Capacitors Having Dielectric Regions That Include Multiple Metal Oxide-Comprising Materials

Abstract

Capacitors and methods of forming capacitors are disclosed, and which include an inner conductive metal capacitor electrode and an outer conductive metal capacitor electrode. A capacitor dielectric region is received between the inner and the outer conductive metal capacitor electrodes and has a thickness no greater than 150 Angstroms. Various combinations of materials of thicknesses and relationships relative one another are disclosed which enables and results in the dielectric region having a dielectric constant k of at least 35 yet leakage current no greater than 1×10−7 amps/cm2 at from −1.1V to +1.1V.

Description

TECHNICAL FIELD

Embodiments disclosed herein pertain to capacitors having dielectric regions that include multiple metal oxide-comprising materials, and to methods of forming such capacitors.

BACKGROUND

Capacitors are commonly-used electrical components in semiconductor integrated circuitry, for example memory circuitry such as DRAM circuitry. A typical capacitor is comprised of two conductive electrodes separated by a non-conducting capacitor dielectric region. As integrated circuit density increases, there is a continuing challenge to maintain sufficiently high storage capacitance despite decreasing capacitor area. One way of increasing cell capacitance is through cell structure techniques. Such techniques include three-dimensional cell capacitors, such as trenched and stack capacitors. Other ways of increasing cell capacitance include the development and utilization of new materials for one or both of the electrodes and the capacitor dielectric region.

One type of capacitor utilizes a metal-insulator-metal (MIM) construction. Such can provide capacitance increase in comparison to where at least one of the capacitor electrodes is conductively doped semiconductor material. However, such capacitance increase also undesirably significantly increases leakage current across the capacitor. Further, deposition of oxide-containing capacitor dielectric materials to form a part of a capacitor dielectric region can be problematic in the fabrication of metal-containing capacitor electrodes.

Accordingly, needs remain for improved capacitor constructions and methods of forming capacitors.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 2 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 3 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 4 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 5 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 6 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 7 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 8 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 9 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 10 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 11 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

FIG. 12 is a diagrammatic cross sectional view of a capacitor construction in accordance with an embodiment of the invention.

DETAILED DESCRIPTION OF EXAMPLE EMBODIMENTS

A first embodiment capacitor 10 in accordance with the invention is described with reference to FIG. 1. Such is diagrammatically shown, and would be received over or as part of a substrate, for example a semiconductor substrate. In the context of this document, the term “semiconductor substrate” or “semiconductive substrate” is defined to mean any construction comprising semiconductive material, including, but not limited to, bulk semiconductive materials such as a semiconductive wafer (either alone or in assemblies comprising other materials thereon), and semiconductive material layers (either alone or in assemblies comprising other materials). The term “substrate” refers to any supporting structure, including, but not limited to, the semiconductive substrates described above.

Capacitor 10 includes an inner conductive metal capacitor electrode 12, an outer conductive metal capacitor electrode 14, and a capacitor dielectric region 16 received there-between. In the context of this document, “metal” requires the capacitor electrode to comprise, consist essentially of, or consist of one or more conductive elemental metals, one or more conductive metal alloys, and/or one or more conductive metal compounds. Specific examples include one or more of TiN, Pt, and Ru. Further in the context of this document, “inner” and “outer” are relative to thickness of the substrate over or upon which the capacitor (or the capacitor in fabrication) is received in a direction orthogonal/vertical to a major/horizontal surface of such substrate. Accordingly, the inner conductive metal capacitor electrode is received elevationally deeper within the substrate thickness than is the outer conductive metal capacitor electrode. Accordingly, inner conductive metal capacitor electrode 12 would be received over or as part of underlying/more-inner substrate material (not shown). Conductive metal capacitor electrodes 12 and 14 may be of the same or different composition, construction, size, and/or shape relative one another, and whether existing or yet-to-be developed. An example elevational thickness range for inner conductive metal capacitor electrode 12 is from about 70 Angstroms to about 250 Angstroms, while that for outer conductive metal capacitor electrode 14 is from about 50 Angstroms to about 100 Angstroms.

Capacitor dielectric region 16 has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16 are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16. In one embodiment, the capacitor dielectric region 16 has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16 includes a first Al₂O₃-comprising material 18 outward of inner electrode 12. Material 18 may comprise, consist essentially of, or consist of Al₂O₃, and has a thickness of from 2 Angstroms to 10 Angstroms. In one embodiment, material 18 has a thickness of from 2 Angstroms to 4 Angstroms. A ZrO₂-comprising material 20 is received outward of first Al₂O₃-comprising material 20. Material 20 may comprise, consist essentially of, or consist of ZrO₂, and has a thickness of from 30 Angstroms to 70 Angstroms. In one embodiment, material 20 has a thickness from 40 Angstroms to 60 Angstroms.

A second Al₂O₃-comprising material 22 is received outward of ZrO₂-comprising material 20. Material 22 may be of the same or different composition from that of material 18, and may comprise, consist essentially of, or consist of Al₂O₃. Second Al₂O₃-comprising material 22 has a thickness of from 2 Angstroms to 16 Angstroms. In one embodiment, material 22 has a thickness of from 4 Angstroms to 7 Angstroms. A TiO₂-comprising material 24 is received outward of second Al₂O₃-comprising material 22. TiO₂-comprising material 24 may comprise, consist essentially of, or consist of TiO₂, and has a thickness of from 40 Angstroms to 80 Angstroms. A sum “T” of the thicknesses of first Al₂O₃-comprising material 18, ZrO₂-comprising material 20, and second Al₂O₃-comprising material 22 is no greater than 70 Angstroms.

A combination of the above stated materials for dielectric region 16 in the stated order in combination with the stated thickness values for the respective largest stated ranges produces the unexpected result of capacitor dielectric region 16 having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region 16 has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16 has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

In the above embodiments for capacitor dielectric region 16, first Al₂O₃-comprising material 18 may or may not be in direct physical touching contact with inner electrode 12. Likewise, TiO₂-comprising material 24 may or may not be in direct physical touching contact with outer electrode 14. Accordingly, dielectric material other than Al₂O₃ may or may not be received between material 18 and inner capacitor electrode 12, and dielectric material other than TiO₂ may or may not be received between material 24 and outer capacitor electrode 14. Further in one embodiment and as shown, each of materials 18, 20, 22 and 24 is in direct physical touching contact with the immediately adjacent of such materials. However, dielectric material of different composition from that of the respective immediately adjacent of materials 18, 20, 22 and 24 may be received between any one or more of such immediately adjacent materials.

For example, a capacitor 10a is shown in FIG. 2. Like numerals from FIG. 1 have been utilized where appropriate, with some construction differences being indicated with the suffix “a” or with different numerals. In FIG. 2, an Al_xZr_yO_z-comprising material 26 is received between first Al₂O₃-comprising material 18 and ZrO₂-comprising material 20, and where material 18 and material 20 are in direct physical touching contact with Al_xZr_yO_z-comprising material 26. Where “x” is from 0.3 to 0.7, “y” is from 2.8 to 3.1 and “z” is from 6.0 to 7.4. Where “x” is from 0.1 to 0.3, “y” is from 3.0 to 3.4 and “z” is from 6.1 to 7.4. Where “x” is from 2.8 to 3.2, “y” is from 0.6 to 0.9 and “z” is from 5.3 to 6.7. Other quantities for “x”, “y”, and “z” falling within the respective x:y:z ratios may be used. Al_xZr_yO_z-comprising material 26 may comprise, consist essentially of, or consist of Al_xZr_yO_z. An example thickness range for Al_xZr_yO_z-comprising material 26 is from 2 Angstroms to 32 Angstroms.

An Al_xZr_yO_z-comprising material 28 is received between ZrO₂-comprising material 20 and second Al₂O₃-comprising material 22, and where material 20 and material 22 are in direct physical touching contact with Al_xZr_yO_z-comprising material 28. Ranges for “x”, “y”, and “z” are as stated above for material 26. Such may be of the same or different composition as material 26. Al_xZr_yO_z-comprising material 28 may comprise, consist essentially of, or consist of Al_xZr_yO_z. An example thickness range for Al_xZr_yO_z-comprising material 28 is from 2 Angstroms to 32 Angstroms.

A Ti_xAl_yO_z-comprising material 30 is received between second Al₂O₃-comprising material 22 and TiO₂-comprising material 24, and where material 22 and material 24 are in direct physical touching contact with Ti_xAl_yO_z-comprising material 30. In one embodiment, “x” is from 0.3 to 0.7, “y” is from 3.0 to 3.5 and “z” is from 5.0 to 6.8. In one embodiment, “x” is from 4 to 10, “y” is from 0.1 to 0.4 and “z” is from 8 to 20. Other quantities for “x”, “y”, and “z” falling within such x:y:z ratios may be used. Material 30 may comprise, consist essentially of, or consist of Ti_xAl_yO_z. An example thickness range for Ti_xAl_yO_z-comprising material 30 is from 2 Angstroms to 66 Angstroms.

Capacitor dielectric region 16a has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16a are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16a. In one embodiment, capacitor dielectric region 16a has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Materials other than the above-described materials 26, 28, 30 might be received intermediate immediately adjacent of materials 18, 20, 22 and 24. Regardless, provision of one or more of the above stated materials 26, 28 and 30 is expected to provide one or both of a further increase in dielectric constant k and a further reduction in leakage current for capacitor dielectric region 16a as compared to capacitor dielectric region 16.

Another embodiment capacitor 10b is described with reference to FIG. 3. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “b” or with different numerals. In FIG. 3, capacitor dielectric region 16b includes first Al₂O₃-comprising material 18 outward of inner electrode 12, and has a thickness of from 2 Angstroms to 10 Angstroms. TiO₂-comprising material 24 is received outward of first Al₂O₃-comprising material 18, and has a thickness of from 40 Angstroms to 80 Angstroms. A second Al₂O₃-comprising material 32 is received outward of TiO₂-comprising material 24. Such may comprise, consist essentially of, or consist of Al₂O₃ and may or may not be of the same composition as first Al₂O₃ comprising material 18. Regardless, second Al₂O₃-comprising material 32 has a thickness of from 2 Angstroms to 10 Angstroms, and may or may not be in direct physical touching contact with outer capacitor electrode 14. In one embodiment, material 32 has a thickness of from 4 Angstroms to 7 Angstroms.

Capacitor dielectric region 16b has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16b are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16b. In one embodiment, capacitor dielectric region 16b has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

A combination of the above stated materials for dielectric region 16b in the stated order in combination with the stated thickness values for the respective largest stated ranges produces the unexpected result of capacitor dielectric region 16b having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region 16b has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16b has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

As in the above-described embodiments, immediately adjacent of materials 18, 24 and 32 may be in direct physical touching contact with one another, or have intervening dielectric material received there-between. For example and by way of example only, material 30 (not shown in FIG. 3) could be received between one or both of material pairs 32/24 or 24/18.

Another capacitor 10c is shown in FIG. 4. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “c” or with different numerals. Capacitor dielectric region 16c has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16c are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16c. In one embodiment, capacitor dielectric region 16c has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

The capacitor of FIG. 4 is similar to that of FIG. 3, and comprises specific additional material within capacitor dielectric region 16c received outwardly of second Al₂O₃-comprising material 32. Specifically, ZrO₂-comprising material 20 is received outward of second Al₂O₃-comprising material 32, and has a thickness of from 30 Angstroms to 70 Angstroms. A third Al₂O₃-comprising material 34 is received outward of ZrO₂-comprising material 20, and has a thickness of from 2 Angstroms to 10 Angstroms. Third Al₂O₃-comprising material 34 may comprise, consist essentially of, or consist of Al₂O₃, and may be of the same or of different composition from that of either of materials 18 or 32. Material 34 may or may not be in direct physical touching contact with outer capacitor electrode 14. Further, third Al₂O₃-comprising material 34 may or may not be in direct physical touching contact with ZrO₂-comprising material 20, and ZrO₂-comprising material 20 may or may not be in direct physical touching contact with second Al₂O₃-comprising material 32. In one embodiment, Al_xZr_yO_z material 26 (not shown in FIG. 4) may be received between either of material pairs 32/20 and 34/20. Regardless, providing of materials 20 and 34 as shown and described is expected to provide one or both of a further increase in dielectric constant k and a further reduction in leakage current for capacitor dielectric region 16c as compared to capacitor dielectric region 16b.

Another embodiment capacitor 10d is shown in FIG. 5. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “d” or with different numerals. Capacitor dielectric region 16d has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16d are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16d. In one embodiment, capacitor dielectric region 16d has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16d includes optional first Al₂O₃-comprising material 18 outward of inner capacitor electrode 12, and has a thickness of from 0 Angstroms to 10 Angstroms. Accordingly, optional first Al₂O₃-comprising material 18 may be present in the capacitor construction 10d (as shown), or may not be present in the capacitor construction.

ZrO₂-comprising material 20 is received outward of inner capacitor electrode 12 and outward of optional first Al₂O₃-comprising material 18 if optional first Al₂O₃-comprising material 18 is present. ZrO₂-comprising material 20 has a thickness of from 30 Angstroms to 70 Angstroms. Second Al₂O₃-comprising material 22 is received outward of ZrO₂-comprising material 20, and has a thickness of from 2 Angstroms to 16 Angstroms. TiO₂-comprising material 24 is received outward of second Al₂O₃-comprising material 22, and has a thickness of from 40 Angstroms to 80 Angstroms. Third Al₂O₃-comprising material 32 is received outward of TiO₂-comprising material 24, and has a thickness of from 2 Angstroms to 10 Angstroms. A sum T of the thicknesses of optional first Al₂O₃-comprising material 18 if such is present, ZrO₂-comprising material 20, and second Al₂O₃-comprising material 22 totals no more than 70 Angstroms.

A combination of the above stated materials for dielectric region 16d in the stated order in combination with the stated thickness values for the respective largest stated ranges produces the unexpected result of capacitor dielectric region 16d having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region 16d has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16d has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Materials 18, 20, 22, 24 and 32 are shown as being in direct physical touching contact relative to immediately adjacent of such materials. However, any dielectric material may be received between any pair of immediately adjacent such materials. For example, in some embodiments Al_xZr_yO_z material 26 (not shown in FIG. 5) may be received between one or both of material pairs 20/18 and 22/20. Further in some embodiments, Ti_xAl_yO_z material 30 (not shown in FIG. 5) may be received between one or both of material pairs 24/22 and 32/24.

Another capacitor construction 10e is shown in FIG. 6. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “e” or with different numerals. Capacitor dielectric region 16e has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16e are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16e. In one embodiment, capacitor dielectric region 16e has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16e includes first Al₂O₃-comprising material 18 outward of inner capacitor electrode 12, and has a thickness of from 2 Angstroms to 10 Angstroms. ZrO₂-comprising material 22 is received outward of first Al₂O₃-comprising material 18, and has a thickness of from 30 Angstroms to 70 Angstroms. TiO₂-comprising material 24 is received outward of ZrO₂-comprising material 22, and has a thickness of from 40 Angstroms to 80 Angstroms. Second Al₂O₃-comprising material 34 is received outward of TiO₂-comprising material 24, and has a thickness of from 2 Angstroms to 10 Angstroms.

A combination of the above stated materials for dielectric region 16e in the stated order in combination with the stated thickness values for the respective largest stated ranges produces the unexpected result of capacitor dielectric region 16e having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region 16e has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16e has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Materials 18, 22, 24 and 34 are shown as being in direct physical touching contact relative to immediately adjacent of such materials. However, any dielectric material may be received between any pair of immediately adjacent such materials. For example, in some embodiments Al_xZr_yO_z material 26 (not shown in FIG. 6) may be received between material pair 22/18. In some embodiments, Ti_xAl_yO_z material 30 (not shown in FIG. 6) may be received between material pair 34/24. Further in some embodiments, a Ti_xZr_yO_z-comprising material (not shown in FIG. 6) may be received between material pair 24/22. Relative ratio quantities for “x”, “y”, and “z” in Ti_xZr_yO_z are as follows. Where “x” is from 0.6 to 0.8, “y” is from 2.5 to 3.6 and “z” is from 6.1 to 8.9. Where “x” is from 0.1 to 0.3, “y” is from 3.0 to 3.4 and “z” is from 6.1 to 7.5. Where “x” is from 3.5 to 4.0, “y” is from 0.1 to 0.3 and “z” is from 7.1 to 8.7. Where “x” is from 1.0 to 2.0, “y” is from 0.2 to 0.5 and “z” is from 2.3 to 5.1. Other quantities for “x”, “y”, and “z” falling within the respective x:y:z ratios may be used. The Ti_xZr_yO_z-comprising material may comprise, consist essentially of, or consist of Ti_xZr_yO_z. An example thickness range for a Ti_xZr_yO_z-comprising material is from 2 Angstroms to 76 Angstroms.

Another capacitor construction 10f is shown in FIG. 7. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “f” or with different numerals. Capacitor dielectric region 16f has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16f are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16f. In one embodiment, capacitor dielectric region 16f has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16f includes an HfO₂-comprising material 38 outward of inner capacitor electrode 12, and has a thickness of from 10 Angstroms to 50 Angstroms. Material 38 may or may not be in direct physical touching contact with inner capacitor electrode 12. TiO₂-comprising material 24 is received outward of HfO₂-comprising material 38, and has a thickness of from 40 Angstroms to 80 Angstroms. Al₂O₃-comprising material 32 is received outward of TiO₂-comprising material 24, and has a thickness of from 2 Angstroms to 10 Angstroms.

A combination of the above stated materials for dielectric region 16f in the stated order in combination with the stated thickness values produces the unexpected result of capacitor dielectric region 16f having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region 16f has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16f has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Materials 38, 24, and 32 may be in direct physical touching contact relative to immediately adjacent of such materials, or intervening dielectric material may be received between one or both of material pairs 38/24 and 32/24. For example, another capacitor construction 10g is shown in FIG. 8. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “g” or with different numerals. Capacitor dielectric region 16g has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16g are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16g. In one embodiment, capacitor dielectric region 16g has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

In capacitor dielectric region 16g, TiO₂-comprising material 24 is not in direct physical touching contact with HfO₂-comprising material 38, rather having a material 40 received there-between. In one embodiment, such comprises a Ti_xHf_yO_z-comprising material, where TiO₂-comprising material 24 and HfO₂-comprising material 38 are in direct physical touching contact with Ti_xHf_yO_z-comprising material 40. Where “x” is from 0.6 to 0.9, “y” is from 2.8 to 3.5 and “z” is from 6.7 to 8.9. Where “x” is from 1.0 to 2.0, “y” is from 0.2 to 0.5 and “z” is from 2.3 to 5.1. Other quantities for “x”, “y”, and “z” falling within such x:y:z ratio may be used. Material 40 may comprise, consist essentially of, or consist of Ti_xHf_yO_z. An example thickness range for Ti_xHf_yO_z-comprising material 40 is from 2 Angstroms to 94 Angstroms. Ti_xAl_yO_z material 30 is received between Al₂O₃-comprising material 32 and TiO₂-comprising material 24. Regardless, provision of one or more of the above stated materials 40 or 30 is expected to provide one or both of a further increase in dielectric constant k and a further reduction in leakage current for capacitor dielectric region 16g as compared to capacitor dielectric region 16f.

Another capacitor construction 10h is shown in FIG. 9. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “h” or with different numerals. Capacitor dielectric region 16h has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16h are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16h. In one embodiment, capacitor dielectric region 16h has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16h includes a Ti_xM_yO_z-comprising material 44 outward of inner capacitor electrode 12, and has a thickness of from 5 Angstroms to 100 Angstroms. “M” is at least one of Zr, Hf, Ta, Si, Nb, or Al. Where “x” is from 0.6 to 0.9, “y” is from 2.8 to 3.5 and “z” is from 5.3 to 10.7. Other quantities for “x”, “y”, and “z” falling within such x:y:z ratio may be used. In one embodiment, Ti_xM_yO_z-comprising material 44 has a thickness of from 30 Angstroms to 75 Angstroms. Ti_xM_yO_z-comprising material 44 may or may not be in direct physical touching contact with inner electrode 12. A TiO₂-comprising material 45 is received outward of Ti_xM_yO_z-comprising material 44. TiO₂-comprising material 45 may comprise, consist essentially of, or consist of TiO₂, and has a thickness of from 5 Angstroms to 100 Angstroms.

A combination of the above stated materials for dielectric region 16h in the stated order in combination with the stated thickness values produces the unexpected result of capacitor dielectric region 16h having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, capacitor dielectric region 16h has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16h has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Materials 45 and 44 may be in direct physical touching contact with each other, or intervening dielectric material may be received between materials 45 and 44.

Another capacitor construction 10i is shown in FIG. 10. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “i” or with different numerals. Capacitor dielectric region 16i has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16i are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16i. In one embodiment, capacitor dielectric region 16i has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16i includes first Al₂O₃-comprising material 18 outward of inner capacitor electrode 12, and has a thickness of from 2 Angstroms to 10 Angstroms. ZrO₂-comprising material 20 is received outward of first Al₂O₃-comprising material 18, and has a thickness of from 30 Angstroms to 70 Angstroms. Second Al₂O₃-comprising material 22 is received outward of ZrO₂-comprising material 20, and has a thickness of from 2 Angstroms to 16 Angstroms.

Ti_xM_yO_z-comprising material 44 is received outward of second Al₂O₃-comprising material 22, and has a thickness of from 5 Angstroms to 100 Angstroms. Material 44 may or may not be in direct physical touching contact with outer electrode 14. A sum T of the thicknesses of first Al₂O₃-comprising material 18, ZrO₂-comprising material 20, and second Al₂O₃-comprising material 22 totals no more than 70 Angstroms.

A combination of the above stated materials for dielectric region 16i in the stated order in combination with the stated thickness values produces the unexpected result of capacitor dielectric region 16i having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, capacitor dielectric region 16i has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16i has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Immediately adjacent of materials 18, 20, 22 and 44 may be in direct physical touching contact with one another, or have intervening dielectric material received there-between. For example, material 26/30 (not shown in FIG. 10) could be received between one or both of material pairs 18/20 and 20/22. Regardless, material different from that of materials 22 and 44 could be received between materials 22 and 44.

Another capacitor construction 10j is shown in FIG. 11. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “j” or with different numerals. Capacitor dielectric region 16j has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16j are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16j. In one embodiment, capacitor dielectric region 16j has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16j includes optional first Al₂O₃-comprising material 18 outward of inner capacitor electrode 12, and has a thickness from 0 Angstroms to 10 Angstroms. Accordingly, capacitor construction 10j may or may not include first Al₂O₃-comprising material 18. A first material 46 is received outward of inner capacitor electrode 12 and outward of optional first Al₂O₃-comprising material 18 if such is present. First material 46 has a thickness of from 20 Angstroms to 50 Angstroms. First material 46 comprises at least one of ZrO₂ and HfO₂, including any combination or mixture thereof. First material 46 may comprise, consist essentially of, or consist of one or more of ZrO₂ and HfO₂.

An optional second Al₂O₃-comprising material 22 is received outward of first material 46, and has a thickness of from 0 Angstroms to 16 Angstroms. Accordingly, optional second Al₂O₃-comprising material 22 may or may not be present in capacitor dielectric region 16j, and independent of whether optional first Al₂O₃-comprising material 18 is present. TiO₂-comprising material 24 is received outward of first material 46 and outward of optional second Al₂O₃-comprising material 22 if such is present. TiO₂-comprising material 24 has a thickness of from 40 Angstroms to 80 Angstroms.

A second material 48 is received outward of TiO₂-comprising material 24, and comprises at least one of ZrO₂ or HfO₂, including any combination or mixture thereof. Such may comprise, consist essentially of, or consist of one or more of ZrO₂ and HfO₂, and may or may not be of the same composition as first material 46. Second material 48 has a thickness of from 10 Angstroms to 40 Angstroms, with a sum of the thicknesses of first material 46 and second material 48 alone totaling no more than 70 Angstroms.

Optional third Al₂O₃-comprising material 32 is received outward of second material 48, and has a thickness of from 0 Angstroms to 10 Angstroms. Accordingly, optional third Al₂O₃-comprising material 32 may or may not be present in capacitor dielectric region 16j, and independent of presence of one or both of optional first Al₂O₃-comprising material 18 and optional second Al₂O₃-comprising material 22. Accordingly, zero, one, two, or three of Al₂O₃-comprising materials 18, 22 and 32 may or may not be present in capacitor dielectric region 16j.

A combination of the above stated materials for dielectric region 16j in the stated order in combination with the stated thickness values produces the unexpected result of capacitor dielectric region 16j having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, capacitor dielectric region 16j has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16j has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Materials 18, 46, 22, 24, 48, and 32 are shown as being in direct physical touching contact relative to immediately adjacent of such materials. However, any dielectric material may be received between any pair of immediately adjacent such materials. For example, in some embodiments Al_xZr_yO_z material 26/28 (not shown in FIG. 11) may be received between any of material pairs 46/18, 46/22, and 48/32 where for example materials 46 and/or 48 comprise ZrO₂. In some embodiments, Al_xHf_yO_z material (not shown in FIG. 11) may be received between any of material pairs 46/18, 46/22, and 48/32 where for example materials 46 and/or 48 comprise HfO₂. In some embodiments, Ti_xAl_yO_z material 30 (not shown in FIG. 11) may be received between material pair 24/22. In some embodiments where second material 48 comprises HfO₂, a Ti_xHf_yO_z-comprising material 40 (not shown in FIG. 11) may be received between material pair 48/24.

Another capacitor construction 10k is shown in FIG. 12. Like numerals from the above-described embodiments have been utilized where appropriate, with some construction differences being indicated with the suffix “k” or with different numerals. Capacitor dielectric region 16k has a thickness no greater than 150 Angstroms. Further thickness limitations for different materials included as part of capacitor dielectric region 16k are provided herein, and are in addition to a maximum stated thickness for capacitor dielectric region 16k. In one embodiment, capacitor dielectric region 16k has a thickness no greater than 100 Angstroms, and in one embodiment has a thickness no greater than 75 Angstroms.

Capacitor dielectric region 16k includes optional first Al₂O₃-comprising material 18 outward of inner capacitor electrode 12, and has a thickness from 0 Angstroms to 2 Angstroms. Accordingly, capacitor construction 10k may or may not include first Al₂O₃-comprising material 18. Al_xZr_yO_z-comprising material 26 is received outward of inner capacitor electrode 12 and outward of optional first Al₂O₃-comprising material 18 if such is present. Al_xZr_yO_z-comprising material 26 has a thickness of from 2 Angstroms to 30 Angstroms.

Optional second Al₂O₃-comprising material 22 is received outward of Al_xZr_yO_z-comprising material 26, and has a thickness of from 0 Angstroms to 10 Angstroms. Accordingly, optional second Al₂O₃-comprising material 22 may or may not be present in capacitor dielectric region 16k, and independent of whether optional first Al₂O₃-comprising material 18 is present.

A first material 52 is received outward of Al_xZr_yO_z-comprising material 26 and outward of optional second Al₂O₃-comprising material 22 if optional second Al₂O₃-comprising material 22 is present. First material 52 comprises at least one of ZrO₂ or Ti_xZr_yO_z or Zr_aTi_xAl_yO_z, including any combinations or mixtures thereof. Relative ratio quantities for “x”, “y”, and “z” in Ti_xZr_yO_z are as follows. Where “x” is from 0.6 to 0.8, “y” is from 2.5 to 3.6 and “z” is from 6.1 to 8.9. Where “x” is from 0.1 to 0.3, “y” is from 3.0 to 3.4 and “z” is from 6.1 to 7.4. Where “x” is from 3.5 to 4.0, “y” is from 0.1 to 0.3 and “z” is from 7.1 to 8.7. Where “x” is from 1.0 to 2.0, “y” is from 0.2 to 0.5 and “z” is from 2.3 to 5.1. Other quantities for “x”, “y”, and “z” falling within the respective x:y:z ratios may be used. Relative ratio quantities for “a”, “x”, “y”, and “z” in Zr_aTi_xAl_yO_z are as follows. Where “a” is from 0.1 to 0.5, “x” is from 0.2 to 2.0, “y” is from 0.01 to 0.1 and “z” is from 0.8 to 5.2. Other quantities for “a”, “x”, “y”, and “z” falling within the respective a:x:y:z ratios may be used. First material 52 has a thickness of from 30 Angstroms to 60 Angstroms. First material 52 may comprise, consist essentially of, or consist of one or more of ZrO₂ or Ti_xZr_yO_z or Zr_aTi_xAl_yO_z. During formation of capacitor dielectric region 16k, first material 52 may or may not be annealed prior to deposition of any material thereover. If annealed, an example annealing temperature range is from about 400° C. to about 650° C., and an example time range for such annealing is from about 10 seconds to about 300 seconds. Plasma may or may not be used.

Optional third Al₂O₃-comprising material 32 is received outward of first material 52, and has a thickness of from 0 Angstroms to 4 Angstroms. Accordingly, optional third Al₂O₃-comprising material 32 may or may not be present in capacitor dielectric region 16k, and independent of whether optional first Al₂O₃-comprising material 18 or whether optional second Al₂O₃-comprising material 22 are present.

A second material 54 is received outward of first material 52 comprising at least one of ZrO₂ or Ti_xZr_yO_z or Zr_aTi_xAl_yO_z and outward of optional third Al₂O₃-comprising material 32 if optional third Al₂O₃-comprising material 32 is present. Second material 54 comprises at least one of TiO₂ or Ti_xZr_yO_z or Zr_aTi_xAl_yO_z, including any combinations or mixtures thereof. Example materials for Ti_xZr_yO_z and Zr_aTi_xAl_yO_z, are those as described above for capacitor dielectric region 16k. Second material 54 has a thickness of from 10 Angstroms to 70 Angstroms. Second material 54 may comprise, consist essentially of, or consist of one or more of ZrO₂ or Ti_xZr_yO_z or Zr_aTi_xAl_yO_z. During formation of capacitor dielectric region 16k, second material 54 may or may not be annealed prior to deposition of any material thereover. If annealed, example conditions include those described above for annealing first material 52.

An optional fourth Al₂O₃-comprising material 56 is received outward of second material 54, and has a thickness of from 0 Angstroms to 4 Angstroms. Accordingly, optional fourth Al₂O₃-comprising material 56 may or may not be present in capacitor dielectric region 16k, and independent of whether optional first Al₂O₃-comprising material 18, whether optional second Al₂O₃-comprising material 22, or whether optional third Al₂O₃-comprising material 32 are present. Accordingly, zero, one, two, three, or four of Al₂O₃-comprising materials 18, 22, 32, and 56 may or may not be present in capacitor dielectric region 16k.

A combination of the above stated materials for dielectric region 16k in the stated order in combination with the stated thickness values produces the unexpected result of capacitor dielectric region 16k having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, capacitor dielectric region 16k has a dielectric constant k of at least 40. In one embodiment, capacitor dielectric region 16k has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Materials 18, 26, 22, 52, 32, 54, and 56 are shown as being in direct physical touching contact relative to immediately adjacent of such materials. However, any dielectric material may be received between any pair of immediately adjacent such materials.

Embodiments of the invention also encompass various methods of forming capacitors encompassing any existing or yet-to-be-developed deposition and anneal techniques. Such encompass depositing inner conductive metal capacitor electrode material over a suitable substrate, for example a semiconductor substrate. Example materials include any of those described above with respect to inner conductive metal capacitor electrode 12. A capacitor dielectric region is formed outward of the inner conductive metal capacitor electrode material to a thickness no greater than 150 Angstroms, to have a dielectric constant k of at least 35, and to have leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V.

In one embodiment, the forming of the capacitor dielectric region includes depositing an amorphous ZrO₂-comprising material to a thickness no greater than 35 Angstroms outward of the inner conductive metal capacitor electrode material. The ZrO₂-comprising material formed outward of the inner conductive metal capacitor electrode material may or may not be in direct physical touching contact therewith. The amorphous ZrO₂-comprising material is annealed after its deposition to form crystalline ZrO₂-comprising material having a thickness no greater than 35 Angstroms. Such annealing may or may not be conducted in an inert atmosphere, and may or may not be subatmospheric. An example annealing ambient is any of air, Ar, N₂, O₂, O₃, and any combination or sub-combinations thereof. An example annealing temperature range is from about 400° C. to about 650° C., and an example time range for such annealing is from about 10 seconds to about 300 seconds. Plasma may or may not be used.

After the annealing of the amorphous ZrO₂-comprising material, an Al₂O₃-comprising material is deposited outward of the crystalline ZrO₂-comprising material, and to have a thickness of from 2 Angstroms to 16 Angstroms. The Al₂O₃-comprising material formed over the crystalline ZrO₂-comprising material may or may not be in direct physical touching contact therewith. In one embodiment, an Al_xZr_yO_z-comprising material is provided between such Al₂O₃-comprising material and the crystalline ZrO₂-comprising material, with the Al₂O₃-comprising material and the ZrO₂-comprising material there-under being in direct physical touching contact with the Al_xZr_yO_z-comprising material.

An amorphous TiO₂-comprising material is deposited to a thickness no greater than 50 Angstroms outward of the Al₂O₃-comprising material. The amorphous TiO₂-comprising material having thickness no greater than 50 Angstroms may or may not be in direct physical touching contact therewith. Regardless, such amorphous TiO₂-comprising material is annealed in the presence of oxygen after its deposition to form crystalline TiO₂-comprising material. The oxygen may be provided in the form of O₂, O₃, and/or by compounds which include oxygen and other elements. Example anneal conditions include those described above for the anneal of the ZrO₂-comprising material.

After the annealing of the amorphous TiO₂-comprising material, an outer conductive metal capacitor electrode material is deposited outward of the crystalline TiO₂-comprising material. Example materials include any of those described above with respect to capacitor electrodes 12 and 14.

A combination of the above stated processing steps for the capacitor dielectric region in the stated order in combination with the stated thickness values produces the unexpected result of the capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region has a dielectric constant k of at least 40. In one embodiment, the capacitor dielectric region has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

In one embodiment including the above described method, an intervening Al₂O₃-comprising material may be deposited outward of the inner conductive metal capacitor electrode material prior to the depositing of the amorphous ZrO₂-comprising material, and to a thickness of from 2 Angstroms to 10 Angstroms, and in one embodiment to a thickness of from 2 Angstroms to 4 Angstroms. In such event, a sum of the thicknesses of the intervening Al₂O₃-comprising material, the crystalline ZrO₂-comprising material, and the Al₂O₃-comprising material deposited over the crystalline ZrO₂-comprising material totals no more than 70 Angstroms.

The intervening Al₂O₃-comprising material may or may not be in direct physical touching contact with the crystalline ZrO₂-comprising material. In one embodiment, an Al_xZr_yO_z-comprising material is provided between the intervening Al₂O₃-comprising material and the crystalline ZrO₂-comprising material, with the intervening Al₂O₃-comprising material and the ZrO₂-comprising material being in direct physical touching contact with the Al_xZr_yO_z-comprising material. Any of the above Al_xZr_yO_z-comprising materials are examples.

The crystalline TiO₂-comprising material may or may not be in direct physical touching contact with the Al₂O₃-comprising material formed thereover. In one embodiment, a Ti_xAl_yO_z-comprising material is provided between such Al₂O₃-comprising material and the crystalline TiO₂-comprising material. In one embodiment, such Al₂O₃-comprising material and the crystalline TiO₂-comprising material are in direct physical touching contact with the Ti_xAl_yO_z-comprising material. Any of the Ti_xAl_yO_z-comprising materials described above are examples.

Another Al₂O₃-comprising material may be deposited outward of the crystalline TiO₂-comprising material prior to the depositing of the outer conductive metal capacitor electrode material, and to have a thickness of from 2 Angstroms to 10 Angstroms. Such may or may not be formed in direct physical touching contact with the crystalline TiO₂-comprising material. In one embodiment, a Ti_xAl_yO_z-comprising material is provided between such another/outer Al₂O₃-comprising material and the crystalline TiO₂-comprising material. In one embodiment, such another/outer Al₂O₃-comprising material and the crystalline TiO₂-comprising material are provided in direct physical touching contact with the Ti_xAl_yO_z-comprising material.

In additional embodiments, processing may proceed as described in the above methods through the depositing of the Al₂O₃-comprising material outward of the crystalline ZrO₂-comprising material, and to have a thickness of from 2 Angstroms to 16 Angstroms. Then, an amorphous TiO₂-comprising material is deposited to a thickness greater than 50 Angstroms outward of the Al₂O₃-comprising material having thickness of from 2 Angstroms to 16 Angstroms. In such event, the outer conductive metal capacitor electrode material is then deposited outward of the TiO₂-comprising material at a temperature which transforms the amorphous TiO₂-comprising material to be crystalline during such act of depositing the outer conductive metal capacitor electrode material. For example, exposure to a temperature of at least 500° C. for at least 1 minute occurring during deposition of the outer conductive metal capacitor electrode material will achieve such amorphous-to-crystalline phase transformation of a TiO₂-comprising material having thickness greater than 50 Angstroms.

Alternately in such additional embodiments, the outer conductive metal capacitor electrode material is deposited outward of the TiO₂-comprising material at a temperature which does not transform the TiO₂-comprising material to be crystalline during such act of depositing the outer conductive metal capacitor electrode material. After deposition of the outer conductive metal capacitor electrode material, the substrate is then exposed to a temperature to transform the amorphous TiO₂-comprising material having thickness greater than 50 Angstroms to be crystalline. Example anneal conditions include exposure to a temperature of at least 500° C. for at least 1 minute.

A combination of the above stated processing steps in such additional embodiments for the capacitor dielectric region in the stated order in combination with the stated thickness values produces the unexpected result of the capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region has a dielectric constant k of at least 40. In one embodiment, the capacitor dielectric region has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V. Further, one or both of an intervening Al₂O₃-comprising material and outer/another Al₂O₃-comprising material might also be deposited in such additional embodiments as described above.

In a further embodiment, the forming of the capacitor dielectric region includes depositing a first Al₂O₃-comprising material outward of the inner conductive metal capacitor electrode material, and to have a thickness of from 2 Angstroms to 10 Angstroms. Such first Al₂O₃-comprising material may or may not be in direct physical touching contact with the inner conductive metal capacitor electrode material. Example first Al₂O₃-comprising material includes any of those described above for materials 18, 22 and 32.

A TiO₂-comprising material is deposited outward of the first Al₂O₃-comprising material, and to a thickness of from 40 Angstroms to 80 Angstroms. Example materials include those described above for material 20. Such may or may not be in direct physical touching contact with the first Al₂O₃-comprising material. In one embodiment, a Ti_xAl_yO_z-comprising material is provided between the first Al₂O₃-comprising material and the TiO₂-comprising material. In one embodiment, the first Al₂O₃-comprising material and the TiO₂-comprising material are provided in direct physical touching contact with such Ti_xAl_yO_z-comprising material.

A second Al₂O₃-comprising material is deposited outward of the TiO₂-comprising material, and to have a thickness of from 2 Angstroms to 10 Angstroms. Examples include any of those described above for materials 18/22/32. The second Al₂O₃-comprising material may or may not be in direct physical touching contact with the TiO₂-comprising material. In one embodiment, a Ti_xAl_yO_z-comprising material is provided between the second Al₂O₃-comprising material and the TiO₂-comprising material. In one embodiment, the second Al₂O₃-comprising material and the TiO₂-comprising material are provided in direct physical touching contact with such Ti_xAl_yO_z-comprising material.

An amorphous ZrO₂-comprising material is deposited to a thickness no greater than 35 Angstroms outward of the second Al₂O₃-comprising material. The amorphous ZrO₂-comprising material is annealed after its deposition to form crystalline ZrO₂-comprising material having a thickness of no greater than 35 Angstroms. Example anneal conditions include those described above. The ZrO₂-comprising material may or may not be in direct physical touching contact with the second Al₂O₃-comprising material. In one embodiment, an Al_xZr_yO_z-comprising material is provided between the ZrO₂-comprising material and the second Al₂O₃-comprising material. In one embodiment, the ZrO₂-comprising material and the second Al₂O₃-comprising material are provided in direct physical touching contact with such Al_xZr_yO_z-comprising material.

After the annealing of the amorphous ZrO₂-comprising material, an outer conductive metal capacitor electrode material is deposited outward of the crystalline ZrO₂-comprising material. Example materials include any of those described above with respect to capacitor electrodes 12 and 14.

A combination of the above-stated processing steps for the capacitor dielectric region in the further stated embodiments in the stated order in combination with the stated thickness values produces the unexpected result of the capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region has a dielectric constant k of at least 40. In one embodiment, the capacitor dielectric region has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

Another Al₂O₃-comprising material may be deposited outward of the crystalline ZrO₂-comprising material prior to the depositing of the outer conductive metal capacitor electrode material, and to have a thickness of from 2 Angstroms to 10 Angstroms. Such may or may not be formed in direct physical touching contact with the crystalline ZrO₂-comprising material. In one embodiment, an Al_xZr_yO_z-comprising material is provided between such another/outer Al₂O₃-comprising material and the crystalline ZrO₂-comprising material. In one embodiment, such another/outer Al₂O₃-comprising material and the crystalline ZrO₂-comprising material are provided in direct physical touching contact with the Al_xZr_yO_z-comprising material.

In additional further embodiments, processing may proceed as described above through the depositing of the second Al₂O₃-comprising material outward of the TiO₂-comprising material, and to have a thickness of from 2 Angstroms to 16 Angstroms. Then, an amorphous ZrO₂-comprising material is deposited to a thickness greater than 35 Angstroms outward of the second Al₂O₃-comprising material. In such event, the outer conductive metal capacitor electrode material is then deposited outward of the ZrO₂-comprising material at a temperature which transforms the amorphous ZrO₂-comprising material to be crystalline during such act of depositing the outer conductive metal capacitor electrode material. For example, exposure to a temperature of at least 500° C. for at least 1 minute occurring during deposition of the outer conductive metal capacitor electrode material will achieve such amorphous-to-crystalline phase transformation of a ZrO₂-comprising material having thickness greater than 35 Angstroms.

Alternately in such additional further embodiments, the outer conductive metal capacitor electrode material is deposited outward of the ZrO₂-comprising material at a temperature which does not transform the ZrO₂-comprising material to be crystalline during such act of depositing the outer conductive metal capacitor electrode material. After deposition of the outer conductive metal capacitor electrode material, the substrate is then exposed to a temperature to transform the amorphous ZrO₂-comprising material having thickness greater than 35 Angstroms to be crystalline. Example anneal conditions include exposure to a temperature of at least 500° C. for at least 1 minute.

A combination of the above-stated processing steps for the capacitor dielectric region in the last stated embodiments in the stated order in combination with the stated thickness values produces the unexpected result of the capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10⁻⁷ amps/cm² at from −1.1V to +1.1V. In one embodiment, the capacitor dielectric region has a dielectric constant k of at least 40. In one embodiment, the capacitor dielectric region has leakage current no greater than 5×10⁻⁸ amps/cm² at from −1.1V to +1.1V.

In compliance with the statute, the subject matter disclosed herein has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the claims are not limited to the specific features shown and described, since the means herein disclosed comprise example embodiments. The claims are thus to be afforded full scope as literally worded, and to be appropriately interpreted in accordance with the doctrine of equivalents.

Claims

1-18. (canceled)

19. A capacitor comprising: an inner conductive metal capacitor electrode and an outer conductive metal capacitor electrode; anda capacitor dielectric region received between the inner and the outer conductive metal capacitor electrodes and having a thickness no greater than 150 Angstroms, the capacitor dielectric region comprising: an HfO2-comprising material outward of the inner electrode, the HfO2-comprising material having a thickness of from 10 Angstroms to 50 Angstroms;a TiO2-comprising material outward of the HfO2-comprising material, the TiO2-comprising material having a thickness of from 40 Angstroms to 80 Angstroms;an Al2O3-comprising material outward of the TiO2-comprising material, the Al2O3-comprising material having a thickness of from 2 Angstroms to 10 Angstroms; andthe capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10−7 amps/cm2 at from −1.1V to +1.1V.

20. The capacitor of claim 19 wherein the HfO2-comprising material is in direct physical touching contact with the inner electrode.

21. The capacitor of claim 19 wherein the TiO2-comprising material is in direct physical touching contact with the HfO2-comprising material.

22. The capacitor of claim 19 wherein the TiO2-comprising material is not in direct physical touching contact with the HfO2-comprising material.

23. The capacitor of claim 22 comprising a HfxTiyOz-comprising material received between the TiO2-comprising material and the HfO2-comprising material, the TiO2-comprising material and the HfO2-comprising material being in direct physical touching contact with the HfxTiyOz-comprising material.

24-26. (canceled)

27. A capacitor comprising: an inner conductive metal capacitor electrode and an outer conductive metal capacitor electrode; anda capacitor dielectric region received between the inner and the outer conductive metal capacitor electrodes and having a thickness no greater than 150 Angstroms, the capacitor dielectric region comprising: a first Al2O3-comprising material outward of the inner electrode, the first Al2O3-comprising material having a thickness of from 2 Angstroms to 10 Angstroms;a ZrO2-comprising material outward of the first Al2O3-comprising material, the ZrO2-comprising material having a thickness of from 30 Angstroms to 70 Angstroms;a TiO2-comprising material outward of the ZrO2-comprising material, the TiO2-comprising material having a thickness of from 40 Angstroms to 80 Angstroms;a second Al2O3-comprising material outward of the TiO2-comprising material, the second Al2O3-comprising material having a thickness of from 2 Angstroms to 10 Angstroms; andthe capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10−7 amps/cm2 at from −1.1V to +1.1V.

28. A capacitor comprising: an inner conductive metal capacitor electrode and an outer conductive metal capacitor electrode; anda capacitor dielectric region received between the inner and the outer conductive metal capacitor electrodes and having a thickness no greater than 150 Angstroms, the capacitor dielectric region comprising: a first Al2O3-comprising material outward of the inner electrode, the first Al2O3-comprising material having a thickness of from 2 Angstroms to 10 Angstroms;a ZrO2-comprising material outward of the first Al2O3-comprising material, the ZrO2-comprising material having a thickness of from 30 Angstroms to 70 Angstroms;a second Al2O3-comprising material outward of the ZrO2-comprising material, the second Al2O3-comprising material having a thickness of from 2 Angstroms to 16 Angstroms;a TixMyOz-comprising material outward of the second Al2O3-comprising material, where M is at least one of Zr, Hf, Ta, Si, Nb, or Al; the TixMyOz-comprising material having a thickness from 5 Angstroms to 100 Angstroms; anda sum of the thicknesses of the first Al2O3-comprising material, the ZrO2-comprising material, and the second Al2O3-comprising material totals no more than 70 Angstroms; the capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10−7 amps/cm2 at from −1.1V to +1.1V.

29. A capacitor comprising: an inner conductive metal capacitor electrode and an outer conductive metal capacitor electrode; anda capacitor dielectric region received between the inner and the outer conductive metal capacitor electrodes and having a thickness no greater than 150 Angstroms, the capacitor dielectric region comprising: a TixMyOz-comprising material outward of the inner electrode, where M is at least one of Zr, Hf, Ta, Si, Nb, or Al; the TixMyOz-comprising material having a thickness from 5 Angstroms to 100 Angstroms;a TiO2-comprising material outward of the TixMyOz-comprising material, the TiO2-comprising material having a thickness of from 40 Angstroms to 80 Angstroms; andthe capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10−7 amps/cm2 at from −1.1V to +1.1V.

30. A capacitor comprising: an inner conductive metal capacitor electrode and an outer conductive metal capacitor electrode; anda capacitor dielectric region received between the inner and the outer conductive metal capacitor electrodes and having a thickness no greater than 150 Angstroms, the capacitor dielectric region comprising: an optional first Al2O3-comprising material outward of the inner electrode, the optional first Al2O3-comprising material having a thickness of from 0 Angstroms to 10 Angstroms;a first material outward of the inner electrode and outward of the optional first Al2O3-comprising material if the optional first Al2O3-comprising material is present, the first material comprising at least one of ZrO2 or HfO2, the first material having a thickness of from 20 Angstroms to 50 Angstroms;an optional second Al2O3-comprising material outward of the first material comprising at least one of ZrO2 or HfO2, the optional second Al2O3-comprising material having a thickness of from 0 Angstroms to 16 Angstroms;a TiO2-comprising material outward of the first material that comprises the at least one of ZrO2 or HfO2 and outward of the optional second Al2O3-comprising material if the optional second Al2O3-comprising material is present, the TiO2-comprising material having a thickness of from 40 Angstroms to 80 Angstroms;a second material outward of the TiO2-comprising material, the second material comprising at least one of ZrO2 or HfO2, the second material having a thickness of from 10 Angstroms to 40 Angstroms, a sum of the thicknesses of the first material and the second material totaling no more than 70 Angstroms;an optional third Al2O3-comprising material outward of the second material comprising at least one of ZrO2 or HfO2, the optional third Al2O3-comprising material having a thickness of from 0 Angstroms to 10 Angstroms; andthe capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10−7 amps/cm2 at from −1.1V to +1.1V.

31. The capacitor of claim 30 wherein the first material comprises ZrO2.

32. The capacitor of claim 30 wherein the first material comprises HfO2.

33. The capacitor of claim 30 wherein the second material comprises ZrO2.

34. The capacitor of claim 30 wherein the second material comprises HfO2.

35. The capacitor of claim 30 wherein the capacitor dielectric region comprises each of the optional first, second, and third Al2O3-comprising materials.

36. The capacitor of claim 30 wherein the capacitor dielectric region is void of each of the optional first, second, and third Al2O3-comprising materials.

37. The capacitor of claim 30 wherein the capacitor dielectric region comprises the optional third Al2O3-comprising material.

38. The capacitor of claim 37 wherein the capacitor dielectric region is void of each of the optional first and second Al2O3-comprising materials.

39. The capacitor of claim 37 wherein the capacitor dielectric region is void of the optional first Al2O3-comprising material and comprises the optional second Al2O3-comprising material.

40. The capacitor of claim 37 wherein the capacitor dielectric region is void of the optional second Al2O3-comprising material and comprises the optional first Al2O3-comprising material.

41. The capacitor of claim 30 wherein the capacitor dielectric region is void of the optional third Al2O3-comprising material.

42. The capacitor of claim 41 wherein the capacitor dielectric region comprises each of the optional first and second Al2O3-comprising materials.

43. The capacitor of claim 41 wherein the capacitor dielectric region is void of the optional first Al2O3-comprising material and comprises the optional second Al2O3-comprising material.

44. The capacitor of claim 41 wherein the capacitor dielectric region comprises the optional first Al2O3-comprising material and is void of the optional second Al2O3-comprising material.

45. A capacitor comprising: an inner conductive metal capacitor electrode and an outer conductive metal capacitor electrode; anda capacitor dielectric region received between the inner and the outer conductive metal capacitor electrodes and having a thickness no greater than 150 Angstroms, the capacitor dielectric region comprising: an optional first Al2O3-comprising material outward of the inner electrode, the optional first Al2O3-comprising material having a thickness of from 0 Angstroms to 2 Angstroms;an AlxZryOz-comprising material outward of the inner electrode and outward of the optional first Al2O3-comprising material if the optional first Al2O3-comprising material is present, the AlxZryOz-comprising material having a thickness of from 2 Angstroms to 30 Angstroms;an optional second Al2O3-comprising material outward of the AlxZryOz-comprising material, the optional second Al2O3-comprising material having a thickness of from 0 Angstroms to 10 Angstroms;a first material outward of the AlxZryOz-comprising material and outward of the optional second Al2O3-comprising material if the optional second Al2O3-comprising material is present, the first material comprising at least one of ZrO2 or TixZryOz or ZraTixAlyOz, the first material having a thickness of from 30 Angstroms to 60 Angstroms;an optional third Al2O3-comprising material outward of the first material comprising at least one of ZrO2 or TixZryOz or ZraTixAlyOz, the optional third Al2O3-comprising material having a thickness of from 0 Angstroms to 4 Angstroms;a second material outward of the first material comprising at least one of ZrO2 or TixZryOz or ZraTixAlyOz and outward of the optional third Al2O3-comprising material if the optional third Al2O3-comprising material is present, the second material comprising at least one of TiO2 or TixZryOz or ZraTixAlyOz, the second material having a thickness of from 10 Angstroms to 70 Angstroms;an optional fourth Al2O3-comprising material outward of the second material comprising at least one of TiO2 or TixZryOz or ZraTixAlyOz, the optional fourth Al2O3-comprising material having a thickness of from 0 Angstroms to 4 Angstroms; andthe capacitor dielectric region having in combination a dielectric constant k of at least 35 and leakage current no greater than 1×10−7 amps/cm2 at from −1.1V to +1.1V.

46-51. (canceled)

52. The capacitor of claim 19 wherein the capacitor dielectric region has a dielectric constant k of at least 40.

53. The capacitor of claim 19 wherein the capacitor dielectric region has leakage current no greater than 5×10−8 amps/cm2 at from −1.1V to +1.1V.

54. The capacitor of claim 19 wherein the capacitor dielectric region has a dielectric constant k of at least 40 and has leakage current no greater than 5×10−8 amps/cm2 at from −1.1V to +1.1V.