Patent Application
20080093009
The present invention relates to a method and apparatus for bonding materials by combustion synthesis. The invention comprises providing two or more materials to be bonded with a combustion synthesis material interspersed between them. One or more carbon fibers are laid into the combustion synthesis material. Preferably the fibers are spaced evenly and parallel across the combustion synthesis material with no more than a few millimeters between parallel fibers. The fibers are connected to a voltage source. The voltage source should provide a voltage sufficient to heat the fibers rapidly. Typical voltages would be about 100 volts. Preferably, the fibers are rapidly heated to about 2000° C. or higher. The heating is performed until ignition of the combustion synthesis material occurs.
Combustion synthesis materials. The combustion synthesis materials that are used with this invention can be any that are typically known and used in the art for combustion synthesis. Preferably, the product of the combustion synthesis reaction will be a ceramic. Preferably, the combustion synthesis materials consist of a finely ground metal and a finely ground material capable of oxidizing the metal. In a highly preferred embodiment the mixture will form titanium carbide after reaction.
Carbon fibers. The carbon fibers that can be used with this invention are not particularly limited. The carbon fibers of this invention are usually produced by pyrolysis of an organic precursor fiber in an inert atmosphere at high temperature. The carbon fibers may also be used in the form of carbon fiber bundles of two or more carbon fibers. Preferably, the carbon fibers have a diameter between about 3 and 100 microns and are spaced about 10 mm apart or less. More highly preferred the carbon fibers have a diameter between about 5 and 20 microns. Even more highly preferred the carbon fibers have a diameter between about 9 and 12 microns. More highly preferred the carbon fibers are spaced between about 3 and 8 mm apart. Even more preferably the carbon fibers are spaced between about 4 and 6 mm apart.
Carbon fibers may be produced from different types of materials known as precursor fibers, such as polyacrylonitrile (PAN), rayon, and petroleum pitch. Carbon fibers are typically produced by the pyrolytic scission of the oxygen, nitrogen, and other non-carbon fractions of the precursor fiber, leaving only carbon in the fiber. Following this reducing step, the fibers are typically heat-treated in a furnace to produce fibers with the desired state of graphitization. Carbon fibers are produced at furnace temperatures of typically around 1,000-2,000° C.
Carbon-carbon composites. Any carbon carbon-carbon composites that are known in the art can be used with this invention. Preferably the carbon-carbon composites are those that would typically be used in friction material for brakes, more preferably aircraft brakes. Carbon-carbon composites are generally made of carbon fibers, and a carbon matrix. Carbon-carbon composites and methods of their manufacture are well known to those in the art. Carbon-carbon composites are described, for example, in Carbon-Carbon Materials and Composites, John D. Buckley and Dan D. Edie, Noyes Publications, 1993, which is incorporated herein by reference. The carbon-carbon composites of the present invention can be made with thermosetting resins as matrix precursors. These materials generally possess low densities 1.55-1.75 g/cm3 and have well-distributed microporosity. Composites made with resins as the matrix generally exhibit high flexural strength, low toughness, and low thermal conductivity.
The carbon-carbon composites of the present invention can also be made with pitch as the matrix precursor. These materials, after densification, can exhibit densities in the range of 1.7-2.0 g/cm3 with some mesopores. The carbon-carbon composites of the present invention can also be made by chemical vapor deposition (CVD). This technique uses hydrocarbon gases, and the carbon-carbon composites that are produced possess intermediate densities, and have matrices with closed porosities. Composites with pitch as the precursor, and the CVD-based composites, can be made with very high thermal conductivity (about 400-700 W/MK) in the fiber direction.
In one preferred embodiment, the carbon-carbon composites of the present invention are prepared from carbon preforms. Carbon preforms are made of carbon fibers, which can be formed from pre-oxidized acrylonitrile resin. The carbon fibers can be layered together to form a shape, such as a friction brake annular disc. The shape is heated and infiltrated with methane, or another pyrolyzable carbon source, to form the carbon-carbon composite. A carbon-carbon composite prepared in this manner is preferred, and will have a density in the range of about 1.6 g/cm3 to about 1.9 g/cm3. More highly preferred is a carbon-carbon composite with a density of approximately 1.75 g/cm3.
One highly preferred carbon-carbon composite is CARBENIX® 4000. This carbon/carbon composite material is manufactured by Honeywell International, Inc. as an aircraft brake carbon/carbon composite friction material. CARBENIX® 4000 is made of non-woven polyacrylonitrile precursor carbon fibers, densified with carbon utilizing chemical vapor deposition.
Another highly preferred carbon-carbon composite is CARBENIX® 2400, also manufactured by Honeywell International, Inc. CARBENIX® 2400 is an aircraft brake carbon/carbon composite friction material, consisting of pitch precursor carbon fibers, densified with carbonized phenolic resin and with carbon from chemical vapor deposition.
Heating methods. Methods of heating the parts to be bonded include any that would typically be known in the art for heating parts in combustion synthesis. Electrical heating methods are preferred. Heating in a conventional furnace may also be used. Heating is generally performed under an non reactive gas such as nitrogen or argon.
Combustion synthesis apparatus. One embodiment of a combustion synthesis apparatus in accord with the present invention is shown in
Preferred embodiment. The surfaces of the parts to be bonded are first prepared. The surfaces are ground smooth or other mating surfaces are created. The Combustion Synthesis materials are then prepared. The combustion synthesis materials consist of a finely ground metal and a finely ground material capable of oxidizing the metal. The preferred mixture will form titanium carbide. These are mixed in stoichiometric or non-stoichiometric quantities and the powder is placed on the surface of one of the parts to be bonded. The mating part is then placed on top of the powder.
Multiple carbon fibers are laid into the powder mixture before the mating piece is placed onto the powder. The fibers have a diameter of between about 3 and 100 microns. They are spaced evenly and parallel across the powder with no more than about 6 millimeters between parallel fibers. The fibers are then connected to a voltage source at each end sufficient to heat the fibers rapidly to over approximately 2000° C. Force is then applied to join the parts during combustion. Once initiated throughout the powder layer, the energy created by the combustion itself is sufficient to complete the combustion reaction and the bonding process.
The powder is then ignited. The entire load of powder is ignited within about 1 second so that all of the combustion synthesis material is liquid at the same time. This may be done by heating the entire assembly to above the ignition point of the powder mixture. For titanium carbide this is over approximately 1500° C. While the material is in the liquid phase, the parts are pressed together. The melting point of the resulting titanium carbide is very high, i.e., over approximately 2500° C. The liquid titanium carbide then quickly freezes bonding the carbon-carbon parts together.
The preferred embodiments given above are only examples of the invention, and are not intended to define the full scope of the invention. One skilled in the art would recognize many variations of this invention that are also intended to be encompassed by the claims.