Patent Application
20110259056
The present application claims priority from Japanese Patent Application No. JP 2010-100093, filed in the Japanese Patent Office on Apr. 23, 2010, the disclosure of which is hereby incorporated herein by reference.
1. Field of the Invention
The present invention relates to a burner for manufacturing a porous glass preform, which can improve the gas mixing efficiency and improve deposition efficiency without increasing turbulence of the flame.
2. Description of Related Art
Conventionally, various methods have been proposed to manufacture an optical fiber preform.
As a burner for synthesizing the soot, a concentric multiple tube burner has been used. However, the burner having this configuration has been insufficient to generate glass particulates because glass source gas, combustible gas, and supporting gas are not mixed sufficiently. As a result, the deposition efficiency has not increased, and therefore it has been difficult to accomplish the synthesis at high speed.
To solve this problem, Patent Document 1 proposes a multiple nozzle burner in which, as shown in
Furthermore, Patent Document 2 proposes a method of preventing the turbulence of source gas flow by making the focal distance L1 of the small-diameter supporting gas injection ports longer than the distance L2 from the front end of the small-diameter supporting gas injection port small-diameter supporting gas injection port to the preform deposition surface. Patent Document 3 proposes a method of improving the deposition efficiency by inversely making the distance L1 shorter than the distance L2 to enhance the gas mixing efficiency.
Patent Document 1: Japanese Patent No. 1773359
Patent Document 2: Japanese Patent No. 3543537
Patent Document 3: JP 2003-226544 A
In the above-described proposals, the multiple nozzle burner that supplies supporting gas through the small-diameter gas injection ports arranged in a row concentrically and having a focal point has features of improving the mixing efficiency of combustible gas, supporting gas, and glass source gas and improving the deposition efficiency.
Therefore, as a method of further improving the mixing efficiency, the optimization of the focal distance of the small-diameter supporting gas injection ports has been studied.
Concerning the focal distance of the small-diameter supporting gas injection ports, generally, the focal point of the small-diameter gas injection ports is adjusted by bending the small-diameter gas injection ports at certain positions from the burner front end in the burner longitudinal direction.
As the result of extensive research, it has been revealed that it is important to prevent the flame from becoming more turbulent than necessary, in addition to enhancement of the mixing efficiency of injected gases.
Specifically, as shown in
Also, if the focal distance is equal, as the bend angle of the small-diameter gas injection port increases, the PCD of the small-diameter gas injection ports at the burner front end increases, so that the diameter of the combustible gas injection port involving the small-diameter gas injection port row inevitably becomes large. This not only makes the burner larger than necessary but also enlarges the flow path area of combustible gas more than necessary. Therefore, if the amount of supplied combustible gas is equal, the density of a porous glass preform decreases.
Consequently, to adjust the soot density to a proper range, the quantity of combustible gas and supporting gas consumed is inevitably increased, which results in an increase in manufacturing cost. Furthermore, the thermal stress applied to the device increases, which presents a problem of formation of cracks on the wall surface of the device.
An object of the present invention is to provide a burner for manufacturing a porous glass preform, which is capable of enhancing the gas mixing efficiency, improving the deposition efficiency, and reducing the thermal load applied to the device without an increase in the quantity of combustible gas and supporting gas consumed and without turbulence of the flame flow.
The present invention provides a burner for manufacturing a porous glass preform, which is provided with a combustible gas injection port involving a plurality of small-diameter supporting gas injection ports such that the injection ports of the same row have the equal focal distance, the small-diameter supporting gas injection ports being arranged on the outside of a glass source gas injection port in the center so as to be in a row or in a plurality of rows and concentric with the glass source gas injection port, wherein the small-diameter supporting gas injection ports are bent toward the burner center axis at predetermined positions from the tip ends of the small-diameter supporting gas injection ports so that the focal points of the small-diameter supporting gas injection ports of the same row agree with each other, and the bend angle of the small-diameter supporting gas injection port row closest to the glass source gas injection port in the center of the small-diameter supporting gas injection port rows arranged in the plurality of rows is at most 5 degrees with respect to the burner center axis. The bend angle is preferably at least 4 degrees and at most 5 degrees.
The present invention also provides a method of manufacturing a porous glass preform by using the above-described burner for manufacturing a porous glass preform.
According to the burner for manufacturing a porous glass preform of the present invention, the flame is not made more turbulent than necessary, and high mixing efficiency is maintained, so that the deposition efficiency is improved. Furthermore, not only can the burner be made compact and the thermal load applied to the device be reduced, but also the supply amount of combustible gas and supporting gas can be reduced, and therefore the manufacturing cost of a porous glass preform can be reduced.
An embodiment of the present invention will now be described in detail with reference to the accompanying drawings. The present invention is not limited to the embodiment described below.
Furthermore, the porous glass preform for optical fiber is dehydrated in a heating furnace, and thereafter is transparently vitrified to form a glass preform for optical fiber.
The burner 3 used is configured by involving one row or a plurality of rows of small-diameter supporting gas injection ports 7 having the same focal distance in a combustible gas injection port 8 provided on the outside of a glass source gas injection port 6 in the center. The small-diameter supporting gas injection ports 7 arranged in the same row each are bent toward the burner center axis at a predetermined position from the tip end so that the focal points thereof agree with each other. The bent angle of at least the small-diameter supporting gas injection port row closest to the glass source gas injection port 6 in the center of the small-diameter supporting gas injection port rows is in the range of 5 degrees or smaller, preferably in the range of degrees or more and 5 degrees or less. Thereby, the gas flows injected from the small-diameter supporting gas injection ports are caused to collide with a glass source gas flame flow at an acute angle, so that the flame is not made turbulent, and the gas flows gradually approach each other and are mixed.
Consequently, the flame is not made more turbulent than necessary, and high mixing efficiency is maintained, so that the deposition efficiency is improved. If the bent angle is 5 degrees or less, the effect on the turbulence of the flame is slight, so that the difference in deposition efficiency with angle is small. However, as the bend angle of the small-diameter supporting gas injection port decreases, the small-diameter gas injection port comes closer to the gas injection port tip end located on the inside thereof, so that the bent angle must be set in the non-contact range. Also, if the bend angle is less than 4 degrees, it is sometimes difficult to manufacture the burner. Therefore, the bend angle is preferably made in the range of 4 degrees or more and 5 degrees or less.
Furthermore, if the bend angle is small, the PCD of the small-diameter gas injection port tip end is also short, so that the inside diameter of the combustible gas injection port involving the small-diameter gas injection ports can also be made small. Thereby, not only can the burner be made compact, but also the gas flow path area is made small, and the gas can be supplied so as to concentrate at the flame center. Therefore, in the case in which porous glass preforms having the same density is to be obtained, the supply amount of combustible gas and supporting gas can be reduced, and the manufacturing cost can be reduced.
In an example, porous glass preforms for optical fiber were manufactured by the outside vapor deposition process using the device shown in
The burner used was a burner for synthesizing glass particulates, which is provided with the combustible gas injection port 8 on the outside of the glass source gas injection port 6 in the center as shown in
The burner characteristics other than the focal distance were made the same, and five types of burners in which the focal distance L of the supporting gas injection port row was made 100 mm, 125 mm, 150 mm, 175 mm and 200 mm were prepared. By using these burners, 100 kg of porous glass particulates were deposited on a starting member in which dummy rods, each having an outside diameter of 55 mm, were welded to both end portions of a core rod having an outside diameter of 55 mm and a length of 1500 mm.
Concerning the supplied gases, to the first tube of the burner, SiCl4 was supplied as the glass source gas, and O2 was supplied as the supporting gas; to the second tube thereof, N2 was supplied as the combustible gas; and to the small-diameter gas injection ports involved in the third tube thereof, O2 was supplied as the supporting gas. The amounts of these gases were made equal in five types of burners.
As the result, as shown in
Five types of burners were prepared, in which the focal distance L of burner was fixed at 175 mm based on the above-described result, the bend angle of small-diameter gas injection port was made 4.0, 4.5, 5.0, 5.5 and 6.0 degrees, and the burner particulars other than the bend angle of small-diameter gas injection port were made equal as given in Table 1. One hundred kilograms of porous glass particulates were deposited on a starting member in which dummy rods each having an outside diameter of 55 mm were welded to both end portions of a core rod having an outside diameter of 55 mm and a length of 1500 mm. The inside diameter of the combustible gas injection port involving the small-diameter gas injection ports was made 42 mm so as to correspond to the burner having a bend angle of 6.0 degrees.
As the result, when the bend angle was greater than 5 degrees, as the bend angle increased, the flame turbulence near the focal distance increased, and therefore the deposition efficiency decreased as shown in
Next, the bend angle was made 5 degrees, which was equal to the bend angle of type C, the inside diameter of the combustible gas injection port involving the small-diameter supporting gas injection ports was decreased to 36 mm, although the inside diameter in example 1 was 42 mm, and the gas flow rate was regulated so that the soot density was 0.7 g/cm3, which was equal to that in example 1. As the result, the gas flow rate given in Table 2 was attained, and the gas flow rate of combustible gas could be decreased by 20%.
The present invention contributes to reduction in size of a burner and improvement of quality.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2010-100093 | Apr 2010 | JP | national |