Capped polymers

Abstract

Microbiocidal quaternary ammonium polymers which are made by condensing a difunctional tertiary amine with an excess of 1,4-dihalo-2-butene, then after removing the unreacted 1,4-dihalo-2-butene, adding to the reaction product a calculated quantity of monofunctional tertiary amine for the purpose of forming a linear polymer whose termini at both ends are quaternary ammonium moieties.

Description

This invention relates to a new class of microbiocidal agents. More particularly, this invention relates to linear quaternary ammonium polymers in which the quaternary ammonium moieties are part of the linear polymeric chain rather than appendages to, or part of, branches on the linear chain. Even more particularly, this invention relates to such linear polymeric quaternary chains in which the chains terminate in quaternary ammonium moieties, thereby making further chain propagation impossible. Such polymers may, therefore, be called "capped" polymers.

The products of this invention can be made by a two step reaction. In the first step, a difunctional tertiary amine is condensed with slightly more than the molar equivalent of a 1,4-dihalo-2-butene, after which the unreacted dihalo compound is removed, and the reaction is completed in a second step by adding a calculated quantity of monofunctional tertiary amine. A slight excess of the dihalo compound is required in the first step.

If the difunctional amine is represented by N(R') (R") ZN (R') (R") and the 1,4-dihalo-2-butene by X--CH.sub.2 --CH = CH--CH.sub.2 --X, where X is a halogen, then when the 1,4-dihalo-2-butene is not in excess, the first step of the reaction may be represented by the chemical equation: ##STR1## where X is a halogen such as chlorine or bromine, where n is an integer from about 2 to about 30; where R' and R" may be either (1) a primary or secondary alkyl radical having from 1 to 20 carbon atoms, (2) hydroxy or dihydroxy derivatives of R' and R", (3) benzyl, or (4) benzyl containing at least one alkyl group bonded to the benzene ring but where the sum of the carbon atoms on all such alkyl groups is less than 7; where Z consists of from one to three aliphatic divalent radicals, each of which has 2 to 10 carbon atoms, each aliphatic radical containing 0 to 2 double bonds and 0 to 2 hydroxy substituents; where the group (R') (R") N, taken together, may be N-piperidino, N-pyrolidino, N-morpholino or N-homopiperidino; and where the group (R') (R") --N--Z--N(R') (R"), taken together, may be N,N'-di-lower alkyl piperazine or 1,4-diazabicyclo (2.2.2) octane.

However, in the presence of a relatively small excess of 1,4-dihalo-2-butene, the terminal atoms of the linear polymeric product of the first step are halogen atoms, the product being: ##STR2## where the symbols have the same value or meaning as above.

Since these linear polymeric chains contain active halogen termini, the chains can be made to propogate if more difunctional tertiary amine is added to the reaction container already holding an excess of 1,4-dihalo-2-butene. However, if the unreacted dichloro compound is extracted and a monofunctional tertiary amine is added to the reaction container after the excess dichloro compound is removed, then it reacts with the two terminal halogen atoms of the linear chain to form two terminal quaternary moieties.

This latter reaction constitutes the second step of the process of the present invention, and may be represented as follows: ##STR3## where R'", R.sup.IV, R.sup.V may be either (1) primary or secondary alkyl containing from 1 to 20 carbon atoms, or (2) hydroxyethyl; where the group (R'") (R.sup.IV) (R.sup.V) taken together may be either N-lower alkylpyrolidino, N-lower alkyl piperidino or N-lower alkyl homopiperidino; and where the other symbols have the same value or meaning as described previously.

The following examples are illustrative of the present invention:

EXAMPLE 1

To 42.6 grams of 1,4-bis(dimethylamino)-2-butene (0.3 mole) dissolved in 100 ml. of water, there was added dropwise 50.0 grams of 1,4-dichloro-2-butene (0.4 mole) with constant stirring. The rate of addition was maintained at a rate to keep the exothermic reaction at a temperature of 60.degree. to 70.degree. C. When addition was complete, the reaction mixture was heated on a steam bath at about 90.degree. to 95.degree. C for more than two hours. Then it was cooled to 20.degree. C and extracted with three 100 ml. portions of ethyl ether to remove the unreacted 1,4-dichloro-2-butene, and the residue warmed in vacuo to remove ether from the layer containing the polyquaternary.

The polyquaternary aqueous layer was analyzed for total chlorine, and also for ionic chloride. The difference represented the quantity of terminal chlorine atoms on the polymeric chains.

The calculations showed that the equivalent of .03 moles of chlorine terminal atoms remained in the polyquaternary chains. Therefore, 4.75 grams of octyl dimethyl amine (0.03 mole) was added to the aqueous layer, and the mixture heated on a steam bath for 2 more hours at about 90.degree. to 95.degree. C. The reaction mixture was analyzed for total polymer quaternary content, and the concentration was adjusted to 50% active polyquaternary.

The experiment was repeated using petroleum ether instead of ethyl ether to extract the excess dichloro compound. The similar results indicated that any inactive organic solvent may be used to extract the unreacted 1,4-dichloro-2-butene.

EXAMPLE 2

In addition to the compound of Example 1, the following "capped" polymers were made by substituting other tertiary amines for octyl dimethyl amine, using the procedure of Example 1. They were as follows:

a. the polymeric quaternary formed by the reaction of 1,4-bis(dimethylamino)-2-butene and 1,4-dichloro-2-butene, capped by decyl dimethyl amine b. the polymeric quaternary formed by the reaction of 1,4-bis-(dimethylamino)-2-butene and 1,4-dichloro-2-butene, capped by dodecyl dimethyl amine c. the polymeric product formed by the reaction of 1,4-bis-(dimethylamino)-2-butene and 1,4-dichloro-2-butene, capped by tetradecyl dimethyl amine d. the polymeric product formed by the reaction of 1,4-bis-(dimethylamino)-2-butene and 1,4-dichloro-2-butene, capped by hexadecyl dimethyl amine

EXAMPLE 3

The following tertiary amines were also used to cap the polymeric quaternary of 1,4-bis-(dimethylamino)-2-butene and 1,4-dichloro-2-butene, using the procedure shown in example 1:

a. Propyl dimethyl amine, b. butyl dimethyl amine, c. pentyl dimethyl amine, d. hexyl dimethyl amine, e. dibutyl methyl amine, f. didecyl methyl amine, and g. di-octyl methyl amine.

Microbiocidal evaluations were made as follows:

EXAMPLE 4

Each potential microbiocidal capped quaternary ammonium polymer to be tested was dissolved in distilled water to the test concentration, and was added aseptically to previously sterilized cotton-stoppered 125 ml. Erlenmeyer flasks.

One set of flasks containing the potential microbiocide at concentrations of 25 ppm, 50 ppm, 75 ppm, 100 ppm, 150 ppm, 200 ppm, 250 ppm, and 300 ppm was inoculated by introducing into each flask 0.5 ml. of a 1/10 nutrient broth dilution of a 24 hour nutrient broth culture of Aerobacter aerogenes. Another set of test flasks containing the potential microbiocide at similar concentrations was inoculated by introducing into each flask 0.5 ml. of a 1/10 nutrient broth culture of Pseudomonas aeruginosa.

At intervals of 30, 60 and 180 minutes following inoculation, a 1 ml. aliquot was withdrawn from each flask and added to 9 ml. of sterile azolectin/"Tween 80" naturalizer from which tenfold serial dilutions were prepared in the sterile neutralizer solution.

Agar plates were prepared from 1 .times. 10.sup..sup.-2 and 1 .times. 10.sup..sup.-3 dilutions.

Simultaneously with each set of test flasks, a control of sterile distilled water was similarly inoculated, and aliquots were taken at the same time intervals and plated at 1 .times. 10.sup.4, 1 .times. 10.sup.5, and 1 .times. 10.sup.6 dilutions.

A comparison of the surviving organisms for various test concentrations of the test material at different time intervals was made and tabulated.

The results were as follows:

Table 1

Number of survivors of A. Aerogenes following exposure to various capped polyquaternaries at different concentrations for varying periods of time.

Table 1__________________________________________________________________________Number of survivors of A. Aerogenes following ex-posure to various capped polyquaternaries at different con-centrations for varying periods of time. Concentration No. of surviving Organisms/ml .times. 10.sup.2Compound in ppm After 30 Min. 60 Min. 180 Min.__________________________________________________________________________Example 1 50 45 10 0 75 24 4 0Example 2 (a) 50 72 9 0 75 46 6 0Example 2 (b) 50 24 6 0 75 12 5 0Example 2 (c) 50 37 14 0 75 28 10 0Example 2 (d) 50 56 29 0 75 24 13 0Untreated Control 45,000 55,000 111,000__________________________________________________________________________

Table 2

Number of survivors of P. aeruginosa following exposure to various capped polyquaternaries at different concentrations for varying periods of time.

Table 2__________________________________________________________________________Number of survivors of P. aeruginosa following exposureto various capped polyquaternaries at different concentrations forvarying periods of time. Concentration No. of Surviving Organisms/ml .times. 10.sup.2Compound in ppm After 30 Min. 60 Min. 180 Min.__________________________________________________________________________Example 1 50 940 466 0 75 480 275 0 100 84 26 0Example 2 (a) 50 750 205 0 75 230 140 0 100 105 44 0Example 2 (b) 50 695 137 0 75 192 59 0 100 82 30 0Example 2 (c) 50 746 150 0 75 412 81 0 100 65 17 0Example 2 (d) 50 746 176 0 75 390 89 0 100 74 26 0Untreated Control 40,000 65,000 90,000__________________________________________________________________________

The results of these tests show that the "capped" polyquaternary ammonium products are very effective microbiocides in concentrations at least as low as 50 ppm.

Claims

1. A method of making a capped polymer which comprises (a) adding dropwise to a difunctional unsubstituted tertiary amine, a greater than molar equivalent of 1,4-dihalo-2-butene at a rate to maintain the resulting exothermic reaction at between about 60.degree.-70.degree. C, (b) heating the reaction mixture to a temperature immediately below the boiling point of the mixture for more than 2 hours, (c) cooling the mixture to about room temperature, (d) extracting, with a solvent, any unreacted 1,4-dihalo-2-butene from the resulting polyquaternary compound, and then (e) reacting the residue with an unsubstituted monotertiary amine at a temperature immediately below the boiling point of the mixture, said monotertiary amine having the formula N(R'") (R.sup.IV) (R.sup.V) where R'", R.sup.IV and R.sup.V are selected from the group consisting of (a) primary and secondary alkyls having 1 to 20 carbon atoms and (b) hydroxyethyl, and being in a quantity which is about equal to the molar equivalent of the halogen termini of the residue.

2. The method of claim 1 wherein the difunctional tertiary amine has the formula N(R') (R")Z--N(R') (R") in which Z consists of one to three divalent aliphatic radicals, each of 2 to 10 carbon atoms and each having 0 to 2 double bonds and 0 to 2 hydroxyl substituents, and wherein R' and R" are selected from the group consisting of (a) primary or secondary alkyl having 1 to 20 carbon atoms, (b) hydroxy or dihydroxy derivatives of alkyl groups having 1 to 20 carbon atoms, (c) benzyl, and (d) benzyl having at least one alkyl group bonded to the benzene ring with the sum of all alkyl carbons being less than 7, R' being absent when Z consists of two divalent aliphatic radicals, and both R' and R" being absent when Z consists of three divalent aliphatic radicals.

3. The method of claim 1 wherein the di-tertiary amine is 1,4-bis(dimethylamino)-2-butene.

4. The method of claim 1 wherein the mono tertiary amine is selected from the group consisting of octyl dimethyl amine, decyl dimethyl amine, dodecyl dimethyl amine, tetradecyl dimethyl amine, hexadecyl dimethyl amine, propyl dimethyl amine, butyl dimethyl amine, pentyl dimethyl amine, hexyl dimethyl amine, dibutyl methyl amine, didecyl methyl amine, and dioctyl methyl amine.