Calcium carbonate filler

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention finds its application in the field of resin molding compounds which are used in a wide variety of commercial applications from automotive parts, household appliances to business machines.
2. Description of the Prior Art
Resin molding compounds have been used for many years to produce molded products in the building construction and automotive fields. For example, automotive hoods, front grille elements, doors and other panels are now being made of molded resin to replace metal stamped parts. Not only does the use of resin molding technique enable greater design flexibility but there can be a great reduction in the number of individual parts or components. Other resin molded parts are rapidly finding their way in the consumer field as casings or housings for small appliances and in the business world as business machine housings and cabinets.
It is known that the resin component of the molding compounds is an expensive ingredient and adds to the cost of the finished product in greater proportion than any other ingredient. Thus, it is well-known technique to add fillers of various kinds to the resin to replace much of the resin with a view to economy. Obviously, for the same physical characteristics of a given molding compound, the greater the amount of filler, the more economical will be the ultimate product. Conversely, if, for the same amount of filler, a given filler will impart improved molding properties to the resin compound, for the same cost, greater flexibility in molding technique will be found. In other instances improvement in molding properties by a suitable filler will result in greater penetration of the resin compound into reinforcing ingredients such as glass fibers or filamentary mats.
SUMMARY OF THE INVENTION
This invention relates to a novel filler for resin compounds.
It is an object of the present invention to provide a novel resin compound filler which will permit increased production of compound with a reduction in the more costly resin component without reduction of molding properties.
It is another object of the present invention to provide a novel resin compound filler which will extend a given amount of resin to make more compound.
It is yet another object of the present invention to provide a novel resin compound filler which will produce enhanced molding properties with the same amount of filler.
It is still another object of the present invention to provide a novel resin filler which will provide improved properties in the final molded product without additional resin.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The following examples will show that
(A) FOR A GIVEN AMOUNT OF RESIN, THE AMOUNT OF THE NOVEL FILLER OF THE INVENTION IN THE COMPOUND CAN BE DRAMATICALLY INCREASED FOR THE SAME VISCOSITY. In this instance, viscosity will be used as a constant, as viscosity will, to a great extent, determine the workability of the resin compound, and
(B) FOR A PREDETERMINED VISCOSITY, THE AMOUNT OF THE NOVEL FILLER OF THE INVENTION CAN BE INCREASED OVER COMPARABLE FILLERS TO SAVE MONEY OR TO IMPROVE THE PHYSICAL CHARACTERISTICS OF THE FINAL MOLDED PRODUCT.
In addition, the versatility of the novel filler of the invention will be shown by the fact that it imparts the improved results in various types of molding compounds and with various techniques of preparing molding compounds.
In the following examples, many of the ingredients will be referred to by their common trade names. Appended to the end of the description is an Exhibit A which will completely identify those ingredients. Exhibit A has subparts A1 (Polyester resins), A2 (Peroxide catalysts). For purposes of this disclosure, the novel calcium carbonate filler of the invention will be referred to as Gama-Sperse LV-10 as made by The Georgia Marble Company of Atlanta, Georgia. Exhibit C describes the calcium carbonate fillers. Other ingredients will be referred to by their common chemical names, and for completeness, Exhibit B is attached hereto to show other chemicals named in this invention and how they are utilized.
Before explaining the various examples cited hereinafter in terms of the improved filler of the invention, a short explanation of the techniques of resin molding is deemed to be helpful. There are two general techniques for resin molding; one is making a bulk molding compound, and the other a sheet molding compound. The bulk molding compound is a mixture of polyester resin, mineral filler, catalyst, mold release, colorants (optional), thickeners (optional) and generally 1/4" chopped glass fibers or sisal fibers.
The mixture is prepared commercially in batch mixers; commonly a Baker-Perkins spiral blade or sigma blade mixer.
Any order of addition of ingredients may be followed, except that the reinforcing glass is generally added last. The bulk molding compound resembles wet grass or a paste mass with fibers prominent throughout. It may be compressed by extrusion into a rope-like form. Pieces of the rope of compound are cut or pulled from the bulk and placed in the mold. Fillers aid in flow control and help carry fibers to all parts of the part.
The sheet molding compound is a mixture of polyester resin, filler, catalyst, mold release, colorant (optional), thickener (necessary) and generally 1"-2" chopped glass fibers. The material is prepared in a manner to give a large flat sheet of molding compound. A "maturation" period is required for the thickener [MgO or Mg(OH).sub.2 ] to chemically thicken the polyester resin after it is formed into the sheet. This period is 48 hours to 7 days.
The molding compound is generally deposited on a polyethylene sheet as a paste in suitable thickness. Chopped glass is then distributed over the exposed paste as the sheet is moved over a conveyor belt. A second polyethylene sheet has the molding compound as a paste distributed over its underside. The two paste layers are brought together and the outer sheets are run between compacting rollers. The sandwich of sheet molding compound encased between the two polyethylene sheets is rolled up for packaging.
For molding, the sheet molded compound is unrolled and the films or sheets removed. A flexible, leathery sheet of molding compound is obtained. This is cut, weighed, stacked or rolled and placed in the mold.
Sheet molded compound generally has less filler than bulk molded compound since it must be of lower viscosity in order to penetrate and set the chopped glass fibers. Poor wetting of fibers results in delamination and defects in molded parts. Viscosity of sheet molded compound paste is a critical issue in sheet molded compound operations.

Having now explained the environment in which the filler is used, the following examples will be more specific.
EXAMPLE 1
A mixture (Example 1A) comprising 100 parts of Paraplex P-340 resin and 150 parts of Gama-Sperse 6451 filler was blended thoroughly with a paddle mixer. The time required to completely disperse the solid was 5 minutes. The viscosity of the resulting paste by Brookfield Helipath Viscometer was 35,000 cps. A similar mixture (Example 1B) comprising 100 parts of Paraplex P-340 and 150 parts of Gama-Sperse 6532 formed a homogeneous paste in 5 minutes with a viscosity of 50,000 cps. A similar mixture (Example 1C) comprising 100 parts of Paraplex P-340 and 150 parts of Camel-Wite dispersed in 5 minutes and the paste had a viscosity of 43,000 cps. A similar mixture (Example 1D) of 100 parts of Paraplex P-340 and 150 parts of Gama-Sperse LV-10 dispersed in 2 minutes and the paste viscosity was 22,000 cps. In the above examples, the mixing was carried on until complete dispersion of ingredients occurred.
______________________________________ Time to Parts by Disperse Viscosity Weight minutes cps______________________________________Example 1AResin 100Gama-Sperse 6451 filler 150 5 35,000Example 1BResin 100Gama-Sperse 6532 filler 150 5 50,000Example 1CResin 100Camel-Wite filler 150 5 43,000Example 1DResin 100Gama-Sperse LV-10 filler 150 2 22,000______________________________________
From this example, it is clear that the time for dispersal of the novel filler (Gama-Sperse LV-10) was 2 minutes, or less than 1/2 that of the other fillers and the viscosity was 22,000 cps. or about two thirds that of the next best filler. Thus, for the same loading, the novel filler of the invention not only cut the compounding time in about one half, but produced a compound with a sharply reduced viscosity. The wetting power and workability was increased markedly.
EXAMPLE 2
A sheet molding compound paste (Example 2A) comprising 100 parts of Glidpol 4297, 1 part of t-butyl perbenzoate, 150 parts of Gama-Sperse 6451, 2.5 parts of zinc stearate and 2.0 parts of magnesium hydroxide was blended thoroughly in a high shear mixer. The viscosity of the resultant paste was 37,000 cps. A similar paste (Example 2B) comprising 100 parts of Glidpol 4297, 1 part of t-butyl perbenzoate, 175 parts of Gama-Sperse LV-10, 2.5 parts of zinc stearate and 2.0 parts of magnesium hydroxide had a viscosity of 36,500 cps.
______________________________________ Parts by Viscosity Weight cps______________________________________Example 2A 100Glidpol 4297 resin 100t-butyl perbenzoate (catalyst) 1Gama Sperse 6451 (filler) 150Zinc Stearate 2.5Magnesium hydroxide 2.0 37,000Example 2BGlidpol 4297 resin 100t-butyl perbenzoate (catalyst) 1Gama-Sperse LV-10 175Zinc stearate 2.5Magnesium hydroxide 2.0 36,500______________________________________
From this example, it is seen that to achieve substantially the same viscosity of the compound, the loading of the novel filler of the invention was significantly higher, in fact, about 16% higher. Thus, for a given amount of resin (100 parts) a greater quantity of compound can be made. Thus, an economic gain is involved.
EXAMPLE 3
A sheet molding compound paste (Example 3A) comprising 100 parts of Paraplex P-19D, 150 parts of Gama-Sperse 6451, 1 part of t-butyl perbenzoate, 2 parts zinc stearate and 1 part magnesium hydroxide was blended for 8 minutes in a Baker-Perkins sigma blade mixer until a smooth paste was obtained. The viscosity of the paste by Brookfield Helipath Viscometer was 60,000 cps. at 98.degree. F. A similar paste (Example 3B) comprising 100 parts of Paraplex D-19D, 200 parts of Gama-Sperse LV-10, 1 part of t-butyl perbenzoate, 2 parts of zinc stearate and 1 part of magnesium hydroxide formed a smooth paste in 5 minutes which had a viscosity of 62,000 cps at 97.degree. F.
______________________________________ Time of Parts by Blending Viscosity Weight Minutes cps______________________________________Example 3AParaplex P-19D resin 100Gama Sperse 6451 150t-butyl perbenzoate 1zinc stearate 2Magnesium hydroxide 1 8 60,000Example 3BParaplex P-19D resin 100Gama-Sperse LV-10 200t-butyl perbenzoate 1Zinc stearate 2Magnesium hydroxide 1 5 62,000______________________________________
It is clear that again a greater quantity of the novel filler of the present invention was used for a fixed amount of resin to make a compound with substantially the same viscosity. It should be noted that the amount of time to blend the compound was remarkedly reduced.
EXAMPLE 4
The pastes described in Example 3 were used to prepare 20% glass reinforced sheet molding compound by impregnation of a single ply of glass mat composed of 1 inch glass fiber strands. The impregnated mat was rolled between polyethylene films and stored for 96 hours. During this time a chemical thickening of the polyester resin by the magnesium hydroxide occurred. When the films were removed from the impregnated mat, a flexible, non-sticky sheet of molding compound was obtained. This was cut into 6 inch.times. 6 inch squares. Five plys of the thickened sheet molding compound sheet were used to form a test sample, which was molded in a two-piece, matched metal mold at 325.degree. F. for 3 minutes. Test pieces were cut from the molded sample for a comparison of physical properties of sheet molding compound made by each of the formulations given in Example 3.
______________________________________Physical Properties of Sheet Molding Compound 150 pbw 200 pbwProperties Gama-Sperse 6451 Gama-Sperse LV-10______________________________________Flexural Strength.sup.(1) 20,000 psi 23,000 psiFlexural Modulus.sup.(1) 1.79 .times. 10.sup.6 psi 1.9 .times. 10.sup.6 psiImpact Strength.sup.(2) 9.7 ft-lbs/inch 10.7 ft-lbs/inch(notched)Barcol Hardness.sup.(3) 58 60______________________________________ .sup.(1) ASTM D-790 .sup.(2) ASTM D-256 .sup.(3) Barcol Impressor - Barber-Colman Co. Rockford, Illinois
From Example 4 it is seen that when about 33% more of the novel compound of the invention was used there was an increase in the flexural strength, the flexural modulus and impact strength. Again the amount of resin for the same quantity of molding compound was reduced with the filler of the invention as compared to the other filler.
EXAMPLE 5
A bulk molding compound paste prior to the addition of colorant and reinforcing fiber (Example 5A) comprising 100 parts Paraplex P-19P, 1 part t-butyl perbenzoate, 200 parts Gama-Sperse 6451 and 3 parts of zinc stearate was mixed for 10 minutes in a spiral blade mixer until a smooth paste was formed. The viscosity of the paste was found to be 900,000 cps at 77.degree. F. by Brookfield Helipath Viscometer. A similar paste (Example 5B) comprising 100 parts of Paraplex P-19P, 1 part t-butyl perbenzoate, 245 parts of Gama-Sperse LV-10 and 3.0 parts of zinc stearate formed a smooth paste in less than 8 minutes with a viscosity of 950,000 cps at 77.degree. F.
______________________________________ Time of Parts by Blending Viscosity Weight Minutes cps______________________________________Example 5AResin 100t-butyl perbenzoate 1Gama-Sperse 6451 200Zinc stearate 3 10 900,000Example 5BResin 100t-butyl perbenzoate 1Gama-Sperse LV-10 245Zinc stearate 3 8 950,000______________________________________
For an increased loading of the novel filler of the invention (about 23% greater) the blending time was reduced by 20% and the viscosity was substantially unchanged in comparison to the more conventional filler.
EXAMPLE 6
An automotive grade sheet molding compound paste (Example 6A) comprising 60 parts of Stypol 40-2955, 33 parts of LP-40A, 7 parts styrene, 1 part t-butyl perbenzoate, 150 parts of Gama-Sperse LV-10, 4 parts zinc stearate and 1 part magnesium oxide was prepared in a Hobart mixer. The paste had a Brookfield Helipath viscosity of 45,000 cps. A glass fiber mat was impregnated with the paste and rolled between polyethylene films. A similar paste (Example 6B) was prepared except that 150 parts of Gama-Sperse 6532 was used in place of Gama-Sperse LV-10. The viscosity of the paste was 67,000 cps. A glass fiber mat was impregnated with this paste and rolled between polyethylene films. After 72 hours, the impregnated mats were unrolled and examined for completeness of glass mat impregnation and molding quality.
______________________________________ Parts by Viscosity Weight cps______________________________________Example 6AStypol 40-2955 resin 60LP-40A 33Styrene 7t-butyl perbenzoate 1Gama-Sperse LV-10 150Zinc stearate 4Magnesium oxide 1 45,000Example 6BStypol 40-2955 resin 60LP-40A 33Styrene 7t-butyl perbenzoate 1Gama Sperse 6532 150Zinc stearate 4Magnesium oxide 1 67,000______________________________________
The sheet molding compound paste prepared using Gama-Sperse LV-10 completely wetted the glass fiber mat due to the ability of the low viscosity paste to spread over the surface of the reinforcing fibers. Conversely, the higher viscosity paste prepared using Gama-Sperse 6532 did not wet all of the glass fibers in the mat, although the same volume of paste was applied in both preparations. Matched metal die moldings of these sheet molding compounds at 325.degree. F. showed smooth, uniform surface appearance for the sheet molding compound prepared with Gama-Sperse LV-10, while the sheet molding compound prepared with Gama-Sperse 6532 resulted in pits and numerous small blisters on the surface of molded articles due to poor resin distribution. The lower viscosity of the LV-10 greatly facilitated processing of polyester molding compound.
EXAMPLE 7
A wet mat molding compound comprising 100 parts of Stypol 40-2364, 0.5 part benzoyl peroxide, 125 parts Gama-Sperse 6532 and 0.7 part calcium stearate was blended in a Cowles Dissolver for 10 minutes. The viscosity as recorded by a Brookfield Viscometer was 54,000 cps. at 77.degree. F. A similar composition comprising 100 parts of Stypol 40-2364; 0.5 part benzoyl peroxide, 170 parts of Gama-Sperse LV-10 and 0.7 part calcium stearate was found to have a viscosity of 55,000 cps.
In this Example 7, an increased amount of the novel filler of the invention (170 parts by weight) was used in place of the conventional filler (125 parts by weight) and yet the viscosity was substantially the same.
The following data will differentiate the various calcium carbonate powders used in the examples by particle size distribution, by surface area measurements, by sub-sieve size analysis, and by pore volume analysis. From this information, the unique calcium carbonate filler of the invention can be described and claimed.
Table 1______________________________________Camel-WiteHarry T. Campbell Sons CorporationTowson, Baltimore, MarylandParticle Size Distribution determined by Sedigraph 5000(Instrument distributed byMicrometrics Instrument CorporationNorcross, Georgia Diameter*Cumulative (Microns,Mass Percent finer than Micrometers)______________________________________100 1895 1390 1085 8.680 7.475 6.470 5.665 5.060 4.455 4.050 3.545 3.240 2.735 2.330 2.025 1.720 1.415 1.210 0.925 0.602 0.400 0.20______________________________________ *Actual Sedigraph curve
Table 2______________________________________Gama-Sperse 6451(The Gerogia Marble CompanyAtlanta, Georgia) Particle Size distribution - Sedigraph 5000 TypicalCumulative Diameter** ValueMass Percent finer than (Microns, Micrometers)______________________________________100 2095 1690 1385 11.580 10.375 9.270 8.465 7.560 6.755 6.050 5.445 4.640 4.035 3.530 2.925 2.320 1.915 1.4510 1.055 0.702 0.460 0.20______________________________________ **Published Values
Table 3______________________________________Gama-Sperse 6532(The Georgia Marble Company)Atlanta, Georgia)Particle Size Distribution - Sedigraph 5000 TypicalCumulative Diameter** ValueMass Percent finer than (Microns, Micrometers)______________________________________100 1395 9.290 8.085 7.080 6.275 5.670 5.065 4.660 4.155 3.650 3.245 2.840 2.535 2.130 1.825 1.520 1.215 0.9610 0.725 0.462 0.290 0.20______________________________________ **Published Values
Table 4______________________________________Gama-Sperse LV-10(The Georgia Marble CompanyAtlanta, Georgia)Particle Size Distribution - Sedigraph 5000Cumulative Diameter Range*Mass Percent finer than (Microns, Micrometers)______________________________________100 20-2295 17-1890 15-1785 14-1680 13.5-1575 13.0-1470 12.0-13.565 11.5-13.360 11.0-13.055 10.0-12.550 9.8-12.045 9.0-11.540 8.0-10.535 6.8-10.030 5.1- 8.025 5.0-5.820 2.5-3.515 1.7-2.210 1.0-1.25 0.55-0.652 0.35-0.400 0.20-0.20______________________________________ *By actual measurement
From these tables it can be seen that at a given cumulative mass percent, the particle size of the calcium carbonate filler of the present invention is greater than for any of the other fillers used. A few examples will make this clear.
______________________________________ Finer than Gama- Gama-Cumulative Gama-Sperse Sperse Sperse Camel-Mass LV-10 6532 6451 WitePercent (Microns) (Microns) (Microns) (Microns)______________________________________100 20-22 13 20 1880 13.5- 15 6.2 10.3 7.450 9.8- 12 3.2 5.4 3.530 5.1-8 1.8 2.9 2.0______________________________________
Porosimetry
Pore Volume Analysis
A mercury penetration porosimeter Model 905, Micromeritics Instrument Corp. was employed to determine the pore volume of selected calcium carbonate fillers. Pore volume analyses indicate that calcium carbonate fillers have non-porous surfaces. The porosity values actually are void volume determinations arising from the spaces between particles in packed powders. The void volume is a function of the packing arrangement of the variously sized particles in a powder. Lower values indicate a more complete packing of particles such as indicated by the lower value obtained for LV-10 due to the unique particle size distribution.
______________________________________ Porosity (%)______________________________________Camel-Wite 64.21Gama-Sperse 6451 55.12Gama-Sperse LV-10 52.87 (below 53)______________________________________
From this data, it is clear that the novel calcium carbonate filler of the invention has a porosity percentage below 53.
Fisher Sub-Sieve Sizer
Characterization of calcium carbonate fillers by Fisher Sub-Sieve Sizer. This device is commonly employed in the filler industry as a quality control tool and to differentiate mineral filler products in the size range of 0.2 microns to 50 microns. The instrument employs the air permeability principle in determining the average diameter of particles in a sample. The instrument may be purchased from Fisher Scientific Co., Pittsburgh, Pennsylvania.
The following values are used to characterize (in part) the fillers mentioned:
______________________________________ Sub-Sieve Diameter (Microns)______________________________________Gamma-Sperse 6532 1.60-1.80Gamma-Sperse 6451 1.90-2.20Gamma-Sperse LV-10 2.60-2.90Camel-Wite avg. 2.0______________________________________
Comment
Gama-Sperse LV-10 has a larger average particle diameter than other fillers in the same size range due to the unusual particle size distribution.
Surface Area
Characterization of calcium carbonate fillers by specific surface measurements. The Model 2205 Automatic Surface Area Analyzer, Micromeritics Instrument Corp. was designed for low surface area materials with specific surface areas from 0.2 m.sup.2 /gram to 100 m.sup.2 /gram. The unit employed for these measurements uses Argon gas as the adsorbate, and is particularly useful in the range of 0.5 m.sup.2 /gram to 5.m.sup.2 /gram.
______________________________________ Approximate Specific Surface Area (Square Meters/gram)______________________________________Gama-Sperse 6532 2.80Gama Sperse 6451 2.70-2.60Gama Sperse LV-10 1.75-2.00Camel-Wite 2.76______________________________________
While all these fillers have low specific surface areas, Gama-Sperse LV-10 has specific surface area at or below 2.0 m.sup.2 /gram. This is due to the unusual particle size distribution and is not characteristic of fillers in this size range.
In summary, the present invention describes and claims a novel calcium carbonate filler with a particle size distribution as determined by a Sedigraph 5000 analyzer to be within a given range having a limited pore volume porosity, having a range of average particle sizes and having a surface area in square meters per gram different from other calcium carbonate fillers. The physical properties as determined by measurement define a calcium carbonate filler which has unusual properties resulting in improved molding compounds, in less expensive molding compounds and molding compounds with better molding properties.
POLYESTER RESIN
Paraplex P-19D
Rohm and Haas
Type: Two-component, low-shrink polyester resin system consisting of:
60% Paraplex P-340 highly reactive polyester resin, styrene monomer.
40% Paraplex P-701 acrylic polymer dissolved in styrene monomer.
The above ratio is recommended for minimum shrinkage.
Uses: Suitable for mat, preform, premix, bulk molding compound and sheet molding compound molding where surface smoothness is required.
______________________________________Typical Properties (uncured resin)______________________________________P-340Viscosity at 25.degree. C. 970 cps% solids 65.9Specific Gravity 1.120-1.140SPI gel time at 180.degree. F. 6-9 minutesSPI peak exotherm 458.degree. F.Acid number 22.5P-701Viscosity at 25.degree. C. 1400 cp% solids 33.3Specific Gravity 0.980______________________________________
Glidpol 4297*
Glidden-Durkee
Type: Single-component, low-shrink polyester, styrene monomer.
Uses: Low profile molding system recommended for bulk molding compound, sheet molding compound, and wet molding process.
______________________________________Typical Properties (uncured resin)______________________________________Viscosity at 77.degree. F. 1100-1400 cps.Weight per gallon 8.76 lbs.SPI gel time 180.degree. F. 12.0 minutesSPI peak exotherm 425.degree. F.______________________________________
Typical Properties (cured resin)
(None listed)
*All data from Manufacturer's product bulletin.
Paraplex P-19P
Rohm and Haas
Type: Two-component, pigmentable, low-shrink polyeater resin consisting of:
60% Paraplex P-340 highly reactive polyester resin, styrene monomer.
40% Paraplex P-713 acrylic polymer syrup dissolved in styrene monomer.
The above ratio is recommended for minimum shrinkage.
______________________________________Typical Properties (uncured resin)______________________________________P-340Viscosity at 25.degree. C. 970 cps.% solids 65.9Specific gravity 1.120SPI gel time 180.degree. F. 9.6 minutesSPI peak exotherm 450.degree. F.P-713Viscosity at 75.degree. C. 1550 cps.% solids 29.5Specific Gravity 0.950______________________________________
Stypol 40-2955*
Freeman Chemical Corp.
Type: Isophthalic polyester, styrene monomer.
Uses: Rigid resin for compression molding sheet molding compound, premix, preform and mat low profile parts where a special "low profile additive" is incorporated into the formulation.
______________________________________Typical Properties (uncured resin)Specific gravity 1.115Viscosity at 25.degree. C. 1700 cps (Brookfield)SPI gel time at 180.degree. F 5.5 minutesSPI peak exotherm 425.degree. F.Typical properties (cured resin)Barcol hardness 49Heat distortion point 126.degree. C. (264 psi)Specific Gravity 1.190______________________________________
*All data from Manufacturer's product bulletin.
LP-40A
Union Carbide Corp., New York, N.Y.
Type: Thermoplastic acrylic polymer dissolved in styrene monomer.
Uses: A special "low-profile additive" for polyester molding compositions where shrinkage is to be minimized.
______________________________________Typical Properties (uncured resin)Viscosity at 25.degree. C. 4250 cps% solids 40______________________________________
Stypol 40-2364*
Freeman Chemical Corp., Port Washington, Wis.
Type: Isophthalic Polyester, styrene monomer.
Uses: Medium reactive resilient resin for matched metal die molding and premix molding.
______________________________________Typical Properties (uncured resin)Specific Gravity 1.152Viscosity at 25.degree. C. 2850 cps (Brookfield)SPI gel time 180.degree. F. 6.5 minutesSPI peak exotherm 415.degree. F.Typical Properties (cured resin)Barcol hardness 41Heat distrotion point 77.degree. C. (264 psi)Specific Gravity 1.20______________________________________
*All data from Manufacturer's product bulletin.
PEROXIDE CATALYSTS
Tert.-Butyl Perbenzoate (Peroxybenzoate)
Pennwalt Lucidol Chemicals
Type: Peroxide type catalyst, good stability. Heat activated. decomposition into free radicals.
Use: Widely used in matched die molding (prepreg, preform, sheet molding compound, bulk molding compounds) of polyester resin systems.
Properties: Liquid 98% active ingredient.
Typical use is in polyester molding compound but other peroxides may be used to cure polyester molding compositions:
e.g. Benzoyl peroxide (Example 7)
2,4-dichlorbenzoyl peroxide
2,5-dimethyl-2,5-Bis (Benzoylperoxy) Hexane
tert.-Butyl hydroperoxide
COMMON CHEMICAL RESINS
Polyester resin--linear polyesters containing unsaturation which provides sites for subsequent cross-linking reactions. Prepared by the condensation reaction of a diol with a mixture of an unsaturated dibasic acid and a saturated dibasic acid (or corresponding anhydrides of same). The linear polyesters are commonly dissolved in liquid vinyl monomers which, upon initiation, serve as cross-linking agent. Monomers reduce viscosity and facilitate the impregnation of substrates and wetting of fillers and reinforcing in the preparation of molding compositions.
e.g. - diol - propylene glycol, ethylene glycol, diethylene glycol, neopentylene glycol.
- unsaturated dibasic acid or anhydride - maleic acid, maleic anhydride, fumaric acid, chlorofumaric acid.
- saturated dibasic acid or anhydride - phthalic acid, phthalic anhydride, adipic acid, "nadic" anhydride, sebacic acid.
Vinyl monomers--Styrene, methyl methacrylate, vinyl toluene, diallyl phthalate, triallyl cyanurate (or mixtures of above).
OTHER INGREDIENTS
Initiators of cross-linking reaction--Generally comprising that group of substances known as peroxy and hydroperoxy compounds which rapidly decompose into free radicals.
Methyl ethyl ketone peroxide, cyclohexanone peroxide, benzoyl peroxide, tert.-butyl perbenzoate, cumene hydroperoxide.
Activators (accelerators) are often used in order to speed up the decomposition of the peroxy initiator.
e.g.--Salts of metals: cobalts, cerium, iron, manganese, tin, vanadium such as the naphthenates and octoates; and tertiary amine compounds: dimethylaniline, diethylaniline, dimethyl-p-toluidine.
PROCESSING--GENERAL
Polyester resins are useful in the preparation of laminates, and in various kinds of molding compounds which are subsequently formed into shapes by a variety of molding techniques.
MOLDING COMPOUND
Essentially a mixture of polyester resin, filler, catalyst, a mold release agent and some form of reinforcement such as glass fiber. Colorants and many other specialty ingredients are frequently combined with the above mixture. It may be conveniently prepared in a spiral blade or sigma blade mixer by blending various combinations of the above ingredients to a dough-like consistency, (bulk molding compound). Other methods of preparation include the formation of a paste comprising all but the reinforcement, which is added in a subsequent step to produce a thin layer between sheets of nonpermeable films, (sheet molding compound).
______________________________________CALCIUM CARBONATE FILLERS______________________________________Physical Data of Camel-Wite CumulativeParticle Size Distribution Mass PercentFiner than 40 microns --30 microns --25 microns --20 microns --10 microns --8 microns 100%6 microns 845 microns 784 microns 702 microns 50Physical Data Camel-WiteSpecific Gravity 2.80-2.71One lb. bulk (gallons) 0.0443Wt. per Solid Gal. (lbs.) 22.57pH of Saturated Sol. 9.5Index of Refraction 1.6Oil Absorption (lbs./100 lbs.) 15Average Particle Dia. 2.0 micronsParticle Range 0.3 to 8.0 micronsDry Brightness (G.E. 550 Ang.) 96Bulk Density (Loose) (lbs./cu./ft.) 40Solubility in water (%) 0.08Moh Hardness 3.0______________________________________Physical Data of Gama-Sperse LV-10, Gama-Sperse 6532,Gama-Sperse 6451Gama-Sperse LV-10 has been designed for use in liquid Polyestersystems. It is a finely ground Calcium Carbonate with lessthan .008% being retained on a U.S. 325 Wet Screen.______________________________________Hardness (Moh's scale) 3.0Specific Gravity 2.71Typical Chemical Composition:Total Carbonates (Ca,Mg) 95.0% MinimumMgCO.sub.3 3.0 MaximumAl.sub.2 O.sub.3 0.1% to 0.35%Fe.sub.2 O.sub.3 .02% to .16%SiO.sub.2 .02% to 1.4%Mn Trace______________________________________

Calcium carbonate filler

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims