosing optical fibers as disclosed herein may be formed of polyolefins (e.g., polyethylene or polypropylene), including fluorinated polyolefins, polyesters (e.g., polybutylene terephthalate), polyamides (e.g., nylon), as well as other polymeric materials and blends. In general, a buffer tube may be formed of one or more layers. The layers may be homogeneous or include mixtures or blends of various materials within each layer.
In this context, the buffer tube may be extruded (e.g., an extruded polymeric material) or pultruded (e.g., a pultruded, fiber-reinforced plastic). By way of example, the buffer tube may include a material to provide high temperature and chemical resistance (e.g., an aromatic material or polysulfone material).
Although buffer tubes typically have a circular cross section, buffer tubes alternatively may have an irregular or non-circular shape (e.g., an oval or a trapezoidal cross-section).
Alternatively, one or more of the present optical fibers may simply be surrounded by an outer protective sheath or encapsulated within a sealed metal tube. In either structure, no intermediate buffer tube is necessarily required.
Multiple optical fibers as disclosed herein may be sandwiched, encapsulated, and/or edge bonded to form an optical fiber ribbon. Optical fiber ribbons can be divisible into subunits (e.g., a twelve-fiber ribbon that is splittable into six-fiber subunits). Moreover, a plurality of such optical fiber ribbons may be aggregated to form a ribbon stack, which can have various sizes and shapes.
For example, it is possible to form a rectangular ribbon stack or a ribbon stack in which the uppermost and lowermost optical fiber ribbons have fewer optical fibers than those toward the center of the stack. This construction may be useful to increase the density of optical elements (e.g., optical fibers) within the buffer tube and/or cable.
In general, it is desirable to increase the filling of transmission elements in buffer tubes or cables, subject to other constraints (e.g., cable or mid-span attenuation). The optical elements themselves may be designed for increased packing density. For example, the optical fiber may possess modified properties, such as improved refractive-index profile, core or cladding dimensions, or primary-coating thickness and/or modulus, to improve microbending and macrobending characteristics.
By way of example, a rectangular ribbon stack may be formed with or without a central twist (i.e., a “primary twist”). Those having ordinary skill in the art will appreciate that a ribbon stack is typically manufactured with rotational twist to allow the tube or cable to bend without placing excessive mechanical stress on the optical fibers during winding, installation, and use. In a structural variation, a twisted (or untwisted) rectangular ribbon stack may be further formed into a coil-like configuration (e.g., a helix) or a wave-like configuration (e.g., a sinusoid). In other words, the ribbon stack may possess regular “secondary” deformations.
As will be known to those having ordinary skill in the art, such optical fiber ribbons may be positioned within a buffer tube or other surrounding structure, such as a buffer-tube-free cable. Subject to certain restraints (e.g., attenuation), it is desirable to increase the density of elements such as optical fibers or optical fiber ribbons within buffer tubes and/or optical fiber cables.
A plurality of buffer tubes containing optical fibers (e.g., loose or ribbonized fibers) may be positioned externally adjacent to and stranded around a central strength member. This stranding can be accomplished helically in one direction, known as “S” or “Z” stranding, or via Reverse Oscillated Lay stranding, known as “S-Z” stranding. Stranding about the central strength member reduces optical fiber strain when cable strain occurs during installation and use.
Those having ordinary skill in the art will understand the benefit of minimizing fiber strain for both tensile cable strain and longitudinal compressive cable strain during installation or operating conditions.
With respect to tensile cable strain, which may occur during installation, the cable will become longer while the optical fibers can migrate closer to the cable's neutral axis to reduce, if not eliminate, the strain being translated to the optical fibers. With respect to longitudinal compressive strain, which may occur at low operating temperatures due to shrinkage of the cable components, the optical fibers will migrate farther away from the cable's neutral axis to reduce, if not eliminate, the compressive strain being translated to the optical fibers.
In a variation, two or more substantially concentric layers of buffer tubes may be positioned around a central strength member. In a further variation, multiple stranding elements (e.g., multiple buffer tubes stranded around a strength member) may themselves be stranded around each other or around a primary central strength member.
Alternatively, a plurality of buffer tubes containing optical fibers (e.g., loose or ribbonized fibers) may be simply placed externally adjacent to the central strength member (i.e., the buffer tubes are not intentionally stranded or arranged around the central strength member in a particular manner and run substantially parallel to the central strength member).
Alternatively still, the present optical fibers may be positioned within a central buffer tube (i.e., the central buffer tube cable has a central buffer tube rather than a central strength member). Such a central buffer tube cable may position strength members elsewhere. For instance, metallic or non-metallic (e.g., GRP) strength members may be positioned within the cable sheath itself, and/or one or more layers of high-strength yarns (e.g., aramid or non-aramid yarns) may be positioned parallel to or wrapped (e.g., contrahelically) around the central buffer tube (i.e., within the cable's interior space). As will be understood by those having ordinary skill in the art, such strength yarns provide tensile strength to fiber optic cables. Likewise, strength members can be included within the buffer tube's casing.
Strength yarns may be coated with a lubricant (e.g., fluoropolymers), which may reduce unwanted attenuation in fiber optic cables (e.g., rectangular, flat ribbon cables or round, loose tube cables) that are subjected to relatively tight bends (i.e., a low bend radius). Moreover, the presence of a lubricant on strength yarns (e.g., aramid strength yarns) may facilitate removal of the cable jacketing by reducing unwanted bonding between the strength yarns and the surrounding cable jacket.
In other embodiments, the optical fibers may be placed within a slotted core cable. In a slotted core cable, optical fibers, individually or as a fiber ribbon, may be placed within pre-shaped helical grooves (i.e., channels) on the surface of a central strength member, thereby forming a slotted core unit. The slotted core unit may be enclosed by a buffer tube. One or more of such slotted core units may be placed within a slotted core cable. For example, a plurality of slotted core units may be helically stranded around a central strength member.
Alternatively, the optical fibers may also be stranded in a maxitube cable design, whereby the optical fibers are stranded around themselves within a large multi-fiber loose buffer tube rather than around a central strength member. In other words, the large multi-fiber loose buffer tube is centrally positioned within the maxitube cable. For example, such maxitube cables may be deployed in optical ground wires (OPGW).
In another cabling embodiment, multiple buffer tubes may be stranded around themselves without the presence of a central member. These stranded buffer tubes may be surrounded by a protective tube. The protective tube may serve as the outer casing of the fiber optic cable or may be further surrounded by an outer sheath. The protective tube may tightly or loosely surround the stranded buffer tubes.
As will be known to those having ordinary skill in the art, additional elements may be included within a cable core. For example, copper cables or other active, transmission elements may be stranded or otherwise bundled within the cable sheath. Passive elements may also be placed within the cable core, such as between the interior walls of the buffer tubes and the enclosed optical fibers. Alternatively and by way of example, passive elements may be placed outside the buffer tubes between the respective exterior walls of the buffer tubes and the interior wall of the cable jacket, or within the interior space of a buffer-tube-free cable.
For example, yarns, nonwovens, fabrics (e.g., tapes), foams, or other materials containing water-swellable material and/or coated with water-swellable materials (e.g., including super absorbent polymers (SAPs), such as SAP powder) may be employed to provide water blocking and/or to couple the optical fibers to the surrounding buffer tube and/or cable jacketing (e.g., via adhesion, friction, and/or compression). Exemplary water-swellable elements are disclosed in commonly assigned U.S. Pat. No. 7,515,795 for a Water-Swellable Tape, Adhesive-Backed for Coupling When Used Inside a Buffer Tube, which is hereby incorporated by reference in its entirety.
Moreover, an adhesive (e.g., a hot-melt adhesive or curable adhesive, such as a silicone acrylate cross-linked by exposure to actinic radiation) may be provided on one or more passive elements (e.g., water-swellable material) to bond the elements to the buffer tube. An adhesive material may also be used to bond the water-swellable element to optical fibers within the buffer tube. Exemplary arrangements of such elements are disclosed in commonly assigned U.S. Pat. No. 7,599,589 for a Gel-Free Buffer Tube with Adhesively Coupled Optical Element, which is hereby incorporated by reference in its entirety.
The buffer tubes (or buffer-tube-free cables) may also contain a thixotropic composition (e.g., grease or grease-like gels) between the optical fibers and the interior walls of the buffer tubes. For example, filling the free space inside a buffer tube with water-blocking, petroleum-based filling grease helps to block the ingress of water. Further, the thixotropic filling grease mechanically (i.e., viscously) couples the optical fibers to the surrounding buffer tube.
Such thixotropic filling greases are relatively heavy and messy, thereby hindering connection and splicing operations. Thus, the present optical fibers may be deployed in dry cable structures (i.e., grease-free buffer tubes).
Exemplary buffer tube structures that are free from thixotropic filling greases are disclosed in commonly assigned U.S. Pat. No. 7,724,998 for a Coupling Composition for Optical Fiber Cables (Parris et al.), which is hereby incorporated by reference in its entirety. Such buffer tubes employ coupling compositions formed from a blend of high-molecular weight elastomeric polymers (e.g., about 35 weight percent or less) and oils (e.g., about 65 weight percent or more) that flow at low temperatures. Unlike thixotropic filling greases, the coupling composition (e.g., employed as a cohesive gel or foam) is typically dry and, therefore, less messy during splicing.
As will be understood by those having ordinary skill in the art, a cable enclosing optical fibers as disclosed herein may have a sheath formed from various materials in various designs. Cable sheathing may be formed from polymeric materials such as, for example, polyethylene, polypropylene, polyvinyl chloride (PVC), polyamides (e.g., nylon), polyester (e.g., PBT), fluorinated plastics (e.g., perfluorethylene propylene, polyvinyl fluoride, or polyvinylidene difluoride), and ethylene vinyl acetate. The sheath and/or buffer tube materials may also contain other additives, such as nucleating agents, flame-retardants, smoke-retardants, antioxidants, UV absorbers, and/or plasticizers.
The cable sheathing may be a single jacket formed from a dielectric material (e.g., non-conducting polymers), with or without supplemental structural components that may be used to improve the protection (e.g., from rodents) and strength provided by the cable sheath. For example, one or more layers of metallic (e.g., steel) tape, along with one or more dielectric jackets, may form the cable sheathing. Metallic or fiberglass reinforcing rods (e.g., GRP) may also be incorporated into the sheath. In addition, aramid, fiberglass, or polyester yarns may be employed under the various sheath materials (e.g., between the cable sheath and the cable core), and/or ripcords may be positioned, for example, within the cable sheath.
Similar to buffer tubes, optical fiber cable sheaths typically have a circular cross section, but cable sheaths alternatively may have an irregular or non-circular shape (e.g., an oval, trapezoidal, or flat cross-section).
By way of example, the present optical fiber may be incorporated into single-fiber drop cables, such as those employed for Multiple Dwelling Unit (MDU) applications. In such deployments, the cable jacketing must exhibit crush resistance, abrasion resistance, puncture resistance, thermal stability, and fire resistance as required by building codes. An exemplary material for such cable jackets is thermally stable, flame-retardant polyurethane (PUR), which mechanically protects the optical fibers yet is sufficiently flexible to facilitate easy MDU installations. Alternatively, a flame-retardant polyolefin or polyvinyl chloride sheath may be used.
In general, and as will be known to those having ordinary skill in the art, a strength member is typically in the form of a rod or braided/helically wound wires or fibers, though other configurations will be within the knowledge of those having ordinary skill in the art.
Optical fiber cables containing optical fibers as disclosed may be variously deployed, including as drop cables, distribution cables, feeder cables, trunk cables, and stub cables, each of which may have varying operational requirements (e.g., temperature range, crush resistance, UV resistance, and minimum bend radius).
Such optical fiber cables may be installed within ducts, microducts, plenums, or risers. By way of example, an optical fiber cable may be installed in an existing duct or microduct by pulling or blowing (e.g., using compressed air). An exemplary cable installation method is disclosed in commonly assigned U.S. Pat. No. 7,574,095 for a Communication Cable Assembly and Installation Method, (Lock et al.), and U.S. Pat. No. 7,665,902 for a Modified Pre-Ferrulized Communication Cable Assembly and Installation Method, (Griffioen et al.), each of which is incorporated by reference in its entirety.
As noted, buffer tubes containing optical fibers (e.g., loose or ribbonized fibers) may be stranded (e.g., around a central strength member). In such configurations, an optical fiber cable's protective outer sheath may have a textured outer surface that periodically varies lengthwise along the cable in a manner that replicates the stranded shape of the underlying buffer tubes. The textured profile of the protective outer sheath can improve the blowing performance of the optical fiber cable. The textured surface reduces the contact surface between the cable and the duct or microduct and increases the friction between the blowing medium (e.g., air) and the cable. The protective outer sheath may be made of a low coefficient-of-friction material, which can facilitate blown installation. Moreover, the protective outer sheath can be provided with a lubricant to further facilitate blown installation.
In general, to achieve satisfactory long-distance blowing performance (e.g., between about 3,000 to 5,000 feet or more), the outer cable diameter of an optical fiber cable should be no more than about 70 to 80 percent of the duct's or microduct's inner diameter.
Compressed air may also be used to install optical fibers in an air blown fiber system. In an air blown fiber system, a network of unfilled cables or microducts is installed prior to the installation of optical fibers. Optical fibers may subsequently be blown into the installed cables as necessary to support the network's varying requirements.
Moreover, the optical fiber cables may be directly buried in the ground or, as an aerial cable, suspended from a pole or pylori. An aerial cable may be self-supporting, or secured or lashed to a support (e.g., messenger wire or another cable). Exemplary aerial fiber optic cables include overhead ground wires (OPGW), all-dielectric self-supporting cables (ADSS), all dielectric lash cables (AD-Lash), and figure-eight cables, each of which is well understood by those having ordinary skill in the art. Figure-eight cables and other designs can be directly buried or installed into ducts, and may optionally include a toning element, such as a metallic wire, so that they can be found with a metal detector.
In addition, although the optical fibers may be further protected by an outer cable sheath, the optical fiber itself may be further reinforced so that the optical fiber may be included within a breakout cable, which allows for the individual routing of individual optical fibers.
To effectively employ the present optical fibers in a transmission system, connections are required at various points in the network. Optical fiber connections are typically made by fusion splicing, mechanical splicing, or mechanical connectors.
The mating ends of connectors can be installed to the optical fiber ends either in the field (e.g., at the network location) or in a factory prior to installation into the network. The ends of the connectors are mated in the field in order to connect the optical fibers together or connect the optical fibers to the passive or active components. For example, certain optical fiber cable assemblies (e.g., furcation assemblies) can separate and convey individual optical fibers from a multiple optical fiber cable to connectors in a protective manner.
The deployment of such optical fiber cables may include supplemental equipment, which itself may employ the present optical fiber as previously disclosed. For instance, an amplifier may be included to improve optical signals. Dispersion compensating modules may be installed to reduce the effects of chromatic dispersion and polarization mode dispersion. Splice boxes, pedestals, and distribution frames, which may be protected by an enclosure, may likewise be included. Additional elements include, for example, remote terminal switches, optical network units, optical splitters, and central office switches.
A cable containing the present optical fibers may be deployed for use in a communication system (e.g., networking or telecommunications). A communication system may include fiber optic cable architecture such as fiber-to-the-node (FTTN), fiber-to-the-telecommunications enclosure (FTTE), fiber-to-the-curb (FTTC), fiber-to-the-building (FTTB), and fiber-to-the-home (FTTH), as well as long-haul or metro architecture. Moreover, an optical module or a storage box that includes a housing may receive a wound portion of the optical fiber disclosed herein. By way of example, the optical fiber may be wound around a bending radius of less than about 15 millimeters (e.g., 10 millimeters or less, such as about 5 millimeters) in the optical module or the storage box.
Moreover, present optical fibers may be used in other applications, including, without limitation, fiber optic sensors or illumination applications (e.g., lighting).
The present optical fibers may include Fiber Bragg Grating (FBG). As will be known by those having ordinary skill in the art, FBG is a periodic or aperiodic variation in the refractive index of an optical fiber core and/or cladding. This variation in the refractive index results in a range of wavelengths (e.g., a narrow range) being reflected rather than transmitted, with maximum reflectivity occurring at the Bragg wavelength.
Fiber Bragg Grating is commonly written into an optical fiber by exposing the optical fiber to an intense source of ultraviolet light (e.g., a UV laser). In this respect, UV photons may have enough energy to break molecular bonds within an optical fiber, which alters the structure of the optical fiber, thereby increasing the optical fiber's refractive index. Moreover, dopants (e.g., boron or germanium) and/or hydrogen loading can be employed to increase photosensitivity.
In order to expose a coated glass fiber to UV light for the creation of FBG, the coating may be removed. Alternatively, coatings that are transparent at the particular UV wavelengths (e.g., the UV wavelengths emitted by a UV laser to write FBG) may be employed to render coating removal unnecessary. In addition, silicone, polyimide, acrylate, or PFCB coatings, for instance, may be employed for high-temperature applications.
A particular FBG pattern may be created by employing (i) a photomask placed between the UV light source and the optical fiber, (ii) interference between multiple UV light beams, which interfere with each other in accordance with the desired FBG pattern (e.g., a uniform, chirped, or titled pattern), or (iii) a narrow UV light beam for creating individual variations. The FBG structure may have, for example, a uniform positive-only index change, a Gaussian-apodized index change, a raised-cosine-apodized index change, or a discrete phase shift index change. Multiple FBG patterns may be combined on a single optical fiber.
Optical fibers having FBG may be employed in various sensing applications (e.g., for detecting vibration, temperature, pressure, moisture, or movement). In this respect, changes in the optical fiber (e.g., a change in temperature) result in a shift in the Bragg wavelength, which is measured by a sensor. FBG may be used to identify a particular optical fiber (e.g., if the optical fiber is broken into pieces).
Fiber Bragg Grating may also be used in various active or passive communication components (e.g., wavelength-selective filters, multiplexers, demultiplexers, Mach-Zehnder interferometers, distributed Bragg reflector lasers, pump/laser stabilizers, and supervisory channels).
To supplement the present disclosure, this application incorporates entirely by reference the following commonly assigned patents, patent application publications, and patent applications: U.S. Pat. No. 4,838,643 for a Single Mode Bend Insensitive Fiber for Use in Fiber Optic Guidance Applications (Hodges et al.); U.S. Pat. No. 7,623,747 for a Single Mode Optical Fiber (de Montmorillon et al.); U.S. Pat. No. 7,587,111 for a Single-Mode Optical Fiber (de Montmorillon et al.); U.S. Pat. No. 7,356,234 for a Chromatic Dispersion Compensating Fiber (de Montmorillon et al.); U.S. Pat. No. 7,483,613 for a Chromatic Dispersion Compensating Fiber (Bigot-Astruc et al.); U.S. Pat. No. 7,555,186 for an Optical Fiber (Flammer et al.); U.S. Patent Application Publication No. US2009/0252469 A1 for a Dispersion-Shifted Optical Fiber (Sillard et al.); U.S. patent application Ser. No. 12/098,804 for a Transmission Optical Fiber Having Large Effective Area (Sillard et al.), filed Apr. 7, 2008; International Patent Application Publication No. WO 2009/062131 A1 for a Microbend-Resistant Optical Fiber, (Overton); U.S. Patent Application Publication No. US2009/0175583 A1 for a Microbend-Resistant Optical Fiber, (Overton); U.S. Patent Application Publication No. US2009/0279835 A1 for a Single-Mode Optical Fiber Having Reduced Bending Losses, filed May 6, 2009, (de Montmorillon et al.); U.S. Patent Application Publication No. US2009/0279836 A1 for a Bend-Insensitive Single-Mode Optical Fiber, filed May 6, 2009, (de Montmorillon et al.); U.S. Patent Application Publication No. US2010/0021170 A1 for a Wavelength Multiplexed Optical System with Multimode Optical Fibers, filed Jun. 23, 2009, (Lumineau et al.); U.S. Patent Application Publication No. US2010/0028020 A1 for a Multimode Optical Fibers, filed Jul. 7, 2009, (Gholami et al.); U.S. Patent Application Publication No. US2010/0119202 A1 for a Reduced-Diameter Optical Fiber, filed Nov. 6, 2009, (Overton); U.S. Patent Application Publication No. US2010/0142969 A1 for a Multimode Optical System, filed Nov. 6, 2009, (Gholami et al.); U.S. Patent Application Publication No. US2010/0118388 A1 for an Amplifying Optical Fiber and Method of Manufacturing, filed Nov. 12, 2009, (Pastouret et al.); U.S. Patent Application Publication No. US2010/0135627 A1 for an Amplifying Optical Fiber and Production Method, filed Dec. 2, 2009, (Pastouret et al.); U.S. Patent Application Publication No. US2010/0142033 for an Ionizing Radiation-Resistant Optical Fiber Amplifier, filed Dec. 8, 2009, (Regnier et al.); U.S. Patent Application Publication No. US2010/0150505 A1 for a Buffered Optical Fiber, filed Dec. 11, 2009, (Testu et al.); U.S. Patent Application Publication No. US2010/0171945 for a Method of Classifying a Graded-Index Multimode Optical Fiber, filed Jan. 7, 2010, (Gholami et al.); U.S. Patent Application Publication No. US2010/0189397 A1 for a Single-Mode Optical Fiber, filed Jan. 22, 2010, (Richard et al.); U.S. Patent Application Publication No. US2010/0189399 A1 for a Single-Mode Optical Fiber Having an Enlarged Effective Area, filed Jan. 27, 2010, (Sillard et al.); U.S. Patent Application Publication No. US2010/0189400 A1 for a Single-Mode Optical Fiber, filed Jan. 27, 2010, (Sillard et al.); U.S. Patent Application Publication No. US2010/0214649 A1 for an Optical Fiber Amplifier Having Nanostructures, filed Feb. 19, 2010, (Burow et al.); U.S. Patent Application Publication No. US2010/0254653 A1 for a Multimode Fiber, filed Apr. 22, 2010, (Molin et al.); U.S. patent application Ser. No. 12/794,229 for a Large Bandwidth Multimode Optical Fiber Having a Reduced Cladding Effect, filed Jun. 4, 2010, (Molin et al.); U.S. patent application Ser. No. 12/878,449 for a Multimode Optical Fiber Having Improved Bending Losses, filed Sep. 9, 2010, (Molin et al.); U.S. patent application Ser. No. 12/884,834 for a Multimode Optical Fiber, filed Sep. 17, 2010, (Molin et al.); U.S. patent application Ser. No. 12/887,813 for an Optical Fiber for Sum-Frequency Generation, filed Sep. 22, 2010, (Richard et al.); U.S. patent application Ser. No. 12/944,422 for a Rare-Earth-Coped Optical Fiber Having Small Numerical Aperture, filed Nov. 11, 2010, (Boivin et al.); U.S. patent application Ser. No. 12/953,948 for a High-Bandwidth, Multimode Optical Fiber with Reduced Cladding Effect, filed Nov. 24, 2010, (Molin et al.); U.S. patent application Ser. No. 12/954,036 for a High-Bandwidth, Dual-Trench-Assisted Multimode Optical Fiber, filed Nov. 24, 2010, (Molin et al.); U.S. patent application Ser. No. 12/959,688 for a Multimode Optical Fiber with Low Bending Losses and Reduced Cladding Effect, filed Dec. 3, 2010, (Molin et al.); U.S. patent application Ser. No. 12/959,866 for a High-Bandwidth Multimode Optical Fiber Having Reduced Bending Losses, filed Dec. 3, 2010, (Molin et al.); U.S. patent application Ser. No. 13/017,089 for a Non-Zero Dispersion Shifted Optical Fiber Having a Large Effective Area, filed Jan. 31, 2011, (Sillard et al.); and U.S. patent application Ser. No. 13/017,092 for a Non-Zero Dispersion Shifted Optical Fiber Having a Short Cutoff Wavelength, filed Jan. 31, 2011, (Sillard et al.).
To supplement the present disclosure, this application further incorporates entirely by reference the following commonly assigned patents, patent application publications, and patent applications: U.S. Pat. No. 5,574,816 for Polypropylene-Polyethylene Copolymer Buffer Tubes for Optical Fiber Cables and Method for Making the Same; U.S. Pat. No. 5,717,805 for Stress Concentrations in an Optical Fiber Ribbon to Facilitate Separation of Ribbon Matrix Material; U.S. Pat. No. 5,761,362 for Polypropylene-Polyethylene Copolymer Buffer Tubes for Optical Fiber Cables and Method for Making the Same; U.S. Pat. No. 5,911,023 for Polyolefin Materials Suitable for Optical Fiber Cable Components; U.S. Pat. No. 5,982,968 for Stress Concentrations in an Optical Fiber Ribbon to Facilitate Separation of Ribbon Matrix Material; U.S. Pat. No. 6,035,087 for an Optical Unit for Fiber Optic Cables; U.S. Pat. No. 6,066,397 for Polypropylene Filler Rods for Optical Fiber Communications Cables; U.S. Pat. No. 6,175,677 for an Optical Fiber Multi-Ribbon and Method for Making the Same; U.S. Pat. No. 6,085,009 for Water Blocking Gels Compatible with Polyolefin Optical Fiber Cable Buffer Tubes and Cables Made Therewith; U.S. Pat. No. 6,215,931 for Flexible Thermoplastic Polyolefin Elastomers for Buffering Transmission Elements in a Telecommunications Cable; U.S. Pat. No. 6,134,363 for a Method for Accessing Optical Fibers in the Midspan Region of an Optical Fiber Cable; U.S. Pat. No. 6,381,390 for a Color-Coded Optical Fiber Ribbon and Die for Making the Same; U.S. Pat. No. 6,181,857 for a Method for Accessing Optical Fibers Contained in a Sheath; U.S. Pat. No. 6,314,224 for a Thick-Walled Cable Jacket with Non-Circular Cavity Cross Section; U.S. Pat. No. 6,334,016 for an Optical Fiber Ribbon Matrix Material Having Optimal Handling Characteristics; U.S. Pat. No. 6,321,012 for an Optical Fiber Having Water Swellable Material for Identifying Grouping of Fiber Groups; U.S. Pat. No. 6,321,014 for a Method for Manufacturing Optical Fiber Ribbon; U.S. Pat. No. 6,210,802 for Polypropylene Filler Rods for Optical Fiber Communications Cables; U.S. Pat. No. 6,493,491 for an Optical Drop Cable for Aerial Installation; U.S. Pat. No. 7,346,244 for a Coated Central Strength Member for Fiber Optic Cables with Reduced Shrinkage; U.S. Pat. No. 6,658,184 for a Protective Skin for Optical Fibers; U.S. Pat. No. 6,603,908 for a Buffer Tube that Results in Easy Access to and Low Attenuation of Fibers Disposed Within Buffer Tube; U.S. Pat. No. 7,045,010 for an Applicator for High-Speed Gel Buffering of Flextube Optical Fiber Bundles; U.S. Pat. No. 6,749,446 for an Optical Fiber Cable with Cushion Members Protecting Optical Fiber Ribbon Stack; U.S. Pat. No. 6,922,515 for a Method and Apparatus to Reduce Variation of Excess Fiber Length in Buffer Tubes of Fiber Optic Cables; U.S. Pat. No. 6,618,538 for a Method and Apparatus to Reduce Variation of Excess Fiber Length in Buffer Tubes of Fiber Optic Cables; U.S. Pat. No. 7,322,122 for a Method and Apparatus for Curing a Fiber Having at Least Two Fiber Coating Curing Stages; U.S. Pat. No. 6,912,347 for an Optimized Fiber Optic Cable Suitable for Microduct Blown Installation; U.S. Pat. No. 6,941,049 for a Fiber Optic Cable Having No Rigid Strength Members and a Reduced Coefficient of Thermal Expansion; U.S. Pat. No. 7,162,128 for Use of Buffer Tube Coupling Coil to Prevent Fiber Retraction; U.S. Pat. No. 7,515,795 for a Water-Swellable Tape, Adhesive-Backed for Coupling When Used Inside a Buffer Tube (Overton et al.); U.S. Patent Application Publication No. 2008/0292262 for a Grease-Free Buffer Optical Fiber Buffer Tube Construction Utilizing a Water-Swellable, Texturized Yarn (Overton et al.); European Patent Application Publication No. 1,921,478 A1, for a Telecommunication Optical Fiber Cable (Tatat et al.); U.S. Pat. No. 7,702,204 for a Method for Manufacturing an Optical Fiber Preform (Gonnet et al.); U.S. Pat. No. 7,570,852 for an Optical Fiber Cable Suited for Blown Installation or Pushing Installation in Microducts of Small Diameter (Nothofer et al.); U.S. Pat. No. 7,526,177 for a Fluorine-Doped Optical Fiber (Matthijsse et al.); U.S. Pat. No. 7,646,954 for an Optical Fiber Telecommunications Cable (Tatat); U.S. Pat. No. 7,599,589 for a Gel-Free Buffer Tube with Adhesively Coupled Optical Element (Overton et al.); U.S. Pat. No. 7,567,739 for a Fiber Optic Cable Having a Water-Swellable Element (Overton); U.S. Pat. No. 7,817,891 for a Method for Accessing Optical Fibers within a Telecommunication Cable (Lavenne et al.); U.S. Pat. No. 7,639,915 for an Optical Fiber Cable Having a Deformable Coupling Element (Parris et al.); U.S. Pat. No. 7,646,952 for an Optical Fiber Cable Having Raised Coupling Supports (Parris); U.S. Pat. No. 7,724,998 for a Coupling Composition for Optical Fiber Cables (Parris et al.); U.S. Patent Application Publication No. US2009/0214167 A1 for a Buffer Tube with Hollow Channels, (Lookadoo et al.); U.S. Patent Application Publication No. US2009/0297107 A1 for an Optical Fiber Telecommunication Cable, filed May 15, 2009, (Tatat); U.S. Patent Application Publication No. US2009/0279833 A1 for a Buffer Tube with Adhesively Coupled Optical Fibers and/or Water-Swellable Element, filed Jul. 21, 2009, (Overton et al.); U.S. Patent Application Publication No. US2010/0092135 A1 for an Optical Fiber Cable Assembly, filed Sep. 10, 2009, (Barker et al.); U.S. Patent Application Publication No. US2010/0067857 A1 for a High-Fiber-Density Optical Fiber Cable, filed Sep. 10, 2009, (Louie et al.); U.S. Patent Application Publication No. US2010/0067855 A1 for a Buffer Tubes for Mid-Span Storage, filed Sep. 11, 2009, (Barker); U.S. Patent Application Publication No. US2010/0135623 A1 for Single-Fiber Drop Cables for MDU Deployments, filed Nov. 9, 2009, (Overton); U.S. Patent Application Publication No. US2010/0092140 A1 for an Optical-Fiber Loose Tube Cables, filed Nov. 9, 2009, (Overton); U.S. Patent Application Publication No. US2010/0135624 A1 for a Reduced-Size Flat Drop Cable, filed Nov. 9, 2009, (Overton et al.); U.S. Patent Application Publication No. US2010/0092138 A1 for ADSS Cables with High-Performance Optical Fiber, filed Nov. 9, 2009, (Overton); U.S. Patent Application Publication No. US2010/0135625 A1 for Reduced-Diameter Ribbon Cables with High-Performance Optical Fiber, filed Nov. 10, 2009, (Overton); U.S. Patent Application Publication No. US2010/0092139 A1 for a Reduced-Diameter, Easy-Access Loose Tube Cable, filed Nov. 10, 2009, (Overton); U.S. Patent Application Publication No. US2010/0154479 A1 for a Method and Device for Manufacturing an Optical Preform, filed Dec. 19, 2009, (Milicevic et al.); U.S. Patent Application Publication No. US 2010/0166375 for a Perforated Water-Blocking Element, filed Dec. 29, 2009, (Parris); U.S. Patent Application Publication No. US2010/0183821 A1 for a UVLED Apparatus for Curing Glass-Fiber Coatings, filed Dec. 30, 2009, (Hartsuiker et al.); U.S. Patent Application Publication No. US2010/0202741 A1 for a Central-Tube Cable with High-Conductivity Conductors Encapsulated with High-Dielectric-Strength Insulation, filed Feb. 4, 2010, (Ryan et al.); U.S. Patent Application Publication No. US2010/0215328 A1 for a Cable Having Lubricated, Extractable Elements, filed Feb. 23, 2010, (Tatat et al.); U.S. patent application Ser. No. 12/843,116 for a Tight-Buffered Optical Fiber Unit Having Improved Accessibility, filed Jul. 26, 2010, (Risch et al.); U.S. patent application Ser. No. 12/881,598 for Methods and Devices for Cable Insertion into Latched Conduit, filed Sep. 14, 2010, (Leatherman et al.); U.S. patent application Ser. No. 12/907,241 for a High-Fiber-Density Optical-Fiber Cable, filed Oct. 19, 2010, (Overton et al.); U.S. patent application Ser. No. 12/907,265 for an Optical-Fiber Cable Having High Fiber Count and High Fiber Density, filed Oct. 19, 2010, (Tatat et al.); and U.S. patent application Ser. No. 13/009,118 for a Water-Soluble Water-Blocking Element, filed Jan. 19, 2011, (Parris).
In the specification and/or figures, typical embodiments of the invention have been disclosed. The present invention is not limited to such exemplary embodiments. The use of the term “and/or” includes any and all combinations of one or more of the associated listed items. The figures are schematic representations and so are not necessarily drawn to scale. Unless otherwise noted, specific terms have been used in a generic and descriptive sense and not for purposes of limitation.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 51489 | Mar 2010 | FR | national |
This application claims the benefit of commonly assigned pending French application Ser. No. 10/51489 for a “Fibre Optique Multimode à Large Bande Passante et à Faibles Pertes par Courbure” (filed Mar. 2, 2010, at the National Institute of Industrial Property (France)), which is hereby incorporated by reference in its entirety. This application further claims the benefit of commonly assigned U.S. Patent Application No. 61/323,619 for a “Fibre Optique Multimode à Large Bande Passante et à Faibles Pertes par Courbure” (filed Apr. 13, 2010), which is hereby incorporated by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4111525 | Kaminow et al. | Sep 1978 | A |
| 4184744 | Onoda et al. | Jan 1980 | A |
| 4222631 | Olshansky | Sep 1980 | A |
| 4229070 | Olshansky et al. | Oct 1980 | A |
| 4230396 | Olshansky et al. | Oct 1980 | A |
| 4339174 | Levin | Jul 1982 | A |
| 4406517 | Olshansky | Sep 1983 | A |
| 4465335 | Eppes | Aug 1984 | A |
| 4636235 | Glessner et al. | Jan 1987 | A |
| 4636236 | Glessner et al. | Jan 1987 | A |
| 4653042 | d'Auria et al. | Mar 1987 | A |
| 4715695 | Nishimura et al. | Dec 1987 | A |
| 4723828 | Garel-Jones et al. | Feb 1988 | A |
| 4838643 | Hodges et al. | Jun 1989 | A |
| 5142603 | Forrester | Aug 1992 | A |
| 5194714 | Le Sergent | Mar 1993 | A |
| 5278687 | Jannson et al. | Jan 1994 | A |
| 5381503 | Kanamori et al. | Jan 1995 | A |
| 5522007 | Drouart et al. | May 1996 | A |
| 5574816 | Yang et al. | Nov 1996 | A |
| 5702497 | Oh et al. | Dec 1997 | A |
| 5717805 | Stulpin | Feb 1998 | A |
| 5761362 | Yang et al. | Jun 1998 | A |
| 5841933 | Hoaglin et al. | Nov 1998 | A |
| 5911023 | Risch et al. | Jun 1999 | A |
| 5982968 | Stulpin | Nov 1999 | A |
| 6002818 | Fatehi et al. | Dec 1999 | A |
| 6035087 | Bonicel et al. | Mar 2000 | A |
| 6066397 | Risch et al. | May 2000 | A |
| 6085009 | Risch et al. | Jul 2000 | A |
| 6134363 | Hinson et al. | Oct 2000 | A |
| 6175677 | Yang et al. | Jan 2001 | B1 |
| 6181857 | Emeterio et al. | Jan 2001 | B1 |
| 6185346 | Asawa et al. | Feb 2001 | B1 |
| 6202447 | Drouart et al. | Mar 2001 | B1 |
| 6210802 | Risch et al. | Apr 2001 | B1 |
| 6215931 | Risch et al. | Apr 2001 | B1 |
| 6269663 | Drouart et al. | Aug 2001 | B1 |
| 6292603 | Mizuochi et al. | Sep 2001 | B1 |
| 6292612 | Golowich et al. | Sep 2001 | B1 |
| 6314224 | Stevens et al. | Nov 2001 | B1 |
| 6321012 | Shen | Nov 2001 | B1 |
| 6321014 | Overton et al. | Nov 2001 | B1 |
| 6334016 | Greer, IV | Dec 2001 | B1 |
| 6381390 | Hutton et al. | Apr 2002 | B1 |
| 6470126 | Mukasa | Oct 2002 | B1 |
| 6490398 | Gruner-Nielsen et al. | Dec 2002 | B2 |
| 6493491 | Shen et al. | Dec 2002 | B1 |
| 6580863 | Yegnanarayanan et al. | Jun 2003 | B2 |
| 6603908 | Dallas et al. | Aug 2003 | B2 |
| 6606437 | Mukasa et al. | Aug 2003 | B1 |
| 6618538 | Nechitailo et al. | Sep 2003 | B2 |
| 6658184 | Bourget et al. | Dec 2003 | B2 |
| 6724965 | Abbott et al. | Apr 2004 | B2 |
| 6724966 | Mukasa | Apr 2004 | B2 |
| 6735985 | DiGiovanni et al. | May 2004 | B2 |
| 6749446 | Nechitailo | Jun 2004 | B2 |
| 6750294 | Sugiyama et al. | Jun 2004 | B2 |
| 6771865 | Blaszyk et al. | Aug 2004 | B2 |
| 6904218 | Sun et al. | Jun 2005 | B2 |
| 6912347 | Rossi et al. | Jun 2005 | B2 |
| 6922515 | Nechitailo et al. | Jul 2005 | B2 |
| 6941049 | Risch et al. | Sep 2005 | B2 |
| 7006751 | Provost et al. | Feb 2006 | B2 |
| 7043126 | Guan et al. | May 2006 | B2 |
| 7043128 | DiGiovanni et al. | May 2006 | B2 |
| 7045010 | Sturman, Jr. | May 2006 | B2 |
| 7089765 | Schaper et al. | Aug 2006 | B2 |
| 7162128 | Lovie et al. | Jan 2007 | B2 |
| 7315677 | Li et al. | Jan 2008 | B1 |
| 7322122 | Overton et al. | Jan 2008 | B2 |
| 7346244 | Gowan et al. | Mar 2008 | B2 |
| 7356234 | de Montmorillon et al. | Apr 2008 | B2 |
| 7400835 | Sardesai et al. | Jul 2008 | B2 |
| 7406235 | Guan et al. | Jul 2008 | B2 |
| 7421172 | Matthijse et al. | Sep 2008 | B2 |
| 7421174 | Fleming, Jr. et al. | Sep 2008 | B2 |
| 7483613 | Bigot-Astruc et al. | Jan 2009 | B2 |
| 7515795 | Overton et al. | Apr 2009 | B2 |
| 7526177 | Matthijsse et al. | Apr 2009 | B2 |
| 7539381 | Chen et al. | May 2009 | B2 |
| 7555186 | Flammer et al. | Jun 2009 | B2 |
| 7567739 | Overton et al. | Jul 2009 | B2 |
| 7570852 | Nothofer et al. | Aug 2009 | B2 |
| 7574095 | Lock et al. | Aug 2009 | B2 |
| 7587111 | de Montmorillon et al. | Sep 2009 | B2 |
| 7599589 | Overton et al. | Oct 2009 | B2 |
| 7623747 | de Montmorillon et al. | Nov 2009 | B2 |
| 7639915 | Parris et al. | Dec 2009 | B2 |
| 7646952 | Parris | Jan 2010 | B2 |
| 7646954 | Tatat | Jan 2010 | B2 |
| 7646955 | Donlagic | Jan 2010 | B2 |
| 7665902 | Griffioen et al. | Feb 2010 | B2 |
| 7702204 | Gonnet et al. | Apr 2010 | B2 |
| 7724998 | Parris et al. | May 2010 | B2 |
| 7783149 | Fini | Aug 2010 | B2 |
| 7787731 | Bookbinder et al. | Aug 2010 | B2 |
| 7817257 | Takenaga et al. | Oct 2010 | B2 |
| 7817891 | Lavenne et al. | Oct 2010 | B2 |
| 7826691 | Matthijsse et al. | Nov 2010 | B2 |
| 7865050 | Sun | Jan 2011 | B1 |
| 7878712 | Shimotakahara et al. | Feb 2011 | B2 |
| 7903918 | Bickham et al. | Mar 2011 | B1 |
| 8009950 | Molin et al. | Aug 2011 | B2 |
| 8145027 | Overton et al. | Mar 2012 | B2 |
| 8184936 | Zhang et al. | May 2012 | B2 |
| 20020102082 | Sarchi et al. | Aug 2002 | A1 |
| 20020176678 | Mukasa | Nov 2002 | A1 |
| 20020197038 | Abbott et al. | Dec 2002 | A1 |
| 20030024276 | Anderson et al. | Feb 2003 | A1 |
| 20040247269 | Hirano et al. | Dec 2004 | A1 |
| 20050008312 | Jang et al. | Jan 2005 | A1 |
| 20060039665 | Matsuo et al. | Feb 2006 | A1 |
| 20070172182 | Lee et al. | Jul 2007 | A1 |
| 20080292262 | Overton et al. | Nov 2008 | A1 |
| 20090010596 | Matthijsse et al. | Jan 2009 | A1 |
| 20090059353 | Fini | Mar 2009 | A1 |
| 20090060437 | Fini et al. | Mar 2009 | A1 |
| 20090092365 | Donlagic | Apr 2009 | A1 |
| 20090154888 | Abbott, III et al. | Jun 2009 | A1 |
| 20090169163 | Abbott, III et al. | Jul 2009 | A1 |
| 20090175583 | Overton | Jul 2009 | A1 |
| 20090214167 | Lookadoo et al. | Aug 2009 | A1 |
| 20090252469 | Sillard et al. | Oct 2009 | A1 |
| 20090279833 | Overton et al. | Nov 2009 | A1 |
| 20090279835 | de Montmorillon et al. | Nov 2009 | A1 |
| 20090279836 | de Montmorillon et al. | Nov 2009 | A1 |
| 20090297107 | Tatat | Dec 2009 | A1 |
| 20100021170 | Lumineau et al. | Jan 2010 | A1 |
| 20100028020 | Gholami et al. | Feb 2010 | A1 |
| 20100040336 | Chen et al. | Feb 2010 | A1 |
| 20100067855 | Barker | Mar 2010 | A1 |
| 20100067857 | Lovie et al. | Mar 2010 | A1 |
| 20100067858 | Kim et al. | Mar 2010 | A1 |
| 20100092135 | Barker et al. | Apr 2010 | A1 |
| 20100092138 | Overton | Apr 2010 | A1 |
| 20100092139 | Overton | Apr 2010 | A1 |
| 20100092140 | Overton | Apr 2010 | A1 |
| 20100118388 | Pastouret et al. | May 2010 | A1 |
| 20100119202 | Overton | May 2010 | A1 |
| 20100135623 | Overton | Jun 2010 | A1 |
| 20100135624 | Overton et al. | Jun 2010 | A1 |
| 20100135625 | Overton | Jun 2010 | A1 |
| 20100135627 | Pastouret et al. | Jun 2010 | A1 |
| 20100142033 | Regnier et al. | Jun 2010 | A1 |
| 20100142969 | Gholami et al. | Jun 2010 | A1 |
| 20100150505 | Testu et al. | Jun 2010 | A1 |
| 20100154479 | Milicevic et al. | Jun 2010 | A1 |
| 20100166375 | Parris | Jul 2010 | A1 |
| 20100171945 | Gholami et al. | Jul 2010 | A1 |
| 20100183821 | Hartsuiker et al. | Jul 2010 | A1 |
| 20100189397 | Richard et al. | Jul 2010 | A1 |
| 20100189399 | Sillard et al. | Jul 2010 | A1 |
| 20100189400 | Sillard et al. | Jul 2010 | A1 |
| 20100202741 | Ryan et al. | Aug 2010 | A1 |
| 20100214649 | Burov et al. | Aug 2010 | A1 |
| 20100215328 | Tatat et al. | Aug 2010 | A1 |
| 20100220966 | Bennett | Sep 2010 | A1 |
| 20100254653 | Molin et al. | Oct 2010 | A1 |
| 20100310218 | Molin et al. | Dec 2010 | A1 |
| 20110002590 | Ooizumi et al. | Jan 2011 | A1 |
| 20110026889 | Risch et al. | Feb 2011 | A1 |
| 20110037183 | Tudury et al. | Feb 2011 | A1 |
| 20110044594 | Tudury et al. | Feb 2011 | A1 |
| 20110044595 | Sillard et al. | Feb 2011 | A1 |
| 20110044596 | Zhang et al. | Feb 2011 | A1 |
| 20110054861 | Lane | Mar 2011 | A1 |
| 20110054862 | Pimpinella et al. | Mar 2011 | A1 |
| 20110058781 | Molin et al. | Mar 2011 | A1 |
| 20110064367 | Molin et al. | Mar 2011 | A1 |
| 20110064371 | Leatherman et al. | Mar 2011 | A1 |
| 20110069724 | Richard et al. | Mar 2011 | A1 |
| 20110069932 | Overton et al. | Mar 2011 | A1 |
| 20110085770 | Bigot-Astruc et al. | Apr 2011 | A1 |
| 20110091171 | Tatat et al. | Apr 2011 | A1 |
| 20110116160 | Boivin et al. | May 2011 | A1 |
| 20110123161 | Molin et al. | May 2011 | A1 |
| 20110123162 | Molin et al. | May 2011 | A1 |
| 20110135262 | Molin et al. | Jun 2011 | A1 |
| 20110135263 | Molin et al. | Jun 2011 | A1 |
| 20110176782 | Parris | Jul 2011 | A1 |
| 20110188823 | Sillard et al. | Aug 2011 | A1 |
| 20110188826 | Sillard et al. | Aug 2011 | A1 |
| 20110217012 | Bigot-Astruc et al. | Sep 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 0131729 | Jan 1985 | EP |
| 1164393 | Dec 2001 | EP |
| 1727302 | Nov 2006 | EP |
| 1921478 | May 2008 | EP |
| 2299303 | Mar 2011 | EP |
| 08-304636 | Nov 1996 | JP |
| 09-048629 | Feb 1997 | JP |
| 11-064665 | Mar 1999 | JP |
| 2000-347057 | Dec 2000 | JP |
| 2001-235648 | Aug 2001 | JP |
| 2002-318315 | Oct 2002 | JP |
| 2006-047719 | Feb 2006 | JP |
| 2006-078543 | Mar 2006 | JP |
| 2006-227173 | Aug 2006 | JP |
| 2007-272239 | Oct 2007 | JP |
| 03081301 | Oct 2003 | WO |
| 2005106544 | Nov 2005 | WO |
| 2006010798 | Feb 2006 | WO |
| 2008085851 | Jul 2008 | WO |
| 2009062131 | May 2009 | WO |
| 20091078962 | Jun 2009 | WO |
| 20101036684 | Apr 2010 | WO |
| 2011040830 | Apr 2011 | WO |
| Entry |
|---|
| Sasaki, P.L. Francois, D.N. Payne, “Accuracy and resolution of preform index-profiling by the spatial-filtering method,” ECOC'81, 6.4-1, Copenhagen, Denmark. |
| Kashima et al., “Transmission characteristics of graded-index optical fibers with a lossy outer layer,” Applied Optics USA, vol. 17, No. 8, Apr. 15, 1978. |
| Jacomme, “Modal dispersion in multimode graded-index fibers,” Applied Optics USA, vol. 14, No. 11, Nov. 1, 1975, pp. 2578-2584. |
| Okamoto et al., “Computer-Aided Synthesis of the Optimum Refractive-Index Profile for a Multimode Fiber,” IEEE Transaction on Microwave Theory and Techniques, USA, vol. MTT-25, No. 3, Mar. 1977, pp. 1-10. |
| Donalagic, “Opportunities to Enhance Multimode Fiber Links by Application of Overfilled Launch,” Journal of Lightwave Technology, vol. 23, No. 11, (Nov. 2005) pp. 3526-3540. |
| Morikuni et al., “Simulation-Based Prediction of Multimode Fiber Bandwidth for 10 Gb/s Systems,” LEOS 2002, 15th Annual Meeting of IEEE Lasers & Electro-Optics Society, Glascow, Scotland, pp. 1-2. |
| Guan et al., “Multimode Fibers for Compensating Intermodal Dispersionof Graded-Index Multimode Fibers”, Jul. 2004, Journal of Lightwave Technology, vol. 22, No. 7, pp. 1714-1719. |
| Kaminow et al., “Profile synthesis in multicomponent glass optical fibers”, Applied Optics, vol. 16, No. 1, Jan. 1, 1977, pp. 108-112. |
| Molin et al., “Low Bending Sensitivity of Regular OM3/OM4 Fibers in 10GbE Applications”, Optical Fiber Communication (OFC) Collocated National Fiber Optic Engineers Conference, 2010 Conference on (OFC/NFOEC), IEEE, Piscataway, NJ, Mar. 21, 2010, pp. 1-3. |
| French Search Report in counterpart French Application No. 1051489 dated Oct. 22, 2010, pp. 1-8. |
| Freund et al., “High-Speed Transmission in Multimode Fibers” Journal of Lightwave Technology, vol. 28, No. 4, Feb. 15, 2010, pp. 569-586 [Cited in FR Search Report]. |
| Kolesar et al., “Understanding Multimode Bandwidth and Differential Mode Delay Measurements and Their Applications,” Proceedings of the 51st International Wire and Cable Symposium, pp. 453-460. |
| Coleman et al., “Calculated EMB Enhances 10GbE Performance Reliability for Laser-Optimized 50/125 μm Multimode Fiber,” Corning Cable Systems Whitepaper, Mar. 2005, pp. 1-6. |
| Gloge et al., “Multimode Theory of Graded-Core Fibers”, Bell system Technical Journal 1973, pp. 1563-1578. |
| Yarbe, “Comprehensive Theory of Dispersion in Graded-Index Optical Fibers”, Journal of Lightwave Technology, Feb. 2000, vol. 18, No. 2, pp. 166-177. |
| Pepeljugoski et al., “15.6-Gb/s Transmission Over 1 km of Next Generation Multimode Fiber”, IEEE Photonics Technology Letters, vol. 14, No. 5, May 2002, pp. 1-3. |
| Number | Date | Country | |
|---|---|---|---|
| 20110217012 A1 | Sep 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61323619 | Apr 2010 | US |