Patent Application
20080127600
This invention relates to building systems which largely replace concrete, whether ready-mix concrete or pre-fabricated concrete blocks, or other pre-fabricated concrete products, in construction projects. In general, the invention replaces the concrete in below-grade frost walls and foundation walls, in above-grade walls, in concrete footers, and in post pads. Such concrete structures are replaced, in the invention, with structures based on resin-impregnated, fiber-based layers, as composite materials, also known as fiber-reinforced polymer materials (FRP). Such structures optionally include insulating foam, and optionally include regularly-spaced “studs”, especially in upright wall sections. Thus, with the exception of concrete flat work such as concrete floors, the conventional ready-mix concrete truck is not needed at the construction site.
In conventional foundation construction, first a concrete footer is formed and poured using ready-mix concrete. After the poured concrete footer has cured to a sufficient degree, such as a few days later, concrete forms, e.g. 4-8 feet high, are brought in, assembled on site, and erected on top of the footer. Ready-mix concrete is then poured, from a ready-mix truck, into the forms and allowed to set up and cure, to thus create the foundation walls, or a frost wall if no basement is planned.
In the alternative, and still addressing conventional foundation construction, the upright portion of the foundation wall can be built using pre-fabricated concrete masonry units (cmu's) and mortar, typically supported by conventional poured concrete footers.
In yet another conventional type construction, the frost walls or foundation walls are built using mortared concrete blocks.
In any event, in such conventional structures, as the concrete is being finished at the tops of the forms, or at the top course of concrete blocks, bolts or other hold-down anchors are partially embedded in the setting-up concrete or mortar such that the anchors extend from the top of the foundation wall and, once the poured concrete, or mortar, has set up, such anchors serve as hold-down anchors, for example to mount a top plate to the top of the foundation wall, thus to anchor the overlying building structure to the foundation or frost wall. Once the concrete in a conventionally-poured foundation wall sets up, the forms are removed, e.g. 1-2 days after the ready-mix concrete is poured into the forms, and a wood, or wood-product, or other top plate is anchored to the top of the concrete foundation wall, using the anchors which are embedded in the concrete at the top of the concrete foundation wall. A similar waiting time is needed with a mortared concrete block wall, before the top plate is anchored to the top of the so fabricated wall.
The above-noted poured concrete wall construction process, and concrete block construction process, both require a substantial quantity of concrete materials, investment in forms, substantial on-site labor and several days of time to fabricate the building foundation on which the ground floor of the building can then be erected. If construction is done in winter in a northern climate, the concrete is typically heated in order to facilitate curing of the concrete.
In addition, a resulting such concrete foundation wall is permeable to water and so must be water-proofed though, even after a conventional water-proofing coating has been applied to make the foundation wall water-proof, water leakage through such concrete foundation wall, whether ready-mix wall or concrete block wall, is rather common. Further, a concrete wall is a good heat conductor, and thus should be insulated to avoid heat loss by conduction through the concrete to the soil or other fill which surrounds the building. However, the affect of such insulation is limited because only relatively thin insulation materials are commonly used with underground concrete wall construction.
Yet further, if the level of the building inside the concrete wall is to be inhabited, whether below grade, e.g. foundation wall, or above grade, then stud furring e.g. 2×4 studs or 2×6 studs are typically attached to the concrete wall as a substrate which facilitates installation of insulation and utilities, and serves as a substrate for installing a finished interior wall surface such as sheet rock or paneling. Such furring takes up interior space inside the building as well as costing additional time and money to install.
The overall time required to construct such building foundation can be reduced by fabricating concrete walls off-site and erecting the fabricated walls in place on site, using a crane. However, each such wall element must be custom-designed, adding to the cost; and mechanical lifting equipment, e.g. the crane, must be brought to the construction site.
Getting foundation walls installed in a timely manner, to accommodate timely delivery of constructed homes and other buildings to buyers, is a significant issue in the construction business. There are many reasons why foundations are not installed in accord with a planned schedule. A substantial such problem is the weather. The weather in northern climates can be below freezing for several months of the year, which makes it difficult to get foundations installed. In addition, installing quality concrete foundation walls requires skilled labor, as well as skilled subcontractors, including the subcontractors' skilled labor.
Another known method of constructing structural walls is the use of Insulated Concrete Form (ICF) walls. In such construction, insulated forms are erected on the footers, and receive ready-mix poured concrete. After curing, the outer portions of the forms are left as a layer of thermal insulation between the concrete and at least one of the inner and outer surfaces of the resulting wall. Although ICF walls do offer a relatively higher level of thermal insulation than a conventional uninsulated concrete wall, an ICF wall is typically more expensive than a plain concrete wall, and is more difficult to finish than a plain concrete wall, whether finishing the insulated interior of the wall or the insulated exterior of the wall.
Yet another alternative conventional foundation wall system is constructed of wood which has been treated to inhibit decay, and corresponding decomposition of the wood. Such treated wood is well known and is conventionally available. Such foundation walls typically include at least a bottom plate, and can be wrapped in plastic and then set on an aggregate stone footer. Wood foundations have a number of advantages, including enabling a manufacturer of such wood foundations to fabricate sections of such wall in the closed and controlled environment of a manufacturing facility, whereby selling and delivering such product is generally insensitive to weather conditions. Further, wood offers beneficial speed in constructing a building.
The primary problem with wood foundations is that wood foundations are not well received by the consuming public, as the public does not perceive quality in a building where wood is used in a below-grade application.
There is a need, in the construction industry, for light weight structural building panels, for example generally continuous wall panels of any desired length up to a maximum length per panel, selectable in length, in height, and in thickness, which structural building panels can be used in applications where concrete is conventionally used in residential, light commercial, and light industrial construction, and which structural building panels are strong enough to bear both the compressive loads and the lateral loads which are typically imposed on such concrete walls in a building structure.
There is also a need for walls which have superior moisture and water barrier properties.
There is yet further a need for walls which can be installed so as to be ready to support overlying building structure in a shorter period of time.
There is still further a need for walls which can be installed at a lower life cycle cost.
These and other needs are alleviated, or at least attenuated, by the novel construction products and methods of the invention.
This invention is a tough, water-proof building system which provides structural building panels which support the building structure. The walls have both vertical compression-resistance strength, and horizontal bending-resistance strength, sufficient that the wall system can be used in both above-ground and below-ground building wall structural applications, including applications where such wall systems are exposed to severe wind and other weather, such as hurricanes, tornadoes, and the like. Such walls can replace concrete, and can be adequate to meet corresponding required strength specifications for typical single-family residential, light commercial, and light industrial applications.
A wall structure of the invention has an outer waterproof layer, comprised of reinforcing fibers embedded in polymeric resin, and defining the outwardly-facing surface of the panel. At least one fiber-reinforced polymeric structurally-reinforcing member extends, typically as a layer, the full height of the erected wall panel, and extends from at or proximate the inner surface of the outer layer to a location at or proximate an inner surface of the wall structure, at spaced locations along the length of the wall panel.
The inwardly-facing surface of the wall structure, considered in an orientation where a wall panel is installed as an upright wall in a building, can be formed by a separate structurally-reinforcing inner layer of fiber-reinforced polymeric (FRP) material, whereby the reinforcing layer is entirely enclosed between the inner layer and the outer layer.
Any or all of the inner layer, the outer layer, and the reinforcing layer can be thought of as fiber-reinforced resin layers or as resin-impregnated fiber layers. Either approach in materials description recognizes the structural contribution of both the fiber and the resin to the desired physical properties of the panels, and the benefit of having both materials in the panel structure.
Optionally, a reinforcing stud is attached to, or overlaid by, the inner layer, and extends inwardly into the building from what is otherwise the inner surface of the building panel/wall panel. Alternatively, the stud can originate at the outer layer, and extend into the building beyond what is otherwise the inner surface of the building panel.
The spaces between the inner-to-outer runs of the structurally reinforcing member, and between the inner and outer layers, are optionally filled with rigid insulating foam material such as polyurethane foam or polystyrene foam, or polyisocyanurate foam.
Any of a wide variety of rigidifying, stiffening materials can be used as the structurally-reinforcing member to provide stiffness, rigidity to the structural building panel. Each such material has its own structural characteristics which direct desired cross-section shapes of the respective materials. Relatively more advantageous materials have insulating “R” values of greater than 0.5, optionally greater than 10.
The structurally-reinforcing members are attached to, or form portions of, both the outer layer and the inner layer of the structural building panel, whether by cured resin bonding or by adhesive bonding, or by extrusion/pultrusion with the inner and outer layers, whereby the reinforcing elements of the structurally-reinforcing members, which extend between the inner and outer layers of the panel, function in a capacity similar to the web of an I-beam, and inner and outer regions of the structurally reinforcing members function in capacities similar to the functioning of flanges of such I-beam. The overall I-beam effect provides, in an upstanding wall panel, or wall, both horizontal bending strength and vertical compressive strength, sufficient to support both the vertical compressive loads, and the lateral side loads, for which building walls are designed, and provides such sufficient levels of strength in cross-sections which are no greater than the cross-sections of concrete walls which are conventionally used in such applications, while avoiding the drawbacks of concrete.
Walls and wall structures of the invention can be used in below-grade applications such as in foundation walls and frost walls, as well as in above-grade applications such as building sidewalls.
In a first family of embodiments, the invention comprehends a building, comprising a load-bearing foundation, the load-bearing foundation having a bottom thereof below grade, and a top, and comprising (i) a load-bearing footer, and (ii) a load-bearing foundation wall, overlying the footer, and interfacing with the footer, optionally through a deformed bridging material, and applying a downwardly-directed force on, the footer, the foundation wall having a top, a bottom, and a length, and an above-grade structure supported by the load-bearing foundation, the footer comprising a settled fabricated base selected from the group consisting of pre-fabricated concrete blocks, cured ready-mix concrete, aggregate stone, and a fiber-reinforced polymer pad, the load-bearing foundation wall comprising a plurality of upright foundation wall panels connected to each other in side-by-side relationship, a given foundation wall panel extending upwardly from loci at or adjacent the footer, and having a height defined between a top and a bottom, a length, and a thickness, and comprising (iii) an outer fiber-reinforced polymeric layer, the outer layer defining an outwardly-facing surface of the foundation wall panel, (iv) an inner fiber-reinforced polymeric layer, the inner layer defining an inwardly-facing surface of the foundation wall panel, and (v) a plurality of structurally-reinforcing members extending between the top and the bottom of the given foundation wall panel, and extending from locations at or proximate the outer layer to locations at or proximate the inner layer.
In some embodiments, the building further comprises rigid insulating foam elements in one or more of the foundation wall panels, and extending between, and being in surface-to-surface contact with, the inner layer and the outer layer.
In some embodiments, the inner layer and the outer layer comprise resin-impregnated fiberglass layers.
In some embodiments, the inner layer forms a unitary structural element in combination with portions of the structurally reinforcing members.
In some embodiments, at least one of the inner layer and the outer layer has a nominal thickness of between about 0.03 inch thick and about 0.15 inch thick.
In some embodiments, the structurally-reinforcing members comprise a weaving layer comprising resin-impregnated fiberglass, the weaving layer defining crossing portions thereof which cross the foundation wall, between the inner layer and the outer layer at crossing locations which are spaced from each other along the length of the foundation wall.
In some embodiments, the building further comprises a bottom plate attached to the foundation wall adjacent the bottoms of the foundation wall panels, the bottom plate extending along the length of the foundation wall, and extending along the thickness of the foundation wall, and further extending inwardly into the building beyond the inner layer, the bottom plate comprising a composition selected from the group consisting of a natural treated wood bottom plate, a manufactured wood bottom plate, a composite fiber-reinforced polymeric bottom plate, and a pultruded bottom plate.
In some embodiments, the building further comprises a support bracket mounted to the foundation wall in association with a top of the foundation wall, the support bracket comprising a floor support panel adapted to support an edge of a floor which edge overlies the floor support panel, and a brick support panel adapted to support bricks as an outwardly-disposed layer on a building which uses the support bracket.
In some embodiments, the rigid insulating foam elements comprise closed cell foam having densities of about 1 pound per cubic foot to about 12 pounds per cubic foot.
In some embodiments, first and second foundation wall panels collectively define adjoining portions of the foundation wall, and the first and second foundation wall panels are connected to each other at a joint where the first and second foundation wall panels meet in edge-to-edge relationship, by a connecting bracket, the connecting bracket comprising a first bridging flange on the first side of the foundation wall, which interfaces with one of the inner layers and the outer layers on both of the first and second foundation wall panels, and extends across the joint, the connecting bracket further comprising a connector web, connected with the first bridging flange and extending along the thicknesses of the foundation wall panels, in the joint, from the first side toward the second side.
In some embodiments, the footer comprises a concrete footer, further comprising deformed bridging material between the foundation wall and the footer.
In some embodiments, the building further comprises a concrete slab floor overlying a portion of the bottom plate and abutting the inner layer of at least one the foundation wall panels.
In some embodiments, the foundation wall further comprises structural reinforcing studs extending between tops and bottoms of the foundation wall panels, the reinforcing studs being combined into the foundation wall panels so as to receive and absorb stresses imposed on the wall panels, a such structural reinforcing stud extending inwardly from the inwardly-facing surface and away from the outer layer, to an end panel of the respective stud, the end panel being displaced from the inner layer by about 1 inch to about 6 inches.
In some embodiments, the foundation wall further comprises reinforcing studs extending between the top and the bottom of the foundation, the reinforcing studs being associated with the inner layer so as to receive and absorb bending stresses from the foundation wall panels, and interior sheet material installed over the studs and spanning between the studs so as to define a cavity between the interior sheet material and the inwardly-facing surface of the foundation wall.
In some embodiments, the building further comprises at least one of wiring, piping, air ducting, and thermal insulation material in the cavity between the interior sheet material and the inwardly-facing surface of the foundation wall.
In some embodiments, the building further comprises a support beam extending across an open span between first and second portions of the foundation, the support beam being disposed at an elevation proximate the top of the foundation, and being supported by at least first and second ones of the plurality of foundation wall panels, the support beam being constructed of a material selected from the group consisting of natural wood, manufactured wood products, metal I-beams, and fiber-reinforced plastic composite beams.
In some embodiments, the foundation wall further comprises at least one of a wood top plate and a fiber-reinforced polymeric bottom plate, optionally a pultruded bottom plate and wherein such bottom plate is at least about 0.18 inch thick.
In some embodiments, the foundation wall has a vertical crush resistance of at least 6000 pounds per lineal foot, and optionally has a horizontal point loading bending moment resistance of at least about 1500 pounds per square foot.
In a second family of embodiments, the invention comprehends a building, comprising one or more below-grade load-bearing foundation walls, each having a height defined by a top and a bottom, a length, and a thickness. A respective one of the one or more load-bearing foundation walls comprises an outer fiber-reinforced polymeric layer, the outer layer defining an outwardly-facing surface of the foundation wall; an inner fiber-reinforced polymeric layer, the inner layer defining an inwardly-facing surface of the foundation wall; a plurality of structurally-reinforcing members extending along substantially an entirety of the height of a foundation wall panel, and extending between locations proximate the outer layer and locations at or proximate the inner layer, the one or more load-bearing foundation walls further comprising at least one of (i) a top plate, or (ii) a bottom plate, or (iii) a plurality of studs extending inwardly from the inwardly-facing surface, or (iv) rigid insulating foam elements extending between, and being in surface-to-surface contact with, respective ones of the structurally-reinforcing members, the inner layer, and the outer layer, or (v) the one or more structurally-reinforcing members comprising fiber-reinforced polymeric members, or (vi) the building panel, in an upright use orientation, having a top-to-bottom crush resistance capacity of at least about 4000 pounds per lineal foot.
In some embodiments, the building further comprises one or more reinforcing studs in the foundation wall, such studs extending away from the inner layer and the outer layer in a common direction, the one or more reinforcing studs making a substantial contribution to at least one of vertically-directed compressive strength and lateral bending resistance to horizontally directed stresses on a respective one of the one or more foundation walls.
In some embodiments, a such foundation wall further comprises reinforcing studs extending substantially the height of the foundation wall, the reinforcing studs being combined into the foundation wall so as to make a substantial contribution to at least one of vertically-oriented compressive strength and lateral bending resistance to horizontally-directed stresses, a such reinforcing stud having one or more legs extending away from the inner layer and away from the outer layer, to an end panel of the respective stud, the end panel being displaced from the inwardly-facing surface by about 1 inch to about 6 inches, and interior sheet material installed over the studs and spanning between the studs so as to define a utility and/or insulation cavity between the interior sheet material and the inwardly-facing surface of the foundation wall.
In some embodiments, a such foundation wall further comprises at least one of a wood top plate and a fiber-reinforced polymeric bottom plate, optionally a pultruded bottom plate and wherein such bottom plate is at least about 0.18 inch thick.
In a third family of embodiments, the invention comprehends a building fabricated without structural use of concrete other than as floor slabs. The building comprises a load-bearing foundation, the load-bearing foundation having a bottom thereof below grade, and a top, and comprising (i) a load-bearing footer devoid of structural use of concrete, (ii) a load-bearing wall, overlying the footer and applying downwardly-directed force on the footer, the load-bearing wall having a top, a bottom, and a length, and being devoid of structural use of concrete, the load-bearing wall comprising a plurality of load-bearing upright building panels connected to each other, in side-by-side relationship, a given such building panel extending upwardly from loci at or adjacent the footer and having a height defined between the top and the bottom, and a length, and a thickness, and comprising (iii) an outer fiber-reinforced polymeric layer, the outer layer defining an outwardly-facing surface of the building panel, (iv) an inner fiber-reinforced polymeric layer, the inner layer defining an inwardly-facing surface of the building panel, and (v) a plurality of structurally reinforcing members extending from locations at or proximate the outer layer to locations at or proximate the inner layer.
The invention is not limited in its application to the details of construction, or to the arrangement of the components set forth in the following description or illustrated in the drawings.
The invention is capable of other embodiments or of being practiced or carried out in various other ways. Also, it is to be understood that the terminology and phraseology employed herein is for purpose of description and illustration and should not be regarded as limiting. Like reference numerals are used to indicate like components.
Referring to
As illustrated in
Referring now to
The foam core layer is of sufficient density, rigidity, and polymer selection to fix the positions of the fiber-reinforced polymer layers in their respective positions as illustrated. Thus, in the embodiments illustrated in
Bottom plate 16 can be a fiber-reinforced, e.g. fiberglass-reinforced, polymeric structural member, of such dimensions as to be sufficiently rigid, and with sufficient strength, to support both the foundation wall and the overlying building superstructure, from an underlying fabricated base defined by e.g. a settled bed 53 (
A pultruded fiber-reinforced product e.g. 0.075 inch (1.9 mm) to about 0.5 inch (13 mm) thick has been found to be satisfactory as the bottom plate for general-purpose and typical single-family residential, light commercial, and light industrial construction.
The bottom plate can be attached to the upstanding wall section, and optional support brackets 24, by adhesive, by curable resin such as that used in the wall panel, by steel bolts which extend through an upright leg of the bottom plate e.g. adjacent the outer surface of the upstanding wall section and through the adjacent portion of the upstanding wall section, or by a combination of metal anchors and adhesive and/or resin or by other attachment mechanism. In any event, the bottom plate, when attached to the upstanding wall section, is sufficiently wide, thick, dense, and rigid, to provide effective compression and bending support, thus to support the foundation wall from the underlying soil and/or rock and/or stone, or other natural base albeit typically through a fabricated footing.
The bottom plate typically extends laterally inwardly into the building beyond the primary surface of the inner layer by a distance corresponding to at least the maximum thickness of the building panel which includes stud 23, thus to present a suitably-sized bearing surface to the underlying support base whereby the overlying load can be borne by the underlying support base without causing substantial movement in the underlying support base of soil, stone, or rock. In the alternative, the bottom plate can extend outwardly from the building panel, away from the building, to provide the recited suitably-sized bearing surface, or can extend both inwardly and outwardly from the building panel.
The top plate can be made of wrapped layers of fiberglass, can be a pultruded resin-fiber composite, can be conventional wood, or a manufactured wood product, or other conventional construction material, each such structure being sufficiently wide and thick to provide a support surface, interfacing with the underlying upstanding wall section, and from which the overlying superstructure of the building can be supported. The top plate can conveniently be made from conventional wood building materials whereby overlying building structures can be conventionally attached to the underlying foundation wall structure at the building site by use of conventional fasteners, conventionally attached to the top plate.
The combination of the inner and outer fiberglass layers 34, 36, and the reinforcing studs 23, for example wood 2×4's, 2×6's, as illustrated in
A suitable illustrative footer can be fabricated from aggregate stone, illustrated as 53 in
Referring to
Inwardly-directed lateral forces which are imposed on the foundation wall at or adjacent top plate 20 are transferred to main floor 40 of the building (
Still referring to the main run wall section 22 (
In the embodiments illustrated in
Compared to e.g. a 2.0 inch thick wall section, 8 feet in height, having no reinforcing member, a corresponding wall which incorporates 2×4 studs on 24 inch centers, wrapped on 3 sides by the inner layer as illustrated, exhibits about 25% increased bending resistance. Such bending resistance is measured by applying a linear load which runs the length of the wall panel at mid-height of the wall panel, and which load is opposed by linear opposing blocking of corresponding lengths at the top and bottom of the wall panel.
Referring to
Flange 47 of the “T” section can be positioned against either outer layer 36 as shown, or against inner layer 34. In either case, web 49 extends inwardly across the thickness of the wall panel from the inner surface of the respective inner or outer layer. The surface of flange 47, which faces the inner surface of the respective inner or outer layer, is bonded, e.g. adhesively bonded, to the respective inner surface of the inner or outer layer. As adhesive, there can be mentioned respective known construction adhesives. In some instances, the curable resin which is used in making the respective inner or outer layer is also effective to secure the “T” section flange 47 to the respective inner or outer layer. Where the “T” section is placed against outer layer 36, the “T” section can receive fasteners which attach additional layers, such as siding, to the building outwardly of the outer surface of the wall panel.
In place of “T” section reinforcements, a wide variety of other elongate structural constructs 46 can be embedded in the interior of the wall panel. As other cross-section constructs, there can be mentioned, for example and without limitation, cross-section profiles which represent elongate perpendicular-angle 2-leg constructs e.g. eliminating half of the flange 47 shown in
Typically, the number of such structural constructs 46 is no greater than the number of reinforcing studs 23, or the like which run the full thickness of the main run wall section.
As desired, the “T” section or other structural constructs 46 can be omitted, whereby the resistance to e.g. gravitational compressive forces and lateral forces, on the wall panel are derived largely from inner and outer layers 34, 36, and reinforcing members/studs 23 and wherein attachment fasteners are directed to stud 23.
Studs 23 can be conventional wood studs as illustrated in
Still referring to
Wall section thickness “T” (
The top plate and bottom plate can be conventional e.g. wood materials, with suitable waterproofing as appropriate for the intended use. In order to avoid issues of moisture contact with wood, typically the bottom plate is a fiberglass-reinforced resinous composite, of sufficient thickness and rigidity to provide the level of weight bearing capacity anticipated as being necessary, for supporting the structure to be supported.
As used herein, all fiberglass/resin composite structures, such as bottom plate 16, top plate 20, studs 23, and the like, can be fabricated using known techniques of dry or pre-impregnated fiberglass blanket manipulation and construction, and resin impregnation of such materials, chop spray processes, vacuum infusion processes, pultrusion, or other known processes for making fiber-reinforced composites, in order to make the desired 3-dimensional shapes. Such techniques can be used, for example, to make bottom plate 16, to make studs 23, the wedge-shaped stud extensions illustrated in dashed outline
Structural building panels of the invention can be manufactured in any of the standard dimensional sizes, as well as in a variety of other size combinations desired for a particular building project. Thus, for example and without limitation, such panels can have heights of about 4 feet, which accommodates use of the panels in 4-foot frost walls. Height of about 9 feet accommodates use of the panels in standard-height basement walls and standard-height above-grade walls.
Thickness of the panels typically ranges from about 3 inches nominal thickness to about 8 inches nominal thickness. Studs described elsewhere herein can extend inwardly from such nominal dimensions. At least 3 inches is typically desired in order to obtain necessary bending resistance, as well as desired thermal insulation properties. However, additional bending resistance can be obtained through the use of studs which extend inwardly from the nominal thickness. Further, additional thermal insulation properties can be obtained by adding conventional insulation material between studs at the inner surface of the panel.
Typically, thickness greater than 8 inches is not needed in order to satisfy structural demands of thermal insulation demands. However, in some instances, where extraordinary thermal or structural demands are to be imposed on the building panels, then thickness greater than 8 inches is contemplated.
Lengths of the panels is limited only by transportation limitations. For example, such panels can be as long as the length of the truck bed which will transport the panels to the construction site. Thus, length is generally limited to about 40 feet, but can be longer as desired where suitable transport is available. However, since an advantage of the panels is limited weight such that the panels can be installed below grade and at grade level without use of a crane, length is in some embodiments limited to lengths which can readily be handled by manual lifting. Thus, lengths are typically no more than about 40 feet based on weight which can be accepted for manual lifting of the panels.
On the other hand, where a crane is to be used, and where suitable transportation is available, the panels can be as long as desired for the purpose intended.
Structural building panels of the invention provide a number of advantages. For example, the structural building panels can be manufactured in a continuous length, and but for shipping, to any desired length, which may be a generic length, for example 10 feet, or 20 feet, or 40 feet, or whatever length or lengths is or are desired. The length needed for a particular portion of a building wall can be cut from a generic-length building panel, at the construction site, to meet specific needs, or can be cut to specific length at the panel manufacturing site. Thus if a shorter length is needed for a particular portion of the wall run, the needed length can be cut e.g. from a 20-foot section or from a continuous section. If a longer length piece is needed, either a longer length panel can be fabricated as a unitary product at the panel-manufacturing site, or 2 pieces can be joined together using suitable straight-run connectors, or corner connectors, as suitable for the particular assembly to be made. The respective building panels can be cut to length, using e.g. a circular saw, a ring saw, or a reciprocating saw, employing e.g. a masonry blade, and assembled on site.
Because the wall assembly is made primarily from fiberglass, resin, and foam, the pounds per cubic foot density, and thus the unit weight per foot of length is relatively small compared to a concrete wall of corresponding dimensions. For example, a building panel 20 feet in length, 8 feet in height, and nominally 3 inches thick, weighs about 230 pounds, including studs 23, and anchor brackets discussed elsewhere herein.
Similarly, a wall 9 feet high weighs about 10 pounds to about 15 pounds per lineal foot. Accordingly, no crane is needed on site for wall erection at or near ground level, or below ground level such as for a foundation wall. Rather, such wall panels can readily be moved by manual labor only. Indeed, 2-4 workers can lift by hand, and emplace, a typical wall section which is 20 feet long, 8 feet high, and 3-5 inches thickness “T”. Rough openings for windows 27 and/or doors 29, illustrated in
As best seen in
Thus, referring to
The respective layers 34, 36, 50, and foam blocks 32, are all integrally bonded to each other to make a unitary composite structural product. Thus, the weaving layer is attached to respective elements of both the inner and outer layers, whereby the thicknesses of the inner and outer layers, as combined with the weaving layer, vary between relatively substantially thicker portions and relatively substantially thinner portions. Typically, the relatively thicker portions of the combined layers 34, 50 and 36, 50 are at least 50 percent thicker than the relatively thinner portions of the layers 34 and 36. The resultant composite product functions much like an I-beam where layers 34 and 36, and combined elements of layer 50, serve as flange elements of the I-beam-like structure, and the crossing portions of weaving layer 50, function as web elements of such I-beam-like structures.
The foam blocks provide a thermally insulating function. In addition, foam blocks 32, along with the bonding of the respective elements to each other, and the absence of substantial voids in the wall structure, serve to fix each layer 34, 36, and 50 in position along its intended path of traverse, relative to remaining elements of the structural building panel, thereby unifying layers 34, 36, 50 and blocks 32 into a single structural product where the respective elements cooperatively respond together, in support of each other, sharing, with each other, respective portions of the load when outside forces are imposed on the structural building panel.
In general, all the space between the inner surface 57 of the panel and the outer surface 56 of the panel is occupied by one of layers 34, 36, and 50, or by the foam blocks, whereby little, if any, of the space between layers 34 and 36 is not occupied by one of the above-recited panel materials. Typically, substantially all of the inner space is occupied. By so generally filling the space between layers 34, 36, all of the panel members are fixed in their positions relative to each other, and the panel is dimensionally quite stable under designed loading, whereby especially laterally-directed loads imposed on the panel, from outside the building, whether subterranean ground loads or above-grade e.g. wind loads, are efficiently transferred from outer layer 36 to the other members of the panel, and respective portions of layers 34, 36, and 50, and multiple ones of the foam blocks, share in the support of any one load. The resulting panel is stiff, rigid, and sufficiently strong to support all loads, including severe weather loads, to which the building is expected to be typically subjected under normal use environments, including normal seasonal environmental extremes in the given geographical location.
Flanges 126, legs 128, and end panel 130 generally form a unitary structure. The structure of channel stud 123 can be relatively thin, for example end panel 130 and legs 128 can be about 0.75 mm to about 3.8 mm thick. Typically, the end panel is displaced from the flanges by about 1 inch to about 5.5 inches, optionally about 2 inches to about 3.5 inches. Even in the recited such thin cross-section, in light of the distance between the end panel and the flanges, stud 123 makes a meaningful contribution to the ability of the panel to resist lateral, e.g. bending, forces imposed by ground forces, or wind forces, from outside the building.
Additional contributions to lateral-resistance strength can be developed by making studs according to a more robust structural specification or by placing a rigidifying insert inside the cavities in the studs. For example, studs 123 can be fiber-reinforced pultruded rectangular cross-section studs about e.g. 0.07 inch (1.8 mm) to about 0.5 inch (13 mm) wall thickness.
Studs 123 serve multiple functions. As a first function, studs 123 serve as mounting locations, for mounting surface materials such as sheet rock, paneling, or other interior sheet material 129, as illustrated in
Base panel 134 of bracket 24 is positioned against inner layer 34 of the wall panel 14 and is mounted to inner layer 34 and optionally is mounted to stud 123 at side panel 138. Panels 134 and 138 can be mounted to inner layer 34 and stud 123 adhesively, or can be pressed into inner layer 34 and/or stud 123 before the inner layer resin, or the stud resin, is cured, whereby the curing of the resin in the inner layer or stud serves to bond panel 134 to inner layer 34 and/or stud 123. Top panel 136 interfaces with and supports top plate 20, and typically is bolted to the top plate as illustrated in
As suggested in
The interfacing surfaces 152 of corner brackets 148, 150 and wall panels 14A and 14C, at panels 152 of the brackets, are bonded to each other. Such bonding can be achieved with known adhesives. Brackets 148, 150 can be held in place with e.g. self-tapping mechanical fasteners while bonding is being achieved. In the alternative, the surfaces of the angle brackets and/or the panels can be coated with uncured portions of curable resin, which is subsequently cured after the panels are joined with the angle brackets at the construction site. Such curing can be done with e.g. heat guns or the like if and as heat is a necessary element of such curing.
Still referring to
Support bracket 48 can be installed facing inwardly at the top of an e.g. garage wall, thereby providing vertical edge support to a subsequently-poured concrete garage floor. Similarly, bracket 48 can be installed facing outwardly at the top of an e.g. garage or other wall, thereby providing vertical edge support to subsequently-installed brick or stone. First and second complementary brackets 48 can be mounted, one on top of the other, with brick support panel 176 of the first bracket 48 facing away from the building and the brick support panel 176 of the second bracket facing into the building. Such use of 2 brackets provides for wall support of both an adjoining edge of the garage floor and brick or stone exterior fascia, both of which are adjacent the foundation wall.
A line representation of support bracket 48 is illustrated in
As with support bracket 48, the two-sided support bracket 188 is installed at the top of the wall panel such that upper panel 182 bears upon the top surface of the wall panel. Base panel 178A extends downwardly from upper panel 182. Support panel 176A extends outwardly from base panel 178A, and is supported by bracing panel 180A. A second base panel 178B extends downwardly from upper panel 182, typically but not necessarily, a similar distance as base panel 178A so as to terminate at a lower edge having generally the same installed elevation as base panel 178A. Support panel 176B extends outwardly from base panel 178B, and is supported by bracing panel 180B.
A single support bracket 188 can thus be used in place of the above-recited first and second support brackets 48 where a concrete grade-level garage floor abuts the top of the foundation wall and a brick or stone fascia is mounted to the other side of the foundation wall.
Similar to the operation of bracket 48, support panels 176A, 176B transfer the weight of the overlying e.g. loads of the brick or stone fascia, and the edge of the garage floor, to the wall, thence through the footer, and to the underlying natural base of e.g. soil or rock which supports the building. As illustrated in
Similarly, brackets 48 can be configured to support the bottoms of the floor joists at any desired elevation below the top of the wall such that the top of the floor is at any corresponding elevation, relative to the top of the foundation wall, up to a maximum height which is about the same as the elevation shown in
While brackets 48 and 188 have been described herein as being used with building panels of the invention, brackets 48 and 188, when properly sized and configured, can be used with conventional e.g. concrete walls such as frost walls and foundation walls so long as upper panel 182 is sized to fit on such conventional wall.
Returning again to
In some embodiments, an e.g. conventional concrete footer 55 is interposed between the natural underlying soil, or clean aggregate stone base, and the bottom plate 16. In such instance, any of a wide variety of conventionally available pliable, crushable, and curable liquid, paste, or the like deformable gasketing or other bridging material 51 of changeable form, or gasketing or other bridging material of defined but crushable form, such as sheet material, is laid down on the footer before the wall panel is placed on the footer. Bridging material 51 is illustrated as a somewhat irregular thick dark line between concrete footer 55 and bottom plate 16 in
When the deformable material cures, the deformable material becomes a load-bearing, bridging material, whereby the bridging material transfers corresponding portions of the overlying load across the potentially-existing spaces, which have been filled with the bridging material, thus to provide a continuous load sharing interface between the wall panel and the footer along the full length of the wall panel. Such bridging material can be any material sufficiently deformable to take on the contours of both the lower surface of plate 16 and the upper surface of the footer, and which is curable to create the afore-mentioned structural bridging configuration.
Referring again to
While described using differing nomenclature, namely wall surface and inner surface, inner surface 57 and wall surface 25 both represent the same face of wall panel 14 when considered away from studs 23 and 123. Contrary to surface 25, inner surface 57 also includes the respective surface of the wall panel at studs 23, 123.
Inwardly-directed forces which reach the upper end of the wall panel are opposed by conventional attachments between the overlying main floor 40 and top plate 20. Inwardly-directed forces which are imposed on wall panel 14 between the top of the wall panel and the bottom of the wall panel are transferred to the top and bottom of the wall panel, thence to the concrete floor and the overlying main floor or floor system, through the stiffness and rigidity of the wall panel as collectively defined by the interactions of the structure defined by layers 34, 36, 50, foam blocks 32, and studs 23, 123, if used. Other reinforcing structure can be included, added to the wall, as desired in order to achieve the desired level of lateral strength and rigidity in the wall structure.
In residential construction, a typical maximum vertical load experienced by an underlying e.g. foundation wall is about 3000 pounds per lineal foot to about 5000 pounds per lineal foot. The vertical crushing load can be applied to the full width of the top of the wall anywhere along the length of the wall
Typical maximum horizontal point load bending moment on such wall is about 1000 pounds per square foot to about 1500 pounds per square foot. The horizontal loading is measured at 39 percent of the height up from the bottom of the otherwise horizontally-unsupported wall.
Referring to
Depending on the safety factors desirably built into the building panels, the vertical crush resistance can be as little as about 4000 pounds per lineal foot, optionally at least about 6000 pounds per lineal foot, typically at least about 8000 pounds per lineal foot. At least 10,000 pounds per lineal foot can be specified, as can at least 12,000 pounds per lineal foot.
The bending resistance of the wall panel at the locus of maximum horizontal underground loading is typically at least about 1500 pounds per square foot, and up to about 3000 pounds per square foot. Both the vertical crush resistance and the horizontal point loading bending moment resistance can be designed for greater or lesser magnitudes by specifying, for example and without limitation, density of included foam; thickness of layers 34, 36, 50; wall thickness, spacing, and/or depth “T1” of studs 23, 123, or thickness “T” of the panel, or thickness “T” in combination with depth “T1” the structure.
Above-ground side loads, such as wind loads, are less than the above-recited 1500 pounds per square foot. Accordingly, the bending resistance capabilities of building panels intended for above-ground applications can be less than the above-recited 1500 pounds per square foot.
Panels expected to be used in below-grade applications are designed to satisfy the load requirements experienced in below-grade applications, while panels expected to be used in above-grade applications are designed to satisfy the load requirements experienced in above-grade applications. Such design process includes considering weather and/or ground movement history of the use location, as well as other environmental factors. Thus, building panels of the invention include a wide range of panel structures and properties, so as to provide engineered solutions which can be designed to fit the stress environments expected to be imposed on the specific building panels which are to be used in specific uses. One can, of course, also make building panels of generic design which are designed to tolerate a wide range of expected loadings. For example, a first design specification can be made to satisfy most below-grade uses while a second design specification can be made to satisfy most above-grade uses.
Returning to
In the invention, in place of a concrete footer, multiple layers of reinforced polymer composite, such as is used in wall panel 14, are used in fabricating a support pad 30. A typical such support pad 30 is illustrated in
A cross-section of a representative pad 30, on an underlying support base SB is illustrated in
Such layering can be created by folding and stacking a resin-wetted fiberglass layer in a mold, closing the mold and evacuating the air, thus to consolidate the pad, then curing the resin, resulting in the hardened fiber-reinforced polymeric pad. In the alternative, the fiberglass layering can be placed in the mold in dry condition, and the resin can be added while the mold is being evacuated.
Pad 30 is illustrated as having a generally square or round projected area, and as being used for spot support such as in support of a post 28. Pad 30 can have an expanded projected area of any desired projected configuration such as to underlie and support multiple posts in a single area. Further, pad 30 can have an elongate configuration whereby pad 30 can be used as an elongate footer under, and supporting any number of foundation panels 14 when such panels are used in a fabricated foundation wall.
Thus, a typical support pad can have a projected area of about 1 square foot to about 10 square feet when designed to support a point load such as a single post. A pad which is designed to support an e.g. elongate load such as a wall having a length of e.g. 10 feet, 20 feet, 40 feet, or more has an elongate dimension corresponding in magnitude to the length of the wall.
The thickness of the pad is designed to support the magnitude of the anticipated overlying load. Thus, as with the building panels, for each building application, the pad represents an engineered solution based on the anticipated load and load distribution. Magnitude of the load as supported by pad 30 generally corresponds to the load distribution conventionally contemplated for typical single-family residential construction. Thus, the load distribution recited herein for foundation walls can apply such that an elongate pad can support at least 5000 pounds per lineal foot and a round or square pad can support loads of at least about 2000 to about 5000 pounds per square foot, more typically at least 3000-5000 pounds per square foot. Higher loadings can be supported by suitably engineered such pads.
The thickness of a pad, between top 30T and bottom 30B depends in part on the load magnitude and load distribution, and in part on the specific resin as well as the specific structure of the reinforcing fibers and fiber layers, as well as on the nature of the construct of the pad. For light-weight construction, where the pad carries a relatively lighter load, the thickness of the pad can be as little as 1 inch thick. Where the pad bears heavier loads, the pad is thicker, and has the same order of magnitude of thickness that would have been used if the material were steel-reinforced concrete. Thus, pad thickness typically ranges from about 3 inches thick to about 16 inches thick, optionally about 6 inches thick to about 16 inches thick, optionally about 8 inches thick to about 16 inches thick, with all thicknesses between 1 inch and 16 inches being contemplated. Thicknesses less than 3 inches and greater than 16 inches are contemplated where the anticipated vertical load and load distribution, along with the material properties, indicate such thicknesses.
In general, the dimension of thickness is less than either the length or width dimension. As illustrated in e.g.
In any event, the structure shown in
In the alternative, as illustrated in
The post 28 is generically represented in
Such resin-fiber composite post 28 has a generally enclosing structural sidewall. The post sidewall is made of fiberglass-reinforced polymer composite or other fiber reinforced resinous structure. The thickness and rigidity of the post sidewall is designed as known in the art to carry a specified load, thereby to support the weight of an overlying portion of typically an above-grade structure, though below grade structures can be supported as well. The enclosing post sidewall defines an interior chamber disposed inwardly of the enclosing sidewall. The interior chamber is typically empty, but can contain structural or non-structural material as desired.
Where the fiberglass post 28 is used, a fiberglass-reinforced polymer composite cap 58 is typically mounted over the top of the post. Cap 58 has a top wall 60, and one or more downwardly-depending structural skirts 62. Top wall 60 of the cap is sufficiently thick and rigid to receive the load from the overlying beam and transmit the load generally uniformly about the perimeter of the upstanding outer walls of the post, including where the outer walls may be disposed laterally outwardly from the edges of the beam. The structural skirt or skirts are configured such that, when the cap is mounted on the post, with the top wall of the cap bearing down on the top of the post, the inner surface of the structural skirt or skirts is/are in generally surface-to-surface contact with, or close proximity with, the outer surface of the post, such that the skirt structure receives and absorbs typically encountered lateral forces and transfers such lateral forces to the sidewall of the post, thereby preventing the top of the cap from moving laterally relative to the top of the post.
The cap distributes the lateral loads to the post side walls with limited bending of the top wall of the cap, so as to utilize substantially the full load-bearing capacity of the post sidewalls, from at or near the upper edge of the post, along the full height of the post to the underlying pad 30. The cap skirts thus capture lateral forces and transfer such lateral forces to the post.
An alternative to cap 58 is to use a conventional adjustable screw 59 on the top of post 28. Such screw 59 can be used in place of cap 58, or in combination with cap 58, e.g. between cap 58 and overlying beam 26. Where both cap 58 and screw 59 are used, a suitable screw/cap interface is configured in the screw and/or cap to ensure suitable cooperation of the cap and screw with respect to each other.
While the pad/post/cap combinations shown in
In other embodiments, the fiberglass post 28 can extend above grade, and can support any of a wide variety of suitable overlying structures.
As indicated above, one of the objectives of the invention is to use wall panels and accessory structure in places, and for structural purposes, where concrete would conventionally be used. Use of concrete in foundation walls is common, and the products of the invention are readily adapted to be used in foundation structures.
However, especially in more tropical climates, above-ground outside walls are, in some instances, required to be built with concrete for the purpose of, among other advantages, inhibiting mold growth. Where high wind conditions, such as hurricanes or tornadoes, are common, above-grade outside walls are, in some instances, required to be built with concrete in order to achieve additional lateral strength which can withstand such wind forces.
In such situations, such as in areas frequented by hurricanes or tornadoes, above-ground wall structures of the invention can be used in place of concrete, while achieving the lateral load-bearing properties of concrete and avoiding the e.g. water penetration, and other, limitations inherent in concrete. Accordingly, the wall structures of the invention are contemplated to be useful in above-ground applications as well as below-ground/foundation wall applications.
The reinforcing fiber materials used in products of the invention can be selected from a wide variety of conventionally available fiber products. Glass fiber has been illustrated in the general description of the invention, and is believed to be the most cost effective material. Other fibers which are contemplated as being acceptable include, without limitation, carbon fibers, Kevlar fibers, and metal fibers such as copper and aluminum. Other fibers can be selected to the extent their reinforcing and other properties satisfy the structural demands of the building panel applications contemplated in the invention, and so long as the fibers are not pre-maturely degraded in the use environment contemplated for the respective wall panels.
To that end, use of cellulosic fibers is limited to those compositions where the cellulosic fiber can be suitably protected from the deleterious affect of moisture reaching the fiber and degrading the fiber. Thus, use of cellulosic fiber without moisture protection is not contemplated as part of the invention, except in amounts of less than 10 percent by weight of the overall composition of a given structural element, e.g. panel, bracket, or the like. However, where the fiber is impregnated with a suitable quantity of resin, the resin protects the cellulosic fiber from attack by moisture, and so such composite compositions can be used.
The lengths, widths, and cross-sectional shapes of the fibers are selectable according to the structural demands of the structures in which the building panels or other structures are to be used.
Woven-fiber base sheets, such as woven fiberglass cloth, are contemplated as being efficiently processed into layers for use in building panels of the invention. However, those skilled in the art will recognize that a wide variety of processes, and corresponding ways of handling and processing the fibers, as well as the resin, are available for making the building panels of the invention. The selection of fiber structures can be specified to accommodate all such processes, whereby all fibers which can be employed in all such processes, for example chop, matt, or woven fibrous material, to achieve the desired structural, insulation, and other properties typically desirable in a foundation wall, or an above-grade wall, can be used in building panels and other elements of the invention.
Reinforcing fibers are generally known as dry fibers or pre-impregnated fibers for purposes of the process of fabricating reinforced resinous products with such fibers. The fibers contemplated for use herein are typically dry fibers, though some wet fiber processes are contemplated as being useful in making products of the invention.
The polymer which is used to impregnate and/or carry the fiber can be selected from a wide variety of conventionally available multiple-part reaction-curing resin compositions. Typical resin is a 2-part liquid where two liquid parts are mixed together before the resin is applied to the fiber substrate. Third additional components can be used in the reaction mixture as desired in order to achieve the desired level of reaction curing of the resin. The resin mixture should be sufficiently liquidous to be readily applied and spread about a fiber base sheet/substrate thereby to fill in all of the voids in the substrate. Examples of useful 2-part reaction curing resins include, without limitation, epoxy resins, vinyl ester resins, polyester resins, polyurethane resins, and phenolic resins. Those skilled in the art know that each of the above noted resins represents a large family of reactable materials which can be utilized to make the resultant reaction-cured resin, and are capable of selecting reaction resin combinations for the uses contemplated in the invention. In addition, more than two such resins can be mixed to obtain a desired set of properties in the reaction product or process.
For any set of reaction materials which are used to make the resins illustrated here, any conventional additive package can be included such as, for example and without limitation, catalysts, anti-oxidants, UV inhibitors, fire retardants, and fluidity-control agents, to enhance the process of applying the resin and/or curing the resin, and/or to enhance the properties of the finished product, e.g. weather resistance, fire resistance, hardness, and the like.
Each set of two or more materials which can be mixed and reacted to make the resultant resin product has its own reaction parameters, including desired reaction temperature, catalysts, time required for the curing reaction to take place, and the like. Further, each set of such two or more materials develops its own set of resultant physical and chemical properties as a result of the curing process. Especially the physical properties are influenced by the affect of the included fibers, such that more than two such reactants may be useful in achieving, in the reacted polymer, a desired set of physical properties.
In general, dry fiber substrate, woven cloth, or fiber matt, is used as the fiber base for all structural layers such as layers 34, 36, 50; as well as for all other structural elements of the invention such as posts, 28, pads 30, caps 58, channel studs 123, and brackets 48, 140, 148, 150, 160, 170, and 188. Since the objective is to fill in substantially all voids in the fiber substrate with resin, enough resin is added to the fiber substrate to fill all such voids, whereby there should be no air inclusions, or so few air inclusions as to have no material affect on the physical or chemical stability, or the physical properties, of a building panel or other structure built with such resin-impregnated fiber-based layer. Overall, the glass/resin ratio is as high as can be achieved, and not leaving any significant, deleterious voids in the resultant layer once the resin is cured.
In the alternative, layers 34, 36, 50 can be fabricated using pre-impregnated layers of fiberglass, namely fiberglass substrates which have been pre-impregnated with resin before being fabricated into a structural element pre-form, and which can be cured by e.g. application of heat as in a curing oven.
Given the requirement to minimize voids, and using conventional layer-development techniques, the resultant structural layer product, e.g. layer 34, 36, or 50, or other product, is about 30 percent by weight to about 65 percent by weight fiberglass, and correspondingly about 70 percent by weight to about 35 percent by weight resin. Optionally, the resultant layer is about 40 percent by weight to about 60 percent by weight fiber and about 60 percent by weight to about 40 percent by weight resin. A typical resultant layer is about 45 percent by weight to about 55 percent by weight fiberglass and about 55 percent by weight to about 45 percent by weight resin, optionally about 50 percent by weight fiberglass and about 50 percent by weight resin.
According to well-known technology, the number of layers of glass, in combination with the weight of the glass per layer, in general determines the thickness of the resultant layer after the resin-impregnated layer is cured. For example, multiple layers of a 12-17 ounce per square yard layer of woven fiberglass cloth can be impregnated to fill all voids, and to thereby achieve a resultant cured structure which is typically between about 1 millimeter thick and about 2.5 millimeters thick (between about 0.04 inch thick and about 0.10 inch thick). The greater the number of layers of fiberglass which are impregnated, typically the greater the thickness of the resulting impregnated and cured composite reinforced layer.
The top and bottom plates, as well as layers 34, 36, and 50 can be made of such polymer/fiber composite. The bottom plate can be any material which can bear the load imposed on the overlying wall panel. A typical bottom plate is an e.g. about 0.18 inch thick to about 0.50 inch thick fiber-reinforced pultrusion, which is sufficiently stiff and rigid to spread the overlying load to the underlying soil substrate generally uniformly along the length of the panel through an e.g. leveled clean aggregate stone base. The stone may be a crushed stone or an uncrushed aggregate stone.
Top plate 20 can be made of, without limitation, fiberglass-reinforced, or other fiber-reinforced, resinous materials, or other materials such as wood, in the shape conventionally used for a top plate. It is contemplated that a conventional wood-based top plate serves the purpose adequately, and provides for attachment of overlying wood elements such as wood framing, using conventional fasteners and conventional fastening methods.
The purpose of the foam, such as in foam blocks 32, is generally two-fold. First, the foam contributes to the structural integrity of the building panel structure by being sufficiently rigid, namely a rigid foam, that the foam contributes significantly to fixing the structural layers 34, 36, and 50 in their designated positions under normal loading of the panel, whether vertical gravitational loading, or lateral loading such as lateral ground loads in below-grade applications, and lateral wind and/or water loads in above-grade applications. Thus, the foam makes a substantial contribution to the dimensional stability of panel 14.
Second, the foam provides substantial thermal insulation to the resulting building panel construct.
In achieving a desirable level of thermal insulation while retaining the foam as a rigid closed-cell material, the foam has a density of about 1 pound per cubic foot (pcf) to about 12 pcf, optionally about 2 pcf to about 8 pcf, optionally about 2.0 pcf to about 5 pcf. Lighter weight foams generally do not provide sufficient rigidity to perform the role of the foam in fixing the structural layers in their designated locations and such lighter-weight foams may be open-cell foams. While heavier weight foams can be used, and typically provide more structural strength, such heavier weight foams provide less than the desired level of thermal insulation properties, and are more costly. In general, the foams used in the invention are closed-cell foams.
Foam blocks 32 can be made from a wide variety of compositions including, without limitation, extruded polystyrene foam, expanded bead polystyrene foam, rigid urethane foam, or polyisocyanurate foam. The foam is moisture resistant, preferably moisture proof, and is chemically and physically compatible with the compositions and structures of layers 34, 36, and 50.
Regarding fixing the respective structural layers in their designated positions, the foam fills all, or substantially all, of the spaces between the respective surfaces of the structural layers 34, 36, and 50, and is in surface-to-surface contact with the respective layers as such layers define the cavities in which the foam is received. In addition, the foam is adhered to the respective structural layers so as to absorb sheer forces between the foam and the respective structural layers.
The foam blocks 32 can be brought into surface-to-surface relationship with one or more of the structural layers 34, 36, 50 after the resin has been applied to the respective fiber substrate which is used to form the layers and before the resin has cured, whereby respective one or more surfaces of the foam blocks, which are in surface-to-surface contact with the respective resin-coated fiber substrate, become wetted with the uncured resin. With the foam in contact with the to-be-cured fiber-reinforced layer, and wetted by the fiber-reinforced layer, the curing of the resin bonds the foam blocks to the structural layer 34, 36, 50 as applies, whereby no separate adhesive is necessarily required to bond the foam blocks to the structural layers.
Throughout this teaching, reference has been made to affixing various elements of the building panels to each other. In some cases, mechanical accessories such as bolts have been mentioned, such as for attaching the top plate to bracket 24. In instances where two elements are affixed to each other, and where both elements contain resin components, especially reaction-cured components, the curing of the resin in any two such structural elements being formed or joined can be used to affix the elements to each other such that no further adhesive need be used. On the other hand, where components are assembled to each other at the construction site, at least in some instances, use of e.g. conventional adhesives and sealants which are known for utility in construction projects, is contemplated.
One example of use of construction adhesive in assembling the foundation wall is affixing the bottom plate to a wall panel 14. Wall panels 14 can be transported to the construction site without top plate or bottom plate, and wherein top plate materials and bottom plate materials can be transported to the construction site separately, although potentially on the same vehicle. Bottom plates and top plates are then affixed to the wall panels at the construction site, as desired. The bottom plate is typically affixed to the bottom of the wall panel with a construction adhesive, with or without the assistance of brackets 24. The top plate can be affixed to the top of the wall panel using brackets 24 and bolts 139, and/or other support as needed, and optionally in addition, adhesive between the top plate and the top of the wall panel.
Brackets 48, 140, 148, 150, 160, and 170 can be adhesively mounted to the building panels. In the alternative, the surfaces of the respective parts, including the respective areas of the building panels, can be coated with a supply of the curing resin before the parts are assembled, and the parts can then be held together for a sufficient time, under satisfactory conditions, which result in the curing of the resin, whereby the curing of the resin develops the necessary level of affixation between the respective parts of the wall.
In the same way, either adhesively or by use of curable resin materials, channel studs 123, support brackets 24, 48, and floor-and-garage apron brackets 188 can be mounted to a wall panel after the wall panel reaches the construction site.
It will be understood that any affixation of bracket 24 to the inner surface of the wall panel must be generally fully developed as to its required operating strength before the top plate or bottom plate, as applies, can be affixed to the wall panel and apply its rated load to bracket 24.
In general, wall structures of the invention can be engineered to support any level of compressive load which is contemplated to be applied to the building. For example, and without limitation, using conventional woven fiberglass substrate, a demonstrative foundation building panel, such as the panel illustrated in cross-section in
Woven fiberglass is used for the base, e.g. substrate of structural layers 34, 36, and 50, as well as for the base substrate for channel studs 123. The fiberglass substrate can be triax woven fiber substrate having basis weight of about 22 ounces per square yard. Another exemplary fiberglass substrate is a bi/uniax woven fiber substrate having basis weight of about 12 ounces per square yard to about 22 ounces per square yard. Yet another example is a woven roving having basis weight of about 17 ounces per square yard.
The selected fiberglass substrate, for example a 22 ounce woven substrate, is laid out on a horizontally-disposed release material such as a layer of MYLAR® oriented nylon. Other materials may be substituted for the release sheet and become part of the finished wall panel while achieving separation from the processing line as well as to achieve a desired exterior finish on the wall panel. The fiberglass substrate is brushed or otherwise impregnated with a curable 2-part epoxy resin in sufficient quantity and in such process as to fill in substantially all of the voids in the woven fiber substrate, thus to create a first pre-form for outer layer 36 for the wall structure, and wherein the so-prepared pre-form is wet with the epoxy resin which fills substantially all of the voids in the fiberglass substrate.
A plurality of closed-cell foam blocks, about 3 inches thick, 8 inches wide, and extending the full height of the set-up layer 36, are laid on the set-up layer 36, parallel to each other, at spaced locations along the length of the panel. As used herein, height, length, and thickness of a wall panel refers to the panel in its upright use orientation in an upright e.g. foundation wall or above-grade wall. “Width” refers to such height dimension of the construct while the construct is being fabricated in the above-noted horizontal orientation. As the foam blocks are laid on the horizontal pre-form of the first layer, some of the web resin on the pre-form of the first layer transfers to the dry blocks of foam. In the alternative, one or more surfaces of the foam blocks can be pre-wetted with a desired amount of the curable resin. In any event, the foam blocks, on the wet pre-form, bear a certain level of surface liquid in the form of curable resin.
A second wetted weaving layer pre-form, wetted with the same 2-part epoxy resin, is prepared in the same manner as the first outer layer, and is weaved back and forth over the combination of the outer layer pre-form and the foam blocks 32, with the wetted weaving layer weaving back and forth in face-to-face contact with the blocks and the layer 36 pre-form, along the full overall surface of the respective construct, leaving elongate voids in the construct between the respective blocks.
A second set of a plurality of foam blocks 32, optionally pre-wetted with the epoxy resin, is then inserted into the voids between the foam blocks which are already in the structure, thus filling in the entirety of the length and the width of the layer 36 pre-form. Accordingly, the combination of foam blocks 32 and weaving layer 50 pre-form present a generally uniformly flat and continuous top surface of the resulting construct at this stage of assembly of the building panel, and all of the blocks, the layer 36 pre-form, and the layer 50 pre-form, are wet with the epoxy resin.
A third wetted inner layer 34 pre-form is prepared in the same manner as the first outer layer pre-form and the weaving layer pre-form, and is laid on top of, and pressed onto, the construct, such that the third layer pre-form serves as a covering layer covering the entirety of the top surface of the resulting construct. At this stage, the foam blocks are urged toward each other to consolidate the foam blocks and the weaving layer together.
Channel studs 123 can be pressed into, onto the construct at that time if and as desired. Flanges 126 of the channel studs can be pre-coated with the epoxy resin, or can simply be pressed into the wetted surface of the layer 34 pre-form. In general, legs 128 and end panels 130 of the channel studs remain dry, and are not coated with the epoxy resin. A loading bar, loading belt, or other loading structure can optionally be applied across the tops of the channel studs, at end panels 130, pressing the channel studs into the inner layer 34, and correspondingly applying a load in general tending to consolidate the building panel, top to bottom, including channel studs 123, inner layer 34 pre-form, foam blocks 32, weaving layer 50 pre-form, and outer layer 36 pre-form.
The construct is held in the so-assembled and consolidated condition while the resin cures sufficiently to permanently fix the respective elements in the panel construct in their respective locations, thereby to form the resultant building panel 14.
In the resulting panel, the epoxy-resin impregnated 22-ounce fiberglass layers develop cured fiber-reinforced polymeric layers which are about 0.035 inch (0.9 mm) thick.
A first layer of fiberglass substrate 72 is unwound from a roll of such material and is fed generally downwardly through a pair of nip rolls 74 which carry a puddle 76 of 2-part curable resin, and apply such resin to substrate 72, and squeeze such resin into substrate 72, as the substrate passes through the nip defined between rolls 74, thus to develop a progressively resin-impregnated outer layer 36 pre-form. The wetted pre-form is carried across one or more guiding rolls downwardly and onto carrier web 66, and wherein the carrier web and the progressively-impregnated outer layer 36 pre-form are travelling at approximately the same speed along processing line 68.
Still referring to
A second layer of fiberglass substrate 78 is unwound from a roll of such substrate material and is fed vertically downwardly through a pair of nip rolls 80 which carry a puddle 82 of 2-part curable resin, and apply such resin to substrate 78, and squeeze such resin into substrate 78, as the substrate passes through the nip defined between rolls 80, thus to develop a resin-wetted weaving layer 50 pre-form. The wetted pre-form is carried across one or more guiding rolls downwardly and onto the outer layer 36 pre-form and blocks 32, and wherein the weaving layer pre-form, as it approaches the construct on the carrier web, is travelling at a speed which is faster than the speed of travel of outer layer 36 and foam blocks 32, and which is consistent with weaving the weaving layer into the entirety of the upper surface of the construct, including the upper surface of the outer layer 36 pre-form, the upper surfaces of blocks 32, and the side surfaces of blocks 32 which extend away from and toward the outer layer 36 pre-form.
The weaving layer pre-form thus lies in intimate contact with all previously-exposed surfaces of the underlying construct. The resulting construct has no substantial voids, no substantial air pockets between the weaving layer and the outer layer 36 pre-form, or between the weaving layer and the foam blocks, which cannot be eliminated subsequently in the process. The weaving layer then forms the entirety of the top surface of the resulting intermediate construct. The resulting intermediate construct defines channels extending along the width of the construct, as viewed into the paper in
The voids 84 are then filled with additional foam blocks 32 from a second stack 86B of such foam blocks. The foam blocks may or may not be pre-wetted with curable resin, as desired. After the blocks are in place, the voids 84 have been completely filled by the foam blocks, resulting in a generally flat, and continuous, surface as illustrated in
A third layer of fiberglass substrate 88 is unwound from a roll of such material and is fed generally downwardly through a pair of nip rolls 90 which carry a puddle 92 of 2-part curable resin, and apply such resin to substrate 88, and squeeze such resin into substrate 88, as the substrate passes through the nip defined between rolls 90, thus to develop a resin-wetted inner layer 34 pre-form. The wetted pre-form is carried across one or more guiding rolls downwardly and onto the top surface of the underlying resin-wetted construct, and wherein the inner layer 34 pre-form and the underlying construct, as carried by the carrier web 66, are travelling at approximately the same speed along processing line 68.
After the inner layer 34 pre-form has been applied to the construct, the resin-wetted inner layer pre-form covers the entirety of the width of the top surface of the construct. Channel studs 123 are then optionally applied to the construct, along the width of the construct, at spaced locations along the length of the construct, consistent with the desired spacing of the studs from each other in the finished building panels.
As desired, a weighting or other downwardly-directed force can be applied to the channel studs to assist the channel studs in becoming wetted with the resin which is contained in the inner layer 34 pre-form, and to urge the studs into intimate and bonding contact with the inner layer 34 pre-form. Such load can be applied to each channel stud by a loading structure which is distinct for each stud. In the alternative, a loading structure such as a plate or a belt can be applied to multiple studs, thus bridging the spaces between the respective studs. Such loading structure can take the form of, for example and without limitation, a loading belt. As desired, the load can be applied to the entire surface of the construct in order to further urge resin into remaining voids. As a result of the loading, the number and size of any remaining voids is sufficiently reduced such that any remaining voids are of little or no consequence to the strength of the overall construct.
In the alternative, or in addition, more resin can be applied to the bottom surfaces of flanges 126 of the channel studs, thus to facilitate wetting contact between the stud flanges and the inner layer pre-form.
Once the inner layer pre-form is applied to the construct, and with the channel studs applied according to design, if studs are used, the so-formed construct is passed through a curing oven 94 or other curing process, as needed, thus to cure the curable resin. As the resin cures, it sets up, also known as hardening. The chemical concept is that the reactable moieties, in the curable resin components, react to form long chain polymers, with a substantial increase in molecular weight, which results in the transformation of the reacting materials from the liquid form to what is known generally as a solid plastic; thus generally fixing the dimensions of the reaction products such that the reaction products are dimensionally stable, and making the resultant panel into the stiff and rigid fiber-reinforced product which is desired for building panels 14.
As the reacted, hardened, construct emerges from the curing process, the construct/product is sufficiently rigid, stiff, durable, dimensionally stable as to have no further need for carrier web 66, whereby carrier web 66 is stripped away from the construct/product and wound up on wind-up roll 70.
An additional layer can be added between carrier web 66 and outer layer 36, for example as an appearance layer to enhance the appearance of the outer surface of the resultant building panel. Such layer can be added as e.g. a gel coat, or as a pre-formed layer. As a pre-formed layer, such layer can be used in place of carrier web 66; such additional layer becoming part of the so-manufactured building panel product. In such instance, the additional layer is installed at unwind roll 64 instead of the MYLAR material, and wind-up 70 is no longer needed.
In the alternative, or in addition, and still referring to
The product made according to the process illustrated in
Still reflecting on the machines and processes illustrated and described with respect to
Turning now to
A first layer of fiberglass substrate 72 is unwound from a roll of such material and is fed generally downwardly through a pair of nip rolls 74 which carry a puddle 76 of 2-part curable resin, and apply such resin to substrate 72, and squeeze such resin into substrate 72, as the substrate passes through the nip defined between rolls 74, thus to develop a progressively resin-impregnated outer layer 36 pre-form. The wetted pre-form is carried across one or more guiding rolls downwardly and onto carrier web 66, and wherein the carrier web and the progressively-impregnated outer layer 36 pre-form are travelling at approximately the same speed along processing line 68.
Still referring to
A second layer of fiberglass substrate 78 is unwound from a roll of such substrate material and is fed vertically downwardly through a pair of nip rolls 80 which carry a puddle 82 of 2-part curable resin, and apply such resin to substrate 78, and squeeze such resin into substrate 78, as the substrate passes through the nip defined between rolls 80, thus to develop a resin-wetted weaving layer 50 pre-form. The wetted pre-form is carried across one or more guiding rolls downwardly and onto the outer layer 36 pre-form and blocks 32, and wherein the weaving layer pre-form, as it approaches the construct on the carrier web, is travelling at a speed which is faster than the speed of travel of outer layer 36 and foam blocks 32, and which is consistent with weaving the weaving layer into the entirety of the upper surface of the construct, including the upper surface of the outer layer 36 pre-form, the upper surfaces of blocks 32, and the side surfaces of blocks 32 which extend away from and toward the outer layer 36 pre-form.
The weaving layer pre-form thus lies in intimate contact with all previously-exposed surfaces of the underlying construct. The resulting construct has no substantial voids, no substantial air pockets between the weaving layer and the outer layer 36 pre-form, or between the weaving layer and the foam blocks, which cannot be eliminated subsequently in the process. The weaving layer then forms the entirety of the top surface of the resulting intermediate construct. The resulting intermediate construct defines channels extending along the width of the construct, as viewed into the paper in
The voids 84 are then filled with additional foam blocks 32 from a second stack 86B of such foam blocks. The foam blocks may or may not be pre-wetted with curable resin, as desired. After the blocks are in place, the voids 84 have been completely filled by the foam blocks, resulting in a generally flat, and continuous, surface as illustrated in
Channel studs 123 are then applied to the construct, along the width of the construct, at spaced locations along the length of the construct, consistent with the desired spacing of the studs from each other in the finished building panels. In the embodiment illustrated in
A third layer of fiberglass substrate 88 is unwound from a roll of such material and is fed generally downwardly through a pair of nip rolls 90 which carry a puddle 92 of 2-part curable resin, and apply such resin to substrate 88, and squeeze such resin into substrate 88, as the substrate passes through the nip defined between rolls 90, thus to develop a resin-wetted inner layer 34 pre-form. The wetted pre-form is carried across one or more guiding rolls downwardly and onto the top surface of the underlying resin-wetted construct. The speed of layer 34 is accelerated relative to the speed of travel of the underlying construct, whereby layer 34 is applied over studs 123 such that the full strength of layer 34, when cured, holds the studs in their designated locations in the completed wall structure.
After the inner layer 34 pre-form has been applied to the construct, the resin-wetted inner layer pre-form covers the entirety of the width of the top surface of the construct, including covering studs 123.
By positioning studs 123 over those portions of the weaving layer which are remote from outer layer 36, the weaving layer and the inner layer reinforce each other adjacent studs 123, whereby the coordinated locations of the weaving layer, the inner layer, and the studs provide cooperative and cumulative bending strength/resistances to external forces which are directed inwardly into the building.
Once the inner layer is cured as at curing station 94, the configuration of the inner layer adjacent the studs 123 permanently takes on generally the same configuration as the studs. Accordingly, the strength characteristics taught above for studs 123 are much less important in embodiments represented by
Another embodiment of building panels of the invention is illustrated in
The resin may be added to the wrapped fiberglass layers on one or more sides of the foam blocks before the foam blocks are introduced into the process of assembling building panels of the invention. Such pre-added resin in the wrapped fiberglass layers may be cured prior to assembly of the foam blocks into a panel. In the alternative, the resin may be cured later, along with the curing of the resin in the inner and outer layers.
In the alternative, the entirety of the resin used to consolidate the wrapping layers and bond the wrapping layers to the foam can be added to, dispersed in, the fiberglass layers of the foam blocks after the foam blocks have been assembled with some or all of the remaining elements of the panel structure.
The fiberglass in a wrapping layer can be applied as a winding of overlapping strands of fiber in a pattern which extends along the length of a given block of foam. In the alternative, the fiberglass can be a pre-woven matt of fiberglass which is wrapped about the foam block so as to form e.g. a butt joint or an overlapping joint where the ends of the wrap layer meet.
Whether the wrapping layer is applied as a winding of overlapping strands or as a woven fabric, the wrapping layer can represent an open pattern where some of the foam surface is exposed to casual visual observation through openings in the wrapped pattern. In the alternative, the wrapping layer can represent a closed pattern where the fiberglass strands visually obscure substantially all of the underlying surface of the foam block.
Given the presence of the wrapping layers, weaving layer 50 is not used.
An exemplary process for making building panels of
In some instances, the wrapping layers 190 are not resin-filled before the vacuum-infusion process, whereby the resin which enters the bag during the vacuum infusion processing fills the voids in the wrapping layers as well as the voids in the layer 34 and 36 pre-forms. In other instances, the wrapping layers 190 have already been filled with resin. In some instances, the resin has been cured, in which case the resin introduced in the vacuum infusion process serves to adhere the respective wrapped blocks to each other, as well as to permeate the inner and outer layer pre-forms thereby consolidating all of the respective components into a unitary composite structure. In other cases, the resin has not been cured, in which case the resin introduced in the vacuum infusion process serves both to adhere the blocks to each other and to the inner and outer layers, and to fabricate the blocks and the inner and outer layers into a single unitary structure. In any such structure, the portions of the resin-impregnated wrapping layers which traverse between the inner and outer layers function as structurally reinforcing layers in the resulting building panel.
Blocks 32B, 32E, and 32H thus perform as structurally-reinforcing members, previously illustrated as studs 23 and 123, and are hereinafter referred to as studs.
In the first set of foam blocks/elements, the relatively wider sides 199 of the foam elements face toward the inner and outer layers. In the second set of foam elements, the relatively wider sides 199 of the foam elements face along the length of the building panel.
In some embodiments, and depending on the specifications requiring that structural strength be contributed by the structurally-reinforcing foam studs 32C, 32F, the density of the foam in the reinforcing foam studs illustrated as 32B, 32E, and 32H can be greater than the density of the foam in the remaining foam blocks, in order to achieve the desired level of structural reinforcement. In other implementations of
In the alternative, or in combination, such reinforcement strength can be captured according to the thickness and rigidity of the wrapping layers 190 about the respective foam block studs 32B, 32E, and 32H. In some implementations, the wrapping layers 190 about foam block studs 32B, 32E, and 32H are the same as the wrapping layers 190 about the remaining foam blocks. In other implementations, the wrapping layers 190 about foam block studs 32B, 32E, and 32H are thicker or otherwise more rigid than the layers 190 about the remaining foam blocks, in order to achieve greater levels of strength and rigidity in the studs.
In light of the pre-wrapped structure of foam blocks 32, the fiberglass-reinforced wrapping layer 190 can serve the functions of either or both of inner layer or outer layer 36, whereby layers 34 and 36 are optional elements of the building panel of
In any event, the strength provided in the reinforcing block studs 32B, 32E, and 32H can be manipulated by selectively specifying both the foam density in the respective blocks and the thickness and other characteristics of the fiberglass reinforced wrapping layers 190.
Given the structural orientation of foam blocks 32 in
Given the above dimensions, the size of space 131 between a pair of adjacent studs is the same as conventional depth, namely 3.5 inches of conventional wood stud spacings, and a width of 13 inches. Further, the 16 inch center-to-center spacing of the foam block studs provides for conventional attachment of conventional building materials such as 48-inch wide sheeting 129 on the inside of the building panel. Thus, the embodiment of
The embodiment of the building panel illustrated in
The embodiment of
Pre-wrapped foam blocks 32 in the
Or by wrapping the foam block 32 in additional layers, or thicker layers, of fiberglass-reinforced resin, the strength contribution of the fiberglass wrapping can be increased sufficiently to enable the width of the foam block to be reduced to 1.5 inches, whereupon the width of cavity 131 is again 14.5 inches.
As desired, the width of a stud 23 or a stud 123 can be greater than 3 inches, such as 4 inches, 5 inches, or 6 inches, with corresponding adjustment in the widths of the laid-flat foam blocks to achieve a desired center-to-center spacing of the foam blocks such as 16 inches center-to-center or 24 inches center-to-center.
The first 202 and second 212 ends of a given layer element 200 overlap the adjoining layer elements 200 at the reinforcing members 209, whereby each layer element overlies or underlies three of the reinforcing members 209 and reaches proximity to four of the foam blocks.
The depiction of the layers and layer elements in
Studs 123, as illustrated, are optionally added as desired in the embodiments of
Now speaking generically of the invention, fiberglass layers used in the invention, such as and without limitation, layers 34 and 36, can also be made using the well-known chop spray method. In the chop spray method, a layer of fibers is sprinkled or sprayed onto a substrate, and are then covered with a spray of resin. The resin impregnates the sprayed layer of fibers and is cured, thus to develop the respective fiberglass-impregnated layer.
For example, the chop spray method, or any other known method of fabricating fiberglass panels, can be used to fabricate outer layer 36 and inner layer 34. Such inner and outer layers can then be brought together with e.g. the pre-wrapped foam blocks to do the final assembly using either additional resin or suitable construction adhesive. Studs 123 can be added as desired on the outer surface of inner layer using either hardenable resin or construction adhesive.
As an alternative, the inner layer, the outer layer, and the weaving layer can be pre-manufactured as hardened layers of resin-impregnated fiberglass. The pre-manufactured weaving layer is in the configuration shown in e.g.
Cells 196 may or may not contain thermally insulating material such as closed cell foam as is used in foam blocks 32 in others of the illustrated embodiments. Where insulating foam is used, an e.g. foam-in-place process can be used to install the foam into the respective cells.
As a further illumination of the empty-space embodiments represented by
In the embodiment illustrated in
Further, the structurally-reinforcing member can be the wrapping layers 190 illustrated in
Given that the closed cavities 196 in the structure are empty, all of the strength in the structure is derived from structural elements 234, 236, and 250. Thus, structural elements 234, 236, and 250 are designed as structural members in and of themselves, whereby inner layer 234, outer layer 236, and bridging member 250 have thicknesses relatively greater than the thicknesses of layers 34, 36, and 50 in the embodiments of e.g. s. Thicknesses of layers 234, 236, and 250, in the example illustrated in
Cavities 196 can be used as utility runs as desired. In any of the pultruded structures, cavities 196 can be filled with insulating foam or other known insulating materials, as desired, for example and without limitation, by injecting the foam material as a latter stage of the pultrusion process. Any rigidity provided by such insulating material, if any, can be considered in designing especially the thicknesses of elements 234, 236, and 250.
Exemplary structures of ends of the pultruded building panels, and joinders of adjacent panels, are shown in
So long as the panels are not cut, the panels can be joined end-to-end using end structures which have been fabricated as part of the process of initially fabricating the panel. Where an initially-fabricated end structure of a panel is cut off, such as at the construction site, the cut-off end of that panel can be joined to another panel using an “H” bracket 140.
An inner layer of fiberglass-reinforced polymer is applied over both the laid-flat blocks 32 and studs 123.
A hollow space 133 is defined inside each such stud. Hollow space 133 can be filled with thermally-insulating foam as desired. The panel illustrated in
Both pultruded blocks 232 and pultruded studs 223 are illustrated with hollow spaces 133. In another embodiment, not shown, insulating foam, for example polyurethane foam, is injected into the hollow spaces in one or both of blocks 232 and studs 223, providing enhanced thermal insulation characteristics.
Referring to
At the beginning of the process, the upper and lower mold elements, including recesses 302, are optionally coated with mold release material. In the alternative, a mold release agent can be incorporated into the resin. Next, foam stud blocks 323, pre-wrapped with layers 308 of fiberglass, are placed into recesses 302. Foam stud blocks 323 and recesses 302 are so sized and configured that the foam blocks fit snugly in the recesses, and the top surfaces of the foam stud blocks are generally co-planar with the upper surface 304 of the lower mold element.
As part of the process of placing the foam stud blocks into the recesses, each foam stud block is drawn through a resin wetting machine which applies coatings of liquid resin on three of the four elongate surfaces of the foam block. The three surfaces which are coated are the bottom surface and the two side surfaces, as indicated by arrows 310 in
Next, a dry layer 334 of 22 ounce fiberglass fabric, which will become the inner layer of the so-fabricated building panel, is unrolled from a roll of such material mounted adjacent e.g. the right end of the mold table as illustrated in
Next, foam blocks 332, pre-wrapped with layers 314 of fiberglass, are laid flat on top of the dry fabric, edge-to-edge as illustrated in
Thus, by the time all the blocks 332 have been laid onto dry layer 334, a layer of resin has been placed over the entirety of the top surface of layer 334, by the resin on the bottom surfaces of blocks 332. In addition, the resin applied to the one or more side surfaces of the foam blocks readily transfers in part to the facing side surfaces of the adjacent foam blocks. Or if both the right and left side surfaces of foam blocks 332 have been resin-coated, then the coatings on the facing side surfaces merge and cooperate with each other. As part of the process of placing foam blocks 332 on layer 334, and if only one side surface of the blocks 332 is being coated with resin, the otherwise-uncoated side surface of the terminal end ones of the foam blocks is coated with resin on both side surfaces, whereby the outwardly-facing side surface of the last-placed foam block 332 is also coated with resin.
At this stage of the process, foam blocks 332 collectively form a dry upper surface 324 of the assemblage of elements, generally free from liquid resin. Next, another dry layer of the 22 ounce fiberglass fabric, which will become the outer layer 336 of the so-fabricated building panel, is unrolled from the roll of such material mounted adjacent e.g. the right end of the vacuum table and is pulled over the dry laid-flat foam blocks 332, from the right side of mold 300 to the left side of the mold. Since the upper surfaces of foam blocks 332 are generally free from resin, the fabric layer can be easily pulled and dragged over the top surface 324 of the foam blocks, which form the top surface of the assembly at this stage. Layer 336 of dry fabric is laid over the entirety of the assemblage of foam blocks 332, whereby layer 336 becomes the top surface of the assemblage.
Resin is then applied to the top surface of layer 336, such as by a drip coating, a roll coating, a liquid curtain coating, or other known surface-coating process, providing a resin coating over the entirety of the top surface of the assemblage. At this stage of the assembly, all of the bottom and side surfaces of foam blocks 323 and 332 are coated with liquid resin, and the top surfaces are uncoated with resin. In the case of foam blocks 323, inner layer 334 is next adjacent the dry top surface of foam blocks 323, and a layer of resin is located at the top surface of inner layer 334, whereby the dry top surfaces of foam blocks 323 are separated from resin by only inner layer 334.
In the case of foam blocks 332, outer layer 336 is next adjacent the dry top surface 324 of foam blocks 332, and a layer of resin is located at the top surface of outer layer 336, whereby the dry top surfaces of foam blocks 332 are separated from resin by only outer layer 336.
The upper and lower mold elements are then brought together, with a seal therebetween, so as to form a closed and sealed mold, with the respective elements of the building panel in the mold cavity.
The mold cavity is then evacuated, drawing a vacuum which removes substantially all of the air out of the cavity. As the air is withdrawn from the cavity, the resin flows to all areas of the mold where air has been removed, including through layers 334 and 336, thus to fill in all voids left by the evacuating air and to form a continuous resin matrix about and through all of layers 334, 336, and the wrapping layers 308 and 314 of fiberglass which encompass foam blocks 323 and 332.
Thus, resin flows downwardly through layer 334 and into intimate bonding contact with the top surfaces of foam blocks 323. Resin also flows downwardly through layer 336 and into intimate bonding contact with the top surfaces of foam blocks 332. As a result, the resin in the mold flows to all areas which have been evacuated by the removed air, thus creating a continuous matrix of resin throughout the structure in all of the fiberglass layers. However, in instances where the foam in foam blocks 323 and 332 is a closed cell foam, the resin does not penetrate generally beyond the outer surfaces of the foam blocks. Where the foam is an open-cell foam, the resin can penetrate more deeply into the foam blocks as permitted by the permeability of the foam.
Once the mold has been closed and evacuated, the resin is cured in the mold. In the process of curing the resin, the mold may be heated, or not, depending on the thermal requirements associated with the curing of the specific resin being used. Where heat is required, heat is applied. Where heat is not required, the resin is typically cured at ambient temperature.
After curing, the cured fiber-reinforced polymeric building panel product is removed from the mold. The mold is cleaned if and as needed, and the process is repeated to make another building panel.
In another embodiment, not shown, all of the elements shown in
The dimensions of the honeycomb cells, as well as the thicknesses of the walls 250 of the cells, can be designed for the desired, anticipated, vertical and horizontal loadings. The dimension “T3” across the honeycomb cell is typically between about 0.25 inch and about 2 inches. The thickness of a bridging member 250 is typically about 0.02 inch to about 0.20 inch. Cell size and bridging member thickness have known relationships which can be used by those skilled in the art to design honeycomb building panels having desired structural strength characteristics.
The honeycomb structure illustrated in
Studs 123 can be used as optional, for example to create a cavity 131 for running utilities or to receive a batt of fiberglass insulation, or to further contribute to the strength of the building panel.
The building panels illustrated in
Throughout this teaching, fiber-reinforced studs 123 have been illustrated and taught as having an end panel 130, first and second legs 128, and outwardly-extending flanges 126. See, for example,
Studs 123 can be located over a structurally-reinforcing member 50, 209, 250, as at 123A in
Among the requirements of the structurally-reinforcing member is that the materials in the structurally-reinforcing member cannot be sensitive to, susceptible to substantial degradation by, water or any inclusions commonly found in water, whether dissolved minerals or organic materials such as life forms which live on or transform the compositions of the fibers. Namely, the materials cannot be susceptible to degradation by water or anything in water, to the extent such degradation jeopardizes the ability of the structure made from such building panels, to provide the compressive strength necessary to support the overlying building loads, and the bending loads imposed by subterranean forces, and above-grade weather forces.
Accordingly, the structurally-reinforcing member typically does not include uncoated corrugated wood fiber structures commonly referred to as corrugated cardboard structures, or any other fibers whose strengths are substantially affected by moisture or moisture vapor, or any inclusions which can be expected to occur in moisture found in or around the soil adjacent a building structure. Further, the fibers cannot be susceptible to insect infestation, or any other degrading factors. Thus, the fibers are inert inorganic materials such as are illustrated elsewhere herein.
In the alternative, susceptible fibers can be used where such fibers are combined with sufficient coating of e.g. a resin to preclude such deleterious elements from reaching the fibers over the expected use life of the building panel; or where one or more layers disposed outwardly of a fiber layer in the panel is capable of preventing enough moisture from getting to the fibers that the fibers can become degraded as a result of exposure to moisture.
In any of the embodiments of the invention, one or more gel coats can be applied to the panel structure at one or both of the inner and outer surfaces.
Whatever the materials used for the reinforcing fiber, the foam, and the resin, all of such elements, including UV inhibitors and fire retardant additives, are chemically and physically compatible with all other elements with which they will be in contact, such that no deleterious chemical or physical reaction takes place in wall systems of the invention.
One of the substantial benefits of wall structures made using the teachings of the invention is that the wall structures are water-proof and moisture proof. For example, in areas where hurricanes are frequent, building codes require concrete structure in above-grade housing walls. Experience has shown that hurricane-force winds drive rain forcefully through such concrete wall structures so as to cause substantial water damage even when the building structure, itself, is not damaged.
By contrast, wall structures of the invention are essentially water proof; and such water proof characteristic is not affected by hurricane-driven rain. Layer 36 is, itself, water proof. While layer 36 is quite tough for water to penetrate, even if outer layer 36 is breached, the foam blocks 32 are water proof in that the individual cells of the foam blocks 32 are closed cells. If the foam layer is also breached, inner layer 34 is also water proof. In addition, where a weaving layer is used, before the breaching force reaches layer 34, it has to pass through weaving layer 50, which is another tough and waterproof layer, whether layer 50 is encountered adjacent layer 36 or adjacent layer 34. In any event, any breaching force has to penetrate multiple waterproof layers, at least two of which are substantially tough layers when considered in light of the types of forces which are typically imposed on buildings by weather or other typical outside loads. The structures which do not include foam are similarly-effective barriers to water penetration.
Regarding the joint between the bottom of the wall panel and the bottom plate, such joint can be filled with curable resin, adhesive, caulk, or other barrier material, thus to positively block any penetration of water at the joint between the wall panel and the bottom plate.
Similarly, vertical joints in the foundation wall using e.g. “H” brackets 146 can be closed to water penetration by applying curable resin, adhesive, caulk, or other water-proofing coatings to the joint. In addition, as mentioned elsewhere herein, adhesives, resins, and the like can be applied to the building panels and/or to the various brackets before the brackets are applied to the respective building panels, thereby to provide further water-proofing characteristics to the finished foundation wall, or above-ground wall.
Building panels of the invention find use in various residential, light commercial and industrial construction applications. The strength and other specifications of a given wall panel are specified in accord with the loads to be imposed during the anticipated use life of the building.
Wall structures of the invention find application in and as, for example and without limitation, the construction of foundation walls; frost walls e.g. in buildings which have no basement; manufactured home base curtain walls; floor systems; ceiling systems, roof systems; exterior above-grade walls; curtain walls as in high rise construction replacing concrete block; and exterior walls in areas that use masonry exteriors, such as in coastal construction. While the specification and drawings have focused on foundation walls, the principles disclosed herein apply in the same way to other uses of panels and accessories of the invention.
A variety of accessories and parts can be used with projects which use walls of the invention, for example and without limitation, posts to support beams/girders, fiber-reinforced piers which optionally include structural top and bottom, post pads, inside corner brackets, outside corner brackets, “H∞ channel brackets, top plate connectors, garage floor shelves, support brackets, floor-and-garage apron brackets, service door cut outs, garage door cut outs, frost wall transitions, and stud profiles.
In addition, there can be mentioned fiber and resin patch kits suitable for use to patch a damaged building panel, angled wall connectors, full basement wall to garage transition, frost wall returns, attachment of top and bottom plates, along with potential shipping advantages where the top and bottom plates are affixed at the construction site, beam pockets, post pads in the footer to distribute load, and window bucks. There can also be mentioned fasteners to apply exterior product and to provide connections to other parts of the building. Such fasteners can be, for example and without limitation, metal or fiber-reinforced polymer composite. A wide variety of accessories can be affixed to the wall structure using conventionally available adhesives for field applications.
A specific advantage of wall systems of the invention is that such wall systems can be readily sized and configured for use with already-available standard size conventional building products, e.g. construction materials.
Building panels of the invention can be cut, using conventional tools commonly available at a construction site, to fit the needs of the job at hand. For example, a panel can be cut for length. A window opening can be cut out. A door opening can be cut out. Utility perforations of the foundation wall can be cut, such as for furnace fresh air intake or combustion gas exhaust, or the like, or such utilities can be run in cavities 131 between studs 123 and inwardly or inner layer 34.
Advantages of the invention include, without limitation, a composite bottom plate which has potential to provide a wider footprint to the underlying soil than the projected area of the wall panel, for distributing the overlying weight of the building. The bottom plate can be applied on site or off site. The wall structures of the invention are light weight compared to the concrete structures they replace. The wall structures of the invention are waterproof, versatile, mold resistant, termite resistant, and rot resistant. The substantial polymeric component of the compositions of wall structures of the invention provides a desired level of radon barrier in accord with existing building codes whereby the conventionally-used polymeric layer on the outside of the foundation wall is not needed, and can be omitted, along with corresponding savings in material and labor costs.
Typical wall structures of the invention can be installed with manual labor, and do not require bringing any large machines to the construction site for the purpose of installing a footer, a foundation wall, or an above-grade wall, no form truck, no crane to install the building panels.
The invention does contemplate larger wall panels, e.g. thicker, higher, and/or longer, which can weigh at least 250-750 pounds or more, whereupon a light-duty lifting device, such as a light-duty crane, is optionally used to install such wall panels, with corresponding reduction in labor cost. Further, where a wall or roof panel is being erected above the ground floor, a suitable-weight crane facilitates such greater-height installation.
Wall structures of the invention can be installed in all seasons and all weather, so long as the excavation can be dug to a suitable natural support base. Panels of the invention are environmentally friendly. Panels of the invention are consistent with the requirements to qualify as Green buildings and/or as Energy Star buildings whereby buildings built with building panels of the invention may qualify for such ratings. No damp proofing is needed. Once the foundation walls are in place, the interior of the so-enclosed space is ready to be finished. HVAC cavities are available between studs 123. Plumbing and electric can also be run through the walls easily, again between studs 123, optionally inside studs 123.
Additional insulation can be easily installed in the wall cavities between studs 123, thereby to achieve e.g. at least R26 insulation factor. The building panels can be repaired more readily than concrete. Openings can be cut more easily than concrete. Wall changes can be made more easily than concrete. Any typical wall height can be achieved. The building panels can be installed on an aggregate stone footer, whereby no pouring of a concrete footer is required. Thus, the lowest level wall of the building can be completed with no need for any ready-mix concrete at the construction site.
Insulation property gained as part of the wall structure can be about R-15 without additional installation of insulation by using 3 inches of R5 per inch foam insulation blocks 32. Additional insulation can be added in cavity 131 to increase the thermal insulation value of the wall. In the alternative, the thermal insulation value of the wall can be increased by increasing the thickness of the wall between the inner and outer layers, using correspondingly thicker foam blocks 32, and filling all of the space with the foam blocks.
Wall structures of the invention have multiple desirable properties, including being fire resistant where fire retardant ingredients are included in the resin formulation, being a good barrier to ultraviolet rays, providing good sound attenuation, being generally free from insect infestation, being generally not susceptible to infestation by rot-generating organisms, being a good water barrier, and being a good barrier to transmission of radon gas.
Wall structures of the invention are sturdy, durable, and have very favorable expansion and contraction ratings compared to the concrete they replace. The wall structures tolerate a wide range of temperatures such as are encountered in building construction. The building panels of the invention are easy to transport to the construction site. The building panels can be mass-produced and do not have to be project-specific like known e.g. insulated wall systems which are produced off-site, and transported to the construction site as pre-fabricated wall systems. Wall, ceiling, roof, and floor structures of the invention can be installed in locations where it is difficult to get delivery of ready-mix concrete, such as on islands, in weight restricted areas, in high-rise curtain walls, and the like.
Although the invention has been described with respect to various embodiments, it should be realized this invention is also capable of a wide variety of further and other embodiments within the spirit and scope of the appended claims.
Those skilled in the art will now see that certain modifications can be made to the apparatus and methods herein disclosed with respect to the illustrated embodiments, without departing from the spirit of the instant invention. And while the invention has been described above with respect to the preferred embodiments, it will be understood that the invention is adapted to numerous rearrangements, modifications, and alterations, and all such arrangements, modifications, and alterations are intended to be within the scope of the appended claims.
To the extent the following claims use means plus function language, it is not meant to include there, or in the instant specification, anything not structurally equivalent to what is shown in the embodiments disclosed in the specification.
| Number | Date | Country | |
|---|---|---|---|
| 60923822 | Apr 2007 | US | |
| 60876403 | Dec 2006 | US | |
| 60872929 | Dec 2006 | US |