Patent Application
20170313630
The present disclosure relates to a building assembly containing a water barrier coating film and a method of making the building assembly.
Hotmelt coated gypsum boards for the tile-backer market are highly water resistive but have the disadvantage that water vapor cannot penetrate through the boards. It is desirable to develop a coated gypsum board which has both a high resistance to fluid water but allows water vapor penetration.
According to one embodiment, a building assembly comprises a substrate and a water barrier coating film. The substrate comprises a first surface and a second surface opposite to the first surface, and the coating film overlies the first surface, the second surface, or the first surface and the second surface of the substrate. The coating film comprises a thermoplastic polymer and microporous particles; and the coating film has a water vapor permeability of at least 2 US perms as tested according to ASTM E96 (2014) at 21° C. and 50% average relative humidity.
According to another embodiment, a method for making a building assembly comprises: providing a substrate comprising a first surface and a second surface opposite to the first surface; preparing a water barrier coating film comprising a thermoplastic polymer and microporous particles; and applying the water barrier coating film on the first surface, the second surface, or the first surface and second surface of the substrate.
According to a further embodiment, a water barrier coating film comprises a thermoplastic polymer and microporous particles, the water barrier coating film having a water vapor permeability of at least 2 US perms as tested according to ASTM E96 (2014) at 21° C. and 50% average relative humidity.
The present disclosure may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.
As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of features is not necessarily limited only to those features but may include other features not expressly listed or inherent to such process, method, article, or apparatus.
As used herein, and unless expressly stated to the contrary, “or” refers to an inclusive- or and not to an exclusive- or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).
Also, the use of “a” or “an” are employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.
Various embodiments of the present disclosure will now be described, by way of example only, with reference to the accompanying drawings.
The present disclosure relates to a building assembly comprising a substrate that is protected by a water barrier coating film. The water barrier coating film includes at least one thermoplastic polymer and microporous particles, and can have a water vapor permeability (WVP) of at least 2 US perms.
As used herein, when referring to the WVP of the water barrier coating film, the cited WVP value is described in US perms and has been measured according to standard ASTM E96 (2014) at 21° C. and 50% relative humidity, unless indicated otherwise. 1 US perm converts to 0.659045 metric perms.
In one embodiment, as illustrated in
The substrate 12 can be any structure involved in the construction of buildings that would benefit from a coating film 13 that can protect against fluid water, but may be permeable for water vapor to a certain extent. A non-limiting example for building substrates can be a wall assembly, a board, a siding, a sheet good, or a panel. In a particular embodiment, the substrate 12 may be a board comprising gypsum.
The microporous particles 14 can comprise microporous glass beads, microporous ceramic beads, microporous polymer beads, beads formed from a naturally microporous material, or any combination thereof. In a particular embodiment, the microporous particles can consist essentially of microporous glass beads.
In certain embodiments, the microporous particles may have an average particle size of at least 25 μm, such as at least 40 μm, at least 50 μm, at least 70 μm, at least 100 μm, or at least 130 μm. In other embodiments, the microporous particles may be not greater than 1000 μm, such as not greater than 900 μm, not greater than 800 μm, not greater than 700 μm, not greater than 600 μm, or not greater than 500 μm. The average particle size of the microporous particles can be a value between any of the maximum and minimum values noted above, such as from 25 μm to 1000 μm, from 80 μm to 850 μm, or from 120 μm to 500 μm.
As used herein, when referring to the average microporous particle size, the recited values refer to the D50 values of the particle distribution.
The average particle size of the microporous particles can be further defined by the ratio of the average particles size to the maximum thickness of the coating film. In embodiments, a ratio of the average microporous particles size to the maximum thickness of the coating film can be at least 0.1 to 1, at least 0.2 to 1, or at least 0.3 to 1. In other embodiments, the ratio of the average microporous particles size to the total thickness of the coating film may be not greater than 1 to 1, such as not greater than 0.9 to 1, or not greater than 0.8 to 1.
In embodiments, the thickness of the water barrier coating film of the present disclosure can be at least 25 μm, such as at least 30 μm, at least 40 μm, or at least 50 μm. In other embodiments, the thickness of the coating film may be not greater than 1000 μm, such as not greater than 900 μm, not greater than 800 μm, or not greater than 700 μm. The thickness of the water barrier coating film can be a value within any of the maximum and minimum values noted above, such as from 25 μm to 1000 μm, from 50 μm to 900 μm, or from 100 μm to 800 μm.
In further embodiments, the amount of the microporous particles in the coating film can be at least 1 vol %, such as at least 5 vol %, at least 10 vol %, or at least 15 vol % based on the total weight of the coating. In other embodiments, the amount of the microporous particles may be not greater than 60 vol %, such as not greater than 55 vol %, not greater than 50 vol %, not greater than 40 vol %, not greater than 35 vol %, or not greater than 30 vol % based on the total weight of the coating film. The amount of the microporous particles in the coating film can be a value between any of the maximum and minimum values noted above, such as from 1 vol % to 60 vol %, from 10 vol % to 50 vol %, or from 16 vol % to 35 vol % based on the total volume of the coating film.
In yet further embodiments, the microporous particles contained in the coating film of the present disclosure may have an average pore diameter of at least 30 nm, such as at least 50 nm, at least 70 nm, or at least 100 nm; in other embodiments, the average pore diameter may not be greater than 100 μm, such as not greater than 50 μm, not greater than 10 μm, or not greater than 1 μm. The average pore diameter of the microporous particles can be a value between any of the maximum and minimum values noted above, such as from 30 nm to 100 μm, from 50 nm to 50 μm, or from 100 nm to 1 μm.
In yet other embodiments, the microporous particles contained in the water barrier coating film of the present disclosure can have an average pore volume of at least 0.05 cm3/g, such as at least 0.1 cm3/g, at least 0.2 cm3/g, at least 0.3 cm3/g, or at least 0.5 cm3/g. In other embodiments, the average pore volume may not greater than 2 cm3/g, such as not greater than 1.5 cm3/g, not greater than 1.0 cm3/g, not greater than 0.9 cm3/g, or not greater than 0.8 cm3/g. The average pore volume of the microporous particles can be a value between any of the maximum and minimum values noted above, such as from 0.05 cm3/g to 2.0 cm3/g, from 0.2 cm3/g to 0.9 cm3/g, or from 0.3 cm3/g to 0.8 cm3/g.
In further embodiments, the microporous particles can have an aspect ratio of length to width of not greater than 5, such as not greater than 3, not greater than 2, or not greater than 1.5. In a particular embodiment, the microporous particles contained in the coating film can be spherical.
The at least one thermoplastic polymer of the water barrier coating film can include, for example, an ethylene vinyl acetate copolymer, a polyolefin, an ethylene methacrylate (EMA) copolymer, an ethylene acrylic acid copolymer (EAA), a styrene block copolymer, a polyurethane, a polyamide, or any combination thereof.
In certain embodiments, the amount of the thermoplastic polymer in the coating film can be at least 10 wt %, such as at least 20 wt %, or at least 30 wt %. In other embodiments, the amount of thermoplastic polymer may be not greater than 70 wt %, such as not greater than 60 wt %, not greater than 50 wt %, or not greater than 45 wt % based on the total weight of the coating. The amount of thermoplastic polymer in the coating film can be a value between any of the minimum and maximum values noted above, such as from 10 wt % to 70 wt %, from 15 wt % to 65 wt %, or from 20 wt % to 55 wt %.
In addition to the thermoplastic polymer, the water barrier coating film of the present disclosure can comprise a wax, a tackifying resin, or both.
Non-limiting examples of a suitable wax can be polar and non-polar polyethylene (PE) wax, polypropylene wax (PP), metallocene PE or PP wax, maleic anhydride grafted PE or PP wax, Montan wax, silane-modified PE wax, amide wax, ester wax, or PE/polytetrafluoroethylene (PTFE) wax, or any combination thereof.
The wax may be present in the water barrier coating film in an amount of at least 5 wt %, such as at least 7 wt %, at least 10 wt %, or at least 15 wt % based on the total weight of the coating film. In other aspects, the amount of wax in the coating film may be not greater than 40 wt %, such as not greater than 35 wt %, not greater than 30 wt %. The amount of wax in the coating film can be a value between any of the maximum and minimum values noted above, such as from 5 wt % to 40 wt %, from 8 wt % to 35 wt % or from 20 wt % to 30 wt % based on the total weight of the coating film.
With regard to the tackifying resin that may be present in the water barrier coating film, non-limiting examples of tackifying resin can be aliphatic resin, such as mixed monomers of petroleum origin, aromatic resin, such as mixtures of petroleum derived feed streams, pure monomer resin, hydrogenated pure monomer resin, hydrogenated aliphatic resin, or any combination thereof.
In embodiments, the amount of tackifying resin in the coating film can be at least 10 wt %, such as at least 15 wt %, at least 20 wt %, or at least 25 wt % based on the total weight of the coating film. In other embodiments, the amount of tackifying resin may be not greater than 50 wt %, such as not greater than 45 wt %, not greater than 40 wt %, or not greater than 35 wt %. The amount of tackifying resin in the coating film can be a value between any of the maximum and minimum values noted above, such as from 10 wt % to 50 wt %, from 15 wt % to 45 wt %, or from 20 wt % to 40 wt % based on the total weight of the coating film.
In one embodiment, the water barrier coating film can further comprise a cellulose ester, for example, cellulose acetate, cellulose propionate, cellulose butyrate, cellulose acetate propionate, cellulose acetate butyrate, cellulose propionate butyrate, or any combination thereof. In a particular embodiment, the cellulose ester can be cellulose acetate propionate.
In other embodiments the coating film can further include a UV absorber, a light stabilizer, a filler, a dye, a dispersant or any combination thereof.
The water barrier coating film of the present disclosure can allow to a certain extent water vapor flow from the substrate to the exterior air, but can protect the substrate from being reached from exterior liquid water. In embodiments, the water barrier coating film can have a water vapor permeability (WVP) of at least 2 US perms, such as at least 3 perms, at least 5 US perms, at least 7 US perms, at least 10 US perms, at least 15 US perms, at least 20 US perms, or at least 25 US perms. In further embodiments, the water barrier coating film of the present disclosure can have a WVP of not greater than 150 US perms, such as not greater than 100 US perms, not greater than 50 US perms, or not greater than 30 US perms. The WVP of the coating film can be a value between any of the maximum and minimum values noted above, such as from 2 US perms to 10 US perms, from 3 US perms to 120 US perms, from 5 US perms to 110 US perms, or from 10 US perms to 80 US perms.
In certain embodiments, the water barrier coating film can be a one-layer coating in direct contact with at least one surface layer of the building substrate. In further particular embodiments, the water barrier coating film may be also a multi-layer coating, for examples, a two-layer coating or a three-layer coating.
In a particular embodiment, the water barrier coating film can include at least one thermoplastic polymer in an amount of 20 wt % to 60 wt % based on the total weight of the coating film, a wax in an amount of 5 wt % to 40 wt % based on the total weight of the coating film; a tackifying resin in an amount of 15 wt % to 50 wt % based on the total weight of the coating film; and microporous particles in an amount of 16 vol % to 35 vol % based on the total volume of the coating film. Optionally, the coating film may further include a UV absorbent in an amount of 0.1 wt % to 3 wt % based on the total weight of the coating film.
In a particular embodiment, the water barrier coating film can be a hotmelt coating including embedded microporous particles.
The present disclosure is further directed to a method for making the above-described building assembly. The method can comprise: providing a substrate having a first surface and a second surface opposite to the first surface; preparing a water barrier coating film comprising a thermoplastic polymer and microporous particles; and applying the water barrier coating film on the first surface, the second surface, or the first and the second surface of the substrate.
In one embodiment, the water barrier coating film 13 can be prepared as follows: melting a coating composition, wherein the coating composition comprises a thermoplastic polymer; applying a layer of the melted coating composition onto a removable liner; adding microporous particles on top of the applied melted coating composition that a majority of the microporous particles is embedded into the melted coating composition; and allowing the melted coating composition to cool and to solidify to form the water barrier coating film 13, comprising microporous particles 14 embedded into a coating composition 15 (see
The adding of the microporous particles can be performed by spreading the microporous particles over the applied layer of the melted coating composition and by further pressing, e.g., with a heavy plate or a heavy roller, the microporous particles into the melted coating layer. The pressing of the microporous particles into the melted coating layer can be assisted by placing a removable liner on top of the spreaded microporous particles and underneath the applied weight. In a particular aspect, the liner can be a non-sticking polymeric film, e.g., a PTFE film.
In certain embodiments, a ratio Tp to Tm can be equal or larger then 1:1, with Tp being the average particle size of the microporous particles before adding to the layer of the melted coating composition, and Tm being the thickness of the layer of the melted coating composition before adding of the microporous particles. In aspects, the ratio Tp to Tm can be from 1:1 to 3:1, from 1:1 to 2:1, from 1:1 to 1.7:1, from 1:1 to 1.5:1, or from 1.1:1 to 1.7:1.
The water barrier coating film illustrated in
The water barrier coating film 13 can be applied to a surface of a substrate 12 by laminating. During laminating, the coating film is softened at elevated temperatures up to 110° C., but not melted, and adhered to the respective surface of the substrate. In a particular aspect, applying the water barrier coating film via laminating can be conducted when the substrate is a gypsum board.
In another embodiment, depending on the material of the substrate, the water barrier coating film may be also formed directly on a surface of a substrate. In this embodiment, the above-described procedure can be the same, except that the removable liner is a surface of the substrate.
It has been surprisingly discovered that by selecting microporous particles having a certain particle size and porosity in relation to the coating layer thickness and type of coating composition, a water barrier coating film can be obtained having a desired water vapor permeability and while being resistive to fluid water.
Building assemblies comprising the water barrier coating films of the present disclosure can be used, for example, as backing boards for tiles.
Many different aspects and embodiments are possible. Some of those aspects and embodiments are described herein. After reading this specification, skilled artisans will appreciate that those aspects and embodiments are only illustrative and do not limit the scope of the present invention. Embodiments may be in accordance with any one or more of the embodiments as listed below.
A building assembly comprising a substrate and a water barrier coating film, wherein the substrate comprises a first surface and a second surface opposite to the first surface, and the coating film overlies the first surface, the second surface, or the first surface and the second surface of the substrate; the coating film comprises a thermoplastic polymer and microporous particles; and the coating film has a water vapor permeability of at least 2 US perms as tested according to ASTM E96 (2014) at 21° C. and 50% average relative humidity.
The building assembly of embodiment 1, wherein the microporous particles comprise microporous glass beads, microporous ceramic beads, microporous polymer beads, a naturally microporous material, or any combination thereof.
The building board of embodiment 2, wherein the microporous particles are consisting essentially of microporous glass beads.
The building assembly of any of the preceding embodiments, wherein the microporous particles have an average particles size of at least 25 microns, such as at least 30 microns, at least 30 microns, at least 50 microns, at least 70 microns, or at least 100 microns.
The building assembly of any of the preceding embodiments, wherein the microporous particles have an average particles size of not greater than 1000 microns, such as not greater than 800 microns, not greater than 700 microns, or not greater than 500 microns.
The building assembly of any of the preceding embodiments, wherein the coating film has a thickness of at least 25 microns, such as at least 30 microns, at least 40 microns, at least 50 microns, or at least 100 microns.
The building assembly of any of the preceding embodiments, wherein the coating film has a thickness of not greater than 1000 microns, such as not greater than 900 microns, not greater than 800 microns, not greater than 700 microns, not greater than 500 microns, not greater than 300 microns, or not greater than 200 microns.
The building assembly of any of the preceding embodiments, wherein a ratio of an average size of the microporous particles to an average thickness of the coating film ranges from 0.1:1 to 1:1.
The building assembly of any of the preceding embodiments, wherein an amount of the microporous particles in the coating film is at least 1 vol %, such as at least 5 vol %, at least 10 vol %, or at least 15 vol % based on the total volume of the coating film.
The building assembly of any of the preceding embodiments, wherein an amount of the microporous particles in the coating film is not greater than 60 vol %, such as not greater than 55 vol %, not greater than 50 vol %, not greater than 40 vol %, not greater than 35 vol %, not greater than 30 wt %, or not greater than 25 wt %, based on the total volume of the coating film.
The building assembly of any of the preceding embodiments, wherein the microporous particles have an average pore diameter of at least 50 nm, such as at least 70 nm, or at least 100 nm.
The building assembly of any of the preceding embodiments, wherein the microporous particles have an average pore diameter of not greater than 100 microns, such as not greater than 80 microns, not greater than 60 microns, not greater than 30 microns, or not greater than 10 microns.
The building assembly of any of the preceding embodiments, wherein the microporous particles have an average pore volume of at least 0.05 cm3/g, such as at least 0.1 cm3/g, at least 0.3 cm3/g, or at least 0.5 cm3/g.
The building assembly of any of the preceding embodiments, wherein the microporous particles have an average pore volume of not greater than 2 cm3/g, such as not greater than 1.5 cm3/g, not greater than 1.0 cm3/g, or not greater than 0.8 cm3/g.
The building assembly of any of the preceding embodiments, wherein the microporous particles have an aspect ratio of length to width not greater than 5, such as not greater than 3, not greater than 2, or not greater than 1.5.
The building assembly of any of the preceding embodiments, wherein the microporous particles are spherical.
The building assembly of any of the preceding embodiments, wherein the thermoplastic polymer includes an ethylene vinyl acetate copolymer, a polyolefin, an ethylene methacrylate copolymer, an ethylene acrylic acid copolymer, a styrene block copolymer, a polyurethane, a polyamide, or any combination thereof.
The building assembly of any of the preceding embodiments, wherein an amount of the thermoplastic polymer is at least 10 wt %, such as at least 20 wt %, or at least 30 wt % based on the total weight of the coating film.
The building assembly of any of the preceding embodiments, wherein an amount of the at least one thermoplastic polymer is not greater than 70 wt %, such as not greater than 60 wt %, not greater than 50 wt %, or not greater than 45 wt % based on the total weight of the coating film.
The building assembly of any of the preceding embodiments, wherein the coating film further comprises a wax and a tackifying resin.
The building assembly of any of the preceding embodiments, wherein the coating film further comprises a cellulose ester.
The building assembly of embodiment 21, wherein the cellulose ester includes cellulose acetate, cellulose propionate, cellulose butyrate, cellulose acetate propionate, cellulose acetate butyrate, cellulose propionate butyrate, or any combination thereof.
The building assembly of embodiment 22, wherein the cellulose ester includes cellulose acetate propionate.
The building assembly of any of embodiments 20 to 23, wherein the wax of the coating film is present in an amount of at least 5 wt %, such as at least 7 wt %, or at least 10 wt % based on the total weight of the coating film.
The building assembly of any of embodiments 20 to 24, wherein the wax of the coating film is present in an amount of not greater than 40 wt %, such as not greater than 35 wt %, not greater than 30 wt %, or not greater than 25 wt % based on the total weight of the coating film.
The building assembly of any of embodiments 20 to 25, wherein the tackifying resin is present in an amount of at least 15 wt %, such as at least 20 wt %, or at least 25 wt % based on the total weight of the coating film.
The building assembly of any of embodiments 20 to 26, wherein the tackifying resin is present in an amount of not greater than 50 wt %, such as not greater than 45 wt %, or not greater than 40 wt % based on the total weight of the coating film.
The building assembly of any of the preceding embodiments, wherein the coating film further comprises a UV absorber, a light stabilizer, a filler, a dye, a dispersant or any combination thereof.
The building assembly of any of the preceding embodiments, wherein the coating film has a water vapor permeability of not greater than 100 US perms, such as not greater 50 US perms, or not greater than 20 US perms.
The building assembly of any of the preceding embodiments, wherein the coating has a water vapor permeability of at least 3 US perms, such as at least 5 US perms, at least 8 US perms, or at least 10 US perms.
The building assembly of any of the precedent embodiments, wherein the coating film comprises a non-curing hotmelt composition.
The building assembly of any of the preceding embodiments, wherein the coating film is a one-layer coating and the coating is in direct contact with at least one outer surface of the building substrate.
The building assembly of any of embodiments 1 to 31, wherein the coating film is a multi-layer coating.
The building assembly of any of the preceding embodiments, wherein the substrate is a board, a panel, or a siding.
The building assembly of embodiment 34, wherein the substrate is a board comprising gypsum.
The building assembly of any of embodiments 20 to 35, wherein the thermoplastic polymer is present in an amount of 20 wt % to 60 wt % based on the total weight of the coating film, the wax is present in an amount of 5 wt % to 40 wt % based on the total weight of the coating film; the tackifying resin is present in an amount of 15 wt % to 50 wt % based on the total weight of the coating film; and the microporous particles are present in an amount of 1 wt % to 30 wt % based on the total weight of the coating film.
The building assembly of embodiment 36, wherein the coating film further includes an UV absorbent in an amount of 0.1 wt % to 3 wt % based on the total weight of the coating film.
A method for making a building assembly, comprising: providing a substrate comprising a first surface and a second surface opposite to the first surface; preparing a water barrier coating film comprising a thermoplastic polymer and microporous particles; and applying the water barrier coating film on the first surface, the second surface, or the first surface and second surface of the substrate.
The method of embodiment 38, wherein preparing the water barrier coating film comprises in the following order: melting a coating composition, the coating composition comprising a thermoplastic polymer; applying a layer of the melted coating composition onto a removable liner; adding microporous particles on top of the layer of the melted coating composition, wherein a majority of the microporous particles is embedded into the melted coating composition; and allowing the melted coating composition to cool and to solidify to form a coating film, wherein the coating film has a water vapor permeability of at least 2 US perms, as tested according to ASTM E96 (2014) at 21° C. and 50% average relative humidity.
The method of embodiments 38 or 39, wherein applying the water barrier coating film to the substrate comprises softening the coating film by heating the coating film to a temperature between 70° C. to 110° C., and adhering the heated coating film on the first surface or the second surface of the substrate.
The method of any of embodiments 38 to 40, wherein the substrate is a board comprising gypsum.
The method of any of embodiments 38 to 41, wherein the microporous particles comprise microporous glass beads, microporous ceramic beads, microporous polymer beads, a naturally microporous material, or any combination thereof.
The method of embodiment 42, wherein the microporous particles are consisting essentially of microporous glass beads.
The method of any of embodiments 38 to 43, wherein the microporous particles have an average particle size of at least 25 microns and not greater than 1000 microns.
The method of any of embodiments 38 to 44, wherein a thickness of the layer of the melted coating composition is at least 50 microns and not greater than 1000 μm.
The method of embodiment 39, wherein a ratio Tp to Tm is equal to or greater than 1, with Tp being an average size of the microporous particles before added to the coating composition, and Tm being an average size of a thickness of the layer of the melted coating composition before adding of microporous particles.
The method of embodiment 46, wherein a ratio of Tp to Tm ranges from 1:1 to 3:1, such as from 1:1 to 2:1, from 1:1 to 1.8:1, or from 1:1 to 1.5:1.
The method of any of embodiments 38 to 47, wherein an amount of the microporous particles in the coating film is at least 1 vol %, such as at least 5 vol %, at least 10 vol %, at least 15 vol %, or at least 20 vol % based on the total volume of the coating film.
The method of any of embodiments 38 to 48, wherein an amount of the microporous particles in the coating film is not greater than 60 vol %, such as not greater than 55 vol %, not greater than 50 vol %, not greater than 40 vol %, or not greater than 30 vol % based on the total weight of the coating film.
The method of any of embodiments 38 to 49, wherein the microporous particles have an average pore diameter of at least 50 nm, such as at least 70 nm, or at least 100 nm.
The method of any of embodiments 38 to 50, wherein the microporous particles have an average pore diameter of not greater than 100 microns, such as not greater than 80 microns, not greater than 60 microns, not greater than 30 microns, or not greater than 10 microns.
The method of any of embodiments 38 to 51, wherein the microporous particles have an average pore volume of at least 0.05 cm3/g, such as at least 0.1 cm3/g, at least 0.3 cm3/g, or at least 0.5 cm3/g.
The method of any of embodiments 38 to 52, wherein the microporous particles have an average pore volume of not greater than 2 cm3/g, such as not greater than 1.5 cm3/g, not greater than 1.0 cm3/g, or not greater than 0.8 cm3/g.
The method of any of embodiments 38 to 53, wherein the microporous particles have an aspect ratio of length to width of not greater than 5, such as not greater than 3, not greater than 2, or not greater than 1.5.
The method of any of embodiments 38 to 53, wherein the microporous particles are spherical.
The method of any of embodiments 38 to 55, wherein the thermoplastic polymer includes an ethylene vinyl acetate copolymer, a polyolefin, an ethylene methacrylate copolymer, an ethylene acrylic acid copolymer, a styrene block copolymer, a polyurethane, a polyamide, or any combination thereof.
The method of any of embodiments 38 to 56, wherein an amount of the at least one thermoplastic polymer is at least 10 wt %, such as at least 20 wt %, at least 30 wt %, or at least 40 wt % based on the total weight of the coating film.
The method of any of embodiments 38 to 57, wherein an amount of the at least one thermoplastic polymer is not greater than 95 wt %, such as not greater than 90 wt %, or not greater than 80 wt % based on the total weight of the coating film.
The method of any of embodiments 38 to 58, wherein the coating film further comprises a wax and a tackifying resin.
The method of any of embodiments 38 to 59, wherein the coating film further comprises a cellulose ester.
The method of embodiment 60, wherein the cellulose ester includes cellulose acetate, cellulose propionate, cellulose butyrate, cellulose acetate propionate, cellulose acetate butyrate, cellulose propionate butyrate, or any combination thereof.
The method of embodiment 61, wherein the cellulose ester includes cellulose acetate propionate.
The method of any of embodiments 38 to 62, wherein the coating film has a water vapor permeability of not greater than 100 US perms, such as not greater 50 US perms, or not greater than 20 US perms.
The method of any of embodiments 38 to 63, wherein the coating film has a water vapor permeability of at least 3 US perms, such as at least 5 US perms, at least 8 US perms, or as at least 10 US perms.
The method of any of embodiments 38 to 64, wherein the coating composition is a non-curing hotmelt coating.
A water barrier coating film, comprising a thermoplastic polymer and microporous particles, the water barrier coating film having a water vapor permeability of at least 2 perms.
A water barrier coating film, comprising a thermoplastic polymer and microporous particles, wherein the microporous particles provide an interconnected porous structure throughout a thickness of the water barrier coating film, and the water barrier coating film has a water vapor permeability of at least 2 US perms as tested according to ASTM E96 (2014) at 21° C. and 50% average relative humidity.
The following non-limiting examples illustrate the concepts as described herein.
An EVA based hotmelt (PA4441 from Applied Adhesives, Pewaukee, Wis.) was applied onto a PTFE liner with a thickness of approximately 127 microns (5 mils) and approximately 254 microns (10 mils). Immediately thereafter, while the hotmelt coatings were still fluid or semi-fluid, 0.5 g microporous glass beads (PORAVER™), which have been heated in an oven at 300° C., were sprinkled on top of the hotmelt coatings over a section of 10.16 cm (4 inches) by 10.16 cm (4 inches). Thereafter, the coatings with the sprinkled glass beads were covered by a further PTFE liner and medium pressure was applied by hand with a large metal bar (7 pounds weight) to press the glass beads into the hotmelt coatings. The experiments were conducted using two different fraction sizes of PORAVER™ glass beads: 40 microns to 125 microns and 250 microns to 500 microns:
After the hotmelt of the coatings was cooled and solidified, the PTFE liners were removed from the coatings to obtain independent coating films. The coating films were inspected for pinholes or defects and tested for water vapor permeability according to ASTM E96 at 21° C. and 50% relative humidity (RH).
Table 1 summarizes the results of the conducted experiments.
Hotmelt coatings without microporous particles did not allow water vapor flow. Also, hotmelt coatings including microporous particles which were smaller then the thickness of the hotmelt coating layer (before adding the particles) did not result in coating films that can allow water vapor flow. Coating films that provided water vapor flow could be obtained if the microporous glass beads had a nearly equal or larger average particle size then the thickness of the layer of the melted coating composition (before adding the particles).
Water barrier coating films were prepared and tested the same way as in Example 1, except that the microporous glass beads were mixed into the fluid hotmelt before applying the hot-melt coatings onto the liner. In addition to the size of the glass beads, also the amount of glass beads was varied, as summarized in Table 2.
Independent of the type and the amount of porous glass beads, no bridging effect could be achieved to obtain a water vapor flow through the coating films. An explanation can be that the hotmelt clogged the pores of the beads during mixing the beads with the hotmelt.
A lamination process was developed to adhere the hotmelt coating films containing the PORAVER™ beads produced in Example 1 to the surface of a gypsum board without directly coating the board.
As illustrated in
In the foregoing specification, the concepts have been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the invention as set forth in the claims below. Accordingly, the specification and figures are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of the invention.
This application claims priority under 35 U.S.C. §119(e) to U.S. Provisional Patent Application No. 62/329,610, entitled “BUILDING SUBSTRATE WITH INTEGRATED WATER BARRIER COATING,” by Jeffrey H. PEET et al., filed Apr. 29, 2017, which is assigned to the current assignee hereof and incorporated herein by reference in its entirety.