Patent Application
20200277193
This invention relates generally to the field of nanotechnology and concerns carbon nanosphere-decorated carbon nanotubes.
Carbon nanotubes (CNTs) have unique features, such as high mechanical strength, electrical and thermal conductivity, high chemical stability, and large surface area to volume ratios. They could be useful for various applications including catalytic processes, water purification, drug delivery, gene transfer, transparent conducting films and electrochemical analysis.
Previously CNTs have been decorated with either organic compounds or metallic nanoparticles. Decorated carbons reported in literature or available in markets are composites (or complexes) prepared from carbon and metal ions. Regardless of the method of inserting metal ions into a matrix of carbon materials, the insertion of metal ions is often mediated by complex formation.
Carbon aerogels (CA), or carbon nanogels, are ultralight and porous, have electric double-layer properties, and low thermal conductivity. Carbon aerogels could be used in catalysis, catalysis support, ion separations, supercapacitors, and battery materials.
There is a need in the field for improved materials that combine the properties of carbon nanotubes and carbon aerogels. Nano-carbon decoration, based on decorating carbon by carbon has not been described in literature.
In one aspect, provided herein is a process for preparing a carbon nanotube in contact with an aerogel carbon nanosphere, the process comprising:
In another aspect, provided herein is a composition comprising carbon nanotubes in contact with aerogel carbon nanospheres. In a further aspect, provided herein is a composition comprising carbon nanotubes in contact with aerogel carbon nanospheres, where the carbon nanotubes in contact with aerogel carbon nanospheres are prepared by a process described herein in the detailed description section and/or the Examples section.
Also provided herein are methods for preparing carbonized resorcinol-formaldehyde aerogels which can be decorated onto carbon nanotubes.
The features and advantages of the invention will be more readily understood from the following detailed description which should be read in conjunction with the accompanying drawings.
Described herein are methods for decorating a first carbon form with a second carbon form different in shape from the first carbon form. As used herein “decorate” means contacting, adhering, annealing, impregnating, or any other non-covalent bonding method of contacting the first carbon form with the second carbon form. Described herein are activated resorcinol/formaldehyde aerogel carbon nanospheres (RFA-CNs) decorating multiwalled carbon nanotubes (MWCNTs).
“Carbon nanotubes” refers to allotropes of carbon with a cylindrical nanostructure.
“Aerogel” or “carbon aerogel” refers to a synthetic material derived from a gel, in which the liquid component for the gel has been replaced with a gas, rendering the material porous and light. A carbon aerogel consists primarily of porous carbon.
“Nanosphere,” “Nanospherical,” or “Nanosphere-dimensioned” refers to spherical material (e.g., particles) with a nanometer diameter e.g., diameters ranging from 1 nm to about 100 nm.
“Resorcinol-formaldehyde aerogel carbon nanosphere” refers to powdered or otherwise solid nanosphere-dimensioned resorcinol-formaldehyde aerogels. The resorcinol-formaldehyde aerogels are formed by the reaction of resorcinol with formaldehyde to form a gel, then replacing the solvent in the gel with a gas (e.g., carbon dioxide gas).
“Room temperature” refers to ambient temperature, and depending on location, may range from about 18° C. to about 35° C. Room temperature is understood to mean 25° C. unless stated otherwise explicitly.
“Solvent exchange” refers to a technique of washing out or substituting a first solvent (e.g., from a gel) and replacing it with a second solvent. Solvent exchange is typically accomplished by adding an excess of a second solvent to a mixture comprising the first solvent, then removing (e.g., decanting) the excess solvents from the mixture and repeating the process till the first solvent is substantially (e.g., more than 50%) replaced by the second solvent.
“Organic solvent” refers to any carbon-hydrogen based solvent. Examples of organic solvents include and are not limited to methanol, ethanol, isopropanol, acetone, tetrahydrofuran, benzene, toluene, acetonitrile, dichloromethane, and the like.
As used herein, the term “about,” when qualifying a number, e.g., about 15% w/w, refers to the number qualified and optionally the numbers included in a range about that qualified number that includes ±10% of the number. For example, “about 75° C.,” includes 75° C. as well 68° C., 69° C., 70° C., 71° C., 72° C., 73° C., 74° C., 75° C., 76° C., 77° C., 78° C., 79° C., 80° C., 81° C., 82° C., or 83° C.
Processes
In a first aspect, provided herein is a process for preparing a carbon nanotube in contact with a carbon nanosphere, the process comprising:
In some instances, described herein is a process for preparing a carbon nanotube in contact with a carbon nanosphere, the process comprising:
In a group of embodiments, the carbon nanospheres and the carbon nanotubes are mixed in a dry weight ratio of about 1:1 and stirred in the solvent.
In some instances, the solvent is a protic solvent (e.g., an alcohol). In some instances the solvent is methanol, ethanol or isopropanol. In some instances, the solvent is methanol. In other instances, the solvent is ethanol. In other instances, the solvent is isopropanol.
In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 1 day-500. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 185 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 1 day-400 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 1 day-300 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 1 day-200 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 1 day-100 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 400 days-500 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 300 days-500 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 200 days day-500 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 100 days-500 days. In some embodiments of the process, the mixture in step (iii) is refluxed for a period of about 415 days. In some embodiments the refluxing is conducted in a sealed system.
In a group of embodiments, the reflux temperature is about 75° C.-125. In a group of embodiments, the reflux temperature is about 100° C. In other instances, the reflux temperature is any suitable temperature based on the solvent being used in the mixture and may be at least the boiling point of the solvent or higher.
In some instances, the residue of step (iv) is dried for a period of about 1 day-5. In some instances, the residue of step (iv) is dried for a period of about 3 days. In some instances, the residue of step (iv) is dried for a period of about 5 days-15 days. In further instances, the residue of step (iv) is dried for any suitable length of time so as in order to obtain carbon nanotubes decorated with carbon nanospheres with low moisture and/or solvent content.
In some instances, the carbon nanotubes are multiwalled carbon nanotubes. In some instances, the multiwalled carbon nanotubes have lengths ranging from 1 μm to 1 cm. In some instances, the multiwalled carbon nanotubes have widths ranging from 1 μm to 1 cm. In some instances, the multiwalled carbon nanotubes have thickness ranging from 0.5 nm to 500 nm in width. In some instances, the multiwalled carbon nanotubes have.
In a group of embodiments, the carbon nanosphere is a resorcinol-formaldehyde aerogel carbon nanosphere, (e.g., a resorcinol-formaldehyde aerogel which is carbonized and/or activated).
In some instances, provided herein is a process wherein the resorcinol-formaldehyde aerogel carbon nanosphere is prepared by a process comprising carbonizing and activating resorcinol-formaldehyde aerogels.
In some instances, provided herein is a process for preparing resorcinol-formaldehyde aerogel carbon nanospheres, the process comprising
In some instances of the process, the resorcinol-formaldehyde aerogel is prepared by a process comprising:
In some other instances of the process, the resorcinol-formaldehyde aerogel is prepared by a process comprising:
In some instances, the vials are propylene vials. In other instances the vials are glass vials.
In a group of embodiments, the acetic acid is 2% acetic acid. In other instances, the acetic acid is 4%, 6%, 8% or 10% acetic acid. In some instances, the acetic acid is glacial acetic acid.
In some instances the catalyst is an inorganic carbonate. In some instances, the catalyst is sodium carbonate, potassium carbonate, or cesium carbonate, or a combination thereof. In a specific instance, the catalyst is sodium carbonate.
In any of the embodiments described above for the preparation of the resorcinol-formaldehyde aerogel, the pH of about 7 is obtained by addition of an acid and a base. In some of such instances, the pH of about 7 is obtained by addition of nitric acid and ammonium hydroxide.
In some instances, the processes herein comprises
In the process for synthesis of the resorcinol-formaldehyde aerogel described above, the process comprises, in some instances, the further steps of
In some instances the organic solvent is an aprotic water miscible solvent. In some instances, the organic solvent is acetone or tetrahydrofuran. In other instances, the organic solvent is dimethyl formamide (DMF), dimethylsulfoxide (DMSO), or acetonitrile (ACN). In a specific instance, the organic solvent is acetone.
In some instances, the process comprises flowing liquid or supercritical carbon dioxide through the cured gel.
In some cases, the process described above for the preparation of the resorcinol-formaldehyde aerogel further comprises the steps of
In a group of embodiments, the cured gel which is placed in an extractor under liquid carbon dioxide is at a pressure ranging from 1 to 10 MPa and a temperature ranging from about 15° C. to about 25° C. In a group of embodiments, the cured gel which is placed in an extractor under liquid carbon dioxide is at a pressure of 5 MPa and a temperature of 20° C.
In a group of embodiments, the extractor is depressurized to about 1.2 MPa.
In a group of embodiments, after depressurizing, the liquid carbon dioxide is allowed to flow through the gel at a temperature of 20° C. for a time ranging from about 1 to 2.5 hours. In a group of embodiments, after depressurizing, the liquid carbon dioxide is allowed to flow through the gel at 20° C. for a time of 2 hours.
In certain instances, the temperature of the extractor is increased to a temperature of 25° C., and the pressure in the extractor is raised to 5 MPa. In some of such instances, the extractor is maintained at the temperature of 25° C. and the pressure of 5 MPa for at least 2 hours.
In some instances, the carbonizing and activating of the dried resorcinol-formaldehyde aerogel comprises the steps of
In some instances, after complete purging of air with nitrogen, the heating of the dried resorcinol-formaldehyde aerogel is conducted at a rate of about 5-15° C./min In some instances, after complete purging of air with nitrogen, the heating of the dried resorcinol-formaldehyde aerogel is conducted at a rate of about 10° C./min up to a temperature of about 600° C.-1000° C., where the furnace has a carbon dioxide gas flow rate of about 100-250 cm3/min, and maintaining the sample at the said temperature. In some instances, the heating of the dried resorcinol-formaldehyde aerogel is conducted at a rate of 10° C./min up to a temperature of 700° C., where the furnace has a carbon dioxide gas flow rate of about 150 cm3/min, and maintaining the sample at the said temperature.
In some instances, after complete purging of air with nitrogen, the heating of the dried resorcinol-formaldehyde aerogel is conducted at a rate of about 5-15° C./min In some instances, after complete purging of air with nitrogen, the heating of the dried resorcinol-formaldehyde aerogel is conducted at a rate of about 10° C./min up to a temperature of 500° C., where the furnace has a nitrogen gas flow rate of about 100 cm3/min, maintaining the sample at the said temperature for 3 hours, and cooling to room temperature while flowing nitrogen to produce carbonized gel. In some instances, the heating of the carbonized gel is conducted at a rate of 10° C./min up to a temperature of 700° C., where the furnace has a carbon dioxide gas flow rate of about 150 cm3/min, maintaining the sample at the said temperature for 1 hour and then cooling to room temperature to produce an activated carbon gel.
In some examples of the processes described herein, the carbon nanotubes are characterized by X-ray diffraction pattern comprising peaks at one or more, or all of 26°, 42° and 53.8° degrees 2θ.
In some examples of the processes described herein, the carbon nanotubes are characterized by Raman spectra shifts of 1314 cm−1 (D band), 1576 cm−1 (G band), and 2625 cm−1 (G′ band).
In some examples of the processes described herein, the carbon nanotubes are characterized by Raman spectra shifts of 1314 cm−1 (D band) of intensity ID, 1576 cm−1 (G band) of intensity IG, and 2625 cm−1 (G′ band), and wherein the carbon nanotubes in contact with carbon nanospheres are characterized by ID/IG ratios of 0.48, 1.25, 0.50, 0.52 and 1.00 for the MWCNTs, RFA-CNs, OD, 185D and 415D samples, respectively.
Also provided herein is a carbon nanotube in contact with carbon nanospheres prepared by any process described above and herein.
Further provided herein is a composition comprising carbon nanotubes in contact with carbon nanospheres described herein.
In an instance, provided herein is a composition comprising carbon nanotubes in contact with carbon nanospheres where the carbon nanotubes in contact with carbon nanospheres are prepared by any process described above and in the Examples section.
In a specific instance, the carbon nanospheres are resorcinol-formaldehyde aerogel carbon nanospheres prepared by a process described above and in the Examples section.
In an instance, for the compositions described herein, the carbon nanotubes are characterized by Raman spectra shifts of 1314 cm−1 (D band) of intensity ID, 1576 cm−1 (G band) of intensity IG, and 2625 cm−1 (G′ band), and wherein the carbon nanotubes in contact with an aerogel carbon nanosphere are characterized by ID/IG ratios of 0.48, 1.25, 0.50, 0.52 and 1.00 for the MWCNTs, RFA-CNs, OD, 185D and 415D samples, respectively.
Provided herein is a catalyst comprising the composition comprising carbon nanotubes in contact with carbon nanospheres.
Also provided herein is a drug delivery agent comprising the composition comprising carbon nanotubes in contact with carbon nanospheres.
In some embodiments, provided herein are drug delivery devices. For example, set forth herein are uploaded drugs with MWCNTs/RFA-CNs, coated MWCNTs/RFA-CNs onto drugs, and mixed drugs with MWCNTs/RFA-CNs.
In some embodiments, provided herein are compositions useful for gene transfer or electrochemical analysis. For example, in some embodiments, set forth herein is a sensor that combines nucleic acid layers with electrochemical transducers to produce a biosensor for simple, accurate and inexpensive patient diagnosis. Examples include but are not limited to nanoparticle-based electrochemistry amplification, direct of DNA electrochemistry. See also T. Gregory Drummond, Michael G. Hill, Jacqueline K Barton. Electrochemical DNA Sensors. Nature Biotechnology, volume 21, pages 1192-1199 (2003), the entire contents of which are herein incorporated by reference in their entirety for all purposes.
Further provided herein is a transparent conducting film comprising the composition comprising carbon nanotubes in contact with aerogel carbon nanospheres.
In one instance, described herein is a method for water purification, the method comprising contacting water with a composition comprising carbon nanotubes in contact with carbon nanospheres.
In another instance, provided herein is a method for gene transfer or electrochemical analysis comprising the use of a composition comprising carbon nanotubes in contact with carbon nanospheres.
Contemplated uses for the carbon nanotubes in contact with carbon nanospheres described herein (e.g., MWCNTs/RFA-CNs described herein) could include and are not limited to alcohol detection (e.g., ethanol gas sensors), modification of mechanical, electrical, thermal and chemical properties, field effect transistors, laser components, energy storage materials and biotechnology applications, elastomer application, lithium-sulfur batteries, biosensor, antioxidant, membranes, super hydrophobicity and corrosion resistance, esterification of acetic acid with methanol, dyes removal, paint applications, self-imaging applications, antimicrobial materials, carbon dioxide sensors, supercapacitor electrodes, printing process, DNA sensors, humidity sensing, removal of antibiotics, polymer actuator, anti-cancer treatments, lubricant additives, adsorption of proteins, shape-memory composites, supercapacitors, hydrogen storage, gas adsorption, adsorption of organic compounds, photosensitization, catalytic applications, sensors for aromatics, thermal insulation materials, biomedical applications, removal of organic solvents/oils, methane storage, emulsion separation, artificial neural network, proton exchange membrane fuel cells, sodium-ion batteries, solar steam generation, pulmonary delivery, solar thermal receivers, molecular sieves, photovoltaics, H2O2 sensing, electromagnetic interference shielding, strain sensors, direct methanol microfluidic fuel cell, water purification, microwave absorption, building retrofits, removal of heavy metal ions, and the like.
FT-Raman spectra were measured by a Bruker FT-Raman spectrometer of type RFS 100/S that is attached to a Bruker-IFS 66/S spectrometer, which provides high resolution to better than 0.10 cm−1, and high sensitivity and stability. The diode-pumped, air-cooled Nd: YAG laser source with maximum laser power of 1500 mW at 1064 nm is controlled with full automation. The standard RFS 100/S configuration provides a spectral range of 70-3600 cm−1 (Stokes shift) and 100 to 2000 cm−1 (anti-Stokes shift).
The morphology of carbon materials were observed with a FEI Nova™ nanoscanning electron microscope 450 (Nova NanoSEM).
Transmission electron microscopy of (TEM) was conducted with a FEI Tecnai G2 F20 FE-TEM.
Thermogravimetric analyses (TGA) were carried out using a Perkin Elmer Pyris6 TGA analyzer under a flow of N2 gas in range of 30° C. to 800° C. with a heating rate of 10° C./min.
X-ray diffraction (XRD) measurements were conducted by Miniflex II Benchtop XRD apparatus, manufactured by Rigaku Corporation Japan. The 2θ scan data were collected at 0.05° intervals over the range of 5 to 90°, and at a scan speed of 0.05°/min. XRD Cu k alpha.
Synthesis of aerogels.
Aerogels were prepared from resorcinol and formaldehyde in presence of Na2CO3, which was used as catalyst. The pH of the starting solution was adjusted to a neutral value (pH ˜7) with HNO3 and NH4OH. The quantities of resorcinol (R), Na2CO3 catalyst (C), formaldehyde (F), and water (W) that were utilized in the preparation of the aerogel were 12.44 gram, 0.0240 gram, 17.40 ml, and 32.60 ml, respectively. These quantities correspond to the molar ratios of R:F=0.5 R:C=500, and R:W=0.05 at pH 7. The medium reaction temperature was fixed at 70±1° C. Resorcinol and Na2CO3 were weighed and mixed with H2O in Erlenmeyer flasks, and the solution was stirred magnetically until the resorcinol and Na2CO3 are fully dissolved. Then, formaldehyde was added to the solution while stirring. After that, the pH value was adjusted at −7 by using HNO3 and NH4OH solutions. The RF solution was then transferred into polypropylene vials, sealed, and placed in an oven at 70±1° C. for 7 days. To prohibit the dehydration of the gel formed, and to improve their crosslinking density, 2% of CH3COOH solution was added onto the gel surface upon its solidification. After 7 days, the polypropylene vials are transferred from the oven and let to cool down to room temperature. The excess solution on top of the formed gel was decanted and disposed. The remaining (wetting) solution was solvent exchanged with acetone at ambient temperature by casting acetone on top of the sample and keeping it at ambient temperature for 24 h, and then replacing the remaining acetone with fresh acetone daily for 3 days. After the third day of solvent exchange, the samples were dried by supercritical carbon dioxide extraction. This process was carried out by multiple steps; after the cured gel was placed in the dryer, liquid carbon dioxide was introduced at a pressure of 5 MPa and a temperature of 20° C. to replace the acetone within the gel structure. The exit valve was opened and the extractor was depressurized to 1.2 MPa, letting the liquid carbon dioxide flow through the gel at 20° C. for a time ranging from 60 to 150 min. Then, the temperature was increased to approach the supercritical state of CO2 at 25° C. and 5 MPa. This supercritical state was maintained for 120 min. After that, the extractor was depressurized slowly to atmospheric pressure and the dried resorcinol/formaldehyde aerogel was retrieved. The supercritical drying was conducted by using a critical point dryer (E3100 Critical Point Dryer, Quorum Technologies—Preparation for Excellence, UK).
Carbonization and Activation of Carbon Aerogels
The dried resorcinol/formaldehyde aerogel was placed in a ceramic boat crucible into a programmable electric-heated tube furnace (Nabertherm GmbH, Germany), with a continuous flow of N2 gas (100 cm3/min). The furnace was first maintained at room temperature for 30 min to ensure that air is fully purged with the flowing N2 gas. Afterwards, the furnace was heated up to a temperature of 500° C. with a heating rate of 10° C./min, was maintained at 500° C. for 180 min, and then allowed to cool down spontaneously to ambient temperature while flowing N2 gas. The resulting RF carbon aerogel was then activated in the same tube furnace (after cleaning it thoroughly) by switching the N2 gas with carbon dioxide gas flow (150 cm3/min), heating the sample again at a rate of 10° C./min up to 700° C., maintaining the sample at this temperature for 60 min, and letting the sample to cool down spontaneously to room temperature while flowing the carbon dioxide gas. The outcome sample is redeemed to be an activated carbon aerogel and is called resorcinol-formaldehyde aerogel activated carbon nanospheres, which are denoted hereafter as RFA-CNs.
Synthesis of Carbon Nanosphere-Decorated Carbon Nanotubes
The MWCNTs and RFA-CNs were mixed in a fixed weight proportion of 1:1 in reflux with methanol while stirring for 0 (OD), 185 (185D) and 415 (415D) days at 100° C. The time “0 day” refers to mixing the samples manually in dry state. The identity of these samples will be called hereafter; OD, 185D and 415D, respectively. Samples are then dried at 110° C. for 3 days.
Table 1 below shows the Thermogravimetric analysis (TGA) weight losses of the hybrid MWCNTs/RFA-CNs at 0 days, 185 days, and 415 days of reaction time, at different temperatures, compared to MWCNTs and RFA-CNs.
As can be seen from
While several particular forms of the invention have been illustrated and described, it will also be apparent that various modifications can be made without departing from the scope of the invention. It is also contemplated that various combinations or subcombinations of the specific features and aspects of the disclosed embodiments can be combined with or substituted for one another in order to form varying modes of the invention. Accordingly, it is not intended that the invention be limited, except as by the appended claims.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/IB2019/051690 | Mar 2019 | US |
| Child | 16804212 | US |