Carbodiimide compound and water repellent compositions

TECHNICAL FIELD
This invention relates to a new carbodiimide compound and to compositions comprising a fluorochemical oil and water repellent agent and said carbodiimide compound. This invention, in another aspect, relates to a method for imparting oil and water repellent properties to fibrous substrates and other materials and to the resulting treated substrates.
BACKGROUND
The use of various fluorochemical compositions on fibers and fibrous substrates, such as textiles, paper and leather, to impart oil and water repellency is known. See for example, Banks, Ed., Organofluorine Chemicals and Their Industrial Applications, Ellis Horwood Ltd., Chichester, England, 1979, pp. 226-234. Such fluorochemical compositions include, for example, fluorochemical guanidines (U.S. Pat. No. 4,540,497), compositions of cationic and non-ionic fluorochemicals (U.S. Pat. No. 4,566,981), compositions containing fluorochemical carboxylic acid and epoxidic cationic resin (U.S. Pat. No. 4,426,466), and fluoroaliphatic alcohols (U.S. Pat. No. 4,468,527).
Additives have been employed to assist in the oil and water repellency of fluorochemical treating agents. U.S. Pat. No. 4,215,205 teaches that durable launderable and dry-cleanable repellency to water and oil is conferred on fabrics consisting of hydrophobic synthetic fibers by application of a blend of a fluoroaliphatic vinyl polymer and a carbodiimide.
Fluorochemicals are generally expensive. Therefore, hydrocarbon additives, also called extenders, have been developed in order to reduce cost. Modified synthetic resins, waxes, melamines, paraffin emulsions, and similar products have been used as extenders.
U.S. Pat. No. 4,834,764 describes a process for obtaining wash- and cleaning-resistant textile finishes by impregnating with reactive perfluoroalkyl-containing (co)polymers and/or precondensates in aqueous dispersion and heating, wherein the dispersions have NCO-containing compounds which have a molecular weight of at least 450 and/or contain a diphenylmethane-based polyisocyanate mixture in blocked form.
U.S. Pat. No. 5,164,252 teaches that phobicity effects of high quality and permanence are obtained on textile materials of the most diverse types if they are finished with combinations of A) a polymer containing perfluoroalkyl groups and B) a cationically modified polyurethane.
U.S. Pat. No. 5,132,028 discloses compositions for imparting water and oil repellency to fabrics such as silk, said compositions containing a fluorochemical-type, water and oil repellent agent, a carbodiimide, and at least one component selected from the group consisting of plasticizer, metal alcoholate or ester, zirconium salt, alkylketene dimer, aziridine, and alkenyl succinic anhydride.
DISCLOSURE OF INVENTION
It is an object of the present invention to provide a new carbodiimide compound which can be used as an extender. It is a further object of the present invention to provide a water and oil repellency imparting composition which has a low fluorine content. Furthermore it is an object of the invention to provide a composition and a process for conferring both static and especially dynamic water resistance onto fibers, particularly to cellulosic type fibers.
The present invention provides a carbodiimide compound obtainable from a reaction mixture comprising an isocyanate compound and a monofunctional alcohol in a non-reactive solvent in the presence of a suitable catalyst, characterized in that the isocyanate compound and the monofunctional alcohol, except for the hydroxy group, are free from isocyanate reactive hydrogen atoms and the monofunctional alcohol is a branched aliphatic alcohol containing at least 8 carbon atoms.
In a further aspect, the present invention provides a water repellent composition comprising (A) a fluorochemical oil and water repellent agent; and (B) said carbodiimide as extender. The treatment composition of the invention is characterized by a low overall fluorine content. The invention provides an oil and water repellent treatment composition suitable for synthetic and especially for cellulosic fibers and substrates. The treatment provides a gentle touch to the fibers and substrates and displays a high durability to cleaning. Said carbodiimides are amorphous in nature, are essentially fluorine free and contain terminal portions which are branched aliphatic moieties, preferably derived from branched higher alcohols.
In another aspect, the present invention provides a method for imparting oil- and water-repellent properties to a fibrous substrate comprising the steps of (1) applying to the surface of a fibrous substrate an amount of the water repellent composition just described, wherein said fluorochemical agent and said carbodiimide extender are present in a total combined amount of 0.01% to 5% by weight based on the weight of the fibrous substrate, and (2) heating the treated substrate from step 1 at a temperature and for a time sufficient to cure the treated substrate. In another aspect, this invention provides substrates treated with the fluorochemical composition of this invention.
The amorphous carbodiimides useful in the compositions of this invention act as excellent extenders in treatment of fibrous substrates, thus allowing more efficient use of the more expensive fluorochemical agent.
DETAILED DESCRIPTION
In general, fluorochemical agents useful in the invention include any of the known fluoroaliphatic radical-containing agents useful for the treatment of fabrics to obtain oil and water repellency. Fluorochemical radical-containing agents include condensation polymers such as polyesters, polyamides or polyepoxides and vinyl polymers such as polyacrylates, polymethacrylates or polyvinyl ethers. Such known agents include, for example, those described in U.S. Pat. No. 3,546,187; U.S. Pat. No. 3,544,537; U.S. Pat. No. 3,470,124; U.S. Pat. No. 3,445,491; U.S. Pat. No. 3,341,497 and U.S. Pat. No. 3,420,697.
Further examples of such fluoroaliphatic radical-containing water and oil repellency imparting agents include those formed by the reaction of perfluoroaliphatic glycols or thioglycols with diisocyanates to provide perfluoroaliphatic group-bearing polyurethanes. These products are normally applied as aqueous dispersions for fibre treatment. Such reaction products are described, for example, in U.S. Pat. No. 4,054,592. Another group of compounds which can be used are fluoroaliphatic radical-containing N-methylolcondensation products. These compounds are described in U.S. Pat. No. 4,477,498. Further examples include fluoroaliphatic radical containing polycarbodiimides which can be obtained by, for example, reaction of perfluoroaliphatic sulfonamido alkanols with polyisocyanates in the presence of suitable catalysts.
The fluorochemical compound is preferably a copolymer of one or more fluoroaliphatic radical-containing acrylate or methacrylate monomers, and one or more fluorine-free (or hydrocarbon) terminally ethylenically-unsaturated comonomers. Classes of the fluorochemical monomers can be represented by the formulas
R.sub.f R.sup.1 OCOC(R.sup.2).dbd.CH.sub.2
and R.sub.f SO.sub.2 N(R.sup.3)R.sup.4 OCOC(R.sup.2).dbd.CH.sub.2
where R.sub.f is a fluoroaliphatic radical;
R.sup.1 is an alkylene with 1 to 10 carbon atoms, e.g. methylene or ethylene, or --CH.sub.2 CH(OR)CH.sub.2 --, in which R is hydrogen or COCH.sub.3 ;
R.sup.2 is hydrogen or methyl;
R.sup.3 is hydrogen or an alkyl with 1 to 20, preferably 1 to 10 carbon atoms, e.g. methyl or ethyl; and
R.sup.4 is an alkylene with 1 to 20, preferably 1 to 10 carbon atoms, e.g. methylene or ethylene.
The fluoroaliphatic radical, called R.sub.f for brevity, is a fluorinated, stable, inert, preferably saturated, non-polar, monovalent aliphatic radical. It can be straight chain, branched chain, cyclic or combinations thereof It can contain heteroatoms, bonded only to carbon atoms, such as oxygen, divalent or hexavalent sulfur, or nitrogen. R.sub.f is preferably a fully-fluorinated radical, but hydrogen or chlorine atoms can be present as substituents if not more than one atom of either is present for every two carbon atoms. The R.sub.f radical has at least 3 carbon atoms, preferably 3 to 14 carbon atoms, and preferably contains about 40% to about 80% fluorine by weight, more preferably about 50% to about 78% fluorine by weight. The terminal portion of the R.sub.f radical is a perfluorinated moiety, which will preferably contain at least 7 fluorine atoms, e.g., CF.sub.3 CF.sub.2 CF.sub.2 --, (CF.sub.3).sub.2 CF--, F.sub.5 SCF.sub.2 --. The preferred R.sub.f radicals are fully or substantially fluorinated and are preferably those perfluorinated aliphatic radicals of the formula C.sub.n F.sub.2n+1 -- where n is 3 to 14.
Representative examples of fluorochemical monomers include: ##STR1##
Preferred co-monomers which can be copolymerized with the above-described fluoroaliphatic radical-containing monomers include those selected from the group consisting of octadecylmethacryate, 1,4-butanediol diacrylate, laurylmethacrylate, butylacrylate, N-methylol acrylamide, isobutylmethacrylate, ethylhexyl acrylate, ethylhexyl methacrylate, vinylchloride and vinylidene chloride. The relative weight ratio of the fluoroaliphatic monomer(s) to the hydrocarbon co-monomer(s) can vary as is known in the art.
The carbodiimide extenders of this invention are amorphous in nature with a typical glass transition temperature between -30.degree. C. and +80.degree. C. and are represented by the general formulas (I)-(III): ##STR2## wherein: n is 0 or an integer from 1 to 4; m is an integer from 1 to 20, preferably from 1 to 10.p and r+s are 1, 2 or 3, respectively for di-, tri- or tetraisocyanates; q, u+t and v+w are 0, 1 or 2 respectively for di-, tri- or tetraisocyanates.
Y is a divalent linking group obtained by removing active hydrogens from a poly(oxy)alkylene diol, tertiary amino group containing diol or quaternary ammonium group containing diol.
The linking group A is an organic residue obtained by removing all isocyanate groups from an isocyanate compound. The A-groups may be the same or different. Some of the A-groups may be, for example trivalent or tetravalent derived from triisocyanates or tetraisocyanates such as polymethylene polyphenyl isocyanates. When A is polyvalent, branched or crosslinked polycarbodiimides can result. Different A-groups may be used together to give slight branching in order to modify properties. Substituents may be present in A provided they contain no isocyanate-reactive hydrogen atoms; that is, groups such as --OH are normally excluded. Unsubstituted organic linking groups are preferred. Preferred groups A are for example ##STR3##
The terminal and pending groups R.sup.5, R.sup.6 and R.sup.7 are independently monovalent organic radicals free from isocyanate reactive hydrogen atoms and containing a branched aliphatic terminal moiety of at least 8 carbon atoms. More preferably at least 8 to 60 carbon atoms, especially 14 to 60 carbon atoms. The branching can be random, but preferably it is alpha-branching.
In a preferred embodiment, the R.sup.5, R.sup.6 and R.sup.7 groups are each independently a group of the general formula ##STR4##
wherein R.sup.14 is a branched C.sub.8-60 alkyl group.
Preferably, R.sup.5, R.sup.6, R.sup.7 and A are essentially free from fluorine (i.e. do not contain more than 0.3% by weight of fluorine).
The terminal groups R.sup.8, R.sup.9 and R.sup.12 are monovalent organic radicals containing a poly(oxy)alkylene moiety and/or tertiary amino group and/or quaternary ammonium function. Useful examples for R.sup.8, R.sup.9 and R.sup.12 include ##STR5##
The terminal groups R.sup.10, R.sup.11 and R.sup.13 are monovalent organic radicals obtained by removing an active hydrogen from a poly(oxy)alkylene diol monoalkylether, tertiary amino group containing alcohol or quaternary ammonium group containing alcohol. Useful examples of R.sup.10, R.sup.11 and R.sup.13 include e.g. ##STR6##
Carbodiimides can be obtained by condensation of isocyanates in the presence of suitable catalysts as described, for example by K Wagner et al., Angew. Chem. Int. Ed. Engl., vol 20, p 819-830 (1981); by S. R. Sandler et al., Org. Functional Group Prep., vol 2, p 205-222 (1971) and by A Williams et al., Chem. Rev., vol 81, p 589-636 (1981). The preparation of urethane containing or urethane terminated polycarbodiimides has been described in e.g. U.S. Pat. No. 2,941,983 and by T. W. Campbell et al. in J. Org. Chem., 28, 2069 (1963).
The carbodiimides of the invention are usually made in a two step reaction starting from diisocyanates or multifunctional isocyanates and monofunctional alcohols in a non-reactive solvent such as methyl isobutyl ketone, at a concentration of about 40% of dissolved materials. The reaction mixture is prepared so that water is removed before addition of isocyanates, and is heated until the urethane reaction is complete. After completion of the urethane reaction, in a second step, the carbodiimide is formed after adding a phospholine oxide or other suitable catalyst. Representative examples of suitable catalysts are described in e.g. U.S. Pat. No. 2,941,988, U.S. Pat. No. 3,862,989 and U.S. Pat. No. 3,896,251. Examples include 1-ethyl- 3-phospholine, 1-ethyl-3-methyl-3-phospholine-1-oxide, 1-ethyl-3-methyl-3-phospholine-1-sulfide, 1-ethyl-3-methyl-phospholidine, 1-ethyl-3-methyl-phospholidine-1-oxide, 3-methyl-1-phenyl-3-phospholine-1-oxide and bicyclic terpene alkyl or hydrocarbyl aryl phosphine oxide or camphene phenyl phosphine oxide.
The particular amount of catalyst used will depend to a large extent on the reactivity of the catalyst itself and the organic polyisocyanate being used. A concentration range of 0.1-10 parts of catalyst per 100 parts of organic diisocyanate is suitable. About 0.5-2.0 parts of catalyst is satisfactory when aromatic diisocyanates are used. The final reaction mixture can be dispersed in water and further diluted with water before application.
In order to improve the stability of the emulsions prepared from the carbodiimides of the present invention, poly(oxy)alkylene and/or tertiary or quaternary amino-group containing reactants with at least one active hydrogen may be incorporated into the carbodiimide. Therefore, in a further embodiment of the present invention the reaction mixture used for the preparation of the carbodiimides comprises an amount of a poly(oxy)alkylene and/or a tertiary or quaternary amino group containing reactant with at least one active hydrogen.
Poly(oxy)alkylene reactants with at least one active hydrogen used in the preparation of carbodiimides are normally liquid or low melting solids. They can be represented by the general formula:
H--(R').sub.n --OR"
wherein
R' is an oxyalkylene group with 2 to 4 carbon atoms; n is an integer of at least 4, generally 10 to 75 and can be as high as 100 or higher
R" is hydrogen or an alkyl group having 1 to 4 carbon atoms.
Said R' group is an oxyalkylene group having 2 to 4 carbon atoms, such as --OCH.sub.2 CH.sub.2 --, --OCH.sub.2 CH.sub.2 CH.sub.2 --, --OCH(CH.sub.3)CH.sub.2 --and --OCH(CH.sub.3)CH(CH.sub.3)--. Preferably the oxyalkylene units in said poly(oxyalkylene) are the same, as in poly(oxypropylene), or are present as two types of groups, as in a straight or branched chain or randomly distributed oxyethylene and oxypropylene units, or as in a straight or branched chain of blocks of oxyethylene units and blocks of oxypropylene units. Poly(oxy)alkylene reactants having amino functionality can be used as well.
The molecular weight of the poly(oxyalkylene) reactant can be as low as 200 but preferred is about 300 to 4000 or higher. When used, the poly(oxyalkylene) reactant can be present up to about 20% by weight based on the total weight of the carbodiimide. The poly(oxyalkylene)radicals in the carbodiimide can be the same or different, and they can be pendent.
Representative active hydrogen-group containing tertiary organo amine reactants useful in the preparation of carbodiimides include 2-dimethylaminoethanol, 2-diethylaminoethanol, 2-diisopropylaminoethanol, N-methyldiethanolamine, triethanolamine, 1-methyl-3-pyrrolidinol, 2(2-hydroxyethyl)pyridine, N(2-hydroxyethyl)morpholine, 1,4-bis(2-hydroxypropyl)-piperazine, 1,1-dimethyl-4-dimethylamino-n-butanol, N(2-hydroxyethyl)-N-methylaniline, 2-dimethylaminoethanethiol, N,N-bis(2-mercaptoethyl)methylamine, 4-diethylamino-1-methyl-n-butanol, 1 -dimethylamino-2propanol, 3-dimethylamino-1-propanol, 3-dimethylamino-2hydroxy-n-propanol and mixtures thereof.
The amino-group containing carbodiimides can be converted to quaternary compounds using alkylating agents or acids. Quaternizing alkylating agents and acids useful in this invention include methyl iodide, methyl bromide, allyl chloride, benzyl chloride, diethylsulfate, dimethylsulfate, epichlorohydrin, hydrochloric acid, acetic acid, glycolic acid and the like. When used, the reactant containing aminofunctional groups will be present up to about 5% by weight based on the total weight of reactants.
The water repellent compositions of the invention can be prepared by blending emulsions of fluorochemical oil and water repellent agent and carbodiimide, together with any desired compatible additives. Alternatively, the fluorochemical agent and the carbodiimide can be prepared in solution and the solutions blended, diluted if necessary and applied to the substrate.
In order to improve fixing of the composition of the invention to a substrate, it is sometimes advantageous to include in the dispersion certain additives, polymers, thermo-condensable products and catalysts capable of promoting interaction with the substrate. Among these are the condensates or precondensates of urea or melamine with formaldehyde (sometimes referred to herein as resins) and glyoxal resins. Particular suitable additives and amounts thereof can be selected by those skilled in the art.
The amount of the treating composition applied to a substrate in accordance with this invention is chosen so that sufficiently high or desirable water and oil repellencies are imparted to the substrate surface, said amount usually being such that 0.01% to 5% by weight, preferably 0.05% to 2% by weight, based on the weight of the substrate, of water repellent composition (fluorochemical and carbodiimide) is present on the treated substrate. The amount which is sufficient to impart desired repellency can be determined empirically and can be increased as necessary or desired.
The carbodiimide extender is present in an amount sufficient to improve the fluorine efficiency of the fluorochemical agent. "Improvement in fluorine efficiency" as used herein designates that improved or equal repellency properties are obtained when part of the fluorochemical treating agent, preferably 10 to 50% by weight of fluorochemical treating agent, is replaced by the carbodiimide. Generally, the carbodiimide is present in an amount of about 5 to about 500, preferably about 10 to about 200, and most preferably about 25 to about 100 parts by weight based on 100 parts by weight of the fluorochemical treating agent.
The composition of this invention can be applied using conventional application methods and can be used as an aqueous dispersion or alternatively it can be used as a treatment composition in solvent. A dispersion will generally contain water, an amount of composition effective to provide repellent properties to a substrate treated therewith, and a surfactant in an amount effective to stabilize the dispersion. Water is preferably present in an amount of about 70 to about 20000 parts by weight based on 100 parts by weight of the composition of the invention. The surfactant is preferably present in an amount of about 1 to about 25 parts by weight, preferably about 5 to about 10 parts by weight, based on 100 parts by weight of the inventive composition. Conventional cationic, nonionic, anionic, and zwitterionic surfactants are suitable.
In order to effect treatment of a substrate, the substrate can be immersed in the dispersion and agitated until it is saturated. The saturated substrate can then be run through a padder/roller to remove excess dispersion, dried in an oven at a relatively low temperature (eg., 70.degree. C.) for a time sufficient to remove the dispersion medium (e.g.; water, ethylene glycol, or a mixture thereof), and cured at a temperature and for a time sufficient to provide a cured treated substrate. This curing process can be carried out at temperatures between about 110.degree. C. and about 190.degree. C. depending on the particular system or application method used. In general, a temperature of about 150.degree. C. for a period of about 20 seconds to 10 minutes, preferably 3 to 5 minutes, is suitable. The cured treated substrate can be cooled to room temperature and used as desired, eg. incorporated or fashioned into a garment such as rainwear.
The substrates treated by the water and oil repellency imparting composition of this invention are not especially limited and include, e.g., textile fabrics, fibres, non-wovens, leather, paper, carpet, plastic, wood, metal, glass, concrete and stone. Preferred are textile fabrics, fibres and non-wovens, especially of the cellulosic type, such as eg. rayon, cotton, linen.
Formulation and Treatment Procedure
Treatment baths were formulated containing a defined amount of the fluorochemical treatment agent and the carbodiimide. Treatments were applied to the test substrates by padding at a concentration of 0.3% solids (based on fabric weight and indicated as SOF (solids on fabric)) unless otherwise indicated, and drying and curing at 150.degree. C. for 3 minutes. Substrates used for the evaluation of treatments of this invention are all commercially available and are listed below:
PES/CO: Grey polyester/cotton 65/35, style No. 2681, obtained through Utexbel N.V., Ghent, BELGIUM
100% Cotton: bleached, mercerized cotton poplin, style No. 407, purchased from Testfabrics, Inc., USA
100% Polyamide: Polyamide microfiber, obtained from Sofinal BELGIUM
100% Polyester: Polyester microfiber, obtained from Sofinal BELGIUM
Respective data of water and oil repellency shown in the Examples and Comparative Examples are based on the following methods of measurement and evaluation criteria.
Bundesmann Test
The impregnating effect of rain on treated substrates is determined using the Bundesmann Test Method (DIN 53888). In this test, the treated substrates are subjected to a simulated rainfall, while the back of the substrate is being rubbed. The appearance of the upper exposed surface is checked visually after 1, 5 and 10 minutes and is given a rating between 1 (complete surface wetting) and 5 (no water remains on the surface). Besides the observation of the wetting pattern also the water absorption (% ABS) and penetration after 10 min rain test can be quantitatively measured. Well treated samples give low absorption and penetration results.
Spray Rating (SR)
The spray rating of a treated substrate is a value indicative of the dynamic repellency of the treated substrate to water that impinges on the treated substrate. The repellency is measured by Standard Test Number 22, published in the 1985 Technical Manual and Yearbook of the American Association of Textile Chemists and Colorists (AATCC), and is expressed in terms of `spray rating` of the tested substrate. The spray rating is obtained by spraying 250 ml water on the substrate from a distance of 15 cm. The wetting pattern is visually rated:using a 0 to 100 scale, where 0 means complete wetting and 100 means no wetting at all.
Oil Repellency (OR)
The oil repellency of a treated substrate is measured by the American Association of Textile Chemists and Colorists (AATCC) Standard Test Method No. 118-1983, which test is based on the resistance of a treated substrate to penetration by oils of varying surface tensions. Treated substrates resistant only to Nujol.RTM., mineral oil (the least penetrating of the test oils) are given a rating of 1, whereas treated substrates resistant to heptane (the most penetrating of the test oils) are given a rating of 8. Other intermediate values are determined by use of other pure oils or mixtures of oils, as shown in the following table.
______________________________________Standard Test LiquidsAATC Oil RepellencyRating Number Compositions______________________________________1 Nujol .RTM.2 Nujol .RTM. /n-hexadecane 65/353 n-Hexadecane4 n-Tetradecane5 n-Dodecane6 n-Decane7 n-Octane8 n-Heptane______________________________________
Laundering Procedure
The procedure set forth below was used to prepare treated substrate samples designated in the examples below as "5 Launderings (5L)".
A 230 g sample of generally square, 400 cm.sup.2 to about 900 cm.sup.2 sheets of treated substrate was placed in a washing machine along with a ballast sample (1.9 kg of 8 oz fabric in the form of generally square, hemmed 8100 cm.sup.2 sheets). Conventional detergent (Tide, 46 g) is added and the washer is filled to high water level with hot water (40.degree. C. .+-.3.degree. C.). The substrate and ballast load is washed five times (no drying in between the cycles) using a 12-minute normal wash cycle followed by five rinse cycles and centrifuging. The dry substrate is pressed using a hand iron set at the temperature recommended for the particular substrate fabric.
Abbreviations
The following abbreviations and trade names are used in the examples:
MeFOSEA: C.sub.8 F.sub.17 SO.sub.2 N(CH.sub.3)CH.sub.2 CH.sub.2 OC(O)CH.dbd.CH.sub.2
MeFOSEMA: C.sub.8 F.sub.17 SO.sub.2 N(CH.sub.3)CH.sub.2 CH.sub.2 OC(O)C(CH.sub.3).dbd.CH.sub.2
EHMA: n--C.sub.4 H.sub.9 CH(C.sub.2 H.sub.5)CH.sub.2 OC(O)C(CH.sub.3).dbd.CH.sub.2
N-MAM: HOCH.sub.2 NHC(O)CH.dbd.CH.sub.2 (48 wt% aqueous solution)
MDI: 4,4'methylene diphenyl diisocyanate (available as Desmodur 44 MS from Bayer, Leverkusen, Germany)
TDI: toluene diisocyanate (available as Desmodur T100 from Bayer, Leverkusen, Germany)
Voranate M220: polymethylene polyphenyl isocyanate, available from Dow Chemical, Terneuzen, The Netherlands
Guerbitol-16: 2-alkylalkanols, known as Guerbet alcohols,
Guerbitol-18: the number indicating the average chain
Guerbitol-20: length; available from Henkel, Dusseldorf, Germany
Isofol-14T: 2-alkylalkanols
Isofol-16: the number indicating the
Isofol-18T: average chain length;
Isofol-20: available from Condea, Brunsbuttel,
Isofol-24: Germany
Prisorine 3515: methyl branched isostearylalcohol available from Unichema Chemie, Gouda, The Netherlands
Jeffamine 715: monofunctional polyoxyalkyleneamine with an average molecular weight (Mw) of 715, available from Huntsman, Tex., USA
MPEG 750: monofunctional methoxyterminated polyethylene-
MPEG 350: glycols with an average Molecular weight of 750 and 350 respectively, available from Acros Chimica, Geel, Belgium
DEAE: N-diethylaminoethanol, available from Acros Chemica, Geel, Belgium
Ethoquad 18/25: Methyl polyoxyethylene(15)octadecyl ammonium chloride, available from Akzo, Littleborough, UK
Ethoquad HT-25: Methyl polyoxyethylene (15) hydrogenated tallow ammonium chloride, available from Akzo, Littleborough, UK
Arquad T-50: tallow trimethyl ammonium chloride, available from Akzo, Littleborough, UK
Arquad 2HT-75: dimethyl-dihydrogenated tallow ammonium chloride; available from Akzo, Littleborough, UK
Atpol E5721: alkylethoxylate, available from ICI, Wilton, UK
Atlas G1281: polyoxyethylene fatty glyceride, available from ICI, Wilton, UK
Marlowet 5401: polyethoxylated amine salt, available from Hulls, Marl, Germany
All parts, ratios, percentages, etc. in the following examples and the rest of the specification, are by weight unless otherwise noted.
Preparation of the Carbodiimide Compounds
Several hydrocarbon carbodiimides (HCD) as given in table 1 have been prepared according to the general procedure as described for the synthesis of the carbodiimide made from MDI/Guerbitol-18 in a molar ratio of 2/1. The carbodiimides are emulsified before addition to the fluorochemical composition.
A. Preparation of Hydrocarbon Carbodiimide
The hydrocarbon carbodiimides are prepared in two steps. First a urethane reaction is carried out between the branched alcohol and an isocyanate. In a second step, the carbodiimide is formed.
1. For the first reaction, a 1 liter 3-necked glass reaction flask, equipped with a thermometer, a Dean-Stark condenser, a nitrogen inlet tube, a mechanical stirrer, and an electric heating mantle is charged with 0.4 mole Guerbitol-18 in methyl isobutyl ketone (MIBK) at a concentration of 22% by weight, under an atmosphere of dry nitrogen. The solution is heated until reflux and 100 g distillate is removed via the Dean Stark condenser. The Dean Stark condenser is subsequently replaced by a normal reflux condenser. The reaction mixture is cooled to 55.degree. C., after which 0.8 mole of MDI is added. The reaction mixture is heated to 60.degree. C. and stirred until a clear solution is obtained. 40 mg dibutyl tin dilaurate catalyst (available from Air Products Company) is added and the reaction mixture is stirred for 3 hours at 80.degree. C.
2. In a second step, the carbodiimide is formed. A camphene phenyl phosphine oxide catalyst is added to the mixture (2% based on MDI solids). The reaction is then run for 10 hours at 100.degree. C. at which time the isocyanate functional groups have been fully converted into carbodiimide functions as shown by FTIR spectroscopy. The final product is a slightly hazy solution.
B. Emulsification
The carbodiimides prepared can be emulsified using different surfactants or mixtures of surfactants, following the general procedure as described for the Marlowet 5401 surfactant. A solution of 126 g deionized water and 4 g Marlowet 5401 surfactant is heated to 75.degree. C. in a 500 ml beaker. 100 g carbodiimide solution (50% solids) as prepared under A is heated to 75.degree. C. and added to the surfactant solution while stirring vigourously. This preemulsion is converted into a stable milky dispersion using a Branson 250 Sonifier. The MIBK solvent can be distilled off with a Buchi rotavapor using waterjet vacuum. The carbodimides given in table 1 have been emulsified according to this general method.
The kind and amount of surfactant may be varied, depending on the carbodiimide used, especially the carbodiimides that contain poly(oxyalkylene) or amine groups can be emulsified with lower level of or no surfactant added. Depending on the solubility of the surfactant, the surfactant can be added to the aqueous or to the organic phase.
TABLE 1__________________________________________________________________________Structure of carbodiimides Poly(oxy)alkylene or amino-groupAbbrev. Isocyanate Alcohol containing reactant Molar Ratio__________________________________________________________________________HCD-1 MDI Prisorine 3515 3/2HCD-2 MDI Prisorine 3515 2/1HCD-3 MDI Guerbitol-16 3/2HCD-4 MDI Guerbitol-18 3/2HCD-5 MDI Guerbitol-18 2/1HCD-6 MDI Guerbitol-20 3/2HCD-7 MDI Guerbitol-20 2/1HCD-8 MDI Isofol-14T 3/2HCD-9 MDI Isofol-16 3/2HCD-10 MDI Isofol-18T 3/2HCD-11 MDI Isofol-18T 2/1HCD-12 MDI Isofol-20 3/2HCD-13 MDI Isofol-24 3/2HCD-14 MDI 2-Ethylhexanol 3/2HCD-15 TDI Guerbitol-18 2/1HCD-16 Voranate Prisorine 3515 3/5 M220HCD-17 MDI Guerbitol-18 Jeffamine 715 3/1.8/0.2HCD-18 MDI Guerbitol-18 MPEG 750 3/1.8/0.2HCD-19 MDI Guerbitol-18 DEAE 3/1.8/0.2HCD-20 MDI Guerbitol-18 MPEG 750 3/1.9/0.1HCD-21 MDI Guerbitol-18 MPEG 750/DEAE 3/1.8/0.1/0.1HCD-22 MDI Isofol-18T MPEG 350 3/1.9/0.1HCD-23 MDI Isofol-18T MPEG 350 3/1.8/0.2HCD-24 MDI Isofol-18T MPEG 350 4/1.9/0.1HCD-25 MDI Isofol-18T MPEG 350 4/1.8/0.2__________________________________________________________________________
It has been found that the use of ammonium surfactants having two long chain alkyl groups or mixtures of said ammonium surfactants and nonionic surfactants afford increased emulsion stability, especially when hard water is used to dilute the emulsion.
Ammonium surfactants having two long chain alkyl groups can be represented by the general formula ##STR7## wherein: --R.sup.15 and R.sup.16 each and independently are long chain alkyl groups containing at least eight carbon atoms, preferably from 8 to 24 carbon atoms or benzyl and --R.sup.17 and R.sup.18 each and independently are short chain alkyl groups having from 1 to 8 carbon atoms or hydrogen. X can be halogen (Cl--, Br--, I--)HSO.sub.4 --CH.sub.3 --COO--.
The use of ammonium surfactants having two long chain alkyl groups increases emulsion stability, without sacrifice of the properties of the treated substrate. It seems that the same effects are observed not only for carbodiimide emulsions but in general for hydrocarbon and fluorochemical emulsions.
Synthesis of the fluorochemical carbodiimide (FCD) used in comparative examples C-2 to C-8, C-10, C-12, C-14 and C-16
The fluorochemical carbodiimide FCD, used in comparative examples C-2 to C-8, C-10, C-12, C-14 and C-16 has been prepared according to example 2 in U.S. Pat. No. 4,024,178, with the exception that MDI was used instead of toluene diisocyanate (TDI) and the molar ratio of fluorochemical/isocyanate was 2/3 instead of 1/3.
Fluorochemical agents
Several of the fluorochemical treating agents used in the examples of the present invention are commercially available from Minnesota Mining and Manufacturing Company, others have been prepared:
Commercially available fluorochemical treating agents
FC 3531 is a weakly cationic fluorochemical emulsion polymer
FC 461 is a nonionic fluorochemical emulsion polymer
FX 889 is a cationic fluorochemical emulsion polymer
FC 217 is a cationic fluorochemical emulsion polymer
Experimental fluorochemical treating agents
The experimental fluorochemical agents that are used in the examples are made according to the procedure described below for the synthesis of MEFOSEA/EHMA 80/20.
A polymerization bottle was charged with 150 g N-methylperfluorooctylsulfonamidoethyl acrylate (MEFOSEA), 37.5 g 2-ethylhexyl methacrylate, 9.4 g Ethoquad TM 18/25, 1.4 g n-octylmercaptan, 0.94 g V-50 TM initiator (2,2'-azobis(2-methylpropionamidine)dihydrochloride, available from Wacko, Osaka, Japan), 109 g acetone and 434 g deionized water. The reaction mixture was deaerated and covered with a nitrogen atmosphere. The polymerization bottle was capped and run in a Launder-o-meter at 73.degree. C. for 16 hours. Acetone was removed from the resulting transparent dispersion via vacuum distillation.
Table 2 lists the weight ratio of the raw materials used in the preparation of the fluorochemical polymer emulsions that are used in combination with hydrocarbon carbodiimides.
TABLE 2______________________________________Experimental fluorochemical agentsMEFOSEMA MEFOSEA EHMA N-MAM______________________________________FC-1 80 20FC-2 80 17 3FC-3 80 20FC-4 80 17 3______________________________________

Examples 1 to 7 and comparative examples C-1 to C-10
In Examples 1 to 7, blends were made of FC-3531 fluorochemical with hydrocarbon carbodiimide HCD-1 in different ratio's as given in table 3. The blends were applied to PES/CO fabric as outlined in the general treatment procedure. Comparative example C-1 only contains fluorochemical treatment agent FC-3531; comparative examples C-2 to C-8 were made using a blend of FC-3531 and fluorochemical carbodiimide FCD comparative examples C-9 and C-10 are made with the hydrocarbon and fluorocarbon carbodiimides (HCD-1 and FCD) respectively, but without addition of FC-3531.
The performance results are given in table 3.
TABLE 3__________________________________________________________________________Performance properties of PES/CO fabric treated withFC-353 1/carbodiimide mixtures (0.3% SOF) Ratio of FX-3531/ BundesmannCarbo- Carbodi- 1 5 10 % OR SREx. diimide imide min min min ABS Init. 5L Init. 5L__________________________________________________________________________C-1 / 100/0 5 3 2 17 4 4 100 801 HCD-1 90/10 5 4 3 18 5 4 100 90C-2 FCD 90/10 4 3 2 14 4 4 100 802 HCD-1 80/20 5 4 3 16 5 4 100 100C-3 FCD 80/20 3 2 1 19 4 4 100 803 HCD-1 70/30 5 4 3 15 5 4 100 90CA FCD 70/30 3 1 1 19 5 4 100 804 HCD-1 60/40 5 4 3 15 5 4 100 90C-5 FCD 6O/40 2 1 1 20 5 4 100 805 HCD-1 50/50 5 4 2 19 4 4 100 90C-6 FCD 50/10 2 1 1 21 5 4 100 806 HCD-I 40/60 5 4 2 20 4 3 100 90C-7 FCD 40/60 2 1 1 22 5 4 100 807 HCD-I 30/70 4 2 1 20 3 2 100 90C-8 FCD 30/70 2 1 1 20 5 3 100 80C-9 HCD-1 0/100 1 1 1 40 0 0 70 50C-10 FCD 0/100 1 1 1 23 5 3 100 70__________________________________________________________________________
The results of the experiments shown in this table indicate that improvement in overall repellency is obtained, even when small amounts (10%) of fluorochemical FC-3531 are replaced by hydrocarbon carbodiimide. A 40/60 mixture of FC-3531 with hydrocarbon carbodiimide still gives comparable results as the fluorochemical treatment alone. Compared to fluorocarbodiimide, overall better performance is obtained with the hydrocarbon carbodiimides. This is remarkable, especially if the fluorine content of the treatment composition is considered. In table 4, the cumulative Bundesmann ratings are given as a function of the fluorine content of the treatment solutions.
TABLE 4______________________________________Cumulative Bundesmann results of PESICO fabric treated withFC-3531/carbodiimide mixtures FC- Carbo- 3531/Carbod. Fluorine CumulativeEx. No. diimide Ratio Content* Bundesmann**______________________________________C-1 / 100/1 3.8 102 HCD-1 80/20 19.0 12C-3 FCD 80/20 26.0 64 HCD-1 60/40 14.3 12C-5 FCD 60/40 28.3 46 HCD-1 40/60 9.5 11C-7 FCD 40/60 30.5 4C-9 HCD-1 0/100 0 3 C-10 FCD 0/100 35.0 3______________________________________ Note: *fluorine content is given as weight % organically bonded fluorine **Cumulative Bundesmann is the sum of the visual ratings after 1, 5 and 1 min.
The results given in table 4 clearly demonstrate that, despite the lower fluorine content, the treatment solutions comprising fluorochemical agent and hydrocarbon carbodiimide outperform the solutions containing only fluorochemical or a combination of fluorochemical and fluorocarbodiimide.
Examples 8 to 10 and comparative examples C-11 to C-16
In examples 8 to 10 a treatment solution containing fluorochemical agent FC-3531 and hydrocarbon carbodiimide HCD-1 in a ratio of 60/40 by weight was used to treat substrates as cotton, polyester (PES) and polyamide (PA) microfibers. Comparative examples C-11, C-13 and C-15 were made without addition of carbodiimide and comparative examples C-12, C-14 and C-16 were made with a mixture of FC-3531 and fluorocarbon carbodiimide FCD in a ratio of 60/40. The results of oil and water repellency of the treated fabrics are given in table 5.
TABLE 5__________________________________________________________________________Performance properties of fabrics treated with FC-3531/carbodiimide60/40 mixtures (0.3% SOF) BundesmannEx. 1 5 10 OR SRNo. Carbod. Substrate min min min % ABS Init. 5L Init. 5L__________________________________________________________________________ 8 HCD-1 Cotton 4 2 1 25 4 5 100 90C-11 / Cotton 1 1 1 29 4 3 100 70C-12 FCD Cotton 1 1 1 32 4 4 80 70 9 HCD-1 PES 5 5 5 5 3 2 100 90C-13 / PES 5 5 5 4 2 2 100 70C-14 FCD PES 3 1 1 21 3 2 100 9010 HCD-1 PA 5 5 4 10 3 2 100 90C-15 / PA 5 4 3 27 4 0 100 60C-16 FCD PA 3 3 1 26 3 1 100 80__________________________________________________________________________
Examples 11 to 16 and Comparative examples C-17 to C-22
In examples 11 to 16 treatment solutions of different commercially available fluorochemical treatment agents and hydrocarbon carbodiimide HCD-1, in a ratio of 60/40, were applied to polyester/cotton and to polyamide microfibers. Comparative examples C-17 to C-22 were made without addition of carbodiimide. The results of oil and water repellency, also after dry cleaning (DC), of the treated substrates are in table 6.
TABLE 6__________________________________________________________________________Performance properties of substrates treated with a 60/40 blend offluorochemical agent and carbodiimide (0.3% SOF)Fluoro- Carbo- Bundesmann OR SREx. No. chemical diimide 1 min 5 min 10 min % ABS Init. 5L DC Init. 5L DC__________________________________________________________________________Polyester/cotton substrate11 FC-461 HCD-1 2 1 1 25 4 3 4 90 60 70C-17 FC-461 / 1 1 1 33 6 5 3 100 60 5012 FX-889 HCD-1 5 4 3 12 6 5 4 100 80 60C-18 FX-889 1 2 1 1 21 5 4 4 100 60 6013 FC-217 HCD-1 1 1 1 26 5 4 3 70 60 50C-19 FC-217 / 1 1 1 34 5 4 3 70 50 50Polyamide microfiber14 FC-461 HCD-1 5 5 5 9 4 2 1 100 90 90C-20 FC-461 / 5 1 1 23 5 0 3 100 50 7015 FX-889 HCD-1 5 5 5 10 5 2 2 100 80 80C-21 FX-889 / 1 5 5 5 12 4 3 100 50 8016 FC-217 HCD-1 3 2 2 35 5 2 3 90 80 80C-22 FC-217 / 2 1 1 47 6 1 3 80 50 80__________________________________________________________________________
Not only on cotton fabrics, but also on synthetic substrates, very high performance is obtained. A replacement of 40% of the fluorochemical treating agent with carbodiimide does not harm the water repellency of the treated fabric; in many cases better performance is observed.
Examples 17 to 24 and comparative examples C-23 to C-30
The same experiment was repeated with experimental fluorochemical agents. The composition of the fluorochemical treating agents is given in table 2. Examples 17 to 24 were made by treating polyester/cotton and polyamide microfiber with a blend of fluorochemical agent and hydrocarbon carbodiimide in a ratio of 50/50 by padding in order to provide a concentration of 0.4% SOF. The hydrocarbon carbodiimide used was made from MDI and Guerbitol-20 in a ratio 2/1 (same as hydrocarbon carbodiimide HCD-7 in table 1). Comparative examples C-23 to C-30 were made with fluorochemical treating agent, but without carbodiimide. The results of oil and water repellency are given in table 7.
TABLE 7__________________________________________________________________________Performance properties of substrates treated with fluorochemicaltreating agents and carbodiimide HCD-7 (0.4% SOF)Ex. Fluoro- Ratio Bundesmann OR SRNo. chemical FC/HCD 1' 5' 10' % ABS Init. 5L Init. 5L__________________________________________________________________________Polyester/cotton substrate17 FC-1 50/50 5 4 3 12 3 3 100 80C-23 FC-1 100/0 1 1 1 35 4 1 90 018 FC-2 50/50 5 4 3 10 4 2 100 80C-24 FC-2 100/0 2 1 1 25 4 2 90 5019 FC-3 50/50 5 5 4 9 6 5 100 80C-25 FC-3 100/0 1 1 1 33 6 3 90 020 FCA 50/50 5 5 4 14 6 4 100 80C-26 FC-4 100/0 2 1 1 27 6 5 90 50Polyamide microfiber21 FC-1 50/50 5 5 5 10 4 2 100 100C-27 FC-1 100/0 4 3 3 29 2 0 100 022 FC-2 50/50 5 5 4 9 3 2 100 90C-28 FC-2 100/0 4 3 2 34 2 0 100 5023 FC-3 50/50 5 5 5 11 6 4 100 80C-29 FC-3 100/0 5 4 3 19 4 0 100 024 FC-4 50/50 5 4 3 13 5 3 100 80C-30 FC-4 100/0 5 4 3 17 5 1 90 50__________________________________________________________________________
Examples 25 to 51 and comparative examples C-31 and C-32
The influence of the structure of the hydrocarbon carbodiimide was evaluated in examples 25 to 51. The carbodiimides evaluated were based on different isocyanates and various alcohols as indicated in table 1. Blends of FC-3531 fluorochemical with the hydrocarbon carbodiimides (ratio 60/40) were applied to polyester/cotton fiber and to polyamide microfiber. Comparative examples C-31 and C-32 were made without addition of hydrocarbon carbodiimide. The results of oil and water repellency are given in table 8.
TABLE 8__________________________________________________________________________Performance properties of substrates treated with blends of FC-3531with hydrocarbon carbodiimides (0.3% SOF)Ex. Hydrocarbon Bundesmann OR SRNo. Carbodiimide 1 min 5 min 10 min % ABS Init. 5L Init. 5L__________________________________________________________________________Polyester/cotton substrate25 HCD-2 4 4 3 14 5 5 100 9026 HCD-3 5 54 3 15 5 5 100 8027 HCD-4 5 4 3 15 5 5 100 7028 HCD-5 4 4 3 14 5 5 100 9029 HCD-6 5 4 2 17 5 5 100 8030 HCD-7 5 4 3 10 5 5 100 8031 HCD-8 4 3 2 21 5 5 100 6032 HCD-9 5 4 3 18 5 5 100 8033 HCD-10 5 4 2 17 5 5 100 8034 HCD-12 5 3 2 15 5 5 100 7035 HCD-13 5 4 2 20 5 5 100 8036 HCD-14 5 4 3 17 2 2 100 8037 HCD-15 5 4 2 20 5 5 100 8038 HCD-16 5 3 2 22 5 5 100 70C-31 / 5 3 1 24 5 3 100 60Polyamide microfiber39 HCD-2 5 5 5 5 5 4 100 9040 HCD-3 5 5 4 10 5 5 100 8041 HCD-4 5 5 5 9 5 5 100 8042 HCD-5 5 5 5 7 5 4 100 9043 HCD-6 5 5 4 14 5 5 100 8044 HCD-7 5 5 5 7 5 4 100 9045 HCD-8 5 4 4 13 4 5 100 6046 HCD-9 5 5 5 11 5 5 100 8047 HCD-10 5 5 4 13 5 5 100 7048 HCD-12 5 5 4 11 5 5 100 8049 HCD-13 5 4 4 13 5 5 100 8050 HCD-15 5 5 5 11 5 3 100 8051 HCD-16 5 5 5 11 5 5 100 60C-32 / 5 4 3 14 4 3 100 50__________________________________________________________________________
In both experiments it becomes clear that the hydrocarbon carbodimides improve the overall water and oil repellency of the treated fabrics, both of cellulose type fabrics and synthetic fabrics.
Examples 52 to 63
Examples 52 to 63 were made to illustrate that the disclosed carbodiimides can be emulsified using a variety of surfactants or mixtures of surfactants. The carbodiimide evaluated was made from MDI/Isofol 18T (2/1; same as HCD-11 in table 1). The carbodiimide was emulsified according to the general procedure. The kind and the level of surfactants evaluated are given in table 9. The carbodiimide emulsion was blended with fluorochemical treating agent FC-3531 at a ratio of 60/40 FC/HCD. Polyester/cotton and polyamide fibers were treated with this mixture at 0.3% SOF and cured for 3 minutes at 150.degree. C. The results of oil and water repellency and durability are given in table 9.
TABLE 9__________________________________________________________________________Performance properties of fabrics treated witb FC-3531/hydrocarboncarbodiimide HCD-11 (60/40 0.3% SOF) using various surfactants BundesmannEx. (%) 1 5 10 % OR SRNo. Surfactant Surf. min. min. min. ABS Init. 5L Init. 5L__________________________________________________________________________Polyester/cotton substrate52 Marlowet 5401 5 5 3 2 17 5 4 100 8053 Ethoquad HT-25 5 5 4 3 16 5 4 100 9054 Arquad T-50 5 5 3 3 13 5 4 100 8055 Arquad 2HT-75 5 5 5 3 11 5 4 100 9056 Arquad 2HT-75 + 4 5 4 3 13 5 3 100 90 Atpol E5721 457 Arquad 2HT-75 + 4 5 5 4 12 5 4 100 90 Atlas G1281 4Polyamide substrate58 Marlowet 5401 5 5 4 4 14 5 4 100 8059 Ethoquad HT-25 5 5 5 4 13 5 4 100 9060 Arquad T-50 5 5 3 2 26 5 4 100 8061 Arquad 2HT-75 5 5 5 5 7 5 4 100 9062 Arquad 2HT-75 + 4 5 5 5 6 5 3 100 90 Atpol E5721 463 Arquad 2HT-75 + 4 5 5 5 12 5 4 100 90 Atlas G1281__________________________________________________________________________
Examples 52-63 illustrate that the disclosed carbodiimides can be emulsified using a variety of surfactants or a mixture of surfactants. In particular, examples 55 to 57 and 61 to 63, show that substrates, treated with compositions emulsified with ammonium surfactants having two long chain alkyl groups, show high overall performance.
Examples 64 to 73
Examples 64 to 73 were done in order to evaluate the performance of compositions comprising fluorochemical treating agent and hydrocarbon carbodiimide containing emulsion aids. The carbodiimide emulsions from examples 64 and 69 were prepared according to the general method (10% surfactant based on hydrocarbon carbodiimide solids); the carbodiimide emulsions from examples 65, 67, 68, 70 and 72 to 73 contain only 5% surfactant and the emulsions from example 66 and 71 do not contain any emulsifier at all. Blends of FC-3531 with the hydrocarbon carbodimides (ratio 60/40) were applied to polyester/cotton and to polyamide microfiber. The results of oil and water repellency are given in table 10.
TABLE 10__________________________________________________________________________Performance properties ofsubstrates treated with blends of FC-3531and hydrocarbon carbodiimide (0.3% SOF)Ex. Hydrocarbon % Bundesmann OR SRNo. Carbodiimide Surfact. 1' 5' 10' % ABS Init. 5L Init. 5L__________________________________________________________________________Polyester/cotton substrate64 HCD-18 10 5 3 2 17 5 4 100 7065 HCD-18 5 5 3 2 18 5 4 100 8066 HCD-18 0 4 2 1 21 5 3 100 7067 HCD-19 5 4 3 2 18 5 4 100 8068 HCD-21 5 5 4 2 17 5 4 100 80Polyamide microfiber69 HCD-18 10 5 4 4 18 4 3 100 8070 HCD-18 5 3 2 1 31 4 3 90 8071 HCD-18 0 4 2 2 33 4 2 100 8072 HCD-19 5 5 5 5 10 4 3 100 9073 HCD-21 5 5 5 5 19 4 3 100 90__________________________________________________________________________
Examples 74 to 77 and comparative examples C-33 to C-36
Following experiment is done in order to illustrate the influence of the addition of resins to the fluorochemical/carbodiimide treatment formulations. Examples 74 and 76 were made by treating cotton and polyester/cotton with a blend containing fluorochemical agent FC-3531, hydrocarbon carbodiimide HCD-1 (ratio 60/40 FC/HCD-1), Reaknitt DFL (a carbamid resin, available from CHT R. Beitlich GmbH, Tuebingen, Germany) and CHT-catalyst (available from CHT R. Beitlich, Tuebingen, Germany). The resin was added to the treatment solution containing fluorochemical agent and hydrocarbon carbodiimide at a concentration of 50 g/l. The catalyst was added at a concentration of 5 g/l. The treated substrates were cured at 150.degree. C. for 3 min. The performance of the treated substrates was compared to substrates treated with a mixture of FC-3531 and HCD-1 (examples 75 and 77) and to substrates treated with only FC-3531 (Comparative examples C-33 and C-35) or with a mixture of FC-3531 and resin (C-34 and C-36). The results of oil and water repellency test are given in table 11.
TABLE 11__________________________________________________________________________Performance properties of substrates treated with blends of FC-3531/hydrocarbon carbodiimide/resin (0.3% SOF) BundesmannEx. FC- 1 5 10 % OR SRNo. 3531 HCD-1 Resin min min min ABS Init. 5L Init. 5L__________________________________________________________________________Cotton Substrate74 x x x 5 3 2 21 3 3 100 9075 x x 3 2 100 80C-33 x 2 1 90 50C-34 x x 2 1 1 41 2 2 90 70Polyester/cotton76 x x x 5 4 3 14 6 4 100 10077 x x 5 3 2 17 5 4 100 80C-35 x 4 3 2 19 5 4 100 70C-36 x x 5 4 3 12 6 5 100 90__________________________________________________________________________
The results of this test show that the dynamic water repellency and the durability of the treatment can further be improved by adding a carbamid resin to the solution of fluorochemical treating agent and hydrocarbon carbodiimide. Compared to the samples without hydrocarbon carbodiimide, the improvement in properties is considerable.

Number	Name	Date
2941983	Smeltz	Jun 1960
2941988	Wolf	Jun 1960
3341497	Sherman et al.	Sep 1967
3420697	Sweeney et al.	Jan 1969
3445491	Pacini	May 1969
3470124	Van Eygen	Sep 1969
3544537	Brace	Dec 1970
3546187	Tandy	Dec 1970
3862989	Hansen	Jan 1975
3896251	Landucci	Jul 1975
3993833	Esmay	Nov 1976
4054592	Dear et al.	Oct 1977
4067945	Elmer	Jan 1978
4215205	Landucci	Jul 1980
4426466	Schwartz	Jan 1984
4468527	Patel	Aug 1984
4477498	Deine et al.	Oct 1984
4540497	Chang et al.	Sep 1985
4560487	Brinkley	Dec 1985
4566981	Howells	Jan 1986
4834764	Deiner et al.	May 1989
5132028	Nagase et al.	Jul 1992
5164252	Henning et al.	Nov 1992
5498747	Pohl et al.	Mar 1996

Carbodiimide compound and water repellent compositions

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (24)

Foreign Referenced Citations (1)

Non-Patent Literature Citations (4)