Patent Grant
7094282
The present invention is related to a calcium phosphate cement, and in particular a fast-setting calcium phosphate cement, for use in dental and bone prosthesis.
A calcium phosphate cement (abbreviated as CPC) has been widely used as an implant or filling material in dental and bone prosthesis, and its technical details can be found in many patents, for examples U.S. Pat. Nos. 4,959,104; 5,092,888; 5,180,426; 5,262,166; 5,336,264; 5,525,148; 5,053,212; 5,149,368; 5,342,441; 5,503,164; 5,542,973; 5,545,254; 5,695,729 and 5,814,681. In general, the prior art calcium phosphate cements suffer one or more drawbacks as follows: 1) additives having a relatively poor bioactivity being required; 2) a complicated preparation process; 3) an undesired setting time or working time of CPC, which are difficult to be adjusted; 4) not capable of being set to a desired shape in water, blood or body fluid; and 5) poor initial strength after setting of the CPC.
An object of the present invention is to provide a calcium phosphate cement.
Another object of the present invention is to provide a calcium phosphate cement comprising particles having whiskers or fine crystals on surfaces of the particles.
Still another object of the present invention is to provide a process for preparing a calcium phosphate cement.
A further object of the present invention is to provide a method of treating a bone or a tooth having a defect in a patient by using a calcium phosphate cement.
In order to accomplish the above objects of the present invention a calcium phosphate cement prepared in accordance with the present invention comprises calcium phosphate particles having a diameter of 0.05 to 100 microns, wherein said calcium phosphate particles on their surfaces have whiskers or fine crystals having a width ranging from 1 to 100 nm and a length ranging from 1 to 1000 nm. By adjusting the diameter of the calcium phosphate particles, the width and/or the length of the whiskers or fine crystals, the inventors of the present invention are able to adjust the working time and/or the setting time of the calcium phosphate cement of the present invention to conform to requirements for various purposes. Moreover, the calcium phosphate cement of the present invention is fast-setting, and is non-dispersive in water or an aqueous solution.
a to 5c are photographs showing a conventional CPC paste injected into water via a syringe at 3, 10 and 30 seconds after the conventional CPC paste being formed.
a to 6c are photographs showing a CPC paste of the present invention injected into water via a syringe at 3, 10 and 30 seconds after the CPC paste being formed in accordance with the following Example 7.
a to 7c are photographs showing two cylinders prepared by separately molding a conventional CPC paste and a CPC paste of the present invention prepared in the following Example 7, which were taken at 5, 20 and 60 seconds after the two cylinders being immersed in the water.
A suitable process for preparing the calcium phosphate cement of the present invention comprises mixing a calcium phosphate powder or small pieces of calcium phosphate with a wetting agent, and controlling growth of whiskers or fine crystals on surfaces of said calcium phosphate powder or small pieces of calcium phosphate by an controlling treatment.
Suitable calcium phosphates for use as the calcium phosphate powder or small pieces of calcium phosphate in the present invention can be any known calcium phosphates such as calcium dihydrogen phosphate, calcium dihydrogen phosphate hydrate, acid calcium pyrophosphate, anhydrous calcium hydrogen phosphate, calcium hydrogen phosphate hydrate, calcium pyrophosphate, calcium triphosphate, calcium polyphosphate, calcium metaphosphate, anhydrous tricalcium phosphate, tricalcium phosphate hydrate, apatite, hydroxyapatite, a mixture thereof and an adduct thereof. Moreover, the shape of the calcium phosphate powder and the shape of the small pieces of calcium phosphate are not limited, which can be spherical or irregular; and the crystal structure thereof can be single crystal, polycrystal, mixed crystals, semi-crystal, or amorphous.
The process for preparing the calcium phosphate cement preferably further comprises grinding the resulting product from the controlling treatment to form calcium phosphate particles having a diameter of 0.05 to 100 microns, wherein said whiskers or fine crystals have a width ranging from 1 to 100 nm and a length ranging from 1 to 1000 nm.
Said controlling treatment is a vacuuming treatment, an organic solvent treatment, a microwave treatment, a heating treatment, or any other treatments which can controll growth of whiskers or fine crystals on surfaces of said calcium phosphate powder or small pieces of calcium phosphate.
Said wetting agent is used to wet the calcium phosphate powder or small pieces of calcium phosphate, and preferably is a diluted aqueous solution containing phosphoric acid or phosphate. The amount of said wetting agent mixed with the calcium phosphate powder or small pieces of calcium phosphate, in general, should be enough to wet substantially all the calcium phosphate powder or small pieces of calcium phosphate. However, it is not necessarily the case when said controlling treatment is the organic solvent treatment, where a water miscible organic solvent is added to the mixture of said wetting agent and said calcium phosphate powder or small pieces of calcium phosphate to form a paste for a subsequent processing step.
Preferably, said wetting agent is a diluted aqueous solution containing more than 20 ppm of phosphoric acid or phosphate, more preferably more than 50 ppm, and most preferably more than 100 ppm of phosphoric acid or phosphate.
Preferably, the process for preparing the calcium phosphate cement of the present invention comprises soaking said calcium phosphate powder or said small pieces of calcium phosphate with said diluted aqueous solution containing more than 100 ppm of phosphoric acid or phosphate, and carrying out (a) said heating treatment comprising drying the resulting soaked calcium phosphate powder or soaked small pieces of calcium phosphate at a temperature higher than 45° C.; (b) said vacuuming treatment comprising drying the resulting soaked calcium phosphate powder or soaked small pieces of calcium phosphate under vacuum; or (c) said microwave treatment comprising drying the resulting soaked calcium phosphate powder or soaked small pieces of calcium phosphate by microwave heating. More preferably, the resulting soaked calcium phosphate powder or soaked small pieces of calcium phosphate is well mixed to form a uniform mixture prior to being subjected to treatment (a), (b) or (c).
Alternatively, the process for preparing the calcium phosphate cement of the present invention comprises mixing said calcium phosphate powder or said small pieces of calcium phosphate with said diluted aqueous solution containing more than 100 ppm of phosphoric acid or phosphate, and carrying out said organic solvent treatment comprising mixing the mixture of said wetting agent and said calcium phosphate powder or small pieces of calcium phosphate with a water miscible organic solvent, and drying the resulting mixture under vacuum. Preferably, said organic solvent treatment is carried out while stirring, and more preferably, the mixture of said diluted aqueous solution containing more than 100 ppm of phosphoric acid or phosphate and said calcium phosphate powder or small pieces of calcium phosphate is well mixed prior to being subjected to said organic solvent treatment.
Preferably, said calcium phosphate particles of the calcium phosphate cement of the present invention have a diameter of 0.2 to 80 microns, and more preferably 0.5 to 50 microns.
The width of a whisker means an average value of lateral cross-sectional diameters of the whisker, and the width of a fine crystal means an average value of the first 30% of the diameters of the fine crystal, which are shorter than the other 70% thereof. The length of a fine crystal means an average value of the last 30% of the diameters of the fine crystal, which are longer than the other 70% thereof.
Preferably, said whiskers or fine crystals have a width ranging from 2 to 70 nm and a length ranging from 5 to 800 nm, and more preferably a length ranging from 10 to 700 nm.
Preferably, said calcium phosphate particles have a molar ratio of calcium to phosphate ranging from 0.5 to 2.5, more preferably 0.8 to 2.3, and most preferably 1.0 to 2.2.
The calcium phosphate cement of the present invention is biocompatible and a paste made therefrom is non-dispersive in water, which has a working time from several minutes to hours and a setting time from a few minutes to hours. Consequently, the calcium phosphate cement of the present invention is extremely suitable for use as an implant or filling material in dental or bone prosthesis, where the paste must contact water, blood or body fluid. Particularly, the paste made from the calcium phosphate cement of the present invention is able to be directly injected into a bone defect or cavity as an implant or filling material.
The present invention also discloses a method of treating a bone or a tooth having a defect in a patient, comprising mixing the calcium phosphate cement of the present invention and a hardening-promoter-containing aqueous solution to form a paste, and a) injecting said paste into a bone defect or cavity of said patient or b) shaping said paste and implanting the resulting shaped paste into a bone defect or cavity of said patient.
In the method of the present invention, said calcium phosphate cement may further comprise a growth factor, a bone morphology protein or a pharmaceutical carrier, or said hardening-promoter-containing aqueous solution further comprises a growth factor, a bone morphology protein or a pharmaceutical carrier.
Said hardening-promoter-containing aqueous solution can be an aqueous solution comprising any known compounds or compositions which enable the solidification of calcium phosphate, for examples phosphates, calcium salts, and fluorides. That is said hardening-promoter-containing aqueous solution may be an aqueous solution comprising phosphate ions, calcium ions, fluorine ions, or phosphate ions together with fluorine ions as a hardening promoter.
The content of said hardening promoter in said hardening-promoter-containing aqueous solution has no special limitation, but preferably ranges from 1 mM to 3 M, and more preferably from 10 mM to 1 M.
The mixing ratio of the calcium phosphate cement of the present invention and said hardening-promoter-containing aqueous solution is not restricted to any particular ranges; however, the amount of said hardening-promoter-containing aqueous solution mixed should be sufficient to provide substantial wetting of the calcium phosphate cement of the present invention. It should be noted that more water can be supplied in-situ from saliva or body fluid, when the paste is injected or implanted into the bone defect or cavity. Further, the content of said hardening promoter in said hardening-promoter-containing aqueous solution should be adjusted to a higher level corresponding to a less amount of said hardening-promoter-containing aqueous solution being mixed.
5 g of Ca(H2PO4)2.H2O powder and 1.6 ml of 25 mM phosphoric acid aqueous solution were mixed, and stirred for one minute. The resulting mixture was placed into an oven at 50° C. for 15 minutes, and the resulting dried mixture was mechanically ground for 20 minutes to fine particles after being removed from the oven. 1 g of the fine particles and 0.4 ml of phosphate aqueous solution (1.0 M, pH=6.0) were mixed to form a paste, which was tested every 30 seconds to determine the working time and the setting time. The setting time is the time required when a 1 mm diameter pin with a load of ¼ pounds can be inserted only 1 mm deep into the surface of the paste. The working time is the time after which the paste is too viscous to be stirred. The working time of the paste of this example is 30 minutes and the setting time thereof is one hour.
The paste was placed in a relatively large amount of deionized water immediately following the formation thereof, and it was observed that the paste was non-dispersive in deionized water.
5 g of CaHPO4 (DCPA) powder and 1.2 ml of 25 mM phosphoric acid aqueous solution were mixed, and stirred for one minute. The resulting mixture was placed in a vacuum environment of −100 Pa for 30 minutes, and the resulting dried mixture was mechanically ground for 20 minutes to fine particles. 1 g of the fine particles and 0.4 ml of phosphate aqueous solution (1.0 M, pH=6.0) were mixed to form a paste, which was tested every 30 seconds to determine the working time and the setting time. The working time of the paste of this example is 20.5 minutes and the setting time thereof is 24 minutes.
The paste was placed in a relatively large amount of deionized water immediately following the formation thereof, and it was observed that the paste was non-dispersive in deionized water.
5 g of CaHPO4 (DCPA) powder and 1.6 ml of 25 mM phosphoric acid aqueous solution were mixed, and stirred for one minute. To the resulting mixture 1.6 ml of acetone was added while stirring to form a paste followed by placing in a vacuum environment of −100 Pa for one hour, and the resulting dried mixture was mechanically ground for 20 minutes to fine particles. 1 g of the fine particles and 0.4 ml of phosphate aqueous solution (1.0 M, pH=6.0) were mixed to form a paste, which was tested every 30 seconds to determine the working time and the setting time. The working time of the paste of this example is 20.0 minutes and the setting time thereof is 22.0 minutes.
The paste was placed in a relatively large amount of deionized water immediately following the formation thereof, and it was observed that the paste was non-dispersive in deionized water.
3 g of a mixed powder of CaHPO4 (DCPA) and Ca4(PO4)2O (TTCP) in 1:1 molar ratio was mixed with 2.0 ml of 25 mM phosphoric acid aqueous solution, and the mixture was stirred for five minutes. The resulting mixture was placed in a microwave oven where it was heated under low power for five minutes. The resulting dried mixture was mechanically ground for 20 minutes to fine particles. 1 g of the fine particles and 0.42 ml of phosphate aqueous solution (1.0 M, pH=6.0) were mixed to form a paste, which was tested every 30 seconds to determine the working time and the setting time. The working time of the paste of this example is 2.0 minutes and the setting time thereof is 4.0 minutes.
The paste was placed in a relatively large amount of deionized water immediately following the formation thereof, and it was observed that the paste was non-dispersive in deionized water.
5 g of a mixed powder of DCPA and TTCP in 1:1 molar ratio was mixed with 1.6 ml of 25 mM phosphoric acid aqueous solution, and the mixture was stirred for one minute. The resulting mixture was placed in a high temperature oven at 500° C. for five minutes. The resulting dried mixture was mechanically ground for 20 minutes to fine particles. 1 g of the fine particles and 0.4 ml of phosphate aqueous solution (1.0 M, pH=6.0) were mixed to form a paste, which was tested every 30 seconds to determine the working time and the setting time. The working time of the paste of this example is 1.5 minutes and the setting time thereof is 2.5 minutes.
The paste was placed in a relatively large amount of deionized water immediately following the formation thereof, and it was observed that the paste was non-dispersive in deionized water.
5 g of a mixed powder of DCPA and TTCP in 1:1 molar ratio was mixed with 1.6 ml of 25 mM phosphoric acid aqueous solution, and the mixture was stirred for one minute. The resulting mixture was placed in a high temperature oven at 1000° C. for one minute. The resulting dried mixture was mechanically ground for 20 minutes to fine particles. 1 g of the fine particles and 0.4 ml of phosphate aqueous solution (1.0 M, pH=6.0) were mixed to form a paste, which was tested every 30 seconds to determine the working time and the setting time. The working time of the paste of this example is 31 minutes and the setting time thereof is 35 minutes.
The procedures of Example 1 were repeated except that the Ca(H2PO4)2.H2O powder was replaced by a mixed powder of DCPA and TTCP in 1:1 molar ratio and the 25 mM phosphoric acid aqueous solution was replaced by a diluted phosphoric acid aqueous solution having a pH of 1.96. The heating treatments were carried out with conditions listed in Table 1. The performance is also listed in Table 1.
1 g of a mixed powder of DCPA and TTCP in 1:1 mole and 0.4 ml of a diluted phosphoric acid aqueous solution having a pH of 1.96 were mixed to form a paste, which was tested every 30 seconds to determine the working time and the setting time. The paste of this example can not set within hours. The performance is listed in Table 1.
The procedures of Example 2 were repeated except that the DCPA powder was replaced by a mixed powder of DCPA and TTCP in 1:1 molar ratio and the 25 mM phosphoric acid aqueous solution was replaced by a diluted phosphoric acid aqueous solution having a pH of 1.96. The performance is listed in Table 1.
The procedures of Example 3 were repeated except that the DCPA powder was replaced by a mixed powder of DCPA and TTCP in 1:1 molar ratio and the 25 mM phosphoric acid aqueous solution was replaced by a diluted phosphoric acid aqueous solution having a pH of 1.96. The performance is listed in Table 1.
The procedures of Example 4 were repeated except that the 25 mM phosphoric acid aqueous solution was replaced by a diluted phosphoric acid aqueous solution having a pH of 1.96. The performance is listed in Table 1.
The pastes prepared in Control Example 1 and Example 7 were injected into water via a syringe at 3, 10 and 30 seconds after the paste being formed. The results are shown in
Two cylinders were prepared by separately molding the pastes prepared in Control Example 1 and Example 7, and were then placed in water.
It can be concluded from the results shown in
Two samples of the calcium phosphate cement prepared in Example 7 were observed by transmission electron microscopy (TEM), and two TEM pictures (not shown in the drawings) indicate that there are whiskers on surfaces of calcium phosphate particles having different diameters of the calcium phosphate cement.
The calcium phosphate cement prepared in Example 6 has a particle diameter distribution shown in
The procedures of Example 7 were repeated by using the calcium phosphate powders and the wetting solutions listed in Table 2. The performance is also listed in Table 2.
The procedures of Control Example 1 were repeated by using the calcium phosphate powders and the wetting solutions listed in Table 2. The performance is also listed in Table 2.
The procedures of Example 7 were repeated by using the wetting solutions having different pH values listed in Table 3. The performance is also listed in Table 3.
The procedures of Control Example 1 were repeated by using the wetting solutions having different pH values listed in Table 3. The performance is also listed in Table 3.
This application is a continuation-in-part and claims the benefit of priority under 35 U.S.C. § 120 of U.S. application Ser. No. 09/615,384, filed Jul. 13, 2000, now abandoned. The disclosure of the prior application is considered part of and is incorporated by reference in the disclosure of this application.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3679360 | Rubin et al. | Jul 1972 | A |
| 4371484 | Inukai et al. | Feb 1983 | A |
| 4612053 | Brown et al. | Oct 1986 | A |
| RE33161 | Brown et al. | Feb 1990 | E |
| 5017518 | Hirayama et al. | May 1991 | A |
| 5149368 | Liu et al. | Sep 1992 | A |
| 5164187 | Constantz et al. | Nov 1992 | A |
| 5180426 | Sumita | Jan 1993 | A |
| 4959104 | Iino et al. | Aug 1994 | A |
| 5342441 | Mandai et al. | Aug 1994 | A |
| 5476647 | Chow et al. | Dec 1995 | A |
| 5496399 | Ison et al. | Mar 1996 | A |
| 5503164 | Friedman | Apr 1996 | A |
| 5522893 | Chow et al. | Jun 1996 | A |
| 5525148 | Chow et al. | Jul 1996 | A |
| 5536575 | Imura et al. | Jul 1996 | A |
| 5542973 | Chow et al. | Aug 1996 | A |
| 5545254 | Chow et al. | Aug 1996 | A |
| 5550172 | Regula et al. | Aug 1996 | A |
| 5569490 | Imura et al. | Oct 1996 | A |
| 5652016 | Imura et al. | Jul 1997 | A |
| 5683496 | Ison et al. | Nov 1997 | A |
| 5695729 | Chow et al. | Dec 1997 | A |
| 5697981 | Ison et al. | Dec 1997 | A |
| 5766669 | Pugh et al. | Jun 1998 | A |
| 5814681 | Hino et al. | Sep 1998 | A |
| 5820632 | Constantz et al. | Oct 1998 | A |
| 5846312 | Ison et al. | Dec 1998 | A |
| 5891448 | Chow et al. | Apr 1999 | A |
| 5899939 | Boyce et al. | May 1999 | A |
| 5954867 | Chow et al. | Sep 1999 | A |
| 5964932 | Ison et al. | Oct 1999 | A |
| 5976234 | Chow et al. | Nov 1999 | A |
| 5993535 | Sawamura et al. | Nov 1999 | A |
| 5997624 | Chow et al. | Dec 1999 | A |
| 6013591 | Ying et al. | Jan 2000 | A |
| 6117456 | Lee et al. | Sep 2000 | A |
| 6123731 | Boyce et al. | Sep 2000 | A |
| 6162258 | Scarborough et al. | Dec 2000 | A |
| 6325987 | Sapieszko et al. | Apr 2001 | B1 |
| 6277149 | Boyle et al. | Aug 2001 | B1 |
| 6294041 | Boyce et al. | Sep 2001 | B1 |
| 6294187 | Boyce et al. | Sep 2001 | B1 |
| 6325992 | Chow et al. | Dec 2001 | B1 |
| 6332779 | Boyce et al. | Dec 2001 | B1 |
| 6340648 | Imura et al. | Jan 2002 | B1 |
| 6379453 | Lin et al. | Apr 2002 | B1 |
| 6440444 | Boyce et al. | Aug 2002 | B1 |
| 6478825 | Winterbotton et al. | Nov 2002 | B1 |
| 6530955 | Boyle et al. | Mar 2003 | B1 |
| 6547866 | Edwards et al. | Apr 2003 | B1 |
| 6616742 | Lin et al. | Oct 2003 | B1 |
| 6648960 | Lin et al. | Nov 2003 | B1 |
| 6840995 | Lin et al. | Jan 2005 | B1 |
| 20020019635 | Wenstom, Jr. et al. | Feb 2002 | A1 |
| 20020073894 | Genge et al. | Jun 2002 | A1 |
| 20020137812 | Chow et al. | Sep 2002 | A1 |
| 20030019396 | Edwards et al. | Jan 2003 | A1 |
| 20030031698 | Roeder et al. | Feb 2003 | A1 |
| 20030078317 | Lin et al. | Apr 2003 | A1 |
| 20030121450 | Lin et al. | Jul 2003 | A1 |
| 20040003757 | Lin et al. | Jan 2004 | A1 |
| 20040031420 | Lin et al. | Feb 2004 | A1 |
| 20040175320 | Lin et al. | Sep 2004 | A1 |
| 20040180091 | Lin | Sep 2004 | A1 |
| 20040186481 | Lin et al. | Sep 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 06-228011 | Aug 1994 | JP |
| WO 03055418 | Jul 2003 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20040031420 A1 | Feb 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09615384 | Jul 2000 | US |
| Child | 10414582 | US |