Broadband polarizer made using ion exchangable fusion drawn glass sheets

Abstract
The disclosure is directed to broadband, glass optical polarizers and to methods for making the glass optical polarizers. The glass optical polarizer includes a substantially bubble free fusion drawn glass having two pristine glass surfaces and a plurality of elongated zero valent metallic particle polarizing layers.
Description
FIELD

This disclosure is directed to glass polarizers made from ion-exchangeable fusion drawn sheet glass, and a method of making such polarizers using ion-exchangeable fusion drawn glass sheets. The polarizers described herein are broadband glass polarizers operative in the infrared region of the electromagnetic spectrum.


BACKGROUND

Glass optical polarizers are made by a number of different corporations using different methods. Among these glass optical polarizers are the Polarcor™ (Corning Incorporated, Corning, N.Y.) glass polarizing products which are formed by heat treating a glass containing silver and halide ions to precipitate silver halide particles, which particles are then stretched in a redraw step which is followed by a reduction step in which the silver halide particles are reduced to form anisotropic silver particles in the glass. Other polarizers are made from sodium silicate (soda lime) glass by ion exchanging silver ions for sodium ions near the glass surface, followed by heat treating and drawing the soda lime glass to elongate silver particles in the glass.


While the presently available polarizers have served industry well, with increasing miniaturization, particularly in the telecommunications industry, there is a need for glass optical polarizers that are both thin and strong. The present disclosure is directed to such polarizer products and to a method for making the same.


SUMMARY

According to an embodiment of the present disclosure, a glass optical polarizer is provided. The glass optical polarizer includes a substantially bubble free fusion drawn glass having two pristine glass surfaces and a plurality of elongated zero valent metallic particle polarizing layers.


According to another embodiment of the present disclosure, a method for making a glass optical polarizer is provided. The method includes providing a fusion drawn alkali-containing glass substrate and ion-exchanging a noble metal ion into the glass substrate using an ion-exchange molten metal salt bath. The molten metal salt bath includes a noble metal salt and an alkali metal salt. The method further includes removing excess ion-exchange salts from the glass substrate, and reducing the noble metal ion in hydrogen to form a plurality of zero valent metallic particle polarizing layers. The method further includes redrawing the glass substrate to form a plurality of elongated zero valent metallic particle polarizing layers. The glass optical polarizer has two pristine glass surfaces and is substantially bubble free.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a graph illustrating contrast ratio (in dB) versus wavelength of redrawn glass polarizers prepared as described herein.



FIG. 2 is a graph illustrating % transmission versus wavelength of redrawn glass polarizers prepared as described herein.



FIG. 3 is an SEM (scanning electron microscopy) photograph of the cross section of polarizing glass prepared as described herein after the hydrogen reduction.



FIG. 4A is an SEM photograph of polarizing glass prepared as described herein after hydrogen reduction at 420° C. for 20 hours and stretching at a tension of 6000 psi.



FIG. 4B is an SEM photograph of polarizing glass prepared as described herein after hydrogen reduction at 420° C. for 20 hours and stretching at a tension of 2000 psi.



FIG. 4C is an SEM photograph of polarizing glass prepared as described herein after hydrogen reduction at 420° C. for 20 hours and stretching at a tension of 4000 psi.



FIG. 5 is a graph illustrating sodium and potassium ion concentration for two different glass samples.



FIG. 6A is the maximum transmission for the glass polarizer of FIGS. 4A, 4B and 4C.



FIG. 6B is the minimum transmission for the glass polarizer of FIGS. 4A, 4B and 4C.



FIG. 7 depicts a prior art polarizer.



FIG. 8 is a schematic depiction of a fusion drawn glass.





DETAILED DESCRIPTION

Herein, contrast of a polarizer is the ratio Tmax/Tmin and the contrast ratio is the log10 (Tmax/Tmin), where Tmax is the maximum transmission value and Tmin is the minimum transmission value.


This disclosure is directed to glass optical polarizers made from fusion drawn glass, and to a method for making the polarizers using ion-exchange. This disclosure describes a process by which metal ions are ion-exchanged into a fusion drawn glass sheet, and then the ion-exchanged glass sheet is further processed to make glass optical polarizers. Metal ions such as, but not limited to, noble metal ions can be ion-exchanged into the glass to create optical polarizers. For the purposes of the present disclosure, noble metals include, but are not limited to, copper, gold, iridium, mercury, osmium, palladium, platinum, rhenium, rhodium, ruthenium, and silver.


The polarizers disclosed herein may have a thickness of about 100 μm to about 350 μm and a contrast ratio of at least about 20 dB over a wavelength range of about 900 nm to about 2,000 nm. The polarizers may have a thickness of about 200 μm to about 300 μm. Alternatively, the polarizers may have a contrast ratio of at least about 30 dB over a wavelength range of about 1,000 nm to about 2,000 nm. The polarizers can be made of any fusion drawn glass containing ion-exchangeable alkali metal ions, for example but without limitation, an alkali-containing aluminosilicate glass, alkali-containing aluminoborosilicate glass and soda lime glass. The glass may be fusion drawn glass containing exchangeable alkali metal ions. Exemplary glass compositions can be found in U.S. Pat. Nos. 8,431,301 and 8,158,543, and in U.S. Patent Application Publication Nos. 2011/0045962, 2011/0201490, 2013/0122284 and 2013/0122313, the specifications of which are incorporated by reference in their entirety.


Referring to FIG. 8, the polarizers disclosed herein may include a plurality of elongated zero valent metallic particle polarizing layers 16 having a thickness of about 0.2 μm to about 0.5 μm. The metallic particle polarizing layers 16 may be situated within about 1.0 μm to about 2.0 μm of at least one of the pristine surfaces 12, 14 of the fusion drawn glass 10. Some of the metallic particle polarizing layers may be situated within about 1.0 μm to about 2.0 μm of a first of the two pristine surfaces 12, and some of the metallic particle polarizing layers may be situated within about 1.0 μm to about 2.0 μm of a second of the pristine surfaces 14. The metallic particles correspond to the metal ions which are ion-exchanged into the glass 10.


The ion-exchanged, optical polarizers disclosed herein may find utility in the infrared (IR) region and can be used in, among other things, telecommunications and supporting equipment. The polarizers described herein may be thin, broadband final products that have a good quality surface finish. Due to the fact they are made from fusion drawn glass, the polarizers do not require additional finishing steps. The use of fusion drawn glass imparts characteristics to the surface of the finished glass, as well as to the internal glass network structure, that cannot be obtained using other types of glass, for example, slot drawn glass, float glass and cast glass.


A method for making a glass optical polarizer is provided herein. The method described herein does not affect the pristine nature of the fusion drawn glass surfaces and does not introduce scratches, sub-surface defects, or bubbles into the formed glass. The method may include providing a fusion drawn alkali-containing glass sheet as a substrate. The sheet may have a thickness of about 0.5 mm to about 2.0 mm. The composition of the provided glass sheet may be, but is not limited to, alkali-containing aluminosilicate and alkali-containing aluminoborosilicate glasses.


The method may further include ion-exchanging a noble metal ion into the fusion glass substrate using an ion-exchange molten metal salt bath. The molten metal salt bath may include a noble metal salt. The molten metal salt bath may optionally include an alkali metal salt in which the noble metal salt may be dissolved. At least one of the noble metal salt and the alkali metal salt may be, for example, a nitrate salt. As a further example, the noble metal salt may be a silver nitrate salt and the alkali metal salt may be a potassium nitrate salt.


Examples of ion-exchange methods are described in U.S. Pat. No. 8,312,739, and U.S. Patent Application Publication Nos. U.S. 2008/00407300 and U.S. 2009/0142568, the specifications of which are incorporated by reference in their entirety.


Ion-exchanging a noble metal ion into the fusion glass substrate may be done, for example, for a period of about 1.0 hour to about 20 hours and at a temperature of about 300° C. to about 500° C. The time period and the temperature during ion-exchange may be varied in order to modify the depth to which the noble metal ion diffuses into the fusion glass substrate.


The method may further include removing excess ion-exchange salts from the ion-exchanged substrate to thereby yield a fusion glass substrate having a noble metal ion therein.


The method may further include reducing the noble metal ion in pure hydrogen to form a fusion drawn glass substrate having a plurality of zero valent metallic particle polarizing layers. Reducing the noble metal ion may be done at a pressure of about 1.0 atm to about 20 atm. The pressure may be varied as desired, as higher pressures may be used to affect the rate of reduction. Reducing the noble metal ion may be done at a temperature of about 350° C. to about 550° C. Further, reducing the noble metal ion may be done for a time of about 1.0 hour to about 30 hours.


The method may further include redrawing the fusion drawn glass substrate having a plurality of zero valent metallic particle polarizing layers. Redrawing the fusion glass substrate may be done by heating and stretching the substrate at a viscosity of 105-1010 poise (e.g., 106-107 poise or 107-109 poise). Redrawing the fusion glass substrate may be done, for example, at a temperature above the annealing point Tanneal (i.e., a glass viscosity less than 10−13 poise), but at least about 50° C. below the softening point Tsoft of the glass (i. e., glass viscosity above 10−7.5 poise). The annealing point Tanneal may be about 550° C. to about 650° C. (for example 590° C.<Tanneal<610° C.); and the softening point Tsoft may be about 800° C. to about 900° C. (for example 860° C.<Tsoft<870° C.).


Redrawing the fusion drawn glass substrate may reduce the scale (primarily the thickness) of the substrate to form a glass optical polarizer having a thickness of about 300 μm or less. Redrawing the fusion drawn glass substrate may also yield a stretched microstructure of the noble metal particles embedded in the substrate, which in turn yields polarizing properties suitable for glass optical polarizers. The resultant glass optical polarizer may have two pristine glass surfaces and may be substantially bubble free.


Examples of a redraw process are shown in U.S. Pat. Nos. 7,510,989 and 7,618,908, the specifications of which are incorporated by reference in their entirety.


After redrawing the fusion drawn glass substrate, the resulting polarizers may have a thickness of about 400 μm or less. Alternatively, the thickness may be about 300 μm or less. The polarizers described herein have a transmission of at least about 80% over a wavelength range of about 1,000 nm to about 2,100 nm. The polarizers may have an average redrawn thickness of about 300 μm or less with a good quality surface finish that does not require additional finishing steps due to the fact that the polarizers are formed from fusion drawn glass.


Subsequent to redrawing the fusion drawn glass substrate, the method disclosed herein may further include chemically strengthening the glass optical polarizer. Chemically strengthening may include ion-exchanging a larger alkali metal ion for a smaller alkali metal ion in the fusion glass substrate using an ion-exchange molten metal salt bath. The alkali metal ion may be, for example, a potassium ion, and the smaller alkali metal ion may be, for example, a sodium ion. The molten metal salt bath may include an alkali metal salt. The alkali metal salt may be, for example, a nitrate salt. As a further example, the alkali metal salt may be a potassium nitrate salt. Chemically strengthening may restore any compressive strength that is lost during hydrogen reduction or during the redrawing of the fusion drawn glass substrate and provide a strong, damage resistant glass optical polarizer.


As previously mentioned, fusion drawn glass has two pristine glass surfaces and the method used to make the polarizers described herein does not substantially affect the pristine surfaces. The fusion draw process has been described in U.S. Pat. Nos. 3,338,696, 3,682,609, and 6,974,786, and in U.S. Patent Application Publication No. 2008/0047300, the specifications of which are incorporated by reference in their entirety, and has been employed in the production of active-matrix liquid-crystal-displays (AMLCD). Although display applications dictate the use of alkali-free glass, optical polarizers are not limited to alkali-free glass.


The fusion draw process imparts characteristics to fusion drawn glass not observed in other glass. For example, the process provides precise geometry control which enables uniform glass thickness. The process also eliminates bubbles (also called seeds, voids or inclusions) within the glass. Bubbles can affect light transmission through glass by changing the angle of the light's path as is passes from glass to void and back into glass. This causes birefringence in the glass which affects light transmission by introducing scattering and detrimentally affects optical polarizers, particularly when used in telecommunications equipment. The pristine surfaces of the fusion drawn glass are substantially flat, smooth, and substantially free of any surface contamination in the as-formed state. Furthermore, fusion drawn glass does not contain surface roughness or sub-surface flaws such as arise in any grinding and/or polishing procedure. Unlike other glass processes the fusion draw process buries the forming surfaces of the glass that contact the forming surface of an element, called an isopipe, within the formed sheet of glass. Thus the exterior surfaces of the glass are contact free and pristine.


The use of thin (about 0.5 mm to about 2.0 mm) fusion drawn glass as the starting glass material provides optical polarizers having high quality pristine surfaces (without the need for extensive post processing such as grinding and polishing) and having final thicknesses of about 300 μm or less, a contrast ratio of at least about 20 dB and a transmission of at least about 75% over a wavelength range of about 900 nm to about 2,000 nm. Optical polarizers as described herein may also have a transmission of greater than about 82% over a wavelength range of about 1,000 nm to about 2,000 nm. Within the telecommunications range of about 1,300 nm to about 1,550 nm, the transmission may be greater than about 85%. The contrast ratio may be equal to or greater than about 25 dB over a wavelength range of about 900 nm to about 2,000 nm. Alternatively, the contrast ratio may be greater than about 30 dB over a wavelength range of about 900 nm to about 2,000 nm.


Properties, for example, contrast ratio, of the polarizers described herein, are less sensitive to pulling tensions such as those applied during the redraw process in which glass viscosity is 105-1010 poise (for example 105-107, or 107-109). The viscosity may vary based on the composition of the glass stretched.


EXAMPLES

Embodiments of the present disclosure are further described below with respect to certain exemplary and specific embodiments thereof, which are illustrative only and not intended to be limiting.


In the examples described herein, silver ions were used as the exemplary noble metal ion-exchanged into the fusion drawn glass. However, other noble metal ions can also be ion-exchanged into the fusion drawn glass. In addition, while an alkali-containing aluminoborosilicate glass was used in the examples, other glasses, such as, but not limited to, alkali-containing aluminosilicate glass, can also be used. Exemplary alkali-containing aluminoborosilicate and aluminosilicate glasses may include, but are not limited to, those shown in Table I. Further, while the ion-exchange of noble metal ions and alkali metal ions into the glass is exemplified herein using a molten salt bath method, the ions can also be exchanged into the glass using a paste that is applied to the surface of the glass and then heated.


Table I lists a number of exemplary glass compositions that can be used to make fusion drawn glass for use in an optical polarizer as described herein. The general glass composition, before any ion-exchange, comprises about 60 mol % to about 70 mol % SiO2, about 13 mol % to about 15 mol % Na2O, about 7.0 mol % to about 15 mol % Al2O3, less than about 8.0 mol % B2O3, less than about 8.0 mol % MgO, less than about 2.0 mol % K2O, less than about 1.0 mol % CaO and less than about 0.5 mol % SnO2.









TABLE I







Exemplary Compositions (in mol %) Used in the Examples












Glass 1
Glass 2
Glass 3
Glass 4

















SiO2
64.44
64.65
66.00
69.17



Al2O3
13.9
13.93
10.26
8.53



B2O3
7.15
5.11
0.58
0



Na2O
14.03
13.75
14.23
13.94



K2O
0.54
0
2.37
1.17



MgO
0.01
2.38
5.75
6.45



CaO
0.06
0.14
0.59
0.54



SnO2
0.12
0.08
0.21
0.19










The fusion drawn glass sheets used in the example were obtained using a fusion draw process and were then ion-exchanged for a period of about 20 hours at a temperature of about 420° C. in an ion-exchange bath containing about 2.0 wt. % AgNO3 and about 98 wt. % KNO3. After completion of the ion-exchange, the silver ions were reduced in about 1.0 atm of pure hydrogen at a temperature of about 400° C. for about 10 hours in a hydrogen furnace. The silver-containing glass sheets were then stretched using a redraw process at various temperatures T ranging from about 750° C. to about 900° C. to yield various strips with differing amounts of stretching force applied to them. The contrast ratio and % transmission measurement data for the resulting glass polarizers are shown in FIGS. 1 and 2, respectively.



FIG. 3 is an SEM photograph of a hydrogen reduced silver-containing fusion drawn glass prepared according to the present disclosure. FIG. 3 illustrates four bands or layers comprising zero valent metallic particle layers. More specifically, FIG. 3 shows broken segments of silver-containing sheets of various sizes and shapes which appear as bright lines or broken line segments. When the glass of FIG. 3 is redrawn, the zero valent metallic particles become elongated, thereby polarizing the bands or layers. FIGS. 4A-4C show a variety of sizes and aspect ratios that lead to the broadband properties of the polarizer disclosed herein. FIGS. 4A-4C exemplify the glass polarizers produced according to this disclosure. In contrast to what is illustrated in FIGS. 4A-4C, the prior art polarizers, as shown in FIG. 7, do not show the broad range of particle size and shape.


The scientific literature indicates that the wavelength of maximum absorption for an elongated noble metal nano-particle depends on its aspect ratio. As used herein, the aspect ratio is the ratio of length:diameter. As such, a distribution of aspect ratios of respective nano-particles may provide high contrast and good transmission over a wide wavelength range. Further, as shown in FIG. 3, a distribution of silver metal particle sizes in the hydrogen treated glass leads to a corresponding distribution in aspect ratios. It is believed that during the redraw process, the softened glass acts as a flowing fluid exerting elongation forces on the noble metal particle. Nano-sized particles can be elongated in such a fluid flow field if the forces exerted by the flowing fluid are sufficient to overcome the restoring forces of surface tension, which tend to maintain the particle's spherical shape. These restoring forces are proportional to the surface tension and inversely proportional to the particle radius. Hence, the larger the particle, the less the restoring force and the more easily the particle can be elongated. As such, for a given stress during the redraw process, larger particles will be elongated to higher aspect ratios. This is verified by FIGS. 4A-4C, which show the microstructure of glass polarizers after the redraw process at three different pull tensions.



FIG. 6A illustrates the maximum transmission for the glass polarizer of FIGS. 4A, 4B and 4C. FIG. 6B illustrates the minimum transmission for the glass polarizer of FIGS. 4A, 4B and 4C. As FIGS. 6A and 6B exhibit by their maximum and minimum transmissions, the three polarizers of FIGS. 4A-C are deemed substantially equivalent.


It is believed that the production of the microstructure exhibited in FIG. 3 is the result of instability in a typical reaction-diffusion system, also known as Liesegang effect. The bands of silver particles and line segments shown in FIG. 3 are also referred to as “Liesegang bands”. Without being held to any particular theory, it is believed that the explanation for this behavior or effect is that the fusion drawn glass compositions undergo a reaction-diffusion based instability during hydrogen reduction leading to the production of layers of silver particles that have a wide distribution of both size and aspect ratio. The appearance of the Liesegang layers is believed to be dependent on parameters such as, but not limited to, the glass composition, the silver concentration in the glass, the hydrogen partial pressure, the time and temperature of the ion exchange process, and the time and temperature of the hydrogen reduction process.



FIG. 5 is the ion profile, potassium or sodium ion concentration in mol %, determined as the oxide, versus depth from the glass surface. Potassium oxide (curve 22) and sodium oxide (curve 24) concentrations were measured in fusion drawn glass sheets which had undergone hydrogen reduction and the redraw process. For comparison, potassium oxide (curve 20) and sodium oxide (curve 26) concentrations in fusion drawn glass sheets which had undergone hydrogen reduction, had been redrawn and were subsequently treated in an ion-exchange molten metal salt bath which included a potassium nitrate salt. Table III summarizes the curves shown in FIG. 5.









TABLE III







Numeral meaning for FIG. 5










Numeral, Species
K Ion-exchange after redraw







20, K2O
Yes



22, K2O
No



24, Na2O
No



26, Na2O
Yes










The exchange of potassium ions for sodium ions is known to increase glass strength; however, it was unexpected that an exchange of potassium ions for sodium ions after the formation of Liesegang bands or layers would be possible because it was believed that the bands or layers would block or interfere with the ion-exchange. As seen from FIG. 5, there is a definite exchange of potassium ions for sodium ions near the surface of the glass after treatment in the subsequent ion-exchange molten metal salt bath. As such, FIG. 5 indicates that the polarizers of the present disclosure can be chemically strengthened.


While the disclosure has been described with respect to a limited number of embodiments, those skilled in the art, having benefit of this disclosure, will appreciate that other embodiments can be devised which do not depart from the scope of the disclosure as disclosed herein. Accordingly, the scope of the disclosure should be limited only by the attached claims.

Claims
  • 1. A glass optical polarizer comprising a substantially bubble free fusion drawn glass comprising two pristine glass surfaces and a plurality of polarizing layers comprising elongated metallic particles, wherein the polarizer has a contrast ratio of at least about 20 dB and a % transmission of at least about 75% over a wavelength range of about 900 nm to about 2,000 nm.
  • 2. The glass optical polarizer of claim 1, wherein the polarizer has a thickness of about 300 μm or less.
  • 3. The glass optical polarizer of claim 1, wherein each of the polarizing layers has a thickness of about 0.2 μm to about 0.5 μm, and wherein each of the polarizing layers are situated within about 1.0 μm to about 2.0 μm of at least one the pristine glass surfaces.
  • 4. The glass optical polarizer of claim 1, wherein the polarizer has a thickness of about 200 μm to about 300 μm.
  • 5. The glass optical polarizer of claim 1, wherein the polarizer has a contrast ratio of at least about 25 dB.
  • 6. The glass optical polarizer of claim 1, wherein the elongated metallic particles comprise a noble metal.
  • 7. The glass optical polarizer of claim 6, wherein the noble metal is selected from the group consisting of copper, palladium and silver.
  • 8. The glass optical polarizer of claim 1, wherein the fusion drawn glass is selected from the group consisting of alkali-containing aluminosilicate glass and alkali-containing aluminoborosilicate glass.
  • 9. The glass optical polarizer of claim 1, wherein the fusion drawn glass comprises about 60 mol % to about 70 mol % SiO2, about 13 mol % to about 15 mol % Na2O, about 7.0 mol % to about 15 mol % Al2O3, less than about 8.0 mol % B2O3, less than about 8.0 mol % MgO, less than about 2.0 mol % K2O, less than about 1.0 mol % CaO and less than about 0.5 mol % SnO2.
  • 10. A glass optical polarizer comprising a substantially bubble free fusion drawn glass comprising two pristine glass surfaces and a plurality of polarizing layers comprising elongated metallic particles, wherein each of the polarizing layers has a thickness of about 0.2 μm to about 0.5 μm, and wherein each of the polarizing layers are situated within about 1.0 μm to about 2.0 μm of at least one of the pristine glass surfaces.
  • 11. The glass optical polarizer of claim 10, wherein the polarizer has a thickness of about 300 μm or less.
  • 12. The glass optical polarizer of claim 10, wherein the polarizer has a thickness of about 200 μm to about 300 μm.
  • 13. The glass optical polarizer of claim 10, wherein the polarizer has a contrast ratio of at least about 25 dB.
  • 14. The glass optical polarizer of claim 10, wherein the elongated metallic particles comprise a noble metal.
  • 15. The glass optical polarizer of claim 14, wherein the noble metal is selected from the group consisting of copper, palladium and silver.
  • 16. The glass optical polarizer of claim 10, wherein the fusion drawn glass is selected from the group consisting of alkali containing aluminosilicate glass and alkali containing aluminoborosilicate glass.
  • 17. The glass optical polarizer of claim 10, wherein the fusion drawn glass comprises about 60 mol % to about 70 mol % SiO2, about 13 mol % to about 15 mol % Na2O, about 7.0 mol % to about 15 mol % Al2O3, less than about 8.0 mol % B2O3, less than about 8.0 mol % MgO, less than about 2.0 mol % K2O, less than about 1.0 mol % CaO and less than about 0.5 mol % SnO2.
  • 18. A glass optical polarizer comprising a substantially bubble free fusion drawn glass comprising two pristine glass surfaces and a plurality of polarizing layers comprising elongated metallic particles, wherein the fusion drawn glass comprises about 60 mol % to about 70 mol % SiO2, about 13 mol % to about 15 mol % Na2O, about 7.0 mol % to about 15 mol % Al2O3, less than about 8.0 mol % B2O3, less than about 8.0 mol % MgO, less than about 2.0 mol % K2O, less than about 1.0 mol % CaO and less than about 0.5 mol % SnO2.
Parent Case Info

This application is a divisional of and claims the benefit of priority under 35 U.S.C. § 120 of U.S. application Ser. No. 14/483,306 filed on Sep. 11, 2014, now U.S. Pat. No. 10,209,419, which claims the benefit of priority of U.S. Application Ser. No. 61/878,720 filed on Sep. 17, 2013 the content of which is relied upon and incorporated herein by reference in its entirety.

US Referenced Citations (40)
Number Name Date Kind
815843 Lightbody Mar 1906 A
3338696 Dockerty Aug 1967 A
3682609 Dockerty Aug 1972 A
4479819 Borelli et al. Oct 1984 A
4486213 Lentz et al. Dec 1984 A
5122907 Slocum Jun 1992 A
5886820 Tajima Mar 1999 A
5999315 Fukano et al. Dec 1999 A
6563639 Borrelli et al. May 2003 B1
6753279 Kohli Jun 2004 B2
6761045 Hasui Jul 2004 B2
6887808 Hasui May 2005 B2
6912087 Borrelli Jun 2005 B1
6974786 Helfinstine et al. Dec 2005 B2
7256937 Volke et al. Aug 2007 B2
8063999 Jabri et al. Nov 2011 B2
8158543 Dejneka et al. Apr 2012 B2
8312739 Lee et al. Nov 2012 B2
8431301 Ninomiya et al. Apr 2013 B2
8778820 Gomez et al. Jul 2014 B2
10209419 Borrelli Feb 2019 B2
20030136152 Borrelli et al. Jul 2003 A1
20040172974 Naylor Sep 2004 A1
20060107696 Aoki May 2006 A1
20070093373 Borrelli et al. Apr 2007 A1
20070139770 Morimoto et al. Jun 2007 A1
20070141350 Borrelli et al. Jun 2007 A1
20080047300 Rhoads Feb 2008 A1
20090142568 Dejneka et al. Jun 2009 A1
20090217705 Filippov et al. Sep 2009 A1
20090237787 Yoneda Sep 2009 A1
20110045962 Ruiz De Veye et al. Feb 2011 A1
20110201490 Barefoot et al. Aug 2011 A1
20120111055 Allan et al. May 2012 A1
20120216570 Abramov et al. Aug 2012 A1
20120237674 Kumai Sep 2012 A1
20130122284 Gross May 2013 A1
20130122313 Gross May 2013 A1
20140049708 Murata et al. Feb 2014 A1
20140139910 Gafsi et al. May 2014 A1
Foreign Referenced Citations (9)
Number Date Country
20110607 Apr 2002 DE
10227393 Dec 2003 DE
10227379 Jan 2004 DE
20220607 Jan 2004 DE
07097235 Apr 1995 JP
199959006 Nov 1999 WO
2007050443 May 2007 WO
2010141832 Dec 2010 WO
2013063207 May 2013 WO
Non-Patent Literature Citations (8)
Entry
Bocko, “The challenges of higher-generation glass” Information Display 11/03, SID 2003, pp. 12-15.
Borrelli and Seward, III. “Polarcor polarizing glasses” New Glass 27(104) 2012, pp. 27-35.
CN201480050851.5 First Office Action dated Sep. 29, 2017, China Patent Office.
Ellison and Cornejo, “Glass substrates for liqui crystal displays” International Journal of Applied Glass Science 1(1) pp. 87-103 (2010).
English Translation of JP2016542867 Office Action dated Jul. 3, 2018; 5 Pages; Japanese Patent Office.
International Search Report and Written Opinion PCT/US2014/055802 dated Nov. 28, 2014.
Seward, III. “Elongation and spheroidization of phase-seperated particles in glass” Journal of Non-Crystalline Solids, 15 (1974) pp. 487-504.
Machine Translation of JP2016542867 Office Action dated May 29, 2019, Japan Patent Office, 3 Pgs.
Related Publications (1)
Number Date Country
20190094439 A1 Mar 2019 US
Provisional Applications (1)
Number Date Country
61878720 Sep 2013 US
Divisions (1)
Number Date Country
Parent 14483306 Sep 2014 US
Child 16185320 US