The present application is based on, and claims priority from JP Application Serial Number 2021-184691, filed Nov. 12, 2021, the disclosure of which is hereby incorporated by reference herein in its entirety.
The present disclosure relates to a buffer material.
In recent years, there has been a demand for a buffer material with a reduced environmental load in place of plastic materials. In the related art, a processing method of reusing used paper has been known. For example, JP-A-2015-183297 discloses that a buffer material is produced by reusing used paper.
A device described in JP-A-2015-183297 includes a defibrating unit that defibrates used paper serving as a raw material, a removing unit that removes foreign matter from the defibrated material generated by the defibrating unit, a mixing unit that mixes a binding material with the defibrated material from which the foreign matter has been removed, an accumulating unit that accumulates the mixture generated by the mixing unit, and a molding unit that molds the accumulated material generated by the accumulated unit. With such a device, a buffer material with a reduced environmental load can be produced.
However, there is a concern in that relatively short fibers among the fibers contained in the used paper are scattered in the middle of the production of the buffer material described in JP-A-2015-183297 and are scattered from the surface even after the production of the buffer material.
According to an aspect of the present disclosure, there is provided a buffer material including a buffer sheet that contains cellulose fibers and a binding material binding the cellulose fibers and has a sheet shape; and a nonwoven fabric sheet that is provided on at least one surface side of the buffer sheet and is formed of nonwoven fabric.
Hereinafter, preferred embodiments of the present disclosure will be described in detail.
Examples of the present disclosure will be described in the embodiments described below. The present disclosure is not limited to the following embodiments and include various modifications within a range not departing from the scope of the present disclosure. Further, configurations described below may not all necessarily be essential configurations.
First, a buffer material will be described.
As shown in
The buffer sheet 1A contains a plurality of cellulose fibers and a binding material that binds the cellulose fibers.
The cellulose fibers are an abundant natural material derived from a plant, and it is preferable that the cellulose fibers be used as fibers from the viewpoints of suitably dealing with the environmental problems, saving reserve resources, stably supplying the buffer material WS, reducing the cost, and the like. Further, the cellulose fibers have a particularly high theoretical strength among various fibers and are also advantageous from the viewpoint of improving the strength of the buffer material.
Typically, cellulose fibers are mainly formed of cellulose, but may contain components other than cellulose. Examples of such components include hemicelluloses and lignin.
Here, the content of lignin in the cellulose fibers is preferably 5.0% by mass or less, more preferably 3.0% by mass or less, and still more preferably 1.0% by mass or less.
In this manner, buffering performance, particularly compression characteristics, of the buffer material WS is further improved.
The content of the cellulose in the cellulose fibers is preferably 50.0% by mass or greater, more preferably 60.0% by mass or greater, and still more preferably 80.0% by mass or greater.
For example, fibers which have been subjected to a bleaching treatment or the like may be used as the cellulose fibers. Further, the cellulose fibers may have been subjected to a treatment such as an ultraviolet irradiation treatment, an ozone treatment, or a plasma treatment.
As the cellulose fibers, chemical cellulose fibers such as organic cellulose fibers, inorganic cellulose fibers, and organic-inorganic composite cellulose fibers may be used in addition to the natural cellulose fibers such as animal cellulose fibers and plant cellulose fibers. More specifically, examples of the cellulose fibers include cellulose fibers consisting of cellulose, cotton, cannabis, kenaf, linen, ramie, jute, manila hemp, sisal hemp, conifer, and hardwood. These cellulose fibers may be used alone or in the form of a mixture as appropriate, or may be used as regenerated cellulose fibers which have been purified or the like. Further, the cellulose fibers may be subjected to various surface treatments.
The average length of the cellulose fibers is not particularly limited, but is preferably 10 μm or greater and 50 mm or less, more preferably 20 μm or greater and 5.0 mm or less, and still more preferably 30 μm or greater and 3.0 mm or less in terms of the length-length weighted average cellulose fiber length.
In this manner, the stability of the shape of the buffer material WS, the strength of the buffer material, and the like can be further improved. Further, the buffering performance of the buffer material WS can be further improved.
When the cellulose fibers contained in the buffer sheet 1A are considered to be one independent cellulose fiber, the average thickness thereof is preferably 1.0 μm or greater and 1000 μm or less and more preferably 2.0 μm or greater and 100.0 μm or less.
In this manner, the stability of the shape of the buffer material WS, the strength of the buffer material, and the like can be further improved. Further, the buffering performance of the buffer material WS can be further improved. Further, it is possible to more effectively prevent the surface of the buffer material WS from being unexpectedly uneven.
Further, when a cross section of the cellulose fiber is not circular, a circle having the same area as the area of the cross section is assumed, and the diameter of the circle is used as the thickness of the cellulose fiber.
The average aspect ratio of the cellulose fibers, that is, the average length with respect to the average thickness is not particularly limited, but is preferably 10 or greater and 1000 or less and more preferably 15 or greater and 500 or less.
In this manner, the stability of the shape of the buffer material WS, the strength of the buffer material, and the like can be further improved. Further, the buffering performance of the buffer material WS can be further improved. Further, it is possible to more effectively prevent the surface of the buffer material WS from being unexpectedly uneven.
In the present specification, the term “cellulose fibers” denote a single cellulose fiber or an aggregate of a plurality of cellulose fibers. Further, the cellulose fibers may be cellulose fibers loosened into fibers by performing a defibration treatment on a material to be defibrated, that is, a defibrated material. Examples of the material to be defibrated here include cellulose fibers obtained by being entangled or bound, such as pulp sheets, paper, used paper, tissue paper, kitchen paper, cleaners, filters, liquid absorbing materials, sound absorbing bodies, buffer materials, mats, and corrugated cardboard.
The content of the cellulose fibers in the buffer sheet 1A is preferably 63.0% by mass or greater and 90.0% by mass or less, more preferably 67.0% by mass or greater and 88.0% by mass or less, and still more preferably 72.0% by mass or greater and 86.0% by mass or less.
In this manner, the strength and the buffering performance of the buffer material WS can be further improved.
The buffer sheet 1A contains a binding material.
The binding material has a function of binding a cellulose fiber to a cellulose fiber and may further have other functions. More specifically, the binding material may have a function of suppressing a component other than the cellulose fibers, for example, a colorant or the like described below from falling off from the buffer material.
It is preferable that the binding material have thermal plasticity.
In this manner, the binding material is melted or softened by applying heat in the process of producing the buffer material to spread between cellulose fibers, and thus the cellulose fibers are likely to be bound to each other.
The binding material is melted or softened preferably at 200° C. or lower and more preferably at 160° C. or lower.
In this manner, the cellulose fibers can be more suitably bound to each other by carrying out a heat treatment at a relatively low temperature, which is more preferable from the viewpoint of energy saving.
The glass transition temperature of the binding material is preferably 45° C. or higher and 95° C. or lower and more preferably 50° C. or higher and 90° C. or lower.
In this manner, the cellulose fibers can be more suitably bound to each other by carrying out a heat treatment at a relatively low temperature, which is more preferable from the viewpoint of energy saving. Further, for example, it is possible to effectively prevent the natural binding material from being unexpectedly softened when the buffer material stands in a high temperature environment.
The binding material may be a petroleum-based binding material derived from petroleum or a natural binding material derived from the nature.
Examples of the petroleum-based binding material include various synthetic resins such as thermoplastic resins, thermosetting resins, and photocuring resins.
Examples of the thermoplastic resins among the synthetic resins include an AS resin, an ABS resin, polypropylene, polyethylene, polyvinyl chloride, polystyrene, an acrylic resin, a polyester resin, polyethylene terephthalate, polyphenylene ether, polybutylene terephthalate, nylon, polyamide, polycarbonate, polyacetal, polyphenylene sulfide, and polyether ether ketone.
Among the synthetic resins, biodegradable resins such as polylactic acid, polybutylene succinate, and polyhydroxybutanoic acid may be used as the binding materials other than the natural binding material.
The environmental suitability of the buffer material can be further improved by using the biodegradable resins.
Further, the resins may be, for example, copolymerized or modified.
Examples of the natural binding material include natural resins such as rosin, dammar, mastic, copal, amber, a shellac resin, dragon tree, sandarac, and colophonium, starch which is a natural polymer, and modified products thereof, and one or two or more selected from among these can be used in combination, but it is preferable that the natural binding material contain a shellac resin.
In this manner, the strength and the buffering performance of the buffer material WS can be further improved, and the workability of the buffer material WS can also be further improved.
The starch is a polymer material obtained by polymerizing a plurality of α-glucose molecules with glycoside bonds. The starch may be linear or branched.
For example, starch derived from various plants can be used as the starch. Examples of raw materials of starch include cereals such as corn, wheat, and rice, beans such as broad beans, mung beans, and adzuki beans, tubers such as potatoes, sweet potatoes, and tapioca, wild grasses such as dogtooth violet, bracken, and kadzu, and palms such as sago palm.
For example, processed starch or modified starch may be used as the starch. Examples of the processed starch include acetylated adipic acid crosslinked starch, acetylated starch, oxidized starch, sodium octenyl succinate starch, hydroxypropyl starch, hydroxypropylated phosphoric acid crosslinked starch, phosphorylated starch, phosphoric acid monoesterified phosphoric acid crosslinked starch, urea phosphorylated esterified starch, sodium starch glycolate, and high amylose cornstarch. Further, examples of the modified starch include pregelatinized starch, dextrin, laurylpolyglucose, cationized starch, thermoplastic starch, and carbamic acid starch.
The content of the binding material in the buffer sheet 1A is preferably 12.0% by mass or greater and 28.0% by mass or less, more preferably 14.0% by mass or greater and 25.0% by mass or less, and still more preferably 15.0% by mass or greater and 22.0% by mass or less.
In this manner, the above-described effects are more significantly exhibited.
The buffer sheet 1A is not limited as long as the buffer sheet 1A contains the cellulose fibers and the binding material, but may further contain other components in addition the above-described components. Hereinafter, such components will also be referred to as “other components”.
Examples of other components include a flame retardant, a colorant, an aggregation inhibitor, a surfactant, a fungicide, a preservative, an antioxidant, an ultraviolet absorbing agent, and an oxygen absorbing agent.
The content of other components in the buffer sheet 1A is preferably 7.0% by mass or less, more preferably 5.0% by mass or less, and still more preferably 3.0% by mass or less.
As shown in
In this manner, the strength and the rigidity of the buffer material WS can be further improved. Further, for example, the workability when the sheet-like buffer material WS is processed into a buffer material WS having a three-dimensional shape by carrying out a process of deep drawing or the like can be further improved, and occurrence of wrinkles or breakage can be more effectively prevented.
Next, the nonwoven fabric sheets 1B will be described.
In the present embodiment, the nonwoven fabric sheets 1B are respectively provided on both surface sides of the buffer sheet 1A. The nonwoven fabric sheets 1B are bonded to the buffer sheet 1A. Since the respective nonwoven fabric sheets 1B have the same configuration, one nonwoven fabric sheet 1B will be described below.
As described above, the both surfaces of the buffer sheet 1A are covered with the nonwoven fabric sheet 1B, and thus it is possible to prevent or suppress powder of the cellulose fibers or the like of the buffer sheet 1A from being scattered. Therefore, adhesion of powder of the cellulose fibers or the like to an object to be protected can be prevented or suppressed. Further, as described above, it is possible to prevent or suppress paper powder from being scattered in the middle of the production.
The constituent material for the fibers constituting the nonwoven fabric sheet 1B is not particularly limited, and it is preferable that the nonwoven fabric sheet 1B be formed of one or two or more kinds of materials selected from the group consisting of resin materials such as nylon, polyethylene terephthalate, polypropylene, and polytetrafluoroethylene, inorganic materials such as glass, alumina, and carbon, and natural materials such as metal materials, cellulose, and pulp.
Among these, it is preferable that the fibers constituting the nonwoven fabric sheet 1B be the same as the cellulose fibers used for the buffer sheet 1A.
Further, it is preferable that the average length of the fibers constituting the nonwoven fabric sheet 1B be greater than the average length of the cellulose fibers contained in the buffer sheet 1A. In this manner, it is possible to prevent or suppress paper powder from being scattered from the nonwoven fabric sheet 1B.
The average length of the fibers constituting the nonwoven fabric sheet 1B is not particularly limited, but is preferably 12 μm or greater and 60 mm or less, more preferably 25 μm or greater and 6.0 mm or less, and still more preferably 40 μm or greater and 4.0 mm or less in terms of the length-length weighed average fiber length.
In this manner, it is possible to effectively prevent or suppress the cellulose fibers of the buffer sheet 1A from being scattered from between the fibers constituting the nonwoven fabric sheet 1B.
When the fibers constituting the nonwoven fabric sheet 1B are considered to be one independent cellulose fiber, the average thickness thereof is preferably 1.0 μm or greater and 1000 μm or less and more preferably 2.0 μm or greater and 100.0 μm or less.
In this manner, it is possible to effectively prevent or suppress the cellulose fibers of the buffer sheet 1A from being scattered from between the fibers constituting the nonwoven fabric sheet 1B.
The average aspect ratio of the fibers constituting the nonwoven fabric sheet 1B, that is, the average length with respect to the average thickness thereof is not particularly limited, but is preferably 10 or greater and 1000 or less and more preferably 15 or greater and 500 or less.
Further, the nonwoven fabric sheet 1B may contain a binding material that binds the fibers. The binding material is not particularly limited and can be appropriately selected from, for example, those exemplified as the binding material contained in the buffer sheet 1A and then used.
The thickness (average thickness) of the nonwoven fabric sheet 1B is not particularly limited, but is preferably 0.05 mm or greater and 1 mm or less and more preferably 0.1 mm or greater and 0.5 mm or less.
In this manner, the first projections 11A and the second projections 12A can sufficiently exhibit the above-described effects. Further, it is possible to more effectively prevent or suppress powder of the cellulose fibers or the like of the buffer sheet 1A from being scattered.
The thickness of the nonwoven fabric sheet 1B is preferably 5% or greater and 90% or less and more preferably 10% or greater and 80% or less of the thickness of the buffer sheet 1A. In this manner, the first projections 11A and the second projections 12A can sufficiently exhibit the above-described effects. Further, it is possible to more reliably prevent or suppress powder of the cellulose fibers or the like of the buffer sheet 1A from being scattered.
Further, the basis weight of the fibers of the nonwoven fabric sheet 1B is less than the basis weight of the cellulose fibers in the buffer sheet 1A. In this manner, it is possible to prevent or suppress the buffering performance of the buffer sheet 1A from being decreased due to the nonwoven fabric sheet 1B.
Further, the basis weight of the fibers of the nonwoven fabric sheet 1B is preferably 10 g/m2 or greater and 100 g/m2 or less and more preferably 10 g/m2 or greater and 50 g/m2 or less. In this manner, it is possible to more effectively prevent or suppress powder of the cellulose fibers or the like of the buffer sheet 1A from being scattered and to sufficiently ensure the buffering performance of the buffer sheet 1A.
As described above, the buffer material WS includes the buffer sheet 1A that contains cellulose fibers and a binding material binding the cellulose fibers and has a sheet shape, and the nonwoven fabric sheet 1B that is provided on at least one surface side of the buffer sheet 1A and is formed of nonwoven fabric. With such a configuration, it is possible to prevent or suppress powder of the cellulose fibers or the like of the buffer sheet 1A from being scattered. Therefore, adhesion of powder of the cellulose fibers or the like to an object to be protected can be prevented or suppressed. Further, as described above, it is possible to prevent or suppress paper powder from being scattered in the middle of the production.
Further, in the present embodiment, the nonwoven fabric sheets 1B are respectively provided on both surface sides of the buffer sheet 1A, but the present disclosure is not limited thereto and the nonwoven fabric sheet 1B may be provided only on one surface side thereof. In this case, it is preferable that the side where the nonwoven fabric sheet 1B is provided be in contact with the object to be protected.
Next, a production device that can be used for production of the buffer material WS will be described.
As shown in
The supply unit 10 supplies the raw material to the crushing unit 12. The supply unit 10 is an automatic charging unit for continuously charging the crushing unit 12 with the raw material. The raw material to be supplied to the crushing unit 12 may contain the cellulose fibers.
The crushing unit 12 cuts the raw material supplied by the supply unit 10 in the atmosphere, for example, in the air to form small pieces. As the shape and the size of the small pieces, small pieces with a size of several cm square may be exemplified. In the example shown in the figure, the crushing unit 12 includes crushing blades 14, and the raw material added to the crushing unit 12 can be cut by the crushing blades 14. For example, a shredder is used as the crushing unit 12. The raw material cut by the crushing unit 12 is received by a hopper 1 and transported to the defibrating unit 20 through a pipe 2.
The defibrating unit 20 defibrates the raw material cut by the crushing unit 12. Here, the term “defibrate” denotes that the raw material formed by binding a plurality of cellulose fibers, that is, a material to be defibrated is loosened into individual cellulose fibers. The defibrating unit 20 also has a function of separating substances, such as resin particles, an ink, a toner, a filler, and a bleeding inhibitor, adhering to the raw material from the cellulose fibers.
The material having passed through the defibrating unit 20 is referred to as “defibrated material”. In some cases, “defibrated material” contains, in addition to the loosened cellulose fibers, resin particles separated from the cellulose fibers during loosening of the cellulose fibers, a coloring agent such as an ink, a toner, or a filler, and an additive such as a bleeding inhibitor or a paper strength enhancer. Examples of the resin particles separated from the cellulose fibers include particles containing a resin for binding a plurality of cellulose fibers.
The defibrating unit 20 performs dry type defibration. A treatment of performing defibration or the like in the atmosphere, for example, in the air without performing wet type defibration of dissolving a material in a liquid such as water in a slurry form is referred to as dry type defibration. In the present embodiment, an impeller mill is used as the defibrating unit 20. The defibrating unit 20 has a function of generating an air flow that sucks the raw material and discharges the defibrated material. In this manner, the defibrating unit 20 can suck the raw material from an introduction port 22 together with the air flow, perform the defibration treatment, and transport the defibrated material to a discharge port 24 by the air flow generated by itself. The defibrated material that has passed through the defibrating unit 20 is transferred to the sorting unit 40 through the pipe 3. Further, as the air flow for transporting the defibrated material to the sorting unit 40 from the defibrating unit 20, the air flow generated by the defibrating unit 20 may be used or an airflow generating device such as a blower is provided and an air flow generated by the device may be used.
The sorting unit 40 introduces the defibrated material defibrated by the defibrating unit 20 from the introduction port 42 and sorts out the defibrated material according to the length of the cellulose fibers. The sorting unit 40 includes a drum portion 41 and a housing unit 43 that accommodates the drum portion 41. For example, a sieve is used as the drum portion 41. The drum portion 41 has a net and can divide the defibrated material into a first sorted material that is cellulose fibers or particles having a size smaller than the size of the mesh of the net and thus passing through the net and a second sorted material that is cellulose fibers, undefibrated pieces, or lumps having a size greater than the size of the mesh of the net and thus not passing through the net. For example, the first sorted material is transferred to the mixing unit 50 through the pipe 7. The second sorted material is returned to the defibrating unit 20 from a discharge port 44 through a pipe 8. Specifically, the drum portion 41 is a cylindrical sieve rotationally driven by a motor. As the net of the drum portion 41, for example, a wire net, an expanded metal obtained by expanding a metal plate with cuts, or a punching metal in which holes are formed in a metal plate with a press machine or the like is used.
The first web forming unit 45 transports the first sorted material having passed through the sorting unit 40 to the mixing unit 50. The first web forming unit 45 includes a mesh belt 46, a stretching roller 47, and a suction unit 48.
The suction unit 48 can suck the first sorted material having passed through the opening of the sorting unit 40, that is, the opening of the net and dispersed in the air, onto the mesh belt 46. The first sorted material is accumulated on the moving mesh belt 46 to form a web V. The basic configurations of the mesh belt 46, the stretching roller 47, and the suction unit 48 are the same as the configurations of a mesh belt 72, a stretching roller 74, and a suction mechanism 76 of the second web forming unit 70 described below.
The web V passes through the sorting unit 40 and the first web forming unit 45 and is thus formed in a soft and inflated state due to containing a large amount of air. The pipe 7 is charged with the web V accumulated on the mesh belt 46, and the web V is transported to the mixing unit 50.
The rotating body 49 can cut the web V before the web V is transported to the mixing unit 50. In the example shown in the figure, the rotating body 49 includes a base portion 49a and protrusions 49b protruding from the base portion 49a. The protrusions 49b have, for example, a plate shape. In the example shown in the figure, four protrusions 49b are provided and the four protrusions 49b are provided at equal intervals. Since the base portion 49a rotates in a direction R, the protrusions 49b can rotate using the base portion 49a as an axis. Since the web V is cut by the rotating body 49, for example, a fluctuation in amount of the defibrated material supplied to the accumulating unit 60 per unit time can be reduced.
The rotating body 49 is provided in the vicinity of the first web forming unit 45. In the example shown in the figure, the rotating body 49 is provided in the vicinity of the stretching roller 47a positioned on the downstream in the path of the web V, that is, next to the stretching roller 47a. The rotating body 49 is provided at a position where the protrusions 49b can come into contact with the web V and does not come into contact with the mesh belt 46 on which the web V is accumulated. The shortest distance between the protrusions 49b and the mesh belt 46 is, for example, 0.05 mm or greater and 0.5 mm or less.
The mixing unit 50 mixes the first sorted material having passed through the sorting unit 40, that is, the first sorted material transported by the first web forming unit 45 with an additive containing the natural binding material. The mixing unit 50 includes an additive supply unit 52 that supplies the additive, a pipe 54 that transports the first sorted material and the additive, and a blower 56. In the example shown in the figure, the additive is supplied to the pipe 54 through the hopper 9 from the additive supply unit 52. The pipe 54 is connected to the pipe 7.
The mixing unit 50 allows the blower 56 to generate an air flow so that the first sorted material and the additive can be transported while being mixed with each other in the pipe 54. Further, the mechanism of mixing the first sorted material and the additive is not particularly limited, and the first sorted material and the additive may be mixed by being stirred using a blade rotating at a high speed or may be mixed by using rotation of a container as in a case of a V type mixer.
A screw feeder as shown in
Further, the additive to be supplied from the additive supply unit 52 may contain, in addition to the natural binding material, a colorant for coloring the cellulose fibers, an aggregation inhibitor for suppressing aggregation of the cellulose fibers or aggregation of the natural binding material, and a flame retardant for making the cellulose fibers and the like difficult to burn, depending on the type of the buffer material WS to be produced. The composition for producing a buffer material which is the mixture having passed through the mixing unit 50, that is, the mixture of the first sorted material and the additive is transferred to the accumulating unit 60 through the pipe 54.
The accumulating unit 60 introduces the mixture having passed through the mixing unit 50 from the introduction port 62, loosens the defibrated material of the entangled cellulose fibers, and drops the mixture while dispersing the mixture in the air. In this manner, the accumulating unit 60 can uniformly accumulate the mixture on the second web forming unit 70.
The accumulating unit 60 includes a drum portion 61 and a housing unit 63 that accommodates the drum portion 61. A cylindrical rotating sieve is used as the drum portion 61. The drum portion 61 has a net and drops the cellulose fibers or particles which are contained in the mixture having passed through the mixing unit 50 and have a size smaller than the size of the mesh of the net. The configuration of the drum portion 61 is the same as the configuration of the drum portion 41.
Further, “sieve” of the drum portion 61 may not have a function of sorting out a specific object. That is, “sieve” used as the drum portion 61 denotes a portion provided with a net, and the drum portion 61 may drop the entire mixture introduced to the drum portion 61.
The second web forming unit 70 accumulates the material having passed through the accumulating unit 60 to form a web W which is an accumulated material serving as the buffer material WS. The second web forming unit 70 includes a nonwoven fabric sheet supply unit 70A and a nonwoven fabric sheet supply unit 70B that supply the nonwoven fabric sheet 1B, the mesh belt 72, the stretching roller 74, and the suction mechanism 76. For example, a molding die having a shape corresponding to the shape of the buffer sheet 1A shown in
The nonwoven fabric sheet supply unit 70A is a roller that develops and delivers the nonwoven fabric sheet 1B wound in a roll shape. The nonwoven fabric sheet supply unit 70A is disposed above the mesh belt 72 and on the upstream of the mesh belt 72 in the transport direction. The nonwoven fabric sheet 1B developed and delivered by the nonwoven fabric sheet supply unit 70A is supplied onto the mesh belt 72.
The mesh belt 72 accumulates the material having passed through the opening of the accumulating unit 60, that is, the opening of the net on the molding die while moving. The mesh belt 72 is configured to be stretched by the stretching roller 74 and circulate the air to make the material having passed through the accumulating unit difficult to pass through. The mesh belt 72 moves by rotation of the stretching roller 74. The mesh belt 72 continuously drops and accumulates the material having passed through the accumulating unit 60 while continuously moving and transporting the nonwoven fabric sheet 1B on the mesh belt 72, and thus the web W is formed on the molding die provided on the nonwoven fabric sheet 1B. The mesh belt 72 is made of, for example, a metal, a resin, cloth, or nonwoven fabric.
The suction mechanism 76 is provided below the mesh belt 72, that is, on a side opposite to the side of the accumulating unit 60. The suction mechanism 76 can generate an air flow flowing downward, that is, an air flow flowing to the mesh belt 72 from the accumulating unit 60. The mixture dispersed in the air by the accumulating unit 60 can be sucked onto the nonwoven fabric sheet 1B on the mesh belt 72 by the suction mechanism 76. In this manner, the discharge rate of the material from the accumulating unit 60 can be increased. Further, the suction mechanism 76 can form a downflow in the path where the mixture falls, and thus it is possible to suppress the defibrated material and the additive from being entangled with each other during the fall.
The nonwoven fabric sheet supply unit 70B is a roller that develops and delivers the nonwoven fabric sheet 1B wound in a roll shape. The nonwoven fabric sheet supply unit 70B is disposed above the mesh belt 72 and on the upstream of the mesh belt 72 in the transport direction. The nonwoven fabric sheet 1B developed and delivered by the nonwoven fabric sheet supply unit 70A is supplied onto the web W accumulated on the nonwoven fabric sheet 1B. In this manner, a laminate S in which the nonwoven fabric sheet 1B, the web W, and the nonwoven fabric sheet 1B are laminated in order is generated. The laminate S is transported to the buffer material forming unit 80.
As described above, the laminate S in which the nonwoven fabric sheet 1B, the web W, and the nonwoven fabric sheet 1B are laminated in order is formed by carrying out the web forming step performed by the accumulating unit 60 and the second web forming unit 70.
The thickness of the web W is preferably 2.0 mm or greater and 150 mm or less, more preferably 3.0 mm or greater and 120 mm or less, and still more preferably 5.0 mm or greater and 100 mm or less.
Further, the density of the web W is preferably 0.01 g/cm3 or greater and 0.05 g/cm3 or less and more preferably 0.02 g/cm3 or greater and 0.04 g/cm3 or less.
Further, the basis weight of the web W is preferably 150 g/m2 or greater and 650 g/m2 or less, more preferably 160 g/m2 or greater and 600 g/m2 or less, and still more preferably 200 g/m2 or greater and 500 g/m2 or less.
The buffer material forming unit 80 forms the buffer material WS by heating the web W accumulated on the molding die provided on the mesh belt 72. The buffer material forming unit 80 heats the web W which is the accumulated material of the mixture of the defibrated material and the additive mixed in the second web forming unit 70, and thus the natural binding material is softened and melted. In this manner, the plurality of cellulose fibers are bound to each other. Further, the fibers of the nonwoven fabric sheet 1B and the fibers contained in the web W can be bound by the binding material contained in the web W. In this manner, the buffer sheet 1A and the nonwoven fabric sheet 1B can be bonded to each other, and thus the buffer material WS to which the buffer sheet 1A and the nonwoven fabric sheet 1B have been bonded can be obtained.
The buffer material forming unit 80 includes a heating unit 84 that heats the laminate S. For example, a heat press or a heating roller may be used as the heating unit 84, and an example of using a heating roller will be described below. The number of heating rollers in the heating unit 84 is not particularly limited. In the example shown in the figure, the heating unit 84 includes a pair of heating rollers 86. The buffer material WS can be molded while the laminate S is continuously transported by configuring the heating unit 84 as the heating rollers 86.
The heating rollers 86 are disposed such that the rotation axes thereof are in parallel with each other. The roller radius of the heating roller 86 is preferably 2.0 cm or greater and 5.0 cm or less, more preferably 2.5 cm or greater and 4.0 cm or less, and still more preferably 2.5 cm or greater and 3.5 cm or less.
The heating rollers 86 come into contact with the laminate S and heat the laminate S while transporting the web W in a state of interposing the web W.
The rotation speed of the heating rollers 86 is, for example, preferably 20 rpm or greater and 500 rpm or less, more preferably 30 rpm or greater and 350 rpm or less, and still more preferably 50 rpm or greater and 300 rpm or less.
In this manner, the surface region of the web W can be sufficiently heated with high accuracy.
The heating rollers 86 transport the laminate S in a state of interposing the laminate S to form the buffer material WS having a predetermined thickness.
Here, the pressure applied to the web W by the heating rollers 86 is preferably 0.50 MPa or less, more preferably 0.01 MPa or greater and 0.45 MPa or less, and still more preferably 0.05 MPa or greater and 0.40 MPa or less.
The surface temperature of the heating rollers 86 when the web W is heated is preferably 160° C. or higher, more preferably 165° C. or higher and 250° C. or lower, and still more preferably 170° C. or higher and 220° C. or lower.
The heating and pressing time in the present step is preferably 1 second or longer and 300 seconds or shorter, more preferably 10 seconds or longer and 60 seconds or shorter, and still more preferably 15 seconds or longer and 45 seconds or shorter.
In this manner, the productivity of the buffer material WS can be further improved, and the strength, the buffering performance, and the like of the buffer material WS can be further improved. It is also preferable that the heating and pressing time be in the above-described ranges even from the viewpoint of energy saving.
The production device 100 of the present embodiment may include the cutting unit 90 as necessary. In the example shown in the figure, the cutting unit 90 is provided on the downstream of the buffer material forming unit 80. The cutting unit 90 cuts the molding die containing the buffer material WS molded by the buffer material forming unit 80. In the example shown in the figure, the cutting unit 90 includes a first cutting unit 92 cutting the molding die of the buffer material WS in a direction intersecting the transport direction of the buffer material WS and a second cutting unit 94 cutting the buffer material WS in a direction parallel to the transport direction. The second cutting unit 94 cuts, for example, the molding die containing the buffer material WS having passed through the first cutting unit 92.
Further, the production device 100 of the present embodiment may include the humidifying unit 78. In the example shown in the figure, the humidifying unit 78 is provided on the downstream of the cutting unit 90 and on the upstream of a discharge unit 96. The humidifying unit 78 is capable of applying water or water vapor to the buffer material WS. Specific examples of the aspect of the humidifying unit 78 include an aspect of spraying mist of water or an aqueous solution, an aspect of spraying water or an aqueous solution, and an aspect of jetting water or an aqueous solution from an ink jet head for adhesion.
Since the production device 100 includes the humidifying unit 78, the buffer material WS to be formed can be humidified. In this manner, the cellulose fibers are humidified and softened. Therefore, when a container or the like is three-dimensionally molded by using the buffer material WS, wrinkles or breakage is less likely to occur. Further, since a hydrogen bond is easily formed between cellulose fibers by humidifying the buffer material WS, the density of the buffer material WS is increased, and for example, the strength can be improved.
In the example of
The buffer material WS is obtained, for example, as a three-dimensional molded body having a convex shape by demolding only the buffer material WS from the molding die where the buffer material WS has been molded.
Hereinafter, the second embodiment of the buffer material of the present disclosure will be described with reference to the accompanying drawings, but the description will be made mainly on the points different from those in the above-described embodiment and the description of the same points as described above will not be provided.
In the configuration as shown in
As shown in
With such a configuration, when the buffer material WS is bent or rolled, the buffer material WS can be similarly deformed regardless of which direction the buffer material WS is bent or rolled. Further, the first projections 11A are first brought into contact with the object to be protected and can be preferentially deformed as compared with a buffer material having a flat surface without the first projections 11A. Therefore, the impact applied from the object to be protected can be absorbed in stages. As a result, the buffering performance is improved. As described above, the buffering performance can be enhanced while the degree of freedom during deformation is ensured, by allowing the buffer material to have the first projections 11A.
The length (maximum length) of a side of the first projection 11A in plan view is preferably 0.1 mm or greater and 5 mm or less and more preferably 0.2 mm or greater and 3 mm or less.
In this manner, when the buffer material WS is bent or rolled, it is possible to prevent the operation from being hindered.
The projection amount (maximum projection amount) of the first projection 11A is preferably 0.1 mm or greater and 5 mm or less and more preferably 0.2 mm or greater and 3 mm or less.
In this manner, the buffering performance can be sufficiently exhibited, and it is possible to prevent the operation from being hindered when the buffer material WS is bent or rolled.
Further, the buffer sheet 1A further has a plurality of second projections 12A with a projection amount greater than that of the first projections 11A. Since the buffer sheet 1A is provided with the second projections 12A, the second projections 12A and the first projections 11A are sequentially brought into contact with the object to be protected and can be deformed. Therefore, the impact applied from the object to be protected can be absorbed in multiple stages. As a result, the buffering performance is further improved.
Further, the second projections 12A have a semispherical shape. Therefore, the buffering performance can be further enhanced, and it is possible to more effectively prevent the operation from being hindered when the buffer material WS is bent or rolled.
The diameter (maximum length) of the second projection 12A in plan view is preferably 0.4 mm or greater and 20 mm or less and more preferably 1 mm or greater and 5 mm or less.
In this manner, when the buffer material WS is bent or rolled, it is possible to prevent the operation thereof from being hindered.
The projection amount (maximum projection amount) of the second projection 12A is preferably 0.2 mm or greater and 10 mm or less and more preferably 1 mm or greater and 5 mm or less.
In this manner, the buffering performance can be sufficiently exhibited, and it is possible to prevent the operation from being hindered when the buffer material WS is bent or rolled.
Further, the maximum projection amount of the second projection 12A is preferably 1.1 times or greater and 8 times of less and more preferably 1.5 times or greater and 4 times or less the maximum projection amount of the first projection 11A. In this manner, the buffering performance can be further enhanced, and it is possible to more effectively prevent the operation from being hindered when the buffer material WS is bent or rolled.
The density of the buffer sheet 1A is not particularly limited, but is preferably 0.02 g/cm3 or greater and 0.20 g/cm3 or less, more preferably 0.03 g/cm3 or greater and 0.15 g/cm3 or less, and still more preferably 0.05 g/cm3 or greater and 0.11 g/cm3 or less.
In this manner, the strength and the rigidity of the buffer material WS can be further improved. Further, the durability of the buffer material WS against an impact can be further improved. Further, for example, the workability when the buffer material WS is processed into a buffer material WS having a three-dimensional shape by carrying out a process of deep drawing or the like can be further improved, and occurrence of wrinkles or breakage can be more effectively prevented.
Particularly, when the buffer material WS satisfies the above-described conditions for the thickness and the above-described conditions for the density, the effects obtained by satisfying the conditions are synergistically enhanced so that the above-described effects are more significantly exhibited.
The basis weight of the cellulose fibers in the buffer sheet 1A is not particularly limited, but is preferably 150 g/m2 or greater and 650 g/m2 or less, more preferably 160 g/m2 or greater and 600 g/m2 or less, and still more preferably 200 g/m2 or greater and 500 g/m2 or less. In this manner, the strength and the rigidity of the buffer material WS can be further improved. Further, the durability of the buffer material against an impact can be further improved. Further, for example, the workability when the sheet-like buffer material WS is processed into a buffer material WS having a three-dimensional shape by carrying out a process of deep drawing or the like can be further improved, and occurrence of wrinkles or breakage can be more effectively prevented.
Further, the shape of the first projection 11A in plan view is not particularly limited, and the first projection 11A may have, for example, a triangular or pentagonal or higher polygonal shape or a circular shape.
Further, the shape of the second projection 12A in plan view is not particularly limited, and the second projection 12A may have, for example, a triangular shape, a rectangular shape, or a pentagonal or higher polygonal shape.
As described above, the buffer sheet 1A has unevenness on the surface. According to such a configuration, the first projections 11A, which are convex portions, are first brought into contact with the object to be protected and can be preferentially deformed as compared with a buffer material having a flat surface without unevenness. Therefore, the impact applied from the object to be protected can be absorbed in stages. As a result, the buffering performance is improved.
Hereinafter, the third embodiment of the buffer material of the present disclosure will be described with reference to the accompanying drawing, but the description will be made mainly on the points different from those in the above-described embodiments and the description of the same points as described above will not be provided.
In the present embodiment, the buffer material WS has a wavy shape in which a curve to one side and a curve to the other side in the thickness direction are repeated as shown in
The wavy pitch is not particularly limited, but is, for example, preferably 0.1 mm or greater and 10 mm or less and more preferably 0.2 mm or greater and 5 mm or less.
As described above, the buffer sheet 1A has unevenness on the surface. According to such a configuration, the convex portions are first brought into contact with the object to be protected and can be preferentially deformed as compared with a buffer material having a flat surface without unevenness. Therefore, the impact applied from the object to be protected can be absorbed in stages. As a result, the buffering performance is improved. Further, according to the present embodiment, when the buffer material is bent such that the fold comes in a direction orthogonal to a direction in which the wavy shape is repeated, the operation can be easily performed.
Hereinbefore, the suitable embodiments of the present disclosure have been described, but the present disclosure is not limited thereto.
For example, the present disclosure has configurations that are substantially the same as the configurations described in the embodiments, for example, configurations with the same functions, the same methods, and the same results as described above or configurations with the same purposes and the same effects as described above. Further, the present disclosure has configurations in which parts that are not essential in the configurations described in the embodiments have been substituted. Further, the present disclosure has configurations exhibiting the same effects as the effects of the configurations described in the embodiments or configurations capable of achieving the same purposes as the purposes of the configurations described in the embodiments. Further, the present disclosure has configurations in which known techniques have been added to the configurations described in the embodiments.
For example, the buffer material of the present disclosure is not limited to the buffer material produced by the above-described method using the above-described production device.